Science.gov (United States)

The specification describes a semiconductor solar cell and fabrication process therefor wherein a thin N-type gallium arsenide layer is deposited on a larger P-type substrate layer which is selected from the group of III-V ternary compounds consisting of aluminum phosphide antimonide, AlPSb, and aluminum indium phosphide, AlInP. P-type impurities are diffused from the substrate layer into a portion of the thin N-type gallium arsenide layer to form P-type region wherein which defines a PN junction in the thin gallium arsenide layer. Thus, the quantity of gallium arsenide required to provide this PN photovoltaic junction layer in the cell is minimized, and th P-type substrate serves as a high bandgap window layer for the cell. Such high bandgap of this window material is especially well suited for efficiently transmitting the blue spectrum of sunlight to the PN ...

Science.gov (United States)

Counting characteristics of X-ray detectors fabricated from indium-doped, gallium-doped, and chlorine-doped CdTe have been investigated. The detectors fabricated from indium-doped and gallium-doped crystals showed radiation-induced polarization, namely, a progressive decrease of count rate with an increase of photon fluence in the high-photon-fluence region, while the detectors fabricated from chlorine-doped crystals did not. Results from current-voltage characteristics of the detectors indicated that the different counting characteristics of these detectors originated from the difference in internal electric fields in each detector.

Science.gov (United States)

A high-efficiency 3- or 4-junction solar cell is disclosed with a theoretical AM0 energy conversion efficiency of about 40%. The solar cell includes p-n junctions formed from indium gallium arsenide nitride (InGaAsN), gallium arsenide (GaAs) and indium gallium aluminum phosphide (InGaAlP) separated by n-p tunnel junctions. An optional germanium (Ge) p-n junction can be formed in the substrate upon which the other p-n junctions are grown. The bandgap energies for each p-n junction are tailored to provide substantially equal short-circuit currents for each p-n junction, thereby eliminating current bottlenecks and improving the overall energy conversion efficiency of the solar cell. Additionally, the use of an InGaAsN p-n junction overcomes super-bandgap energy losses that are present in conventional multi-junction solar cells. A method is also disclosed for fabricating the ...

International Nuclear Information System (INIS)

Al, Ga and In complexing with methylthymol blue (H_6R) purified by gel filtration is studied. in the case of metal excess complexes with the ratio of components M:H_6R=2:1 with #lambda#=587(Al), 590(Ga) and 593 nm(In) appear. In the case of reacting agent excess complexes with the ratio of component 1:1 with #lambda#_m_a_x=480-490 (Al) and 480 nm(Ga, In) appear. The mechanism of complexing reactions is studied. Molar extinction coefficients and stability constants are calculated.

Energy Technology Data Exchange (ETDEWEB)

This patent describes a process for the preparation of acrylonitrile or methacrylonitrile by the reaction of propylene or isobutylene, molecular oxygen and ammonia at a temperature of about 200/sup 0/ to 600/sup 0/C in the presence of an oxidation catalyst. The improvement consists of using as the oxidation catalyst an antimony-free catalyst having the atomic ratios described by the formula: X/sub a/A/sub b/C/sub c/Fe/sub d/Bi/sub e/Mo/sub 12/O/sub x/ wherein X is Ga, In or mixtures thereof; A is alkali metal; C is Ni, Co or mixture thereof; and wherein a is 0.01 to about 4; b is 0 to about 4; c and d are 0.01 to about 12; e is 0.01 to about 6; and x is a number sufficient to satisfy the valence requirements of the other elements present. In a process for the preparation of acrylonitrile or methacryloniotrile by the reaction of propylene or isobutylene, molecular oxygen and ammonia at a temperature of about 200/sup 0/ to 600/sup 0/C in the presence of an oxidation catalyst.

Science.gov (United States)

Robert A. Martock. Cleveland State University, Cleveland, Ohio. Synthesis and Structural Characterization of a. Novel Indium Mercapto Derivative. [Clln(SCH. 2 ...

International Nuclear Information System (INIS)

The thermodynamic aspects of indium-face InN growth by radio frequency plasma-assisted molecular-beam epitaxy (rf-MBE) and the nucleation of InN on gallium-face GaN (0001) surface were investigated. The rates of InN decomposition and indium desorption from the surface were measured in situ using reflected high-energy electron diffraction and the rf-MBE 'growth window' of In-face InN (0001) was identified. It is shown that sustainable growth can be achieved only when the arrival rate of active nitrogen species on the surface is higher than the arrival rate of indium atoms. The maximum substrate temperature permitting InN growth as a function of the active nitrogen flux was determined. The growth mode of InN on Ga-face GaN (0001) surface was investigated by reflected high-energy electron diffraction and atomic force microscopy. It was found to be of the Volmer-Weber-type for substrate temperatures less ...

Energy Technology Data Exchange (ETDEWEB)

A burgeoning interest in technetium coordination chemistry has been spurred by its widespread use in nuclear medicine. Recent focus has been on the design and preparation of new technetium complexes, the lipophilicity, polarity, and overall charge of which can be readily altered by simple substitutions in the molecular framework of the ligand in order to optimize the biodistribution and target specific organs. Examples are cationic (Cardiolite) and neutral (Ceretec) technetium complexes, used as myocardial and brain imaging agents, respectively. The authors have been pursuing a continuing study of tris(3-hydroxy-4-pyridinonato)gallium and -indium complexes that are water soluble, are hydrolytically stable, and are of varying lipophilicity and neutral charge. Studies of in vivo in rabbits and mice have revealed that several of these cationic complexes may be useful as morphologic kidney imaging agents, with [{sup 99m}Tc(pap){sub 3}]{sup +} ...

