Energy Technology Data Exchange (ETDEWEB)

Recent developments on plastic forming technology of magnesium alloys are presented. Attempts have been undergoing with an aim at forming magnesium alloy parts at lower temperatures. It is believed that fine microstructure magnesium alloys usually have much higher plasticity at lower temperatures and even room temperatures. Extrusion is a method to form magnesium profile products and tube products, which is also one of the effective ways to make fine microstructure magnesium alloys. Superplasticity forming is another method to form high plasticity magnesium alloys. Hot forming of magnesium sheet parts is an important process to form magnesium products. Some developments related to above issues are discussed in the ...

British Library Electronic Table of Contents (United Kingdom)

Despite advances in polymer and drug technology, the underlying stent platform remains a key determinant of clinical outcome. A clear understanding of stent design and the differences between various stent platforms are of increasing importance for the interventional cardiologist. Reduction in stent strut thickness has been associated with improved stent deliverability, improved procedural outcome, and lower rates of subsequent restenosis. Newer-generation 316L-SS stent designs have enabled reduced strut thickness while retaining radial strength and minimizing recoil, but with significant loss of radiopacity, leading to reduced visibility. Cobalt chromium alloys have enabled a reduction in stent strut thickness to around 80?90 mm while retaining modest radiopacity, but due to higher elasti...

Energy Technology Data Exchange (ETDEWEB)

Gas and plasma nitriding processes were executed in the magnesium with modification by titanium in search for an effective surface treatment method for magnesium alloys. Magnesium-nitrogen system has completely no solid solution or solubility, so that nitride should be only formed by eutectic reaction in the liquid phase. Hence, magnesium is difficult or nearly impossible to have its surface modified by nitriding. Addition of nitride forming element into magnesium enables us to lower the onset temperature of nitriding. Magnesium-titanium alloys with 1 to 5 wt% are yielded by the bulk mechanical alloying and, subjected to gas nitriding for various process conditions. Successful co-formation of Mg{sub 3}N{sub 2} as well as TiN becomes a proof to demonstrate the possibility of gas/plasma nitriding in ...

Energy Technology Data Exchange (ETDEWEB)

Plastic formability of cast magnesium alloy that were hot rolled after roll strip casting was investigated to ascertain the feasibility of semi-solid strip casting process of AZ31B magnesium alloy. Hot rolling and heat treatment conditions were changed to examine which conditions were appropriate for producing AZ31B wrought magnesium alloys after strip casting process. Microscopic observation of the crystals of the manufactured wrought magnesium alloys was performed. It has been found that a limiting drawing ratio of 2.7 was possible in a warm deep drawing test of the cast magnesium alloy sheets after being hot rolled. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The aim of this study was to qualitatively and quantitatively study MR artifacts of various stents on the basis of in vitro experiments. We were particularly interested whether sequence type and orientation of the stent with respect to the static magnetic field influences the artifact. We examined 18 stents of different material (nitinol, stainless steel, cobalt alloy), different design of the stent meshes (AccuLink, OmniLink, DynaLink, Xact, Protoge, Wallstent Monorail), different diameter (5-10 mm) and different length (18-58 mm) with a turbo spin echo (TSE), a 2D-fast low angle shot (FLASH) and a 3D-FLASH sequence. The MR images were examined qualitatively with respect to possible artifacts. Furthermore we examined the MR data quantitatively: The contrast-noise-ratio (CNR) was determined both within the stent and outside (within the tube); based on these ...

Energy Technology Data Exchange (ETDEWEB)

Magnesium alloys are being increasingly utilized in a variety of fields as an alternative material to organic materials and aluminum alloys, owing to excellent properties. Those include low density, and excellent damping properties. When compared to organic materials, furthermore, Mg alloy excels at recyclability, heat radiation, and electromagnetic-shielding. Though most of magnesium alloy products are manufactured through die-casting and thixo-molding at present, the demand for the expanding of magnesium wrought alloy market is increasing. Taking full advantage of a drawing technique and applying it to the conventional extruded pipe, we have developed a new type of magnesium alloy pipe. The strength of the developed pipe is significantly higher than that of the conventional ...

Science.gov (United States)

... alloys--Lanthanum-- Magnesium--Magnasium &11oy8--Hagn*31Uft compounds--Manxganese--Manganes. alloys-- Mercury ...

International Nuclear Information System (INIS)

An experimental approach has been performed to ascertain the effectiveness of semi-solid strip casting using a horizontal twin roll caster. The demand for light-weight products with high strength has grown recently due to the rapid development of automobile and aircraft technology. One key to such development has been utilization of magnesium alloys, which can potentially reduce the total product weight. However, the problems of utilizing magnesium alloys are still mainly related to high manufacturing cost. One of the solutions to this problem is to develop magnesium casting-rolling technology in order to produce magnesium sheet products at competitive cost for commercial applications. In this experiment, magnesium alloy AZ31B was used to ascertain the effectiveness of semi-solid roll strip casting for producing ...

International Nuclear Information System (INIS)

The development of light-weight vehicle is in great demand for enhancement of fuel efficiency and dynamic performance. The vehicle weight can be reduced effectively by using lightweight materials such as magnesium alloys. However, the use of magnesium alloys in sheet forming processes is still limited because of their low formability at room temperature and the lack of understanding of the forming process of magnesium alloys at elevated temperatures. In this study, uniaxial tensile tests of the magnesium alloy AZ31B-O at various temperatures were performed to evaluate the mechanical properties of this alloy relevant for forming of magnesium sheets. To construct a FLD (forming limit diagram), a forming limit test were conducted at temperature of 100 and 200 deg. C. For the ...

Energy Technology Data Exchange (ETDEWEB)

Magnesium cast parts as well as indirectly and hydrostatically extruded profiles were used in order to investigate the influence of different microstructures on the damping behaviour of magnesium AZ-alloys. Especially, hydrostatic extrusion leads to a significant grain refinement in the extruded profile compared to indirect extrusion. Strain dependent damping measurements were carried out at room temperature using alloys AZ31, AZ61 and AZ80. Damping was determined as the logarithmic decrement of free bending beam vibrations. The results of these measurements after indirect and hydrostatic extrusion are shown and discussed. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The effects of carbon inoculation by C{sub 2}Cl{sub 6} addition were investigated using commercial AZ31 magnesium alloy. The additions of C{sub 2}Cl{sub 6} to AZ31 magnesium alloy significantly reduce the grain size from 280 {mu}m to about 120 {mu}m and the tensile properties are also increased due to grain refinement. EPMA analysis shows that Al-C-O compounds are formed in the castings which are considered to function as nucleants. (orig.)

Energy Technology Data Exchange (ETDEWEB)

A new technique has been developed for improving corrosion resistance on magnesium alloys. Specimens of AZ31 magnesium alloy were dipped into molten salt of NaBF{sub 4} at 723 K for various times, and then cooled, rinsed with water, and dried in air. Corrosion resistance in the surface treated specimens was evaluated by salt immersion test using 1% NaCl solution as a time for occurring filiform corrosion. On an un-treated AZ31 alloy, the time for starting the filiform corrosion was about 1.2 ks, while on the surface treated specimen, the time was prolonged into about 1300 ks. Moreover, the surface treated specimen showed corrosion resistance in low pH solutions, such as 1% HNO{sub 3} and HCl solutions. (orig.)

Energy Technology Data Exchange (ETDEWEB)

In this paper, for an acceleration of utilization of magnesium alloy which is being interested in recent years, friction welding of AZ31 magnesium alloy was carried out, and the joint performance was discussed in relation to the deformation heat input in the upset stage and upset loss as a evaluation factor. Where, the deformation heat input in the upset stage is mechanical work represented by the product of upset speed and axial pressure. As a result, it was made clear that the friction welding of AZ31 magnesium alloy was easy in the atmosphere, and good welded joints without a non- adhesion area at the weld interface could de obtained. Moreover, the evaluation factors discussed were possible to evaluate to joint performance. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The purpose of this study was to test a large sample of different coronary artery stents using four image reconstruction approaches with respect to lumen visualization, lumen attenuation, and image noise in 64-slice multidetector-row computed tomography (MDCT) in vitro and to provide a catalogue of currently used coronary artery stents when imaged with state-of the-art MDCT. We examined 68 different coronary artery stents (57 stainless steel, four cobalt-chromium, one cobalt-alloy, two nitinol, four tantalum) in a coronary artery phantom (vessel diameter 3 mm, intravascular attenuation 250 HU, extravascular density -70). Stents were imaged in axial orientation with standard parameters: 32x0.6 collimation, pitch 0.24, 680 mAs, 120 kV, rotation time 0.37 s. Four different image reconstructions were obtained with varying convolution kernels and section thicknesses: (1) soft, 0.6 mm, ...

Energy Technology Data Exchange (ETDEWEB)

To improve the surface properties of magnesium alloy, a lining process using shot peening was carried out. The lining of magnesium alloy with metals such as titanium and nickel is useful in heightening the corrosion and wear properties for the components. In the shot peening experiment, the foil set on the magnesium workpiece is pelted with many shots at a high velocity. The foil is bonded to the surface of the workpiece due to plastic deformation induced by the collision of the shots. A pure aluminum foil is inserted between the hard foil and magnesium workpiece to assist the bonding. To heighten the bondability, the foil and workpiece are heated and the flow stresses of the metals are reduced. In this experiment, a centrifugal shot peening machine with an electrical heater was employed. The workpieces were commercially magnesium ...

Energy Technology Data Exchange (ETDEWEB)

In order to investigate the extrusion characteristics of magnesium alloy (AZ31), a computer simulation was attempted. Tensile properties of as-cast billet with different strain rates were incorporated into the simulation. The results showed a great change in distribution of stress and strain at near die region by the ram travel. It was found that the average grain size at longitudinal edge of the extruded sheet was smaller than that at center region, which might be attributed to recrystallization caused by severe plastic deformation. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Materials and processing designs for advanced magnesium alloys with fine microstructures and superior properties were established by the combination of the repeated plastic working and the Mg{sub 2}Si synthesis in solid-state. The grain size was less than 1 {mu}m via RPW process due to its severe plastic working on raw powder. The hot extruded magnesium alloys produced in industries showed high ultimate tensile strength, e.g. 420{proportional_to}450 MPa, when employing Mg-Zn-Al-Ca-RE (Rare Earth) alloy coarse powder, having 0.5{proportional_to}2 mm diameter, as input materials. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Although magnesium is not attacked by hydrocarbons, it reacts vigorously with anhydrous methanol, raising concerns about the compatibility of the metal with methanol blend fuels. This paper describes the behavior of magnesium alloys in laboratory tests in static contact with methanol-containing fuels at 110/sup 0/F. Water in small concentrations (above 0.25% by weight of the methanol content) is shown to prevent the destructive attack of magnesium by these fuels. The required water content is well within the water tolerance of methanol-GTBA (gasoline grade tertiary-butyl alcohol) cosolvent fuel blends. Die cast AZ91HP shows greater resistance to methanol reaction than does AZ31B sheet.

Energy Technology Data Exchange (ETDEWEB)

Optimum conditions for microstructural control in industrial hot working of cast and homogenized AZ31 magnesium alloys are evaluated by using a processing map. The recommended window for bulk metal working of this alloy is the domain in the temperature range 300-450 C and strain rate range 1-10 s{sup -1}, and the optimum processing parameters are 400 C and 10 s{sup -1}, where grain-boundary self diffusion is the rate-controlling mechanism. (Abstract Copyright [2009], Wiley Periodicals, Inc.)

Science.gov (United States)

A number of alloys of zirconium have been investigated as part of a program aimed at improving the high-temperature tensile and creep strength of zirconium. These alloys include aluminum, beryllium, lead, magnesium, molybdenum, niobium, tantalum, tin, titanium, tungsten, vanadium, and zinc, binary and ternary alloys. The data indicate that aluminum, lead, molybdenum niobium, tin, titanium, tungsten, and vanadium can be used successfully to harden zirconium, and that aluminum, tin, titanium, and vanadium are particularly effective in maintaining the strength of zirconium at elevated temperatures.

