The sunlight-induced photocatalytic oxidation of aqueous benzene on TiO(2)-supported gold nanoparticles was considerably improved when the reaction was conducted under a CO(2) atmosphere. 13% yield and 89% selectivity of phenol was obtained on P25-supported gold nanoparticles under 230 kPa of CO(2). PMID:21952312

Science.gov (United States)

We report on the single-particle properties of lanthanide-ion doped oxide nanoparticles. We have demonstrated that their size can be accurately determined from their luminosity. The optically determined size distribution is in very good agreement with the distribution obtained from transmission electron microscopy (TEM). We also showed that the photobleaching of these nanoparticles is related to a reduction process and that we can use it to sense in a concentration-dependent manner the presence of an oxidant like H2O2. Finally, we propose a way to perform nanoparticle-protein coupling and to determine the protein-nanoparticle ratio at the single-particle level.

UK PubMed Central (United Kingdom)

The purpose of this study was to synthesize biocompatible polyvinylpyrrolidone (PVP)-coated iron oxide (PVP-IO) nanoparticles and to evaluate their efficacy as a magnetic resonance imaging (MRI)...Full Text Available

British Library Electronic Table of Contents (United Kingdom)

Fluoroalkyl end-capped vinyltrimethoxysilane oligomer suffered the sol-gel reaction under alkaline conditions in the presence of titanium oxide nanoparticles in tetrahydrofuran to afford the corresponding fluorinated oligomer/titanium oxide nanocomposites[RF-(VM-SiO2)n-RF/TiO2] in excellent to moderate isolated yields. These fluorinated composites thus obtained were nanometer size-controlled fine particles, and exhibited good dispersibility and stability in traditional organic solvents except for water. These fluorinated nanocomposites were applied to the surface modification of glass to exhibit not only a completely superhydrophobic characteristic (a water contact angle: 180degree) with a non-wetting property against water droplets but also a good oleophobicity imparted by fluoroalkyl seg...

Science.gov (United States)

Nanosized particles are important because of their unique properties, different from the bulk, which leads to their enhanced catalytic, photocatalytic and electronic properties. This work has dealt with three different nanoparticle systems in the context of three different aspects of nanoparticle properties: (a) photocatalytis (TiO2/metal) system, (b) luminescence (CdSe) (c) alloying (Pt-Ag and Pd-Ag). The initial photocatalytic enhancement obtained by adding noble metal on semiconductor nanoparticles, degrades as fast as in 15 minutes and questions their long-term performance. XANES measurements on such irradiated systems like TiO2/Au, TiO2/Pt, TiO2/Ir indicates a positive oxidation state of these noble metals which renders them as recombination centers for photo-excited electrons and explains the decreased photocurrent. The oxidation is caused by holes. The EXAFS results also ...

British Library Electronic Table of Contents (United Kingdom)

Nanoparticle metal oxides offer a wide variety of potential applications in medicine due to the unprecedented advances in nanobiotechnology research. In this work, the effect of zinc oxide (ZnO) nanoparticles prepared by mechano-chemical method on the antibacterial activity of different antibiotics was evaluated using disk diffusion method against Staphylococcus aureus and Escherichia coli. The average size of ZnO nanoparticles was between 20 nm and 45 nm. Although ZnO nanoparticles (500 mg/disk) decreased the antibacterial activity of amoxicillin, penicillin G, and nitrofurantoin in S. aureus, the antibacterial activity of ciprofloxacin increased in the presence of ZnO nanoparticles in both test strains. A total of 27% and 22% increase in inhibition zone areas was observed for ciprofloxac...

UK PubMed Central (United Kingdom)

To capitalize on the response of tumor cells to ionizing radiation, we developed a controlled-release nanoparticle drug delivery system using a targeting peptide that recognizes a radiation-induced...Full Text Available

UK PubMed Central (United Kingdom)

The aim of this study is to determine the effects of silver nanoparticles (Ag-NP) on vascular endothelial growth factor (VEGF)-and interleukin-1 beta (IL-1β)-induced vascular permeability, and...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

We describe the synthesis and characterization of superparamagnetic iron oxide nanoparticle based heavy metal sorbents with various surface chemistries that demonstrate an excellent affinity for the separation of heavy metals in contaminated water systems (i.e. spiked Columbia river water). The magnetic nanoparticle sorbents are prepared from an easy to synthesize iron oxide precursor, followed by a simple, one-step ligand exchange technique to introduce the organic surface functionality of interest chosen to target either specific or broader classes of heavy metals. Functionalized superparamagnetic nanoparticles are excellent sorbent materials for the extraction of heavy metal contaminants from environmental and clinical samples since they are easily removed from the media once bound to the contaminant by simply applying a magnetic field. These engineered magnetic ...

British Library Electronic Table of Contents (United Kingdom)

Size-controllable Ag nanoparticle ultrathin films, which were fabricated by vacuum deposition method from high purity Ag wire onto cleaned indium tin oxide conducting glass, have different color fabricated by variation of preparation conditions. The UV/Vis spectra showed that optical absorption peak of these Ag nanoparticle films can be tuned in a range from 457nm to >650nm. Scanning electron microscopy images showed that with increasing film thickness Ag particle size was larger. Ag/WO3 composite films were prepared by cathodic electrodeposition of WO3 onto the surface of Ag nanoparticle films. Spectroelectrochemistry and electrochromic properties of the resulting composite films were characterized. It was found that the electrochemical and electrochromatic properties of the composite fil...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Using {gamma}-irradiation-induced reduction in the field of a {sup 60}Co {gamma}-ray source, colloidal silver and gold nanoparticles were prepared from their corresponding metal salts in aqueous solution and compared with those by chemical reduction. The radiation-based method provided silver nanoparticles with higher concentration and narrower size distribution than those obtained by chemical reduction method while there was no significant difference between the two strategies for the preparation of gold nanoparticles. {gamma}-Irradiation of 1.0 x 10{sup -3} M AgNO{sub 3} solution resulted in nearly 100 times more highly concentrated silver colloids than those by citrate reduction. Furthermore, the radiation method could lead to more highly concentrated silver colloids by simply increasing the concentration of AgNO{sub 3} solution up to 2.0 x 10{sup -2} M. The two metal ...

Energy Technology Data Exchange (ETDEWEB)

The rapid growth in the use of in vitro methods for nanoparticle toxicity assessment has proceeded with limited consideration of the unique kinetics of these materials in solution. Particles in general and nanoparticles specifically, diffuse, settle and agglomerate in cell culture media as a function of several systemic and particle factors: media density and viscosity, particle size, shape and density. Cellular dose then is also a function of these factors as they determine the rate of transport of nanoparticles to cells in culture. Here we develop and apply the principles of particokinetics and dosimetry in vitro and outline an approach for simulation of nanoparticle particokinetics in cell culture systems. We illustrate that where equal mass concentrations (?g/ml) imply equal doses for dissimilar materials, the corresponding particle number or surface area concentration doses differ by orders of ...

British Library Electronic Table of Contents (United Kingdom)

In this paper, multilayer oxide nanorods were deposited in the nanopores of anodic aluminum oxide (AAO) via solution infiltration followed by heat treatment. The nanorods have a core-shell structure. First, the shell (nanotube) with the thickness of about 40nm was made of TiO"2 through the hydrolysis of (NH"4)"2TiF"6. Second, silver nanoparticles with the diameter of about 3nm were added into the TiO"2 layer through thermal decomposition of AgNO"3 at elevated temperatures. Then, cylindrical cores (nanorods) of CoO and ZnO with 200nm diameter were prepared, respectively. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the structure and composition of the nanorods. UV-vis light absorption measurements in the wavelength range from 350 to...

British Library Electronic Table of Contents (United Kingdom)

Iron nanoparticles were produced using extracts of green tea leaves (GT-Fe NPs). The materials were characterized using TEM, SEM/EDX, XPS, XRD, and FTIR techniques and were shown to contain mainly iron oxide and iron oxohydroxide. The obtained nanoparticles were then utilized as a Fenton-like catalyst for decolorization of aqueous solutions containing methylene blue (MB) and methyl orange (MO) dyes. The related experiments investigated the removal kinetics and the effect of concentration for both MB and MO. The concentrations of dyes in aqueous solution were monitored using ultraviolet-visible (UV-vis) spectroscopy. The results indicated fast removal of the dyes with the kinetic data of MB following a second order removal rate, while those of MO were closer to a first order removal rate. T...

Energy Technology Data Exchange (ETDEWEB)

This paper presents a study on the crystallization and growth mechanism of selenium nanowires induced by silver nanoparticles at ambient conditions with special reference to the effects of factors such as the shapes and size of silver nanoparticles, the induced reaction time, and the molar ratio of Ag{sup 0} to SeO{sub 3}{sup 2-} ions. The synthesis approach is conducted with no need of any stabilizers, and with no sonochemical process and/or templates. It is found that whether silver spherical particles or colloids can lead to the formation of nanowires with average diameter of 25 nm and lengths up to a few micrometers, and silver nanoplates lead to the formation of flat Se nanostructures. In particular, Au, Cu, Pt, and Pd particles cannot induce the growth of selenium nanowires in aqueous solution at room temperature. The results indicate that silver particles play a critical role ...

Energy Technology Data Exchange (ETDEWEB)

In an aim to develop photo-responsive composites, the UV photo-reduction of aqueous titanium oxide nanoparticle-graphene oxide (TiO{sub 2}-GO) dispersions (Lambert et al. J Phys. Chem. 2010 113 (46), 19812-19823) was undertaken. Photo-reduction led to the formation of a black precipitate as well as a soluble portion, comprised of titanium oxide nanoparticle-reduced graphene oxide (TiO{sub 2}-RGO). When allowed to slowly evaporate, self assembled titanium oxide nanoparticle-graphene oxide (SA-TiO{sub 2}-RGO) films formed at the air-liquid interface of the solution. The thickness of SARGO-TiO{sub 2} films range from {approx}30-100 nm when deposited on substrates, and appear to be comprised of a mosaic assembly of graphene nanosheets and TiO{sub 2}, as observed by scanning electron microscopy. Raman ...

UK PubMed Central (United Kingdom)

Systemic administration of lipopolysaccharide (LPS), which causes endotoxemia and systemic inflammation, has been reported to induce expression of the gene for type II inducible nitric oxide synthase...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The oxide colloidal route, developed in the laboratory for mono-metallic catalysts, consists in preparing a metallic oxide hydro-sol which leads to the supported catalyst after deposition onto a support and an activation stage. In this work, this method has been adapted to the preparation of alumina supported bimetallic Pd-Sn catalysts to determine its interest for the control of the properties of the bimetallic phase (size, composition and structure). In the preliminary study concerning tin oxide sols, SnO{sub 2} (size=2,3 nm) and Sn{sub 6}O{sub 4}(OH){sub 4} (size = 25 nm) nano-particles were synthesized by neutralization respectively for tin(IV) and tin(H). The control through the pH of the aggregation of the PdO and SnO{sub 2} particles revealed that increasing oxide solubility promotes integral re-dispersion of the oxide particles. To synthesize ...

International Nuclear Information System (INIS)

... compilation fission products j codes mixed oxide fuels neutron reactions

British Library Electronic Table of Contents (United Kingdom)

The evaluation of the bactericidal effect of different silver-containing materials where silver is available as Ag^+ (silver nitrate and different silver-exchanged zeolites), as metallic Ag^0 (commercial silver nanoparticles) or as oxide (silver (I) oxide) was carried out in order to elucidate the importance of the bioavailability of silver (i.e., as free ions, metallic particles, combination of them, clusters, complexes, partially soluble or insoluble salts, etc.) on its bactericidal action. For the different materials tested, their bactericidal effect is ordered in the following sequence: AgNO"3>Ag-ZSM-5>Ag"2O>commercial silver-exchanged zeolite (granular)>commercial silver-exchanged zeolite (pellets)>Ag nanoparticles. In general, as the content of bioavailable ionic silver increases, th...

British Library Electronic Table of Contents (United Kingdom)

Abstract A diacrylate polysulfone oligomer is synthesized and used as the acrylic oligomer for the in situ synthesis of noble metal/PSU nanocomposites through UV-induced simultaneous radical polymerization of acrylic functionalities and NP formation by reduction of their precursors. Thus, silver or gold NPs are formed in situ during polymer network formation. FESEM analysis of the morphology of the cured systems demonstrates that the nanoparticles of the noble metals are homogeneously distributed in the network without macroscopic agglomeration.

Science.gov (United States)

The optical and nonlinear optical properties of colloidal solutions of silver obtained by laser ablation in water and ethanol are studied. It is shown that freshly prepared colloids experience a full or partial sedimentation by changing their nonlinear optical properties. Aqueous colloids undergo a partial sedimentation and their nonlinear optical absorption changes to nonlinear optical transmission. The obtained results are interpreted using the Drude model for metal particles taking the particle size into account and can be explained by the sedimentation of larger silver particles accompanied by the formation of a stable colloid containing silver nanoparticles with a tentatively silver oxide shell. The characteristic size of particles forming such a stable colloid is determined and its optical nonlinearity is estimated.

British Library Electronic Table of Contents (United Kingdom)

Polymer-coated magnetic nanoparticles (MNPs) have been prepared and used as an immobilization matrix for the fabrication of solid-state tris(2,2prime-bipyridyl)ruthenium(II) (Ru(bpy)32+) electrogenerated chemiluminescence (ECL) sensor. The pre-synthesized maghemite (g-Fe2O3) MNPs were coated with poly(3-thiopheneacetic acid) based on an oxidative polymerization method using KMnO4. The poly(3-thiopheneacetic acid)-coated MNPs have formed the clusters with average diameter of 200-500nm. The multilayer films of poly(3-thiopheneacetic acid)-coated MNPs were uniformly formed on the surface of a Pt electrode by an external magnet. The Ru(bpy)32+ was rapidly incorporated into the multilayer films within 5min through the electrostatic interaction between the Ru(bpy)32+ and the negatively charged c...

