Impacts of membrane properties on reactive dye removal from dye/salt mixtures by asymmetric cellulose acetate and composite polyamide nanofiltration membranes  

British Library Electronic Table of Contents (United Kingdom)

This paper aims to study fundamentally the impacts of membrane properties on the reactive dye removal from dye/salt mixtures by nanofiltration membranes. To begin with, two types of nanofiltration membranes of similar pore size, namely asymmetric cellulose acetate membrane and thin-film composite polyamide membrane were fabricated, and their key physical, chemical and performance properties were characterized. After that, these resultant membranes were employed to perform dye removal experiments with aqueous solutions of reactive black 5 and NaCl under different operational parameters. The dye removal rate and steady permeate flux were determined and correlated with the measured membrane properties. It was found that there were significant differences between the dye removal performances o...

2010-01-01

2

Sulfonated poly(ether ether ketone) based composite membranes for nanofiltration of acidic and alkaline media  

British Library Electronic Table of Contents (United Kingdom)

Several thin film composite nanofiltration membranes have been prepared by spin coating a sulfonated poly(ether ether ketone) solution on a polyethersulfone support, followed by thermal treatment. The most optimal developed nanofiltration membrane shows a clean water permeance of ~4.5Lm^-^2h^-^1bar^-^1 and a molecular weight cut off (MWCO) of ~500gmol^-^1. No irreversible changes in membrane performance have been observed after prolonged exposure (up to several weeks) of this membrane to solutions with a pH in the range 0-14. Compared to Desal-5-DK, the developed membrane displays a similar water permeance and a higher NaCl retention. In comparison to commercially available pH stable membranes, MPF-34 and NP030P, it reveals a higher water permeance. Permeance and MWCO analysis at varying p...

2011-01-01

3

Study on polyamide thin-film composite nanofiltration membrane by interfacial polymerization of polyvinylamine (PVAm) and isophthaloyl chloride (IPC)  

British Library Electronic Table of Contents (United Kingdom)

A novel thin-film composite polyamide nanofiltration membrane was prepared through interfacial polymerization of polymeric polyamine polyvinylamine (PVAm) with isophthaloyl chloride (IPC) on a polysulfone supporting film. The composite membranes were prepared under different conditions and characterized in terms of chemical and morphological structures, surface zeta potential, pure water permeability, and rejection to different solutes including electrolytes and sucrose. The results showed that the membrane performance was significantly affected by the content of amine units of PVAm and the concentrations of PVAm and IPC. The increase of the content of amine units of PVAm and the concentration of IPC resulted in an augment in salt rejection and a decrease in permeability, while the increas...

2011-01-01