International Science & Technology Center (ISTC)

Metal Matrix Composites on the Basis of Nano-Materials

Energy Technology Data Exchange (ETDEWEB)

DC resistivity, dc magnetization, and specific heat of eight Sc/sub 5/Co/sub 4/Ge/sub 10/-type crystal structure compounds R/sub 5/T/sub 4/Ge/sub 10/ for R = Dy, Ho, Er, Tm, and T = Rh and Ir are presented. The resistivity, single crystal magnetization, and specific heat results show that in all those compounds, the magnetic moments order antiferromagnetically in the c direction at low temperature. However, in the Er and Tm compounds, the magnetizations along x-y hard directions do not show any anomalies above 2.0 K. This suggests that the ordered Er and Tm ions, which have positive quadrupole coefficients ..cap alpha../sub j/, interact with a crystal field that has an electronic potential valley along the c axis. The fitting of the hard axis magnetizations to Curie-Weiss law suggests that the resulting antiferromagnetic-like theta reflects ...

British Library Electronic Table of Contents (United Kingdom)

Nanomaterials are increasingly being used to modify adhesives used in aerospace and materials applications. Improvements in thermal and mechanical properties have been found by incorporation of small amounts of nanosize materials in to such adhesives. However, the introduction of nanomaterials to adhesives used in civil engineering applications is still a new approach which needs to be explored, especially in retrofitting of structures. This paper presents part of an ongoing research to address the effect of adding nanomaterials to modify a thermosetting adhesive used for bonding carbon fibre reinforced polymer (CFRP) composites to concrete members. Vapour grown carbon fiber (VGCF) was chosen to modify the adhesive. Different concentrations of carbon nanofibres PR-24 XT-LHT were adopted fo...

CERN Document Server

An in-plane uniaxial magnetic anisotropy has been observed in thin Co films normally deposited onto obliquely sputtered Ta and Pt underlayers. Associated with this anisotropy is an augmented easy axis coercivity. The in-plane easy axis is, in most cases, perpendicular to the incident deposition plane. Microstructural results indicate that grains are well connected along the magnetic easy axis but are separated by long continuous voids along the hard axis, which is ascribed to a geometric shadowing effect due to the oblique incidence deposition of the underlayer. Hence, the magnetic anisotropy mimics the film growth anisotropy. It is therefore believed that the observed magnetic properties are due to magnetostatic shape anisotropy effects. In-plane coercivity and anisotropy field are shown to increase with underlayer deposition angle, underlayer thickness and ...

Energy Technology Data Exchange (ETDEWEB)

A new magnetic macroparticle filter design consisting of two 90{sup o} filters forming an S-shape is described. Transport properties of this S-filter are investigated using Langmuir and deposition probes. It is shown that filter efficiency is product of the efficiencies of two 90{sup o} filters and the deposition rate is still acceptably high to perform thin film deposition. Films of amorphous hard carbon have been deposited using a 90{sup o} filter and the S-filter, and macroparticle content of the films are compared.

CERN Document Server

We aim to obtain a consistent description of non-thermal emissions from Abell 2256 and to give a prediction for a gamma-ray emission from this galaxy cluster. Assuming that a radio relic illuminates a localization of an ongoing merger, and that both radio and non-thermal part of hard X-ray emission are due to electron component of cosmic rays filling the relic, we derived from radio and hard X-ray properties of the relic in A2256 the magnetic field strength and number densities for relativistic electrons and protons. Due to the interpretation of the radio relic as a structure formed just where a shock front is, we discuss a gamma-ray emission at the cluster periphery. The estimated strength of the magnetic field in the relic is equal to 0.05 \\muG, while the amplitude of the electron number density varies from 3 x 10^{-4} to 3 x 10^{-5} cm^{-3} (respectively for the relic thickness of 50 to 500 kpc). We ...

UK PubMed Central (United Kingdom)

During the last few years, research on toxicologically relevant properties of engineered nanoparticles has increased tremendously. A number of international research projects and additional activities...Full Text Available

British Library Electronic Table of Contents (United Kingdom)

In this article, several applications of nanomaterials in food packaging and food safety are reviewed, including: polymer/clay nanocomposites as high barrier packaging materials, silver nanoparticles as potent antimicrobial agents, and nanosensors and nanomaterial-based assays for the detection of food-relevant analytes (gasses, small organic molecules and food-borne pathogens). In addition to covering the technical aspects of these topics, the current commercial status and understanding of health implications of these technologies are also discussed. These applications were chosen because they do not involve direct addition of nanoparticles to consumed foods, and thus are more likely to be marketed to the public in the short term.

Science.gov (United States)

MAGNETIC FORMING .............. MAGNETIC INDUCTION ............ MAGNETIC MATERIALS ............ MAGNETIC MEASUREMENT .......... MAGNETIC PERMEABILITY . ...

International Nuclear Information System (INIS)

Ternary R_2TSi_3 intermetallic compounds (R=Rare Earth, T=Transition Metal) with hexagonal AlB_2-type crystallographic structure are known because of their interesting physical properties. Pr_2PdSi_3 single crystals were grown by a vertical floating zone method. The compound exhibits congruent melting behavior at a liquidus temperature of about 1770 C. Single crystalline samples show a huge anisotropy at low temperatures due to the crystal electric field effect and order antiferromagnetically below the Neel temperature T_N=2.17 K. This value approximately obeys the linear de Gennes scaling for this class of compounds. The [001] orientation was identified as the magnetic easy axis at room temperature. At lower temperature (#approx#20 K) magnetic easy and hard axes interchange with each other. Two additional magnetic phase transitions were observed at temperatures below 1 K.

British Library Electronic Table of Contents (United Kingdom)

A range of new nanomaterials to replace the active materials in lithium ion batteries are currently being studied and employed in an attempt to overcome various performance limitations of previous technologies. Nanomaterial production and manufacturing techniques appear to fit into a general trend towards more energy intensive production methods for high-tech goods. This does not necessarily imply an increase in lifecycle energy use; artefacts that consume or transform energy during use could possibly regain this increased initial input via increased efficiency in use. In particular, this paper highlights that larger gains could be possible if the artefact in question allows a given service to be provided via an alternative and more efficient system entirely.The lifecycle energy efficienci...

Environmental Research Database

Objectives1. To establish the present capacity and capability across all the sectors within the UK for - a) Undertaking research in the areas of toxicology and ecotoxicology and environmental hazard and risk assessment work on chemical subtances including emerging containments (e.g. enginerred nanomaterials); and b) Applying these skills in the policy and regulatory context. 2) The range of chemicals involved should include pharmaceutical and medical products, crop protection agents, biocides, vet [continued...]DescriptionThe aim of this project is to identify the current status of the scientific community, areas of expertise, and identify the gaps in skills, knowledge or recruitment. The project will use a questionnaire approach to obtain this information for all sectors of the business community. The analysis will identify the gaps in provision, and areas where investment is needed in future training and/or recruitment.

Energy Technology Data Exchange (ETDEWEB)

Colloidal nanocrystals attract significant interest due to their potential applications in electronic, magnetic, and optical devices. Nanocrystal supercrystals (NCSCs) are particularly appealing for their well ordered structure and homogeneity. The interactions between organic ligands that passivate the inorganic nanocrystal cores critically influence their self-organization into supercrystals, By investigating the mechanical properties of supercrystals, we can directly characterize the particle-particle interactions in a well-defined geometry, and gain insight into both the self-assembly process and the potential applications of nanocrystal supercrystals. Here we report nanoindentation studies of well ordered lead-sulfide (Pbs) nanocrystal supercrystals. Their modulus and hardness were found to be similar to soft polymers at 1.7 GPa and 70 MPa respectively and the fractures toughness was 39 KPa/m1/2, revealing the extremely brittle nature of ...

Energy Technology Data Exchange (ETDEWEB)

Four general topics are covered in respect to the natural space radiation environment: (1) particles trapped by the earth`s magnetic field, (2) cosmic rays, (3) radiation environment inside a spacecraft, (4) laboratory radiation sources. The interaction of radiation with materials is described by ionization effects and displacement effects. Total-dose effects on MOS devices is discussed with respect to: measurement techniques, electron-hole yield, hole transport, oxide traps, interface traps, border traps, device properties, case studies and special concerns for commercial devices. Other device types considered for total-dose effects are SOI devices and nitrided oxide devices. Lastly, single event phenomena are discussed with respect to charge collection mechanisms and hard errors. (GHH)

Energy Technology Data Exchange (ETDEWEB)

Superconducting rf cavities are increasingly used in accelerators. Gradient is a parameter of particular importance for the ILC. Much progress in gradient has been made over the past decade, overcoming problems of multipacting, field emission, and breakdown triggered by surface impurities. However, the quenching limit of the surface magnetic field for niobium remains a hard limitation on cavity fields sustainable with this technology. Further exploration of materials and preparation may offer a path to surpassing the current limit. For this purpose, we have designed a resonant test cavity. One wall of the cavity is formed by a flat sample of superconducting material; the rest of the cavity is copper or niobium. The H field on the sample wall is 75% higher than on any other surface. Multipacting is avoided by use of a mode with no surface electric field. The cavity will be resonated through a coupling iris with high-power rf at superconducting ...