International Nuclear Information System (INIS)

The concept of nanocrystal conversion chemistry, which involves the use of pre-formed nanoparticles as templates for chemical transformation into derivative solids, has emerged as a powerful approach for designing the synthesis of complex nanocrystalline solids. The general strategy exploits established synthetic capabilities in simple nanocrystal systems and uses these nanocrystals as templates that help to define the composition, crystal structure, and morphology of product nanocrystals. This article highlights key examples of 'conversion chemistry' approaches to the synthesis of nanocrystalline solids using a variety of techniques, including galvanic replacement, diffusion, oxidation, and ion exchange. The discussion is organized according to classes of solids, highlighting the diverse target systems that are accessible using similar chemical concepts: metals, oxides, chalcogenides, phosphides, alloys, intermetallic ...

UK PubMed Central (United Kingdom)

4-Hydroxynonenal (HNE), a major electrophilic product of lipid peroxidation, is regarded as both a marker of oxidative stress and a mediator of oxidative damage. At subtoxic concentrations,...Full Text Available

UK PubMed Central (United Kingdom)

BackgroundClara cell protein (CC16), the main secretory product of bronchiolar Clara cells, plays an important protective role in the respiratory tract against oxidative stress and...Full Text Available

British Library Electronic Table of Contents (United Kingdom)

Gold-coated iron nanoparticles (NPs) selectively and significantly (P <0.0001) inhibit proliferation of oral- and colorectal-cancer cells in vitro at doses as low as 5 mg/mL, but have little adverse effect on normal healthy control cells. The particle treatment caused delay in cell-cycle progression, especially in the S-phase. There was no significant difference in the NP uptake between cancer and control cells, and cytotoxicity resulted primarily from the iron core, before oxidation, rather than from the Fe ions released from the core. In contrast with magnetic NPs that usually serve as drug carriers, diagnostic probes or hyperthermia media, the iron, before oxidation, in the NPs selectively suppressed cancer cell growth and left healthy control cells unaffected in vitro and in vivo. This...

UK PubMed Central (United Kingdom)

Calorie restriction (CR) induces a metabolic shift towards mitochondrial respiration; however, molecular mechanisms underlying CR remain unclear. Recent studies suggest that CR-induced mitochondrial...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Stearic acid gel is employed to study the phase evolution of MgTiO{sub 3} nanoparticles by thermal gravimetric analysis, X-ray diffraction, and Fourier transform infrared. During the preparation of stearic acid gel, tetrabutyl titanate easily absorbed moisture to hydrolyze into Ti(OH){sub 4} firstly, and then reacts with stearic acid and magnesium stearate to form magnesium-titanium oxide network polymer gel, meanwhile n-butanol is generated. When stearic acid gel is calcined in air, a series of oxidation and combustion reactions occur, meanwhile apparent heat is given off. The results show that a metastable intermediate phase Mg{sub 2}TiO{sub 4} is generated at 450 {sup o}C and nearly disappeared at 550 {sup o}C. Simultaneously, a new solid phase of MgTiO{sub 3} appears. The metastable intermediate phase Mg{sub 2}TiO{sub 4} is successfully identified in the current work.

Science.gov (United States)

Not Available

J-STORE (Japan)

Full Text Available

British Library Electronic Table of Contents (United Kingdom)

The objective of materials research is the development of economical, safe and efficient synthesis routes that lead to the formation of a photocatalyst which is able to overcome performance problems related to particle size, crystallinity, or low surface area. Here, we report high-quality functional nanoparticles of calcium bismuth mixed oxide with 15nm nominal size corresponding to a specific surface area of 41m^2/g which were produced by single-step flame spray synthesis (FSS). The high temperature of the flame afforded creation of oxygen vacancies which were quantified by near edge X-ray absorption fine structure (NEXAFS) spectra. These two parameters, developed active surface area and created in the flame oxygen vacancies, allowed to enhance the photocatalytic activity of calcium bismu...

Science.gov (United States)

Besides the multifunctionality, another equally important aspect of nanoparticles is their engineerability to control the geometrical and chemical properties during fabrication. In this work, we exploited this aspect to define asymmetric surface chemistry of an iron oxide nanosphere by controlling the topology of ligand expression on its surface resulting in a particle with two faces, one displaying only amines and the other only thiols. Specifically, amine-functionalized iron oxide nanospheres were attached on a solid support via a crosslinker containing a disulfide bridge. Liberation of the nanosphere using thiolytic cleavage created thiols on the portion of the particle's surface that interacted with the solid support. Employing a solid-phase strategy and a step-by-step addition of particles, the two unique faces on the same nanosphere served as fittings to assemble them into linear nano-chains. Assembly of chains with ...

Energy Technology Data Exchange (ETDEWEB)

The quantitative determination of oxide concentration by laser-induced breakdown spectroscopy is relevant in various fields of applications (e.g.: analysis of ores, concrete, slag). Calibration free laser-induced breakdown spectroscopy and the multivariate calibration are among the methods employed for quantitative concentration analysis of complex materials. We measured the intensity of neutral and ionized atomic emission lines of oxide materials by laser-induced breakdown spectroscopy and we modified the calibration free laser-induced breakdown spectroscopy method to increase the accuracy. The concentration of oxides was obtained by using stoichiometric relations. Sample materials were prepared from oxide powder (Fe{sub 2}O{sub 3}, MgO, CaO) by mixing and pressing. The concentration was 9.8-33.3 wt.% Fe{sub 2}O{sub 3}, ...

Energy Technology Data Exchange (ETDEWEB)

Nanoparticles represent versatile building blocks in material science and nanotechnology. Thereby, the defined assembly of nanostructures (13 and 56 nm in diameter, respectively) is of significant importance. Short DNA sequences can be bound to the nanoparticle surface thus enabling highly specific DNA hybridization-driven events that direct the formation of nanoparticle constructs.In this paper, examples for the defined formation of gold nanoparticle constructs are demonstrated. In addition, gold-silver core-shell nanoparticles are introduced as further building blocks for the hybridization-controlled formation of nanoparticle constructs.

Energy Technology Data Exchange (ETDEWEB)

Ultraviolet (UV) photoirradiation of Ag(I) compounds in the presence of an aqueous Triton X-100 solution has been exploited for the first time to prepare reproducible yellow silver hydrosol. The evolution of nanosized silver particles has been examined critically under the influence of different anions/ligands. Hence, time dependent evolution of silver hydrosol from different silver compounds in micelle via photochemical reduction is observed. Anions/ligands of precursor salts have been found to show profound influence (due to electron scavenging property, solubility, stability etc.) on the evolution route and efficiency of photochemical reduction of Ag(I) to Ag(O) in micelle and thereby classification of silver compounds becomes possible. Kinetic results reveal that the formation of silver particles proceeds via autocatalytic growth mechanism. The observed variation in rate constant values for the evolution of nanoparticles from different silver compounds have ...

International Nuclear Information System (INIS)

In laser ablation inductively coupled plasma mass spectrometry (LA-ICPMS), the properties of laser-generated aerosols, such as size and composition, are crucial for matrix-independent quantification. In this study, the aerosol particle morphology and elemental composition generated by two state-of-the-art laser systems (ArF excimer nanosecond-UV laser and Ti:sapphire femtosecond-IR laser) were investigated by electron microscopic techniques. Electrostatic sampling of the aerosols directly onto transmission electron microscopy (TEM) grids allowed us to study the morphology and elemental composition of the aerosols using TEM and TEM-EDX (energy dispersive X-ray spectroscopy) analyses, respectively. The results of the electron microscopic studies were finally compared to the LA-ICPMS signals of the main matrix components. The investigations were carried out for non-conducting materials (glass and zircon), metallic samples (steel and brass) and semiconductors (sulfides). The studies ...

Energy Technology Data Exchange (ETDEWEB)

In vitro cytocompatibility and cellular interactions of lauric acid and dextran-coated magnetite nanoparticles were evaluated with two different cell lines (mouse fibroblast and human cervical carcinoma). Lauric acid-coated magnetite nanoparticles were less cytocompatible than dextran-coated magnetite nanoparticles and cellular uptake of lauric acid-coated magnetic nanoparticles was more than that of dextran-coated magnetite nanoparticles. Lesser cytocompatibility and higher uptake of lauric acid-coated magnetite nanoparticles as compared to dextran-coated magnetic nanoparticles may be due to different cellular interactions by coating material. Thus, coating plays an important role in modulation of biocompatibility and cellular interaction of magnetic nanoparticles.

Environmental Research Database

ObjectivesThe development of novel formulations of nanoparticles in the nanotechnology industry and their increasing importance and use in industry means there is certainty of human environmental exposures in both the workplace and the general environment. The pulmonary route of exposure to airborne nanoparticles is a major one, as nanoparticles are handled in industry, escape from workplaces and products containing nanoparticles undergo attrition in the environment. There is a substantial problem for ris [continued...]DescriptionNanoparticles are extremely small particles, each individual particlel being less than one ten millionth of a metre in size. We are exposed to nanoparticles in busy streets as they are present in traffic exhaust produced from combustion of fuel and such nanoparticles are considered to be important in causing the ...

UK PubMed Central (United Kingdom)

Thioredoxin, a small, ubiquitous protein which participates in redox reactions through the reversible oxidation of its active center dithiol to a disulfide, is an essential protein in Bacillus...Full Text Available

UK PubMed Central (United Kingdom)

Cancer cells constantly adapt to oxidative phosphorylation (OXPHOS) suppression resulting from hypoxia or mitochondria defects. Under the OXPHOS suppression, AMP-activated protein kinase (AMPK) regulates...Full Text Available

UK PubMed Central (United Kingdom)

As the result of genetic alterations and tumor hypoxia, many cancer cells avidly take up glucose and generate lactate through lactate dehydrogenase A (LDHA), which is encoded by a target gene of c-Myc...Full Text Available

UK PubMed Central (United Kingdom)

Alveolar enlargement, which is characteristic of bronchopulmonary dysplasia, congenital matrix disorders, and cigarette smoke-induced emphysema, is thought to result from enhanced inflammation and ensuing...Full Text Available

British Library Electronic Table of Contents (United Kingdom)

Chemical modification of poly(?-caprolactone) PCL by oxidation with potassium permanganate in solution was investigated. According to the data obtained from Fourier transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance 1H NMR, after the oxidation reactions the PCL chains exhibited new functional groups (vinyl and hydroxyl) and possible intermolecular recombination, producing an oxidized-polycaprolactone (PCL-OX). Solution viscometry indicated that degradation also occurred during the oxidation reactions (30% drop in viscosity average molecular weight was detected). Differential scanning calorimetry (DSC) also indicated that PCL was chemically modified and degraded. The successive self-nucleation/annealing (SSA) treatment confirmed that a reduction (or interruption) in line...

International Nuclear Information System (INIS)

Boron is implanted in crystalline silicon through oxide layers with different thicknesses. The implantation is carried out at various doses and energies of interest in ultra large scale integration (ULSI) application. Rapid thermal annealings (RTA) are used to obtain shallow junctions and electrical activation of the B atoms. However, transient enhanced diffusion induced by implantation damage can be observed. The boron concentration profiles before and after annealing are obtained with secondary ion mass spectrometry (SIMS). It is found that the diffusion transient in the tail region of the boron profile increases with decreasing oxide thickness. Even more, if the implantation damage concerns mostly the oxide, i.e. when the concentration peak is located in this oxide, the oxygen knocked into the silicon substrate could play this way an important role in restricting the boron ...

UK PubMed Central (United Kingdom)

Acetaminophen (APAP) overdose, which causes liver injury in animals and humans, activates c-jun N-terminal kinase (JNK). Although it was shown that the JNK inhibitor SP600125 effectively reduced...Full Text Available

International Nuclear Information System (INIS)

For the advanced fusion reactor FFHR2 (Force Free Helical Reactor) that has been proposed by NIFS, molten salt Flibe (LiF:BeF2=64:36) breeder blanket system is selected because of Flibe's features such as chemical stability, low-pressure operation and low electric conductivity. The Flibe is however high Prandtl number fluid since it has high viscosity and low thermal conductivity. Therefore its heat transfer performance is low compared with liquid Li or Pb-Li. In addition to heat removal of 1MW/m2 on the first wall, electrolysis of molten salt due to MHD effect will take place under high flow rate condition. This indicates that heat transfer enhancement under low flow rate is essential for the Flibe blanket system. In our laboratory, heat transfer characteristics of molten salt HTS (KNO3:NaNO2:NaNO3=53:40:7), have been evaluated, which is used as a simulant fluid of Flibe from the points of view of Be's toxicity and similar Prandtl number. In this paper, we adopt ...

Environmental Research Database

Objectives1. We will use reduction of lysosomal stability as an indicator of cell injury induced by C-60 fullerenes and carbon nanotubes in the liver analogue or digestive gland (hepatopancreas) of marine mussels. Molluscan hepatopancreatic digestive cells are key to normal function and are a sensitive key interface with the environment. Reduction of lysosomal stability is mechanistically linked with impaired health of the whole animal. 2. We will also test the hepatopancreatic digestive cells for evide [continued...]DescriptionNanotechnology is a major innovative scientific and economic growth area, which may present a variety of hazards for environmental and human health. The surface properties and very small size of nanoparticles and nanotubes provides surfaces that may bind and transport toxic chemical pollutants, as well as possibly being toxic in their own right by generating reactive oxygen species (ROS). There is a wealth of evidence ...

British Library Electronic Table of Contents (United Kingdom)

We report a solution-phase synthetic route to copper nanoparticles with controllable size and shape. The synthesis of the nanoparticles is achieved by the reduction of copper(II) salt in aqueous solution with hydrazine under air atmosphere in the presence of poly(acrylic acid) (PAA) as capping agent. The results suggest that the pH plays a key role for the formation of pure copper nanoparticles, whereas the concentration of PAA is important for controlling the size and geometric shape of the nanoparticles. The average size of the copper nanoparticles can be varied from 30 to 80 nm, depending on the concentration of PAA. With a moderate amount of PAA, faceted crystalline copper nanoparticles are obtained. The as-synthesized copper nanoparticles appear red in color and are stable for weeks, ...

