Science.gov (United States)

By gas-source molecular-beam epitaxy, we obtained a device-quality GaInP epitaxial layer lattice matched to (100)-GaAs substrates, with a photoluminescence efficiency comparable to that of a crystal grown by liquid-phase epitaxy. A GaInP/AlInP double heterostructure laser with a GaInP active layer was fabricated, and pulsed lasing operation was achieved at room temperature for, we believe, the first time.

Energy Technology Data Exchange (ETDEWEB)

In this work, we describe the fabrication and operating characteristics of GaAs/AlGaAs thin film solar cells processed by the epitaxial liftoff (ELO) technique. This technique allows the transfer of these cells onto glass substrates. The performance of the lifted-off solar cell is demonstrated by means of electrical measurements under both dark and illuminated conditions. We have also optimized the light trapping conditions in this direct-gap material. The results show that good solar absorption is possible in active layers as thin as 0.32 {mu}m. In such a thin solar cell, the open circuit voltage would be enhanced. We believe that the combination of an epitaxial liftoff thin GaAs film, and nano-texturing can lead to record breaking performance. {copyright} {ital 1997 American Institute of Physics.}

Energy Technology Data Exchange (ETDEWEB)

GaAs material and device structure optimization studies on optical-grade, millimeter-and-less grain-size polycrystalline Ge substrates are presented. We discuss the growth of high-quality epitaxial layers across various crystalline orientations of a polycrystalline substrate; this is important for obtaining high-performance solar cells. The GaAs solar cell on n-type poly-Ge substrate is a p-on-n type, with an undoped spacer between the p-emitter and the n-base. An experimental study of dark currents in these junctions, with and without the spacer, as a function of temperature (77K to 288K) is presented; this study suggests that the spacer reduces the tunneling contribution to dark current. In addition, we describe device-structure optimization studies that have led us to achieve an open-circuit voltage (V{sub oc}) exceeding 1 Volt and an AM1.5 efficiency of {approximately}19{percent} for a 4-cm{sup ...

Science.gov (United States)

For visible-light-emitting laser diodes, InGaAsP double heterostructures have been grown on GaAs substrates using liquid-phase epitaxy. As the growth temperature is as high as about 780 /sup 0/C, a large amount of phosphorus evaporates from the solutions for the cladding layers during the growth process. The phosphorus vapor disturbs the solution composition for the active layer, so that very thin and uniform active layers cannot be obtained. By using In-P-Sn solution and supplying the phosphorus partial pressure around the graphite boat, the influence of phosphorus vapor ambient for InGaAsP (lambda/sub P//sub L/ = 805 nm) growth is confirmed. When the phosphorus partial pressure increases, the surface of epitaxial layer becomes rough and the substrate is partly etched back. From x-ray diffraction and photoluminescence spectral measurements, ...

International Nuclear Information System (INIS)

Electron spin polarization in excess of 70% has been observed in photoemission from a 0.1 #mu#m-thick epitaxial layer of In_xGa_1_-_xAs with x #approx# 0.13 grown on a GaAs substrate. Under these conditions, the epitaxial layer is expected to be highly strained by the 0.9% lattice mismatch, as confirmed by x-ray diffractometer measurements of the lattice parameter. The electron polarization and the quantum efficiency have been measured as a function of the excitation photon energy from 1.25 to 2.0 eV. A significant enhancement of the electron polarization occurs in the vicinity of 1.33 eV where the expected strain-induced level splitting permits optical excitation of a single band transition. Measurements made on a control sample of 1.14 #mu#m thickness, significantly larger than the critical thickness for pseudomorphic strain, show no polarization enhancement. These measurements ...

Energy Technology Data Exchange (ETDEWEB)

Atomic layer epitaxy (ALE) was used to grow several components of the cascade solar cell structure in the AlGaAs/GaAs system. An ALE reactor was constructed for multiwafer growth with a growth rate of 0.6 {mu}m h{sup -1}. Device quality GaAs and Al{sub x}Ga{sub 1-x}As films were grown with p-type background carbon doping in the ranges 10{sup 16}-10{sup 19} cm{sup -3} and 10{sup 16}-10{sup 20} cm{sup -3} respectively. N-type films were achieved by SiH{sub 4} doping, producing carrier concentrations in the range 10{sup 16}-10{sup 18} cm{sup -3}. In addition, the potential applications of the ALE technique in the photovoltaic field are discussed. (orig.).

International Nuclear Information System (INIS)

Self-assembled quantum dots (QDs) are envisioned as building blocks for realization of novel nanoelectronic devices, for which the site-selective growth is highly desirable. This thesis presents a successful route toward selective positioning of self-assembled InAs QDs on patterned GaAs surface by combination of in situ focused ion beam (FIB) implantation and molecular beam epitaxy (MBE) technology. First, a buffer layer of GaAs was grown by MBE before a square array of holes with a pitch of 1-2 #mu#m was fabricated by FIB implantation of Ga and In, ions respectively. Later, an in-situ annealing step followed by InAs deposition was performed. The InAs QDs were preferentially formed in the holes generated by FIB. The influence of ion dose, annealing parameters and InAs amount was investigated in this work. With optimized parameters, more than 50 % single dot occupancy per hole is achieved. Furthermore, ...

Energy Technology Data Exchange (ETDEWEB)

A p[sup +]-Al[sub 0.3]Ga[sub 0.7]As/n[sup +]-GaAs heterojunction tunnel diode was fabricated using Atomic Layer Epitaxy (ALE) growth technique. Background carbon doping of [similar to]10[sup 20] cm[sup [minus]3] was achieved in the p-side of the diode by optimizing growth conditions such as V/III ratio, exposure times to reactant gases, and growth temperature. In the n-side of the diode GaAs was doped with silane and doping concentrations as high as 7[times]10[sup 18] cm[sup [minus]3] were also achieved. The dopants are chosen to satisfy the high levels and low diffusion requirements. The diode can be used to interconnect the high and low band-gap cells in the AlGaAs/GaAs cascade solar cell structure. The reactor used in this investigation is a commercial MOCVD system which has been specially modified for dual operation of ALE and MOCVD growth modes.

Science.gov (United States)

AlGaInP double heterostructure laser diodes with a GaInP active layer constitute a basic laser structure for visible-light lasers using an AlGaInP alloy system. This paper gives a detailed description of (Al/sub x/Ga/sub 1 - x/)/sub 0.5/In/sub 0.5/P metalorganic vapor phase epitaxial growth, laser-fabrication processes, and basic device-characteristics for these lasers. The obtained pulsed-threshold-current was about 3.8 kA/cm/sup 2/(3.2 kA/cm/sup 2/ minimum) for laser diodes with an 8-10 /n//m wide and 150-300 ..mu..m long injection stripe. High characteristic-temperature T/sub o/ for the temperature dependence of pulsed threshold current was obtained and was found to be dependent on band-gap-energy differences between active layers and cladding layers. The maximum value for T/sub o/ was 222 K. The lasing wavelength of an AlGaInP double heterostructure laser diode with a GaInP active ...

Energy Technology Data Exchange (ETDEWEB)

In the last two years, rapid progress has been made in the energy conversion efficiencies of GaAs solar cells fabricated from molecular beam epitaxy (MBE) material. The efficiencies of cells fabricated from MBE material are now comparable with those fabricated from metal-organic chemical vapor deposition material, even for cells of dimension 2 cmx4 cm. This paper reviews the progress in MBE cell efficiencies. Also discussed is the role oval defects play in GaAs diode and solar cell performance. (orig.).

Science.gov (United States)

Room-temperature continuous-wave (cw) operation is achieved in the MBE (molecular-beam epitaxy)-grown InGaP/InGaAlP double-heterostructure (DH) visible laser diodes with a threshold current of 110 mA. The lasing wavelength and threshold current density under pulsed operation are 666 nm and as low as 3.9 kA/cm/sup 2/, respectively. This result is achieved by the introduction of H/sub 2/ into the growth chamber during growth, the continuous growth from one layer to the next layer, and the introduction of a GaAs buffer layer. InGaP/InGaAlP quantum well structures are also grown. From photoluminescence measurements, the conduction-band discontinuity ..delta..E/sub c/ is estimated to be 0.43 of the band-gap difference ..delta..E/sub g/. Furthermore, the multiquantum-well (MQW) structure is found to be stable under thermal treatment at temperatures as high as 750 /sup 0/C. ...

Science.gov (United States)

The (Al/sub x/Ga/sub 1-x/)/sub 0.5/In/sub 0.5/P material system, lattice matched to GaAs substrates, is useful for visible laser diodes. Here, low pressure organometallic vapor phase epitaxial growth of Ga/sub 0.5/In/sub 0.5/P and (Al/sub x/Ga/sub 1-x/)/sub 0.5/In/sub 0.5/P is examined. Epitaxial layers of bulk materials are characterized using photoluminescence, electroreflectance, Raman scattering spectroscopy, and surface morphology studies to determine lattice match and optimum growth conditions. Lattice matching at the growth temperature produces featureless growth surfaces, while lattice matching at room temperatures results in minimum photoluminescence linewidth but cracked surface due to tensile strain during growth. Raman scattering spectra of the quaternary reveal a three-mode structure, with spectral peaks due to GaP-like, in P-like, and AIP-like LO phonons. Additionally, (Al/sub x/Ga/sub ...

Energy Technology Data Exchange (ETDEWEB)

This paper reports advances in the development of solar cells made from GaAs-on-Si structures prepared by metalorganic chemical vapor deposition (MOCVD). The use of concentrator cells, operating at [similar to]200 suns, has led to the efficiency achievements of 21.3% (AM1.5D) for a GaAs-on-Si solar cell, and 27.6 (AM1.5D) for a homoepitaxial GaAs cell. The development of epitaxial multilayer dielectric mirrors (Bragg reflectors), as back-surface reflectors in thin-film GaAs cells, on both Si and GaAs substrates, is shown to lead to modest efficiency increases, over that of conventional designs.

Energy Technology Data Exchange (ETDEWEB)

The properties of Mn-doped GaAs layers grown by laser deposition were investigated with measurements of Hall effect and magneto-optical Kerr effect (MOKE). The electrical and magnetic parameters of the layers were defined by growth temperature and quantity of sputtered Mn. It was shown that room-temperature ferromagnetism is revealed by MOKE and, after ruby laser 25 ns pulse annealing, by Hall effect measurements.

Science.gov (United States)

We present results from the first studies of electric-field effects on optical transitions in visible-band-gap InGaP/InAlGaP multiple-quantum-well (MQW) structures. These structures, grown at 775 [degree]C by metalorganic vapor phase epitaxy on (100) GaAs substrates misoriented 6[degree] towards P(111)[r angle][l angle]111[r angle]A, consist of nominally undoped MQWs surrounded by doped In[sub 0.49]Al[sub 0.51]P cladding layers to form [ital p]-[ital i]-[ital n] diodes. The Stark shifts of various allowed and forbidden quantum-well transitions were observed in bias-dependent electroreflectance spectra of In[sub 0.49]Ga[sub 0.51]P/In[sub 0.49](Al[sub 0.5]Ga[sub 0.5])[sub 0.51]P MQW samples with 10-nm-thick layers. We find the magnitude of these shifts to depend on the details of the Mg doping profile, confirming the importance of Mg diffusion and unintentional background doping in these materials. Our ...

International Nuclear Information System (INIS)

Silicon layered structures containing porous silicon modified with various thermal treatments and epitaxial layers deposited on porous layers were studied with a number of complementary X-ray diffraction methods using synchrotron source. The methods of characterization included recording of rocking curves for reflections with various asymmetry as well as projection, section and micro-Laue topography. It was found that oxidizing and sintering of porous silicon seriously modified the strains in the porous layer and in some cases even inverting the sense of strain with respect to that in initially formed porous layer. Consequently the deposited epitaxial layer usually was not laterally coherent with the substrate. Some of investigated layers were not stable in time and after few months period exhibited ...

International Nuclear Information System (INIS)

A new structure of GaAs MESFET with high radiation tolerance is proposed. Changes in electrical parameters of a GaAs MESFET as a function of total #gamma#-ray dose have been found to be caused mainly by a decrease in the effective carrier concentration in an active layer. The authors have designed a new structure from a simulation based on an empirical relationship between the changes of the effective carrier concentration and the total #gamma#-ray dose. It has been successfully demonstrated by utilizing a highly-doped thin active layer (4 x 10"1"8 cm"-"3, 100 Angstrom) grown by OMVPE. This MESFET can withstand a dose ten times higher [1 x 10"9 rads(GaAs)] than a conventional one can.

Science.gov (United States)

The authors present electric-field dependent electroreflectance and photocurrent spectra of visible-bandgap In{sub x}(Al{sub y}Ga{sub 1{minus}y}){sub 1{minus}x}P/In{sub x{prime}}(Al{sub y{prime}}Ga{sub 1{minus}y{prime}}){sub 1{minus}x{prime}}P multiple-quantum-well (MQW) structures. These structures, grown by metal-organic vapor phase epitaxy on 6{degrees}-misoriented (100) GaAs substrates, have undoped MQWs sandwiched between doped In{sub 0.5}Al{sub 0.5}P layers, forming p-i-n diodes. Quantum-well compositions in the range 0.46{le}x{le}0.52 and 0{le}y{le}0.4, corresponding to bandgaps in the red to yellow-green range, were used. The Stark shifts in these various samples were measured and found to depend on the details of the Mg p-type doping profile, confirming important diffusion effects, in agreement with secondary ion mass spectrometry and capacitance-voltage data. The results show that these new materials are promising ...

International Nuclear Information System (INIS)

The use of Auger electron spectroscopy (AES) combined with in situ sputter etching for revealing the metallurgy of the metal-semiconductor interface is presented. The physical basis, measurement techniques, and data interpretation for Auger analysis of thin-film structures are briefly reviewed. Results of a detailed study of an alloyed multilayered contact (Ni/Au-Ge) on n-type epitaxial GaAs are summarized to illustrate how electrical and metallurgical contact properties can be correlated using AES. In addition, the results of a study of the growth kinetics and chemical phase identification of palladium silicide on single-crystal Si is given, as well as the initial results of a study of aluminum-palladium silicide interaction at elevated temperature.

CERN Document Server

A new monolithic semi-insulating (SI) GaAs sensor design for X-ray imaging applications between 10-100keV has been proposed. Monolithic pixel detectors offer a number of advantages over hybrid bump-bonded detectors, such as high device yield, low costs and are easier to produce large scale arrays. In this thesis, an investigation is made of the use of a SI GaAs wafer as both a detector element and substrate for the epitaxially grown High Electron Mobility Transistors (HEMTs). The design of the HEMT transistors, optimised for this application, were produced with the aid of the Silvaco 'Virtual Wafer Fab' simulation package. It was determined that the device characteristics would consist of a small positive threshold voltage, a low off-state drain current and high transconductance. The final HEMT transistor design, that would be integrated to a pixel detector, had a threshold voltage of 0.17V, an off-state leakage current of ...

