International Nuclear Information System (INIS)

Plasma nitriding is a powerful technique for modifying the phase-structure of the material surface layers, which affect the mechanical, physical and chemical properties of material. The effect of plasma nitriding on the surface properties of three types of steel (low carbon, AISI-304 and H13 (hardened)) has been investigated. The steel samples were plasma nitrided in vacuum of 10"-"1Pa with gas mixture of (N_2, H_2) at 530 Centigrade degree for a duration of 14 hours. Vickers microhardness measurements and XRD phase analysis of the treated and untreated samples were carried out. The diffraction patterns of treated steels revealed that new phases of #gamma#-Fe_4N, #epsilon#-Fe_3N and (Fe,Cr)_2N were formed. The maximum treated depths were about 5, 6 and 45 #mu#m for low carbon, AISI-304 and H13 (hardened) nitrided steel respectively. The microhardness was ...

Energy Technology Data Exchange (ETDEWEB)

Hard surface finishing represents the final manufacturing step for functional areas of machine elements in state-of-the-art production. Raceways of rolling bearing rings are ground and honed to the required low roughness. Plastic deformation is restricted to a narrow edge zone of the hardened steel. Reheating of the machined components below the martensite tempering or bainite transformation temperature results in a marked decrease of the XRD line width on the surface. The investigated samples are made of through-hardened standard bearing steel 100Cr6 (international denotation: SAE 52100). On the basis of a material model that explains the effect as a complex diffusion process of dislocational carbon segregation, i.e. static strain aging, the measured kinetics of the XRD line width reduction is simulated by an Arrhenius-type equation, which describes the rate-controlling reaction step of temper carbide dissolution. The ...

Energy Technology Data Exchange (ETDEWEB)

The influence of a decarburisation process during austenitising of the through-hardenable rolling bearing steel 100Cr6 (SAE 52100) on the rim zone properties of the martensitic through-hardened material was investigated by means of material analysis and diffusion calculations. For this purpose, two specimens were prepared under defined heat treatment conditions, and the near-surface carbon distribution was determined micro-chemically by using secondary ion mass spectrometry (SIMS). In part 1 of the present work, these concentration profiles are compared with the depth variation of the micro-hardness and with the distance curves of the residual stresses and the line broadening ({l_brace}211{r_brace} {alpha}'-Fe diffraction line) both measured by X-ray diffraction (XRD). In addition, microstructure investigations were performed. In part 2, a refined kinetics model of a diffusion-controlled reaction based on the ...

International Nuclear Information System (INIS)

Bench Scale methane cracking tests have been completed using a stack of ten whole SAES(R) St909 pellets - a 6 gram sample size. Methane was found to be the most difficult impurity to process and can impact diffuser operation.

Energy Technology Data Exchange (ETDEWEB)

The quantitative measurement of carbon concentration-distance curves serves as fundamental prerequisite for the evaluation of rim zone properties connected with decarburisation processes in material science. This was shown in part 1 of the present work with two samples from through-hardenable rolling bearing steel 100Cr6 (SAE 52100) austenitised in different oxidising atmospheres by position dependent determination of hardness, residual stresses, and X-ray line broadening ({l_brace}211{r_brace} {alpha}'-Fe diffraction line). In practice, it is important to predict carbon concentration-distance curves under prevailing heat treatment conditions or to conclude conversely from profile measurements. Based on a refined kinetics model of a diffusion-controlled process, part 2 therefore presents a simulation tool developed by means of the finite element method (FEM). Apart from the concentration dependence of the diffusion coefficient, it also ...

Science.gov (United States)

... Fuels", Paper AIAA-91-2451, 27th AIAA/SAE/ASME ... to-surface ballistic missiles than space-based space-to ... an effective hit-to-kill weapon without the ...

Science.gov (United States)

... HARDENED CUP AND CARBURIZED AND HARDENED CORES HAVE BEEN PROFILED USING 2 TYPES OF EDDY CURRENT PROBES. ...

Energy Technology Data Exchange (ETDEWEB)

Sulfur poisoning from engine fuel and lube is one of the most recognizable degradation mechanisms of a NOx adsorber catalyst system for diesel emission reduction. Even with the availability of 15 ppm sulfur diesel fuel, NOx adsorber will be deactivated without an effective sulfur management. Two general pathways are currently being explored for sulfur management: (1) the use of a disposable SOx trap that can be replaced or rejuvenated offline periodically, and (2) the use of diesel fuel injection in the exhaust and high temperature de-sulfation approach to remove the sulfur poisons to recover the NOx trapping efficiency. The major concern of the de-sulfation process is the many prolonged high temperature rich cycles that catalyst will encounter during its useful life. It is shown that NOx adsorber catalyst suffers some loss of its trapping capacity upon high temperature lean-rich exposure. With the use of a disposable SOx trap to remove large portion of the sulfur poisons from the ...

International Nuclear Information System (INIS)

The electrochemical behaviour and fracture morphology of homogenized and sensitized type SAE 304 stainless steel U bent specimens, in 3% NaCl solution, at pH=2.0 and pH=7.0 both at room temperature and 100"0C was studied. Polarization curves, galvanostatic and potentiostatic experiments were run. It could be observed that high temperature and low pH favour transgranular cracking and longer sensitization times lower fracture time and tend to give rise to intergranular fracture. Light sensitization can produce transgranular cracking even at room temperature, when the homogenized alloy does not present stress-corrosion cracking for the same condition. (Author).

British Library Electronic Table of Contents (United Kingdom)

A formula is obtained which describes the kinetics of low-temperature radiation hardening caused by creation of dislocation loops of interstitial type during irradiation. The radiation hardening of aluminum and vanadium is estimated using this formula and results of experiments on studying processes of nucleation and growth of interstitial dislocation loops in these materials by transparent electron microscopy. It is shown that the proposed formula is valid for description of the kinetics of low-temperature radiation hardening.

International Nuclear Information System (INIS)

... defects doped materials germanium infrared radiation monocrystals neutron

International Nuclear Information System (INIS)

Argon ions irradiation of 12% Cr steels and Fe/Cr alloys results in the hardening up to 10000 MPa. This value exceeds the hardening level even for martensitic transformation. Along with the increase of microhardness following irradiation the shape of X-ray graph of the affected materials changes considerable. Hardening value and behavior are determined by temperature radiation doze, preliminary ageing, extent of cold strain and alloying. The odserved phenomenon is supposed to be caused by irradiation-induced structural transformations. Reversibility of radiation hardening of the materials in question was observed.

International Nuclear Information System (INIS)

The radiation hardening studies started in the mid decade 1960-1970. To survive the different military or space radiative environment, a new engineering science was born, to understand the degradation of electronics components. The different solutions to improve the electronic behavior in such environments have been named 'radiation hardening' of the technologies. Improvement of existing technologies, and qualification methods have been widely studied. However, on the other hand, specific technologies were developed: the Silicon On Insulator technologies for CMOS or Bipolar. The HSOI3HD technology offers today the highest hardening level for the integration density of hundreds of thousand transistors on the same silicon. Full complex systems could be produced on a single die with a technological radiation hardening and no more system hardening.

Energy Technology Data Exchange (ETDEWEB)

Smooth and notched specimens of the bearing steel 100Cr6 (SAE 52100) in a bainitic condition were used to determine the S-N-curves under tensile, torsional and combined in- and out-of-phase loading. In the area of high-cycle-fatigue, crack initiation was most likely caused by inclusions like Titanium Carbonitrides or Aluminium Oxides. A model was developed to describe the influence of the magnitude of these inclusions on the lifetime. A weakest link model, using the statistical distribution of inclusions and surface flaws, was used to describe the fatigue limit. (orig.)

International Nuclear Information System (INIS)

This talk sketches out the main parameters (technology, circuit design) that have an influence on the hardening of digital CMOS integrated circuits. For each technology the more common defects are mentioned. General design rules are proposed to prevent or limit those defects. (D.L.). 2 refs., 2 figs.

International Nuclear Information System (INIS)

This paper addresses the background and the continuously evolving topics of hardening and electronic components. Typical radiation environments from 1960 are described. Examples of a civilian satellite and of future particle physics colliders help illustrate hardening problems. Effects in components, limits of shielding, and three methods of providing components are described. The authors conclude by focusing on both future trends of radiation environments and anticipated progress in electronics. (authors). 10 refs., 9 figs., 4 tabs.

International Nuclear Information System (INIS)

A program was undertaken to radiation harden an existing power integrated circuit technology (BCDMOS) to total dose, gamma dot, SEU, and neutrons. Efforts have centered around hardening and optimizing our CMOS, DMOS, and NPN devices. Initial results indicate a substantial improvement in hardness over our existing commercial technology.

International Nuclear Information System (INIS)

The Guarantee Outline presents the technical demands of design and contents of assessment for radiation hardening in satellite engineering in China. It includes the basis of design in space environment of polar orbit, the contents of design for general radiation hardening, the requirements and assessments of the single-board computer, the requirements of design for circuits (including hardware and software), the choices and assessments for devices, and the primary stipulations for the requirements of design and assessments against the phenomenon of charge and discharge.

International Nuclear Information System (INIS)

During electrolysis of a "2"4"8Cm(III) solution in 2M K_2CO_3 at pH=13, partial oxidation of curium to a higher oxidation state, probably Cm(IV), was observed. The absorption spectra of Cm(III) and Cm(IV) in K_2CO_3 solution were recorded and the molar extinction coefficients of main absorption bands of curium were evaluated. (author).

International Nuclear Information System (INIS)

Neutron irradiation embrittlement of reactor pressure vessel (RPV) steels is one of the critical issues on aging management for long term operation of nuclear power plants. Mechanistic understanding of embrittlement is a key to accurate prediction of embrittlement, especially after long term operation where the mechanical test data are sparse. Since matrix hardening is the source of the embrittlement, we focus on matrix hardening of A533B bainitic pressure vessel steel. Bainitic matrix is composed of lath structure made by ferrite and carbides, therefore it is important to understand how this structure affects hardening behavior, and to understand irradiation response of each phase. As the typical dimension of lath structure of A533B is about one micron, nanoindentation technique is suitable for the estimation of hardening of each phase. MV ion accelerators were used for controlled irradiation because ...

International Nuclear Information System (INIS)

Assessments of the hardening and embrittlement of pressure vessel steels and welds as a function of neutron dose use trend curves derived from surveillance programs and accelerated irradiation data. A temperature dependent factor is incorporated for assessing vessel locations operating at different temperatures. As hardening and embrittlement arise from the sum of matrix damage and copper impurity precipitation, the influence of irradiation temperature on each process needs to be established. For irradiations performed below #approx# 300 C recent data shows that the dose-dependent growth of copper precipitates ceases at a mean diameter of about 2 nm that also corresponds to peak hardening and embrittlement by copper. For doses beyond this peak copper dose the property-dependence on irradiation temperature can be identified with that of matrix damage alone. An analysis of several experiments on plate steels, performed at ...

International Nuclear Information System (INIS)

Comprehensive investigation has been made into the application of the polymerization hardening by radiation, particularly electron beam, to the composites of polymers and other materials. The report is divided into four parts, namely 1) characteristics and problems of the reaction of curing by radiation polymerization, 2) improvement of the bonding capability of high molecular weight materials, 3) bonding by radiation, and 4) composites made by the impregnation and polymerization hardening of monomers. The first part includes the effects of dose rate, temperature rise during the hardening, the peculiarity of electron beam irradiation at high dose rate, reaction environment and additive effects. Main conclusions are as follows: caution must be taken to the amount of residual double bonds because they affect the quality of hardened polymers; the polymerization hardening reaction at ...

CERN Document Server

We report on the detection of SiO and water masers toward a newly found bipolar nebula, IRAS 19312+1950. This object exhibits extreme red IRAS color log (F25/F12)=0.5 and log (F60/F25)=0.7 and a nebulosity having a size of about 30" extended to the South-West in the 2MASS near-infrared image. Toward this object, we have detected emission from the H2O 6(1,6)-5(2,3) transition, the SiO J=1-0, v=1 and 2, and J=2-1, v=1 transitions, and the SO 2(2)--1(1) and H13CN J=1-0 transitions. The thermal lines of SO and H13CN are shifted by about 12 km/s in radial velocity with respect to the maser lines, indicating that thermal emission comes from the background molecular cloud. However, the SiO J=2-1, v=2 spectrum shows another component of SiO emission separated by 26 km/s from the main component, that might be formed in a rotating or expanding shell.

International Nuclear Information System (INIS)

High temperature deformation behavior of an alpha + beta titanium alloy Ti-3Al-4V has been investigated at 910 deg. C. by using the method of cross head speed cycling. On the basis of flow stress, strain rate and strain rate sensitivity data, the alloy was found to exhibit strain hardening at this temperature which resulted in degradation in superplastic properties of the alloy. A high beta-phase volume fraction and grain-growth in both alpha and beta phases were considered responsible for the observed hardening effect. (author)

International Nuclear Information System (INIS)

Total dose irradiation effects on a VDMOS developed at Institute of Microelectronics, CAS were investigated, particularly the electric parameter changes under different bias conditions. It was found that the breakdown voltage degradation by the irradiation depended mainly on the drain bias, whereas the threshold voltage degradation depended mainly on the gate bias. Thus, an innovative and effective method to domestic VDMOS total dose ionization characterization is that threshold voltage radiation hardening characterization should be tested on gate bias condition, and the breakdown voltage radiation hardening characterization, be tested on the drain bias. (authors)

International Nuclear Information System (INIS)

... University, Fracture and Reliability Research Institute, Sendai, Miyagi (Japan)

Energy Technology Data Exchange (ETDEWEB)

Formulas were developed based on an aqueous solution of hydrolyzed polyacrylonitrile widely used in the oil industry. The additive used consisted of products of industrial production: synthetic resin TEG-1 with hardening agent PEPA (polyehtylene polyamine) and technical formalin. The mixtures containing about 80-85% by volume 5% hydrolyzed polyacrylonitrile, 10-15% by volume of resin TEG-1 with hardening agent PEPA and 3-5% by volume formalin satisfy the requirements made for the plugging materials. The initial mixtures are distinguished by technological efficiency of preparation and have controllable hardening periods. Physical-chemical properties are given for the gel polymers. In the set of properties, the mixtures based on hydrolyzed polyacrylonitrile, resin TEG-1 with hardening agent PEPA and formalin can be recommended as plugging materials of temporary action with complex treatment of the ...

