International Nuclear Information System (INIS)

Dysprosium ion doped fluorophosphate glasses with compositions of PKMAFDy: (56-x/2) P2O5+17K2O+8Al2O3+(15-x/2)MgO+4AlF3+xDy2O3 (x=0.01, 0.05, 0.1, 1.0 and 2.0 mol%) have been prepared by melt quenching technique and are characterized by optical absorption, emission spectra and fluorescence lifetime measurements. The observed bands in the absorption spectrum are analysed by using free-ion Hamiltonian (HFI) model. The Judd-Ofelt (JO) analysis has been performed and the intensity parameters (??, ?=2, 4, 6) have been evaluated that are used to predict radiative properties. From emission spectra, the effective bandwidth (??eff) and the stimulated emission cross-section (?(?p)) were evaluated. The fluorescence decay from the 4F9/2 level of Dy3+ ions have been measured by monitoring the intense 4F9/2#->#6H13/2 transition ...

International Nuclear Information System (INIS)

We present the effect of P2O5 addition on barium calcium aluminum borosilicate BCABS glasses of composition (mol %) 35BaO-15CaO-5Al2O3-(37-x)SiO2-8B2O3-xP2O5 (0?x?5). The incorporation of P2O5 increased network polymerization and crystallization tendency. However, addition of P2O5 leads to the formation of Cr2O3 at the interface, saturating it in the ions of the metal. This improves glass-to-metal bonding. (author)

International Nuclear Information System (INIS)

The formation of a porous coating is the decisive feature for the bio-compatibility of silica-free calcium phosphate glass ceramics on alloy surfaces like the #beta#-Ti structured Ti-29Nb-13Ta-4.6Zr used in this work. The ceramic composition is highly important: 50CaO-40P_2O_5-7Na_2O-3TiO_2 glass powder produces a pore-free coating unable to bind hydroxyapatite, whereas 60CaO-30P_2O_5-7Na_2O-3TiO_2 glass incorporates pores from which a crystalline hydroxyapatite phase can grow over the surface from simulated body fluid (see Figure). (Abstract Copyright [2003], Wiley Periodicals, Inc.)

British Library Electronic Table of Contents (United Kingdom)

The glasses with the composition of 37.5Li2O?(25?x)Fe2O3?xNb2O5?37.5P2O5 (mol%) (x=5,10,15) are prepared, and it is found that the addition of Nb2O5 is effective for the glass formation in the lithium iron phosphate system. The glass?ceramics consisting of Nasicon-type Li3Fe2(PO4)3 crystals with an orthorhombic structure are developed through conventional crystallization in an electric furnace, showing electrical conductivities of 3?10?6?Scm?1 at room temperature and the activation energies of 0.48?eV (x=5) and 0.51?eV (x=10) for Li+ ion conduction in the temperature range of 30?200??C. A continuous wave Nd:YAG laser (wavelength: 1064?nm) with powers of 0.14?0.30?W and a scanning speed of 10??m/s is irradiated onto the surface of the glasses, and the formation of Li3Fe2(PO4)3 crystals is c...

Energy Technology Data Exchange (ETDEWEB)

The aim of our research was to identify structures and chemical compositions of phases formed during internal oxidation of multi-component Ag-Zn-Mg-based alloys. Since the ability of inoculation mostly depends on large free energy of formation of oxides of microalloying elements and their crystallographic similarity, Mg in quantities of 0.001-0.5 mass% was selected as a micro-alloying element. These correspond to the quantities of 0.005-2.5 vol.% of MgO in the selected Ag-Zn-based alloys. Ag-based metal matrix, heterogeneous nuclei of MgO and oxide (ZnO) of the main alloying element were analysed by transmission electron microscopy (TEM). Structural inter-connections among them were also investigated and analysed. In situ phenomenon of heterogeneous nucleation of MgO and ZnO was proved. (orig.)