International Nuclear Information System (INIS)

... range magnetic fields magnetic susceptibility magnetization neutron diffraction

Energy Technology Data Exchange (ETDEWEB)

Nano-materials in which a large fraction of atoms resides within a few atomic layers near the surface can be designed to have novel properties by manipulating their surface parameters. We show that the effective elastic constants of nano-porous/cellular materials can be made to exceed those of the parent materials provided the pore surface elastic parameters satisfy certain conditions. These stiff nano-porous materials herald a radical breakthrough in sandwich-type construction.

British Library Electronic Table of Contents (United Kingdom)

Purpose - This paper aims to describe the technology and applications of nanocomposite materials. Design/methodology/approach - This paper discusses products, applications and technological developments in polymer, ceramic and metal nanocomposites. It concludes with a brief consideration of electronic component applications. Findings - It is shown that polymer nanocomposites and the materials used in their production are commercially available and finding applications in several industries, including automotive, military, food, electronics and leisure, due to their enhanced mechanical, electrical and thermal properties. Ceramic and metallic nanocomposites are at an earlier stage of development and a critical issue to resolve is optimising the dispersion of nanomaterials in the matrices. Pa...

International Science & Technology Center (ISTC)

Hard Nano-Strutural Coatings Resistant to the Extreme Conditions of Chemical, Abrasive and High Energy Media for Thermonuclear Power, Oil and Gas and Chemical Industries

CERN Document Server

The nature of the hard X-ray source XSSJ12270-4859 is still unclear though it was claimed to be a magnetic Cataclysmic Variable. We here present a broad-band X-ray and gamma ray study based on a recent XMM-Newton observation and archival INTEGRAL and RXTE data. From the Fermi/LAT 1-year point source catalogue, we tentatively associate XSSJ12270-4859 with 1FGLJ1227.9-4852, a source of high energy gamma rays with emission up to 10GeV. We complement the study with UV photometry from XMM-Newton and ground-based optical and near-IR photometry. The X-ray emission is highly variable showing flares and intensity dips. The X-ray flares consist of flare-dip pairs. Flares are also detected in the UV range but not the dips. Aperiodic dipping behaviour is also observed during X-ray quiescence but not in the UV. The 0.2-100keV spectrum is featureless and described by a power law model with Gamma=1.7. The 100MeV-10GeV spectrum is instead represented by a ...

CERN Document Server

We construct models for gamma-ray bursts where the emission comes from internal shocks in a relativistic wind with a highly non uniform distribution of the Lorentz factor. We follow the evolution of the wind using a very simplified approach where a large number of layers interact by direct collisions but where all pressure waves have been suppressed. We suppose that the magnetic field and the electron Lorentz factor reach large equipartition values in the shocks. Synchrotron photons emitted by the relativistic electrons have a typical energy in the gamma-ray range in the observer frame. Synthetic bursts are constructed as the sum of the contributions from all the internal elementary shocks and their temporal and spectral properties are compared to the observations. We reproduce the diversity of burst profiles, the ``FRED'' shape of individual pulses and the short time scale variability. Synthetic bursts also satisfy the duration-hardness ...

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

... Title : Refining the Magnetic Forming Capability. ... Abstract : The purpose of this project was to refine the in-house magnetic forming capability. ...

Science.gov (United States)

... Examples include magnetic forming tools, magnetic shielding, magnetohydrodynamic propulsion systems, and various magnetic containment ...

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

We have investigated the nanocrystalline microstructure and the hard magnetic properties of Sm(Co{sub 0.725}Fe{sub 0.1}Cu{sub 0.12}Zr{sub 0.04}B{sub 0.015}){sub 7.4} melt-spun ribbons. The coercivity (H{sub c}) of the as-spun ribbons increased with the wheel surface speed from 2.8kOe for 10m/s to 14.5kOe for 40m/s. The post-annealing of the melt-spun ribbons from 700 to 900 deg. C for 10min did not lead to a substantial increase of H{sub c}. However, after isothermal aging at 820 deg. C and subsequent slow cooling (0.5 deg. C/min) to 120 deg. C, H{sub c} increased from 2.8 to 10.9kOe for 10m/s, while it decreased from 14.5 to 13.5kOe for 40m/s ribbons. The grain size of the melt-spun ribbon reduced with structural transformation from 2:17H (Th{sub 2}Ni{sub 17}-hexagonal type) to 1:7H (TbCu{sub 7}-hexagonal type) as the wheel surface speed was increased. Three-dimensional atom probe analysis showed a boron enriched precipitate at the grain ...

Energy Technology Data Exchange (ETDEWEB)

Nanoparticles of silver halides have been prepared by mixing silver halide powder with a single liquid phase consisting of an ionic liquid, isooctane, n-decanol and water. Much higher nanoparticle concentrations may be formed with ionic liquids using this new simple method than are found with conventionally applied surfactants. This method also emphasizes the applicability of ionic liquids as versatile components in microemulsions and as solvents for the synthesis of nanomaterials. The effect on the nanoparticles of changing the composition of the liquid mixtures and the nature of the ionic liquid is analysed. High nanoparticle concentrations were only found with chloride based ionic liquids, indicating the importance of the ionic liquid anion in the mechanism of the reaction.

British Library Electronic Table of Contents (United Kingdom)

This study addresses the solar thermal decomposition of natural gas for the co-production of hydrogen, as well as Carbon Black as a high-value nano-material, with the bonus of zero CO2 emissions. The work focused on the development of a medium-scale solar reactor (10kW) based on the concept of indirect heating. The solar reactor is composed of a cubic cavity receiver (20cm side), which absorbs concentrated solar irradiation through a quartz window via a 9cm-diameter aperture. The reacting gas flows inside four graphite tubular reaction zones that are settled vertically inside the cavity. Experimental results were as follows: methane conversion and hydrogen yield of up to 98% and 90%, respectively, were achieved at 1770K, and acetylene was the most important by-product, with a mole fraction...

CERN Document Server

A novel algebraic topology approach to supersymmetry (SUSY) and symmetry breaking in quantum field and quantum gravity theories is presented with a view to developing a wide range of physical applications. These include: controlled nuclear fusion and other nuclear reaction studies in quantum chromodynamics, nonlinear physics at high energy densities, dynamic Jahn-Teller effects, superfluidity, high temperature superconductors, multiple scattering by molecular systems, molecular or atomic paracrystal structures, nanomaterials, ferromagnetism in glassy materials, spin glasses, quantum phase transitions and supergravity. This approach requires a unified conceptual framework that utilizes extended symmetries and quantum groupoid, algebroid and functorial representations of non-Abelian higher dimensional structures pertinent to quantized spacetime topology and state space geometry of quantum operator algebras. Fourier transforms, generalized Fourier-Stieltjes ...

Science.gov (United States)

Radial Halbach magnetic bearings have been investigated as part of an effort to develop increasingly

Science.gov (United States)

Necessary theoretical foundation is given for the treatment of magnetic stresses applied to

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

Discussion of an electrohydraulic and magnetic forming process

Energy Technology Data Exchange (ETDEWEB)

Magnetic separation of several classes of antibiotics was investigated using electrochemical magnetic seeding. Electrocoagulation with a sacrificial anode followed by addition of magnetite particles was applied for the magnetic seeding of antibiotics. With electrochemical magnetic seeding using an iron anode, tetracycline antibiotics (oxytetracycline, chlortetracycline, doxycycline and tetracycline) and cephalosporin antibiotic (cefdinir) were rapidly removed from synthetic wastewater by magnetic separation using a neodymium magnet. Iron and aluminium anodes were suitable for magnetic seeding of the antibiotics. The results indicated that the ability of antibiotics to form strong complex with iron and aluminium allowed the higher removal by magnetic separation. This method would be appropriate for rapid treatment of ...

Science.gov (United States)

Sep 1, 2011 ... Title: Hardness, density, and shrinkage characteristics of silk-oak from Hawaii. Author: Youngs, R. L.. Date: 1964. Source: Research note FPL ...

Energy Technology Data Exchange (ETDEWEB)

This report covers the test methods and equipment for testing aircraft armor both hard and soft. The hard armor are the typical ceramic type while the soft armor are various types of layered composite materials. 10 figs. (JEF)

Energy Technology Data Exchange (ETDEWEB)

This paper addresses the stability aspects of several successful dc superconducting magnets such as large bubble chamber magnets, and magnets for the Mirror Fusion Test Facility and MHD Research Facility. Specifically, it will cover Argonne National Laboratory 12-Foot Bubble Chamber magnets, the 15-foot Bubble Chamber magnets at Fermi National Laboratory, the MFTF-B Magnet System at Lawrence Livermore National Laboratory, the U-25B Bypass MHD Magnet, and the CFFF Superconducting MHD magnet built by Argonne National Laboratory. All of these magnets are cooled in pool-boiling mode. Magnet design is briefly reviewed. Discussed in detail are the adopted stability critera, analyses of stability and disturbance, stability simulation, and the final results of magnet ...

International Nuclear Information System (INIS)

We investigate the magnetic braking of the core of an axisymmetric cloud whose rotation axis is parallel to the mean direction of the magnetic field. (author).