Energy Technology Data Exchange (ETDEWEB)

We conduct the static and dynamic loading fracture experiments on magnesium alloy (AZ31B) under the equitable and inequitable biaxial stress. We process specimens as cross type with cracks. There are different kinds of cracks defined by their crack angles. By using a hydraulic high-speed biaxial experiment machine, we put the equitable and inequitable stresses on the specimen. We analyze results using the caustic method. The experiments reveal a few important results. There is negative correlation between the fracture toughness value and the plate thickness in the magnesium alloy sheet specimen. The fracture toughness value decrease in the case the crack has the angle different from the loading direction. The fracture toughness value decreases significantly under the inequitable biaxial stress. (orig.)

Energy Technology Data Exchange (ETDEWEB)

A new technique was proposed in order to improve poor corrosion resistance in magnesium. That is, magnesium hydroxide film was formed on the surface of 3 N-Mg by artificial corrosion in 1% MgCl{sub 2} solution for 3.6 ks, which followed by oxidation at 673 K for 3.6 ks in air. Corrosion resistance was evaluated by salt immersion tests in 1% NaCl solution under in situ laser microscopic observations. Bubble evolution, which occurred immediately at the beginning of the immersion test in the case of non-treated specimen, was suppressed by the process. And also, formation of filiform corrosion was suppressed for about 3.6 ks, which occurred at 180 s in the non-treated specimen. (orig.)

Science.gov (United States)

The biocompatibility and corrosion resistance of various materials for use as sacrificial anodes in in vivo hybrid fuel cells were studied. Aluminium, zinc, and magnesium alloy AZ31B were studied, and the results are discussed.

International Nuclear Information System (INIS)

Chemical and phase homogeneity of titanium-niobium sponge, produced by a combined magnesium-thermic reduction of niobium pentachloride and titanium tetrachloride mixtures, is investigated. It is ascertained that a sponge consists of spherical shape particles and has a large number of pores. Particle sizes are reduced with niobium being substituted for titanium from 50-500 #mu#m for titanium sponge to 1-40 #mu#m for niobium one, which testifies to the bormation in a titanium-niobium sponge of an alloy and not a mechanical mixture. A number of solid solutions is detected by X-ray phase analysis. Lattice parameters are determined.

Energy Technology Data Exchange (ETDEWEB)

Magnesium is known to have poor formability at room temperature, mainly attributed to its hexagonal lattice structure. This paper presents the findings generated from development of warm forming to produce thin-walled magnesium components. Finite element analysis was conducted to evaluate the formability of the material and the simulated results were compared to the tensile results and product formability. Tensile tests were used to verify the formability of the sheet metal at difference temperatures. The process parameters considered in the feasibility study were forming temperature, in the range of 28 C to 300 C and magnesium sheet (AZ31B-H24) thickness, in the range of 0.4 mm to 1 mm. Magnesium hand phone covers of a thickness down to 0.4 mm have been successfully produced. The feasible forming temperature was found to be between 200 C and 250 C. Metallographic examination shows evident of ...

Energy Technology Data Exchange (ETDEWEB)

Purpose: To evaluated artifacts of unexpended stents and to determine their exact position for MR-guided percutaneous transluminal angioplasty using real-time sequences. Materials and Methods: By using an in vitro model, 11 unexpended stents - 9 nitinol, 1 stainless steel, and 1 cobalt alloy - were investigated by MR. Each stent was studied in a vessel-phantom filled with saline solution. Imaging was performed using five different realtime sequences: fast low angle shot (Flash 2D), fast imaging with steady precession (true FISP, FISP, interactive true FISP) and segmented echo planar imaging (seg. EPI). Artifacts of the introducer system and the stent were calculated by four blinded radiologists (scale: 1 - artifacts, making an excellent contribution to visualization; 2 - artifacts, making mainly a contribution to visualization; 3 - artifacts, making no contribution to ...

Energy Technology Data Exchange (ETDEWEB)

A press formability of magnesium alloy sheet cannot be evaluated by only general characteristics in tensile test; tensile strength, elongation n-value and r-value. For example, AZ31-alloy elongates about 20% in room temperature but breaks easily at shallow stage in deep drawing, which is caused by little local elongation (local necking). Crystallographic restriction of slip deformation in this alloy produces high strength, which almost equal to macroscopic fracture strength. In press forming, the bending under high tension requires a large deformability. A great difference in the deformability between AZ31 magnesium alloy and a strain hardened A1100 Aluminum (only 5% in elongation) is shown by static bending test with V-notch. In a rolled plate of AZ31, a crack is produced by stress concentration and propagates with reduced load at all testing temperature up to ...

Energy Technology Data Exchange (ETDEWEB)

There are many factors affecting diffusion bonding in order to obtain high quality joining. Therefore, in the beginning, we constructed diffusion bonding model based on void growth mechanism to predict bonding pressures and times. In addition, in order to compare theoretical values with experimental values, diffusion bonding tests were carried out by using commercial AZ31 magnesium alloy sheets with different grain sizes, 16 and 130 {mu}m. The present AZ31 alloys were successfully diffusion bonded at several conditions, and the bonding strength was more than 0.8 of each parent materials. The experimental bonding conditions in high quality joining, times and pressures, were good agreed with prediction analysis. (orig.)

Energy Technology Data Exchange (ETDEWEB)

AZ31 magnesium alloy was friction-welded to AM60 and the microstructures and the friction welding process were studied. The microstructures changed near the weld interface. The AZ31 was refined to a grain size of several {mu}m near the weld interface. The nucleation occurred in the shear bands that were introduced during the welding process. On the other hand, the eutectic structure was deformed and the lamellar structure which was composed of {alpha}-Mg and Mg{sub 17}Al{sub 12} was formed near the weld interface in AM60 alloy. In the friction process, the adhesion and peel off occurred alternately between AZ31 and AM60. Eventually, bonding was completed during upset process. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The possibility of improving the cold formability of wrought magnesium alloys is considered in light of their good hot forming characteristics. Magnesium alloy AZ31B sheet is selected as a model system. Parameters affecting formability, such as strain hardening rate, strain rate sensitivity, and the degree of anisotropy are examined systematically by conducting tensile tests over a range of temperatures (room temperature to 250 C) and strain rates (1 x 10{sup -5} to 0.1 s{sup -1}). The plastic anisotropy and deformation texture evolution are examined in samples aligned with the sheet rolling and transverse directions. Polycrystal plasticity simulations using a viscoplastic self-consistent (VPSC) formulation are used to model the observed anisotropy and texture evolution. The adjustable parameters in the model are the relative critical resolved shear stresses of the dislocation mechanisms known to ...

Energy Technology Data Exchange (ETDEWEB)

Car weight corresponds directly to fuel consumption and driving performance. So in order to improve the fuel efficiency and performance of a car the weight has to be reduced. Magnesium as a light metal offers a wide range of weight saving opportunities, especially Magnesium wrought alloys with their improved mechanical properties have a high potential for structural applications. Mechanical properties in terms of their quality and anisotropy are dependent on the microstructure of the material and can be characterized by their degree of inhomogeneity, their grain size distribution and their crystallographic texture. Therefore the orientation distribution of grains, the grain size, its size distribution, the chemical composition (precipitates) itself influence the mechanical parameters and their anisotropy. In this presentation first results of mechanical anisotropy are given: differences in yield stress, r-values and their ...

Energy Technology Data Exchange (ETDEWEB)

Superplasticity of polycrystalline metallic materials is a phenomenon which shows hundreds to thousands of percents of large plastic deformation without necking in a steady state of low stress, when the uni-axial tensile loading is done in some special thermo-mechanical conditions (some limited ranges of properly high temperature and low strain rate). The main mechanism of superplastic phenomenon is the grain boundary sliding, while the main mechanism of usual plastic deformation is the trans-granular sliding. In this research, the possibility of superplastic deformation in a magnesium alloy (AZ31Mg alloy) was experimentally investigated, because generally speaking, the magnesium alloy whose atomic structure is hexagonal does not have enough formability in a form of trans-granular sliding mechanism. In this paper, the detail of experimental results are shown and discussed. Moreover, ...

Energy Technology Data Exchange (ETDEWEB)

Better properties of magnesium make it a natural choice for use as an anode material in rechargeable batteries. However, the magnesium alloy thin sheets used in rechargeable batteries were produced by ingot casting and rolling. That technology was so complex and the cost was high. Rapidly solidification by melt spinning is an effect way to solve that problem. In this paper, the technology of rapidly solidified (RS) ribbons in Mg-3%Al-1%Zn-0.2%Mn alloy has been investigated using melt spinning technique. The effect of wheel speed on thickness and microhardness of the ribbons is presented. Microhardness is found to increase with the wheel speed. Rapidly solidification leads to small grains (1{proportional_to}2 {mu}m). The plasticity of the ribbons was well. The quantity of Mg{sub 17}Al{sub 12} decreases with the increase in wheel speed. When the wheel speed reaches 1600 rpm, no Mg{sub 17}Al{sub 12} phase ...

International Nuclear Information System (INIS)

In situ spectroscopic ellipsometry was employed to investigate the initial regime of rare earth metal (REM) conversion coatings formation on AZ31 magnesium alloy. Three REM salts solutions, 0.05 mol.dm"-"3 Ce(NO_3)_3, La(NO)_3 and Sm(NO)_3 solutions, were used for REM conversion coatings preparation. By deconvoluting the ellipsometric data, the surface of the fresh well-polished AZ31 magnesium alloy was found to be covered with 15.80 nm thick native (hydr)oxide film; the refractive indices and the thickness of Ce, La and Sm conversion coatings were obtained. The formation kinetics of three REM coatings follows different exponential functions and the coatings exhibit different optical properties. La conversion coating has the largest n values and the lowest k values while Sm conversion coating is just opposite. Moreover, the pH variation of the bulk conversion solutions upon the coatings formation was ...

Energy Technology Data Exchange (ETDEWEB)

This research investigated the inhibiting effects that sodium salts of linear monocarboxylic acids displayed towards the corrosion process of AZ31 Mg alloy in ASTM D 1387 saline solution (a synthetic industrial cooling water). The length of the aliphatic chain of the acids ranged between 7 and 15 carbon atoms. The inhibiting action of these salts can be related to the precipitation of an insoluble magnesium salt, which mainly affected the anodic reaction. The aliphatic chain length controlled the anion solubility and the reaction rate of magnesium carboxylate formation. For all the salts, an optimum concentration was experienced: 10{sup -2} M for sodium decanoate (caprate), 10{sup -3} M for sodium dodecanoate (laurate), 10{sup -4} M for sodium tetradecanoate (myristate); when this concentration was exceeded, a diminution (even a disappearance) in the inhibiting action was found. (Abstract Copyright [2009], Wiley ...