International Nuclear Information System (INIS)

YBa_2Cu_3O_7_-_x thick films have been deposited on silver sheets and MgO single crystals by spray pyrolysis. Film texture is related to film thickness and sintering temperature. The X-ray intensity ratio of the 005 peak to the 110 peak is higher for thin films deposited at the higher temperatures. However, elevated temperatures promote copper diffusion and second-phase formation in films deposited on silver. Films deposited on MgO can have larger grain sizes and are more oriented than those deposited on silver.

Energy Technology Data Exchange (ETDEWEB)

FT-IR spectroscopic studies of the adsorption of natural and {sup 18}O-enriched NO gases on thermally and cleaned MgO powders were carried out. The temperature dependence of the IR spectra was investigated to characterize the adsorbate species. Three types [1, 2, and 3] of NO adsorptions were obtained in the wavenumber region of 1500--1000 cm{sup {minus}1}. Those types were examined using density functional theory [(U)B3-LYP/6-31G*] vibrational analyses of (MgO){sub n}-NO cluster calculations. Types 1, 2, and 3 were assigned to monodentate, asymmetric, and symmetric bidentate geometries, respectively. A type 4, a tridentate model which involves a NO{sub 3}-like species, was calculated and was found to give wavenumbers of less than 1,000 cm{sup {minus}1}. The splitting of IR bands of type 3 due to the {sup 15}N{sup 18}O adsorbate was ascribed to the oxygen exchange, {sup 15}N{sup 18}O {yields} {sup 15}N{sup 16}O, via the reaction {sup 16}O-{sup 15}N-{sup 18}O ...

Energy Technology Data Exchange (ETDEWEB)

A focused ion beam (FIB) system has been applied to prepare a thin foil specimen of Si, MgO and alumina which contained cracks in the plan of foil. It was possible to observe a much larger area at and near a crack tip than has been hitherto possible. FIB was also applied to observation of microstructure near a crack tip evolved during severe rolling contact fatigue in a steel.

International Nuclear Information System (INIS)

The effect is reported of seven inorganic oxide additives on both the formation mechanism and the densification of X-Sialon prepared by a silicothermal process. The oxides were added to the starting mixture of halloysite clay, alumina and elemental silicon at a level of 1 wt% of the calculated final product, and fired in nitrogen at 1200-1500 deg C. The formation of X-Sialon was monitored by thermal analysis, powder XRD and 2"7"Al and "2"9Si solid state MAS NMR The effects of the additives are temperature dependent and influence the various stages of the reaction by differing degrees. The oxides which best promote the formation of crystalline X-Sialon (Y_2O_3, CaO and MgO) are also those which facilitate the conversion of initially-formed Si_3N_4 to SiO_2N_2 and SiO_3N units. Densification is most enhanced by Y_2O_3 CaO and CeO_2; MgO exerts its maximum effect on sintering at lower temperatures. Copyright (1998) Australasian Ceramic Society

Energy Technology Data Exchange (ETDEWEB)

The deformation characteristics of pellets of electrolyte-binder (EB) mixes based on MgO were measured under simulated, thermal-battery conditions. Measurements (using a statistically designed experimental strategy) were made as a function of applied pressure, temperature, and percentage of theoretical density for four molten-salt electrolytes at two levels of MgO. The EB mixes are used as separators in Li-alloy thermal batteries. The electrolytes included LiCl-KCI eutectic, LiCl-LiBr-KBr eutectic, LiBr-KBr-LiF eutectic, and a LiCl-LiBr-LiF electrolyte with a minimum-melting composition. The melting points ranged from 313 C to 436 C. The experimental data were used to develop statistical models that approximate the deformation behavior of pellets of the various EB mixes over the range of experimental conditions we examined. This report, discusses the importance of the deformation response surfaces to thermal-battery design.

International Nuclear Information System (INIS)

A complete electron paramagnetic resonance power pattern characterization of Fe"3"+ in cubic sites in presented. A one-to-one correspondence among the peaks appearing in the powder pattern and the outer fine-structure transitions (Mnot = 1/2 ) observed in the single crystal along the , , and directions is shown. It is shown that the process of mechanically grinding the single crystal to a powder (particle size approx.1--10 #mu#) does not remove the cubic symmetry sites. No axial or lower symmetry sites which may be induced by lattice distortion of the crystallites due to strain have been observed.