International Nuclear Information System (INIS)

The #beta#-CEZ alloy : Ti-5%Al-2%Sn-4%Zr-4%Mo-2%Cr-1%Fe is a near #beta# titanium alloy. Since its processing routes include heat treatment (consisting of solution treatment and ageing), it has been decided to study the influence of the #beta# phase stability on #alpha# phase precipitation and hardening kinetics. Small sized specimens, coming from industrial heats, have been heat treated above and below the #beta# transus, and then water quenched. Therefore, several degree of #beta# stability are obtained. When it is increased (i.e. the solution treatment temperature is lowered), #alpha# or #omega# phases precipitations are delayed, as well as the hardening phenomena. Moreover, the #omega# stability domain is reduced. The mechanisms of #alpha# or #omega# precipitation are discussed, and related to the hardening kinetics. (orig.).

British Library Electronic Table of Contents (United Kingdom)

A fully lamellar ferrite/cementite nanostructure was designed in a low C steel by using a specific thermal treatment. The strengthening of such microstructure has been investigated as a function of prestrain by rolling up to a deformation of 300%. As in usual pearlitic structure, its work-hardening shows no saturation and its elongation to fracture remains rather constant instead of decreasing drastically as conventional steels. The hardening by a similitude effect is thus not the privilege of pearlitic steels. Nevertheless, its lower initial work-hardening rate at low strain compared to an equivalent pearlitic steel and a lower hardening potential at high strain let us suspect major differences in the nature and the behaviour of ferrite channels in relation to the morphogenesis of the mic...

Energy Technology Data Exchange (ETDEWEB)

Smooth and notched specimens of the bearing steel 100Cr6 (SAE 52100) in a bainitic condition were used to determine the S-N curves under tensile, torsional and combined in- and out-of-phase loading. In the area of high-cycle fatigue, crack initiation was most likely caused by inclusions like Titanium Carbonnitrides or Aluminium Oxides. A micro mechanical model for the crack initiation by inclusions was developed. Another model was developed to describe the influence of these inclusions on the lifetime. A weakest-link model, using the statistical distribution of inclusions and surface flaws, was used to describe the endurance limit. (orig.) [German] Es wurden Woehlerlinien unter Zug-Druck-, Torsions- sowie kombinierter phasengleicher und phasenverschobener Zug-Druck- und Torsionsbelastung fuer glatte und gekerbte Proben des Stahls 100Cr6 (SAE 52100) im bainitischen Zustand erstellt. Im Bereich der Langzeitermuedung gingen die Risse meistens von ...

Science.gov (United States)

The effect of solution treatment temperature and oxygen content on the microstructure and age hardening response of the metastable beta alloy Ti-11.5Mo-6Zr-4.5Sn have been studied. Kinetics of formation of the equilibrium alpha-phase and the metastable om...

International Nuclear Information System (INIS)

Mechanical properties of vanadium, irradiated with fast neutrons up to 8.6x10"-"4 dpa depending on postirradiation annealing temperature, are studied. It is shown that radiation-annealing hardening (RAH) is observed at 300 deg C, which agrees with earlier performed studies. It is first stated that RAH is accompanied by plasticity decrease. Phenomenological model permitting to explain RAH dependence on irradiation temperature and dose and also on content of chemically active alloying impurities is suggested.

Energy Technology Data Exchange (ETDEWEB)

An evaluation of eastern shale oil (ESO) residue as an asphalt additive to reduce oxidative age-hardening and moisture susceptibility was conducted. Rheological and infrared analyses of the unaged and aged asphalts and blends were then conducted to evaluate oxidative age-hardening. 18 refs., 5 figs., 6 tabs.

International Nuclear Information System (INIS)

Generally, neutron, ion and electron Irradiations cause a substantial amount of hardening and significantly alter the deformation behavior of metals and alloys at relatively low irradiation temperatures. A radiation hardening is caused by the formation of microstructural defects such as dislocation loops, voids and precipitates under irradiation. Therefore, it is important to have a better knowledge of the irradiation induced microstructural defects under irradiation condition. As a part of the National mid- and long-term atomic energy R and D program, we are dealing with the radiation hardening behavior in Fe-Cr binary alloy. Fe-Cr binary alloy is a base alloy of Ferritic/Martensitic steel(F/M steel) planning to use for the Gen IV nuclear system. In this work, we investigated the radiation hardening and microstructural defect evolution in ion irradiated Fe-Cr alloys with irradiation temperature using ...

International Nuclear Information System (INIS)

Fe-Cu binary alloys are often used to mimic the behaviour of reactor pressure vessel steels. Their study allows identifying some of the defects responsible for irradiation-induced hardening. But recently the influence of manganese and nickel in low-Cu steels has been found to be important as well. In contrast with existing models found in the literature, which predict that hardening saturates after a certain dose, Fe alloys containing nickel and manganese irradiated in a material test reactor (BR2) show a continuous increase of hardening, up to doses equivalent to about 40 years of operation. Considerations based on positron annihilation spectroscopy analyses suggest that the main objects causing hardening in Cu-free alloys are most probably self-interstitial clusters decorated with manganese. In low-Cu reactor pressure vessel steels and in Fe-CuMnNi alloys, the main effect is still due to Cu-rich ...

International Nuclear Information System (INIS)

The effects of key metallurgical variables on the low fluence hardening in a set of A533B model steels were evaluated over a wide range of irradiation temperatures. Above about 163 degrees C hardening increased with higher copper and nickel contents, as is typical of the pressure vessel operating regime around 290 degrees C. However, at 121 degrees C the hardening was generally lower and unaffected by copper and nickel variations. This observation of decreased hardening with lower temperature (e.g. an open-quotes invertedclose quotes temperature dependence) is tentatively attributed to a reduced contribution of copper precipitation. Tensile data for a set of commercial steels with a range of (uncontrolled) compositions also showed minimal sensitivity to copper variations at 121 degrees C. Unlike the hardness data no systematic reductions in the yield stress increases were observed between 163 and 121 ...

Energy Technology Data Exchange (ETDEWEB)

Fatigue tests were accomplished with a series of specimens doped with trace elements of a hardened Fe-Ni-Cr alloy, cast and hardened with intermetallic phases for determining the influence of these elements on the high temperature strength properties. The results of extensive fatigue tests show that even small contents of Te, Bi, Se, Pb, Tl and Zn considerably influence the life and creep processes especially after longer running periods, when added individually or combinedly. In contrast to this, the fatigue ductility is reduced by trace element additions even with short running periods. The order in which the metallic trace elements influence the fatigue properties nearly correlates with earlier work concerning Ni- and Co-superalloys. (orig.)

International Nuclear Information System (INIS)

Defect cluster formation in 14-MeV neutron irradiated polycrystalline copper has been observed by transmission electron microscopy (TEM) and correlated with the increase in yield stress. The measurements indicate that the radiation hardening component of the yield strength in polycrystals is not directly additive to the unirradiated yield strength. A transitional behavior was observed for radiation hardening at low fluences, which produces an anomalous variation of the defect cluster barrier strength with fluence. The behavior is attributed to the effect of grain boundaries on slip band transmission. An upper limit for the room temperature barrier strength of defect clusters in neutron-irradiated copper was determined to be #alpha#=0.23. (orig.).

International Nuclear Information System (INIS)

Nano indentation analysis and transmission electron microscopy observation were performed to investigate a microstructural evolution and its influence on the hardening behavior in Fe-Cr alloys after an irradiation with 8 MeV Fe4+ ions at room temperature. Nano indentation analysis shows that an irradiation induced hardening is generated more considerably in the Fe-15Cr alloy than in the Fe-5Cr alloy by the ion irradiation. TEM observation reveals a significant population of the a0 dislocation loops in the Fe-15Cr alloy and an agglomeration of the 1/2a0 dislocation loops in the Fe-5Cr alloy. The results indicate that the a0 dislocation loops will act as stronger obstacles to a dislocation motion than 1/2a0 dislocation loops.

International Nuclear Information System (INIS)

By method of transmission electron microscopy and measuring of microhardness the peculiarities of influence of radiation defect clusters on molybdenum radiation hardening along range path of protons with 30 MeV initial energy are studied. Decrease effect of hardening growth value and even its absence depending on irradiation dose in the range of 10-20 MeV proton energies in presence of high density of radiation defect dispersed clusters is revealed. It is shown experimentally that this effect is connected with accumulation of hydrogen up to not very high concentrations (not more than 5x10"-"4 at.%) at the expense of elastic and inelastic proton scattering. 5 refs.; 5 figs.

British Library Electronic Table of Contents (United Kingdom)

This paper provides a physically-based engineering model to estimate radiation hardening of 9%Cr-steels under both displacement damage (dpa) and helium. The model is essentially based on the dispersed barrier hardening theory and the dynamic re-solution of helium under displacement cascades but incorporating a number of assumptions and simplifications [Trinkaus, J. Nucl. Mater. 318 (2003) 234-340]. As a result, the kinetics of the damage accumulation kept fixed, its amplitude is fitted on one experimental condition. The model was rationalized on an experimental database that mainly consists of 9%Cr-steels irradiated in the range of 50-600degreeC up to 50dpa and with a He-content up to 5000appm. The test temperature effect is taken into account through a normalization procedure based on the...

International Nuclear Information System (INIS)

This work describes the ability of ion beam analysis techniques IBA to simultaneously determine the concentration and the possible depth profile of some light elements, such as carbon, oxygen and nitrogen, in matrices of high atomic number Z, such as stainless steel materials. In fact, the nitriding process of some materials has the potential to improve their tribological and mechanical properties and to offer various advantages as compared with other methods used in the modification of surfaces. Gas and Plasma nitriding were applied to certain types of steel, such as AISI-304 and H-13 which are commonly used in the industry, in order to improve their hardness and their surface corrosion resistance. The improvement was correlated with the depth profile of N and the consequent structure variations. More specifically, non-Rutherford elastic backscattering (alpha, alpha) at 5 MeV was performed on different samples, before and after nitriding, in ...

Energy Technology Data Exchange (ETDEWEB)

The wear behaviour of 722M24 (En40B) steel plasma nitrided at high temperatures for long durations was investigated. Under dry sliding and abrasive-containing lubricated conditions, the wear characteristics of the steel were studied as a function of load, time and white layer thickness. The white layer and the wear debris were characterized by X-ray diffraction. The topography of the wear surface was examined in a scanning electron microscope. The plasma nitriding process was carried out using a 20 kW plasma processing unit in cracked ammonia atmosphere. Treatment times of up to 100 h were employed with temperatures of 550, 570 and 590 C. Wear tests were performed with plasma nitrided AMS 6472 as the counterface material. The tests under abrasive-containing lubricated conditions were carried out with 10% carborundum powder 10 [mu]m in size in SAE-30 machine oil. The wear resistance of the steel was improved by plasma nitriding and the abrasive wear resistance of ...

International Nuclear Information System (INIS)

Simultaneous nitriding and ageing heat treatments of precipitation hardenable tool steel was carried out inside a DC-pulsed plasma nitriding reactor. A single heat treatment cycle was done, as the plasma nitriding and age hardening processes occur approximately at the same ranges of temperatures and times. Specimens of Cr-Ni-Mo-Al age hardenable steel, in the solubilized and solubilized and aged conditions, were tested. Plasma nitriding and ageing, carried out at 500 deg. C for times ranging between 2 and 8 h, increased the surface hardness up to 1000 HV, producing case depths between 100 and 200 #mu#m. The core hardness of solubilized samples increased from 30 to 39 Rockwell C after the plasma nitriding treatment proving the possibility of nitriding and ageing at the same treatment cycle. The pre-aged samples did not show any overageing after the simultaneous plasma nitriding and ageing treatments. The corrosion resistance ...

International Nuclear Information System (INIS)

The methods of surface modification of Ti-Zr alloy by laser treatment are considered. Characteristics of laser modification without- and with surface melting and with melting in different gaseous environments and with nickel microalloying are presented. Maximum depth, hardness and corrosion resistance are observed under nickel laser alloying.

International Nuclear Information System (INIS)

Field Programmable Gate Arrays (FPGAs) are being used in space applications because of attractive attributes: good density, moderate speed, low cost, and quick turn-around time. However, these devices are susceptible to Single Event Upsets (SEUs). An approach using triple modular redundancy (TMR) and feedback was developed for flip-flop hardening in these devices. Test data showed excellent results for this circuit topology. Total dose and Single Event Effect (SEE) testing have been performed on recently released technologies. Failures are analyzed and test methodology is discussed.

Energy Technology Data Exchange (ETDEWEB)

The authors have measured the noise of MOS transistors of the United Technology Microelectronics Center (UTMC) 1.2 [mu]m radiation hardened CMOS P-well process from the weak to moderate inversion region. The noise power spectral densities of both NMOS and PMOS devices were measured from 1 KHz to 50 MHz. The bandwidth was chosen such that the important components of the spectral densities such as the white thermal noise and the 1/f noise could be easily resolved and analyzed in detail. In this paper the effects of different device terminal DC biases and channel geometries on the noise are described.

British Library Electronic Table of Contents (United Kingdom)

There is proposed the nonlinear model of dose dependence saturation of the yield strength on the base of the vacancy and interstitial barrier interaction in this work. Processes of mutual recombination of vacancy and interstitial barriers and formation of vacancy and interstitial clusters are taken into consideration. In the framework of the model, the analytical equations corresponding to the evolution of the barrier densities and yield strength are obtained. It is shown that the yield strength of irradiated materials decreases with the increasing intensity of barrier recombination processes, the dependence being nonlinear. Also it is shown that the model is valid both for low doses and large doses on the stage of radiation hardening.

