The biosynthesis of rubber from ?-hydroxy-?-methylglutaryl-coenzyme A in Hevea brasiliensis latex  

UK PubMed Central (United Kingdom)

1. β-Hydroxy-β-methyl[3-14C]glutaryl-CoA is efficiently incorporated into rubber on incubation with Hevea brasiliensis latex, and the incorporation is diminished...Full Text Available

1969-09-01

2

Comparative study on the technological properties of latex and natural rubber from Hancornia speciosa Gomes and Hevea brasiliensis  

British Library Electronic Table of Contents (United Kingdom)

This work reports a systematic comparative study of the technological properties of natural lattices and rubbers extracted from Hancornia speciosa Gomes and Hevea brasiliensis [(Willd. ex Adr. de Juss.) Muell.-Arg.] (clone RRIM 600) trees from 11 collections in Brazil throughout 2004. Natural rubber latex particle sizes and distributions were quite similar with an average diameter around 1 mm. Molecular weight, Wallace plasticity, and Mooney viscosity values were approximately the same for both rubbers. Fourier transform infrared spectroscopy peaks characteristic of natural rubber were observed for both Hancornia and Hevea. The measured differences in technological properties included lower values for Hancornia dry rubber content, % ash, % nitrogen, and plasticity retention index but highe...

2009-01-01

3

Seasonal and clonal variations in technological and thermal properties of raw Hevea natural rubber  

British Library Electronic Table of Contents (United Kingdom)

Abstract This study was undertaken over a 10-month period under environmental conditions within the state of Mato Grosso, Brazil, to evaluate the causes of variation in the technological and thermal properties of raw natural rubber (NR) from different clones of Hevea brasiliensis (GT 1, PR 255, FX 3864, and RRIM 600). These clones were chosen to represent good clones available in Brazil. The technological properties of raw NR were evaluated in terms of their dry rubber content (DRC), Wallace plasticity, plasticity retention index (PRI), and Mooney viscosity. The thermal performance was evaluated with the thermogravimetry (TG)/differential thermogravimetry (DTG) technique. There were significant variations (p < 0.01 and p < 0.05) between clones and tappings for all technological properties,...

2011-01-01

4

Thermal characterization of rubberwood-polymer composites  

International Nuclear Information System (INIS)

The thermal properties of five types of radiation-induced wood-polymer composites based on a tropical hardwood, rubberwood (Hevea braziliensis), was studied by oxygen index measurement, differential thermal analysis (DTA) and thermogravimetry (TG). The DTA and TG curves of composites were different from those of rubberwood, which can be attributed to the presence of the incorporated polymers. Of the five composites, the one impregnated with bis(2-chloroethyl)vinyl phosphonate reduced the initial temperature of decomposition, increased the peak temperatures of exothermic reactions, and increased the char yield. Comparison with physical blends of rubberwood and the corresponding polymer provided some evidence of chemical interaction of wood and polymer in some of the composites. (author).

1989-01-01

5

Surface characteristics and overlaying properties of flat-pressed wood plastic composites  

British Library Electronic Table of Contents (United Kingdom)

This study evaluated surface characteristics and overlaying properties of wood plastic composite (WPC) panels made from dry-blended rubber wood fiber-polypropylene (PP) powder formulations using a conventional flat-press process under laboratory conditions. Three levels of rubberwood fibers (Hevea brasiliensis), 40%, 50%, and 60%, based on the composition by weight, were mixed with the PP powder without and with 3% (based on weight) maleic anhydride grafted PP (MAPP) as a coupling agent. Contact angle measurements on the WPC samples were performed using a goniometer connected with a digital camera which collected one image per second. Roughness measurements, average roughness (R a), mean peak-to-valley height (R z), and maximum roughness (R y), were taken from the sanded samples along and ...

2011-01-01