Energy Technology Data Exchange (ETDEWEB)

Grain refinement in AZ31 magnesium alloy has been attempted by hot-rolling and annealing process. Specimens were solution heat treated at 673 K for 36 ks, then hot-rolled at 423-773 K with total reduction of 20-80% by multi pass process. The rolled specimens were annealed at 473-673 K for 3.6 ks. Grain sizes after the solution heat treatment were about 20 to 150 {mu}m. After hot-rolling at 573 K and annealing at 473 K, grain sizes decreased into about 5 to 10 {mu}m. Suppression of grain growth by pinning due to precipitates was observed by transmission electron microscopic observations. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Self-expanding metallic stent insertion has been widely applied for the palliative treatment of malignant esophageal strictures. Although it is known as an easy, safe, and effective procedure, complications are well known and include things such as stent migration and esophageal stent occlusion caused by tumor in growth. However, metallic stent fractures have been rarely reported in the esophagus, especially for nitinol stents. We report a case of a stent fracture associated with migration in a patient with a malignant esophageal stricture near the gastroesophageal junction. It is highly probable that the stent fracture was due to chemical erosion of the stent caused by gastric juice

Energy Technology Data Exchange (ETDEWEB)

The effect of concentration on the corrosion behavior of Mg-based alloy AZ91D was investigated in ethylene glycol-water solutions using electrochemical techniques i.e. potentiodynamic polarization, electrochemical impedance measurements (EIS) and surface examination via scanning electron microscope (SEM) technique. This can provide a basis for developing new coolants for magnesium alloy engine blocks. Corrosion behavior of AZ91D alloy by coolant is important in the automotive industry. It was found that the corrosion rate of AZ91D alloy decreased with increasing concentration of ethylene glycol. For AZ91D alloy in chloride >0.05 M or fluoride <0.05 M containing 30% ethylene glycol solution, they are more corrosive than the blank (30% ethylene glycol-70% water). However, at concentrations <0.05 for chloride or >0.05 M for fluoride ...

UK PubMed Central (United Kingdom)

BackgroundThere is a strong inverse relationship between final vessel diameter and subsequent risk of treatment failure after coronary stent deployment. The aim of this study was...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

In this study, isothermal torsion tests were carried out on magnesium AZ31B alloy under constant strain rate conditions, in the range of 250 to 400 C at 0.01, 0.1, and 1.0 s{sup -1}. Alloy flow stress dependence on strain rate and temperature can be described by a power law with activation energy of 130 kJ/mol. Microstructural examination of hot deformed samples shows very fine recrystallized grains decorating grain boundaries of larger gains in the form of a necklace. These fine grains are produced by dynamic recrystallization at the grain boundaries of original grains. Microstructure evolution, based on samples quenched at different strain levels, indicates that increasing deformation strain has little effect on recrystallized grain size but widens the recrystallized region, with full recrystallization achieved at a certain high strain level. Recrystallized grain size increases with increasing deformation temperature and ...

Energy Technology Data Exchange (ETDEWEB)

Extruded and hot-rolled 200 C {proportional_to} 500 C AZ31B plates were studied their texture using ODFs analysis. The as-extruded specimen has the strongest intensity of (0001)-ND fiber and 300 C and 400 C hot-rolled ones have the next, but the 200 C hot-rolled one has the lowest intensity. Compared with the corresponding tensile properties, this feature evidents that a pronounced (0001) basal texture will reduce ductility of AZ31B alloy. The ODFs results also indicate that (05 anti 52)- and (01 anti 10)-ND fibers are related to the ductility of AZ31B alloy. (orig.)

International Nuclear Information System (INIS)

Corrosion tests of titanium alloys VTI-0, OT4, VT5-1 and steel Kh18N1OT in 10% and 18% HCl with additions of carnallite at 40 deg C have been carried out. It has been established that titanium alloys in 10% and 18% HCl containing 5 and 10% carnallite are sufficiently corrosion resistant in the presence of 0.1-1% FeCl or HNO_3 and can be used for manufacturing the equipment of recirculation gas scrubbers. Steel Kh18N10T is unstable in all the media tested. It is subjected to intensive pitting. Specimens of steel Kh18N10T have also revealed edge cracking.

Energy Technology Data Exchange (ETDEWEB)

Material testing of SPF-sheet is usually done with coupon hot tensile testing. The optimum range of strain rates is determined with stepped strain tests. To overcome the problem of very few available testing facilities and time consuming and costly procedure, cone cup testing has been developed since long. This test can be generated directly in the workshop, no machining of samples is necessary and it is very much related to the real SPF-process. The analysis of suitable temperature and strain rate is done by simple measurement of resulting cone height. This paper describes a unique and novel variant of the above mentioned baseline design. It provides on-line data of the actual status of the cone cup forming resulting from the applied, constant pressure. Strain rate variations as a result from texture or from the alloy-related behaviour is detectable. Thinning and ''hardening'' behaviour of different alloys ...

Energy Technology Data Exchange (ETDEWEB)

We wanted to evaluate the usefulness of a new type of a complex expandable nitinol stent that was designed to reduce the stent's propensity to migration during the treatment of malignant gastroduodenal obstructions. Two types of expandable nitinol stent were constructed by weaving a single thread of 0.2mm nitinol wire in a tubular configuration: an uncovered stent 18mm in diameter and a covered stent 16mm in diameter. Both ends of the covered stent were fabricated by coaxially inserting the covered stent into the tubular uncovered stent and then attaching the two stents together with using nylon monofilament. Under fluoroscopic guidance, the stent was placed in 29 consecutive patients (20 men and 9 women, mean age: 65 years) who were suffering with malignant gastric ...

Energy Technology Data Exchange (ETDEWEB)

Three kinds of thin AZ31 wrought magnesium alloys sheets were used in order to investigate the influence of the second phase particles on fracture toughness. From the theoretical model, the ratio of {lambda}{sub p}/d{sub p} would be estimated 5 {proportional_to} 6. On the other hand, from the microstructural observation, average particle spacing on each material was sample A: 13.1 {mu}m, sample B: 14.1, and sample C: 12 {mu}. In addition, average particle size on each sample was sample A: 2.1, sample B: 1.9, and sample C: 2.3 {mu}m. Therefore, the ratio of {lambda}{sub p}/d{sub p} calculated from fracture surface observation would be predicted 6 {proportional_to} 7. In comparison with the result of the prediction by theoretical analysis was in good agreement with the result of fracture toughness observation. It was found that the variation in plane-strain fracture toughness on AZ31 were affected by both of particle spacing and particle size. ...

Energy Technology Data Exchange (ETDEWEB)

The deformation behavior and structure changes of magnesium alloy AZ31 were studied in compression at temperatures ranging from 523 K to 673 K and at a strain rate of 3 x 10{sup -3} s{sup -1}. They depend sensitively on deformation temperature. At high temperatures, grain fragmentation takes place due to frequent formation of kink bands initially at corrugated grain boundaries and then in grain interiors, followed by full development of new grains in high strain. At lower temperatures, in contrast, twinning takes place in rather coarse grains and kink bands are formed mainly in finer original ones in low strain. It is concluded that new grain evolution can be controlled by a deformation-induced continuous reaction resulting in grain fragmentation by kink bands, i.e. continuous dynamic recrystallization (cDRX). The latter is discussed comparing with conventional, i.e. discontinuous, DRX. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Microstructure evolution under hot deformation was investigated in compression of a magnesium alloy AZ31 at 673 K (0.73T{sub m}). Two kinds of samples were machined along the parallel and transverse direction of the extruded rods. New fine grains are evolved at corrugated grain boundaries at low strains and developed rapidly in grain interiors in the medium range of strain, finally leading to a roughly full evolution of equiaxial fine grains. Kink bands are evolved at corrugated grain boundaries and in grain interiors at low strains. The boundary misorientation of kink band increases rapidly with increasing strain. These characteristics of new grain evolution process are not changed by the orientation of the samples, while the flow behaviors clearly depend on it. It is concluded that new grain evolution can be controlled by a deformation-induced continuous reaction resulting in grain fragmentation by kink bands, i.e. continuous dynamic ...

International Nuclear Information System (INIS)

The description is presented of binary phase diagrams of titanium alloyed with the following elements: silver, aluminium, arsenic, gold, boron, barium, beryllium, bismuth, carbon, calcium, cadmium, cobalt, chromium, copper, iron, gallium, germanium, hydrogen, hafnium, indium, iridium, potassium, lithium, magnesium, manganese, molybdenum, nitrogen, sodium, niobium, nickel, oxygen, osmium, phosphorus, lead, palladium, platinum, plutonium, rhenium, lanthanium, cerium, preseodymium, neodymium, gadolinium, erbium, terbium, thulium, lutetium, rhodium, ruthenium, scandium, silicon, tin, strontium, tantalum, technetium, thorium, uranium, vanadium, tungsten, yttrium, ytterbium, zinc and zirconium.

British Library Electronic Table of Contents (United Kingdom)

Background: Mechanisms underlying the association between myocardial bridge (MB)-stenting and in-stent restenosis (ISR) are still unclear. Objective: To assess the impact of MB on ISR using intravascular ultrasound (IVUS). Methods: In the Harmonizing Outcomes with Revascularization and Stents in Acute Myocardial Infarction (HORIZONS-AMI) trial, 100 left anterior descending artery (LAD) culprit lesions (79 treated with paclitaxel-eluting stents [PES] and 21 treated with bare metal stents) were imaged with serial IVUS immediately postprocedure and at 13 months. Results: At baseline the LAD stent extended into the MB segment beyond the culprit lesion in seven patients (MB-stent group). In the remaining 93 patients the LAD stent was implanted only in the culprit lesion without extending into t...

Energy Technology Data Exchange (ETDEWEB)

Materials for the construction of cold neutron sources must satisfy a range of demands. The cryogenic temperature and irradiation create a severe environment. Candidate materials are identified and existing cold sources are briefly surveyed to determine which materials may be used. Aluminum- and magnesium-based alloys are the preferred materials. Existing data for the effects of cryogenic temperature and near-ambient irradiation on the mechanical properties of these alloys are briefly reviewed, and the very limited information on the effects of cryogenic irradiation are outlined. Generating mechanical property data under cold source operating conditions is a daunting prospect. It is clear that the cold source material will be degraded by neutron irradiation, and so the cold source must be designed as a brittle vessel. The continued effective operation of many different cold sources at a number of reactors makes it clear ...

International Nuclear Information System (INIS)

The grain size dependence of the tensile properties and the deformation mechanisms responsible for those properties are examined for Mg alloy, AZ31B, sheet. Specifically, the Hall-Petch effect and strain anisotropy (r-value) are characterized experimentally, and interpreted using polycrystal plasticity modeling. {1 0 . 2} extension twins, {1 0 . 1} contraction twins, and so-called 'double-twins' are observed via microscopy and diffraction-based techniques, and the amount of twinning is found to increase with increasing grain size. For the sheet texture and tensile loading condition examined, {1 0 . 2} extension twinning is not expected, yet the polycrystal plasticity model predicts the observed behavior, including this 'anomalous' tensile twinning. The analysis shows that the Hall-Petch strength dependence, of the polycrystal as a whole, is primarily determined by the grain size dependence of the strength of the prismatic slip systems.

Energy Technology Data Exchange (ETDEWEB)

Nitinol has found growing applications in vascular stents, with the recent introduction on the market of a number of new nitinol tubular devices for coronary and peripheral usage. These stents can be produced either through the expansion of a pattern cut on a small tube (pre-cut) or by cutting the deployed design on a tube of a larger size (pre-expanded). The aim of the study was to analyze the differences of properties induced by the two manufacturing methods. For this purpose, differential scanning calorimetry (DSC) measurements were performed on various specimens from the two types of stents. A first set of measurements shows that pre-expanded stents exhibit usual A<->R<->M transformations whereas multi-stage transformations occur for pre-cut stents. Two types of DSC specimens were then prepared for each stent, corresponding to the ...

UK PubMed Central (United Kingdom)

ObjectivesWe undertook a meta-analysis to assess outcomes for drug-eluting (DES) and bare metal stents (BMS) in percutaneous coronary intervention (PCI) for unprotected...Full Text Available

International Nuclear Information System (INIS)

Uranium-aluminum alloys with a significant enrichment of uranium with "2"3"3U or "2"3"5U serve as nuclear fuels in research reactors. The quality assurance of this fuel requires, among other things, precise knowledge that all trace metal constituents that affect neutron economy, fuel integrity, and fuel fabrication process parameters are well within the specification limits. Trace metal characterization of "2"3"5U-Al alloy has been carried out by atomic spectrometry. The trace metal constituents of interest are grouped into common metals (silver, boron, calcium, cadmium, cobalt, chromium, copper, iron, magnesium, manganese, molybdenum, sodium, nickel, lead, silicon, tin, titanium, vanadium, tungsten, and zinc) and lanthanides (cerium, dysprosium, europium, gadolinium, holminium, lutetium, samarium, and terbium). The elements yttrium and zirconium are grouped with the latter in view of the chemical separation procedure used. ...