Energy Technology Data Exchange (ETDEWEB)

Gallium is present in surplus weapons-grade plutonium (WG-Pu) at a concentration of approximately 1 wt %. Plans are to dispose of surplus WG-Pu by converting it to UO{sub 2}-PuO{sub 2} mixed oxide (MOX) fuel and irradiating it in commercial power reactors. However, the presence of high concentrations of gallium in plutonium poses a potential corrosion problem during the process of MOX fuel irradiation. The batch experiments performed in this study were designed to measure the capability of the PUREX solvent extraction process to separate gallium from plutonium under idealized conditions. Radioactive tracing of the gallium with {sup 72}Ga enabled the accurate measurement of low concentrations of extractable gallium. The experiments approximated the proposed flowsheet for WG-Pu purification, except that only one stage was used for each process: extraction, scrubbing, and stripping. ...

British Library Electronic Table of Contents (United Kingdom)

Indium sulfide thin films consisting of porous network of nanoplatelets, have been deposited using chemical bath deposition (CBD) method onto the tin-doped indium oxide (ITO) coated glass substrate. Aqueous solutions of indium sulfate and thioacetamide have been used as indium and sulfur precursors. As a complexing agent, acetic acid was used. The chemically deposited indium sulfide thin films were examined for their structural, surface morphological and optical characterizations. The X-ray diffraction analysis revealed the formation of the cubic b-In2S3 onto the substrate. From scanning electron micrograph, it is observed that the surface of substrate is covered by nanoporous platelets type morphology. The optical studies showed a direct band gap of 2.84eV for indium sulfide platelets. Ph...

International Nuclear Information System (INIS)

The indium implant damage and diffusion behavior in thin silicon-on-insulator (SOI) with a 200 nm top silicon layer were studied for different implantation energies and doses. Rutherford backscattering spectrometry in the channeling mode (RBS/C) was used to characterize the implant damage before and after annealing. Secondary ion mass spectrometry (SIMS) was used to study the indium transient enhanced diffusion (TED) behavior in the top Si layer of the SOI structure. An anomalous redistribution of indium after relatively high energy (200 keV) and dose (1 x 10"1"4 cm"-"2) implantation was observed in both bulk Si and SOI substrates. However, there exist differences in these two substrates that are attributable to the more predominant out-diffusion of indium as well as the influence of the buried oxide layer in the SOI structure.

International Nuclear Information System (INIS)

... 67 gamma detection hafnium 180 half-life indium 111 iodine 125 iodine 131

Science.gov (United States)

... used in our aluminum process include a barrier to isolate aluminum from the gold-based ohmic contacts, thereby preventing "purple plague," and a ...

Energy Technology Data Exchange (ETDEWEB)

A cooperative effort of the Center for Solar Energy and Hydrogen Research (ZSW) and Phototronics Solartechnik GmbH (PST) aimed at the transfer of highly efficient solar cells developed on a laboratory scale, to large-area thin-film solar modules suitable for production. This work was based on research and development at the Institute for Physical Electronics (IPE) of Stuttgart University and ZSW on one hand, and on the know-how of PST in regard to large-area module fabrication on the other hand. The various thin-film layers of the cells and modules comprize molybdenum as rear contact, copper-indium(gallium)-diselenide (CIGS) as absorber material, the combination of cadmium sulphide (CdS) and ZnO as window layer. To produce these layers on large areas (30x30 cm{sup 2}), equipment was constructed and procedures were developed. Monolithic series connection of cells, used in other thin-film technologies, was studied and optimized by suitable patterning procedures, such ...

International Nuclear Information System (INIS)

We developed a new systematic calibration procedure which was applied to the prediction of the diffusivity, the segregation, and transient enhanced diffusion (TED) of an indium impurity. The TED of the indium impurity was studied using four different experimental conditions. Although indium is susceptible to TED, rapid thermal annealing (RTA) is effective in suppressing the TED effect and maintaining a steep retrograde profile. Like boron impurities, the indium shows significant oxidation-enhanced diffusion in silicon and has segregation coefficients much less than 1 at the Si/SiO_2 interface. In contrast to boron, the segregation coefficient of indium decreases as the temperature increases. The accuracy of the proposed procedure was validated by using secondary ion mass spectrometry (SIMS) data and by using the 0.13-#mu#m device characteristics, such as V_t_h and I_d_s_a_t, for ...

International Nuclear Information System (INIS)

It has been demonstrated that, by incorporating a thin #approx#20 nm Si_1_-_yC_y (with y as low as 0.1%) layer at the deep indium implant end-of-range (EOR) region, the EOR defects and enhanced diffusion behavior associated with indium implant can be eliminated. The Si_1_-_yC_y layer was grown epitaxially followed by a silicon epitaxy cap of 60 nm. Indium implantations were performed at 1x10"1"4 cm"-"2 at 115 keV followed by spike annealing at 1050 deg. C. The experimentally observed EOR defect and enhanced diffusion elimination are explained based on the undersaturation of implantation-induced silicon interstitials with the presence of substitutional carbon at the Si_1_-_yC_y layer.

British Library Electronic Table of Contents (United Kingdom)

Indium sulfide thin films were deposited onto indium-tin-oxide coated glass substrate by electrochemical deposition from an aqueous solution containing In2 (SO4) 3 and Na2S2O3. The deposition conditions were optimized on the basis of data obtained by scanning electron microscope, Auger electron spectroscopy and optical transmission measurements. Furthermore, the photosensitivity of the films was observed by means of photoelectrochemical measurements, which confirmed that the indium sulfide showed n-type conduction. The X-ray diffraction and Raman studies revealed that the as-grown films were amorphous or nanocrystalline in nature and became polycrystalline In2S3 after annealing.

British Library Electronic Table of Contents (United Kingdom)

In the present study the optical properties of co-evaporated indium sulfide thin films are investigated. Before being optically characterized, the composition as well as the crystalline properties of the film have been checked with the help of energy dispersive spectroscopy (EDX) and X-Ray diffraction (XRD) analyses. The optical absorption coefficient ? of this indium sulfide film has been deduced from reflectivity R(?) and transmission T(?) measurements. The fit of the curve representing ?(h?) suggests that the ?-In2S3 has an indirect bandgap of 2.01?eV. Density functional theory (DFT) calculations are performed on this indium sulfide compound, using TB-LMTO code. Through these band structure investigations, an indirect bandgap is predicted as observed experimentally. The top of the valen...

