Physical properties of wood-polymer composites prepared by an electron beam accelerator  

Energy Technology Data Exchange (ETDEWEB)

The dual characteristics in the performance of polymers in wood-polymer composites systems have been pursued with regard to the resolution of mechanical anisotropy of wood and the improvement in dimensional stability. The objective of the present study is to pursue the polymerization mechanism in wood under electron beam irradiation and the temperature dependence of polymer-wood interactions induced at various levels of higher order structure of wood in order to understand the polymer performance. Veneers used in the study were of rotary-cut beech (Fagus crenata Blume) 0.65 mm thick. All samples were oven-dried in vacuo at 80/sup 0/C for 30 hr. The monomers used in the study were methyl methacrylate, styrene, acrylic acid, acrylonitrile, and unsaturated polyester. Experimental details are given. Results are given and discussed.

1981-01-01

2

Possible preparation of wood-plastic materials based on unsaturated polyester resins and methyl metacrylate, by radiation and chemical methods in combination  

Energy Technology Data Exchange (ETDEWEB)

The preparation of wood-plastic combinations (WPC) using combined methods for curing intermediate products and final products is described. In the first step, impregnated wood was irradiated using doses of 1 to 10 kGy in the presence of chemical initiators of polymerization. Thereafter, curing of this partly cured impregnating mixture was accomplished in the wood at elevated temperatures with the aid of chemical initiators of polymerization. Impregnation mixtures based on unsaturated polyester resins and methyl methacrylate, and the wood species European Beech (Fagus silvatica) and Black Alder (Alnus glutinosa) were used. The results indicate that this method of preparing WPC allows substantially lower radiation doses to be used, i.e., doses in the range of 1 to 2.5 kGy. These doses gelatinate the impregnation mixture in the wood so that the subsequent curing by chemical polymerization initiators proceeds without the impregnation mixture flowing out of the wood, ...

1982-04-01

3

Possible preparation of wood-plastic materials based on unsaturated polyester resins and methyl metacrylate, by radiation and chemical methods in combination  

International Nuclear Information System (INIS)

The preparation of wood-plastic combinations (WPC) using combined methods for curing intermediate products and final products is described. In the first step, impregnated wood was irradiated using doses of 1 to 10 kGy in the presence of chemical initiators of polymerization. Thereafter, curing of this partly cured impregnating mixture was accomplished in the wood at elevated temperatures with the aid of chemical initiators of polymerization. Impregnation mixtures based on unsaturated polyester resins and methyl methacrylate, and the wood species European Beech (Fagus silvatica) and Black Alder (Alnus glutinosa) were used. The results indicate that this method of preparing WPC allows substantially lower radiation doses to be used, i.e., doses in the range of 1 to 2.5 kGy. These doses gelatinate the impregnation mixture in the wood so that the subsequent curing by chemical polymerization initiators proceeds without the impregnation mixture flowing out of the wood, ...

1982-01-01

4

Simulated nitrogen deposition affects wood decomposition by cord-forming fungi.  

Science.gov (United States)

Anthropogenic nitrogen (N) deposition affects many natural processes, including forest litter decomposition. Saprotrophic fungi are the only organisms capable of completely decomposing lignocellulosic (woody) litter in temperate ecosystems, and therefore the responses of fungi to N deposition are critical in understanding the effects of global change on the forest carbon cycle. Plant litter decomposition under elevated N has been intensively studied, with varying results. The complexity of forest floor biota and variability in litter quality have obscured N-elevation effects on decomposers. Field experiments often utilize standardized substrates and N-levels, but few studies have controlled the decay organisms. Decomposition of beech (Fagus sylvatica) blocks inoculated with two cord-forming basidiomycete fungi, Hypholoma fasciculare and Phanerochaete velutina, was compared experimentally under realistic levels of simulated N deposition at Wytham Wood, Oxfordshire, ...

2011-07-01