Energy Technology Data Exchange (ETDEWEB)

The aim of this study was to evaluate imaging features of different coronary artery stents during multislice CT Angiography (MSCTA). Nineteen stents made of varying material (steel, nitinol, tantalum) and of varying stent design were implanted in plastic tubes with an inner diameter of 3 mm to simulate a coronary artery. The tubes were filled with iodinated contrast material diluted to 200 Hounsfield units (HU), closed at both ends and positioned in a plastic container filled with oil (-70 HU). The MSCT scans were obtained perpendicular to the stent axes (detector collimation 4 x 1 mm, table feed 2 mm/rotation, 300 mAs, 120 kV). Axial images and multiplanar reformations were evaluated regarding artifact size, lumen visibility, and intraluminal attenuation values. Artifacts characterized by artifactual thickening of the stent struts leading to apparent reduction in the lumen diameter ...

International Nuclear Information System (INIS)

To compare clinical effectiveness of Viabil-covered stents versus uncovered metallic Wallstents, for palliation of malignant jaundice due to extrahepatic cholangiocarcinoma, 60 patients were enrolled in a prospective and randomized study. In half of the patients a bare Wallstent was used, and in the other half a Viabil biliary stent. Patients were followed up until death. Primary patency, survival, complication rates, and mean cost were calculated in both groups. Stent dysfunction occurred in 9 (30%) patients in the bare stent group after a mean period of 133.1 days and in 4 (13.3%) patients in the covered stent group after a mean of 179.5 days. The incidence of stent dysfunction was significantly lower in the covered stent group (P = 0.046). Tumor ingrowth occurred exclusively in the bare stent group (P = 0.007). Median ...

Energy Technology Data Exchange (ETDEWEB)

We wanted to evaluate the long-term results of a dual expandable nitinol stent for the palliative treatment of malignant gastroduodenal strictures. The dual stent consists of two stents; an outer partially nylon covered stent and an inner bare nitinol stent. The outer stent was placed into the stricture and this was followed by coaxial placement of the inner bare stent. Using fluoroscopic guidance, dual expandable stents were placed in 86 patients with inoperable malignant gastroduodenal strictures. The technical and clinical success, the complication, survival and the stent patency were evaluated during the follow-up period. Stent placement was technically successful in 83 of the 86 patients. After stent placement, 74 of the 85 patients showed improvement of ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

To evaluate the feasibility and clinical effectiveness of using a polyurethane-covered expandable nitinol stent in the palliative treatment of malignant duodenal obstruction. Under fluoroscopic guidance, a polyurethane-covered expandable nitinol stent was placed in 12 consecutive patients with malignant duodenal obstructions. All presented with severe nausea and recurrent vomiting. The underlying causes of obstruction were duodenal carcinoma (n=4), pancreatic carcinoma (n=4), gall bladder carcinoma (n=2), distal CBD carcinoma (n=1), and uterine cervical carcinoma (n=1). The sites of obstruction were part I (n=1), part II (n=8), and III (n=3). Due to pre-existing jaundice, eight patients with part II obstructions underwent biliary decompression prior to stent placement. An introducer sheath with a 6-mm outer diameter and stents 16 mm in diameter were employed, and to place the stent, ...

KoreaScience (Korea)

Full Text Available

British Library Electronic Table of Contents (United Kingdom)

Biodegradable helicoidal stent prototypes made up of layers of poly-L-lactic acid (PLLA) and poly(L-lactic-co-glycolic acid) (PLGA) polymers were fabricated by temperature conditioning the stents at different stages of fabrication. The process incorporated elastic memory, or self-expandability in the stent, which is desirable to minimize stent recoil. The collapse pressures of such stents were studied, with and without in vitro degradation. The effects of thickness and the composition of each layer on the collapse pressure were modeled using the simple series model. Results of the in vitro studies for over 3 months showed that collapse pressure of the stents depended mainly on the degradation and other side-effects brought about by the degradation of different polymer compositions. General...

Energy Technology Data Exchange (ETDEWEB)

The advent of light metal alloys and advanced materials (polymer, composites, etc.) have brought the possibility of achieving important energy reductions into the full life cycle of these materials, especially in transportation applications. 1 These materials have gained acceptance in the aerospace industry but use of light metal alloys needs to gain wider acceptance in other commercial transportation areas. Among the main reasons for the relatively low use of these materials are the lack of manufacturability, insufficient mechanical properties, and increased material costs due to processing inefficiencies. Considering the enormous potential energy savings associated with the use of light metal alloys and advanced materials in transportation, there is a need to identify R&D opportunities in the fields of materials fabrication and forming aimed at developing materials with high specific mechanical properties combined ...

International Nuclear Information System (INIS)

Purpose: To evaluate the effect on dilatation of three types of covering materials used for endovascular stent-grafts.Methods: Stent-grafts with three types of covering material [0.1-mm polytetrafluoroethylene (PTFE), 0.2-mm PTFE, and 0.15-mm woven polyester] were placed in a fluid circuit. For the pulsatile pressure test, the luminal pressure of 190/130 mmHg was loaded up to 300,000 pulses. For the static pressure test, the luminal pressure was increased from 50 to 300 mmHg at 50-mmHg increments. The percent of dilatation of each stent-graft was compared.Results: The 0.1-mm PTFE stent-graft was significantly more dilated than the 0.2-mm PTFE and the 0.15-mm woven polyester stent-graft (p < 0.005) in both examinations. There was no significant difference between the 0.2-mm PTFE and the 0.15-mm woven polyester stent-grafts. The dilatation of the 0.1-mm PTFE ...

International Nuclear Information System (INIS)

Microstructure and properties of a Mg AZ31B laser beam weld without filler are studied using electron microscopy, X-ray diffraction and mechanical tests. The microstructure of the weld is characterized by a narrow heat affected zone, columnar grains and precipitate coarsening in the fusion zone. Texture in the fusion zone is significantly different from the texture of the base material. The residual stress distribution observed is similar at the top and the bottom of the weld, maximum tensile residual stress values are observed in the fusion zone. Tensile tests reveal differences in the mechanical behavior of the fusion zone and the parent material, which can be related to the differences of texture and the resulting deformation mechanisms.

UK PubMed Central (United Kingdom)

Fasting plasma concentrations of magnesium were measured by neutron activation analysis in 30 non-diabetics and 87 diabetics (55 non-insulin-treated, 32 insulin treated). Plasma concentrations of magnesium...Full Text Available

International Nuclear Information System (INIS)

We present our initial experience with a new biodegradable (BD) esophageal stent in two patients, one for a therapy-resistant benign esophageal stricture, and the other as a temporary measure during curative radiotherapy for oesophageal carcinoma. The BD stents need to be loaded into a conventional pull-back delivery system but are then placed in a standard fashion. Pre-dilatation should be avoided to reduce the risk of migration, however if migration occurs the stents can be left to dissolve in the stomach. The stents are radiolucent but easily identified on CT with minimal artefact and thus might even aid with radiotherapy planning. BD stents offer an exciting new strategy for therapy-resistant benign strictures as well as a supportive measure for oesophageal cancer undergoing non-surgical treatment. (orig.)

Energy Technology Data Exchange (ETDEWEB)

AIM: The purpose of the study was to evaluate the percutaneous use of the new nitinol SMARTeR stents in patients with biliary obstruction. MATERIALS AND METHODS: Four stents were placed in three patients percutaneously under ultrasound and fluoroscopic guidance. RESULTS: The deployment of the stents was successful in all three patients. All stents maintained their patency and position after short-term follow-up. CONCLUSION: The nitinol SMARTeR stent is useful in the management of patients with biliary obstruction although accurate placement across the ampulla was found to be technically more difficult than with the Wallstent. Larger, long-term follow-up studies are required to evaluate the long-term patency of these new devices.

International Nuclear Information System (INIS)

Separate effect of impurities and alloying additions of phosphorus, silicon, boron, carbon, sulphur, magnesium, copper, aluminium and molybdenum on the tendency to intergranular corrosion (IGC) of quenched highly pure steel Fe-20% Cr-20Ni in boiling solution 27% HNO_3+40 g/l Cr"6"+, as well as in sulphuric and nitric acids mainly at potentials, corresponding to repassivation range, has been studied. It is shown that steel susceptibility to IGC depends on impurity nature and to a high extent is determined by the potential value independent of the way of its achieving. The most unfavourable effect on stability of grain boundaries is produced by microadditions of boron as well as by impurities of phosphorus and silicon. To ensure increased corrosion resistance of the investigated steel against IGC in highly oxidative media the pontent of phosphorus and silicon impurities unit should not exceed 0.01 and 0.2% respectively. At that, boron ...

International Nuclear Information System (INIS)

Coiling or infusion of embolic materials into a wide necked aneurysm can be performed with stenting. The purpose of our study is to assess the technical feasibility of aneurysm treatment with glue embolization after stenting. We used four Wallstents for surgically repairing eight canine carotid aneurysms. After confirmation of the aneurysms on the angiogram, we introduced a 6-7 F guiding catheter in order to deploy the stents. After stenting, we passed a microcatheter into the aneurysm lumen through the stent mesh. 28% glue was slowly injected until the glue cast completely filled the lumen. We evaluated the passage of a microcatheter through the stent meshwork, formation of the glue cast and the stents' ability to protection for any leakage of glue. The follow-up angiogram was obtained for two dogs, one to three times until 8 weeks, and ...

UK PubMed Central (United Kingdom)

To treat or prevent some of the 795,000 annual strokes in the U.S., self-expanding endo-vascular stents deployed under fluoroscopic image guidance are often used. Neuro-interventionalists need...Full Text Available

UK PubMed Central (United Kingdom)

AIM: To evaluate the efficacy of self expandable metallic stents (SEMS) in patients with malignant esophageal obstruction and fistulas.METHODS: SEMS were implanted in the presence of fluoroscopic...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Infrainguinal peripheral occlusive disease is increasingly being treated by endovascular techniques. Bare metal stainless steel, self-expanding nitinol stents, drug-eluting and covered stents (stent grafts) are becoming increasingly more important adjuncts to percutaneous translumninal angioplasty in the treatment of peripheral artery disease. In this article the available evidence supporting the use of stents in the femoropopliteal and tibial arteries will be described as well as their limitations. Future stent developments will also be discussed. (orig.) [German] Die endovaskulaere Therapie spielt bei der Therapie der peripheren arteriellen Verschlusskrankheit (PAVK) eine wichtige Rolle. Unbeschichtete ballonexpandierbare Stahlstents, selbstexpandierende Nitinolstents sowie medikamentenbeschichtete und ''covered stents'' ...

UK PubMed Central (United Kingdom)

AIM: To compare 2 different types of covered esophageal nitinol stents (Ultraflex and Choostent) in terms of efficacy, complications, and long-term outcome.METHODS: A retrospective review of...Full Text Available

Science.gov (United States)

Carotid Artery Disease; Stroke; Amaurosis Fugax; Transient Ischemic Attack (TIA)

Wastenet

as a by-product during the purification of molten magnesium chloride prior to its electrolysis and during the

Energy Technology Data Exchange (ETDEWEB)

The feasibility of self-expanding nitinol stents for treatment of infragenicular arteries following unsuccessful balloon angioplasty was assessed. Options for lower limb percutaneous revascularization are limited, especially for complex vessel obstruction. Depending on the lesion and the experience of the interventionalist, the failure rate of balloon angioplasty (PTA) ranges between 10 and 40%. Until recently, no self-expanding stent for the use in the infragenicular arteries was available. This is the first report of the results for 18 consecutive patients who received 4F sheath compatible self-expanding nitinol stents following unsuccessful PTA or early restenosis. Twenty-four stents were implanted in 21 lesions for various indications residual stenosis >50% due to heavy calcification, flow-limiting dissection, occluding thrombus resistant to thrombolyis, thrombaspiration, and PTA, and early ...

