British Library Electronic Table of Contents (United Kingdom)

Amino-rich polymeric coatings are widely used in biomedical applications, since they promote adsorption of diverse biomolecules or facilitate cell growth. As a consequence, there is a growing interest in fabrication of such coatings that is focused predominantly on the optimization of the deposition process in terms of high density of primary amino groups. In addition, the nature of biomedical applications requires also sufficient stability of the films in aqueous environments. This aspect is investigated in this contribution. In particular, the effect of water and phosphate buffer saline on the coatings prepared by RF magnetron sputtering of Nylon 6,6 in Ar/N2 and N2/H2 gas mixtures is evaluated. The samples exposed to liquids are characterized by various diagnostic methods and their prop...

International Nuclear Information System (INIS)

Chromium nitride thin films were deposited on SA-304 stainless steel substrates by using direct-current reactive magnetron sputtering. The influence of process conditions such as nitrogen content in the fed gas, substrate temperature, and different sputtering gases on microstructural characteristics of the films was investigated. The films showed (200) preferred orientation at low nitrogen content (< 30%) in the fed gas. The formation of Cr_2N and CrN phases was observed when 30% and 40% N_2 were used, with a balance of Ar, respectively. Field emission scanning electron microscopy and atomic force microscopy were used to characterize the morphology and surface topography of the thin films, respectively. Microhardness tests showed a maximum hardness of 16.95 GPa for the 30% nitrogen content.

International Nuclear Information System (INIS)

For direct writing of electrically conducting connections and areas into insulating gold oxide thin films a scanning Ar"+ laser beam and a 30 keV Ga"+ focused ion beam (FIB) have been used. The gold oxide films are prepared by magnetron sputtering under argon/oxygen plasma. The patterning of larger areas (dimension 10-100 #mu#m) has been carried out with the laser beam by local heating of the selected area above the decomposition temperature of AuO_x(130-150 C). For smaller dimensions (100 nm to 10 #mu#m) the FIB irradiation could be used. With both complementary methods a reduction of the sheet resistance by 6-7 orders of magnitude has been achieved in the irradiated regions (e.g. with FIB irradiation from 1.5 x 10"7#OMEGA#/#square# to approximately 6 #OMEGA#/#square#). The energy-dispersive X-ray analysis (EDX) show a considerably reduced oxygen content in the irradiated areas, and scanning electron microscopy (SEM), as ...

International Nuclear Information System (INIS)

Based on the results obtained for C-N and Si-C-N films, a systematic investigation of reactive magnetron sputtering of hard quaternary Si-B-C-N materials has been carried out. The Si-B-C-N films were deposited on p-type Si(100) substrates by dc magnetron co-sputtering using a single C-Si-B target (at a fixed 20% boron fraction in the target erosion area) in nitrogen-argon gas mixtures. Elemental compositions of the films, their surface bonding structure and mechanical properties, together with their oxidation resistance in air, were controlled by the Si fraction (5-75%) in the magnetron target erosion area, the Ar fraction (0-75%) in the gas mixture, the rf induced negative substrate bias voltage (from a floating potential to -500 V) and the substrate temperature (180-350 deg. C). The total pressure and the discharge current on the magnetron target were held ...

Energy Technology Data Exchange (ETDEWEB)

There has been considerable interest in producing and studying nanoparticle materials because of the effect of size on their structure, physical and chemical structure. Most studied nanoparticle semiconductors belong to the II-VI group, as they are relatively easy to synthesize and are generally prepared as particulates or in thin film form. Among II-VI compounds, CdS is one of the most studied materials. There are different ways to synthesize CdS nanoparticles such as colloidal particles, chemical decomposition, sol-gel, gas evaporation, magnetron sputtering, electrostatic deposition, and etc. {gamma}-irradiation is one of the effective methods for synthesis of nanomaterials. These nonomaterials have been extensively used in the preparation of nanocrystalline metals, metal oxides, and metal-polymer composites. However, The preparation of CdS nanoparticle and CdS/ polyacrylonitrile nanocomposite by {gamma}-irradiation ...

Energy Technology Data Exchange (ETDEWEB)

The properties of polycrystalline (Ti, Al)N coatings deposited on non-nitrided, classically plasma-nitrided and low pressure plasma-nitrided AISI H11 steel samples were investigated. The plasma deposition and low pressure plasma nitriding were performed in a Z700-LH magnetron sputter ion plating unit, while a separate unit was used for plasma nitriding of specimens at a pressure of several millibars. The (Ti, Al)N coating was deposited onto all the samples using the same equipment as for the plasma deposition and low pressure plasma nitriding. For the characterization of the composite structures, the following methods were used: scratch test, X-ray diffraction analysis, scanning electron microscopy, scanning tunnelling microscopy and microhardness testing. It was found that plasma nitriding prior to coating deposition strongly affects the growth and properties of hard coatings, such as the microhardness, adhesion, preferred ...

International Nuclear Information System (INIS)

The authors show that dramatically different in-plane crystallographic textures can be produced in body centered cubic (bcc) metal thin films deposited under different conditions. The orientation distribution of polycrystalline bcc thin films on amorphous substrates often has a strong (110) fiber texture, and an in-plane texture may develop when deposition takes place with an off-normal incidence flux of energetic ions or atoms. Three orientations in Nb films have been observed in which the energetic particle flux coincides with crystal channeling directions. In-plane orientations in Mo films have also been obtained in magnetron sputtering systems. The selected orientations are reviewed, and examples are given in which the in-plane orientation of Mo deposited in two similar magnetron system differs by a 90 deg C rotation. The origins of in-plane texture in rectangular magnetron ...

Energy Technology Data Exchange (ETDEWEB)

Highly resistant, high-transmittance woodceramic thin films were prepared using rf magnetron sputtering of a woodceramic disk in argon plasma. A film series was deposited based on substrate temperature, which was varied from 50 to 500 degree C. The film's electrical and optical properties depended on substrate temperature. Films deposited below 300 degree C were insulative, {rho}>10{sup 10} {omega} {center_dot} cm. Films deposited at 50 degree C had a density of 1.9-2.2 g/cm{sup 3} comparable to that of single crystal graphite. Below 200 degree C, films had higher transmittance than typical DLC films in the visible and infrared region. Infrared C-H absorption spectrum was observed by Ft-IR and there exist two types of bonding corresponding to sp{sup 2} or SP{sup 3}. (author)

International Nuclear Information System (INIS)

Nitrogen doped Diamond-like carbon thin films were deposited on n-Si and SiO_2 substrates by rf magnetron sputtering using pure graphite (99.999%) as the target material and mixtures of Ar, N_2 and H_2 for plasma generation. The dependence of structural and optical properties on nitrogen content was investigated using XPS, Raman spectroscopy, FT-IR spectroscopy, and Ellipsometry studies. It was found that as the nitrogen content was increased in the plasma, sp"2 bonding favored. Also it was observed that oxygen contamination increased with nitrogen content. Typical C-H stretching modes connected with diamond-like carbon could be seen in FT-IR spectra. The I_D and I_G bands were well defined and it was observed that as nitrogen content increased I_G band was enhanced. Ellipsometry studies revealed that the optical constants like refractive index (n) and extinction co-efficient (k) increased with increase in nitrogen content as well as substrate ...

International Nuclear Information System (INIS)

Magnetic materials such as yttrium iron garnet (YIG) are of great importance for its magneto-optic properties and for their potential applications in the domain of optical telecommunications. The deposition of thin films of YIG, on quartz or GGG (gadolinium gallium garnet) substrate, was performed using radio frequency non reactive magnetron sputtering, followed by high temperature annealing which is needed to enhance the crystallinity of the layers. Rutherford backscattering spectrometry RBS was used to determine the thickness and stoichiometry of the performed layers in order to investigate correlations between growth conditions and the quality of the final material. RBS measurements showed the influence of the deposition time and the temperature substrate on the film growth and its stoichiometry. (author)

International Nuclear Information System (INIS)

Some magnetron sputtering systems experience rapid oscillations in the current and voltage of the plasma discharge after several hours when equipped with certain targets. These oscillations often lead to the plasma becoming extinguished, a condition known as ''flame-out.'' This article details the study of two 90% W--10% Ti magnetron targets which differed in density. The higher density targets sometimes experienced flame-out after approximately 3 h of sputtering. The less dense material could be sputtered for the entire 15 h life of the target. Scanning electron microscopy pictures and atomic composition depth profiles were obtained using Auger electron spectroscopy. In addition, a Colutron-based ion source with a high vacuum system was used to measure ion-induced secondary electron emission coefficients as a function of energy, ion specie, and gas coverage. Analysis of the sample ...

Energy Technology Data Exchange (ETDEWEB)

The refractory nature and high ductility of body centered cubic (bcc) phase tantalum makes it a suitable material for corrosion- and wear-resistant coatings on surfaces that are subjected to high stresses and harsh chemical and erosive environments. Sputter deposition can produce thick tantalum films but is prone to forming the brittle tetragonal beta phase of this material. Efforts aimed at forming thick bcc phase tantalum coatings in both flat plate and cylindrical geometries by high-rate triode sputtering methods are discussed. In addition to substrate temperature, the bcc-to-beta phase ratio in sputtered tantalum coatings is shown to be sensitive to other substrate surface effects.

CERN Document Server

In order to reduce the activation temperature of the TiZrV alloy, thin films of various compositions were produced by three-cathode magnetron sputtering on stainless-steel substrates. For the characterisation of the activation behaviour the surface chemical composition has been monitored by Auger electron spectroscopy during specific in situ thermal cycles. The volume elemental composition of the film has been measured by energy dispersive X-ray spectroscopy and the morphology (crystal structure and size of the crystallites) has been investigated by X-ray diffraction. The criteria indicating the sample quality and its dependence on film structure and chemical composition are presented and discussed. (13 refs).

Energy Technology Data Exchange (ETDEWEB)

A radio frequency sputtering apparatus with a pair of targets has been developed for depositing a film of uniform thickness onto a complex-geometric specimen such as the retainer of a ball bearing. The deposition characteristics of the apparatus were compared with those of the conventional sputtering apparatus. Lubrication properties of MoS/sub 2/ films made by these devices were also compared under a variety of conditions. Finally, friction and wear of MoS/sub 2/ films applied to angular-contact type ball bearings of 20 mm bore were studied in air, nitrogen and vacuo. The two-target sputtering has an advantage mentioned above. However, the films deposited by the method exhibited a rather short wear life because of the temperature rise of the substrate during ion bombardment and during the sputtering process. This temperature dependence was observed in films on those substrates that ...

Energy Technology Data Exchange (ETDEWEB)

There is presently considerable interest in wear resistant coatings produced using closed field unbalanced magnetron sputtering technology. For example, layered films of diamond-like carbon (DLC) with tungsten or titanium additions have been widely reported. The benefit is that the mechanical properties are enhanced (e.g. giving greater toughness); also it is possible to control the stress state and enhance adhesion. Here we report the further development of this concept by the addition of TiN, TiCN and TiC layers in DLC-based composites, utilizing an additional source of electrons in the vicinity of substrate to enhance ionisation of the plasma and increase coating density. Composite coatings of ceramics TiN, TiC{sub x}N{sub y}, TiC, CrN, TiCrN, TiCrCN, TiCrC, metal doped Ti{sub x%}-DLC and their combinations were deposited on 316 stainless steel substrates. The mass flow of reactive gases into the chamber was controlled using plasma optical ...

International Nuclear Information System (INIS)

Magnetron sputter deposition was used to fabricate body centered cubic (bcc) and A-15 crystal structure W thin films. Previous work demonstrated that the as-deposited crystal structure of the films was dependent on the deposition parameters and that the formation of a metastable A-15 structure was favored over the thermodynamically stable bcc phase when the films contained a few atomic percent oxygen. However, the A-15 phase was shown to irreversibly transform into the bcc phase between 500 C and 650 C and that a significant decrease in the resistivity of the metallic films was measured after the transformation. The current investigation of 150 nm thick, sputter deposited A-15 and bcc tungsten thin films on silicon wafers consisted of a series of experiments in which the stress, resistivity and crystal structure of the films was measured as a function of temperatures cycles in a Flexus 2900 thin film stress measurement ...