Energy Technology Data Exchange (ETDEWEB)

The magnetic fluid is a colloidal suspension of magnetite in kerosene, prepared by a low-cost process. Separation is accomplished in an open trough filled with magnetic fluid. A magnetic field is established in the fluid, by energizing an electromagnet having poles on each side of the trough. Due to the design of the magnet poles and air gaps, the magnetic field is strongest at the bottom, about 10,000 oersteds, and uniformly decreases in strength to about 2000 oersteds at the top of the fluid. Therefore, the magnetic field gradient increases with depth. The magnetic force attracts the entire separation medium (magnetic fluid) creating a reaction force of equal magnitude and acting in the opposite direction. This reaction created within a magnetic fluid/magnetic field combination ...

Energy Technology Data Exchange (ETDEWEB)

Airbag pressure vessels for the north-American market mainly are made by forging and by the use of steel alloys. In Europe aluminum alloys are common and the manufacturing process is extrusion of circular blanks - made from cold rolled plates - in a form applying a 100 t press at room temperature. Then by heat treatment the strength/hardness of the material is properly adjusted and after that the pressure vessel parts have to be continuously inspected with an inspection and handling cycle time of 3 s. Inspection of the axis-symmetric parts is asked for surface breaking extrusion defects as well as for surface parallel delaminations in the bulk volume. Furthermore, the material strength is a quality characteristic that has to be nondestructively registered and documented. The inspection is performed by eddy current probes and an EMAT, of which the eddy current impedance measurements are used for surface breaking extrusion defect detection and sizing (single ...

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

Magnetic Forming Studies. The use of transient high magnetic-field devices has made possible the generation of very large accurately ...

International Nuclear Information System (INIS)

... susceptibility magnetization magnetoresistance monocrystals order-disorder

Science.gov (United States)

... magnetic containment field lines which is zero on the center line of the toroidal containment tube and increases in magnitude with ...

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

In order to examine the state of technology of all areas of magnetic suspension and to review related recent developments in sensors and controls approaches, superconducting magnet technology, and design/implementation practices, a symposium was held. The proceedings are presented. The sessions covered the areas of bearings, sensors and controls, microgravity and vibration isolation, superconductivity, manufacturing applications, wind tunnel magnetic suspension systems, magnetically levitated trains (MAGLEV), space applications, and large gap magnetic suspension systems.

Energy Technology Data Exchange (ETDEWEB)

CeO{sub 2} undergoes a first-order phase transition from fluorite to {alpha}-PbCl{sub 2}-type structure under high pressure. To evaluate the changes in physical properties of CeO{sub 2} nanomaterials as the particle size decreasing, high-pressure Raman study under quasi-hydrostatic condition has been performed on CeO{sub 2} nanospheres self-assembled by 5 nm CeO{sub 2} nanoparticles at room temperature. Surprisingly, as the pressure elevate to 34 GPa, the CeO{sub 2} nanospheres still retain the cubic fluorite-type structure, indicating the sample is more stable than the bulk counterpart. Whereas, previous high-pressure studies show the phase transition at 22.3/26.5 GPa for 12 nm CeO{sub 2} nanoparticles, which is less stable than the bulk materials. The enhancement of phase stability might be attributed to the increase of surface energy of CeO{sub 2} nanospheres as the size of the building units decrease. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. ...

British Library Electronic Table of Contents (United Kingdom)

This study addresses the solar thermal decomposition of natural gas for the co-production of hydrogen and carbon black (CB) as a high-value nano-material with the bonus of zero CO2 emission. The work focused on the development of a medium-scale solar reactor (10kW) based on the indirect heating concept. The solar reactor is composed of a cubic cavity receiver (20cm-side), which absorbs concentrated solar irradiation through a quartz window by a 9cm-diameter aperture. The reacting gas flows inside four graphite tubular reaction zones that are settled vertically inside the cavity. Experimental results in the temperature range 1740-2070K are presented: acetylene (C2H2) was the most important by-product with a mole fraction of up to about 7%, depending on the gas residence time. C2H2 content i...

Energy Technology Data Exchange (ETDEWEB)

The peak flux relationship between hard X-rays and microwaves from solar flares is studied using about 400 events simultaneously recorded with the hard X-ray burst spectrometer on the SMM satellite and the Nobeyama 17 GHz radiometer. The data indicate that the hard X-ray and microwave peak fluxes correlate best for X-ray energies of less than about 80 keV for impulsive flares and greater than about 360 keV for extended flares. By postulating that electrons responsible for microwave emission at 17 GHz are those emitting hard X-rays at these photon energies, it is concluded that: (1) in impulsive flares, microwaves at about 20 GHz are emitted mainly by electrons of less than about 200 keV from a layer through which the electrons stream down into the thick-target hard X-ray source; and (2) in extended flares, microwaves are emitted mainly by MeV electrons trapped in a coronal loop or ...

International Nuclear Information System (INIS)

The major details of the inspection and replacement of the bearing journals on each of the four heat transport pumps (HTPs) at Wolsung nuclear generating station in Korea are presented in this paper. Investigation following fracture of one of the journals in 1985 revealed that it was excessively hard. The journal material (ASTM A296 CA 40) is considered to be prone to stress corrosion fatigue if the hardness exceeds Rc 40. In 1986 May, during a planned outage, the HTPs were disassembled, the journals were inspected, found to be excessively hard, and all were replaced. At the same time, the pump to motor couplings were all refurbished to ensure proper alignment.

International Nuclear Information System (INIS)

Hardness of beta-sialon with four different composition index values of 0.25, 0.50, 0.75 and 1.0 in the system Ni/sub 3/N/sub 4/-AlN-Al/sub 2/O/sub 3/ with the addition of 6% Y/sub 2/O/sub 3/ as sintering aid has been reported. These composition were pressureless sintered for 90, 180 and 270 min in nitrogen atmospheres at temperatures ranging from 1650 to 1800 deg. C. Highest hardness was achieved when the composition index was 0.25 was sintered for 270 minutes at 1750 deg. C. (author).

Science.gov (United States)

... of Hanoi or Missionaries and Cannibals, It is not immediately obvious what constitutes a "move"--that is, what actual manipulations of the physical ...

International Nuclear Information System (INIS)

Monolithic SiAlON ceramics are hard and brittle with little possibility for property design, but multi-phase SiAlON ceramics offer great scope for controlling microstructural development and desired properties. The ceramics can also be reinforced by separate additions of other hard, refractory compounds. The toughness in all these SiAlON composites can be increased by several mechanisms, and the best effect is reached if they are combined. When glassy phase is present, crack paths are affected by the strains caused by different thermal expansion of the glassy phase and the crystals and also by the interface properties. The crystal shape influence toughness, especially pronounced is the effect of the elongated #beta#- grains. Different toughening mechanisms are achieved by separately added reinforcement phases. The hardness is raised by the presence of #alpha# SiAlON and other hard constituents, such as ...

Science.gov (United States)

... interacting systems in which common-envelope evolutionary effects make it hard to generalize the results to single-star evolution, although they ...

UK PubMed Central (United Kingdom)

Necrotizing sialometaplasia, is a benign inflammatory lesion primarily involving the minor salivary glands of the hard palate. The lesion often presents itself as a deep-seated palatal ulcer with clinical...Full Text Available

International Nuclear Information System (INIS)

Turkish English ... Authors Sahin, O. (Suleyman Demirel University, Department of Physics, Isparta (Turkey))

DEFF Research Database (Denmark)

Interest in optics for hard X-ray broad-band application is growing. In this paper, we compare the hard X-ray (20-100 keV) reflectivity obtained with an energy-dispersive reflectometer, of a standard commercial gold thin-film with that of a 600 bilayer W/Si X-ray supermirror. The reflectivity of the multilayer is found to agree extraordinarily well with theory (assuming an interface roughness of 4.5 Angstrom), while the agreement for the gold film is less, The overall performance of the supermirror is superior to that of gold, extending the band of reflection at least a factor of 2.8 beyond that of the gold, Various other design options are discussed, and we conclude that continued interest in the X-ray supermirror for broad-band hard X-ray applications is warranted.

International Nuclear Information System (INIS)

To investigate the magnetic fluctuations and for further transport study, the poloidal and radial magnetic field measurement is conducted on the Sino United Spherical Tokamak (SUNIST). Auto-power spectral density indicates that the magnetic fluctuation energy mainly concentrates in the frequency region lower than 10 kHz. The magnetic field oscillations, which are characterized by harmonic frequencies of 40 kHz, are observed in the scrape-off layer; by contrast, in the plasma core, the magnetic fluctuations are of Gaussian type. The time-frequency profiles show that the poloidal magnetic fluctuations are temporally intermittent. The autocorrelation calculation indicates that the fluctuations in decorrelation time vary between the core and the edge. (authors)

Energy Technology Data Exchange (ETDEWEB)

Potassium clusters arrayed in zeolite A are known to show ferromagnetic properties at low temperature. The origin of the spontaneous magnetization has been explained by a model of spin-canting in an antiferromagnetically ordered state. The direct information for the magnetic structure, however, has not been obtained so far. In the present work, we measure the neutron powder diffraction by using pulsed neutron source at KEK-KENS below and above the Curie temperature. No significant temperature-dependence was, however, obtained within the statistical errors, namely, magnetic scattering could not be detected separately. We also estimate the intensity of magnetic scattering by assuming some possible magnetic structures with considering the magnetic form factor of the cluster wave function. The intensity of magnetic scattering is estimated to be ...