International Nuclear Information System (INIS)

Radiotherapy has been reported to be of benefit in prolonging the survival of patients with cholangiocarcinoma. This study examined whether radiotherapy in addition to endoscopic stenting improved survival. The survival advantage of radiotherapy in those with a type II/III stricture is seen only in the first 10 months after diagnosis. The costs of radiotherapy and significantly increased time spent in hospital, however, raise doubts over its routine use in the management of non-resectable cholangiocarcinoma. (Author).

Energy Technology Data Exchange (ETDEWEB)

The mechanical stability of diamond-like carbon (DLC) films coated on nitinol vascular stents was investigated under cyclic loading condition by employing a stent crimping system. DLC films were coated on the vascular stent of a three dimensional structure by using a hybrid ion beam system with rotating jig. The cracking or delamination of the DLC coating occurred dominantly near the hinge connecting the V-shaped segments of the stent where the maximum strain was induced by a cyclic loading of contraction and extension. However the failures were significantly suppressed as the amorphous Si (a-Si) buffer layer thickness increased. Interfacial adhesion strength was estimated from the spalled crack size in the DLC coating for various values of the a-Si buffer layer thickness.

International Nuclear Information System (INIS)

Objective: Traditional nasolacrimal duct stenting possesses some shortcoming including difficulty of pulling ball head guide wire from the nasal cavity with turbinate hypertrophy and nasal septal deviation. The new method of nose-oral tube track establishment can overcome the forementioned and increase the successful rate. Methods: 5 F catheter and arterial sheath were modified to be nasolacrimal duct stent delivery device respectively. Antegrade dacryocystography was taken firstly to display the obstructed site and followed by the modified protocol of inserting the guide wire through nasolacrimal duct and nasal cavity, and establishing the stent delivery track for retrograde stent placement. Results: 5 epiphora patients with failure implantation by traditional method were all succeeded through the modified stenting (100%). During 6-mouth follow-up, no serious complications and ...

Energy Technology Data Exchange (ETDEWEB)

To evaluate the efficacy of newly designed covered and non-covered coated colorectal stents for colonic decompression. Twenty-six patients, (15 palliative cases and 11 preoperative) underwent treatment for the relief of colorectal obstruction using metallic stents positioned under fluoroscopic guidance. In 24 of the 26, primary colorectal carcinoma was diagnosed, and in the remaining two, recurrent colorectal carcinoma. Twenty-one patients were randomly selected to receive either a type A or type B stent; for the remaining five, type C was used. Type A, an uncovered nitinol wire stent, was lightly coated to ensure structural integrity. Type B (flare type) and C (shoulder type) stents were polyurethane covered and their diameter was 24 and 26mm, respectively. The rates of technical success, clinical success, and complications were analyzed using the chi-square test, and to analyse ...

Science.gov (United States)

It is well known that one of the main advantages of the high speed forming (HSF) processes is the improvement in the forming limits of the used materials.Using the Electromagnetic Forming (EMF) technology two materials have been tested with different mechanical and physical properties: the AA5754 aluminium and the AZ31B magnesium alloys.The EMF process principle can be described as follows: A significant amount of electrical energy is stored in a bank of capacitors which are suddenly discharged releasing all the stored energy. This electric discharge runs through a coil which generates an intense transient magnetic field. At the same time transient Eddy currents are induced in the electrically conductive part placed some millimetres far from the coil. Another intense magnetic field is generated due to those Eddy currents but on the opposite direction as the one generated by the coil. A big magnetic repulsion force is created between the part ...

Energy Technology Data Exchange (ETDEWEB)

Various methods for storing hydrogen have been examined in an effort to find ways to store hydrogen in increasingly smaller volumes with decreasing weight of the whole hydrogen storage system. Metal hydrides, in which hydrogen is chemically bound to a metal atom, are considered to be very promising candidates for hydrogen storage because they have high gravimetric and volumetric storage capacities. This study investigated the effect of different magnesium (Mg) and aluminium (Al) ratios on the absorption and desorption properties of thin films. Neutron reflectometry (NR) was used in this study to better understand the absorption and desorption properties of commercially promising hydrogen storage materials. The large negative scattering length of hydrogen atoms changes the reflectivity curve substantially, so that NR can determine the total amount of stored hydrogen as well as the hydrogen distribution along the film normal, with nanometer resolution. In order to ...

International Nuclear Information System (INIS)

Purpose: The lifelong persistence of foreign bodies within the arteries may contribute to restenosis. Thus,biodegradable devices might decrease recurrence rates. Methods: Eleven polyhydroxybutyrate biodegradable stents and 13 tantalum stents were implanted into the iliac arteries of New Zealand white rabbits for up to 30 weeks. After killing the animals,the specimens were harvested, fixed in formalin, processed in paraffin,and stained. Results: Polyhydroxybutyrate instigated intense inflammatory and proliferative reactions with an increase in collagen (2.4- to 8-fold vs native segments), thrombosis and in-stentlumen narrowing (375.5-606.6 mm vs 655.6 #+-# 268.8 mm in native segments). The elastic membranes were destroyed in all specimens. The tantalum stents increased the in-stent lumen progressively (769.7 #+-# 366.6 mm vs 1309.9 #+-# 695.3 mm),penetrated the external elastic membrane, and increased ...

Science.gov (United States)

... Both magnesium and aluminium phosphides are therefore potentially more efficient than either calcium or sodium phosphide. ...

International Nuclear Information System (INIS)

Russian (1972). USSR Desyatnik, VN Kurbatov, NN Raspopin, SP Trifonov,

Energy Technology Data Exchange (ETDEWEB)

Measurements of the double-electron-capture process in which a positive ion of iodine becomes a negative ion in a single collision with a magnesium atom are reported between 20 and 90 keV. The cross section is comparable to that for the rare gases and not as large as might be expected from a two-valence-electron atom. This process is probably insignificant in the production of negative ion beams using a magnesium-vapor target.

Energy Technology Data Exchange (ETDEWEB)

The objective of this study was to compare contrast-enhanced magnetic resonance angiography (CE MRA) and multislice computed tomographic angiography (MS CTA) in the follow-up of thoracic stent-graft placement. The CE MRA and MS CTA were performed following nitinol stent-graft treatment due to thoracic aneurysm (n=4), intramural bleeding (n=2) and type-B aortic dissection (n=5). Corresponding evaluation of arterial-phase imaging characteristics focused on the stent-graft morphology and leakage assessment. Stent-graft and aneurysm extensions were comparable between both techniques. Complete exclusion (aneurysm, n=4; dissection, n=2) was assessed with high confidence with CE MRA and MS CTA. Incomplete exclusion (intramural bleeding, n=2; dissection, n=3) was assigned to lower confidence scores on CE MRA compared with MS CTA. On CE MRA the stent-graft lumen demonstrated an inhomogeneous ...

Energy Technology Data Exchange (ETDEWEB)

We wanted to determine the technical and clinical efficacy of placing a self-expandable PTFE-covered nitinol stent for the management of inoperable malignant biliary obstruction. Thirty six patients with inoperable malignant biliary obstructions were treated by placement of self-expandable PTFE-covered nitinol stents (S and G Biotech Corporation, Seongnam, Korea). Clinical evaluation was done with assessment of the serum bilirubin and alkaline phosphatase levels, which were measured before and after stent placement within 1 week, at 1 month and at 3 months. The patient survival rate and stent patency rate were calculated with performing Kaplan-Meier survival analysis. Successful stent placement was achieved in all the patients without procedure-related complication. Pancreatitis as an early complication occurred in two cases. The serum bilirubin and alkaline phosphatase levels were ...

Energy Technology Data Exchange (ETDEWEB)

The Partnership for a New Generation of Vehicles (PNGV) program intends to develop new designs for automobiles that will reduce fuel consumption by two thirds but otherwise have price, comfort, safety, and other measures of performance similar to the typical automobile now on the market. PNGV vehicle designs are expected to substitute lightweight materials, such as aluminum, magnesium, carbon-reinforced polymer composites, glass-reinforced polymer composites, and ultra- light steel, for heavier materials such as steel and iron in automobile components. The target mass of a PNGV vehicle is 1,960 pounds, as compared to the average current vehicle that weights 3,240 pounds. Other changes could include the use of different ferrous alloys, engineering changes, or incorporation of advanced ceramic components. Widespread adoption of these vehicle designs would affect materials markets and require concurrent development and adoption of supporting ...

Energy Technology Data Exchange (ETDEWEB)

To assess the feasibility of transluminal radiofrequency thermal ablation using a stent-type electrode and to determine, by means of in-vivo and in-vivo animal studies, the appropriate parameters. In-vivo: the radiofrequency electrode used was a self-expandable nitinol stent with 1cm insulated ends. A stent was placed in the portal vein of bovine liver, and ablations at target temperatures of 70, 80, 90, and 100 .deg. C were performed. Ablated sizes were measured longitudinally. In vivo: four mongrel dogs were anesthetized, and a stent was inserted in the common bile duct under fluoroscopic guidance through an ultrasound-guided gall bladder puncture site. The ablation temperature was set at 80 .deg. C, and each dog underwent proximal and distal esophageal ablations lasting 12 minutes. They were sacrificed immediately. In-vivo: ablated sizes showed significant correlation with target temperatures ...

UK PubMed Central (United Kingdom)

Background. New-generation drug-eluting stents (DES) may solve several problems encountered with first-generation DES, but there is a lack of prospective head-to-head comparisons between...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

As an alternative to surgery, endovascular therapy with stent grafts has become the second main treatment option for infrarenal abdominal aortic aneurysms. Unlike surgery, endovascular treatment with stent grafts is also applicable in patients unfit for open repair. Despite current improvements in endovascular repair devices, significant anatomic barriers still exclude this technique for a large number of patients. Computed tomography, magnetic resonance imaging, and ultrasound are essential for diagnostics, preintervention planning, and postintervention follow-up of abdominal aneurysms treated with stent grafts. This review covers etiology, pathology, and diagnostic aspects. Materials and methods for endovascular treatment of abdominal aortic aneurysms are presented in detail, and clinical results and complications are discussed. (orig.) [German] Die endovaskulaere Therapie des infrarenalen Bauchaortenaneurysmas hat sich ...

Science.gov (United States)

We present a sample preparation method for measuring magnesium in individual whole lymphocytes by electron probe X-ray microanalysis. We use Burkitt's lymphoma cells in culture as the test sample and compare X-ray microanalysis of individual cells with atomic absorption analysis of pooled cell populations. We determine the magnesium peak-to-local continuum X-ray intensity ratio by electron probe X-ray microanalysis and calculate a mean cell magnesium concentration of 39 +/- 19 mmol/kg dry weight from analysis of 100 cells. We determine a mean cell magnesium concentration of 34 +/- 4 mmol/kg dry weight by atomic absorption analysis of pooled cells in three cell cultures. The mean cell magnesium concentrations determined by the two methods are not significantly different. We find a 10% coefficient of variation for both methods of analysis and a 30% coefficient of variation in ...

Science.gov (United States)

Increasing the Mg(2+) concentration results in a depression of succincoxidase-linked state 3

Energy Technology Data Exchange (ETDEWEB)

This patent describes a catalyst composition. It consists of the catalytic oxides of iron, bismuth, molybdenum and magnesium as essential components and optionally the oxides of cobalt, nickel, phosphorus and arsenic.

