Dye-sensitized solar cells (DSSCs) based on anatase TiO2 hollow spheres (TiO2HS)/multi-walled carbon nanotubes (CNT) nanocomposite films are prepared by a directly mechanical mixing and doctor blade method. The prepared samples are characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV-vis absorption spectroscopy and N2 adsorption-desorption isotherms. The photoelectric conversion performances of the DSSCs based on TiO2HS/CNT composite film electrodes are also compared with commercial-grade Degussa P25 TiO2 nanoparticles (P25)/CNT composite solar cells at the same film thickness. The results indicate that the photoelectric conversion efficiencies () of the TiO2HS/CNT composite DSSCs are dependent on CNT loading in the electrodes. A small amou...

British Library Electronic Table of Contents (United Kingdom)

The electrical characteristics of thin TiO2 films prepared by metal?organic chemical vapor deposition grown on a p-type InP substrate were studied. For a TiO2 film of 4.7?nm on InP without and with ammonium sulfide treatment, the leakage currents are 8.8?10?2 and 1.1?10?4?A/cm2 at +2 V bias and 1.6?10?1 and 8.3?10?4?A/cm2 at ?2?V bias. The lower leakage currents of TiO2 with ammonium sulfide treatment arise from the improvement of interface quality. The dielectric constant and effective oxide charge number density are 33 and 2.5?1013?cm2, respectively. The lowest mid-gap interface state density is around 7.6?1011?cm?2?eV?1. The equivalent oxide thickness is 0.52?nm. The breakdown electric field increases with decreasing thickness in the range of 2.5 to 7.6?nm and reaches 9.3?MV/cm at 2.5?n...

British Library Electronic Table of Contents (United Kingdom)

Randomly oriented ZnO microsheets were successfully self-assembled on TiO2 nanoparticle (TN) film to act as the scattering layer via a cathodic electrodeposition process. The light scattering properties of ZnO microsheets were studied by UV-Vis spectrometer in the 400?800 nm wavelength range. It was found that ZnO microsheets exhibited excellent ability to scatter the incident light for ZnO microsheet-TiO2 nanoparticle (ZT) composite films. The results showed that dye-sensitized solar cells (DSSCs) fabricated with ZT composite films showed higher short-circuit density (J sc) and conversion efficiency than TN-based DSSCs, due to the light scattering properties of ZnO microsheets.

Energy Technology Data Exchange (ETDEWEB)

Titanium oxides were grown anodically to selected final potentials on grade II polycrystalline titanium under different anodization rates. XPS and RBS results show that the oxide consists of primarily TiO2 with a non-stoichiometric oxide/metal interface, with the slower growth rate associated with a thicker layer at the interface. Characterization using TEM reveals that the structure of the oxide evolves from a primarily amorphous phase to islands of crystallites in an amorphous matrix, to an entirely crystalline phase by increasing the polarization potential. Slower growth rates tend to remain crystalline at higher potentials. The mechanical strength of oxide films extracted from load-depth data by nanoindentation varies dramatically for oxide films grown by different rates at 9.4 V, and to a lesser extent at lower potentials. The variation of film strength is associated with both compositional and structural ...

Science.gov (United States)

Feasibility of depositing continuous films of nano-porous alumino-silicates, primarily zeolites and MCM-41, on metallic and non-metallic substrates was examined with an aim to develop membranes for separation of gaseous mixtures and also for application as hydrogen storage material. Mesoporous silica was deposited in-side the pores of these nano-porous disks with an aim to develop membranes for selective separations. Our study involves supported zeolite film growth on substrates using in-situ hydrothermal synthesis. Faujasite, Silicalite and Mesoporous silica have been grown on various metallic and non-metallic supports. Metallic substrates used for film growth included anodized titanium, sodium hydroxide treated Titanium, Anodized aluminum, and sintered copper. A non-metallic substrate used was nano-porous aluminum oxide. Zeolite film ...

KoreaScience (Korea)

Full Text Available

British Library Electronic Table of Contents (United Kingdom)

A new series of anatase TiO2 hollow structures were prepared by a facile hydrothermal process. When the hydrothermal time was increased from 20min to 72h, the resulting TiO2 solid spheres gradually transformed into TiO2 hollow spheres with higher surface crystallinity and exposed {001} facets. The as-prepared TiO2-72h sample exhibited the highest activity comparing to other TiO2-based samples and commercial product Degussa P-25 towards the selective photocatalytic oxidation of toluene to benzaldehyde. Such great photocatalytic performance was mainly attributed to enhanced UV-adsorption and better charge separation efficiency due to higher surface crystallinity of TiO2-72h.

British Library Electronic Table of Contents (United Kingdom)

TiO2 hollow microspheres with sea urchin-like hierarchical architectures were synthesized by a simple hydrothermal method. The as-synthesized hollow microspheres with hierarchical architectures consisting of many rhombic building units exhibit high specific surface area. Electrorheological (ER) properties of hierarchical hollow TiO2-based suspension were investigated under steady and oscillatory shear. The hollow TiO2-based suspensions show much higher yield stress and elasticity than pure TiO2 suspension at the same electric field strength. This phenomenon was elucidated well in view of their dielectric spectra analysis. The sea urchin-like architectures result in stronger interfacial polarization of hollow TiO2 suspension upon an electric field, showing higher ER activity. Also, hollow i...

International Nuclear Information System (INIS)

Yttria stabilized zirconia (YSZ) with 8 mol% Y was deposited by reactive magnetron sputtering onto oxidized (100) silicon substrates. It was possible to switch film texture from (111) to (200) by applying a strong RF substrate bias. Transmission electron microscopy showed that the film deposited under bias is porous and exhibits nanoscaled grains, whereas the film deposited without bias is dense and columnar. The ionic conductivity as a function of temperature revealed an activation energy of 1.04 eV. The mechanical stress could be tuned to low values by thermal post-annealing. Using the dense (111) film as electrolyte layer, and the porous (200) film as an interlayer to a porous Pt anode, an open circuit voltage of 0.85 V was obtained in a micro machined fuel cell structure.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

When nanometer scale holes (diameters of 50 to a few hundred nm) are imaged in a scanning electron microscope (SEM) at pressures in the 10{sup -5} to 10{sup -6} torr range, hydrocarbon deposits built up and result in the closing of holes within minutes of imaging. Additionally, electron beam deposition of material from a gas source allows the closing of holes with films of platinum or TEOS oxide. In an instrument equipped both with a focused ion beam (FIB), and an SEM, holes can be formed and then covered with a thin film to form nanopores with controlled openings, ranging down to only a few nanometers.

Science.gov (United States)

A WO(3)/TiO(2) composite, hollow-sphere photocatalyst with average diameter of 320 nm and shell thickness of 50 nm was successfully prepared using a template method. UV-vis diffuse reflectance spectra illustrated that the main absorption edges of the WO(3)/TiO(2) hollow spheres were red-shifted compared to the TiO(2) hollow spheres, indicating an extension of light absorption into the visible region of the composite photocatalyst. The WO(3) and TiO(2) phases were confirmed by X-ray diffraction analysis. BET isotherms revealed that the specific surface area and average pore diameter of the hollow spheres were 40.95 m(2)/g and 19 nm, respectively. Photocatalytic experiments indicate that 78% MB was degraded by WO(3)/TiO(2) hollow spheres under visible light within 80 min. Under the same conditions, only 24% MB can be photodegraded by TiO(2). The photocatalytic mineralization of MB, catalyzed by TiO(2) and WO(3)/TiO(2), proceeded at a significantly higher rate under UV irradiation than ...

Science.gov (United States)

A simple one-step method to fabricate hierarchically porous TiO2/Pd composite hollow spheres without any template was developed by using solvothermal treatment. Pd nanoparticles (2-5 nm) were well dispersed in the mesopores of the TiO2 hollow spheres via in-situ reduction. In our experiment, polyvinylpyrrolidone played an important role in the synthetic process as the reducing agent and the connective material between TiO2 and Pd nanoparticles. HF species generated from solvothermal reaction leaded to the formation of TiO2 hollow spheres and Ostwald ripening was another main factor that affected the size and structure of the hollow spheres. The as-prepared TiO2/Pd composite hollow spheres exhibited high electrocatalytic activity towards the reduction of H2O2. The sensitivity was about 226.72 ?A mM-1 cm-2 with a detection limit of 3.81 ?M at a signal-to-noise ratio of 3. These results made the hierarchically porous TiO2/Pd composite a promising platform for fabricating new nonenzymic ...

International Nuclear Information System (INIS)

Research highlights: ? Correlations between microstructure and internal stress during Ti anodising are established. ? Large internal compressive stresses are accumulated in the film during anodising upto 12 V. ?A transition from compressive to tensile stress is observed when the cell voltage exceeds 12 V. ? At 40 V, the oxide films consist of two regions with different compositions and microstructures. Crystallisation of amorphous to anatase TiO2 contributes to the compressive stress relaxation. - Abstract: The relationship between the microstructural and internal stress evolution during Ti anodising is discussed. Samples anodised galvanostatically to 12 V and 40 V, corresponding to different stages of the internal stress evolution, were examined by in-plane and cross-section transmission electron microscopy. Electron diffraction patterns have been complemented with stoichiometry data obtained from energy loss near edge structure spectra. The ...

CERN Document Server

The intrinsic decay rate of orthopositronium formed in SiO/sub 2/ powder is measured using the direct 2 gamma correction method such that the time dependence of the pick-off annihilation rate is precisely determined. The decay rate of orthopositronium is found to be 7.0396+or-0.0012(stat.)+or-0.0011(sys.)/ mu s/sup -1/, which is consistent with our previous measurements with about twice the accuracy. Results agree well with the O( alpha /sup 2/) QED prediction, and also with a result reported very recently using nanoporous film.

Science.gov (United States)

We prepared submicron-scale spherical hollow particles of anatase TiO2 by using a polystyrene-bead template. The obtained particles were very uniform in size, with a diameter of 490 nm and a shell thickness of 30 nm. The Brunauer-Emmett-Teller surface area measurements revealed a large value of 70 m2/g. The photocatalytic property was investigated by the complete decomposition of gaseous isopropyl alcohol under UV irradiation. It was indicated that the activity of the hollow spheres was 1.8 times higher than that of the conventional P25 TiO2 nanoparticles with a diameter of 30 nm. Furthermore, we fabricated a dye-sensitized solar cell (DSC) using an electrode of the TiO2 hollow spheres, and examined the photovoltaic performance under simulated sunlight. Although the per-area efficiency was rather low (1.26%) because of a low area density of TiO2 on the electrode, the per-weight efficiency was 2.5 times higher than those of the conventional DSCs of TiO2. PMID:18088147

International Nuclear Information System (INIS)

TiO2 addition into boiling water reactor (BWR) primary system is being developed as a method to mitigate stress corrosion cracking (SCC) of the BWR structural materials. This technique aims for electrochemical corrosion potential (ECP) decrease of reactor materials by photo-excitation reaction under Cherenkov irradiation. ECP measurement tests have been conducted in the test loop in BWR to investigate the feasibility of the SCC mitigation method with TiO2. The test results showed that the ECP of TiO2 deposited materials was decreased to 2 technique was confirmed to be feasible as a SCC mitigation method for BWR structural materials without hydrogen injection. (author)

British Library Electronic Table of Contents (United Kingdom)

Hierarchical TiO2 hollow spheres had been prepared based on bubble templates by a simple one-step hydrothermal method. The diameter of hollow spheres was about 700nm and the shell thickness of them was 69nm. They were composed of similar spindle- or needle-like building units. Furthermore, hydrothermal time had an important influence on the morphology and crystallinity of hollow spheres. Moreover, the UV-Vis diffuse reflectance spectra of TiO2 hollow spheres heated at 150^oC for 10h showed the strongest absorption in the UV-Vis region and the Raman spectrum demonstrated the anatase sample. Additionally, a possible formation mechanism of TiO2 hollow spheres was proposed. So this novel and simple method would provide a development direction to fabricate all kinds of inorganic hollow spheres ...

International Nuclear Information System (INIS)

A combined application of several microtechniques is presented and discussed with the Ti/TiO_2 and Zr/ZrO_2-systems as an example. All measurements were carried out on single grains of technical materials in order to detect and quantify the effect of substrate microstructure on the properties of anodic passive films formed potentiodynamically in 0.5 M H_2SO_4 (dU/dt = 20 mVs"-"1). Anisotropy-micro-ellipsometry (AME) was employed to determine the crystallographic orientation of the substrate grains along with passive film thickness and crystallinity in dependence on the anodization potential. Both the isotropic (amorphous) TiO_2- and the anisotropic (crystalline) ZrO_2-films exhibit a systematic dependence of film thickness on the grain orientation. Local LASER-scanning photocurrent measurements (#lambda#=257 nm) on the same grains likewise show a heterogeneity of the photoelectrochemical reactivity in ...