Energy Technology Data Exchange (ETDEWEB)

The following is the optimized pulsed laser deposition (PLD) procedure by which we prepared the final samples that were sent to LLNL. These samples are epitaxial multilayer structures of Si/YSZ/CeO/NSMO, where the abbreviations are explained in the following table. In this heterostructure, YSZ serves as a buffer layer to prevent deleterious chemical reactions, and also serves to de-oxygenate the amorphous SiO{sub 2} layer to generate a crystalline template for epitaxy. CeO and BTO serve as template layers to minimize the effects of thermal and lattice mismatch strains, respectively. More details on the buffer and template layer scheme are included in the manuscript [Yong et al., 2008] attached to this report.

Energy Technology Data Exchange (ETDEWEB)

AlGaInP epitaxial layers grown at 690 {degree}C by atmospheric pressure organometallic vapor phase epitaxy are investigated by transmission electron microscopy. For the first time, compositionally modulated and ordered structures are simultaneously observed in AlGaInP alloys. The ordering is of the CuPt type with ordering along the {l brace}111{r brace} directions. The ordered regions appear as plate-like microdomains, while the composition modulation takes the form of a fine columnar constrast oriented along the growth direction. In addition, from the results of (001) plan-view diffraction contrast examination, the principal strain direction associated with the modulation structures is found to be perpendicular to the growth direction and lies in the surface plane. Thus, it is concluded that the spinodal decomposition is initiated and developed on the surface during the growth of the AlGaInP epitaxial ...

Science.gov (United States)

Homogenous Al{sub x}Ga{sub 1{minus}x}P liquid phase epitaxial layers have been obtained with the temperature difference method under controlled vapor pressure (TDM-CVP). Very clear fine structures near band edge in photoluminescence spectra have been observed at 77 K for the first time. Photoluminescence measurement results confirmed that the free exciton recombination without phonon assistance plays an important role in the luminescence at 77 K and becomes dominant at room temperature. It is considered that Zero-phonon assisted free exciton recombination is intensified by some local perturbations to electrical potentials against carriers or excitons introduced by Al atoms in Al{sub x}Ga{sub 1{minus}x}P layers, which can give momentum change necessary for recombination.

Science.gov (United States)

The phase stability of silicides of Ni, Pt and Pd in contact with single crystal or amorphous silicon is examined. The presence of a particular silicide phase is identified by X-ray diffraction, and Rutherford backscattering is used to study composition. It is concluded that Pt or Pd silicides are suitable for Schottky barriers. Layers of silicon can be grown quickly by solid phase epitaxy at temperatures of 300-500C and using an intermediate metal film. Experimental results are reported. Doped layers have been obtained which have electrical characteristics suitable for the junctions in solar cells. The effects of impurities and orientation of the substrate on the growth kinetics are discussed.

Energy Technology Data Exchange (ETDEWEB)

Epitaxial cobalt disilicide (CoSi{sub 2}) layers are grown on n-Si{sub 0.83}Ge{sub 0.17}/n-Si(001) using a sacrificial Si capping layer at the growth temperature T{sub s}=650 deg. C by reactive chemical vapor deposition using cyclopentadienyl dicarbonyl cobalt (Co({eta}{sup 5}-C{sub 5}H{sub 5})(CO){sub 2}). Structural and electrical properties of epi-CoSi{sub 2}/Si{sub 0.83}Ge{sub 0.17}/Si(001) were measured by transmission electron microscopy, X-ray diffraction, Auger electron spectroscopy and sheet resistance measurement as a function of annealing temperature. The combined results showed that the epitaxial CoSi{sub 2} phase by the reaction of Co with the Si capping layer was formed in the as-grown layers. Rapid thermal anneals for the investigation of thermal stability of the as-grown layers showed good thermal stability of the ...

Energy Technology Data Exchange (ETDEWEB)

The reactions between (100) GaAs and the near-noble metals Ni, Pd, and Pt have been investigated by application of high-resolution transmission electron microscopy (TEM), energy-dispersive analysis of x rays in the scanning TEM and Rutherford backscattering spectrometry. Emphasis is placed on the evolution of the phase distributions, film compositions, and interface morphologies during annealing at temperatures up to 480 /sup 0/C. The first phase in the Ni/GaAs reaction is shown to have the nominal composition Ni/sub 3/GaAs. Ternary phases of the type Pd/sub x/GaAs are also found to be the dominant products of the Pd/GaAs reaction. Conversely, only binary phases result from the Pt/GaAs reaction. These observations are used to construct isothermal sections of the M--Ga--As thin-film phase diagrams. The behavior of a thin (1--2 nm) native oxide--hydrocarbon layer during the Ni/GaAs, Pd/GaAs, and Pt/GaAs reactions is also ...

Energy Technology Data Exchange (ETDEWEB)

We report on the elimination of defect formation which is associated with high dose indium implantations under solid phase epitaxial regrowth (SPER) annealing conditions of 650-800 deg. C. This is achieved by incorporating a layer of epitaxially grown Si{sub 1-y}C {sub y} layer, strategically located at the end-of-range (EOR) of the implant profile. An indium implant of 115 keV at 1 x 10{sup 14} cm{sup -2} was performed followed by annealing at temperature ranges of 650-800 deg. C. Samples with the Si{sub 1-y}C {sub y} layer revealed the elimination of secondary EOR defects with effectively suppressed indium transient enhanced diffusion (TED), indicating the function of carbon as an efficient sink for silicon interstitials at reduced annealing temperatures, in the SPER dopant activation regime.

International Nuclear Information System (INIS)

The dependence of the photoluminescent properties of In_0_._4_8(Al_yGa_1_-_y)_0_._5_2P alloys (0#<=#y#<=#0.5) on growth temperature and substrate misorientation off GaAs(100) has been studied. Samples were grown using low-pressure metalorganic vapor phase epitaxy. By studying the dependence of ordering behavior in InGaP as a function of substrate misorientation and growth temperature simultaneously, a very large range in low-temperature photoluminescence emission energy---135 meV---has been obtained. The photoluminescence linewidth exhibits a strong, continuous dependence on the extent of atomic ordering (the emission energy) in the alloys. The results indicate that inhomogeneity in the microstructure of the material (i.e., between ''ordered'' domains and the ''disordered'' matrix) is the dominant photoluminescence broadening mechanism. This investigation has allowed a significant optimization of the optical properties of these materials, ...

Energy Technology Data Exchange (ETDEWEB)

This report describes progress during the first year of a three-year project. The objective of the research is to examine new design approaches for achieving very high conversion efficiencies. The program is divided into two areas. The first centers on exploring new thin-film approaches specifically designed for III-V semiconductors. The second area centers on exploring design approaches for achieving high conversion efficiencies without requiring extremely high quality material. Research activities consisted of an experimental study of minority carrier recombination in n-type, metal-organic chemical vapor deposition (MOCVD)-deposited GaAs, an assessment of the minority carrier lifetimes in n-GaAs grown by molecular beam epitaxy, and developing a high-efficiency cell fabrication process.

International Nuclear Information System (INIS)

An annealing with the nanosecond laser light pulse is applied for crystal lattice reconstruction of a disturbed near-surface layer, which was created in semiconductor material as a result of the implantation process. Radiation with energy density higher than the threshold value causes the melting of the surface layer and than the epitaxial recrystallization from the melt on a different substrate. Structural changes occurring in the Ge implanted Si crystals after annealing with different energy densities are investigated by means of the cross-section high-resolution transmission electron microscopy. (author)

Science.gov (United States)

The growth of an oxide interfacial layer was recently found to increase the open-circuit voltage (OCV) and efficiency by up to 60 per cent in GaAs metal-semiconductor solar cells. Details of oxidation techniques to provide the necessary oxide thickness and chemical structure and using ozone, water-vapor-saturated oxygen, or oxygen gas discharges are described, as well as apparent crystallographic orientation effects. Preliminary results of the oxide chemistry obtained from X-ray, photoelectron spectroscopy are given. Ratios of arsenic oxide to gallium oxide of unity or less seem to be preferable. Samples with the highest OVC predominantly have As(+3) in the arsenic oxide rather than As(+5). A major difficulty at this time is a reduction in OCV by 100-200 mV when the antireflection coating is vacuum deposited.

Science.gov (United States)

Partial Contents: Ternary Compounds; Granular Superconductors; Superconductivity in (SN)x and its Halogen Derivative (SNBr0.4)x; Studies of cuCl at Elevated Pressures; Superconducting Properties of Hydride Systems; Thin Film Superconducting Materials Research; Synthesis of Superconducting Nb3Si using High Pressures; Synthesis of Unstable A-15 Compounds by Epitaxial Recrystallization of Ion Implanted Layers; and Sputtering of Nb3Si.

Energy Technology Data Exchange (ETDEWEB)

Two window layer materials, Al{sub 0.51}In{sub 0.49}P (E{sub g} = 2.3 eV) and Ga{sub 0.51}In{sub 0.49}P (E{sub g} = 1.88 eV) were compared for gas-source and solid-source MBE grown GaAs and Ga{sub 0.84}In{sub 0.16}As{sub 0.68}P{sub 0.32} (E{sub g} = 1.55 eV) solar cells. Due to the wider band-gap of Al{sub 0.51}In{sub 0.49}P, the increased spectral response was observed for both GaAs and Ga{sub 0.84}In{sub 0.16}As{sub 0.68}P{sub 0.32} material based solar cells. In the case of the GaAs cells, the short-circuit current density was observed to increase from 32.5 mA/cm{sup 2} to 34.4 mA/cm{sup 2} with the Al{sub 0.51}In{sub 0.49}P window layer at AM0. Similar improvement was observed for the Ga{sub 0.84}In{sub 0.16}As{sub 0.68}P{sub 0.32} solar cells.

Energy Technology Data Exchange (ETDEWEB)

Buried ridge stripe lasers have been grown on InP in two steps by gas source molecular beam epitaxy. The active structure consists of a compressively strained layer multi quantum well with an equivalent wavelength emission at 1.5 [mu]m. The stripe was defined by reactive ion etching. A threshold current of 22 mA was reproducibly obtained on a laser length of 500 [mu]m. A CW output power of 48 mW per facet was achieved. In addition, preliminary accelerated aging tests have shown the high reliability the structure. (orig.)

Energy Technology Data Exchange (ETDEWEB)

This SBIR Phase I developed neutron detectors made from gallium arsenide (GaAs) p-type/ intrinsic/n-type (P-I-N) diodes grown by metalorganic chemical vapor deposition (MOCVD) onto semi-insulating (S1) bulk GaAs wafers. A layer of isotonically enriched boron-10 evaporated onto the front surface serves to convert incoming neutrons into lithium ions and a 1.47 MeV alpha particle which creates electron-hole pairs that are detected by the GaAs diode. Various thicknesses of ''intrinsic'' (I) undoped GaAs were tested, as was use of a back-surface field (BSF) formed from a layer of Al{sub x}Ga{sub 1-x}As. Schottky-barrier diodes formed from the same structures without the p+ GaAs top layer were tested as a comparison. After mesa etching and application of contacts, devices were tested in ...

International Nuclear Information System (INIS)

Epitaxial metastable (GaSb)/sub 1-x/Ge/sub x/ alloys with compostions across the pseudobinary phase diagram have been grown on (100) GaAs substrates by multitarget rf sputtering. An essential feature allowing the growth of these metastable materials was low-energy ion bombardment of the growing film during deposition to enhance surface diffusion, promote mixing, and preferentially sputter incipient second-phase precipitates. Annealing experiments indicated that the metastable films exhibit good high-temperature stability and that they transform through a continuous series of GaSb-rich and Ge-rich phases in which the solute concentrations decrease until the equilibrium two-phase alloy is obtained. While the calculated free-energy difference between the single-phase metastable and equilibrium states is approx.18 meV, the measured activation barrier for the transformation is approx.3 eV. All films were p-type with room-temperature hole ...

Science.gov (United States)

The strain dependence of Si-Ge interdiffusion in epitaxial Si/Si{sub 1-y}Ge{sub y}/Si heterostructures on relaxed Si{sub 1-x}Ge{sub x} substrates has been studied using secondary ion mass spectrometry, Raman spectroscopy, and simulations. At 800 and 880 deg. C, significantly enhanced Si-Ge interdiffusion is observed in Si/Si{sub 1-y}Ge{sub y}/Si heterostructures (y=0.56, 0.45, and 0.3) with Si{sub 1-y}Ge{sub y} layers under compressive strain of -1%, compared to those under no strain. In contrast, tensile strain of 1% in Si{sub 0.70}Ge{sub 0.30} layer has no observable effect on interdiffusion in Si/Si{sub 0.70}Ge{sub 0.30}/Si heterostructures. These results are relevant to the device and process design of high mobility dual channel and heterostructure-on-insulator metal oxide semiconductor field effect transistors.

Science.gov (United States)

The authors suggest a method of calculation of the isotherms of the spinodal and the heterogeneous equilibria in four-component systems in the framework of a unified thermodynamic model of the solution. The results of their calculations predict the existence of extended regions of immiscibility in the solid phase in the interval of temperatures usually used to obtain epitaxial layers of InAs/sub x/P/sub y/Sb/sub 1-x-y/ and AlAs/sub x/P/sub y/Sb/sub 1-x-y/.

International Nuclear Information System (INIS)

The application of medium energy ion scattering in combination with channelling and blocking to the study of the initial stages of palladium silicide formation is discussed. After a brief description of the experimental arrangement and method, the effects on the Rutherford backscattering spectra of depositing small quantities of palladium on clean Si(111) are reported. The uniformity and thermal stability of thin palladium silicide films grown at room temperature were measured. Finally, channelling and blocking results were used to carry out a structural analysis of thin epitaxial Pd_2Si layers. (Auth.).

International Nuclear Information System (INIS)

We report on the transport properties of a high mobility two-dimensional hole system (2DHS) confined in GaAs/AlGaAs quantum wells grown by molecular-beam epitaxy on the (100) surface of GaAs. The quantum wells are modulation doped with carbon utilizing a resistive filament source. At T=0.3 K and carrier density p=1x10"1"1 cm"-"2, a mobility of 10"6 cm"2/Vs is achieved. At fixed carrier density p=10"1"1 cm"-"2, the mobility is found to be a nonmonotonic function of the quantum well width. The mobility peaks at 10"6 cm"2/Vs for a 15-nm well and is reduced for both smaller and larger well widths for these (100) samples. The mobility anisotropy is found to be small. Mobility along [011] is approximately 20% higher than along the [011] direction. In addition, the low-temperature carrier density is found to have low sensitivity to light. The hole density increases by only #approx#10% after exposure to red light at T=4.2 K. In structures designed for ...