International Nuclear Information System (INIS)

Corrosion testings of model alloys, corresponding by chemical composition to simple and complex-alloyed #gamma#- and #gamma#'-phases of nickel heat-resistant alloys are conducted in sodium sulfate and chloride melts. It is ascertained that heat resistant nickel alloys containing over 50 % of hardening #gamma#'-phase, are subject to disastrous sulfide corrosion (SC). Resistance against SC alloys containing below 50 % of #gamma#'-phase is determined by the resistance of #gamma#-solid solution. 10 refs., 3 figs., 2 tabs.

International Nuclear Information System (INIS)

Full text of publication follows: Radiation hardening and embrittlement due to high-energy neutron radiation around 623 K are the important issues on reduced-activation ferritic/martensitic (RAF/M) steels. It is expected that the improvement of radiation hardening might be one of effective ways to control the mechanical properties of RAF/M after irradiation. It has been reported that the weld joint has less hardening than the base metal from the tensile test results of TIG weldments irradiated in HFIR. This report indicated that radiation hardening can be reduced by the optimization of heat treatment condition for F82H. The purposes of this study are to establish the condition of heat treatment for minimum of radiation hardening in F82H steel using Neutron/Ion-irradiation and to examine a correlation between tensile property and micro-hardness before/after irradiation. The materials ...

International Nuclear Information System (INIS)

Hardened CMOS/SOI 29101 microprocessor, elementary cells and transistor shave been irradiated at levels between 10 Mrad(SiO_2) and 1 Grad(SiO_2) ("6"0Co and 10 keV x-rays). SIMOX buried oxide behavior in the range of 100 Mrad(SiO_2) and a channel-stopped MOS/SOI structure avoiding lateral leakage current are presented. These two items indicate the feasibility of a CMOS/SOI technology operating in the hundred Mrad(SiO_2) range.

Energy Technology Data Exchange (ETDEWEB)

Biomass and nutrient dynamics of black spruce seedlings during the hardening phase of the greenhouse rotation were examined after four pre-hardening fertilization regimes - conventional, constant-rate loading, exponential loading, and high exponential loading (delivering respectively 15, 40, 40 and 60 mg N seedling{sup -1}) - in order to assess nutrient dilution and steady-state nutrition. Although height growth of seedlings had virtually ceased during hardening, shoot biomass increased 99-142% and root biomass increased five- to tenfold depending on treatment. The biomass increase compromised steady-state nutrient status by diluting internal nutrient pools as nutrient supply was unable to keep up with growth. Soil nutrient levels were rapidly depleted during this period because of plant uptake and lack of fertilizer supplementation. Pre-hardening nutrient loading partly countered and delayed dilution ...

International Nuclear Information System (INIS)

An experimental investigation of the effect of nickel content on irradiation hardening of reactor pressure vessel steels was conducted. The alloys studied, with nickel contents ranging from 0 to 1.7%, included five sets of steels representing variations in copper contents and other metallurgical variables. Various subsets of the alloys were irradiated at selected combinations of flux, fluence, and irradiation temperature. Irradiation hardening was measured by either changes in the uniaxial yield stress or diamond pyramid hardness. Higher hardening rates with increasing nickel were observed in controlled experiments on commercial-type steels containing high copper concentrations (0.4% Cu). The effect of nickel increased with increasing fluence and decreasing temperature. At high fluence (>10"1"9 n/cm"2) the hardening increased with nickel at an average rate of about 100 MPa/%Ni. There also appeared to ...

International Nuclear Information System (INIS)

The first essential before embarking on the radiation-hardening of electrical insulation - mostly magnet coils - in any beam line application is to obtain a reliable estimate of the dose to the components. These are examples ( switchyards at SLAC and LAMPF) where the degree of hardness specified was much higher than was required. Although experience shows that the cost premium for substantial radiation - hardening is of the order of 10%, it has also become clear that well - designed beam line have negligible losses: hardening is required only in the vicinity of targets, collimators or other beam - intercepting devices. Where the beam is deliberately scraped, local shielding will minimize the associated radiation in the surroundings. Electron machines have their own special problems due to synchrotron radiation, so certainly coils and other electrical equipment should be kept away from the beam bend - plane. Because proton ...

Science.gov (United States)

Al2O3-based ceramic is one of the most widely used materials for tools employed in hardened steel turning applications due to its high hardness, wear resistance, heat resistance and chemical stability. The objective of this work is to predict the lives of Al2O3-(W, Ti)C ceramic tools in intermittent turning of hardened AISI 1045 steel by means of damage evolution model taking into account the mechanical loading and thermal effect in the cutting process. A damage evolution model analyzing the RVE with uniformly distributed interacting cracks is constructed based on micromechanics. The calculated results of the proposed damage evolution model are compared with the lives of two kinds of Al2O3-(W, Ti)C ceramic tools obtained through experiments. It is found that the proposed model can be used to predict the lives of the ceramic cutting tools in intermittent turning operation.

International Nuclear Information System (INIS)

Type 316 stainless steel is the primary candidate austenitic structural material for fusion first wall constructions. Here, type 316L(N) stainless steel plate material has been irradiated up to 10 dpa at temperatures of 80, 225, 325, and 425 C in the High Flux Reactor (HFR) of Petten. Tensile tests have been performed in the temperature range from RT to 575 C at a conventional strain rate of 5 x 10"-"4 s"-"1. The results of the tensile tests are analyzed in terms of irradiation hardening and loss of ductility due to irradiation. Tensile properties saturate in the early stage (within 0.65 dpa) at the lowest applied irradiation temperature. It is indicated that the most severe degradation of tensile ductility occurs in the temperature range of 275 to 350 C. Comparison with literature data revealed a large scatter in irradiation hardening at irradiation temperatures above 325 C.

International Nuclear Information System (INIS)

Pressureless-sintered AlN and hot-pressed, pressureless-sintered and reaction-bonded SiC were neutron irradiated at temperatures between 100 and 785degC up to a fluence of 5.2 x 10"2"4 n/m"2. The hardness was increased by up to 51% in AlN and 84% in SiC. The hardness decreased after annealing at temperatures around the irradiation temperature. At the same temperatures, the macroscopic length, which was increased by irradiation, also began to decrease. The hardness and length were almost recovered after 1,200 #approx# 1,400degC annealing. Thus, hardening in irradiated AlN and SiC is controlled by the number of point defects, or, more precisely, by the strain caused by small point defect clusters which pin down dislocation movement. Dislocation loops were still observed in some samples after 1,400degC annealing while the hardness was almost recovered to that in the unirradiated state. Thus, the existence of dislocation loops is not grounds for ...

CERN Document Server

Volume sources is used for standard sources by radioactive measurement using Ge semiconductor detector of environmental sample, e.g. water, soil and etc. that require large volume. The commercial volume source used in measurement of the water sample is made of agar-agar, and that used in measurement of the soil sample is made of alumina powder. When the plastic receptacles of this two kinds of volume sources were damaged, the leakage contents cause contamination. Moreover, if hermetically sealing performance of volume source made of agar-agar fell, volume decrease due to an evaporation off moisture gives an error to radioactive measurement. Therefore, we developed the two type methods using unsaturated polyester resin, vinilester resin, their hardening agent and acrylicresin. The first type is due to dispersing the hydrochloric acid solution included the radioisotopes uniformly in each resin and hardening the resin. The second is due to ...

CERN Document Server

The massive stars in the Galactic center inner arcsecond share analogous properties with the so-called Hot Jupiters. Most of these young stars have highly eccentric orbits, and were probably not formed in-situ. It has been proposed that these stars acquired their current orbits from the tidal disruption of compact massive binaries scattered toward the proximity of the central supermassive black hole. Assuming a binary star formed in a thin gaseous disk beyond 0.1 pc from the central object, we investigate the relevance of disk-satellite interactions to harden the binding energy of the binary, and to drive its inward migration. A massive, equal-mass binary star is found to become more tightly wound as it migrates inwards toward the central black hole. The migration timescale is very similar to that of a single-star satellite of the same mass. The binary's hardening is caused by the formation of spiral tails lagging the stars inside the binary's ...

British Library Electronic Table of Contents (United Kingdom)

A series of thiazolo[3,2-b][1,2,4]triazole incorporating diphenylsulfone moieties were synthesized starting from 5-[4-(4-X-phenylsulfonyl)phenyl]-4H-1,2,4-triazole-3-thioles 3a-c, X=H, Cl, Br. Thus, alkylation of 1,2,4-triazoles 3 with phenacyl bromide or 4-bromophenacyl bromide afforded S-substituted 1,2,4-triazoles 4, 5. These new intermediates 4 and 5, in the presence of H2SO4 (c), were cyclized to 2-[4-(4-X-phenylsulfonyl)phenyl]-6-(4-Y-phenyl)[1,3]thiazolo[3,2-b]-[1, 2,4]-triazoles 6, 7 (I) and not to isomeric thiazolo[2,3-c][1,2,4]-triazoles 6, 7 (II). The newly synthesized compounds were characterized by IR, 1H, 13C NMR and elemental analysis. MS spectra confirmed the formation of thiazolo[3,2-b][1,2,4]triazole 6, 7 (forms I) in detriment of [2,3-c] isomeric compounds (forms II). Th...

British Library Electronic Table of Contents (United Kingdom)

A general approach has been designed to synthesize some mononuclear and binuclear cyclometalated platinum(II) complexes, containing aromatic N-donor ligands with the presence of one Cl- trans to carbon. In this way, cyclometalated platinum(II) complex [Pt(C^N)Cl(dmso)], 1, C^N = N(1),C(2prime)-chelated, deprotonated 2-phenylpyridine and dmso = dimethylsulfoxide, was used as a precursor to react with imidazole derivatives (1-methylimidazole, 2a, imidazole, 2b,), monodentate pyridine derivatives (4-methylpyridine, 2c, pyridine, 2d,) and bidentate pyridine derivative (4,4prime-bipyridine, 3 and 4,). Synthesized complexes were fully characterized by using multinuclear NMR spectroscopy (1H, 13C{1H} and 195Pt), correlation NMR spectroscopy (1H-1H COSY, 13C{1H}-1H Heteronuclear Multiple Quantum C...

British Library Electronic Table of Contents (United Kingdom)

The structure of the O-antigen polysaccharide (PS) from Escherichia coli O177 has been determined. Component analysis together with 1H and 13C NMR spectroscopy experiments was used to determine the structure. Inter-residue correlations were determined by 1H,13C-heteronuclear multiple-bond correlation and 1H,1H-NOESY experiments. PS is composed of tetrasaccharide repeating units with the following structure: 2)-a-l-Rhap-(13)-a-l-FucpNAc-(13)-a-l-FucpNAc-(13)-b-d-GlcpNAc-(1 An a-l-Rhap residue is suggested to be present at the terminal part of the polysaccharide, which on average is composed of 20 repeating units, since the 1H and 13C chemical shifts of an a-linked rhamnopyranosyl group could be assigned by a combination of 2D NMR spectra. Consequently, the biological repeating unit has a 3-...

International Nuclear Information System (INIS)

This work describes the ability of ion beam analysis techniques IBA to simultaneously determine the concentration and the possible depth profile of some light elements, such as carbon, oxygen and nitrogen, in matrices of high atomic number Z, such as stainless steel materials. In fact, the nitriding process of some materials has the potential to improve their tribological and mechanical properties and to offer various advantages as compared with other methods used in the modification of surfaces. Gas and Plasma nitriding were applied to certain types of steel, such as AISI-304 and H-13 which are commonly used in the industry, in order to improve their hardness and their surface corrosion resistance. The improvement was correlated with the depth profile of N and the consequent structure variations. More specifically, non-Rutherford elastic backscattering (alpha, alpha) at 5 MeV was performed on different samples, before and after nitriding, in ...

International Nuclear Information System (INIS)

Tungsten (W) coating on fusion candidate V-4Cr-4Ti (NIFS-HEAT-2) substrate was demonstrated with plasma spray process for the purpose of applying to protection of the plasma facing surface of a fusion blanket. Increase in plasma input power and temperature of the substrate was effective to reduce porosity of the coating, but resulted in hardening of the substrate and degradation of impact property at 77 K. The hardening seemed to be due to contamination with gaseous impurities and deformation by thermal stress during the coating process. Since all the samples showed good ductility at room temperature, further heating seems to be acceptable for the vanadium substrate. The fracture stress of the W coating was estimated from bending tests as at least 313 MPa, which well exceeds the design stress for the vanadium structure in fusion blanket. (author)

International Nuclear Information System (INIS)

By means of the light microscopy and by the measurement of the mechanical properties one investigated into the phase composition and the properties of Al-Mg-Ce and Al-Mg-Y system alloys. One plotted the isothermal cross sections of the mentioned systems under 430 and 275 deg C temperatures at up to 16% magnesium concentration and up to 0.7% yttrium concentration. One determined the yield limit and strength, the relative elongation of Al-Mg base hardened and deformed alloys containing 7.0-9.9% Mg and Ce, Y, Mn, Zr dopes upon ageing under 175, 200, 250 and 300 deg C temperatures within the ageing time ensuring the hardening maximum effect

International Nuclear Information System (INIS)

Smooth and notched fatigue behavior is presented for an age-hardenable metastable #beta#-titanium alloy (Ti-3Al-8V-6Cr-4Mo-4Zr). The as-solution heat treated condition exhibits low fatigue limits and high ductility, while the high-strength condition has higher fatigue limits, but poor ductility. A new thermomechanical technique employs shot peening and heat treating to selectively age-harden only the surface. The fatigue limit is improved to levels well above that of the high strength condition, while retaining appreciable ductility, since the bulk material remains in the solution heat treated condition. (orig./MM).