Science.gov (United States)

In this Communication, we report the fabrication of well-crystallized rutile-phase TiO2 hollow spheres using potassium titanium oxalate as the precursor. The spheres exhibited unique three-dimensional hierarchical architectures and demonstrated a significantly improved photocatalytic performance. The synthetic strategy used in this process represents a general approach and therefore may contribute to the formation mechanisms of hollow nanostructures. PMID:16634578

British Library Electronic Table of Contents (United Kingdom)

Fe-doped TiO2 hollow spheres (Fe-THs) were synthesized by sol?gel process using carbon spheres as templates. The prepared samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV?vis diffuse reflectance spectrum (DRS), N2 adsorption?desorption isotherms, Electron paramagnetic resonance (EPR) spectroscopy and Photoluminescence emission spectroscopy (PL). UV?vis spectra showed that Fe3+ doping could extend the absorption edge to the visible region. EPR spectra showed that Fe3+ was incorporated into the crystal lattice of TiO2, which could inhibit the recombination of photo-induced electron?hole pairs and improve the photocatalytic activity. The photocatalytic activities of the prepared samples were evaluated for the degradation of dye Reactive Brillia...

International Nuclear Information System (INIS)

Sodium benzene sulfonate (BS) was decomposed in aqueous TiO_2 dispersions under highly concentrated solar light illumination to examine the photocatalytic characteristics of a parabolic round concentrator (PRC) reactor to degrade the pollutant without visible light absorption. The effects of such operational parameters as initial concentration, volume of the aqueous BS solution, oxygen purging, and TiO_2 loading on the kinetics of decomposition of BS were investigated. An effective photodegradation necessitates a suitable combination of initial volume and concentration of BS solution. Relative to atmospheric air, oxygen purging significantly accelerates the degradation process at high initial concentrations of BS (0.40 mM or 1.0 mM). Optimal TiO_2 loading was 9 gl "-"1, greater than previously reported. Elimination of TOC (total organic carbon) followed pseudo first-order kinetics in the initial stages of the photodegradation process. The relative photonic efficiency for the ...

International Nuclear Information System (INIS)

Conduction-band electrons, formed by pulse radiolysis of Degussa P25 TiO_2 particles, have been monitored by time-resolved microwave conductivity and found to undergo equilibrium localization and eventual recombination at the particle surface. In the presence of isopropyl alcohol recombination is retarded due to surface hole scavenging. The particle bulk can then be pumped with mobile electrons, which survive for seconds.

International Nuclear Information System (INIS)

(Cu_4_7Zr_1_1Ti_3_4Ni_8)_1_0_0_-_xMo _x bulk metallic glasses (BMGs) with x = 0, 1 and 2 at.% and a bulk metallic glass matrix composite with x = 5 at.% were successfully prepared by water-cooled copper mold casting. The effect of the addition of a small amount of Mo on the glass forming ability (GFA), thermal properties of the base alloy (i.e. x = 0) were investigated by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and differential thermal analyzer (DTA). It is found that the addition of appropriate amount of Mo can enhance the GFA of the Cu-based BMG, as indicated by the increase in the reduced glass transition temperature T _r_g (=T _g/T _l) and the parameter #gamma# (=T _x/(T _g + T _l)) with the increase of Mo. On the other hand, the corrosion resistance of the Cu-based BMGs with different Mo contents was examined by electrochemical polarization and weight loss measurement in 1 mol/L H_2SO_4 and 1 mol/L NaOH solutions, respectively. It is found that the ...

Energy Technology Data Exchange (ETDEWEB)

We report on the fouling of Focused Ion Beam (FIB)-fabricated silicon oxide nanopores after exposure to tap water for two weeks. Pore clogging was monitored by Scanning Electron Microscopy (SEM) on both bare silicon oxide and chemically functionalized nanopores. While fouling occurred on hydrophilic silicon oxide pore walls, the hydrophobic nature of alkane chains prevented clogging on the chemically functionalized pore walls. These results have implications for nanopore sensing platform design.

British Library Electronic Table of Contents (United Kingdom)

To improve the photocatalytic application performances of TiO2, in this work, firstly CdS modified Degussa P25 TiO2 (CdS/TiO2) composites were prepared by two methods, sol-gel method and precipitation method. Next they, sol-gel-CdS/TiO2 (sg-CdS/TiO2) and precipitation-CdS/TiO2 (pp-CdS/TiO2), were loaded on activated carbon fibers (ACFs) by dip-coating method using the sodium carboxymethyl cellulose as adhesives. The composites were characterized by XRD, UV-vis absorbance spectra, SEM, EDS and BET. The photocatalytic activities under sunlight were investigated by the degradation of methylene blue. The results showed that CdS/TiO2 composites were mainly composed of anatase-TiO2 and little CdS cubic phases. The absorption wavelengths of sg-CdS/TiO2 and pp-CdS/TiO2 composites were extended to ...

British Library Electronic Table of Contents (United Kingdom)

N-doped TiO2 has been prepared by use of sol?gel systems containing titanium alkoxide, with nitric acid as the nitrogen source. The time needed for gelation of the systems was drastically reduced by ultrasonic irradiation. The peaks assigned to the nitrate and nitrous ions were observed by FT-IR measurement during the sol?gel reaction. The N-doping was confirmed by the observation of N?O peaks in the XPS spectrum of the sample heated at 400??C. The nitrate ion acted as an oxidizer of the ethanol solvent and titanium species. The TiO2 became doped with nitrogen oxide species as a result of reduction of nitrate ion incorporated into the dried gel samples. These results indicated that the added nitric acid was reduced during the sol?gel transition and heating process, and the resulting NO spe...

British Library Electronic Table of Contents (United Kingdom)

Herein, we demonstrate the structure of the PS colloidal crystals which were fabricated on the hydrophilic/hydrophobic Si wafers by a spin-coating technique. Monodisperse PS colloids are spin-coated onto self-assembled monolayers of 3-(aminopropyl)triethoxysilane and propyltrimethoxysilane coated Si wafers. PS spheres organized as ordered close-packed face-centered cubic structure with (111) planes on the hydrophilic surface while they gathered without the crystal structure on the hydrophobic surface. This paper also reports a simple and rapid method to fabricate the close-packed structure of hollow TiO2 spheres. The colloidal crystal of TiO2 hollow spheres was prepared using the PS sphere template on the hydrophobic surface. The mechanism for the growing multilayers of self-assembled PS p...

Energy Technology Data Exchange (ETDEWEB)

The addition of carbon to samples, during imaging, presents a barrier to accurate TEM analysis, the controlled deposition of hydrocarbons by a focused electron beam can be a useful technique for local nanometer-scale sculpting of material. Here we use hydrocarbon deposition to form nanopores from larger focused ion beam (FIB) holes in silicon nitride membranes. Using this method, we close 100-200nm diameter holes to diameters of 10nm and below, with deposition rates of 0.6nm per minute. I-V characteristics of electrolytic flow through these nanopores agree quantitatively with a one dimensional model at all examined salt concentrations.

International Nuclear Information System (INIS)

TEM and HRTEM have been used to characterise the microstructures of materials formed by hot-pressing silicon nitride with an Al_2O_3-SiO_2-TiO_2 densification aid system, to form #beta#'-sialon-TiN composites in which the TiN particles are of 20-100 nm dimension. (orig.).

International Nuclear Information System (INIS)

The formation of porous structures of nanometre size (nanoporous structures) on germanium (Ge) surfaces by focused ion beam (FIB) irradiations was investigated using various FIB conditions such as ion species, irradiation energies, total fluences, fluence rates, and incident angles. FIB-irradiated regions were observed using a scanning electron microscope and an atomic force microscope. It is found that, using a focused Ga ion beam (Ga FIB) at an energy of 100 keV, the irradiated Ge surface swelled up to ion fluence of 2 x 10"1"7 cm"-"2 with nanoporous structures and then was etched for larger fluences. The shape of swollen nanoporous structures depended on the fluence rate and the incident angle of the Ga FIB. However, such porous structures were observed neither for low-energy (15-30 keV) FIB irradiations using Si and Au ions nor for high-energy (200 keV), heavy ion (Au) irradiation. These observations might be helpful in ...

International Nuclear Information System (INIS)

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutions of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controlled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle synthesis have been proposed.

International Nuclear Information System (INIS)

Ceramic matrix composites in the TiC-Ti, Y-TZP system can be synthesized by the reaction between carbon and the TiO_2-Y_2O_3-ZrO_2 solid solution nanopowder. This method results in the more homogeneous powders than those prepared by the physical mixing of TiC and zirconia s.s. powders. Twelve TiO_2-Y_2O_3-ZrO_2 solid solution nanopowders differing in the proportions of the constituent oxides were prepared by the coprecipitation- calcination route. They were reacted with the pyrolytic carbon evenly distributed within the system. Carbon was introduced by the thermal decomposition of the phenol-formaldehyde resin dissolved in ethyl alcohol and mixed with the zirconia s.s. nanopowder. Reaction was performed in vacuum. Compacts of the composite powders sintered in vacuum give dense materials of evenly distributed TiC inclusions of sizes not surpassing 400 nm. Hardness of such materials was dependent on their chemical and phase composition but was generally higher than that of the pure ...

Science.gov (United States)

Nanosized particles are important because of their unique properties, different from the bulk, which leads to their enhanced catalytic, photocatalytic and electronic properties. This work has dealt with three different nanoparticle systems in the context of three different aspects of nanoparticle properties: (a) photocatalytis (TiO2/metal) system, (b) luminescence (CdSe) (c) alloying (Pt-Ag and Pd-Ag). The initial photocatalytic enhancement obtained by adding noble metal on semiconductor nanoparticles, degrades as fast as in 15 minutes and questions their long-term performance. XANES measurements on such irradiated systems like TiO2/Au, TiO2/Pt, TiO2/Ir indicates a positive oxidation state of these noble metals which renders them as recombination centers for photo-excited electrons and explains the decreased photocurrent. The oxidation is caused by holes. The EXAFS results also indicate a change of the interfacial structure under the effect of UV-irradiation, thus affecting the ...

UK PubMed Central (United Kingdom)

Integration of solid-state biosensors and lipid bilayer membranes is important for membrane protein research and drug discovery. In these sensors, it is critical that the solid-state sensing...Full Text Available

Wastenet

... In recent years workers in this field have focused on nucleation by nano-porous materials . This was in part motivated by a theoretical study by Page and Sear (2006) who proposed a two step model for nucleation in pores which suggest that there is ...

International Nuclear Information System (INIS)

Nano-materials in which a large fraction of atoms resides within a few atomic layers near the surface can be designed to have novel properties by manipulating their surface parameters. We show that the effective elastic constants of nano-porous/cellular materials can be made to exceed those of the parent materials provided the pore surface elastic parameters satisfy certain conditions. These stiff nano-porous materials herald a radical breakthrough in sandwich-type construction.

International Nuclear Information System (INIS)

Twelve powders of TiO_2-Y_2O_3-ZrO_2 solid solution of the methodically changed composition were prepared by a coprecipitation-calcination technique. After mixing with phenol-formaldehyde resin, the powders were calcinated for 2 hours at 1200"oC in vacuum. The resultant composite powders contained TiC and non-reacted carbon. Green compacts were sintered in vacuum at 1500"oC for 2 hours. A temperature increase was stopped at 1200"oC to react remains of carbon. There were two carbides in the composites TiC and ZrC. TiC non-stoichiometry depended on carbon content in the system. Phase composition of the depended on of titania and yttria in zirconia solid solution. The majority of the samples showed two tetragonal zirconia phases differing in lattice parameter and tetragonality. (author)

British Library Electronic Table of Contents (United Kingdom)

AbstractBackground In recent years nano-metaloxides which easily penetrate into the cells with special interest due to their higher chemical reactivity as compared to that of similar materials in the bulk form. Of particular interest are nano-TiO2 and ZnO, which have been widely used for their bactericidal and anticancerous properties. Purpose The aim of the present study was to examine the bactericidal properties of nano-TiO2 and ZnO combined with visible light on S. aureus and S. epidermitis, known for their high prevalence in infected wounds. Study Using the technique of electron-spin resonance (ESR) coupled with spin trapping, we examined the ability of TiO2 and ZnO nanoparticle suspensions in water to produce reactive oxygen species (ROS) with and without visible light irradiation. Th...

International Nuclear Information System (INIS)

When liquids are confined in nano-scopic dimensions, their properties differ from the corresponding bulk liquid, due to their reduced dimensionality and surface effects. Phase transition temperatures and pressures are often shifted from the bulk values and new phases can appear due to the strong interactions of the molecules with the confining walls. We have studied the structural and dynamical properties of aromatic liquids such as benzene, toluene, and ortho-terphenyl confined in nano-porous materials, MCM-41 and SBA-15, synthesized and characterized in our laboratory. A non-trivial dependence of the glass transition temperature, Tg, on the pore size and surface treatment of nano-porous materials is confirmed and interpreted as resulting from a competition between the fluid-wall and fluid-fluid intermolecular interactions. An increase of Tg is observed for small pore sizes and attractive surface while Tg decreases for non attractive surface, ...

