Energy Technology Data Exchange (ETDEWEB)

Deposition of hard coatings may influence the mechanical properties of the bulk material and its corrosion resistance. In this work we study the hardness of the coated and the back side of 100Cr6 steel plates. Electrochemical corrosion tests were performed in O{sub 2}-saturated acetate buffer of pH 5.6 at 25degC. Chromium nitride and titanium nitride coatings prepared by different physical vapour deposition processes, such as arc, thermionic arc evaporation, magnetron sputtering and ion-beam-assisted deposition (IBAD) were compared. The results show that, for sufficient corrosion protection, chromium nitride layers have to be thicker than 500 nm. An increased nitrogen partial pressure in the evaporation chamber of the IBAD process improves the corrosion resistance significantly. The hardness of the substrates was reduced in the case of thermoionic arc evaporation only, indicating a deposition temperature of more than ...

International Nuclear Information System (INIS)

Chromium nitride thin films were deposited on SA-304 stainless steel substrates by using direct-current reactive magnetron sputtering. The influence of process conditions such as nitrogen content in the fed gas, substrate temperature, and different sputtering gases on microstructural characteristics of the films was investigated. The films showed (200) preferred orientation at low nitrogen content (< 30%) in the fed gas. The formation of Cr_2N and CrN phases was observed when 30% and 40% N_2 were used, with a balance of Ar, respectively. Field emission scanning electron microscopy and atomic force microscopy were used to characterize the morphology and surface topography of the thin films, respectively. Microhardness tests showed a maximum hardness of 16.95 GPa for the 30% nitrogen content.

International Nuclear Information System (INIS)

High quality Nb_3Sn films have been fabricated using a recently developed magnetron sputtering process capable of deposition rates approaching 1 #mu#m/min at sputtering voltages less than 500 V and power levels of about 5 KW. Low sputtering voltages allow more complete thermalization at lower pressures of the material condensing on the substrate which can improve long range order. Transition temperatures of up to 18.3"0K, J/sub c/(0)'s of 15 x 10"6 A/cm"2 and Hc_2 as high as 240 k0e have been achieved in 1-3 #mu#m films deposited from a Nb_3Sn reacted powder target with substrate temperatures between 600 and 800"0C. The films exhibit smooth surfaces and, generally, a (200) preferred orientation. The growth of the film is columnar in nature. The sputtering parameters, substrate material and temperature will be related to film structure, T/sub c/ and J/sub c/(H,T) and the Nb/Sn ratio ...

International Nuclear Information System (INIS)

Nano structured carbon nitride thin films were deposited at different RF powers in the range of 50 W to 225 W and constant gas ratio of (argon: nitrogen) Ar:N_2 by RF magnetron sputtering. The atomic percentage of Nitrogen: Carbon (N/C) content and impedance of the films increased from 14.36% to 22.31% and 9 x 10"-"1 #OMEGA# to 7 x 10"5 #OMEGA# respectively with increase in RF power. The hardness of the deposited films increased from 3.12 GPa to 13.12 GPa. The increase in sp"3 hybridized C-N sites and decrease of grain size with increase in RF power is responsible for such variation of observed mechanical and electrical properties.

International Nuclear Information System (INIS)

The crystallite size and orientation in molybdenum films prepared by magnetron sputtering at a low rate of typical 1 (angstrom)s and a pressure of 0.45 Pa was investigated by X-ray diffraction and texture analysis. The surface topography was studied using atomic force microscopy. Increasing the film thickness from 20 nm to 3 microm, the films show a turnover from a (110) fiber texture to a (211) mosaic-like texture. In the early state of growth (20 nm thickness) the development of dome-like structures on the surface is observed. The number of these structures increases with film thickness, whereas their size is weakly influenced. The effect of texture turnover is reduced by increasing the deposition rate by a factor of six, and it is absent for samples mounted above the center of the magnetron source. The effect of texture turnover is related to the bombardment of the films with high energetic argon neutrals resulting from ...

International Nuclear Information System (INIS)

The structure and properties of composite powder coatings on the base of titanium carbide are studied. It is shown the electron-beam welding deposition of powders on the base of nickel and titanium carbide allows to produce of high-quality wear-resistant coatings which superior in density and hardness compared with sputtered ones. Changes of hardening phase volume percentage as well as composition of metal matrix make possible to control coatings hardness

Energy Technology Data Exchange (ETDEWEB)

Highly resistant, high-transmittance woodceramic thin films were prepared using rf magnetron sputtering of a woodceramic disk in argon plasma. A film series was deposited based on substrate temperature, which was varied from 50 to 500 degree C. The film's electrical and optical properties depended on substrate temperature. Films deposited below 300 degree C were insulative, {rho}>10{sup 10} {omega} {center_dot} cm. Films deposited at 50 degree C had a density of 1.9-2.2 g/cm{sup 3} comparable to that of single crystal graphite. Below 200 degree C, films had higher transmittance than typical DLC films in the visible and infrared region. Infrared C-H absorption spectrum was observed by Ft-IR and there exist two types of bonding corresponding to sp{sup 2} or SP{sup 3}. (author)

International Nuclear Information System (INIS)

Nitrogen doped Diamond-like carbon thin films were deposited on n-Si and SiO_2 substrates by rf magnetron sputtering using pure graphite (99.999%) as the target material and mixtures of Ar, N_2 and H_2 for plasma generation. The dependence of structural and optical properties on nitrogen content was investigated using XPS, Raman spectroscopy, FT-IR spectroscopy, and Ellipsometry studies. It was found that as the nitrogen content was increased in the plasma, sp"2 bonding favored. Also it was observed that oxygen contamination increased with nitrogen content. Typical C-H stretching modes connected with diamond-like carbon could be seen in FT-IR spectra. The I_D and I_G bands were well defined and it was observed that as nitrogen content increased I_G band was enhanced. Ellipsometry studies revealed that the optical constants like refractive index (n) and extinction co-efficient (k) increased with increase in nitrogen content as well as substrate ...

International Nuclear Information System (INIS)

Magnetic materials such as yttrium iron garnet (YIG) are of great importance for its magneto-optic properties and for their potential applications in the domain of optical telecommunications. The deposition of thin films of YIG, on quartz or GGG (gadolinium gallium garnet) substrate, was performed using radio frequency non reactive magnetron sputtering, followed by high temperature annealing which is needed to enhance the crystallinity of the layers. Rutherford backscattering spectrometry RBS was used to determine the thickness and stoichiometry of the performed layers in order to investigate correlations between growth conditions and the quality of the final material. RBS measurements showed the influence of the deposition time and the temperature substrate on the film growth and its stoichiometry. (author)

Energy Technology Data Exchange (ETDEWEB)

Thin Fe and Ta layers of 30-45 nm thickness, deposited via magnetron sputtering on Si (1 0 0) substrates, were bombarded at room temperature with 100 keV Ar{sup 1+} or Ar{sup 8+} or with 250 keV Xe{sup 1+} or Xe{sup 19+} ions in order to test the influence of the ion charge state on the surface sputtering and interface mixing. The samples were characterized by means of Rutherford backscattering at 0.9-3.0 MeV {alpha}-particle energy, time-of-flight elastic recoil detection analysis with a 53 MeV {sup 127}I{sup 10+} beam and atomic force microscopy. No influence of the charge state on the sputtering and athermal mixing rate was observed in the case of the Ta/Si system. However, in the case of the Fe/Si system, the ion charge was observed to have an influence on the mixing rate.

Energy Technology Data Exchange (ETDEWEB)

A complex modulated structure is described for reactive elements that have the capability of considerably more heat than organic explosives while generating a working fluid or gas. The explosive and method of fabricating same involves a plurality of very thin, stacked, multilayer structures, each composed of reactive components, such as aluminum, separated from a less reactive element, such as copper oxide, by a separator material, such as carbon. The separator material not only separates the reactive materials, but it reacts therewith when detonated to generate higher temperatures. The various layers of material, thickness of 10 to 10,000 angstroms, can be deposited by magnetron sputter deposition. The explosive detonates and combusts a high velocity generating a gas, such as CO, and high temperatures. 2 figs.

Energy Technology Data Exchange (ETDEWEB)

Silicon thin film with thickness in range 1000-5300 A deposited on rough Cu foil by a radio frequency magnetron sputtering is used as anode materials for Li-ion rechargeable batteries. The SEM, XRD and TEM analysis reveals that the Si thin film has a floccular nano-sized multi-crystalline structure. Li ions insertion/extraction evaluation is performed mainly with constant current charge/discharge cycling and cyclic voltammetry (CV) at room temperature. The cycleability and reversible discharge capacity are found to depend on the film thickness, and thinner films give larger accommodation capacity. A 3120 A Si film provides a reversible specific capacity over 3500 mA hg{sup -1} with excellent cycleability under 0.5 C charge/discharge rate.

Energy Technology Data Exchange (ETDEWEB)

By magnetron sputtering model steel films with specific properties can be prepared for purposive surveys. By changing the deposition parameters certain properties of these films can be influenced. For this thesis steel films with 18% Cr and 8% Ni have been prepared in order to study specific parameters on the corrosion resistance of bulk stainless steel. Chemical composition, microstructure, and surface morphology of these films have been characterized. In comparison to bulk steel sheets with the same chemical composition they have a smaller grain size and a ferritic structure. In contrast to bulk steel sheets they don`t contain any nonmetallic inclusions like Mn-sulfides. The influence of these structural differences on the corrosion resistance has been studied. For this purpose the electrochemical properties of the sputter-deposited steels have been compared with the properties of steel sheets with a similar chemical ...

Energy Technology Data Exchange (ETDEWEB)

Thin films of new metastable materials from the system Ti-B-C-N were deposited on metallic substrates by d.c. magnetron sputtering in different Ar+N{sub 2} atmospheres. The multiphase compound targets used were based on various compositions on the TiC-TiB{sub 2} and TiB{sub 2}-C tie lines of the Ti-B-C phase diagram. The structure and chemical composition of the films were characterized by electron microprobe analysis, depth profiling Auger electron spectroscopy, X-ray diffraction and transmission electron microscopy. The hardness, critical load of failure and the tribological behavior of the coatings were investigated. Superhard single-phase crystalline metastable Ti-B-C-N layers with hardness values exceeding 5000 HV{sub 0.05} and extremely low sliding wear against 100Cr6 and Al{sub 2}O{sub 3} counterparts could be produced by reactive sputtering of various TiC-TiB{sub 2} targets in Ar+N{sub 2} atmospheres with low ...

British Library Electronic Table of Contents (United Kingdom)

The pentenary compound semiconductor Cu(In,Ga)(Se,S)2 is one of the most attractive materials for high-efficiency solar cells due to its tunable band gap to match well the solar spectrum. In this study, semiconducting Cu(In,Ga)(Se,S)2 thin films were prepared by a classical two-step growth process, which involves the selenization and/or sulfurization of In/Cu?Ga precursor. During the precursor formation step metallic In/Cu?Ga alloys were deposited onto the Mo-coated soda-lime glass substrates by DC magnetron sputter process. The respective precursors were subsequently reacted with H2Se and/or H2S gasses, at elevated temperatures. By optimizing the selenization parameters, such as the gas concentrations, reaction time, reaction temperature, and the flow of H2Se and H2S, high quality, single...

Energy Technology Data Exchange (ETDEWEB)

Duplex-coating procedures consisting of plasma nitriding and Me-C:H hard coating lead to an improved performance of the devices because the Me-C:H coating is supported by the nitrided phase and, therefore, the `eggshell-effect` is avoided. Furthermore, this support leads to a higher load-bearing capacity of the thin film. Two standard procedures (classical high-pressure plasma nitriding and unbalanced magnetron sputtering of Ti-C:H) were performed subsequently to prepare the duplex coatings on X20Cr13 ferritic stainless steel. The corrosion resistance of the steel could be improved by nitriding at 450 C compared to the untreated ferritic substrate. The roughness is determined by the nitriding step. The weakest point of the coating is the transition zone between the nitrided and the untreated substrate and not the interface between the Ti-C:H coating and the nitrided substrate as shown by the Rockwell and scratch tests. The adhesion of the ...

Science.gov (United States)

Attempt to form the Schottky barrier on mercury indium telluride (MIT) surface by deposition transparent conducting electrode (TCE) and avoid the negative results by non-rectifier contacts nature, we have investigated the oxidation of clean MIT surfaces to form an insulating layer to overcome this disadvantage by metal-insulator-semiconductor (MIS) photodetectors designing. Oxide film is grown on the MIT surface by plasma enhance chemical vapor deposition (PECVD). Previously cleaned MIT wafers were dipped and boiled in solution, which consists of mixture of bromine and an organic solvent in ratio of 1:50. By the way of using these films as intermediate slightly conducting insulator, a fast-response MIT based surface-barrier photodetectors have been developed. Pt films were used as TCE frontal electrode by vacuum magnetron sputtering (VMS). The current-voltage characteristic is described quantitatively based on the energy diagram and the found ...

British Library Electronic Table of Contents (United Kingdom)

The properties of ZnO films were investigated as functions of annealing temperatures in H2/Ar and vacuum. The resistivities and mobilities of ZnO films decreased with increase of annealing temperatures in vacuum and H2/Ar ambients. However, the carrier densities of ZnO films increased with increase of annealing temperatures in vacuum and H2/Ar ambients. The resistivities of ZnO2 films annealed at 300degreeC were 2186cm and 798cm in H2/Ar and vacuum ambients, respectively. The resistivities of ZnO films annealed in vacuum and H2/Ar ambients at 600degreeC were similar with 0.040cm and 0.035cm, respectively. The hydrogen donor was more dominant than the oxygen vacancy or Zn interstitial donor in ZnO films annealed in ambient H2/Ar at low temperatures. The average optical transmission was >82%...

