International Nuclear Information System (INIS)

In this study nanocrystalline powders of yttria-stabilized zirconia (ZrO_2-8Y_2O_3) have been synthesized through 'polymerized complex method'. Zirconium chloride, yttrium nitrate, citric acid and ethylene glycol were polymerized at 80 "oC to produce a gel-like mass in which metallic ions were uniformly distributed. During the thermal treatment of dried gel, nanocrystalline powder was formed at 450 "oC and 650 "oC for 2 h. Thermal reactions and crystalline phase formation of the dried gel were investigated through thermal analysis and X-ray diffraction analysis, respectively. The results of thermal analysis and XRD showed the formation of nanocrystalline powder at less than 600 "oC. Chemical bonding of the dried gel was investigated by Fourier transform infrared spectroscopy analysis. Morphology of powder calcined at 650 "oC was analyzed by scanning electron microscope. ...

International Nuclear Information System (INIS)

Highly conductive biaxially textured RuO_2 thin films were deposited on technically important SiO_2/Si substrates by pulsed laser deposition, where yttria-stabilized zirconia (YSZ) produced by ion-beam-assisted-deposition (IBAD) was used as a template to enhance the biaxial texture of RuO_2 on SiO_2/Si. The biaxially oriented RuO_2 had a room-temperature resistivity of 37 #mu##OMEGA#-cm and residual resistivity ratio above 2. We then deposited Ba_0_._5Sr_0_._5TiO_3 thin films on RuO_2/IBAD-YSZ/SiO_2/Si. The Ba_0_._5Sr_0_._5TiO_3 had a pure (111) orientation normal to the substrate surface and a dielectric constant above 360 at 100 kHz. copyright 1998 Materials Research Society.

International Nuclear Information System (INIS)

Yttria stabilized zirconia (YSZ) with 8 mol% Y was deposited by reactive magnetron sputtering onto oxidized (100) silicon substrates. It was possible to switch film texture from (111) to (200) by applying a strong RF substrate bias. Transmission electron microscopy showed that the film deposited under bias is porous and exhibits nanoscaled grains, whereas the film deposited without bias is dense and columnar. The ionic conductivity as a function of temperature revealed an activation energy of 1.04 eV. The mechanical stress could be tuned to low values by thermal post-annealing. Using the dense (111) film as electrolyte layer, and the porous (200) film as an interlayer to a porous Pt anode, an open circuit voltage of 0.85 V was obtained in a micro machined fuel cell structure.

Energy Technology Data Exchange (ETDEWEB)

The project has been developing Yttria Stabilized Zirconia (YSZ)-Alumina Composites as an electrolyte of a self-support type planar Solid Oxide Fuel Cell (SOFC) from the following points of view: a path of alumina particles with high thermal conductivity can be designed as an electrolyte sheet; there are some possibilities that the electrolyte can be enhanced in mechanical strength. As previously reported, these composite materials have higher mechanical strength and better thermal shock resistance than those of YSZ. These composites containing 0-30 wt% of Al[sub 2]O[sub 3] were measured by AC impedance method at temperatures of 250-1,000[degree]C. Electrical conductivities of 8YSZ without Al[sub 2]O[sub 3] and a composite consisting of 80 wt% YSZ and 20 wt%Al[sub 2]O[sub 3] as sintered samples were 1.2 x 10[sup -1]S/cm and 1.0 x 10[sup -1]S/cm respectively at 1,000[degree]C. The composite containing 20 wt% of Al[sub ...

British Library Electronic Table of Contents (United Kingdom)

One of the major limitations of the nickel (Ni) - yttria-stabilized zirconia (YSZ) anode support for solid oxide fuel cells (SOFC) is its low capability to withstand transients between reducing and oxidizing atmospheres (''RedOx'' cycle), owing to the Ni-to-NiO volume expansion. This work presents results on different anode supports fabricated by tape casting. Three compositions are prepared, as the outcome of a preceding design of experiment approach. The NiO proportion is 40, 50 and 60wt% of the anode composite. The anode support characteristics like shrinkage during sintering, in-situ conductivity at high temperature, electrochemical performance and tolerance against RedOx cycles have been measured. Performance up to 0.72Wcm^-^2 (0.62V, 800^oC) is recorded for the 60wt% NiO sample on sm...

Energy Technology Data Exchange (ETDEWEB)

NO{sub x} compounds, specifically NO and NO{sub 2}, are pollutants and potent greenhouse gases. Compact and inexpensive NO{sub x} sensors are necessary in the next generation of diesel (CIDI) automobiles to meet government emission requirements and enable the more rapid introduction of more efficient, higher fuel economy CIDI vehicles. Because the need for a NO{sub x} sensor is recent and the performance requirements are extremely challenging, most are still in the development phase. Currently, there is only one type of NO{sub x} sensor that is sold commercially, and it seems unlikely to meet more stringent future emission requirements. Automotive exhaust sensor development has focused on solid-state electrochemical technology, which has proven to be robust for in-situ operation in harsh, high-temperature environments (e.g., the oxygen stoichiometric sensor). Solid-state sensors typically rely on yttria-stabilized zirconia (YSZ) as the ...

British Library Electronic Table of Contents (United Kingdom)

Spherical nano-sized YSZ (yttria stabilized ZrO2) powders were successfully synthesized via a reverse microemulsion system. The water droplets in the microemulsion system of yclohexane/water/span85/Triton X-100/hexyl alcohol can act as the nano-reactors which solubilize zirconium oxychloride and ammonia water separately. The minute original reactors are favor to the formation of nano-sized spherical YSZ powders and the dispersibility of the powders can be controlled effectually by adjusting the weight ratio of the LiNO3 molten salt to the precursor. The phase transformation from cubic to monoclinic starts at and 500??C and finally monoclinic and cubic phase with increased crytallinity coexist at 800??C. The effect of LiNO3 molten salt in the formation of YSZ powders was also discussed.

