Energy Technology Data Exchange (ETDEWEB)

Abstract not provided

British Library Electronic Table of Contents (United Kingdom)

Ferroelectric barium strontium titanate (Ba0.7Sr0.3TiO3)(BST) thin films have been prepared from barium 2-ethylhexanoate [Ba[CH3(CH2)3CH(C2H5)CO2]2], strontium 2-ethylhexanoate [Sr[CH3(CH2)3CH(C2H5)CO2]2] and titanium(IV) isopropoxide [TiOCH(CH3)2]4 precursors using a modified sol-gel technique. The precursor except [TiOCH(CH3)2]4 were synthesized in the laboratory. Transparent and crack-free films were fabricated on pre-cleaned quartz substrates by spin coating. The structural and optical properties of films annealed at different temperatures have been investigated. The as-fired films were found to be amorphous that crystallized to the tetragonal phase after annealing at 550degreeC for 1h in air. The lattice constants "a" and "c" were found to be 3.974A and 3.990A, respectively. The grain...

International Nuclear Information System (INIS)

Holmium doped barium based hexaferrites BaFe_1_2_-_2_xHo_2_xO_1_9 with (x = 0.0-1.0) were synthesized by solid state reaction method. Structural and magnetic characterization of these ferrites provide significant information about their reactive physical properties. X-ray analysis reveals that in all samples M-type structure exist with few secondary phases. Scanning electron microscope revealed the grain size of the specimen. The results show that grain size decreases with the substitution degree of Holmium. Thus rare earth element Holmium Ho"3"+ acts as a grain growth inhibitor. The magnetic hysteresis loops show the variation in the values of magnetic parameters like saturation magnetization (M_s), remanent magnetization (M_r) and coercivity (H_c) were observed by changing Ho"3"+ content in BaFe_1_2_-_2_xHo_2_xO_1_9 ferrites. Coercivity showed a maximum value of 2230 Oe for (x = 0.4) and then decreasing trend were ...

British Library Electronic Table of Contents (United Kingdom)

Holmium doped barium based hexaferrites BaFe12-2xHo2xO19 with (x=0.0-1.0) were synthesized by solid state reaction method. Structural and magnetic characterization of these ferrites provide significant information about their reactive physical properties. X-ray analysis reveals that in all samples M-type structure exist with few secondary phases. Scanning electron microscope revealed the grain size of the specimen. The results show that grain size decreases with the substitution degree of Holmium. Thus rare earth element Holmium Ho^3^+ acts as a grain growth inhibitor. The magnetic hysteresis loops show the variation in the values of magnetic parameters like saturation magnetization (Ms), remanent magnetization (Mr) and coercivity (Hc) were observed by changing Ho^3^+ content in BaFe12-2xH...

Energy Technology Data Exchange (ETDEWEB)

Holmium doped barium based hexaferrites BaFe{sub 12-2x}Ho{sub 2x}O{sub 19} with (x = 0.0-1.0) were synthesized by solid state reaction method. Structural and magnetic characterization of these ferrites provide significant information about their reactive physical properties. X-ray analysis reveals that in all samples M-type structure exist with few secondary phases. Scanning electron microscope revealed the grain size of the specimen. The results show that grain size decreases with the substitution degree of Holmium. Thus rare earth element Holmium Ho{sup 3+} acts as a grain growth inhibitor. The magnetic hysteresis loops show the variation in the values of magnetic parameters like saturation magnetization (M{sub s}), remanent magnetization (M{sub r}) and coercivity (H{sub c}) were observed by changing Ho{sup 3+} content in BaFe{sub 12-2x}Ho{sub 2x}O{sub 19} ferrites. Coercivity showed a maximum value of 2230 Oe for (x = ...

Energy Technology Data Exchange (ETDEWEB)

We present the synthesis, magnetic and UV spectrometry of NiZn-ferrite nanofiber. The single phase of spinel ferrite was obtained at 600 {sup o}C. The NiZn-ferrite fibers fabricated by an electrospinning process were formed as a polygonal grain growth with firing temperature in fiber matrix. It appeared that the saturation magnetization (M{sub S}) of NiZn-ferrite nanofiber was dependent on Ni/Zn molar ratio which is similar to that of the inverse spinel ferrites. The NiZn-ferrite fibers showed good DNA adsorption efficiency that can be modified and utilized for DNA separation with magnetic nanofiber as a novel material in clinical applications.

International Nuclear Information System (INIS)

Structure of ferrite in drawn pearlitic steel containing 0.9 mass% C was investigated with X-ray diffraction technique using synchrotron radiation. In the detailed analysis of diffraction peaks of ferrite during the drawing process, it was experimentally revealed that the transformation of ferrite from bcc to bct due to the supersaturation of carbon in ferrite of heavily drawn pearlitic steel.

Energy Technology Data Exchange (ETDEWEB)

Double-contrast barium enema has a reduced sensitivity in patients with severe sigmoid diverticulosis. Therefore a carboxy methyl cellulose enema was employed after the conventional double-contrast examination in 15 patients with sigmoid diverticulosis. A significant increase in lumen diameter and a superior removal of barium residue from the diverticulas facilitated the interpretation of the sigmoid loops. Conclusion: The addition of methyl cellulose enema to double-contrast barium imaging improves diagnostic imaging in diverticulosis by expanding the lumen and emptying the diverticulas. (orig.).

Science.gov (United States)

... Title : THE INFLUENCE OF GRAIN BOUNDARY CARBIDE DENSITY ON THE BRITTLE FRACTURE OF FERRITE PEARLITE STEELS. ...

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

Nanodimensional powders of cubic copper ferrite are synthesized by two-steps procedure of co-precipitation of copper and iron hydroxide carbonates, followed by mechanochemical treatment. X-ray powder diffraction, Moessbauer spectroscopy and temperature-programmed reduction are used for the characterization of the obtained materials. Their catalytic behavior is tested in methanol decomposition to hydrogen and CO and total oxidation of toluene. Formation of nanosized ferrite material is registered even after one hour of milling time. It is established that the prolonging of treatment procedure decreases the dispersion of the obtained product with the appearance of Fe2O3. It is demonstrated that the catalytic behavior of the samples depends not only on their initial phase composition, but on the concomitant ferrite phase transformations by the influence of the reaction medium. -- Graphical abstract: It is demonstrated that the ...

International Nuclear Information System (INIS)

Interest to thin film of metals' silicides first of all is conditioned intrinsic al them unique physical properties. On their basis of it is possible to produce extremely sophisticated devices of solid-state electronics, production which needs the controlled change of physics, chemical and electrical properties with high-level of accuracy. On the present time most are in detail investigated composition, structure and properties of three-dimensional samples of metals' silicides. In the last years the intensive are led to researches in the direction of creation and study of physical-chemical properties thin (500-1000 Angstroms) and ultrafine (100-120 Angstroms) films silicides. It has information about composition, morphology of surface and emission of properties of thin film of silicides of barium, of cobalt and of palladium, was obtained in conditions of ultra-high vacuum. Low energy ion implantation ...