International Nuclear Information System (INIS)

Scanning ion microscopy with polarization analysis (SIMPA) is used to study the spin-resolved surface magnetic structure of nano-sized magnetic systems. SIMPA is utilized for in situ topographic and spin-resolved magnetic domain imaging as well as for focused ion beam (FIB) etching of desired structures in magnetic or non-magnetic systems. Ultra-thin Co films are deposited on surfaces of Si(1 0 0) substrates, and ultra-thin, tri-layered, bct Fe(1 0 0)/Mn/bct Fe(1 0 0) wedged magnetic structures are deposited on fcc Pd(1 0 0) substrates. SIMPA experiments clearly show that ion-induced electrons emitted from magnetic surfaces exhibit non-zero electron spin polarization (ESP), whereas electrons emitted from non-magnetic surfaces such as Si and Pd exhibit zero ESP, which can be used to calibrate sputtering rates in situ. We ...

Energy Technology Data Exchange (ETDEWEB)

A model is available in predicting flocculation frequencies between particles of various properties under the influence of a magnetic field. This model provides a basic understanding of fundamental phenomena, such as particle-particle and particle-collector interactions, occurring in HGMF (high gradient magnetic field), and will be extended to describe experimental data of particle flocculation and filtration and predict the performance of high- gradient magnetic filters. It is also expected that this model will eventually lead to a tool for design and optimization of magnetic filters for environmental, metallurgical, biochemical, and other applications.

International Nuclear Information System (INIS)

The structure and properties of composite powder coatings on the base of titanium carbide are studied. It is shown the electron-beam welding deposition of powders on the base of nickel and titanium carbide allows to produce of high-quality wear-resistant coatings which superior in density and hardness compared with sputtered ones. Changes of hardening phase volume percentage as well as composition of metal matrix make possible to control coatings hardness

Energy Technology Data Exchange (ETDEWEB)

A tutorial account is given of the main characteristics and distinctive features of conceptual magnetic fusion systems employing the magnetic mirror principle. These features are related to the potential advantages that mirror-based fusion systems may exhibit for the generation of economic fusion power.

Energy Technology Data Exchange (ETDEWEB)

An introduction to time-of-flight neutron spectroscopy is presented in the context of the study of magnetic materials. Examples are taken from the class of rare earth and actinide magnetic materials known as `strongly correlated electron` systems. (author) 11 figs., 24 refs.

Energy Technology Data Exchange (ETDEWEB)

The disclosure is directed to an active magnetic regenerator apparatus and method. Brayton, Stirling, Ericsson, and Carnot cycles and the like may be utilized in an active magnetic regenerator to provide efficient refrigeration over relatively large temperature ranges.

CERN Document Server

We explore the relationship between the hard X-ray photon index $\\Gamma$ and the Eddington ratio (\\xi=L_{X}(0.5-25 keV)/L_{Edd}) in six XRBs. We find that different XRBs follow different anti-correlations between $\\Gamma$ and $\\xi$ when $\\xi$ is less than a critical value, while they follow the same positive correlation when $\\xi$ is larger than the critical value. This anti-correlation and positive correlation are also found in LLAGNs and QSOs respectively, and the anti-correlation and positive correlation of different XRBs roughly converge to the same point ($\\log \\xi=-2.1, \\Gamma=1.5$), which may correspond to the accretion mode transition, since that the anti-correlation and positive correlation are consistent with the prediction of ADAFs and standard disk/corona system respectively. The traditional low/hard state are divided into two parts by the cross point $\\log \\xi\\sim-2.1$, i.e., faint-hard state in the ...

CERN Document Server

Context: The colliding-wind binary Eta Car exhibits soft X-ray thermal emission that varies strongly around periastron, and non-thermal emission seen in hard X-rays and gamma-rays. Aims: To definitively identify Eta Car as the source of the hard X-ray emission, to examine how changes in the 2-10 keV band influence changes in the hard X-ray band, and to understand more clearly the mechanisms producing the non-thermal emission using new INTEGRAL observations obtained close to periastron. Methods: A Chandra observation encompassing the ISGRI error circle was analysed, and all other soft X-ray sources (including the outer shell of Eta Car itself) were discarded as likely counter-parts. New hard X-ray images of Eta Car were studied close to periastron, and compared to previous observations far from periastron. Results: The INTEGRAL component, when represented by a power law (with a photon index of 1.8), ...

International Nuclear Information System (INIS)

Parameters of permanent magnets result from the combination of intrinsic properties such as saturation magnetization, magnetic exchange, and magnetocrystalline energy, as well as microstructural parameters such as phase structure, grain size, and orientation. Reduction of grain size into nanocrystalline regime (#approx# 50 nm) leads to the enhanced remanence which derives from ferromagnetic exchange coupling between highly refined grains. In this study the fundamental phenomena, quantities, and structure parameters, which define nanophase permanent magnets are presented and discussed. The theoretical considerations are confronted with experimental data for nanocrystalline Sm-Fe-N type permanent magnets. (author)

UK PubMed Central (United Kingdom)

OBJECTIVE--The study was performed to examine the influence of the exposure to magnetic fields in the potrooms of an electrolysis plant on the occurrence of musculoskeletal symptoms among the employees....Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The Muon Ionization Cooling Experiment (MICE) focusing solenoid magnets focus the muon beam within the MICE cooling channel on a liquid or solid absorber that is within the warm bore of solenoid. The focusing magnet has a warm bore of 470 mm. his magnet consists of two coils 210-mm long that is separated by an aluminum mandrel that is 200 mm long. Each of the coils has its own leads. The coils may be operated in either the non-flip mode (solenoid mode with both coils at the same polarity) or the lip mode (quadrupole focusing mode where both coils are at opposite polarity). This report describes the focusing solenoid magnet design that will be built by the vendor. The progress on the construction of the first of the focusing magnets will also be discussed in this report. Ultimately three of these magnets will be built. These magnets will be ...

Science.gov (United States)

... 31. New electric forming methods offer potentials for light metals; magnetic forming and plasma forming. ... 3, 25 Magnetic Forming ..... ...

International Nuclear Information System (INIS)

Highly ordered arrays of Ni nanoholes and Fe20Ni80 antidots have been prepared, respectively, by replica/antireplica processing and sputtering techniques using nanoporous alumina membranes as templates. Geometrical characteristics as nanohole/antidot diameter, interpore distance and the overall hexagonal symmetry of arrays are controlled through the original templates. Experimental data on their hysteresis and magnetic domain structure have been taken by vibrating sample magnetometry and magnetic force microscopy, respectively. An analysis of the magnetization process, resulting magnetic anisotropy and magnetic domain structure is summarized considering the influence of those geometry aspects. In particular, the hexagonal symmetry and the density of nanohole/antidots determine the overall magnetic behavior, which is of interest in future high-density ...

Science.gov (United States)

... M(TH) in applied magnetic fields up to ± 7 T and for temperatures ranging from 2 to 300 K. The superparamagnetic (SPM) behavior of these metallic ...

International Science & Technology Center (ISTC)

Development of Portable Normobaric Hypoxia and Pulsed Magnetic Field Firmware System for Enhancement of Radio- and Non-specific Resistance in Workers of Environmentally Hazardous Industries

International Nuclear Information System (INIS)

... dipole moments magnetic fields monocrystals neutron diffraction order-disorder

Science.gov (United States)

With the increased costs of maintaining boilers and chillers entrepreneurs around the country have offered magnetic and similar devices to facilities as viable alternatives to their maintenance program. This report gives a brief history of some of the pre...

Science.gov (United States)

Magnetic coil pressure wave generation for magnetic forming

Energy Technology Data Exchange (ETDEWEB)

From optical point of view and due to the magnetic interaction of the cold neutrons with the unpaired electron shell, magnetic materials hae a neutron spin-dependent refractive index n[sup +] [spin up] and n[sup -] [spin down]. Magnetic media such as Fe, Co and Ni react like birefringent uniaxial crystals in ordinary optica. n[sup +] and n[sup -] are the equivalent of the ordinary and extraordinary refractive indices. The specular reflection of spin polarized neutrons which is due to the discontinuity of the magnetic induction at the surface of the ferromagnet is a sensitive probe of surface and interface magnetism. We shall first give the background of the art of polarized neutron optics. Secondly, some recent examples from surface and interface magnetism will be given to illustrate the power of this technique such as the magnetic coupling ...

Science.gov (United States)

magnet research at several national laboratories through its Advanced Accelerator Technology Program. The HEP Conductor Development Program, a collaboration among national...

Energy Technology Data Exchange (ETDEWEB)

A study on development of magnetic drive packless valves for commercial purpose showed the results as follows; 1. Study on the radial rays effecting to the permanent magnets -Measurement of the strength of Nd-magnets according to irradiation of radial rays. 2. Effects of temperature on the magnetic driving device -Temperature dependency of the Nd-casting magnets. -Effects of temperature on the heat releasing fins of high-temperature valve. 3. Optimization of torque -Arranging method of permanent magnets -Measuring method and results of torque. 4. Design, manufacture and test for the pressure-resisting structure of magnetic power transmitting device -Calculation and design for the flat circular plates under pressure of the magnetic power transmitting device -Design, manufacture and test for the pressure-resisting ...