Energy Technology Data Exchange (ETDEWEB)

Alloy 800 has been proposed for use in the receiver tube panel arrays of advanced solar central receiver (SCR) designs. In this application the alloy will be exposed to a molten mixture of sodium and potassium nitrate salts at temperatures ranging up to approximately 600/sup 0/C While these salts are routinely used in a variety of applications including metal heat treating and process heat transfer, common industrial experience has been limited to maximum temperatures of 400/sup 0/C - 450/sup 0/C. There is, therefore, considerable interest in the compatibility of these salts with containment alloys at the higher temperatures associated with SCR designs. Additionally, the containment alloy may be subject to thermally induced fatigue damage resulting from intermittent cloud cover and diurnal cycling. Previous work has found that slower near-threshold fatigue crack growth rates (FCGR) in Alloy 800 result when it is tested in molten nitrate salt at 600/sup 0/C ...

British Library Electronic Table of Contents (United Kingdom)

A magnetic core/shell Fe3O4/FeMnOx catalyst was prepared by a simple oxidation-precipitation method. The catalyst was characterized by X-ray diffraction, transmission electron microscope, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis and cyclic voltammetry. The characterization studies verified that Fe3O4 core was coated with a layer of Fe-Mn oxide. The Fe3O4/FeMnOx was found to be an effective and stable heterogeneous catalyst for the discoloration of methylene blue (MB) in aqueous solution by H2O2. The high catalytic activity is due to the FeMnOx shell, which not only increased the surface hydroxyl groups, but also enhanced the interfacial electron transfer. The discoloration of MB could be due to the decomposition of H2O2 into ?OH ...

British Library Electronic Table of Contents (United Kingdom)

The results of following the oxidative degradation of a plastic-bonded explosive (PBX 9501) are reported. Into over 1100 sealed containers were placed samples of PBX 9501 and combinations of its components and aged at relatively low temperatures to induce oxidative degradation of the samples. One of the components of the explosive is a poly(ester urethane) polymer and the oxidative degradation of the samples were following by measuring the molecular weight change of the polymer by gel permeation chromatography (coupled with both differential refractive index and multiangle laser light scattering detectors). Multiple temperatures between 40 and 64 degreeC were used to accelerate the aging of the samples. Interesting induction period behavior, along with both molecular weight increasing (cro...

J-STORE (Japan)

Full Text Available

DEFF Research Database (Denmark)

Udgivelsesdato: 2008/5

Energy Technology Data Exchange (ETDEWEB)

Monodisperse noble metal nanoparticles are of tremendous interest for numerous applications, such as surface-enhanced Raman spectroscopy, catalysis or biosensing. However, preparation of monodisperse metal nanoparticles is still a challenging task, because typical preparation methods yield nanoparticle ensembles with broad shape and/or size distributions. To overcome this drawback, tailoring of metal nanoparticles with laser light has been developed, which is based on the pronounced shape- and size-dependent optical properties of metal nanoparticles. I will demonstrate that nanoparticle tailoring with ns-pulsed laser light is a suitable method to prepare nanoparticle ensembles with a narrow shape and/or size distribution. While irradiation with ns-pulsed laser light during nanoparticle growth permits a precise shape ...

Energy Technology Data Exchange (ETDEWEB)

W have introduced template-synthesized metal phosphate nanoparticle labels for electrochemical immunoassay. Such use of an apoferritin template offers a simple and convenient route to prepare metallic nanoparticle labels for electrochemical immunoassays and avoid the complicated and time-consuming nanoparticle synthesis process (QD synthesis). Releasing metal ions from metal phosphate in an acetate buffer (pH 4.6) eliminates the harsh condition in the traditional metallic nanoparticle dissolution (e.g., strong acid dissolution of QDs and gold nanoparticles). This method is ultrasensitive and its DL is low to 77fM. The simultaneous detection of multiple protein targets is easily performed by using different metal phosphate nanoparticle labels (cadmium phosphate and lead phosphate). This approach can be extended to prepare multiple metal (such as zinc, lead, ...

Science.gov (United States)

Spectral and energy luminescence characteristics of R6G dye solutions in ethanol with addition of Ag nanoparticle suspensions in different aggregate states are experimentally investigated. It is demonstrated that incorporation of non-aggregated and aggregated nanoparticles causes the superluminescence thresholds in R6G solutions to decrease. It is established that the optical properties of the laser beam propagation channel are transformed when low-power (20 mW) cw laser radiation passes through the suspension of nanoparticles. This is manifested through the occurrence of a region with enhanced nanoparticle density in the laser beam center, on which diffraction of laser radiation is observed.

International Nuclear Information System (INIS)

Iron oxide films have been deposited on Si(100) substrates by chemical vapour deposition (CVD) of iron(III) tert-butoxide ([Fe(O "tBu)_3]_2) in the temperature range 350-450 deg. C. The precursor flux and substrate temperature were varied to control the phase composition, average grain size and film thickness. The nature of substrate and deposition temperature markedly influence the morphology and iron-oxygen stoichiometry in the CVD deposits. Phase transformations in iron oxide films were achieved through precise local and periodic heating of the films by interfering laser beams. The interaction of iron oxide films with short laser pulses (Nd:YAG, 355 nm) induced partial transformation of hematite (#alpha#-Fe_2O_3) to magnetite (Fe_3O_4) or magnetite to wuestite (Fe_1_-_xO), respectively. The phase characterization and morphology of the hematite and magnetite films were investigated before and after ...

British Library Electronic Table of Contents (United Kingdom)

Abstract The treatment of advanced colorectal cancer with 5-fluorouracil has two major problems: development of tumor resistance and toxicity toward normal tissues. The aim of this study was to investigate the possible advantages of combining 5-fluorouracil (5-FU) with resveratrol (trans-3, 4prime, 5-trihydroxystilbene) for treating HT-29 and SW-620 colorectal carcinoma cell lines. Since combined treatment using 5-FU with resveratrol resulted in a significant decrease in long-term cell survival, we investigated the possible basis of this synergistic interaction at a molecular level, focusing on oxidative stress as a possible mediator of cell death. Resveratrol established interactions with the mitochondria of cancer cells and induced an imbalance in cellular antioxidant activities, leading...

Science.gov (United States)

BackgroundIn recent years, near-infrared fluorescence (NIRF)-labeled iron nanoparticles have been synthesized and applied in a number of applications, including the labeling of human cells for monitoring the engraftment process, imaging tumors, sensoring the in vivo molecular environment surrounding nanoparticles and tracing their in vivo biodistribution. These studies demonstrate that NIRF-labeled iron nanoparticles provide an efficient probe for cell labeling. Furthermore, the in vivo imaging studies show excellent performance of the NIR fluorophores. However, there is a limited selection of NIRF-labeled iron nanoparticles with an optimal wavelength for imaging around 800 nm, where tissue autofluorescence is minimal. Therefore, it is necessary to develop additional alternative NIRF-labeled iron nanoparticles for application in this area.ResultsThis study manufactured 12-nm ...

British Library Electronic Table of Contents (United Kingdom)

Novel fluoroalkyl end-capped vinyltrimethoxysilane oligomeric nanoparticles were prepared by the hydrolysis of the corresponding oligomer under alkaline conditions. The size of fluorinated nanoparticles thus obtained is of submicrometer levels and is not sensitive to the refractive indices of a variety of solvents; however, the turbidity of the dispersed fluorinated nanoparticles is extremely sensitive to the refractive indices of these solvents. In particular, the solvents of which the refractive indices are from 1.378 to 1.408 were found to afford the transparent colorless dispersed particle solutions. More interestingly, the modified glass surface treated with fluorinated nanoparticles exhibited a completely superhydrophobic characteristic (a water contact angle: 180?) with a nonwetting...

British Library Electronic Table of Contents (United Kingdom)

By choosing appropriate microemulsion systems, hexagonal cobalt (Co) and cobalt-nickel (1:1) alloy nanoparticles have been obtained with cetyltrimethylammonium bromide as a cationic surfactant at 500degreeC. This method thus stabilizes the hcp cobalt even at sizes (<10nm) at which normally fcc cobalt is predicted to be stable. On annealing the hcp cobalt nanoparticles in H2 at 700degreeC we could transform them to fcc cobalt nanoparticles. Microscopy studies show the formation of spherical nanoparticles of hexagonal and cubic forms of cobalt and Co-Ni (1:1) alloy nanoparticles with the average size of 4, 8 and 20nm, respectively. Electrochemical studies show that the catalytic property towards oxygen evolution is dependent on the applied voltage. At low voltage (less than 0.65V) the Co (he...

Energy Technology Data Exchange (ETDEWEB)

The article deals with a novel electrochemical method of preparing long-lived silver nanoparticles suspended in aqueous solution as well as silver powders. The method does not involve the use of any chemical stabilising agents. The morphology of the silver nanoparticles obtained was studied using transmission electron microscopy, scanning electron microscopy, atomic force microscopy and dynamic light scattering measurements. Silver nanoparticles suspended in water solution that were produced by the present technique are nearly spherical and their size distribution lies in the range of 2 to 20 nm, the average size being about 7 nm. Silver nanoparticles synthesised by the proposed method were sufficiently stable for more than 7 years even under ambient conditions. Silver crystal growth on the surface of the cathode in the electrochemical process used was shown to result in micron-sized structures ...

Energy Technology Data Exchange (ETDEWEB)

A numerical model was developed to simulate the combined effects of heat transfer, magnetite oxidation, and NO{sub x} formation in a grate-kiln furnace for taconite pellet induration. Heat transfer from the flame in the kiln was described by the net radiation method. The shrinking core model was used to account for magnetite oxidation on the grate. A novel approach to oxidation of tumbling pellets in a kiln was derived. The Zeldovich mechanism was used to predict thermal NO generation. Temperature fluctuations in the gas streams were estimated with a clipped Gaussian probability density function. The thermal energy balances and mass balances resulted in coupled systems of first-order differential equations, which were solved numerically. The model is capable of predicting NO production and magnetite oxidation in agreement with observation of plant performance. Although the design of the grate-kiln ...

Energy Technology Data Exchange (ETDEWEB)

Porous SnO{sub 2} nanotubes were prepared via electrospinning followed by calcination in air. As anode materials for lithium ion batteries, the porous nanotubes delivered a high discharge capacity of 807 mAh g{sup -1} after 50 cycles. Even after cycled at high rates, the electrode still retained a high fraction of its theoretical capacity. Such excellent performances of porous SnO{sub 2} nanotubes could be attributed to the porous and hollow structure which facilitated liquid electrolyte diffusion into the bulk materials and buffered large volume changes during lithium ions insertion/extraction. Furthermore, the nanoparticles of nanotubes provided the shorter diffusion length for lithium ions insertion which benefited in retaining the structural stability and good rate performance. Our results demonstrated that this simple method could be extended for the synthesis of porous metal oxide nanotubes with high performances in the applications of ...

Energy Technology Data Exchange (ETDEWEB)

Our institute has been investigating laser-produced tin, lithium and xenon plasma for extreme ultraviolet (EUV) light source of EUV lithography system, and found the highest conversion efficiency of 3% at 13.5 nm in 2% bandwidth. In the present paper, we introduce fabrication methods of density-controlled tin targets to generate relatively monochromatic EUV, and higher conversion efficiency than bulk tin. The first method is the nano-template method, where liquid tin solution was immersed into a polymer film with monodispersed size nano-particle. The density can be controlled by tin concentration of the solution. The target can be classified into mass-limited target. We have shown a tendency of monochromatic EUV emission around 13.5 nm with decreasing of tin density. The intensity was higher than tin foil with bulk density. The tendency has a merit to mitigate heat effect of the first EUV mirror. The fabrication method has another merit to control not only density ...

UK PubMed Central (United Kingdom)

Bovine microvascular endothelial cells (MEC) were able to degrade the H2O2 generated by phorbol myristate acetate-activated bovine neutrophils or by glucose oxidase with a maximal capacity of 4.0 +/-...Full Text Available

International Nuclear Information System (INIS)

The influence of RTA (Rapid Thermal Anneal) treatment on MOS radiation hardness is demonstrated and compared with classical furnace treatment. In the case of the RTA, the oxide trapped charge is found to depend on: (i) the anneal temperature as expected, data are in good agreement with a recently developed model of oxygen out-diffusion; (ii) the location across the wafer with a radial dependence, results could be related to stress induced by thermal gradient.

UK PubMed Central (United Kingdom)

Neutrophils from people with poorly controlled diabetes present a primed phenotype and secrete excessive superoxide. Phospholipase A₂ (PLA₂)-derived arachidonic acid (AA)...Full Text Available

UK PubMed Central (United Kingdom)

We compared the effects of treatment with methylprednisolone or the 21-aminosteroids, U-74389 and U-74006F (Tirilizad mesylate), on hyperoxic lung injury and the associated expression of mRNA for several...Full Text Available

Science.gov (United States)

Hybridization and thermal evolution of the Ni+C{sub 60} composites, deposited on Si(001) at room temperature, were studied using Scanning Electron Microscopy, {mu}-Raman spectroscopy and Rutherford Backscattering. As-deposited, the hybrid films exhibited a granular nano-structure with Ni nano-particles encapsulated in C{sub 60} polymerized rinds. The Ni and C (C{sub 60}) distributions in a top layer were found homogeneous with a stable Ni/C (C{sub 60}) ratio; in the larger depth the distributions were inhomogeneous and their ratio dramatically varied. At elevated temperatures, all structural parameters were changed. In the subsurface layer Ni- and C (C{sub 60})-rich zones were formed (due to the induced phase separation), C{sub 60}-molecules decayed and their fragments were transformed into amorphous carbon (a-C). The free volume distribution of the stressed hybrid matter was analyzed by the Hg marker that (in a form of vapors) in-diffused in ...

International Nuclear Information System (INIS)

Research highlights: The dental implant of titanium could be modified by anodic oxidation. It was found that incorporation of strontium ions into the matrix increase the bone formation. In this study, we try to investigate the effect of corrosion property and bioactivity on coatings containing strontium by anodic oxidation. The results suggest that coatings containing strontium on titanium by anodic oxidation has the potential to show the stability and bioactivity in the clinical use. - Abstract: Pure titanium (Ti) and titanium alloys are considered as bio-inert materials in clinical use. Bioactivity is the ability to induce bone-like apatite on the material surface. The micro-arc oxidation (MAO) technique is an effective method for improving the surface properties of titanium. The aim of this study was to investigate the bioactivity and corrosion behavior of MAO coatings containing ...