Science.gov (United States)

An American Society of Mechanical Engineers task group on stainless steel weld materials was organized to determine the need for ferrite measurements of production welds required by the US Nuclear Regulatory Commission Regulatory Guide 1.31 (Rev. 1). The task group studied paired ferrite measurements (i.e., calculated and measured ferrite numbers (FNs) for the material qualifications versus measured ferrite numbers for corresponding production welds (PWs)). Our purpose was to compare delta-ferrite content as measured in the filler metal weld qualification pad with that in the resultant PW. Welds made predominantly by three common processes (submerged arc, shielded metal arc, and gas tungsten arc) were included in the study. Weld metals investigated included types 308, 308L, 316, and 316L stainless steel. An initial evaluation of the paired ferrite measurements ...

International Nuclear Information System (INIS)

As part of a study into the properties of ferroelectric single crystals at nanoscale dimensions, the effects that focused ion beam (FIB) processing can have, in terms of structural damage and ion implantation, on perovskite oxide materials has been examined, and a post-processing procedure developed to remove such effects. Single crystal material of the perovskite ferroelectric barium titanate (BaTiO_3) has been patterned into thin film lamellae structures using a FIB microscope. Previous work had shown that FIB patterning induced gallium impregnation and associated creation of amorphous layers in a surface region of the single crystal material some 20 nm thick, but that both recrystallization and expulsion of gallium could be achieved through thermal annealing in air. Here we confirm this observation, but find that thermally induced gallium expulsion is associated with the formation of gallium-rich platelets on the surface of the annealed ...

Science.gov (United States)

... Accession Number : ADD323869. Title : EFFECTS OF SHIELDING ON PROPERTIES OF EDDY CURRENT PROBES WITH FERRITE CUP CORES. ...

International Nuclear Information System (INIS)

Full text of publication follows: Radiation hardening and embrittlement due to high-energy neutron radiation around 623 K are the important issues on reduced-activation ferritic/martensitic (RAF/M) steels. It is expected that the improvement of radiation hardening might be one of effective ways to control the mechanical properties of RAF/M after irradiation. It has been reported that the weld joint has less hardening than the base metal from the tensile test results of TIG weldments irradiated in HFIR. This report indicated that radiation hardening can be reduced by the optimization of heat treatment condition for F82H. The purposes of this study are to establish the condition of heat treatment for minimum of radiation hardening in F82H steel using Neutron/Ion-irradiation and to examine a correlation between tensile property and micro-hardness before/after irradiation. The materials used in this study were F82H IEA heat and F82H heat treatment variants. Neutron ...

Energy Technology Data Exchange (ETDEWEB)

To establish a relationship between the molecular structure of polycarboxylates and their growth-retarding influence on barium sulfate, seeded-suspension-growth experiments were performed at various inhibitor concentrations and pH values. Two types of polycarboxylates with a molecular structure based on their polyacrylic or maleic acid were studied. The molecular structure of these compounds were varied by particle substitution with monomers containing hydroxyl, amide, and sulfonic acid, as well as hydrophobic groups. Hydrophobic groups are detrimental to good inhibitor performance, whereas the introduction of OH, NH {sub 2}, or SO {sub 3} H groups presents opportunities to enhance the inhibitor effectiveness. The sequence in performance of the compounds on barium sulfate was compared with the sequence formerly obtained for calcium sulfate dihydrate.

UK PubMed Central (United Kingdom)

BackgroundUnderstanding the interactions between ion channels and blockers remains an important goal that has implications for delineating the basic mechanisms of ion channel function...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Mixed microstructures have been studied in low- carbon microalloyed steels suitable for automotive applications, after continuous cooling from the hot-rolled condition. Microstructural features such as polygonal ferrite, bainitic and acicular ferrite and microphase constituent are identified using transmission electron microscopy. The influence of these mixed structures on the tensile strength, impact toughness and fracture behaviour is examined. It is found that improvements in impact toughness as compared with microalloyed medium- carbon ferrite/pearlite steels can be achieved from these predominantly acicular structures developed by controlling alloy composition and continuous cooling of these lower carbon steels. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Four low activation alloy classes, two austenitic and two ferritic, have been incorporated into the MOTA-1B experiment in the FFTF reactor to provide an early assessment of the suitability of such alloys for reactor service.

British Library Electronic Table of Contents (United Kingdom)

This paper reports the results of in situ observation of fatigue crack growth in a ferrite?pearlite steel. Stress intensity factor range (?K) decreasing/increasing and constant-?K fatigue tests have been carried out. In banded pearlite orientation, intense crack branching was observed which leads to fatigue crack retardation. Crack closure during the test was monitored to understand the fatigue crack growth behaviour.

Energy Technology Data Exchange (ETDEWEB)

Effect of ultrasonic-wave irradiation on the Mn-Zn ferrite powder suspension prepared by solid-state reaction and alcoholic dehydration methods was investigated. Size, distribution, and morphology of the powders prepared at different temperatures were examined, as a function of irradiation time. It was observed that the powders were reduced in size by ultrasonic energy through distinct routes. 8 refs., 7 figs., 1 tab.

Energy Technology Data Exchange (ETDEWEB)

To establish the optimum barium-based reduced-laxative tagging regimen prior to CT colonography (CTC). Ninety-five subjects underwent reduced-laxative (13 g senna/18 g magnesium citrate) CTC prior to same-day colonoscopy and were randomised to one of four tagging regimens using 20 ml 40%w/v barium sulphate: regimen A: four doses, B: three doses, C: three doses plus 220 ml 2.1% barium sulphate, or D: three doses plus 15 ml diatriazoate megluamine. Patient experience was assessed immediately after CTC and 1 week later. Two radiologists graded residual stool (1: none/scattered to 4: >50% circumference) and tagging efficacy for stool (1: untagged to 5: 100% tagged) and fluid (1: untagged, 2: layered, 3: tagged), noting the HU of tagged fluid. Preparation was good (76-94% segments graded 1), although best for regimen D (P = 0.02). Across all regimens, stool tagging quality was high (mean 3.7-4.5) and not significantly ...

Energy Technology Data Exchange (ETDEWEB)

In a fluoroscopic imaging system, image quality and patient dose are both affected by the optical system linking the image intensifier with the video camera. The effect on patient exposure of increasing the optical iris aperture size over that required for other procedures performed on the same imaging system was investigated for the air-contrast barium enema examination. Using a large-area transmission ionisation chamber to monitor the Roentgen-area-product of entrance exposure, a decrease in fluoroscopic radiation of greater than 50% was clinically documented for a fluoroscopic system utilising kVp and mA variable automatic brightness control. For this iris change, the video image was of acceptable quality for positioning and monitoring the patient, and no deleterious effect was detected in the conduct of the air-contrast exam. The availability of a variable-sized operator-selectable iris diaphragm would permit this dose-reduction approach to be extended to other ...

