British Library Electronic Table of Contents (United Kingdom)

In this project, nanocrystalline SnO2 powders were successfully prepared by (a) citrate sol-gel and (b) direct precipitation methods. Powders were characterized using thermal analysis techniques (DTA-TG-DSC), X-ray powder Diffraction (XRD), surface area (BET) and electrical conductivity measurements. XRD patterns showed the presence of the cassiterite structure. SnO2 particles, prepared through sol-gel method exhibit crystallite sizes in the range from 3.1 to 22.3 nm when the gel is heat treated at different temperatures up to 900?C. SnO2 nanocrystallites prepared by the precipitation method are comparatively larger in size. The higher specific surface area was obtained for the powder prepared using sol-gel method and the obtained average grain size (d) is relatively large compared with th...

British Library Electronic Table of Contents (United Kingdom)

We have investigated the effect of manganese (Mn) doping on properties of nanosized biphasic calcium phosphate powders and their dense bodies. Manganese levels of 0.6, 1.3, 1.9, 4.3, 7.0 and 11.9at.% were successfully incorporated into biphasic calcium phosphate via a sol-gel route. The prepared powders were calcined at temperatures of 500-1200^oC. The X-ray diffraction analysis revealed that a mix phase comprising of hydroxyapatite and @b-tricalcium phosphate were present, however the content of each phases in the structure was affected by the Mn content. The studies found that the largest portion of @b-tricalcium phosphate was detected at 4.3at.% Mn doping. The incorporation of Mn has also greatly increased the crystallinity of the biphasic calcium phosphate powder due to progressive den...

Science.gov (United States)

Not Available

International Nuclear Information System (INIS)

The nanosized luminescent Tb-MCM-41 (1:10) is synthesized by means of sol-gel-assisted self-assembly under basic conditions at room temperature. The results of "2"9Si-MAS NMR and XRD prove that Tb"3"+ doped Si-O framework. The HRTEM image shows that the regular uniform particles with a diameter of 10 nm possess ultralarge pore with diameter 2.0 nm, which is consistent with the result of N_2 adsorption. The BET surface area and porosity of Tb-MCM-41 (1:10) are 1127 m"2/g and 0.84 cm"3/g, respectively. The patterns of selected-area electron diffraction and XRD of Tb-MCM-41 (1:10) show an Fm3m space group in the cubic. FT-IR results show that the peaks near 970 cm"-"1 are assigned to the deformation vibration of silanol group. The as-products are calcined at 800 deg. C and the mesoporous materials possess enormous specific areas and large porosity, it shows that the mesoporous materials are ultrastable.

Energy Technology Data Exchange (ETDEWEB)

Porous nanostructured LiFePO{sub 4} powder with a narrow particle size distribution (100-300nm) for high rate lithium-ion battery cathode application was obtained using an ethanol based sol-gel route employing lauric acid as a surfactant. The synthesized LiFePO{sub 4} powders comprised of agglomerates of crystallites <65nm in diameter exhibiting a specific surface area ranging from 8m{sup 2}g{sup -1} to 36m{sup 2}g{sup -1} depending on the absence or presence of the surfactant. The LiFePO{sub 4} obtained using lauric acid resulted in a specific capacity of 123mAhg{sup -1} and 157mAhg{sup -1} at discharge rates of 10C and 1C with less than 0.08% fade per cycle, respectively. Structural and microstructural characterization were performed using X-ray diffraction (XRD), scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM) with energy dispersive X-ray (EDX) analysis while electronic conductivity and ...

International Nuclear Information System (INIS)

Nano-sized zinc oxide was synthesized and deposited onto cellulosic fibers using the sol-gel process at ambient temperature. The prepared materials were characterized using several techniques including scanning electron microscopy, transmission electron microscopy, diffuse reflectance spectroscopy, X-ray diffraction and thermogravimetric analysis. X-ray diffraction studies of the ZnO-coated fiber indicate formation of the hexagonal crystal phase which was satisfactory crystallized on the fiber surface. The electron micrographs show formation of zinc oxide nanoparticles within 10-15 nm in size which have been homogeneously dispersed on the fiber surface. The prepared materials show significant photocatalytic self-cleaning activity, which was monitored by diffuse reflectance spectroscopy. The photoactivity was studied upon measuring the photodegradation of methylene blue and eosin yellowish under UV-Vis irradiation. The ...

Energy Technology Data Exchange (ETDEWEB)

Y{sub 2-x}Tb{sub x}SiO{sub 5} and Y{sub 2-x}Eu{sub x}SiO{sub 5} nanophosphors with seven different kinds of silicate sources were synthesized by sol-gel method. The structures have been investigated to be composed of nanometer-size grains of 30-60 nm through X-ray diffraction (XRD) and scanning electron microscopy (SEM) was used to compare the different morphology of patterns from seven different silicon sources. The photoluminescence of Y{sub 2-x}Tb{sub x}SiO{sub 5} was investigated as a function of silicate sources and the results revealed that these nanometer materials showed the characteristic emission {sup 5}D{sub 4} {yields} {sup 7}F{sub J} (J 6, 5, 4, 3) of Tb ions. The characteristic emission {sup 5}D{sub 0} {yields} {sup 7}F{sub J} (J = 1, 2, 4) of Eu ions was also found in the materials of Y{sub 2-x}Eu{sub x}SiO{sub 5}.

Energy Technology Data Exchange (ETDEWEB)

In order to study the effects of microwaves on chemical reactions equipment was designed to acquire in-situ vibrational spectra of sol-gel components as they are irradiated with microwaves. Fourier Transform Infrared (FTIR) and Raman spectroscopy were used. A low temperature (10K) FTIR cell was used to trap samples in an argon matrix at 10{sup -7} Torr. For the liquid samples no differences were seen in spectra of irradiated and nonirradiated samples, but the argon matrix isolation technique showed dramatic differences.

British Library Electronic Table of Contents (United Kingdom)

In this research a sol-gel auto-combustion route has been proposed to synthesize strontium hexaferrite nanopowder, using metal nitrates, ammonia as pH adjusting agent, n-decyltrimethylammonium bromide as a cationic surfactant and different fuels such as citric acid, glycine, acetylacetone and oxalic acid. The formation temperature of strontium hexaferrite and its crystallite size in presence of different fuels were compared together. The results showed the lowest formation temperature as well as the smallest crystallite size in the presence of citric acid as 900degreeC and 37.3nm respectively.

Energy Technology Data Exchange (ETDEWEB)

Nano-particles of CeO{sub 2} with the smallest average particle size (18.7 nm) and spherical morphology were obtained from a mixture solution of Ce(NO{sub 3}){sub 3}{center_dot}6H{sub 2}O, citric acid, polyvinyl alcohol by an auto-combustion process exploiting sol-gel as precursors. The course of size control and shape control by polyvinyl alcohol was examined in detail. A transmission electron microscopy (TEM) and an atomic force microscopy (AFM) were employed to characterize the particle-size and morphology of CeO{sub 2} particles. In addition, a sort of nano-metric solid acid SO{sub 4}{sup 2-}/CeO{sub 2} based on CeO{sub 2} nano-particles was prepared by macerating, filtering, drying and calcining processes. The particle-size of SO{sub 4}{sup 2-}/CeO{sub 2} was also assessed by TEM. The composition of SO{sub 4}{sup 2-}/CeO{sub 2} was analyzed by X-ray diffraction (XRD) and infrared spectra (IR). The influencing factors in the formation of ...

International Nuclear Information System (INIS)

Hybrid organic-inorganic coatings with phosphonate functionalities have been synthesized and evaluated as prospective surface treatments for magnesium materials. These coatings have been processed via a sol-gel route by hydrolysis and condensation of a mixture of diethylphosphonatoethyltriethoxy-silane and tetraethoxy-silane with variable molar ratios. The coatings morphology and the surface chemistry at the coating/substrate interface have been characterized using scanning electron microscopy, X-ray photoelectron spectroscopy, "3"1P nuclear magnetic resonance spectroscopy, and time-of-flight secondary ion mass spectrometry. The corrosion protection performance of the coatings deposited on magnesium alloy AZ31B has been examined by a group of electrochemical techniques including potentiodynamic polarization and electrochemical impedance spectroscopy. In addition, a scanning Kelvin probe technique has been used to investigate interfacial properties of the coatings. ...

British Library Electronic Table of Contents (United Kingdom)

A highly sensitive and stable tris(2,2prime-bipyridyl)ruthenium(II) (Ru(bpy)32+) electrogenerated chemiluminescence (ECL) sensor was developed based on carbon nanotube (CNT) dispersed in mesoporous composite films of sol-gel titania and perfluorosulfonated ionomer (Nafion). Single-wall (SWCNT) and multi-wall carbon nanotubes (MWCNT) can be easily dispersed in the titania-Nafion composite solution. The hydrophobic CNT in the titania-Nafion composite films coated on a glassy carbon electrode certainly increased the amount of Ru(bpy)32+ immobilized in the ECL sensor by adsorption of Ru(bpy)32+ onto CNT surface, the electrocatalytic activity towards the oxidation of hydrophobic analytes, and the electronic conductivity of the composite films. Therefore, the present ECL sensor based on the CNT-...

British Library Electronic Table of Contents (United Kingdom)

Silica-reinforced natural rubber (NR) composite was prepared by using tetraethoxysilane (TEOS) as a precursor to generate silica particles inside the rubber. The silica was generated in situ by the sol-gel process of TEOS that was mixed directly into commercial-graded NR latex having 60% dry rubber content and 0.7% ammonia. The conversions of TEOS to silica inside the rubber were ranging from 90 to 97%. The silica particles dispersed evenly without extensive aggregation with sizes between 100 and 500 nm, as determined by scanning electron microscopy (SEM). An experimental design methodology, namely "two-level factorial design," was used to evaluate the influence of the amounts of TEOS, ammonia, and gelation time on the tensile modulus, tensile strength, and tear strength of the vulcanizate...

Energy Technology Data Exchange (ETDEWEB)

Ion storage CeO{sub 2} and CeO{sub 2}/SnO{sub 2} coatings were prepared by sol-gel dip-coating method using aqueous-based process. The influence of added SnO{sub 2} in the CeO{sub 2} oxide coatings on the inserted/extracted charge was determined by chronocoulometric measurements. It was found that for 60 nm thick film the inserted/extracted charge was twice larger (Q = 10mC/cm{sup 2}) for films containing 17 mol % SnO{sub 2} if compared to pure CeO{sub 2}. The addition of SnO{sub 2} to the mixed oxides coatings on their optical properties and structural characteristics were studied.

International Nuclear Information System (INIS)

Lead lanthanum zirconate titanate (PLZT) nanopowders with chemical compositions x/65/35 PLZT (x = 6 - 10 mol%) were prepared by sol-gel method. PLZT ceramics was obtained by the conventional sintering method and utilizing the hot pressing method. The investigations of dielectric and ferroelectric measurements of as obtained PLZT ceramics have revealed the influence of lanthanum concentration on the properties of PLZT electroceramics. (author)

British Library Electronic Table of Contents (United Kingdom)

Abstract A series of compounds with the general formula (La1-xSmx)2Ti2O7 (0-- x --1.0) has been synthesized by a sol-gel method and characterized by XRD, Raman spectroscopy, and scanning electron microscopy (SEM). These compounds are structurally isomorphic to perovskite-type La2Ti2O7 until a substitution rate of x = 0.8. Above this substitution rate (x >-0.8), a biphasic mixture is obtained between the substituted perovskite layered phase and the pyrochlore Sm2Ti2O7 phase. The unusual phosphor (La1-xSmx)2Ti2O7 has been elaborated and its luminescent properties were investigated for low rates of substitution. The emission and excitation spectra were used to study the luminescent properties. The (La1.9Sm0.1)2Ti2O7 powders emit bright red-orange lightunder UV excitation. The emission propert...

British Library Electronic Table of Contents (United Kingdom)

In this paper, we prepared by the sol-gel method alkaline titania catalysts, doped by gelling titanium alkoxide with aqueous solutions containing potassium, rubidium or cesium chlorides. XRD patterns showed that samples annealed at 400 and 600degreeC contained a single crystalline phase, anastase. Specific surface areas were higher in samples annealed at 400degreeC (>100m2/g) than in those annealed at 600degreeC (25m2/g). The weight density of basic sites determined by CO2-TPD drastically diminished in samples treated at 600degreeC. Catalysts were tested for the self-condensation of acetone at 300degreeC; main reaction products were isomesityl oxide, mesityl oxide and mesitylene. Samples annealed at 600degreeC showed lower acetone conversion rate and low formation of mesitylene than that o...

British Library Electronic Table of Contents (United Kingdom)

In this paper, an environmentally friendly metal corrosion inhibitor, phytic acid, was assembled into the walls of silica nanoparticles via layer-by-layer self-assembly technique (LbL) with poly(allylamine hydrochloride). Such functionalized nanoparticles were uniformly distributed into sol-gel films for metal anticorrosion. The films showed very pronounced and lasting protective efficiency in concentrated salt aqueous solutions as indicated by electrochemical impedance spectroscopy (EIS) measurement. These results may provide a new route for the preparation of environment-friendly anticorrosion coatings.

International Nuclear Information System (INIS)

The sol-gel-immobilized Tris(2,2'-bipyridyl)ruthenium(II) [Ru(bpy)_3 "2"+] electrogenerated chemiluminescence (ECL) sensor was applied to the reversed-phase high-performance liquid chromatography (HPLC) determination of phenothiazine derivatives (promazine, chlorpromazine, triflupromazine, thioridazine, and trifluoperazine) and erythromycin in human urine samples. In this method, Ru(bpy)_3 "2"+ was immobilized in sol-gel-derived titania (TiO_2)-Nafion nanocomposite films coated on a dual platinum electrode. This method eliminates an extra pump needed for the delivery of Ru(bpy)_3 "2"+ reagent into a reaction/observation zone in front of photomultiplier tube because the immobilized-Ru(bpy)_3 "2"+ is recycled on the electrode surface by an applied potential at +1.3 V versus Ag/AgCl (3 M NaCl) reference electrode. The resulting analytical performances such as detection limit, working range, sensitivity, and measurement precision were slightly ...

Science.gov (United States)

The liquid-phase synthesis of metal oxide nanoparticles in organic solvents under exclusion of water is nowadays a well-established alternative to aqueous sol-gel chemistry. In this article, we highlight some of the advantages of these routes based on selected examples. The first part reviews some recent developments in the synthesis of ternary metal oxide nanoparticles by surfactant-free nonaqueous sol-gel routes, followed by the discussion of the morphology-controlled synthesis of lanthanum hydroxide nanoparticles, and the presentation of structural peculiarities of manganese oxide nanoparticles with an ordered Mn vacancy superstructure. These examples show that nonaqueous systems, on the one hand, allow the preparation of compositionally complex oxides, and, on the other hand, make use of the organic components (initially present or formed in situ) in the reaction mixture to tailor the morphology. Furthermore, obviously even the crystal ...

Energy Technology Data Exchange (ETDEWEB)

Metallic nanoparticles was synthesized in SiO{sub 2} matrices by means of a process of two stages. The first one proceeded via sol-gel, incorporating the metallic precursors to the reaction system before the solidification of the matrix. Later on, the samples underwent a thermal treatment in atmosphere of H{sub 2}, carrying out the reduction of the metals that finally formed to the nanoparticles. Then it was detected the presence of smaller nanoparticles than 20 nm, dispersed and with the property of being liberated easily of the matrix, conserving a free surface, chemically reactive and with response to external electromagnetic radiation. The system SiO{sub 2}-Pd showed an important thermoluminescent response. (Author)

Energy Technology Data Exchange (ETDEWEB)

The catalytic oxygen transfer properties of vanadium containing zeolites and vanadium based sol-gel catalysts with hydrogen peroxides are well known. The severe problem of vanadium leaching caused by the presence of the by-product water has been addressed. To avoid any interference with homogeneously catalyzed reactions, our study focusses on selective oxidations in a moisture-free medium with tert.-butylhydroperoxide. We have investigated the catalytic properties of amorphous microporous materials based on SiO{sub 2}, TiO{sub 2}, ZrO{sub 2} and Al{sub 2}O{sub 3} as matrix material and studied the effects of surface polarity on the oxidation of 1-octene and cyclohexane. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Three different fuels UO{sub 2}-only, UO{sub 2}-Gd{sub 2}O{sub 3}(5%), and UO{sub 2}-Gd{sub 2}O{sub 3}(10%) were produced by sol-gel technique. Their powder characteristics such as flowability, BET surface area, average pore diameter, and cumulative pore volume were determined. The pore size distributions of powders, green pellets, and sintered fuels were determined by using a mercury porosimeter. The theoretical densities of sintered fuels were found to be 98.01, 95.3, and 95.9 %, respectively. Their ruggedness fractal dimensions were 1.111, 1.044, and 1.042, while the fractal dimensions associated with the size distribution of grains were 1.44, 1.58, and 1.60, respectively. (orig.).