International Nuclear Information System (INIS)

As part of a study into the properties of ferroelectric single crystals at nanoscale dimensions, the effects that focused ion beam (FIB) processing can have, in terms of structural damage and ion implantation, on perovskite oxide materials has been examined, and a post-processing procedure developed to remove such effects. Single crystal material of the perovskite ferroelectric barium titanate (BaTiO_3) has been patterned into thin film lamellae structures using a FIB microscope. Previous work had shown that FIB patterning induced gallium impregnation and associated creation of amorphous layers in a surface region of the single crystal material some 20 nm thick, but that both recrystallization and expulsion of gallium could be achieved through thermal annealing in air. Here we confirm this observation, but find that thermally induced gallium expulsion is associated with the formation of gallium-rich ...

Science.gov (United States)

... 19. AmSTR.ACT (Continuq 9n =usff i En " Adentity by bo nwnb Agallumarsemoe t(a.") MEtFET ... 2%ITE 4T (Include Area Code) InghE SMO ...

Energy Technology Data Exchange (ETDEWEB)

We report on the elimination of defect formation which is associated with high dose indium implantations under solid phase epitaxial regrowth (SPER) annealing conditions of 650-800 deg. C. This is achieved by incorporating a layer of epitaxially grown Si{sub 1-y}C {sub y} layer, strategically located at the end-of-range (EOR) of the implant profile. An indium implant of 115 keV at 1 x 10{sup 14} cm{sup -2} was performed followed by annealing at temperature ranges of 650-800 deg. C. Samples with the Si{sub 1-y}C {sub y} layer revealed the elimination of secondary EOR defects with effectively suppressed indium transient enhanced diffusion (TED), indicating the function of carbon as an efficient sink for silicon interstitials at reduced annealing temperatures, in the SPER dopant activation regime.

Science.gov (United States)

May 31, 2011 ... Synthesis and Structural Characterization of a Novel Indium Mercapto Derivative [Clln(SCH2(CO)O)2]2-[(4-MepyH)2]2+. 284. System Mass ...

International Nuclear Information System (INIS)

The optical spectroscopy measurements of gadolinium gallium garnet (GGG) crystals doped with Yb show evidence of the presence of non-equivalent optical centers with very similar radiative decay rates. The energy level schemes of those centers have been determined on the basis of optical absorption, luminescence and Raman experiments. Crystal field fitting resulted in two sets of slightly different crystal field parameters for two non-equivalent Yb centers. Both sets of parameters describe perfectly the experimentally detected Y b3+ energy levels. Correlation between systematic trends in the experimental energy level schemes and crystal field parameters is discussed.

International Nuclear Information System (INIS)

The feasibility of continuous production of gallium arsenide ribbon single crystals, by passage of a molten zone through boron-oxide encapsulated GaAs feedstock, is being investigated. Polycrystalline GaAs ribbons have been grown in graphite boats by passage of a wide zone through B2O3-encapsulated feed-stock, confined by a quartz cover plate. Failure to remove the encapsulant above its glass transition temperature, however, resulted in cracking of the ribbons on cooling to room temperature. In order to study the crucial zone melting step in isolation from the encapsulation steps of the continuous process, a constrained-zone melting apparatus has been constructed in which the boron oxide serves only as a sealant to suppress arsenic vaporization. Large grained polycrystalline samples have been produced with this apparatus.

International Nuclear Information System (INIS)

The structure of a demountable vacuum joint designed for operation from -120 to +120 deg C is developed and tested. Requirements of especially low gas release from the materials used have been fulfilled; the same concerns low sealing efforts, repeated action and keeping tightness under loads, indium being used as a sealant. Experimental studies of demountable vacuum joints, dia 100,125,140,160,180 and 200 mm, with an indium sealant permit to make the following conclusions: 1. The joints are sealed at sealing specific efforts of 0.4 kg/mm (without considering atmospheric pressure). 2. The joints retain tightness at opening and closing a cover five times and under +-120 deg C. 3. To ensure repeated operation of the joint with continued stable sealing effort, one should make sure the sealed surfaces coincide at repeated sealing. 4. When operating demountable vaccum joints with indium sealant, one must take into account the ...

International Nuclear Information System (INIS)

The project is intended to yield information on the transfer factors describing the transfer of ingested radionuclides to breast milk for the following elements: antimony, cerium, chromium, cobalt, gallium, lanthanum, molybdenum, niobium, radium, ruthenium, silver, thorium, titanium, and uranium. Those yet unknown or poorly known transfer factors are required in order to be able to develop a reliable model for description and assessment of the transfer of the radionuclides and the possibly resulting hazardous doses to infants, and for subsequent formulation of recommendations for radiological protection of the population. (orig./CB)

Energy Technology Data Exchange (ETDEWEB)

Qualitative technetium Tc 99m bone scintigraphy using phosphate compounds and gallium 67 scintigraphy were described as a helpful means in diagnosing necrotizing external otitis (NEO). They were, however, claimed to be nonspecific. Quantitative Tc 99m methylene diphosphonate bone scintigraphy and gallium 67 scintigraphy were performed in eight patients with NEO and in 20 patients with severe external otitis, in order to prove usefulness of scintigraphy in the diagnosis of NEO. Ratios of lesion to nonlesion for bone scintigraphy were 1.67 {plus minus} 0.16 in patients with NEO and 1.08 {plus minus} 0.09 in patients with severe external otitis, and for gallium 67 scintigraphy they were 1.35 {plus minus} 0.24 in NEO patients and 1.05 {plus minus} 0.03 in patients with severe external otitis. There was no difference in uptake between diabetic patients with severe external otitis and nondiabetic patients. The scintigraphic ...

Energy Technology Data Exchange (ETDEWEB)

The authors investigate the breakdown luminescence spectra in reverse-biased p-n heterojunctions based on gallium and aluminum phosphides and arsenides for the purpose of determining their behavior as lasing and photodetection materials. Data are given on temperature coefficients, band gap structure, bremsstrahlung, hot carrier mobility and photon emission, and transition and recombination parameters.