UK PubMed Central (United Kingdom)

PURPOSEThe purpose of this study was to compare the linear sintering behavior of presintered zirconia blocks of various densities. The mechanical properties of the resulting sintered...Full Text Available

KoreaScience (Korea)

Full Text Available

British Library Electronic Table of Contents (United Kingdom)

Mesoporous films of platinized carbon nanotube-zirconia-Nafion composite have been used for the immobilization of tris(2,2prime-bipyridyl)ruthenium (II) (Ru(bpy)32+) on an electrode surface to yield a solid-state electrogenerated chemiluminescence (ECL) sensor. The composite films of Pt-CNT-zirconia-Nafion exhibit much larger pore diameter (3.55 nm) than that of Nafion (2.82 nm) and thus leading to much larger ECL response for tripropylamine (TPA) because of the fast diffusion of the analyte within the films. Due to the conducting and electrocatalytic features of CNTs and Pt nanoparticles, their incorporation into the zirconia-Nafion composite films resulted in the decreased electron transfer resistance within the films. The present ECL sensor based on the Pt-CNT-zirconia-Nafion gave a lin...

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline and nanostructured materials offer unique microstructure-dependent properties that are superior to coarse-grained materials. These materials have been shown to have very high hardness, strength, and wear resistance. However, most current methods of producing nanostructured materials in weapons-relevant materials create powdered metal that must be consolidated into bulk form to be useful. Conventional consolidation methods are not appropriate due to the need to maintain the nanocrystalline structure. This research investigated new ways of creating nanocrystalline material, new methods of consolidating nanocrystalline material, and an analysis of these different methods of creation and consolidation to evaluate their applicability to mesoscale weapons applications where part features are often under 100 {micro}m wide and the material's microstructure must be very small to give ...

UK PubMed Central (United Kingdom)

BackgroundTitanium and titanium alloys are widely used for fabrication of dental implants. Since the material composition and the surface topography of a biomaterial play a fundamental...Full Text Available

UK PubMed Central (United Kingdom)

BackgroundOsseointegration is crucial for the long-term success of dental implants and depends on the tissue reaction at the tissue-implant interface. Mechanical properties and biocompatibility...Full Text Available

International Nuclear Information System (INIS)

Parameters of permanent magnets result from the combination of intrinsic properties such as saturation magnetization, magnetic exchange, and magnetocrystalline energy, as well as microstructural parameters such as phase structure, grain size, and orientation. Reduction of grain size into nanocrystalline regime (#approx# 50 nm) leads to the enhanced remanence which derives from ferromagnetic exchange coupling between highly refined grains. In this study the fundamental phenomena, quantities, and structure parameters, which define nanophase permanent magnets are presented and discussed. The theoretical considerations are confronted with experimental data for nanocrystalline Sm-Fe-N type permanent magnets. (author)

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline zeolites with discrete crystal sizes of less than 100 nm have different properties relative to zeolites with larger crystal sizes. Nanocrystalline zeolites have improved mass transfer properties and very large internal and external surface areas that can be exploited for many different applications. The additional external surface active sites and the improved mass transfer properties of nanocrystalline zeolites offer significant advantages for selective catalytic reduction (SCR) catalysis with ammonia as a reductant in coal-fired power plants relative to current zeolite based SCR catalysts. Nanocrystalline NaY was synthesized with a crystal size of 15-20 nm and was thoroughly characterized using x-ray diffraction, electron paramagnetic resonance spectroscopy, nitrogen adsorption isotherms and Fourier Transform Infrared (FT-IR) spectroscopy. Copper ions were exchanged into ...

International Nuclear Information System (INIS)

Recent advances made in the area of amorphous and nanocrystalline alloys exhibiting high saturation inductions are reviewed. A new chemical composition was identified that achieves a saturation induction of 1.64 T in an iron-based amorphous alloy. This alloy, when used in electrical transformers, shows a much improved performance over the existing amorphous alloy. Nanocrystalline FeCoCuNbSiB alloys are found to have saturation induction levels reaching 1.7 T. These materials are suited for use in sensors and inductors carrying large currents. Some of these nanocrystalline alloys show a BH squareness ratio exceeding 90%, which can be utilized in pulse power devices. Recent developments in the applications of these materials are also pointed out.

International Nuclear Information System (INIS)

ZrO_2/O'-sialon composites were obtained via reaction sintering of ZrSiO_4 and Si_3N_4 powders at about 1700 deg C. Y_2O_3 was effective in both stabilizing of zirconia and densifying the composites. However, it is not easy to select an optimum value of the single additive to balance these two requirements simultaneously. With low Y_2O_3 addition, some tetragonal zirconia grains in the sintered samples are transformable during mechanical grinding but the full densification of the material is then sacrificed. On the other hand, addition more Y_2O_3 to achieve complete densification results in the zirconia being stabilized into undesirable t' or cubic forms. Therefore no improved toughening effects have been achieved in the composites. Heat-treatment of the materials at 1400 deg C. results in the diffusion of yttria from the grain boundary phase to zirconia and the formation of the O'-cubic ...

Energy Technology Data Exchange (ETDEWEB)

This report contains detailed information of the research program entitled "Development of Bulk Nanocrystalline Cemented Tungsten Carbide Materials for Industrial Applications". The report include the processes that were developed for producing nanosized WC/Co composite powders, and an ultrahigh pressure rapid hot consolidation process for sintering of nanosized powders. The mechanical properties of consolidated materials using the nanosized powders are also reported.