Energy Technology Data Exchange (ETDEWEB)

The refractory nature and high ductility of body centered cubic (bcc) phase tantalum makes it a suitable material for corrosion- and wear-resistant coatings on surfaces which are subjected to high stresses and harsh chemical and erosive environments. Sputter deposition can produce thick tantalum films but is prone to forming the brittle tetragonal beta phase of this material. Efforts aimed at forming thick bcc phase tantalum coatings in both flat plate and cylindrical geometries by high-rate triode sputtering methods are discussed. In addition to substrate temperature, the bcc-to-beta phase ratio in sputtered tantalum coatings is shown to be sensitive to other substrate surface effects.

British Library Electronic Table of Contents (United Kingdom)

The pentenary compound semiconductor Cu(In,Ga)(Se,S)2 is one of the most attractive materials for high-efficiency solar cells due to its tunable band gap to match well the solar spectrum. In this study, semiconducting Cu(In,Ga)(Se,S)2 thin films were prepared by a classical two-step growth process, which involves the selenization and/or sulfurization of In/Cu?Ga precursor. During the precursor formation step metallic In/Cu?Ga alloys were deposited onto the Mo-coated soda-lime glass substrates by DC magnetron sputter process. The respective precursors were subsequently reacted with H2Se and/or H2S gasses, at elevated temperatures. By optimizing the selenization parameters, such as the gas concentrations, reaction time, reaction temperature, and the flow of H2Se and H2S, high quality, single...

Energy Technology Data Exchange (ETDEWEB)

Duplex-coating procedures consisting of plasma nitriding and Me-C:H hard coating lead to an improved performance of the devices because the Me-C:H coating is supported by the nitrided phase and, therefore, the `eggshell-effect` is avoided. Furthermore, this support leads to a higher load-bearing capacity of the thin film. Two standard procedures (classical high-pressure plasma nitriding and unbalanced magnetron sputtering of Ti-C:H) were performed subsequently to prepare the duplex coatings on X20Cr13 ferritic stainless steel. The corrosion resistance of the steel could be improved by nitriding at 450 C compared to the untreated ferritic substrate. The roughness is determined by the nitriding step. The weakest point of the coating is the transition zone between the nitrided and the untreated substrate and not the interface between the Ti-C:H coating and the nitrided substrate as shown by the Rockwell and scratch tests. The adhesion of the ...

Energy Technology Data Exchange (ETDEWEB)

There is an increasing number of applications for hard coatings in engineering where the properties of the single-layer coating are not sufficient. One way to solve this problem is to use a multilayer coating that combines the properties of several coating materials. In this study, TiN-CrAlN and CrN-CrAlN multilayer coatings were deposited on 100Cr6 and S6-5-2 (DIN) steel substrates, by means of unbalanced magnetron sputtering. For comparison, TiN, CrN and CrAlN single-layer coatings were also prepared. For all depositions the coating temperature was below 473 K. Indentation testing, hardness measurements and scratch tests were performed to characterize the mechanical properties. The correlation between the wear behavior in rolling contact and the mechanical properties of the multilayer coatings is reported. A ball crater preparation technique through scratch tests and wear tracks was used to observe the deformation and fracture behavior ...

International Nuclear Information System (INIS)

In this work, the effects of substrate temperature that was changed from 100 to 500 "oC on the structural, chemical and electrical properties of carbon films, prepared by direct current magnetron sputtering technique, on 316L stainless steel as bipolar plate had been investigated. Raman spectroscopy and scanning electron microscopy (SEM) were performed to study the structure and the morphology of the deposited films, respectively. The corrosion resistance and the electrical resistivity were carried out by using corrosion tests and four point-probe technique. The results show that the carbon films change the structure from amorphous to graphite-like by increasing temperatures. At the temperatures higher than 300 "oC, the holes and porosities are formed on the film indicating a decrease of film quality. According to our results, corrosion resistance and electrical properties are depended strongly on the substrate temperature.

Energy Technology Data Exchange (ETDEWEB)

Deposition of hard coatings may influence the mechanical properties of the bulk material and its corrosion resistance. In this work we study the hardness of the coated and the back side of 100Cr6 steel plates. Electrochemical corrosion tests were performed in O{sub 2}-saturated acetate buffer of pH 5.6 at 25degC. Chromium nitride and titanium nitride coatings prepared by different physical vapour deposition processes, such as arc, thermionic arc evaporation, magnetron sputtering and ion-beam-assisted deposition (IBAD) were compared. The results show that, for sufficient corrosion protection, chromium nitride layers have to be thicker than 500 nm. An increased nitrogen partial pressure in the evaporation chamber of the IBAD process improves the corrosion resistance significantly. The hardness of the substrates was reduced in the case of thermoionic arc evaporation only, indicating a deposition temperature of more than 250degC. For this process, ...

International Nuclear Information System (INIS)

Nonevaporable getters (NEGs) have been extensively studied in the last several years for their sorption properties toward many gases. In particular, an innovative alloy as a thin film by magnetron sputtering was developed and characterized at the European Organization for Nuclear Research. It is composed of Ti-Zr-V and protected by an overlayer of palladium (Pd), according to a technology for which the authors got the licence. NEG-Pd thin films used in combination with ion getter pumps is a simple, easy way to handle pumping devices for ultrahigh and extremely high vacuum applications. To show how to apply this coating technology to the internal surface of different types of ion pumps, the authors carried out several tests on pumps of various shapes, sizes (in terms of nominal pumping speed), and types (diode, noble diode, and triode). Special care was taken during the thermal cycle of baking and activation of the pumps to preserve the internal ...

International Nuclear Information System (INIS)

In this work, amorphous hydrocarbon (a-C:H) film deposition on metallic mirrors was studied during working shots in tokamak T-10 and at exposure in Ar/CHD3/D2 dc magnetron discharge in a special laboratory high vacuum setup. Analysis of film composition (including hydrogen content) was carried out using nuclear physical methods. Thickness and optical parameters (refractive and extinction coefficients) of the films were estimated by ellipsometry. Laboratory films can be characterized as soft a-C:H films in comparison with hard tokamak films (? = 1.2 and 1.8 g/cm3, respectively). For the first one, a linear dependence of deposition rate on mirror temperature was observed in a wide temperature range. The addition of methane into initial Ar/D2 magnetron gas mixture leads to an increase of deposition rate. The data obtained should be taken into account to prevent hydrocarbon film formation on the surface of first mirrors in ...

Energy Technology Data Exchange (ETDEWEB)

In the Ti-Si-C and Ti-Si-C-N systems, metastable layers were precipitated by means of non-reactive magnetron sputtering of hot-pressed two-phase TiC/SiC and TiN/SiC targets with 20 mole% and 50 mole% SiC. The preparation parameters were varied as follows: ion bombardment during precipitation (bias sputtering), substrate temperature, and annealing times when annealing amorphous 50%:50% TiC/SiC and 50%:50% TiN/SiC layers. Sputtering of targets containing 20% SiC was found to result in monophase fcc layers (NaCl structure). This was documented on the basis of X-ray and electron diffraction patterns. Direct precipitation of targets with 50 mole% SiC resulted in amorphous layers. Increasing the ion bombardment during accretion, raising the substrate temperature, and annealing amorphous 50%:50% TiC/SiC and 50%:50% TiN/SiC (layers precipitated directly) resulted in the crystallization of TiC and TiN ...

Energy Technology Data Exchange (ETDEWEB)

To improve mirrors coating, we have modeled sputtering of binary oxide targets using TRIM code. First, we have proposed a method to calculate TRIM input parameters using on the one hand thermodynamic cycle and on the other hand Malherbe`s results. Secondly, an iterative processing has provided for oxide steady targets caused by ionic bombardment. Thirdly, we have exposed a model to get experimental sputtering yields. Fourthly, for (Ar - SiO{sub 2}) pair, we have determined that steady target is a silica one. A good agreement between simulated and experimental yields versus ion incident angle has been found. For (Ar - Ta{sub 2} O{sub 5}) pair, we have to introduce preferential sputtering concept to explain discrepancy between simulation and experiment. In this case, steady target is tantalum monoxide. For (Ar - Ta+O{sub 2}) pair, tantalum sputtered by argon ions in reactive oxygen ...

Science.gov (United States)

... Accession Number : ADD257320. Title : Sputter Deposition of Yttrium-Oxides. Descriptive Note : Journal article,. Corporate ...

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline processing by inert gas condensation has the inherent advantages of generating: (1) high surface area nanoclusters, (2) non-stoichiometric oxides, and (3) high dispersions of dopants. This approach is exploited in the synthesis of fluorite-structured catalysts for SO{sub 2} reduction by CO. Nanocrystalline CeO{sub 2{minus}x}, La-doped CeO{sub 2{minus}x}, and Cu-doped CeO{sub 2{minus}x} were produced by magnetron sputtering from a pure or mixed metal target, followed by controlled oxidation of the metallic clusters. The as-prepared doped and undoped nanocrystalline CeO{sub 2{minus}x} materials were found to be excellent catalysts for complete SO{sub 2} conversion to elemental sulfur. Undoped nanocrystalline CeO{sub 2{minus}x} enabled light-off at 460 C, a temperature {approximately} 120 C lower than that over polycrystalline CeO{sub 2}, which is a novel effective catalyst itself. The high catalytic activity of the nanocrystals ...

Energy Technology Data Exchange (ETDEWEB)

Copper coatings deposited on Al-6061 substrates by radio frequency magnetron sputtering, to prevent the retention and permeation of energetically implanted tritium in Al-6061, were evaluated by a variety of characterization techniques. The coatings, weighing in the 0.03 to 0.088 kg/m{sup 2} range, were smooth and had a fine grain structure. They contained the intermetallic phases Cu{sub 9}Al{sub 4} and CuAl{sub 2} as well as copper. The fractions of Al and Cu in any coating increased and decreased, respectively, with increasing depth below the surface. Furthermore, the fractions of Al and Cu on the coating surface decreased and increased, respectively, with increasing coating weight. There was no texture or preferred orientation in the Cu phase of the coatings. A significant amount of oxygen was also detected at the original substrate surface. Residual stress measurements revealed that, in both Cu and CuAl{sub 2}, the stresses in the coating ...

Energy Technology Data Exchange (ETDEWEB)

A focused ion beam (FIB) is used to accurately sculpt predetermined micron-scale, curved shapes in a number of solids. Using a digitally scanned ion beam system, various features are sputtered including hemispheres and sine waves having dimensions from 1-50 {micro}m. Ion sculpting is accomplished by changing pixel dwell time within individual boustrophedonic scans. The pixel dwell times used to sculpt a given shape are determined prior to milling and account for the material-specific, angle-dependent sputter yield, Y({theta}), as well as the amount of beam overlap in adjacent pixels. A number of target materials, including C, Au and Si, are accurately sculpted using this method. For several target materials, the curved feature shape closely matches the intended shape with milled feature depths within 5% of intended values.

International Nuclear Information System (INIS)

A single plasma process involving three consecutive steps has been developed for producing high gas flow catalytic nanostructures on the electrodes of proton exchange membrane (PEM) fuel cells (FC). Using a high density helicon radio frequency (13.56 MHz) plasma, nickel is sputtered onto a porous carbon support. Changing the background gas from argon to methane/hydrogen allowed 2 ?m long, 37 nm diameter carbon nanofibres (CNFs) to be grown by diffusion through the nickel clusters in a 'tip growth' mechanism at the relatively low temperature of 400 deg. C. The third step involves plasma sputtering of platinum onto the CNFs, resulting in nanoclusters (3-8 nm) being formed on the periphery of the CNFs. Four FC cathodes were synthesized on carbon paper and PTFE/carbon loaded cloth (known as gas diffusion layer, GDL), both with and without CNFs, with the Pt/CNFs nanostructures grown on PTFE/carbon loaded cloth having the best FC performances. ...

International Nuclear Information System (INIS)

The possibilities and problems of PCA in phase separation are shown on Ni, Pd, and Pt silicides. The PCA depth profiles are less influenced by sputter and matrix effects than usual Auger depth profiles. The position of the silicide-Si interface is well defined by the component distribution crossover in PCA profiles. An interface component between Pd and Pt silicides and Si substrate is determined by PCA. (author).

International Nuclear Information System (INIS)

A method using a focused ion beam (FIB) to prepare a silicon amorphous material is presented. The method involves the redeposition of sputtered material generated during the interaction of the Ga"+ ion beam with a silicon substrate material. The shape and dimensions of this amorphous material are self-organized and reproducible. The stability of this amorphous material under electron irradiation was investigated in the transmission electron microscopy (TEM). Electron irradiation can induce recrystallization of the amorphous material, resulting in the lateral and vertical growth, starting at an amorphous-crystalline interface, of polysilicon containing defects.