International Nuclear Information System (INIS)

The RD50 collaboration has been exploring the development of radiation hard semiconductor devices for very high-luminosity colliders since 2002. The target fluence to qualify detectors set by the anticipated dose for the innermost tracking layers of the future upgrade of the CERN large hadron collider (LHC) is 1016 1 MeV neutron equivalent (neq) cm-2. This is about an order of magnitude higher than the maximum dose for the most exposed silicon detectors in the current machine. RD50 investigates the radiation hardening of silicon sensors from many angles: improvement of the intrinsic tolerance of the substrate material, optimisation of the readout geometry and study of novel design of detectors. A review of some of the recent activities within RD50 is here presented.

International Nuclear Information System (INIS)

Modern commercial alloys are not suited for future steam turbines of operating temperatures beyond 700 C. #gamma#'-hardened alloys like Waspaloy have good mechanical characteristics but have defects when large batches are melted. #gamma#'/#gamma#''-hardened alloys like Inconel 706, on the other hand, are easy to produce but have insufficient microstructural long-term stability and insufficient creep strength. Mixed crystal solidified alloys like Inconel 617 have excessive yield stress at forging temperatures. Two new alloys were therefore developed. Results so far show that they have good production characteristics but insufficient mechanical characteristics. The reasons for this are currently under investigation. (orig.)

International Nuclear Information System (INIS)

The condition for obtaining a calorimetric response linear with energy for hadronic showers and an energy resolution that improves as the incident energy increases is the equalization of the electromagnetic (e) and the hadronic (#pi#) signal responses. This equalization is obtained by exploiting a local hardening effect realized through the insertion of low-Z thin plates between the high-Z absorbers and the active material in a hadronic calorimeter with silicon readout. This effect, which allows the reduction of the calorimeter response to the electromagnetic component of the incoming hadronic showers, has been investigated for different low-Z materials. The relevance of some aspects of this study to the radiation hardness of the calorimeters is also addressed. (orig.).

Energy Technology Data Exchange (ETDEWEB)

This patent describes a preflush fluid for preventing lost circulation during the cementing of a well, the fluid consisting essentially of: (a) water; (b) about 10 to about 30 percent by weight of water (% BWOW) cement; (c) about 5 to about 30% BWOW calcium sulfate selected from the group consisting of calcium sulfate hemihydrate, calcium sulfate dihydrate, and mixtures thereof; and (d) an alkali metal-containing quick-hardening accelerator.

Energy Technology Data Exchange (ETDEWEB)

Plasma nitriding is usually used for ferrous materials to improve their surface properties. Knowledge of the properties of thin surface layers is essential for designing engineering components with optimal wear performance. In our study, we investigated the microstructural, mechanical and tribological properties of plasma- and pulse plasma-nitrided AISI 4140 steel in comparison to hardened steel. The influence of nitriding case depth as well as the presence of a compound layer on its tribological behaviour was also examined. Plasma and pulse plasma nitriding were carried out using commercial nitriding processes. Nitrided samples were fully characterised, using metallographic, SEM microscopic, microhardness and profilometric techniques, before and after wear testing. Wear tests were performed on a pin-on-disc wear testing machine in which nitrided pins were mated to hardened ball bearing steel discs. The wear tests were carried out under dry ...

Energy Technology Data Exchange (ETDEWEB)

In this study, deformation modes and precipitations have been characterized in test pieces made of alloy 800, grade 2 hyper-hardened state and age-conditioned for 3000 h at 550/sup 0/C, used for steam generator tubes of the Super Phenix Reactor, after continuous fatigue and fatigue-relaxation tests in the oligocyclic range. This microstructural study has provided an interpretation of the fatigue behaviour of the material.

International Nuclear Information System (INIS)

The structure and properties of composite powder coatings on the base of titanium carbide are studied. It is shown the electron-beam welding deposition of powders on the base of nickel and titanium carbide allows to produce of high-quality wear-resistant coatings which superior in density and hardness compared with sputtered ones. Changes of hardening phase volume percentage as well as composition of metal matrix make possible to control coatings hardness

Science.gov (United States)

A number of alloys of zirconium have been investigated as part of a program aimed at improving the high-temperature tensile and creep strength of zirconium. These alloys include aluminum, beryllium, lead, magnesium, molybdenum, niobium, tantalum, tin, titanium, tungsten, vanadium, and zinc, binary and ternary alloys. The data indicate that aluminum, lead, molybdenum niobium, tin, titanium, tungsten, and vanadium can be used successfully to harden zirconium, and that aluminum, tin, titanium, and vanadium are particularly effective in maintaining the strength of zirconium at elevated temperatures.

Science.gov (United States)

This paper describes the anelastic strain recovery and the strain hardening of amorphous metals and presents the experimental result that creep deformation is represented by a viscoelastic model consisting of rheological elements. Materials studied were 80Pd--20Si, 80Fe--13P--7C, and 60 Cu--40 Zr. (DLC)

International Nuclear Information System (INIS)

Simulation irradiation experiments were carried out to investigate the formation processes and contribution to hardening of radiation-induced features in low alloy steels. Medium Cu (0.12 and 0.16%) and low Cu (0.03%) A533B steels were irradiated with 3 MeV Ni ions and 5 MeV electrons, and in KUR at 290degC. Irradiated steels were examined by three-dimensional atom probe, positron annihilation, high-resolution transmission electron microscopy and hardness measurements. Electron irradiation caused almost the same hardening as KUR irradiation in medium Cu steels under almost the same dose rate and dose conditions, whereas the formation of larger, denser and more Cu enriched clusters and smaller accumulation of single vacancies were confirmed for KUR irradiation. This indicated that cascade damage provides additional cluster nucleation sites to compensate for lower free point defect production. High dose rate Ni ion irradiation produced Mn-Ni-Si ...

Energy Technology Data Exchange (ETDEWEB)

A hose lining process, used widely for underground service structures, such as for city gas, and water and sewerage pipes, was adopted to repair interiors of underground wire raceways, and improvements were made for power cable pipe use, including long size construction, inner diameter assurance, and flame retardation. The sealing hose as a lining material consists of a fabric layer woven by warps of polybutylene terephthalate (PBT) and wefts of combined PBT fibers and glassfibers, the fabric being coated with polyurethane resin on one side. The other side of the fabric is coated with heat hardening resin made of epoxy resin as the main ingredient and aromatic amine as the hardening agent to assure close adhesion of the sealing hose onto the pipe interior. Mimic raceways were used to verify the lining material for its abrasion coefficient, mechanical strength, wear resistance, water cut-off performance, chemical resistance, and shape retention ...

International Nuclear Information System (INIS)

Radiation damage of the final optical components in an Inertial Confinement Fusion (ICF) reactor is a crucial issue for development of a laser-fusion reactor. To some extent, this problem will be encountered in the National Ignition Facility (NIF), but there, the integrated radiation dose will be considerably less than that encountered in a future reactor. This extremely harsh radiation environment necessitates shielding the ICF optics from direct neutron and x-ray bombardment. Several approaches have been suggested, such as the use of grazing incidence metal mirrors or fused silica wedge deflectors. While metal mirrors can withstand a larger radiation dose, their focusing qualities pose problems. Therefore wedge deflectors, originally suggested by Lawrence Livermore National Laboratory (LLNL) staff, represent a promising alternative. Radiation hardening of the fused silica deflectors using a new combined thermal/optical annealing approach is examined here as a ...

International Nuclear Information System (INIS)

Total-dose irradiation seriously damages MOS devices and their circuit performance. Threshold voltage shifts, transconductance degradation and increase in off-state leakage current are generally observed for irradiated devices. These instabilities are essentially due to positive and/or negative charge trapping in SiO_2 and interface trap generation at the SiO_2/Si interface. Radiation hardening of CMOS VLSIs is to eliminate these trapping effects, and for this purpose, special considerations for fabrication processes and layout design are necessary. In this paper, basic mechanisms for radiation-induced charge trapping and related effects on MOS devices are reviewed. Also discussed are radiation-hardening technologies from both fabrication-process and layout-design viewpoints. Using these technologies, 1 #mu#m radiation-hard CMOS gate arrays have been successfully developed. Experimental data taken for 2k-gate test chips indicate that radiation ...

Energy Technology Data Exchange (ETDEWEB)

The objective of this program is to tool-harden and make commercially available an existing wireless MWD tool to reliably operate in an air, air-mist, or air-foam environment during Appalachian Basin oil and gas directional drilling operations in conjunction with downhole motors and/or (other) bottom-hole assemblies. The application of this technology is required for drilling high angle (holes) and horizontal well drilling in low-pressure, water sensitive, tight gas formations that require air, air-mist, and foam drilling fluids. The basic approach to accomplishing this objective was to modify GEC's existing electromagnetic (e-m) CABLELESS''{trademark} MWD tool to improve its reliability in air drilling by increasing its tolerance to higher vibration and shock levels (hardening). Another important aim of the program is to provide for continuing availability of the resultant tool for use on DOE-sponsored, and other, ...

International Nuclear Information System (INIS)

Contrary to previous plans for the preparation of diagnostic systems for D-T break-even experiments in the Tokamak Fusion Test Reactor (TFTR), it now appears that a limited Q#approx#1 demonstration can be carried out without constructing a close-fitting igloo radiation shield around the tokamak. In order to assess the impact of D-T operation of TFTR without an igloo shield, particularly with regard to hardening of diagonstic systems, we have mapped neutron and gamma fluxes inside the test cell and test cell basement, using a variety of radiation measurements. The measurements are sufficiently detailed to resolve massive hardware components, such as neutral beams and shielded diagnostic systems, and can be used to predict local fluxes. By comparing the measurements with transport code calculations for the case of a bare tokamak, we conclude that the models have substantially overestimated fluxes both inside and outside the TFTR shield walls. It may be possible to ...

International Nuclear Information System (INIS)

For an assessment of the future US spallation neutron source (SNS) target performance, radiation induced hardening and microstructural evolution were investigated as a function of ion dose for EC316LN stainless steel. Irradiation was carried out using 3.5 MeV Fe"+, 360 keV He"+, and 180 keV H"+ simultaneous ion-beams at 200 deg. C to simulate the damage, He and H production in the SNS target vessel wall. At low dose (< 1 dpa), the predominant defects were black dots whose number density saturated rapidly within a few dpa. This was followed by the evolution of interstitial loops whose number density saturated below 15 dpa. Although He-bubbles were not visible, severely scalloped loops suggested that the implanted He/H atoms existed in the form of small clusters. Comparison with reported neutron irradiation data showed that hardening and ductility loss occurred mostly in the black dot regime (< 1 dpa), but that good ductility (>20% ...

Energy Technology Data Exchange (ETDEWEB)

Effect of the coverage of shot peening, the surface roughness and shot shape, etc. on the stress corrosion cracking (SCC) of Alloy 800 in alkaline solutions was studied. Alloy 800 specimens were cracked in boiling alkaline solutions at the potntial range of {minus} 100 to 0mV in the boiling 50%NaOH+0.3%SiO {sub 2} solution. U bend specimens were tested under the polarized condition at the controlled potential to 0mV, showing that shot peened specimens cracked more easily. Tests of specimens with the same hardness showed that specimens hardened by cold working showed the higher susceptivity than that of surface hardened specimens. In these connections, U bend specimens of higher shot peened coverage were cracked at conditions of 593K and 10%NaOH solution. O-ring specimens of smaller stress level did not show any cracks independent of surface treatments. 8 refs., 9 figs., 5 tabs.

Energy Technology Data Exchange (ETDEWEB)

A model is presented that describes the development of texture during the production process of bake-hardening steel recrystallized in a batch-annealing furnace. Proper conditions are analyzed to generate a pronounced {gamma}-fiber texture and a pancake microstructure that shows superior deep drawability. The {gamma}-fiber texture is assumed to be caused by the interaction between tertiary precipitating aluminum nitride particles and the recrystallization process during heating in the furnace. Deep drawability is presented in terms of the logarithmic {gamma}- and {alpha}-fiber X-ray intensity ratio. The computer simulation of the coupled aluminum nitride precipitation and recrystallization kinetics is based on an iterative procedure. A comparison between simulation results and available experimental data proves the ability of the model to predict the final deep drawability, taking into account the initial aluminum and nitrogen contents, the time/temperature history ...

Energy Technology Data Exchange (ETDEWEB)

We have investigated tailoring damage effects of explosive devices by addition of unconventional materials, specifically combustible metals. Initial small-scale as well as full-scale testing has been performed. The explosives functioned to disperse and ignite these materials. Incendiary, enhanced-blast, and fragment-damage effect have been identified. These types of effects can be used to extend the damage done to hardened facilities. In other cases it is desirable to disable the target with minimal collateral damage. Use of unconventional materials allows the capability to tailor the damage and effects of explosive devices for these and other applications. Current work includes testing of an incendiary warhead for a penetrator.

International Nuclear Information System (INIS)

Generally, Hardening and irradiated brominating phenomena are occurred in the reactor vessel under operation conditions by atomic cavities and creation of impurity atoms which are led by high fast neutron flux. To assure the mechanical integrity of pressure vessel until the end of power plant life after monitoring the sample specimens on the vessel inside, a series of tests is performed over the retrieved surveillance capsule to examine the changes according to the plant operation in accordance with regulations. Monitoring surveillance capsules attached to neutron shield wall of outer core are consists of impact sample, tensile sample and temperature monitor

International Nuclear Information System (INIS)

SP-700, an emerging #beta#-rich #alpha#+#beta# titanium alloy, is designed to improve superplastic formability as well as mechanical properties over Ti-6Al-4V alloy. Owing to its fine microstructure and low #beta#-transus temperature, it is superplastic-formable at temperature below 1,073K (800 C) with low flow stress. Remarkable workability of this alloy is also retained in conventional Manufacturing processes. Another advantage of SP-700 is heat treatment response which includes deep hardenability and quick aging kinetics. Corrosion resistance and machinability are equivalent to or better than Ti-6Al-4V alloy.