International Nuclear Information System (INIS)

Objective: To explore the interventional method to treat biliary recurrent jaundice after T tube drainage in patients with malignant obstructive jaundice due to cholangiocarcinoma. Methods: 7 biliary metallic stents were placed in 7 patients with recurrent jaundice after T-tube drainage in cholangiocarcinoma cases. Results: Stent placement was once successful in all 7 cases with successful rate of 100%. For all cases, TBIL, ALT, GTP and AKP values 7 days postoperatively were significantly lower than that of preoperation together with subsidence of jaundice satisfactorily for 100% after the treatment. Conclusions: Percutaneous placement of biliary metallic stents was effective economic, minimal invasive and safe for palliation of biliary recurrent jaundice after T tube drainage in cholangiocarcinoma-induced obstructive jaundice

International Nuclear Information System (INIS)

Chronic mesenteric arterial ischemia is an uncommon condition associated a high morbidity and mortality. It is most Commonly caused by atherosclerotic occlusive disease. Patients may suffer epigastric or periumbilical postprandial pain ten to thirty minutes after eating. A case of chronic mesenteric artery stenosis, the diagnosis was performance with colonoscopy and biopsy. We present a case report of a patient with chronic mesenteric ischemia. Mesenteric arteriography was performed and documented estenosis of the mesenteric superior artery. Then percutaneous arteriography with angioplasty and implant of stent was performed. The patients became completely asymptomatic and normal colon mucous is observed in control colonoscopy. The purpose of this report is to present the case endoscopy, clinic and radiological features and to describe the percutaneous angioplasty and implant of stent. We believe that angioplasty treatment offers and improvement ...

British Library Electronic Table of Contents (United Kingdom)

PurposeTo evaluate the safety and effectiveness of the Zilver vascular stent in the treatment of de novo or restenotic lesions in the external and common iliac arteries.Materials and MethodsRegardless of the results of an initial percutaneous transluminal angioplasty (PTA), 151 consecutive patients were implanted with Zilver vascular stents (Cook, Bloomington, Ind) in up to two stenotic (?10 cm) or occluded (?5 cm) atherosclerotic lesions of the external or common iliac arteries. The primary endpoint was the rate of major adverse events within 9 months after the procedure. Major adverse events were defined as death, myocardial infarction, target lesion revascularization, and limb loss. Secondary endpoints included acute procedural success, 30-day clinical success, 9-month pat...

Energy Technology Data Exchange (ETDEWEB)

The purpose of this study was to evaluate the usefulness of a multifunctional gastrointestinal coil catheter for stent placement in 98 patients with colorectal strictures. The catheter was used in 98 consecutive patients for stent placement in the rectum (n = 24), recto-sigmoid (n = 13), sigmoid (n = 38), descending (n = 6), transverse (n = 11), splenic flexure (n = 3), hepatic flexure (n = 2), and ascending (n = 1) colon. The catheter was made of a stainless steel coil (1.3 mm in inner diameter), a 0.4-mm nitinol wire, a polyolefin tube, and a hemostasis valve. Usefulness of the catheter was evaluated depending on whether the catheter could pass a stricture over a guide wire and whether measurement of the stricture length was possible. The passage of the catheter over a guide wire beyond the stricture was technically successful and well tolerated in 93 (94.9%) of 98 patients. In the failed five patients, it was not possible to negotiate the ...

UK PubMed Central (United Kingdom)

Leakage after oesophageal anastomosis or perforation remains a challenge for the surgeon. Traditional management has been operative repair or intensive conservative management. Both treatments are...Full Text Available

UK PubMed Central (United Kingdom)

Incidence of esophageal cancer (EC) is rising more rapidly in the Western world than that of any other cancer. Despite advances in therapy, more than 50% of patients have incurable disease at the time...Full Text Available

UK PubMed Central (United Kingdom)

Gastrointestinal perforations are conservatively managed at endoscopy by through-the-scope endoclips and covered self expandable stents, according to the size and tissue features of the perforation....Full Text Available

UK PubMed Central (United Kingdom)

BackgroundObservational clinical studies have shown that patients with diabetes have less favorable results after percutaneous coronary intervention compared with the non-diabetic...Full Text Available

UK PubMed Central (United Kingdom)

Endovascular treatment of post-traumatic pseudoaneurysms has become a viable, less invasive option when compared to open repair. Due to the relative youth of this technology, studies have yet to be...Full Text Available

UK PubMed Central (United Kingdom)

Tracheobronchial balloon dilation and stent placement have been well used in the treatment of patients with benign and/or malignant diseases. Balloon dilation is the first option in the treatment of...Full Text Available

UK PubMed Central (United Kingdom)

Endovascular surgery is a new multidisciplinary field that applies the recently innovated techniques of angioscopy, intraluminal ultrasound, balloon angioplasty, laser, mechanical atherectomy, and stents....Full Text Available

UK PubMed Central (United Kingdom)

Hemoptysis in patients with lung cancer is not uncommon and sometimes have dangerous consequences. Hemoptysis has been managed with various treatment options other than surgery and medicine, such as...Full Text Available

UK PubMed Central (United Kingdom)

ObjectiveTo determine if an aggressive approach to coronary revascularisation with oversized balloons is counterproductive, we studied the effect of increasing balloon‐to‐artery...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Objective: To determine the efficacy of a covered stent prototype designed for protected carotid angioplasty to reduce cerebral embolization. Material and Method: The covered stent tested is made of nitinol, coated with a polyurethane membrane (MembraX{sup TM}; porous size 80 {mu}m). In a bench-top model (flow-rate 650 ml/min, pulsatile flow [dicrote] 123 Pulses/min, pressure 100/60 mm Hg [mean pressure 80 mmHg]) with inserted human carotid (n=6) stent implantation was performed (8/32 mm). Passed particles (mg) were determined in the effluent of a 100 {mu}m filter prior to intervention, after stent deployment and after final dilation (5 mm). Results: When stenting carotid arteries obtained from human cadavers, the highest rate of particle embolization was measured while crossing the lesion with the delivery device (6,8 mg; for all p<0,05), embolization after additional ...

International Nuclear Information System (INIS)

We present a sample preparation method for measuring magnesium in individual whole lymphocytes by electron probe X-ray microanalysis. We use Burkitt's lymphoma cells in culture as the test sample and compare X-ray microanalysis of individual cells with atomic absorption analysis of pooled cell populations. We determine the magnesium peak-to-local continuum X-ray intensity ratio by electron probe X-ray microanalysis and calculate a mean cell magnesium concentration of 39 +- 19 mmol/kg dry weight from analysis of 100 cells. We determine a mean cell magnesium concentration of 34 +- 4 mmol/kg dry weight by atomic absorption analysis of pooled cells in three cell cultures. The mean cell magnesium concentrations determined by the two methods are not significantly different. We find a 10% coefficient of variation for both methods of analysis and a 30% coefficient of variation in ...

Energy Technology Data Exchange (ETDEWEB)

Inferior vena cava (IVC) obstruction is a well-described clinical entity. Most IVC obstructions from malignant neoplasms are a direct result of tumor compression [Oviedo J, Cerda S. Vascular invasion by hepatocellular carcinoma. Arch Pathol Lab Med 2001;125: 454-5; Furui S, Sawada S, et al. Gianturco stent placement in malignant caval obstruction: analysis of factors for predicting the outcome. Radiology 1995;195:147-52; Fletcher WS, Lakin PC, et al. Results of treatment of inferior vena cava syndrome with expandable metallic stents. Arch Surg 1998;133:935-8]. The symptoms of IVC obstruction include progressive ascites, scrotal edema and lower body edema. These constellations of symptoms are described as IVC syndrome and are devastating to a patient with end-stage cancer. We describe a palliative therapy utilizing Luminexx nitinol self-expanding stents to treat intracaval hepatoma thrombus obstructing the IVC. The procedure ...

International Science & Technology Center (ISTC)

The New Titanium Alloys With Increased Mechanical Properties and Corrosion Resistance for Medical Instruments and their Coatings

CERN Document Server

Metals and alloy - Atmospheric corrosion testing

International Nuclear Information System (INIS)

Objective: To evaluate the effect of PTBD in treating malignant biliary obstruction caused by hilar cholangiocarcinoma. Methods: We retrospectively analyzed the data of 103 patients(M:62,F:41)with malignant obstructive jaundice caused by hilar cholangiocarcinoma. After taking percutaneous transhepatic cholangiography, metallic stent or plastic external catheter or external-internal catheter for drainage was deployed and then followed up was undertaken with clinical and radiographic evaluation and laboratory. examination. Results: All patients went though PTBD successfully (100%). According to Bismuth classification, all 103 cases consisted of I type(N=30), II type (N=30), III type (N=26) and IV type (N=17). Thirty-nine cases were placed with 47 stents and 64 eases with drainage tubes. 4 cases installed two stems for bilateral drainage, 2 cases installed two stents because of long segmental strictures with ...

Energy Technology Data Exchange (ETDEWEB)

To assess the technical feasibility of a newly designed stent-like electrode in rabbits. A stent-like electrode was knitted from a single thread of nitinol wire and interconnected to a generator using similar wire. In order to gauge the extent of radiofrequency ablation (RFA), we measured the depth of the ablated area in cow liver using a combination of 180-sec time intervals and 20- watt power increments. For data processing, Cox regression analysis was used. RFA was also applied to the small intestine of rabbits using this stent-like electrode under six different sets of conditions: 10 watts for 1 min, 10 watts for 2 mins, 20 watts for 1 min, 20 watts for 2 mins, 30 watts for 1 min, and 30 watts for 2 mins. To determine the gross and microscopic findings, six animals were sacrificed immediately after the procedure and the results obtained under the different sets of conditions were correlated. Eight rabbits were monitored ...

Science.gov (United States)

... MOLYBDENUM ALLOY GUN BARREL LINERS o0 in ... NEW POWDER TECHNOLOGIES FOR MOLYBDENUM ALLOY GUN BARREL LINERS ...

International Nuclear Information System (INIS)

... filters molybdenum alloys production sulfuric acid alloys chemical reactions ...

International Nuclear Information System (INIS)

Luminescence and reflection spectra as well as luminescence kinetics of the 1 mol% Sm3+-doped crystalline lanthanum magnesium meta borate (LaMgB5O10) and gadolinium magnesium meta borate (GdMgB5O10) were analyzed. Materials were synthesized by conventional solid state route and showed bright orange-red emission under UV excitation. Emission spectra contain sharp and well resolved Sm3+4G5/2#->#6HJ transitions indicating a strong crystal-field effect. In case of gadolinium compound energy transfer between Gd3+ and Sm3+ was detected. The luminescent kinetics of the Sm3+ in analyzed powders is characterized by single exponential decay and experimental values vary in the range 2.2-2.4 ms. - Research highlights: ? Phosphorescence of samarium-doped lanthanide magnesium meta borates. ? Bright and well resolved orange-red emission of Sm3+ under UV excitation. ? Energy transfer from Gd3+ to Sm3+ in gadolinium ...

Science.gov (United States)

The effects of various fixative agents, pH, ionic strength, stain concentration, and magnesium concentration on DNA staining with the antibiotics olivomycin, chromomycin A3, and mithramycin were examined with DNA in solution and in mammalian cells.

British Library Electronic Table of Contents (United Kingdom)

ObjectivesThe SPIRIT V (A Clinical Evaluation of the XIENCE V Everolimus-Eluting Coronary Stent System in the Treatment of Patients With De Novo Coronary Artery Lesions) study is a post-market surveillance experience of the XIENCE V (Abbott Vascular, Santa Clara, California) everolimus-eluting stent (EES) in patients with higher-risk coronary anatomy. BackgroundPrevious pre-approval studies have shown the safety and efficacy of EES in highly selected groups of patients. MethodsThe SPIRIT V trial is a prospective, open label, single arm, multicenter study. Two thousand seven hundred patients with multiple de novo coronary artery lesions suitable for treatment with a planned maximum of 4 EES were enrolled at 93 centers in Europe, Asia Pacific, Canada, and South Africa. Lesions had a referenc...