Energy Technology Data Exchange (ETDEWEB)

The dependence of the photoluminescent properties of In{sub 0.48}(Al{sub {ital y}}Ga{sub 1{minus}{ital y}}){sub 0.52}P alloys (0{le}{ital y}{le}0.5) on growth temperature and substrate misorientation off GaAs(100) has been studied. Samples were grown using low-pressure metalorganic vapor phase epitaxy. By studying the dependence of ordering behavior in InGaP as a function of substrate misorientation and growth temperature simultaneously, a very large range in low-temperature photoluminescence emission energy---135 meV---has been obtained. The photoluminescence linewidth exhibits a strong, continuous dependence on the extent of atomic ordering (the emission energy) in the alloys. The results indicate that inhomogeneity in the microstructure of the material (i.e., between ordered'' domains and the disordered'' matrix) is the dominant photoluminescence broadening mechanism. This investigation has allowed a ...

Science.gov (United States)

Efficient, low-temperature conversion of infrared light into visible light (red, orange, green) is reported at single heterojunctions and undoped quantum wells of GaAs and ordered Al{sub {ital x}}Ga{sub 1{minus}{ital x}}InP{sub 2}; an increase in photon energy of 700 meV is obtained. The signal originates from the high-band-gap layers and disappears only if the excitation energy is tuned below the GaAs band gap. The intensity of the up-converted photoluminescence (PL) is found to decrease significantly slower with increasing temperature than that of the regular PL and it remains observable up to 200 K. Interface-induced cold Auger processes along with the presence of trapped states for both electrons and holes in these ordered alloys account for this nonlinear mechanism. A colinear double-beam experiment confirms this. {copyright} {ital 1996 The American Physical Society.}

International Nuclear Information System (INIS)

Monte-Carlo simulations of 2-MeV #alpha#-particle channeling in Si_1_-_xSn_x alloys with 0#<=#x#<=#1 have been performed. The simulations are compared with measured channeling-angular scans for strained Si_0_._9_5Sn_0_._0_5 layers grown by molecular beam epitaxy (MBE). Agreement between simulated and measured angular scans can only be achieved if we assume a deviation of the crystal structure from the ideal one. This deviation can be attributed to a mosaic structure in the films and to an atomic-scale distortion of the crystal lattice due to an expected difference in the bond lengths between the Si-Si, Si-Sn and Sn-Sn atoms (such a difference in bond lengths has been observed in the epitaxial Si_1_-_xGe_x system). The contributions from both of these imperfections are estimated and discussed.

Energy Technology Data Exchange (ETDEWEB)

In order to fabricate high temperature superconducting tapes for power applications, the authors have analyzed different buffer layer architectures grown on textured Ni substrates suitable for YBCO deposition. Due to its optimal lattice matching the studied structures present as top layer a CeO{sub 2} film. The deposition of CeO{sub 2} on Ni substrates was performed by pulsed laser ablation and by e-beam evaporation at different temperatures. The films obtained by the two deposition techniques have not optimal structural properties, having a polycrystalline component. The misorientation of CeO{sub 2} is probably due to the formation of NiO at the interface between the film and the substrate during the deposition process even if no oxygen is introduced. In order to prevent Ni oxidation an intermediate 2000 {angstrom} Pd thick film was deposited by e-beam. Furthermore, the lattice mismatch between Pd and CeO{sub 2} is smaller than that between Ni ...

Science.gov (United States)

... The approach is to perform noise spectral density measurements and selected materials structure measurements on GaAs detector materials, with ...

Energy Technology Data Exchange (ETDEWEB)

YBCO films were fabricated on PLD-CeO{sub 2}/IBAD-Gd{sub 2}Zr{sub 2}O{sub 7}/Hastelloy substrates using the advanced TFA-MOD process. The effective thickness of the CeO{sub 2} buffer layer for obtaining high I{sub c} was investigated in short samples of YBCO films. The CeO{sub 2} buffer layer was epitaxially grown on an IBAD-Gd{sub 2}Zr{sub 2}O{sub 7} template tape with 18 deg. of {delta}{phi} by a reel-to-reel PLD system. The in-plane grain alignment of PLD-CeO{sub 2} buffer layers rapidly improved with the thickness and saturated at a critical thickness of 0.8 {mu}m. The size of CeO{sub 2} grains was about 1 {mu}m at the saturated thickness of {delta}{phi}. YBCO films with the thickness of 1 {mu}m were deposited by the TFA-MOD on the CeO{sub 2} buffer layer with different thickness films. Improvement of the CeO{sub 2} in-plane grain alignment resulted in increase of I{sub c}. The ...

International Nuclear Information System (INIS)

Analytical TEM and high resolution TEM were used in the microstructural characterization of hot-press sintered Si_3N_4-SiC platelets composites. The quantity of sintering additives, Er_2O_3 and AlN, was varied to produce different matrices, e. g. Si_3N_4, #beta#'+#alpha#'-Sialon and #alpha#'-Sialon. Detailed analysis of platelet-sialon matrix interfaces revealed the presence of AlN polytypoids. The polytypoids nucleate preferentially onto the (0001) plane of SiC and growth epitaxially in several ten nanometer layers contributing in this way to crystallize, partially, the matrix intergranular glass pockets contacting the platelets. Possible applications of the phenomena to microstructural control, grain boundary phase control and enhanced creep resistance are discussed. (orig.).

International Nuclear Information System (INIS)

The initial growth process and surface structure of thin Pd(silicide) films on clean Si(111)-7x7 surfaces have been studied by low energy ion scattering (ISS) and LEED-Auger techniques. Considerable reaction between Pd and Si at room temperature is observed to extend up to 25 ML thickness of deposited Pd. Heat treatment of the room temperature film produced epitaxial silicide Pd_2Si(0001) films covered with the accumulated elementary Si layers of 1-2 ML thickness. Deposition of 1/3 ML Pd onto a heated substrate gives a Pd-embedded ordered surface of Si(111)-#sq root#3x#sq root#3R30"0, the feature being similar to the cases of Ag, Au/Si(111) systems. (orig.).

International Nuclear Information System (INIS)

We have investigated B diffusion in pre-amorphized silicon. In our experiments, the crystalline surface layer of silicon-on-insulator (SOI) substrates was completely amorphized by Ge ion implantation. Using SOI substrates in this fashion suppressed solid-phase-epitaxy regrowth, making it possible to investigate B diffusion in pre-amorphous silicon over a wider range of temperatures (500-650 deg. C) and times (5-1000 s) than has previously been reported. Diffusivities were determined with the aid of computational processes modeling. The results from this work demonstrate the B diffusion in a-Si is concentration dependent, exhibits a transient enhanced diffusion, and possesses an Arhennius behavior with activation energy of #approx#2.1 eV.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

Science.gov (United States)

The simultaneous diffusion of Si and the dopants B, P, and As has been studied by the use of a multilayer structure of isotopically enriched Si. This structure, consisting of 5 pairs of 120 nm thick natural Si and {sup 28}Si enriched layers, enables the observation of {sup 30}Si self-diffusion from the natural layers into the {sup 28}Si enriched layers, as well as dopant diffusion from an implanted source in an amorphous Si cap layer, via Secondary Ion Mass Spectrometry (SIMS). The dopant diffusion created regions of the multilayer structure that were extrinsic at the diffusion temperatures. In these regions, the Fermi level shift due to the extrinsic condition altered the concentration and charge state of the native defects involved in the diffusion process, which affected the dopant and self-diffusion. The simultaneously recorded diffusion profiles enabled the modeling of the coupled dopant and ...

Energy Technology Data Exchange (ETDEWEB)

Si/Pd-based contact schemes based on the solid phase regrowth (SPR) principle have been developed to form low resistance ohmic contacts to n type Al{sub 0.5}In{sub 0.5}P and Ga{sub 0.5}In{sub 0.5}P lattice matched to GaAs grown by gas source molecular beam epitaxy (GSMBE). Lowest contact resistivities of {approximately} 6 {times} 10{sup {minus}6} {Omega}-cm{sup 2} and {approximately} 1 {times} 10{sup {minus}5} {Omega}-cm{sup 2} have been obtained on Al{sub 0.5}In{sub 0.5}P and Ga{sub 0.5}In{sub 0.5}P respectively (both doped to {approximately} 2 {times} 10{sup 18} cm{sup {minus}3}). In this article, the electrical properties and the ohmic contact formation model of the Si/Pd-based contacts to n-Al{sub 0.5}In{sub 0.5}P and n-Ga{sub 0.5}In{sub 0.5}P are presented.

International Nuclear Information System (INIS)

We measure the transient enhanced diffusion of shallow molecular-beam-epitaxy grown marker layers of Sb and B due to deep MeV Si"+ ion implants at very high doses (#approx#10"1"6cm"-"2). We expect the near-surface region of these implants to be vacancy rich, and we observe transient enhanced diffusion of Sb (the classic vacancy diffuser). The large enhancements imply a significant vacancy supersaturation (#approx#700 at 740 degree C). Double implantation of the high-dose MeV Si followed by a shallow (40 keV) Si implant and annealing produces a greatly reduced number of #left brace#311#right brace# defects compared to a 40 keV implant into virgin Si, again consistent with a vacancy-rich region in the near-surface region of an MeV implant. However, the shallow B marker layers also show transient enhanced diffusion for the same MeV implant under similar annealing conditions, implying that an interstitial supersaturation is ...

International Nuclear Information System (INIS)

Fluorine is known to have a beneficial role for the B diffusion reduction in preamorphized Si, and is promising for the realization of ultra-shallow junctions. Thus, we studied the F incorporation in Si during the solid phase epitaxy (SPE) process, pointing out the effects of the implanted F energy and fluence and the role played by the possible presence of dopants. The incorporation of fluorine proceeds by F segregation at the amorphous-crystalline interface, with a kinetics driven by the SPE rate. In fact, the quicker the SPE rate, the higher is the F fluence retained. Moreover, we demonstrated that F incorporated in Si layers does not appreciably affect the Is emission from spatially separated end-of-range (EOR) defects. The modification, induced by the presence of F, of the point defect density (Is and Vs) was also studied by means of B and Sb spike layers, used as local markers for Is and Vs, respectively. We showed ...

Energy Technology Data Exchange (ETDEWEB)

Modelization of crack propagation and theoretical prediction of rupture are the two main objectives of researchers in stress corrosion cracking. Nevertheless, to reach this aim, the behavior of the passive film which appears spontaneously on the substrate in contact with an environment has to be known. This structural and mechanical characterization is all the more difficult because the number of parameters is important: crystallinity rate, defects concentration, thickness (about a few nanometers), electric field, chemical composition (a lot of oxides are present), peeling layers (atomic structure for example) and some hypothesis can be made about their multi-layer structure, their chemical composition or their epitaxial character... Passive films formed on 316L or 304L stainless steels in different aqueous solutions (in ambient air, in MgCl{sub 2} at 117 deg. C...) have been studied and some important remarks about their ...

International Nuclear Information System (INIS)

Interest to thin film of metals' silicides first of all is conditioned intrinsic al them unique physical properties. On their basis of it is possible to produce extremely sophisticated devices of solid-state electronics, production which needs the controlled change of physics, chemical and electrical properties with high-level of accuracy. On the present time most are in detail investigated composition, structure and properties of three-dimensional samples of metals' silicides. In the last years the intensive are led to researches in the direction of creation and study of physical-chemical properties thin (500-1000 Angstroms) and ultrafine (100-120 Angstroms) films silicides. It has information about composition, morphology of surface and emission of properties of thin film of silicides of barium, of cobalt and of palladium, was obtained in conditions of ultra-high vacuum. Low energy ion implantation and further annealing on composition, electronic and crystalline structure of Si ...

Energy Technology Data Exchange (ETDEWEB)

The structure of hydroxylated oxide films (passive films) formed on Cr(110) in 0.5 M H{sub 2}SO{sub 4} at +0.35, +0.55, and +0.75 V/SHE has been investigated by in situ scanning tunneling microscopy (STM). Cathodic reduction pretreatments at {minus}0.54, {minus}0.64, and {minus}0.74 V/SHE destroy the well-defined topography of the single-crystal electrode and they have been excluded from the passivation procedure. Two different passive film structures have been observed, depending on the potential and time of passivation. At low potential (+0.35 V/SHE), the passive film, consisting mostly of chromium hydroxide, has a noncrystalline and granular structure whose roughness suggests local variations of thickness of ca. {+-} 0.5 nm. A similar structure is observed at higher potential (+0.55 V/SHE), but only for a short polarization time. For longer polarization at 0.55 V/SHE, and at higher potentials (+0.75 V/SHE), a crystalline structure is formed; the higher the potential, the faster the ...

Science.gov (United States)

The study of the intrinsic behavior of high transition temperature copper-oxide superconductors (HTSC) has proven to be challenging because of the extreme sensitivity of their transport properties on material quality. These compounds are characterized by a high degree of structural and electrical anisotropy, and a very short superconductive coherence length of the same order as the size of the crystalline unit cell (~5-30 A). As a result, microscopic defects such as oxygen vacancies, cationic disorder, and the presence of minute impurities have a significant effect on electrical transport in these materials. Therefore, much effort has been expended in synthesizing sizable samples that are homogeneous, well characterized, and emenable to the study of the anisotropic properties of the HTSC. We have demonstrated that thin films of HTSC compounds such as rm YBa_2Cu_3O_{7 -delta}, which is a 92 K superconductor, can be synthesized easily by a technique known as pulsed laser deposition, and ...

Energy Technology Data Exchange (ETDEWEB)

The work in the past year has primarily involved four areas of magnetic thin films: amorphous rare earth-transition metal alloys, epitaxial CoPt{sub 3} and Ni-Pt alloy thin films, amorphous rare earth doped Si (a new class of dilute magnetic semiconductor with large negative magnetoresistance which the authors have discovered), and exchange-coupled antiferromagnetic insulators. In the amorphous alloys, they made a systematic study of the effects of local anisotropy, macroscopic (perpendicular) anisotropy, and exchange constant on the fundamental (and practical) properties of these magnetic alloys, as originally described in the grant proposal. The work on the epitaxial Co-Pt (and more recently Ni-Pt) alloys was originally undertaken as a comparison study to the amorphous alloys. Crystalline Co-Pt alloys have many striking similarities to the amorphous rare earth-transition metal alloys: perpendicular magnetic anisotropy, magneto-optic activity, ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

International Nuclear Information System (INIS)

The profile imaging technique is used to study the oxidation of ZnTe and InP surfaces induced by in situ reaction due to the electron beam of the microscope and by ex situ heating in air. For both materials, in situ reaction with the electron beam resulted in desorption of the anion species and the formation of the metal oxide. The observation of In metal particles, and the fact that the rate of formation of In_2O_3 was substantially reduced by an improvement of the vacuum near the specimen region, suggested that the presence of oxygen is not involved in the desorption process. The ex situ heating of ZnTe up to 260 degrees C in air resulted in crystals of ZnO and Te metal, generally in a layered surface region with the sequence of ZnTe/Te/ZnO. The large Te crystals usually had an epitaxial relationship with the bulk ZnTe but the small ZnO crystals had random orientations. The ex situ heating of InP to 380 degrees C in air only gave rise to ...