British Library Electronic Table of Contents (United Kingdom)

Simplified strain-based fracture mechanics equations, established for external surface cracked pipelines subjected to an external bending load, are presented and used in probabilistic assessment of a pipeline girth weld. The model takes into account several parameters, such as variation in crack depth, crack length, internal pressure and material hardening. The critical strain from ductile tearing in the cracked pipeline is found by using the tangency criterion. The reliability problem is solved using first and second order reliability methods for different pipe dimensions and load levels.

Science.gov (United States)

Deformation experiments performed in-situ in the transmission electron microscope have led to an increased understanding of dislocation dynamics. To illustrate the capability of this technique two examples will be presented. In the first example, the processes of work hardening in Mo at room temperature will be presented. These studies have improved our understanding of dislocation mobility, dislocation generation, and dislocation-obstacle interactions. In the second example, the interaction of matrix dislocations with grain boundaries will be described. From such studies predictive criteria for slip transfer through grain boundaries have been developed.

Energy Technology Data Exchange (ETDEWEB)

The production of many important commercial materials involves the evolution of a complex fluid through a cooling phase into a hardened product. Textile fibers, high-strength fibers(KEVLAR, VECTRAN), plastics, chopped-fiber compounds, and fiber optical cable are such materials. Industry desires to replace experiments with on-line, real time models of these processes. Solutions to the problems are not just a matter of technology transfer, but require a fundamental description and simulation of the processes. Goals of the project are to develop models that can be used to optimize macroscopic properties of the solid product, to identify sources of undesirable defects, and to seek boundary-temperature and flow-and-material controls to optimize desired properties.

International Nuclear Information System (INIS)

Remote-controlled handling systems are required for work to be done in the decommissioning and dismantling of nuclear facilities. These systems are equipped with electronic devices suitable for use in working environments affected by ionizing radiation. The publication explains the step-wise progress achieved for improving the radiation resistance of electronic devices with the example of a four-quadrant controlling device for the motors of a manipulator. The radiation resistance of the device could be enhanced to radiation energies of 5.500 Gy. This means that a manipulator vehicle equipped with this controlling device can take up to approx. 15 kGy all in all, taking into account its own shielding properties. (DG).

International Nuclear Information System (INIS)

Radiation hardening and radiation-induced chromium (Cr) depletion were related to intergranular stress corrosion cracking (IGSCC) response among various stainless steels (SS). Available data on neutron-irradiated materials were analyzed and correlations developed between fluence, yield strength, grain-boundary Cr concentration, and cracking susceptibility in high-temperature water environments. Large heat-to-heat differences in the critical fluence (0.2 neutrons/cm"2 to 2.5 x 10"2"1 neutrons/cm"2) for IGSCC were documented. Variability often was consistent with yield strength differences among irradiated materials. IGSCC correlated better to yield strength than to fluence for most heats, suggesting a possible role for radiation-induced hardening (and microstructure) on cracking. However, isolated heats revealed a wide range of yield strengths (450 MPa to 800 MPa) necessary to promote IGSCC which could not be explained by strength effects alone. ...

Energy Technology Data Exchange (ETDEWEB)

Alloyed steels containing retained austenite after martensitic hardening are widely applied in technical practice. Although many practical investigations have been made into the mechanical behaviour of composite microstructures with retained austenite, there is still a lack of knowledge concerning their fatigue and crack propagation behaviour. For this reason, the author investigated the effects of retained austenite concentration and stability on the transformation and deformation behaviour of hardened states of the steels X210Cr12 and 100Cr6. For this purpose, monotone tensile tests, cyclic tensile pressure tests, and supplementary crack propagation experiments were carried out. The concentrations of retained austenite were varied between 10 and 100% by volume by means of different heat treatments. [Deutsch] Legierte Staehle, die nach martensitischer Haertung noch Restaustenit enthalten, finden in der technischen Praxis verbreitete Anwendung. ...

International Nuclear Information System (INIS)

Effects of helium and hydrogen production on irradiation hardening of martensitic steel F82H (Fe-8Cr-2W-0.2V-0.04Ta-0.1C) were examined by dual or triple beam experiments. The effects of tempering and cold working were also examined. The irradiations were performed at about 500degC to 50 dpa under simultaneous dual beams of 10.5 MeV Fe"3"+ and 1.05 MeV He"+ or triple beams of those and 380 keV H"+ ions. The value of appm-He/dpa for the dual ion beams was about 15, and the values of appm-He/dpa and appm-H/dpa for the triple ion beams were 15 and 15 (or 150), respectively. The hardness of the irradiated specimens measured at room temperature using a micro indentation after the irradiations. Irradiation softening and hardening was observed in F82H-std, F82H+20%CW and a non-tempered F82H steels irradiated at about 500degC to 18 and 50 dpa, respectively, by dual ion beams. The hardness of the specimens irradiated at about 500degC to 18 dpa under ...

International Nuclear Information System (INIS)

Full text of publication follows: Low activation ferritic/martensitic steels are receiving a high priority in the European long term materials research. Although extensively investigated, the available experimental data do not cover all required parameter ranges and cannot unambiguously be used to produce hardening/embrittlement trend curves. Therefore, the main objective of this work is to provide a physically-based engineering model offering a rational to experimental observations. From the literature, experimental data were selected to establish a database that mainly consists of 8 to 9Cr-steels irradiated in the range of 50 to 600 deg. C up to 30 dpa and with a He-content up to 5000 appm. The database includes neutron and proton irradiations, He-implanted as well as B- and Ni-doped steels. Because of the difficulty of interpretation inherent to the Charpy impact test, only tensile data were considered. The difficulty stems from the large range of specimen sizes ...

Science.gov (United States)

A way to synthesize the transient zwitterionic silylene L'Si: 8 {L'=CH[(C=CH(2))CMe(N(tBu))(2)]} and achieve its facile dimerization to the remarkable N-heterobicyclic disilane 8(2) is described. At first, employing the beta-diketiminate ligand L [L=CH(CMeN(tBu))(2)], both starting materials LH (2) and its N-lithium salt LLi (3) can react with SiBr(4) to yield the silylene precursor L'SiBr(2) (4) by silicon-induced C-H activation at an exocyclic methyl group on the backbone of the ligand. Compound 4 reacts with SiBr(4) above room temperature to afford the unexpected terminal CH(SiBr(3))-substituted dibromosilane 6 along with the unique tricyclic trisilane 7. Reduction of 4 with KC(8) at 0 degrees C furnishes the novel N-heterobicyclic disilane 8(2), which is a formal dimer of the desired zwitterionic silylene L'Si: (8). It has been reasoned that compound 8(2) may results from [4+1] cycloaddition of two molecules of 8 to give the transient dimer 8(2)', which subsequently undergoes ...

International Nuclear Information System (INIS)

A series of nine model ferritic alloys were ion irradiated at #propor to#300 C using 2.5 MeV He ions to a dose of 1.4 x 10"2"1 ion/m"2, which corresponds to #propor to#0.1 dpa at a depth of 2 #mu#m and #propor to#3.5 dpa at the peak damage region which occurs at about 4 #mu#m deep. The resultant changes in hardness as a function of depth were measured using a Nanoindenter "t"r"a"d"e"m"a"r"k. TEM was used to investigate the defect distributions. The effect of various solutes, Cu and N in particular, but Mn and Ti as well, on the change of hardness and the defect distribution due to the ion irradiation are discussed. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The operation of the Bullhouse Minewater System, used to treat iron-rich minewaters discharged from long-abandoned coal mines, was studied to minimise pollution of the Upper Don river in the UK. Tests were carried out to determine optimal operating conditions. Ochre flocculation with polyacrylamide was efficient in batch tests as the ochre self-flocculated and sedimented in the lagoon without the need for chemical enhancement. The rate of accretion of the pipework in the system was modified by partial dewatering, reshaping and hardening of the deposits during ageing. Samples of ochre recovered from the drying beds and sump deposits were converted to ferric sulphate coagulant by dissolution with sulphuric acid and used with a polyelectrolyte to successfully purify reservoir water and pretreat wastewater. There was considerable local interest in the scheme with educational opportunities for schools and colleges.

British Library Electronic Table of Contents (United Kingdom)

The purpose of this study is to investigate the influence of tungsten carbide/carbon (WC/C) coating on the surface durability of casehardened steel gear. Two kinds of WC/C coatings were deposited on the ground gear pair made of chromium molybdenum steel with carburizing and quenching. One is the conventional WC/C coating, and the other is WC/C coating with about 1 ?m CrN interlayer. Here, the WC/C-coated test pinion and the WC/C-coated one with CrN interlayer are represented by WT and ST, respectively. Non-coated test pinion is represented by NT. The surface roughness along the tooth profile direction of WT and ST was almost the same as that of NT. A spur gear test was carried out with an IAE power circulating type gear test rig under EP gear oil lubricating condition. The fatal failure mo...

British Library Electronic Table of Contents (United Kingdom)

The X-ray storage phosphor CsBr:Eu2+ in form of needle image plates is believed to be a promising alternative to the granular BaFBr:Eu2+ with regard to PSL yield and spatial resolution. Unfortunately, CsBr:Eu2+ exhibits poor radiation hardness, which is caused by a migration of europium ions initiated by naturally existing defect centers like (Eu2+-VCs)-centers and X-ray generated MEu-centers. It will be shown that the formation of (Eu2+-O2?)-dipoles at the expense of (Eu2+-VCs)-dipoles, incorporated by thermal annealing in O2-containing and humid atmosphere, does not improve the radiation stability. There is, however, a strong improvement in the radiation hardness by codoping of CsBr:Eu2+ with lithium ions, which is accompanied by a complete suppression of the previously observed MEu-cent...

International Nuclear Information System (INIS)

The radiation polymerization of multifunctional unsaturated polyester-monomer mixtures in wood forms interpenetrating network system. The mechanical resistance (compression, abrasion, hardness, etc.) of these composite materials are generally well over the original wood, however the impact strength is almost the same or even reduced, in comparison to the wood itself. An attempt is made using elastic polyester resins to produced wood-polyester composite materials with improved modulus of elasticity and impact properties. For the impregnation of European beech wood two types of elastic unsaturated polyester resins were used. The exothermic effect of radiation copolymerization of these resins in wood has been measured and the dose rate effects as well as hardening dose was determined. Felxural strength and impact properties were examined. Elastic unsaturated polyester resins improved the impact strength of wood composite materials. (author).

International Nuclear Information System (INIS)

Consideration is given to the data, demonstrating the effect of ion radiation on strength characteristics of ionic crystals, presented by magnesium oxide. Crystals, prepared in the form of plates, were irradiated by Si"+, Fe"+, C"+ ions by the dose of 10"1"6-10"1"7 ion/cm"2 at room temperature in vacuum. The following characteristics were investigated: dislocation density, microhardness, crack resistance. Investigation of dislocation structure showed, that dislocation density in irradiated sample was 2-3 times higher, as compared to nonirradiated one. Sufficient increase of fracture viscosity of MgO crystals was revealed. It can be conditioned by occurrence of compression stresses in the surface layer, decelerating crack formation and propagation.

International Nuclear Information System (INIS)

To study #beta# #reversible# #omega#-transformation in pseudo-#beta#-titanium alloy VT30, doped by hydrogen, methods of X-ray diffraction and thermodifferential analyses are used. It is established that in the process of heating of the hardened alloy from 0.004-0.1% H first formation and then dissolution of #omega# phase take place. An increase in hydrogen content to 0.1% decreases thermal effect of the processes and does not affect the temperature of #beta# #reversible# #omega#-transformation. Introduction of hydrogen in the concentration of 0.2% and higher suppresses completely #beta# #reversible# #omega# - transformation. A decrease in heating rate displaces #beta# #reversible# #omega#-transformation to lower temperatures.

CERN Document Server

Google's Android is a comprehensive software framework for mobile communication devices (i.e., smartphones, PDAs). The Android framework includes an operating system, middleware and a set of key applications. The incorporation of integrated access services to the Internet on such mobile devices, however, increases their exposure to damages inflicted by various types of malware. This paper provides a comprehensive security assessment of the Android framework and the security mechanisms incorporated into it. A methodological qualitative risk analysis that we conducted identifies the high-risk threats to the framework and any potential danger to information or to the system resulting from vulnerabilities that have been uncovered and exploited. Our review of current academic and commercial solutions in the area of smartphone security yields a list of applied and recommended defense mechanisms for hardening mobile devices in general and the Android in particular. ...

Energy Technology Data Exchange (ETDEWEB)

The authors obtain the critical load levels corresponding to the onset of spalling microdamage for Armco iron and steels St.3 and 12Kh18N10T in a broad temperature range (-196-800 degrees C. The results of the investigation of the effect of the temperature on spalling fracture are presented. The effect of the loading time on the strength of the investigated materials is also given. The authors assume that at -196 degrees C impact-wave strain-hardening may also be characterized by the value of H obtained for the center of the specimen since measurements on great thicknesses, including those reaching as far as the opposite surface, did not reveal any substantial change of microhardness.

International Nuclear Information System (INIS)

Computer experiments imitating specimen strain on tension with constant deformation rate have been carried out. A formation possibility of atmosphere from defects around gliding dislocations (I) and a work of Frank-Read sources (II) have been accounted for. In result deformation curves until stresses do not exceed a critical shear stress were calculated. Influence of effects (I) and (II) was analyzed. It is determined that both by pass of dislocations over defect ''atmospheres'' and dislocation multiplication can cause a peak in flow stress occurrence on the deformation curves. Reasons and conditions of such peak occurrence have been studied. 12 refs.; 9 figs. (author).

International Nuclear Information System (INIS)

The diagnostic designs for the Laser Megajoule (LMJ) will require components to operate in environments far more severe than those encountered in present facilities. This harsh environment will be induced by fluxes of neutrons, gamma rays, energetic ions, electromagnetic radiations, and, in some cases, debris and shrapnel, at levels several orders of magnitude higher than those experienced today on existing facilities. The lessons learned about the vulnerabilities of present diagnostic parts fielded mainly on OMEGA for many years, have been very useful guide for the design of future LMJ diagnostics. The present and future LMJ diagnostic designs including this vulnerability approach and their main mitigation techniques will be presented together with the main characteristics of the LMJ facility that provide for diagnostic protection.