UK PubMed Central (United Kingdom)

This work describes the synthesis and characterization of novel thermoresponsive highly-branched polyamidoamine-polyethylene glycol-poly (D, L-lactide) (PAMAM-PEG-PDLLA) core-shell nanoparticles....Full Text Available

UK PubMed Central (United Kingdom)

BackgroundSilica nanoparticles (SiNPs) are being formulated for cellular imaging and for nonviral gene delivery in the central nervous system (CNS), but it is unclear what potential...Full Text Available

UK PubMed Central (United Kingdom)

The interior of 237 nm spherical vinylsilsesquioxane nanoparticles has been covalently modified and their surface functionalized under mild conditions to yield a novel type of hybrid silsesquioxane...Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The purpose of this study is fabrication and characterization of silver nanofluid by the submerged arc nanoparticle synthesis system (SANSS). The silver metal electrodes under the electrical discharge will melt and evaporate rapidly and condense to form the nanoparticles in the lower temperature dielectric liquid and produce the suspended nanoparticle. The results showed that the spherical nanosilver particle formed in the ethylene glycol and the mean particle size is about 12.5 nm. The prepared silver nanofluid was irradiated under the 410 nm visible light, electrons could be excited from the valence band to the conduction band. The silver nanofluid more closely resembles Newtonian fluids.

International Nuclear Information System (INIS)

Studies have linked cell phone radiation to health problems such as headaches, high blood pressure, cancer and more. There is a latency period for most diseases and it may take years and more studies before the required weight of evidence is established. But the effects are cumulative and precautions should be taken now before it is too late. The aim of the present study was to investigate if supplementation with antioxidants would protect heart and liver tissues from harmful radiation emitted by cell phone. Thirty two male albino rats were randomly divided into four equal groups: I- Control, II- Antioxidants treated group, III- 950 MHz EMR, IV- 950 MHz EMR + antioxidants. A 950 MHz EMR radiation (217-Hz pulse rate, 2-W maximum peak power, SAR Specific Absorption Rate"1.6 W/Kg) was applied to groups III and IV 60 min/day, for 30 days using an experimental exposure device. Antioxidants supplement (Vitamins A, E and C + Se) was administered to rats daily, by gavages, during the period of ...

Science.gov (United States)

The effects of the structure of a carboxylic acid on the processes of oxidation and reduction of iron ions in irradiated aqueous solutions were directly observed during irradiation. The solutions contained the mono- or dicarboxylic acid, H/sub 2/SO/sub 4/, Fe(NH/sub 4/)/sub 2/(SO/sub 4/)/sub 2/ and O/sub 2/. Th e ferrous oxidation was rather independent of the acid and its concentration, but the reduction of ferric was possible in the presence of formic, oxalic, or valeric acid only. The radical formed from the valeric acid acts similar to those formed from hydrocarbons. The G-values of oxidation and reduction of the iron ions were established. The molar extinction coefficients for oxalic and malonic complexes of ferric ions were determined. (auth)

Energy Technology Data Exchange (ETDEWEB)

In this paper we describe a fractal assembly of copper nanoparticles on different substrates by controlling the chemical replacement reaction. Through calculation, we found that the 'fractal dimensions' of copper dendrites synthesized by us were about 1.832, which agreed well with the 'fractal dimensions' of natural fern leaves (fractal dimension, 1.826), suggesting that the fern fractal model was useful to describe the self-assembly of our copper nanoparticles during the chemical replacement reaction process. These results will be beneficial for the understanding of the role that highly nonequilibrium conditions play in the formation of fractal clusters as well as the self-assembly mystique of metallic nanoparticles in nonequilibrium conditions and also helpful in the future assembly of complicated nanoarchitectures of metallic nanoparticles for potential ...

British Library Electronic Table of Contents (United Kingdom)

The growth of silver chloride nanoparticles on ancient textile was achieved by sequential dipping steps in alternating bath of potassium chloride and silver nitrate under ultrasound irradiation. The effect of ultrasound irradiation and sequential dipping steps in growth of the AgCl nanoparticles has been studied. These systems depicted a decrease in the particles size accompanying a decrease in the sequential dipping steps. The samples were characterized with powder X-ray diffraction (XRD) and scanning electron microscopy. XRD analyses indicated that the prepared AgCl nanoparticles on fiber were crystalline. The textile samples containing AgCl nanoparticles were tested for their antibacterial efficacy against Escherichia coli and were found to possess significant antibacterial activity.

Energy Technology Data Exchange (ETDEWEB)

We demonstrate that the nanoparticle formation during laser ablation of metals by short (of a few tens of ps) laser pulses strongly depends on the concentration of surrounding gas. While, at vacuum conditions, nanoparticle formation shows very ''sharp'' atomic force microscope images of aggregated clusters, following with clear appearance of plasmon resonance on the absorption spectra of deposited films, an addition of gas particles starts to decrease the probability of cluster formation. This process shows a threshold for both helium (33 torr) and xenon (12 torr) above which no surface plasmon resonance and correspondingly no observable nanoparticles on the deposited surfaces were detected. The destruction of nanoparticle formation was attributed to the negative influence of surrounding gas particles on ablated particles aggregation. (orig.)

International Nuclear Information System (INIS)

We described the use of silica nanoparticles as building blocks for the immobilization of electrogenerated chemiluminescence (ECL) reagent Ru(bpy)_3"2"+ and the fabrication of layer-by-layer assembly film by alternating the deposition of the Ru(bpy)_3"2"+-doped silica nanoparticles and Au nanoparticles. UV-vis absorption spectroscopy, scanning electron microscopy (SEM), cyclic voltammetry and ECL were used to characterize the uniform growth of the multilayer film. Since Ru(bpy)_3"2"+ could still maintain its ECL property when doped into the silica nanoparticles, the as-prepared multilayer film could be used as an effective ECL sensor, and the sensor showed high sensitivity and good stability.

British Library Electronic Table of Contents (United Kingdom)

Gold nanoparticles were synthesized by using banana peel extract (BPE) as a simple, non-toxic, eco-friendly 'green material'. The boiled, crushed, acetone precipitated, air-dried peel powder was used to reduce chloroauric acid. A variety of nanoparticles were formed when the reaction conditions were altered with respect to pH, BPE content, chloroauric acid concentration and temperature of incubation. The reaction mixtures displayed vivid colors and UV-vis spectra characteristic of gold nanoparticles. Dynamic light scattering (DLS) studies revealed that the average size of the nanoparticles under standard synthetic conditions was around 300nm. Scanning electron microscopy and energy dispersive spectrometry (EDS) confirmed these results. A coffee ring phenomenon, led to the aggregation of th...

International Nuclear Information System (INIS)

Radiation-induced enteritis is a well-recognized sequel of therapeutic irradiation. Therefore we examined the radioprotective properties of Punica granatum peel extract (PPE) on the oxidative damage in the ileum. Rats were exposed to a single whole-body X-ray irradiation of 800 cGy. Irradiated rats were pretreated orally with saline or PPE (50 mg/kg/day) for 10 days before irradiation and the following 10 days, while control rats received saline or PPE but no irradiation. Then plasma and ileum samples were obtained. Irradiation caused a decrease in glutathione and total antioxidant capacity, which was accompanied by increases in malondialdehyde levels, myeloperoxidase activity, collagen content of the tissue with a concomitant increase 8-hydroxy-2'-deoxyguanosine (an index of oxidative DNA damage). Similarly, pro-inflammatory cytokines (TNF-?, IL-1? and IL-6) and lactate dehydrogenase were elevated in irradiated groups as ...

Energy Technology Data Exchange (ETDEWEB)

Size-selected SnO{sub 1.8}:Ag mixed nanoparticle films have been prepared using a gas phase condensation method. Transmission electron microscopy showed that the applied size-selection technique yields well-defined, monodisperse and spherical SnO{sub 1.8} and Ag nanoparticles, both with a fixed diameter of 20 nm. The technique allows an independent variation of the particle size of both materials as well as the concentration of Ag. It allows to assess the influence of these parameters on the gas-sensing properties of the films, here for ethanol vapor in synthetic air. SnO{sub 1.8}:Ag nanoparticle films show optimal values of the sensor signal and response time at a Ag nanoparticle concentration of 5%. Due to the fact that the Ag nanoparticles are clearly distinct from the SnO{sub 1.8} nanoparticles in the film, the most probable mechanism leading to improved ...

Energy Technology Data Exchange (ETDEWEB)

Background: The difficulty of directly measuring cellular dose is a significant obstacle to application of target tissue dosimetry for nanoparticle and microparticle toxicity assessment. As a consequence, the target tissue paradigm for dosimetry and hazard assessment of nanoparticles has largely been ignored in favor of using metrics of exposure (e.g. ?g particle/mL culture medium, particle surface area/mL, particle number/mL). We have developed a computational model of solution particokinetics (sedimentation, diffusion) and dosimetry for non-interacting spherical particles and their agglomerates in monolayer cell culture systems. Particle transport to cells is calculated by simultaneous solution of Stokes Law (sedimentation) and the Stokes-Einstein equation (diffusion). Results: The In vitro Sedimentation, Diffusion and Dosimetry model (ISDD) was tested against measured transport rates or cellular doses for multiple sizes of polystyrene ...

British Library Electronic Table of Contents (United Kingdom)

Abstract Male infertility continues to be a clinical challenge of increasing significance. While male factors such as decreased semen quality are responsible for 25% of all infertility issues, the etiology of suboptimal semen quality is poorly understood. Many physiological, environmental, and genetic factors have been implicated, including oxidative stress. Oxidative stress is induced by reactive oxygen species (ROS), or free radicals, and although ROS are required for critical aspects of sperm function, excessive levels of ROS can negatively impact sperm quality. The origin of ROS generation, and the etiologies of increased ROS in men with suboptimal sperm quality have only recently been elucidated, offering multiple targets for potential therapy. Here, we present a critical review of th...

British Library Electronic Table of Contents (United Kingdom)

Nitric oxide (NO) and related molecules such as peroxynitrite, S-nitrosoglutathione (GSNO), and nitrotyrosine, among others, are involved in physiological processes as well in the mechanisms of response to stress conditions. In sunflower seedlings exposed to five different adverse environmental conditions (low temperature, mechanical wounding, high light intensity, continuous light, and continuous darkness), key components of the metabolism of reactive nitrogen species (RNS) and reactive oxygen species (ROS), including the enzyme activities L-arginine-dependent nitric oxide synthase (NOS), S-nitrosogluthathione reductase (GSNOR), nitrate reductase (NR), catalase, and superoxide dismutase, the content of lipid hydroperoxide, hydrogen peroxide, S-nitrosothiols (SNOs), the cellular level of N...

International Nuclear Information System (INIS)

A method, based on anion exchange chromatography, is presented for the isolation of "1"3"9Ce after production by a proton-induced nuclear reaction on a thick praseodymium target. After bombardment the target is dissolved in nitric acid and "1"3"9Ce oxidised to the Ce(IV) oxidation state with bromic acid. "1"3"9Ce is then separated form the praseodymium by anion exchange chromatography on a Ag MP-1 resin column in a nitric acid - bromic acid mixture. "1"3"9Ce is sorbed onto the resin column and praseodymium eluted with the acid mixture. The bromic acid is washed out of the column with nitric acid and "1"3"9Ce finally eluted with dilute nitric acid containing sulphur dioxide.

International Nuclear Information System (INIS)

1-Furan-2-yl-3-pyridin-2-yl-propenone (FPP-3) is an anti-inflammatory agent with a propenone moiety and chemically synthesized recently. In this study, we examined the chemopreventive effect of FPP-3 on 7,12-dimethylbenz[a]anthracene (DMBA)-induced genotoxicity in MCF-7 cells. FPP-3 reduced the formation of the DMBA-DNA adduct. DMBA-induced CYP1A1 and CYP1B1 gene expression and enzyme activity were inhibited by FPP-3. It inhibited DMBA-induced aryl hydrocarbon receptor (AhR) transactivation and DMBA-inducible nuclear localization of the AhR. Induction of detoxifying phase II genes by chemopreventive agents represents a coordinated protective response against oxidative stress and neoplastic effects of carcinogens. Transcription factor NF-E2 related factor 2 (Nrf2) regulates antioxidant response element (ARE) of phase II detoxifying and antioxidant enzymes, such as glutathione ...

International Nuclear Information System (INIS)

Oxide superconducting thin films were irradiated with X-rays and ultra-violet (UV) light, and induced radiation effects on electrical and chemical properties were examined by transport measurement, X-ray diffraction analysis (XRD), diamagnetization measurement and X-ray photoemission spectroscopy (XPS). After irradiation for ErBa_2Cu_3O_x films with X-rays emitted from a Rh tube for 100 hours, superconductivity was remarkably damaged, destroying the zero-resistance state. The UV-light irradiation for Bi_2Sr_2CaCu_2O_x films was performed in He gas of about 500 Pa with a low pressure mercury lamp. The superconductivity was gradually degraded with the UV irradiation time up to 70 minutes. In both cases, adequate oxygen-annealing treatments restored superconductivity. The X-ray photoemission spectra showed that the mean Cu valence of the films was decreased approximately from +2 to +1 by the irradiation. From these results we can find that ...

Science.gov (United States)

We have constructed a 27-kDa hTERT C-terminal polypeptide (hTERTC27) devoid of domains required for telomerase activity and demonstrated that it is capable of nuclear translocation/telomere-end targeting. Here we showed that expression of a low level of hTERTC27 renders hTERT positive HeLa cells sensitive to H(2)O(2)-induced oxidative stress and subsequent cell senescence. The senescence-associated gene, the cyclin/cdk inhibitor p21(Waf1), was up-regulated. This occurs without changing the expression of endogenous hTERT, causing significant telomere shortening or inhibiting telomerase activity. Results from this study suggest for the first time that in addition to telomerase activity, the C-terminus of hTERT also plays a role in hTERT-mediated cellular resistance to oxidative stress. PMID:12565825

International Nuclear Information System (INIS)

We have studied the correlation between the chemical state and the oxygen-sensing properties of an iron oxide thin film using a setup that allows simultaneous sensor resistance measurements and X-ray photoelectron spectroscopy (XPS) data acquisition. The gas exposures were performed at the highest operating pressure of the XPS spectrometer at a controlled sample temperature which allows direct comparison between the sensor response and the chemical state of the surface. The iron oxide film was modified by a sequence of argon ion sputtering steps and the induced changes in the chemical state, resistance, and sensitivity to oxygen were investigated. The sputtering was found to reduce the iron from the Fe"3"+ to the Fe"2"+ state and to decrease the sensor resistance. The measured sensitivity to oxygen first increased by a factor of two but then collapsed to its original level. The mechanism for oxygen sensing was found to be ...

