Stability of A-15 compounds in multifilamentary superconducting wires  

International Nuclear Information System (INIS)

With the preeminence of A-15 superconducting multifilamentary wires in magnet technology, it has become important to understand the thermodynamic factors influencing the formation of these compounds under solid-state reaction conditions. The six systems Nb--Sn, Nb--Ga, Nb--Ge, Nb--Al, V--Si, and V--Ga were prepared as single filament bronze wires and heat treated in an attempt to precipitate the appropriate A-15 compound. The compounds observed to form were categorized using a formation temperature ratio (stability index) based on the melting temperatures of the constituents which make up the single filament composites. This study has led to several predictions regarding the formation of A-15 compounds using a solid-state bronze diffusion technique. The results of experimentation based on these predictions are presented.

2

A15 superconductors through direct solid-state precipitation: V/sub 3/Ga and Nb/sub 3/Al  

Energy Technology Data Exchange (ETDEWEB)

A solid-state precipitation process was used to prepare superconducting tapes containing an A15 phase, V/sub 3/Ga or Nb/sub 3/Al, in a ductile niobium or vanadium containing BCC matrix. Ingots weighing as large as 30 to 50 gms of V-(14 approx. 19 at. %) Ga and Nb-(13 approx. 22 at. %) Al were prepared by arc-melting, homogenized, quenched, warm-rolled over 99% into tape, and aged at temperatures in the range 600/sup 0/C to 1000/sup 0/C to precipitate the superconducting A15 phase. The features demonstrated by the process are very attractive for practical applications. In the V-Ga system, transmission electron microscopy (TEM) studies revealed the A15 precipitates in an elongated form. However, for the Nb-Al samples, deformed and aged at 750/sup 0/C, TEM studies revealed A15 precipitation in fine equi-axed particles which formed as a semi-continuous network over sub-grain boundaries formed by the recovery of deformation-induced dislocations. In the ...

1980-09-01