International Nuclear Information System (INIS)

A radiation hard low power, low voltage dynamic memory is obtained by the use of a dummy cell concept. Compared to conventional dummy cell concepts, this concept applies a fully sized dummy cell. By optimizing the dummy cell precharge voltage for 5 V and 3 V operation and the timing of the dummy word-line, the overall soft error rate (SER) of the chip is improved by 2 orders of magnitude. An additional improvement of 1 order of magnitude is possible for 3 V operation by adjusting substrate bias and cell plate voltage. The results are verified by an accelerated SER measurement with a radium 226 source and an additional field soft error study.

International Nuclear Information System (INIS)

There are reported the results of corrosion resistance investigation of aluminium bronzes, containing about 8 and 10% of aluminium and modifying quantities of zirconium. The tests of corrosion resistance were carried out in synthetic seawater, in 3% NaCl aqueous solution and in 10% H_2SO_4 aqueous solution, with reference to industrial bronze BA93 (CuAl9Fe3). The bronzes were tested in an annealed, hardened, tempered state and after plastic hot working. The conclusion is that corrosion resistance of aluminium bronzes, especially against selective corrosion, depends more on material structure, resulted form heat treatment, than on chemical composition. (author). 6 refs, 8 figs, 6 tabs.

Energy Technology Data Exchange (ETDEWEB)

Computed tomography (CT) has been incorporated in an industrial Diode-Array Digital Radiography (DADR) system. An input data size of 512 pixel points x 400 projections yielded a 400x400 output image matrix. Reconstruction algorithms used are the filtered backprojection (FBP) and the direct Fourier reconstruction (DFR). Various filters were used in the FBP reconstruction process and their effects on image quality were evaluated. A spatial resolution of 100 {mu}m was measured with a block of plates and a minimum detectable feature size in the range of 10-100 {mu}m was measured using thin wires. Industrial specimens imaged have included ceramic samples, ball bearings and integrated circuits. A number of engineering problems have been solved, such as adjustment of the X-ray source, centering of the rotator spindle in the view field and beam-hardening corrections. (orig.).

Energy Technology Data Exchange (ETDEWEB)

An approach to the ductile fracture of ultra high strength steels has been evaluated. According to this approach the critical crack tip opening, delta/sub IC/, will scale with X/sub 0/(R/sub V//R/sub I/vertical bar/sub R//sub 0/. X/sub 0/ is an average inclusion spacing and (R/sub V/R/sub I/)vertical bar/sub R//sub 0/ is the void radius divided by the radius of the inclusion nucleating the void evaluated at the average inclusion size. AF1410 was selected to test this approach because it has exceptionally high fracture toughness on aging at 510/sup 0/C and because its toughness varies markedly with aging temperature. The results from this and earlier work showed a linear relationship exists between delta/sub IC/ and X/sub 0/(R/sub V//R/sub I/)vertical bar /sub R//sub 0/ for values of delta/sub IC/ ranging from about 8 ..mu..m to 60 ..mu..m. The values of (R/sub V//R/sub I/)vertical bar /sub R//sub 0/ for AF1410 aged at 425/sup 0/C and 510/sup 0/C differed by a factor of two. Because the ...

International Nuclear Information System (INIS)

Post-irradiation annealing was used to help identify the role of radiation-induced segregation (RIS) in irradiation-assisted stress corrosion cracking (IASCC) by preferentially removing dislocation loop damage from proton-irradiated austenitic stainless steels while leaving the RIS of major and minor alloying elements largely unchanged. The goal of this study is to better understand the underlying mechanisms of IASCC. Simulations of post-irradiation annealing of RIS and dislocation loop microstructure predicted that dislocation loops would be removed preferentially over RIS due to both thermodynamic and kinetic considerations. To verify the simulation predictions, a series of post-irradiation annealing experiments were performed. Both a high purity 304L (HP-304L) and a commercial purity 304 (CP-304) stainless steel alloy were irradiated with 3.2 MeV protons at 360 deg. C to doses of 1.0 and 2.5 dpa. Following irradiation, post-irradiation anneals were performed at temperatures ranging ...

Energy Technology Data Exchange (ETDEWEB)

Roller compacted concretes (RCC) were developed for the Norwegian Skjerka hydropower project. RCCs were developed to have a high-volume fly ash content to address environmental issues, including the reduction of carbon dioxide emissions associated with dam construction. They also makes good use of waste product and conserve natural resources. This study examined a series of mixtures to determine the appropriateness of using RCC as a competing alternative to the traditional rock fill dam proposed for the Skjerka hydropower project. The main advantage of RCC is speed, allowing a relatively large dam to be constructed in just one summer season, saving financial costs and providing early return on the investment. In addition, fly ash can be used in the structure, using clean and renewable energy. Several procedures to proportion RCC mixtures were proposed, including the optimal paste volume method which is based on the assumption that an optimal RCC should have just enough paste to fill ...

International Nuclear Information System (INIS)

Three ternary austenitic alloys (Fe-15Cr-25Ni, Fe-15Cr-25Ni-0.04P, Fe-15Cr-45Ni in both annealed and cold worked conditions) were irradiated at 465 C to 0.15, 0.28, and 0.42 dpa at above core position in the Fast Flux Test Facility utilizing the Materials Open Test Assembly to study the separate and synergistic effects of He/dpa ratio, phosphorus addition, nickel content and cold work level on microstructural evolution and hardening. The helium/dpa ratio was varied by isotopic doping with "5"9Ni to enhance the production rate of helium. The helium production rate was evaluated to be 62 appm He/dpa in the "5"9Ni-doped specimens and 0.26 appm He/dpa in the undoped specimens. Transmission electron microscopic examinations revealed that alloy composition affected significantly the evolution of microstructure during irradiation. Phosphorus addition prevented the formation of Frank loops through the precipitation of phosphide. Nickel content influenced the nucleation of ...

Science.gov (United States)

An evaluation of eastern shale oil as an asphalt additive to reduce oxidative age hardening and moisture susceptibility is being conducted. An eastern shale oil residue having a viscosity of 1.30 Pa`s at 60{degrees}C (140{degrees}F) was blended with three different petroleum-derived asphalts that are known to be very susceptible to oxidative aging. In addition, blends of the eastern shale oil residue and the petroleum-derived asphalts are being coated onto three different aggregates that are known to be susceptible to water stripping. The oxidative age hardening portion of this study is not complete at this time. To date, information has been obtained on the unaged samples and two of the aged petroleum-derived asphalts (AAD-1 and AAK-1). When complete, this data will include rheological data on the unaged, RTFO-aged, and the RTFO/PAV-aged samples and infrared data on the unaged and RTFO/PAV-aged samples. With respect to the rheological data, ...

Energy Technology Data Exchange (ETDEWEB)

Titanium alloys are characterized by poor tribological properties, and the traditional use of titanium alloys has been restricted to nontribological applications. The deposition of a well adherent diamond coating is a promising way to solve this problem. In this study, the tribological properties of diamond-coated titanium were studied using a pin-on-disk tribometer, and the results were compared with those of pure titanium and plasma nitrided titanium. The tribological behavior of pure titanium was characterized by high coefficient of friction and rapid wear of materials. Plasma nitriding improved the wear resistance only under low normal load; however, this hardened layer was not efficient in improving the wear resistance and the friction properties under high normal load. Diamond coating on pure titanium improved the wear resistance of titanium significantly. Surface profilometry measurement indicated that little or no wear of the diamond coating occurred under ...

Energy Technology Data Exchange (ETDEWEB)

The effect of accelerated thermal cycling on a joint between modified 9Cr-1Mo steel (Grade 91) and Alloy 800 welded with Inconel 82 and 182 filler material is discussed. This is part of a trimetallic transition joint involving Grade 91-Alloy 800-316LN austenitic stainless steel for steam generator application. It has been shown that, during thermal cycling following the typical post-weld tempering treatment at 760 deg. C for 2 h, no carbon diffusion occurs from the ferritic steel towards the weld metal. There is, in fact, a hardness increase at the ferritic steel/weld metal interface which is probably a result of work hardening. Carbon migration sets in only after unusually long post-weld heat treatments for 20 and 50 h at 760 deg. C followed by thermal cycling. Significantly, even under the most severe thermal cycling test conditions imposed, no cracking or oxide notching could be detected, thus demonstrating the superior performance potential of modified 9Cr-1Mo ...

Energy Technology Data Exchange (ETDEWEB)

By using a plasma nitriding procedure at the PUPR Mirror Cusp Plasma machine, surface hardness is increased in 302/304-type stainless steel samples by exposing them to high-ion-density plasma at high vacuum. This method successfully dopes the surface of the material with strengthening nitrogen ions, without the use of chemical procedures that sacrifice the resistance to corrosion of the given material. A 500 V negative bias is placed on the sample exposed to the nitrogen plasma, where high-energy ions are therefore attracted and immersed into the metallic matrix microns into the surface of the stainless steel. This potential maintains a constant surface temperature at approximately 800 deg. C. The plasma parameters including ion density and plasma temperature were diagnosed using single Langmuir probes. The stainless steel samples were then tested using scanning electron microscopy (SEM), and Vickers micro-hardness testing to determine the increment in the surface harness of the ...

International Nuclear Information System (INIS)

In interventional radiology (IVR) of cerebral aneurysms, it is important to understand the form and physical relationships between the cerebral aneurysm and the surrounding vessels. However, because the vessels in the head area are highly complex, it can be difficult to comprehend the structure using conventional angiography. Therefore, three-dimensional rotational angiography (3D-RA) has been used in recent years. This article discusses studies of the spatial resolution of 3D-RA. We reconstructed 3D-RA of an acrylic slit phantom (slit widths: 0.5, 0.75, 1.0, 1.5 mm) and examined spatial resolution by visual evaluation and profile curves. When the slit phantom was arranged to avoid the effect of beam hardening, the spatial resolution of 3D-RA was found to be as high as 0.75 mm. When the slit phantom was placed orthogonal to the rotational axis of the C-arm, the spatial resolution of 3D-RA was decreased because of the cone angle effect of X-rays. However, it was ...

Energy Technology Data Exchange (ETDEWEB)

Material testing of SPF-sheet is usually done with coupon hot tensile testing. The optimum range of strain rates is determined with stepped strain tests. To overcome the problem of very few available testing facilities and time consuming and costly procedure, cone cup testing has been developed since long. This test can be generated directly in the workshop, no machining of samples is necessary and it is very much related to the real SPF-process. The analysis of suitable temperature and strain rate is done by simple measurement of resulting cone height. This paper describes a unique and novel variant of the above mentioned baseline design. It provides on-line data of the actual status of the cone cup forming resulting from the applied, constant pressure. Strain rate variations as a result from texture or from the alloy-related behaviour is detectable. Thinning and ''hardening'' behaviour of different alloys up to maximum failure ...

International Nuclear Information System (INIS)

Technique, allowing to investigate straggling zone (full braking) from high-energy charged particles in detail, is described. Experimental results on investigation of efective structure, created in polycrystalline molybdenum (99.97%) within 29 MeV alpha-particles straggling zone for fluences from 3.8x10"1"9 up to 3.7x10"2"1 #alpha#/m"2 by methods of microhardness (H_#mu#, X-ray structural analysis (#DELTA#a/a) and transparent electron microscopy (TEM), are presented. It is determined, that for doses from 3.8x10"2"0 #alpha#/m"2 and higher, at #approx#6 MeV energy, molybdenum ''softening'' is observed, H_#mu# curve within straggling zone is well described by alloyage calculated profile. #DELTA#a/a measurements within straggling zone are well described by damage profile. TEM-investigations have shown the developed defective structure even within molybdenum ''softening'' range.

International Nuclear Information System (INIS)

The aim of this work is to describe the processes during plasma nitriding of Nb-containing, powder metallurgy prepared (PM) tool steel. PM steel was studied containing 2.5% C, 3.3% Si, 6.2% Cr, 2.2% Mo, 2.6% V, 2.6% Nb and 1.0% W, produced by melt atomization and hot isostatic pressing. The hardened and tempered steel was plasma nitrided at temperatures ranging from 470 to 530 deg. C. The nitriding time was 30-180 min. Optical microscopy, electron microscopy, XRD, EDS, WDS and hardness measurements were used to study the steel's properties, microstructure, phases and chemical composition. The nitriding temperature of 470 deg. C was found to be unsuitable for practical use because the layers prepared at this temperature were non-uniform. The compound layer formed by M_2_,_3(C,N) and M_4N was found after nitriding at temperatures of 500 and 530 deg. C for at least 60 min. The effect of niobium on the formation of this layer was studied.

International Nuclear Information System (INIS)

The service conditions for high-temperature heat-exchangers with helium coolant of HTGRs and requirements imposed on materials for their production are discussed. The choice of nickel-base alloys with solid-solution hardening for long-term service at high temperatures is grounded. Results of study on properties and structure of types Ni-25Cr-5W-5Mo and Ni-20Cr-20W alloy in the temperature range of 900 deg. - 1,000 deg. C are given. The ageing of Ni-25Cr-5W-5Mo alloy at 900 deg. - 950 deg. C results in decreased corrosion-mechanical properties and is caused by the change of structural metal stability. Alloy with 20% tungsten retains a high stability of both structure and properties after prolonged exposure in helium at above temperatures. The alloy has also increased resistance to delayed fracture and low-cycle fatigue at high temperatures. The developed alloy of type Ni-20Cr-20W with microalloying is recommended for production of tubes for HTGR high-temperature ...