Energy Technology Data Exchange (ETDEWEB)

The properties of polycrystalline (Ti, Al)N coatings deposited on non-nitrided, classically plasma-nitrided and low pressure plasma-nitrided AISI H11 steel samples were investigated. The plasma deposition and low pressure plasma nitriding were performed in a Z700-LH magnetron sputter ion plating unit, while a separate unit was used for plasma nitriding of specimens at a pressure of several millibars. The (Ti, Al)N coating was deposited onto all the samples using the same equipment as for the plasma deposition and low pressure plasma nitriding. For the characterization of the composite structures, the following methods were used: scratch test, X-ray diffraction analysis, scanning electron microscopy, scanning tunnelling microscopy and microhardness testing. It was found that plasma nitriding prior to coating deposition strongly affects the growth and properties of hard coatings, such as the microhardness, adhesion, preferred orientation, ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A systematic study of structure-mechanical properties relation is reported for MoSi{sub 2}-SiC nanolayer composites. Alternating layers of MoSi{sub 2} and SiC were synthesized by DC magnetron and rf-diode sputtering, respectively. Cross-sectional transmission electron microscopy was used to examine three distinct reactions in the specimens when exposed to different annealing conditions: Crystallization and phase transformation of MoSi{sub 2}, crystallization of SiC, and spheroidization of the layer structures. Nanoindentation was employed to characterize the mechanical response as a function of structural changes. As-sputtered material exhibits amorphous structures in both types of layers and has a hardness of 11 GPa and a modulus of 217GPa. Subsequent heat treatment induces crystallization of MoSi{sub 2} to form the C40 structure at 500C and SiC to form the a structure at 700C. The crystallization process is directly ...

Energy Technology Data Exchange (ETDEWEB)

In the Ti-Si-C and Ti-Si-C-N systems, metastable layers were precipitated by means of non-reactive magnetron sputtering of hot-pressed two-phase TiC/SiC and TiN/SiC targets with 20 mole% and 50 mole% SiC. The preparation parameters were varied as follows: ion bombardment during precipitation (bias sputtering), substrate temperature, and annealing times when annealing amorphous 50%:50% TiC/SiC and 50%:50% TiN/SiC layers. Sputtering of targets containing 20% SiC was found to result in monophase fcc layers (NaCl structure). This was documented on the basis of X-ray and electron diffraction patterns. Direct precipitation of targets with 50 mole% SiC resulted in amorphous layers. Increasing the ion bombardment during accretion, raising the substrate temperature, and annealing amorphous 50%:50% TiC/SiC and 50%:50% TiN/SiC (layers precipitated directly) resulted in the crystallization of TiC and TiN ...

Science.gov (United States)

... Accession Number : ADD257320. Title : Sputter Deposition of Yttrium-Oxides. Descriptive Note : Journal article,. Corporate ...

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline processing by inert gas condensation has the inherent advantages of generating: (1) high surface area nanoclusters, (2) non-stoichiometric oxides, and (3) high dispersions of dopants. This approach is exploited in the synthesis of fluorite-structured catalysts for SO{sub 2} reduction by CO. Nanocrystalline CeO{sub 2{minus}x}, La-doped CeO{sub 2{minus}x}, and Cu-doped CeO{sub 2{minus}x} were produced by magnetron sputtering from a pure or mixed metal target, followed by controlled oxidation of the metallic clusters. The as-prepared doped and undoped nanocrystalline CeO{sub 2{minus}x} materials were found to be excellent catalysts for complete SO{sub 2} conversion to elemental sulfur. Undoped nanocrystalline CeO{sub 2{minus}x} enabled light-off at 460 C, a temperature {approximately} 120 C lower than that over polycrystalline CeO{sub 2}, which is a novel effective catalyst itself. The high catalytic activity of the nanocrystals ...

Energy Technology Data Exchange (ETDEWEB)

Copper coatings deposited on Al-6061 substrates by radio frequency magnetron sputtering, to prevent the retention and permeation of energetically implanted tritium in Al-6061, were evaluated by a variety of characterization techniques. The coatings, weighing in the 0.03 to 0.088 kg/m{sup 2} range, were smooth and had a fine grain structure. They contained the intermetallic phases Cu{sub 9}Al{sub 4} and CuAl{sub 2} as well as copper. The fractions of Al and Cu in any coating increased and decreased, respectively, with increasing depth below the surface. Furthermore, the fractions of Al and Cu on the coating surface decreased and increased, respectively, with increasing coating weight. There was no texture or preferred orientation in the Cu phase of the coatings. A significant amount of oxygen was also detected at the original substrate surface. Residual stress measurements revealed that, in both Cu and CuAl{sub 2}, the stresses in the coating ...

International Science & Technology Center (ISTC)

Research and Development of Resource-Saving Technology for Manufacturing of Titanium Semifinished Items from Chips

International Nuclear Information System (INIS)

Sputter-removal rates of overlayer and interfacial species on silicon are analyzed to determine sputtering yields for the species involved. Sputtering yields up to two orders of magnitude lower than those measured for silicon are found, and the results are interpreted in terms of a cascade mixing process which continually reburies much of the overlayer material beyond the escape depth of the sputtered atoms.

UK PubMed Central (United Kingdom)

BackgroundTitanium and titanium alloys are widely used for fabrication of dental implants. Since the material composition and the surface topography of a biomaterial play a fundamental...Full Text Available

Science.gov (United States)

Metastable yttrium-oxide films are synthesized using reactive sputter deposition. The yttrium concentration of the as-deposited film is found to vary as a function of the sputter deposition rate. In addition to the synthesis of the cubic equilibrium phase...

International Nuclear Information System (INIS)

Short communication.

Science.gov (United States)

... Title : Effect of Yttrium on the Microstructure of Titanium Alloys,. ... The yttrium was added in the melting stage as an oxide or in the elemental form. ...

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning the properties of tantalum and tantalum compound films formed by sputtering techniques. Topics include processes, and electrical, magnetic, and dielectric properties of the sputtered films. Tantalum compounds studied include nitrates, oxides, and aluminides. The structural properties of sputtered films are also discussed. (Contains a minimum of 105 citations and includes a subject term index and title list.)

Energy Technology Data Exchange (ETDEWEB)

The objective of the current study was the gradual development of the formation of the nitride layer during inductive r.f. plasma nitriding. The study centers on characterization of refined layers and plasma diagnostics in the vicinity of the sample, and raises critical questions of how the layers and interfacial microstructure might affect the near-surface properties. The composition of the plasma near the surface of the sample (plasma layer) was examined by optical emission spectroscopy and mass spectrometry during plasma nitriding and while sputtering the sample after the nitriding process. It was observed that during the nitriding process, the plasma layer contains Ti, NH[sub n] species, N (or/and N[sup +]), H[sub n] species (or/and H[sup +][sub 2]). However, when the nitrided sample was exposed to argon plasma, Ti, Al and NH were observed. It was found that two distinct sublayers, comprising [delta]-TiN and [delta]-TiN + [epsilon]-Ti[sub 2]N phases, were ...

International Nuclear Information System (INIS)

Chemical and phase homogeneity of titanium-niobium sponge, produced by a combined magnesium-thermic reduction of niobium pentachloride and titanium tetrachloride mixtures, is investigated. It is ascertained that a sponge consists of spherical shape particles and has a large number of pores. Particle sizes are reduced with niobium being substituted for titanium from 50-500 #mu#m for titanium sponge to 1-40 #mu#m for niobium one, which testifies to the bormation in a titanium-niobium sponge of an alloy and not a mechanical mixture. A number of solid solutions is detected by X-ray phase analysis. Lattice parameters are determined.

Science.gov (United States)

... Accession Number : ADD151811. Title : Ultra High Strength Beta Titanium Alloy for Fasteners. Descriptive Note : Journal article,. ...

Science.gov (United States)

... Accession Number : ADD109273. Title : THERMAL STABILITY OF ALPHA-BETA TITANIUM ALLOY Ti-5Al-2Cr-1Fe,. Corporate Author : ...

International Nuclear Information System (INIS)

Consideration is given to the process of the formation of a titanium sponge alloyed with niobium or tantalum, in the joint metallic reduction of titanium, niobium and tantanum chlorides. A percentage composition of the phases observed and the structure of the alloyed sponge have been studied. It is shown that after one remelting operation of the alloyed sponge the alloys of titanium with niobium and tantalum have a uniform component distribution. At the stage of chloride reduction there appear solid solutions based on titanium and an alloying component. The stage of vacuum separation of the reaction mass is associated with a mutual dissolution of the primary phases and the formation of the solid solutions of the alloyed titanium sponge, which, by their composition, are close to the desired alloy composition. The principal features of the formation of a titanium ...

Science.gov (United States)

... Accession Number : ADD120492. Title : Environmental Cracking of the Alpha-Beta Titanium Alloy, Ti-6Al-6V-2Sn,. Corporate ...

Science.gov (United States)

... Title : DUCTILITY RATIO OF AGED BETA TITANIUM ALLOY. Corporate Author : NEW YORK UNIV NY SCHOOL OF ENGINEERING AND SCIENCE. ...

International Nuclear Information System (INIS)

Observations concerned with the formation of isothermal #omega# in the beta-titanium alloy RMI (38-6-44) are presented as part of a more general study of the aging characteristics of the alloy.

Energy Technology Data Exchange (ETDEWEB)

Swift heavy ion-solid interaction leads in volume to track creation and on the surface to the ejection of particles into the vacuum. To learn more about initial mechanisms of track formation, we are focused on the sputtering of uranium dioxide by fast heavy ions. This present study is exclusively devoted to the influence of the electronic stopping power on the emission of neutral particles and especially on their angular distribution. These measurements are completed by those of the ions emitted from UO{sub 2} targets bombarded with swift heavy ions. The whole experimental results give access to: i) the nature of the sputtered particles; ii) the charge state of the emitted particles; iii) the direction of ejection of the sputtered particles ; iv) the sputtering yields deduced from the angular distributions. These results are compared to the prediction of the sputtering models ...

Energy Technology Data Exchange (ETDEWEB)

The refractory nature and high ductility of body centered cubic (bcc) phase tantalum makes it a suitable material for corrosion- and wear-resistant coatings on surfaces that are subjected to high stresses and harsh chemical and erosive environments. Sputter deposition can produce thick tantalum films but is prone to forming the brittle tetragonal beta phase of this material. Efforts aimed at forming thick bcc phase tantalum coatings in both flat plate and cylindrical geometries by high-rate triode sputtering methods are discussed. In addition to substrate temperature, the bcc-to-beta phase ratio in sputtered tantalum coatings is shown to be sensitive to other substrate surface effects.

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning the structural properties of sputtered tantalum and tantalum compounds. The preparation of thin film capacitors and resistors is described. The electrical properties of the sputtered films are also included. The influence of the substrate on the properties of the coatings is considered, including adherence of the coating to the substrate, and the effects of impurities on coating integrity. (Contains 250 citations and includes a subject term index and title list.)

Energy Technology Data Exchange (ETDEWEB)

Modeling is performed for focused-ion-beam (FIB) sputtering and redeposition on trench sidewalls in a steady state approximation. Calculations are carried out to demonstrate the sputtered surface profile under known parameters such as sputtering yield as a function of ion incident angle, the FIB current density profile, and the FIB scan speed. It is found that a steplike slope with a gradient angle of {theta}{sub 0} is formed at the FIB bombarding position. Furthermore, the redeposition flux on the sidewalls is calculated as a function of {theta}{sub 0} for the FIB trench milling assuming the cosine law for the angular distribution of the sputtered atom. The redeposition will be more accurately predictable and controllable when more information about these assumptions is obtained.

International Nuclear Information System (INIS)

(Nov 1973). United States Greenfield, MA Pierce, CM Chicago, IL.

Science.gov (United States)

An economical way to reduce the deleterious effects of titanium, one of the impurities present in metallurgical grade silicon material, is disclosed. By adding copper to approximately the same concentration level of the titanium during the melting process, the conversion efficiency will be restored to about 99.3% of what it would have been if the single crystal silicon had been grown free of titanium impurities.

International Nuclear Information System (INIS)

Cyclic strength of #alpha#+#beta#-titanium alloy BT3-1 is studied under load frequencies of 33 and 300 Hz. The increase in the cyclic strength with growing frequency is caused by formation of FCC interphase layers of titanium hydrides. Their formation is one of possible ways of raising the fatigue strength of titanium alloys. Peculiarities of FCC interlayer formation in #alpha#+#beta# phases under loading frequency variation are revealed.

Science.gov (United States)

... THE STRENGTH, TOUGHNESS, AND STRESS-CORROSION CRACKING SUSCEPTIBILITY OF A METASTABLE BETA TITANIUM ALLOY (Ti-11. ...

Energy Technology Data Exchange (ETDEWEB)

Results are reported which were obtained when investigating the anodic behavior of titanium in sodium iodide solutions. It was concluded that in order to explain the special features in the anodic behavior and anionic anodic activity of titanium one must take into account, both a redistribution of the potential drop between the oxide and the Helmholtz layer and a potential-dependent variation of the catalytic and adsorption properties of the oxidized titanium anode.

Energy Technology Data Exchange (ETDEWEB)

Sputter-deposited tantalum (Ta) and reactively sputter-deposited Ta-nitride films were studied with respect to the passivation capability against copper (Cu) oxidation in thermal O{sub 2} ambient. A 200 {angstrom} Ta or Ta-nitride film was sputter-deposited on a 2,000 {angstrom} Cu film using a Ta target in an Ar/N{sub 2} gas mixture. With Ta passivation, Cu was not oxidized at temperatures up to 400 C, which can be further improved by using passivation of an amorphous Ta-nitride film deposited in an appropriate condition. The absence of long-range defects in the Ta-nitride film was presumably responsible for this improvement. However, sputtering-induced surface damage by excess N{sub 2} in the sputter gas mixture may reduce the passivation capability of Ta-nitride films. When the passivated Cu was oxidized, the Cu oxides always resided in the top surface region. That is, in the ...