Energy Technology Data Exchange (ETDEWEB)

Tests have recently been performed at Fermilab in order to measure the energy losses due to eddy currents and iron and superconductor magnetization. These measurements were performed on six 1.5m long model magnets and eight 15m long full scale collider dipole magnets. AC losses were measured as a function of ramp rate using sawtooth ramps from 500, to 5000 Amps for both types of magnets, while bipolar studies were additionally performed on some of the short magnets. The measured magnet voltage and current for a complete cycle are digitally integrated to yield the energy loss per cycle. Measurement reproducibility is typically 5%, with good agreement between long magnet measurements and extrapolations from short magnet measurement results. Magnetization loss measurements among similar ...

British Library Electronic Table of Contents (United Kingdom)

In the paper, the effect of Ni content, WC grain size and Mo2C addition on WC-6.25wt%TiC-9.3wt%Ni cemented carbide were investigated to improve the properties of Ni-bonded cemented carbides. The results show that the decrease of Ni content will result in the decrease of transverse rupture strength and increase of hardness; with the decrease of WC particle size, hardness increases due to the refinement of WC grains, however, the transverse rupture strength decrease due to the decrease of Ni binder thickness; Mo2C proves to be an effective grain growth inhibitor. With the increase of Mo2C content, the WC grains are refined and the hardness and transverse rupture strength are improved. Generally, when the Ni content is decreased to 8.4wt%, 13.45mm WC is used and 1.2wt% Mo2C is added, a higher...

International Nuclear Information System (INIS)

A study of the influence of the concentration of secondary addition, high concentrations of primary dopant, diffusion enhancer and stabilizer on radiation hardness is presented. It is concluded that the diffusion enhancing technique is the most powerful method for improving radiation hardness. A new polystyrene scintillator which contains 2% pT, 0.02% POPOP, 20% diffusion enhancer and 0.02% stabilizer gave 91% of initial light output immediately after 3 Mrad irradiation in air. Data are presented that show that scintillator prepared from commercial polymer is more radiation-hard and has greater light output than scintillator prepared from monomer. It is assumed that this difference is due to different molecular weight distributions. Some protocols for acceleration of aging (yellowing and crazing) are presented. It is shown that one of the main reasons for aging of plastic scintillators is residual monomer. 10 refs., 18 ...

Energy Technology Data Exchange (ETDEWEB)

Molecular dynamics simulations have been carried out of the radial distribution function of the hard sphere fluid for a range of densities in the equilibrium fluid and just into the metastable region. The first derivative of the hard-sphere radial distribution function at contact was computed and its density dependence fitted to a simple analytic form. Comparisons were made with semi-empirical formulae from the literature, and of these the formula proposed by Tao et al (1992 Phys. Rev. A 46 8007) was found to be in best agreement with the simulation data, although it slightly underestimates the derivative at the higher packing fractions in excess of about 0.45. Close to contact, within a few per cent of the particle diameter, the radial distribution function can be represented well by a second order polynomial. An exponential function, which has some useful analytic features, can also be applied in this region.

International Nuclear Information System (INIS)

The introduction of tolerance to radiation (''radiation-hardness'') into large electronic systems is one of the major tasks to which this Handbook will be put. The practices recommended here for inculcating radiation-tolerance in equipment require advanced physical modeling techniques, precise engineering procedures, and firm assurance procedures. The degree to which these procedures should be used in an equipment project can be measured by the severity of the raw radiation environment, the desired reliability of the system, and the requirement of that project for radiation-sensitive technologies. The balance of device/circuit design versus shielding will depend on whether the radiation is highly penetrating -- as in isotope handling or military environments -- or readily attenuated, as in space. In this chapter the authors have attempted to summarize the essential features of the radiation hardening of large assemblies of equipment and how effective control of ...

International Nuclear Information System (INIS)

Leptonic pair production on nuclei ad EMC-effect are discussed within the frames of the flucton model with scaling distortion. Cumulative production of direct photons and leptonic pairs as a test of the model of hard collisions is considered. The results of calculations of massive leptonic pair production cross sections on nucleus fluctons, caculations of the ratio of deuterium and iron structural functions, cross sections of direct photon production on sup(181)Ta nuclei at Esub(p)=400 GeV and cross section of #pi#-meson production in the model of hard collisions are presented. Experimental discovery of direct cumulative photons is concluded to be important for understanding the mechanism of parton hard scattering from nucleus fluctons.

Science.gov (United States)

PMID:10860471

International Nuclear Information System (INIS)

Three different magnetic regimes; aerial, surface and buried; each with three different forces, have been used to investigate their effects on the water contents and photosynthetic pigments of sweet basil plants (Ocimum basilicum L.). Two groups of sweet basil seeds, Ocimum basilicum L. have been cultivated, one under normal conditions and the second has been subdivided into three portion (aerial, surface and buried) to examine the effect of different magnetic forces coming from the three directions on the resulted plants. At all directions of magnets, water contents have been significantly affected by the magnetic forces. Chlorophyll A and carotene contents have been affected, as well, according to the three magnetic forces coming from soil surface regime only. Chlorophyll B did not significantly affected by differences magnetic forces in the three regimes, but ...

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

UK PubMed Central (United Kingdom)

The effects of a moderate-intensity static magnetic field (SMF) on osteoporosis of the lumbar vertebrae were studied in ovariectomized rats. A small disc magnet (maximum magnetic flux density 180 mT)...Full Text Available

International Nuclear Information System (INIS)

Using the full potential linearized augmented plane wave (FLAPW) method, thickness dependent magnetic anisotropy of ultrathin FeCo alloy films in the range of 1 monolayer (ML) to 5 ML coverage on Pd(0 0 1) surface has been explored. We have found that the FeCo alloy films have close to half metallic state and well-known surface enhancement in thin film magnetism is observed in Fe atom, whereas the Co has rather stable magnetic moment. However, the largest magnetic moment in Fe and Co is found at 1 ML thickness. Interestingly, it has been observed that the interface magnetic moments of Fe and Co are almost the same as those of surface elements. The similar trend exists in orbital magnetic moment. This indicates that the strong hybridization between interface FeCo alloy and Pd gives rise to the large magnetic moment. Theoretically calculated ...

International Nuclear Information System (INIS)

In the present paper the progress of optimization of soft magnetic properties have been studied by applying different experimental techniques (magnetic measurements, electric measurements, X-ray analysis, and high-resolution electron microscopy observation). It has been shown that an increase in magnetic permeability after optimization annealing can be mainly attributed to annealing out of microvoids. (author)

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

Elastodynamic approach to measuring stress-strain relationship of uniaxially stressed wire, and

Science.gov (United States)

Neutron scattering techniques have been used to measure the static structure and magnetic excitations in amorphous magnets. Sum rules and computer models are used to discuss the relationship between the static disorder and the shape of the excitation spectrum. Polarized beam measurements of chi''(Q,E) are compared to analytical theories and computer calculations for the magnetic excitations in amorphous ferromagnets.

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

... crystals and polycrystals. Nevertheless, explosive forming, magnetic forming, etc., are all high-strain-rate processes that ...

Energy Technology Data Exchange (ETDEWEB)

The compound GdPd{sub 2}Si, which is reported to order antiferromagnetically at 13 K, has been investigated by heat capacity and electrical resistivity measurement in the presence of external magnetic fields. In contrast to an earlier report, the zero-field heat capacity and resistivity data indicate two magnetic transitions at 13 and 17 K. The external magnetic field substantially influences the resistivity and heat capacity of the compound around the magnetic ordering temperature. The magnetocaloric effect, which is calculated from in-field heat capacity data, is quite large around the magnetic transition temperature. The magnetoresistance is also large near the magnetic ordering temperature. The metamagnetic transition is observed for 10 kOe magnetic field both in magnetocaloric and in magnetoresistance data. The metamagnetic transition ...

International Nuclear Information System (INIS)

This paper reports that only a few years ago superconducting magnetic separation was viewed as the next major market for superconducting magnets. The first commercial units had been installed, worked flawlessly, and demonstrated real economic viability. The potential market was seen as quite large, and many people believed that superconducting magnetic separation would soon show the same rapid growth that MRI had demonstrated after its initial success. These hopes even prompted IGC, one of the top MRI magnet builders, to form a separate division devoted to magnetic separation. Despite the existence of Magstream, IGC has not been overly active in the market. As a technology that has applications from the clay on the Earth to the soil on the moon, superconducting magnetic separation has yet to become widely used.

Science.gov (United States)

We have analyzed the MHD flow of a conducting couple stress fluid in a slit channel with rhythmically contracting walls. In this analysis we are taking into account the induced magnetic field. Analytical expressions for the stream function, the magnetic force function, the axial pressure gradient, the axial induced magnetic field and the distribution of the current density across the channel are obtained using long wavelength approximation. The results for the pressure rise, the frictional force per wave length, the axial induced magnetic field and distribution of the current density across the channel have been computed numerically and the results were studied for various values of the physical parameters of interest, such as the couple stress parameter ?, the Hartmann number M, the magnetic Reynolds number R and the time averaged mean flow rate ?. Contour plots for the stream and ...

