Energy Technology Data Exchange (ETDEWEB)

The aim of this study was to investigate whether sub-ablative pulsed C0{sub 2} laser (1 0,6 {mu}m) irradiation is capable of reducing the susceptibility of the dental enamel to demineralization, and thus achieving a potential caries-protective effect. The crowns of 51 bovine front teeth, embedded in acrylic resin and polished until exposure of flat enamel surface, were used. The samples were cut in cubes of 10x10 mm, and totally coated with acid-resistant nail varnish, except for an enamel exposed window of 16 mm square. Three groups (n=17) were obtained: control group (CG) not irradiated; group laser A (LA) and group laser B (LB) where the samples were irradiated. The conditions were 60 mJ, 100 Hz, 0,3 J/cm{sup 2} for LA and 135 mJ, 10 Hz, 0,7 J/cm{sup 2} for LB. Two samples of each group were submitted to SEM analysis and fifteen to demineralization in 3 ml acetate buffer solution (0,1 mol/L) with pH 4,5 for 24h at 37 deg C, with regular agitation. After the specimens were removed ...