International Nuclear Information System (INIS)

Zirconia-toughened sialon composites have been fabricated using conventional hot-pressing techniques. The fracture toughness and microstructure were determined for CeO_2- and Y_2O_3-stabilized ZrO_2 additives and also as a function of volume percent ZrO_2. The Yttria system showed a linear increase in fracture toughness with increasing volume fraction zirconia content while the ceria-stabilized system exhibited a peak in fracture toughness at 20 vol% ZrO_2 content. The fracture toughness at 800 C was measured and correlated with the microstructure. High-temperature stability was determined and it was found that the deleterious nitride phases of zirconium could be precluded from the microstructure.

International Nuclear Information System (INIS)

New data about the structure of high-temperature resistant metalloceramic plasma sprayed coatings in micro and nano areas are presented. Application of the new instrumental methods: transmission electron microscopy combined with selected area electron diffraction mode is possible to obtain these data. The first layer in Ni based metallic bond coat shows nanocrystalline structure. External ceramic layer based on stabilised ZrO_2 is polycrystalline and contains both cubic and tetragonal crystalline phases. Local inhomogeneities in coatings phase composition are determined. (author)

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline processing by inert gas condensation has the inherent advantages of generating: (1) high surface area nanoclusters, (2) non-stoichiometric oxides, and (3) high dispersions of dopants. This approach is exploited in the synthesis of fluorite-structured catalysts for SO{sub 2} reduction by CO. Nanocrystalline CeO{sub 2{minus}x}, La-doped CeO{sub 2{minus}x}, and Cu-doped CeO{sub 2{minus}x} were produced by magnetron sputtering from a pure or mixed metal target, followed by controlled oxidation of the metallic clusters. The as-prepared doped and undoped nanocrystalline CeO{sub 2{minus}x} materials were found to be excellent catalysts for complete SO{sub 2} conversion to elemental sulfur. Undoped nanocrystalline CeO{sub 2{minus}x} enabled light-off at 460 C, a temperature {approximately} 120 C lower than that over polycrystalline CeO{sub 2}, which is a novel effective catalyst itself. The high ...

International Nuclear Information System (INIS)

Liquid radioactive raffinates from nuclear fuel reprocessing at the Idaho National Engineering and Environmental Laboratory were solidified, or calcines, in a fluidized bed reactor at approximately 500 C to form a dry granular material. This calcine has been provisionally stored near-surface in concrete-encased stainless steel bins at the Idaho Nuclear Technology Engineering Center. Research addressing the permanent immobilization of radioactive waste has been ongoing. One option is to separate the radioactive constituents from the calcine, thereby reducing the radioactive waste volume to be ultimately stored at a national nuclear waste repository. Nitric acid dissolution of the calcine is a key front-end unit operation in the separations option. In order to design calcine dissolution equipment, quantification of dissolution reaction rate parameters is required. A pilot-plant-produced, non-radioactive calcine was utilized to study the dissolution kinetics of a ...

International Nuclear Information System (INIS)

The concept of nanocrystal conversion chemistry, which involves the use of pre-formed nanoparticles as templates for chemical transformation into derivative solids, has emerged as a powerful approach for designing the synthesis of complex nanocrystalline solids. The general strategy exploits established synthetic capabilities in simple nanocrystal systems and uses these nanocrystals as templates that help to define the composition, crystal structure, and morphology of product nanocrystals. This article highlights key examples of 'conversion chemistry' approaches to the synthesis of nanocrystalline solids using a variety of techniques, including galvanic replacement, diffusion, oxidation, and ion exchange. The discussion is organized according to classes of solids, highlighting the diverse target systems that are accessible using similar chemical concepts: metals, oxides, chalcogenides, phosphides, alloys, intermetallic compounds, sulfides, and ...

British Library Electronic Table of Contents (United Kingdom)

In this work, a new sol-gel auto-combustion method has been performed to synthesize single phase nickel ferrite nanocrystalline powders by using n-cetyltrimethylammonium bromide, as a cationic surfactant. The gels were prepared from ferric and nickel nitrates and citric acid. Ammonia was used as pH adjusting agent as well. The effects of the surfactant on the after combustion calcination process and the reduction of the resulting powder crystallite size which affects the magnetic properties of the material were investigated by XRD and DTA/TGA techniques. The results showed that the ignition of the gels in air have a self-propagating behavior. Addition of surfactant to the starting solution affected the crystallite size of the synthesized powders and their phase constitution. The crystallit...

International Nuclear Information System (INIS)

The use of X-ray diffraction line profile analysis for the study of nanocrystalline powders is described. The fundamentals of the theory are presented in terms of crystallite/domain size, size distribution, lattice distortion, dislocations density and stacking faults. Line profile parameters and the methods of pattern fitting introduced to overcome the diffraction-line overlap problem are discussed. The approaches based of the integral breadth of the measured line profiles and the Fourier method are discussed. In addition, simplified approaches are also commented. Representative examples are selected to illustrate various cases of microstructure, such as nanomaterials with strain-free spherical nano crystallites, strain-free crystallites with anisotropic crystallite shape, anisotropic crystallites with microstrains and spherical crystallites with dislocation densities and crystallite size distributions. (author)

International Nuclear Information System (INIS)

The EXAFS-study (Fe, Sn and Ge K-edges) of disordered by mechanical activation binary supersaturated nanocrystalline solid solutions Fe-Al, Fe-Ge, Fe-Sn and Fe-Si is presented. The EXAFS-spectra are processed by solving the inverse binary problem, using the EXAFS-spectrum of the Fe K-edge only or combining the EXAFS-spectra on two K-edges, Fe and Ge or Fe and Sn. The parameters of partial correlation functions indicate chemical short-range ordering, high local static distortions in the lattice, increasing with metalloid content. The macrostructure of other type is forming through an initial, 'local' stage within the bcc lattice.