International Nuclear Information System (INIS)

We compare experimental data for temperature dependence of the magnetic order parameter and the magnetic excitations (spin waves) in materials with a quenched orbital moment and a well-defined spin quantum number. It is observed that the thermal decrease of the two quantities proceeds according to the same analytical function of the type y(T)=1-cT"#epsilon# with an identical exponent #epsilon#. This power function applies not only asymptotically for T->0 but holds over a wide temperature range. The exponent #epsilon# is universal, i.e. independent of spin order type and lattice symmetry and depends only on the dimensionality of the relevant interactions and on whether the spin quantum number is integer or half-integer. The different T"#epsilon# functions are identified as representations of stable universality classes. The fact that order parameter and magnetic excitations follow the same T"#epsilon# function shows that ...

Science.gov (United States)

We discuss how magnetic phenomena affect superconductivity in simple metals, transition metals and alloys thereof, and dilute Rare-Earth alloys. It is shown both qualitatively and quantitatively that superconductors are sensitive probes for studying itinerant spin excitations, local spin excitations associated with nearly magnetic impurities, the effect of the atomic environment on the stability of local magnetic moments, and the nature of the spin order in Rare-Earth alloys. Also, we discuss how magnetic impurities can be used to study the electronic configuration which is responsible for superconductivity in Laves-phase crystals like A-15 compounds and ..beta..-W crystals, for example.

International Nuclear Information System (INIS)

It has been carried out the magnetic properties determination for high iron oxide content glasses series obtained from a geothite red mud waste from the zinc hydrometallurgy and dolomite and glass cullet as main raw materials. It has been determined the magnetic susceptibility and magnetization values for the glasses here investigated. The results suggest that the magnetic behaviour are depending on the glass chemical composition, so that glasses can be differently classified like ferrimagnetic, ferromagnetic, superparamagnetic and paramagnetic. (Author) 6 refs.

International Nuclear Information System (INIS)

It is suggested that the magnetic Ap stars can be rotationally decelerated to long periods by the braking action of the associated magnetic field on time scales of order 10"7--10"1"0 years depending on whether the star's dipole field is aligned perpendicular or parallel to the rotation axis. Rotation includes a toroidal magnetic field in the plasma surrounding a star, and the accompanying magnetic stresses produce a net torque acting to despin the star. These results indicate that it is not necessary to postulate mass loss or mass accretion for this purely hydromagnetic braking effect.

Energy Technology Data Exchange (ETDEWEB)

As low temperature cryocoolers become more frequently used to cool superconducting magnets, it becomes increasingly apparent that the connection between the cooler and the magnet has an effect on the design and performance of the magnet. In general, the use of small coolers can be considered in two different temperature ranges; (1) from 3.8 to 4.8 K for magnet fabricated with LTS conductor and (2) from 18 to 35 K for magnets fabricated using HTS conductor. In general, both temperature ranges call for the use of a two-stage cooler. The best method for connecting a cooler to the magnet depends on a number of factors. The factors include: (1) whether the cooler must be used to cool down the magnet from room temperature, (2) whether the magnet must have one or more reservoirs of liquid cryogen to keep the ...

UK PubMed Central (United Kingdom)

A stiff skin forms on surface areas of a flat polydimethylsiloxane (PDMS) upon exposure to focused ion beam (FIB) leading to ordered surface wrinkles. By controlling the FIB fluence and area of exposure...Full Text Available

Science.gov (United States)

These sky images are scanned for point sources above a specified ... The threshold criteria are: a) Gold: >4 sigma in both the Soft AND Hard bands. b) Silver: ... Filtering: Currently, there is no plan for filtering within the GCN based ...

UK PubMed Central (United Kingdom)

ObjectivesPericardial tamponade after cardiac surgery is difficult to diagnose, thereby rendering timing of rethoracotomy hard. We aimed at identifying factors predicting the outcome...Full Text Available

International Nuclear Information System (INIS)

Plasma nitriding in glow discharge is a process of modifying surface properties of a material by which surface hardness, corrosion resistance, fatigue strength etc. of a material can be improved

Science.gov (United States)

This report discusses the following topics on superconductivity: nonlinearities in hard superconductors such as surface impedance of a type II superconductimg half space and harmonic generation and intermodulation due to alternating transport currents; and nonlinearities in superconducting weak links such as harmonic generation by a long Josephson Junction in a superconducting slab.

Energy Technology Data Exchange (ETDEWEB)

Excimer laser processing enables both thermally-driven transformations and the incorporation of solutes into the surface of materials through melting and diffusional mixing. We have examined the effect of excimer laser processing on the microstructure and surface mechanical properties of titanium alloys. Changes in the surface hardness due to laser processing were studied using a Nanoindenter [trademark]. Alloying experiments using both mixing of evaporated surface layers of boron and laser gas alloying in air and in nitrogen all result in changes in the surface hardness of the material. Alloying with boron results in an amorphous surface which is somewhat harder than the as polished surface. Laser processing in air and pure nitrogen results in incorporation of oxygen and nitrogen and the development of fine ([approximately] 50 nm) precipitates of TiO and TiN respectively. Substantial increases in surface hardness result ...

Science.gov (United States)

The October 2000 terrorist attack on the guided-missile destroyer USS Cole (DDG 67) in the port of Aden, Yemen, is commonly viewed in the larger context of al-Qa'ida's September 11th campaign. Beyond the initial official investigations, the military force...

Energy Technology Data Exchange (ETDEWEB)

An ex-employee's claims that inadequate enforcement of radiation safety regulations allowed excess radiation exposure thereby causing his deteriorating health was not substantiated by a thorough investigation.

UK PubMed Central (United Kingdom)

BackgroundA goal of human genetics is to discover genetic factors that influence individuals' susceptibility to common diseases. Most common diseases are thought to result from the...Full Text Available

International Nuclear Information System (INIS)

68 replaced carbon steel piping in secondary system of pressurized water reactor (PWR) has been investigated by visual examination for checking thinning conditions. It is well known that the flow-accelerated corrosion (FAC) was inhibited by traces of Cr in steel. Therefore, the chemical compositions of those steels have been measured. In addition, the micro structure and hardness of those steels have been investigated. And the relationship between those material variables and FAC rate was considered. As the results, (1) The Cr contents in those steels were below 0.1 wt% except one sample. Minute quantities of chromium increase the resistance against FAC. But the water velocity was thought to be the dominant factor rather than chemical composition in steel, at least such as below 0.1%Cr. (2) Hardness of all piping has been satisfied the specifications of each materials. The hardness of steels was not correlated with wall ...

UK PubMed Central (United Kingdom)

The adhesive proteins secreted by marine mussels form a natural glue that cures rapidly to form strong and durable bonds in aqueous environments. These mussel adhesive proteins contain an unusual...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The advent of light metal alloys and advanced materials (polymer, composites, etc.) have brought the possibility of achieving important energy reductions into the full life cycle of these materials, especially in transportation applications. 1 These materials have gained acceptance in the aerospace industry but use of light metal alloys needs to gain wider acceptance in other commercial transportation areas. Among the main reasons for the relatively low use of these materials are the lack of manufacturability, insufficient mechanical properties, and increased material costs due to processing inefficiencies. Considering the enormous potential energy savings associated with the use of light metal alloys and advanced materials in transportation, there is a need to identify R&D opportunities in the fields of materials fabrication and forming aimed at developing materials with high specific mechanical properties combined with energy efficient processes and good manufacturability. ...

Energy Technology Data Exchange (ETDEWEB)

Laser surface alloying with gaseous nitrogen was utilized to improve the wear resistance of a Ti-6Al-4V alloy. Wear-resistant composite coatings reinforced by hard TiN dendrites were produced 'in-situ' on a substrate of a Ti-6Al-4V alloy. The hardness and wear resistance of the laser alloyed coating under two-body abrasive and block-on-ring full-sliding wear conditions were significantly enhanced. (orig.)

Energy Technology Data Exchange (ETDEWEB)

A flow field and particle trajectory in a HDD (Hard Disk Drive) between two rotating disks in axisymmetric enclosures is investigated using CFD code FLUENT/UNS. The RNG k-{epsilon} model is used as a turbulent model. In this study, the flow field between two disks are symmetric, and the flow field near the enclosure is very complex. Cross stream vectors are shown both for blowing and no blowing from the hub. The larger a particle, the more fast the particle deposits at the walls. In the case of blowing from the hub, the more fast the particle deposits at the walls. (author). 9 refs., 12 figs., 1 tab.

International Nuclear Information System (INIS)

Wood-plastic combination (WPC) was produced by #gamma#-irradiation of persimmon impregnated with acrylonitrile and styrene. The hardness and strength of WPC obtained were higher than those of an unmodified wood. Thus, it was found that the WPC is suited for a head of golf club, because the Shore hardness value of WPC is 36% greater than that of unmodified wood. An impregnation method of monomers with some pigments could produce colored WPC without diminishing natural grain. Head of golf club could be manufactured from colored WPC in practice. (auhtor).