Energy Technology Data Exchange (ETDEWEB)

Tantalum and tantalum-based thin films have gained precedence as the diffusion barrier for copper interconnects used in the latest generation of integrated circuits (ICs). The paper presents insight and observations on the covariance of texture and grain size of wrought tantalum sputtering targets and their influence on sputtering performance. Previous studies involving deposition trials of tantalum targets of varying metallurgical character had demonstrated that both grain size and textural homogeneity is critical for assuring reliable sputtering performance of tantalum. Subsequently, a model had been proposed to prescribe how localized texture bands and orientation clusters in tantalum are effectively resistant to sputter erosion. In this paper, results of atomic force microscopy (AFM) and orientation imaging microscopy (OIM{sup TM}) analyses on the eroded surface of a tantalum ...

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Computer-aided design/computer-aided manufacturing (CAD/CAM) titanium ceramic restorations were developed with the potential for replacing expensive, high noble metal ceramic restorations. However, there is a lack of information about the clinical performance of CAD/CAM titanium ceramic single crowns. Purpose The purpose of this study was to evaluate CAD/CAM titanium ceramic single crowns after 3 years in function. Material and methods A total of 41 crowns were fabricated for 21 patients. The titanium copings were CAD/CAM milled (Everest CAD/CAM system) with an even thickness of 0.5 mm, and low-fusing veneering porcelain (Vita Titanium Porcelain) was added incrementally. The crowns were cemented using zinc phosphate cement after confirming that there were no mechanical...

International Nuclear Information System (INIS)

The results of an investigation on the production of Group IIA atomic and molecular negative ion beams formed in a cesium-sputter negative ion source are presented. The sputtering material was formed by pressing pellets of stoichiometric mixtures of the Group IIA element carbonates and 10% copper powder. Negative ions of several alkaline-earth elements and their oxides have been observed. Beam intensities as high as 180 pA have been observed for Sr"-and 20 nA for SrO"-. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Average emittance data for ion beams extracted from cesium-sputter negative ion sources equipped with spherical, ellipsoidal, and cylindrical geometry cesium-surface ionizers are presented. The attributes of the respective source geometries are described in terms of their cesium ion optical properties. The results of recent measurement of the emittances of momentum-analyzed beams extracted from the ellipsoidal geometry source are also presented. These measurements indicate the presence of a species-dependent effect. The effect is believed to be attributable to differences in the energy spreads of the respective negative ion beams introduced by the sputter generation process. 11 refs., 8 figs.

Energy Technology Data Exchange (ETDEWEB)

Low-temperature polysilicon thin-film transistors (TFT's) have been fabricated from sputtered silicon films and characterized as a function of as-deposited hydrogen (H) content and laser crystallization fluence. A general trend is observed where TFT performance improves as the H content is lowered. Devices made from {approximately}0% H sputtered films perform similar to those made from low-pressure chemical-vapor deposition processes (LPCVD), but are fabricated at a much lower process temperature (300 C). The best sputtered TFT's had mobilities of {approximately}200 cm{sup 2}/Vs, and on/off current ratios of more than 10{sup 8}.

Science.gov (United States)

Sputtering of glass coatings on cadmium sulfide thin film solar cells

Science.gov (United States)

To study the effects of atmospheric species on the fatigue crack growth behavior of an a+B titanium

Science.gov (United States)

A novel reactor combining a flame-deposited nanostructured titanium dioxide film and a set of embedded ceramic electrodes was designed, developed and tested for degradation of methyl tert-butyl ether (MTBE) in water. On applying a voltage to the ceramic electrodes, a surface coro...

International Nuclear Information System (INIS)

... properties organic bromine compounds organic solvents ph value phenols

International Nuclear Information System (INIS)

17-4PH stainless steel was modified by direct current (DC) plasma nitriding and titanium nitride film duplex treatment in this study. The microstructure, wear resistance and corrosion resistance were characterized by X-ray diffraction (XRD), pin-on-disk tribological test and polarization experiment. The results revealed that the DC plasma nitriding pretreatment was in favor of improving properties of titanium nitride film. The corrosion resistance and wear resistance of duplex treatment specimen was more superior to that of only coated titanium nitride film.

International Nuclear Information System (INIS)

1970. United States Crossley, FA Lindberg, RW Lockheed Missiles and

Science.gov (United States)

... Accession Number : ADD100229. Title : DEFORMATION BEHAVIOR OF AN OMEGA HARDENED ALPHA-BETA TITANIUM ALLOY,. ...

Science.gov (United States)

... Accession Number : ADA136144. Title : Characteristics of the Mechanical Properties and the Fractures of an Alpha Beta Titanium Alloy,. ...

International Nuclear Information System (INIS)

On the basis of symmetry way of texture description a calculation method of elastic moduli of two-phase titanium alloys with rolling texture has been suggested. Efficiency of the calculation formulas is checked by comparing the calculation results of Young modulus anisotropy in the sheet plane of (#alpha#+#beta#)-titanium alloy VT23 with the experimental data.

British Library Electronic Table of Contents (United Kingdom)

Nowadays there are many sun-protection cosmetics incorporating organic or inorganic UV filters as active ingredients. Chemically stable inorganic sunscreen agents, usually metal oxides, are widely employed in high-SPF (sun protection factor) products. Titanium dioxide is one of the most frequently used inorganic UV filters. It has been used as a pigment for a long period of cosmetic history. With the development of micronization techniques, it has become possible to incorporate titanium dioxide in sunscreen formulations without the previous whitening effect, and hence its use in cosmetics has become an important research topic. However, there are very few works related to quantitation of titanium dioxide in sunscreen products. In this research, we analysed the amounts of titanium dioxide i...

Energy Technology Data Exchange (ETDEWEB)

The Sputter coefficient of accelerated CO{sub 2} cluster ions hitting surfaces of various materials is investigated. For copper it varies proportional to the 2nd power of the energy between 155 and 260 keV. The rate of erosion for different target materials varies by two orders of magnitude from tungsten to PMMA. Diamond is eroded fairly quickly, while aluminum is eroded less than corundum (Al{sub 2}O{sub 3}). No simple correlation of the sputter coefficient on the bulk material properties is found. For copper the angular distribution of sputtered material is measured and found to be following roughly a cosine distribution. By using masks different microstructures have been produced in cobalt-samarium magnets, diamond and glass. (orig.)

International Nuclear Information System (INIS)

We have measured K-edge X-ray absorption spectra of argon in sputtered aluminum films at a synchrotron radiation facility (the Photon Factory). We found that the energy and shape of white line change when the film is annealed at 500 C and the spectrum becomes resembling that of argon implanted in silicon. From the analyses of the X-ray absorption spectra and TEM observation we concluded that argon exists as very small atom clusters with a diameter less than 1 nm or exist as isolated atoms in the as-sputtered aluminum film, and that the size of the clusters become as big as 10 nm diameter when the film is heated. (Copyright (c) 1999 Elsevier Science B.V., Amsterdam. All rights reserved.)

British Library Electronic Table of Contents (United Kingdom)

Lithium phosphorous oxynitride(Lipon) thin films as a lithium ion conductive electrolyte were prepared by radio frequency reactive sputtering in N2 plasma. The properties of the amorphous Lipon solid electrolyte were investigated as a function of N2 pressure during reactive sputtering. The ionic conductivity and the electrochemical stability of Lipon thin films improved drastically as the N2 pressure decreased. The ionic conductivity closed to 10?6 S cm?1 and obtained a stability window of 1.0?5.0 V with an N2 pressure of 5 mTorr, where the number of nitrogen bonds between the phosphate groups were more than those formed at higher pressure. It was possible to fabricate the Li//LiCoO2 complete thin film battery using this Lipon solid electrolyte, which exhibited excellent discharge characte...

International Nuclear Information System (INIS)

In this work, amorphous hydrocarbon (a-C:H) film deposition on metallic mirrors was studied during working shots in tokamak T-10 and at exposure in Ar/CHD3/D2 dc magnetron discharge in a special laboratory high vacuum setup. Analysis of film composition (including hydrogen content) was carried out using nuclear physical methods. Thickness and optical parameters (refractive and extinction coefficients) of the films were estimated by ellipsometry. Laboratory films can be characterized as soft a-C:H films in comparison with hard tokamak films (? = 1.2 and 1.8 g/cm3, respectively). For the first one, a linear dependence of deposition rate on mirror temperature was observed in a wide temperature range. The addition of methane into initial Ar/D2 magnetron gas mixture leads to an increase of deposition rate. The data obtained should be taken into account to prevent hydrocarbon film formation on the surface of first mirrors in ITER.

International Nuclear Information System (INIS)

The KAERI compact far-infrared (FIR) free-electron laser (FEL) has been operated successfully in the wavelength range of 97-150 #mu#m. It is the first demonstration of FEL lasing by using a magnetron-based classical microtron. We developed a high precision undulator consisting of 80 periods, with each period being 25 mm. The field strength of the undulator can be changed from 4.5 to 6.8 kG with an amplitude deviation of only 0.05% in r.m.s value. The kinetic energy of the electron beam is 6.5 MeV. The average current and pulse duration of the electron beam macropulses are 45 mA and 5.5 #mu#s, respectively. The measured power of the FEL with the electron beam parameters was more than 50 W for a FIR macropulse having a duration of 4 #mu#s. The spectral width of the FEL was measured to be 0.5% of the central wavelength. The FEL system, aside from the racks for the controlling units, is compact enough to be located inside an area of 3x4 m"2.

International Nuclear Information System (INIS)

A calculation on the stabilization of the sideband instability in the free electron laser (FEL) and inverse FEL (IFEL) was completed. The issue arises in connection with the use of a tapered (''variable-parameter'') undulator of extended length, such as might be used in an ''enhanced efficiency'' traveling-wave FEL or an IFEL accelerator. In addition, the FEL facility at Columbia was configured as a traveling wave amplifier for a 10-kW signal from a 24-GHz magnetron. The space charge field in the bunches of the FEL was measured. Completed work has been published.

International Nuclear Information System (INIS)

The methods of optical and transmission electron microscopy were used to study the influence of different programmes of hot deformation on the structure formation of (#alpha#+#beta#) titanium alloy VT9. The #beta# alloy VT-15 was studied at the same time in order to simulate the dislocation structure generated in the process of hot deformation. During the hot deformation of two-phase titanium alloys in both #beta# and (#alpha#+#beta#) ranges there is found to be an optimum range of deformation in which a homogeneous, polygonized structure is formed.

Science.gov (United States)

... Accession Number : ADD135317. Title : Workability and Heat Treatment Characteristics of Beta Titanium Alloy, Ti-15V-3Cr-3Sn-3Al,. ...

International Nuclear Information System (INIS)

Titanium base 'alpha'-alloys (Pt-7M, RK-20 and Ti-5Al-2Zr-1.5V) are considered for their behaviour under neutron irradiation. The role of alloying elements in radiation hardening is discussed depending of neutron fluence and irradiation temperature. For PK-20 alloy three stages of change in mechanical properties are revealed which are following: incubation period and weak hardening, intense radiation hardening, radiation hardening attenuation. Irradiation temperature rise results in an increase of incubation period and threshold neutron fluence. A special attention is paid to hydrogen absorption in #alpha#-titanium alloys under irradiation. It is concluded that titanium base 'alpha'-alloys are serviceable as structural materials in nuclear plants with allowance made for peculiar features of their radiation behaviour. 4 refs.; 7 figs.; 1 tab.

Science.gov (United States)

... information about, utilized, or discussed these subjects: basic topics: overview materials and material types: ti-6al-4v, ti1100, ti17 , ti6242, imi 550 ...

International Nuclear Information System (INIS)

1972. United States Narayanan, GH Archbold, TF Univ. of California Press.;

Science.gov (United States)

... silicon oxide (BSO), bismuth germanium oxide (BGO), and bismuth titanium oxide (BTO). These crystals are electro-optic, optically active, ...

International Nuclear Information System (INIS)

Titanium and its alloy Ti6Al4V enjoy widespread use in various biomedical applications because of favourable local tissue response, higher corrosion resistance and fatigue strength than the stainless steels and cobalt-chromium alloy previously used. The study reported in this paper aims to optimize the conditions of nitrogen ion implantation on commercially pure titanium and to correlate the implantation parameters to the corrosion resistance. X-ray photoelectron spectroscopy was used to analyse surface concentration and the implantation processes. An improvement in the electrochemical behaviour of the passive film was shown to occur with nitrogen ion implantation on titanium, in simulated body fluids. (UK).

International Nuclear Information System (INIS)

... filters molybdenum alloys production sulfuric acid alloys chemical reactions ...

UK PubMed Central (United Kingdom)

BackgroundOsseointegration is crucial for the long-term success of dental implants and depends on the tissue reaction at the tissue-implant interface. Mechanical properties and biocompatibility...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A multicusp magnetic field plasma surface ion source, normally used for H/sup -/ ion beam formation, has been utilized for the generation of high intensity, pulsed, heavy negative ion beams suitable for a variety of uses including tandem electrostatic accelerator/synchrotron injection applications. Sputter probe voltage limited total ion currents of 5.5, 8.2, 5.1 and 4.5 mA (peak intensity) have been produced from Au, Cu, Ni and CuO sputter probes, respectively. The mass distributions of these ion beams are found to be dominated by Au/sup -/, Cu/sup -/, Ni/sup -/ and O/sup -/ atomic species, respectively. The source offers the interesting prospect of providing cw negative ion beams at mA intensity levels of the commonly used semiconducting material dopants (e.g. B/sup -/, P/sup -/, As/sup -/ and Sb/sup -/) as well as O/sup -/ for isolation barrier formation. Illustrative examples of intensity versus time and the mass distribution of ion beams ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

International Nuclear Information System (INIS)

Aluminium nitride (AlN) is a very interesting ceramic because of its combination of properties such as high thermal stability, high hardness and an unusual combination of high thermal and low electrical conductivity. But it is very difficulty to obtain an AlN layer on the aluminium substrates by thermochemical nitriding process. Since a thin film of aluminium oxide existing on the surface of every aluminium substrate prevents the nitrogen atoms from diffusing into the aluminium lattice. However, it is possible to sputter the oxide film away from the aluminium surface in a glow discharge with the use of plasma nitriding technique and to allow the formation of AlN layer on the aluminium bulk. In the present work specimen of aluminium Al 99.5 has been plasma nitrided in a modified plasma nitriding unit, in which a diffusion pump was used to obtain an especially low partial pressure of oxygen in the vauum chamber. The sputter-cleaning prior to the ...