Energy Technology Data Exchange (ETDEWEB)

A highly sensitive and stable tris(2,2'-bipyridyl)ruthenium(II) (Ru(bpy){sub 3} {sup 2+}) electrogenerated chemiluminescence (ECL) sensor was developed based on carbon nanotube (CNT) dispersed in mesoporous composite films of sol-gel titania and perfluorosulfonated ionomer (Nafion). Single-wall (SWCNT) and multi-wall carbon nanotubes (MWCNT) can be easily dispersed in the titania-Nafion composite solution. The hydrophobic CNT in the titania-Nafion composite films coated on a glassy carbon electrode certainly increased the amount of Ru(bpy){sub 3} {sup 2+} immobilized in the ECL sensor by adsorption of Ru(bpy){sub 3} {sup 2+} onto CNT surface, the electrocatalytic activity towards the oxidation of hydrophobic analytes, and the electronic conductivity of the composite films. Therefore, the present ECL sensor based on the CNT-titania-Nafion showed improved ECL sensitivity for tripropylamine (TPA) compared to the ECL sensors based on both titania-Nafion ...

Energy Technology Data Exchange (ETDEWEB)

Nb{sub 2}O{sub 5} thin films were formed on aluminum foils by a sol-gel process in order to increase the capacitance of the aluminum foils which are used as aluminum electrolytic capacitors. Investigations focussed on the preparation and characterization of the coating solution, the formation of Nb{sub 2}O{sub 5} thin films on aluminum foils, and the heat treatment and anodization of the films. The phase transition and electrical properties, such as capacitance, leakage current, and withstand voltage of the Nb{sub 2}O{sub 5} thin films were also measured. The Nb{sub 2}O{sub 5} thin films annealed at temperatures below 550 degree C were found to be amorphous, but they were crystallized to the orthorhombic phase by annealing at temperatures higher than 580 degree C. The capacitance of the coated samples increased with an increase in the thickness of the formed Nb{sub 2}O{sub 5} thin films, but an increase in leakage current and a decrease in withstand voltage were ...

International Nuclear Information System (INIS)

There has been a growing interest in new laser systems for use at mid-infra-red wavelengths, driven by requirements for a number of diverse applications. Developments in mid-IR coating technology are following three major thrusts. In the first, the potential of ion-assisted process is being exploited and the technology is already becoming well established in the optical coating industry. In the second, the benefits of using gas-phase precursors are being explored, driven by the potential of avoiding the generation of second phase inclusion in the coatings with associated reduction in laser damage threshold. Research is also addressing the use of nanocomposite materials with an engineered microstructure to produce coatings with dielectric properties of choice. This paper presents a review of progress in some of these areas with special emphasis on the comparison of the properties of materials at DF laser wavelengths. Evidence is presented which ...

Energy Technology Data Exchange (ETDEWEB)

Silver silica nanocomposites were obtained by the sol-gel technique using tetraethyl orthosilicate (TEOS) and silver nitrate (AgNO{sub 3}) as precursors. The silver nitrate concentration was varied for obtaining composites with different nanoparticle sizes. The structural and microstructural properties were determined by x-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR) and transmission electron microscopy (TEM). X-ray photoelectron spectroscopic (XPS) studies were done for determining the chemical states of silver in the silica matrix. For the lowest AgNO{sub 3} concentration, monodispersed and spherical Ag crystallites, with an average diameter of 5 nm, were obtained. Grain growth and an increase in size distribution was observed for higher concentrations. The occurrence of surface plasmon resonance (SPR) bands and their evolution in the size range 5-10 nm is studied. For decreasing nanoparticle size, a redshift and broadening of the ...

Energy Technology Data Exchange (ETDEWEB)

The Co-doped BaTiO{sub 3} nanosized powders and ceramics were prepared via the sol-gel process. The powders and ceramics were characterized by methods of XRD, SEM and TEM. The dielectric properties of the ceramics were also determined by these methods. The influence of sintering temperature, sintering time and Co concentration on the microstructure and dielectric properties was discussed. The results revealed that the powders were in nanometer scale (30-50 nm) and were mainly composed of cubic BaTiO{sub 3} phase and small amount of BaCO{sub 3}. After sintering, both the cubic BaTiO{sub 3} and BaCO{sub 3} were transformed into tetrahedron BaTiO{sub 3}. The sintering temperatures of the Co-doped BaTiO{sub 3} ceramics decreased (about 100 deg. C) and the Curie temperatures of the ceramics were then moved to lower temperature. In addition, the dielectric constant of the ceramics doping with Co was higher than that of the pure BaTiO{sub 3} ceramics. The dielectric ...

British Library Electronic Table of Contents (United Kingdom)

Ferroelectric barium strontium titanate (Ba0.7Sr0.3TiO3)(BST) thin films have been prepared from barium 2-ethylhexanoate [Ba[CH3(CH2)3CH(C2H5)CO2]2], strontium 2-ethylhexanoate [Sr[CH3(CH2)3CH(C2H5)CO2]2] and titanium(IV) isopropoxide [TiOCH(CH3)2]4 precursors using a modified sol-gel technique. The precursor except [TiOCH(CH3)2]4 were synthesized in the laboratory. Transparent and crack-free films were fabricated on pre-cleaned quartz substrates by spin coating. The structural and optical properties of films annealed at different temperatures have been investigated. The as-fired films were found to be amorphous that crystallized to the tetragonal phase after annealing at 550degreeC for 1h in air. The lattice constants "a" and "c" were found to be 3.974A and 3.990A, respectively. The grain...

Energy Technology Data Exchange (ETDEWEB)

Threshold pump intensity values leading to irreversible damage to colored laser elements based on elastic polymers were measured. The damage to colored elastomers is connected with absorbing microinclusions but is independent of molecular absorption. It is shown that damage to the elastomers has a pronounced threshold character in contrast to the microdamage accumulation effect in glassy polymers. The damage threshold for elastomers is 1.5 times higher, which is connected with the absence of microstresses (characteristics for organic glasses) in the specimens. 13 references.

International Nuclear Information System (INIS)

Transparent aluminum doped zinc oxide (ZnO:Al, AZO) conducting thin films with a high-preferential c-axis orientation were synthesized using a new sol-gel formula. The films were deposited using a spin-coating route onto borosilicate glass substrates. We used propylene glycol methyl ether (PGME) as the solvent in place of ethylene glycol monomethyl ether (EGME), which is commonly used because it is easier to deposit onto the substrates. PGME is also superior in terms of health and safety. PGME solvent does not need to settle for several days before use and can be spin-coated as soon as the raw material and solvent are mixed. The effects of this novel solvent on the structural, morphological, electrical and optical properties are discussed using XRD, SEM, a four-point probe and UV-VIS spectrophotometry. It was found that the films produced with PGME showed a high-preferential c-axis orientation and compact microstructure in comparison films produced using EGME. The ...

Energy Technology Data Exchange (ETDEWEB)

porous silica ceramics were prepared(with HCL catalyst)using H{sub 2}O/TEOS molar ratios of 2.6-59.0, with the EtOH/TEOS ratio fixed. After preparing 9 kinds of sol, the followings were investigated; measurement of the gelation time, thermal analyses by TG/DTA, property analyses of the intermediates by FT-IR and X-ray diffractometry with dried samples, analyses of SiO{sub 2} polymer by FT-IR, the investigation of specific surface area and pore size distribution by N{sub 2}-adsorption isotherm, and structural change of SiO{sub 2} polymer and pore morphology by TEM observation, with samples heat-treated to 500 deg. C. In the concentrations of investigated compositions and catalyst, gelation time showed a minimum at ca. 11 moles of water per one mole of TEOS, the highest degree of polymerization at ca.8-18 moles, and the largest specific surface area at ca. 11 moles, which means that the polymerization proceeded fastest at ca. 11 moles of water. In conclusion, the more water used, the ...

Energy Technology Data Exchange (ETDEWEB)

Thin solid films of CeO[sub 2] and mixed CeO[sub 2]-TiO[sub 2] were prepared by the sol-gel route via the dip-coating technique. Particulate sols of ceria were made from inorganic ((NH[sub 4])[sub 2]Ce(NO[sub 3])[sub 6]) precursor which were used for preparation of CeO[sub 2] thin solid films while CeO[sub 2]-TiO[sub 2] coatings have been made by using mixed organic-inorganic (Ti(OiPr)[sub 4] and CeCl[sub 3].7H[sub 2]O) precursors. The solar transmission values (T[sub s]) of both coatings are in the range 0.6-0.8 and depend on coating thickness. Cyclic voltammetric (CV) measurements show that the CeO[sub 2]/LiOH system exhibits higher overall electrochemical reversibility when compared to the CeO[sub 2]-TiO[sub 2]/LiOH system. The CeO[sub 2]/LiOH system is also less sensitive with regard to the coating thickness. Coulometric measurements show that CeO[sub 2] exhibits a larger storage capability which was determined as a function of the coating thickness. ...

Energy Technology Data Exchange (ETDEWEB)

V{sub 2}O{sub 5} based compounds are interesting low potential materials for rechargeable cathodes of lithium electrochemical generators. However, the ionic conductivity and the reversibility of electrochemical cycling of V{sub 2}O{sub 5} are limited by the possibilities of lithium insertion. This work shows that the doping of vanadium pentoxide by a M{sup 3+} trivalent transition element (M Fe, Al, Cr or La) allows to intercalate a more important amount of lithium and to improve the behaviour of the material during cycling. These materials of M{sub 0.11}V{sub 2}O{sub 5.16} formula are obtained by sol-gel synthesis. the electrochemical study of the Fe compound has shown that it is a mixed oxide with a behaviour similar to V{sub 2}O{sub 5}. The maximum capacity is of about 2 F/mole in the case of Fe, Al and Cr compounds and of about 1.7 F/mole in the case of La. The structural evolution of the Fe compound has been followed during the chemical insertion of Li and the ...

International Nuclear Information System (INIS)

Europium (Eu) ions-doped titanate nanowires were synthesized via a sol-gel-hydrothermal chemistry and they were found to be roll multilayered trititanate-type nanowires intercalated with Eu3+ and alkali ions. The average diameter was about 20 nm for nanowires synthesized in NaOH solution and about 10 nm for nanowires synthesized in KOH solution. Under ultraviolet excitation the nanowires showed bright red emission corresponding to 5D0-7Fj of Eu3+ ions at room temperature, which was attributed to the non-radiative energy transfer from the surrounding Ti-O octahedral nanosheets to the central Eu3+ ions in interlayer. The luminescent properties of nanowires were influenced by the type of co-intercalated alkali ions, doping degree, hydrothermal and annealing temperatures. The intensity ratio of 5D0-7F2 to 5D0-7F1 of titanate nanowires intercalated with Eu3+ and Na+ ions was higher than that of titanate nanowires intercalated with Eu3+ and K+ ions. The emission ...

Energy Technology Data Exchange (ETDEWEB)

We have grown ferroelectric Pb{sub 0.92}La{sub 0.08}Zr{sub 0.52}Ti{sub 0.48}O{sub 3} (PLZT) films on platinized silicon and LaNiO{sub 3}-buffered nickel substrates by chemical solution deposition using a sol-gel process based on acetic acid chemistry. The following measurements were obtained under zero-bias field: relative permittivity of {approx}960 and dielectric loss of {approx}0.04 on the PLZT film grown on Pt/Si substrates, and relative permittivity of {approx}820 and dielectric loss of {approx}0.06 on the PLZT film grown on LNO-buffered Ni substrates. In addition, a relative permittivity of 125 and dielectric loss of 0.02 were measured at room temperature under a high bias field of 1 x 10{sup 6} V/cm on PLZT deposited on LNO-buffered nickel substrate. Furthermore, a steady-state leakage current density of {approx}8.1 x 10{sup -9} A/cm{sup 2} and mean breakdown field strength of 1.7 x 10{sup 6} V/cm were measured at room temperature. Finally, remanent ...

International Nuclear Information System (INIS)

An attempt has been made to grow L-tartaric acid nicotinamide (LTN); a complex of tartaric acid, by employing a modified unidirectional method. The crystalline structure and quality are investigated by single crystal XRD and rocking curve studies. The linear and nonlinear optical properties are studied by UV-vis-NIR spectral analysis, SHG test, phase matching and laser induced damage threshold measurement. For comparison, parallel growth of the crystal was carried out by conventional method and the properties of the LTN samples grown by the conventional and unidirectional methods are investigated. The mechanical, photoconductivity and dielectric behavior of LTN crystals are also investigated.

Energy Technology Data Exchange (ETDEWEB)

An investigation was made of the accumulation of laser damage to transparent polymers irradiated with nanosecond pulses from neodymium and ruby lasers. The damage was investigated by the method of scattering and luminescence in the visible and near ultraviolet parts of the spectrum. It was established that there were two stages in laser damage by repeated irradiation with pulses of intensity below the single-shot damage threshold. An absorbing defect evolved during the first stage in such a way as to create a thermal instability in the surrounding matrix. During the second stage this thermal instability caused spatial growth of laser damage because of propagation of an ionization-inducing absorption wave with a front traveling at the rate governed by the electron component of the thermal conductivity.

Energy Technology Data Exchange (ETDEWEB)

The partial oxidation of 1,3-butadiene has been investigated over VMoO catalysts synthesized by sol-gel techniques. Surface areas were 9-14 m{sup 2}/g, and compositions were within the solid solution regime, i.e. below 15.0 mol % MoO{sub 3}/(MoO{sub 3} + V{sub 2}O{sub 5}). Laser Raman Spectroscopy and XRD data indicated that solid solutions were formed, and pre- and post-reaction XPS data indicated that catalyst surfaces contained some V{sup +4} and were further reduced in 1,3-butadiene oxidation. A reaction pathway for 1,3-butadiene partial oxidation to maleic anhydride was shown to involve intermediates such as 3,4-epoxy-1-butene, crotonaldehyde, furan, and 2-butene-1,4-dial. The addition of water to the reaction stream substantially increased catalyst activity and improved selectivity to crotonaldehyde and furan at specific reaction temperatures. At higher water addition concentrations, furan selectivity increased from 12% to over 25%. The catalytic effects of ...

Science.gov (United States)

Not Available

Science.gov (United States)

... Accession Number : ADA954164. Title : Electron Diffraction Examination of Gun Barrel Coatings. Descriptive Note : Special rept.,. ...

Energy Technology Data Exchange (ETDEWEB)

This report covers the technical effort through February, 1989. This effort was directed towards the technology associated with the development of a large scale, long pulse DF-CO{sub 2} chemical laser. Optics damage studies performed under Task 1 assessed damage thresholds for diamond-turned salt windows. Task 2 is a multi-faceted task involving the use of PHOCL-50 for laser gain measurements, LTI experiments, and detector testing by LANL personnel. To support these latter tests, PHOCL-50 was upgraded with Boeing funding to incorporate a full aperture outcoupler that increased its energy output by over a factor of 3, to a full kilojoule. The PHOCL-50 carbon block calorimeter was also recalibrated and compared with the LANL Scientech meter. Cloud clearing studies under Task 3 initially concentrated on delivering a Boeing built Cloud Simulation Facility to LANL, and currently involves design of a Cold Cloud Simulation Facility. A Boeing IRAD ...

Science.gov (United States)

No abstract prepared.

International Nuclear Information System (INIS)

Based on theoretical calculations of powder diffraction data it is shown that the assumption of the infinite crystal lattice for small particles is not justified, leads to significant changes of the diffraction patterns, and may lead to erroneous interpretation of the experimental results. An alternate evaluation of diffraction data of nanoparticles, based on the so-called 'apparent lattice parameter', alp, is proposed. (author)

Energy Technology Data Exchange (ETDEWEB)

Structure of ferrite in drawn pearlitic steel containing 0.9 mass% C was investigated with X-ray diffraction technique using synchrotron radiation. In the detailed analysis of diffraction peaks of ferrite during the drawing process, it was experimentally revealed that the transformation of ferrite from bcc to bct due to the supersaturation of carbon in ferrite of heavily drawn pearlitic steel.