British Library Electronic Table of Contents (United Kingdom)

This paper presents studies carried out on tin-doped indium sulfide films prepared using Chemical Spray Pyrolysis (CSP) technique. Effect of both in-situ and ex-situ doping were analyzed. Ex-situ doping was done by thermal diffusion, which was realized by annealing Sn/In2S3 bilayer films. In-situ doping was accomplished by introducing Sn into the spray solution by using SnCl45H2O. Interestingly, it was noted that by ex-situ doping, conductivity of the sample enhanced considerably without affecting any of the physical properties such as crystallinity or band gap. Analysis also showed that higher percentage of doping resulted in samples with low crystallinity and negative photosensitivity. In-situ doping resulted in amorphous films. In contrast to ex-situ doping, `in- situ doping' resulted i...

Energy Technology Data Exchange (ETDEWEB)

This annual report describes progress in studies on hprt mutations induced by radon or Indium 111 along with the corresponding mutation frequency, cloning and molecular spectra in human T-lymphocytes. Parallel studies on the mutation susceptibility between individuals is being investigated by hprt mutation studies on ataxia telangiectasia and xeroderma pigmentosum.

Energy Technology Data Exchange (ETDEWEB)

We report a new case of Lyme disease with cardiac manifestations, which has been possible to follow during the long period of 12 years. We have detected the usual ECG abnormalities, and concentric hypertrophic myocardiopathy, by echocardiography. The acute myocarditis was demonstrated by /sup 111/In-antimyosin scintigraphy, which showed global myocardial uptake of the tracer, constituting the first report, to our knowledge, of Lyme myocarditis diagnosed by this method.

Energy Technology Data Exchange (ETDEWEB)

Infections of aortoarterial prostheses are serious, difficult to detect, and difficult to treat. Scintigraphy with indium-111 labeled autologous leukocytes is an accurate noninvasive method of assessing the presence and extent of such an infection. In three cases of aorto-arterial bypass graft infections, the leukocyte study was successful in establishing the diagnosis and in assessing the extent of infection. Other noninvasive diagnostic techniques are useful, but all have serious limitations. The leukocyte study alone appears to be free of likely sources of error.

International Nuclear Information System (INIS)

Magnetic materials such as yttrium iron garnet (YIG) are of great importance for its magneto-optic properties and for their potential applications in the domain of optical telecommunications. The deposition of thin films of YIG, on quartz or GGG (gadolinium gallium garnet) substrate, was performed using radio frequency non reactive magnetron sputtering, followed by high temperature annealing which is needed to enhance the crystallinity of the layers. Rutherford backscattering spectrometry RBS was used to determine the thickness and stoichiometry of the performed layers in order to investigate correlations between growth conditions and the quality of the final material. RBS measurements showed the influence of the deposition time and the temperature substrate on the film growth and its stoichiometry. (author)

Energy Technology Data Exchange (ETDEWEB)

While bone metastases producing photon deficient defects on bone scintigraphy have previously been reported, this finding has not been emphasized for hepatocellular carcinoma (HCC). Furthermore, ''filling-in'' of such photon deficient defects with 67Ga at skeletal sites of metastatic HCC has not been described. In this case report, the combination of a photon deficient defect on bone scintigraphy and avid accumulation of 67Ga in this same area was of value in confirming the diagnosis of metastatic HCC.

Energy Technology Data Exchange (ETDEWEB)

For diagnosis of loosening or infection after implantation of a single-side or double-side total hip endoprosthesis 59 patients being in pain were investigated by a combination of bone scan (Technetium-99m DPD) and leucocyte scan (Indium-111 labelled leucocytes). The correlation between clinical results and scintigraphic findings revealed: bone scintigraphy detects loosening of prostheses with 95% sensitivity (45/47); bone scintigraphy excludes an instable prosthesis with 89% specificity (3/27). 45% of the loosened prostheses revealed an infection (21/47): leucocyte scintigraphy could detect 17 correct positive. Three leucocyte scans of 53 prostheses without clinical signs of infection were false positive. Therefore, leucocyte scintigraphy had a sensitivity of 91% and a specificity of 94% for detecting infection. Bone scintigraphy can detect loosening of prostheses with 93% accuracy, Indium-111 labelled leucocyte scintigraphy can detect ...

Science.gov (United States)

Attempt to form the Schottky barrier on mercury indium telluride (MIT) surface by deposition transparent conducting electrode (TCE) and avoid the negative results by non-rectifier contacts nature, we have investigated the oxidation of clean MIT surfaces to form an insulating layer to overcome this disadvantage by metal-insulator-semiconductor (MIS) photodetectors designing. Oxide film is grown on the MIT surface by plasma enhance chemical vapor deposition (PECVD). Previously cleaned MIT wafers were dipped and boiled in solution, which consists of mixture of bromine and an organic solvent in ratio of 1:50. By the way of using these films as intermediate slightly conducting insulator, a fast-response MIT based surface-barrier photodetectors have been developed. Pt films were used as TCE frontal electrode by vacuum magnetron sputtering (VMS). The current-voltage characteristic is described quantitatively based on the energy diagram and the found parameters of the ...

Energy Technology Data Exchange (ETDEWEB)

A method is proposed for the quantitative high-temperature isolation of /sup 111/In from silver irradiated by ..cap alpha..-particles into a gas phase containing a mixture of HCl and H/sub 2/O with a total pressure of about 3 Pa for these gases. It is shown that the indium evolved into the gas phase probably occurs in the form of at least three compounds, viz.., the trichloride, monochloride, and oxychloride, which have adsorption temperatures on quartz of around 385, 475, and 655 K, respectively. All these compounds are readily washed from the surface of quartz apparatus by a weak (0.05 M) solution of hydrochloric acid.