International Nuclear Information System (INIS)

In the present study a partial replacement of aggregate with two different ratios of waste rubber (5%, 10%) with the addition of a constant ratio of rice husk ash (RHA), 5% was carried out. The hardened cement mortar used the optimum water of consistency. The specimens were molded into 1 inch cubic moulds .The specimens were first cured for 24 hours, at 100% relative humidity and then cured under tap water for 3, 7 and 28 days followed by irradiation at different doses of gamma irradiation namely 5 and 10 kGy. The physico-chemical and mechanical properties such as compressive strength, total porosity and bulk density were studied for the three types of specimens. The results showed that the values of the compressive strength, bulk density and chemically combined water of the blended cement mortar paste (OPC-RHA) increase ,while blended cement mortar paste with 5% RHA and 5, 10% waste rubber decrease. The results were confirmed by scanning electron microscopy and ...

Science.gov (United States)

The paper briefly describes the nuclear reactor facilities at Sandia Laboratories which are used for simulating nuclear weapon produced neutron environments. These reactor facilities are used principally in support of continuing R and D programs for the Department of Energy/Office of Military Application (DOE/OMA) in studying the effects of radiation on nuclear weapon systems and components. As such, the reactors are available to DOE and DOD agencies and their contractors responsible for the radiation hardening of advanced nuclear weapon systems. Emphasis is placed upon two new reactor simulation sources; the Sandia Pulse Reactor-III (SPR-III) Facility which enhances the neutron exposure volume capabilities over those presently available with the existing SPR-II Facility, and the Upgraded Annular Core Pulse Reactor (ACPR) Facility which enhances the neutron exposure capabilities over those of the former ACPR Facility.

Energy Technology Data Exchange (ETDEWEB)

Aerospace gas turbine disks operate in an environment of relatively high stresses caused by centrifugal forces and elevated temperatures. These severe conditions necessitate the need for materials with high temperature strength and good low cycle fatigue resistance. One class of alloys used for this task is the nickel base superalloys, out of which, IN 718 is the most widely used in the aerospace industry. The properties of IN 718 are attributed to the combined effects of the chemistry, heat treatment, and microstructure. The chemistry is tailored not only for solid solution strengthening but also for precipitation hardening developed during heat treatment, which combined with a fine grained microstructure lead to excellent mechanical properties such as low cycle fatigue resistance and elevated temperature strength. The properties of a gas turbine disk are sensitive to the microstructure, in particular the grain size, which is dependent on the processing history. ...

Energy Technology Data Exchange (ETDEWEB)

The low-cycle fatigue properties of the ferritic-martensitic steels MANET I and II and F82H-mod, have been investigated at a temperature of 200 C. The strain-controlled fatigue has been performed with strain ranges between 0,4% and 1,0% and at a strain rate of 8.10{sup -4} s{sup -1}. The steel F82H-mod, is characterised by a higher plastic strain amplitude compared to MANET I and II. Some of the specimens have beenirradiated with a 104 MeV {alpha}-particle beam. The homogeneous implantation of 400 appm He leads to a hardening of the material. At the beginning of the fatigue tests the stress response of the irradiatedspecimens is higher compared to the unirradiated specimens. In general, thematerial shows softening during fatigue. The softening of irradiated material, which is fatigue tested with a high total strain amplitude, is higher than that of the unirradiated material. The lifetime is reduced. For irradiated specimens fatigued at small total strain amplitudes ...

International Nuclear Information System (INIS)

The corrosion resistance of zircaloy is affected by conditions of heat treatment in the manufacturing steps to be formed into a final product as a structural material. In the manufacturing method of the present invention, a Zr alloy controlled to contain Sn: 0.8 to 1.2wt%, Fe: 0.17 to 0.28wt%, Cr: 0.05 to 0.15wt%, Ni: 0.04 to 0.10wt%, Nb: 0.01 to 0.09wt%, oxygen: 1,000 to 1,500ppm and Si, an Si impurity at a concentration of 120ppm or less and balance of Zr is melted into a cast piece, to which #beta# hardening is applied. Then, rolling and annealing treatment are applied so that the total heat input amount to the material: #SIGMA#Ai ranges from 1 x 10"-"1"9 to 1 x 10"-"1"7. With such procedures, a Zr alloy structural material for a reactor core having excellent homogeneous corrosion resistance and hydrogen absorption resistance for a long period of time while having a sufficient strength can be obtained even in a case where Sn content is relatively low as from 0.8 ...

Energy Technology Data Exchange (ETDEWEB)

Strain controlled fatigue experiments on the modified ferritic-martensitic 12% Cr-steel Manet have been performed during, after and without irradiation. Continuous push-pull cycling of the hollow fatigue specimens with a cycle ratio R=-1, an axial strain rate of 8.10{sup -4} s{sup -1} and total strain ranges {Delta}{epsilon}{sub t} between 0.42% and 1.0% has been applied in vacuum (5.10{sup -3} Pa) at T=250 C. For the irradiation, a 104 MeV {alpha}-particle beam was used. Compared to unirradiated specimens, in-beam specimens undergo irradiation hardening at an advanced fatigue/implantation stage. Post-irradiation specimens show significantly higher total stress amplitudes and reduced fatigue lives. TEM investigations of in-beam and post-irradiation specimens reveal helium bubbles with different diameters on internal surfaces and in the matrix. (orig.).

Energy Technology Data Exchange (ETDEWEB)

High temperature deformation behavior of AZ31 Mg alloy was investigated in this study on the basis of a processing map ({epsilon} {approx} 0.6). To construct a processing map, compression tests were carried out at various temperatures and strain rates. Two regions of high deformation efficiency ({eta}) were identified as: (1) a dynamic recrystallization (DRX) domain at 250 C and 1/s and (2) a superplasticity domain at 450 C and 10{sup -4}/s. The average grain size observed in the DRX region was considerably smaller (2.9{mu}m) than in any other region. In the superplastic condition, tensile elongation to failure approached to 1040%. At the high Z regions, flow softening occurred resulting from the dynamic recrystallization but below 10{sup 10} of Z value, flow hardening occurred due to the grain growth. Possible deformation mechanisms operating at high temperature were discussed in relation to the activation energy. A two-stage deformation method was found to be ...

Energy Technology Data Exchange (ETDEWEB)

Graphite fluoride (CF{sub x}) is investigated as an additive for WS{sub 2} thin films to reduce its sensitivity to moisture. The films are grown onto hardened 440C stainless steel disks by pulsed laser deposition using the 248 nm line from an excimer laser. Substrate temperature and additive concentration are varied to control film chemistry and crystal structure. The effect of relative humidity (i.e., < 1 to 85% RH) on friction is evaluated. Coatings grown at RT from targets with a low concentration of CF{sub x} exhibit ultra-low friction (ULF) behavior in dry air (i.e., {mu} {<=} 0.01), but friction increases with RH. Mechanisms for the ULF behavior are proposed which suggest that further reductions in friction are possible. Films grown at 300 C or with higher concentrations of CF{sub x} are relatively insensitive to humidity, but have more typical friction coefficients ({mu} {<=} 0.04) in dry air. (orig.)

Energy Technology Data Exchange (ETDEWEB)

A press formability of magnesium alloy sheet cannot be evaluated by only general characteristics in tensile test; tensile strength, elongation n-value and r-value. For example, AZ31-alloy elongates about 20% in room temperature but breaks easily at shallow stage in deep drawing, which is caused by little local elongation (local necking). Crystallographic restriction of slip deformation in this alloy produces high strength, which almost equal to macroscopic fracture strength. In press forming, the bending under high tension requires a large deformability. A great difference in the deformability between AZ31 magnesium alloy and a strain hardened A1100 Aluminum (only 5% in elongation) is shown by static bending test with V-notch. In a rolled plate of AZ31, a crack is produced by stress concentration and propagates with reduced load at all testing temperature up to 453 K. In contrast, the point of notch in A1100 is dulled by local plastic deformation with held load in ...

Energy Technology Data Exchange (ETDEWEB)

A modified boundary element approach was used to analyze the response of offshore piles subjected to external soil movements. The computer model employed to solve the pile-soil problem was able to model pile head and tip loading, and loading caused by lateral movement of soil. A nonlinear pile-soil interface element with the ability to represent a hardening or softening plastic response prior to reaching an ultimate state was incorporated. With the program, 4 failure modes can be determined: flow of the soil slide past an intact stationary pile; rotation of the pile with the soil at failure along the full pile length; translation of the pile with the sliding soil, resulting in failure of the supporting soil; and the long-pile mode, in which the maximum bending moment in the pile reaches the yield moment of the pile before complete development of the other 3 modes. Theoretical solutions for a realistic hypothetical offshore pile subjected to submarine slides are ...

Energy Technology Data Exchange (ETDEWEB)

Tensile specimens of the normalized and tempered fully martensitic steel DIN 1.4914 were helium implanted up to 340 appm within the temperature range 300-720/sup 0/C using a 104 MeV alpha particle beam. The high He/damage ratio of 1850 appm He/dpa allowed to determine the effect of helium on material properties. After irradiation tensile strength and ductility were investigated mainly at test temperatures equal to the irradiation temperatures. While short time irradiations with helium contents up to 100 appm have shown no visible effect on the tensile behaviour at all temperatures investigated, long time irradiations reduced the material strength at irradiation temperatures above about 440/sup 0/C. This irradiation induced softening obscured the predicted minor hardening effect of the observed He-bubbles completely and increases with irradiation time and temperature. The fracture mode of helium-implanted and control specimens is found to remain always ductile and ...

Energy Technology Data Exchange (ETDEWEB)

Determination of stacking fault energy (SFE) of the austenite phase of a duplex stainless steel DIN W.-Nr.: 1.4462 has been carried out using transmission electron microscopy. Furthermore, cold rolling tests and microstructural analysis have been realized in order to allow a detailed discussion of the obtained SFE-values. The results of this investigation indicate that the stacking fault energy of the austenite phase within the duplex stainless steel is lower than of one-phase austenitic stainless steels. This is justified by the chemical composition, mainly by the Cr and Ni alloying contents. Nevertheless, work hardening of the austenite during cold deformation is not as accentuated as expected by the SFE-values, because at higher deformation levels the deformation mainly occurs within the ferrite phase 7 refs., 5 figs., 2 tabs.

Energy Technology Data Exchange (ETDEWEB)

This invention relates to the production method of composite electrode substrate for fuel cell. An impermeable material is used for edge sealant. The sealant is put in the clearance between two electrodes consisting of porous carbon material via thermoplastic resin sheet, and heated while being pressed. This production method increases the adherence between the porous carbon bodies and reduces the contact resistivity at the joint interface. Consequently, it becomes possible to produce the composite electrode for fuel cell without separator, resulting in simplification of assembly work, weight reduction, and downsizing. The preferable porous carbon body is made from shrinkage-treated fiber. After sheet forming, the thermosetting resin is impregnated, and then it is burnt to carbonization. Or mixed sheet of rayon and acrylic fiber is laminated to be heated and pressed without impregnating the resin. The pressed resin is then burnt to carbonization. The preferable sealant for the edge of ...

Energy Technology Data Exchange (ETDEWEB)

The mechanical behaviour of wrought magnesium alloy AZ31 has been characterised by tensile testing at room temperature. Tests were carried out at various strain rates between 0.00003 s{sup -1} and 0.01 s{sup -1} on material which had been extruded to a bar of approximately 6 mm thick, and 80 mm wide. Specimens were machined from three orientations relative to the extrusion direction: parallel, perpendicular, and 45 from the extrusion direction. Significant variations of the properties were observed depending on the extrusion orientation and strain rate. At all strain rates the yield stress declined as the test orientation was rotated away from the extrusion direction. Parallel to the extrusion direction, the yield stress was found to increases markedly with increasing strain rate, whereas at 45 and 90 a lesser influence of strain rate was observed. The work hardening exponent was also influenced by the test orientation. Metallographic studies revealed a ...

Energy Technology Data Exchange (ETDEWEB)

The possibility of improving the cold formability of wrought magnesium alloys is considered in light of their good hot forming characteristics. Magnesium alloy AZ31B sheet is selected as a model system. Parameters affecting formability, such as strain hardening rate, strain rate sensitivity, and the degree of anisotropy are examined systematically by conducting tensile tests over a range of temperatures (room temperature to 250 C) and strain rates (1 x 10{sup -5} to 0.1 s{sup -1}). The plastic anisotropy and deformation texture evolution are examined in samples aligned with the sheet rolling and transverse directions. Polycrystal plasticity simulations using a viscoplastic self-consistent (VPSC) formulation are used to model the observed anisotropy and texture evolution. The adjustable parameters in the model are the relative critical resolved shear stresses of the dislocation mechanisms known to operate within magnesium. The experimental results suggest that an ...

International Nuclear Information System (INIS)

This paper presents a new methodology to create realistic 3D microstructures of polycrystals. The virtual microstructures are based on statistical data describing the morphological and crystallographic textures of a sample, obtained from an EBSD analysis. In addition, the methodology can reproduce the observed surface on top of the simulated microstructure. This feature allows finite element calculations on these virtual aggregates to be compared to experimental results of mechanical tests. Such a comparison leads to the identification of the mechanical parameters of constitutive laws, such as critical resolved shear stress and strain hardening, using an optimization algorithm. Two materials were simulated in this study: TiAl and grade 702 zirconium. The first one presents twins inside the microstructure and the second one has an anisotropic texture. Based on 2D simulations, the important parameters necessary to describe a microstructure were identified as grain ...

Science.gov (United States)

With an increased use of fiber reinforced concrete in structural applications, proper characterization techniques and development of design guides are needed. This dissertation presents a multi-scale modeling approach for fiber and fabric reinforced cement-based composites. A micromechanics-based model of the yarn pullout mechanism due to the failure of the interfacial zone is presented. The effect of mechanical anchorage of transverse yarns is simulated using nonlinear spring elements. The yarn pullout mechanism was used in a meso-scale modeling approach to simulate the yarn bridging force in the crack evolution process. The tensile stress-strain response of a tension specimen that experiences distributed cracking can be simulated using a generalized finite difference approach. The stiffness degradation, tension stiffening, crack spacing evolution, and crack width characteristics of cement composites can be derived using matrix, interface and fiber properties. The theoretical models ...