International Nuclear Information System (INIS)

The diffusion of ion beam injected self-interstitials (I) and their interaction with impurities in crystalline Si has been investigated and modeled. In particular, the I-substitutional carbon (C) interactions have been studied, using a molecular-beam-epitaxy grown Si_1_-_yC_y layer interposed between the shallow I-source and a deeper B-spike (marker for I-concentration). Substitutional C atoms are shown to trap I's, to be removed from their substitutional sites, and to form stable precipitates into the C-rich region. The I-trapping mechanism was quantitatively studied by a simulation code. The reactions causing trapping and deactivation are described. In addition, the boron markers approach was extended to the two dimensional (2D) diffusion. High resolution scanning capacitance microscopy was used for quantitative measurements of the 2D boron transient enhanced diffusion induced on a boron delta array by the I's ion beam injected through a ...

International Nuclear Information System (INIS)

A scalar-relativistic procedure for calculating the valence-electron contribution to the total energy of bulk and thin-film solids has been developed and applied to the fcc and bcc phases of the group-VIB transition elements Cr, Mo, and W. This approach, which is based on the linear augmented-plane-wave method and local-density-functional theory, contains no shape approximations for either the charge density or potential. The formulation adopts a rigid-core approximation and incorporates an exact treatment of the core-charge tails that extend beyond the muffin-tin spheres. The application of this procedure to bcc Cr, Mo, and W yields calculated lattice parameters and bulk moduli that are in good (Cr) to excellent (Mo and W) agreement with experiment. The present calculated properties also agree quite well with the results of previous calculations involving a variety of band-structure methods. The calculated fcc-bcc energy difference for Cr, Mo, and W increases in a nearly linear manner ...

International Nuclear Information System (INIS)

In this paper, we propose to characterize boron transient enhanced diffusion (TED) for processes currently used for P"+/N ultra-shallow junctions (USJ) fabrication. Indeed, the fundamental understanding of boron diffusion for low energy boron implantation is mandatory to evaluate the scalability of such processes for the coming complementary metal-oxide-semiconductor (CMOS) transistor generations. In these experiments, we characterize the boron anomalous diffusion, thanks to boron buried marker-layers obtained by epitaxial growth. B"+ and BF_2"+ ultra-low energy (ULE) implantations and plasma doping (PLAD) using BF_3 as precursor gas are carried out to compare the two techniques used for advanced USJ fabrication. Boron diffusion behaviors are analyzed via secondary ion mass spectrometry for annealing at 700 deg. C for 5 min and 15 min. Finally this paper brings some physical insights explaining the technological benefit coming from PLAD ...

Energy Technology Data Exchange (ETDEWEB)

Pd/sub 2/Si layers produced by evaporation or sputtering onto silicon substrates were examined by high resolution electron microscopy, microdiffraction, X-ray, energy loss and Auger spectroscopy. The Si-Pd/sub 2/Si interfaces produced by evaporation were in all cases rougher and more polycrystalline than those produced by sputtering. X-ray microanalysis showed the predictable variation in palladium distribution across the interface but quantification did not produce the expected palladium-to-silicon ratios, primarily because of probe broadening and X-ray-induced fluorescence. Energy loss spectra showed plasmon energy shifts and changes in Si L edge shape due to bond formation with palladium. Auger data provided evidence for a small amount of oxygen at the Si-Pd/sub 2/Si interface. Electrical measurements of the ideality factor for Schottky barriers made from the materials produced higher values for the rougher evaporation-formed interfaces consistent with ...

International Nuclear Information System (INIS)

High concentrations of self-interstitials are trapped by dopant atoms during ion implantation into Si. For group V dopants, these complexes are sufficiently stable to survive solid-phase-epitaxial (SPE) growth but break up on subsequent thermal processing and cause a transient-enhanced diffusion. Dopant diffusion coefficients are enhanced by up to five orders of magnitude over tracer values and are characterized by an activation energy of approximately one half of the tracer values. In the case of group III dopants, any complexes formed during implantation do not survive SPE growth but a second source of self-interstitials becomes significant and leads to similar transient effects. This is the damaged layer underlying the original amorphous/crystalline interface. These observations provide direct evidence for long-range self-interstitial migration in Si, and we believe these are the first observations of the interstitialcy diffusion mechanism ...

International Nuclear Information System (INIS)

In this experiment, a Si wafer containing four lightly doped B marker layers epitaxially grown by CVD has been implanted with 100 keV Si"+ ions to a dose of 2 x 10"1"4 ions/cm"2 and annealed at 850 deg. C for several times in an RTA system in flowing N_2. TEM and SIMS analysis, in conjunction with a transient enhanced diffusion (TED) evaluation method based on the kick-out diffusion mechanism, have allowed us to accurately study the boron TED evolution in presence of extended defects. We show that the silicon surface plays a key role in the recombination of Si interstitial atoms by providing the first experimental evidence of the resulting Si_i_n_ts supersaturation gradient between the defect region and the surface. Our results indicate an upper limit of about 200 nm for the surface recombination length of Si interstitials at 850 deg. C in a N_2 ambient.

International Nuclear Information System (INIS)

Analysis of steady-state and transient photoconductivity measurements at room temperature performed on c-axis oriented GaN nanowires yielded estimates of free carrier concentration, drift mobility, surface band bending, and surface capture coefficient for electrons. Samples grown (unintentionally n-type) by nitrogen-plasma-assisted molecular beam epitaxy primarily from two separate growth runs were examined. The results revealed carrier concentration in the range of (3-6)x10"1"6 cm"-"3 for one growth run, roughly 5x10"1"4-1x10"1"5 cm"-"3 for the second, and drift mobility in the range of 500-700 cm"2/(V s) for both. Nanowires were dispersed onto insulating substrates and contacted forming single-wire, two-terminal structures with typical electrode gaps of #approx =#3-5 #mu#m. When biased at 1 V bias and illuminated at 360 nm (3.6 mW/cm"2) the thinner (#approx =#100 nm diameter) nanowires with the higher background doping showed an abrupt increase in photocurrent ...

Energy Technology Data Exchange (ETDEWEB)

Growth mechanisms and thermal stability of ion-beam-induced epitaxial Pd/sub 2/Si films are investigated using Rutherford backscattering and channelling techniques. Epitaxial growth of Pd/sub 2/Si films was observed at room temperature by argon ion implantation into as-deposited Pd/Si(111) structures and furnace-annealed Pd/sub 2/Si(polycrystalline)/Pd/sub 2/Si(epitaxial)/Si(111) structures. Some additional experiments to check the growth mechanisms are also presented, in which the implantation energies, substrate orientations and dose rates were changed. Finally, the stability of the ion-beam-induced epitaxial Pd/sub 2/Si films on subsequent furnace annealing is studied.

International Nuclear Information System (INIS)

This study aims to investigate the difference in the interaction of antimicrobial peptides with two classes of zwitterionic peptides, phosphatidylethanolamines (PE) and phosphatidylcholines (PC). Further experiments were performed on model membranes prepared from specific bacterial lipids, lipopolysaccharides (LPS) isolated from Salmonella minnesota. The structure of the lipid-peptide aqueous dispersions was studied by small-and wide-angle X-ray diffraction during heating and cooling from 5 to 85 C. The lipids and peptides were mixed at lipid-to-peptide ratios 10-10000 (POPE and POPC) or 2-50 (LPS). All experiments were performed at synchrotron soft condensed matter beamline A2 in Hasylab at Desy in Hamburg, Germany. The phases were identified and the lattice parameters were calculated. Alamethicin and melittin interact in similar ways with the lipids. Pure POPC forms only lamellar phases. POPE forms lamellar phases at low temperatures that upon heating transform into a highly curved ...

Science.gov (United States)

An x-ray diffraction approach has been developed for determination of the kinetics of growth of Pd/sub 2/Si layers. Epitaxial Pd/sub 2/Si films were grown on Si(111) substrates over a temperature range of 160-222/sup 0/C by a solid-state reaction between the substrates and the Pd overlayers. The parabolic rate equation was verified and rate constants showed Arrhenius behavior with an activation energy E/sub a/ = 1.06 eV and prefactor k/sub 0/ = 7 x 10/sup -4/ cm/sup 2//s. The low value of E/sub a/ suggests a short-circuit diffusion mechanism. It is reasonable to expect that impurities and microstructure may play important roles in the growth process. Impurity levels in the specimens were evaluated by analytic techniques suited to thin-film study: Rutherford backscattering spectrometry, secondary ion mass spectrometry, and Auger electron spectrometry. No impurities were present at concentrations approaching 1 at. %. Some O, C, and F were ...

Energy Technology Data Exchange (ETDEWEB)

The various factors that affect the open-circuit voltage ([ital V][sub oc]) of a two-terminal GaInP[sub 2]/GaAs tandem cell are examined. These include a) an anomalous problem associated with the GaAs bottom cell and b) back surface passivation of the thin GaInP[sub 2] top cell. Solutions to these problems are presented and yield tandem [ital V][sub oc]s close to the practical theoretical limits.

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

Excitonic transitions in metalorganic vapor phase epitaxially grown In[sub [ital x

International Nuclear Information System (INIS)

We have investigated the detection performance of GaAs detectors made with different thickness and contact geometries. A comparison is made between these detection capabilities and the imaging requirements for the following medical applications: digital mammography, digital chest radiography and nuclear medicine. Experimental results and preliminary images are presented and discussed. (author)

International Nuclear Information System (INIS)

Nuclear radiation detectors in integral execution were produced by successive epitaxial growth from vapor phase of Zn Te and Cd Se thin layers onto scintillating Zn Se (Te) crystals. The irradiation of combined Zn Se (Te) - Zn Te - Cd Se detectors by Cu_K_a X-rays leads to the appearance of photoreceiver e.m.f., which tends to saturation with the increase of X-ray radiation dose reaching the value of 0.34-0.40 V at 200 R/min. The short circuit current dependence of irradiation dose power is linear. The matching factor for detectors with Zn Te-Cd Se photoreceivers with different doping levels is 0.68-0.92. The absolute monochromatic sensitivity is 0.32-0.35 m A/m W at a quantum efficiency 0.58-0.61 and a time constant 2 x 10"-"4 s. The calculated dose sensitivity for Zn Se(Te)-Zn Te-Cd Se combined detectors at the irradiation with X-rays having effective energy 8.86 keV gives the value 3.9 x 10"-"7 A/cm"2 (R/min); the experimental value of dose ...

International Nuclear Information System (INIS)

Radioactive "3"1Si(Tsub(1/2) = 2.62 h) and Rutherford backscattering were used to study Ni_2Si, Pd_2Si and Pt_2Si formation, silicon self-diffusion in silicides and silicon epitaxy in the Si(100)/Pd_2Si/Si (amorphous) system. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

The strongly localized one-electron (D{sup 0}) and two-electron (D{sup -}) donor states are considered with the lattice deformation around the donor center taken into account. For GaAs, donor energy levels have been calculated as functions of the hydrostatic pressure. The calculated energy positions and pressure coefficients agree with the experimental data. It is shown that the interaction with phonons reduces the probability of radiative transitions between the states of different localization and leads to the metastability of shallow-level donor states with respect to the D{sup -} state in GaAs and both the states (D{sup 0} and D{sup -}) in CdF{sub 2}. (author) 7 refs, 1 fig

Science.gov (United States)

Metal-Semiconductor Solar Cells," J. Appl. Phys. 46,. 1286 (1975). 12) H. B. Kim , G. G. Sweeney and I. S. Heng, "Analysis of ...

UK PubMed Central (United Kingdom)

Electronic and structural properties of antiphase boundaries in group III-V semiconductor compounds have been receiving increased attention due to the potential to integration of optically-active III-V...Full Text Available

UK PubMed Central (United Kingdom)

The tegument of tapeworms is known to be composed of an outer syncytial cytoplasm layer which includes microtriches and cytoplasmic organelles (= syncytial layer), and a parenchymatous cytoplasm layer...Full Text Available

International Nuclear Information System (INIS)

Using the slow electrons spectrometer one can get information on the surface structure, its element composition, chemical bonds, adsorption phenomena, electron state density and surface oscillation. We have developed the methods and created the apparatus that makes it possible to investigate the electron backscattering by solid surface. We have studied the electron scattering by the polycrystalline and monocrystalline. GaAs surface in the energy range of 0 to 9 eV. The FWHM of electron energy distribution function was 70 meV. (author).

Energy Technology Data Exchange (ETDEWEB)

Epitaxial films grown pseudomorphically on substrates provide a way to stabilise non-equilibrium structures of materials. Obviously, there always is a certain lattice misfit between substrate and film material in its bulk equilibrium structure. In the pseudomorphic regime, this misfit can either lead to the growth of films in a strained bulk structure or even yield structures that are not stable in the bulk. Large misfits do not necessarily imply large lateral stress. Theory can help to predict e.g. geometry, stress and magnetic properties of pseusomorphically grown metal films. In this work, we considered the fcc-bcc epitaxial Bain path of 3d, 4d, and 5d transition metals, which provides a reasonable description of tetragonally distorted films on substrates. We carried out density functional calculations in the implementation of the full potential local orbital program package FPLO. Emphasis is put on similarities among the transition metals.

International Nuclear Information System (INIS)

The AlGaInP materials system has recently supported the development of a variety of visible diode laser devices at wavelengths ranging from yellow to red. Presently, the majority of published results are with materials prepared by organometallic vapor phase epitaxy (OMVPE). Many issues with such materials exist, including impurity doping, the role of crystal ordering, defect formation during epitaxial growth, and the proper quantum well heterostructure design required for best device results. This paper addresses these topics and reviews the present state of the art, and projects the anticipated results when the materials' problems have been solved.

Energy Technology Data Exchange (ETDEWEB)

LaAlO{sub 3} and CeO{sub 2} films have been successfully grown using sol-gel precursors. LaAlO{sub 3} precursor solution has been prepared from a metal alkoxide route and spun-cast on a SrTiO{sub 3} (100) single crystal to yield an epitaxial film following pyrolysis at 800{degrees}C in a rapid thermal annealer. A CeO{sub 2} precursor solution has been made using both an aqueous and an alkoxide route.