International Nuclear Information System (INIS)

Optical absorptance spectra of A-15 compounds were taken using a calorimetric technique in the range 0.2 eV to 4.0 eV. Thermomodulation spectra were taken on several A-15 sputtered films.

Energy Technology Data Exchange (ETDEWEB)

Two sources of negative ions are described. An rf source produces up to 14 ..mu..A beams of He/sup -/ by charge exchange in Rb vapor. The other Source of Negative Ions by Cesium Sputtering (SNICS) produces a wide variety of negative ion beams in the ..mu..A range. Two important features of SNICS are its simple, compact construction and its very good beam emittance (2 to 4..pi..mm mrad MeV/sup 1/2/). Both sources have lifetimes >200 hours and they are used extensively on the Wisconsin EN tandem.

Energy Technology Data Exchange (ETDEWEB)

To improve mirrors coating, we have modeled sputtering of binary oxide targets using TRIM code. First, we have proposed a method to calculate TRIM input parameters using on the one hand thermodynamic cycle and on the other hand Malherbe`s results. Secondly, an iterative processing has provided for oxide steady targets caused by ionic bombardment. Thirdly, we have exposed a model to get experimental sputtering yields. Fourthly, for (Ar - SiO{sub 2}) pair, we have determined that steady target is a silica one. A good agreement between simulated and experimental yields versus ion incident angle has been found. For (Ar - Ta{sub 2} O{sub 5}) pair, we have to introduce preferential sputtering concept to explain discrepancy between simulation and experiment. In this case, steady target is tantalum monoxide. For (Ar - Ta+O{sub 2}) pair, tantalum sputtered by argon ions in reactive oxygen atmosphere, we have to ...

International Nuclear Information System (INIS)

The influence of heat treatment on the structure, mechanical properties and fracture peculiarities of high-strength (#alpha#+#beta#)-titanium alloy VT22 has been studied. It is ascertained that thermal cycling and subsequent high-temperature aging permit to reduce considerably crack growth rate. Thermal cycling is realized in the following mode: heating in #beta#-region, cooling and allowance in (#alpha#+#beta#)-region, heating in #beta#-region.

International Nuclear Information System (INIS)

VT6 titanium alloy long-range fibers have been extracted from the suspended melt drop with the following high-rate solidification. Formation of the structure of fibrous porous material prepared from these fibers has been studied. 7 refs.; 5 figs.; 2 tabs.

International Nuclear Information System (INIS)

The influence of structure on mechanical properties in the course of tensile tests in a wide range of temperatures was studied, using the VT16 structure thermally strengthened (alpha+beta)-titanium alloy by way of example. It is ascertained that transition from ductile to brittle fracture at the temperature of -196 deg C is observed only in coarse-grain alloy having alpha-eldging of beta grains.

International Nuclear Information System (INIS)

The relationships of hydrogen alloyed #beta#-titanium alloy deformation behaviour to its microstructure and texture are investigated. It is shown that plasticity increases and strain induced texture changes at low hydrogen contents (0.1-0.2 mass %). Possible mechanisms responsible for specific features of #beta#-Ti alloy deformation are discussed. The study is made using alloy VT35 doped with hydrogen

International Nuclear Information System (INIS)

Peculiarities of metastable #beta#-solid solution decmposition in titanium alloy VT30 in the process of isothermal ageing in the range 500-650 deg C are investigated. Using the methods of transmittion electron microscopy, X-ray diffraction analysis, etc., it is shown that in the case of alloy quenching from the temperature below the point of complete polymorphous transformation (T_t_._t_.), as well as after warm rolling the course of subsequent decomposition of solid solution can be consierably complicated.

UK PubMed Central (United Kingdom)

This study prospectively assessed the outcome of 134 cemented titanium stems and serum ion levels. The stems were polished (0.1 μm Ra) with circular cross section. At the end point,...Full Text Available

International Nuclear Information System (INIS)

Slurry aluminizing is one method of protecting titanium alloys and intermetallics at temperatures at which oxidation would otherwise significantly degrade mechanical properties. The technique produces a continuous layer of alumina-forming TiAl_3 on exposed surfaces. The influence of composition, film thickness, and diffusion temperature upon the oxidation resistance of these slurry aluminides was studied in cyclic tests to 816degC (1500deg F). Degradation of slurry aluminized #beta#-titanium alloy and #alpha#-Z titanium aluminide intermetallic occurs by localized oxidation at cracks in the coating layer. These cracks are probably due to mismatch of coefficients of thermal expansion between the coatings and substrates. Addition of silicon to the slurry modifies the oxidation behaviour around a crack by introducing a continuous layer of titanium silicide at the boundary of the aluminide coating and ...

Energy Technology Data Exchange (ETDEWEB)

New techniques were developed to construct Schottky barrier and homojunction solar cells on GaAs substrates. Schottky barrier metal-semiconductor solar cells were produced for the first time on p-type GaAs substrate using a sputter-deposition method to form the barrier. The sputter deposition of gold or gold/palladium is the key to the method since normal thermal evaporation of gold onto p-type GaAs produces ohmic contacts. The results of this investigation are consistent with the idea that sputter damage produces donor type surface states on GaAs. Barrier heights were measured for both p-type sputtered and n-type thermally evaporated diodes using current-voltage and capacitance-voltage methods. Deep-level transient spectroscopy was used to identify the trap center concentration and energy levels for both diodes in an effort to explain the relatively large dark current in the p-type ...

Science.gov (United States)

Natural bone consists of hard nanostructured hydroxyapatite (HA) in a nanostructured protein-based soft hydrogel template (ie, mostly collagen). For this reason, nanostructured HA has been an intriguing coating material on traditionally used titanium for improving orthopedic applications. In addition, helical rosette nanotubes (HRNs), newly developed materials which form through the self-assembly process of DNA base pair building blocks in body solutions, are soft nanotubes with a helical architecture that mimics natural collagen. Thus, the objective of this in vitro study was for the first time to combine the promising attributes of HRNs and nanocrystalline HA on titanium and assess osteoblast (bone-forming cell) functions. Different sizes of nanocrystalline HA were synthesized in this study through a wet chemical precipitation process following either hydrothermal treatment or sintering. Transmission electron microscopy images showed that ...

Energy Technology Data Exchange (ETDEWEB)

Modifications to the reference concept were studied and the best approaches defined. The impact of the high efficiency multibandgap solar array on the reference concept design is considered. System trade studies for several solid state concepts, including the sandwich concept and a separate antenna/solar concept, are described. Two solid state concepts were selected and a design definition is presented for each. Magnetrons as an alternative to the reference klystrons for dc/rf conversion are evaluated. System definitions are presented for the preferred klystron and solid state concepts. Supporting systems are analyzed, with major analysis in the microwave, structures, and power distribution areas. Results of studies for thermal control, attitude control, stationkeeping, and details of a multibandgap solar cell study are included. Advanced laser concepts and the meteorological effects of a laser beam power transmission concept are considered.

British Library Electronic Table of Contents (United Kingdom)

Fluoroalkyl end-capped vinyltrimethoxysilane oligomer suffered the sol-gel reaction under alkaline conditions in the presence of titanium oxide nanoparticles in tetrahydrofuran to afford the corresponding fluorinated oligomer/titanium oxide nanocomposites[RF-(VM-SiO2)n-RF/TiO2] in excellent to moderate isolated yields. These fluorinated composites thus obtained were nanometer size-controlled fine particles, and exhibited good dispersibility and stability in traditional organic solvents except for water. These fluorinated nanocomposites were applied to the surface modification of glass to exhibit not only a completely superhydrophobic characteristic (a water contact angle: 180degree) with a non-wetting property against water droplets but also a good oleophobicity imparted by fluoroalkyl seg...

International Nuclear Information System (INIS)

A thermodynamic analysis of the behaviour of Alloy 800 in helium based atmospheres relevant to the High Temperature Gas Cooled Reactor indicates that, depending upon the precise gas composition, oxidation and carburisation, or carburisation alone may be expected. The prime influence appears to be the moisture level. The morphology and structure of the reaction products are discussed. It is shown that the 'reactive' elements chromium, manganese, titanium and silicon are concentrated in the oxide scale which is normally duplex in structure. Aluminium oxide is formed at grain boundaries and in an internal oxidation zone together with titanium and sometimes silicon. In carburising conditions, mixed titanium-chromium carbides are formed. When this occurs, intergranular penetration is maximised. Weight gain data are assessed and briefly described and a tentative model for the mechanism of corrosion of Alloy 800 in HTR helium is ...

Energy Technology Data Exchange (ETDEWEB)

Titanium oxides were grown anodically to selected final potentials on grade II polycrystalline titanium under different anodization rates. XPS and RBS results show that the oxide consists of primarily TiO2 with a non-stoichiometric oxide/metal interface, with the slower growth rate associated with a thicker layer at the interface. Characterization using TEM reveals that the structure of the oxide evolves from a primarily amorphous phase to islands of crystallites in an amorphous matrix, to an entirely crystalline phase by increasing the polarization potential. Slower growth rates tend to remain crystalline at higher potentials. The mechanical strength of oxide films extracted from load-depth data by nanoindentation varies dramatically for oxide films grown by different rates at 9.4 V, and to a lesser extent at lower potentials. The variation of film strength is associated with both compositional and structural characteristics.

Energy Technology Data Exchange (ETDEWEB)

An inorganic particulate adsorbent of a titania-alumina is described for treating a superheated water containing radioactive materials such as cobalt ions, which is free from release of corrosive impruities, and which has a high adsorption capacity of radioactive materials and a high mechanical strength is prepared by hydrolyzing a titanium alkoxide and an aluminum alkoxide, thereby forming a hydrous titanium oxide and a hydrous aluminum oxide, respectively; precalcining the hydrous titanium oxide and aluminum oxide, mixing and molding the resulting titania and alumina into a particulate mixture thereof having a titania mole fraction of 0.2 to 0.9, and calcining the particulate mixture at 500/sup 0/-700/sup 0/C. This absorbent is effectively used in treat boiling water-type nuclear reactor core-circulating water to remove radioactive substances therefrom.

Energy Technology Data Exchange (ETDEWEB)

Titanium diboride was heated to high temperatures using microwaves. The highest temperature obtained was 2245/degree/C. Unfortunately, oxidation was a problem, especially at the higher temperatures, although an argon flush and a carbon getter were used. To completely stop oxidation, the oxygen potential must be below 10/sup /minus/18/ atmospheres. Using an argon flush and a carbon getter, titanium diboride was successfully densified to 82% of theoretical without measurable oxidation by heating with microwaves to 1860/degree/C. Density actually decreased upon reaching temperatures above 1860/degree/C due to void formation adjacent to the surface. Void formation is thought to be due to the formation of B/sub 2/O/sub 3/(g) which evolves rapidly above 1860/degree/C because of the loss of a TiO/sub 2/ protective film which melts at this temperature. 9 refs., 12 figs., 2 tabs.

British Library Electronic Table of Contents (United Kingdom)

Asymmetric Incremental Sheet Forming (AISF) is a relatively new manufacturing process. In AISF, a CNC driven forming tool imposes a localized plastic deformation as it moves along the contour of the desired part. Thus, the final shape is obtained by a sequence of localized plastic deformations. AISF is suitable for small series production of sheet metal parts as needed in aeronautical and medical applications. Two main process limits restrict the range of application of AISF in these fields. These are the low geometrical accuracy of parts made from titanium alloys or high strength steels and, for titanium alloys, the limited formability at room temperature. In this paper a new concept for laser-assisted AISF is introduced including the required components. Furthermore, the CAX tools used f...

International Nuclear Information System (INIS)

The effect of various hydrogen concentrations on the crystal lattice period and the hardness of titanium alloy was examined, the alloy containing about 16 at.% Mo (27.5 wt. % Mo) and having #beta# structure. The peculiar features of the mechanism of plastic deformation of the alloy were studied after adding hydrogen to it. A dependence of the crystal lattice period on the concentration of hydrogen was obtained for TixMoxH_2 alloy. It has been established that the hardness of the Ti-Mo alloy does not change when hydrogen is added to it. The presence of hydrogen introduces changes into the mechanism of deformation of #beta#-titanium alloy. The configuration of the inverse pole figures after rolling proves that the transverse slip process in an alloy with hydrogen is hampered, and that the coplanar slip process is developing in it.

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Titanium is the most biocompatible metal used for dental casting; however, there is concern about its marginal accuracy after porcelain application since this aspect has direct influence on marginal fit. Purpose The purpose of this study was to determine the effect that metal selection and the porcelain firing procedure have on the marginal accuracy of metal ceramic prostheses. Material and methods Cast CP Ti, milled CP Ti, cast Ti-6Al-7Nb, and cast Ni-Cr copings (n=5) were fired with compatible porcelains (Triceram for titanium-based metals and VITA VMK 95 for Ni-Cr alloy). The Ni-Cr alloy fired with its porcelain served as the control. Photographs of metal copings placed on a master die were made. Marginal discrepancy was determined on the photographs using an image ...

International Nuclear Information System (INIS)

A method is described for determination of aluminium, cadmium, cobalt, chromium, copper, calcium, magnesium, sodium, potassium, manganese, nickel, lead, strontium, zinc, titanium and vanadium in iron ore. After dissolution, a 1 gram sample of iron ore is applied to a column of AGI-X8 anion exchange resin (chloride form), in 100 ml of 7M HCl. Aluminium, chromium, calcium, magnesium, sodium, potassium, manganese, nickel, lead, strontium, titanium and vanadium are eluted with 7M HCl; iron, copper and cobalt are eluted with 0.5M HCl; cadmium and zinc are eluted with 2M HNO_3. Iron is subsequently removed from copper and cobalt by a solvent extraction with methyl isobutyl ketone. The elements are determined in the eluates by atomic absorption spectrometry, except for titanium and vanadium, which are determined spectrophotometrically.