International Nuclear Information System (INIS)

We present the effect of P2O5 addition on barium calcium aluminum borosilicate BCABS glasses of composition (mol %) 35BaO-15CaO-5Al2O3-(37-x)SiO2-8B2O3-xP2O5 (0?x?5). The incorporation of P2O5 increased network polymerization and crystallization tendency. However, addition of P2O5 leads to the formation of Cr2O3 at the interface, saturating it in the ions of the metal. This improves glass-to-metal bonding. (author)

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

International Nuclear Information System (INIS)

Early failure of an induction-hardening carbon steel pipe, which was used to transport tailing slurry, was caused by pitting corrosion. The microstructure on the internal pipe surface layer was found being a mixture of martensite, pearlite and ferrite. In this work, the pitting corrosion behavior of each constitute in the microstructure of steel is investigated with electrochemical noise analyses; the electronic properties of passive films were studied with Mott-Schottky relationship. It is found that the passive films formed on the materials under investigation are highly disordered n-type semiconductors. The high-to-low pitting susceptibility is ferrite > martensite > pearlite. The pitting resistance is related to the semiconductive nature of the passive film formed on each constitute. The pitting susceptibility increases with the donor concentration in the passive films. (author)

British Library Electronic Table of Contents (United Kingdom)

Fatigue crack growth tests of three ferrite-pearlite steels with different size and spacing of pearlite particles, which were uniformly distributed in the ferrite matrix, were carried out to investigate the effect of microstructure on fatigue crack growth behavior in the Paris regime. The fatigue crack growth rates for the three materials did not coincide with each other, even when the crack growth curves were arranged by the effective stress intensity factor range. From in situ observations, crack tip stress shielding phenomena, such as interlocking and branching, were found on the crack wake, which enhanced fatigue crack growth resistance. A small size and spacing of pearlite particle seemed to induce small but frequent crack deflections, which resulted in crack closure phenomena. On the...

Science.gov (United States)

... Abstract : MANY THIN FILM ACOUSTO-OPTIC INTERACTION EXPERIMENTS FOR ... CONVERTERS, AND FOR FAST SWITCHES HAVE BEEN ...

Energy Technology Data Exchange (ETDEWEB)

Long crack fatigue threshold ({delta} K{sub th}) and crack closure behaviour of two thermomechanically processed microalloyed (MA) ferrite-pearlite steels are reported. {delta} K{sub th} and crack closure were measured using a dynamic compliance measurement technique. Crack closure was observed at low load ratios (R < 0.5) and the fatigue thresholds decreased with increasing load ratio. In both steels, the closure-free intrinsic threshold ({delta} K{sub eff} {sub th}) was found to be independent of the load ratio. (orig.)

Energy Technology Data Exchange (ETDEWEB)

It is known that in size reduction of the granular structure of ferrite and ferrite-pearlite steels the temperature of the transformation from ductile to brittle condition is lowered. This effect can also be caused by an increase in the dispersity of intragrain and intergrain segregations (sulfides, carbonitrides, and segregations of impurity atoms), which accompanies grain size reduction and promotes initiation and propagation of cracks. In order to clarify the mechanism of fracture of steel in the region of the ductile-brittle transition steel 45 with different grain sizes and pearlite morphologies has been investigated.

CERN Document Server

Transformation optics is used to design a gateway that can block electromagnetic waves but allows the passage of other entities. Our conceptual device has the advantage that it can be realized with simple materials and structural parameters and can have a reasonably wide bandwidth. In particular, we show that our system can be implemented by using a magnetic photonic crystal structure that employs a square ray of ferrite rods, and as the field response of ferrites can be tuned by external magnetic fields, we end up with an electromagnetic gateway that can be open or shut using external fields. The functionality is also robust against the positional disorder of the rods that made up the photonic crystal.

Science.gov (United States)

... After strip- ping off the chloroform, the dibromo ethyl (EDBEB) compounds are separated from the m-BDBEB using a thin film evaporator. ...

Science.gov (United States)

Sputtering of glass coatings on cadmium sulfide thin film solar cells

Energy Technology Data Exchange (ETDEWEB)

A series of Gd-substituted M-type barium hexaferrites has been prepared by the ceramic route, according to the formula (Ba{sub 1-x}Gd{sub x})O.5.25Fe{sub 2}O{sub 3} (x=0-0.30). XRD analysis revealed that all the samples present primarily an M-type structure. Samples x=0 and x=0.05 are single-phase. Hematite (Fe{sub 2}O{sub 3}) and GdFeO{sub 3} were detected in the remaining samples. Coercivity (H{sub c}) shows remarkably high values, {approx}293kA/m for x=0.20 and 0.30 with a maximum of 322kA/m for x=0.25. Specific saturation magnetization ({sigma}{sub sat}) of the samples presents a small increase up to x=0.10. The microstructure examination indicates that Gd may act as a grain growth inhibitor.

International Nuclear Information System (INIS)

Radiation damage and its recovery in the light emittance efficiency and the attenuation length of barium fluoride (BaF_2) scintillator have been investigated. The light yield and transmittance of small samples of BaF_2 scintillator were measured after #gamma#-irradiation from 0.5x10"4 to 1.1x10"5 Gy for deterioration, and after sunlight exposure for recovery. Suspension of deterioration was observed both in light yield and in attenuation length at an integrated dose of #gamma#-rays of about 10"4 Gy. Fairly good and quick recovery of the deteriorated BaF_2 scintillator was obtained by sunlight exposure. Using a Monte Carlo simulation method, the dependence of the light emittance efficiency on #gamma#-irradiation and sunlight exposure was studied. It has been found that the light emittance efficiency, as well as the attenuation length, is influenced by #gamma#-irradiation and sunlight exposure. (orig.).

Energy Technology Data Exchange (ETDEWEB)

'The interactions of carbon tetrachloride with strongly basic oxides and hydroxides have been studied by several techniques in order to understand the surface reactions and the subsequent bulk reactions that result in the destruction of the chlorinated hydrocarbon. Emphasis has been placed on understanding the surface phases, as well as the bulk phases, that are present during these transformations. As a result of the study with barium oxide, a reaction cycle has been demonstrated that may have practical significance in the removal of chlorinated hydrocarbons.'

Energy Technology Data Exchange (ETDEWEB)

Study of the rate of dissolution in simulated lung fluid of uranium from 3 different ore matrices and from refined uranium dioxide in an essentially all teflon extraction apparatus; the rate of dissolution of thorium from a nickel metal/2 percent thoria mixture; the effect of neutron irradiation of the studied materials upon the dissolution rates; and the adsorptions of the radioisotope tracers barium 133 (substitute for radium), lead 203 and thorium 234 upon the extraction system components.

International Nuclear Information System (INIS)

The problem of search for new materials for spectrally positioned laser sources, which is central for modern photonics, is discussed. The use of the stimulated Raman scattering effect in crystals offers a highly efficient way to the design of such sources. The recent results of investigations into this effect for a large number of various types of crystalline materials are presented. The most promising compounds, as regards the realisation of different laser operation modes, are considered, including calcium, strontium, barium and lead molybdates and tungstates. Several examples of functioning efficient lasers based on novel materials exhibiting the stimulated Raman light scattering effect are given.

International Nuclear Information System (INIS)

Initial clinical experience in gastrointestinal radiography using Fuji Computed Radiography(FCR) system was reported. Image quality of conventional film/screen radiography and FCR system on upper GI series and barium enema was compared. Reflecting wide dynamic range of the system, improved image quality was confirmed, particularity in visibility of fine mucosal pattern(area gastricae), folds and overall contour. High sensor sensitivity of the system could reduce radiation dose requirement significantly. Diagnostically acceptable images were obtained with approximately 1/5 of routine dose for conventional radiography except in cases of lateral view of the rectum. (author).