British Library Electronic Table of Contents (United Kingdom)

The factors affecting the rate of silica leaching in alkaline aqueous media from surface silanized, nanoporous, amorphous, silica gels and from silanized silica gels that have been modified with polyamines to form the previously reported silica polyamine composites (SPCs), BP-1 and BP-2 have been investigated. Silanization with alkyl trichlorosilanes slows the rate of silica leaching relative to the unmodified silica gels. The use of bulkier aryl silanes somewhat decreases the silica leaching under the same conditions. Interestingly, after modification of the silanized silica with poly(allylamine) (PAA) to make BP-1, the leaching increases, but subsequent modification of the SPC with chloroacetic acid to make BP-2, quenches this increase. A mechanism explaining these results is discussed. ...

International Nuclear Information System (INIS)

The structure of nano-porous carbon, obtained by means of chlorination of carbide compounds with various crystal structure (SiC, TiC, Mo_2C) is studied through the method of small-angle diffraction. The angular dependences of the scattering intensity obtained are interpreted as the result of scattering from the nanoparticles of different size. The functions of the scattering particles distribution by the m(R_g) inertia radii are determined. It is shown that in spite of the source carbide, the highest fraction of the volume in the porous carbon constitute the particles with R_g #approx# 5 A. The nanoparticles in the samples obtained from SiC, wherein the average value of the R_g"a"v < 6 A, are most uniform by size. The nanoparticles in the porous carbon, obtained from Mo_2C, are on the average by two times larger

International Nuclear Information System (INIS)

A powder mixture of #alpha#-Si_3N_4, Al_2O_3, and TiO_2 was hot-pressed using different sintering cycles to search for an optimum in situ formed #beta#-O-sialon-TiN composite. The impulse excitation technique (IET), high-temperature X-ray diffraction (HTXRD), and scanning electron microscopy (SEM) were used to investigate the microstructure. Below the temperature of 1300 deg. C, the high-temperature internal friction (Q "-"1) decreases with the increase of sintering temperature, whereas the density of the material increases with the increase of sintering temperature. At a sintering temperature higher than 1850 deg. C, the ceramic could not be densified and O-sialon was not formed. Also, the mechanical properties of ceramics hot-pressed using different sintering cycles were assessed. The ceramic hot-pressed at 1700 deg. C for 10 min displays a combination of high hardness and good fracture toughness, due to an optimum combination of #beta#-sialon, O-sialon, and TiN-phases. This paper ...

British Library Electronic Table of Contents (United Kingdom)

In this paper, we prepared by the sol-gel method alkaline titania catalysts, doped by gelling titanium alkoxide with aqueous solutions containing potassium, rubidium or cesium chlorides. XRD patterns showed that samples annealed at 400 and 600degreeC contained a single crystalline phase, anastase. Specific surface areas were higher in samples annealed at 400degreeC (>100m2/g) than in those annealed at 600degreeC (25m2/g). The weight density of basic sites determined by CO2-TPD drastically diminished in samples treated at 600degreeC. Catalysts were tested for the self-condensation of acetone at 300degreeC; main reaction products were isomesityl oxide, mesityl oxide and mesitylene. Samples annealed at 600degreeC showed lower acetone conversion rate and low formation of mesitylene than that o...

Energy Technology Data Exchange (ETDEWEB)

The single-electrode capacitance of a nano-porous carbon electrode used as an electric double layer capacitor was measured. The charged state of the electrolyte ion was discussed from the results. Single-electrode capacitance was not proportional to the specific surface area of the electrode. This implies that the whole surface of the electrode is not effective for the formation of an electric double layer. It is considered that edge orientation of the carbon structure would give a dominant contribution to capacitance. For measurements with aqueous solutions of various electrolytes, capacitance was about the same value for each salt compound. For aqueous acid solution, on the other hand, capacitance was twice to three times as large as that for salt compounds. This difference, however, became negligibly small if the concentration of electrolyte solution was lowered. Taking account of the hydrated ionic radius of each ion, it was considered that ions in salt ...

International Nuclear Information System (INIS)

Highly swollen nanoporous layers produced in material surfaces by He implantation are of special interest for applications such as catalysis. Here we investigate whether nanoporous layers can be produced in the covalently bonded insulating ceramic, SiAlON. The retention of highly swollen porous structures in thinned TEM sections prepared from such hard brittle materials is particularly challenging. We have successfully prepared such sections both parallel to, and perpendicular to, the implanted surface. At intermediate doses the bubble structures are very similar to those found in metals. At high helium doses local swellings at depths around the mean projected range of the He ions (#approx#360 nm) are estimated to be well in excess of 200%. Bubble structures are stable under heating to temperatures up to 1200 deg. C. It is found that the highly cavitated layer is buried below a crystalline overlayer of compact SiAlON. This overlayer is ...

Energy Technology Data Exchange (ETDEWEB)

There is increasing demand to functionalize meso- and nano-porous materials by coating and make the porous substrate biocompatible or environment friendly. However, coating on a meso-porous substrate poses great challenges, especially if the pore aspect ratio is high. In the current work the pulsed laser deposition (PLD) method is used for coating Ni{sub 3}Al-based meso-porous membranes with diamond-like carbon (DLC) layers of high thickness homogeneity and adhesion. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Formaldehyde, a well-identified indoor pollutant, was recently classified as carcinogenic. New regulations for the air quality are expected and therefore there is a need for low-cost sensors, sensitive and selective with a fast response time for the detection of formaldehyde at ppb level. In the present work, we had developed a chemical sensor based on nano-porous matrices doped with Fluoral-P and optical methods of detection. The nano-porous matrices, elaborated via the Sol-Gel process, display nano-pores whose cavity is tailored for the trapping of the targeted pollutant. They provide a first selectivity with the discrimination of the pollutants by their size. A second selectivity is obtained with a molecular probe, Fluoral-P, which reacts specifically with formaldehyde leading to the 3,5- di-acetyl-1,4-dihydro-lutidine (DDL). The kinetics of formation of DDL was studied as function of many parameters such as the ...

Energy Technology Data Exchange (ETDEWEB)

The pitting resistance of Fe-Cr and Fe-Cr-Mo alloys has been correlated with characteristics of the passive films analyzed by Auger electron spectroscopy (AES). Increased film protectiveness as a result of increased Cr in the alloy can be directly attributed to Cr enrichment of the film and decreased film thickness. Increased Mo in the alloy or passivation at noble potentials promotes passive film resistance to breakdown, but neither does much to change the macrocharacteristics of the film. Rather, it is suggested that the roles of alloying and/or passivation conditions are related to the susceptibility and distribution of weak points of the film. In solutions in which pitting occurs, chloride is generally not incorporated into the film, suggesting that the role of halides is to interact with weak points of the ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

No abstract prepared.

Science.gov (United States)

... Abstract : MANY THIN FILM ACOUSTO-OPTIC INTERACTION EXPERIMENTS FOR ... CONVERTERS, AND FOR FAST SWITCHES HAVE BEEN ...

Energy Technology Data Exchange (ETDEWEB)

Polyacrylonitrile films have been spin cast and pyrolyzed to produce thin (500--1500 A) carbon films. These films have higher electrical conductivities than films produced by other methods at similar temperatures. The conductivity can be varied by at least four orders of magnitude by changing the pyrolysis temperature. Ultraviolet, infrared, and Raman spectroscopies were used to investigate the chemical structure of the films during different stages of processing.

International Nuclear Information System (INIS)

YBa_2Cu_3O_7_-_x thick films have been deposited on silver sheets and MgO single crystals by spray pyrolysis. Film texture is related to film thickness and sintering temperature. The X-ray intensity ratio of the 005 peak to the 110 peak is higher for thin films deposited at the higher temperatures. However, elevated temperatures promote copper diffusion and second-phase formation in films deposited on silver. Films deposited on MgO can have larger grain sizes and are more oriented than those deposited on silver.

Energy Technology Data Exchange (ETDEWEB)

Chemical looping combustion (CLC) of simulated coal-derived synthesis gas was conducted with NiO oxygen carriers supported on SiO2, ZrO2, TiO2, and sepiolite. The effect of H2S on the performance of these samples for the CLC process was also evaluated. Five-cycle thermogravimetric analysis (TGA) tests at 800 C indicated that all oxygen carriers had a stable performance at 800 C, except NiO/SiO2. Full reduction/oxidation reactions of the oxygen carrier were obtained during the five-cycle test. It was found that support had a significant effect on reaction performance of NiO both in reduction and oxidation rates. The reduction reaction was significantly faster than the oxidation reaction for all oxygen carriers, while the oxidation reaction is fairly slow due to oxygen diffusion on NiO layers. The reaction profile was greatly affected by the presence of H2S, but there was no effect on the capacity due to the presence of H2S in synthesis gas. The presence of H2S decreased reduction ...

British Library Electronic Table of Contents (United Kingdom)

The effects of pore curvature and surface heterogeneity on the adsorption of water on a graphitic surface at 298 K were investigated using a Grand Canonical Monte Carlo (GCMC) simulation. Slit and cylindrical pores are used to study the curvature effects. To investigate the surface heterogeneity the functional group and the structural defect on the surface were specifically considered. The hydroxyl group (OH) is used as a model for the functional group and the water potential model proposed by Muller et al. is used to calculate the water interaction. For the homogeneous cylinder, the pore filling occurs at a pressure lower than the saturation pressure of the water model, while it is greater in the case of homogeneous slit pore. The size of hysteresis loop is more sensitive to the length of...

Energy Technology Data Exchange (ETDEWEB)

An efficient method of hydrogen storage in nano-porous carbons is its reversible sorption by electrochemical decomposition of a KOH water solution [1-3] according to the following equation: C + xH{sub 2}O + xe{sup -} {yields} (CH{sub x}) + xOH{sup -} where (CH{sub x}) stands for the hydrogen inserted into the nano-porous carbon during charging and oxidized during discharging. Although various carbon materials have been investigated as hydrogen adsorbents, the information about the storage mechanism as well as the nature of the hydrogen/carbon interaction is still not sufficient. In order to extend the understanding of the process, carbon samples charged electrochemically were investigated by temperature programmed desorpt(TPD). The nature of the hydrogen/carbon interaction was studied by electrochemical analysis at different temperatures. The TPD experiments consist of heating the samples from room temperature to 950 C and of quantitative ...

International Nuclear Information System (INIS)

Highly ordered arrays of Ni nanoholes and Fe20Ni80 antidots have been prepared, respectively, by replica/antireplica processing and sputtering techniques using nanoporous alumina membranes as templates. Geometrical characteristics as nanohole/antidot diameter, interpore distance and the overall hexagonal symmetry of arrays are controlled through the original templates. Experimental data on their hysteresis and magnetic domain structure have been taken by vibrating sample magnetometry and magnetic force microscopy, respectively. An analysis of the magnetization process, resulting magnetic anisotropy and magnetic domain structure is summarized considering the influence of those geometry aspects. In particular, the hexagonal symmetry and the density of nanohole/antidots determine the overall magnetic behavior, which is of interest in future high-density magnetic storage systems.

Energy Technology Data Exchange (ETDEWEB)

The kinetics of passive film formation on iron in borate buffer solution has been studied at different anodic potentials. The process of film growth has been found to occur in four distinct stages. About 80-90% of the total film thickness formed in 1h grows during the initial two stages which last for only 1-3s (depending upon potential). The electric field strength across the film is not constant but decreases with progressing film growth. The thickness of the film determined ellipsometrically is less than that calculated from the electric charge consumed. The process of anodic film formation is accompanied by the dissolution of iron which occurs over the whole range of potentials.

British Library Electronic Table of Contents (United Kingdom)

The K 2010 exhibition saw the introduction of PolyOne Corps OnCap Antifog Additive for polypropylene (PP) films, the first such additive for PP films that does not require corona treatment. According to the company, this new additive simplifies production of antifog films for the flexible food packaging industry, improving production efficiencies for both cast and blown film producers.

British Library Electronic Table of Contents (United Kingdom)

Metallic Zn films were deposited on glass substrates by electron-beam evaporation. ZnO films were synthesized by thermal oxidation of Zn metallic films in air. At the annealing temperature of 550 ?C, ZnO nanowires appeared on the surface, which mainly result from the decrease of oxidation rate. A ZnO ultraviolet photodetector was fabricated based on a metal-semiconductor-metal planar structure. The detector showed a large UV photoresponse with an increase of two orders of magnitude. It is concluded that promising UV detectors can be obtained on ZnO films by thermal oxidation of Zn metallic films. The ways of performing spectral response measurements for polycrystalline ZnO films are also discussed.

Science.gov (United States)

Manufacture of cadmium sulfide thin film solar cells

Energy Technology Data Exchange (ETDEWEB)

As thin films become increasingly popular (for solar cells, LEDs, microelectronics, batteries), quantitative morphological information is needed to predict and optimize the film's electronic, optical and mechanical properties. This quantification can be obtained quickly and easily with X-ray diffraction using an area detector and synchrotron radiation in two simple geometries. In this paper, we describe a methodology for constructing complete pole figures for thin films with fiber texture (isotropic in-plane orientation). We demonstrate this technique on semicrystalline polymer films, self-assembled nanoparticle semiconductor films, and randomly-packed metallic nanoparticle films. This method can be immediately implemented to help understand the relationship between film processing and microstructure, enabling the development of ...