International Nuclear Information System (INIS)

Stemming from their unique combination of elevated strength, low density, and good overall corrosion resistance, beta titanium alloys have become attractive candidate materials for critical, high-stress, components in corrosive services. An overview of the comparative corrosion resistance of beta alloys to conventional alpha and alpha/beta titanium alloys in common industrial and aerospace service environments generally reveals attractive behavior depending on the environment and alloy composition and, in some cases, alloy condition. Expanded performance windows are especially noted for the molybdenum-rich beta alloys, particularly in regard to resisting reducing acids, stress corrosion, and high temperature localized chloride attack, along with hydrogen and oxidation resistance. Where applicable, implications of this enhanced corrosion performance on current and perspective beta alloy applications are also noted.

Energy Technology Data Exchange (ETDEWEB)

This work analyzes the unoptimized prototype triode-sputtered, 150 microns thick tantalum coatings deposited with a 2.5 microns niobium underlayer on the bore of a large-diameter A723 steel cylinder. The coating was deposited for wear and erosion protection by Pacific Northwest National Laboratory. The phase determination was based on X ray diffraction analysis, wavelength dispersive X ray fluorescence analysis, energy dispersive X ray analysis, and hardness and electrical resistivity measurements. Both X ray diffraction and radius-of- curvature methods were used to determine residual stresses. A locally developed high-resolution pole figure technique was used to perform texture analysis. The post-firing, debonded coating showed alpha-tantalum, preferred 110 orientation, high surface stresses, tantalum oxides, entrapped krypton sputtering gas, interstitial oxygen, and other impurities. The surface and subsurface pole figures revealed broadened ...

International Nuclear Information System (INIS)

A single plasma process involving three consecutive steps has been developed for producing high gas flow catalytic nanostructures on the electrodes of proton exchange membrane (PEM) fuel cells (FC). Using a high density helicon radio frequency (13.56 MHz) plasma, nickel is sputtered onto a porous carbon support. Changing the background gas from argon to methane/hydrogen allowed 2 ?m long, 37 nm diameter carbon nanofibres (CNFs) to be grown by diffusion through the nickel clusters in a 'tip growth' mechanism at the relatively low temperature of 400 deg. C. The third step involves plasma sputtering of platinum onto the CNFs, resulting in nanoclusters (3-8 nm) being formed on the periphery of the CNFs. Four FC cathodes were synthesized on carbon paper and PTFE/carbon loaded cloth (known as gas diffusion layer, GDL), both with and without CNFs, with the Pt/CNFs nanostructures grown on PTFE/carbon loaded cloth having the best FC performances. ...

Energy Technology Data Exchange (ETDEWEB)

A technique has been developed which enables the direct sputter generation of atomic negative ion beams of all members of the Group IA elements (Li, Na, K, Rb and Cs). The method is based on the use of sputter samples formed by pressing mixtures of the carbonates of the Group IA elements and 10% (atomic) Cu, Ag or other metal powders. The following intensities are typical of those observed from carbonate samples subjected to approx. = 3 keV cesium ion bombardment: Li/sup -/: greater than or equal to 0.5 ..mu..A; Na/sup -/: greater than or equal to 0.5 ..mu..A; K/sup -/: greater than or equal to 0.5 ..mu..A; Rb/sup -/: greater than or equal to 0.5 ..mu..A; Cs/sup -/: greater than or equal to 0.2 ..mu..A.

International Nuclear Information System (INIS)

The desire to study negative ion structure and negative ion-photon interactions has spurred the development of ion sources for use in research and industry. The many different types of negative ion sources available today differ in their characteristics and abilities to produce anions of various species. Thus the importance of choosing the correct type of negative ion source for a particular research or industrial application is clear. In this study, the results of an investigation on the production of beams composed of negatively-charged rare-earth ions from a cylindrical-cathode-geometry, cesium-sputter-type negative ion source are presented. Beams of atomic anions have been observed for most of the first-row rare-earth elements, with typical currents ranging from hundreds of picoamps to several nanoamps.

Energy Technology Data Exchange (ETDEWEB)

Pattern formation on GaAs by Ga{sup +} focused-ion-beam (FIB) irradiation and subsequent Cl{sub 2} gas etching was carried out. A higher etch rate at the FIB-irradiated area compared with that not irradiated under Cl{sub 2} gas allows pattern construction without a mask process. The degree of residual crystal damage was evaluated using photoluminescence (PL) intensity measurements. The PL intensity in the etched region was one order of magnitude stronger than that of FIB sputtering, and was several times stronger than that of Ga{sup +} FIB-assisted Cl{sub 2} etching. Etch depths of the order of 100 nm, which is five times deeper than that obtained by FIB sputtering, were efficiently performed using moderate Ga{sup +}-ion doses.

UK PubMed Central (United Kingdom)

Peri-prosthetic infections are notoriously difficult to treat as the biomaterial implant is ideal for bacterial adhesion and biofilm formation, resulting in decreased antibiotic sensitivity....Full Text Available

Science.gov (United States)

This study deals with the torsional response of Ti-8823 and 18Ni (200) maraging steel. The effect of different heat treatments and the subsequent change in microstructure are investigated. In the case of the Ti-8823, a comparison was made between the solu...

Science.gov (United States)

The corrosion behavior of Ta, Ti, and Zr in inorganic acids, bases, chlorides and miscellaneous salts, waters and gases, and organic acids and miscellaneous organic chemicals is summarized. (W.L.H)

International Nuclear Information System (INIS)

Ti-15Mo-2.7Nb-3Al-0.2Si (Timetal-21S), a metastable #beta#-titanium alloy, is a candidate material for titanium matrix composite structures in hydrogen-fueled hypersonic planes because of its excellent formability and adequate mechanical properties in the 500--800 C temperature range. The alloy is strengthened through the precipitation of fine #alpha# particles in the #beta# matrix. The mechanical properties and microstructures are controlled by a solutionizing/aging heat treatment. A major concern in using titanium alloys in hydrogen service is the embrittlement caused by the precipitation of hydrides. It is believed that the large solubility of hydrogen in the #beta#-phase would preclude the precipitation of hydrides in Beta titanium alloys, especially at low hydrogen pressures. However, depending on the hydrogen content, a shift in the ductile/brittle transition temperatures to levels much higher ...

International Nuclear Information System (INIS)

Three types of titanium hydrides have been reported: #delta#, #epsilon# and #gamma# hydrides. The #delta# hydride forms in the composition range from TiH/sub 1.5/ to TiH/sub 1.99/ and has a CaF/sub 2/ structure with metal atoms on an fcc lattice and hydrogen atoms randomly occupying tetrahedral interstitial sites. At higher hydrogen concentrations, TiH/sub 2/, the fct (c/a # #epsilon# transformation is apparently diffusionless, similar to that operating in the cubic/tetragonal transformation in zirconium hydride. The metastable fct #gamma# hydride having a c/a value of 1.09 or 1.12 forms from solid solutions of hydrogen in the hcp #alpha# matrix. While the titanium hydride precipitation in #alpha#-Ti and its alloys has attracted extensive investigation, hydride formation in bcc #beta#-Ti alloys has rarely been studied because they have not been thought to be liable to hydride formation. This paper shows conclusive evidence for the fcc #delta# ...

Energy Technology Data Exchange (ETDEWEB)

The development of structural barriers for nuclear waste packages involves selection of candidate materials, their screening by mechanical and corrosion testing, rigorous accelerated testing, and evaluation and comparison with other package elements. This document presents results from work conducted on titanium and ferrous alloys.

Science.gov (United States)

Wood, R. A.; and Ogden, H. R.: The All-Beta Titanium Alloy (Ti-13V-llCr-3Al). DMIC Rept. 110 (ASTIA AD 214002), Battelle Mem. Inst., Apr. 17, 1959. 22. White ...

International Nuclear Information System (INIS)

The tool materials durability problem, in particular shock and wear resistance, has allowed to formulate a set of requirements and also to stablish the dependence between physical properties and wear. However, for understanding the nature of the process, for example determining the tribological property of the cutting tool, it is necessary to consider the atom interactions in a crystal. A theoretical study of the physical properties of cutting tool materials (W-Ti-C) with varying concentration of titanium is presented. Total and partial local electronic density for each atom in such hard solutions were calculated. (nevyjel)

International Nuclear Information System (INIS)

Strain rate effects for the high strength, metastable beta-titanium alloy Ti-8Mo-8V-2Fe-3Al are assessed in terms of tensile and fracture toughness behavior. It is shown that as the strain rate increases the yield strength, ultimate tensile strength, and ductility also increase. As a result of the decrease in the amount of intergranular fracture as the strain rate is increased, the dynamic fracture toughness values K/sub Id/ are greater than those obtained under static conditions as given by K/sub Q/.

International Nuclear Information System (INIS)

We demonstrate reversible movement of (1/2)[110](110) dislocation loops generated from nanodisturbances in a #beta#-titanium alloy. High resolution transmission electron microscope observations during an in situ tensile test found three reversible deformation mechanisms, nanodisturbances, dislocation loops and martensitic transformation, that are triggered in turn with increasing applied stress. All three mechanisms contribute to the nonlinear elasticity of the alloy. The experiments also revealed the evolution of the dislocation loops to disclination dipoles that cause severe local lattice rotations.

International Nuclear Information System (INIS)

Production of titanium alloys from the mixture containing large amounts of metallurgy wastes is very promising. It is shown that unlimited possibilities of the waste material use in the mixture (up to 100%) are provided by garnissage melting, the size of the cast being limited only by that of the vessel. With garnissage being used as a consumed electrode the metal is refined from hydrogen and the blank ingots to serve as consumed electrodes in electro-slag remelting are chemically homogeneous. The ingots thus obtained have dense structure, rather fine grain homogeneous chemical composition, are no less pure than those obtained by vacuum arc remelting and provide for economic savings.

International Nuclear Information System (INIS)

Studied are the mechanical properties of welded joints and heat affected zones of the Kh8N10T steel and OT4 and VT1-2 titanium alloys on welding in Ar+deltaF_6 and Ar+CCl_2F_2 mixtures contributed to a decrease of porosity. Tensile and impact tests of welded joints have revealed that additions of sulfur hexafluoride into argon causes a decrease of impact strength in titanium alloy when the tensile strength does not depend on the composition of a halogen-containing atmosphere. Freon (CCl_2F_2) additions decrease only slightly the impact strength of the investigated alloys.

International Nuclear Information System (INIS)

Formation of basis type texture at rolling of Ti + 6.0% Al + 1.5% V + 1.0% Mo system alloy with initial prismatic texture is investigated by means of X-ray techniques. Variations of mechanical features in titanium alloy sheets depending on temperature-deformation conditions of rolling are investigated. Main conditions for formation of the intensive basis textute in the investigated alloy sheets which provides for isotropic properties in sheet plane and for increased ductility are determined.

Energy Technology Data Exchange (ETDEWEB)

The recent rapid progress in surface treatment techniques dictates that the titanium alloys should have an improved resistance to frictional wear without any loss of their high corrosion resistance. These requirements can be satisfied by producing surface layers of specified microstructure and phase composition. The present paper describes a modification of the plasma discharge nitriding treatment of titanium alloys, i.e. the glow discharge-assisted oxycarbonitriding, which by introducing oxygen, nitrogen and carbon into the surface zone of the layer [a Ti(NCO) type layer] improves its useful properties, primarily the resistance to frictional wear and the resistance to corrosion [T. Wierzchon, J. Sobiecki, Vacuum, 44 (1993) 975; T. Wierzchon et al., in: G. Hecht, F. Richter, J. Hahn (Eds.), Thin Films, DGM Informationgesellschaft, Germany, 1994, p. 195] [1:2]. This is because titanium shows a good affinity to oxygen, carbon ...

International Nuclear Information System (INIS)

Contrary to the electronic excitation induced phenomena of desorption and sputtering, we observed incorporation of oxygen in a thin Fe film during its irradiation with swift heavy ions. It is observed that the adsorbed oxygen diffuses in to the Fe film. The incorporation of oxygen and its diffusion in the bulk of the film is a manifestation of extremely large electronic energy deposition by the incident ions. It is shown that the experimentally observed high diffusivity of oxygen in Fe during irradiation is due to the existence of transient melt phase of Fe.

International Nuclear Information System (INIS)

The possibilities and problems of PCA in phase separation are shown on Ni, Pd, and Pt silicides. The PCA depth profiles are less influenced by sputter and matrix effects than usual Auger depth profiles. The position of the silicide-Si interface is well defined by the component distribution crossover in PCA profiles. An interface component between Pd and Pt silicides and Si substrate is determined by PCA. (author).

Science.gov (United States)

Partial Contents: Ternary Compounds; Granular Superconductors; Superconductivity in (SN)x and its Halogen Derivative (SNBr0.4)x; Studies of cuCl at Elevated Pressures; Superconducting Properties of Hydride Systems; Thin Film Superconducting Materials Research; Synthesis of Superconducting Nb3Si using High Pressures; Synthesis of Unstable A-15 Compounds by Epitaxial Recrystallization of Ion Implanted Layers; and Sputtering of Nb3Si.

Energy Technology Data Exchange (ETDEWEB)

In a reactor environment, the surface of a limiter or wall is primarily determined by the mechanism of erosion and deposition of surface material. It should be possible to use pellet injection to reduce net erosion to zero everywhere if low-Z materials are used for the surface. Erosion rates can, in general, be minimized by large area limiters and high plasma temperatures, which transmit power to the walls with less sputtering. Under ideal steady state conditions the wall surface is dominated by metallurgical effects in the wall.