Energy Technology Data Exchange (ETDEWEB)

An updated review of the state of the art in the development of GaAs solar cells is provided, with emphasis on AlGaAs-GaAs cells suitable for space applications. A set of theoretically derived characteristics is given for this type of solar cell. Comparison of measured performance with theory shows excellent agreement. Data on the effects of radiation damage (high-energy electrons, protons, and neutrons) is also integrated into a form useful for evaluation purposes. Techniques for fabricating (AlGa)As-GaAs solar cells in quantities large enough for practical applications are discussed and are shown to have been demonstrated. The possibility of extending these techniques to the fabrication of very thin low-weight cells for space applications is also considered. Finally, the results obtained to date in the development of GaAs solar cells for applications requiring concentrated sunlight are reviewed, for terrestrial as well as for space ...

Science.gov (United States)

CuPt-type ordering in In{sub 0.49}Al{sub 0.51}P is studied by TEM. The lattice-matched film was grown by MOCVD on a GaAs substrate oriented 10{sup o} off (001) towards [110], at 650 C and 25 nm/min. TEM [110] and [1{bar 1}0] cross-sections (XS) were made by wedge polishing and 2 kV Ar ion milling. In CuPt-type ordering of In{sub 0.52}Ga{sub 0.48}P, alternating In-Ga-In-Ga {l_brace}111{r_brace} planes of group III atoms produce 1/2 {bar 1}11 and 1/2 1{bar 1}1 order spots in the 110 SADP, while the [1{bar 1}0] SADP shows no order spots [1-3]. A few studies have reported this type of order in In{sub 0.49}Al{sub 0.51}P [4]. The 004 BF image of the [1{bar 1}0] XS in Fig. 1 shows uneven light/dark contrast modulation due to phase separation often observed in In{sub 0.52}Ga{sub 0.48}P. There are also light/dark layers marked ML parallel to the film growth plane; such unintentional multilayers have also been observed [5] but their origin is not ...

Energy Technology Data Exchange (ETDEWEB)

Today TBP and TBAs are the compounds which have the highest potential to replace the hydrides arsine and phosphine in the MOVPE process. The authors have demonstrated the entire material system Ga-In-As-P can be grown without any loss of quality using TBP and TBAs not only in one reactor, but in a complete family of reactors. These reactors range from small-scale single wafer R and D reactors to multiwafer Planetary Reactor systems. Both InP based and GaAs based materials could be grown with an excellent quality. Thus all growth processes for III-V devices--long and short wavelength lasers, LEDs, high speed transistors, etc.--can be switched to TBP and TBAs. This will drastically reduce safety hazards and lead to processes that have advantages both from the ecological and economical point of view.

International Nuclear Information System (INIS)

Pattern formation on GaAs by Ga"+ focused-ion-beam (FIB) irradiation and subsequent Cl_2 gas etching was carried out. A higher etch rate at the FIB-irradiated area compared with that not irradiated under Cl_2 gas allows pattern construction without a mask process. The degree of residual crystal damage was evaluated using photoluminescence (PL) intensity measurements. The PL intensity in the etched region was one order of magnitude stronger than that of FIB sputtering, and was several times stronger than that of Ga"+ FIB-assisted Cl_2 etching. Etch depths of the order of 100 nm, which is five times deeper than that obtained by FIB sputtering, were efficiently performed using moderate Ga"+-ion doses.

International Nuclear Information System (INIS)

The feasibility of continuous production of gallium arsenide ribbon single crystals, by passage of a molten zone through boron-oxide encapsulated GaAs feedstock, is being investigated. Polycrystalline GaAs ribbons have been grown in graphite boats by passage of a wide zone through B2O3-encapsulated feed-stock, confined by a quartz cover plate. Failure to remove the encapsulant above its glass transition temperature, however, resulted in cracking of the ribbons on cooling to room temperature. In order to study the crucial zone melting step in isolation from the encapsulation steps of the continuous process, a constrained-zone melting apparatus has been constructed in which the boron oxide serves only as a sealant to suppress arsenic vaporization. Large grained polycrystalline samples have been produced with this apparatus.

Science.gov (United States)

Not Available

Science.gov (United States)

A modified epitaxial design leads to straightforward implementation of short (1{lambda}) optical cavities and the use of C as the sole {ital p}-type dopant in AlGaInP/AlGaAs red vertical-cavity surface-emitting lasers (VCSELs). Red VCSELs fabricated into simple etched air posts operate continuous wave at room temperature at wavelengths between 670 and 690 nm, with a peak output power as high as 2.4 mW at 690 nm, threshold voltage of 2.2 V, and peak wallplug efficiency of 9%. These values are all significant improvements over previous results achieved in the same geometry with an extended optical cavity epitaxial design. The improved performance is due primarily to reduced optical losses and improved current constriction and dopant stability. {copyright} {ital 1995} {ital American} {ital Institute} {ital of} {ital Physics}.

British Library Electronic Table of Contents (United Kingdom)

Layered carbon fiber mats have been prepared by layer-by-layer (LBL) electrospinning of polyacrylonitrile onto thin natural cellulose paper and subsequent carbonization. The layered carbon fiber mat has been proved to be a promising microbial fuel cell anode for high density layered biofilm propagation and high bioelectrocatalytic anodic current density.

Science.gov (United States)

AlGaInP-based quantum-well laser diodes operating at wavelengths near 680 nm have been grown by all solid source molecular beam epitaxy (SSMBE). The lowest room temperature threshold current densities obtained from shallow rid structures were 300 A/cm{sup 2} and 330 A/cm{sup 2} for pulsed and continuous wave operation, respectively. The dependences of the differential quantum efficiency and threshold current density on the cavity length were also studied in this preliminary SSMBE work. The internal quantum efficiency of 87--89% and the internal losses of 7--10 cm{sup {minus}1} were obtained.

Energy Technology Data Exchange (ETDEWEB)

During the recrystallization by solid-phase-epitaxial (SPE) growth of supersaturated silicon alloys, a high concentration of interstitials is trapped. These are released by subsequent heating causing a transient (greatly enhanced) diffusion of the substitutional dopant by an interstitialcy mechanism. The enhancement may be as much as five orders of magnitude over tracer values, and shows an activation energy of only 1.8 +- 0.2 eV. Following the transient, the interstitials condense into loops, allowing an independent estimate to be made of their concentration. From these observations, we propose that during ion implantation, a fraction of the implanted dopants can acquire their natural valency, and retain it as the crystallization interface passes. For group V dopants this creates the trapped interstitials, giving transient enhanced diffusion when they are released by subsequent annealing.

Energy Technology Data Exchange (ETDEWEB)

The article is the second part of a review dealing with latest developments in the area of solar cell technologies and application. Physical principles, design and efficiency as well as advantages and disadvantages of GaAs- and CdS-solar cells are described. Power generation solar cell systems with voltage converters, combined solar cell/solar collector systems and thermoelectric solar systems are presented in the second part of the article.

Energy Technology Data Exchange (ETDEWEB)

To prove that two-layer, TBP-nitric acid mixtures can be safely stored in the Canyon evaporators, it must be demonstrated that a runaway reaction between TBP and nitric acid will not occur. Previous bench-scale experiments showed that, at typical evaporator temperatures, this reaction is endothermic and therefore cannot run away, due to the loss of heat from evaporation of water in the organic layer. However, the reaction would be exothermic and could run away if the small amount of water in the organic layer evaporates before the nitric acid in this layer is consumed by the reaction. Provided that there is enough water in the aqueous layer, this would occur if the organic layer is sufficiently thick so that the rate of loss of water by evaporation exceeds the rate of replenishment due to mixing with the aqueous layer. Bubbles containing ...

Energy Technology Data Exchange (ETDEWEB)

Craters were produced in the surface of a Pt-specimen by plasma discharge. Using a Focussed Ion Beam (FIB), TEM-foils of the cross section of the craters were prepared in order to examine the microstructural changes occurring as a result of the discharge impact. The molten material pushed to the edge of the craters was able to be identified. The grains beneath the craters reached the surface of the crater by a mechanism of epitaxial growth. (orig.)

Energy Technology Data Exchange (ETDEWEB)

By means of infrared spectroscopy, x-ray diffraction, and differential thermal analysis, the authors investigate the pyrolysis of dichlorodithiourea cadmium, the vapor phase epitaxy of the cadmium sulfide film, and the composition of the solid and gaseous pyrolysis products. Those products are found to include the thiocyanates of guanidine, ammonium, and hydrogen along with cadmium oxides and sulfates and hydrochloric acid.

Energy Technology Data Exchange (ETDEWEB)

This work deals with a rational vision of stratospheric ozone including the threats on ozone layer, the verifications and the fears. After a recalling on the ozone layer history, the authors treats the question of the ultraviolets particularly the beneficial effects. Then an explanation of the ozone layer decrease is given. (O.L.). 29 refs., 6 figs.

International Nuclear Information System (INIS)

Empirical formulae are proposed for the description of relation between optimum energies minimizing the mean-weighted error of gamma absorption measurement of the thickness of layers in two-layer products with the thickness of every layer from 30 up to 150 mm by carbon. Error of informational parameter approximation with the application of tables does not exceed 10% in case of non-accurate assessment of layers thickness not exceeding 2.5%. Generalized equation is derived which binds main parameters of the task and permits to choose optimum energies with the accuracy sufficient for practical purposes

International Nuclear Information System (INIS)

We have investigated the characteristics of ion-beam-induced spontaneous etching (IBISE) of GaAs in Cl_2 ambient by using a Ga-focused ion beam (FIB) with an energy ranging from 3 to 15 keV. The etched depth of the irradiated region was more than 20 times greater than that of unirradiated region. When the sputtered depth by FIB irradiation amounted to around 8 A at each ion energy, the etched depth in Cl_2 ambient for 1 hour became saturated. The saturated etched depths were 450, 550, 750 and 800 A at the ion energy of 3, 5, 10 and 15 keV, respectively. The residual damage of the etched surface was also investigated by photoluminescence (PL) measurement. The maximal PL intensity was obtained at around the threshold dose of IBISE and increased with decreasing ion energy. The full recovery of PL intensity was observed at the ion energy of 3 keV after annealing at 400degC. (author).

Energy Technology Data Exchange (ETDEWEB)

Room-temperature cw operation for InGaP/InGaAlP double heterostructure (DH) laser diodes on GaAs substrates was achieved for the first time. The DH wafers were grown by low-pressure metalorganic chemical vapor deposition using methyl metalorganics. A lasing wavelength of 679 nm and a threshold current of 109 mA at 24C were obtained for an inner stripe structure laser diode with a 250- m-long and 7- m stripe geometry. The laser operated at up to 51C. The characteristic temperature T0 was 87 K at around room temperature. The lowest threshold current density, 5.0 kA/cmS, was obtained with a 20- m stripe width laser diode under room-temperature pulsed operation.

International Nuclear Information System (INIS)

The optoelectronic compounds of GaAs and ZnSe are difficult to analyze by PIXE (particle-induced X-ray emission) due to the strong absorption of the As and Se K_#alpha# X-rays. As part of a program to investigate optoelectronic materials using ion beam techniques, we have explored the possibility of using the high sensitivity of PIXE to check these materials for stoichiometry and dopant concentrations. The K_#alpha# X-ray intensity ratios of Ga to As and Zn to Se have been investigated using H beams of 0.5 to 2.5 MeV and He beams of 1.0 to 2.5 MeV. The variation in the X-ray intensity ratio with beam energy and target thickness is modelled in terms of the cross section for X-ray production and the absorption coefficients of the X-rays in the target. The results of this model show the experimental conditions that must be satisfied in order that the X-ray intensity ratios are not strongly affected by X-ray absorption; and therefore, the conditions necessary for ...

Energy Technology Data Exchange (ETDEWEB)

The variations of thickness of the ozone layer over Denmark in the 1978-1994 period based on monthly figures are presented. (CLS)

Energy Technology Data Exchange (ETDEWEB)

A method of patterning n-type GaAs, InP, InGaAs, and InGaAsP by photoelectrochemical (PEC) etching in conjunction with a submicron focused ion beam (FIB) at low dose is described. The ion beam is used to produce damage in a desired pattern in the material. Subsequent PEC etching of the material reveals the ion induced features in relief. The procedure is highly sensitive, requiring a dose of only 5 x 10/sup 9/ ions/cm/sup 2/ for the differential etch to become apparent. The sensitivity allows rapid pattern generation in our FIB system.

International Nuclear Information System (INIS)

The use of workstations, controllers or embedded systems and their applications have become much more relevant than previously. PC-based systems, a cooker programmer, applications of, for example, Prolog machines, Unix and Ada papers, Robotics and Automation are typical examples of this. The three keynote addresses of this symposium have as their subjects the most spectacular microcomputer fields and are presented by leading experts. The papers presented cover most of the traditional interests of Euromicro. Special emphasis is given to contributions on the use of workstations and personal computers, on RISC and GaAs and on transputers.

Energy Technology Data Exchange (ETDEWEB)

We present the results of a comprehensive study of the temperature dependences of the quantum efficiency for ultraviolet detectors based on GaAs, GaP and 4H--SiC Schottky structures, and on Si, GaAs p-n structures. For ultraviolet detectors based on Schottky structures, the quantum efficiency increases with increasing temperature for all photon energies, even including the semiconductor intrinsic absorption region. On the other hand, for ultraviolet detectors based on p-n structures, the quantum efficiency is practically temperature independent in the semiconductor intrinsic absorption region. The change in the quantum efficiency for the GaAs and Si detectors is less than 0.01% per degree. To explain the measurements, a variable trap occupancy model is presented. Subsurface imperfections of the semiconductor cause fluctuations in the profile of the conduction band and the valence band edges. In the presence of an electric ...

Science.gov (United States)

In an earlier paper (Phys. Rev. Lett. 66, 41 (1991)), we calculated both the dielectric constant ({epsilon}{sub {infinity}}) and the nonlinear optical susceptibilities for second-harmonic generation ({chi}{sup (2)}) in the static limit for AlP, AlAs, GaP, and GaAs in the local-density approximation with and without a self-energy correction in the form of a scissors operator,'' including local-field effects. In this paper, we expand our presentation of this calculation. Agreement with experiment to within 15% for the nonlinear susceptibility is demonstrated where experiments are available (GaP and GaAs); the dielectric constants are in no worse than 4% agreement with experiment. The virtual hole'' contributions are reformulated to avoid large numerical cancellations in the case of near degeneracies. The virtual electron'' terms dominate over the virtual hole'' terms ...