Energy Technology Data Exchange (ETDEWEB)

Purpose: The purpose of this research was to identify the extent and scope of changes to radiography practice. Method: Questionnaires were sent to radiology managers at acute National Health Service (NHS) hospitals in 2000 as a follow-up to an initial survey conducted in 1998. Information was sought on region, teaching/non-teaching status, the nature of extended role tasks undertaken and the year in which these tasks were first undertaken. Results: Some 172 questionnaires were returned from a total of 253 dispatched (68%). In 161 hospitals radiographers administered intravenous injections and performed barium enemas in 119 hospitals, while a red-dot system was in operation in 141 hospitals. Reporting by radiographers had increased since 1998. Replies indicated that, at 124 hospitals, radiographers were reporting in ultrasound. Skeletal reporting was the second most-frequently-reported activity, with 63 hospitals indicating that radiographers reported in this ...

Energy Technology Data Exchange (ETDEWEB)

To avoid the drop in corrosion resistance of stainless steels in conventional nitriding (precipitation of CrN), low-temperature techniques like ion implantation, plasma immersion ion implantation (PIII, PI{sup 3}) and low-temperature plasma nitriding were developed. In this investigation, four stainless-steel grades (ferritic: X6Cr17, austenitic-ferritic: X2CrNiMoN22.5.3, austenitic: X8CrNiTi18.10 and X5CrNi18.10) were plasma-nitrided between 250 and 500 C. Nitrogen-enriched layers with a high nitrogen content were produced, leading to a significant increase in surface hardness. X-ray diffraction indicated that CrN did not precipitate if treatment temperatures did not exceed 400 C. 'Expanded austenite' formed in the austenitic and duplex steels and {epsilon}-nitride (Fe{sub 2}N{sub 1-x}) in the ferritic steel. The optically visible structure of the nitrided cases is comparable with that of the PIII layers, ...

Energy Technology Data Exchange (ETDEWEB)

In the production of heavy-sectioned ferritic spheroidal graphite iron castings for such parts as spent fuel shipping container (cask), undesirable structures like abnormal graphite lamella, pearlite or so-called chinese script type of inclusions tend to appear, deteriorating the mechanical properties at the central part of the section where molten iron freezes last. 500 mm thick cylindrical vessels with bottom, weighing 18 tons and 33 tons, were poured as trial products of casks. Solidification structure and mechanical properties were examined at many portions of the castings. By controlling chemical composition, solidification time and inoculation process the structure and the mechanical properties in the last portion of the section to solidify were improved. Sufficiently homogeneous heavy-sectioned ferritic spheroidal graphite iron castings were successfully produced in the as-cast state. In addition, quality assurance process by using test ...

International Nuclear Information System (INIS)

Neutron irradiation embrittlement of reactor pressure vessel (RPV) steels is one of the critical issues on aging management for long term operation of nuclear power plants. Mechanistic understanding of embrittlement is a key to accurate prediction of embrittlement, especially after long term operation where the mechanical test data are sparse. Since matrix hardening is the source of the embrittlement, we focus on matrix hardening of A533B bainitic pressure vessel steel. Bainitic matrix is composed of lath structure made by ferrite and carbides, therefore it is important to understand how this structure affects hardening behavior, and to understand irradiation response of each phase. As the typical dimension of lath structure of A533B is about one micron, nanoindentation technique is suitable for the estimation of hardening of each phase. MV ion accelerators were used for controlled irradiation because MeV ion irradiation can produce defects to the depth greater ...

International Nuclear Information System (INIS)

The synergistic effects of displacement damage and atomic hydrogen and helium on swelling of the ferritic/martensitic steel, F82H, has been investigated. The irradiation was performed at temperatures between 470 and 600 deg. C to 50 dpa (displacement per atoms) under conditions of simultaneous ion beams consisting of Fe"3"+, He"+ and H"+ ions or Fe"3"+ and He"+ ions. The swelling of F82H steel under triple beams with 18 appm He/dpa and 70 appm H/dpa was larger than that under dual beams with 18 appm He/dpa. The swelling in F82H under triple beams increased with decreasing irradiation temperature from 0.1% to 3.2%, while swelling under dual beams was between 0.04% and 0.08%. On the other hand, in the case of triple beam irradiation with a high ratio of gas/dpa, the swelling tended to increase with irradiation temperature. The swelling in ferritic/martensitic steels is significantly enhanced by the synergistic effect of displacement damage, ...

International Nuclear Information System (INIS)

A series of nine model ferritic alloys were ion irradiated at #propor to#300 C using 2.5 MeV He ions to a dose of 1.4 x 10"2"1 ion/m"2, which corresponds to #propor to#0.1 dpa at a depth of 2 #mu#m and #propor to#3.5 dpa at the peak damage region which occurs at about 4 #mu#m deep. The resultant changes in hardness as a function of depth were measured using a Nanoindenter "t"r"a"d"e"m"a"r"k. TEM was used to investigate the defect distributions. The effect of various solutes, Cu and N in particular, but Mn and Ti as well, on the change of hardness and the defect distribution due to the ion irradiation are discussed. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The purpose of this study is to evaluate the synergistic effect of helium and hydrogen on Fe-Cr ferritic model alloys, to provide basic understanding concerning development of fusion reactor components. Single, dual and triple ion-beams consisting of Fe{sup 3+}, He{sup +} and H{sup +} were used for irradiation, at temperatures 470-600 deg. C and dose to 50 dpa at 1 {mu}m. The dual beam irradiation with He enhanced cavity nucleation extensively to swelling of about 0.4%, whereas the dual beam irradiation with H did not significantly affect the microstructure. In the case of triple ion irradiation, the synergistic effect of He and H was confirmed clearly; relative large void formation and enhanced swelling to almost 5%. The synergistic effect suggests that the role of H is important for void growth and dislocation bias.

British Library Electronic Table of Contents (United Kingdom)

For an ultrafine grain ferrite/cementite (UGF/C) steel, the Charpy impact energy was measured at temperatures from 373K to 4.2K, and tensile tests were carried out at temperatures between 323K and 77K. For the steel with annealed microstructure, the ductile-to-brittle transition appearance temperature (DBTT) was lower than the Charpy transition temperature (CTT). With increasing annealing time at 873K, the DBTT and the CTT increased, and the DBTT approached the CTT. The DBTT decreased with decreasing effective grain size. The effective grain size correlated to the grain size of the larger grain size peak in the distribution of grains with {100} planes. The annealed microstructures had higher yield strength for equivalent toughness (including upper shelf energy, DBTT and CTT) compared to th...

Energy Technology Data Exchange (ETDEWEB)

The impact properties of high-strength low alloy TRIP steels such as 'TRIP-aided dual-phase steel' and 'TRIP-aided bainitic steel' associated with the transformation-induced plasticity (TRIP) of retained austenite were investigated for some applications to the automotive impact members. The TRIP steels possessed far higher impact absorbed value and lower ductile-brittle transition temperature than the conventional ferrite-martensite and ferrite-pearlite steels. The stress relaxation resulting from the strain-induced transformation of retained austenite islands or films improved the impact properties in terms of suppressing void and/or crack initiation and these propagation. The best impact properties were completed in the steel composing of uniform fine bainitic lath structure and a large amount of stable interlath retained austenite films. (author)

British Library Electronic Table of Contents (United Kingdom)

A fully lamellar ferrite/cementite nanostructure was designed in a low C steel by using a specific thermal treatment. The strengthening of such microstructure has been investigated as a function of prestrain by rolling up to a deformation of 300%. As in usual pearlitic structure, its work-hardening shows no saturation and its elongation to fracture remains rather constant instead of decreasing drastically as conventional steels. The hardening by a similitude effect is thus not the privilege of pearlitic steels. Nevertheless, its lower initial work-hardening rate at low strain compared to an equivalent pearlitic steel and a lower hardening potential at high strain let us suspect major differences in the nature and the behaviour of ferrite channels in relation to the morphogenesis of the mic...