Energy Technology Data Exchange (ETDEWEB)

Photoelectrochemical oxidation is a potentially interesting method for destroying toxic organic materials. We have studied the photoelectrocatalytic activity of TiO{sub 2} films made by thermal oxidation of titanium, low pressure chemical vapour deposition (LPCVD), and anodisation of titanium. Two model organic compounds have been investigated for photooxidation: methyl phosphonic acid (MPA) which is a nerve gas analogue and 4-chlorophenol (4-CP) which is a chlorinated aromatic compound considered a standard for the evaluation of the TiO{sub 2} / UV processes. In addition to photoelectrochemical characterisation the films have been characterised by profilometry, XRD, AFM, photocurrent spectroscopy and Raman microscopy. Correlations have been made between the physical properties of the thin films and their catalytic activities. The most catalytic sample of thermally oxidised titanium was prepared at 400 deg C, and the ...

Energy Technology Data Exchange (ETDEWEB)

Radio frequency (RF) plasma nitriding using different input plasma processing powers (250-600 W) improves the surface of titanium by forming hard phases of TiN, Ti{sub 2}N, and Ti (N) into the surface. The characteristics of the compound layer have been investigated by optical microscopy, microhardness measurements, and X-ray diffraction. The effect of plasma power on the sample temperature, electron temperature, and plasma density was studied using Langmuir double probe. The measured surface hardness value of the compound layer is 2190 HV 0.1 for treated sample at plasma power 500 W. The compound thickness continuously increases as the plasma power increases. The highest nitriding rate of 5.88 {mu}m{sup 2}/s was recorded when the input plasma power was adjusted at 550 W. This high nitriding rate of treated titanium samples is ascribed to the high concentration of active nitrogen species in the plasma atmosphere and the formed microcracks near ...

International Nuclear Information System (INIS)

A rapid and sensitive method for the separation and determination of titanium and iron in thiocyanate system has been developed. The extractability of Ti(II) by high molecular weight (HMWA) in organic solvent (HCl/sub 3/) and its separation from Fe(III) was examined. The yellow coloured complex of Ti(II)-SCN in quantitatively extracted into the organic phase containing tribenzyl tribenzylamine (TBA) - a high molecular weight amine, whereas the blood red coloured complex of Fe(III)-SCN formed under the same conditions get separated in the aqueous phase. On the basis of the selective extractability, a method has been developed for the separation as well as simultaneous determination of Ti(II) and Fe(III) in presence of many other elements. The molar extinction coefficients were found to be 1.9 x 10/sup 5/ l mol/sup -1/ cm/sup -1/ and 1.11 x 10/sup 5/ l mol/sup -1/ cm/sup -1/ respectively for Ti(II) and Fe(III). The extractability of the complex of fully applied to ...

International Nuclear Information System (INIS)

Samples of 316L stainless steel, Vitalium and Ti6A14V titanium alloy have been implanted with doses of 1.5, 3, and 4.5 x 10"1"7 Si"+/cm"2. Transmission electron microscopy shows that during ion implantation amorphous layers are formed. When samples of titanium alloy were implanted with a dose of 0.5 x 10"1"7 Si"+/cm"2, the implanted layer consisted of a dispersion of fine silicide crystallites instead of being amorphous. The corrosion resistance was analyzed by electrochemical techniques in 0.9% NaCl at the temperature of 37 C. The increase of corrosion resistance has been observed as a result of structural modifications of the surface layer. (author). 7 refs, 4 tabs.

International Nuclear Information System (INIS)

A new high strength titanium alloy has been developed primarily intended for fastener applications. While Ti-6Al-4V is used extensively as a fastener alloy in the aerospace industry, its shear strength allowable is limited to 655 MPa (95 ksi). For higher shear strength requirements, various steels or nickel-based alloys are used (up to 860 MPa (125 ksi)), but with the attendant density penalty. This new alloy is intended to provide the 860 MPa shear strength at roughly a 40% weight savings. After screening various alloy systems, the optimum chemistry has been selected as follows: Ti-6.0V-6.2Mo-5.7Fe-3Al. In light of its 125 ksi shear strength goal, the alloy has been designated TIMETAL reg-sign 125.

International Nuclear Information System (INIS)

The fatigue life variability of the #alpha#+#beta# titanium alloy, Ti-6Al-2Sn-4Zr-6Mo increased with decreasing stress level. The variability in life was found to be due to segregation of lives due to two failure mechanisms. A bimodal cumulative distribution model was shown to accurately describe the combined failure modes. The nominal failure processes for the two regimes were similar, with crack nucleation occurring in equiaxed #alpha#p particles, irrespective of life or stress level. However the variability in life was not controlled by the size of the crack-nucleating #alpha#p, but rather by the ability of the material to distribute deformation and avoid early crack nucleation.

Energy Technology Data Exchange (ETDEWEB)

Gas and plasma nitriding processes were executed in the magnesium with modification by titanium in search for an effective surface treatment method for magnesium alloys. Magnesium-nitrogen system has completely no solid solution or solubility, so that nitride should be only formed by eutectic reaction in the liquid phase. Hence, magnesium is difficult or nearly impossible to have its surface modified by nitriding. Addition of nitride forming element into magnesium enables us to lower the onset temperature of nitriding. Magnesium-titanium alloys with 1 to 5 wt% are yielded by the bulk mechanical alloying and, subjected to gas nitriding for various process conditions. Successful co-formation of Mg{sub 3}N{sub 2} as well as TiN becomes a proof to demonstrate the possibility of gas/plasma nitriding in the solid-state magnesium with aid of nitride former. (orig.)

International Nuclear Information System (INIS)

Strain embrittlement in Ti base alloys during tensile testing was investigated. Results show that in an #alpha#-#beta# titanium alloy the local activity of H in alpha phase (#alpha#/sub H//sup #alpha#) increases and activity of H in beta phase (#alpha#/sub H//sup #beta#) decreases as the equiaxed #alpha# particle size decreases at constant volume fraction of phases. Thus with decreasing particle size there would be a tendency for H to move from #alpha# to #beta#, decreasing the H content of #alpha#. Also whether H tended to move from #beta# to #alpha# or from #alpha# interiors to the #alpha#-#beta# interface this tendency would be reduced by surface tension effects, making the alloy less susceptible to embrittlement.

Energy Technology Data Exchange (ETDEWEB)

Photodestruction has received much attention in recent years. In particular, titanium dioxide (TiO{sub 2}) and ozonolysis have attained a position of prominence. These technologies hold promise for the destruction of trace amounts of aqueous high explosives that are generated by load and pack operations, as well as demilitarization activities. Currently this water is treated by passing through a bed of activated carbon. The carbon is then steam regenerated and reused, thus creating a second waste stream which must be disposed of, or the carbon is burned directly. Recent trends in environmental regulation have shown that this may not be a viable option for process water remediation in the future. This talk will discuss efforts to employ alternate aqueous treatment techniques that not only remove the explosives compounds but are able to transform the parent compound into carbon dioxide and water. Titanium dioxide photocatalysis as well as ...

Science.gov (United States)

Experimental tests were performed in a continuous-flow hydrotreating unit at Pittsburgh Energy Technology Center to evaluate the performance of hydrous titanium-oxide supported (HTO) catalysts as hydrotreating catalysts for use in two-stage coal liquiefaction. Catalysts containing either a combination of CO, Ni, and Mo as the active metal components or Pd as the active metal componet were tested with representative hydrotreater feed stocks from the Wilsonville Advanced Coal Liquefaction Research and Development Facility. Catalyst performance evaluation was based on desulfurization and denitrogenation activity, the conversion of cyclohexane-insolbule material, and hydrogenation activity during 100-hour reactor runs. Results indicated that the HTO catalysts were comparable to a commercial Ni/Mo-alumina supported catalyst in the areas evaluated. 11 refs., 1 fig., 6 tabs.

British Library Electronic Table of Contents (United Kingdom)

Regularities of deformation-induced dissolution of a surface layer of iron oxides in matrixes of iron-based alloys with bcc and fcc lattices have been studied by the methods of M?ssbauer spectroscopy, transmission electron microscopy, and X-ray diffraction. A method of producing iron alloys strengthened by dispersed oxide nanoparticles and alloyed with elements possessing a high affinity to oxygen (titanium and yttrium) has been proposed, which implies a dynamic dissolution of a surface layer of iron oxides upon strong cold deformation and a precipitation of secondary yttrium and titanium nanooxides upon a subsequent high-temperature sintering of mechanically alloyed powders. There has been demonstrated a possibility of oxide strengthening of pure iron upon its interaction with air without...

International Nuclear Information System (INIS)

To study #beta# #reversible# #omega#-transformation in pseudo-#beta#-titanium alloy VT30, doped by hydrogen, methods of X-ray diffraction and thermodifferential analyses are used. It is established that in the process of heating of the hardened alloy from 0.004-0.1% H first formation and then dissolution of #omega# phase take place. An increase in hydrogen content to 0.1% decreases thermal effect of the processes and does not affect the temperature of #beta# #reversible# #omega#-transformation. Introduction of hydrogen in the concentration of 0.2% and higher suppresses completely #beta# #reversible# #omega# - transformation. A decrease in heating rate displaces #beta# #reversible# #omega#-transformation to lower temperatures.

International Nuclear Information System (INIS)

A study is made into textures of deformation and primary recrystallization forming in a #beta#-titanium alloy doped with hydrogen in amounts from 0.04 to 0.55 mass. %, on cold rolling with a 70%-reduction and dehydrogenating annealing at 860 deg C. It is shown that a volume fraction of recrystallization texture components is determined by the nature of corresponding deformation texture, in its turn, depending on hydrogen concentration in the alloy. At low hydrogen contents the main texture components are #left brace#111#right brace# and #left brace#001#right brace#. A hydrogen content increase up to 0.09 - 0.18 mass. % results in formation of dominant components of #left brace#111#right brace# and #left brace#112#right brace#

International Nuclear Information System (INIS)

Results of investigation on the effect of microstructure and deformation conditions (temperature and strain rate) on flow stress and critical strain in two phase #alpha# + #beta# titanium alloy Ti-6Al-5Mo-5V-1Cr-1Fe is presented in the paper. The alloy is deformed or torsional plastometer at temperature range 1073-1173 K and at the strain rate #epsilon# = 0.04-4.0 s"-"1. Sequential deformation at 1173 K at the strain rate of 0.4 s"-"1 was also performed with holding times in the range 1-100 s. The fraction of dynamically and metadynamically recrystallized #beta# phase was determined on the basis of results of sequential deformation test. Microstructure was examined using LM and TEM techniques. (author)

British Library Electronic Table of Contents (United Kingdom)

ABSTRACT Purpose: The aim of this two-center study was to evaluate screw-type titanium implants with a chemically modified, sandblasted and acid-etched surface when placed in the posterior maxilla or mandible, and loaded 21 days after placement. Material and Methods: All 56 patients met strict inclusion criteria and provided informed consent. Each patient displayed either a single-tooth gap, an extended edentulous space, or a distal extension situation in the posterior mandible or maxilla. Eighty-nine dental implants (SLActive, Institut Straumann AG, Basel, Switzerland) were inserted according to an established nonsubmerged protocol and underwent undisturbed healing for a period of 21 days. Where appropriate, the implants were loaded after 21 days of healing with provisional restorations i...

Science.gov (United States)

During this reporting period two direct coal liquefaction experiments have been completed and a third is underway. These experiments have produced conversion and selectivity data on samples of Alabama bituminous coal slurried in tetralin and catalyzed using iron-titanium hydride. The experiments address the liquefaction of an agglomerating coal. Conversions of 45 to 55% DAF in 30 min have been recorded at 500/sup 0/F and 520 psia. Equipment modifications were made in an attempt to eliminate the problem of alloy binding in the hydride formation vessel. 4 figs., 4 tabs.

International Nuclear Information System (INIS)

The gliding modes of a duplex Ti-6Al-4V titanium alloy were investigated through in situ (scanning electron microscopy) tensile tests. A method based on electron back-scattering diffraction (EBSD) measurements was used to identify activated slip systems. The approach applied to a large number of grains allowed a statistical analysis of the nature (basal, prismatic, pyramidal) and distribution of the slip systems according to the crystallographic texture. A discussion concerning the pertinence of Schmid's law to explain the occurrence and succession of slip events is then proposed. The domain in favor of each type of slip system is finally presented by using inverse pole figures mapped with Schmid's factor iso-curves.

International Nuclear Information System (INIS)

The energy distribution of ion beams is important especially for low energy ion beam applications. The energy distributions of negative-ion beams produced through secondary ion emission by sputtering were measured and compared with theoretically estimated distributions by use of four different negative-ion production probability equations (modified surface ionization model, exponential velocity dependence model, and our modified exponential velocity dependence models (modified decaying factor model and combination model of velocity dependence and surface ionization)). In the measurements, the energy distributions of C"- and Ag"- beams had a peak at a few to several eV and the full width at half maximum were 15 eV and 11 eV, respectively. These results could be well explained by the estimated distributions by virtue of our combination model or the modified surface ionization model. copyright 1996 American Institute of Physics.

International Nuclear Information System (INIS)

Superconductivity of binary alloys spanning the A-15 compounds V_3Si, V_3Ge, V_3Ga, and V_3Al and the pseudobinary derivatives of these stoichiometric compounds was surveyed by studying samples prepared by rf-sputtering from alloy cathodes. The possible formation of the hypothetical A-15 binaries ''V_3P,'' ''V_3B,'' and ''V_3C'' and their pseudobinary formation with V_3Si was also explored. Efforts to form these hypothetical alloys were not successful. The T/sub c/'s were measured resistively and the structure and lattice constants were determined by x-ray analysis. A maximum T/sub c/ of 11.7"0K was obtained for A-15 V_3Al, and the importance of a suitable deposition temperature and high sputtering pressures was examined. It is proposed that large variations of T/sub c/ among pseudobinary alloys imply a rapid variation of the density of states at the Fermi level.