Energy Technology Data Exchange (ETDEWEB)

Efforts concentrated on updating of the Rockwell reference concept, definition of new system options, studies of special emphasis topics, further definition of the transportation system, and further program definition. The Rockwell reference satellite concept has a gallium arsenide (GaAs) solar cell array having flat concentrators with an effective concentration ratio of 1.83at end of life. Alternatives to this concept includes solid state power amplifiers or magnetrons for dc/RF conversion and multibandgap solar cells for solar to dc energy conversion. Two solid state concepts were studied. It was determined that the magnetron approach was the lowest mass and cost system.

British Library Electronic Table of Contents (United Kingdom)

Size-controllable Ag nanoparticle ultrathin films, which were fabricated by vacuum deposition method from high purity Ag wire onto cleaned indium tin oxide conducting glass, have different color fabricated by variation of preparation conditions. The UV/Vis spectra showed that optical absorption peak of these Ag nanoparticle films can be tuned in a range from 457nm to >650nm. Scanning electron microscopy images showed that with increasing film thickness Ag particle size was larger. Ag/WO3 composite films were prepared by cathodic electrodeposition of WO3 onto the surface of Ag nanoparticle films. Spectroelectrochemistry and electrochromic properties of the resulting composite films were characterized. It was found that the electrochemical and electrochromatic properties of the composite fil...

British Library Electronic Table of Contents (United Kingdom)

In this paper, we study the optical properties of indium sulfide thin films to establish the best conditions to obtain a good solar cell buffer layer. The In2S3 buffer layers have been prepared by chemical bath deposition (CBD) and thermal evaporation (PVD). Optical behavior differences have been found between CBD and PVD In2S3 thin films that have been explained as due to structural, morphological and compositional differences observed in the films prepared by both methods. The resultant refractive index difference has to be attributed to the lower density of the CBD films, which can be related to the presence of oxygen. Its higher refractive index makes PVD film better suited to reduce overall reflectance in a typical CIGS solar cell.

Energy Technology Data Exchange (ETDEWEB)

A compact proton accelerator for medical applications is being developed at Lawrence Livermore National Laboratory. The accelerator architecture is based on the dielectric wall accelerator (DWA) concept. One critical area to consider is the switch region. Electric field simulations and thermal calculations of the switch area were performed to help determine the operating limits of rmed SiC switches. Different geometries were considered for the field simulation including the shape of the thin Indium solder meniscus between the electrodes and SiC. Electric field simulations were also utilized to demonstrate how the field stress could be reduced. Both transient and steady steady-state thermal simulations were analyzed to find the average power capability of the switches.

International Nuclear Information System (INIS)

The patients studied were referred for routine abscess localization with indium-111 labelled autologous leukocytes. One series (n=15) was studied at 1 day after reinjection of labelled cells and a second series (n=9) was studied between 4 hours and 4 days after reinjection of labelled cells. The leukocytes were isolated by a gravity sedimentation method and labelled with In-111 oxinate according to Roevekamp and co-workers. The labelled cell suspension administered to the patient contained between 11 and 15 MegaBq (300-400 microCi). The indium-111 concentration in the liver and spleen was quantitated using a scintillation camera and an on-line computer system. Phantom studies were carried out to obtain conversion factors from geometric mean counts to MegaBq of activity for both liver and spleen. Once determined, the amount of activity in liver and spleen was corrected for physical decay of In-111 and expressed as a percentage of the ...

International Nuclear Information System (INIS)

High liver uptake and slow body clearance presently limit the usefulness of "1"1"1In labeled antibodies for tumor imaging. We have investigated "2"0"3Pb as an alternate and better antibody label. The DTPA and cyclohexyl EDTA (CDTA) conjugates of an anticolon carcinoma antibody, 17-1A were labeled (bicyclic anhydride method) with "2"0"3Pb and "1"1"1In with 60 and 90% labeling yields, respectively. The biodistribution of "2"0"3Pb-17-1A conjugates was compared with the corresponding "1"1"1In-labeled preparations and with "2"0"3Pb-DTPA, "2"0"3Pb-nitrate and nonrelevant antibody controls in normal and human tumor (SW948) xenografted nude mice at 24, and 96 hr. Lead-203-labeled CDTA and DTPA antibody conjugates gave similar in vivo distributions. Even though the lead bound to these chelate-antibody conjugates was more labile in serum and in vivo, compared to indium, it cleared much faster from the liver and the whole body. A new series of chelating agents based on the ...

Energy Technology Data Exchange (ETDEWEB)

In this updated second edition, the order of contents of the textbook has been reorganized. It has been divided into main parts: Basic Science and Clinical Nuclear Medicine. Basic Science, Part I, encompasses basic physics, radiation protection, interaction of radiation with matter and radiation detection, imaging, nuclear pharmacy, and radiation biology. Part II, Clinical Nuclear Medicine, covers the central nervous system, bone, gastroenterology (liver/spleen), cardiovascular system, pulmonary system, genitourinary system, thyroid and endocrine systems, gallium studies, radioassay, hematology, and therapy. The total number of pages of the current edition is increased to 250 from the 213 of the first edition but there are fewer questions because those in the basic science area have been carefully selected to 60 of the original 98 questions. Compared with the previous edition, there are two advantages in the current one: (1) the addition of explanatory answers; and ...

Energy Technology Data Exchange (ETDEWEB)

A preliminary design effort directed toward a low concentration ratio photovoltaic array system capable of delivering multihundred kilowatts (300 kW to 1000 kW range) in low earth orbit is described. The array system consists of two or more array modules each capable of delivering between 113 kW to 175 kW using silicon solar cells or gallium arsenide solar cells, respectively. The array module deployed area is 1320 square meters and consists of 4356 pyramidal concentrator elements. The module, when stowed in the Space Shuttle's payload bay, has a stowage volume of a cube with 3.24 meters on a side. The concentrator elements are sized for a geometric concentration ratio (GCR) of six with an aperture area of .25 sq. m. The structural analysis and design trades leading to the baseline design are discussed. It describes the configuration, as well as optical, thermal and electrical performance analyses that support the design and overall performance estimates ...