Energy Technology Data Exchange (ETDEWEB)

Sputter-removal rates of overlayer and interfacial species on silicon are analyzed to determine sputtering yields for the species involved. Sputtering yields up to two orders of magnitude lower than those measured for silicon are found, and the results are interpreted in terms of a cascade mixing process which continually reburies much of the overlayer material beyond the escape depth of the sputtered atoms.

Energy Technology Data Exchange (ETDEWEB)

The motivation of this work is to develop high reflectance normal-incidence multilayer mirrors in the 8-12 nm wavelength region for applications in astronomy and extreme ultraviolet lithography. To achieve this goal, Mo/Sr and Mo/Y multilayers were studied. These multilayers were deposited with a UHV magnetron sputtering system and their reflectances were measured with synchrotron radiation. High normal-incidence reflectances of 23% at 8.8 nm, 40.8% at 9.4 nm, and 48.3% at 10.5 nm were achieved. However, the reflectance of Mo/Sr multilayers decreased rapidly after exposure to air. Attempts to use thin layers of carbon to passivate the surface of Mo/Sr multilayers were unsuccessful. Experimental results on the refractive index {tilde n} = 1-{delta} + i{beta} of yttrium and molybdenum in the 50-1300 eV energy region are reported in this work. This is the first time ever that values on the refractive index of yttrium are measured in this energy ...

Science.gov (United States)

Metastable yttrium-oxide films are synthesized using reactive sputter deposition. The yttrium concentration of the as-deposited film is found to vary as a function of the sputter deposition rate. In addition to the synthesis of the cubic equilibrium phase...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

Energy Technology Data Exchange (ETDEWEB)

The aim of this work was to develop a method to distinguish between different ion formation processes and to determine the influence of these processes on the total number of detected monatomic ions of a certain element. A vector/matrix-formalism was developed, which describes the physical processes of sputtering, ion formation, mass separation and detection in laser-SNMS. In the framework of the method developed, based on this theoretic formalism, changes in the secondary flux contribution of the respective element were observed by comparing the detected monatomic ion yield obtained in specifically aligned (SIMS and) laser-SNMS experiments. The yields resulting from these experiments were used to calculate characteristic numbers to compare the flux composition from different surfaces. The potential of the method was demonstrated for the elements boron, iron and gadolinium by investigating the changes ...

Energy Technology Data Exchange (ETDEWEB)

A brief description of a method for producing relatively intense molecular negative ion beams for the difficult Group IIA elements is given which offers considerable improvement in terms of source operation and beam intensity stability over other methods conventionally utilized. It is particularly suited for use in cesium plasma sources such as the Aarhus geometry and axial geometry versions of the source. The method utilizes H/sub 2/ source feed gas for the production of a hydrogen-rich plasma discharge which sputters a negatively biased probe made of elemental or copper alloy material. Negative ion beams of MgH/sub 3//sup -/>=12 ..mu.. A have been realized during routine operation of the 25 MV tandem accelerator. Negative ion beam intensity data, typical source operational parameters, and examples of mass spectra associated with their production are given. Interesting intermetallic molecular ...

Energy Technology Data Exchange (ETDEWEB)

Swift heavy ion-solid interaction leads in volume to track creation and on the surface to the ejection of particles into the vacuum. To learn more about initial mechanisms of track formation, we are focused on the sputtering of uranium dioxide by fast heavy ions. This present study is exclusively devoted to the influence of the electronic stopping power on the emission of neutral particles and especially on their angular distribution. These measurements are completed by those of the ions emitted from UO{sub 2} targets bombarded with swift heavy ions. The whole experimental results give access to: i) the nature of the sputtered particles; ii) the charge state of the emitted particles; iii) the direction of ejection of the sputtered particles ; iv) the sputtering yields deduced from the angular distributions. These results are compared to the prediction of the sputtering models ...

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning the structural properties of sputtered tantalum and tantalum compounds. The preparation of thin film capacitors and resistors is described. The electrical properties of the sputtered films are also included. The influence of the substrate on the properties of the coatings is considered, including adherence of the coating to the substrate, and the effects of impurities on coating integrity. (Contains 250 citations and includes a subject term index and title list.)

Energy Technology Data Exchange (ETDEWEB)

Modeling is performed for focused-ion-beam (FIB) sputtering and redeposition on trench sidewalls in a steady state approximation. Calculations are carried out to demonstrate the sputtered surface profile under known parameters such as sputtering yield as a function of ion incident angle, the FIB current density profile, and the FIB scan speed. It is found that a steplike slope with a gradient angle of {theta}{sub 0} is formed at the FIB bombarding position. Furthermore, the redeposition flux on the sidewalls is calculated as a function of {theta}{sub 0} for the FIB trench milling assuming the cosine law for the angular distribution of the sputtered atom. The redeposition will be more accurately predictable and controllable when more information about these assumptions is obtained.

Energy Technology Data Exchange (ETDEWEB)

Sputter-deposited tantalum (Ta) and reactively sputter-deposited Ta-nitride films were studied with respect to the passivation capability against copper (Cu) oxidation in thermal O{sub 2} ambient. A 200 {angstrom} Ta or Ta-nitride film was sputter-deposited on a 2,000 {angstrom} Cu film using a Ta target in an Ar/N{sub 2} gas mixture. With Ta passivation, Cu was not oxidized at temperatures up to 400 C, which can be further improved by using passivation of an amorphous Ta-nitride film deposited in an appropriate condition. The absence of long-range defects in the Ta-nitride film was presumably responsible for this improvement. However, sputtering-induced surface damage by excess N{sub 2} in the sputter gas mixture may reduce the passivation capability of Ta-nitride films. When the passivated Cu was oxidized, the Cu oxides always resided in the top surface region. That is, in the ...

Energy Technology Data Exchange (ETDEWEB)

The object and the purpose of the present work was to develop, to assemble and to start running a new TOF (time of flight) mass spectrometer for imaging SNMS analytic which is optimized for the analysis of highly molecular secondary ions. The most important purpose was the characterization of the TOF mass spectrometer. The obtained mass spectra of indium, tantalum and silver clusters reflect the excellent properties of the TOF mass spectrometer for the detection of large clusters with good detection efficiency up to masses of 16000 amu. The possibility of the deflection of selected saturated atom and cluster peaks serves for further improvement of the detection efficiency for large molecules. The accessible mass resolution was determined to be of the order of m/{delta}m=1000 in the high mass region. Numerous measurements were carried out to characterize the useful yield of this spectrometer. For a best possible adaptation of the TOF mass spectrometer for the detection of highly ...

Energy Technology Data Exchange (ETDEWEB)

The results of an investigation on the production of Group IIA atomic and molecular negative ion beams formed in a cesium-sputter negative ion source are presented. The sputtering material was formed by pressing pellets of stoichiometric mixtures of the Group IIA element carbonates and 10% copper powder. Negative ions of several alkaline-earth elements and their oxides have been observed. Beam intensities as high as 180 pA have been observed for Sr{sup -}and 20 nA for SrO{sup -}. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Average emittance data for ion beams extracted from cesium-sputter negative ion sources equipped with spherical, ellipsoidal, and cylindrical geometry cesium-surface ionizers are presented. The attributes of the respective source geometries are described in terms of their cesium ion optical properties. The results of recent measurement of the emittances of momentum-analyzed beams extracted from the ellipsoidal geometry source are also presented. These measurements indicate the presence of a species-dependent effect. The effect is believed to be attributable to differences in the energy spreads of the respective negative ion beams introduced by the sputter generation process.

International Nuclear Information System (INIS)

Electron probe microanalysis (EPMA) offers high sensitivity and high accuracy in quantitative measurements of chemical compositions and mass coverages. Owing to the low detection limits of the wavelength-dispersive technique, monolayers with mass coverages of about 0.05 pg cm z can be detected. Assuming a density of 5 g cm--3 this corresponds to a thickness of 0.1 nm. With these advantages in mind, EPMA was extended to depth profile analysis in the sub-micron range using a surface removal technique. The present paper shows how depth profile analysis can be improved by combining EPMA and the focused ion beam (FIB) technique. The focused ion beam system uses a Ga+ ion beam. The ion beam allows the milling of defined geometries on the nanometer scale, so that very shallow bevels with exactly defined angles in relation to the surface can be obtained. Low surface damage is expected due to low sputtering effects. Calibrated WDX measurements along the bevel deliver ...

Science.gov (United States)

Sputtering of glass coatings on cadmium sulfide thin film solar cells

Energy Technology Data Exchange (ETDEWEB)

In this paper, we report on a comparative study of active screen plasma nitriding (ASPN) and conventional dc plasma nitriding (CPN) behavior of 30CrNiMo8 low-alloy steel that has been examined under various process conditions. The process variables included active screen setup parameters (screen and iron plate top lids placed on the screen setup with 8 mm of hole size), treatment temperature (550 and 580 deg. C), gas mixture (75/25 and 25/75 of N{sub 2}/H{sub 2}) and treatment time (5 and 10 h) in 500 Pa pressure. The structure and phases composition of the diffusion zone and compound layer were studied by X-ray diffraction (XRD), microhardness tests, light optical microscopy and scanning electron microscopy (SEM). It was observed that treated sample surfaces in both CPN and ASPN methods consist of {gamma}' and {epsilon} phases, and while the nitriding time and/or temperature increases, the intensity of {epsilon} phase in the compound layer will increase ...

Energy Technology Data Exchange (ETDEWEB)

The Sputter coefficient of accelerated CO{sub 2} cluster ions hitting surfaces of various materials is investigated. For copper it varies proportional to the 2nd power of the energy between 155 and 260 keV. The rate of erosion for different target materials varies by two orders of magnitude from tungsten to PMMA. Diamond is eroded fairly quickly, while aluminum is eroded less than corundum (Al{sub 2}O{sub 3}). No simple correlation of the sputter coefficient on the bulk material properties is found. For copper the angular distribution of sputtered material is measured and found to be following roughly a cosine distribution. By using masks different microstructures have been produced in cobalt-samarium magnets, diamond and glass. (orig.)

International Nuclear Information System (INIS)

We have measured K-edge X-ray absorption spectra of argon in sputtered aluminum films at a synchrotron radiation facility (the Photon Factory). We found that the energy and shape of white line change when the film is annealed at 500 C and the spectrum becomes resembling that of argon implanted in silicon. From the analyses of the X-ray absorption spectra and TEM observation we concluded that argon exists as very small atom clusters with a diameter less than 1 nm or exist as isolated atoms in the as-sputtered aluminum film, and that the size of the clusters become as big as 10 nm diameter when the film is heated. (Copyright (c) 1999 Elsevier Science B.V., Amsterdam. All rights reserved.)

British Library Electronic Table of Contents (United Kingdom)

Lithium phosphorous oxynitride(Lipon) thin films as a lithium ion conductive electrolyte were prepared by radio frequency reactive sputtering in N2 plasma. The properties of the amorphous Lipon solid electrolyte were investigated as a function of N2 pressure during reactive sputtering. The ionic conductivity and the electrochemical stability of Lipon thin films improved drastically as the N2 pressure decreased. The ionic conductivity closed to 10?6 S cm?1 and obtained a stability window of 1.0?5.0 V with an N2 pressure of 5 mTorr, where the number of nitrogen bonds between the phosphate groups were more than those formed at higher pressure. It was possible to fabricate the Li//LiCoO2 complete thin film battery using this Lipon solid electrolyte, which exhibited excellent discharge characte...

International Nuclear Information System (INIS)

A theoretical model is presented to describe the electromagnetic, heat transfer and fluid flow phenomena within a magnetron plasma torch and in the resultant plume, by using a commercial computational fluid dynamics (CFD) code FLUENT. Specific calculations are presented for a pure argon system (i.e., an argon plasma discharging into an argon environment), operated in a turbulent mode. An important finding of this work is that the external axial magnetic field (AMF) may have a significant effect on the behavior of arc plasma and thus affects the resulting plume. The AMF impels the plasma to retract axially and expand radially. As a result, the plasma intensity distribution on the cross section of torch seems to be more uniform. Numerical results also show that with AMF, the highest plasma temperature decreases and the anode arc root moves upstream significantly, while the current density distribution at the anode is more concentrated with a higher peak value. In ...