Energy Technology Data Exchange (ETDEWEB)

Reflective diffraction grating. A focused ion beam (FIB) micromilling apparatus is used to store color images in a durable medium by milling away portions of the surface of the medium to produce a reflective diffraction grating with blazed pits. The images are retrieved by exposing the surface of the grating to polychromatic light from a particular incident bearing and observing the light reflected by the surface from specified reception bearing.

Energy Technology Data Exchange (ETDEWEB)

Understanding the mechanical properties of biomedical devices is critical in predicting and preventing their failure in the body. Such knowledge is essential, for example, in the design of biomedical stents, which must undergo repeated strain over their ten year lifetimes without breaking. Computational models are used to predict mechanical response of a device, but these models are not complete; there are significant deviations from the predictions, especially when devices are subjected to repeated multi-axial loads. Improving these models requires comparisons with actual measurements of strained nitinol. Local measurements of the full strain tensor can be made using X-ray diffraction techniques, but they are currently limited to materials whose grain size is larger than the X-ray beam size or require several diffraction patterns produced by rotation of the sample. Nitinol stents are nanocrystalline, with grains smaller than any available ...

International Nuclear Information System (INIS)

The results of X-ray and neutron diffraction experiments on molten alkali halides in which some data of our experiments by X-ray diffraction such as those of molten LiCl, NaCl, KCl, LiBr and KBr are included were summarized. The first peak positions in the radial distribution function in molten alkali halides by X-ray or neutron diffraction experiments are always longer than those by computer simulations and the differences of 0.1 -- 0.3 A exceed the experimental error. It seems to be due to the deformation of the electron shell. In the computer simulation, the shell model which has the spherical deformation was expected to have more closer value of the first peak position to the experimental one than the rigid ion model by taking the polarization of ions. However, no change in the first peak position was found. Therefore, the non-spherical deformation of electron shell at the point where ions are in contact with each other ...

Energy Technology Data Exchange (ETDEWEB)

White beam Laue micro-diffraction was performed on directionally solidified, single-crystal Mo pillars in the as-grown state, after focused ion beam (FIB) milling and after pre-straining. The Laue diffraction peaks from the as-grown pillars are very sharp and show no broadening, similar to those from single-crystal Si wafers. Significant broadening and streaking of the peaks occurred after FIB milling and pre-straining, indicative of the damage these treatments induce in the nearly perfect crystal structure of the directionally solidified Mo pillars.

International Nuclear Information System (INIS)

(1973). United Kingdom Baldwin, TO Dunn, JE Southern Illinois Univ.,

International Nuclear Information System (INIS)

... range magnetic fields magnetic susceptibility magnetization neutron diffraction

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

... 7 Page 11. Figure 5. Diffraction pattern shown a and ~ slip directions with the associated misalignment for single colonies of Ti6242 [2]. 8 Page 12. -- ...

Energy Technology Data Exchange (ETDEWEB)

The solid state reaction between a Pd thin film and a Si substrate produces a single new phase, Pd/sub 2/Si, for temperatures <700/sup 0/C. When the substrate is a single crystal of (111) surface orientation, this process is particularly interesting because the silicide grows epitaxially. Growth of epitaxial interfacial Pd/sub 2/Si was the focus of this study using X-ray diffraction techniques.

Energy Technology Data Exchange (ETDEWEB)

Ultrasound tomography is an attractive imaging method for the detection of breast cancer. The complex anatomy of the breast with its different spatial scales and material property contrasts make accurate reconstructions very challenging. This paper proposes a hybrid approach whereby Travel-of-Flight and Diffraction Tomography are combined together to achieve high-resolution and high-accuracy sound-speed reconstructions. The method is validated with several numerical phantoms.

Energy Technology Data Exchange (ETDEWEB)

In a forthcoming paper we describe a new approach to rapidity gap survival (RGS) in the production of high-mass systems (H = dijet, Higgs, etc.) in exclusive double-gap diffractive pp scattering, pp -> p + H + p. It is based on the idea that hard and soft interactions are approximately independent (QCD factorization), and allows us to calculate the RGS probability in a model-independent way in terms of the gluon generalized parton distributions (GPDs) in the colliding protons and the pp elastic scattering amplitude. Here we focus on the transverse momentum dependence of the cross section. By measuring the ''diffraction pattern'', one can perform detailed tests of the interplay of hard and soft interactions, and even extract information about the gluon GPD in the proton from the data.

International Nuclear Information System (INIS)

The results of real-time neutron diffraction measurements during the superconducting phase formation process in the Bi(Pb)-Sr-Ca-Cu-O system are reported. A Sr-Ca-Cu-O type precursor, with the same stoichiometry as the 2223 phase, was used as starting material, and the temperature range favorable to the formation of the 2223 phase was investigated. The diffraction patterns were processed by a multiphase Rietveld refinement. The formation and decomposition of the 2201 and 2212 phases were directly observed. Experimental evidence on the existence of a partially melted phase in the range 855-860 degrees C, involved in the formation of the 2223 phase, is discussed. 14 refs., 9 figs., 1 tab.

International Nuclear Information System (INIS)

Real-time neutron powder diffraction and small-angle scattering techniques have been developed on the TOF diffractometer DN-2 at the IBR-2 pulsed reactor at JINR (Dubna) with a total flux on the sample of 10"7 neutrons cm"-"2s"-"1 and a resolution of about 1%. A special arrangement of the detector system ensures a high counting rate of diffracted neutrons. Depending upon sample type and experimental conditions, the measuring time t_s of one neutron pattern varies from a few minutes to several seconds. The performance of the diffractometer is discussed and typical data are shown to demonstrate current achievements using real-time techniques at a pulsed reactor. (orig.).

International Nuclear Information System (INIS)

In an effort to explore Diffraction Enhanced Imaging of bone tissue, experiments were performed to determine if it was possible to use Diffraction Enhanced Imaging to detect microdamage in bovine cortical bone. Measurements were made at the National Synchrotron Light Source where pre- and post-fatigue rocking curve widths of the bone were studied. The rocking curve widths were then compared. Since no consistent pattern of narrowing or broadening of the rocking curve emerged, it is likely that the ultra-small-angle X-ray scattering present in the bone overshadowed any additional changes to rocking curve caused by microdamage of the bone. Larger bone structures were able to be visualized which suggests that microdamage may be visualized with a higher resolution detector.

International Nuclear Information System (INIS)

A new furnace for neutron diffraction experiments is capable of heating and cooling a sample very rapidly. The rapid heating is done by two circular infrared lamps placed over and under a sample, whose radiation is roughly focused on the sample by a reflector. The rapid cooling is done by high-pressure gas blows against the sample from two circular nozzles which are also placed over and under the sample. This system enables us to obtain the heating rate of over 1000"0C/min and cooling rate of -500"0C/min for an alloy of 10 mm diameter and 30 mm length. The performance is sufficient to carry out some kinetics measurements in real-time neutron diffraction by the use of a position-sensitive detector. This kind of experiment is demonstrated by the observation of the relaxation process of order--disorder transitions in CuZn and Ni_3Mn alloys.

Energy Technology Data Exchange (ETDEWEB)

The energy dispersive beamline X6A at the National Synchrotron Light Source employs a curved crystal monochromator (polychromator) which focuses a range ([similar to]1 keV) of x-ray energies into a narrow (100--120 [mu]m) line image. Although this beamline was constructed primarily for time-dependent EXAFS experiments, we have begun to explore the use of this instrument for energy dispersive diffraction experiments with different types of sample including macromolecular crystals. The tunability ([ital E]=6.5 to 21 keV) and flexibility ([Delta][ital E]=100--1000 eV) of the instrument makes the beamline ideal as a test bed for the application of polychromatic single-crystal diffraction techniques to different chemical or biological materials.

International Nuclear Information System (INIS)

The structure of ammonium azide (NH_4)N_3 was (re-)determined ab initio from x-ray powder diffraction experiment using synchrotron radiation. We tried to detail and comment the different steps involved in the structure determination. The compound crystallize in the orthorhombic Pmna space group (no.53) with a = 8.937(1) A, b= 3.8070(5) A, c = 8.664(1) A, V = 294.79(7) A"3; Z= 4. It was possible to locate and refine the hydrogen coordinates, in two different approaches, and to establish the H-bonds. The final structural parameters are in good agreement with previous results based on three-dimensional neutron diffraction. (Author)

UK PubMed Central (United Kingdom)

Electron microscopic analysis can be used to determine the three-dimensional structures of macromolecules at resolutions ranging between 3 and 30 A. It differs from nuclear magnetic resonance spectroscopy...Full Text Available

UK PubMed Central (United Kingdom)

AbstractX-ray diffraction analysis of pressure-induced structural changes in the Aequorea yellow fluorescent protein Citrine reveals the structural basis for the continuous...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

This article provides a survey of neutron scattering experiments in condensed matter research, which are of interest to chemistry. The theoretical background has been treated in a previous issue. The present article consists of two parts. The first part exhibits the range of experimental possibilities by means of a few selected examples. The starting point is classical neutron diffraction by which the position of atomic nuclei may be determined. Additional information on the spatial distribution in the outer electron shells may be obtained via combined X-ray/neutron-diffraction experiments or via the diffraction of polarized neutrons. Progress in instrumentation, due to the development of more intense sources, has influenced especially the fields of small angle scattering and spectroscopy. The second part features domains of research of current interest, where a combination of several neutron scattering techniques may prove ...

CERN Document Server

Hydroxyapatite samples were produced by two different wet-chemical methods, and characterized by x-ray diffraction, infrared and compression strength measurements. The x-ray diffraction measurements were simulated using the Rietveld method, and structural data as lattice parameters and average crystallite size were obtained. The infrared spectra showed the presence of CO$_3^{2-}$ ions in all samples, indicating a contamination by these ions. By mixing samples produced by both methods, a bioceramic was obtained and, after sintering, samples with very high compression strengths (26--30 MPa) were obtained.

International Nuclear Information System (INIS)

Phase transformations in TiD_#approx#_0_._7_5 subjected to high-pressure treatment were investigated by simultaneous real-time measurements of neutron diffraction and small-angle neutron scattering. The neutron spectra were taken on heating the samples in temperature ranges 100 to 300 K and 300 to 870 K. A sequence of structural transitions was observed, which involves 7 different phases and intermediate states with hcp, fcc, fco or bcc metal sublattices and hydrogen atoms. 30 refs., 9 figs., 1 tab.

Energy Technology Data Exchange (ETDEWEB)

To investigate the influence of equal channel angular pressing on the microstructure and texture of the magnesium alloy AZ31, electron backscattering diffraction and well as neutron diffraction experiments were carried out. Through these experiments it was possible to trace the microstructure and texture evolution with strain accumulated with the increasing number of equal channel angular pressing passes. It was further demonstrated by subsequent compression tests that the microstructural changes produced by equal channel angular pressing have a beneficial effect on both the compressive strength and ductility of AZ31. (orig.)

International Nuclear Information System (INIS)

We calculate the normalized factorial moments of multiplicity distributions through three models for elastic hadron scattering (Chou-Yang, Henzi-Valin and Menon-Pimentel). Connections between the moments and the inelastic overlap function and/or eikonal function are obtained by means of an impact parameter representation for the multiplicity distribution. The predictions are compared with experimental data on factorial moments from both inelastic and non-single-diffractive events. The model results present best agreement with the inelastic events and data favour the model by Henzi and Valin. (author)

International Nuclear Information System (INIS)

The reaction of RbC_2_4 with C_6D_6 vapour was studied by neutron diffraction on a time scale of 5 min/spectrum. As for the reaction of KC_2_4, a second stage phase RbC_2_4(C_6D_6)sub(y) is initially formed and subsequently transformed into a first stage phase. Model calculations indicate that the benzene rings are canted against the graphite planes both in the first and in the second stage phase. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

Fuel irradiation leads to a swelling resulting from the formation of gaseous (Kr, Xe) or solid fission products which are found either in solution or as solid inclusions in the matrix. This phenomena has to be evaluated to be taken into account in fuel cladding Interaction. Fuel swelling was studied as a function of burn up by measuring the corresponding cell constant evolution by X-Ray diffraction. This study was realized on Mixed Oxide Fuels (MOX) irradiated in a Pressurized Water Reactor (PWR) at different burn-up for 3 initial Pu contents. Lattice parameter evolutions were followed as a function of burn-up for the irradiated fuel with and without an annealing thermal treatment. These experimental evolutions are compared to the theoretical evolutions calculated from the hard sphere model, using the fission product concentrations determined by the APPOLO computer code. Contribution of varying parameters influencing the unit cell value is discussed. Thermal ...

International Nuclear Information System (INIS)

Studying the structure of nanoparticles as a function of their size requires a correlation between the image and the diffraction pattern of single nanoparticles. Nanobeam diffraction technique is generally used but requires long and tedious TEM investigations, particularly when nanoparticles are randomly oriented on an amorphous substrate. We bring a new development to this structural study by controlling the nanoprobe of the Bright and Dark Field STEM (BF/DF STEM) modes of the TEM. The particularity of our experiment is to make the STEM nanoprobe parallel (probe size 1 nm and convergence angle <1 mrad) using a fine tuning of the focal lengths of the microscope illumination lenses. The accurate control of the beam position offered by this technique allowed us to obtain diffraction patterns of many single nanoparticles selected in the digital STEM image. By means of this technique, we demonstrate size effects on the ...

Science.gov (United States)

The identification of crystallographic phases in the scanning electron microscope (SEM) has been limited by the lack of a simple way to obtain electron diffraction data of an unknown while observing the micro structure of the specimen. With the development of Charge Coupled Device (CCD) based detectors, backscattered electron Kikuchi patterns (BEKP), alternately referred to as electron backscattered diffraction patterns (EBSP), can be easily collected. Previously, BEKP has been limited to crystallographic orientation studies due to the poor pattern quality collected with video rate detector systems. With CCD detectors, a typical BEKP can now be acquired from a micron or sub-micron-sized crystal using an exposure time of 1-10 seconds with an accelerating voltage of 10-40 kV and a beam current as low as 0.1 nA. Crystallographic phase analysis using BEKP is unique in that the properly equipped SEM permits high magnification images, BEKP`s, and ...

CERN Document Server

The resolution of X-ray diffraction microscopy is limited by the maximum dose that can be delivered prior to sample damage. In the proposed Serial Crystallography method, the damage problem is addressed by distributing the total dose over many identical hydrated macromolecules running continuously in a single-file train across a continuous X-ray beam, and resolution is then limited only by the available molecular and X-ray fluxes and molecular alignment. Orientation of the diffracting molecules is achieved by laser alignment. We evaluate the incident X-ray fluence (energy/area) required to obtain a given resolution from (1) an analytical model, giving the count rate at the maximum scattering angle for a model protein, (2) explicit simulation of diffraction patterns for a GroEL-GroES protein complex, and (3) the frequency cut off of the transfer function following iterative solution of the phase problem, and reconstruction ...

International Nuclear Information System (INIS)

The analytical treatment of the nonperturbative QCD dynamics is one of the main open questions of the strong interactions. Currently, it is only possible to get some qualitative information about this regime considering other QCD-like theories, as, for example, the N=4 super Yang-Mills theory, where one can perform calculations in the nonperturbative limit of large 't Hooft coupling using the anti-de Sitter space/conformal field theory (AdS/CFT). Recently, the high energy scattering amplitude was calculated in the AdS/CFT approach, applied to deep-inelastic scattering and confronted with the F_2 HERA data. In this work we extend the nonperturbative AdS/CFT inspired model for diffractive processes and compare its predictions with a perturbative approach based on the Balitsky-Kovchegov equation. We demonstrate that the AdS/CFT inspired model is not able to describe the current F_2"D"("3") HERA data and predicts a similar behavior to that from the Balitsky-Kovchegov ...

Energy Technology Data Exchange (ETDEWEB)

The physical properties of polymer blends consisting of one or more crystallizable components are affected by the microstructure of these materials. In particular, the degree of crystallinity can be influenced by processing parameters, and the crystallinity, as well as the phase distribution, may vary as a function of depth through an injection molded part Conventional x-ray diffraction techniques can provide information regarding both phase composition and degree of crystallinity, but, because of the relative transparency of these materials to wavelengths generally available in the laboratory, these techniques provide information representative of only the bulk. By employing parallel beam optics at varying grazing incidence angles, the x-ray sampling depth can be varied without loss of resolution. This technique can be used to vary the effective analysis depth from the top several hundred angstroms for low razing incidence to centimeters for transmission ...