Energy Technology Data Exchange (ETDEWEB)

A versatile, high brightness, volume type, low power RF source, capable of producing positive ion beams with intensities as high as 1 mA from gaseous feed materials and microamperes of negative ion beams has been characterized. The source can also be operated as a plasma sputter negative ion source to generate up to 1 mA of a selected species. The performance of the source in the positive and negative volume modes of operation can be greatly enhanced by addition of a removable, water cooled filament assembly in place of the negative sputter probe. For examine, the material utilization efficiencies of gaseous feed species can be more than doubled, total current intensities increased up to 40%, molecular dissociation fractions increased by 20% and minimum operating pressures reduced by a factor of four when operated in the volume mode. These added electrons also favorably effect, as a consequence of lower pressures, the emittance apparently ...

Energy Technology Data Exchange (ETDEWEB)

Nano-wire arrays of Niobium were produced by small angle sputtering on facetted sapphire, using the self shadowing effect of the facets. A wire width of about 80 nm was adjusted, the mean (maximum) wire height was about 20 nm (30 nm), the length can be in the cm range. Meander-film morphologies of 20 nm mean (26 nm maximum) thickness were produced by conventional sputtering onto smooth sapphire substrates at elevated temperatures. The morphology of the wires was investigated with atomic force microscopy (AFM), using contact mode. Meander-films were studied by scanning tunnelling microscopy (STM). Hydrogen loading was performed by instantaneously increasing the hydrogen gas pressure above the solubility limit. Thus, an elongated hydride could be monitored in an about 30 nm thick wire. STM studies on meander-films show the presence of cylindrical hydrides. Local out-of-plane and in-plane expansion can be explained by the formation of hydrides, ...

International Nuclear Information System (INIS)

Epitaxial metastable (GaSb)/sub 1-x/Ge/sub x/ alloys with compostions across the pseudobinary phase diagram have been grown on (100) GaAs substrates by multitarget rf sputtering. An essential feature allowing the growth of these metastable materials was low-energy ion bombardment of the growing film during deposition to enhance surface diffusion, promote mixing, and preferentially sputter incipient second-phase precipitates. Annealing experiments indicated that the metastable films exhibit good high-temperature stability and that they transform through a continuous series of GaSb-rich and Ge-rich phases in which the solute concentrations decrease until the equilibrium two-phase alloy is obtained. While the calculated free-energy difference between the single-phase metastable and equilibrium states is approx.18 meV, the measured activation barrier for the transformation is approx.3 eV. All films were p-type with room-temperature hole ...

International Nuclear Information System (INIS)

Focused ion beam (FIB) processes have been developed for Y--Ba--Cu--O superconductor films. A Y--Cu liquid metal ion source has been fabricated, using a Y_6_7 --Cu_3_3 eutectic alloy as the ion source. As-sputtered Y--Ba--Cu--O film etch rate ratios to GaAs(100) and Si(100) substrates are 0.28 and 1.4 for 130-keV Au"+ FIB ion etching, respectively. Y--Ba--Cu--O submicron patterns have been demonstrated by using FIB lithography and Cl_2 reactive ion beam etching. Moreover, a Y--Ba--Cu--O superconducting line with 4-#mu#m linewidth has been fabricated by annealing an as-sputtered Y--Ba--Cu--O line pattern. T/sub c/ control of Y--Ba--Cu--O film has been achieved by 200-keV Ne"+, using conventional ion implantation and 300 keV Si"+"+ FIB ion implantation.

Energy Technology Data Exchange (ETDEWEB)

A C{sub 60} {sup +} primary ion source has been coupled to an ion microscope secondary ion mass spectrometry (SIMS) instrument to examine sputtering of silicon with an emphasis on possible application of C{sub 60} {sup +} depth profiling for high depth resolution SIMS analysis of silicon semiconductor materials. Unexpectedly, C{sub 60} {sup +} SIMS depth profiling of silicon was found to be complicated by the deposition of an amorphous carbon layer which buries the silicon substrate. Sputtering of the silicon was observed only at the highest accessible beam energies (14.5 keV impact) or by using oxygen backfilling. C{sub 60} {sup +} SIMS depth profiling of As delta-doped test samples at 14.5 keV demonstrated a substantial (factor of 5) degradation in depth resolution compared to Cs{sup +} SIMS depth profiling. This degradation is thought to result from the formation of an unusual platelet-like grain structure on the SIMS crater bottoms. Other ...

Energy Technology Data Exchange (ETDEWEB)

The composition of sputter-deposited HgS films was determined by electron microprobe analysis. From the relative x-ray intensity as a function of film thickness, the depth of the ionizations that produce SK sub(..cap alpha..) and HgM sub(..cap alpha..) was found to be approximately 0.65 ..mu..m at an accelerating voltage of 15 kV. This value agreed well with a value calculated from Castaings' empirical law after absorption correction. The determination of film composition was limited to sufficiently thicker films than this critical value, usually 1 - 2 ..mu..m thick. The relation between the conposition of bulk standard determined by chemical analysis and the x-ray intensity ratio was used for the correction of film composition. The results showed that the crystal structure of HgS films was independent of the composition, i.e., the growth of metastable ..beta..-HgS films was not caused by the nonstoichiometry, and that the composition of ..cap alpha..-HgS ...

Energy Technology Data Exchange (ETDEWEB)

A multicusp magnetic field plasma surface ion source, normally used for H/sup /minus//ion beam formation, has been modified for the generation of high-intensity, pulsed, heavy negative ion beams suitable for a variety of uses. To date, the source has been utilized to produce mA intensity pulsed beams of more than 24 species. A brief description of the source, and basic pulsed-mode operational data, (e.g., intensity versus cesium oven temperature, sputter probe voltage, and discharge pressure), are given. In addition, illustrative examples of intensity versus time and the mass distributions of ion beams extracted from a number of samples along with emittance data, are also presented. Preliminary results obtained during dc operation of the source under low discharge power conditions suggest that sources of this type may also be used to produce high-intensity (mA) dc beams. The results of these investigations are given, as well, and the technical issues that must be ...

Energy Technology Data Exchange (ETDEWEB)

A method using a focused ion beam (FIB) to prepare a silicon amorphous material is presented. The method involves the redeposition of sputtered material generated during the interaction of the Ga{sup +} ion beam with a silicon substrate material. The shape and dimensions of this amorphous material are self-organized and reproducible. The stability of this amorphous material under electron irradiation was investigated in the transmission electron microscopy (TEM). Electron irradiation can induce recrystallization of the amorphous material, resulting in the lateral and vertical growth, starting at an amorphous-crystalline interface, of polysilicon containing defects.

Energy Technology Data Exchange (ETDEWEB)

In situ Auger sputter depth profiles of saturation implants of 3 keV N/sub 2//sup +/ in silicon at room temperature exhibit a sharp peak in the nitrogen concentration in the outermost layers, followed by a monotonic decrease. No broad plateau was observed. The energy of the Auger line corresponding to the Si(2p) core electron excitation, monitored throughout the profiling, exhibits a chemical shift of up to 7 eV at the surface peak concentration. Inert gas ion post-bombardment of unsaturated implants significantly modifies the profile, and supports the suggestion that the surface peak arises through radiation enhanced diffusion of implanted atoms.

Energy Technology Data Exchange (ETDEWEB)

The composition and thickness of etch residues on the base of submicrometer via holes cannot be surmized from data on larger features. Auger sputter depth profiles were used to compare etch residues in 0.55 {mu}m via holes produced by different etch processes and remaining after different cleans. These residues varied significantly in composition and thickness with the processing history of the sample and from those on larger features. A focused ion beam (FIB) sample preparation was developed to expose the bases of via holes and to help reduce sample charging. (author).

Energy Technology Data Exchange (ETDEWEB)

An RF plasma sputter type heavy negative ion source, which can deliver mA-class negative ion beams (12.1 mA, 1.6 mA and 2.3 mA for Cu{sup -}, C{sup -} and C{sub 2}{sup -} currents, respectively) in dc-mode operation, has been developed. In ion source, a dense plasma of 10{sup 11} cm{sup -3} order was generated in the xenon gas pressure of 10{sup -3}-10{sup -2} Pa with an rf (13.56 MHz) power of 200 - 300 W by using an RF coil, and a relatively large sputtering target of 42 mm in diameter was used. As for intense negative ion beams of silicon or boron which are important dopants for semiconductor fabrication, negative ion extraction properties of the negative ion source was investigated. The extracted total negative ion currents of 4.4 mA for a silicon target and 2.8 mA for a LaB{sub 6} target were obtained after electrons were eliminated by magnetic field near the extraction hole. From results of mass-analysis, it was found that Si{sup -} ...

International Nuclear Information System (INIS)

It is shown that it is necessary to take into account locality of the analysis and to introduce additional corrections for partial capture of matrix and fluorescent subexcitation by matrix during quantitative X-ray spectral microanalysis of finely dispersed materials. Cast two-phase (#alpha#+#beta#) titanium alloy VT3-1 is chosen as an investigation object.

Science.gov (United States)

Two-wave mixing in sillenite crystals such as bismuth silicon oxide (Bi12SiO20) and bismuth titanium oxide (Bi12TiO20) of (001)- and (221)-cuts for counterpropagating geometry was studied within the frame of slowly varying amplitude approximation. Electrooptic, photoelastic, piezoelectric, self-diffraction effects and optical activity were taken into account.

International Nuclear Information System (INIS)

The alloy of Ti-Al-Mo-V-Cr system is studied for its structure in a strained state and specific features of #beta#-#alpha# transformation in a #beta#-matrix and deformation twins on ageing. It is determined that preliminary deformation initiates the decomposition of solid solution on aging. In a metastable #beta#-titanium alloy the substructure of deformation twins is shown to vary essentially with aluminium and chromium partial substitution for molybdenum and vanadium

Science.gov (United States)

In a redox battery using a titanium redox system or chromium redox system as an active material for the negative electrode or a manganese redox system as an active material for the positive electrode, the electromotive force of the battery and the stability of electrolyte solutions are enhanced by addition of a chelating agent such as citric acid or a complexing agent such as phosphoric acid to the redox system used therein.

International Nuclear Information System (INIS)

Brief summaries are given of research carried out in the following areas: absorption spectroscopy of titanium, niobium, and molybdenum in uranium alloys; atomic absorption spectroscopy of selenium in stainless steel, computer program improvements for spectrophotometer control, and detection of beryllium in stack gases; electrolysis for inactivation of bacteria in cooling-tower water; improved solvent analysis by gas chromatography; sequential radionuclide separation for various sample matrices; progress on an electron microprobe analyzer; and miscellaneous projects.

Energy Technology Data Exchange (ETDEWEB)

Achievements in the field of sorption recovery of uranium from sea water are considered in brief. Polyacryl amidoxime chelate iorites are shown to exceed in sorption properties both titanium dioxide base natural adsorbents and styrene base synthetic resins. Merits of sorbents containing fixed layer of humic acid are pointed out, different methods of their application are considered. The cost of uranium recovery from sea water using different sorbents is estimated.

International Nuclear Information System (INIS)

The mechanical properties of TS 6 (Ti--10 percent Cr--7 percent V--3.5 percent Mo--3 percent Al) alloy were studied. Results are presented in plots showing yield stress vs cold work, notched tensile strength vs unnotched tensile strength, and ultimate tensile strength vs test temperature.

Science.gov (United States)

In this Communication, we report the fabrication of well-crystallized rutile-phase TiO2 hollow spheres using potassium titanium oxalate as the precursor. The spheres exhibited unique three-dimensional hierarchical architectures and demonstrated a significantly improved photocatalytic performance. The synthetic strategy used in this process represents a general approach and therefore may contribute to the formation mechanisms of hollow nanostructures. PMID:16634578

British Library Electronic Table of Contents (United Kingdom)

The review provides a general idea about the types of metallic alloys and the pure metals used as implant materials in dental and orthopedic surgery. Their corrosive behavior in both real solutions and various media that model human biological fluids is described. Based on the literature data, it is concluded that multicomponent alloys containing titanium, niobium, zirconium, tungsten, molybdenum, aluminum, and silicon are the most resistant to corrosion. Implants made of different types of stainless steel are preferred when manufacturing orthopedic devices for short-term use.

International Nuclear Information System (INIS)

It is shown that bending tests on microsamples can be used to study the conditions in which hydrogen brittleness develops. In such tests hydrogen brittleness develops in the VTI5 alloy within the temperature range +5 to -20"0C. The tendency of VTI5 to develop hydrogen brittleness is enhanced with bending in salt water. (author).

International Nuclear Information System (INIS)

A historical overview of corrosion problems found in power plant condensers and mitigation procedures is presented. The paper is organized according to alloy type and failure mode. Alloys considered are copper-base alloys, stainless steels and titanium. Failure modes discussed include erosion-corrosion, sulfide attack, environmentally assisted cracking, galvanic corrosion, steam condensate corrosion, pitting corrosion, and dealloying. Mitigation procedures discussed include cathodic protection, ferrous ion injection, as well as tube cleaning and layup practices.

Energy Technology Data Exchange (ETDEWEB)

The goal of the invention is to increase the effectiveness of the isolation process through increasing the waterproofing of the stratum. The cited goal is achieved by isolating water influx into a well through introduction of a chemical reagent into the stratum. To interact with the stratum, an alloy of titanium and iron is introduced into the stratum as the chemical reagent with subsequent pumping of hydrogen into the stratum at 100 to 200C.