International Nuclear Information System (INIS)

Fe-Cr amorphous films have been formed by both in situ evaporation of multilayered films and ion beam mixing in a target chamber of a 200 keV implanter. The effects of Cr content and ion irradiation on the amorphization of films were examined by transmission electron microscope (TEM). Corrosion of film was investigated by means of a potential dynamic polarization. Corrosion resistance of amorphous film in 0.5 mol H-2SO-4 solution is considerably increased than that of pure iron. Using X ray photoelectron spectroscopy (XPS) corrosion resistance in atmosphere of amorphous Fe-Cr passive films formed by P"+ mixing was studied. Results show that the richness of Cr and P exist at the surface of Fe-Cr film.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

Sputtering of glass coatings on cadmium sulfide thin film solar cells

Energy Technology Data Exchange (ETDEWEB)

This paper reports that the point defect model for steady-state passive films formed anodically on metal s in aqueous environments has been extended to include irreversible dissolution of the film and the irreversible generation and annihilation of cation and oxygen vacancies at the metal/film and film/solution interfaces. THe model yields a number of diagnostic criteria that can be used to identify the majority (vacancy) charge carrier and to characterize the kinetic nature of the interfacial vacancy generation and annihilation processes. We use these criteria to show that the steady-state passive film that forms on nickel in acidic phosphate buffer solutions is a cation conductor and that cation transport from the metal to the solution involves irreversible ejection of cations from the film. On the other hand, the passive film that forms ...

Energy Technology Data Exchange (ETDEWEB)

The comprehension of passivity and its protective character against corrosion is closely connected with the electronic properties of passive films. Passive films formed anodically on carbon steel in borate/boric acid solution, pH 9.2, have been characterised by electrochemical impedance spectroscopy (EIS). Mott-Schottky plots and impedance measurements were made on films formed at different potentials and times. The investigation allowed the determination of the semiconductive properties of the films. The results of the capacitance response indicate that the passive films behave like highly doped n-type semiconductors, showing that the passive film properties are dominated by iron. The value of donors density (N {sub D}) for the passive film is of the order of 10{sup 21} cm{sup -3} and decreases with increasing formation time and potential, ...

International Nuclear Information System (INIS)

Surface-sensitive UV photoelectron yield spectroscopy was employed to study electron acceptor levels at surfaces of chalcopyrite structure Cu-In-Se thin films. Surface Fermi level pinning was observed for Cu-rich films. Shallow acceptor levels ascribable to defects Cu_I_n and V_C_u were observed for near-stoichiometric and In-rich films respectively. (orig.).

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

Only two years ago, plastic film recycling was considered an onerous task. Different resins had to be identified, colors had to be separated, and minute contaminants had to be weeded out almost by hand to produce a quality material. But the tide of plastic film recycling is changing now that new technologies have emerged and more organized collection infrastructure have been developed. Today, plastic film recycling maintains a lucrative market for those with the right combination of equipment and know-how.

Energy Technology Data Exchange (ETDEWEB)

The authors study the nonuniformity of a-Si:H films obtained by the method of vacuum condensation, with the help of x-ray small-angle scattering (SLS) and transmission electron microscopy. Films of hydrogenated amorphous silicon are greatest interest, because the electronic properties of this material can be controlled by doping. As a result of the compensation of the ruptured bonds, and possibly, effects of melting, the properties of such films are analogous to those of singlecrystalline silicon. XLS enables a quantitative determination of the prameters of the regions of low electron density (RLD) in such objects.

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Short communication.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Passive films formed on stainless steels in a borate buffer solution (pH 9.2) have been investigated by capacitance measurements and photoelectrochemistry. The study was carried out on films formed on AISI type 304 and 316 stainless steels and high purity alloys with differing chromium, nickel, and molybdenum contents. Complementary research by Auger analysis shows that the passive films are composed essentially of an inner chromium region in contact with the metallic substrate and an outer iron oxide region developed at the film/electrolyte interface. The semiconducting properties of the passive films are determined by those of the constituent chromium and iron oxides which are of p-type and n-type, respectively. Thus the influence of the alloying elements on the semiconducting properties of the passive films is explained by changes in the electronic structure ...

Energy Technology Data Exchange (ETDEWEB)

X-Ray reflectivity has been used to investigate the microstructural changes of solution-cast stearic acid films before and after immersion in CoCl{sub 2} solutions. Before immersion, the films possess a well-defined layered structure with an interlayer spacing of 4.01{+-}0.05 nm. After the films were immersed in the CoCl{sub 2} solutions, a new set of equidistant diffraction peaks emerge, the corresponding interlayer spacing of which is 5.13{+-}0.05 nm. The X-ray photoelectron spectra of the films indicate the existence of cobalt ions inside the films after immersion. It is concluded that the permeation of the cobalt ions into the hydrophilic interlayer causes the stearic acid molecules to reorient perpendicular to the films, resulting in the increase of interlayer spacing and the roughening of the interfaces.

Energy Technology Data Exchange (ETDEWEB)

Passive films were formed on a high purity Fe-23 Cr alloy in acid sulfate solutions in the presence and absence of chloride ion. The resulting film composition was investigated by Auger depth profiling. The passivated samples were exposed to a 1M NaCl solution at a constant potential slightly above the critical pitting potential, and the current-time transient was measured in order to compare the relative stability of the different films. The results obtained suggest that the formation conditions influence the chloride content of the passive film and the breakdown behavior. Passive films formed in the presence of chloride contain and are slightly less stable towards breakdown. No chloride was found in films formed in sulfate and subsequently exposed to chloride well below the pitting potential.

British Library Electronic Table of Contents (United Kingdom)

The physical and antioxidant properties of alginate biodegradable film incorporating white, red and extruded white ginseng extracts were investigated. No differences in moisture contents of all alginate film samples were noticeable (p>0.05) except those film samples incorporated without ginseng extract, which had the highest moisture content. The addition of ginseng extract to alginate film decreased tensile strength and elastic modulus (p<0.05) but increased the percent elongation at break. The presence of extracts did not significantly affect the water vapor permeability of the film samples. Alginate film containing extruded white ginseng extract at a barrel temperature of 130degreeC presented the highest (61.12%) free-radical scavenging activity against the 2,2-diphenyl-1-picryhydrazyl ...

International Nuclear Information System (INIS)

New physical objects, ispalators based on free soap films, exhibit persistent flows of the soap solution in open and closed volumes in air with additions of gases of the C_8F_1_8 type (p = 20 Torr) at temperature drops on the films of the order of tenths and hundredths of kelvin. The flows move continuously at a velocity of 5 - 20 cm s"-"1. It is found that the parts of an inclined ispalator film show anomalous behaviour upon heating: their weight increases and they move downward over the film, whereas the unheated parts of the film move upward. Continuous radial vortex flows accompanied by the formation and washing of the regions of a thin black film are observed on circular films in closed volumes upon their uniform external cooling by evaporating water for 5 - 10 hours. The rapid flows make film ispalators the ...

International Nuclear Information System (INIS)

A study of the thin gold film growth, during the deposition on glass substrate under UHV conditions at low temperatures, is presented. The complementary methods, the atomic force microscopy and grazing incidence x-ray reflectometry, are used for the research. It is shown that due to variation of the time of deposition from 2 to 50 min different kinds of thin Au films nanostructures are obtained: from discontinuous films consisting of isolated islands, via formation of the chains of islands, up to continuous films. (author)

CERN Document Server

A simple experiment to observe weak localization in thin Ag films is presented. A clear theoretical signature of weak localization is predicted in mangetoresistive measurements of thin films samples. We present a simple method for making thin Ag film samples, using evaporative deposition, and observing the small magnetoresistive signal, using a resistance bridge technique. Typical results from our students show that Ag films show the predicted behavior for weak localization with spin effects. These effects can be easily observed in a liquid helium dewar.

International Nuclear Information System (INIS)

For obtaining radiation less damagable laser mirrors, a preliminary optimization of film fabrication suitable for the analysis of laser damage mechanism has been done as the first step. Here, the optimization requires not only the stable fabrication process but also the ideal film structure i.e., the amorphous and smooth film structure simultaneously, eliminating latently unwanted secondary effects such as light scattering during laser damage test. For this purpose, we adopted the ion assisted deposition (IAD) method and modified the deposition conditions for titanium and tantalum oxide films, both of which compose typical high index layers, and where SiO_2 layers are also chosen as low index layers because of their amorphous and smooth nature, in alternative multilayer laser mirrors. Surface and cross sectional film structures and film crystallinity are ...

Energy Technology Data Exchange (ETDEWEB)

Poster session: Abstract is full text. Track membranes are thin polymer foils irradiated by heavy ions. The defects created by the heavy ions are located along the ions trajectory, the track. It is possible to open channels by etching with a chemical agent. These channels are very uniform. Small Angle Scattering (of X rays and neutrons) give global information about the characteristics of the channel shape. As the nanochannels are strictly parallel, an excellent sample orientation is required to obtain interpretable spectra. Then shoulders due to the oscillations of the Bessel function (radial part of the channel shape Fourier transform) are easily seen in the scattered intensity in the PXY data treatment software of SAS spectra allow to determine the channel diameter with its dispersion law, to demonstrate the existence of a wall thickness with a linearly varying density, and to assess the roughness. PXY can also detect non cylindric shapes like single or double cones or spindles. ...

Energy Technology Data Exchange (ETDEWEB)

Small angle neutron scattering (SANS) has been a very powerful tool to study nanoscale (1-100 nm) bulk structures in various materials such as polymer, self assembled materials, nano-porous materials, nano-magnetic materials, metal and ceramics. Understanding the importance of the SANS instrument, the 8m SANS instrument was installed at the CN beam port of HANARO in 2001. However, without having a cold neutron source, the beam intensity is fairly low and the Q-range is rather limited due to short instrument length. In July 1, 2003, therefore, the HANARO cold neutron research facility project was launched and a state of the art 40m SANS instrument was selected as top-priority instrument. The development of the 40m SANS instrument was completed as a joint project between Korea Advanced Institute of Science and Technology and the HANARO in 2010. Here, we report the specification of a state of art 40m SANS instrument at HANARO

International Nuclear Information System (INIS)

Mott-Schottky (M-S) analysis is an effective approach to investigate the electronic property of passive films of metals, and it is well suitable for the passive film with single space charge capacitance. But there is no proper method to analyze the Csc-2 vs. Vm plots of passive films with several space charge capacitances in series connection, such as bipolar passive films. In this paper, the relationship between the space charge capacitance of the bipolar passive film and the applied potential was deduced and the features of corresponding plots were given out simultaneously. Accordingly, a non-linear fitting method was presented to analyze the Csc-2 vs. Vm plots of bipolar passive films. Then the method was used to study the semiconductor characteristics of bipolar passive films formed on the surface of Nickel base alloy after being ...

International Nuclear Information System (INIS)

The optical properties and microstructure of germanium (Ge) films, prepared by ion-assisted deposition (IAD) process, were investigated. The Ge films were deposited on sapphire and silicon substrates, with and without simultaneous Ar+ bombardment. Higher index films, with a refractive index 7.7% larger than that of the single crystalline Ge wafer, were obtained with the IAD process. The density of the IAD film could be 1.5% greater than that of the e-beam film. The results of the heat treatment indicated that the optical and structural properties of the IAD films were more stable. Ge nano-crystallites could be observed under high ion power density, which induced a crystalline structure in the Ge thin films. The average size of the nano-crystallites, as determined from both the X-ray diffraction data and the transmission electron microscopy ...

Energy Technology Data Exchange (ETDEWEB)

A radio frequency sputtering apparatus with a pair of targets has been developed for depositing a film of uniform thickness onto a complex-geometric specimen such as the retainer of a ball bearing. The deposition characteristics of the apparatus were compared with those of the conventional sputtering apparatus. Lubrication properties of MoS/sub 2/ films made by these devices were also compared under a variety of conditions. Finally, friction and wear of MoS/sub 2/ films applied to angular-contact type ball bearings of 20 mm bore were studied in air, nitrogen and vacuo. The two-target sputtering has an advantage mentioned above. However, the films deposited by the method exhibited a rather short wear life because of the temperature rise of the substrate during ion bombardment and during the sputtering process. This temperature dependence was observed in films on those substrates that ...

Energy Technology Data Exchange (ETDEWEB)

The temperature dependence of the spontaneous magnetization of epitaxial iron films with a thickness ranging from d=20 to 200nm has been measured. The films are grown on GaAs (100) substrates which are covered by a 150nm thick silver (100) buffer layer. For three-dimensional BCC iron it was observed already in 1929 that saturation of the spontaneous magnetization for T->0 is perfectly described by a T{sup 2} power law. On the other hand, for thin two-dimensional (2D) iron films a T{sup 3/2} law has been established in many recent experimental investigations. In our iron films grown on diamagnetic silver, this dimensionality change occurs at a thickness between d=100 and 200nm. Comparison of the here-observed T{sup 3/2} coefficients with those on iron films grown on paramagnetic tungsten (110) shows that the 2D interactions are {approx}20 times larger in the ...