Energy Technology Data Exchange (ETDEWEB)

Chloride-induced pitting corrosion of stainless steel (Materials No. 1.4301 and 1.4571) was investigated with the aid of chronopotentiostatic tests. Oxide films upon the surface (temper colours), addition of inhibitors (sulphate and nitrate) and temperature were the testing variables. Two different critical pitting potentials have been found, which give information on the potential ranges for stable passivity, latent and stable pitting corrosion. The results only indicate a small effect of Mo content of the material and test temperature. The inhibitors (sulphate and nitrate) have a marked effect. Specimens with a clean surface produced by pickling are markedly more resistant against pitting corrosion than specimens with a yellow temper colour, whereas the difference in corrosion resistance between yellow and blue films is relatively small. The width of the critical potential range for pitting corrosion generally increases with increasing ...

International Nuclear Information System (INIS)

In this study, we measured the effects of different concentrations of paraquat (0,01 mM and 1,0 mM) on the 1-"1"4CO_2 and 6-"1"4CO_2 production of rabbit lung slices and isolated alveolar macrophages, in 20% and 95% oxygen phases respectively. A 95% oxygen phase induced an increase in the 6-"1"4C-glucose oxidation of control lung slices over a 3-hour period, while the increased activity of the pentose pathway over the first 2 hours started to decline during the third hour of incubation. Paraquat (1,0mM) in 20% oxygen caused a consistent increase in the 6-"1"4CO_2 production by lung slices, but in a 95% oxygen phase gradually inhibited the 6-"1"4C-glucose oxidation over a period of 3 hours. The pentose phosphate pathway was highly significantly stimulated by 1,0 mM paraquat in 20% and 95% oxygen over 3 hours. When isolated alveolar macrophages (viability 95%) were incubated in a 20% and 95% oxygen phase respectively, both ...

Energy Technology Data Exchange (ETDEWEB)

Gold and silver nanoparticles display extraordinarily large apparent refractive indices near their plasmon resonance (PR) wavelengths. These nanoparticles show good contrast in a narrow spectral band but are poorly resolved at other wavelengths in differential interference contrast (DIC) microscopy. The wavelength dependence of DIC contrast of gold/silver nanoparticles is interpreted in terms of Mie's theory and DIC working principles. We further exploit this wavelength dependence by modifying a DIC microscope to enable simultaneous imaging at two wavelengths. We demonstrate that gold/silver nanoparticles immobilized on the same glass slides through hybridization can be differentiated and imaged separately. High-contrast, video-rate images of living cells can be recorded both with and without illuminating the gold nanoparticle probes, providing definitive probe ...

International Nuclear Information System (INIS)

Studying the structure of nanoparticles as a function of their size requires a correlation between the image and the diffraction pattern of single nanoparticles. Nanobeam diffraction technique is generally used but requires long and tedious TEM investigations, particularly when nanoparticles are randomly oriented on an amorphous substrate. We bring a new development to this structural study by controlling the nanoprobe of the Bright and Dark Field STEM (BF/DF STEM) modes of the TEM. The particularity of our experiment is to make the STEM nanoprobe parallel (probe size 1 nm and convergence angle <1 mrad) using a fine tuning of the focal lengths of the microscope illumination lenses. The accurate control of the beam position offered by this technique allowed us to obtain diffraction patterns of many single nanoparticles selected in the digital STEM image. By means of this technique, we demonstrate size ...

Science.gov (United States)

We presented a simple approach for in-situ synthesis of poly(dimethylsiloxane) (PDMS)-gold nanoparticles composite film based on the special characteristics of PDMS itself. It is an environmentally safe synthesis method without the requirement of additional reducing/stabilizing agents. The region where the resulting gold nanoparticles distribute (in the matrix or on the surface of the polymer) and the size of the nanoparticles, as well as the colour of the free-standing films, can be simply controlled by adjusting the ratio of curing agent and the PDMS monomer. The chemical and optical properties of these composite films were studied. Using such a method, gold nanoparticle micropatterns on PDMS surfaces can be performed. And based on the gold nanoparticles micropattern, further modification with antibodies, antigens, enzymes and other biomolecules can be achieved. To verify this ...

Energy Technology Data Exchange (ETDEWEB)

CuAg core-shell nanoparticles are synthesized by ultra-high vacuum thermal evaporation. We show on this system how the Energy-Filtered Transmission Electron Microscopy (EFTEM) technique allows one to improve the characterization by precisely pointing out the formation of core-shell arrangements in bimetallic nanoparticle assemblies. A criterion to measure the shell thickness from EFTEM images on unique core-shell nanoparticles is defined, that can be used for core-shell nanoparticles of any sizes, with shell thicknesses over 1 nm. It is based on the intensity variation along a line drawn across a core-shell nanoparticle on a EFTEM image. This criterion has been validated by a close comparison of the shell thickness measurements performed in this work and the ones obtained by acoustic micro-Raman spectroscopy. Using this criterion, we report a strong correlation between the size of ...

Science.gov (United States)

Magnetic drug targeting, using core-shell magnetic carrier particles loaded with anti-cancer drugs, is an emerging and significant method of cancer treatment. Gold shell-iron core nanoparticles (Fe@Au) were synthesized by the reverse micelle method with aqueous reactants, surfactant, co-surfactant and oil phase. XRD, XPS, TEM and magnetic property measurements were utilized to characterize these core-shell nanoparticles. Magnetic measurements showed that the particles were superparamagnetic at room temperature and that the saturation magnetization decreased with increasing gold concentration. The anti-cancer drug doxorubicin (DOX) was loaded onto these Fe@Au nanoparticle carriers and the drug release profiles showed that upto 25% of adsorbed drug was released in 80 h. It was found that the amine (-NH2) group of DOX binds to the gold shell. An in vitro apparatus simulating the human circulatory system was used to determine ...

Energy Technology Data Exchange (ETDEWEB)

We demonstrate the rapid optical characterization of large numbers of individual metal nanoparticles freely diffusing in colloidal solution by confocal laser spectroscopy. We find that hollow gold nanospheres and solid silver nanoparticles linked with a bifunctional ligand, both designed nanostructures, exhibit significantly higher monodispersity in their Rayleigh and Raman scattering response than randomly aggregated gold and silver nanoparticles. We show that measurements of rotational diffusion timescales allow sizing of particles significantly more reliably than can be obtained using translational diffusion timescales.

Energy Technology Data Exchange (ETDEWEB)

Electron paramagnetic resonance was used to investigate surface-coated magnetite-based magnetic fluids doped with TEMPOL. Two magnetic fluid samples, having magnetite nanoparticles with average diameter of 94 A and coated with different coating layers (lauric acid plus ethoxylated polyalcohol in one case and oleoylsarcosine in the other case), were doped with TEMPOL (6 mM and pH 7.4) and investigated as a function of the nanoparticle concentration. The resonance field and the resonance linewidth both scale linearly with the nanoparticle concentration.

International Nuclear Information System (INIS)

Measurements of ion-induced electron emission have been performed with helium and argon ions with energies between 300 and 900 eV on W, W with 10% Ti, Al, Al with 1% Cu, Al with 1% Si, Si, and Be. This article describes many of the important surface characteristics that influence the ion-induced electron emission. For low-energy ions, the substrate material was found to be less important as the velocity of the incident ion decreased. In the case of incident Ar"+ the substrate material had a negligible effect on the emission for this energy range. The presence of an adsorbed layer enhanced emission in all cases. Heating the substrates resulted in oxidation of the surfaces and a subsequent increase in emission. The electron emission from aluminum samples with smaller grain sizes was higher than samples of identical composition with larger grains. This effect is due to the greater number of adsorption sites resulting from the ...

Energy Technology Data Exchange (ETDEWEB)

The variation of surface composition and sintering of the binary Pd{sub 7}Ag{sub 3} nanoparticles prepared by chemical reduction were studied. The composition of the as-prepared Pd{sub 7}Ag{sub 3} nanoparticles across the diameter is inhomogeneous due to different reduction potentials of Pd and Ag. Upon heating, Ag will migrate to the surface because of its lower surface energy. Surface modification results in variation of surface composition during the sintering process. Stearic acid acts as a grain growth inhibitor. The migration of Ag to the surface is suppressed and the sintering is retarded. Modification by polyethylene glycol leads to more migration of Ag atoms from the core to the surface. This makes the nanoparticles easier to sinter.

British Library Electronic Table of Contents (United Kingdom)

Highly dispersed silver nanoparticles embedded in mesoporous thin films (MTFs) have been synthesized by modification of the interior surface of mesoporous silica with ethylenediamine moieties, which provided the coordination sites for the Ag ions, and subsequent reduction under hydrogen atmosphere. TEM observations show the mesoporous parent films have effectively controlled the growth of the synthesized silver nanoparticles. The composite films had an ultrafast nonlinear response time, as fast as 200 fs, and a third-order nonlinear optical susceptibility of 0.94??10?10 esu, which was enhanced by the local field enhancement effect that was present when the silver nanoparticles were embedded in the surrounding dielectric matrix. The origin of the ultrafast nonlinear response and the enhanc...

Energy Technology Data Exchange (ETDEWEB)

Metallic nanoparticles was synthesized in SiO{sub 2} matrices by means of a process of two stages. The first one proceeded via sol-gel, incorporating the metallic precursors to the reaction system before the solidification of the matrix. Later on, the samples underwent a thermal treatment in atmosphere of H{sub 2}, carrying out the reduction of the metals that finally formed to the nanoparticles. Then it was detected the presence of smaller nanoparticles than 20 nm, dispersed and with the property of being liberated easily of the matrix, conserving a free surface, chemically reactive and with response to external electromagnetic radiation. The system SiO{sub 2}-Pd showed an important thermoluminescent response. (Author)

Energy Technology Data Exchange (ETDEWEB)

Ag nanoparticles were prepared in a water-phase system with a mixture of silver-ammonia complex, sodium borohydride, and lauric acid according to molar feed ratio of approximately 6:3:1. The mechanism of preparation and separation by chemical reduction-protection method was explored. The as-synthesized Ag nanoparticles were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD) and UV-vis spectroscopy, respectively. It was found that the size of high purity Ag particles was ranging from 30 to 50 nm with slight agglomeration. In addition, the as-synthesized wet Ag nanoparticles were dispersed stably in organic vehicle to formulate electrically conductive nanopaste. Upon direct-written and sintered, the array pattern of the nanopaste with the resolution of about 30 {mu}m was achieved with the electrical resistivity in the order of magnitude of 10{sup -5} {Omega} cm.

Science.gov (United States)

... metal-oleate complexes. At this point, this method has been reported only for iron nanoparticles [15]. We have demonstrated ...

British Library Electronic Table of Contents (United Kingdom)

The addition of ?-Sialon nanoparticles to lubricants in heavy-duty frictional joints is shown to be effective.

British Library Electronic Table of Contents (United Kingdom)

Bacterial cellulose was produced by Acetobacter xylinum (strain TISTR 975). Bacterial cellulose is an interesting material for using as a wound dressing since it provides moist environment to a wound resulting in a better wound healing. However, bacterial cellulose itself has no antimicrobial activity to prevent wound infection. To achieve antimicrobial activity, silver nanoparticles were impregnated into bacterial cellulose by immersing bacterial cellulose in silver nitrate solution. Sodium borohydride was then used to reduce the absorbed silver ion (Ag+) inside of bacterial cellulose to the metallic silver nanoparticles (Ag0). Silver nanoparticles displayed the optical absorption band around 420nm. The red-shift and broadening of the optical absorption band was observed when the mole rat...

British Library Electronic Table of Contents (United Kingdom)

Emeraldine base (EB) polymer?ZnO nanoparticles composite films has been synthesized by solution casting technique on ITO-coated glass substrate and characterized by XRD, FTIR and TEM for their structure and morphology. Dielectric behaviour of these composite films has been investigated in the very low frequency region to medium frequency region (1?kHz?1?MHz). The dielectric constant of the composite with 30% nanoparticles is almost one-tenth of the pure EB. The dielectric value becomes constant in the frequency region greater than 400?kHz. The change in dielectric behaviour of the composite is explained on the basis of multilayered interface formed between the ZnO nanoparticles and emeraldine chains. Nanoparticles have high energy surface which is responsible for the decrease of free volum...

British Library Electronic Table of Contents (United Kingdom)

Bio-inspired silver nanoparticles were synthesized with the aid of a novel, non-toxic, eco-friendly biological material namely, banana peel extract (BPE). Boiled, crushed, acetone precipitated, air-dried peel powder was used for reducing silver nitrate. Silver nanoparticles were formed when the reaction conditions were altered with respect to pH, BPE content, concentration of silver nitrate and incubation temperature. The colorless reaction mixtures turned brown and displayed UV-visible spectra characteristic of silver nanoparticles. Scanning electron microscope (SEM) observations revealed the predominance of silver nanosized crystallites after short incubation periods. When the reaction mixtures were incubated for 15 days, some micro-aggregates were also observed. Energy dispersive spectr...

Energy Technology Data Exchange (ETDEWEB)

Nanometre-sized materials, like nanowires, nanoparticles or nanobelts, are gaining huge interest as building blocks of modern electronic nanodevices. Their fabrication feasibility has been demonstrated in the last years, and different routes are already well established in order to synthesize these materials. However, the assessment of their electrical properties is still a challenging issue, due to the difficulty to perform a precise nanolithography process allowing the access to such small structures. The fabrication of metallic contacts with precision in the nanometre range is necessary, as well as achieving a flexible system that allows to contact individual structures. Such a system could be a dual-beam Focused Ion Beam instrument, which combines Scanning Electron Microscopy (SEM) and Focused Ion Beam (FIB) in one machine, able to assist deposition of materials with nanometre precision. In this work, the methodology of fabrication of metallic nanocontacts to ...