Energy Technology Data Exchange (ETDEWEB)

The quantitative determination of oxide concentration by laser-induced breakdown spectroscopy is relevant in various fields of applications (e.g.: analysis of ores, concrete, slag). Calibration free laser-induced breakdown spectroscopy and the multivariate calibration are among the methods employed for quantitative concentration analysis of complex materials. We measured the intensity of neutral and ionized atomic emission lines of oxide materials by laser-induced breakdown spectroscopy and we modified the calibration free laser-induced breakdown spectroscopy method to increase the accuracy. The concentration of oxides was obtained by using stoichiometric relations. Sample materials were prepared from oxide powder (Fe{sub 2}O{sub 3}, MgO, CaO) by mixing and pressing. The concentration was 9.8-33.3 wt.% Fe{sub 2}O{sub 3}, 7.6-33.3 wt.% MgO and 33.3-81.2 wt.% CaO for different samples. Nd:YAG laser (wavelength 1064 nm, pulse duration {approx} 6 ...

International Nuclear Information System (INIS)

This paper provides a brief overview of the young, but rapidly growing field of spintronics. Its primary objective is to explain how as electrons tunnel through simple insulators such as MgO, wavefunctions of certain symmetries are preferentially transmitted. This symmetry filtering property can be converted into a spin-filtering property if the insulator is joined epitaxially to a ferromagnetic electrode with the same two-dimensional symmetry parallel to the interface. A second requirement of the ferromagnetic electrodes is that a wavefunction with the preferred symmetry exists in one of the two spin channels but not in the other. These requirements are satisfied for electrons traveling perpendicular to the interface for Fe-MgO-Fe tunnel barriers. This leads to a large change in the resistance when the magnetic moment of one of the electrodes is rotated relative to those of the other electrode. This large tunneling magnetoresistance effect is being used as the ...

Energy Technology Data Exchange (ETDEWEB)

The use of selective additives such as MgO as a sintering aid and a rare earth oxide as a grain growth inhibitor, has allowed the manufacture of beryllia ceramics having close to theoretical density. The grain size and grain size distribution can be controlled by an optimum firing schedule leaving a remnant porosity which is extremely fine (0.2 {mu}m). This structure is compared with conventional BeO ceramics, densified by liquid phase sintering, which develops a glassy grain boundary and retains large pores up to 3 {mu}m. The significantly improved strength properties, extremely fine pores,the 'pinning effect' of rare earth oxide, and the superior surface finish both in the as-fired and polished state are discussed in relation to the micro-structure. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The influence of (%MgO) and (%T.Fe) in slug on the corrosion resistance of Al{sub 2}O{sub 3}-C brick was studied at 1,550-1,800{degree}C to apply it to the post combustion zone of an in-bath smelting reduction furnace. The wear rate of the brick was affected strongly by temperature decreasing to 1 2-2 3 for every temperature reduction of 100{degree}C, and it was also more affected by (%T.Fe) than (%MgO) in slug at every temperature. The observation of brick microstructures by reflecting microscopy revealed the preceding wear of a carbon matrix. Based on the consideration that the growth of degraded structures by decarburization also contributes to movement of Al{sub 2}O{sub 3} clinkers, the wear rate equation of the Al{sub 2}O{sub 3}-C brick was derived taking into account not only elution of Al{sub 2}O{sub 3} clinkers into slug but oxidation and decarburization of the carbon matrix in oxidation atmosphere at high temperature, resulting in the ...

Energy Technology Data Exchange (ETDEWEB)

The durability of ball bearings, 32-mm- and 45-mm-bore, with a retainer or glass cloth-polytetrafluoroethylene (PTFE) laminate was tested under a high radial load at a speed of 20,000 rpm in LOX or LN2. The retainers were characterized as good self-lubricators because the abrasive glass-cloth fiber tips exposed on the retainer were chemicaly etched away with hydrofluoric acid (HF). During testing, the bearing-cartridge-acceleration was monitored to detect bearing damage. Testing in LOX for about 2.2 hr showed that excellent lubricating conditions were obtained for all bearings. Testing in LN2 for about 5.1 hr detected that the fatigue life of the bearing was about the same as the calculated B10 fatigue life. The HF chemical treatment resulted in a reacted fluoride-oxide material which remained in the etched part of the glass fiber. Several chemical products, particularly MgO, CaO, and CaCO3, enhanced adhesion of PTFE transfer film to the counterface, resulting in ...