International Nuclear Information System (INIS)

The composition of sputter-deposited HgS films was determined by electron microprobe analysis. From the relative x-ray intensity as a function of film thickness, the depth of the ionizations that produce SK sub(#alpha#) and HgM sub(#alpha#) was found to be approximately 0.65 #mu#m at an accelerating voltage of 15 kV. This value agreed well with a value calculated from Castaings' empirical law after absorption correction. The determination of film composition was limited to sufficiently thicker films than this critical value, usually 1 - 2 #mu#m thick. The relation between the conposition of bulk standard determined by chemical analysis and the x-ray intensity ratio was used for the correction of film composition. The results showed that the crystal structure of HgS films was independent of the composition, i.e., the growth of metastable #betta#-HgS ...

British Library Electronic Table of Contents (United Kingdom)

Nanocrystalline chromium oxynitride films were deposited by reactive RF magnetron sputtering of metallic chromium target in argon and helium atmospheres. The paper deals with consequence of increase in oxygen partial pressure on structural, hydrophobic and optical properties of chromium oxynitride films. The film stoichiometry changes from CrN and Cr2O3 to only Cr2O3 with increase in oxygen partial pressure as evident from X-Ray Diffraction analysis in both cases. The average crystallite size decreases with increase in oxygen partial pressure for both gas atmospheres. The thickness calculated from transmission data and surface profilometer are in good harmony with each other. The deposited films are hydrophobic by nature and the contact angle of the films varies as a function of surface ro...

Energy Technology Data Exchange (ETDEWEB)

The authors report the fabrication and characterization of a low temperature (200--400 C) thin film gas sensor constructed from a MOCVD-grown yttria-stabilized zirconia (YSZ) layer sandwiched between two platinum thin film electrodes. A reproducible gas-sensing response is produced by applying a cyclic voltage which generates voltammograms with gas-specific current peaks and shapes. Growth conditions are optimized for preparing YSZ films having dense microstructures, low leakage currents, and maximum ion conductivities. In particular, the effect of growth temperature on film morphology and texture is discussed and related to the electrical and gas-sensing properties of the thin film sensor device.

Energy Technology Data Exchange (ETDEWEB)

Grooving CVD diamond films using a focused ion beam (FIB) to quarry micro parts is described. The substrate-side surface of a polycrystalline diamond film which is prepared by means of microwave plasma CVD, is able to be grooved by a focused Ga ion beam scanned straight repeatedly. The groove has cross section whose shape is like an inverted Gaussian distribution curve. And the surface roughness of the films before grooved influences that of grooves. Under the same irradiation conditions, deeper, narrower, in short, high aspect ratio grooves are obtained on B-doped semiconducting microwave plasma CVD diamond films. Coating electrical conductive material is also effective method to obtain high aspect ratio grooves. It is supposed that these results are due to the degree of electrification on the surface and that FIB irradiation is a suitable method for micromachining semiconducting diamond ...

International Nuclear Information System (INIS)

The surface films formed on type 316LN stainless steels (SS) with different nitrogen contents, during potentiodynamic polarization in acidified 1 M NaCl solution, were characterized by Laser Raman Spectroscopy (LRS). LRS confirmed the presence of oxides and oxychlorides of iron and chromium, hydrated chlorides and nitrates in the film. Raman mapping showed increasing nitrate content in the film with increasing nitrogen content. The film on the uncorroded material showed the presence of chromium and molybdenum oxides. The improvement in pitting corrosion resistance of type 316LN SS with increasing nitrogen content was attributed to increased amount of nitrates in the passive film.

International Nuclear Information System (INIS)

The effect of surface treatment on the characteristics of the passive film on a super duplex stainless steel is addressed. Auger Electron Spectroscopy (AES) has been used to provide in-depth chemical profile analyses of the passivation film. This study showed that the constitution of the film is largely dependent on the electrolytic conditions under which it is produced or to which it is submitted. The passive films formed by polarisation in an alkaline solution (boric-borate solution) consist of two regions, an inner region rich in chromium and an outer region rich in iron, whilst the films produced in acid solution only present the chromium - rich region. The film thickness is also greatly affected by the polarisation conditions. It can vary from ca. 8 monolayers to about 20 monolayers for cathodically and anodically polarised specimens respectively. The ...

International Nuclear Information System (INIS)

The effect of Mo addition as an alloying element to stainless steel alloys is investigated by capacitance (Mott Schottky approach), and photoelectrochemistry measurements. Complementary studies were made using Auger electron spectroscopy and X-ray photoelectron spectroscopy. The Mott-Schottky approach and the photoelectrochemical studies showed that the presence of Mo as an alloying element affects the semiconductive properties of the oxide films. The analytical results have shown that the oxide films formed on stainless steels are composed by an external Fe rich region and an inner Cr rich region. No significant amount of Mo was found in the outer layers of the film. The presence of Mo leads to an increase of the chromium content in the inner layers of the film, although without increasing the film thickness. (orig.)

International Nuclear Information System (INIS)

In this work passive films formed in AISI 304 stainless steel were envisaged as semiconductors and studied by means of photoelectrochemistry and Mott-Schottky plots. The passive films were potentiostatically formed at different potentials (0.2-0.8V) in a basic borate/boric acid solution without and with addition of NaCl (0.5 and 1g/l) and at various temperatures in the range 8-60"oC. The influence of these parameters on the photocurrent, quantum efficiency, bandgap energy and density of charge carriers was determined. The results show that the experimental conditions at which the films are formed influence the semiconductive properties of the film, which seem to be related to the higher or lower stability of the film. An Arrhenius type of relationship was also found between the density of charge carriers and temperature, leading to the determination of an activation energy. (author) ...

International Nuclear Information System (INIS)

The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as ...

International Nuclear Information System (INIS)

In this work, amorphous hydrocarbon (a-C:H) film deposition on metallic mirrors was studied during working shots in tokamak T-10 and at exposure in Ar/CHD3/D2 dc magnetron discharge in a special laboratory high vacuum setup. Analysis of film composition (including hydrogen content) was carried out using nuclear physical methods. Thickness and optical parameters (refractive and extinction coefficients) of the films were estimated by ellipsometry. Laboratory films can be characterized as soft a-C:H films in comparison with hard tokamak films (? = 1.2 and 1.8 g/cm3, respectively). For the first one, a linear dependence of deposition rate on mirror temperature was observed in a wide temperature range. The addition of methane into initial Ar/D2 magnetron gas mixture leads to an increase of deposition rate. The data obtained should be taken into account to prevent ...

Energy Technology Data Exchange (ETDEWEB)

This paper addresses one source of degradation in OPV devices: the metal/organic interface. The basic approach was to study the completed device stability vs. the stability of the organic film itself as shown in subsequent devices fabricated from the films.

International Nuclear Information System (INIS)

Semiconductor properties of passive films formed on the Fe-18Cr alloy in a borate buffer solution (pH = 8.4) and 0.1 M H_2SO_4 solution were examined using a photoelectrochemical spectroscopy and an electrochemical impedance spectroscopy. Photo current reveals two photo action spectra that derived from outer hydroxide and inner oxide layers. A typical n-type semiconductor behaviour is observed by both photo current and impedance for the passive films formed in the borate buffer solution. On the other hand, a negative photo current generated, the absolute value of which decreased as applied potential increased in the sulfuric acid solution. This indicates that the passive film behaves as a p-type semiconductor. However, Mott-Schottky plot revealed the typical n-type semiconductor property. It is concluded that the passive film on the Fe-18Cr alloy formed in the borate buffer solution is composed of both ...

British Library Electronic Table of Contents (United Kingdom)

Rheological properties of moderately concentrated solutions of cellulose in methylmorpholine N-oxide-dimethylformamide mixtures containing hydrophilic montmorillonite nanoparticles were studied. Film composite materials were prepared, and their physicomechanical properties and structural organization were studied.

British Library Electronic Table of Contents (United Kingdom)

The nanostructure Ni-doped CdO films have been prepared by sol gel spin coating method. Atomic force microscopy results indicate that the CdO films are formed from the nanoparticles and the grain size is changed with nickel content. X-ray diffraction patterns of the films indicate that the undoped and Ni-doped CdO films have polycrystalline structure with a cubic sodium chloride structure, showing two main characteristic peaks assigned to the (111) and (200) planes. The optical band gap values of undoped and Ni-doped CdO films were determined by optical absorption method. The Eg values of the CdO films were found to be in the range of 2.26?2.60?eV. The Eg values of the CdO films increase with the content of Ni dopant (up to 6% Ni). It is evaluated that the optical band gap and grain size o...

Science.gov (United States)

A thin-film evaporator requires only a short heating time to concentrate a solution since it has a high thermal efficiency and has a small capacity. Thus, the chemical industry often uses this type of evaporator for concentrating materials that are subjec...

International Nuclear Information System (INIS)

Optical absorptance spectra of A-15 compounds were taken using a calorimetric technique in the range 0.2 eV to 4.0 eV. Thermomodulation spectra were taken on several A-15 sputtered films.

UK PubMed Central (United Kingdom)

An examination of the noise of polycrystalline silicon thin film transistors, in the context of flat panel x-ray imager development, is reported. The study was conducted in the spirit of exploring...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The passive films formed on iron metal, alloys or stainless steel are extremely thin oxides or hydroxides and possess the properties of high chemical stability in the environment. These films show characteristics interested both electrical as well as electrochemical point of view due to the thin thickness of the films. Auger Electron Spectroscopy, X-ray Photoelectron spectroscopy and so on which are the conventional electrochemical measurement methods or the surface analysis methods are used for the analysis and evaluation of these films, however, at present, the application of research technique focusing the superconductor characteristics of the films are tried. Although, the potential modulation reflection spectroscopy method has merits like possibility of in-situ measurement, high precision, possibility of stable analysis even for extremely thin film and so ...

Energy Technology Data Exchange (ETDEWEB)

In this work we present an ultra-low temperature method for the oxidation of an amorphous silicon-carbide-nitride (SiCN) material. The SiCN is deposited on silicon substrates by plasma enhanced chemical vapor deposition using CH{sub 4}, SiH{sub 4}, and N{sub 2} chemistry. The physical and chemical properties are characterized for the as-deposited SiCN and post-oxidized films are discussed. The SiCN film is exposed to oxygen plasma, where it undergoes a chemical transformation into a binary SiO{sub 2} material system. A 1.7 nm/min oxidation rate is typical for this process and compares favorably to oxidation methods utilizing much higher temperatures. The substrate temperature remains extremely low throughout the oxidation process, T{sub s} < 200 deg. C. Changes in film stress, optical constants, film thickness, surface roughness, and film density are measured. Chemical ...

Science.gov (United States)

... ordnance requirements. Descriptors : *Combustible cartridge cases, *Patents, Laminates, Felts, Flame inhibitors, Films. Subject ...

International Nuclear Information System (INIS)

... Toshiba Corporation, Isogo Engineering Center, Yokohama, Kanagawa (Japan)

International Nuclear Information System (INIS)

17-4PH stainless steel was modified by direct current (DC) plasma nitriding and titanium nitride film duplex treatment in this study. The microstructure, wear resistance and corrosion resistance were characterized by X-ray diffraction (XRD), pin-on-disk tribological test and polarization experiment. The results revealed that the DC plasma nitriding pretreatment was in favor of improving properties of titanium nitride film. The corrosion resistance and wear resistance of duplex treatment specimen was more superior to that of only coated titanium nitride film.

International Nuclear Information System (INIS)

Microwave Electron Cyclotron Resonance (ECR) Plasma assisted Chemical Vapor Deposition (CVD) technology has been used to prepare Si_3N_4 films, which were analyzed by using infrared (IR) transmission spectroscopy and XPS. The analysis results show that with the increase of the deposition temperature, the H content decrease, and the densification of the film increases. When the temperature is up to 360 degree C, the stoichiometrical rate of Si:N is close to 0.75. The protective property of Si_3N_4 films is also examined

International Nuclear Information System (INIS)

The symposium, Polycrystalline Thin Films - Structure, Texture, Properties, and Applications III, was held at the 1997 Materials Research Society Spring Meeting on March 31--April 4 in San Francisco, California. The topics and investigations were interdisciplinary in nature, and ranged from fundamental to technological. Specifically, the work presented in this volume includes film growth, texture and structural evolution, phase transformation, characterization of grain boundaries and interfaces, stress analysis, and works on polycrystalline Si and SiGe films and devices. Fifty four papers were processed separately for inclusion on the data base.

Science.gov (United States)

... wherever possible. The primary interface for mechanical modeling is through PATRAN, a ... PATRAN Neutral File. PATRAN ...

Energy Technology Data Exchange (ETDEWEB)

The passive corrosion rate of Alloy 22 is exceptionally low in a wide range of aqueous solutions, temperatures and electrochemical potentials, Alloy 22 contains approximately 22% chromium (Cr) by weight; thus, it forms a Cr-rich passive film in most environments. Very little is known about the composition, thickness and other properties of this passive film. The aim of this research was to determine the general characteristics of the oxide film that forms on Alloy 22, as a function of solution pH, temperature and applied electrochemical potential.