Energy Technology Data Exchange (ETDEWEB)

The Co-Si composites with a molar ratio of 2:1 are synthesized by ball-milling method and their potential as negative electrode materials of Ni-MH batteries is investigated. The microstructure, morphology and chemical state of the ball-milled Co-Si composites are characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). XRD patterns show that the ball-milled samples for 10 and 20 h contain Co, Si and Co{sub 2}Si phases, and the ball-milled samples for 40 and 60 h are mainly amorphous Co{sub 2}Si alloys. In contrast to the high initial discharge capacity (1012 mAh/g) obtained for the sample ball-milled for 10 h, the discharge capacities of the samples ball-milled for 40 and 60 h are very low. It indicates that the hydrogen storage capacity of pure Co{sub 2}Si alloy is very low. It is found that the formation of active Co nanoparticles and Si oxidation are responsible for the high ...

UK PubMed Central (United Kingdom)

Zinc tetraaminophthalocyanine-Fe₃O₄ nanoparticle composites were prepared by organic-inorganic complex technology and characterized. It has been proved that the ZnTAPc dispersed...Full Text Available

UK PubMed Central (United Kingdom)

Short and long-term pulmonary response to inhaled nickel hydroxide nanoparticles (nano-Ni(OH)₂, CMD = 40 nm) in C57BL/6 mice was assessed using a whole body exposure system. For short-term...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A mesoscopically ordered lamellar gel phase of a polymer-grafted, lipid-based complex fluid is used as a scaffolding to spatially organize inorganic nanoparticles. The complex fluid provides both a highly anisotropic environment and a segregated aqueous and organic domains in which inorganic nanoparticles can be selectively placed by tailoring their size and surface characteristics. Three types of silver nanoparticles -- underivatized, surfactant-stabilized, and dodecanthiol-derivatized -- were evaluated. Comparison of the surface plasmon resonance of the various silver particles dispersed in conventional solvents to those contained within the complex fluid was used to determine the region of spatial localization in the lamellar gel phase. Silver particles rendered hydrophobic by capping with an alkane thiol insert into the hydrocarbon bilayer region. Surfactant-stabilized and underivatized silver ...

Energy Technology Data Exchange (ETDEWEB)

A microemulsion comprised of water, Brij 78, pentanol and styrene into which PPO and bis-MSB had been dissolved was prepared. Polymerization of the styrene resulted in a suspension of fluor-containing polystyrene nanoparticles (<100 nm). After a concentration step, the aqueous nanosuspension was able to detect {sup 14}C with counting efficiencies over 50% of those of a commercially available scintillation cocktail. Monte Carlo calculations demonstrated that the size and concentration of the nanoparticles were appropriate for optimum detection efficiency.

Energy Technology Data Exchange (ETDEWEB)

Production of porous membranes using heavy ion bombardment and subsequent chemical etching of poly(vinylidene difluoride) (PVDF) films has been reported several years ago. However, porous membranes with pore diameter in the nanometer scale requires a better understanding of the chemical etching mechanism. In this work PVDF foils irradiated with Sn ions (2.85 MeV per nucleon) were exposed to several etching conditions which involved permanganate oxidation in different alkaline environments. The solution of KOH 9 mol L{sup -1} and saturated in KMnO{sub 4} was the best etching reactant for PVDF. Functional groups created in the alkaline and oxidative attack by permanganate were studied by FT-IR and UV-vis spectroscopy. The spectroscopic data reveals that the formation of pores occurs by a two-step mechanism: (i) double bonds as a result of dehydrofluorination induced by alkaline media and (ii) oxidation of ...

International Nuclear Information System (INIS)

We demonstrate detection of a single core-shell magnetite-silica nanoparticle (outer diameter #approx#120 nm, moment #approx#10"4#mu#_B) using an Nb dc superconducting quantum interference device (SQUID) with the loop size of 350 nm operational at T < 10 K. The system noise was minimized down to 0.2 #mu##PHI#_0 Hz"-"1"/"2 using a cryogenic SQUID series array pre-amplifier. Initial measurements of an individual magnetic nanoparticle were performed and a clear change of the noise spectra of the nano-SQUID was detected at low frequencies in the presence of the nanoparticle. Similar behaviour was confirmed with an FePt nanoparticle with a larger magnetic moment (diameter #approx#150 nm, moment #approx#10"6#mu#_B). Thus, we demonstrate a magnetic sensor based on a dc nano-SQUID and enabling detection of small moments (potentially down to a few electron spins). Such a sensor is of considerable significance ...

Energy Technology Data Exchange (ETDEWEB)

An electrochemical detection method for analyzing sequence-specific DNA using gold nanoparticle DNA probes and subsequent signal amplification step by silver enhancement is described. The assay relies on the electrostatic adsorption of target oligonucleotides onto the sensing surface of the glassy carbon electrode (GCE) and its hybridization to the gold nanoparticle-labeled oligonucleotides DNA probe. After silver deposition onto gold nanoparticles, binding events between probe and target were monitored by the differential pulse voltammetry (DPV) signal of the large number of silver atoms anchored on the hybrids at the electrode surface. The signal intensity difference permits to distinguish between the match of two perfectly matched DNA strands and the near-perfect match where just one base pair was wrong. Coupled with this 'nanoparticle-promoted' reduction of silver signal ...

Energy Technology Data Exchange (ETDEWEB)

In the present dissertation, a hierarchical multiscale approach for modeling FePt nanoparticles by atomistic computer simulations is developed. By describing the interatomic interactions on different levels of sophistication, various time and length scales can be accessed. Methods range from static quantum-mechanic total-energy calculations of small periodic systems to simulations of whole particles over an extended time by using simple lattice Hamiltonians. By employing these methods, the energetic and thermodynamic stability of non-crystalline multiply twinned FePt nanoparticles is investigated. Subsequently, the thermodynamics of the order-disorder transition in FePt nanoparticles is analyzed, including the influence of particle size, composition and modified surface energies by different chemical surroundings. In order to identify processes that reduce or enhance the rate of transformation from the disordered to the ...

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Fuel irradiation leads to a swelling resulting from the formation of gaseous (Kr, Xe) or solid fission products which are found either in solution or as solid inclusions in the matrix. This phenomena has to be evaluated to be taken into account in fuel cladding Interaction. Fuel swelling was studied as a function of burn up by measuring the corresponding cell constant evolution by X-Ray diffraction. This study was realized on Mixed Oxide Fuels (MOX) irradiated in a Pressurized Water Reactor (PWR) at different burn-up for 3 initial Pu contents. Lattice parameter evolutions were followed as a function of burn-up for the irradiated fuel with and without an annealing thermal treatment. These experimental evolutions are compared to the theoretical evolutions calculated from the hard sphere model, using the fission product concentrations determined by the APPOLO computer code. Contribution of varying parameters influencing the unit cell value is discussed. Thermal ...

Energy Technology Data Exchange (ETDEWEB)

In this work we present the electrical characterization of non self-aligned p-channel thin film transistors fabricated by using laser doping technique for source/drain contact formation and gate oxide deposited at room temperature by Electron Cyclotron Resonance Plasma Enhanced Chemical Vapour Deposition. These techniques are suitable for a very low temperature process for TFT fabrication. The output characteristics show a current increase at high drain voltage ('kink' effect) rather moderate, if compared to self aligned polysilicon TFTs, probably due to the gradual doping profile induced by laser doping process. After bias stress at low gate voltage and high drain voltage condition a strong reduction of kink current has been observed in the output characteristics at high drain voltage, whereas minor changes has been observed in the transfer characteristics. This behaviour is similar to what observed in n-channel Gate ...

International Nuclear Information System (INIS)

In an attempt to enhance the electrical and mechanical properties of the high temperature superconducting oxides, high T(sub c) composites were prepared composed of the 123 compounds and AgO. The presence of extra oxygen due to the decomposition of AgO at high temperature is found to stabilize the superconducting 123 phase. Ag is found to serve as clean flux for grain growth and precipitates as pinning center. Consequently, almost two orders of magnitude enhancement in critical current densities were also observed in these composites. In addition, these composites also show much improvement in workability and shape formation. On the other hand, proper oxygen treatment of Y5Ba6Cu11Oy was found to possibly stabilize superconducting phase with T(sub c) near 250 K. I-V, ac susceptibility, and electrical resistivity measurements indicate the existence of this ultra high T(sub c) phase in this compound. Detailed structure, microstructure, electrical, magnetic and thermal ...

Energy Technology Data Exchange (ETDEWEB)

In response to a heat shock, the yeast Saccharomyces cerevisiae undergoes a large increase in its resistance to heat and, by the induction of its recombinational DNA repair capacity, a corresponding increase in resistance to radiation. Yeast which lack mitochondrial DNA, mitochondria-controlled protein synthetic apparatus, aerobic respiration, and electron transport (rho/sup 0/ strain) were used to assess the role of O/sub 2/, mitochondria, and oxidative processes controlled by mitochondria in the induction of these resistances. We have found that rho/sup 0/ yeast grown and heat shocked in either the presence or absence of O/sub 2/ are capable of developing both radiation and heat resistance. We conclude that neither the stress signal nor its cellular consequences of induced heat and radiation resistance are directly dependent on O/sub 2/, mitochondrial DNA, or mitochondria-controlled protein synthetic or oxidative ...

British Library Electronic Table of Contents (United Kingdom)

ObjectiveExtended periods of muscle disuse, physical inactivity, immobilization, and bedrest result in a loss of muscle mass and a decrease in muscle force, which are accompanied by an increase in oxidative stress. We investigated the effects of the intake of green tea catechins on unloading-induced muscle dysfunction in tail-suspended mice. MethodsTen-week-old male BALB/c mice were fed a purified control diet or a diet containing 0.5% tea catechins for 14 d. Thereafter, the mice were subjected to continuous tail suspension for 10 d. On the final day, muscle mass, contractile force production, antioxidant potential, and carbonylated protein levels were evaluated. ResultsHind limb unloading caused a loss of soleus muscle weight and muscle force. Intake of tea catechins significantly inhibit...

Energy Technology Data Exchange (ETDEWEB)

Stainless steels can get pitting corrosion in halide containing solution, which make them a big risk in industrial production. Many investigations were made in the past in order to understand processes involved in pitting corrosion, pit initiation and pit growth. Results about the influence of alloying elements, their contents, the state of the structure, the condition of the surface, the content of chloride, the temperature, the pH-value, the velocity of flow and of the oxidizer on the chloride induced pitting corrosion of passive stainless steels are presented. Electrochemical measurements and the application of surface analytical methods (SEM, SAM, XPS) with high lateral resolution are carried out. A part of the samples received a diffusion annealing in order to obtain reproducible results. Pitting Resistance Equivalents (PRE) - Pitting Index - with different multipliers are given and discussed critical. An electrochemical method for ...

International Nuclear Information System (INIS)

With the assistance of mechanical activation, yttrium-stabilized #alpha#-SiAlON was prepared by combustion synthesis in air, instead of high-pressure N_2 atmosphere for the first time. The reaction activity of metallic particles was remarkably enhanced by mechanical activation, which conduced the reduction of grain size, increased the total surface area and formation of fresh surface. The formation of #alpha#-SiAlON by combustion synthesis in air was explained by a kinetically induced reaction mechanism, in which both initial formation of #alpha#-SiAlON and following avoidance of oxidation were fulfilled by the retardation of O_2 infiltration owing to the short reaction period and fast cooling rate.

Energy Technology Data Exchange (ETDEWEB)

Passive films formed on Alloy UNS N06690 were investigated in simulated crevice chemistries. It was found the role of lead in corrosion processes is strongly dependent on the pH value of the testing solutions. At pH 1.5 the effect of lead is narrowly noticeable; while at pH 12.7, lead has a significant influence on the electrochemical performance of alloy UNS N06690. The lead alters the surface morphologies at both pH and account for higher hydroxide content in the surface film at pH 12.7. The lead incorporation hinders the formation of spinel oxides during the passivation in alkaline solution. Nanoindentation tests indicate a significant lead-induced degradation in the mechanical properties of passive films. The passivation degradation is attributed to detrimental effects of lead via interrupting the dehydration process and hindering the formation of protective layers on the alloy surface.

Energy Technology Data Exchange (ETDEWEB)

Culturing human prostate PC-3 cells for 4, 24, or 72 h in the presence of 5,8,11,14-eicosatetraynoic acid (ETYA), an inhibitor of arachidonic acid metabolism and cholesterol biosynthesis, markedly altered the morphology and reduced the number of mitochondria in the treated cells. Using quantitative electron microscopic morphometry, we documented changes in the number, form, area, matrix density, and integrity of the cristae and limiting membranes of mitochondria in cells cultured with ETYA. The inhibition of cholesterol synthesis or the substitution of ETYA for polyunsaturated fatty acids in the inner membrane may participate in the disruption of the mitochondria, which resembles the morphologic sequelae of oxidative stress. If sufficiently extensive, these changes could contribute to the inhibition of cellular proliferation by ETYA.

Science.gov (United States)

In the present work, a new kind of myoglobin (Mb)/Au nanoparticles composite film was fabricated on pyrolytic graphite (PG) electrodes. Oppositely charged chitosan (CS) and silica (SiO(2)) nanoparticles were alternately adsorbed on the PG surface by the electrostatic interaction between them, forming {CS/SiO(2)}(5) layer-by-layer films. Mb and HAuCl(4) in solution were then simultaneously loaded into {CS/SiO(2)}(5) films. The loaded Au(III) in the films were electrochemically reduced into Au nanoparticles, forming nanocomposite films, designated as {CS/SiO(2)}(5)-Mb-Au. Various techniques such as cyclic voltammetry (CV), square wave voltammetry (SWV), quartz crystal microbalance (QCM), electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analysis were used to characterize the films. Compared with {CS/SiO(2)}(5)-Mb films without Au ...