International Nuclear Information System (INIS)

Conventional plasma carburizing or nitriding for austenitic stainless steels results in a degradation of corrosion resistance. However, a low temperature plasma surface treatment can improve surface hardness without deteriorating the corrosion resistance. The 2-step low temperature plasma processes (the combined carburizing and post nitriding) offers the increase of both surface hardness and thickness of hardened layer and corrosion resistance than the individually processed low temperature nitriding and low temperature carburizing techniques. In the present paper, attempts have been made to investigate the influence of the introduction of Ar gas (0#approx#20%) in nitriding atmosphere during low temperature plasma nitriding at 370 .deg. C after low temperature plasma carburizing at 470 .deg. C. All treated specimens exhibited the increase of the surface hardness with increasing Ar level in the atmosphere and the surface hardness value reached up to 1050 HV_0_._1, ...

Energy Technology Data Exchange (ETDEWEB)

The effect of partial and total replacement of tungsten by molybdenum on the mechanical technical properties were investigated with the cold work steel 60 WCrV 7 (DIN 1.2550). While maintaining the total quantity of tungsten atoms and/or molybdenum atoms in the steel, no differences occur in the type of the separated carbides. After annealing in the range of the pearlite stage with annealing times of up to 150 h, the carbide phases M/sub 23/C/sub 6/ and MC are, besides alpha iron, also present. In short-time annealed states also M/sub 6/C carbides occur. These are formed during austeniting and remain in the steel as residual carbides in austeniting treatment carried out under normal conditions. Compared with tungsten alloyed steel, there is an increased formation of M/sub 6/C carbides in molybdenum alloyed steels during austeniting. By a long-time annealing treatment in the range of the pearlite stage, the M/sub 6/C carbides are dissolved in favour of the M/sub 23/C/sub 6/ carbides. ...

Energy Technology Data Exchange (ETDEWEB)

In attempting to detect and map out underground facilities, whether they be large-scale hardened deeply-buried targets (HDBT's) or small-scale tunnels for clandestine border or perimeter crossing, seismic imaging using reflections from the tunnel interface has been seen as one of the better ways to both detect and delineate tunnels from the surface. The large seismic impedance contrast at the tunnel/rock boundary should provide a strong, distinguishable seismic response, but in practice, such strong indicators are often lacking. One explanation for the lack of a good seismic reflection at such a strong contrast boundary is that the damage caused by the tunneling itself creates a zone of altered seismic properties that significantly changes the nature of this boundary. This report examines existing geomechanical data that define the extent of an excavation damage zone around underground tunnels, and the potential impact on rock properties such as P-wave and ...

Energy Technology Data Exchange (ETDEWEB)

The chemical fixation of tritium in stearic acid followed by embedding the tritiated stearic acid into an epoxy resin proved to be a good method for permanent waste disposal of tritium gas. Tc-126 and Tc-136 hardener were used for this purpose. The polymerization temperature of the polymer products was found to be highly decreased by adding stearic acid and slightly decreased by adding stearic acid or by raising the temperature of the leachant medium and slightly decreased by irradiation. On the other hand, small improvement in the compressive strength of the polymer products was achieved by adding silica powder. The polymer product showed high flame points above 573 K although it contains stearic acid. DTA and TG analysis indicate that the thermal stability of polymer products containing stearic acid and silica powder is better than samples containing only stearic acid. Stearic acid was found to possess good resistance to irradiation and the amount of hydrogen and ...

International Nuclear Information System (INIS)

With the fire accident in Browns Ferry nuclear power plant as a turning point, the regulation against fire has been strengthened more strictly as seen in the regulatory guide of the United States Nuclear Regulatory Commission. Fire of cables is caused by either the ignition of a cable itself or spread of fire to cables. The aspect of fire is divided into the local ignition and combution and the fire extension and prepagation because of the line-shaped configuration of cables. This report describes the prevention of the spread of fire. As the materials for the prevention of fire spread, fire spread-preventing paint ''Dannekka'', sealant ''Danseal P and L'', and fire prevention tape ''FD tape'' are reported, and the testing method and the results are described in detail. ''Dannekka'' is classified into the solvent dispersion type and the water dispersion type. It may be coated with brush or by spraying. Seal material is required not only to be flame preventive but also to be leak tight. ...

Energy Technology Data Exchange (ETDEWEB)

The structure and pore morphology, the isothermal and continuous time-temperature conversion characteristics and the effects of heat treatment on the mechanical properties and microstructural processes were investigated in 4 copper-free recycleable PM steels Fe4Ni0,5Mo+0,5%C ({rho}=7,12 g/cm{sup 3}, HT-sintered), Fe4N0,5Mo+0,7%C ({rho}=7,12 g/cm{sup 3}, sinter-hardened), Fe1,5Mo+0,5%C and Fe1,5Mo+0,5%C+0,5%CEP ({rho}=7,3 resp. 7,32 g/cm{sup 3}, HT-sintered). [German] In dieser Arbeit wurden an den vier kupferfreien rezyklierfaehigen PM-Staehlen Fe4Ni0,5Mo+0,5%C ({rho}=7,21 g/cm{sup 3}, hochtemperaturgesintert), Fe4Ni0,5Mo+0,7%C ({rho}=7,12 g/cm{sup 3}, sintergehaertet), Fe1,5Mo+0,5%C und Fe1,5Mo+0,5%C+0,5%CEP ({rho}=7,3 bzw. 7,32 g/cm{sup 3}, hochtemperaturgesintert) die Gefuege und die Porenmorphologie, das isotherme und kontinuierliche Zeit-Temperatur-Umwandlungsverhalten, sowie der Einfluss verschiedener Waermebehandlungen auf die mechanischen Eigenschaften und ...

Science.gov (United States)

The Savannah River Site (SRS) is a 310-square-mile United States Department of Energy nuclear facility located along the Savannah River (SRS) near Aiken, South Carolina. Nuclear weapons material production began in the early 1950s, utilizing five production reactors. In the early 1990s all SRS production reactor operations were terminated. The first reactor closure end state declaration was recently institutionalized in a Comprehensive Environmental Response and Compensation and Liability Act (CERCLA) Early Action Record of Decision. The decision for the final closure of the 318,000 square foot 105-P Reactor was determined to be in situ decommissioning (ISD). ISD is an acceptable and cost effective alternative to off-site disposal for the reactor building, which will allow for consolidation of remedial action wastes generated from other cleanup activities within the P Area. ISD is considered protective by the regulators, U. S. Environmental Protection Agency (US EPA) and the South ...

International Nuclear Information System (INIS)

The convolution/superposition calculations for radiotherapy dose distributions are traditionally performed by convolving polyenergetic energy deposition kernels with TERMA (total energy released per unit mass) precomputed in each voxel of the irradiated phantom. We propose an alternative method in which the TERMA calculation is replaced by random sampling of photon energy, direction and interaction point. Then, a direction is randomly sampled from the angular distribution of the monoenergetic kernel corresponding to the photon energy. The kernel ray is propagated across the phantom, and energy is deposited in each voxel traversed. An important advantage of the explicit sampling of energy is that spectral changes with depth are automatically accounted for. No spectral or kernel hardening corrections are needed. Furthermore, the continuous sampling of photon direction allows us to model sharp changes in fluence, such as those due to collimator tongue-and-groove. The ...

Energy Technology Data Exchange (ETDEWEB)

Nanosatellite space launches could significantly benefit from an electrically powered launch complex, based on an electromagnetic coil launcher. This paper presents results of studies to estimate the required launcher parameters and some fixed facility issues. This study is based on electromagnetic launch, or electromagnetic gun technology, which is constrained to a coaxial geometry to take advantage of the efficiency of closely-coupled coils. A baseline configuration for analysis considers a payload mass of 10 kg, launch velocity of 6 km/s, a second stage solid booster for orbital insertion, and a payload fraction of about 0.1. The launch facility is envisioned as an inclined track, 1-2 km in length, mounted on a hillside at 25 degrees aimed in the orbital inclination of interest. The launcher energy and power requirements fall in the range of 2000 MJ and 2 MW electric. This energy would be supplied by 400 modules of energy storage and magnetic coils. With a prime power generator of 2 ...

International Nuclear Information System (INIS)

Immobilization of a model liquid organic pollutant, i.e. the 2-chloroaniline (2-CA), into a cement matrix using organoclays as pre-sorbent agents was investigated. Five cement-clay pastes were prepared with different nominal water-to-cement ratios (w/c=0.40, 0.25 and 0.15 wt/wt) and various amounts of waste (waste-to-cement o/c=0.20, 0.60 and 1.00 wt/wt); for comparison, a neat cement paste was also prepared. Dynamic leach tests were performed on solidified monoliths in order to assess the successful immobilization of the 2-CA. In monoliths at constant w/c ratio (0.40) the total amount of pollutant released increases with its initial content, and ranges from 15 to 35% with respect to it. By lowering w/c from 0.40 to 0.15 at constant o/c, the performances improved (<25% released). The microstructure of the hardened cement-clay pastes was characterized by quantitative X-ray diffraction (QXRD) and electronic microscopy (SEM-EDS) techniques; hydration degree was ...

International Nuclear Information System (INIS)

Depth sensing indentation tests were carried out to obtain load-penetration depth curves of SiAlON-ZrO_2 ceramics under different peak loads ranging from 200 to 1800 mN. The values of indentation hardness (H_O_P, H_C_C) and reduced elastic modulus (E_O_P, E_C_C) were calculated by using Oliver-Pharr (OP) and Cheng-Cheng (CC) methods. The experimental results revealed that the indentation hardness and reduced elastic modulus exhibit peak-load dependence, i.e. indentation size effect. Both indentation hardness and reduced elastic modulus values were obtained by considering indenter tip roundness and machine compliance. These values obtained from the OP method are higher than from the CC method. On the other hand, h_f/h_m ratios were used to clarify the indentation deformation behaviour of the SiAlON-ZrO_2 ceramic. The experimental h_f/h_m values were lower than the reported critical value (0.7) for all applied test loads, which is attributed to work-hardening ...

Science.gov (United States)

Cryogenic coolers are often used in modern spacecraft in conjunction with sensitive electronics and sensors of military, commercial and scientific instrumentation. The typical space requirements are: power efficiency, low vibration export, proven reliability, ability to survive launch vibration/shock and long-term exposure to space radiation. A long-standing paradigm of exclusively using "space heritage" equipment has become the standard practice for delivering high reliability components. Unfortunately, this conservative "space heritage" practice can result in using outdated, oversized, overweight and overpriced cryogenic coolers and is becoming increasingly unacceptable for space agencies now operating within tough monetary and time constraints. The recent trend in developing mini and micro satellites for relatively inexpensive missions has prompted attempts to adapt leading-edge tactical cryogenic coolers for suitability in the space environment. The primary emphasis has been on ...

Energy Technology Data Exchange (ETDEWEB)

This report summarizes the research conducted during Budget Period One on the project ''Improved Natural Gas Storage Well Remediation''. The project team consisted of Furness-Newburge, Inc., the technology developer; TechSavants, Inc., the technology validator; and Nicor Technologies, Inc., the technology user. The overall objectives for the project were: (1) To develop, fabricate and test prototype laboratory devices using sonication and underwater plasma to remove scale from natural gas storage well piping and perforations; (2) To modify the laboratory devices into units capable of being used downhole; (3) To test the capability of the downhole units to remove scale in an observation well at a natural gas storage field; (4) To modify (if necessary) and field harden the units and then test the units in two pressurized injection/withdrawal gas storage wells; and (5) To prepare the project's final report. This report ...

Energy Technology Data Exchange (ETDEWEB)

Tribological performance of alumina and silicon carbide ceramics as well as of the hardened steel 100Cr6 for reference was studied during reciprocating sliding and cavitation erosion in isooctane as substitute of gasoline and in distilled water. It was the aim to characterize effects of surface finish of the specimens and the liquid media on friction, resistance to sliding wear and cavitation erosion. Sliding wear tests were run on the self-mated ceramics and ceramic/steel pairs under conditions of boundary lubrication using a laboratory tribometer with cylinder-on-plate geometry. Vibratory cavitation erosion tests were conducted according to ASTM G 32-92. High initial surface roughness of coarse ground specimens led to a distinct running-in period during sliding contact with a transition from high to low values of friction coefficient and wear intensity. Incubation time was reduced with increasing surface roughness in the cavitation tests. Depending on the ...

International Nuclear Information System (INIS)

Purpose/Objective: With the advent of computed tomography and magnetic resonance imaging, the three dimensional representation of the patient anatomy has become an invaluable resource for better diagnosis and delineation of the target volume and sensitive structures in radiation therapy. Although the therapeutic linear accelerator industry has made available highly sophisticated equipment, the aggressiveness in dose prescription and delivery has to be complimented by accurate dose computation methods. We have adopted a convolution/superposition algorithm for the calculation of absolute dose that fully accounts for the external shape and internal structure of the patient for photon treatment radiotherapy. In this paper, we will discuss the principles of the convolution algorithm and we will show how the computed dose compares to clinically relevant treatment techniques. Materials and Methods: A computer controlled data acquisition system and a water tank where used to measure depth ...

Energy Technology Data Exchange (ETDEWEB)

Nickel base superalloys for turbine construction are exposed to maximum thermal and mechanical stresses. owing to a change of materials by one of the project partners, the project only comprised analyses of the alloy CMSX-6. Isothermal tensile and fatigue tests provided basic data on the alloy. Thermomechanical fatigue tests showed that material life and microstructural changes are clearly, and to an extreme extent, dependent on the type of combination of the two stress factors `temperature interval` and `total strain amplitude`, while the damage to the material tends to be a function of the maximum stresses for a given stress path. On the one hand, these results make it possible to obtain information real stresses from the structures of real blades. On the other hand, constructional measures can be taken in order to better adapt the stresses to which alloys are exposed to their characteristic potential. (orig./AKF) [Deutsch] Die im Turbinenbau eingesetzten Nickelbasis-Superlegierungen ...