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

Evolution of the passive films formed on AISI 304L and duplex stainless steel SAF 2205 in NaOH 0.1 M was investigated using cyclic voltammetry, electrochemical impedance spectroscopy (EIS) and X-ray photoelectron spectroscopy (XPS). Special attention is paid to the effect of Mo in the generation of the films. Results point out to the stabilising effect of the molybdates on the surface of the film, enhancing the formation of a thin layer on the SAF 2205 with a higher Cr/Fe ratio.

International Nuclear Information System (INIS)

One of the main problems related to optical thin film materials used in high power laser environments is the catastrophic damage caused to them due to laser irradiation. While the influence of ion bombardment on the optical properties of oxide thin films is now a well understood subject, the morphology and crystalline behaviour of these films under ion incidence is not so well studied. Hence, it is of great importance to investigate the effects of ion bombardment during growth on the microstructure and crystalline behaviour of oxide materials.

Energy Technology Data Exchange (ETDEWEB)

Photocurrent measurements for stainless steel type 304 in the as-received condition after dc and AV (alternating voltage) passivation have confirmed that significant changes of the passive film properties occur due to AV passivation. The photocurrents were the highest for the sample treated by the AV passivation process (AVPP). The bandgap energy increased from about 2.8 to about 3.05 eV for this treatment. Very similar results have been obtained for pure chromium, which suggests that the AVPP produces a thicker passive film with a less defective nature due to a partial dehydration of the chromium oxide phase in the film.

Energy Technology Data Exchange (ETDEWEB)

A hydrous oxide film for the application as dielectric film is synthesized by immersion of pure aluminum in hot water. From a Rutherford backscattering analysis, the ratio of aluminum to oxygen atoms was found to be 3:2 in the anodized aluminum oxide film, and 2:1 in the hydrous oxide layer. Anodization of the hydrous oxide layer was more effective for the transition of amorphous anodic oxides to the crystalline aluminum oxides.

Energy Technology Data Exchange (ETDEWEB)

The state of lithium electrode surface after contact with triethylamine-modified propylene carbonate solutions of lithium perchlorate was studied using the pulse galvanostatic technique as well as methods of SIMS and electron microscopy. It was shown that amine added into the solutions stabilizes the state of lithium and prevents the formation of a secondary porous passive film on the lithium surface. Chemical composition of the primary film remains unchanged. Certain properties of passive films formed in electrolyte solutions studied were evaluated.

Energy Technology Data Exchange (ETDEWEB)

Significant ion irradiation during film growth is required for the formation of cubic boron nitride (cBN) films. Meanwhile, a huge level of intrinsic stress possibly induced by the ion bombardment has been frequently reported to result in cracking and/or lack of adhesion of deposited cBN films. The present work has been performed to investigate the interfacial and/or the buffer layer structures with better matching to the cBN film by relaxation of the film stress using ion-beam-assisted deposition (IBAD). Boron nitride films have been synthesized on Si(100) wafer and tungsten carbide (WC) substrates by depositing boron vapor under simultaneous bombardment with nitrogen ions and nitrogen-argon mixture ions in the energy range of 0.5-10 keV. Cubic BN films with enhanced tribological properties have been explored by inserting a BN layer with ...

CERN Document Server

We study the growth of colonies of the yeast Pichia membranaefaciens on agarose film. The growth conditions are controlled in a setup where nutrients are supplied through an agarose film suspended over a solution of nutrients. As the thickness of the agarose film is varied, the morphology of the front of the colony changes. The growth of the front is modeled by coupling it to a diffusive field of inhibitory metabolites. Qualitative agreement with experiments suggests that such a coupling is responsible for the observed instability of the front.

International Nuclear Information System (INIS)

The study by impedance and photoelectrochemical measurements of passive films formed on an AISI 304 type stainless steel shows that important parameters of the electronic structure of these films are modified under #alpha# irradiation, namely: width of the space charge region, donors concentration and diffusion length for minority carriers. The consequences of #alpha# irradiation on localized corrosion processes are discussed.

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Science.gov (United States)

In the present work, a new kind of myoglobin (Mb)/Au nanoparticles composite film was fabricated on pyrolytic graphite (PG) electrodes. Oppositely charged chitosan (CS) and silica (SiO(2)) nanoparticles were alternately adsorbed on the PG surface by the electrostatic interaction between them, forming {CS/SiO(2)}(5) layer-by-layer films. Mb and HAuCl(4) in solution were then simultaneously loaded into {CS/SiO(2)}(5) films. The loaded Au(III) in the films were electrochemically reduced into Au nanoparticles, forming nanocomposite films, designated as {CS/SiO(2)}(5)-Mb-Au. Various techniques such as cyclic voltammetry (CV), square wave voltammetry (SWV), quartz crystal microbalance (QCM), electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analysis were used to characterize the films. Compared with ...

British Library Electronic Table of Contents (United Kingdom)

Deposition of CN-based films by a novel version of active screen plasma nitriding, aiming at surface modification of polymers, is reported. The approach relies on the use of pure graphite as the grid material, which was found to act both as an active screen and as a dry source of carbon atoms for the synthesis of thin films consisting mainly of a stoichiometric CN layer with columnar-type structure and dome-like nanostructured morphology.

Energy Technology Data Exchange (ETDEWEB)

A study has been made of the passive film remaining over pits on stainless steel using a high resolution transmission electron microscope. Type 305 stainless steel was passivated in a borate buffer solution and pitted in ferric chloride. Passive films formed at 0.2 V relative to a saturated calomel electrode were found to be amorphous. Films formed at higher potentials showed only broad diffraction rings. The passive film was found to cover a remnant lacy structure formed over pits passivated at 0.8 V. The metallic strands of the lace were roughly hemitubular in shape with the curved surface facing the center of the pit.

Energy Technology Data Exchange (ETDEWEB)

Moss-Schottky plots and photoelectrochemical measurements were made on films formed at different potentials on AISI 304 stainless steel in a borate/boric acid solution, pH 9.2. The results allowed the determination of the semiconductive properties and band structure of the films, which account for the existence of two kinds of films depending on the formation potential. For potentials below 0 V (SCE), the results point out for a film with an inverse spinel structure constituted by Cr-substituted magnetite with two donor levels. Above 0 V only one donor level is detected, which should be Fe{sup 2 +} on tetrahedral sites.

Energy Technology Data Exchange (ETDEWEB)

The passive films formed on 316L stainless steel in various NaCl solutions have been investigated by capacitance measurements (Mott-Schottky). Pitting parameters have been determined using the galvano-kinetic polarisation method. The obtained results reveal the existence of a shallow and a deep donor level localised in the band gap of the semiconducting oxide film. These energy levels are due to iron ions in the tetrahedral and octahedral positions. It also appears that the participation of the deep donor level effects the electric field. The study developed allows us to compare characteristic parameters of the electronic structure of the passive film to those related to pitting susceptibility. (authors) 25 refs.

British Library Electronic Table of Contents (United Kingdom)

Abstract A series of polypropylene carbonate (PPC)/ZnO nanocomposite films with different ZnO contents were prepared via a solution blending method. The morphological structures, thermal properties, oxygen permeability, water sorption, and antibacterial properties of the films were investigated as a function of ZnO concentration. While all of the composite films with less than 5 wt % ZnO exhibited good dispersion of ZnO in the PPC matrix, FTIR and SEM results revealed that solution blending did not lead to a strong interaction between PPC and unmodified ZnO. As such, poor dispersion was induced in the composite films with a high ZnO content. By incorporating inorganic ZnO filler nanoparticles, the diffusion coefficient, water uptake in equilibrium, and oxygen permeability decreased as the ...

Energy Technology Data Exchange (ETDEWEB)

Photocurrent and capacitance measurements of semiconductor passive films formed on metals and alloys can be used to study the electronic properties and reveal indirect information about structure and composition. The current work used these techniques to investigate the electronic properties of the passive films formed on three austenitic stainless steels, types 304L, 316L and 254SMO, in borate. Evidence was found for the existence of a large number of localised mid bandgap states, consistent with amorphous oxides. However, the flat-band potentials of the austenitic stainless steel passive films were found to be independent of both composition and measuring frequency. The most credible explanation for the bandgap values determined from photocurrent measurements is that the passive films are formed as dual layers, iron oxide outer layer and chromium oxide inner layer. This model does not need to evoke ...

British Library Electronic Table of Contents (United Kingdom)

In this paper, we study the optical properties of indium sulfide thin films to establish the best conditions to obtain a good solar cell buffer layer. The In2S3 buffer layers have been prepared by chemical bath deposition (CBD) and thermal evaporation (PVD). Optical behavior differences have been found between CBD and PVD In2S3 thin films that have been explained as due to structural, morphological and compositional differences observed in the films prepared by both methods. The resultant refractive index difference has to be attributed to the lower density of the CBD films, which can be related to the presence of oxygen. Its higher refractive index makes PVD film better suited to reduce overall reflectance in a typical CIGS solar cell.

Energy Technology Data Exchange (ETDEWEB)

In an effort to develop a simple low-temperature high-performance polysilicon thin-film transistor (TFT) technology, the authors report a fabrication process featuring laser-crystallized sputtered-silicon films. This top Al-gate coplanar TFT process subjects the substrate to a maximum temperature of 300 C, and produces devices with mobilities up to 450 cm{sup 2}/Vs, on/off current ratios greater than 10{sup 7}, without using a post-hydrogenation step. They believe these results represent the highest performance TFT`s to date fabricated from sputtered silicon films.

International Nuclear Information System (INIS)

We have measured K-edge X-ray absorption spectra of argon in sputtered aluminum films at a synchrotron radiation facility (the Photon Factory). We found that the energy and shape of white line change when the film is annealed at 500 C and the spectrum becomes resembling that of argon implanted in silicon. From the analyses of the X-ray absorption spectra and TEM observation we concluded that argon exists as very small atom clusters with a diameter less than 1 nm or exist as isolated atoms in the as-sputtered aluminum film, and that the size of the clusters become as big as 10 nm diameter when the film is heated. (Copyright (c) 1999 Elsevier Science B.V., Amsterdam. All rights reserved.)

Energy Technology Data Exchange (ETDEWEB)

Passive films formed on Alloy 690 in different pH solutions at high temperatures were studied by potentiodynamic polarization, Auger electron spectroscopy, thermodynamic diagrams and the Mott-Schottky relation. The chemical compositions and electronic structures of the passive films were found to be strongly pH-dependent. In alkaline solutions, a secondary passivation was clearly observed on potentiodynamic polarization curves. The passive films were a mixture of Cr{sub 2}O{sub 3} and FeCr{sub 2}O{sub 4} below the flat band potential of nickel oxide and were NiFe{sub 2}O{sub 4} above this potential. Electronic structure models, describing the electrochemical properties of the passive films, are proposed and discussed.

Energy Technology Data Exchange (ETDEWEB)

The evolution of strain in the Pd-Si system during the growth of Pd{sub 2}Si thin films on Si (100) substrate has been followed in situ using a double optical beam technique. As was observed for the Pt-Si system, the reaction to form Pd{sub 2}Si yields a compressive intrinsic surface film stress as well as for the silicon-rich suicides as proposed by Angilello et al. [Thin Film Interfaces and Interactions, edited by J. Baglin and J. Poate (The Electrochemical Society, Pennington, NJ, 1980)]. A transmission electron microscopy analysis has revealed grain growth during the formation of Pd{sub 2}Si which cannot account for the compressive film stresses. The formation of silicide at the interfaces rather than the overall change in volume agrees with the sign of the stresses formed. 29 refs., 4 figs., 3 tabs.

Energy Technology Data Exchange (ETDEWEB)

Passive films formed on Alloy 690 in high-temperature alkaline environments were investigated by potentiodynamic polarization, X-ray photoelectron spectroscopy, transmission electron microscopy and Mott-Schottky approach. Passive current density and donor density of the passive films increase with increasing temperature, due to increased diffusion rates of metallic ions and dehydration of hydroxide phases. The passive films show a duplex structure including an inner layer of fine-grained Cr oxide or spinel oxide and an outer layer of Ni-Fe spinel oxide and Ni hydroxide. A growth model of the passive films on Alloy 690 in high-temperature alkaline environments is proposed and discussed.

Energy Technology Data Exchange (ETDEWEB)

It is well known that a protective film is formed on the graphite negative electrode in ethylene carbonate (EC) electrolyte solution. This film is lithium-ion conductive and protects the decomposition of the electrolyte solution. In the present paper, the electrode/electrolyte interfaces in lithium-ion rechargeable batteries were characterized by three-dimensional complex impedance plots, whose axes are real, imaginary parts and time. The film resistance R {sub sei} and charge transfer resistance R {sub ct} were determined for negative electrodes in EC/ethyl methyl carbonate (EMC) electrolyte solution, and the formation mechanisms of the interfacial film were discussed. Furthermore, the contributions of vinylene carbonate and ethylene sulfite, which are added into the electrolyte solution for the film formation, were investigated.

British Library Electronic Table of Contents (United Kingdom)

In this work, effects of coolant chemistry, including concentrations of chloride ions and ethylene glycol and addition of various ions, on corrosion of 3003 Al alloy were investigated by electrochemical impedance spectroscopy measurements and scanning electron microscopy characterization. In chloride-free, ethylene glycol-water solution, a layer of Al-alcohol film is proposed to form on the electrode surface. With the increase of ethylene glycol concentration, more Al-alcohol film is formed, resulting in the increase in film resistance and charge-transfer resistance. In the presence of Cl- ions, they would be involved in the film formation, decreasing the stability of the film. In 50% ethylene glycol-water solution, the threshold value of Cl- concentration for pitting initiation is within ...