British Library Electronic Table of Contents (United Kingdom)

In the present work, bulk amorphous and nanocrystalline Al83Fe17 alloys were obtained by consolidation of mechanically alloyed powders. Mechanical alloying of Al-17% Fe powder mixture yielded powder with an amorphous structure. Thermal behaviour of the milling product was examined using differential scanning calorimetry. This investigation revealed that the amorphous phase crystallised above 380^oC. The amorphous powder was compacted under a pressure of 7.7GPa in different conditions: at 380^oC for 600s and at 1000^oC for 180s. Structural investigations of the bulk material revealed that the amorphous structure was retained after consolidation process applied at 380^oC. Compaction under high pressure at 1000^oC caused crystallisation of the amorphous phase and appearance of metastable nano...

International Nuclear Information System (INIS)

Iron oxide as sintering aid to Ce-TZP ceramics produces a beneficial effect on the tetragonal phase stabilization. It was found that ceria powder particle size of 2,0 #mu#m turns the grain-boundary electrical conductivity higher than ceria powder of smaller grain size. (author)

International Nuclear Information System (INIS)

Large, complex, high purity ceramic shapes are required by a variety of emerging technologies for their electrical insulation and high temperature strength properties coupled with their refractoriness and purity. Ceramic sealant bonding, using crystalline and vitreous sealant materials, has recently shown significant potential for joining technical ceramics to form the required shapes. Materials and techniques for joining technical ceramics including alumina, magnesia, zirconia and thoria are discussed. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Molecular dynamics computer simulations of a dense nanocrystalline Nickel sample are performed on the parallel Cray T3 (EPFL-Lausanne). The sample contains 50 grains with an average size of 3 nm. By perturbing the relaxed configuration elastic and plastic properties are studied. (author) 1 fig., 1 ref.

Energy Technology Data Exchange (ETDEWEB)

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutions of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controlled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle synthesis have been proposed.

Energy Technology Data Exchange (ETDEWEB)

Three dispersants (stearic acid, oleic acid, and poly-(12-hydroxystearic acid)) are compared for their ability to produce low-viscosity suspensions of zirconia in kerosene. Rheological measurements and sediment packing density measurements show that poly(12-hydroxystearic acid) is a better dispersant than stearic acid or oleic acid; this is explained in terms of the longer tail of the poly-(12-hydroxystearic acid) surfactant molecule. The amount of dispersant can be optimized to reduce viscosity and yield point of the suspension, and to eliminate thixotropic hysteresis. The use of a dispersion medium of lower viscosity than the dispersant makes it easy to detect when complete monolayer coverage has been achieved. The loss of pseudoplasticity, brought about by a higher degree of deflocculation, can be recovered by increasing the volume fraction of solids of a suspension and this is beneficial in the plastic forming of ceramics. Rheological measurements showed that ...

International Nuclear Information System (INIS)

A study has been made of the precipitation and growth processes which occur during cooling from solution treatment and under isothermal hold conditions in a magnesia-partially-stabilized zirconia alloy. Three types of precipitate have been identified which develop during cooling or during isothermal hold treatments just above and below the eutectoid temperature. These precipitate forms are termed (i) primary, (ii) large random, and (iii) secondary. Further precipitation, slow growth of existing precipitates, and subeutectoid decomposition result when an additional 1100"0C aging treatment is given to the previously cooled material. It is shown that type (iii) secondary precipitates from rapidly within the temperature range of 1300"0 to 1375"0C. The secondary precipitates are largely responsible for the improved room-temperature strength properties of the heat-treated samples. The formation and effects on mechanical properties of each type of precipitate are ...

International Nuclear Information System (INIS)

Ceramic matrix composites in the TiC-Ti, Y-TZP system can be synthesized by the reaction between carbon and the TiO_2-Y_2O_3-ZrO_2 solid solution nanopowder. This method results in the more homogeneous powders than those prepared by the physical mixing of TiC and zirconia s.s. powders. Twelve TiO_2-Y_2O_3-ZrO_2 solid solution nanopowders differing in the proportions of the constituent oxides were prepared by the coprecipitation- calcination route. They were reacted with the pyrolytic carbon evenly distributed within the system. Carbon was introduced by the thermal decomposition of the phenol-formaldehyde resin dissolved in ethyl alcohol and mixed with the zirconia s.s. nanopowder. Reaction was performed in vacuum. Compacts of the composite powders sintered in vacuum give dense materials of evenly distributed TiC inclusions of sizes not surpassing 400 nm. Hardness of such materials was dependent on their chemical and phase composition but was ...

Energy Technology Data Exchange (ETDEWEB)

A practical method to determine the ionic diffusion coefficient and activation energy by using quasielastic light scattering (QELS) is presented. It is shown that a temperature dependence curve of the QELS intensity at a fixed frequency can be well fitted by Jonscher's formula and that the diffusion parameters can be obtained from this curve fitting. This method is successfully applied not only to crystals with high optical quality, as reported earlier, but also to opaque ceramics, which are more important than the crystals from a practical point of view. The composition dependence of the ionic diffusion coefficient is studied in sintered YbSZ to show the usefulness of this method.