International Nuclear Information System (INIS)

The effect of a mineralizer, magnesium silicate, on the nitridation of compacts consisting of silicon, clay, silica and silicon carbide was examined in terms of their reaction depth, density, porosity, phase composition and microstructure. It was found that addition of mineralizer slowed down the nitridation significantly. The kinetic process of isothermal nitridation in the presence of magnesium silicate obeys a parabolic rate law. Otherwise it obeys a linear rate law. The results suggest that nitrogen transportation is the limiting step during nitridation when mineralizer is added. The mechanism of nitridation is discussed in terms of phase composition and microstructure. Copyright (2000) The Australian Ceramic Society

British Library Electronic Table of Contents (United Kingdom)

BackgroundAlthough self-expandable metal stent (SEMS) insertion is widely used for relief of malignant colorectal obstructions, the immediate technical and clinical failure rates of SEMSs and the associated risk factors remain largely unknown. ObjectiveTo identify rates and factors predictive of technical and clinical failure of SEMSs when their use is attempted for the decompression of malignant colorectal obstruction. DesignRetrospective chart review. SettingA tertiary-care academic medical center in South Korea. PatientsThis study involved a total of 412 patients with malignant colorectal obstruction in whom SEMS insertion was attempted. InterventionPlacement of colonic SEMSs. Main Outcome MeasurementsTechnical success and immediate and long-term clinical success rates. ResultsTechnical...

International Nuclear Information System (INIS)

Results of hot cracking on welds with compositions between alloy 800 and AWS ER NiCr 3. Investigation of the influence of Si, Mn, Ti and Al on the hot cracking suscpetibility of the alloy 800. (orig.).

CERN Document Server

Metals and alloys : atmospheric corrosion testing : General requirements for field tests

Science.gov (United States)

... Title : Effect of Yttrium on the Microstructure of Titanium Alloys,. ... The yttrium was added in the melting stage as an oxide or in the elemental form. ...

International Nuclear Information System (INIS)

The importance that must be attached to the phenomenon of stress corrosion cracking of austenitic alloys is emphasized. The relation between chemical composition of various alloys and their sensitivity to cracking is shown with particular reference to the behaviour of Alloy 800. The different effects of alkaline anc chloride environments are discussed. Studies are reported of the general corrosion of Alloy 800 and other alloys in an environment representative of the primary coolant of PWR reactors; and of the behaviour of various alloys (including Alloy 800) in the conditions envisaged for their use for steam generators with superheat up to about 550 deg.C. (U.K.).

Energy Technology Data Exchange (ETDEWEB)

Due to the well-establish corrosion problems of Alloy 600 as a steam-generator material and the subsequent focus on thermally treated (TT) Alloy 690 and Alloy 800 as alternative materials, a systematic analysis of the corrosion behavior of these two latter alloys is warranted. Corrosion test results for Alloys 690 TT and 800 were collected and organized in the form of corrosion mode diagrams. Selected data for mill annealed (MA) Alloy 600 were also included for reference. The corrosion mode diagrams correlate the modes of corrosion degradation observed in tests as functions of the environment pH and electrochemical potential (ECP). The diagrams confirm that Alloys 690TT shows some susceptibility in caustic environments, and Alloy 800 shows susceptibility in both caustic and highly acidic environments. (authors). 6 figs., ...

International Nuclear Information System (INIS)

The low cycle fatigue testing was carried out to provide a basis for comparison of the behavior of the two kinds of Alloy 800 (low carbon Alloy 800 and high carbon Alloy 800H). The testing was done at temperatures of 500"0C and 650"0C either with or without hold. The results obtained were as follows: (1) At 650"0C, the low-cycle fatigue life was essentially the same for the two alloys on the basis of strain amplitude, but Alloy 800H had a longer life on the basis of stress amplitude. (2) At 500"0C, the two alloys exhibited longer lives than at 650"0C, with Alloy 800 exhibiting 2-3 times longer life than Alloy 800H when compared on the basis of plastic strain range. At this temperature the stress range showed the maximum for Alloy 800H. (3) When a creep effect was introduced either by way of a hold ...

International Nuclear Information System (INIS)

The influence of various alloy elements on tensile strength of the eutectic, directionally solidified superalloy 73 C was determined. The tensile properties of the base alloy has been increased by Al, Y and C as alloying elements, while Ni and Ti showed a decreasing effect (alloy softening). However, ductility and thermo-fatigue behaviour had been influenced in a positive way by these elements. The specific meachanism caused by the different elements are discussed. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The processing characteristics, tensile properties, and oxidation response of two Nb-Ti-Al-Cr alloys were investigated. One creep test at 650 C and 172 MPa was conducted on the base alloy, which contained 40Nb-40Ti-10Al-10Cr. A second alloy was modified with 0.11 at.% C and 0.07 at.% Y. Alloys were arc melted in a chamber backfilled with argon, drop cast into a water-cooled copper mold, and cold rolled to obtain a 0.8-mm sheet. The sheet was annealed at 1,100 C for 0.5 h. Longitudinal tensile specimens and oxidation specimens were obtained for both the base alloy and the modified alloy. Tensile properties were obtained for the base alloy at room temperature, 400, 600, 700, 800, 900, and 1,000 C and for the modified alloy at room temperature, 400, 600, 700, and 800 C. Oxidation tests the base alloy ...

Energy Technology Data Exchange (ETDEWEB)

The use of nickel alloys in Flue Gas Desulfurization (FGD) applications is described. Recently, nickel alloys 625 and C-276 have been clad to carbon steel plate. Production and properties of the clad plate are reviewed and a brief discussion is presented on production, fabrication and welding. Laboratory and field corrosion tests in SO/sub 2/ scrubber environments suggest that alloy 625 and C-276 clad steel plates are as corrosion resistant as the solid alloy plate.

International Nuclear Information System (INIS)

The relationships of hydrogen alloyed #beta#-titanium alloy deformation behaviour to its microstructure and texture are investigated. It is shown that plasticity increases and strain induced texture changes at low hydrogen contents (0.1-0.2 mass %). Possible mechanisms responsible for specific features of #beta#-Ti alloy deformation are discussed. The study is made using alloy VT35 doped with hydrogen

International Nuclear Information System (INIS)

This work showed the formation of phospholipid vesicle coating on inorganic sericite surface with characterization by combining electron microscopy of FE-SEM, TEM, AFM, and qualitatively evaluated the coated phospholipid vesicle by XPS as a function of etching time. The possibility of phospholipid vesicle mobility on the surface was restrained by the chelation effect of magnesium cation. The stabilization properties of phospholipid vesicles on sericite surface were demonstrated by the various concentration of magnesium cation. The presence of magnesium was found to have a much more pronounced influence on the lipid deposition process. The Mg cation plays an important role for attaching the phospholipids with optimum concentration of 7 mM. Totally, the phospholipid vesicles coating on inorganic powder could be useful for bio-related fields such as cosmetics and drug delivery system as the key functional compounds. We hope ...

Energy Technology Data Exchange (ETDEWEB)

The experiment was carried out on a short rotation coppice culture of poplars (POP-EUROFACE, Central Italy), growing in a free air carbon dioxide enriched atmosphere (FACE). The specific objective of this work was to study whether elevated CO{sub 2} and fertilization (two CO{sub 2} treatments, elevated CO{sub 2} and control, two N fertilization treatments, fertilized and unfertilized), as well as the interaction between treatments caused an unbalanced nutritional status of leaves in three poplar species (P. x euramericana, P. nigra and P. alba). Finally, we discuss the ecological implications of a possible change in foliar nutrients concentration. CO{sub 2} enrichment reduced foliar nitrogen and increased the concentration of magnesium; whereas nitrogen fertilization had opposite effects on leaf nitrogen and magnesium concentrations. Moreover, the interaction between elevated CO{sub 2} and N fertilization amplified some element unbalances such ...

Energy Technology Data Exchange (ETDEWEB)

The development of a twinned microstructure in hexagonal close-packed rolled magnesium compressed in the in-plane direction has been monitored in situ with neutron diffraction. The continuous conversion of the parent to daughter microstructure is tracked through the variation of diffraction peak intensities corresponding to each. Approximately 80% of the parent microstructure twins by 8% compression. Elastic lattice strain measurements indicate that the stress in the newly formed twins (daughters) is relaxed relative to the stress field in the surrounding matrix. However, since the daughters are in a plastically 'hard' deformation orientation, they quickly accumulate elastic strain as surrounding grains deform plastically. Polycrystal modeling of the deformation process provides insight about the crystallographic deformation mechanism involved.

Energy Technology Data Exchange (ETDEWEB)

Three model boilers, manufactured to simulate full-size tube sheet crevices, were tested with various secondary side environments. The first was faulted with organics representative of the decomposition of humic acid. The second was faulted with sodium carbonate and sodium hydroxide, while the third was faulted with sodium sulfate and sodium hydroxide. Each model contained seven tubes, which included Alloy 600 in the mill-annealed (MA) and thermally-treated (TT) conditions and Alloy 690 in the thermally-treated condition. Two models contained Alloy 800 tubes in the mill-annealed condition and one had Alloy 800 in the mill-annealed/cold-worked/glass-bead-peened condition. Two different sizes of tubesheet crevices were used in all model boilers. In the organics-faulted boiler, tubes of Alloy 600MA, Alloy 690TT and Alloy 800MA experienced no ...

International Nuclear Information System (INIS)

The methods of surface modification of Ti-Zr alloy by laser treatment are considered. Characteristics of laser modification without- and with surface melting and with melting in different gaseous environments and with nickel microalloying are presented. Maximum depth, hardness and corrosion resistance are observed under nickel laser alloying.

Energy Technology Data Exchange (ETDEWEB)

Laser surface alloying with gaseous nitrogen was utilized to improve the wear resistance of a Ti-6Al-4V alloy. Wear-resistant composite coatings reinforced by hard TiN dendrites were produced 'in-situ' on a substrate of a Ti-6Al-4V alloy. The hardness and wear resistance of the laser alloyed coating under two-body abrasive and block-on-ring full-sliding wear conditions were significantly enhanced. (orig.)

International Nuclear Information System (INIS)

Corrosion testings of model alloys, corresponding by chemical composition to simple and complex-alloyed #gamma#- and #gamma#'-phases of nickel heat-resistant alloys are conducted in sodium sulfate and chloride melts. It is ascertained that heat resistant nickel alloys containing over 50 % of hardening #gamma#'-phase, are subject to disastrous sulfide corrosion (SC). Resistance against SC alloys containing below 50 % of #gamma#'-phase is determined by the resistance of #gamma#-solid solution. 10 refs., 3 figs., 2 tabs.

Science.gov (United States)

... Accession Number : ADD109273. Title : THERMAL STABILITY OF ALPHA-BETA TITANIUM ALLOY Ti-5Al-2Cr-1Fe,. Corporate Author : ...

Science.gov (United States)

... by the boron doping in most of the alloys except for Al66Mn9Zr25 + 50 ppm B alloy; permanent deformation at ultimate compressive strength is not ...

International Nuclear Information System (INIS)

The nickel-rich superalloys Alloy 600 and Alloy 800 have been corroded in mildly alkaline deuterated aqueous conditions typical of secondary coolant circuits in a nuclear power station. The oxide films and substrates of these alloys have been analysed by imaging SIMS depth profiling, which makes it possible to describe elemental distribution in all three dimensions. The measurement of the distribution of the secondary ions NiO"-, FeO"- and CrO"- appears useful for detailing the behaviour of nickel, iron and chromium within oxidized phases. The measurement of D"- distribution outlines the extent of oxide hydration. For Alloy 800, evidence of sodium migration into the grain boundaries of the alloy substrate is found. For Alloy 600, no grain boundary sodium ingress can be identified under comparable corrosion conditions. (author).

Energy Technology Data Exchange (ETDEWEB)

Four low activation alloy classes, two austenitic and two ferritic, have been incorporated into the MOTA-1B experiment in the FFTF reactor to provide an early assessment of the suitability of such alloys for reactor service.