International Nuclear Information System (INIS)

... ammonium compounds benzilic acid chemical preparation lanthanum oxides

British Library Electronic Table of Contents (United Kingdom)

Randomly oriented ZnO microsheets were successfully self-assembled on TiO2 nanoparticle (TN) film to act as the scattering layer via a cathodic electrodeposition process. The light scattering properties of ZnO microsheets were studied by UV-Vis spectrometer in the 400?800 nm wavelength range. It was found that ZnO microsheets exhibited excellent ability to scatter the incident light for ZnO microsheet-TiO2 nanoparticle (ZT) composite films. The results showed that dye-sensitized solar cells (DSSCs) fabricated with ZT composite films showed higher short-circuit density (J sc) and conversion efficiency than TN-based DSSCs, due to the light scattering properties of ZnO microsheets.

British Library Electronic Table of Contents (United Kingdom)

Antibacterial activity of Transition metals (Mn, Co) doped ZnO nanopowders prepared by a DC thermal plasma method against Escherichia coli and Staphylococcus aureus are investigated. The phase and morphology studies have been carried out by X-ray diffraction, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) respectively. All the samples of the present investigation are found to have hexagonal wurtzite structure and crystallite sizes are found to vary from 25nm to 30nm. Our bacteriological study showed the enhanced antibacterial activity of transition metals doped ZnO nanoparticles than undoped ZnO indicating the great potential of ZnO nanoparticles in relevant clinical and biomedical applications.

British Library Electronic Table of Contents (United Kingdom)

Microgel-clay composite particles were prepared by one-step surfactant-free precipitation polymerization. Laponite nanoparticles present in the reaction mixture become encapsulated during the microgel formation process. Microgel-clay composites based on poly(N-vinylcaprolactam-co-acetoacetoxyethyl methacrylate) containing different amount of incorporated clay nanoparticles were synthesized. The clay content was varied from 2 wt% to 18 wt%. The extremely high incorporation efficiency of the clay nanoparticles into microgels was detected. The size of the hybrid microgels was decreased from 700 nm to 100 nm by increase of the clay concentration in the reaction mixture. Obtained hybrid microgels exhibit negative surface charge and excellent colloidal stability. Microgel-clay composite particle...

British Library Electronic Table of Contents (United Kingdom)

Cellulose whiskers and microfibrillated cellulose (MFC) were extracted from the rachis of date palm tree and characterized. These cellulosic nanoparticles were used as reinforcing phase to prepare nanocomposite films using latex of natural rubber as matrix. These films were obtained by the casting/evaporation method. The properties of the ensuing nanocomposite films were investigated using differential scanning calorimetry, toluene and water uptake experiments, dynamic mechanical analysis and tensile tests. The stiffness of the natural rubber was significantly increased above its glass-rubber transition temperature upon nanoparticles addition. The reinforcing effect was shown to be higher for nanocomposites with MFC compared to whiskers. It was ascribed to the higher aspect ratio and possi...

International Nuclear Information System (INIS)

We report on the fabrication of nanomechanical devices for shuttling of electrons from one electrode to another. Each device consists of a 20 nm diameter gold nanoparticle embedded within the gap between two gold electrodes. In two different kinds of shuttle-junctions the nanoparticle is attached to the electrodes through either (i) a single layer of 1,8-octanedithiol or (ii) a multilayer of 1-octanethiol molecules. The thiol layers play the role of 'damped springs', such that when a sufficient voltage bias is applied to the junction, the nanoparticle is expected to start oscillating and thereby transferring electrons from one electrode to the other. For both kinds of shuttle-junctions we observed an abrupt increase in the transmitted current above a threshold voltage, which can be attributed to a transition from the stationary to the oscillating regime. The threshold voltage was found to be lower for single-layer ...

International Nuclear Information System (INIS)

We report studies of bimetallic nanoparticles with 15%-16% atomic crystal parameters size mismatch. The degree of alloying was probed in a 2-nm Pt core (smallest attainable core size) of Pt-Ag nanoparticles (completely immiscible in bulk) and 20-nm-diameter Pd-Ag nanowires (completely miscible in bulk). Particles were synthesized radiolytically, and depending on the initial parameters, they assume spherical or cylindrical (nanowire) morphologies. In all cases, the metals are seen to follow their bulk alloying characteristics. Pt and Ag segregate in both spherical and wire forms, which indicates that strain due to crystallographic mismatch overcomes the excess surface free energy in the small particles. The Pd-Ag nanowires alloy similar to previously reported spherical Pd-Ag particles of similar diameter and composition.

Energy Technology Data Exchange (ETDEWEB)

In the present study, the immunomodulatory effect of {beta}-endorphin ({beta}-E) and shorter pro-opiomelancortin (POMC) fragments was evaluated by assessing their influence on respiratory burst in human polymorphonuclear leukocytes (PMN). The effect of the peptides on phorbol myristate acetate (PMA)-stimulated production of reactive oxygen metabolites was measured in a lucigenin-enhanced chemiluminescence (CL) assay. Both POMC peptides with opiate-like activity and their non-opioid derivatives were tested. With the exception of {alpha}-E, PMA-stimulated respiratory burst was suppressed by all POMC fragments tested. A U-shaped dose-response relation was observed. Doses lower than 10{sup {minus}17}M and higher than 10{sup {minus}8}M were without effect. {beta}-E and dT{beta}E both suppressed PMA-induced oxidative burst in human PMN at physiological concentrations. {gamma}-E and dT{gamma}E proved to be less potent inhibitors, reaching maximal ...

Energy Technology Data Exchange (ETDEWEB)

This work covers three distinct aspects of deformation and fracture during indentations. In particular, we develop an approach to verification of nanoindentation induced film fracture in hard film/soft substrate systems; we examine the ability to perform these experiments in harsh environments; we investigate the methods by which the resulting deformation from indentation can be quantified and correlated to computational simulations, and we examine the onset of plasticity during indentation testing. First, nanoindentation was utilized to induce fracture of brittle thin oxide films on compliant substrates. During the indentation, a load is applied and the penetration depth is continuously measured. A sudden discontinuity, indicative of film fracture, was observed upon the loading portion of the load-depth curve. The mechanical properties of thermally grown oxide films on various substrates were ...

Science.gov (United States)

The transcriptional silencing of some cell cycle inhibitors and tumor suppressors, such as p16 and retinoic acid receptor beta(2), by DNA hypermethylation at CpG islands is commonly found in human oral squamous carcinoma cells. We examined the effects of the DNA methyltransferase inhibitor 5-Aza-2'-deoxycytidine (5-Aza; 0.25 mg/kg body weight), all-trans retinoic acid (RA; given at 100 microg/kg body weight and 1 mg/kg body weight), and the combination of 5-Aza and the low-dose RA on murine oral cavity carcinogenesis induced by the carcinogen 4-nitroquinoline 1-oxide (4-NQO) in a mouse model. All the drug treatments were done for 15 weeks after a 10-week 4-NQO treatment. Mice in all drug treatment groups showed decreases in the average numbers of neoplastic tongue lesions. The combination of 5-Aza and RA effectively attenuated tongue lesion severity. Although all drug treatments limited the increase in the percentage of proliferating cell ...

UK PubMed Central (United Kingdom)

BackgroundBaculovirus, which has a width of 40 nm and a length of 250-300 nm, can display functional peptides, receptors and antigens on its surface by their fusion with a baculovirus...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The surface enhanced Raman scattering (SERS) spectra of piperidine in silver colloid solution, on roughened silver electrode and on roughened silver electrode modified with silver nanoparticles were studied, and the high-quality SERS spectra of piperidine on roughened silver electrode modified with silver nanoparticles were obtained for the first time. Surface selection rules derived from the EM enhancement model were employed to deduce piperidine orientations on the different surfaces. On the basis of this, two models of piperidine adsorbed on the surface of the silver nanoparticles were built, and DFT-B3PW91/LanL2dz was applied to calculate the Raman frequencies. It proves that, at higher potential values, the piperidine is perpendicularly standing on the roughened silver electrode surface though its lone-electron pair, but in silver colloid solution and on the silver nanoparticles modified silver ...

UK PubMed Central (United Kingdom)

Severe acute respiratory syndrome (SARS) is an infectious disease caused by a novel coronavirus that cost nearly 800 lives. While there have been no recent outbreaks of the disease, the threat...Full Text Available

British Library Electronic Table of Contents (United Kingdom)

The removal of Ni(II) from aqueous solution by magnetic nanoparticles prepared and impregnated onto tea waste (Fe3O4-TW) from agriculture biomass was investigated. Magnetic nanoparticles (Fe3O4) were prepared by chemical precipitation of a Fe^2^+ and Fe^3^+ salts from aqueous solution by ammonia solution. These magnetic nanoparticles of the adsorbent Fe3O4 were characterized by surface area (BET), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and Fourier Transform-Infrared Spectroscopy (FT-IR). The effects of various parameters, such as contact time, pH, concentration, adsorbent dosage and temperature were studied. The kinetics followed is first order in nature, and the value of rate constant was found to be 1.90x10^-^2min^-^1 at 100mgL^-^1 and 303K. Removal ef...

UK PubMed Central (United Kingdom)

BackgroundAntigen sparing and cross-protective immunity are regarded as crucial in pandemic influenza vaccine development. Both targets can be achieved by adjuvantation strategy...Full Text Available

UK PubMed Central (United Kingdom)

Clinical applications of genetic therapies, including delivery of short, interfering RNAs (siRNAs) for RNA interference (RNAi), are limited due to the difficulty of delivering nucleic acids...Full Text Available

UK PubMed Central (United Kingdom)

BackgroundParticulate systems are well known to be able to deliver drugs with high efficiency and fewer adverse side effects, possibly by endocytosis of the drug carriers. On the...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

SnO{sub 2}-carbon nanotube (CNT) composite sheets are synthesized using poly(vinylpyrrolidone) to uniformly load a monolayer of SnO{sub 2} nanoparticles onto the surfaces of CNTs and CNT bundles within cross-stacked CNT sheets. When they are used as high-capacity (over 850 mA h g{sup -1}) and binder-free anodes in rechargeable lithium-ion batteries, they exhibit good cycle performance. (Abstract Copyright [2009], Wiley Periodicals, Inc.)

International Nuclear Information System (INIS)

Based on the results obtained for C-N and Si-C-N films, a systematic investigation of reactive magnetron sputtering of hard quaternary Si-B-C-N materials has been carried out. The Si-B-C-N films were deposited on p-type Si(100) substrates by dc magnetron co-sputtering using a single C-Si-B target (at a fixed 20% boron fraction in the target erosion area) in nitrogen-argon gas mixtures. Elemental compositions of the films, their surface bonding structure and mechanical properties, together with their oxidation resistance in air, were controlled by the Si fraction (5-75%) in the magnetron target erosion area, the Ar fraction (0-75%) in the gas mixture, the rf induced negative substrate bias voltage (from a floating potential to -500 V) and the substrate temperature (180-350 deg. C). The total pressure and the discharge current on the magnetron target were held constant at 0.5 Pa and 1 A, respectively. The energy and flux of ions bombarding the ...

Energy Technology Data Exchange (ETDEWEB)

A hydrous oxide film for the application as dielectric film is synthesized by immersion of pure aluminum in hot water. From a Rutherford backscattering analysis, the ratio of aluminum to oxygen atoms was found to be 3:2 in the anodized aluminum oxide film, and 2:1 in the hydrous oxide layer. Anodization of the hydrous oxide layer was more effective for the transition of amorphous anodic oxides to the crystalline aluminum oxides.

Energy Technology Data Exchange (ETDEWEB)

The novel optical, electronic, and/or magnetic properties of metal and semiconductor nanoparticles have resulted in extensive research on new methods for their preparation. An ideal preparation method would allow the particle size, size distribution, crystallinity, and particle shape to be easily controlled, and would be applicable to a wide variety of material systems. Numerous preparation methods have been reported, each with its inherent advantages and disadvantages; however, an ideal method has yet to emerge. The most widely applied methods for nanoparticle preparation include the sonochemical reduction of organometallic reagents,(1&2) the solvothermal method of Alivisatos,(3) reactions in microemulsions,(4-6) the polyol method (reduction by alcohols),(7-9) and the use of polymer and solgel materials as hosts.(10-13) In addition to these methods, there are a variety of methods that take advantage of the unique properties of a ...

Science.gov (United States)

Treatment Induced Hypertension

Science.gov (United States)

Objectives: We have previously shown that chronic exposure to ambient fine particulate matter (less than 2.5 ?m in aerodynamic diameter, PM(2.5)) pollution in conjunction with high-fat diet induces insulin resistance through alterations in inflammatory pathways. In this study we evaluated the effects of PM(2.5) exposure over a substantive duration of a rodent's lifespan and focused on the impact of long-term exposure on adipose structure and function.Methods and Results: C57BL/6 mice were exposed to PM(2.5) or filtered air (FA) (6 hours/day, 5 days/week) for duration of 10 months in Columbus, OH. At the end of the exposure, PM(2.5)-exposed mice demonstrated insulin resistance (IR) and a decrease in glucose tolerance compared with the FA-exposed group. Although there were no significant differences in circulating cytokines between PM(2.5)- and FA-exposed groups, circulating adiponectin and leptin were significantly decreased in PM(2.5)-exposed group. PM(2.5) ...

UK PubMed Central (United Kingdom)

The oxidative stress theory of aging predicts that manipulations that alter oxidative stress/damage will alter aging. The gold standard for determining whether aging is altered is lifespan,...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Short communication.

International Nuclear Information System (INIS)

Short communication.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

... Accession Number : ADD257320. Title : Sputter Deposition of Yttrium-Oxides. Descriptive Note : Journal article,. Corporate ...

Energy Technology Data Exchange (ETDEWEB)

Chemical oxidation is a treatment technology that uses powertul chemical oxidizers to destroy organic contaminants. Typical oxidizers used in chemical oxidation processes include ozone, hydrogen peroxide, chlorine, and potassium permanganate. The chemical reaction products are usually simple organic compounds, such as carboxylic acids, and/or inorganic compounds, such as carbon dioxide, water, and simple inorganic complexes (e.g., chloride salts, in the case of chemical oxidation treatment of chlorinated solvents).