Energy Technology Data Exchange (ETDEWEB)

This thesis details the first direct ultrafast measurements of the dynamic thermal expansion of a surface and the temperature dependent surface thermal diffusivity using a two-color reflection transient grating technique. Studies were performed on p-type, n-type, and undoped GaAs(100) samples over a wide range of temperatures. By utilizing a 90 fs ultraviolet probe with visible excitation beams, the effects of interband saturation and carrier dynamics become negligible; thus lattice expansion due to heating and subsequent contraction caused by cooling provided the dominant influence on the probe. At room temperature a rise due to thermal expansion was observed, corresponding to a maximum net displacement of {approximately} 1 {Angstrom} at 32 ps. The diffracted signal was composed of two components, thermal expansion of the surface and heat flow away from the surface, thus allowing a determination of the rate of expansion as well as the surface thermal diffusivity, ...

International Nuclear Information System (INIS)

A method was proposed and examined to deposit thick cubic boron nitride (cBN)-rich layer of good adhesion to silicon substrate. The method combined (i) the insertion of a thick sp"2 buffer layer, and (ii) the use of an appropriate assist ion beam energy for the growth of the cBN-rich top layer. The sp"2-bonded boron nitride buffer layer was deposited under irradiation of ions with energies in the range of 200-360 eV. The buffer layer was found to contain curled graphitic basal planes, and so was supposed to be relatively deformable, and facilitate the relaxation of stresses in the cBN-rich top layer. The ion assist introduced during the growth of the cBN-rich layer was supposed to both create and annihilate defects, and so resulted in the generation and relaxation of internal stresses. Results showed that the insertion of a 492 nm sp"2 ...

International Nuclear Information System (INIS)

We present an approach for fabrication of intentionally positioned epitaxial InAs QDs in a micron sized light emitting diode. For site-selective growth, a combination of molecular beam epitaxy (MBE) and focused ion beam (FIB) implantation technology in an all-ultra-high-vacuum (UHV) setup has been employed. Single dot occupancy of almost 55 % on FIB patterned nano-depressions was successfully achieved. Thereafter, carrier injection and subsequent radiative recombination from the positioned InAs/GaAs self-assembled QDs was investigated by embedding these QDs in the intrinsic part of a GaAs-based micron sized p-i-n junction device. Few or single dot are expected to be electrically addressed in these devices. We report results from electroluminescence (EL) measurement which proves the single dot characteristics of our device. The EL spectra consist of sharp emission lines and their dependence on injection current shows linear behavior for exciton ...

International Nuclear Information System (INIS)

The structure of the layers formed on a silver electrode by the adsorption of pyridine, Cl"-, CN"- and SO_4"2"- is discussed. A comparison of the amount of the species adsorbed with their Raman spectra shows that there is no simple relation between the species concentration and the enhancement of the Raman intensity. Furthermore, the inhomogeneity of the layers is shown by Raman microscopy observations. These results lead the authors to propose the formation of a new species stabilized in the colloidal silver layer. The Raman enhancement could be explained by the existence of a resonance effect. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

Governments around the world will soon make decisions on policies that could determine the fate of the ozone layer-the Earth's shield from harmful ultraviolet radiation. The Vienna Convention for the Protection of the Ozone Layer, signed on March 22, 1985, created a framework for scientific cooperation and information exchange that will form the basis for a protocol for controlling substances thought to threaten the ozone layer. As of mid-1987, 29 countries had signed the Convention, including the major producers and users of chlorofluorocarbons (CFCs), the most important of suspect chemicals.

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

Not Available

International Nuclear Information System (INIS)

Planar channeling effects are studied in such well-oriented polycrystalline layers as NiSi_2 and Pb_2Si layers formed on single crystalline Si. Crystalline perfection of such layers is discussed by using the energy- and angular dependences of the axial and planar channeling yields. It has been shown that, in suitable conditions, the energy dependence of the planar yield is more sensitive to the spread of crystallite orientations in polycrystals than that of the axial one. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

Transient, greatly enhanced diffusion has been observed on annealing solid-phase-epitaxial (SPE) grown Si-Sb alloys. This is shown to be due to a high concentration of interstitials being trapped during SPE regrowth. The migration enthalpy, for diffusion of Sb by an interstitialcy mechanism was measured as 1.8 +/- 0.2 eV. The interstitials eventually condensed into loops, marking the end of the transient. In a SPE grown Si-Bi alloy a similar transient enhanced diffusion was observed, with an activation energy of 2.0 +/- 0.2 eV, but no loops formed. 8 figures, 7 references.

Energy Technology Data Exchange (ETDEWEB)

X-ray photoemission spectroscopy has been used to measure the valence band offset {Delta}E{sub v} for the AlP/GaP (001) heterojunction interface. The heterojunction samples were prepared by molecular-beam epitaxy. A value of {triangle}E{sub v}=0.43 eV is obtained (staggered band alignment, with AlP valence band below that of GaP). 24 refs., 8 figs., 1 tab.

Science.gov (United States)

We have investigated the stability and catalytic activity of epitaxial overlayers of rhodium on Au(111) and Pd(111). Both surfaces show a strong affinity for hydrogen. We have calculated the energy of adsorption both for a strongly and a more weakly adsorbed species; the latter is the intermediate in the hydrogen evolution reaction. Both the energy of activation for hydrogen adsorption (Volmer reaction) and hydrogen recombination (Tafel reaction) are very low, suggesting that these overlayers are excellent catalysts. PMID:21847482

International Nuclear Information System (INIS)

Focussed ion beam (FIB) technology has the advantage of being a maskless process compatible with UHV processing. This makes it attractive for use in in situ processing and has been applied to the fabrication of various mesoscopic structures. The present paper reviews these results whilst putting emphasis on in situ processing by a combined FIB and molecular beam epitaxy system. The typical performance of present FIB systems is also presented. In order to utilize the potential advantages of FIB processing, reduction of damage and improvement of throughput are important, and much effort has been devoted to developing processing techniques which require a reduced dose. The importance of low-energy FIB is discussed. (author).

Energy Technology Data Exchange (ETDEWEB)

The effects of reservoir layering and gravity segregation on nonisothermal injection and falloff tests are investigated. Results show that layering does not affect injection or falloff data if all the layers are permeable and accept fluids from the wellbore. In such cases, the average permeability, skin factor, and distance to the thermal front can be calculated using the techniques developed for homogeneous reservoirs. Special considerations have to be taken for cases where several layers are impermeable or are permeable but do not accept fluids of the well face. In the first case (impermeable layers), knowledge of the total thickness of the permeable layers is required for the existing techniques to be applied successfully. In the second case, the existing techniques cannot be applied, but characteristic responses from injection and falloff test are seen; ...

International Nuclear Information System (INIS)

We studied the epitaxial growth of iron silicide (#epsilon#-FeSi,#beta#-FeSi_2, and #alpha#-FeSi_2) nanodots on Si (111) substrates by Fe deposition on Si nanodots on Si (111) substrates with ultrathin Si oxide films using reflection high-energy electron diffraction, scanning tunneling microscopy, and transmission electron microscope (TEM). We formed almost single phase iron silicide nanodots by controlling the Fe deposition conditions; growth temperature, deposition rate, and amount. The #epsilon#-FeSi or #alpha#-FeSi_2 nanodots were epitaxially grown in a dome shape with an average size of #approx#5 nm and an ultrahigh density (>10"1"2 cm"-"2) on the surface. We formed #approx#2-nm high and #approx#8-nm wide #beta#-FeSi_2 nanodots in a dome shape with a density of #approx#5x10"1"1 cm"-"2 on the surface. Cross-sectional TEM images revealed that the #beta#-FeSi_2 growth continued beneath the Si surface. The part of the #beta#-FeSi_2 nanodot ...

International Nuclear Information System (INIS)

Reflection coefficients of electromagnetic waves in a nonuniform plasma layer with electrons, positive ions and negative ions, covering a metal surface are investigated by using the finite-difference-time-domain method. It is shown that the reflection coefficients are influenced greatly by the density gradient on the layer edge, layer thickness and electron proportion, i.e., the effect of the negative ions. It is also found that low reflection or high attenuation can be reached by properly choosing high electron proportion, thick plasma layer, and smooth density gradient in the low frequency regime, but sharp density gradient in the high frequency regime. (authors)

International Nuclear Information System (INIS)

High quality graphene sheets are synthesized through efficient oxidation process followed by rapid thermal expansion and reduction by H2. The number of graphene layers is controlled by tuning the oxidation degree of GOs. The higher the oxidation degree of GOs is getting, the fewer the numbers of graphene layers can be obtained. The material is characterized by elemental analysis, thermo-gravimetric analysis, scanning electron microscopy, atomic force microscopy, transmission electron microscopy and Fourier transform infrared spectroscopies. The obtained graphene sheets with single, triple and quintuplicate layers as anode materials exhibit a high reversible capacity of 1175, 1007, and 842 mA h g-1, respectively, which show that the graphene sheets with fewer layers have higher reversible capacity. -- Graphical abstract: The typical TEM images of the graphene sheets derived from GO3(a), GO2(b) and ...

Energy Technology Data Exchange (ETDEWEB)

Nanowires, films, and membranes comprising ordered porous manganese oxide-based octahedral molecular sieves, and methods of making, are disclosed. A single crystal ultra-long nanowire includes an ordered porous manganese oxide-based octahedral molecular sieve, and has an average length greater than about 10 micrometers and an average diameter of about 5 nanometers to about 100 nanometers. A film comprises a microporous network comprising a plurality of single crystal nanowires in the form of a layer, wherein a plurality of layers is stacked on a surface of a substrate, wherein the nanowires of each layer are substantially axially aligned. A free standing membrane comprises a microporous network comprising a plurality of single crystal nanowires in the form of a layer, wherein a plurality of layers is aggregately stacked, and wherein the nanowires of each layer ...

British Library Electronic Table of Contents (United Kingdom)

In this work AISI 1045 steel were duplex treated via plasma nitriding of chromized layer. Samples were pack chromized by using a powder mixture consisting of ferrochromium, ammonium chloride and alumina at 1273K for 5h. The samples were then plasma-nitrided for 5h at 803K and 823K, in a gas mixture of 75%N2+25%H2. The treated specimens were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) analysis and Vickers micro-hardness test. The thickness of chromized layer before nitriding was about 8mm and it was increased after plasma nitriding. According to XRD analysis, the chromized layer was composed of chromium and iron carbides. Plasma nitriding of chromized layer resulted in the formation of chromium and iron nitrides and carbides. The hardness of the duplex layer...

Energy Technology Data Exchange (ETDEWEB)

The theoretical performance of ideal single- and multijunction cells are compared at 100xconcentration under a range of cloudless-sky conditions. The sensitivities of device performance to cell temperature and spectral variations are shown to depend on the number of junctions (one, two or three), the way in which the junctions are connected (series, parallel or independent), and the band gaps of the devices. The average performances of all of the multijunction devices surpass that of a single-junction GaAs device, but the inconsistency in performance of some of the multijunction devices is significant for large variations in cell temperature and incident spectrum. The choice of band gap and connection scheme is more important than the number of junctions in determining the consistency of device performance. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The current status of non-silicon photovoltaic solar cells is discussed including the identification of current technical and economic issues and future research directions for potential high efficiency low cost technologies. This review covers such advanced materials as CdS/Cu/sub 2/S, CdS/CuInSe/sub 2/, and GaAs homojunction and heterojunction devices; such emerging materials as InP, Zn/sub 3/P/sub 2/ and CdTe; and liquid junction electrochemical photovoltaic cells. An attempt is made to compare the current relative status of these various technologies and to indicate their near term potential where possible. 105 refs.

International Nuclear Information System (INIS)

We provide a brief review of our recent results from optically detected magnetic resonance studies of grown-in non-radiative defects in two most important dilute nitride systems-Ga(In)NAs grown on GaAs substrates and Ga(Al,In)NP grown on Si and GaP substrates. These results have led to the identification of defect complexes in the alloys, involving intrinsic defects such as As_G_a antisites and Ga_i self-interstitials. They have also shed light on formation mechanisms of the defects and on their role in non-radiative carrier recombination that is harmful to the performance of potential optoelectronic and photonic devices based on these dilute nitrides.

British Library Electronic Table of Contents (United Kingdom)

Within the framework of the effective-mass approximation, using a variational method, we have calculated the effect of intense laser radiation on the binding energy of the shallow-donor impurities in a Ga1- x In x N y As1- y /GaAs single quantum well for different nitrogen and indium mole concentrations. Our numerical results show that the binding energy strongly depends on the laser intensity and frequency (via the laser dressing parameter) and it also depends on the nitrogen and indium concentrations. Impurity binding energy under intense laser fields can be tuned by changing the nitrogen and indium mole fraction.

Science.gov (United States)

A general model for the analysis of metal-semiconductor solar cells is presented. The model takes into account the cell optical properties, carrier recombination effects, semiconductor minority-carrier properties, series resistance, cell thickness, and active surface area. Numerical methods are used to solve the appropriate continuity equations and hence compute the photocurrent density under AMO conditions. The operation of the model is demonstrated using p- and n-type Si and GaAs with Au being taken as the barrier metal. Calculations are presented showing the effect on solar energy conversion efficiency of surface recombination velocity, barrier height, minority-carrier lifetime, barrier metal thickness, collecting grid configuration, and cell thickness. A comparison of practical and computed data for the Au/n-GaAs system yields good agreement. (AIP)

Science.gov (United States)

Jump to main content. [logo] US EPA Ozone Layer Protection - Alternatives / SNAP Recent Additions | Contact Us Search: All EPA This Area Go You are here: EPA Home Ozone Layer...

UK PubMed Central (United Kingdom)

Hydrolytic exoenzymes as indicators of metabolically active bacteria were investigated in four consecutive sapropel layers collected from bathyal sediments of the eastern Mediterranean Sea. For comparison,...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A prototype detector based on the inclined boron layer principle is introduced. For typical measurement conditions at the Liquids Reflectometer at the Spallation Neutron Source, its count rate capability is shown to be superior to that of the current detector by nearly two orders of magnitude.

Energy Technology Data Exchange (ETDEWEB)

In this work, the silicon oxynitride layer was studied as a tunneling layer for non-volatile memory application by fabricating low temperature polysilicon thin film transistors on glass. Silicon wafers were oxynitrided by only nitrous oxide plasma under different radio frequency powers and plasma treatment times. Plasma oxynitridation was performed in RF plasma using inductively coupled plasma chemical vapor deposition. The X-ray energy dispersive spectroscopy was employed to analyze the atomic concentration ratio of nitrogen/oxygen in oxynitride layer. The oxynitrided layer formed under radio frequency power of 150 W and substrate temperature of 623 K was found to contain the atomic concentration ratio of nitrogen/oxygen as high as 1.57. The advantage of high nitrogen concentration in silicon oxide layer formed by using nitrous oxide plasma was investigated by capacitance-voltage ...