International Nuclear Information System (INIS)

In 16 female patients wick colpourethrocystography was performed directly successively with large-size films as well as medium-size films (intensifier fluorography). The area exposure products were measured by a dosemeter closely attached to the diaphragm and separately for radiography and fluorography, resp. Surface doses as well as organ doses were calculated according to Rosenstein. The average radiatin doses of the active bone marrow were 6.03 mGy for examination with large-size films and 1.27 mGy for fluorography; the average gonadal doses were 7.45 mGy and 1.56 mGy, resp. The portion of fluoroscopy in radiation exposure amounted to 14.8% in large-size film examination, but was 74.0% in medium-size examination. Thus the comparative results revealed a significant reduction of the patient's radiation dose by application of intensifier fluorography in colpourethrocystography.

British Library Electronic Table of Contents (United Kingdom)

Abstract:- Campylobacter jejuni-is the leading cause of bacterial diarrheal illness worldwide. Many strains are now becoming multidrug resistant. Apple-based edible films containing carvacrol and cinnamaldehyde were evaluated for bactericidal activity against antibiotic resistant and susceptible-C. jejuni-strains on chicken. Retail chicken breast samples inoculated with D28a and H2a (resistant strains) and A24a (a sensitive strain) were wrapped in apple films containing cinnamaldehyde or carvacrol at 0.5%, 1.5%, and 3% concentrations, and then incubated at 4 or 23 C for 72 h. Immediately after wrapping and at 72 h, samples were plated for enumeration of viable-C. jejuni. The antimicrobial films exhibited dose- and temperature-dependent bactericidal activity against all strains. Films with ...

International Nuclear Information System (INIS)

Iron oxide films have been deposited on Si(100) substrates by chemical vapour deposition (CVD) of iron(III) tert-butoxide ([Fe(O "tBu)_3]_2) in the temperature range 350-450 deg. C. The precursor flux and substrate temperature were varied to control the phase composition, average grain size and film thickness. The nature of substrate and deposition temperature markedly influence the morphology and iron-oxygen stoichiometry in the CVD deposits. Phase transformations in iron oxide films were achieved through precise local and periodic heating of the films by interfering laser beams. The interaction of iron oxide films with short laser pulses (Nd:YAG, 355 nm) induced partial transformation of hematite (#alpha#-Fe_2O_3) to magnetite (Fe_3O_4) or magnetite to wuestite (Fe_1_-_xO), respectively. The phase characterization and morphology of the hematite and magnetite ...

Energy Technology Data Exchange (ETDEWEB)

Investigations of the properties of absorbed monolayers have received great experimental and theoretical attention recently, both because of the importance of surface processes in practical applications such as catalysis, and the importance of such systems to the understanding of the fundamentals of thermodynamics in two dimensions. We have adapted the composite bolometer technology to the construction of microcalorimeters. For these calorimeters, the adsorption substrate is an evaporated film deposited on one surface of an optically polished sapphire wafer. This approach has allowed us to make the first measurements of the heat capacity of submonolayer films of /sup 4/He adsorbed on metallic films. In contrast to measurements of /sup 4/He adsorbed on all other insulating substrates, we have shown that /sup 4/He on silver films occupies a two-dimensional gas phase over a broad range of coverages and ...

International Nuclear Information System (INIS)

In this paper, we present the results of Plasma-Enhanced Chemical Vapor Deposition gate-oxide (SiO_2) integrity on ELC (excimer-laser-crystallized), MILC (metal-induced lateral-crystallized) and SPC (solid-phase-crystallized) polysilicon films. We observed that gate oxide strength of poly-Si TFT strongly depends on the crystallization method for the active silicon layer. In the case of ELC films, asperities on the silicon surface reduce the SiO_2 breakdown field significantly. The metallic contaminants in MILC films are responsible for a deleterious impact on gate oxide integrity. Among the three cases, the SiO_2 breakdown field was the highest for the SPC silicon films. The breakdown fields at the 50 % failure points in Weibull plots for the ELC, MILC and SPC cases were 5.1 MV/cm, 6.2 MV/cm, and 8.1 MV/cm, respectively. We conclude that the roughness and metallic contamination of the poly-Si ...

Energy Technology Data Exchange (ETDEWEB)

The total hemispherical emittance of an oxide film that formed on 6061-T6 aluminium alloy parts in the Tower Shielding Reactor-II at Oak Ridge National Laboratory was measured from 295 to 773 K using an emissometer and/or a calorimeter. The emittance of this film was critically needed for heat transfer calculations in a simulated loss-of-coolant accident of the reactor. X-ray diffraction analysis identified the film as boehmite (Al{sub 2}O{sub 3} {times} H{sub 2}O), which dehydrated to alumina (Al{sub 2}O{sub 3}) upon heating above 473 K. The measured emittances for the alumina film are in excellent agreement with published values for anodized aluminum films and for bulk alumina. Published values of the emittance of boehmite could not be found for comparison, but evidence is presented that some anodization processes for aluminum yield boehmite and not alumina ...

Energy Technology Data Exchange (ETDEWEB)

The formation and breakdown of the passive films on stainless steels are mainly controlled by ionic and electronic transport processes. Both these processes are in part controlled by the electronic properties of the oxide film. Consequently, it is vital to gain a detailed perception of the electronic properties of the passive films together with structural and compositional information for a comprehensive understanding of mechanisms behind passivity and localised corrosion. As a step towards this goal the passive films formed on two main austenitic stainless steels AISI 316L and AISI 304L in borate solution were characterised by in situ Raman spectroscopy and photocurrent spectroscopy coupled with electrochemical measurements. This revealed the formation of an Fe-Cr spinel as the dominant constituent in the passive films with more Cr enrichment in the oxide film ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical behaviour of passive films formed on one austenitic stainless steel (AISI 304) and one ferritic stainless steel (AISI 446) in solutions with pH between 0.6 and 8.4 was studied by capacitance measurements and photocurrent spectroscopy. Compositional characterization of the passive films was done by X-ray photoelectron spectroscopy. The capacitance increases with decreasing pH. Doping densities evaluated from Mott-Schottky plots are in the range 2-6 x 10{sup 20} cm{sup -3} and increased with the pH in the neutral/alkaline range while in pH 0.6, values above 10{sup 21} cm{sup -3} were found. The bandgap energy indicates two transitions, at 2.5-2.8 and 3.2 eV. The analytical data reveal that, as the pH increased, the films become enriched in Fe(II) and Fe(III), whereas the Cr(III) gradually decreases. The films formed at very low pH had a behaviour that contrasts with that of the ...

Science.gov (United States)

Thin-film solar cells on flexible, lightweight, space-qualified substrates provide an attractive approach to fabricating solar arrays with high mass-specific power. A polycrystalline chalcopyrite absorber layer is among the new generation of photovoltaic device technologies for thin film solar cells. At NASA Glenn Research Center we have focused on the development of new single-source precursors (SSPs) for deposition of semiconducting chalcopyrite materials onto lightweight, flexible substrates. We describe the syntheses and thermal modulation of SSPs via molecular engineering. Copper indium disulfide and related thin-film materials were deposited via aerosol-assisted chemical vapor deposition using SSPs. Processing and post-processing parameters were varied in order to modify morphology, stoichiometry, crystallography, electrical properties, and optical properties to optimize device quality. Growth at atmospheric pressure ...

Science.gov (United States)

High quality La/sub 1.8/Sr/sub 0.2/CuO/sub 4/ and YBa/sub 2/Cu/sub 3/O/sub 7/ superconducting thin films, with zero resistance at 88 K, have been made by dual-ion-beam sputtering of metal and oxide targets at elevated temperatures. The films are about 1.0 ..mu..m thick and are single phase after annealing. The substrates investigated are Nd-YAP, MgO, SrF/sub 2/, Si, CaF/sub 2/, ZrO/sub 2/-9% Y/sub 2/O/sub 3/, BaF/sub 2/, Al/sub 2/O/sub 3/, and SrTiO/sub 3/. Characterization of the films was carried out using Rutherford backscattering spectroscopy, resistivity measurements, transmission electron microscopy, x-ray diffraction, and secondary ion mass spectroscopy. Substrate/film interaction was observed in every case. This generally involves diffusion of the substrate into the film, which is accompanied by, for example, the replacement of Ba by Sr in the YBa/sub 2/Cu/sub 2/O/sub 7/ ...

International Nuclear Information System (INIS)

Graphical abstract: Ordered mesoporous organic-inorganic composite film has been achieved by sol-gel and spin-coating techniques. We believe that the mesoporous composite films have a potential application as a protect coating of bipolar plate material. Display Omitted Research highlights: ? Ordered mesoporous composite film was deposited on the 304 stainless steel. ? This composite film exhibited excellent protective performance in 0.5 M H_2SO_4. ? The film exhibited a high surface tension with water contact angle close to 90"o. - Abstract: The organic-inorganic composite film was deposited on the 304 stainless steel as bipolar plate material for proton exchange membrane fuel cells by spin-coating method. As shown by XRD, N_2 adsorption-desorption and TEM, the composite films exhibit ordered mesoporous structures. The corrosion tests in 0.5 ...

Energy Technology Data Exchange (ETDEWEB)

Film boiling is the mode if boiling during which the hot surface is separated from the vaporizing liquid by a nearly continuous film vapor. Film boiling is usually considered a very undesirable boiling regime since it is a relatively quiet and inefficient mode of heat transfer, particularly as compared to nucleate boiling. It is customary to analyze the two-phase flow regime of laminar flow film boiling by assuming the two-phase flow regime of laminar flow film boiling by assuming an idealized vapor film flow characterized by a smooth liquid-vapor interface. However, during stable flow film boiling, the wavy nature of the liquid-vapor interface and its role in local heat and mass transport have been largely ignored. The vapor interface is rarely stationary. Interfacial waves may substantially augment the heat transfer rates throughout the ...

Energy Technology Data Exchange (ETDEWEB)

The emittance of aluminum components exposed to low-temperature aqueous solutions were required for thermal analysis of a Loss of Cooling Accident for the Savannah River Site production reactors. Experimental data for the thickness and emittance of oxide films formed under these conditions were collected and reviewed. Correlations were developed for the oxide film thickness and corresponding total hemispherical emittance. Film thickness and emittance were also measured for the specific conditions of interest in order to verify the predictions based on the literature data. After one year of exposure in 30deg C reactor moderator, the aluminum oxide film thickness is predicted to be 6.4 [mu]m[+-]10%; this value is relatively insensitive to exposure time. Some phenomena which would tend to yield thicker oxide films in the reactor environment relative to those obtained under experimental ...

Energy Technology Data Exchange (ETDEWEB)

The entrapment of proteins using the sol-gel route provides a means to retain its native properties and artificially reproduce the molecular crowding and confinement experienced by proteins in the cell allowing investigation of the physico-chemical and structural properties of biomolecules at the biotic/abiotic interface. The biomolecules are spatially separated and 'caged' in the gel structure but solutes can freely permeate the matrix. Thus, properties such as the folding of ensembles of individual molecules can be examined in the absence of aggregation effects that can occur in solution studies. Green fluorescent protein from Aequorea coerulescens was used as a model protein to examine the unfolding/re-folding properties of protein in silica gels. The recombinant protein was isolated and purified from Escherichia coli extracts by cell lysis, three-phase partitioning, dialysis, and anion exchange chromatography. The purity of the protein was greater than 90% as ...

Energy Technology Data Exchange (ETDEWEB)

The influence of small amounts of alloying elements (0.36% Cu and 0.47% Cr) on the semiconducting properties of passive films formed on weathering steels was investigated either in tetraborate/boric acid buffer solution (pH 9.2) or artificial atmospheric environment (SO{sub 2}-containing environment). The electrochemical behaviour was assessed by potentiodynamic polarisation, capacitance measurements and photoelectrochemistry. The chemical characterisation of the films was carried by Auger electron spectroscopy. The polarization results obtained in the buffer solution show that the addition of chromium decreases the passive current density. The capacitance results show that the films behave as an n-type semiconductor with shallow and deep donor levels situated in the forbidden gap. The presence of copper seems to affect the density of the shallow and of the deep donor levels in the forbidden gap, and as chromium, it also ...

Energy Technology Data Exchange (ETDEWEB)

The effect of temperature (60-280{sup o}C) on the properties of the oxide films formed on Alloy 800 in 0.1 M NaCl and 0.1 M Na{sub 2}SO{sub 4} aqueous solutions was studied by in situ AC impedance spectroscopy and polarization in the Fe(CN{sub 6}){sup -3}/Fe(CN){sub 6}{sup -4} redox system. The anodic behavior under the same experimental conditions was examined by potentiodynamic polarization techniques. In both solutions the passive film was found to become more porous, and hence less protective, with increasing temperature. However, at temperatures above 150{sup o}C, the loss of film protectiveness is more pronounced in chloride solutions, in which pitting occurs. Pitting morphology was found to be strongly temperature dependent: isolated and deep pits were found up to 200{sup o}C whereas at higher temperatures a broad, shallow and more generalized type of attack was detected. No effect of temperature on the defect ...