Science.gov (United States)

The relationship between processing, microstructure, and properties was studied for A-15 compounds in multifilamentary composites produced by solid-state diffusion and in thin-film samples produced by vapor deposition. Grain sizes of A-15 superconducting compounds were measured by transmission electron microscopy of multifilamentary composites reacted at various temperatures. Critical current densities at 4.2 K and fields up to 6 T were found to be similar for niobium-tin, vanadium-gallium, and vanadium-silicon of the same grain size. Study of the Cu-V-Si phase diagram led to the production of improved multifilamentary vanadium-silicon conductors. The effects of various alloying elements on A-15 layers produced by solid-state diffusion were studied. The most promising new observation was that tantalum can be incorporated into niobium-tin reaction layers, leading to an enhancement of critical currents at high fields. The critical temperature of vapor-deposited, ...

Energy Technology Data Exchange (ETDEWEB)

The transient enhanced diffusion of low and high dose implanted beryllium in undoped gallium arsenide during post-implant rapid thermal annealing in the temperature range of 700-900 C for 60-240 s has been studied and successfully simulated by the kick-out diffusion model, involving singly positively charged Be interstitials and doubly positively charged Ga self-interstitials. Using the ''plus one'' approach for Ga interstitial generation after implantation with the local Ga interstitial sink concept as well as the appropriate initial and boundary conditions for involved mobile species, and taking into account Fermi-level and built-in electric field effects, the obtained partial differential equations have been solved numerically by means of an explicit finite difference method. The thermal equilibrium concentrations and the diffusivities of Be and Ga interstitials, all as a function of temperature, have been deduced from the ...

International Nuclear Information System (INIS)

One of the refinements of modern Nuclear Medicine is the capacity of providing dynamic and kinetics images of the administered radiopharmaceutical, reproducing its transport mechanism, action sites, receptor binding and excretion route. With the continues technological advances new radiopharmaceuticals have been developed in order to express higher specificity and with higher characters of affinity between receptor/complex. One radiopharmaceutical is formed by a reagent or bio molecule that has in its structure a radioisotope, that has the objectives of carrying it to the organs of affinity or to benign or malign tumoral process. Somatostatin inhibits the growing and proliferation of several tumoral cells. Somatostatin analogs bind to somatostatic receptors that are expressed in different kind of neoplasia DOTA-LANREOTIDE (DOTALAN) is an octapeptide analog to somatostatin. The interest of labeling the bio conjugate with gallium-67 in Nuclear Medicine comes from its ...

International Nuclear Information System (INIS)

The minimum cardiac transit times (MTT's) at rest and following sub-maximum stresses were measured in 97 individual examinations of untrained persons and high performance athletes. It turned out that there is a strong dependence on cardiac frequency of the MTT's. This relation can be described quite satisfactorily by a hyperbolic function and in this way allows a frequency correction to be made of the MTT's. The MTT's standardized in this way (MTT.f values) represent the quotient of the end diastolic segment volume/beat volume. In the whole lesser circulatory system almost identical MTT.f values were found for the two groups under comparison at rest and following stress. In the ventricles, however, and especially so in the left ventricle, the MTT.f values were clearly higher with athletes than with untrained persons, but they strongly decreased after stresses, while the respective values remained almost constant in ordinary persons. (orig./RF).

British Library Electronic Table of Contents (United Kingdom)

Abstract Lithium-indium oxide is one of the candidate materials as solid-state scintillators for solar neutrinos due to an inverse --decay of 115In to 115Sn. On the other hand, when doped with rare-earth ions such as Eu3+ or Sm3+, it becomes a promising phosphor material. In this report we present a simple solid-state procedure for preparation of LiInO2:Eu3+ powders. X-ray diffraction confirmed prod-uct in tetragonal structural form (space group: I41/amd) and no impurity phases were detected. Then, high resolution photoluminescence emission measurements were performed at room and low temperatures to find 5D0 - 7FJ. Emission kinetics from 5D0 level exhibited pure single exponential behavior with lifetime of about 1.5 ms. Maximum energy splitting of 7F1 manifold is recorded as a function of ...

Energy Technology Data Exchange (ETDEWEB)

One of the most challenging topics in the area of organic electronic devices is the growth of transparent electrodes onto flexible polymeric substrates that will be characterized by enhanced conductivity in combination with high optical transparency. An essential aspect for these materials is their synthesis and/or microstructure which define the transparency, the stability and the interfacial chemistry which in turn determine the performance and stability of the organic electronic devices, such as organic light emitting diodes, organic photovoltaics, etc. In this work, we will discuss the latest advances in the growth of organic (e.g. PEDOT:PSS) and inorganic (e.g. zinc oxide-ZnO, indium tin oxide-ITO) conductive materials and their deposition onto flexible polymeric substrates. We will compare the optical, structural, nano-mechanical and nano-topographical properties of the inorganic and organic materials and we investigate the effect of their structure on their ...

Science.gov (United States)

Metal cations of arsenic, antimony, tin, manganese, zinc, cadmium, indium, and thallium have been evaluated in a preliminary way as possible3 inhibitors for controlling denting corrision observed in steam generators used with pressurized water reactors (PWR). The rationale for this approach was based upon the well-known inhibition effects of metal cations on corrosion rates in electrolyte/metal systems. A review of corrosion inhibition by metal cations (H. Leidheiser, Jr., Corrosion 36, 339 (1982)) has identified eleven inhibition mechanisms. The major test methods used for this evaluation were: (1) Isothermal capsule tests of carbon/steel/Inconel 600 tube bulging rates at temperatures up to 288/sup 0/C in seawater/copper-nickel chloride bulge-accelerating solutions. (2) Immersion weight-loss tests of steel coupled to Inconel 600 in boiling (102/sup 0/C) 3% sodium chloride solutions. In addition, electrochemical measuremens and surface analyses were performed. The ...