CERN Document Server

Up to now the long range filaments have been considered as a balance between Kerr focusing and defocusing by plasma generation in the nonlinear focus. However, it is difficult to apply the above explanation of filamentation in far-field zone. There are basically two main characteristics which remain the same at these distances - the super broad spectrum and the width of the core, while the power in a stable filament drops to the critical value for self-focusing. At such power the plasma and higher-order Kerr terms are too small to prevent self-focusing. We suggest here a new mechanism for stable soliton pulse propagation in far-away zone, where the power of the laser pulse is slightly above the critical one, and the pulse comprises super-broad spectra. For such pulses the diffraction is not paraxial and an initially symmetric Gaussian pulse takes parabolic form at several diffraction lengths . The stable soliton propagation appears as a balance ...

International Nuclear Information System (INIS)

Spin-polarized angle-resolved sulfur L_2_,_3VV Auger-electron spectra have been recorded for the c(2x2)S/Fe(001) system. The data show the modulation of the sulfur Auger spin polarization as a function of emission angle, which represents an observation of spin-polarized Auger-electron diffraction (SPAED), a potentially powerful tool for the study of local magnetic structure at surfaces, interfaces, and thin films. Theoretical modeling of the SPAED data indicates a large decrease in the magnetization of the top iron layer, suggesting a magnetic poisoning induced by the sulfur overlayer. These findings are independently supported by the observation of a large decrease of secondary electron spin polarization upon sulfur adsorption.

Energy Technology Data Exchange (ETDEWEB)

The transformation from the as-quenched amorphous to the crystalline state in Fe/sub 78/B/sub 13/Si/sub 9/ alloy has been investigated using a new-type neutron diffractometer. The time resolved diffraction patterns clearly show that this alloy crystallizes into FeSi alloy and Fe/sub 2/B in that order. The time evolution of these crystalline phases can be analyzed by the Kolmogorov-Johnson-Mehl-Avrami equation with the exponent of about 2.5 over a wide temperature range. This suggests that the crystallization occurs by the diffusion-controlled growth with a constant nucleation rate. The scaling behavior in the crystallization kinetics is also discussed.

Energy Technology Data Exchange (ETDEWEB)

As thin films become increasingly popular (for solar cells, LEDs, microelectronics, batteries), quantitative morphological information is needed to predict and optimize the film's electronic, optical and mechanical properties. This quantification can be obtained quickly and easily with X-ray diffraction using an area detector and synchrotron radiation in two simple geometries. In this paper, we describe a methodology for constructing complete pole figures for thin films with fiber texture (isotropic in-plane orientation). We demonstrate this technique on semicrystalline polymer films, self-assembled nanoparticle semiconductor films, and randomly-packed metallic nanoparticle films. This method can be immediately implemented to help understand the relationship between film processing and microstructure, enabling the development of better and less expensive electronic and optoelectronic devices.

Energy Technology Data Exchange (ETDEWEB)

We have performed polarized neutron diffraction measurements on the intermediate valence compound CePd{sub 3} using the D3 spectrometer at the ILL. The results show that at low temperatures, 1.7 K, as well as at 100 K, the field-induced magnetic amplitudes measured in a field of 4.6 T could be interpreted in terms of two contributions: a 4f-type contribution with a Ce{sup 3+} form factor, and an extra delocalized contribution (relatively narrow in q-extent). In particular, we find that the values of the 4f moment deduced from the extrapolation of the neutron data to Q=0 are systematically lower than the values deduced from bulk magnetization measurements performed on the same sample. This difference can be ascribed to a possible positive polarization of the conduction band which is similar at both temperatures.

Energy Technology Data Exchange (ETDEWEB)

The crystal structure of Ca{sub 2}RuD{sub 6} has been determined by neutron powder diffraction: space group Fm3m, K{sub 2}PtCl{sub 6} structure, as found for other hexahydride salts of group 8 metals with alkaline earth or lanthanide counter ions. No structural phase transition was observed between 340 K and 50 K. The deuterium nuclear quadrupole coupling constant, 54.7 kHz, leads to an ionic character of the Ru-D bond of 76%. The known trends in the behaviour of A{sub 2}MH{sub 6} salts are interpreted in terms of the ionization energies of the cation and the central metal atom.

International Nuclear Information System (INIS)

Magnetization, neutron diffraction and "1"6"6Er Moessbauer measurements on ErPd_2Si_2 are reported. Below 4.8 K ErPd_2Si_2 orders AF with complex modulated magnetic structures, where the Er moments are aligned along the c-axis. At 1.5 K a squared structure with #mu#_E_r #approx# 7.8(1)#mu#_B is found while a saturation Er moment of 8.2(2)#mu#_B is inferred from the hyperfine field data. The temperature dependence of the Moessbauer spectra in the paramagnetic region is explained in the framework of a relaxation model implying excited crystal field levels. Its analysis is used to estimate the B"m_n CEF parameters. (orig.).

International Nuclear Information System (INIS)

The structure of nano-porous carbon, obtained by means of chlorination of carbide compounds with various crystal structure (SiC, TiC, Mo_2C) is studied through the method of small-angle diffraction. The angular dependences of the scattering intensity obtained are interpreted as the result of scattering from the nanoparticles of different size. The functions of the scattering particles distribution by the m(R_g) inertia radii are determined. It is shown that in spite of the source carbide, the highest fraction of the volume in the porous carbon constitute the particles with R_g #approx# 5 A. The nanoparticles in the samples obtained from SiC, wherein the average value of the R_g"a"v < 6 A, are most uniform by size. The nanoparticles in the porous carbon, obtained from Mo_2C, are on the average by two times larger

Energy Technology Data Exchange (ETDEWEB)

The development of a twinned microstructure in hexagonal close-packed rolled magnesium compressed in the in-plane direction has been monitored in situ with neutron diffraction. The continuous conversion of the parent to daughter microstructure is tracked through the variation of diffraction peak intensities corresponding to each. Approximately 80% of the parent microstructure twins by 8% compression. Elastic lattice strain measurements indicate that the stress in the newly formed twins (daughters) is relaxed relative to the stress field in the surrounding matrix. However, since the daughters are in a plastically 'hard' deformation orientation, they quickly accumulate elastic strain as surrounding grains deform plastically. Polycrystal modeling of the deformation process provides insight about the crystallographic deformation mechanism involved.

Energy Technology Data Exchange (ETDEWEB)

X-ray diffraction enhanced imaging (DEI) is one of X-ray phase-contrast imaging methods, which is applied to inspect internal structures of weakly absorbing low-Z samples. The key problem of the DEI is how to extract phase information which is expressed by refraction-angle images from a series of DEI images measured in different positions of the rocking curve of the analyzer. Three effective extraction methods are presented in this paper: the statistical geometric-optics-approximation method, the maximum refraction-angle method and the Gaussian curve fitting method. They are compared with the existing methods, such as the D. Chapman's geometric optics approximation method and the multiple-images statistical method. A 2D computer simulation experiment is performed to draw comparisons of these methods. The experimental results prove that the above three methods have more precision of refraction-angle values than existing methods.

Energy Technology Data Exchange (ETDEWEB)

Wood plastic composite (WPC) of kadom, simul, mango and debdaro were prepared with two monomers methylmethacrylate (MMA) and butylmethacrylate (BMA) using high energy ionizing radiation. X-ray diffraction and scanning electron microscope (SEM) studies reveal that significant grafting occurred with wood fiber. Electric properties like resistivity and dielectric constant of both wood and WPC were measured under different moisture contents and relative humidities. The resistivities of wood decreased dramatically with increase of moisture content, but those of WPC decreased very slowly with moisture content. The dielectric constant of wood increased significantly with moisture content but no significant difference was observed in the case of WPC within the range of moisture contents studied. The dielectric constants of untreated wood also increased with their densities. (author).

CERN Document Server

A new methane cold neutron source has been tested at the IBR-2 pulsed reactor at the Frank Laboratory of Neutron Physics. In a paper the results of experiments at neutron diffractometers HRFD and DN-2 which are placed at the IBR-2 from the methane moderator side are given. A comparison with the results obtained with the conventional water comb-like moderator is performed. The perspectives of the cold source for various kinds of neutron diffraction experiments, including atomic and magnetic structural analysis and real time experiments are discussed. It is shown, that for a huge number of the experiments which are performing at both HRFD and DN-2 the methane cold neutron source provides the better conditions than water comb-like moderator.

International Nuclear Information System (INIS)

We have studied the structure of both propanol isomers in their glassy and crystalline states by neutron diffraction. The glass-transition temperatures of 1- and 2-propanol are about 98 and 115 K, respectively and, surprisingly, even larger differences are observed for the melting temperatures of the stable crystals, which are 148 and 185 K, respectively. Their supercooled liquid phases show rather different relaxation spectra, 1-propanol manifesting strong deviations from Debye behavior, whereas 2-propanol shows a far weaker effect. We discuss the spectra obtained for the static structure factor and the static pair correlation function D(r). There is a noticeable difference in the position of the first sharp diffraction peak, which clearly indicates a density change, well correlated with the period of the intermolecular oscillations shown by D(r). (orig.)

International Nuclear Information System (INIS)

Smith-Purcell (S-P) radiation is produced when electrons graze the surface of a grating. Calculations based on the theory of diffraction radiation show that, given severe restrictions on e"--beam quality, S-P radiation is highly efficient. Efficient S-P x-ray generation requires relativistic e"- beams having a transverse momentum and dimension whose product approaches the Heisenberg uncertainty limit.

International Nuclear Information System (INIS)

The n=4 Aurivillius phase, Bi5Ti3CrO15, was synthesised by solid state reaction. Rietveld analysis of high resolution neutron diffraction data demonstrated this material to adopt the polar space group A21am at room temperature, transforming to the aristotype I4/mmm structure above 650 oC. This phase transition is coincident with an anomaly in DSC signal and relative permittivity, which are characteristic of a ferroelectric-paraelectric phase transition. Bi5Ti3CrO15 exhibits paramagnetic behaviour at low temperature, with short range antiferromagnetic interactions, but no evidence for long range magnetic ordering. This is considered a consequence of significant disorder of Ti and Cr over the available octahedral sites, as demonstrated by analysis of neutron diffraction data. -- Graphical abstract: We report here the synthesis, structure and characterisation of the n=4 Aurivillius phase Bi5Ti3CrO15. Analysis of neutron powder ...

International Nuclear Information System (INIS)

We studied the strain introduced in a Si(111) substrate due to MeV ion implantation using extremely asymmetric x-ray diffraction and measured the rocking curves of asymmetrical 113 diffraction for the Si substrates implanted with a 1.5 MeV Au"2"+ ion at fluence values of 1x10"1"3, 5x10"1"3, and 1x10"1"4/cm"2. The measured curves consisted of a bulk peak and accompanying subpeak with an interference fringe. The positional relationship of the bulk peak to the subpeak and the intensity variation of those peaks with respect to the wavelengths of the x rays indicated that crystal lattices near the surface were strained; the lattice spacing of surface normal (111) planes near the surface was larger than that of the bulk. Detailed strain profiles along the depth direction were successfully estimated using a curve-fitting method based on Darwin's dynamical diffraction theory. Comparing the shapes of resultant strain profiles, we ...

Energy Technology Data Exchange (ETDEWEB)

Time resolved phase transition and strain experiments have been performed on the millisecond time scale using a Bragg-edge transmission technique that has been developed at the Los Alamos National Laboratory. The precision with which lattice parameters can be determined from edge positions is sufficient to perform high-resolution strain measurements in uniaxial stress.

Energy Technology Data Exchange (ETDEWEB)

The structural variations of amorphous metals, such as Pd/sub 80/Si/sub 20/, with irradiation of helium ion, neutron, and gamma ray have been mainly pursued by the method of X-ray diffraction and thermal analysis. It should be noticed that the amorphous metals show a radiation resistance, that is, no remarkable structural changes under helium ion, neutron, and gamma ray irradiation.

Energy Technology Data Exchange (ETDEWEB)

By means of infrared spectroscopy, x-ray diffraction, and differential thermal analysis, the authors investigate the pyrolysis of dichlorodithiourea cadmium, the vapor phase epitaxy of the cadmium sulfide film, and the composition of the solid and gaseous pyrolysis products. Those products are found to include the thiocyanates of guanidine, ammonium, and hydrogen along with cadmium oxides and sulfates and hydrochloric acid.

Energy Technology Data Exchange (ETDEWEB)

X-ray diffraction was used to monitor the {ital in} {ital situ} reaction of Pd deposited on Si(111) at room temperature. An ordered silicide forms spontaneously beneath a poorly ordered overlayer. It is commensurate and strained at low coverage, but relaxes to an unstrained state above a critical thickness of 18 A. During both phases of growth sustained intensity oscillations are seen that correspond to a layerwise consumption of the substrate at the buried interface.

Energy Technology Data Exchange (ETDEWEB)

Energy spectra of the Bragg reflection of the Moessbauer ..gamma..-radiation from the /sup 57/Fe/sub 3/BO/sub 6/ weakly ferromagnetic monocrystal are studied. A strong effect of the interference transitions in iron nuclei, being in non-equivalent positions, on the spectra form is revealed. The measurement results are compared with theoretical calculations.

Energy Technology Data Exchange (ETDEWEB)

The radial distribution function (RDF) derived from wide angle X-ray diffraction patterns gives additional information about the spatial distribution of atoms. Their radial distances and relative average coordination numbers can be calculated using appropriate mathematical procedures. 7 refs.

UK PubMed Central (United Kingdom)

α-Galactosidases from thermophilic organisms have gained interest owing to their applications in the sugar industry. The α-galactosidases AgaA, AgaB and AgaA A355E mutant from Geobacillus...Full Text Available

International Nuclear Information System (INIS)

The doping of deuterated polyparaphenylene [C_6D_4]sub(n) with AsF_5 has been investigated by real time neutron diffractometry at 100, 400 and 820 mbar AsF_5 pressure. The reaction appears to be diffusion controlled. Evidence for one doped phase with partial crystalline order was obtained. Structural considerations suggest two polymer chains plus one dopant ''string'' as the repetitive unit. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

We have studied the nucleation and growth processes in a chemical vapor deposition (CVD) diamond film using a tomographic electron backscattering diffraction method (3D EBSD). The approach is based on the combination of a focused ion beam (FIB) unit for serial sectioning in conjunction with high-resolution EBSD. Individual diamond grains were investigated in 3-dimensions particularly with regard to the role of twinning.

Energy Technology Data Exchange (ETDEWEB)

LiNiO{sub 2} is one of the most promising material for positive electrodes of lithium-ion batteries. However, its behaviour during cycling and the existence of several phase transitions induced by the lithium ions de-intercalation process has not been explained so far. A transition electron microscopy study of various Li{sub x}NiO{sub 2} (0.25

Energy Technology Data Exchange (ETDEWEB)

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutions of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controlled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle synthesis have been proposed.

Energy Technology Data Exchange (ETDEWEB)

The Synchrotron Resource of the Howard Hughes Medical Institute will be dedicated to structural analyses of biological macromolecules, primarily through crystallography. This facility is under construction at the X4 port of the National Synchrotron Light Source at Brookhaven National Laboratory, and it will comprise three beamlines. The first line to be built has been devised to apply the multiwavelength anomalous diffraction method which provides direct estimates for the phases of reflections. The second line will be devoted to rapid and essentially routine diffraction measurements, mainly through the rotation method. These two experimental stations are contained within refrigerated radiation enclosures that will maintain clean environments, narrowly defined constant temperatures, and protection against biohazard at biosafety level BL-2. At the same time as the second line will be developed, the swath center is planned to first serve as a ...

International Nuclear Information System (INIS)

Single-crystal neutron diffraction has been used to observe the interactions between deuterated ethanol (CD3CD2OH) and lysozyme in triclinic crystals of hen egg white lysozyme soaked in 25% (v/v) ethanol solutions. A total of 6047 observed reflections to a resolution of 2 A were used, and 13 possible ethanol sites were identified. The three highest occupied sites are close to locations for bromoethanol found in an earlier study by Yonath et al. [Yonath, A., Podjarny, A., Honig, B., Traub, W., Sielecki, A., Herzberg, O., and Moult, J. (1978) Biophys. Struct. Mech. 4, 27-36]. Structure refinements including a model for the flat solvent lead to a final crystallographic agreement factor of 0.097. Comparison with earlier neutron studies on triclinic lysozyme showed that neither the molecular structure nor the thermal motions were affected significantly by the ethanol. A detailed analysis of the ethanol-lysozyme contacts showed 61% of these to be with hydrophobic sites, ...