Energy Technology Data Exchange (ETDEWEB)

Successful interface engineering requires compositional and electronic material characterization as a prerequisite for understanding and intentionally generating interfaces in photovoltaic devices. The paper gives an overview with several examples, all referring to Cu(In,Ga)(S,Se){sub 2} ('CIGSSe')-based solar cells, with an emphasis on characterization using highly specialized methods, such as elastic recoil detection analysis, X-ray emission spectroscopy and photoelectron spectroscopy using synchrotron and ultraviolet light for excitation, inverse photoemission spectroscopy and Kelvin probe force microscopy. First, the determination of the depth profile of the band gap energy E{sub g} in the absorber layer is demonstrated. The modification of E{sub g} towards both interfaces is discussed in terms of beneficial electronic effects. Next, the interface between absorber and buffer layers with alternative and promising non-toxic materials is ...

Energy Technology Data Exchange (ETDEWEB)

The Energy Conversion and Storage Program applies chemistry and materials science principles to solve problems in (1) production of new synthetic fuels, (2) development of high-performance rechargeable batteries and fuel cells, (3) development of advanced thermochemical processes for energy conversion, (4) characterization of complex chemical processes, and (5) application of novel materials for energy conversion and transmission. Projects focus on transport-process principles, chemical kinetics, thermodynamics, separation processes, organic and physical chemistry, novel materials, and advanced methods of analysis. Electrochemistry research aims to develop advanced power systems for electric vehicle and stationary energy storage applications. Topics include identification of new electrochemical couples for advanced rechargeable batteries, improvements in battery and fuel-cell materials, and the establishment of engineering principles applicable to electrochemical ...

International Nuclear Information System (INIS)

A calculation on the stabilization of the sideband instability in the free electron laser (FEL) and inverse FEL (IFEL) was completed. The issue arises in connection with the use of a tapered (''variable-parameter'') undulator of extended length, such as might be used in an ''enhanced efficiency'' traveling-wave FEL or an IFEL accelerator. In addition, the FEL facility at Columbia was configured as a traveling wave amplifier for a 10-kW signal from a 24-GHz magnetron. The space charge field in the bunches of the FEL was measured. Completed work has been published.

International Nuclear Information System (INIS)

The variation in the superconducting properties of various binary alloys of transition metal-germanium systems was surveyed by studying sputter deposited samples prepared under various conditions. The primary interest has been to study the formation of the stoichiometric A-15 compounds T_3Ge.

Energy Technology Data Exchange (ETDEWEB)

Dominating factors in plasma nitriding and plasma condition that makes nitriding possible in plasma nitriding process of metals having hard oxide film were studied. In case of stainless steel, oxide film sputtering was easier comparing to nitriding layer. Three phenomena such as sputtering of oxide layer, formation of nitriding layer and sputtering of nitriding layer occurred simultaneously. Nitriding was achieved when the formation of nitriding layer reached the peak comparing to the removal of nitriding layer after the removal of oxide layer. Situations of metallic surface of stainless steel in surface nitriding were divided into four categories and they were, situation where oxide layer remained as it is, situation where nitriding layer was formed although oxide layer remained in some part, situation where only nitriding layer was formed and situation where sputtering was carried out. It was revealed ...

Energy Technology Data Exchange (ETDEWEB)

Optical absorptance spectra of A-15 compounds were taken using a calorimetric technique in the range 0.2 eV to 4.0 eV. Thermomodulation spectra were taken on several A-15 sputtered films.

Energy Technology Data Exchange (ETDEWEB)

We report experimental evidence of a previously unseen species-dependent effect in the transverse emittances of momentum analysed /sup 28/Si/sup -/, /sup 58/Ni/sup -/ and /sup 197/Au/sup -/ ion beams generated by caesium ion sputtering. The high-resolution emittance measurement techniques employed in this work have enabled us to estimate the energy spreads of these ion beams; differences in the widths of the energy distributions are the origin of the observed differences in emittances of the ion beams investigated. (author).

Energy Technology Data Exchange (ETDEWEB)

Surface probe and laser-induced fluorescence measurements in ISX-B and EBT-S have made significant contributions to the understanding of plasma edge characteristics and plasma-surface interactions in these devices. Where comparison is possible, these techniques have led to results which are consistent with plasma diagnostics. Charge-exchange neutral sputtering and self-ion sputtering have been identified as the dominent heavy impurity release mechanisms in ISX-B and EBT-S, respectively.

Energy Technology Data Exchange (ETDEWEB)

Computation of effective flow properties of fluids in porous media based on three dimensional (3D) pore structure information has become more successful in the last few years, due to both improvements in the input data and the network models. Computed X-ray microtomography has been successful in 3D pore imaging at micron scale, which is adequate for many sandstones. For other rocks of economic interest, such as chalk and diatomite, submicron resolution is needed in order to resolve the 3D-pore structure. To achieve submicron resolution, a new method of sample serial sectioning and imaging using Focused Ion Beam (FIB) technology has been developed and 3D pore images of the pore system for diatomite and chalk have been obtained. FIB was used in the milling of layers as wide as 50 micrometers and as thin as 100 nanometers by sputtering of atoms from the sample surface. The focused ion beam, consisting of gallium ions (Ga+) accelerated by ...

Energy Technology Data Exchange (ETDEWEB)

Modifications to the reference concept were studied and the best approaches defined. The impact of the high efficiency multibandgap solar array on the reference concept design is considered. System trade studies for several solid state concepts, including the sandwich concept and a separate antenna/solar concept, are described. Two solid state concepts were selected and a design definition is presented for each. Magnetrons as an alternative to the reference klystrons for dc/rf conversion are evaluated. System definitions are presented for the preferred klystron and solid state concepts. Supporting systems are analyzed, with major analysis in the microwave, structures, and power distribution areas. Results of studies for thermal control, attitude control, stationkeeping, and details of a multibandgap solar cell study are included. Advanced laser concepts and the meteorological effects of a laser beam power transmission concept are considered.

International Nuclear Information System (INIS)

We have studied the correlation between the chemical state and the oxygen-sensing properties of an iron oxide thin film using a setup that allows simultaneous sensor resistance measurements and X-ray photoelectron spectroscopy (XPS) data acquisition. The gas exposures were performed at the highest operating pressure of the XPS spectrometer at a controlled sample temperature which allows direct comparison between the sensor response and the chemical state of the surface. The iron oxide film was modified by a sequence of argon ion sputtering steps and the induced changes in the chemical state, resistance, and sensitivity to oxygen were investigated. The sputtering was found to reduce the iron from the Fe"3"+ to the Fe"2"+ state and to decrease the sensor resistance. The measured sensitivity to oxygen first increased by a factor of two but then collapsed to its original level. The mechanism for oxygen sensing was found to be filling of the oxygen ...

International Nuclear Information System (INIS)

Selective formation of ZnO nanodots was accomplished by metalorganic chemical vapor deposition on nanopatterned SiO_2/Si substrates. Self-organized ZnO nanodots were selectively formed in nanopatterned lines of Si created by etching of SiO_2 with focused ion beam (FIB), whereas any nanodots were hardly observed on the SiO_2 surface in the vicinity of the FIB-sputtered Si areas. The mechanism of the selective formation of ZnO nanodots on FIB-nanopatterned lines is mainly attributed to the effective migration of Zn adatoms diffusing on the SiO_2 surface into the Si lines followed by the nucleation at surface atomic steps and kinks created by Ga"+ ion sputtering. Cathodoluminescence measurements confirmed that the emission originated from the selectively grown ZnO nanodots.

International Nuclear Information System (INIS)

Pattern formation on GaAs by Ga"+ focused-ion-beam (FIB) irradiation and subsequent Cl_2 gas etching was carried out. A higher etch rate at the FIB-irradiated area compared with that not irradiated under Cl_2 gas allows pattern construction without a mask process. The degree of residual crystal damage was evaluated using photoluminescence (PL) intensity measurements. The PL intensity in the etched region was one order of magnitude stronger than that of FIB sputtering, and was several times stronger than that of Ga"+ FIB-assisted Cl_2 etching. Etch depths of the order of 100 nm, which is five times deeper than that obtained by FIB sputtering, were efficiently performed using moderate Ga"+-ion doses.

International Nuclear Information System (INIS)

Contrary to the electronic excitation induced phenomena of desorption and sputtering, we observed incorporation of oxygen in a thin Fe film during its irradiation with swift heavy ions. It is observed that the adsorbed oxygen diffuses in to the Fe film. The incorporation of oxygen and its diffusion in the bulk of the film is a manifestation of extremely large electronic energy deposition by the incident ions. It is shown that the experimentally observed high diffusivity of oxygen in Fe during irradiation is due to the existence of transient melt phase of Fe.

Science.gov (United States)

Partial Contents: Ternary Compounds; Granular Superconductors; Superconductivity in (SN)x and its Halogen Derivative (SNBr0.4)x; Studies of cuCl at Elevated Pressures; Superconducting Properties of Hydride Systems; Thin Film Superconducting Materials Research; Synthesis of Superconducting Nb3Si using High Pressures; Synthesis of Unstable A-15 Compounds by Epitaxial Recrystallization of Ion Implanted Layers; and Sputtering of Nb3Si.

Energy Technology Data Exchange (ETDEWEB)

In a reactor environment, the surface of a limiter or wall is primarily determined by the mechanism of erosion and deposition of surface material. It should be possible to use pellet injection to reduce net erosion to zero everywhere if low-Z materials are used for the surface. Erosion rates can, in general, be minimized by large area limiters and high plasma temperatures, which transmit power to the walls with less sputtering. Under ideal steady state conditions the wall surface is dominated by metallurgical effects in the wall.

International Nuclear Information System (INIS)

The structure and properties of composite powder coatings on the base of titanium carbide are studied. It is shown the electron-beam welding deposition of powders on the base of nickel and titanium carbide allows to produce of high-quality wear-resistant coatings which superior in density and hardness compared with sputtered ones. Changes of hardening phase volume percentage as well as composition of metal matrix make possible to control coatings hardness

Energy Technology Data Exchange (ETDEWEB)

An x-ray zone plate was fabricated using the novel approach of focused ion beam (FIB) milling. The FIB technique was developed in recent years, it has been successfully used for transmission electron microscopy (TEM) sample preparation, lithographic mask repair, and failure analysis of semiconductor devices. During FIB milling, material is removed by the physical sputtering action of ion bombardment. The sputter yield is high enough to remove a substantial amount of material, therefore FIB can perform a direct patterning with submicron accuracy. The authors succeeded in fabricating an x-ray phase zone plate using the Micrion 9500HT FIB station, which has a 50 kV Ga{sup +} column. Circular Fresnel zones were milled in a 1.0-{micro}m-thick TaSiN film deposited on a silicon wafer. The outermost zone width of the zone plate is 170 nm at a radius of 60 {micro}m. An achieved aspect ratio was 6:1.

Science.gov (United States)

Superconductivity of binary alloys spanning the A-15 compounds V/sub 3/Si, V/sub 3/Ge, V/sub 3/Ga, and V/sub 3/Al and the pseudobinary derivatives of these stoichiometric compounds was surveyed by studying samples prepared by rf-sputtering from alloy cathodes. The possible formation of the hypothetical A-15 binaries ''V/sub 3/P,'' ''V/sub 3/B,'' and ''V/sub 3/C'' and their pseudobinary formation with V/sub 3/Si was also explored. Efforts to form these hypothetical alloys were not successful. The T/sub c/'s were measured resistively and the structure and lattice constants were determined by x-ray analysis. A maximum T/sub c/ of 11.7/sup 0/K was obtained for A-15 V/sub 3/Al, and the importance of a suitable deposition temperature and high sputtering pressures was examined. It is proposed that large variations of T/sub c/ among ...

Energy Technology Data Exchange (ETDEWEB)

A versatile, high brightness, volume type, low power RF source, capable of producing positive ion beams with intensities as high as 1 mA from gaseous feed materials and microamperes of negative ion beams has been characterized. The source can also be operated as a plasma sputter negative ion source to generate up to 1 mA of a selected species. The performance of the source in the positive and negative volume modes of operation can be greatly enhanced by addition of a removable, water cooled filament assembly in place of the negative sputter probe. For examine, the material utilization efficiencies of gaseous feed species can be more than doubled, total current intensities increased up to 40%, molecular dissociation fractions increased by 20% and minimum operating pressures reduced by a factor of four when operated in the volume mode. These added electrons also favorably effect, as a consequence of lower pressures, the emittance apparently ...