International Nuclear Information System (INIS)

Glow discharge plasma nitriding of AISI 304 austenitic stainless steel has been carried out for different processing time under optimum discharge conditions established by spectroscopic analysis. The treated samples were analysed by X-ray diffraction (XRD) to explore the changes induced in the crystallographic structure. The XRD pattern confirmed the formation of an expanded austenite phase (#gamma#_N) owing to incorporation of nitrogen as an interstitial solid solution in the iron lattice. A Vickers microhardness tester was used to evaluate the surface hardness as a function of indentation depth (#mu#m). The results showed clear evidence of surface changes with substantial increase in surface hardness.

International Nuclear Information System (INIS)

The distributions of the effective numbers of 6q-fluctons in the energy, momentum and distance to the center of mass of nucleus are studied. Many characteristics of these distributions are shown to be universal, i.e. independent of the flucton size. The saturation of the flucton density in A > 80 nuclei and other peculiarities are found, which define different behavior of the effective numbers of fluctons and deuterons. This fact provides an explanation of the known underestimate by a factor of 1.5-6 of the cross sections of hard inclusive (p, p'd) process on nuclei calculated in the quasi-elastic approximation.

Energy Technology Data Exchange (ETDEWEB)

The efficiency of NbC on WC grain coarsening in a WC-10wt.%Co hardmetal alloy was demonstrated by hardness measurement and WC granulation observation. The heterogeneous and overall grain growth were controlled. A low temperature experimentally produced NbC was used and compared to the inhibition potential of a commercial NbC powder. The results were the same in terms of structural fineness and hardness. The dispersion of the experimental NbC was not a problem, in spite of its size. The experimental NbC has very large particles, formed by agglomerates of small crystallites. During milling these agglomerates could be broken down. (orig.)

International Nuclear Information System (INIS)

The effect of severe plastic deformation by cold high pressure torsion (HPT) on radio frequency (RF) plasma nitriding of pure iron, as well as St2K50 and X5CrNi1810 steels was investigated. Nitriding was carried out for 3 h in a nitrogen atmosphere at a pressure of 10"-"5 bar and temperatures of 350 and 400 deg. C. Nitrided specimens were analysed by scanning electron microscopy (SEM), X-ray diffraction and micro hardness measurements. It was found that HPT enhances the effect of nitriding leading almost to doubling of the thickness of the nitrided layer for pure iron and the high alloyed steel. The largest increase in hardness was observed when HPT was combined with RF plasma nitriding at 350 deg. C. In the case of pure iron, the X-ray diffraction spectra showed the formation of #epsilon# and #gamma#' nitrides in the compound layer, with a preferential formation of #gamma#' at the expense of the #alpha#-phase at the higher nitriding ...

Energy Technology Data Exchange (ETDEWEB)

The magnetic separation technology using sub-microsized ferromagnetic particle is indispensable in many areas of medical biosciences. For example, ferromagnetic particles (200-500 nm) are widely used for cell sorting in stem cell research with the use of cell surface-specific antigens. Nanosized ferromagnetic particles (10-20 nm) have been suggested as more suitable in drug delivery studies given their efficiency of tissue penetration, however, the magnetic separation method for them has not been established. One of the major reasons is that magnetic force acting on the object particles decreases drastically as a particle diameter becomes small. In this study, magnetic force acting on the targets was enhanced by the combination of superconducting magnet and the filter consisting of ferromagnetic particle. By doing so, we confirmed that Fe{sub 3}O{sub 4} of 20 nm in diameter was ...

International Nuclear Information System (INIS)

With "1"5"1Eu-Moessbauer spectroscopy and other methods the complex magnetic properties of Eu_2PdSi_3, arising from the two crystallographically different lattice sites of the Eu"2"+ ions, have been already studied. Here we study the impact of magnetic dilution of the magnetic Eu"2"+ sites by non-magnetic Y"3"+ ions. A previous specific heat study has found reduced magnetic ordering temperatures with strong indication of disorder effects like in magnetic spin glasses. Here we provide from "1"5"1Eu-Moessbauer spectroscopy detailed information of the impact of Y"3"+ substitution on the magnetic properties of the two lattice sites, well distinguishable in the "1"5"1Eu-spectra. Since the substitution of the larger Eu"2"+ ions by the smaller Y"3"+ ions is connected with a lattice contraction, we also applied high pressure to the Eu_2PdSi_3 sample ...

Energy Technology Data Exchange (ETDEWEB)

The electrical resistivity, Hall effect, and magnetic susceptibility of single-crystal UPd[sub 2]Si[sub 2] have been studied between 4.2 and 300 K. A large anisotropy was observed in both the magnetic and transport properties. There is a quadratic temperature dependence of the resistivity for a range of temperatures between 4.2 and 80 K. At higher temperatures, the resistivity indicates a Kondo-type behavior. The behavior of these quantities is accounted for by the magnetic phase transitions at 108 and 136 K reported from neutron-scattering studies. At high temperatures, the magnetic susceptibility of UPd[sub 2]Si[sub 2] is Curie-Wiess-like along the [ital c] axis. The temperature dependence of the Hall coefficient above 108 K is accounted for by a theoretical model invoking skew scattering of conduction electrons by localized magnetic moments.

CERN Document Server

We report on the magnetic hyperthermia properties of chemically synthesized ferromagnetic 11 and 16 nm Fe(0) nanoparticles of cubic shape displaying the saturation magnetization of bulk iron. The specific absorption rate measured on 16 nm nanocubes is 1690+-160 W/g at 300 kHz and 66 mT. This corresponds to specific losses-per-cycle of 5.6 mJ/g, largely exceeding the ones reported in other systems. A way to quantify the degree of optimization of any system with respect to hyperthermia applications is proposed. Applied here, this method shows that our nanoparticles are not fully optimized, probably due to the strong influence of magnetic interactions on their magnetic response. Once protected from oxidation and further optimized, such nano-objects could constitute efficient magnetic cores for biomedical applications requiring very large heating power.

Science.gov (United States)

Sensitive and quick-response nonlinear inductance characteristics are found for high Tc superconducting (YBa/sub 2/Cu/sub 3/O/sub 7-chi/) disk cores at 77K in which soft magnetic BH hysteresis loops are observed. Various quick response magnetic devices such as modulators, amplifiers and sensors are built using these cores. The magnetizing frequency can be set to more than 20 MHz, which is difficult for conventional ferromagnetic bulk materials such as Permalloy amorphous alloys and ferrite. New quick-response fluxgate type magnetic-field sensors are made using ac and dc voltage sources. The former is used for second-harmonic type sensors, while the latter is for voltage-output multivibrator type sensors. Stable and quick-response sensor characteristics were obtained for two-core type multivibrators.

British Library Electronic Table of Contents (United Kingdom)

We investigated the magnet field dependence of the X-ray pulse height and the critical current of a Ti/Au bilayer TES micro-calorimeter. The pulse height was strongly affected by the magnetic field intensity applied perpendicularly to the TES surface. We found that the critical current at zero temperature, I c0, decreased by a factor of two by applying a magnet field of ?10??T. Our data are consistent with a TES sensitivity proportional to (I/I c0)?2/3, as predicted by the Ginzburg-Landau theory. This fact implies that the shape of the R?T curve of the TES is partly determined by the critical current of the superconductor. In order to make our TES microcalorimeters less sensitive to the external magnetic field, we fabricated devices equipped with on-chip magnetic shielding. One device has ...

International Nuclear Information System (INIS)

Effect of low-frequency pulsating magnetic field on the microstructure and magnetic properties of amorphous alloy Fe_7_8Si_9B_1_3 were investigated. The temperature rise induced by the treatment was measured by a non-contact infrared thermometer. The crystallization behavior and microstructure of specimens were studied by Moessbauer spectroscopy and transmission electron microscope (TEM). Magnetic properties of the specimens were investigated by alternating gradient magnetometer (AGM). The results show that the low-frequency pulsating magnetic field can promote the single-phase crystallization of amorphous alloy Fe_7_8Si_9B_1_3. The frequency, f of applied field is from 10 to 40 Hz, magnetic field, H is from 0.02 to 0.04 T and treatment duration, t is from 180-300 s. The volume fraction of crystallization phase (#alpha#-Fe(Si), the grain size, 2-10 nm) is 3-7%. The temperature rise ...

Energy Technology Data Exchange (ETDEWEB)

The investigated hybrid nanocomposite consists of a porous silicon template with electrochemically embedded Ni or Co nanostructures and offers magnetic characteristics which can be tailored by the electrochemical process parameters during fabrication. A twofold magnetic behaviour can be observed, a first one due to the spinmagnetism at magnetic fields below the saturation magnetization of the deposited metals and a second non-saturating term at higher fields (>1 T up to 7 T) above the saturation magnetization. In case of Ni deposited within the pores this non-saturating term shows a paramagnetic characteristic and follows exactly the Curie-Weiss law, whereas for Co/porous silicon samples the temperature dependent magnetization shows some deviations from the Curie Weiss law. In this high field region a difference in the temperature dependence between Ni ...