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

No abstract prepared.

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

Pitting corrosion is a kind of electrolytic corrosion by which the surface of a material is locally affected owing to inhomogeneities on the part of the material or medium. The paper deals briefly with questions relating to the importance, to parameters medium or materialwise, influence on production and construction, as well as the general conditions for pitting corrosion. In particular oxygen corrosion in unalloyed and low-alloy steel, and pitting corrosion in ferritic chromium-steel and austenitic chromium-nickel (molybdenum) steel is described. (DG).

International Nuclear Information System (INIS)

The structural changes attendant on intermartensitic transformation in a Ni-Mg-Ga shape memory alloy are considered using magneto-optical visualization with the help of ferrite-garnet monocrystalline films. It is established that on the intermartensitic transformation the complete reorganization of martensite macrostructure fails. Martensite crystals resulted from the basic transformation change somewhat their sizes on intermartensitic transition. The existence of large-scale labyrinth magnetic domain structure is revealed

International Nuclear Information System (INIS)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

Various chemical, physical, and mechanical methods to prevent unwanted deposition of mineral scale are described. The suitability of the different methods, which largely depends on the specific features and requirements of the system involved, is discussed. Special emphasis is placed upon the threshold treatment, where the growth process is retarded by the addition of trace amounts of growth inhibitors. Growth experiments have been performed on barium sulfate and calcium sulfate dihydrate seed crystals, suspended in a supersaturated solution with and without organic bisphosphonates as inhibitors. Two methods are selected for the analysis of the growth data. A degree of inhibition is defined to obtain a quantitative description of the influence of a growth inhibitor on the growth rate of the crystals. In addition the influence of the molecular structure of various bisphosphonates with different substituents is shown. The effect of a bisphosphonate on the geometry of ...

British Library Electronic Table of Contents (United Kingdom)

Background/Purpose: Congenital esophageal stenosis (CES) is a rare malformation. Endoscopic dilations represent a therapeutic option. This study retrospectively evaluated the efficacy and safety of a conservative treatment of CES. Patients and Methods: Patients diagnosed with CES since 1980 by a barium study or endoscopy were reviewed. Endoscopic ultrasonography (Olympus UM-3R-20-MHz radial miniprobe, Olympus Corporation, Tokyo, Japan), available from 2001, allowed for the differential diagnosis of tracheobronchial remnants (TBR) and fibromuscular hypertrophy (FMH) CES. All children underwent conservative treatment by endoscopic dilations (hydrostatic and Savary). Results: Forty-seven patients (20 men) had CES. Fifteen were associated with esophageal atresia; and 8, with Down syndrome. Mea...

British Library Electronic Table of Contents (United Kingdom)

An innovative hybrid powder prepared using computer simulation allowed development of a new foundation having a fine, smooth texture that has never been achieved before. The optical structure/design of the powder was based on the results of measurements and analyses conducted on the optical characteristics of a baby's delicate skin, which is the envy of many women. To obtain the optimal optical characteristics, the finite differential time domain (FDTD) method for solving Maxwell's differential equation by difference and time domain was applied to the computer simulation method. For synthesis of the hybrid powder based on the optical model, a proprietary shape regulation coating technology was used in which flaky substrates were coated with microspherical forms of barium sulfate crystals. ...

British Library Electronic Table of Contents (United Kingdom)

Nanoscale yttrium?barium?copper oxide (Y2BaCuO5, Y211) particles were synthesized using the emulsion method and the solution method. The basic water-in-oil (w/o) emulsion system consisted of n-octane (continuous oil phase), cetyltrimethylammonium bromide (cationic surfactant), butanol (cosurfactant) and water. The composition of the emulsion system was varied and characterized by measuring the conductivity of the solutions and droplet size. The droplet size of emulsion was determined by using the dynamic light scattering method. The water content, cosurfactant content, and surfactant/n-octane ratio affected the droplet size which was in the range of 3?8?nm, and hence the w/o emulsion system was referred to as a nano-emulsion system. A model was used to verify the droplet size. The influenc...

International Nuclear Information System (INIS)

This paperwork explain the method of water sampling to obtain the precipitate of BaCO3 solutions that will be used to analyze 13C from field work in Kelana Jaya, Selangor, Langkawi, Kedah and Taiping, Perak. The sampling involves collecting of water samples for groundwater from boreholes and surface water from canal, river, pond and ex-mining pond from several locations at the study sites. This study also elaborates the instruments and chemicals used. The main purpose of this sampling is to obtain the precipitate of BaCO3 for 13C analysis of dissolved inorganic carbon (DIC). A correct sampling method according to standard is very important to ensure an accurate and precise result. With this, the data from the laboratory analysis result can be fully utilized to make the interpretation of the pollutants movement. (Author)

Energy Technology Data Exchange (ETDEWEB)

This short paper (abstract) describes the characteristics and performances of prototypes of ultra-thin lithium micro-batteries (thickness < 0.2 mm) which can be incorporated into microelectronic circuits. (J.S.)

CERN Document Server

Residual Stresses in Ta, Mo, Al and Pd Thin Films Deposited by E-Beam Evaporation Process on Si and Si/SiO 2 Substrates

UK PubMed Central (United Kingdom)

An examination of the noise of polycrystalline silicon thin film transistors, in the context of flat panel x-ray imager development, is reported. The study was conducted in the spirit of exploring...Full Text Available

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

... interactive surfaces and interfaces, and 3) the more complex a ... carbonate or calcium phosphate with a thin interface ... diameter) for nerve prosthesis. ...

Science.gov (United States)

... joined together by a thin ribbon of glass that is bent into a frame shape in a prior operacion. The three glass pieces are ...

International Nuclear Information System (INIS)

(Jun 1978). United States Chino, K. Hitachi Research Lab., Japan Kikuchi,

Science.gov (United States)

... analyzer section for angle resolved measurements, and a thin film evaporator with a quartz crystal microbalance to measure the mass deposition. ...

International Nuclear Information System (INIS)

The concentrations of uranium, arsenic, and radium remain well below the maximum permissible values of < 0.1 mg/l (uranium), < 0.1 mg/l (arsenic) and < 100 mBq/l (radium) due to two separation stages with barium sulfate and GoPur 3000 precipitation and due to iron hydroxide/iron arsenate precipitation. The radioactive arsenates can be separated from the toxic ones by separating the sludge which is analyzed. Processing of radioactive sludges leaves reusable GoPur 3000, sulfuric solutions which contain uranium or solutions which contain carbonate, and radioactive barium sulfate whose radiation intensity of 12 mBq/g is due to the presence of radium. The sludge produced contains adsorbed salts in addition to the dosed chemicals (floated sludges: 40 g/m"3, iron sludges < 20 g/m"3). A solids content < 100 g/m"3 can be selected for both sludge portions. Static-mixer chemicals dosing and technical improvements of the tubular reactor are ...