Science.gov (United States)

Catalytic testing of inorganic catalysts was continued with the highly active sulfate-modified zirconia catalyst prepared here. Using isobutanol as the only reactant over this catalyst, it was demonstrated that high conversion and selectivity to isobutene was achieved at 175[degrees]C. In addition, the high selectivity to isobutene, i.e. 79--86 mol%, was maintained at higher space velocities and higher temperatures. A high productivity of 11.35 mol isobutene was achieved at 225[degrees]C. Utilizing a methanol/isobutanol = 2/1 molar ratio reactant mixture over the ZrO[sub 2]/SO[sub 4][sup 2[minus

Energy Technology Data Exchange (ETDEWEB)

In support of the efforts to apply ceramics in advanced heat engines, a study was made of the sliding performance of ceramics at the ring/cylinder interface of low heat rejection engines. The objective was to understand the basic mechanisms controlling the wear of candidate ceramics and thereby identify means for applying these ceramics effectively. Attempts to operate three different zirconias, silicon carbide, silicon nitride, and several plasma-sprayed ceramic coatings without lubrication were unsuccessful because of high friction and high wear rates. Experiments using a polyalphaolefin lubricant at temperatures to 260 C identified several combinations having wear rates in the general range likely to be acceptable for engines. Plasma-sprayed coatings of chromium oxide and hypersonic powder flame sprayed coatings of cobalt-bonded tungsten carbide performed particularly well as ring coatings. Similar performance was obtained with these ring coatings operating ...

Energy Technology Data Exchange (ETDEWEB)

Dye-sensitized nanocrystalline TiO{sub 2} solar cells are currently under development. Since these cells contain an electrolyte solution we reviewed the health and safety aspects in view of indoor applications, where personal contact cannot be excluded. Only small amounts of chemicals are present in each cell and so there is no danger of acute toxicity. However, long-term effects often can be caused by incidental contact with minute amounts. For this reason we have tested cis-di(thiocyanato)-bis(4,4'-dicarboxy-2,2'-bipyridine)Ru(II), the sensitizer dye in the Ames test. The dye was not mutagenic in the Salmonella typhimurium reverse mutation assay and in the Escherichia coli reverse mutation assay.

International Nuclear Information System (INIS)

Formation of the soft magnetic nanostructure in amorphous Fe_1_4Ni_4_0Zr_7B_1_2 alloy due to heat treatment is studied by the Moessbauer, differential scanning calorimetry, and X-ray diffraction techniques. Annealing at temperatures 520-580 "oC leads to the formation of extremely soft nanocrystalline alloy as revealed by the rf-Moessbauer measurements. The superparamagnetic behaviour was observed for the alloy annealed at 620-640 "oC. At higher annealing temperatures good soft magnetic properties deteriorate. (author)

International Nuclear Information System (INIS)

AlN nanocrystalline layers and superstructures are used in the modern optoelectronic technology as reflecting mirrors in semiconductor layers. In the present work the properties of AlN films prepared by sputtering methods from an AlN target in reactive Ar + N plasma were investigated. The characterization was performed with HRTEM, SEM, glancing angle XRD and RBS methods. The present measurements confirmed the polycrystalline structure of AlN layers and enabled the evaluation of their grain size. The roughness and thickness of the layers were additionally determined by ellipsometric and profilometric measurements. (author)

Energy Technology Data Exchange (ETDEWEB)

In support of the efforts to apply ceramics to advanced heat engines, a study is being performed of the performance of ceramics at the ring/cylinder interface of advanced (low heat rejection) engines. The objective of the study, managed by the Oak Ridge National Laboratory, is to understand the basic mechanisms controlling the wear of ceramics and thereby identify means for applying ceramics effectively. Attempts to operate three different zirconias, silicon carbide, silicon nitride, and plasma-sprayed ceramic coatings without lubrication have not been successful because of excessive friction and high wear rates. Silicon carbide and silicon nitride perform well at ambient temperatures with fully formulated mineral oil lubrication, but are limited to temperatures of 500F because of the lack of suitable liquid lubricants for higher temperatures.

British Library Electronic Table of Contents (United Kingdom)

Objective.The interest of dental research in metal-free restorations has been rising in the last 20 years following the introduction of innovative all-ceramic materials in the daily practice. In particular, high strength ceramics and related CAD/CAM techniques have widely increased the clinical indications of metal-free prostheses, showing more favourable mechanical characteristics compared to the early ceramic materials.The purpose of the present paper is providing a brief review on the all-ceramic dental materials, evaluating pros and cons in the light of the most recent scientific results and of the authors? clinical experience.Materials. A structured review of the literature was given on the basis of medical and engineering papers published in the last decades on the use of dental cera...

British Library Electronic Table of Contents (United Kingdom)

An unsymmetrical squaraine dye which contains an arylamino group was synthesized and used in dye-sensitized solar cells. The molar extinction coefficient of the dye is 77793 M-1 cm-1. Because our synthesized molecule may have no diradical character or the contribution of the diradicaloid component to resonance is quite small, the newly designed squaraine dye has a maximum absorption at 546 nm in the visible region compared with the NIR squaraine sensitizers. Cyclic voltammetry and time dependent density function theory calculation were accomplished to scrutinize the sensitized performance of the dye. Meanwhile, the novel sensitizer has been used to sensitize nanocrystalline TiO2-based solar cell. Under standard global AM 1.5 solar conditions, the squaraine dye-sensitized cell gives a short...

British Library Electronic Table of Contents (United Kingdom)

Nanocrystalline chromium oxynitride films were deposited by reactive RF magnetron sputtering of metallic chromium target in argon and helium atmospheres. The paper deals with consequence of increase in oxygen partial pressure on structural, hydrophobic and optical properties of chromium oxynitride films. The film stoichiometry changes from CrN and Cr2O3 to only Cr2O3 with increase in oxygen partial pressure as evident from X-Ray Diffraction analysis in both cases. The average crystallite size decreases with increase in oxygen partial pressure for both gas atmospheres. The thickness calculated from transmission data and surface profilometer are in good harmony with each other. The deposited films are hydrophobic by nature and the contact angle of the films varies as a function of surface ro...