Energy Technology Data Exchange (ETDEWEB)

A duplex surface treatment technique based on calorizing and plasma nitriding was developed to improve the wear and oxidation resistance of H13 steel at high temperatures. The effects of the relative thickness of the calorized layer to the depth of plasma nitriding on the wear and oxidation properties at temperatures up to 900 C were investigated in this work. High-temperature wear tests were performed at 500 C with dry conditions in open air using a ball-on-disk type tribotest machine. Isothermal oxidation tests were performed at 900 C for up to 100 h under controlled atmosphere. The results indicated that the specimens with a calorized layer as an intermediate phase between the surface duplex layer and the base metal showed higher wear and oxidation resistance than the specimens with a nitrided layer alone. During exposure to elevated temperatures, the aluminum in the calorized ...

UK PubMed Central (United Kingdom)

The mammalian neocortex consists of six layers. By contrast, the reptilian and avian cortices have only three, which are believed to be equivalent to layers I, V and VI of mammals. In mammals, the majority...Full Text Available

Science.gov (United States)

... This pinhole process may be similar to the formation of an oxide layer in aluminum electrolytic capacitors immersed in a borax solution. ...

Energy Technology Data Exchange (ETDEWEB)

Cesium recovery from the polluted layers in the 1/3 scale hydrogen negative ion source for LHD-NBI system has tested. It was found, that the cesium recovery can be produced by additional discharges as from the cesium layer, aged by tungsten and residual gas, so as from the cesium layers, polluted by an occasional water leak. The highest cesium recovery to NI production was produced by a xenon arc, while glow discharge and arcing in hydrogen were less effective. The mechanism of recovery is the ejection of cesium from the underlying enriched layer by the arc and its transport to the surface. (author)

International Nuclear Information System (INIS)

With the aim of optimizing the nitriding process parameters (temperature and gas mixture ) experimental studies of the plasma nitriding of Ck 15 steel were carried out, using a D. C. glow discharge. Nitriding treatments were performed at 450, 500 and 550 and N_2/H_2 volume ratio of 3/1, 1/1 and 1/3 for 5 hours. Nitriding treatment produces modified surface layer consisting of an outer compound layer and an inner diffusion layer.The plasma nitriding of Ck 15 produce single white layer consisting of #gamma#-(Fe_4N).

British Library Electronic Table of Contents (United Kingdom)

There is investigated the role of polymer layers on the metal surface of a fine filler in the formation of a PVC system with electrophysical properties. It is shown that a physicochemical polymer modification takes place under the surface active center influence. Thus, the surface layer properties (density and geometrical characteristics) differ from the PVC ones. The correlation between the electrophysical properties of the PVC composite and the surface layer in the range of the fine copper fraction of 0?11.3 vol % at E ? 106 V m?1 and a frequency response of 20?2 ? 105 Hz is determined. An explanation of the investigated relation is presented.

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

The paper describes an analytical study of two parallel-flowing boundary layers of free and forced convection modes on the facing sides of a vertical thin wall. The two layers are analyzed separately within the framework of boundary layer theory, and coupled by the matching conditions at wall. Numerical data are obtained for a wide range of a dimensionless conjugation parameter {zeta} relating the heat transfer effectiveness of two convection modes. Based on these data, an expression for calculating the conjugate mean Nusselt number as a function of {zeta}-parameter is found by means of a curve-fitting method. (orig.)

Energy Technology Data Exchange (ETDEWEB)

A hydrous oxide film for the application as dielectric film is synthesized by immersion of pure aluminum in hot water. From a Rutherford backscattering analysis, the ratio of aluminum to oxygen atoms was found to be 3:2 in the anodized aluminum oxide film, and 2:1 in the hydrous oxide layer. Anodization of the hydrous oxide layer was more effective for the transition of amorphous anodic oxides to the crystalline aluminum oxides.

International Nuclear Information System (INIS)

In order to investigate the role of amorphous SiO2 particles in corrosion and wear resistance of Ni-based metal matrix composite alloying layer, the amorphous nano-SiO2 particles reinforced Ni-based composite alloying layer has been prepared by double glow plasma alloying on AISI 316L stainless steel surface, where Ni/amorphous nano-SiO2 was firstly predeposited by brush plating. The composition and microstructure of the nano-SiO2 particles reinforced Ni-based composite alloying layer were analyzed by using SEM, TEM and XRD. The results indicated that the composite alloying layer consisted of ?-phase and amorphous nano-SiO2 particles, and under alloying temperature (1000 deg. C) condition, the nano-SiO2 particles were uniformly distributed in the alloying layer and still kept the amorphous structure. The corrosion resistance of composite alloying layer was ...

International Nuclear Information System (INIS)

A patent is claimed for the invention of a hardening (ionizing radiation resistance) process for MOS type components and CMOS or bipolar type components. The ionizing radiation effect on those systems is the electron-hole pair production, which induces interference phenomena. The MOS main structure is successively composed of a silicon substrate layer, a layer of an irradiation resistant material and a layer of partially monocrystalline silicon.

Energy Technology Data Exchange (ETDEWEB)

Visible laser light output from an electrically injected vertical cavity surface emitting laser (VSCEL) diode is enabled by the addition of phase-matching spacer layers on either side of the active region to form the optical cavity. The spacer layers comprise InAlP which act as charge carrier confinement means. Distributed Bragg reflector layers are formed on either side of the optical cavity to act as mirrors. 5 figs.

Energy Technology Data Exchange (ETDEWEB)

A transient-enhanced diffusion has been observed during the furnace or rapid thermal annealing of ion-implanted silicon. We have studied this transient in detail and show that, for doses of Group V dopants sufficient to amorphize the silicon, it arises from the trapping of interstitials by dopant atoms during implantation. These are retained during solidphase-epitaxial (SPE) growth, but can be released by additional thermal processing to cause the observed transient and the formation of a band of extended defects. We have measured the enhanced diffusion coefficients and the duration of the transient for Sb-implanted Si by careful furnace annealing experiments. We obtain general expressions which predict the effects of the transient during any thermal processing based on SPE growth (furnace, CW laser, or rapid thermal annealing). We show that there is no analogous mechanism of vacancy trapping by Group III elements.

International Nuclear Information System (INIS)

We have studied in detail the transient enhanced diffusion observed during furnace or rapid-thermal-annealing of ion-implanted Si. We show that the effect originates in the trapping of Si atoms by dopant atoms during implantation, which are retained during solid-phase-epitaxial (SPE) growth but released by subsequent annealing to cause a transient dopant precipitation or profile broadening. The interstitials condense to form a band of dislocation loops located at the peak of the dopant profile, which may be distinct from the band formed at the original amorphous/crystalline interface. The band can develop into a network and effectively getter the dopant. We discuss the conditions under which the various effects may or may not be observed, and discuss conflicting observations on As"+ implanted Si.

Energy Technology Data Exchange (ETDEWEB)

We have studied in detail the transient enhanced diffusion observed during furnace or rapid-thermal-annealing of ion-implanted Si. We show that the effect originates in the trapping of Si atoms by dopant atoms during implantation, which are retained during solid-phase-epitaxial (SPE) growth but released by subsequent annealing to cause a transient dopant precipitation or profile broadening. The interstitials condense to form a band of dislocation loops located at the peak of the dopant profile, which may be distinct from the band formed at the original amorphous/crystalline interface. The band can develop into a network and effectively getter the dopant. We discuss the conditions under which the various effects may or may not be observed, and discuss conflicting observations on As/sup +/ implanted Si.

British Library Electronic Table of Contents (United Kingdom)

The light-emitting properties of cubic silicon carbide films grown by vacuum vapor phase epitaxy on Si(100) and Si(111) substrates under conditions of decreased growth temperatures (T gr ? 900?700?C) have been discussed. Structural investigations have revealed a nanocrystalline structure and, simultaneously, a homogeneity of the phase composition of the grown 3C-SiC films. Photoluminescence spectra of these structures under excitation of the electronic subsystem by a helium-cadmium laser (?excit = 325 nm) are characterized by a rather intense luminescence band with the maximum shifted toward the ultraviolet (?3 eV) region of the spectral range. It has been found that the integral curve of photoluminescence at low temperatures of measurements is split into a set of Lorentzian components. Th...

International Nuclear Information System (INIS)

There have been several reports of transient-enhanced diffusion during furnace or rapid thermal annealing of ion-implanted silicon and some reports of no enhancement. In this contribution, the authors show that many of the observed effects can be accounted for by an interstitial trapping mechanism, in which large numbers of Si atoms are trapped by group V dopant atoms in the amorphous material during implantation. These trapped atoms are retained during solid-phase-epitaxial (SPE) growth, but can be released later during thermal processing to give the transient-enhanced diffusion. The authors present a model which can predict the transient effects (or lack of them) for any concentration of Sb, Bi, or As dopants sufficient to amorphize the silicon and any thermal processing technology which relies on SPE growth (furnace, cw laser, or rapid thermal annealing).

International Nuclear Information System (INIS)

InP-quantum dots (QDs) are promising sources of single-photons and as active laser medium, emitting in the red part of the visible spectrum and thus in the range of the highest sensitivity of current silicon detectors. The self assembled QDs were grown by metal organic vapor phase epitaxy and are embedded in between distributed Bragg reflectors (DBRs), afterwards the sample was processed by a Focused Ion Beam to fabricate micro-pillars. The DBRs and the high refractive index step between pillar and air results in a three dimensional mode confinement and highly directed emission and thus higher intensity. We have investigated the mode spectra by micro-photoluminescence measurements for different pillar diameters and compared the spectra with a theoretical model showing up good consistency. Q-factors up to 3600 were achieved.

Energy Technology Data Exchange (ETDEWEB)

Nanoscale islands of Cu2O have been synthesized on single-crystal SrTiO3 (100) substrates using oxygen plasma-assisted molecular-beam epitaxy (OPA-MBE). Island growth location has been controlled by using an ex-situ Ga+ focused ion beam (FIB) to modify the growth surface in discrete locations prior to island synthesis. Analysis of Cu2O dot growth on unmodified substrate regions revealed an evolution of dot size and array density. Atomic force microscopy studies show that certain FIB substrate modification and MBE growth condition combinations lead to directed self-assembly of islands. Islands initially formed in the FIB-generated surface topography and filled those features before nucleating on neighboring unmodified surface regions.

Energy Technology Data Exchange (ETDEWEB)

Nanoscale islands of Cu?O have been synthesized on single crystal SrTiO? (100) substrates using oxygen plasma assisted molecular beam epitaxy (MBE). Island growth location has been controlled by using an ex-situ Ga? focused ion beam (FIB) to modify the growth surface in discrete locations prior to island sythesis. The FIB modifications have generated surface topography with lateral dimensions of 150-200 nm. Ex-situ AFM study after island growth reveals that certain FIB substrate modification and MBE growth condition combinations lead to directed self-assembly of metal oxide islands at the edges of the FIB modified zones.

Energy Technology Data Exchange (ETDEWEB)

During the recrystallization by solid-phase-expitaxial (SPE) growth of supersaturated silicon alloys, a high concentration of interstitials is trapped. These are released by subsequent heating causing a transient (greatly enhanced) diffusion of the substitutional dopant by an interstitialcy mechanism. The enhancement may be as much as five orders of magnitude over tracer values, and shows an activation energy of only 1.8 +/- 0.2 eV. Following the transient, the interstitials condense into loops, allowing an independent estimate to be made of their concentration. From these observations, it is proposed that during ion implantation, a fraction of the implanted dopants can acquire their natural valency, and retain it as the crystallization interface passes. For group V dopants this creates the trapped interstitials, giving transient enhanced diffusion when they are released by subsequent annealing. 12 references, 6 figures.

Science.gov (United States)

An interest in electronic materials has led me to investigate new synthetic approaches to III-V' type semiconducting (13-15, current IUPAC designation for B and N groups in the Periodic Table) and magnetic (3-15) compounds. It is now possible to prepare binary (GaAs and GdP) and ternary mixed-metal (Al[sub x]Ga[sub 1-x]As) and mixed-pnictide (GaP[sub x]As[sub 1-x]) compounds in seconds from rapid, low-temperature-initiated metathesis reactions between a metal (III) trihalide and a trisodium pnictide, exemplified by MX[sub 3] + Na[sub 3]Pn [yields] MPn + 3 NaX, where M is Al, Ga, In, (Al,Ga), or a lanthanide; X is F, Cl, or I; and Pn is P, As, Sb, or (P,As). The precursors are mixed together in a dry box and ignited by light grinding with a mortar and pestle, or by brief, local heating from a hot filament. These reactions are very exothermic (calculated [Delta]H[sub rxn] (GaAs) = 138 kcal/mol) and typically reach temperatures in excess ...

Energy Technology Data Exchange (ETDEWEB)

GaAs-based dc high voltage photoguns used at accelerators with extensive user programs must exhibit long photocathode operating lifetime. Achieving this goal represents a significant challenge for proposed high average current facilities that must operate at tens of milliamperes or more. This paper describes techniques to maintain good vacuum while delivering beam, and techniques that minimize the ill effects of ion bombardment, the dominant mechanism that reduces photocathode yield of a GaAs-based dc high voltage photogun. Experimental results presented here demonstrate enhanced lifetime at high beam currents by: (a) operating with the drive laser beam positioned away from the electrostatic center of the photocathode, (b) limiting the photocathode active area to eliminate photoemission from regions of the photocathode that do not support efficient beam delivery, (c) using a large drive laser beam to distribute ion damage over a larger area, and (d) by applying a relatively low bias ...

British Library Electronic Table of Contents (United Kingdom)

An investigation into a three-dimensional, curved shock wave interacting with a three-dimensional, curved boundary layer on a slender body is presented. Three different nose profiles mounted on a cylindrical body were tested in a supersonic wind tunnel and numerically simulated by solving the Navier?Stokes equations. The conical and hemispherical nose profiles tested were found to generate shock waves of sufficient strength to separate the boundary layer on the cylinder, while the shock wave generated by the ogival profile did not separate the boundary layer. For the separated flow, separation was found to occur predominantly on the windward side of the cylinder with the lee-side remaining shielded from the direct impact of the incident shock wave. A thickening of the boundary layer on the...

Energy Technology Data Exchange (ETDEWEB)

Thin films of sodium montmorillonite clay and cationic polyacrylamide were grown on a polyethylene terephthalate film using layer-by-layer assembly. After 30 clay-polymer layers are deposited, with a thickness of 571 nm, the resulting transparent film has an oxygen transmission rate (OTR) below the detection limit of commercial instrumentation (< 0.005 cc/m{sup 2}/day/atm). This low OTR, which is unprecedented for a clay-filled polymer composite, is believed to be due to a brick wall nanostructure comprised of completely exfoliated clay in polymeric mortar. With an optical transparency greater than 90% and potential for microwaveability, this thin composite is a good candidate for foil replacement in food packaging and may also be useful for flexible electronics packaging.