International Nuclear Information System (INIS)

Cervix cancer is the most common female cancer in Korea. In spite of their relatively local invasive tendency, still 44% of patient will develop recurrent cancer This result suggests that more aggressive local treatment may increase the cure rate but increased complication risk also cannot be avoidable. Various institutions proposed different treatment regimen, but recommended dose were about 4500 cGy for whole pelvis and 8000 cGy at point A, even though they agreed that those doses may not be satisfactory for control of bulky disease. 96 cases of invasive cervical cancer, treated with postoperative or primary radiation therapy were analyzed to determine the complication rate and prognostic factor in our treatment regimen which is 500-1000 cGy higher than other institution. Mean follow up duration was 21 months. Symptomatic patients including mild but persistent abdominal discomfort was 46%, but only 1 patient (1%) had operative treatment because of incomplete obstruction of small ...

Energy Technology Data Exchange (ETDEWEB)

The effect of accelerated thermal cycling on a joint between modified 9Cr-1Mo steel (Grade 91) and Alloy 800 welded with Inconel 82 and 182 filler material is discussed. This is part of a trimetallic transition joint involving Grade 91-Alloy 800-316LN austenitic stainless steel for steam generator application. It has been shown that, during thermal cycling following the typical post-weld tempering treatment at 760 deg. C for 2 h, no carbon diffusion occurs from the ferritic steel towards the weld metal. There is, in fact, a hardness increase at the ferritic steel/weld metal interface which is probably a result of work hardening. Carbon migration sets in only after unusually long post-weld heat treatments for 20 and 50 h at 760 deg. C followed by thermal cycling. Significantly, even under the most severe thermal cycling test conditions imposed, no cracking or oxide notching could be detected, thus demonstrating the superior performance potential ...

International Nuclear Information System (INIS)

Superparamagnetic MFe23+O4 (M=Mn2+, Fe2+ and Co2+) inverse spinel ferrite (ISF) nanoparticles with narrow size distribution having average diameters of 6-8 nm were synthesized by a diol reduction of organic metals and the surface was modified to be hydrophilic by coating with succimer. Magnetic resonance imaging (MRI) contrast enhancement by dipolar coupling defined interactions between the synthesized ISFs and protons in the bulk water was investigated with initial susceptibility, magnetization and anisotropy of the succimer-coated ISFs. The relaxivity ratios, r2/r1, for MnFe2O4, Fe3O4 and CoFe2O4 were measured to be 12.2, 23.1 and 62.3, respectively, which demonstrate the potential usefulness of these magnetic nanoparticles as T2 contrast agents for MRI.

Energy Technology Data Exchange (ETDEWEB)

The low-cycle fatigue properties of the ferritic-martensitic steels MANET I and II and F82H-mod, have been investigated at a temperature of 200 C. The strain-controlled fatigue has been performed with strain ranges between 0,4% and 1,0% and at a strain rate of 8.10{sup -4} s{sup -1}. The steel F82H-mod, is characterised by a higher plastic strain amplitude compared to MANET I and II. Some of the specimens have beenirradiated with a 104 MeV {alpha}-particle beam. The homogeneous implantation of 400 appm He leads to a hardening of the material. At the beginning of the fatigue tests the stress response of the irradiatedspecimens is higher compared to the unirradiated specimens. In general, thematerial shows softening during fatigue. The softening of irradiated material, which is fatigue tested with a high total strain amplitude, is higher than that of the unirradiated material. The lifetime is reduced. For irradiated specimens fatigued at small total strain amplitudes ...

International Nuclear Information System (INIS)

Irradiation of ferritic steels with neutrons in the temperture range of room temperature to #propor to# 450deg C results in lattice hardening, which causes an increase in strength and a decrease in ductility. Eight reduced-activation Cr-W-V stels with chromium concentration varying from 2.25 to 12% were irradiated at 365deg C to #propor to# 7 dpa in the Fast Flux Test Facility. A steel with 2.25% Cr and the combination of 2% W and 0.25% V hardened less than those containing vanadium or tungsten alone or a steel with 1% W and 0.25% V. The amount of hardening was similar for Cr-W-V steels with constant vanadium and tungsten concentrations and containing 2.,25, 5, and 9% Cr; a steel with 12% Cr hardened considerably more. Specimens of two conventional Cr-Mo steels, 9Cr-1MoVNb and 12Cr-1MoVW, were also irradiated, and the hardening of these steels was similar to analogous reduced-activation steels. (orig.).

International Nuclear Information System (INIS)

Past elastic-plastic fracture studies for leak-before-break (LBB) assessment of low alloy steel pipings have been focused mostly on the behavior of base metals and their weld metals. In contrast, the heat-affected zone (HAZ) of a welded pipe has not been studied in detail primarily because the size of the HAZ is too small to make specimens for mechanical properties measurements. In this study, microstructural analyses, microhardness tests, tensile tests and J-R tests have been conducted as a function of distance from a fusion line and temperature for HAZ materials of SA106Gr.C low alloy piping steels. For the ferrite-pearlite steels such as SA106Gr.C, the HAZ specimens showed a higher yield strength and fracture toughness compared with those of its base metal. These characteristics, despite of grain coarsening, can be explained by cleaner microstructures of HAZ materials with a finer morphology of carbides compared with pearlitic-ferritic base ...

Energy Technology Data Exchange (ETDEWEB)

Austenitic stainless steel castings, such as SCS 13, SCS 14, which consists of {delta}/{gamma} duplex phase, are extensively used as structural material in seawater environments. It is known that SCS 14 involving 2wt% Mo is more resistant to pitting corrosion than SCS 13. In this paper, effects of Mo on the pitting corrosion are discussed in terms of microstructure of the material. The corrosion behavior of the materials with different {delta} ferrite contents and cleanlinesses have been evaluated by seawater exposure testing, electrochemical polarization, and TEM-EDX analysis. The results indicate that pits mainly nucleate at nonmetallic inclusions such as MnS and {delta}/{gamma} boundaries, and materials containing {delta} ferrite above 7vol% have high pitting corrosion resistance. The nucleation at {delta}/{gamma} boundaries is assumed to be due to the segregation of P. It is considered that because of segregation of Mo along {delta}/{gamma} ...

Energy Technology Data Exchange (ETDEWEB)

This paper reports that the co-deposition of chromium and silicon into a 2.25Cr-1.0Mo-0.15C steel, alloy 800, and type 304 stainless steel has been achieved using the pack cementation process. The ferritic coating produced on the 2.25 Cr-1.0Mo steel was approximately 225 {mu}m (9 mils) thick, whereas the inward diffusion of chromium and silicon produced a two-phase structure of ferrite and austenite for type 304. Chromium and silicon were incorporated into the austenitic solid solution upon diffusion into alloy 800. All coatings had approximately 25 to 35 wt% Cr and 2 to 3% Si at the surface. Cyclic oxidation testing in air of the coated 2.25Cr-1.0Mo steel (T = 700{degrees} C) and type 304 (T = 1035{degrees} C) showed a dramatic decrease in the oxidation kinetics compared to the original uncoated alloys. The cyclic oxidation of alloy 800 was also improved.