British Library Electronic Table of Contents (United Kingdom)

Nanocrystalline MnFe"2O"4 ferrite was prepared by using autocombustion technique (flash). The microstructure and magnetic properties are studied. The results of XRD and TEM clarified that, this ferrite is nanosized with particle size (39 nm). Magnetic measurements showed a ferromagnetic behavior with T"C = 613 K, the saturation magnetization M"s = 13.71 emu/g, remanent magnetization M"r = 0.1694 emu/g and, coercivity H"c = 25.6 Oe. Natural material, egg white used as an aqueous medium to extend prepare nanoparticles better than other chemical interesting materials.

International Nuclear Information System (INIS)

Nanocrystalline powders of GaN with grain sizes ranging from 2 to 30 nm were examined under high external pressures by in situ diffraction techniques in a diamond anvil cell at DESY (HASYLAB, Station F3). The experiments on densification of pure powders under high pressure were performed without a pressure medium. The mechanism of generation and relaxation of internal strains and their distribution in nanoparticles was deduced from Bragg reflections recorded in situ under high pressures at room temperature. The microstrain was calculated from the full-width at half-maximum (FWHM) values of the Bragg lines. It was found that microstrains in GaN crystallites are generated and subsequently relaxed by two mechanisms: generation of stacking faults and change of the size and shape of the grains occurring under external stress. (author)

Energy Technology Data Exchange (ETDEWEB)

TiB{sub 2} appears to be a promising material for the wear protection in various tribological systems, e.g. the diecasting of Al. This study focuses on the development of titanium boride coatings deposited by PACVD, a deposition method which is most suitable for the coating of substrates with complex shapes. All layers analysed are very smooth and exhibit a quasi-amorphous fracture surface. XRD and TEM analysis indicate a nanocrystalline structure with grain sizes in the order of 2 nm. The diffraction patterns can well be correlated to titanium diboride. WDS reveals an over stoichiometric B/Ti ratio. The layer hardness reaches the value of 33 GPa and the critical load in scratch tests rises to 35 N. Neither 100Cr6 nor Al as a counterpart in pin-on-disk tests leads to wear of the coating. (orig.)

British Library Electronic Table of Contents (United Kingdom)

In this study a novel sol-gel auto-combustion method, using n-decyltrimethylammonium bromide as a cationic surfactant, has been used to synthesize strontium hexaferrite nanocrystalline powder. The dried nitrate-citrate gel, prepared from a solution of ferric nitrate, strontium nitrate, citric acid, trimethylamine and cationic surfactant, exhibited an auto-combustion behavior after ignition in air. The formation reaction temperature, phase identification, crystallites size, particles size distribution and morphology of resultant strontium hexaferrite powder were investigated by DTA/TGA, FTIR, XRD, LPSA, TEM and SEM techniques. The results showed that in presence of the cationic surfactant, the combustion intensity increases and the crystallite size decreases. The crystallite size of stronti...

Energy Technology Data Exchange (ETDEWEB)

Damage and cyclic fatigue failure under alternating loading in transformation-toughened zirconia ceramics is reviewed and compared to corresponding behavior under quasi-static loading (static fatigue). Current understanding of the role of transformation toughening in influencing cyclic fatigue-crack propagation behavior is examined based on studies which altered the extent of the tetragonal-to-monoclinic phase transformation in MG-PSZ through subeutectoid aging. These studies suggest that near-tip computations of the crack-driving force (in terms of the local stress intensity) can be used to predict crack-growth behavior under constant amplitude and variable-amplitude (spectrum) loading, using spatially resolved Raman spectroscopy to measure the extent of the transformation zones. In addition, results are reviewed which rationalize distinctions between the crack-growth behavior of preexisting, long'' (> 2 mm), through-thickness cracks and ...

International Nuclear Information System (INIS)

Solid oxide fuel cell (SOFC) is a promising source of power generation in terms of conversion efficiency which is higher than the conventional one, as it is not limited by the Carnot efficiency. Theoretically, the SOFC have an efficiency of the order of 60-80 % but it is limited by the number of active side available for the reaction i.e. TPB (triple phase boundary) at the electrode-electrolyte interface which depends on the particle size of the materials employed during the fabrication of SOFC components (i.e. the method employed during the synthesis). Literally, there are several methods used in the syntheses of oxide materials such as conventional solid-state reaction, co-precipitation, hydrothermal rout, sol-gel and Glycine nitrate process (GNP) but among these GNP found to be effective over the other because of homogeneity, phase purity and smaller particle size of final product. In this work, the Nano-crystalline Ln_0_._6Sr_0_._4Co_0_._8Fe_0_._2O_3_-_#delta# ...

Energy Technology Data Exchange (ETDEWEB)

Chlorophyll-a (Chl-a) assembled in hydrophobic domain by fatty acid with long alkyl hydrocarbon chain such as myristic acid (Myr), stearic acid (Ste) and cholic acid (Cho) modified onto nanocrystalline TiO{sub 2} electrode is prepared and the photovoltaic properties of the nanocrystalline TiO{sub 2} film by Chl-a are studied. Incident photon to current efficiency (IPCE) value at 660 nm in photocurrent action spectrum of Chl-a/Ste-TiO{sub 2}, Chl-a/Myr-TiO{sub 2} and Chl-a/Cho-TiO{sub 2} electrodes are 5.0%, 4.1% and 4.1%, respectively. Thus, the IPCE is maximum using Chl-a/Ste-TiO{sub 2} electrode. From the results of photocurrent responses with light intensity of 100 mW cm{sup -2} irradiation or monochromatic light with 660 nm, generated photocurrent increases using Chl-a/Ste-TiO{sub 2} electrode compared with the other Chl-a assembled TiO{sub 2} electrodes. These results show that the hydrophobic domain formed by stearic acid with long alkyl ...