International Nuclear Information System (INIS)

Zinc oxide thin films were obtained by laser ablation of a Zn target in oxygen reactive atmosphere, the oxygen being supplied either by a standard gas inlet valve or from a radio-frequency (rf) oxygen plasma. Pt-coated silicon and MgO were used as substrates. The influence of the deposition parameters as laser wavelength (266, 355, 1064 nm), laser fluence (1.5-20 J/cm2) and oxygen pressure (1-60 Pa) was studied. The influence of the rf plasma beam addition on the morphological proprieties of zinc oxide films was particularly investigated, simultaneously with several configurations of the direction of the ablation plasma, the rf plasma beam and the substrate. The obtained films, with thicknesses in the range of 50 nm to 1 ?m have been characterized by atomic force microscopy (AFM), X-ray diffraction (XRD), transmission electron microscopy (TEM).

Energy Technology Data Exchange (ETDEWEB)

A room-temperature process for stabilizing mineral waste streams has been developed, based on acid-base reaction between MgO and H3PO4 or acid phosphate solution. The resulting waste form sets into a hard ceramic in a few hours. In this way, various alumina industry wastes, such as red mud and treated potliner waste, can be solidified into ceramics which can be used as structural materials in waste management and construction industry. Red mud ceramics made by this process were low-porosity materials ({approx}2 vol%) with a compression strength equal to portland cement concrete (4944 psi). Bonding mechanism appears to be result of reactions of boehmite, goethite, and bayerite with the acid solution, and also encapsulation of red mud particles in Mg phosphate matrix. Possible applications include liners for ponds and thickned tailings disposal, dikes for waste ponds, and grouts. Compatability problems arising at the interface of the liner and the waste are avoided.

Energy Technology Data Exchange (ETDEWEB)

The work in the past year has primarily involved four areas of magnetic thin films: amorphous rare earth-transition metal alloys, epitaxial CoPt{sub 3} and Ni-Pt alloy thin films, amorphous rare earth doped Si (a new class of dilute magnetic semiconductor with large negative magnetoresistance which the authors have discovered), and exchange-coupled antiferromagnetic insulators. In the amorphous alloys, they made a systematic study of the effects of local anisotropy, macroscopic (perpendicular) anisotropy, and exchange constant on the fundamental (and practical) properties of these magnetic alloys, as originally described in the grant proposal. The work on the epitaxial Co-Pt (and more recently Ni-Pt) alloys was originally undertaken as a comparison study to the amorphous alloys. Crystalline Co-Pt alloys have many striking similarities to the amorphous rare earth-transition metal alloys: perpendicular magnetic anisotropy, magneto-optic activity, and a {Tc} (for CoPt{sub 3}) somewhat ...

Science.gov (United States)

High quality La/sub 1.8/Sr/sub 0.2/CuO/sub 4/ and YBa/sub 2/Cu/sub 3/O/sub 7/ superconducting thin films, with zero resistance at 88 K, have been made by dual-ion-beam sputtering of metal and oxide targets at elevated temperatures. The films are about 1.0 ..mu..m thick and are single phase after annealing. The substrates investigated are Nd-YAP, MgO, SrF/sub 2/, Si, CaF/sub 2/, ZrO/sub 2/-9% Y/sub 2/O/sub 3/, BaF/sub 2/, Al/sub 2/O/sub 3/, and SrTiO/sub 3/. Characterization of the films was carried out using Rutherford backscattering spectroscopy, resistivity measurements, transmission electron microscopy, x-ray diffraction, and secondary ion mass spectroscopy. Substrate/film interaction was observed in every case. This generally involves diffusion of the substrate into the film, which is accompanied by, for example, the replacement of Ba by Sr in the YBa/sub 2/Cu/sub 2/O/sub 7/ structure, in the case of SrTiO/sub 3/ substrate. The best substrates were those that ...