International Nuclear Information System (INIS)

The electrochemical behaviour of passive films formed on one austenitic stainless steel (AISI 304) and one ferritic stainless steel (AISI 446) in solutions with pH between 0.6 and 8.4 was studied by capacitance measurements and photocurrent spectroscopy. Compositional characterization of the passive films was done by X-ray photoelectron spectroscopy. The capacitance increases with decreasing pH. Doping densities evaluated from Mott-Schottky plots are in the range 2-6 x 10"2"0 cm"-"3 and increased with the pH in the neutral/alkaline range while in pH 0.6, values above 10"2"1 cm"-"3 were found. The bandgap energy indicates two transitions, at 2.5-2.8 and 3.2 eV. The analytical data reveal that, as the pH increased, the films become enriched in Fe(II) and Fe(III), whereas the Cr(III) gradually decreases. The films formed at very low pH had a behaviour that contrasts with that of the films formed in the neutral/alkaline media. The films are described by a bilayer ...

Energy Technology Data Exchange (ETDEWEB)

Transition joints in power plants between ferritic steels and austenitic stainless steels suffer from a mismatch in coefficients of thermal expansion (CTE) and the migration of carbon during service from the ferritic to the austenitic steel. To overcome these, nickel-based consumables are commonly used. The use of a trimetallic combination with an insert piece of intermediate CTE provides for a more effective lowering of thermal stresses. The current work envisages a trimetallic joint involving modified 9Cr-1Mo steel and 316LN austenitic stainless steel as the base materials and Alloy 800 as the intermediate piece. Of the two joints involved, this paper describes the choice of welding consumables for the joint between Alloy 800 and 316LN. Four consumables were examined: 316, 16-8-2, Inconel 82 and Inconel 182. The comparative evaluation was based on hot cracking tests and estimation of mechanical properties and coefficient of thermal expansion. ...

Energy Technology Data Exchange (ETDEWEB)

The report covers the results of exposing materials for steam turbines to increased steam temperatures in two modules of the KOMET 650 testing facility at the Westfalen power plant. Ferritic/martensitic steels with 9 to 12% Cr and austenite and nickel-based alloys were investigated. Some experimental coatings on low-alloy Cr steel were also tested. The principal findings are presented. It will become possible to construct advanced power stations to be operated at higher temperatures. (orig.)

International Nuclear Information System (INIS)

A preliminary investigation was completed on the characterization and decontamination of coral samples from Johnston Island. These samples were found to contain individual particles (2 to 0.25 mm) of contaminated coral as well as a piece of contaminated magnetic metal. They ranged in activity from about 70 to 811 nCi Am-241. The decontamination methods investigated were froth flotation, ferrite treatment, attrition scrubbing, ultrasonic treatment and dry sieving. Dry sieving, the more effective technique, separated about 42 wt % of the coral into a decontaminated fraction. This fraction (>4 mm) contained about 0.5% of the total activity. 7 refs., 3 tabs.

Energy Technology Data Exchange (ETDEWEB)

The electrochemical dissolution behaviour of armco-iron and of the steels C15, C45, C60 and 100Cr6 in concentrated sodium chloride media has been investigated. Anodic metal dissolution experiments have been carried out using the flow channel cell (parallel plate reactor), the rotating cylinder electrode (RCE) and the capillary cell. The microstructure of the steel has been varied through variation of carbon content and heat treatment (e.g. soft annealed with globular carbides or pearlitic). Current-efficiency values have been obtained by gravimetric measurements in the current-density range from i=5 to 60 A/cm{sup 2}. For the soft annealed steels, the divalent ferrite dissolution in combination with electroless cementite removal dominates. For the pearlitic steels, the occurrence of oxygen evolution electronically conductive metal carbides or trivalent ferrite dissolution, depending on the current density applied, was detected. Microstructure ...

Energy Technology Data Exchange (ETDEWEB)

The degradation status of outlet feeders in Wolsung unit 1 is analyzed using feeder thickness measurement data during overhaul period in 2000. DBs related to feeder thinning are made for parameters affecting dissolution rate and parameters affecting mass transfer rate. The initial thickness of feeder in Wolsung unit 1 is analyzed using initial thickness data of Wolsung unit 2, 3 and 4 as there are no initial thickness data of Wolsung unit 1. The initial thickness is varied as feeder diameter and bending degree, and CANDU feeders can be divided as 3 types for 2.5'' feeders and 3 types for 2'' feeders. The average initial thickness value for each type is defined as the initial thickness value of the type for Wolsung unit 1 feeders. Thinning rate is evaluated as the value dividing difference between initial thickness and minimum measured thickness by operation time. It is found that the distribution of ...

Energy Technology Data Exchange (ETDEWEB)

This paper will discuss initial studies of thin-film GaAs grown by molecular-beam epitaxy for use in developing a thin-film GaAs solar cell. Photocurrent and photoluminescence intensity are related to the material morphology as a function of growth conditions. Growth temperature and V/III ratio have a dramatic effect on the photocurrent. However, it seems likely that even after optimizing such growth parameters, it will be necessary to provide substrates that can provide templates to enhance grain size from the start of thin-film growth. {copyright} {ital 1997 American Institute of Physics.}

International Nuclear Information System (INIS)

A study of the thin gold film growth, during the deposition on glass substrate under UHV conditions at low temperatures, is presented. The complementary methods, the atomic force microscopy and grazing incidence x-ray reflectometry, are used for the research. It is shown that due to variation of the time of deposition from 2 to 50 min different kinds of thin Au films nanostructures are obtained: from discontinuous films consisting of isolated islands, via formation of the chains of islands, up to continuous films. (author)

Energy Technology Data Exchange (ETDEWEB)

We compared the characteristics on thin-section CT images with the histological structure of thirty-four surgically resected peripheral lung lesions 30 mm or less in diameter with a greater than 50% area of GGA on thin-section CT. Pathologically, focal area of GGA corresponded to alveolar replacement growth of tumor or interstitial fibrotic thickening of inflammation. It is considered that determination of the GGA in small peripheral lung lesions on thin-section CT is useful for the diagnosis of early adenocarcinomas. (author)

UK PubMed Central (United Kingdom)

The primary determinants of pulmonary disease are environmental. The same thinness and delicacy of the air-blood barrier which allows rapid exchange of oxygen and carbon dioxide also reduce its effectiveness...Full Text Available

Science.gov (United States)

A silicon solar cell assembly comprising a large, thin silicon solar cell bonded to a metal mount for use when there exists a mismatch in the thermal expansivities of the device and the mount.

Science.gov (United States)

... The phenol and cresylic acid stream is flashed in a thin film evaporator over a concentrated sulfuric acid mixture to remove pyridine type substances ...

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline MnO thin film has been prepared by a pulsed laser deposition (PLD) method. The reversible lithium storage capacity of the MnO thin film electrodes at 0.125C is over 472 mAh g{sup -1} (3484 mAh cm{sup -3}) and can be retained more than 90% after 25 cycles. At a rate of 6C, 55% value of the capacity at 0.125C rate can be obtained for both charge and discharge. As-prepared MnO thin film electrodes show the lowest values of overpotential for both charge and discharge among transition metal oxides. All these performances make MnO a promising high capacity anode material for Li-ion batteries. (author)

Science.gov (United States)

... In: Separated Flows, AGARD CP No. ... on thin wings in two-dimensional incompressible flow. ... fields in the region of separating and reattaching flows. ...

Science.gov (United States)

... A few applications, such as magnetic forming and levitation, have exploited the dynamic force pro- ducing capability of eddy currents. ...