Energy Technology Data Exchange (ETDEWEB)

It has been discovered that the presence of MoO/sub 3/ lowers the ..cap alpha..-..beta.. transition in Sb/sub 2/O/sub 4/ from 935 to 850/sup 0/C with concurrent dissolution of Mo in the high-temperature (..beta..) form. The structure of Mo-doped ..beta..-Sb/sub 2/O/sub 4/ has been investigated by powder neutron diffraction, extended X-ray absorption fine structure (EXAFS) and Raman spectroscopies, and scanning-electron microscopy (SEM). Cell parameters: a = 12.0571 (12) A, b = 4.8335 (1) A, c = 5.3838 (6) A, ..beta.. = 105.579 (5)/sup 0/, monoclinic, space group C2/c, Z = 4. Combining the results of these techniques leads to the hypothesis that Mo is located interstitially within channels of electron density in the Sb/sub 2/O/sub 4/ structure with concurrent vacancy of two Sb/sup III/ atoms. There is no apparent oxygen deficiency in the resulting structure. 25 references, 6 figures, 3 tables.

International Nuclear Information System (INIS)

The amorphization of a quenched sample of the GaSb-II high-pressure phase was studied at ambient pressure by real-time neutron diffraction in the course of the sample heating from 100 K to room temperature at a rate of 0.4 K min-1. The transformation to the amorphous state begins at 140 K and is completed near room temperature. The ?-Sn type structure was shown to represent only the mean lattice of the high-pressure GaSb-II phase. The superstructure of this phase widely varied with temperature and is caused by the ordered displacement of atoms. The temperature range of the metastable crystalline phase relaxation is divided into three intervals according to the temperature dependence of the tetragonality ratio (c/a). At the boundaries of these temperature intervals, i.e. temperatures T = 170 and 230 K, two second-order phase transitions are observed. Anomalous heat and volumetric effects were observed earlier by means of calorimetry and dilatometry in the same ...

Energy Technology Data Exchange (ETDEWEB)

Nanocomposites containing polyethylene (PE) and montmorillonite clay organically modified (OMMT) with quaternary ammonium salts were obtained via direct melt intercalation. A montmorillonite sample from the Brazilian state of Paraiba was treated with four different types of quaternary ammonium salts. After the treatment, the powder was characterized by X-ray diffraction and scanning electron microscopy. The dispersion and morphologies of OMMT within PE were investigated by X-ray diffraction and transmission electron microscopy. The results revealed the formation of intercalated montmorillonite layers in the PE matrix. The thermal stability and flammability of the PE/montmorillonite clay nanocomposites were measured by thermogravimetry and horizontal burning tests for HB classification, Underwrites Laboratories (UL 94), respectively. It was shown that the samples do not degrade at the processing temperature. By adding only 3 wt.% ...

International Nuclear Information System (INIS)

In this work we report a study of the induced changes in structure and corrosion behavior of martensitic stainless steels nitrided by plasma immersion ion implantation (PI"3) at different previous heat treatments. The samples were characterized by x-ray diffraction and glancing angle x-ray diffraction, scanning electron microscopy, energy dispersive x-ray spectroscopy, and potentiodynamic measurements. Depending on the proportion of retained austenite in the unimplanted material, different phase transformations are obtained at lower and intermediate temperatures of nitrogen implantation. At higher temperatures, the great mobility of the chromium yields CrN segregations like spots in random distribution, and the #alpha#"'-martensite is degraded to#alpha#-Fe (ferrite). The nitrided layer thickness follows a fairly linear relationship with the temperature and a parabolic law with the process time. The corrosion resistance depends strongly on ...

International Nuclear Information System (INIS)

Neutron powder diffraction and magnetometric studies of the HoRh_2_-_xPd_xSi_2 series of solid solutions (x=0, 0.5, 0.75, 1.0, 1.5, 1.8) are reported. The intermetallics investigated crystallize in the body-centred-tetragonal ThCr_2Si_2-type structure (space group I4/mmm). All the samples order antiferromagnetically at low temperatures. For low values of the dilution parameter x a simple collinear antiferromagnetic structure of the AFI type is stable. Below T_N the magnetic moments are parallel to the c-axis and then, below T_t, deflect forming an angle #psi# with the c-axis. Further replacement of Rh by Pd results in the development of a sine-wave-modulated magnetic structure with one two-component propagation vector and magnetic moments in the basal plane. For x=1.8 a sine-wave-modulated structure similar to that reported for HoPd_2Si_2 (i.e. with a two-component propagation vector and magnetic moments parallel to the b-axis) was found. (author)

International Nuclear Information System (INIS)

We report the results of neutron-diffraction experiments on CeM_2Si_2 (M = Ag,Au,Pd,Rh) which were performed to explore the role of valence fluctuations and 4f hybridization in the magnetic ordering of cerium compounds. All four order antiferromagnetically, the first three exhibiting structures consisting of ferromagnetic layers with moments perpendicular to the layers, which are believed to be characteristic of 4f-4f interactions mediated through hybridization with conduction electrons. CePd_2Si_2 has an anomalously small moment (0.62#mu#/sub B/) in the ordered state. CeAg_2Si_2 exhibits an incommensurate longitudinal, static magnetization wave with moment and propagation direction along the a axis. The fourth compound, CeRh_2Si_2, has the highest known transition temperature (39 K) reported for cerium ordering; it exhibits another second-order transition at 27 K to a complex commensurate structure with modulated moments. The results are discussed in terms of the ...

CERN Document Server

This paper presents diffraction-limited 1-18 micron images of the young quadruple star system HD 98800 obtained with the W. M. Keck 10-m telescopes using speckle and adaptive optics imaging at near-IR wavelengths and direct imaging at mid-IR wavelengths. The two components of the visual binary, A and B, both themselves spectroscopic binaries, were separable at all wavelengths, allowing us to determine their stellar and circumstellar properties. Combining these observations with spectroscopic data from the literature, we derive an age of 10 Myr, masses of 0.93 and 0.64 M_sun and an inclination angle of 58 deg for the spectroscopic components of HD 98800 B, and an age of 10 Myr and a mass of 1.1 M_sun for HD 98800 Aa. Our data confirm that the large mid-IR excess is entirely associated with HD 98800 B. This excess exhibits a black body temperature of 150 K and a strong 10 micron silicate emission feature. The theoretical equilibrium radius of large, perfectly ...

Science.gov (United States)

A knowledge of surface film growth kinetics can be quite useful in the production of materials for uses ranging from protective coatings to microelectronic devices. A technique for determining the kinetics of film growth is presented which should prove to be a valuable alternative to the array of spectroscopies (AES, RBS, etc.) currently favored for these measurements. Some of the virtues of this X-ray diffraction approach are its non-destructive nature, thickness resolution better than 50 {angstrom} and conventional equipment requirements. Results obtained for the growth of Pd{sub 2}Si films during thermal annealing of Pd coatings on Si, indicate parabolic growth over a temperature range of 160-222 C. The rate constant was found to be k{prime} = 7 {times} 10{sup {minus}4} exp ({minus}1.06 eV/kT) cm{sup 2}/sec, where (film thickness){sup 2} = k{prime} x time. This activation energy is in agreement with results obtained by other techniques. A comparison of this ...

International Nuclear Information System (INIS)

Much research has been done to estimate the residual stress on a dissimilar metal weld. There are many methods to estimate the weld residual stress and FEM (Finite Element Method) is generally used due to the advantage of the parametric study. And the X-ray method and a Hole Drilling technique for an experimental method are also usually used. The aim of this paper is to develop the appropriate FEM model to estimate the residual stresses of the dissimilar overlay weld pipe. For this, firstly, the specimen of the dissimilar overlay weld pipe was manufactured. The SA 508 Gr3 nozzle, the SA 182 safe end and SA376 pipe were welded by the Alloy 182. And the overlay weld by the Alloy 52M was performed. The residual stress of this specimen was measured by using the Neutron Diffraction device in the HANARO (High-flux Advanced Neutron Application ReactOr) research reactor, KAERI (Korea Atomic Energy Research Institute). Secondly, FEM Model on the dissimilar overlay weld pipe ...

International Nuclear Information System (INIS)

X-ray magnetic diffraction (XMD) technique was applied to an orbital ordering compound of ferromagnetic YTiO_3 for the first time. The orbital-magnetic form factor #mu# _L(k) and the spin-magnetic form factor #mu# _S(k) were independently measured by utilizing the LS separation ability of the XMD. The #mu# _L(k) was measured for ten reciprocal-lattice points. No significant values of the #mu# _L(k) were observed for most of the reciprocal-lattice points within the estimated statistical errors, which suggested quenching of the orbital moment. The #mu# _S(k) was measured for 22 reciprocal-lattice points. Fourier synthesis of the #mu# _S(k) gave the spin density distribution m _S(r) in the real space. The obtained m _S(r) map shows the characteristic feature of the electron distribution of 3d electron in the t_2_g state of a Ti atom coordinated by O"2"- ions, in which the electrons are distributed away from the negative O"2"- ions. It is concluded that the electron ...

International Nuclear Information System (INIS)

Single crystals of semi-organic L-histidine hydrobromide have been grown by slow evaporation technique from a mixture of L-histidine and hydrobromic acid in aqueous solution at ambient temperature. From high-resolution X-ray diffraction analysis, the crystalline perfection of the grown crystal has been studied. Single crystal X-ray diffraction analyses, Nuclear Magnetic Resonance spectral analysis, Thermo-Gravimetry (TG), Differential Thermal Analysis (DTA) and hardness test have been employed to characterize the as-grown crystals. The UV cutoff wavelength of the grown crystal is below 300 nm and has a wide transparency window, which is suitable for second harmonic generation of laser in the blue region. Nonlinear optical characteristics have been studied using Q switched Nd:YAG laser (#lambda#=1064 nm). The second harmonic generation conversion efficiency of the grown crystals confirms their suitability for frequency conversion applications.

Energy Technology Data Exchange (ETDEWEB)

Coal demineralization mechanism and its optimum condition were studied by hydrothermal reaction between Ca(OH)2 and quartz as a coal demineralization model. In experiment, the mixture of powder quartz and Ca(OH)2 water slurry was subjected to reaction in an autoclave under spontaneous pressure at 175-340{degree}C. After dried in N2 gas atmosphere at 105{degree}C, the reaction product was analyzed by X-ray diffraction, thermo-balance and differential thermal analysis. In measurement of quartz conversion, the specimen was analyzed by X-ray diffraction after removal of bound water by heat treatment at 850{degree}C. The mixture of clean coal deashed by NaOH and a fixed amount of quartz was also used as specimen for experiment. As the experimental result, dicalcium silicate hydrate was mainly produced at 175{degree}C, and the product changed into xonotlite through tobermorite by longer treatment at higher temperature. For complete reaction of ...

Energy Technology Data Exchange (ETDEWEB)

The Heusler alloy Ni{sub 2}MnIn is a promising material as spin injector because of its predicted half-metallicity at the interface to InAs. We grow thin films of this Heusler alloy by thermal coevaporation of Nickel and the alloy MnIn. The alloy is grown on Si{sub 3}N{sub 4} membranes and amorphous carbon films for transmission-electron microscopy (TEM) as well as on Si and InAs. The degree of the transport spin polarization of the films grown on Si(100), InAs(100) and in-situ cleaved (110) surfaces of InAs is determined by point-contact Andreev reflection spectroscopy (PCAR). The almost perfect lattice match between InAs and Ni{sub 2}MnIn supports highly oriented growth, as we have proven by electron diffraction under grazing incidence. Lateral spin valves with Heusler electrodes are lithographically defined. In view of the temperature-sensitivity of the optical and electron-beam resists, the samples are grown at substrate temperatures of 50 C and annealed up to ...

Energy Technology Data Exchange (ETDEWEB)

Neutron diffraction was used to monitor elastic strains during in situ tension testing of a directionally solidified (DS) superalloy at 900 deg. C. Changes in misfit and thermal expansion coefficients of individual phases were obtained. In the {gamma} phase, it is demonstrated that elastic strains saturate at 350 MPa, which is well below the yield strength of the alloy. This is interpreted as the onset of dislocation glide through less stressed vertical channels. The critical resolved shear stress (CRSS) of {gamma} is found to be 143 {+-} 11 MPa, in agreement with a calculated CRSS that is dominated by Orowan bowing of dislocations through nanoscale-wide {gamma} channels. This provides confirmation of Orowan bowing in plasticity/creep of the {gamma} phase. Implications of CRSS and misfit in a 'threshold stress' for creep and rafting are discussed. The CRSS of {gamma}' is found to be consistent with pairwise penetration of dislocations ...

Energy Technology Data Exchange (ETDEWEB)

Discontinuously reinforced aluminium-based composites containing particulate or whisker SiC reinforcements at different volume fractions, were produced via a powder-route. Isothermal creep tests have been carried out at 270, 300 and 320 C. During these tests axial and transverse strains were monitored using a non-contacting laser scanning extensometer arrangement. At the same time neutron diffraction has been used to measure the elastic phase strain evolution with composite creep deformation. It was found that after the initial loading the phase strains remained essentially constant during primary and secondary creep. This indicates that the initial matrix/reinforcement inelastic misfits remain largely unchanged, probably due to the setting up of a dynamic equilibrium between misfit generation and stress relaxation. For each system, the neutron data has been combined with Eshelby modelling to obtain a measure of the load transfer. It was found that while the ...

Energy Technology Data Exchange (ETDEWEB)

We have described the x-ray optics and beamline performance of the ANL X6B beam line at the NSLS. Considerable flexibility has been built into the beam line to accommodate a wide range of x-ray diffraction, scattering, and spectroscopy experiments with various requirements. We presented selected examples of experimental results and showed that with the high intensity, high energy resolution, high-q resolution, and energy tunability, the X6B beam line has become a versatile facility.

Energy Technology Data Exchange (ETDEWEB)

17-4PH stainless steel was modified by direct current (DC) plasma nitriding and titanium nitride film duplex treatment in this study. The microstructure, wear resistance and corrosion resistance were characterized by X-ray diffraction (XRD), pin-on-disk tribological test and polarization experiment. The results revealed that the DC plasma nitriding pretreatment was in favor of improving properties of titanium nitride film. The corrosion resistance and wear resistance of duplex treatment specimen was more superior to that of only coated titanium nitride film.

British Library Electronic Table of Contents (United Kingdom)

Methods of X-ray diffraction and transmission electron microscopy were used to study the microstructure of dispersion-strengthened Cu-Al2O3 nanocomposites obtained by the method of simultaneous deposition of Cu and Al2O3 from the vapor phase. The effect of the size of particles of the oxide (Al2O3) and of their content on the electrical resistance of the composite has been considered. The results obtained make it possible to suppose that the main structural factor that determines the electrical resistance of the composite are nanodispersed particles of Al2O3 with a size of less than 20 nm.

British Library Electronic Table of Contents (United Kingdom)

The mechanism of abrupt increase of the giant magneto impedance (GMI) ratio in the ion irradiated Co-based amorphous ribbon has been investigated. The grazing incident X-ray diffraction and transmission electron microscope were used to characterize the samples before and after ion irradiation. The GMI-ratio considerably increased in the ion irradiated samples and the GMI response showed strong dependence on the driving frequencies. The Barkhausen noise (BN) signals are increased for the Ar ion irradiated sample with dose of 1x10^1^7 ion/cm^2. The results are interpreted in terms of GMI variation associated with domain wall dynamics.

Energy Technology Data Exchange (ETDEWEB)

Metallic multilayers offer a fantastic playground to investigate elastic stresses in films of nanometer thickness. We will present and discuss a few examples from our recent work on Au-Ni and Ag-Cu systems where we combined plate bending measurements and electron or X-ray diffraction to investigate stress buildup and interfacial mixing. Comparing these two cases we discuss the results with respect to basic parameters like the misfits in lattice parameters and in elastic moduli, the mixing enthalpies and the surface energies.