International Nuclear Information System (INIS)

Several Mg-Y binary ribbons with Y content up to #approx#17.9 at.% were fabricated by melt-spinning. X-ray diffraction (XRD) revealed that the phase structure changes with increasing Y content from extended solid solution to partially amorphous, and then fully intermetallic Mg_2_4Y_5. Anodic potentiodynamic polarization performed in 0.01 M NaCl electrolyte (pH=12) revealed improved anodic passivity behavior compared to pure Mg for all the Mg-Y alloys. X-ray photoelectron spectroscopy (XPS) revealed that the improved passivity of Mg-Y was more related to the elemental oxidation state rather than the concentration of the surface components. To study the effect of Cl"- ion on the passivity behavior, anodic potentiodynamic and potentiostatic polarization were performed on Mg-17.9 at.% Y in alkaline (pH=12) NaCl electrolytes containing Cl"- ion in the concentration range from 0.00 to 0.50 M. The passive films formed in 0.01 M NaCl electrolyte were similar to the native film, which were ...

International Nuclear Information System (INIS)

The effects of catalytic metal additives on the hydrogen desorption properties of the submicrocrystalline magnesium hydride (#beta#-MgH_2) formed after hydrogenation of the Mg + 10 wt.%X (X = V, Y, Zr) mechanically (ball) milled composites were studied. The composites with catalytic metals were processed by controlled mechanical milling (CMM) in the magneto-mill Uni Ball Mill 5 under protective Ar atmosphere. X-ray diffraction of the milled powders revealed the formation of Mg nanograins (50-60 nm range) interdispersed with the nanograined metal additives within the powder particles. Scanning electron microscopy showed particle size reduction after milling. After activation and hydrogenation in a Sieverts-type apparatus under about 2 MPa pressure of hydrogen, the tetragonal #beta#-MgH_2 hydride co-exists with the small amount of retained unreacted Mg phase and the small amount of MgO in all three composites. The #beta#-MgH_2 phase after hydrogenation is ...

Energy Technology Data Exchange (ETDEWEB)

Polycrystalline Al2O3, magnesium aluminate spinel (MgAl2O4), MgO, Si3N4, and SiC were irradiated with various ions at 200-450 K, and microstructures were examined following irradiation using cross-section TEM. Amorphization was not observed in any of the irradiated oxide ceramics, despsite damage energy densities up to {similar_to}7 keV/atom (70 displacements per atom). On the other hand, SiC readily amorphized after damage levels of {similar_to}0.4 dpa at room temperature (RT). Si3N4 exhibited intermediate behavior; irradiation with Fe{sup 2+} ions at RT produced amorphization in the implanted ion region after damage levels of {similar_to}1 dpa. However, irradiated regions outside the implanted ion region did not amorphize even after damage levels > 5 dpa. The amorphous layer in the Fe-implanted region of Si3N4 did not appear if the specimen was simultaneoulsy irradiated with 1-MeV He{sup +} ions at RT. By comparison with published results, it is concluded that ...

Energy Technology Data Exchange (ETDEWEB)

The use of standard cementitious material creates pulses of pH in the magnitude of 12-13 in the leachates and release alkalis. Such a high pH is detrimental and also unnecessarily complicates the safety analysis of the repository. As no reliable pH-plume models exist, the use of products giving a pH below 11 in the leachates facilitates the safety analysis. Also, according to current understanding, the use of low-pH cement (pH = 11) will not disturb the functioning of the bentonite, although limiting the amount of low-pH cement is recommended. A result of the project is that there are both low-pH cementitious material for grouting larger fractures (= 100 {mu}m) and non-cementitious material for grouting smaller fractures (< 100 {mu}m) that will, after further optimisation work, be recommended for grouting of deep repositories. This project concentrated on the technical development of properties for the low pH grouts. Long-term safety and environmental aspects and durability of ...