Science.gov (United States)

A new type of radiation which occurs when particles are accelerated in the field of a longitudinal wave and in a transverse magnetic field is studied. The characteristics of such spontaneous radiation are obtained, and the influence of collective effects on the radiation is analyzed. The application of the findings to the theory of free electron lasers is discussed. 8 references.

UK PubMed Central (United Kingdom)

The magnetic susceptibility and the density of human oxy-(HbO₂) and carbonmonoxyhemoglobin (HbCO) solutions of various concentrations have been measured at room temperature, with pure water...Full Text Available

Science.gov (United States)

Electro-Magnet. Antenna Panels Types Simulated Hail Stone Damage A.Panel ...... X-Band Klystron Electro Magnet. 11. I I. 333-6104 AcBc. 333-6105 Color ...

International Nuclear Information System (INIS)

The magnetic properties of as-grown Ga1-xMnxAs have been investigated by the systematic temperature and magnetic field dependent soft x-ray magnetic circular dichroism (XMCD) measurements in the Mn L2,3 absorption edge region. The XMCD intensity at high temperatures obeys the Curie-Weiss law, but residual spin magnetic moment appears already around 100 K, significantly above Curie temperature (Tc), suggesting that short-range ferromagnetic correlations are developed significantly above Tc. The high-field magnetic susceptibility becomes T-independent below TC, indicating that the AF interaction between the substitutional Mn (Mnsub and interstitial Mn (Mnint) ions, which becomes strong as the Mn concentration x increases, exists and that the amount of the Mnint affects Tc. The present experimental findings should give valuable insight into the inhomogeneous ...

Energy Technology Data Exchange (ETDEWEB)

A considerable amount of chemical knowledge of marine sediments has been acquired in recent years but has not yet been utilized by paleomagnetists. On the other hand, geochemists are often unaware of the usefulness of numerous magnetic techniques. In this review we try to bridge this gap, and in particular, we outline many of the chemical and magnetic principles that should allow paleomagnetists to better identify and undertand chemical changes that affect the magnetic properties of marine sediments. The chemical principles include those for distinguishing the four major sources of sediments (continental, biological, authigenic/hydrogenous, volcanic/hydrothermal) from one another by determining elemental abundance distributions, as well as for investigating the stabilities of mineral phases relative to changes in pE and pH. The magnetic principles include the effects of authigenesis and diagenesis on ...

UK PubMed Central (United Kingdom)

Major breakthroughs have recently been reported that can help overcome two inherent drawbacks of NMR: the lack of sensitivity and the limited memory of longitudinal magnetization. Dynamic nuclear polarization...Full Text Available

UK PubMed Central (United Kingdom)

OBJECTIVES: To appraise epidemiological evidence of the purported association between residential exposure to power frequency magnetic fields and adult cancers. METHODS: Literature review and epidemiological...Full Text Available

UK PubMed Central (United Kingdom)

Naturally occurring and contaminant ferromagnetic and ferrimagnetic particles have been found within or near cells, and might allow pulsed magnetic fields to create transient cell membrane opening ("pores")....Full Text Available

International Nuclear Information System (INIS)

Bone metastases of an Ewing's sarcoma were detected by magnetic resonance imaging (MRI), when bone scan, CT and plain films were still normal. This is due to the ability of MRI to detect intramedullary metastases before involvement of the cortex. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

The magnetically controlled plasma opening switch (MCPOS) is an advanced plasma opening switch that utilizes magnetic fields to improve operation. Magnetic fields always dominate terawatt, pulsed power plasma opening switches. For that reason, the MCPOS uses controlled applied magnetic fields with magnitude comparable to the self-magnetic field of the storage inductor. One applied field holds the plasma in place while energy accumulates in the storage inductor, then another applied field pushes the plasma away from the cathode to allow energy to flow downstream. Over a ten month period, an MCPOS was designed, built, and tested on DECADE Module 2 at Physics International. The peak drive current was 1.8 MA in 250 ns. The output parameters were up to 1 MA into an electron beam load. The radiation temporal pulse width averaged 60 nanoseconds full-width at half-maximum. The peak load ...

UK PubMed Central (United Kingdom)

OBJECTIVES--This case cohort study examines whether there is an association between exposure to electric and magnetic fields and suicide in a population of 21,744 male electrical utility workers from...Full Text Available

International Nuclear Information System (INIS)

A variable-dispersion electron spectrometer is being installed for use by the Stanford Superconducting Accelerator in conjunction with its Free Electron Laser program. The system has been designed to operate with electron beam energies from 20 MeV to 200 MeV, with a maximum energy resolution of 0.01% FWHM. The maximum energy acceptance is approximately #+-# 5%, as determined by the bending magnet aperture. Resolution is controlled by adjusting the focal conditions at the entrance to a 90 degree bending magnet, while the dispersion is controlled by changing the magnitude and polarity of the field in a quadrupole magnet which immediately follows the bending magnet. 4 refs., 5 figs.

International Nuclear Information System (INIS)

... Union (INTAS), Brussels (Belgium) Science and Technology Center in Unkraine,

Science.gov (United States)

... The Effect of the Temperature to Which the Material is Heated on the Process of Formation of Intermetallic Compounds in Magnetic Pulse Welding,. ...

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

... electron reactions electrons excitation inelastic scattering m1-transitions proton

International Nuclear Information System (INIS)

The read/write characteristics for perpendicular magnetic recording media of focused-ion-beam (FIB)-etched recording heads were investigated. It was found that the trailing edge of an FIB-etched head produces a higher gradient in the magnetic field perpendicular to the medium than a head which has not been etched. The signal-to-noise ratio of the medium increased with the FIB-etched write gap. A high-Bs and thin pole increased the magnetic field's gradient in the perpendicular direction, resulting in excellent read/write characteristics.

International Nuclear Information System (INIS)

... excited states iridium 187 isomeric nuclei magnetic fields nuclear electric

Energy Technology Data Exchange (ETDEWEB)

XVTa and XXTa nuclei were oriented at low temperature as dilute impurities in Fe. The magnetic hyperfine splitting frequencies = B sub(HF)/Ih of the XVTa and XXTa ground states have been measured to be 320.45(11) and 317.552(55) MHz by using the technique of NMR-ON. Taking the known hyperfine field of Y Ta in Fe, the magnetic moments have been deduced: ( XVTa, 7/2 ) =2.270(45) and ( XXTa, 7/2 ) =2.250(45) sub(N). These values of the magnetic moments are discussed in the framework of the rotational model.

British Library Electronic Table of Contents (United Kingdom)

A method to achieve NMR of dilute samples in the earth's magnetic field by applying para-hydrogen induced polarization is presented. Maximum achievable polarization enhancements were calculated by numerically simulating the experiment and compared to the experimental results and to the thermal equilibrium in the earth's magnetic field. Simultaneous 19F and 1H NMR detection on a sub-milliliter sample of a fluorinated alkyne at millimolar concentration (1018 nuclear spins) was realized with just one single scan. A highly resolved spectrum with a signal/noise ratio higher than 50:1 was obtained without using an auxiliary magnet or any form of radio frequency shielding.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

International Nuclear Information System (INIS)

(Feb 1977). Japan Syamal, A. Bombay Univ. (India). Univ. Dept. of Chemical

International Nuclear Information System (INIS)

The combined magnetic braking-ambipolar diffusion problem in weakly ionized, rigidly rotating disks is studied. An analytical solution is presented for a disk whose angular velocity and magnetic yield vectors are aligned with the symmetry axis, illustrating the effects of the relative azimuthal drift of neutrals and ions. The effects of radial drift are added, commenting on the ratio of the characteristic ambipolar diffusion and magnetic braking time scales in high-mass and low-mass disks. A numerical calculation is used to show the combined action of these two processes. 31 references.

British Library Electronic Table of Contents (United Kingdom)

The effect of elastic and plastic strains on the magnetic properties of ferrite-pearlite steels has been studied. It has been shown that the sensitivity to elastic-tensile and bending strains is four to five times greater for remnant magnetization than for coercive force. In order to determine the degree of cold plastic deformation of high-carbon steels, a two-parametric testing technique based on the use of remnant magnetization and coercive force was suggested. An MMT-2 device was recommended for measurement of the required parameters.

Science.gov (United States)

PMID:9226309

Science.gov (United States)

Not Available

International Nuclear Information System (INIS)

2010 [1 p.] Germany Repp, Felix El-Miladi, Nouri Hoehl, Christian Jahanbakhsh,

International Nuclear Information System (INIS)

... spin-lattice relaxation angular momentum electronic circuits magnetic

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

... Report Date : JUL 1961. Pagination or Media Count : 39. Abstract : Open-ende Terms: Electrohydraulic forming, Magnetic forming. ...

Science.gov (United States)

... Casting Explosive forming Forging Electrohydraulic forming Extruding Magnetic forming Rolling Electroforming Drawing Powdered metal forming ...

Energy Technology Data Exchange (ETDEWEB)

The results of the investigations show that magnetic treatment is a quite practical and effective method of intensifying certain technological processes in the coking industry. Magnetic treatment was utilized for improving the production of ammonium sulfate, refining of the naphthalene fraction, removal of sludge from wash oil in the benzol division, and the treatment of tar before fractionation. 2 references, 3 tables.