Energy Technology Data Exchange (ETDEWEB)

Depth resolved positron annihilation studies on Pd/Si thin film system have been carried out to investigate silicide phase formation and vacancy defect production induced by thermal annealing. The evolution of defect sensitive S-parameter clearly indicates the presence of divacancy defects across the interface, due to enhanced Si diffusion beyond 870 K consequent to silicide formation. Corroborative glancing incidence X-ray diffraction (GIXRD), Auger electron spectroscopy (AES) and Rutherford backscattering spectrometry (RBS) have elucidated the aspects related to silicide phase formation and Si surface segregation.

International Nuclear Information System (INIS)

The wide-angle neutron diffractometer recently installed at the HFIR has the capability of performing time-resolved or time-slicing measurements. One of the interesting problem areas the authors have explored using this time-slicing function of the diffractometer is the kinetics of structural changes occurring after a temperature jump across a value at which a first-order phase transition occurs. Two measurements of this sort have been carried out: the phase III to II transition in RbNO_3 and the transition between the alpha and beta phases in Sn.

International Nuclear Information System (INIS)

The first successful application of a new method to investigate phase transformations in real time, like the decomposition of austenite into bainite in grey iron, is described. During the ongoing transformation, transmission spectra of thermal neutrons, which contain Bragg edges corresponding to the crystal structure of the transforming phases, are recorded. By evaluating the height of these Bragg edges, which is a measure of the volume fraction of the phase, at different transformation times, the transformation can be followed in-situ in a time resolved manner. The method is compared to other previously used methods (micrographs, dilatometry, diffraction techniques); also a summary and an outlook are given. ((orig.)).

International Nuclear Information System (INIS)

The following are reported: colorimetric determination of Ti in Cr, decontamination of metals by anodic dissolution, computer code for x-ray peak identification, gel-permeation chromatography of CoRezyn 1664 polyester resin, infrared monitoring of gases and vapors, particle size analysis of dusts, nondestructive analysis of Oralloy for removable alpha contamination, dissolution (digestion) of high-fired oxides, assay of U in a Pu-U alloy, measurement of oxide thickness on Pu metal by x-ray diffraction, analysis of precipitated Pu peroxide, differentiation of Dowex SBR and 11 resins, and determination of Pu solubility in simulated lung fluid.

International Nuclear Information System (INIS)

The low alloy steels were nitrided in the plasma atmosphere generated by using hollow cathode discharge. For comparison, specimens of 40 Cr steel were in two different potential states. One kind is isolated from cathode and anode between them the discharge was created. The other kind is placed on the plate which is connected to the cathode. The nitriding was carried out at different temperatures. The surface morphology, phase of compound layers and microhardness profiles were analyzed. The optical microscopy observation and X-ray diffraction showed that the compound layers were formed in all experiments. The results of the nitriding treatment are weakly dependent on the potentials applied on the specimens.

Energy Technology Data Exchange (ETDEWEB)

Magneto-striction and magnetic form factors in 5f itinerant antiferromagnets UNiGa{sub 5} and UPtGa{sub 5} are studied by means of neutron scattering. Remarkable magneto-striction was observed around T{sub N}, indicating large spin-orbit coupling in the itinerant system. The orbital magnetic moment is found to be strongly suppressed due to the hybridization of uranium 5f with Ga-4p electron.

International Nuclear Information System (INIS)

New data about the structure of high-temperature resistant metalloceramic plasma sprayed coatings in micro and nano areas are presented. Application of the new instrumental methods: transmission electron microscopy combined with selected area electron diffraction mode is possible to obtain these data. The first layer in Ni based metallic bond coat shows nanocrystalline structure. External ceramic layer based on stabilised ZrO_2 is polycrystalline and contains both cubic and tetragonal crystalline phases. Local inhomogeneities in coatings phase composition are determined. (author)

Energy Technology Data Exchange (ETDEWEB)

This paper reports the presence of face centered cubic cobalt precipitates inside tungsten carbide in nanocomposite of WC-Co synthesized by spray conversion processing. EDS was used to identify the presence and micro-diffraction was employed to determine the nature of the precipitates. There is entrapment of cobalt in tungsten carbide during the spray conversion process used to form WC/Co powder. During consolidation, at high temperatures, the cobalt attains enough mobility to precipitate inside WC. A vanadium containing compound was seen at the interfaces in samples which incorporated VC as a grain growth inhibitor. (orig.)

International Nuclear Information System (INIS)

A basic treatment of the principle of the linac-driven free-electron laser (FEL) is given. The first part of the paper describes the FEL in low-gain approximation, and in the second part the high-gain FEL theory is given. The majority of the treatment describes FELs in one dimensional approximation, neglecting effects by diffraction of radiation and by electron beam emittance. Only in the final section a few remarks on these issues are given. The ambition of the paper is by no means any progress in FEL theory but a clear presentation of basic FEL theory concepts with explicit derivation of the formulae from first principles. (orig.)

British Library Electronic Table of Contents (United Kingdom)

Spectral and energy luminescence characteristics of R6G dye solutions in ethanol with addition of Ag nanoparticle suspensions in different aggregate states are experimentally investigated. It is demonstrated that incorporation of non-aggregated and aggregated nanoparticles causes the superluminescence thresholds in R6G solutions to decrease. It is established that the optical properties of the laser beam propagation channel are transformed when low-power (20?mW) cw laser radiation passes through the suspension of nanoparticles. This is manifested through the occurrence of a region with enhanced nanoparticle density in the laser beam center, on which diffraction of laser radiation is observed.

International Nuclear Information System (INIS)

The influence of microalloying vanadium or titanium on improving the corrosion resistance of mild steel in saturated calcium hydroxide solution was investigated. Potential-time, potentiodynamic polarization, and impedance measurement techniques were employed. The corrosion products have been examined by infrared and X-ray diffraction analysis and by scanning electron microscopy. It has been shown that the grain refining, due to microalloying, plays an important role in enhancing the corrosion resistance of steel. Scales of calcite and iron oxides on top of a protective oxide are formed on the investigated steels.

Science.gov (United States)

The crystal structure and optical reflectivity of AlP has been studied in a diamond anvil cell using energy dispersive x-ray diffraction to 43 GPa and micro-optical reflectance spectroscopy to 36 GPa. AlP undergoes a first order phase transformation from zincblende to a NiAs structure which exhibits metallic reflectivity in the near-infrared. The decrease in volume on transformation is 17%[plus minus]1%. The transformation is reversible but has large hysteresis. The equilibrium transformation pressure is 9.5[plus minus]5 GPa.

CERN Document Server

multi-parton interactions and underlying event structure, $\\gamma$-mediated processes and luminosity determination, Monte Carlo tuning and even MSSM Higgs discovery in central exclusive production. In this article, the forward detector instrumentation around the CMS interaction point is described and the prospects for diffractive and forward physics using the CMS forward detectors are summarized. In addition, first observation of forward jets as well as early measurements of the forward energy flow in the pseudorapidity range $3.15

International Nuclear Information System (INIS)

AlN nanocrystalline layers and superstructures are used in the modern optoelectronic technology as reflecting mirrors in semiconductor layers. In the present work the properties of AlN films prepared by sputtering methods from an AlN target in reactive Ar + N plasma were investigated. The characterization was performed with HRTEM, SEM, glancing angle XRD and RBS methods. The present measurements confirmed the polycrystalline structure of AlN layers and enabled the evaluation of their grain size. The roughness and thickness of the layers were additionally determined by ellipsometric and profilometric measurements. (author)

Energy Technology Data Exchange (ETDEWEB)

Crystal structure of monoclinic telluric acid ammonium phosphate (TAAP) has been studied by an X-ray diffraction method in the paraelectric phase at 333 K and in the ferroelectric phase at room temperature. It is confirmed that the space group in the paraelectric phase is P2/n. Comparison of the results between the two temperatures suggests that the plane which is made by the PO{sub 4} tetrahedron linked by hydrogen bonds has an important role for the ferroelectric phase transition. This plane is almost parallel to the direction of spontaneous polarization.

Energy Technology Data Exchange (ETDEWEB)

The study is concerned with the combined effect of high pressure and shear strain on the properties of the A-15 intermetallics Nb3Sn and Nb3Al0.75Ge0.25. The properties discussed are the superconducting transition temperature, the width and intensity of the X-ray diffraction lines, and the width and shape of the Mossbauer absorption lines. It is shown that the combined effect of high pressure and shear strain leads to an intense generation of defects in polycrystalline specimens; the size of the ordered regions does not exceed 300 A even under the least severe conditions. 5 references.

Energy Technology Data Exchange (ETDEWEB)

The crystal and molecular structures of the anti-acquired immunodeficiency syndrome agent 3'-azido-3'-deoxythymidine (AZT) have been determined by x-ray diffraction. There are two crystallographically independent AZT molecules in the crystal asymmetric unit; they have similar conformation and differ primarily in the glycosyl torsion angle. Comparisons with a hydrated thymidylate structure indicate that the azido group does not significantly affect the gross conformational preference of the molecule. The comparisons also suggest possible functional roles for the azido group in enzyme binding.

British Library Electronic Table of Contents (United Kingdom)

In this paper we describe a Ni-Sn intermetallic material obtained via template electroplating synthesis. The structure and the morphology of this material are investigated by X ray diffraction (XRD) and Scanning Electron Microscopy (SEM) analyses. We demonstrate that Ni-Sn behaves as a sub-micrometric electrode showing a favourable response when cycled in a lithium cell. The results here reported suggest that the template electroplating is a promising synthetic approach that can lead to an optimized structure and morphology of the Ni-Sn electrode, such as to confer it a role of a high capacity anode in advanced lithium ion batteries.

Energy Technology Data Exchange (ETDEWEB)

The present paper is a comparative study of the cerium-containing nickel catalysts supported on x- and y-zeolites. In general, the addition of cerium ions caused an increase in the catalytic activity for CO hydrogenation and shifted the product selectivity to high molecular weight hydrocarbons. The degree of the effect of cerium additive depends on the ratio of cerium to nickel contents, the reduction temperature, and the nature of the supporting materials. Catalyst characterization, including volumetric hydrogen chemisorption, temperature programmed reduction/desorption, x-ray diffraction, surface area measurements, in-situ infrared spectroscopy and x-ray photoelectron spectroscopy, was performed in order to interpret the phenomena due to the effects of cerium additives and the support effect on Ni/zeolite catalysts.

Science.gov (United States)

Self-amplifying spontaneous radiation free-electron lasers, such as the LCLS or the European X-FEL, rely on the incoherent, spontaneous radiation as the seed for the amplifying process. Though this method overcomes the need for an external seed source one drawback is the incoherence of the effective seed signal. The FEL process allows for a natural growth of the coherence because the radiation phase information is spread out within the bunch due to slippage and diffraction of the radiation field. However, at short wavelengths this spreading is not sufficient to achieve complete coherence. In this presentation we report on the results of numerical simulations of the LCLS X-ray FEL. From the obtained radiation field distribution the coherence properties are extracted to help to characterize the FEL as a light source.

International Nuclear Information System (INIS)

In this paper, the influence of plasma nitriding at temperature 720 deg. C for 20 h on the surface microstructure and interface microstructure of electroplated chromium coating was investigated. In these conditions, interdiffusion, mixing and reaction phenomena of elements originating from the substrate and coating material are more likely to occur, thus increasing the bonding strength between the coating and carbon steel substrate. The change of the structures from the substrate side to the coating surface, and the effect of the substrate steel on the interface structure were studied by cross-sectional transmission electron microscope observation (XTEM). The nitride layer formed on the surface was analyzed by X-ray diffraction method (XRD). After treatment at above conditions a 6-7 #mu#m thick nitride compound layer was formed in surface region and the same thick carbide compound layer was also formed in the interface region between electroplated chromium coating ...

International Nuclear Information System (INIS)

We have investigated the microstructure evolutions in the Ti17 near #beta# titanium alloy during heat treatments. The phase transformation has first been studied experimentally by combining X-ray diffraction analysis, electrical resistivity and microscopy observations. From a series of isothermal treatments, a IT diagram has been determined, which takes into account the different morphologies. Then, a Johnson-Mehl-Avrami-Kolmogorov (JMAK) model has been successfully used to describe the phase transformation kinetics during either isothermal or cooling treatments. Finally, the coupling of the JMAK model to the finite element software ZeBuLoN allowed us to investigate the evolution of the spatial distribution of the different morphologies during the cooling of an aircraft engine shaft disk after forging.

British Library Electronic Table of Contents (United Kingdom)

The thermal stability of nanoscale grains in cryomilled aluminum powders containing 1% diamantane was investigated. Diamantane is a diamondoid molecule consisting of 14 carbon atoms in a diamond cubic structure that is terminated by hydrogen atoms. The nanostructures of the resulting cryomilled powders were characterized using both transmission electron microscopy (TEM) and X-ray diffraction (XRD) techniques. The average grain size was found to be on the order of 22?nm, a value similar to that obtained for cryomilled Al without diamantane. To determine thermal stability, the powders were heated in an inert gas atmosphere at constant temperatures between 423 and 773?K (0.51T m to 0.83T m) for exposure times of up to 10?h. The average grain size for all powders containing diamantane was obse...

Energy Technology Data Exchange (ETDEWEB)

By means of neutron diffraction, using the standard polycrystalline sample of Al{sub 2}O{sub 3}, measurements on three (of four spectrometers) already installed in the front of horizontal channels of MARIA reactor have been performed. Basing on these experiments as well as on activation measurements carried out earlier, the fluxes of monoenergetic neutrons have been estimated. These experiments allowed to determine (for a given geometry and kind of monochromators chosen) the resolution efficiency of instruments and high order contamination in the reflected beam. With the help of polycrystalline vanadium and TbBr{sub 3} sample, the possibility of studies using the inelastic scattering process have been tested. (author) 7 refs, 15 figs, 7 tabs

British Library Electronic Table of Contents (United Kingdom)

Antibacterial activity of Transition metals (Mn, Co) doped ZnO nanopowders prepared by a DC thermal plasma method against Escherichia coli and Staphylococcus aureus are investigated. The phase and morphology studies have been carried out by X-ray diffraction, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) respectively. All the samples of the present investigation are found to have hexagonal wurtzite structure and crystallite sizes are found to vary from 25nm to 30nm. Our bacteriological study showed the enhanced antibacterial activity of transition metals doped ZnO nanoparticles than undoped ZnO indicating the great potential of ZnO nanoparticles in relevant clinical and biomedical applications.

British Library Electronic Table of Contents (United Kingdom)

In this article, we describe a method used to prepare an in situ sodium-activated, organomodified bentonite clay/styrene-butadiene rubber nanocomposite master batch via a latex blending technique. The clay master batch was used for compound formulation. Octadecyl amine was used as an organic intercalate. The clay was purchased from local suppliers and was very cheap. Sodium chloride was used for in situ activation of the clay. The wide-angle X-ray diffraction data indicated that the in situ sodium activation helped to increase the intergallery distance from 1.28 to 1.88 nm. A transmission electron micrograph indicated intercalation and partial exfoliation. The thermal properties were relatively better in the case of the sodium-activated, organomodified bentonite-clay-containing compound. A...

Energy Technology Data Exchange (ETDEWEB)

A micellar method has been used to prepare silver-coated cobalt (Co-Ag) nanoparticles. The synthesized particles have been deeply characterized by several methods, i.e., XRD, UV-Vis, TEM, XPS, and electrochemical techniques. There is every indication that the obtained particles show a truly core-shell structure. All the nanoparticles obtained under different conditions are in the size range 3-5 nm. High-resolution TEM (HRTEM), Fast Fourier Transformation (FFT), and Selected Area Electron Diffraction (SAED) indicated that the presence of hcp-Co and fcc-Ag, in which cobalt is located in the central area; meanwhile silver is at the edges of the nanoparticle. The absorption band of the Co-Ag colloid shifts to a longer wavelength and broadens relative to that of pure silver colloid. Voltammetric characterization allowed to determine the coverage of the cobalt core.

British Library Electronic Table of Contents (United Kingdom)

Bilayers of pure palladium and gold films were evaporated alternatively on (100) and (111) monocrystalline silicon substrates. After annealing, in a vacuum furnace from 100 to 650degreeC during 30min, the growth sequence of the Pd2Si and PdSi phases that evolved as the result of the diffusion reaction was examined by means of Rutherford backscattering spectrometry (RBS), X-ray diffraction (XRD), whereas the surface morphology was investigated by scanning electron microscopy (SEM) technique. The effect of the intermediate gold layer is investigated in order to test its effectiveness as barrier for Cu and Si atoms interdiffusion and its influence on the morphology of the formed palladium silicides. The effect of substrate orientation on the palladium silicides growth and formation was also e...