Energy Technology Data Exchange (ETDEWEB)

Metal nanoparticles have many potential technological applications. Biological routes to the synthesis of these particles have been proposed including production by vascular plants, known as phytoextraction. While many studies have looked at metal uptake by plants, particularly with regard to phytoremediation and hyperaccumulation, few have distinguished between metal deposition and metal salt accumulation. This work describes the uptake of AgNO{sub 3}, Na{sub 3}Ag(S{sub 2}O{sub 3}){sub 2}, and Ag(NH{sub 3}){sub 2}NO{sub 3} solutions by hydroponically grown Brassica juncea and the quantitative measurement of the conversion of these salts to silver metal nanoparticles. Using X-ray absorption near edge spectroscopy (XANES) to determine the metal speciation within the plants, combined with atomic absorption spectroscopy (AAS) for total Ag, the quantity of reduction of Ag{sup I} to Ag{sup 0} is reported. Transmission electron microscopy (TEM) ...

International Nuclear Information System (INIS)

Ultraviolet (UV) upconversion (UC) luminescence in Yb3+/Er3+-codoped yttrium oxide (Y2O3) nanocrystals can be enhanced by orders of magnitude via tridoping further with Li+ ions under diode laser excitation of 970 nm. Sensitized three-photon UC radiations at 390 and 409 nm, corresponding to the 4G11/2?4I15/2 and 4H9/2?4I15/2 of Er3+ ions, respectively, present an enhancement time of about 33 times, which is larger than the 24 times enhancement for the UC green radiation. The UV UC radiation at 320 nm that corresponds to the 2P3/2?4I15/2 of Er3+ ions has also been greatly enhanced. Theoretical calculations interpret that all the observed enhancement times of UV UC radiations arise from the prolonged lifetimes of their intermediate states.

DEFF Research Database (Denmark)

There is increasing evidence that chemicals/test substances cannot only have adverse effects, but that there are many substances that can (also) have a beneficial effect on health. As this journal regularly publishes papers in this area and has every intention in continuing to do so in the near future, it has become essential that studies reported in this journal reflect an adequate level of scientific scrutiny. Therefore a set of essential characteristics of studies has been defined. These basic requirements are default properties rather than non-negotiables: deviations are possible and useful, provided they can be justified on scientific grounds. The 10 basic requirements for a scientific paper reporting antioxidant, antimutagenic or anticarcinogenic potential of test substances in in vitro experiments and animal studies in vivo concern the following areas: (1) Hypothesis-driven study design; (2) The nature of the test substance; (3) Valid and invalid test systems; (4) The selection ...

Energy Technology Data Exchange (ETDEWEB)

Poly(methyl methacrylate), PMMA, Acrigel, a Brazilian polymer, is used in the manufacture of medical supplies sterelizable by ionizing radiation. However, when PMMA is gamma-irradiated it undergoes main chain scissions, which promote molecular degradation causing reduction in its mechanical properties. Therefore, radiolytic of PMMA is important for it to become commercially radiosterizable. In this work some commercial additives, originally used in photo-and thermo-oxidate stabilization of polymers, were tested. Only two additives, type HALS (Hindered Amine Light Stabilizer), denoted Scavenger, showed a good protective quality. The investigation of radiation-induced main scissions was carried out by viscosimetric method. The most effective additive, added to the polymer system at 0.3 w/w%, promotes a great molecular radioprotection of 93%. That means a reduction of G-value (scissions/100 eV) from 0.611 to 0.053. In addition, the glassy ...

Science.gov (United States)

Erectile dysfunction following radical prostatectomy remains a frequent problem despite the development of nerve-sparing techniques. This erectile dysfunction is believed to be neurogenic, enhanced by hypoxia-induced structural changes which result in additional veno-occlusive dysfunction. Recently, daily use of intracavernous vasoactive substances and oral use of PDE5-inhibitors have been clinically studied for treatment of postprostatectomy erectile dysfunction. Since these studies showed benefits of "penile rehabilitation therapy," these effects have been studied in a preclinical setting. We reviewed experimental literature on erectile tissue preserving and neuroregenerative treatment strategies, and found that preservation of the erectile tissue by the use of intracavernous nitric oxide donors or vasoactive substances, oral PDE5-inhibitors, and hyperbaric oxygen therapy improved erectile function by antifibrotic effects and preservation of ...

Energy Technology Data Exchange (ETDEWEB)

The pitting behavior of Alloy 800 was investigated as a function of temperature and prefilming in high temperature water. The pitting behavior was characterized in terms of the pitting potential and the pit density. The pitting potential decreases with increasing temperature and chloride activity. Prefilming of test coupons over a time period between 100 and 5,000 hours in ammoniated water at 300 C has no apparent influence on the pitting potential at room temperature, 180 C and 300 C. However, the number of pits in prefilmed coupons is much higher than in coupons covered with an air passive layer. The effect of prefilming on pit nucleation was investigated in more detail with regard to a model and test methods developed by Bianchi and co-workers. Density of pits in prefilmed coupons is at least one order of magnitude higher than in air passive coupons. Maximum pit density was measured after a prefilming period of 1 00 hours. The effect is discussed in terms of Bianchi`s model and in ...

Energy Technology Data Exchange (ETDEWEB)

The diffusion of ion beam injected self-interstitials (I) and their interaction with impurities in crystalline Si has been investigated and modeled. In particular, the I-substitutional carbon (C) interactions have been studied, using a molecular-beam-epitaxy grown Si{sub 1-y}C{sub y} layer interposed between the shallow I-source and a deeper B-spike (marker for I-concentration). Substitutional C atoms are shown to trap I's, to be removed from their substitutional sites, and to form stable precipitates into the C-rich region. The I-trapping mechanism was quantitatively studied by a simulation code. The reactions causing trapping and deactivation are described. In addition, the boron markers approach was extended to the two dimensional (2D) diffusion. High resolution scanning capacitance microscopy was used for quantitative measurements of the 2D boron transient enhanced diffusion induced on a boron delta array by the I's ion beam injected through a ...

Energy Technology Data Exchange (ETDEWEB)

In this paper, we propose to characterize boron transient enhanced diffusion (TED) for processes currently used for P{sup +}/N ultra-shallow junctions (USJ) fabrication. Indeed, the fundamental understanding of boron diffusion for low energy boron implantation is mandatory to evaluate the scalability of such processes for the coming complementary metal-oxide-semiconductor (CMOS) transistor generations. In these experiments, we characterize the boron anomalous diffusion, thanks to boron buried marker-layers obtained by epitaxial growth. B{sup +} and BF{sub 2}{sup +} ultra-low energy (ULE) implantations and plasma doping (PLAD) using BF{sub 3} as precursor gas are carried out to compare the two techniques used for advanced USJ fabrication. Boron diffusion behaviors are analyzed via secondary ion mass spectrometry for annealing at 700 deg. C for 5 min and 15 min. Finally this paper brings some physical insights explaining the technological benefit coming from PLAD ...

International Nuclear Information System (INIS)

To elucidate the mechanism of sunlight-induced skin damage, guinea pigs exposed to UV light (280-320 nm, UV B, 4J/cm"2) and a homogenate of the epidermis was examined by means of the thiobarbituric acid (TBA) test. Three hours after the exposure, TBA-malondialdehyde adducts had increased while glutathione reductase activity had decreased, indicating lipid peroxidation. To detect the initial species, spin trapping with 5,5-dimethyl-1-pyrroline-N-oxide (DMPO) was applied to a suspension of illuminated epidermal cells (0.5 J/cm"2). An ESR signal obtained only with irradiation comprised a 1 : 2 : 2 : 1 quartet [a (N) =a (#beta#H) =1.49 mT] attributable to a spin adduct of hydroxyl radicals. These results suggest that sunlight exposure of skin may lead to hydroxyl radical generation and simultaneous lipid peroxidation. (author).

Science.gov (United States)

Metabolic engineering of photosynthetic organisms is required for utilization of light energy and for reducing carbon emissions.Control of transcriptional regulators is a powerful approach for changing cellular dynamics, because a set of genes is concomitantly regulated. Here, we show that overexpression of a group 2 ? factor, SigE, enhances the expressions of sugar catabolic genes in the unicellular cyanobacterium, Synechocystis sp. PCC 6803. Transcriptome analysis revealed that genes for the oxidative pentose phosphate pathway and glycogen catabolism are induced by overproduction of SigE. Immunoblotting showed that protein levels of sugar catabolic enzymes, such as glucose-6-phosphate dehydrogenase, 6-phosphogluconate dehydrogenase, glycogen phosphorylase, and isoamylase, are increased. Glycogen levels are reduced in the SigE-overexpressing strain grown under light. Metabolome analysis revealed that metabolite levels of the TCA cycle and ...

Energy Technology Data Exchange (ETDEWEB)

In our previous work, we demonstrated that biomass-generated producer gas can be converted to ethanol and acetic acid using a microbial catalyst Clostridium carboxidivorans P7{sup T}. Results showed that the producer gas (1) induced cell dormancy, (2) inhibited H{sub 2} consumption, and (3) affected the acetic acid/ethanol product distribution. Results of this work showed that tars were the likely cause of cell dormancy and product redistribution and that the addition of a 0.025{mu}m filter in the gas cleanup negated the effects of tars. C. carboxidivorans P7{sup T} can adapt to the tars (i.e. grow) only after prolonged exposure. Nitric oxide, present in the producer gas at 150ppm, is an inhibitor of the hydrogenase enzyme involved in H{sub 2} consumption. We conclude that significant conditioning of the producer gas will be required for the successful coupling of biomass-generated producer gas with fermentation to produce ethanol and acetic ...

Energy Technology Data Exchange (ETDEWEB)

Bacteriophage M13 mp10 DNA were irradiated with near-UV light in the presence of tetracycline derivatives and primed with synthetic oligonucleotide to be used for DNA synthesis using Escherichia coli DNA polymerase. Chain terminations were observed by denaturing polyacrylamide gel electrophoresis and mapped precisely. All the synthesis stops occurred before or at the level of guanine residues, showing that the photoreaction mediated by tetracycline derivatives led to a preferential alteration of guanine residues. These lesions were demonstrated to be induced in DNA through a pathway involving singlet oxygen. Tetracycline derivatives also photoinduced the breakage of the DNA sugar-phosphate backbone monitored by the conversion of supercoiled phi X174 DNA to a relaxed form. This lesion was shown to be initiated by hydroxyl radicals. The production of this free radical has been confirmed by electron paramagnetic resonance (EPR) spin trapping experiments using ...

Energy Technology Data Exchange (ETDEWEB)

This paper contains literature from American Power Conference Air Toxics Being Measured Accurately, Controlled Effectively NO{sub x} and SO{sub 2} Emissions Reduced; Surface Condensers Improve Heat Rate; Usable Fuel from Municipal Solid Waste; Cofiring Technology Reduces Gas Turbine Emissions; Trainable, Rugged Microsensor Identifies of Gases; High-Tc Superconductors Fabricated; High-Temperature Superconducting Current Leads; Vitrification of Low-Level Radioactive and Mixed Wastes; Characterization, Demolition, and Disposal of Contaminated Structures; On-Line Plant Diagnostics and Management; Sulfide Ceramic Materials for Improved Batteries; Flywheel Provides Efficient Energy Storage; Battery Systems for Electric Vehicles; Polymer-Electrolyte Fuel Cells for Transportation; Solid-Oxide Fuel Cells for Transportation; Surface Acoustic Wave Sensor Monitors Emissions in Real-Time; Advance Alternative-Fueled Automotive Technologies; Thermal & Mechanical Process; ...

Energy Technology Data Exchange (ETDEWEB)

The aim of this work is to be able to describe transformations, occurring when solids and gases are in non isothermal and non isobaric conditions, with kinetic models. A methodology has been used. Two essential processes have to be taken into account: the germination and the growth. The germs are supposed to be formed (at constant temperature and pressure) in the grains surface with a constant velocity by surface unit, (gamma), called germination surface frequency (number of germs.m{sup -2}.s{sup -1}. The growth velocity is characterized by a growth surface reactivity, (phi) (in mol.m{sup -2}.s{sup -1}). With an appropriate transformation model, it is possible to obtain the variations of (gamma) and (phi) in terms of the temperature and pressure which are then used in the calculation of the velocity in non isothermal and non isobaric conditions. In order to validate the developed method, two reactions have been studied. For the first one, the kaolinite de-hydroxylation, an anisotropic ...

International Nuclear Information System (INIS)

This study was designed to evaluate the influence of inhalational agents on the intestinal circulation in an isolated loop preparation. Sixty dogs were studied, using three intestinal segments from each dog. Selected intestinal segments were pumped with aortic blood at a constant pressure of 100 mmHg. A mixture of _8_6Rb and 9-microns spheres labeled with "1"4"1Ce was injected into the arterial cannula supplying the intestinal loop, while mesenteric venous blood was collected for activity counting. A very strong and significant correlation was found between rubidium clearance and microsphere entrapment (r = 0.97, P less than 0.0001). Nitrous oxide anesthesia was accompanied by a higher vascular resistance (VR), lower flow (F), rubidium clearance (Cl-Rb), and microspheres entrapment (Cl-Sph) than pentobarbital anesthesia, indicating that the vascular bed in the intestinal segment was constricted and flow (total and nutritive) decreased. Halothane, enflurane, and ...

International Nuclear Information System (INIS)

The CaWO_4:Ln"3"+ SiO_2 (Ln=Tb, Dy and Ho) nanoparticles were synthesized via a combustion process at 800 "oC, using citric acid as chelating agent and fuel, ammonium nitrate as fuel, boric acid as flux material and silica as supports. The persistent phosphor nanoparticles were characterized by X-ray diffraction (XRD), reflectance UV-vis and fluorescence spectroscopy (PL) and transmission electron microscopy (TEM) techniques. XRD patterns indicated that crystalline calcium tungstate with scheelite structure was produced. The reflectance UV-vis spectra showed the broad absorption band of WO_4"2"- groups and the PL spectra showed the WO_4"2"- wide excitation band, broad emission band of WO_4"2"- and characteristic emissions of Ln"3"+ ions. The average particle sizes were determined by TEM, which are about 50 nm.