International Nuclear Information System (INIS)

Measurements of the Kapitza conductance to liquid helium II across the (100) surface of single crystals of copper are presented. The temperature range of these measurements was 1.6-- 2.1 K. The sample surfaces were subjected to several different treatments. Some surfaces were cleaned by low-energy argon ion bombardment, annealed in an ultrahigh-vacuum system, and preserved under vacuum until purified liquid helium was admitted. Other surfaces were intentionally damaged by machining and/or exposure to the atmosphere. The conductance after these latter treatments was found to be about a factor of three higher than that of the more ideally cleaned and annealed surfaces, and a significant difference in the temperature dependence of the conductance was also observed. Conductances were reproducible for similarly treated surfaces and correlated with surface damage determined by x-ray diffraction. The relationship of these results to the numerous current theories of the Kapitza conductance is ...

International Nuclear Information System (INIS)

Research was conducted at Pacific Northwest Laboratory to develop high photosensitivity adaptive optical elements utilizing ion implanted lanthanum-doped lead-zirconate-titanate (PLZT). One centimeter square samples were prepared by implanting ferroelectric and anti-ferroelectric PLZT with a variety of species or combinations of species. These included Ne, O, Ni, Ne/Cr, Ne/Al, Ne/Ni, Ne/O, and Ni/O, at a variety of energies and fluences. An indium-tin oxide (ITO) electrode coating was designed to give a balance of high conductivity and optical transmission at near uv to near ir wavelengths. Samples were characterized for photosensitivity; implanted layer thickness, index of refraction, and density; electrode (ITO) conductivity; and in some cases, residual stress curvature. Thin film anti-ferroelectric PLZT was deposited in a preliminary experiment. The structure was amorphous with x-ray diffraction showing the beginnings of a structure at substrate temperatures of ...

Energy Technology Data Exchange (ETDEWEB)

W have introduced template-synthesized metal phosphate nanoparticle labels for electrochemical immunoassay. Such use of an apoferritin template offers a simple and convenient route to prepare metallic nanoparticle labels for electrochemical immunoassays and avoid the complicated and time-consuming nanoparticle synthesis process (QD synthesis). Releasing metal ions from metal phosphate in an acetate buffer (pH 4.6) eliminates the harsh condition in the traditional metallic nanoparticle dissolution (e.g., strong acid dissolution of QDs and gold nanoparticles). This method is ultrasensitive and its DL is low to 77fM. The simultaneous detection of multiple protein targets is easily performed by using different metal phosphate nanoparticle labels (cadmium phosphate and lead phosphate). This approach can be extended to prepare multiple metal (such as zinc, lead, cadmium, copper, indium, gold, silver) phosphate nanoparticle labels or hybrid metal (bimetallic or ...

Energy Technology Data Exchange (ETDEWEB)

This SBIR Phase I developed neutron detectors made from gallium arsenide (GaAs) p-type/ intrinsic/n-type (P-I-N) diodes grown by metalorganic chemical vapor deposition (MOCVD) onto semi-insulating (S1) bulk GaAs wafers. A layer of isotonically enriched boron-10 evaporated onto the front surface serves to convert incoming neutrons into lithium ions and a 1.47 MeV alpha particle which creates electron-hole pairs that are detected by the GaAs diode. Various thicknesses of ''intrinsic'' (I) undoped GaAs were tested, as was use of a back-surface field (BSF) formed from a layer of Al{sub x}Ga{sub 1-x}As. Schottky-barrier diodes formed from the same structures without the p+ GaAs top layer were tested as a comparison. After mesa etching and application of contacts, devices were tested in visible light before application of the boron coating. Internal quantum efficiency (IQE) of the best diode near the GaAs bandedge is over 90%. The ...

Energy Technology Data Exchange (ETDEWEB)

New techniques were developed to construct Schottky barrier and homojunction solar cells on GaAs substrates. Schottky barrier metal-semiconductor solar cells were produced for the first time on p-type GaAs substrate using a sputter-deposition method to form the barrier. The sputter deposition of gold or gold/palladium is the key to the method since normal thermal evaporation of gold onto p-type GaAs produces ohmic contacts. The results of this investigation are consistent with the idea that sputter damage produces donor type surface states on GaAs. Barrier heights were measured for both p-type sputtered and n-type thermally evaporated diodes using current-voltage and capacitance-voltage methods. Deep-level transient spectroscopy was used to identify the trap center concentration and energy levels for both diodes in an effort to explain the relatively large dark current in the p-type sputtered diodes. Homojunction GaAs solar cells were fabricated using several techniques. One involved ...

Energy Technology Data Exchange (ETDEWEB)

This paper discusses the mineralogy and geochemistry of the No. 6 Coal (Pennsylvanian) in the Junger Coalfield, Ordos Basin, China. The results show that the vitrinite reflectance (0.58%) is lowest and the proportions of inertinite and liptinite (37.4% and 7.1%, respectively) in the No. 6 Coal of the Junger Coalfield are highest among all of the Late Paleozoic coals in the Ordos Basin. The No. 6 Coal may be divided vertically into four sections based on their mineral compositions and elemental concentrations. A high boehmite content (mean 6.1%) was identified in the No. 6 Coal. The minerals associated with the boehmite in the coal include goyazite, rutile, zircon, and Pb-bearing minerals (galena, clausthalite, and selenio-galena). The boehmite is derived from weathered and oxidized bauxite in the weathered crust of the underlying Benxi Formation (Pennsylvanian). A high Pb-bearing mineral content of samples ZG6-2 and ZG6-3 is likely of hydrothermal origin. The No. 6 coal is enriched in ...

Energy Technology Data Exchange (ETDEWEB)

Computation of effective flow properties of fluids in porous media based on three dimensional (3D) pore structure information has become more successful in the last few years, due to both improvements in the input data and the network models. Computed X-ray microtomography has been successful in 3D pore imaging at micron scale, which is adequate for many sandstones. For other rocks of economic interest, such as chalk and diatomite, submicron resolution is needed in order to resolve the 3D-pore structure. To achieve submicron resolution, a new method of sample serial sectioning and imaging using Focused Ion Beam (FIB) technology has been developed and 3D pore images of the pore system for diatomite and chalk have been obtained. FIB was used in the milling of layers as wide as 50 micrometers and as thin as 100 nanometers by sputtering of atoms from the sample surface. The focused ion beam, consisting of gallium ions (Ga+) accelerated by potentials of up to 30 kV and ...