International Nuclear Information System (INIS)

Nuclear forensic activities, such as in illicit trafficking, can solve a problem who did it and can gain the basis for a response. Other than that, the forensics can be also applied to solve on what are materials, who is responsible, is there more, where was material diverted and what route did the material taken. BATAN, in fact , owns a lot of equipment which can be supported for nuclear forensics activities, such as, Transmission Electron Microscope (TEM), Scanning Electron Microscope (SEM) as well as X-Ray Diffraction (XRD). For the first step, BATAN has to be an active, participate member of The International Technical Working Group on Nuclear Smuggling (ITWG). BATAN can then collaborate not only with Indonesia Arm Forces and Police, but also with other foreign institutions to develop this activity with mutual advantages agreement.

British Library Electronic Table of Contents (United Kingdom)

The influence of selenium dioxide (SeO2) on the microstructure and electrodeposition of manganese coatings obtained from a sulfate based neutral solution was investigated by material characterization methods and electrochemical techniques. The crystal structure and surface morphology of these coatings were studied by scanning electron microscopy (SEM) and powder X-ray diffraction spectroscopy (XRD), respectively. The SEM and XRD data showed that SeO2 could effectively accelerate phase transformation, and facilitate leveled and fine grain growth. The electrochemical results indicated that SeO2 could inhibit hydrogen evolution reaction and promote manganese deposition. The action of selenium dioxide in manganese deposition was found to be a reduction and adsorption mechanism. The process cou...

International Nuclear Information System (INIS)

Phase and structural transformations in a multicomponent (5.05 mas.% Mo-4.95V-3.00Cr-3.05Al) metastable #beta#-titanium alloy on aging after plastic deformation are studied using methods of electron microscopy and X-ray diffraction analysis. The alloy is deformed by twinning in a #left brace#332#right brace# system, and even at initial stages the formation of a twin skeleton takes place in the structure, on further loading the deformation of the skeleton is by secondary twinning resulting in a high plasticity of the alloy. On annealing mechanical twins transform into #alpha#-phase - a ductile twin skeleton is replaced by a rigid skeleton of #alpha#-phase plates. The aging enhances the yield strength of the alloy but decreases sharply its plasticity

International Nuclear Information System (INIS)

We have studied the ion-beam synthesis of GaSb nanocrystals in Si by high-fluence '' hot '' implantation of Sb and Ga ions followed by thermal annealing. The Rutherford backscattering, transmission electron microscopy/transmission electron diffraction, Raman spectroscopy and photoluminescence were used to characterize the implanted layers. It was found that the nanocrystal size increases from 5 to 60 nm in the samples annealed at 900"oC up to 20-90 nm in those annealed at 1100"oC. For the samples annealed at 900"oC a broad band in the region of 0.75-1.05 eV is registered in the photoluminescence spectra. The nature of this photoluminescence band is discussed. (author)

International Nuclear Information System (INIS)

The constituent phases and associated deformed microstructure of the quenched Ti-xNb-(0.5-1.5) at.% Si alloy consisting of non-cytotoxicity elements, where x = 24-30 at.%, were investigated to provide pseudoelasticity for biomedical and sensor applications. Optical microscopy revealed that stress-induced martensitic transformation takes place during the deformation in the present alloys. It is confirmed from the X-ray diffraction results of the deformed specimens that the crystal structure of the stress-induced martensite phase is the orthorhombic so-called #alpha#'' structure. Within the alloys having #beta#(bcc) phase studied Nb-poor region appeared to exhibit a dominant behavior for stress-induced martensitic transformation than Nb-rich region. This result suggests that metastable #beta# phase is superior to stable #beta# phase for the occurrence of stress-induced martensitic transformation in the present alloy system.

British Library Electronic Table of Contents (United Kingdom)

Soluble starch?based biodegradable and microporous microspheres (SDM-Ms) were prepared by emulsion chemical cross-linking technique using trisodium trimetaphosphate (TSTP) as the cross-linker. The resultant amorphous SDM-Ms were excellently identified by scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR). The internal rupture and surface-controlled erosion were the predominant degradation mechanisms for SDM-Ms. The obtained SDM-Ms were applied to adsorb coix seed oil (CSO) by immersing method. The adsorption capacity of CSO within SDM-Ms was determined, namely 0.5238?g/g, and the thermal stability was shown higher than that of the free CSO. A burst release appeared in the second hour, followed by controlled release. Diffusion, d...

International Nuclear Information System (INIS)

The purpose of this experimental study is to investigate the micromechanical fatigue behavior, in terms of slip nature and preferential cracking sites, of a commercial #alpha#/#beta#-forged Ti-6Al-4V alloy. Electron backscattering diffraction is extensively used to identify the deformation (prismatic, basal, pyramidal slip) and crack formation modes activated by fatigue at the surface of several hundred primary #alpha# nodules. Some fatal crack formation sites are also characterized. Cracking in basal planes is identified as the most critical damage mode leading to fracture. An explanation is proposed which involves the resolved shear stress, taking into account the Schmid factor and the normal stress in relation to the elastic anisotropy of the #alpha#-phase. Finally, the spatial distribution of the secondary cracks is analyzed according to the crystallographic textures (macrozones) present on a mesoscopic scale in the Ti-6Al-4V alloy.

Energy Technology Data Exchange (ETDEWEB)

Ag nanoparticles were prepared in a water-phase system with a mixture of silver-ammonia complex, sodium borohydride, and lauric acid according to molar feed ratio of approximately 6:3:1. The mechanism of preparation and separation by chemical reduction-protection method was explored. The as-synthesized Ag nanoparticles were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD) and UV-vis spectroscopy, respectively. It was found that the size of high purity Ag particles was ranging from 30 to 50 nm with slight agglomeration. In addition, the as-synthesized wet Ag nanoparticles were dispersed stably in organic vehicle to formulate electrically conductive nanopaste. Upon direct-written and sintered, the array pattern of the nanopaste with the resolution of about 30 {mu}m was achieved with the electrical resistivity in the order of magnitude of 10{sup -5} {Omega} cm.

Energy Technology Data Exchange (ETDEWEB)

Membranes in Palladium and its alloys, in particular Pd/Ag alloys, are selectively permeable to hydrogen and can therefore be used to purify hydrogen. It is intended to use them as material for electrodes in fuel cells. As the manufacturing process of a substrate Pd/Ag-layer consists of several stages and is still not completely understood, it would be advantageous to be able to characterise separately the layers of noble metals obtained by electro-plating . Attempts are being made in this work to vary the cristallographical structure of the deposited alloy by the choice of test parameters and by sintering when depositing the Pd/Ag. The layers produced are to be examined using an interference microscope and X-ray diffraction. Moreover, the diffusion behaviour of the hydrogen is to be examined with an electro-chemical pulse method specifically developed for this purpose. figs., tabs., 27 refs.

British Library Electronic Table of Contents (United Kingdom)

The growth of silver chloride nanoparticles on ancient textile was achieved by sequential dipping steps in alternating bath of potassium chloride and silver nitrate under ultrasound irradiation. The effect of ultrasound irradiation and sequential dipping steps in growth of the AgCl nanoparticles has been studied. These systems depicted a decrease in the particles size accompanying a decrease in the sequential dipping steps. The samples were characterized with powder X-ray diffraction (XRD) and scanning electron microscopy. XRD analyses indicated that the prepared AgCl nanoparticles on fiber were crystalline. The textile samples containing AgCl nanoparticles were tested for their antibacterial efficacy against Escherichia coli and were found to possess significant antibacterial activity.

International Nuclear Information System (INIS)

The phase composition and microstructure of O'-sialon prepared from Chinese coal gangue have been studied. The use of Si powder is more effective than that of activated carbon or mainly carbon with a little silicon for reduction-nitridation. For specimens with 40% Si addition, more than 80% of O'-sialon may be obtained when nitrided at 1500 degree sign C. The formed O'-sialon was characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The parameters for O'-Sialon preparation are optimized by computer pattern recognition program based on principal component analysis, the target parameter optimum regions with higher relative content of O'-Sialon was indicated by this way.

International Nuclear Information System (INIS)

An imaging position sensitive detector for charged particles, neutrons, X-and gamma rays has been developed. The novel feature of this scintillation imaging radiation detector is its ability to detect individual nuclear particle scintillations with a h igh degree of spatial resolution. The key elements of this detector system are a high gain, low noise image intensifier tube, a CCD camera and commercially available image processing hardware and software. This detector system is highly effective for applications such as low fluence and real time neutron radiography, mapping of radioactive contamination in nuclear reactor fuel rods, X-ray diffraction imaging, high speed autoradiography and in general position sensitive detection of nuclear radiation. Results of some of the exploratory experiments carried out using this detector system are presented in this paper. (orig.).

International Nuclear Information System (INIS)

In connection with the different cyclical strengths of the two-phase (#alpha# + #beta#) titanium alloy in the case of the acicular and rounded formations of the #alpha#-phase, we have studied, employing the X-ray diffraction method, the phase composition of the alloy and the influence of heat treatment upon it. Using the method of electronic fractography, we examined the fractures in samples destroyed by the asymmetric twisting, in order to find out why the durability of the alloy is dependent upon the #alpha# - phase structure. It has been found that in the BT22 alloy, the decay the #beta#-phase may proceed in two ways; either with the formation of the martensite #alpha#'-phase of the acicular shape or with the separation of the non-martensite round-shaped #alpha#-phase. The character of the phase transformations #beta# - #alpha# or #beta#-#alpha#' is, to a considerable extent, the conseguence of the prehystory of the alloy and is dependent but weakly on the ...

Energy Technology Data Exchange (ETDEWEB)

Thin passive layers of uranium nitride were formed by nitriding pure metallic uranium in non-equilibrium, low pressure radio-frequency plasma of nitrogen. Plasma nitriding at low substrate temperature of 230 C-250 C was found to cause the formation of adherent layers of uranium sesquinitride ({alpha}-U{sub 2}N{sub 3}) which provide a considerable protection against hydrogen attack. The characteristics of these passivation layers were determined by X-ray diffraction and Auger electron spectroscopy. The incipient hydriding kinetics of the plasma-treated samples were compared with those of untreated and nitrogen-ion implantation ones, utilizing a hot-stage microscope that was monitored continuously with a TV camera and videotape. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Copper complexes of the amino acids histidine, arginine and lysine have been introduced into the supercages of zeolite Y and, for the first time, into the large intracrystalline cavities of zeolites EMT and MCM-22. The resulting host/guest compounds are characterized by X-ray powder diffraction, UV/VIS-spectroscopy in the diffuse reflectance mode and by catalytic tests in the liquid-phase oxidation of aromatic alcohols (viz. benzyl alcohol, 2- and 3-methylbenzyl alcohol and 2,5-dimethylbenzyl alcohol) with tertiary-butylhydroperoxide as oxidant. It was observed that intracrystalline copper-amino acid complexes possess remarkable catalytic activity, yielding the corresponding aromatic aldehydes and acids. (orig.)

International Nuclear Information System (INIS)

Beta-SiAlON powders have been synthesized using natural clay containing kaolin and quartz by carbothermal reduction and nitridation (CRN), then beta-SiAlON bonded corundum multiphase materials have been sintered using the as prepared powders. The results indicated that both the holding time and sintering temperature are relatively significant in accordance with optimal analysis by orthogonal method. Reaction process can be briefly interpreted by means of X-ray Diffraction and Difference Temperature Analysis as well as phase diagram principle. Bending strength and bulk density were measured in SiAlON in situ bonded corundum materials with doped various sintering agents. Furthermore, the relevant mechanical properties and microstructure were discussed in detail.

Energy Technology Data Exchange (ETDEWEB)

With the aim of optimizing the nitriding process, experimental studies of the plasma nitriding of four selected steels were carried out, using a d.c. glow discharge. The process parameters were varied systematically. By means of transmission and scanning electron microscopy and X-ray diffraction, the microstructures, including the thicknesses of the compound zones and the diffusion zones of the nitrided steels, were obtained. Using cross-sectional samples and a micro-Vickers indenter, hardness depth profiles were also obtained. From the time and temperature dependences of the hardness profiles, effective diffusion constants and corresponding activation enthalpies were obtained. Furthermore, in an attempt to shed some light on the atomistic nitriding mechanisms, the glow discharges were studied by measuring energy spectra of the energetic ions hitting the cathode (the steel test specimens). It was shown that an increase of the mean energy of the ions bombarding the ...

Energy Technology Data Exchange (ETDEWEB)

Potassium clusters arrayed in zeolite A are known to show ferromagnetic properties at low temperature. The origin of the spontaneous magnetization has been explained by a model of spin-canting in an antiferromagnetically ordered state. The direct information for the magnetic structure, however, has not been obtained so far. In the present work, we measure the neutron powder diffraction by using pulsed neutron source at KEK-KENS below and above the Curie temperature. No significant temperature-dependence was, however, obtained within the statistical errors, namely, magnetic scattering could not be detected separately. We also estimate the intensity of magnetic scattering by assuming some possible magnetic structures with considering the magnetic form factor of the cluster wave function. The intensity of magnetic scattering is estimated to be extremely weak and higher S/N of {approx}10{sup 4} or more is required to detect the magnetic scattering of this material.

British Library Electronic Table of Contents (United Kingdom)

The present investigation deals with the synthesis of nanostructured nickel ferrite (NiFe2O4) and their liquid petroleum gas-sensing characteristics. The 15-20nm size nickel ferrite has been synthesized at 700degreeC by a simple molten-salt route using sodium chloride as grain growth inhibitor. These nanoparticles exhibit significantly high response towards liquid petroleum gas (LPG) in comparison with ethanol vapor, hydrogen sulfide, ammonia and hydrogen. The gas response towards various gases at their 200ppm concentrations is investigated at 200-450degreeC. Different characterization techniques have been employed, such as differential thermal analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high resolution transmission elec...

British Library Electronic Table of Contents (United Kingdom)

Commercially available organoclay (Closite 30B) was modified by using 3-aminopropyltriethoxysilane (APS) via a silylation reaction. Sodium clay (Closite Na) was treated by APS directly as a control. Such modified clays were further melt-compounded with polybutylene terephthalate (PBT). The morphology and properties of the modified organoclays were characterized with X-ray diffraction (XRD), transmission electrical microscopy (TEM), Infra-red spectroscopy, contact angle measurement, and thermogravimetric analysis (TGA). The effects of modified clays on the crystallization behavior of PBT were characterized by differential scanning calorimetry. The basal spacing of Closite Na was enlarged from 1.01 to 1.41 nm after APS treatment, indicating that the APS was intercalated into the clay interga...

International Nuclear Information System (INIS)

Transmission electron microscopy and x-ray diffraction data show that rapid thermal anneals of SrS:Ce thin films enhance grain size and reduce crystalline defects. Electron paramagnetic resonance results suggest that these anneals lead to less variance in the crystal field environments at the nearly cubic Ce"3"+ sites along with the formation of another type of Ce"3"+ site believed to involve a nearby Sr vacancy. We suggest that the association of Ce"3"+ sites with V_S_r shifts the electroluminescence towards larger wavelengths as the symmetry of the activator site is lowered. copyright 1997 American Institute of Physics.

Energy Technology Data Exchange (ETDEWEB)

X-Ray reflectivity has been used to investigate the microstructural changes of solution-cast stearic acid films before and after immersion in CoCl{sub 2} solutions. Before immersion, the films possess a well-defined layered structure with an interlayer spacing of 4.01{+-}0.05 nm. After the films were immersed in the CoCl{sub 2} solutions, a new set of equidistant diffraction peaks emerge, the corresponding interlayer spacing of which is 5.13{+-}0.05 nm. The X-ray photoelectron spectra of the films indicate the existence of cobalt ions inside the films after immersion. It is concluded that the permeation of the cobalt ions into the hydrophilic interlayer causes the stearic acid molecules to reorient perpendicular to the films, resulting in the increase of interlayer spacing and the roughening of the interfaces.

British Library Electronic Table of Contents (United Kingdom)

Laser welding of AISI 904 L super austenitic stainless steel using a diffusion cooled slab 3.5kW CO2 laser and employing two different shielding gases, namely argon and helium, was carried out. The laser weld bead profile depends on various parameters such as beam power (BP), travel speed (TS) and focal position (FP) of the laser spot. These parameters have to be selected suitably to obtain the desirable output. The cross sectioned area of the bead profiles measured using an optical microscope to determine the bead width and depth of penetration. X-ray diffraction used for phase identification confirmed that the weld structure was fully austenitic and dendritic. Hardness was observed to increase in the weld bead with respect to the parent metal and it was related to the microstructural ref...