International Nuclear Information System (INIS)

This report summarizes the findings of a five-month LDRD project funded through Sandia's NTM Investment Area. The project was aimed at providing the foundation for the development of advanced functional materials through the application of ultrathin coatings of microporous or mesoporous materials onto the surface of substrates such as silicon wafers. Prior art teaches that layers of microporous materials such as zeolites may be applied as, e.g., sensor platforms or gas separation membranes. These layers, however, are typically several microns to several hundred microns thick. For many potential applications, vast improvements in the response of a device could be realized if the thickness of the porous layer were reduced to tens of nanometers. However, a basic understanding of how to synthesize or fabricate such ultra-thin layers is lacking. This report describes traditional and novel approaches to the ...

Energy Technology Data Exchange (ETDEWEB)

As for surface treatment of steel, the ion nitriding method has a lot of advantages and is practically used, while the plasma nitriding is known as a method which is faster in nitriding than the ion nitriding method. However, there are few reports and many unclear points on the plasma nitriding method. In this study, the plasma nitriding of pure iron and SUS304 is conducted using r.f. nitrogen plasma glow discharge to examine composition of the nitrided layers, microstructures, nitriding rate, etc. Moreover, by exposing the specimen once nitrided to H2 plasma, a phenomenon that nitrogen comes out of the specimen surface is examined. It is found from the result that the nitrided layer is divided into a compound layer and a diffusion layer in order from the surface, that in case of pure iron, the compound layer grows predominantly at a low temperature, and the diffusion ...

Energy Technology Data Exchange (ETDEWEB)

A brief review and assessment of field measurement programs that provide data for mixed layer diffusion research is presented. The majority of programs emphasize either the meteorological aspects of the mixed layer or plume characterization. Few programs are available that provide the complimentary blend of plume and appropriate meteorological measurements needed to adequately validate mixed layer diffusion theory. Three major U.S. EPA (Environmental Protection Agency) field programs that provide data bases for model development and validation of mixed layer diffusion processes are described and discussed in more detail. The Regional Air Pollution Study (RAPS) focused on measurements of surface and mixed layer turbulent transport processes in the urban environment. The Tennessee Plume Study (TPS) obtained a database with coincident measurement of boundary layer ...

Energy Technology Data Exchange (ETDEWEB)

The present work describes the surface improvement and biocompatibility of TiAl{sub 24}Nb{sub 10} intermetallic alloy using rf plasma nitriding. The nitriding process was carried out at different plasma power from 400 W to 650 W where the other plasma conditions were fixed. Grazing incidence X-ray diffractometry (GIXRD), Auger electron spectroscopy (AES), tribometer and a nanohardness tester were employed to characterize the nitrided layer. Further potentiodynamic polarization method was used to describe the corrosion behavior of the un-nitrided and nitrided alloy. It has been found that the Vickers hardness (HV) and corrosion resistance values of the nitrided layers increase with increasing plasma power while the wear rates of the nitrided layers reduce by two orders of magnitude as compared to those of the un-nitrided layer. This improvement in surface properties of the intermetallic alloy is due to ...

International Nuclear Information System (INIS)

We have developed a chemical process for incorporating copper into indium gallium selenide layers with the goal of creating a precursor structure for the formation of copper indium gallium diselenide (CIGS) photovoltaic absorbers. Stylus profilometry, EDX, Raman spectroscopy, XRD and SIMS measurements show that when indium gallium selenide layers are immersed in a hot copper chloride solution, copper is incorporated as copper selenide with no increase in the thickness of the layers. Further measurements show that annealing this precursor structure in the presence of selenium results in the formation of CIGS and that the supply of selenium during the annealing process has a strong effect on the morphology and preferred orientation of these layers. When the supply of Se during annealing begins only once the substrate temperature reaches ? 400 deg. C , the resulting CIGS layers are ...

International Nuclear Information System (INIS)

The layer-by-layer (LBL) self-assembly has been extensively used as a simple and effective method for the preparation of polyelectrolyte multilayer films. In this work, we utilized this unique method to prepare polyimide precursor/layered double hydroxide (LDH) ultrathin films. Well-crystallized Co-Al-CO_3 LDH and subsequent anion exchanged Co-Al-NO_3 LDH were prepared and characterized by scanning electron microscopy and X-ray diffraction (XRD). By vigorous shaking of the as-prepared Co-Al-NO_3 LDH, positively charged and exfoliated LDH nanosheets were obtained. Atomic force microscopy and XRD investigations indicated the delamination of LDH nanosheets. The precursor of polyimide, poly(amic acid) tertiary amine salt (PAS) was prepared by the polycondensation of dianhydride and diamine, and subsequent amine salt formation. By using the LBL method, heterogeneous ultrathin films of PAS and LDH were prepared. The formation of the ordered ...

Science.gov (United States)

Target vessel materials used in spallation neutron source will be exposed to proton and neutron irradiation and mercury immersion environments. In order to evaluate the surface degradation of the vessel candidate materials due to such environment, the triple-ion beam irradiation taking the spallation reaction into account and mercury immersion tests were carried out. Mechanical properties of the gradient surface layer were evaluated by the inverse analysis with multi-layer model that considers distribution of surface characteristic was applied to the load and depth curves measured by using the instrumented indentation machine. Transmission electron microscopic observations were performed to evaluate the changes of microstructure in irradiated surface layer using focused ion-beam cut micro-specimen. The mechanical properties distributions in the surface layer were evaluated quantitatively and the changes ...

International Nuclear Information System (INIS)

A highly reliable screening method was developed for the determination of lead in tin plated layers and tin-bismuth plated layers. The contents of lead in the layers of the various samples were determined by inductively coupled plasma optical emission spectrometry. The calibration curve for lead in the tin and tin-bismuth plated layers by using WD-XRF exhibited linear correlation from 130 #mu#g/g to 2070 #mu#g/g. Calibration curve of lead normalized with Pb-L#alpha#/Sn-K#alpha# intensity was more linear, and this method was possible to evaluate very small sample. The calibration curve for lead in the tin plated layers by using ED-XRF was good linearly, but it for lead in the tin-bismuth plated layers was affected by Pb-L#alpha# spectrum and Bi-L#alpha# spectrum overlap each other. It was effective for decreasing affect of Bi-L#alpha# spectrum by using curve ...

Energy Technology Data Exchange (ETDEWEB)

Thin passive films formed on highly corrosion-resistant type-312L stainless steel, containing 20 mass% chromium and 6 mass% molybdenum, in 2 mol dm{sup -3} HCl solution at 293 K have been analyzed by glow discharge optical emission spectroscopy (GDOES). The stainless steel does not suffer pitting corrosion even in this aggressive solution, showing a wide passive potential region. The depth profiles obtained clearly show a two-layer structure of the air-formed and passive films: an outer iron-rich layer and an inner layer highly enriched in chromium. Alloy-constituting molybdenum is deficient in the inner layer of the passive films and is enriched in the outer layer, particularly at the active dissolution potential. The molybdenum species in the outer layer may retard the active dissolution of stainless steel, promoting the formation of stable passive films ...

Energy Technology Data Exchange (ETDEWEB)

An approximate analyzing model was developed to predict the azimuth of zigzag streamline, the distribution ratio between two neighboring layers and the radial distribution among the layers of the gas passing through the shaft of blast furnace loaded in layers. The theoretical basis of the approximate analysis is composed of the material balance derived from the assumption that any stream line surrounded with two streamlines is isolated and no material transfer occurs through the tube wall, and of the energy theory that the stream tube and passage are formed so that the total pressure drop in the whole system is the minimum. The effects of the apparent angle of repose between two layers, the packing volume and the passage resistance on the non-uniform flow in the layer were evaluated on the basis of the model. The result calculated by the approximate analysis agrees with the result ...

Science.gov (United States)

The properties of the mixing layer in dynamic systems were studied by the example of a mathematical model of the cubic image type. Its role in the generation of information and the evolution of its significance was shown. At the moment of generation, information is of zero significance, and this significance then increases. A criterion of efficiency was proposed, and the optimum moment of making a decision in creative work was determined. It was shown that the increase in the variability of the parameters of a living system upon entry into the mixing layer and its decrease upon exit can serve as objective indicators of the transition of the system from one dynamic regime (attractor) to another. PMID:12723364

Science.gov (United States)

This letter describes the first lasing experiment of the heterostructure semiconductor Raman laser with lateral confinement of both the Stokes and pump fields. It has a GaP Raman active layer with thickness of 10 ..mu..m and Al/sub 0.1/Ga/sub 0.9/P cladding layers. The stripe of the active layer has been fabricated by a plasma etching technique. Steps should be taken to realize the semiconductor Raman laser pumped by an injection laser, applicable to wideband optical communication.

International Nuclear Information System (INIS)

Extended X-ray absorption fine structure (EXAFS) measurements of bismuth clusters in the temperature range of 23 -300 K have been performed using synchrotron radiation in order to investigate the size dependent phase transition. The inter-atomic distances around 3.0 A and 3.6 A are attributed to the nearest neighbors within the layer and between layers, respectively. EXAFS functions were analysed by the curve fitting method within a symmetric distribution approximation. The nearest neighbor distance of the 0.5 nm thick films is shorter than that of the 300 nm thick films at all the temperatures, which is related to the reduction of the inter-layer correlation.

International Nuclear Information System (INIS)

The changes in microstructure of a specially prepared boron nitride (BN) film as a function of film depth were studied by high resolution transmission electron microscopy (HRTEM) and other materials analysis tools. These changes were then correlated to the changes in processing parameters during film growth. The analyzed film was fabricated by the four-step ion-assisted deposition procedure known to be effective in film-stress engineering for the formation and retention of a thick cubic BN (cBN) layer with a three-step buffer-layer deposition. In this deposition, the energy of the ions assisting cBN formation was increased stepwise from 200 to 280, and then to 360 eV [S.F. Wong, C. W. Ong, G.K.H. Pang, K.Z. Baba-Kishi, W. M. Lau, J. Vac. Sci. Technol. A 22 (2004) 676]. The nominal thickness of the cBN layer was 650 nm and that for each of the three buffer layers was about 160 nm. Both the HRTEM and ...

British Library Electronic Table of Contents (United Kingdom)

The acoustic hyperlens can be realized by an alternating layered structure of water and fluid with negative mass density. Based on this alternating layered principle, we propose that an acoustic metamaterial consisting of three layers in water background can be designed to replace the fluid with negative mass density. The effective mass density and bulk modulus of the system which is composed of acoustic metamaterial and water are functions of the frequency. The effective mass density of such a system is close to the negative mass density of the fluid at a specific frequency; thus an acoustic metamaterial hyperlens can be achieved.

International Nuclear Information System (INIS)

This thesis is devoted to the study and development of Heterojunction Bipolar Transistors (HBTs) designed for high voltage operation. The work concentrates on the use of wide bandgap III-V semiconductor materials as the collector material and their associated properties influencing breakdown, such as impact ionisation coefficients. The work deals with issues related to incorporating a wide bandgap collector into double heterojunction structures such as conduction band discontinuities at the base-collector junction and results are presented which detail, a number of methods designed to eliminate the effects of such discontinuities. In particular the use of AlGaAs as the base material has been successful in eliminating the conduction band spike at this interface. A method of electrically injecting electrons into the collector has been employed to investigate impact ionisation in GaAs, GaInP and AlInP which has used the intrinsic gain of the devices to extract impact ...

British Library Electronic Table of Contents (United Kingdom)

We carried out theoretical analyses based on ab initio calculations incorporates in which free energy of the vapor phase is incorporated in order to determine the initial growth kinetics of c-GaN on GaN(001)-(4x1). The feasibility of the theoretical approach had been confirmed by calculations of Ga adsorption-desorption transition temperature and transition beam equivalent pressures on the GaAs(001)-(4x2)b2 surface in our previous work [Y. Kangawa, T. Ito, A. Taguchi, K. Shiraishi, T. Ohachi, Surf. Sci. 493 (2001) 178]. The results of calculations suggest that no Ga adsorption occurs on the initial surface under typical growth conditions but that a Ga adsorption site appears after N adsorption on GaN(001)-(4x1). That is, in the initial growth stage of c-GaN on GaN(001)-(4x1), a N-adsorbed ...

International Nuclear Information System (INIS)

Thinning specimens to electron transparency for electron microscopy analysis can be done by conventional (2-4 kV) argon ion milling or focused ion beam (FIB) lift-out techniques. Both these methods tend to leave 'mottling' visible on thin specimen areas, and this is believed to be surface damage caused by ion implantation and amorphisation. A low energy (250-500 V) Argon ion polish has been shown to greatly improve specimen quality for crystalline silicon samples. Here we investigate the preparation of technologically important materials for nanoanalysis using conventional and lift-out methods followed by a low energy polish in a GentleMill"T"M low energy ion mill. We use a low energy, low angle (6-8 deg.) ion beam to remove the surface damage from previous processing steps. We assess this method for the preparation of technologically important materials, such as steel, silicon and GaAs. For these materials the ability to create specimens from specific sites, and ...

Science.gov (United States)

A high-efficiency 3- or 4-junction solar cell is disclosed with a theoretical AM0 energy conversion efficiency of about 40%. The solar cell includes p-n junctions formed from indium gallium arsenide nitride (InGaAsN), gallium arsenide (GaAs) and indium gallium aluminum phosphide (InGaAlP) separated by n-p tunnel junctions. An optional germanium (Ge) p-n junction can be formed in the substrate upon which the other p-n junctions are grown. The bandgap energies for each p-n junction are tailored to provide substantially equal short-circuit currents for each p-n junction, thereby eliminating current bottlenecks and improving the overall energy conversion efficiency of the solar cell. Additionally, the use of an InGaAsN p-n junction overcomes super-bandgap energy losses that are present in conventional multi-junction solar cells. A method is also disclosed for fabricating the high-efficiency 3- or 4-junction solar cell by metal-organic chemical vapor deposition (MOCVD). ...

Science.gov (United States)

A newly developed 220 Mbps free-space 4-ary pulse position modulation (PPM) direct detection optical communication system is described. High speed GaAs integrated circuits were used to construct the PPM encoder and receiver electronic circuits. Both PPM slot and word timing recovery were provided in the PPM receiver. The optical transmitter consisted of an AlGaAs laser diode (Mitsubishi ML5702A, lambda=821nm) and a high speed driver unit. The photodetector consisted of a silicon avalanche photodiode (APD) (RCA30902S) preceded by an optical interference filter (delta lambda=10nm). Preliminary tests showed that the self-synchronized PPM receiver could achieve a receiver bit error rate of less than 10(exp -6) at 25 nW average received optical signal power or 360 photons per transmitted information bit. The relatively poor receiver sensitivity was believed to be caused by the insufficient electronic bandwidth of the APD preamplifier and the poor linearity of the ...