International Nuclear Information System (INIS)

The effect of various hydrogen concentrations on the crystal lattice period and the hardness of titanium alloy was examined, the alloy containing about 16 at.% Mo (27.5 wt. % Mo) and having #beta# structure. The peculiar features of the mechanism of plastic deformation of the alloy were studied after adding hydrogen to it. A dependence of the crystal lattice period on the concentration of hydrogen was obtained for TixMoxH_2 alloy. It has been established that the hardness of the Ti-Mo alloy does not change when hydrogen is added to it. The presence of hydrogen introduces changes into the mechanism of deformation of #beta#-titanium alloy. The configuration of the inverse pole figures after rolling proves that the transverse slip process in an alloy with hydrogen is hampered, and that the coplanar slip process is developing in it.

Science.gov (United States)

... CLOSURE DURING HOT WORKING OF AN ALPHA/BETA TITANIUM ALLOY (PREPRINT) ... HOT WORKING OF AN ALPHA/BETA TITANIUM ALLOY ...

Science.gov (United States)

... Accession Number : ADD336001. Title : Development of a FeCoNb Alloy to be used in Eddy Current Probes for Testing Ferromagnetic Tubes,. ...

Science.gov (United States)

... Title : DUCTILITY RATIO OF AGED BETA TITANIUM ALLOY. Corporate Author : NEW YORK UNIV NY SCHOOL OF ENGINEERING AND SCIENCE. ...

International Nuclear Information System (INIS)

Stemming from their unique combination of elevated strength, low density, and good overall corrosion resistance, beta titanium alloys have become attractive candidate materials for critical, high-stress, components in corrosive services. An overview of the comparative corrosion resistance of beta alloys to conventional alpha and alpha/beta titanium alloys in common industrial and aerospace service environments generally reveals attractive behavior depending on the environment and alloy composition and, in some cases, alloy condition. Expanded performance windows are especially noted for the molybdenum-rich beta alloys, particularly in regard to resisting reducing acids, stress corrosion, and high temperature localized chloride attack, along with hydrogen and oxidation resistance. Where applicable, implications of this enhanced corrosion performance on current ...

International Nuclear Information System (INIS)

Intracranial atherosclerosis is a major cause of ischemic stroke, and depending on the studied population, it accounts for 8%-15% of all strokes that are due to cerebral atherosclerosis. The prognosis of patients with symptomatic intracranial stenoses seems to depend on the location and extent of intracranial atherosclerosis. Currently, the primary treatment in intracranial atherosclerosis is the control of vascular risk factors such as hypertension, diabetes, hypercholesterolemia, and smoking. Secondary prevention with antiplatelet therapy has been shown to reduce the risk of subsequent vascular events in patients who have suffered a recent ischemic stroke or transient ischemic attack (TIA). Unfortunately, a significant number of patients with intracranial atherosclerosis continue to suffer from repeated strokes or TIA despite maximal medical treatment. Although endovascular revascularization for symptomatic intracranial stenoses remains at the investigational stage and much of the ...

International Nuclear Information System (INIS)

Basic studies of the oxidation resistance of Fe-Cr binary and Fe-Cr-Ni ternary alloys in pure oxygen have shown that the excellent corrosion resistance of Alloy 800 is explicable in terms of the low defect concentrations and diffusion rates in the oxide forming on alloys of this composition in sufficiently oxidising environments. The performance of Alloy 800 in environments of particular importance to nuclear power generation is briefly reviewed to determine to what extent ideas derived from the basic studies of Fe-Cr-Ni ternary alloys are borne out in practice. The good corrosion resistance of Alloy 800 in steam and CO_2 and, to some extent, in molten salt environments is in agreement with the behaviour of ternary alloys in oxygen. Minor aliovalent alloying additions are only expected to have a significant effect on the ...

International Nuclear Information System (INIS)

At 650"0C, the low-cycle fatigue life was essentially the same for the two alloys on the basis of strain amplitude, but Alloy 800H had a longer life on the basis of stress amplitude. A 500"0C, Alloy 800 and 800H exhibited longer fatigue lifetime than at 650"0C, with Alloy 800 exhibiting a 2-3 times longer life than Alloy 800H when compared on the basis of plastic strain range, whereas the difference was less pronounced when compared on the basis of stress amplitude. When a creep effect was introduced either by way of a hold time or a reduced frequency, Alloy 800 exhibited a greater reduction in life than did Alloy 800H. The dislocation structure changed from planar to cellular with increase in strain range, and extensive precipitation of M_2_3C_6 was noted within the grains for Alloy 800H and along grain boundaries for ...

UK PubMed Central (United Kingdom)

Vacuolar ion channels in guard cells play important roles during stomatal movement and are regulated by many factors including Ca²⁺, calmodulin, protein kinases, and phosphatases....Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Nutrient elements contained in litter fall flux, that of uptake flux and turnover rate had generally tended to increase with the increase in the Warmth Index, while the amount of nutrient in the A[sub 0] horizon and nutrient use efficiency did not. However, it is suggested that topographic and climatic aridity, and the amount of available and exchangeable phosphorus, calcium and magnesium greatly affect the nutrient dynamics in a each forest ecosystem as the Warmth Index increases. (J.P.N.).

International Nuclear Information System (INIS)

In-reactor testing of bolt-loaded compact tension specimens was performed in 360 C water to determine the irradiation-assisted stress corrosion cracking (IASCC) behavior of HTH Alloy X-750 and direct-aged Alloy 625. New data confirm previous results showing that high irradiation levels reduce SCC resistance in Alloy X-750. Heat-to-heat variability correlates with boron content, with low boron heats showing improved IASCC properties. Alloy 625 is resistant to IASCC, as no cracking was observed in any Alloy 625 specimens. Microstructural, microchemical and deformation studies were performed to characterize the mechanisms responsible for IASCC in Alloy X-750 and the lack of an effect in Alloy 625. The mechanisms under investigation are: boron transmutation effects, radiation-induced changes in microstructure and deformation characteristics, and ...

Energy Technology Data Exchange (ETDEWEB)

To clarify the acidic and alkaline Intergranular Stress Corrosion Cracking (IGSCC) mechanism of thermally treated alloy 690 (alloy 690 TT) and shot peened alloy 800 (alloy 800 SP), C-ring tests were conducted in deaerated HCl solutions and in deaerated NaOH solutions at 350degC, compared with the acidic and the alkaline IGSCC susceptibilities of mill-annealed alloy 600 (alloy 600 MA), full-sensitized one (alloy 600 FS) and thermally treated one (alloy 600 TT). Grain boundary characteristics, such as chromium depleted zone and chromium carbide precipitation, were examined using modified Huey test and Transmission Electron Microscopy. Potential-pH diagram for Ni, Cr, Fe-H{sub 2}O system at 350degC was constructed and the solubilities of NiO, Cr{sub 2}O{sub 3} and Fe{sub 3}O{sub 4} were also calculated to evaluate the ...

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

The investigations carried out on Alloy 800 in aqueous high-temperature environments in France as well as in other countries are reviewed. These studies are mainly concerned with nuclear industry where Alloy 800 can be used as structural material for steam generators of PWR, breeders or HTR. As results referred to in the literature on cracking in caustic environmens do not always agree, a discussion is presented on the matter. The behaviour of Alloy 800 in superheated steam is examined. (Auth.).

International Nuclear Information System (INIS)

(Nov 1973). United States Greenfield, MA Pierce, CM Chicago, IL.

KoreaScience (Korea)

Full Text Available

International Science & Technology Center (ISTC)

Investigation of Destruction Mechanisms in Reactor Steels and Alloys under Cycling Deformation

Energy Technology Data Exchange (ETDEWEB)

Short communication. 6 refs., 2 figs.

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

This paper describes a process for the direct production of a superconductive niobium-titanium alloy during reduction of niobium pentoxide. It comprises: mixing at least one of titanium metal powder and titanium dioxide powder with niobium pentoxide powder and aluminum powder; heating the resulting mixture to form a niobium-titanium alloy and a slag consisting essentially of aluminum oxide; and separating the alloy and the slag.

International Nuclear Information System (INIS)

In this paper a study is made of the structure and mechanical properties of the #beta# alloy system Ti-Mo-Zr-Sn (the composition of which is equivalent to the #beta# III alloy used abroad) containing different amounts of carbon. Study of the #beta#-titanium alloy containing 0.1% C revealed the presence of particles of titanium carbide. Separation of the titanium carbide promotes a reduction in impact strength, an increased tendency toward cold shortness, and poorer workability. (author).

International Nuclear Information System (INIS)

A new high strength titanium alloy has been developed primarily intended for fastener applications. While Ti-6Al-4V is used extensively as a fastener alloy in the aerospace industry, its shear strength allowable is limited to 655 MPa (95 ksi). For higher shear strength requirements, various steels or nickel-based alloys are used (up to 860 MPa (125 ksi)), but with the attendant density penalty. This new alloy is intended to provide the 860 MPa shear strength at roughly a 40% weight savings. After screening various alloy systems, the optimum chemistry has been selected as follows: Ti-6.0V-6.2Mo-5.7Fe-3Al. In light of its 125 ksi shear strength goal, the alloy has been designated TIMETAL reg-sign 125.

Energy Technology Data Exchange (ETDEWEB)

In a work studying the corrosion and tarnishing properties of a variety of copper alloys, the alloy Cu-A110-Sn5 was found to show an excellent corrosion resistance in neutral solutions, where copper and most conventional Cu alloys are covered by thick nonprotective surface layers. The passive films formed on this alloy were characterized with electrochemical and photoelectrochemical methods. The pH dependence of the passivation and of the photocurrent behavior of the Cu-A110-Sn5 alloy clearly indicates that the passivity of this alloy in neutral solutions is due to a formation of passive film enriched with aluminum oxide. At corrosion potential a strong increase in the corrosion resistance with time is due to a gradual enrichment of the surface with aluminum oxide. This can be seen in the photocurrent spectra which change from cooper-type to aluminum-type with ...

Energy Technology Data Exchange (ETDEWEB)

It is hypothesized that the good performance of Alloy 800 in steam generator service is due to its relative immunity to two distinct mechanisms of stress corrosion cracking; the argument also applies to intergranular corrosion. One mechanism operates in the high-nickel region (Alloy 600 and nearby model alloys) and is due to internal intergranular oxidation. The other operates in the low-nickel (stainless steel) region and is due to de-alloying of Fe and/or Cr. This latter mechanism may, under special conditions, operate in high-Ni, high-Cr alloys such as 690. Some essential features of the de-alloying mechanism are demonstrated using strong caustic solutions, and the prospect of extending this approach to dilute high-temperature environments is discussed. (author)

International Nuclear Information System (INIS)

Zirconium-base alloys are used primarily as fuel cladding material and other core structure material in water cooled nuclear power reactors. Main research achievements and problems about corrosion of zirconium alloys are reviewed; the present theories and challenge are summarized. In the 1980s, great progress had been made towards correlating alloy composition, microstructure and irradiation with corrosion resistance. In the 1990s, main researches are focused on exploring actual mechanism of corrosion, optimizing both alloy composition and microstructure in order to minimize the fuel cycle costs through burnup optimization.

International Nuclear Information System (INIS)

SP-700, an emerging #beta#-rich #alpha#+#beta# titanium alloy, is designed to improve superplastic formability as well as mechanical properties over Ti-6Al-4V alloy. Owing to its fine microstructure and low #beta#-transus temperature, it is superplastic-formable at temperature below 1,073K (800 C) with low flow stress. Remarkable workability of this alloy is also retained in conventional Manufacturing processes. Another advantage of SP-700 is heat treatment response which includes deep hardenability and quick aging kinetics. Corrosion resistance and machinability are equivalent to or better than Ti-6Al-4V alloy.