Energy Technology Data Exchange (ETDEWEB)

Nano-wire arrays of Niobium were produced by small angle sputtering on facetted sapphire, using the self shadowing effect of the facets. A wire width of about 80 nm was adjusted, the mean (maximum) wire height was about 20 nm (30 nm), the length can be in the cm range. Meander-film morphologies of 20 nm mean (26 nm maximum) thickness were produced by conventional sputtering onto smooth sapphire substrates at elevated temperatures. The morphology of the wires was investigated with atomic force microscopy (AFM), using contact mode. Meander-films were studied by scanning tunnelling microscopy (STM). Hydrogen loading was performed by instantaneously increasing the hydrogen gas pressure above the solubility limit. Thus, an elongated hydride could be monitored in an about 30 nm thick wire. STM studies on meander-films show the presence of cylindrical hydrides. Local out-of-plane and in-plane expansion can be explained by the formation of hydrides, ...

International Nuclear Information System (INIS)

Epitaxial metastable (GaSb)/sub 1-x/Ge/sub x/ alloys with compostions across the pseudobinary phase diagram have been grown on (100) GaAs substrates by multitarget rf sputtering. An essential feature allowing the growth of these metastable materials was low-energy ion bombardment of the growing film during deposition to enhance surface diffusion, promote mixing, and preferentially sputter incipient second-phase precipitates. Annealing experiments indicated that the metastable films exhibit good high-temperature stability and that they transform through a continuous series of GaSb-rich and Ge-rich phases in which the solute concentrations decrease until the equilibrium two-phase alloy is obtained. While the calculated free-energy difference between the single-phase metastable and equilibrium states is approx.18 meV, the measured activation barrier for the transformation is approx.3 eV. All films were p-type with room-temperature hole ...

Energy Technology Data Exchange (ETDEWEB)

In order to enhance the resistance to the pitting corrosion due to asepsis processes and to avoid structural fractures in dentistry drills, a plasma immersion ion implantation (PIII) treatment using nitrogen has been performed. The selected drill samples, made of AISI 434 based stainless steel with a 0.670 mm diameter, were treated at a -1kV bias between 350 C and 450 C, this temperature being controlled by both a 20-50 {mu}s pulse width and a 200-1000 Hz repetition rate in the bias. The drills were analysed by cyclic potentiodynamic tests showing a good pitting corrosion resistance when treated at around 400 C, as follows from a resulting very low hysteresis loop. Yet, the resistance appears somehow diminished by the presence of sputtering when processed at temperatures near 450 C. It is also found that the PIII nitriding effectiveness appears to be limited by the appearance of uniform corrosion. Finally, X-ray diffraction of the samples has revealed the presence ...

Science.gov (United States)

A focused ion beam (FIB) technique was applied to cross-sectional specimen preparation to observe an interface between a plasma sprayed coating and an aluminum (Al) substrate by transmission electron microscopy (TEM). The surface of the sprayed coating film has a roughness of several tens of microns. Sputter rates for the coating film and the substrate are greatly different. The rough surface and the difference in sputter rate cause problems in making TEM specimens with smooth side walls. The top surface of the coating film was planerized by the FIB before fabricating the TEM specimen. The interfaces were investigated by TEM and energy-dispersive X-ray (EDX) analysis. The TEM observation revealed that there is a 10 nm thick amorphous layer at the interface between the coating film and substrate. The coating film consists of two kinds of sublayers with bright and dark contrast. The bright contrast sublayers were amorphous layers with thickness ...

International Nuclear Information System (INIS)

The composition of sputter-deposited HgS films was determined by electron microprobe analysis. From the relative x-ray intensity as a function of film thickness, the depth of the ionizations that produce SK sub(#alpha#) and HgM sub(#alpha#) was found to be approximately 0.65 #mu#m at an accelerating voltage of 15 kV. This value agreed well with a value calculated from Castaings' empirical law after absorption correction. The determination of film composition was limited to sufficiently thicker films than this critical value, usually 1 - 2 #mu#m thick. The relation between the conposition of bulk standard determined by chemical analysis and the x-ray intensity ratio was used for the correction of film composition. The results showed that the crystal structure of HgS films was independent of the composition, i.e., the growth of metastable #betta#-HgS films was not caused by the nonstoichiometry, and that the composition of #alpha#-HgS films was not always ...

International Nuclear Information System (INIS)

In the context of sputtering experiments, studying the back-scattering of fast ion beams is a useful way to study inelastic ion-surface interactions, since then the trajectories and energies of the particles are well defined. This same argument holds for the scattering of fast molecular ions. We give a short account of our experiment where N"+_2 was scattered from a Ni(111) surface. The measured energy distributions of scattered N atoms are discussed with regard to vibrational and rotational energy transfer during scattering. (G.Q.).

Energy Technology Data Exchange (ETDEWEB)

The composition and thickness of etch residues on the base of submicrometer via holes cannot be surmized from data on larger features. Auger sputter depth profiles were used to compare etch residues in 0.55 {mu}m via holes produced by different etch processes and remaining after different cleans. These residues varied significantly in composition and thickness with the processing history of the sample and from those on larger features. A focused ion beam (FIB) sample preparation was developed to expose the bases of via holes and to help reduce sample charging. (author).

Energy Technology Data Exchange (ETDEWEB)

An RF plasma sputter type heavy negative ion source, which can deliver mA-class negative ion beams (12.1 mA, 1.6 mA and 2.3 mA for Cu{sup -}, C{sup -} and C{sub 2}{sup -} currents, respectively) in dc-mode operation, has been developed. In ion source, a dense plasma of 10{sup 11} cm{sup -3} order was generated in the xenon gas pressure of 10{sup -3}-10{sup -2} Pa with an rf (13.56 MHz) power of 200 - 300 W by using an RF coil, and a relatively large sputtering target of 42 mm in diameter was used. As for intense negative ion beams of silicon or boron which are important dopants for semiconductor fabrication, negative ion extraction properties of the negative ion source was investigated. The extracted total negative ion currents of 4.4 mA for a silicon target and 2.8 mA for a LaB{sub 6} target were obtained after electrons were eliminated by magnetic field near the extraction hole. From results of mass-analysis, it was found that Si{sup -} ...

International Nuclear Information System (INIS)

An IAEA databank lists a number of reported cases of illicitly trafficked nuclear or other radioactive materials. Apart from the traditional concern with nuclear proliferation, the post September 11th public is now wary of a possible attack by terrorists with a nuclear or radiation dispersion device (RDD). Until now, the seized quantities have not been sufficient to manufacture a nuclear explosive device, but they might be enough to construct an RDD. Recognizing the latent global challenge to public health and safety, the G8 States (Japan, USA, Germany, France, UK, Italy, Canada, and Russia) have called for 'joint international efforts to identify and suppress illicit supply' of, and demand for, nuclear material and to deter potential traffickers. One measure gaining in significance is to identify seized material and trace it back to its origin the objective of an emerging science known as nuclear forensics. Repeatedly nuclear or other radioactive material of unknown origin are ...

International Nuclear Information System (INIS)

Reactively sputtered tantalum nitride (Ta_2N) has been investigated as a diffusion barrier between Pd_2Si and aluminum and CoSi_2 and Al. Ta_2N is found to be an excellent matallurgical diffusion barrier for the two systems up to 555 "0C, with no intermixing observed in Rutherford backscattering and Auger electron spectroscopic studies. Schottky barrier devices n-Si/Pd_2Si/Ta_2N/Al were excellent and showed no deterioration after annealing at 500 "0C. However, similar devices with CoSi_2 contacts and Ta_2N barrier showed a creation of high contact resistance between the silicide and the as-deposited nitride.

Energy Technology Data Exchange (ETDEWEB)

Carbon films have been made by a variety of techniques, including evaporation, sputtering, and laser or thermal pyrolysis of organic polymers. Polyacrylonitrile (PAN) is often used as a carbon precursor, since low-temperature thermo-oxidative pretreatment produces a material which can be pyrolyzed without loss of shape. This is the basis for the production of carbon fibers with good mechanical properties. We report here the formation of very thin films of carbon (500 to 1500 A) by pyrolysis of spin-cast PAN. Using this technique, large, conductive films can be made which are sufficiently robust to allow intact lift-off and transfer of the films from one substrate to another. Such films are chemically inert, but can be photolithographically patterned and etched with an oxygen plasma.

Energy Technology Data Exchange (ETDEWEB)

We have investigated via SQUID magnetometry and polarised neutron reflectivity the exchange-bias effect in CoO/Co sputtered multilayers. In particular, we studied the magnetisation reversal and the time relaxation of the exchange-bias field close to the coercive field H{sub c1}. Neutron intensities of all four cross sections (I++, I+-, I-+, I-) were recorded at the position of the first multilayer Bragg peak while scanning the magnetic field. From such scans we infer that the magnetisation reversal for the ascending as well as for the descending branch of the magnetic hysteresis occurs not by in-plane rotation but through domain-wall movements. The exchange-bias field, H{sub EB}, is strongly affected by thermal fluctuations. H{sub EB} decreases, following an exponential decay function with a half-life time of about 580 s at T=240 K. (orig.)

International Nuclear Information System (INIS)

Highly ordered arrays of Ni nanoholes and Fe20Ni80 antidots have been prepared, respectively, by replica/antireplica processing and sputtering techniques using nanoporous alumina membranes as templates. Geometrical characteristics as nanohole/antidot diameter, interpore distance and the overall hexagonal symmetry of arrays are controlled through the original templates. Experimental data on their hysteresis and magnetic domain structure have been taken by vibrating sample magnetometry and magnetic force microscopy, respectively. An analysis of the magnetization process, resulting magnetic anisotropy and magnetic domain structure is summarized considering the influence of those geometry aspects. In particular, the hexagonal symmetry and the density of nanohole/antidots determine the overall magnetic behavior, which is of interest in future high-density magnetic storage systems.

Energy Technology Data Exchange (ETDEWEB)

The optical emission of excited H reflected from clean Cu(110) after impingement of H/sup +/ and H/sub 2//sup +/ in the energy range of 250 eV to 20 keV per nucleon at 70/sup 0/ angle of incidence to the surface normal was measured. For incident 10 keV H/sub 2//sup +/, the highest excited hydrogen state detected was the n=10 level. The Hsub(..cap alpha..) yield was found to be fluence and energy dependent. This effect is attributed either to fast sputtered hydrogen, surface roughness or to an increase with hydrogen concentration in electron states of p-like symmetry near the Fermi level of copper. The Hsub(..cap alpha..) yield per reflected nucleon shows approximately an exponential dependence on both projectile energy per nucleon and scattered particle reciprocal velocity perpendicular to the surface.

International Nuclear Information System (INIS)

A series of sputtered tungsten-carbon multilayer structures with periods ranging from 2 to 12 nm in the as-prepared state and after annealing at 500 degrees C for 4 hours has been studied with high resolution transmission electron microscopy. The evolution with annealing of the microstructure of these multilayers depends on their period.As-prepared structures appear predominantly amorphous from TEM imaging and diffraction. Annealing results in crystallization of the W-rich layers into WC in the larger period samples, and less complete or no crystallization in the smaller period samples. X-ray scattering reveals that annealing expands the period in a systematic way. The layers remain remarkably well-defined after annealing under these conditions.

International Nuclear Information System (INIS)

Focussed ion beam (FIB) processing has been applied to the fabrication of novel InP-based cleaved coupled cavity (CCC) quantum cascade lasers (QCL). Gas assisted etching using XeF_2 has been shown to significantly reduce the redeposition of sputtered material onto the mirror surfaces during final milling. For the unprocessed laser a broad spread of lasing peaks are observed between 9.72#mu#m to 9.78#mu#m at a current of 380mA (1kA/cm"-"2). After FIB processing, substantial side mode suppression is observed on applying a current of 20mA (100A/cm"-"2) to the short section and the main lasing peak is observed at 9.77#mu#m.

International Nuclear Information System (INIS)

The authors present an investigation of structural changes occurring in bilayer stacks with crystalline columnar growth when one of the layers is substituted by layers known to grow amorphous. In Co/Cu multilayers the Co layers were substituted by CoZr layers of varying Zr content and layer thickness. Structural characterization was performed by transmission electron microscopy (TEM). They show that the amorphization of the CoZr layers leading to a destruction of the columnar growth depends both on the Zr content and on the thickness of the CoZr layers. Additionally a change to textured growth with a normal to the substrate occurs with increasing Zr content. They explain their observations by a simple picture based on the hard sphere model.

