The dual characteristics in the performance of polymers in wood-polymer composites systems have been pursued with regard to the resolution of mechanical anisotropy of wood and the improvement in dimensional stability. The objective of the present study is to pursue the polymerization mechanism in wood under electron beam irradiation and the temperature dependence of polymer-wood interactions induced at various levels of higher order structure of wood in order to understand the polymer performance. Veneers used in the study were of rotary-cut beech (Fagus crenata Blume) 0.65 mm thick. All samples were oven-dried in vacuo at 80/sup 0/C for 30 hr. The monomers used in the study were methyl methacrylate, styrene, acrylic acid, acrylonitrile, and unsaturated polyester. Experimental details are given. Results are given and discussed.