Energy Technology Data Exchange (ETDEWEB)

An advanced process for the separation of hydrogen sulfide (H{sub 2}S) from coal gasification product streams through an electrochemical membrane is being developed. H{sub 2}S is removed from the syn-gas stream, split into hydrogen, which enriches the exiting syn-gas, and sulfur, which is condensed from an inert sweep gas stream. The process allows removal of H{sub 2}S without cooling the gas stream and with negligible pressure loss through the separator. The process is made economically attractive by the lack of need for a Claus process for sulfur recovery. Membrane manufacturing coupled with full-cell experimentation was the primary focus this quarter. A tape-casted zirconia membrane was developed and utilized in one full-cell experiment (run 25); run 24 utilized a fabricated membrane purchased from Zircar Corporation. Results are discussed.

Energy Technology Data Exchange (ETDEWEB)

An experimental investigation of premixed methane-air combustion within the one-dimensional porous ceramic burners for various burner configurations is presented. The burner is nonhomogeneous because of different pore size ceramic block used in different section of the burner. Therefore, the thermophysical and transport properties are nonuniform along the burner core length. The burners are constructed of partially stabilized zirconia. The CO and NO{sub x} emissions, flame speed, and flame stability are examined and compared at lean equivalence ratios for five different burner configurations. The sandwich-structured burner has very favorable flame stabilizing characteristic due to the radiation reflecting region. While the combustion proceeds at faster rate than other burner configurations, the radiation reflecting region and the exit surface have low temperature. Thus the NO{sub x} emission can be kept at the same low level as the other burner configurations ...

Energy Technology Data Exchange (ETDEWEB)

BaTiO{sub 3} compacts, when fluxed with {lt} 2 vol% of a complex borate glass phase, were sintered to near theoretical density at temperatures {lt} 1175{degrees}C in 2 h. Microstructural analysis showed a uniform grain size {lt} 1.0 {mu}m with 0.75 wt% ZrO{sub 2} added to the flux phase as a grain growth inhibitor. TEM analysis revealed a microcrystalline grain-boundary phase with the ZrO{sub 2} resident along the grain boundaries. These samples displayed an essentially flat dielectric profile, low dissipation factors ({lt} 2%) over the range 25{degrees} to 125{degrees}C, a near linear dependence ({approx} {+-} 15%) between 25{degrees} and {minus} 55{degrees}C, and significantly increased voltage stability. X-ray diffraction analysis of these small-grained materials indicates a suppression of the tetragonal structure toward a more cubic modification.

Energy Technology Data Exchange (ETDEWEB)

The feasibility of using hydrogen as the sole fuel in a direct injection diesel engine was investigated. An air cooled single cylinder Lister ST1 diesel engine was modified to operate as a low-heat-rejection engine for this study. Partially stabilized zirconia ceramic parts were used to shield the combustion space of the engine. Using a compression ratio of 17.9:1 and motoring the test engine at 21000 rpm, a maximum compression temperature of approximately 900 K was achieved. Under these operating conditions, all lubricants tested were found to burn. Lowering the speed to 1450 rpm and the compression ratio to 17.1, lubricant combustion and hot spots were successfully eliminated. The maximum compression temperature, when compression ignition of hydrogen was tried, was in the 800 K range. The corresponding ceramic surface temperature was estimated to reach 600-700 K. Only sporadic compression ignition of hydrogen was achievable. (author).

International Nuclear Information System (INIS)

Electrodeposition of semiconducting iron oxide (Fe_2O_3) thin film was carried out from an alkaline sulphate bath. A 0.1 M ferrous sulphate (FeSO_4#centre dot#7H_2O) was complexed with 0.1 M citric acid. By addition of 1 N NaOH, pH of the solution was made alkaline (pH=9) and deposition of iron oxide (Fe_2O_3) thin films was carried out potentiostatically at room temperature (300 K). From cyclic voltametry (CV), electrochemical studies were carried out for deposition of iron oxide thin films. The XRD studies reveal that Fe_2O_3 with epsilon (#epsilon#) phase having monoclinic crystal structure is formed. By observing scanning electron microscope (SEM), it is seen that iron oxide films were homogeneous, uniform and well covered to surface of the substrate. Grain size was found to be in nanometers range from XRD analysis. The optical band gap of Fe_2O_3 thin film was estimated to be 1.90 eV. Electrical resistivity was order of 10"4 #OMEGA# cm. Dielectric constant and loss (tan #delta#) ...

International Nuclear Information System (INIS)

Nanocrystalline cemented tungsten carbide has attracted considerable interests for use in cutting tool because of its superior mechanical properties. In this study, nano-sized powders of mixed WC and Co were prepared from attrition-milled oxides by a gas reduction-carburization process. The effects of compacting pressure, heating schedule, additional ball-milling, and the presence of a grain growth inhibitor on the sintering properties of the nano-sized WC-Co powders were examined. The grain size and phases in WC-Co alloy were clearly affected by compacting pressure. Because of the trapped gases and the lower melting point of the cobalt binder, when a compact of nano-sized WC-Co powder was sintered through a heating schedule with holding steps, the sintered alloy maintained the small size of WC grains without any #eta# phase. In addition, the additional ball-milling improved the microstructure and mechanical properties of the nano-sized WC-Co powder by producing a ...