International Nuclear Information System (INIS)

Neutron diffraction and magnetometric measurements on polycrystalline samples of DyPd_2Si_2 and ErPd_2Si_2 were carried out in the temperature range from 2 to 293 K. Both compounds show tetragonal ThCr_2Si_2 type crystal structure and order at 12 K in a sine modulated magnetic structure with propagation vectors k=[0.609,0,0.155] and [0.575, 0, 0.083] respectively. The oscillatory character of magnetic order found in RPd_2Si_2 (R=Tb-Er) compounds suggests exchange interaction described by the RKKY model to be dominant, but the non-monotonic dependence of respective Neel temperatures on the number of f-electrons indicates the influence of a crystalline electric field (CEF) on the magnetic behaviour in this series. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Cold spray was employed as a novel low temperature approach to deposit titanium dioxide (TiO{sub 2}) photocatalytic film. The film microstructure was characterized using X-ray diffraction and scanning electron microscopy. The photocatalytic performance was examined through acetaldehyde degradation under ultraviolet illumination. Results showed that TiO{sub 2} film was successfully deposited on substrate surface through cold spray. The film thickness reached up to 15 {mu}m. The film presented a rough surface and porous structure. Owing to the low temperature of spray powder, no phase and particle size changes occurred to TiO{sub 2} during deposition. It was found that the cold-sprayed TiO{sub 2} film was active for photodegradation of acetaldehyde.

British Library Electronic Table of Contents (United Kingdom)

The cephalosporin class antibacterial agent, cefazolin, was intercalated into layered double hydroxides (LDHs) in order to improve the drug efficiency as well as to achieve the controlled release property. Cefazolin molecules were incorporated into LDH through conventional ion exchange reaction. X-ray diffraction pattern analyses confirmed that cefazolin molecules were intercalated between the interlayer spaces of LDH. Fourier-transform infrared spectra and high performance liquid chromatographs clearly showed that the drug molecules were stabilized in LDH lattice through electrostatic interaction and released without any changes in their chemical integrity. Antibacterial activity of the cefazolin-LDH nanohybrid was also examined by an in vitro test, such as the minimal inhibitory concentr...

International Nuclear Information System (INIS)

High-resolution electron microscope observations confirm the presence of small crystallites in thin TbFeCo films protected by Si_3N_4 overcoats. Selected area electron diffraction patterns in top-view projection indicate that the crystals have a face-centered-cubic structure. Microscope analysis reveals grain growth following annealing of these protected thin films at 200 degree C in vacuum, and Kerr measurements yield large reductions in coercivity relative to the room-temperature value. The typical grain size visible in top-view observations increases from about 3 nm in the as-deposited samples to about 30 nm after annealing at 200 degree C for 36 h while the static coercivity, H_c, drops by about 40%. The fcc structure of the crystals is retained after annealing.

Energy Technology Data Exchange (ETDEWEB)

Interest in the tribological properties of plasma nitriding has increased substantially over the past years because plasma nitriding provides a high nitride depth and improved hard facing. The present study examines the tribological properties of AISI H11 plasma nitrided, hot-worked steel. Different nitriding temperatures and durations were considered. Characterization of the composite structures was investigated with wear tests, x-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), and microhardness tests. The depth profile of the nitrided zone was measured using the nuclear reaction analysis (NRA) technique. Plasma nitriding affected the microhardness, wear properties, and morphology considerably. Increase in process temperature increased the nitride zone depth.

International Nuclear Information System (INIS)

Intergranular corrosion (IGC) resistance of types 304LN and 316LN stainless steels (SS) thermally aged at 823, 873, and 923 K for various durations was assessed by ASTM A262 practice A test (electrolytic etch test) and electrochemical potentiodynamic reactivation (EPR) test. The results indicated that the type 316LN SS has significantly improved IGC resistance compared to 304LN SS. Based on the results of these tests, time-temperature-sensitization (TTS) diagrams were developed for both alloys. The secondary precipitates formed during thermal aging treatments were electrochemically extracted and analyzed by X-ray diffraction (XRD) to determine the types of precipitates formed during the aging treatments. The results indicated that the precipitates were mostly of M_2_3C_6 carbides.

International Nuclear Information System (INIS)

The penumbra of the profile function describing the nuclear collisions of relativistic heavy ions is related to the cross section for their producing a specific target-nucleus #gamma#-ray, sigmasub(#gamma#). The analysis assumes that the diffuse-edge diffraction model suffices to calculate the inelastic cross sections to the particle-stable states of the target nucleus. When the deformation lengths, deltasub(L) = #beta#sub(L)R, characterizing all important excitations are available from other experiments and the #gamma#-branching of these states is also known, the only unknown quantity determining sigmasub(#gamma#) is found to be the ratio of the diffuseness parameter of the profile function, d, to its radius, R. The most reliably determined values of d/R, for the target "4"0Ca, imply a rather wide penumbra, consistent with microscopic calculations. (orig.).

British Library Electronic Table of Contents (United Kingdom)

In situ synthesis of silver chloride (AgCl) nanoparticles was carried out under ambient conditions in nanoporous bacterial cellulose (BC) membranes as nanoreactors. The growth of the nanoparticles was readily obtained by alternating dipping of BC membranes in the solution of silver nitrate or sodium chloride followed by a rinse step. X-ray diffraction (XRD) patterns indicated the existence of AgCl nanoparticles in the BC and scanning electron microscopy (SEM) images showed that the AgCl nanoparticles well dispersed on the surface of BC and penetrated into the BC network. The AgCl nanoparticle-impregnated BC membranes exhibited high hydrophilic ability and strong antimicrobial activity against Escherichia coli (Gram-negative) and Staphylococcus aureus (Gram-positive). The preparative proced...

Science.gov (United States)

Photoacoustic microscopy (PAM) offers label-free, optical absorption contrast. A high-speed, high-resolution PAM system in an inverted microscope configuration with a laser pulse repetition rate of 100,000 Hz and a stationary ultrasonic transducer was built. Four-dimensional in vivo imaging of microcirculation in mouse skin was achieved at 18 three-dimensional volumes per second with repeated two-dimensional raster scans of 100 by 50 points. The corresponding twodimensional B-scan (50 A-lines) frame rate was 1800 Hz, and the one-dimensional A-scan rate was 90,000 Hz. The lateral resolution is 0.23+/-0.03 ?m for Au nano-wire imaging, which is 2.0 times below the diffraction limit.

British Library Electronic Table of Contents (United Kingdom)

''Hybrid'' hydrogen storage, where hydrogen is stored in both the solid material and as a high pressure gas in the void volume of the tank can improve overall system efficiency by up to 50% compared to either compressed hydrogen or solid materials alone. Thermodynamically, high equilibrium hydrogen pressures in metal-hydrogen systems correspond to low enthalpies of hydrogen absorption-desorption. This decreases the calorimetric effects of the hydride formation-decomposition processes which can assist in achieving high rates of heat exchange during hydrogen loading-removing the bottleneck in achieving low charging times and improving overall hydrogen storage efficiency of large hydrogen stores. Two systems with hydrogenation enthalpies close to -20kJ/mol H2 were studied to investigate the h...

Energy Technology Data Exchange (ETDEWEB)

Nd{sub 40}Fe{sub 30}Al{sub 10}Co{sub 15}B{sub 5} alloys were fabricated by high energy ball milling method under various conditions. Microstructure of the alloys was investigated by X-ray diffraction and electron microscopy techniques. Magnetic properties were characterized by hysteresis and thermomagnetic measurements. The high coercive fields up to 2.36 T have been observed on the samples consisting of Nd{sub 2}(Fe,Co,Al){sub 14}B, Nd{sub 6}(Fe,Co,Al){sub 14} and Nd crystallites imbedded in a residual amorphous matrix.

International Nuclear Information System (INIS)

The thermodynamic aspects of indium-face InN growth by radio frequency plasma-assisted molecular-beam epitaxy (rf-MBE) and the nucleation of InN on gallium-face GaN (0001) surface were investigated. The rates of InN decomposition and indium desorption from the surface were measured in situ using reflected high-energy electron diffraction and the rf-MBE 'growth window' of In-face InN (0001) was identified. It is shown that sustainable growth can be achieved only when the arrival rate of active nitrogen species on the surface is higher than the arrival rate of indium atoms. The maximum substrate temperature permitting InN growth as a function of the active nitrogen flux was determined. The growth mode of InN on Ga-face GaN (0001) surface was investigated by reflected high-energy electron diffraction and atomic force microscopy. It was found to be of the Volmer-Weber-type for substrate temperatures less than 350 deg. C and of the ...

International Nuclear Information System (INIS)

Nanocrystalline powders of GaN with grain sizes ranging from 2 to 30 nm were examined under high external pressures by in situ diffraction techniques in a diamond anvil cell at DESY (HASYLAB, Station F3). The experiments on densification of pure powders under high pressure were performed without a pressure medium. The mechanism of generation and relaxation of internal strains and their distribution in nanoparticles was deduced from Bragg reflections recorded in situ under high pressures at room temperature. The microstrain was calculated from the full-width at half-maximum (FWHM) values of the Bragg lines. It was found that microstrains in GaN crystallites are generated and subsequently relaxed by two mechanisms: generation of stacking faults and change of the size and shape of the grains occurring under external stress. (author)

British Library Electronic Table of Contents (United Kingdom)

Yb3+?Tm3+ codoped tellurite glasses containing silver nanoparticles (NPs) were synthesized and characterized using transmission electron microscopy and optical techniques. The samples? composition and the nucleation of NPs were investigated using electron diffraction and energy dispersive spectroscopy. For the optical experiments, the samples were excited using a diode laser operating at 980?nm, in resonance with the Yb3+ transition 2F7/2?2F5/2. Photoluminescence (PL) bands corresponding to Tm3+ transitions were observed at 480, 650, and 800?nm due to the Yb3+? Tm3+ energy transfer. PL enhancement was achieved by heat-treatment of the samples at 325?C during different time intervals. The growth of the PL bands correlates with the increase of the silver NPs concentration. The relevant mecha...

British Library Electronic Table of Contents (United Kingdom)

The transformation of ferrihydrite to siderite (FeCO3) in the presence of supercritical CO2 (scCO2) and aqueous sulfide has been investigated by in situ attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) and ex situ X-ray diffraction (XRD). The chemical transformation of iron-bearing minerals to form iron carbonates may play a role in the chemistry related to the geological sequestration of carbon dioxide in the Earth's (sub)surface. The iron oxyhydroxide ferrihydrite in an aqueous solution containing sodium sulfide in contact with scCO2 at 100^oC reacts within 24h to form siderite and elemental sulfur. In situ studies of this reaction with ATR-FTIR show that ferrihydrite exists with an adsorbed layer of carbonate. However, the presence of the carbonate adsorbat...

International Nuclear Information System (INIS)

Up to 90% of the life time of cyclically loaded components is determined by short crack initiation and propagation. This stage of the fatigue damage process is strongly influenced by microstructural features, e.g. grain boundaries and crystallographic grain orientation. Therefore LEFM can not be applied in a reasonable manner explaining the demand for a mechanism-related modelling method. The present study deals with mechanical testing and microstructural examinations applied to the relatively new #beta#-titanium alloy LCB. The results are used as data base to develop a new short crack model that is based on the model of Navarro and de los Rios. By using various techniques such as electron back-scattered diffraction and finite-element calculations the origin of crack initiation is revealed and the characteristics of crack propagation is determined. (orig.)

Science.gov (United States)

The phase stability of silicides of Ni, Pt and Pd in contact with single crystal or amorphous silicon is examined. The presence of a particular silicide phase is identified by X-ray diffraction, and Rutherford backscattering is used to study composition. It is concluded that Pt or Pd silicides are suitable for Schottky barriers. Layers of silicon can be grown quickly by solid phase epitaxy at temperatures of 300-500C and using an intermediate metal film. Experimental results are reported. Doped layers have been obtained which have electrical characteristics suitable for the junctions in solar cells. The effects of impurities and orientation of the substrate on the growth kinetics are discussed.

Science.gov (United States)

We report significant enhancement in superconducting properties of yttrium substituted Ce1-xYxOFFeAs superconductors. The polycrystalline samples were prepared by two step solid state reaction technique. X-ray diffraction confirmed tetragonal ZrCuSiAs structure with decrease in both a and c lattice parameters on increasing yttrium substitution (with fixed F content). With smaller ion Y in place of Ce, the transition temperature increased by 6 K. Yttrium doping also lead to higher critical fields as well as broader magnetization loops, particularly at elevated temperature.

Energy Technology Data Exchange (ETDEWEB)

Nanosized CaSnO{sub 3} is synthesized by a hydrothermal process and characterized by X-ray diffraction (XRD), Raman spectroscopy, and scanning electron microscopy (SEM). The SEM observation shows the sample has a porous flowerlike morphology. The electrochemical results exhibit that the stable and reversible capacity of 547 mAh g{sup -1} is obtained after 50 cycles at 60 mA g{sup -1} (0.1 C) and the corresponding charge capacity is determined to be 316 mAh g{sup -1} at the current density of 2.5 C. Cyclic voltammetry and electrochemical impedance spectroscopy data are analyzed to complement the galvanostatic results. The observed excellent performance is attributed to the porous structure and large surface area of flowerlike CaSnO{sub 3}.

Energy Technology Data Exchange (ETDEWEB)

The effect of the composition of multicomponent Zr-Ti-V-Mn-Cr-Ni alloys on their hydrogen-storage capacity and on the rate of electrosorption/desorption hydrogen was investigated under potentiodynamics as well as single-pulse and long-term galvanostatic conditions. The main characteristics of alloys and alloy electrodes were determined by their structural analysis by means of X-ray diffraction and scanning electron microscope, by specific surface area test and by determination of the hydrogen absorption/desorption isotherms in the gas/solid phase system. It was found that only the alloys with a manganese content below a threshold could be used as electrode materials for Ni-MH batteries, whereas the modification of the electrode material by micro-encapsulation of alloy particles should limit the dissolution of manganese from the electrode material in a strong alkaline solution. (orig.)

International Nuclear Information System (INIS)

We investigate the effects of the velocity-dependent force on the magnetic form factors and magnetic moments of odd-Z nuclei. The form factors are calculated with the harmonic-oscillator wavefunctions. It is found that the contributions of the velocity-dependent force manifest themselves in the very large momentum transfer region (q?4 fm-1). In the low and medium q region the contributions of the velocity-dependent force are very small compared with those without this force. However, in the high-q region the contributions of the velocity-dependent force are larger than the normal form factors. The diffraction structures beyond the existing experimental data are found after the contributions of the velocity-dependent force are included. The formula of the correction to the single particle magnetic moment due to the velocity-dependent force is reproduced exactly in the long-wavelength limit (q=0) of the M1 form factor. (authors)

International Nuclear Information System (INIS)

Recent research carried out in laboratories showed that Saddle field neutral fast atom beam source is a promising method for nitriding of stainless steel. In the present work, the effect of treatment time on the microstructural and mechanical properties of plasma-nitrided stainless steel sample was investigated by this new method. Plasma nitriding was carried out at 420 deg. C and at a pressure of 0.1 Pa for a time range of 1 to 12 h. SEM-EDX, microhardness tests, optical microscopy and X-ray diffraction (XRD) were used to evaluate the mechanical and structural properties of the nitrided layer. It was found that nitriding time has a pronounced effect on the structural and mechanical properties of low-temperature plasma-nitrided samples and produced a precipitation-free thin hard nitrided layer within a short processing time.

Energy Technology Data Exchange (ETDEWEB)

The authors present results of grazing incidence X-ray diffraction studies concerning the effect of pH (and thus, of headgroup dissociation) on Langmuir monolayers of fatty acids, in the absence of any divalent cations in the aqueous subphase. An increase in pH transforms the distorted-hexagonal S phase first to the partially disordered Rotator-I phase with less distortion, and then to the completely disordered Rotator-II phase with an undistorted hexagonal structure. The S-Rotator-I and Rotator-I-Rotator-II transitions are pushed to lower temperatures with increase in pH. The fact that the effects of pH increase are almost identical to the effects of increasing temperature indicates the important role of headgroup-headgroup interactions in these monolayer phases.