International Nuclear Information System (INIS)

The introduction of oxygen in the vicinity of a metallic target surface, bombarded with positive argon ions of twenty kiloelectron-volts, increases the number of sputtered atoms in the excited state. This phenomenon of exaltation, very sensitive in the case of nickel and aluminium, is much less marked in the case of molybdenum. Moreover, the emission of excited particles coming from the beam's ions is not modified. A quantum-mechanical model of a kinetic emission process, which permits the interpretation of the clean metallic target's emission phenomena, seems insufficient to explain all of the results obtained in the presence of oxygen. In this last case one can therfore use a thermodynamic model in which excited metallic particles can be formed directly by chemical surface reactions of neutralization or reduction. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Reactively sputtered tantalum nitride (Ta/sub 2/N) has been investigated as a diffusion barrier between Pd/sub 2/Si and aluminum and CoSi/sub 2/ and Al. Ta/sub 2/N is found to be an excellent matallurgical diffusion barrier for the two systems up to 555 /sup 0/C, with no intermixing observed in Rutherford backscattering and Auger electron spectroscopic studies. Schottky barrier devices n-Si/Pd/sub 2/Si/Ta/sub 2/N/Al were excellent and showed no deterioration after annealing at 500 /sup 0/C. However, similar devices with CoSi/sub 2/ contacts and Ta/sub 2/N barrier showed a creation of high contact resistance between the silicide and the as-deposited nitride.

Energy Technology Data Exchange (ETDEWEB)

Carbon films have been made by a variety of techniques, including evaporation, sputtering, and laser or thermal pyrolysis of organic polymers. Polyacrylonitrile (PAN) is often used as a carbon precursor, since low-temperature thermo-oxidative pretreatment produces a material which can be pyrolyzed without loss of shape. This is the basis for the production of carbon fibers with good mechanical properties. We report here the formation of very thin films of carbon (500 to 1500 A) by pyrolysis of spin-cast PAN. Using this technique, large, conductive films can be made which are sufficiently robust to allow intact lift-off and transfer of the films from one substrate to another. Such films are chemically inert, but can be photolithographically patterned and etched with an oxygen plasma.

Energy Technology Data Exchange (ETDEWEB)

We have investigated via SQUID magnetometry and polarised neutron reflectivity the exchange-bias effect in CoO/Co sputtered multilayers. In particular, we studied the magnetisation reversal and the time relaxation of the exchange-bias field close to the coercive field H{sub c1}. Neutron intensities of all four cross sections (I++, I+-, I-+, I-) were recorded at the position of the first multilayer Bragg peak while scanning the magnetic field. From such scans we infer that the magnetisation reversal for the ascending as well as for the descending branch of the magnetic hysteresis occurs not by in-plane rotation but through domain-wall movements. The exchange-bias field, H{sub EB}, is strongly affected by thermal fluctuations. H{sub EB} decreases, following an exponential decay function with a half-life time of about 580 s at T=240 K. (orig.)

International Nuclear Information System (INIS)

Highly ordered arrays of Ni nanoholes and Fe20Ni80 antidots have been prepared, respectively, by replica/antireplica processing and sputtering techniques using nanoporous alumina membranes as templates. Geometrical characteristics as nanohole/antidot diameter, interpore distance and the overall hexagonal symmetry of arrays are controlled through the original templates. Experimental data on their hysteresis and magnetic domain structure have been taken by vibrating sample magnetometry and magnetic force microscopy, respectively. An analysis of the magnetization process, resulting magnetic anisotropy and magnetic domain structure is summarized considering the influence of those geometry aspects. In particular, the hexagonal symmetry and the density of nanohole/antidots determine the overall magnetic behavior, which is of interest in future high-density magnetic storage systems.

Energy Technology Data Exchange (ETDEWEB)

The optical emission of excited H reflected from clean Cu(110) after impingement of H/sup +/ and H/sub 2//sup +/ in the energy range of 250 eV to 20 keV per nucleon at 70/sup 0/ angle of incidence to the surface normal was measured. For incident 10 keV H/sub 2//sup +/, the highest excited hydrogen state detected was the n=10 level. The Hsub(..cap alpha..) yield was found to be fluence and energy dependent. This effect is attributed either to fast sputtered hydrogen, surface roughness or to an increase with hydrogen concentration in electron states of p-like symmetry near the Fermi level of copper. The Hsub(..cap alpha..) yield per reflected nucleon shows approximately an exponential dependence on both projectile energy per nucleon and scattered particle reciprocal velocity perpendicular to the surface.

International Nuclear Information System (INIS)

A series of sputtered tungsten-carbon multilayer structures with periods ranging from 2 to 12 nm in the as-prepared state and after annealing at 500 degrees C for 4 hours has been studied with high resolution transmission electron microscopy. The evolution with annealing of the microstructure of these multilayers depends on their period.As-prepared structures appear predominantly amorphous from TEM imaging and diffraction. Annealing results in crystallization of the W-rich layers into WC in the larger period samples, and less complete or no crystallization in the smaller period samples. X-ray scattering reveals that annealing expands the period in a systematic way. The layers remain remarkably well-defined after annealing under these conditions.

International Nuclear Information System (INIS)

Focussed ion beam (FIB) processing has been applied to the fabrication of novel InP-based cleaved coupled cavity (CCC) quantum cascade lasers (QCL). Gas assisted etching using XeF_2 has been shown to significantly reduce the redeposition of sputtered material onto the mirror surfaces during final milling. For the unprocessed laser a broad spread of lasing peaks are observed between 9.72#mu#m to 9.78#mu#m at a current of 380mA (1kA/cm"-"2). After FIB processing, substantial side mode suppression is observed on applying a current of 20mA (100A/cm"-"2) to the short section and the main lasing peak is observed at 9.77#mu#m.

International Nuclear Information System (INIS)

The authors present an investigation of structural changes occurring in bilayer stacks with crystalline columnar growth when one of the layers is substituted by layers known to grow amorphous. In Co/Cu multilayers the Co layers were substituted by CoZr layers of varying Zr content and layer thickness. Structural characterization was performed by transmission electron microscopy (TEM). They show that the amorphization of the CoZr layers leading to a destruction of the columnar growth depends both on the Zr content and on the thickness of the CoZr layers. Additionally a change to textured growth with a normal to the substrate occurs with increasing Zr content. They explain their observations by a simple picture based on the hard sphere model.

International Nuclear Information System (INIS)

The use of Auger electron spectroscopy (AES) combined with in situ sputter etching for revealing the metallurgy of the metal-semiconductor interface is presented. The physical basis, measurement techniques, and data interpretation for Auger analysis of thin-film structures are briefly reviewed. Results of a detailed study of an alloyed multilayered contact (Ni/Au-Ge) on n-type epitaxial GaAs are summarized to illustrate how electrical and metallurgical contact properties can be correlated using AES. In addition, the results of a study of the growth kinetics and chemical phase identification of palladium silicide on single-crystal Si is given, as well as the initial results of a study of aluminum-palladium silicide interaction at elevated temperature.

International Nuclear Information System (INIS)

Composite nitrides (such as BN, TiN) are widely used in various industrial applications because of their extreme wear and corrosion resistance, thermal and electrical properties. in order to obtain composite materials with these optimal properties, it is important to elucidate whether any chemical reactions occur at nitride/metal interfaces, e.g., those involving BN-Ti/TiN. Materials of interest include the deposition by PVD of Ti and TiN on BN substrates. Some of these systems were then subjected to varying degrees of physical and thermal alteration. Detailed X-ray photoelectron spectroscopy (XPS) has therefore been rendered of these interfaces using cross-sectional display and sputter etching. Resulting structural and morphological features have been investigated with transmission electron microscopy (TEM) and X-ray diffraction (XRD). Diffusion of the nitridation, oxynitride formation and interfacial growth are of general interest.

International Nuclear Information System (INIS)

Beta-21S is a new, metastable-beta titanium alloy which exhibits excellent oxidation resistance and mechanical properties at elevated temperatures. From a weld solidification standpoint, this alloy chemistry is of particular interest because its major beta-stabilizing elements (Mo and Nb) both exhibit equilibrium partitioning ratios (k_o) greater than unity, indicating their simultaneous partitioning during weld solidification to the initial solid to form (i.e., dendrite cores), and correspondingly their depletion in the final regions of solidification (i.e., dendrite interstices). Such elemental partitioning, if retained down to room temperature, may be expected to promote local variations in the postweld aging response. The objectives of the present investigation were to characterize Gas Tungsten-Arc weld solidification and HAZ liquation phenomena in Beta-21S and to examine the influence of residual microsegregation in the weld zone on alpha precipitation during ...

Science.gov (United States)

The spectral dependences of absorption photoinduced in a pure bismuth titanium oxide crystal by 532-nm laser pulses are studied. It is shown that optical absorption in the crystal in the range from 492 to 840 nm increases with increasing exposure. The photoinduced absorption relaxes in the dark for more than 60 hours. A model of photoinduced absorption is proposed which assumes the population of two trap centres with the normal energy distribution law for the concentrations of electrons photoexcited from donors to the conduction band. This model well describes the spectral dependences of photoinduced absorption by using the average ionisation energies of the traps E{sub 1} = 1.60 eV and E{sub 2} = 2.57 eV. The model is used to estimate the increase in the photorefractive sensitivity of a bismuth titanium oxide crystal in the near IR region, which was earlier observed after exposing the crystal to visible radiation. It is predicted that the ...

International Nuclear Information System (INIS)

Based on information contained in literature, patents and catalogs a review is presented of powder-rolling metallurgy abroad. Statistics are given on the output of powder metallurgy in several countries. In the USA both the dense type of rolled metal for manufacturing various machine parts and the porous variety for making filters are produced. Four main types of technological processes are analysed: the usual flow chart for cold rolling, rolling of preheated powder, rolling in free-flowing state, and rolling with heated rollers. Of these four processes the first is most widely used. Fowders consisting of spherical particles (heat-stable alloys from nickel or high titanium alloys), which are difficult to work with, have not yet found wide practical application in powder metallurgy abroad. Literature data show that granulated heat-resistant alloys can be cold-treated under pressure only after they are powdered. The best methods for pulverizing are: cold-stream ...

International Nuclear Information System (INIS)

Mechanical properties of cold-worked molybdenum, grade 4 titanium, and an #alpha#-#beta# titanium alloy are measured with tensile tests and by indentations using conical indenters with 105, 120, and 137 deg included angles. The extent of plastic deformation and pileup around an indentation is measured using profilometry. Various models predicting the extent of plastic deformation and pileup are compared to the actual measured values. As inferred from indentation, the calculated yield strength of the material from the mean pressure does not correlate well to the yield strength measured by tensile testing. The plastic zone size surrounding an indentation can also be used to determine the yield strength of the material, and this does correlate to the yield strength measured by tensile tests. Furthermore, the extent of plastic deformation is relatively independent of the included angle of the indenter for the range of materials used in this system. ...

Energy Technology Data Exchange (ETDEWEB)

Transmission electron microscopy studies on solution-annealed Alloy 800 revealed small (100-200 nm), spherical-shaped titanium carbide (face centered cubic structure) and large (200 nm-5 {mu}m), faceted titanium nitride (hexagonal structure) particles randomly distributed in the austenite matrix. The volume fraction of former particles was found to be greater than that of the latter. Corrosion studies of the alloy in acidic, chlorides and acidic chloride environments at room temperature indicated that the passivity of Alloy 800 was adversely affected by the addition Cl{sup -} ions. X-ray photoelectron spectroscopy revealed that the surface film formed on the alloy at the onset of passivity consisted of Cr{sup 3+} (as Cr{sub 2}O{sub 3}), without any Fe{sup 3+}/Fe{sup 2+} or Ni{sup 2+}. Scanning electron microscopy studies indicated initiation of pitting at large, faceted particles, not at small, spherical-shaped ones.

Energy Technology Data Exchange (ETDEWEB)

To improve the surface properties of magnesium alloy, a lining process using shot peening was carried out. The lining of magnesium alloy with metals such as titanium and nickel is useful in heightening the corrosion and wear properties for the components. In the shot peening experiment, the foil set on the magnesium workpiece is pelted with many shots at a high velocity. The foil is bonded to the surface of the workpiece due to plastic deformation induced by the collision of the shots. A pure aluminum foil is inserted between the hard foil and magnesium workpiece to assist the bonding. To heighten the bondability, the foil and workpiece are heated and the flow stresses of the metals are reduced. In this experiment, a centrifugal shot peening machine with an electrical heater was employed. The workpieces were commercially magnesium alloys AZ31B and AZ91D, and the foils were commercially pure aluminum, pure titanium and pure nickel. The effects ...

Energy Technology Data Exchange (ETDEWEB)

The usually low wear resistance of titanium materials can be increased by the thermochemical surface treatment nitriding. In result of comparative investigations of gas and plasma nitriding it will be shown that it is possible to obtain a specific variation of the properties in the highly stressed case by means of these both technologies on example of the ({alpha}+{beta}) alloy Ti-6Al-4V. Gas and plasma nitriding was carried out in the temperature range from 650 to 800 C over 4 to 48 h in different gas atmospheres, i.e. 100% NH{sub 3} (gas), 100% N{sub 2} (gas and plasma), 20% H{sub 2} + 80% N{sub 2} and 20% Ar + 20% H{sub 2} (plasma). The temperature range was fixed in the middle of ({alpha}+{beta}) region, because the core properties are influenced negative in the field of {beta}-transustemperature. The relations between the applied nitriding technologies, the layer structure (chemical, phases, geometrical) and selected layer properties (microroughness, ...

International Nuclear Information System (INIS)

The effect of mean stress, or the stress ratio (R), on the fatigue-crack growth (FCG) behavior of #alpha#-aged and #omega#-aged microstructures of the beta titanium alloy Ti-10V-2Fe-3Al was investigated. While the mean stress had a negligible effect on the FCG behavior of the #alpha#-aged microstructure, a strong effect was observed in the #omega#-aged microstructure. In particular, the values of the threshold stress-intensity range (#DELTA#K_t_h) exhibited a strong dependence on R in the #omega#-aged microstructure, while this dependence was weak in the #alpha#-aged microstructure. These effects seem to arise primarily from fracture-surface roughness-induced crack closure. The crack closure levels for the #alpha#-aged microstructure were found to be very low compared to those for the #omega#-aged microstructure. Transmission electron microscopy and scanning electron microscopy studies of microstructures and fracture surfaces were performed to gain insight into the ...