Science.gov (United States)

Thin-film solar cells on flexible, lightweight, space-qualified substrates provide an attractive approach to fabricating solar arrays with high mass-specific power. A polycrystalline chalcopyrite absorber layer is among the new generation of photovoltaic device technologies for thin film solar cells. At NASA Glenn Research Center we have focused on the development of new single-source precursors (SSPs) for deposition of semiconducting chalcopyrite materials onto lightweight, flexible substrates. We describe the syntheses and thermal modulation of SSPs via molecular engineering. Copper indium disulfide and related thin-film materials were deposited via aerosol-assisted chemical vapor deposition using SSPs. Processing and post-processing parameters were varied in order to modify morphology, stoichiometry, crystallography, electrical properties, and optical properties to optimize device quality. Growth at atmospheric pressure in a horizontal hotwall reactor at 395 C ...

International Nuclear Information System (INIS)

An experimental study was performed in order to study the nuclear structure in odd--odd In isotopes. Low lying nuclear energy levels in "1"1"0In and "1"1"2In were determined from de-excitation #gamma#-rays produced with "1"0"7AG(#alpha#,n#gamma#)"1"1"0In, "1"0"8Pd("6Li,4n#gamma#)"1"1"0In, "1"0"9Ag(#alpha#,n#gamma#)"1"1"2In and "1"1"0Pd("6Li,4n#gamma#)"1"1"2In reactions. In addition, the "1"1"4In energy level structure was investigated with the "1"1"0Pd("7Li,3n#gamma#)"1"1"4In reaction. Properties of de-excitation #gamma#-rays were determined from #gamma#--#gamma# coincidence excitation and angular distribution measurements conducted with Ge(Li) and Ge(intr.) #gamma#-ray detectors. A sequence of intraconnected levels in each of "1"1"0 "1"1"2 "1"1"4In were assigned to the (#pi#"-"1/sub 9/2/, #nu#h/sub 11/2) configuration. For the "1"1"0 "1"1"2"1"1"4In energy level schemes a model calculation was performed using the pairing-plus-quadrupole model, which reproduced states of the ...

International Nuclear Information System (INIS)

We describe the growth, fabrication, and characterization of an ultraviolet (UV) photoconductive detector based on In_xAl_yGa_1_-_x_-_yN quaternary alloy that is lattice matched to GaN. The detector consisted of 0.1 #mu#m In_xAl_yGa_1_-_x_-_yN alloy grown on 0.5-1.0 #mu#m GaN epilayer by metalorganic chemical vapor deposition. With varying indium concentration, the cut-off wavelength of the In_xAl_yGa_1_-_x_-_yN detectors could be varied to the deep UV range. The most important and intriguing result is that the responsivity of the In_xAl_yGa_1_-_x_-_yN quaternary alloy exceeded that of AlGaN alloy of a comparable cutoff wavelength by a factor of five. This makes the nitride quaternary alloy very important material for solar blind UV detectors applications particularly in the deep UV range where Al rich AlGaN alloys have problems with low quantum efficiency and cracks due in part to lattice mismatch with GaN. The advantages of In_xAl_yGa_1_-_x_-_yN quaternary over ...

Energy Technology Data Exchange (ETDEWEB)

The thermochemical calculations performed with a large number of elements to describe the chemical system in a Phebus FP test allow the following conclusions: The metallic absorber materials play a significant role in fission product speciation. At around 1000 C and above, silver iodide is the dominant iodine carrier in a full steam atmosphere in both FPT0 and FPT1. At lower temperatures, cadmium iodide takes over. In a reduced environment, indium iodide becomes important. Caesium iodide does certainly appear; at certain test conditions it becomes the major iodine transporting vehicle. But its role is not greater than that of the other iodides. It has more chances in FPT1 than in FPT0. Chlorine, which was present in FPT0 as a contaminant in relatively large amounts, does not prevent the iodine from forming Csl. Both share the caesium like partners. The evolution of caesium chloride and iodide proceeds in parallel. When CsCl is abundant, Csl is strong, too. Should ...

International Nuclear Information System (INIS)

Evaluation of severe functional gastrointestinal motility disorders requires an investigation of the entire gastrointestinal tract. This should be possible with a single radionuclide imaging study. The purpose of this study was (1) to define normal values of small-bowel transit in men and women and (2) to assess a possible difference between gender or test meal, since it has been shown that women have slower gastric emptying than men, and gastric emptying of solids is slower than liquids. A standard gastric-emptying test for a solid (technetium-99m sulphur colloids, 230 Kcal) and liquid (indium-111 DTPA water) test meal was performed in 12 healthy male and 12 healthy female volunteers. After 135 min, the volunteer was place in the supine position for static imaging of the abdomen every 15 min for 6 h. Decay and crossover-corrected geometric mean gastric-emptying data were fit to a modified power exponential function to determine the 10% stomach emptying time for ...

Energy Technology Data Exchange (ETDEWEB)

Carbon dioxide is receiving renewed interest as an efficient and environmentally safe refrigerant in a number of applications, including mobile air conditioning and heat pump systems, and hot water heat pumps. Compact heat exchangers for CO{sub 2} systems are designed with small-diameter tubing. The purpose of this study is therefore to provide a better basis for understanding and predicting heat transfer and pressure drop during flow vaporization of CO{sub 2} in microchannels. The ''unusual'' properties of carbon dioxide give heat transfer and two-phase flow characteristics that are very different from those of conventional refrigerants. Examples of these differences are the much higher pressure, the resulting high vapour density, a very low surface tension, and a low liquid viscosity. High pressure and low surface tension has a major effect on nucleate boiling characteristics, and earlier test data have shown a clear dominance of nucleate boiling ...