International Nuclear Information System (INIS)

The use of Auger electron spectroscopy (AES) combined with in situ sputter etching for revealing the metallurgy of the metal-semiconductor interface is presented. The physical basis, measurement techniques, and data interpretation for Auger analysis of thin-film structures are briefly reviewed. Results of a detailed study of an alloyed multilayered contact (Ni/Au-Ge) on n-type epitaxial GaAs are summarized to illustrate how electrical and metallurgical contact properties can be correlated using AES. In addition, the results of a study of the growth kinetics and chemical phase identification of palladium silicide on single-crystal Si is given, as well as the initial results of a study of aluminum-palladium silicide interaction at elevated temperature.

International Nuclear Information System (INIS)

Composite nitrides (such as BN, TiN) are widely used in various industrial applications because of their extreme wear and corrosion resistance, thermal and electrical properties. in order to obtain composite materials with these optimal properties, it is important to elucidate whether any chemical reactions occur at nitride/metal interfaces, e.g., those involving BN-Ti/TiN. Materials of interest include the deposition by PVD of Ti and TiN on BN substrates. Some of these systems were then subjected to varying degrees of physical and thermal alteration. Detailed X-ray photoelectron spectroscopy (XPS) has therefore been rendered of these interfaces using cross-sectional display and sputter etching. Resulting structural and morphological features have been investigated with transmission electron microscopy (TEM) and X-ray diffraction (XRD). Diffusion of the nitridation, oxynitride formation and interfacial growth are of general interest.

Energy Technology Data Exchange (ETDEWEB)

PVD-coatings based on TiB{sub 2} are expected to show high wear resistance and low tendency of adhesion on metal forming tools. Coating adhesion and morphology can be modified over a wide range by varying the content of nitrogen (N{sub 2}) and the deposition parameters power and bias voltage. All coatings were deposited using commercial unbalanced magnetron equipment, the deposition was homogeneous in a volume of 400 x 400 x 400 mm{sup 3}. Hipped and hot pressed TiB{sub 2}-targets were used, nitrogen (N{sub 2}) was added as gas, Ti and Al by a solid Ti-Al-target. The tribological behaviour was tested by a pin-on-disc wear test. The coatings investigated were TiB{sub 2}, TiAlB(N), TiAl(N) and TiB{sub 2}/TiAl(N). As counterpart in the pin-on-disc wear test, 6 mm diameter spheres of steel (100Cr6), aluminium, brass and bronze were used. The experiments showed a non-uniform wear behaviour. For the combinations TiAlB(N) and TiB{sub 2} versus aluminium, a low wear volume ...

CERN Document Server

Neutrosphic methods in general relativity

CERN Document Server

Applied survey methods

Science.gov (United States)

High quality La/sub 1.8/Sr/sub 0.2/CuO/sub 4/ and YBa/sub 2/Cu/sub 3/O/sub 7/ superconducting thin films, with zero resistance at 88 K, have been made by dual-ion-beam sputtering of metal and oxide targets at elevated temperatures. The films are about 1.0 ..mu..m thick and are single phase after annealing. The substrates investigated are Nd-YAP, MgO, SrF/sub 2/, Si, CaF/sub 2/, ZrO/sub 2/-9% Y/sub 2/O/sub 3/, BaF/sub 2/, Al/sub 2/O/sub 3/, and SrTiO/sub 3/. Characterization of the films was carried out using Rutherford backscattering spectroscopy, resistivity measurements, transmission electron microscopy, x-ray diffraction, and secondary ion mass spectroscopy. Substrate/film interaction was observed in every case. This generally involves diffusion of the substrate into the film, which is accompanied by, for example, the replacement of Ba by Sr in the YBa/sub 2/Cu/sub 2/O/sub 7/ structure, in the case of SrTiO/sub 3/ substrate. The best substrates were those that ...

International Nuclear Information System (INIS)

The purpose of this work was to investigate the optical properties of several high T/sub c/ compounds in the form of sputtered films. The measurements are used toward this end: optical absorptance (using a calorimetric technique near 4.2K), which yields (after Kramers-Kronig analysis) the complex dielectric function, and thermoreflectance (which measures the change in reflectance in the optical range when a 1 to 10_0K temperature wave is applied), performed at two ambient temperatures (80 and 300_0K), yielding the differential dielectric function. The sputtered films included Nb"3Ge, Nb"3Al, V"3Ga and Nb"3Ir. It is noted that Nb"3Ir is not a high T/sub c/ superconductor. The thermoreflectance on the bulk samples V"3Si, V"3Ge and single crystal Cr"3Si were not performed because the samples were not in the form of thin films. The thermomodulation studies are correlated with the absorptance measurements in comparison to band structure ...

International Nuclear Information System (INIS)

Several metallurgical coatings have been developed that provide good tribological performances in high-temperature liquid sodium and that are relatively unaffected by neutron fluences to 6 X 10/sup 22/ n/cm/sup 2/ (E > 0.1 MeV). The coatings that have consistently provided the best tribological performance have been the nickel aluminide diffusion coatings created by the pack cementation process, chromium carbide or Tribaloy 700 trade mark (a nickel-base hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing materials applied by the electro-spark deposition process. The latter process is a relatively recent development for nuclear applications and is expected to find wide usage. Other coating processes, such as plasma-spray coating, sputtering, and chemical vapor deposition, were candidates for use on various components, but the ...

International Nuclear Information System (INIS)

This paper deals with the characterization of passive films formed on stainless steel (26% Cr and 0 to 3%Mo). The influence of the applied passivation potential and the effect of molybdenum additions to steel upon the composition profiles of passive films formed in an aqueous NaCl solution (3.5% at pH 2.5) are studied. The technique involved is Auger electron spectroscopy combined with ion sputtering. Some electrochemical techniques have been used in conjunction. A quantitative approach of the Auger spectra during the progressive removal of the passive film is described. The peak-to-peak height of the Auger lines are treated in order to yield the atomic fraction of the various elements present in a given subsurface layer. The analytical study of the film by electron spectroscopy indicates that molybdenum plays a part at the metal-oxide interface where this element acts on the chromium diffusion process. This phenomenon, which depends on the imposed potential, may ...

International Nuclear Information System (INIS)

Marker experiments for studying the mass transport through a palladium silicide layer on a crystalline substrate during thermal oxidation at 700 to 850 deg C have been reported recently. In this work argon gas embedded in amorphous silicon during sputtering was implemented as the inert marker and the oxidation of PdSi was processed above 900 deg C. At this high-temperature oxidation silicon-rich silicide PdSisub(y), with y exceeding 5, may be obtained. This can be anticipated by considering the Pd-Si phase diagram which shows the liquid phase may appear at an annealing temperature above 892 deg C. As a result, a non-stoichiometric and non-uniform silicide layer may develop at the sample surface. Marker analysis showed that both palladium and silicon dissociated at the Pdsub(x)Si/ SiO_2 interface and moved to the substrate with the silicon being the dominant diffuser. The Rutherford backscattering spectra (RBS) showing the oxide film and composition isothermally ...

Energy Technology Data Exchange (ETDEWEB)

A systematic study was made on MoSi{sub 2}-based nanolayer coatings. Alternating layers with thickness 1-20 nm were prepared by sputtering. Nitrided MoSi{sub 2} has a very high crystallization temperature, >1000 C, and MoSi{sub 2}Nx (x=3-4) can be used as a stable second phase reinforcement or diffusion barrier coatings. Mechanical properties depend strongly on phase and morphology of the layers: hardness and modulus is significantly increased in the crystallization. The nanolayers have much higher hardness but lower modulus (which project higher toughness in the nanolayers). Wear resistance is improved with decreasing layer thickness. Single phase MoSi{sub 2}Nx (x=0-4.2) has a wide range of hardness and modulus with varying N content and annealing, suggesting the possibility of engineering MoSi{sub 2}Nx to produce different material properties for different mechanical applications. Most of this paper is made up of viewographs.

Energy Technology Data Exchange (ETDEWEB)

The Ti and Ti-Al coatings were deposited onto hot-worked AISI H11 steel substrates and plasma nitrided at 900 C. The Ti coated samples were successfully nitrided, while cracking and delamination of the Ti-Al coating was observed during nitriding. The formation of [delta]-TiN and [epsilon]-Ti[sub 2]N phases were detected after plasma nitriding of the Ti coating. During plasma treatment of the Ti-Al coating, the initial Ti[sub 3]Al and Al phases were paartially transformed into TiAl phase. The martensite transformation of the substrate material was found. The as-deposited Ti coating has a fibrous structure, while the structure of the as-sputtered Ti-Al coating is columnar. The superficial Vickers microhardness of plasma-nitrided Ti coating was 2200 HV 0.03 and the critical load of higher than 50 N indicates very good coating-to-substrate adhesion. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The enhancement of positive secondary ion yields of silicon due to the presence of oxygen has been investigated quantitatively by low-energy (5 keV) oxygen implantation. Implantation and sputter profiling with 9 keV In/sup +/ were performed in the same ion microprobe instrument. Depth profiles of substrate and implanted oxygen atoms were measured for fluences ranging from 5x10/sup 15/ to 4x10/sup 16/ O-atoms/cm/sup 2/. The oxygen concentration, c(O), in the sample was deduced from the implanted fluence and the range distribution in the Gaussian approximation. It was found that the oxygen-enhanced Si/sup +/ intensity is proportional to c(O)sup(x) (with x=1.4) in the concentration regime, 1.5<=c(O)<=30 at%. The O/sup +/ intensity shows a similar dependence for c(O)> or approx.20 at.%.

International Nuclear Information System (INIS)

Microfabrication processes for Y-Ba-Cu-O films have been investigated, using ion-beam techniques. High-T_c superconducting lines as narrow as 0.8 #mu#m have been fabricated from epitaxial YBa_2Cu_3O_7 _- _y films by Ar ion-beam etching (IBE), combined with focused ion-beam (FIB) lithography. The resulting lines, 1.3 #mu#m wide and 2 mm long, showed a zero resistance temperature of 81 K and a critical current density of 1.9 x 10"4 A/cm"2 at 77.3 K. Maskless etching was carried out using 130-keV au"+ focused ion-beam (FIB) with a 0.1-#mu#m-diameter beam. A 50-nm-thick film was patterned into 0.3-#mu#m-wide lines at a dose of 5 x "1"6 ions/cm"2. In comparison with Ar IBE, Cl_2 reactive ion-beam etching (RIBE) exhibited an enhancement effect in sputtering yield. Ion implantation with 300-keV Si"+ "+ FIB also indicated the possibility to produce submicrometer patterns by selectively modifying film properties from superconductive to normal or insulting.

CERN Document Server

An in-plane uniaxial magnetic anisotropy has been observed in thin Co films normally deposited onto obliquely sputtered Ta and Pt underlayers. Associated with this anisotropy is an augmented easy axis coercivity. The in-plane easy axis is, in most cases, perpendicular to the incident deposition plane. Microstructural results indicate that grains are well connected along the magnetic easy axis but are separated by long continuous voids along the hard axis, which is ascribed to a geometric shadowing effect due to the oblique incidence deposition of the underlayer. Hence, the magnetic anisotropy mimics the film growth anisotropy. It is therefore believed that the observed magnetic properties are due to magnetostatic shape anisotropy effects. In-plane coercivity and anisotropy field are shown to increase with underlayer deposition angle, underlayer thickness and magnetic layer thickness. The choice of capping layer is also observed to dramatically alter the magnetics, ...

Energy Technology Data Exchange (ETDEWEB)

The Holifield Radioactive Ion Beam Facility (HRIBF) now under construction at the Oak Ridge National Laboratory will use the 25-MV tandem accelerator for the acceleration of radioactive ion beams to energies appropriate for research in nuclear physics; negative ion beams are, therefore, required for injection into the tandem accelerator. Because charge exchange is an efficient means for converting initially positive ion beams to negative ion beams, both positive and negative ion sources are viable options for use at the facility; the choice of the type of ion source will depend on the overall efficiency for generating the radioactive species of interest. A high-temperature version of the CERN-ISOLDE positive ion source has been selected and a modified version of the source designed and fabricated for initial use at the HRIBF because of its low emittance, relatively high ionization efficiencies and species versatility, and because it has been engineered for remote installation, removal ...