International Nuclear Information System (INIS)

The microstructure, microhardness, corrosion, and wear resistance of d.c.-plated Ni electrodeposits prepared from different types of electrolysing Watts-type baths, without or with organic compounds, ceramic powder - SiC and polymer - polytetrafluoroethylene (PTFE), on Cu substrate, which was subsequently removed from the deposits, were investigated. With the change of the type of bath, the deposit grain size was found to decrease markedly, e.g. deposits with an average grain size of about 50 nm could be produced from the bath containing 45 g/dm"3 Ni"2"+ ions, 5 g/dm"3 SiC, and 20 g/dm"3 PTFE. The surface morphology on the bath side of the electrode-posited Ni or Ni-SiC-PTFE foils was characteristic of the type of bath, and its roughness correlated well with the observed grain size. Microhardness and wear resistance increased with decreasing grain size, as expected. On discussing the factors controlling deposit grain size, it is concluded that the Ni"2"+ ion content in the bath and the ...

International Nuclear Information System (INIS)

The synthesis of narrowly dispersed nanocrystalline TiO_2 was investigated with a surfactant aided solvothermal synthetic method in toluene solutions. When a sufficient amount of titanium isopropoxide, Ti[OCH(CH_3)_2]_4 (TIP), was added to the solution, the shapes of TiO_2 nanoparticles changed from spheres to rods. The aggregated microstructures of the nano-sized TiO_2 in systems of spheres, rods, and mixtures of spheres and rods was studied using TEM. The morphological shape of the aggregation was described in terms of the fractal dimensions. We used a box-counting method to get the fractal dimension of these systems. The fitted fractal dimensions for spheres, sphere/rod mixtures, and rods are D = 1.54, D = 1.81, and D = 1.89, respectively. The fractal dimension changed from 1.54 to 1.9 with the TIP/toluene ratio, indicating that the growth mechanism for aggregations showed different behaviors.

Energy Technology Data Exchange (ETDEWEB)

Investigations of alternative renewable energy resources continue, with many studies concentrating on hydrogen storage. However, there are a few problems such as storage, transportation, delivery to the user and usage safely, to be addressed to facilitate commercialization and wide usage of the hydrogen. The absorbed form within the metal hydrides seems to be the best solution of this problem. Since Li is the lightest metal, it has the advantage as the stored amount of hydrogen mass ratio. LiBH{sub 4} production process was investigated using elemental Li, B and H{sub 2}. Spex type ball milling with tungsten carbide, stainless steel and zirconia type vessels, was used to mix the different amount of Li and B under argon atmosphere. X-ray diffraction pattern demonstrated that the LiB was obtained. A system was designed to provide a hydrogen atmosphere of 60 bars to force hydrogen into the LiB structure. FTIR analysis strongly indicated the LiBH{sub 4} compound when ...

Energy Technology Data Exchange (ETDEWEB)

By magnetron sputtering model steel films with specific properties can be prepared for purposive surveys. By changing the deposition parameters certain properties of these films can be influenced. For this thesis steel films with 18% Cr and 8% Ni have been prepared in order to study specific parameters on the corrosion resistance of bulk stainless steel. Chemical composition, microstructure, and surface morphology of these films have been characterized. In comparison to bulk steel sheets with the same chemical composition they have a smaller grain size and a ferritic structure. In contrast to bulk steel sheets they don`t contain any nonmetallic inclusions like Mn-sulfides. The influence of these structural differences on the corrosion resistance has been studied. For this purpose the electrochemical properties of the sputter-deposited steels have been compared with the properties of steel sheets with a similar chemical composition (DIN 1.4301, AISI 304) in neutral and acidic Cl{sup ...

Energy Technology Data Exchange (ETDEWEB)

We have investigated the nanocrystalline microstructure and the hard magnetic properties of Sm(Co{sub 0.725}Fe{sub 0.1}Cu{sub 0.12}Zr{sub 0.04}B{sub 0.015}){sub 7.4} melt-spun ribbons. The coercivity (H{sub c}) of the as-spun ribbons increased with the wheel surface speed from 2.8kOe for 10m/s to 14.5kOe for 40m/s. The post-annealing of the melt-spun ribbons from 700 to 900 deg. C for 10min did not lead to a substantial increase of H{sub c}. However, after isothermal aging at 820 deg. C and subsequent slow cooling (0.5 deg. C/min) to 120 deg. C, H{sub c} increased from 2.8 to 10.9kOe for 10m/s, while it decreased from 14.5 to 13.5kOe for 40m/s ribbons. The grain size of the melt-spun ribbon reduced with structural transformation from 2:17H (Th{sub 2}Ni{sub 17}-hexagonal type) to 1:7H (TbCu{sub 7}-hexagonal type) as the wheel surface speed was increased. Three-dimensional atom probe analysis showed a boron enriched precipitate at the grain boundaries in the as-spun ...

Energy Technology Data Exchange (ETDEWEB)

This report describes the QUEOS facility and gives the results of the first test series performed up to 6/1995. The premixing phase of a steam explosion is investigated experimentally with simulant materials. The transient three-dimensional multi-component interaction of molten corium with water is studied using a large number of small solid spheres at temperatures up to 2300 C. The objective of the experiments is to establish a data base for testing the models of heat and momentum transfer in multi-fluid codes as well as the code`s capability to correctly describe multiphase flows. The experiments have the advantage that the diameter of the `coarse melt fragments` are known and that detailed measurements can be performed without the danger of a steam explosion. In this first series of experiments up to 10 kg of spheres (max. 24000 pieces) were used. The spheres, made of molybdenum or zirconia, were heated to temperatures up to 2000 C and are discharged into 0.5 ...