International Nuclear Information System (INIS)

Electrodeposition of semiconducting iron oxide (Fe_2O_3) thin film was carried out from an alkaline sulphate bath. A 0.1 M ferrous sulphate (FeSO_4#centre dot#7H_2O) was complexed with 0.1 M citric acid. By addition of 1 N NaOH, pH of the solution was made alkaline (pH=9) and deposition of iron oxide (Fe_2O_3) thin films was carried out potentiostatically at room temperature (300 K). From cyclic voltametry (CV), electrochemical studies were carried out for deposition of iron oxide thin films. The XRD studies reveal that Fe_2O_3 with epsilon (#epsilon#) phase having monoclinic crystal structure is formed. By observing scanning electron microscope (SEM), it is seen that iron oxide films were homogeneous, uniform and well covered to surface of the substrate. Grain size was found to be in nanometers range from XRD analysis. The optical band gap of Fe_2O_3 thin film was estimated to be ...

Energy Technology Data Exchange (ETDEWEB)

In 1977 and 1978, Sandia National Laboratories, located in Albuquerque, New Mexico, and operated for the US Department of Energy (DOE), filmed a series of crash and fire tests performed on three casks designed to transport irradiated nuclear fuel assemblies. While the tests were performed to assess the applicability of scale and computer modeling techniques to actual accidents, films of them were quickly pressed into service by the DOE and nuclear utilities as proof'' to the public of the safety of the casks. In the public debate over the safety of irradiated nuclear fuel transportation, the films have served as the mainstay for the nuclear industry. Although the scripts of all the films were reviewed by USDOE officials before production, they contain numerous misleading concepts and images, and omit significant facts. The shorter versions eliminated qualifying statements contained in ...

Energy Technology Data Exchange (ETDEWEB)

The temperature effect on corrosion behaviors of PbCaSnCe alloy in 4.5 M H{sub 2}SO{sub 4} solution was investigated by using potentiodynamic curve, electrochemical impedance spectra (EIS), Mott-Schottky plot and photocurrent response methods. It was found that PbCaSnCe alloy was in passive state in sulfuric acid solution, a passive film can be formed on alloy surface. The compositions of passive films formed at 0.9 V for 2 h under different temperatures were detected by X-ray photoelectron spectroscopy (XPS). The results showed that the film resistance and the transfer resistance decreased with the increment of the solution temperature. Mott-Schottky analysis and the photocurrent response revealed that the passive film exhibited n-type semi-conductive character, the donor density of the passive film decreased with increasing the solution temperature. Photocurrent response revealed ...

Energy Technology Data Exchange (ETDEWEB)

Electronic properties of passive films formed on Fe at various applied potentials in pH 8.5 buffer solution were examined through the photocurrent measurement and impedance spectroscopy. Passive film formed on Fe at relatively low potentials was found to be r-FeOOH layer and internal r-Fe{sub 2}O{sub 3} layer. However, the r-FeOOH layer became unstable and disappeared at potentials below 400mV and hence may be an adsorbed layer. An electronic band structure model for the passive film of Fe was suggested on the basis of the spinel band model with involving two types of electronic excitation processes, i. e., the p-d and the d-d transition together. The effects of applied potential on the photocurrent behaviors of the passive film on Fe were explained appropriately by separating the photocurrent spectra depending on the transition type. The Mott-Schottky behavior for the passive film ...

International Nuclear Information System (INIS)

In the region of annular liquid film-mist flow, the behavior of the droplets formed from the liquid film and the rate of formation are the subjects to be clarified in connection with the forecast of dry-out point, which becomes a problem in the region of high dryness such as reactor cooling system and steam generators. Many researches have been performed on such problem in vertical tubes, but the characteristics in horizontal flow have not yet been sufficiently clarified. This series of research is to clarify various characteristics, such as the velocity of vapor phase, the flow rate distribution of droplets, the formation and adhesion of droplets and the structure of liquid film, in the region of liquid film-mist flow, where liquid film exists on the bottom of a horizontal rectangular channel, and vapor flow is accompanied by droplets. In this study, by the measurement of the flow ...

International Nuclear Information System (INIS)

Since April, 1985, we have, in co-operation with the Fuji Film Co., Ltd., used Fuji Computed Radiography (FCR) in the diagnosis of spinal disorders. FCR is a new computed radiographic system which uses an energy-storage phosphorus panel called an ''Imaging Plate'' as an image sensor. The ''Imaging Plate'' can be used to obtain radiographs in exactly the same way as the screen-film combination used in conventional radiography; X-rays are exposed on the ''Imaging Plate'' instead of X-ray film in the conventional fashion, and then the ''Imaging Plate'' is calculated. The processed digital data from the scans is transformed into a picture by means of digital-to-analogue conversion. The pictures are always clear and beautiful. Plain films of the spine taken by FCR are even clearer, even in the cervicothoracic region, where it is usually difficult to obtain clear cervicothoracic films in ...

Energy Technology Data Exchange (ETDEWEB)

The changes in the electrical and structural properties of metal-silicide films caused by ion implantation and subsequent thermal annealing have been investigated. Epitaxial silicide films such as those of CoSi/sub 2/, NiSi/sub 2/ and Pd/sub 2/Si grown on Si(111) substrates were implanted with Ar ions and annealed in a vacuum furnace at temperatures ranging from 200 to 800/sup 0/C. Rutherford backscattering and channeling techniques and the four-point probe method were used to measure the crystalline quality and the sheet resistance of the films, respectively. It was found that the sheet resistances of CoSi/sub 2/, NiSi/sub 2/ and Pd/sub 2/Si films were increased by factors of 70, 6, and 3, respectively, by implantation to a dose of 1 x 10/sup 16/ Ar-ions/cm/sup 2/, but that they were almost restored by subsequent annealing to the values before implantation. A phase transformation from Pd/sub 2/Si to ...

Energy Technology Data Exchange (ETDEWEB)

The effects of gate and drain bias stresses on thin film transistors fabricated in polysilicon films crystallized using the advanced sequential lateral solidification excimer laser annealing (SLS ELA) process, which yields very elongated polysilicon grains and allows the fabrication of TFTs without grain boundary barriers to current flow, are investigated as a function of the active layer thickness and of the TFT orientation relative to the grains. The application of hot carrier stress, with a condition of V{sub GS} = V{sub DS}/2, was determined to induce threshold voltage, subthreshold swing and transconductance degradation for TFTs in thicker polysilicon films and the associated stress-induced increase in the active layer trap density was evaluated. However, this device degradation was drastically reduced for TFTs fabricated in ultra-thin films. Furthermore, the application of the same stress ...

International Nuclear Information System (INIS)

In this work, the effects of substrate temperature that was changed from 100 to 500 "oC on the structural, chemical and electrical properties of carbon films, prepared by direct current magnetron sputtering technique, on 316L stainless steel as bipolar plate had been investigated. Raman spectroscopy and scanning electron microscopy (SEM) were performed to study the structure and the morphology of the deposited films, respectively. The corrosion resistance and the electrical resistivity were carried out by using corrosion tests and four point-probe technique. The results show that the carbon films change the structure from amorphous to graphite-like by increasing temperatures. At the temperatures higher than 300 "oC, the holes and porosities are formed on the film indicating a decrease of film quality. According to our results, corrosion resistance and electrical properties are ...

International Nuclear Information System (INIS)

Thin passive films formed on highly corrosion-resistant type-312L stainless steel, containing 20 mass% chromium and 6 mass% molybdenum, in 2 mol dm-3 HCl solution at 293 K have been analyzed by glow discharge optical emission spectroscopy (GDOES). The stainless steel does not suffer pitting corrosion even in this aggressive solution, showing a wide passive potential region. The depth profiles obtained clearly show a two-layer structure of the air-formed and passive films: an outer iron-rich layer and an inner layer highly enriched in chromium. Alloy-constituting molybdenum is deficient in the inner layer of the passive films and is enriched in the outer layer, particularly at the active dissolution potential. The molybdenum species in the outer layer may retard the active dissolution of stainless steel, promoting the formation of stable passive films highly enriched in chromium. Chloride ions are ...

Energy Technology Data Exchange (ETDEWEB)

Ion bombardment during deposition can significantly modify the film properties. In the partially ionized beam deposition, ions derived from the depositing material, i.e., the self-ions, are used during deposition. Cu films were deposited on SiO{sub 2} substrates at room temperature using 1% Cu self-ions with an energy ranging between 0--4 keV. We studied the microstructures of the Cu films using x-ray diffraction and transmission electron microscopy, measured the impurity level inside the films using secondary ion mass spectrometry, and performed the resistivity measurements using a four point probe. The results indicate that there is an optimum ion energy around 2 keV at which, the integrated x-ray intensity ratio {ital I}(111)/{ital I}(200) reaches its maximum value indicating a strong {l angle}111{r angle} texture, while the impurity concentration and resisitivity are minimum. The correlation between ...

International Nuclear Information System (INIS)

Objective: To evaluate the quality and usefulness of direct digital radiography system in roentgenogram of chest in clinical practice. Methods: 1000 cases of chest roentgenograms with digital radiography and high kV conventional radiography were selected for analysis by 3 senior radiologists. Results: 1. With digital radiography system, the quality of chest film was assessed as grade A in 50.6%, grade B in 38.5%, grade C in 10.9%, and no waste film. 2. With conventional high kV radiography, the quality of chest film was assessed as grade A in 41.1%, grade B in 44.1%, grade C in 13.3%, and waste film in 1.5%. The direct digital radiography was statistically superior to the conventional high kV radiography. 3. The fine structure of the lungs could be revealed in 100.0% of chest roentgenogram with direct digital radiograph system, which was significantly higher than that acquired with the conventional high ...

International Nuclear Information System (INIS)

Magnetic materials such as yttrium iron garnet (YIG) are of great importance for its magneto-optic properties and for their potential applications in the domain of optical telecommunications. The deposition of thin films of YIG, on quartz or GGG (gadolinium gallium garnet) substrate, was performed using radio frequency non reactive magnetron sputtering, followed by high temperature annealing which is needed to enhance the crystallinity of the layers. Rutherford backscattering spectrometry RBS was used to determine the thickness and stoichiometry of the performed layers in order to investigate correlations between growth conditions and the quality of the final material. RBS measurements showed the influence of the deposition time and the temperature substrate on the film growth and its stoichiometry. (author)

Energy Technology Data Exchange (ETDEWEB)

Thin films of La{sub 0.6}Ca{sub 0.4}CoO{sub 3} perovskite were deposited on nickel plates by thermal decomposition of the metal nitrates. The electrochemical activity of the films for oxygen evolution in KOH solutions (0.1-1 M) was investigated. The reaction order with respect to OH{sup -} ion was found to be around 0.7. The results correlate fairly well with a mechanism in which breaking of the intermediate metal-peroxide bond at the Co ion is the rate-determining step. (author) 4 figs., 4 refs.

Energy Technology Data Exchange (ETDEWEB)

The magnetization of ultrathin bcc Fe films (two and three monolayers) on MgO was measured and compared with the behavior predicted for a two-dimensional ferromagnet. The experiment indicated that no hysteresis was present in the magnetization. Instead, the magnetization at low temperature was affected by a marked field cooling effect. These observations lead to the conclusion that films of Fe on MgO of such thickness exhibit superparamagnetic behavior as if they were not entirely continuous. In contrast, films thicker than five monolayers exhibit a magnetic response close to that of bulk iron.

International Nuclear Information System (INIS)

The effects of #alpha# particle irradiation on a passive film formed on a 304 type stainless steel are studied in situ. The experimental arrangement minimizes the radiolysis effects due to the electrolyte. Under irradiation, a modification of the electronic structure of the oxide layers is revealed by photo-electrochemistry and impedance measurements. The influence of irradiation on the corrosion resistance of the passive film is investigated. Comparing the rest potential and the breakdown potential respectively under and without irradiation, a drop in the passivity range under irradiation is shown. this is interpreted as a decrease in the corrosion resistance. (author).

International Nuclear Information System (INIS)

The capability of screen-film combinations of detection and representation of information is described by the detective quantum efficiency (DQE). The DQE may be calculated from the sensitivity, the gradient of the characteristic curve, the modulation transfer function and the Wiener spectrum. These parameters have been determined for fourteen screen-film combinations and the DQE's have been calculated. It is shown that the low frequency region the DQE does not depend on spatial frequency. This constant level of DQE is mostly dependent on the absorbance of the screens. Consequences from this fact, as well for the manufacturer as for the user of the screens, are discussed. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Carbon nano tubes are easily produced in macroscopic quantities, however their characterisation and possible applications are still rather limited. We have developed a new method to make aligned nano tube films which open new opportunities, not only for basic research but also for eventual applications. With this method the tubes can be aligned either parallel or perpendicular to the surface. We give a short review of the microscopic properties of single tubes and the bulk properties of the aligned films. (author). 24 refs., 6 figs.