International Nuclear Information System (INIS)

Focused-ion beam (FIB) milling provides rapid fabrication of individual cylindrical submicrometer channels with reproducible dimensions (#+-#5% diameters) through 8-#mu#m thick poly(methylmethacrylate) (PMMA) films. PMMA films are spincast on sacrificial Si carriers and sputter-coated with Au before the 30-kV gallium FIB milling process. By adding a trace amount of poly(ethyleneoxide) and poly(dimethylsiloxane) to the PMMA solution before casting, the films can be released for subsequent mounting in microfluidic devices to create hybrid microfluidic-nanofluidic multilevel architectures. In situ FIB sectioning demonstrates the smooth cylindrical surface within the pore. Placing a milled film in contact with an aqueous fluorescein solution fills the channel by capillary action, as verified by confocal fluorescence microscopy. Confocal fluorescence of dyed films reveals that the pores span the thickness of the PMMA film. Small arrays of channels with a defined number ...

Energy Technology Data Exchange (ETDEWEB)

The goal of this project was to develop a new technology for preparing samples for transmission electron microscopy (TEM) on the basis of ion fine beam processing. For this purpose processes of ion-beam-assisted removal (sputtering), separation, sample handling and ion-beam-assisted chemical etching as well of system-inherent components were examined. As an alternative to a Ga-source a liquid-metal ion source based on a AuGeSi alloy was developed, characterised and used in the FIB 4400. [German] Aufgabe des Projektes war die Entwicklung einer neuen Technologie zur Probenpraeparation fuer die Transmissions-Elektronenmikroskopie (TEM) auf der Basis der Ionenfeinstrahlbearbeitung. Dazu wurden Prozesse der ionenstrahlgestuetzten Abtragung (Sputtern), der Abscheidung, des Probenhandling, des ionenstrahlgestuetzten chemischen Aetzens sowie systemeigener Komponenten untersucht. Als Alternative zur Ga-Quelle wurde eine Fluessigmetall-Ionenquelle auf der Basis einer AuGeSi ...

Energy Technology Data Exchange (ETDEWEB)

Most of the organic electronic devices are nowadays fabricated under poor vacuum conditions. In this regard, there is only little knowledge about the impact of contamination of the metal electrode on the charge injection barrier in this kind of electronic devices. In our study we have performed X-ray and ultra violet photoemission spectroscopy (XPS, UPS) on interfaces between the organic semiconductor -sexithiophene and sputter cleaned (ideal) metals as well as contaminated (realistic) metals. As metal substrates we have used silver, gold, palladium, and platinum. These metals provide us a wide range of metal work functions from 4.2 eV for silver up to 5.5 eV for platinum. For all interfaces of -sexithiophene and contaminated metals we have observed a reduction of the interface dipole and the hole injection barrier. The charge injection barrier in all four cases is almost independent of the underlying metal (within an error of 0.2 eV) and the interface dipole ...

International Nuclear Information System (INIS)

Computational fluid dynamics are applied to the study of three-dimensional fluid flow in a dense medium plasma reactor (DMPR) under different operating conditions. Reaction mechanisms and rates for the removal of methyl t-butyl ether (MTBE) in a DMPR are developed from experimental data to determine the plasma volume, the rate of interphase mass transfer and the photolysis rate of MTBE via UV emission from the plasma. The simulations utilize the plasma volume determined from the kinetic data to show that the volume of fluid in contact with the plasma in the DMPR only constitutes a maximum of approximately 10% of the fluid intended to be cycled through the plasma tubules. The simulations also predict appreciable pressure gradients on the surface of the pin electrodes, resulting in a small discharge area located away from the region in which the electric field strength is a maximum. This result has been confirmed indirectly through observation in that the pin electrodes ...

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

CERN Document Server

Methods and Procedures for the Verification and Validation of Artificial Neural Networks

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

The three determination methods of alpha activity ration are described, namely geometric progression method, extrapolation method and curve fitting method. The validity of the geometric progression method is demonstrated in the present work. The "2"3"8Pu/("2"3"9Pu + "2"4"0Pu) evaluated by extrapolation method is compared with that by geometric progression method. Also, the "2"3"8Pu/("2"3"9Pu + "2"4"0Pu)evaluated by curve fitting method is compared with that by geometric progression.

Energy Technology Data Exchange (ETDEWEB)

X-ray diffraction enhanced imaging (DEI) is one of X-ray phase-contrast imaging methods, which is applied to inspect internal structures of weakly absorbing low-Z samples. The key problem of the DEI is how to extract phase information which is expressed by refraction-angle images from a series of DEI images measured in different positions of the rocking curve of the analyzer. Three effective extraction methods are presented in this paper: the statistical geometric-optics-approximation method, the maximum refraction-angle method and the Gaussian curve fitting method. They are compared with the existing methods, such as the D. Chapman's geometric optics approximation method and the multiple-images statistical method. A 2D computer simulation experiment is performed to draw comparisons of these ...

Science.gov (United States)

Page 1. Database Creation for Information Processing Methods, ... ARL-TN-0348 May 2009 Database Creation for Information Processing Methods, ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

J-STORE (Japan)

Full Text Available

Science.gov (United States)

PMID:7075772

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Optimization methods are applied to complex problems power systems, economics, and geodesy. Transformation methods and conjugated gradient methods are used to solve the constrained problems in power systems and economics. Conjugated gradient methods are used to solve the unconstrained geodesy problem. Broad applications of the transformation methods are emphasized. In the geodesy problem, the computational efficiency of the Fletcher-Reeves method for optimization of quadratic functions is emphasized. In this problem special storage schemes were used. The method of solution of the economics problem is compared with Beale's method.

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

Science.gov (United States)

Page 1. Adaptive system and method for responding to computer network security attacks Abstract A dynamic network security ...

International Nuclear Information System (INIS)

Austenitic stainless steels (304-type) have been implanted with nitrogen ions in order to investigate the effects of implanted nitrogen on their electrochemical behaviour and on the nature of the passive film formed on the steels in acid (0.5M H_2SO_4). Alloys with two nitrogen doses have been prepared (2.5x10"1"6 and 2x10"1"7 N atoms/cm"2). The implanted alloys have been characterized by "1"5N-NRA (nuclear reaction analysis) and XPS (X-ray photoelectron spectroscopy). Alloy surfaces with well-defined N concentrations were prepared, prior to the electrochemical measurements, by argon-ion sputtering of the implanted material for a fixed time in order to reach a well-defined point on the nitrogen depth profile. The samples were then transferred without exposure to air to an electrochemical cell mounted in an inert gas glove box. The implanted nitrogen modifies the electrochemical behaviour of the alloy. The anodic dissolution in the active state is enhanced, and the ...

Energy Technology Data Exchange (ETDEWEB)

This study attempts to elucidate some of the effects of adding argon, neon and hydrogen to low pressure thermionically supported discharges used for plasma nitriding AISI M2 steel substrates. Four runs were performed at the same substrate temperature (550 C) and bias voltage (500 V), using the following gas mixtures: 8% N{sub 2} in Ar, 8% N{sub 2} in Ne, N{sub 2}+H{sub 2} in equal proportions, and N{sub 2} only. By careful control of the discharge parameters, most of the bombardment energy was transported to the substrates by 500 eV ions in all cases; these were mainly Ar{sup +} ions in the N{sub 2}+Ar run and N{sub 2}{sup +} ions in the other runs, notably by the action of Penning ionization in the N{sub 2}+Ne run. We found that the surface hardness was not significantly influenced by the type of ion delivering the bombardment energy, although we suggest that ions would need sufficient mass to cause (for example) sputtering, if the substrate is susceptible to ...

International Nuclear Information System (INIS)

Scanning ion microscopy with polarization analysis (SIMPA) is used to study the spin-resolved surface magnetic structure of nano-sized magnetic systems. SIMPA is utilized for in situ topographic and spin-resolved magnetic domain imaging as well as for focused ion beam (FIB) etching of desired structures in magnetic or non-magnetic systems. Ultra-thin Co films are deposited on surfaces of Si(1 0 0) substrates, and ultra-thin, tri-layered, bct Fe(1 0 0)/Mn/bct Fe(1 0 0) wedged magnetic structures are deposited on fcc Pd(1 0 0) substrates. SIMPA experiments clearly show that ion-induced electrons emitted from magnetic surfaces exhibit non-zero electron spin polarization (ESP), whereas electrons emitted from non-magnetic surfaces such as Si and Pd exhibit zero ESP, which can be used to calibrate sputtering rates in situ. We report on new, spin-resolved magnetic microstructures, such as magnetic 'C' states and magnetic vortices, found at surfaces of FIB patterned ...

Energy Technology Data Exchange (ETDEWEB)

Amorphization and a dual implant technique have been used to manipulate residual defects that persist following implantation and post-implant thermal treatments. Residual defects can often be attributed to ion-induced defect excesses. A defect is considered to be excess when it occurs in a localized region at a concentration greater than its complement. Sources of excess defects include spatially separated Frenkel pairs, excess interstitials resulting from the implanted atoms, and sputtering. Preamorphizing prior to dopant implantation has been proposed to eliminate dopant broadening due to ion channeling as well as dopant diffusion during subsequent annealing. However, transient-enhanced diffusion (TED) of implanted boron has been observed in pre-amorphized Si. The defects driving this enhanced boron diffusion are thought to be the extended interstitial-type defects that form below the amorphous-crystalline interface during implantation. A dual implantation ...

Energy Technology Data Exchange (ETDEWEB)

Nitrogen has been added to stainless steels to improve mechanical strength and corrosion resistance. High nitrogen steel production is limited by high gas pressure requirements and low nitrogen solubility in the melt. One way to overcome this limitation is the addition of nitrogen in solid state because of its higher solubility in austenite. However, gas and salt bath nitriding have been done at temperatures around 550 C, where nitrogen solubility in the steel is still very low. High temperature nitriding has been, thus proposed to increase nitrogen contents in the steel but the presence of oxide layers on top of the steel is a barrier to nitrogen intake. In this paper a modified plasma nitriding process is proposed. The first step of this process is a hydrogen plasma sputtering for oxide removal, exposing active steel surface improving nitrogen pickup. This is followed by a nitriding step where high nitrogen contents are introduced in the outermost layer of the ...

Energy Technology Data Exchange (ETDEWEB)

The Holifield Radioactive Ion Beam Facility now under construction at the Oak Ridge National Laboratory will use the 25 MV tandem accelerator for the acceleration of radioactive ion beams to energies appropriate for research in nuclear physics; negative ion beams are, therefore, required for injection into the tandem accelerator. Because charge exchange is an efficient means for converting initially positive ion beams to negative ion beams, both positive and negative ion sources are viable options for use at the facility. The choice of the type of ion source will depend on the overall efficiency for generating the radioactive species of interest. Although direct-extraction negative ion sources are clearly desirable, the ion formation efficiencies are often too low for practical consideration; for this situation, positive ion sources, in combination with charge exchange, are the logical choice. The high-temperature version of the CERN-ISOLDE positive ion source has been selected and a ...

Energy Technology Data Exchange (ETDEWEB)

Microfabrication processes for Y-Ba-Cu-O films have been investigated, using ion-beam techniques. High-{Tc} superconducting lines as narrow as 0.8 {mu}m have been fabricated from epitaxial YBa{sub 2}Cu{sub 3}O{sub 7 {minus} {ital y}} films by Ar ion-beam etching (IBE), combined with focused ion-beam (FIB) lithography. The resulting lines, 1.3 {mu}m wide and 2 mm long, showed a zero resistance temperature of 81 K and a critical current density of 1.9 {times} 10{sup 4} A/cm{sup 2} at 77.3 K. Maskless etching was carried out using 130-keV au{sup +} focused ion-beam (FIB) with a 0.1-{mu}m-diameter beam. A 50-nm-thick film was patterned into 0.3-{mu}m-wide lines at a dose of 5 {times} {sup 16} ions/cm{sup 2}. In comparison with Ar IBE, Cl{sub 2} reactive ion-beam etching (RIBE) exhibited an enhancement effect in sputtering yield. Ion implantation with 300-keV Si{sup + +} FIB also indicated the possibility to produce submicrometer patterns by selectively modifying film ...

Science.gov (United States)

Silicon is an attractive alloy-type anode material because of its highest known capacity (4200 mAh/g). However, lithium insertion into and extraction from silicon are accompanied by a huge volume change, up to 300%, which induces a strong strain on silicon and causes pulverization and rapid capacity fading due to the loss of the electrical contact between part of silicon and current collector. Si nanostructures such as nanowires, which are chemically and electrically bonded to the current collector, can overcome the pulverization problem, however, the heavy metal current collectors in these systems are larger in weight than Si active material. Herein we report a novel anode structure free of heavy metal current collectors by integrating a flexible, conductive carbon nanotube (CNT) network into a Si anode. The composite film is free-standing and has a structure similar to the steel bar reinforced concrete, where the infiltrated CNT network functions as both mechanical support and ...

International Nuclear Information System (INIS)

In this work, a focused ion beam (FIB) milling process has been developed to fabricate 50 nm Bi nanowire and transistor structures using FEI-200 dual beam FIB system. For the fabrication, 50 nm bismuth film was thermally evaporated through EBL patterned PMMA windows onto SiO_2 substrates with pre-defined contact pads. Bi nanowire widths ranging from 30 nm to 100 nm have been successfully fabricated by milling out unwanted areas using 30 KeV Ga+ ion beam. A single-pixel-line ion beam blanking technique has been utilised to fabricate Bi nanowire as small as 30 nm in diameter and few micrometers long. In order to form good ohmic contacts for sub 50 nm bismuth nanowires, a drill-and-fill process has been developed using FIB to sputter away the surface oxide of bismuth after the in-situ platinum nanowire contacts deposition. To our knowledge, this is the first time a focused ion beam process has been used to fabricate bismuth nanowire. The fabricated Bi nanowires were ...

International Nuclear Information System (INIS)

A wide variety of thin film coatings, deposited by different techniques and with potential applications in various important areas, have been characterised by the Phase Modulated Spectroscopic Ellipsometer, installed recently in the Spectroscopy Division, B.A.R.C. The Phase Modulated technique provides a faster and more accurate data acquisition process than the conventional ellipsometry. The measured Ellipsometry spectra are fitted with theoretical spectra generated assuming an appropriate model regarding the sample. The fittings have been done objectively by minimising the squared difference (#chi#"2) between the measured and calculated values of the ellipsometric parameters and thus accurate information have been derived regarding the thickness and optical constants (viz, the refractive index and extinction coefficient) of the different layers, the surface roughness and the inhomogeneities present in the layers. Measurements have been done on (i) ion-implanted Si-wafers to ...

Energy Technology Data Exchange (ETDEWEB)

The defects localization in power cables follows several steps: identification, pre-localization and precise localization. Pre-localization methods, other than echo-metry, are presented first: bridge methods, particular case of low voltage networks, future perspectives. Then, the precise localization methods are described: magneto-acoustic method, audible frequencies method. The particular case of underwater and high-voltage cables is considered too (oil and gas leaks detection). (J.S.)

Energy Technology Data Exchange (ETDEWEB)

The Kernel Polynomial Method (KPM) has been successfully applied to tight-binding electronic structure calculations as an O(N) method. Here the authors extend this method to nonorthogonal basis sets with a sparse overlap matrix S and a sparse Hamiltonian H. Since the KPM method utilizes matrix vector multiplications it is necessary to apply S{sup {minus}1}H onto a vector. The multiplication of S{sup {minus}1} is performed using a preconditioned conjugate gradient method and does not involve the explicit inversion of S. Hence the method scales the same way as the original KPM method, i.e. O(N), although there is an overhead due to the additional conjugate gradient part. The authors show an application of this method to defects in a titanate/platinum interface and to a large scale electronic structure calculation of ...

Energy Technology Data Exchange (ETDEWEB)

A new method of pinpointing dielectric fluid leaks on pipe-type and self-contained cables using perfluorocarbon tracer (PFT) is presented. The method has successfully been used on the Con Edison transmission system to locate leaks of dielectric fluid on both types of cables. Application of the PFT technique does not require feeder deenergization and provides major advantages over the conventional method of freeze and pressure testing. Description of the method and results of field application are presented in the paper.

Science.gov (United States)

Skip to Content Cancer Control and Population Sciences Home Applied Research Home Risk Factor Monitoring and Methods Home Diet Usual Dietary Intakes: Background The NCI Method Details of the NCI Method Food Intakes, US Population, 2001-04 Selected Intakes

UK PubMed Central (United Kingdom)

Susceptibility disks impregnated with 35 different antibiotics were assayed by the current Code of Federal Regulations method and by a new method employing an agar overlay. The new...Full Text Available

International Nuclear Information System (INIS)

The applicability of two nuclear analytical methods: radionuclide X-ray fluorescence analysis and radiometric titrations based on precipitate formations was studied in order to determine the heptacaine hydrochloride in solutions. The applied methods were evaluated based on the obtained sensitivity values. (author).

International Nuclear Information System (INIS)

On the problem of alarm when parts are falling in nuclear power plant, the artificial neural network (ANN) alarm method based on the signal time-frequency characteristics was developed. The method was realized by the improved BP algorithm, and demonstrated with the data from simulation experiments

Energy Technology Data Exchange (ETDEWEB)

Abstracts are presented of 63 papers on the following topics: large-scale optimization, interior-point methods, algorithms for optimization, problems in control, network optimization methods, and parallel algorithms for optimization problems.

Science.gov (United States)

... Abstract : Interlaboratory evaluation of the Radiant Panel Method (ASTM E 162-67) for flame spread testing of two flexible foam and one hardboard ...

International Nuclear Information System (INIS)

X-ray diffraction enhanced imaging (DEI) is applied to inspect internal structures of weakly absorbing low-Z sample. How to extract phase information from raw images measured in different positions of rocking curve is the key problem of DEI. In this paper, we present an effective extraction method called polynomial curve fitting method, in order to extract accurate information angular in a fast speed. It is com- pared with the existing methods such as multiple-images statistical method and Gaussian curve fitting method. The experiments results on a plastic cylinder and a black ant at the Beijing Synchrotron Radiation Facility prove that the polynomial curve fitting method can obtain most approximate refraction-angle values and its computation speed is 10 times faster than the Gaussian curve fitting method. (authors)

Energy Technology Data Exchange (ETDEWEB)

The invention relates to a method for purifying a gas mixture containing at least one undesirable gas compound utilizing certain sulfonamide or sulfamide solvents.

International Nuclear Information System (INIS)

The possibility of gamma-absorption identification of the analyzed substance is considered. the basic provisions of the proposed method are concentrated on the example of carbohydrates and hydrocarbons. The above method is tested experimentally on polyethylenes and polystyrene

UK PubMed Central (United Kingdom)

Dynamic clamp is a powerful method that allows the introduction of artificial electrical components into target cells to simulate ionic conductances and synaptic inputs. This method is based...Full Text Available

International Nuclear Information System (INIS)

Radioactive "3"1Si was used as a marker to study metal silicide formation. Activity profiles in the silicides were measured by a combination of ion beam sputtering, radioactivity counting and Rutherford backscattering of charged nuclear particles. It was found that the metal is the diffusing species during Co_2Si, Pt_2Si, NiSi and PtSi formation, while silicon diffuses during CrSi_2, TiSi_2 and ZrSi_2 formation. Silicon was also found to be the diffusing species during second phase formation of CoSi from Co_2Si. However, in this case it was established that the silicon diffuses by a grain boundary and/or interstitial mechanism. Both the metal and silicon diffuse during Ni_2Si and Pd_2Si formation. In an attempt to interpret complex radioactivity profiles a computer program, simulating various diffusion mechanisms during both first and second phase silicide formation, was written. A numerical approach was used whereby silicide growth occurs in small increments and ...

Energy Technology Data Exchange (ETDEWEB)

The partial oxidation of 1,3-butadiene has been investigated over VMoO catalysts synthesized by sol-gel techniques. Surface areas were 9-14 m{sup 2}/g, and compositions were within the solid solution regime, i.e. below 15.0 mol % MoO{sub 3}/(MoO{sub 3} + V{sub 2}O{sub 5}). Laser Raman Spectroscopy and XRD data indicated that solid solutions were formed, and pre- and post-reaction XPS data indicated that catalyst surfaces contained some V{sup +4} and were further reduced in 1,3-butadiene oxidation. A reaction pathway for 1,3-butadiene partial oxidation to maleic anhydride was shown to involve intermediates such as 3,4-epoxy-1-butene, crotonaldehyde, furan, and 2-butene-1,4-dial. The addition of water to the reaction stream substantially increased catalyst activity and improved selectivity to crotonaldehyde and furan at specific reaction temperatures. At higher water addition concentrations, furan selectivity increased from 12% to over 25%. The catalytic effects of water addition were ...

International Nuclear Information System (INIS)

The radionuclide X-ray fluorescence and particle induced X-ray emission methods were used for rapid and nondestructive analysis of metallic glasses. The methods were compared for accuracy and precision with the atomic absorption method. Some results of the analyses of Fe_xNi_8_0_-_xB_2_0 materials are briefly reviewed. The distribution of elements along the width as well as the length and a qualitative analysis of the composition of material surfaces are considered. (author).

Energy Technology Data Exchange (ETDEWEB)

A simple and effective method is presented for the sizing and passage apportionment of multistream plate-fin heat exchangers. Methods for passage arrangement are discussed, and it is shown that a symmetric or mixed passage arrangement is more efficient than a segregated arrangement. A method for assessing the relative merits of various passage arrangements is presented. The use of the methods is illustrated through a worked example.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Abstract not provided

International Nuclear Information System (INIS)

... p. SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS algorithms

Energy Technology Data Exchange (ETDEWEB)

Stability constants for uranium-tetracycline complexes were determined by the method of average number of ligands, the method of limiting values, the method of two parameters and the method of weighted least squares. Solvent extraction technique was used to obtain experimental data. (author). 10 refs.; 5 figs.

Science.gov (United States)

Not Available

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Pyrheliometric methods are described (particularly methods for measuring the solar constant), and theoretical and experimental studies in this field are surveyed and systematized. Particular attention is given to the analysis of instruments intended for pyrheliometers used as standards, reference instruments, and solar-constant meters is examined, and consideration is given to methods for determining the thermal-radiation properties of absorbing coatings and methods for calculating the absorption coefficients of cavity receivers.

Science.gov (United States)

Not Available

International Nuclear Information System (INIS)

... ammonium compounds benzilic acid chemical preparation lanthanum oxides

KoreaScience (Korea)

Full Text Available

International Science & Technology Center (ISTC)

Determination of Special Molybdenum Alloys Optimal Structure Using the Cybernetic Method

Energy Technology Data Exchange (ETDEWEB)

Reported on here are studies of various methods for liquefying coal. Hydropyrolysis as an alternative method for producing liquid hydrocarbons and a carbon enriched char is discussed. Other methods described involve supercritical gas extraction of coal and use of natural gas as a hydrogenating agent. Relevant waste water treatments are discussed as well. 65 refs., 9 figs.

Energy Technology Data Exchange (ETDEWEB)

A method is provided for detecting pathological macromolecules in a patient. The method is comprised of the following: obtaining body fluid from the patient; pretreating the body fluid; subjecting the pretreated body fluid to size-exclusion chromatography to create an excluded fluid; and analyzing the excluded fluid to detect macromolecules having a predetermined molecular weight. The method also allows for comparing elution spectra with reference spectra of suspect pathologic proteins.

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

International Science & Technology Center (ISTC)

Methods of Decontamination, Utilization, and Deactivation of Liquid Radioactive Wastes

Energy Technology Data Exchange (ETDEWEB)

A new method for the determination of the cmc using a dialysis technique which allows monometric species to diffuse through but no micelles has been applied for determining the mixed micelle composition. The method is based on determining the amount of surfactant that diffuses through at two different times which allows for the calculation of the cmc by use of the appropriate equation. This method requires the preparation of only one concentration of solution and lends itself particularly well to the determination of the composition of mixed micelles. (orig.)

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

International Science & Technology Center (ISTC)

Development of the Method of Electrodepositing Nanostructured Composite Coatings with Improved Engineering Properties

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

A procedure for the determination of lead in various biological and environmental samples by "2"0"3Pb radioisotope dilution substoichiometric method is presented. The accuracy of the method by comparison with the literature values of reference materials appears to be good. The standard deviation of the method is less than 10%, and detection limit is about 0.1 #mu#g of lead. (author) 5 refs.

J-STORE (Japan)

Full Text Available