Energy Technology Data Exchange (ETDEWEB)

In this paper, the design of large thin PIN detector with a membrane stress avoidance configuration is proposed, and the related device fabrication process is developed. Ultra-thin PIN detector {approx} 1.13 cm{sup 2} in area is fabricated on a thin ( {approx} 35{mu}m) silicon membrane, and characterized. Detector performance improvement has been successfully demonstrated. With the membrane stress avoidance design, the improved detector exhibits a leakage of 6nA, which is at least 5 times lower than that of detector of identical junction area. The new detector features a full depleted capacitance of 110 pF, and a FWHM of 40.86 keV energy resolution for 5.486 MeV alpha particle spectrography.

Science.gov (United States)

Figure 23 presented detailed layout of the cooling system designed for the Mach 6 hypersonic- transport. The distribution system consisted of thin-wall ...

International Nuclear Information System (INIS)

The authors observed an extremely high permittivity (#approx#35 000 at T_C) in barium zirconate titanate (BaZr_0_._1Ti_0_._9O_3) ceramics with holmium substitution (1-5 mol %) in Ba site. Careful microstructural investigation and energy dispersive spectroscopy analysis of the 1-2 mol % of Ho substituted ceramics showed the enrichment of a Ho-phase along the grain boundaries with a composition close to the Ho_2Ti_2O_7 pyrochlore. The formation of Ho rich phase resulted in the Maxwell-Wagner polarization mechanism, which leads to this unusually high permittivity. Ceramics with 3 mol % or higher Ho content showed lesser permittivity values compared to 1-2 mol %, probably due to the increase in pyrochlore phase. These high dielectric constant ceramics are useful in nanoscale devices.

Energy Technology Data Exchange (ETDEWEB)

BaTiO{sub 3} compacts, when fluxed with {lt} 2 vol% of a complex borate glass phase, were sintered to near theoretical density at temperatures {lt} 1175{degrees}C in 2 h. Microstructural analysis showed a uniform grain size {lt} 1.0 {mu}m with 0.75 wt% ZrO{sub 2} added to the flux phase as a grain growth inhibitor. TEM analysis revealed a microcrystalline grain-boundary phase with the ZrO{sub 2} resident along the grain boundaries. These samples displayed an essentially flat dielectric profile, low dissipation factors ({lt} 2%) over the range 25{degrees} to 125{degrees}C, a near linear dependence ({approx} {+-} 15%) between 25{degrees} and {minus} 55{degrees}C, and significantly increased voltage stability. X-ray diffraction analysis of these small-grained materials indicates a suppression of the tetragonal structure toward a more cubic modification.

Science.gov (United States)

Using an expanded nuclear data base, the transmutation of PCA, AMCR33 (a reduced activation austenitic steel), HT-9, Rafer2 (a reduced activation ferritic steel), V-15%Cr-5%Ti alloy, and SiAlON (a ceramic) were calculated for two positions in the Fast Flux Test Facility (FFTF), three positions in the High Flux Isotope Reactor (HFIR), and the first wall position of both the STARFIRE and MARS conceptual fusion reactors. The peripheral test (PTP) position, and to a lesser extent the radial beryllium (RB) position, of HFIR show significant transmutations which are often in the opposite direction to the transmutations in the fusion conceptual designs. The positions in FFTF, as well as the hafnium covered location in the HFIR RB position show relative minor transmutations.

British Library Electronic Table of Contents (United Kingdom)

Irradiation of EP-823 (16Cr12MoWsiVNbB) ferritic-martensitic steel with 7-MeV Ni++ ions and with 30- and 70-keV He+ ions at a temperature of 500?C was followed by an increase in the microhardness, which was due to both radiation point defects and changes in the phase composition and the dislocation structure of the steel. It was found that the dependence of the largest relative increase in the microhardness on the concentration of radiation-induced point defects in the near-surface region of the steel under irradiation with different ions correlated with an analogous dependence of the surface segregation of silicon and chromium.

Energy Technology Data Exchange (ETDEWEB)

There have been many stress measurements on welds by neutron diffraction over the past 20 years but there are still a number of serious experimental issues that are often not addressed. The primary fact is that the microstructure generally changes across the weld and accompanying this may be a change in the concentration of strengthening elements in solution. This will lead to a shift in lattice spacing which may be incorrectly interpreted as a strain. Secondly, a gradient of plastic deformation near the weld may be expected. Since plastic deformation by application of a stress always generates intergranular (type-2) strains this may lead to a range of intergranular effects superposed on the conventional weld-related strains. The effects are illustrated by neutron diffraction studies of Zr-4, ferritic and austenitic welds where chemistry, intergranular effects and crystallographic texture can all play a role.

Energy Technology Data Exchange (ETDEWEB)

The pitting resistance of Fe-Cr and Fe-Cr-Mo alloys has been correlated with characteristics of the passive films analyzed by Auger electron spectroscopy (AES). Increased film protectiveness as a result of increased Cr in the alloy can be directly attributed to Cr enrichment of the film and decreased film thickness. Increased Mo in the alloy or passivation at noble potentials promotes passive film resistance to breakdown, but neither does much to change the macrocharacteristics of the film. Rather, it is suggested that the roles of alloying and/or passivation conditions are related to the susceptibility and distribution of weak points of the film. In solutions in which pitting occurs, chloride is generally not incorporated into the film, suggesting that the role of halides is to interact with weak points of the film at the solution/film interface. At 260/sup 0/C, the films are much thicker and likely to be much more defective in structure than those formed at 80/sup 0/C.

British Library Electronic Table of Contents (United Kingdom)

This paper presents a procedure for transferring the CTOD fracture toughness obtained from laboratory specimens to an equivalent CTOD for structural components, taking constraint loss into account. The Weibull stress criterion is applied to correct the CTOD for constraint loss, which leads to an equivalent CTOD ratio, b, defined as b=d/dWP, where d and dWP are CTODs of the standard fracture toughness specimen and the structural component, respectively, at the same level of the Weibull stress. The CTOD ratio b is intended to apply to the fracture assessment of ferritic steel components to stress levels beyond small-scale yielding. Nomographs are given to determine the b-value as a function of the crack type and size in the component, the yield-to-tensile ratio of the material and the Weibul...

International Nuclear Information System (INIS)

The magnetic and magnetostrictive properties of polycrystalline Co1-xMnxFe2O4 (0 ? x ? 0.4) have been studied. Although the Curie temperature decreases continuously with increasing concentration of Mn, the magnetization remains high up to x = 0.3 and unexpectedly low coercivity is observed for this composition showing an unusual magnetostrictive behaviour. This composition shows a relatively larger magnetostriction at low fields. Moreover, the strain derivative which is the slope of the magnetostriction curve at low magnetic fields is almost doubled and the field at which maximum magnetostriction is observed is reduced to almost half for 30% of Mn substitution. The results show that x ? 0.3 in Co1-xMnxFe2O4 is an optimum composition with superior magnetostrictive properties for many applications.

British Library Electronic Table of Contents (United Kingdom)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically conductive and corrosion-resistant CrN or Cr2N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of commercially available, high Cr (30-35wt%) Ni-Cr alloys and a ferritic high Cr (29wt%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effect...

Energy Technology Data Exchange (ETDEWEB)

The preliminary design of a far-infrared free-electron laser with a Coaxial Hybrid Iron (CHI) wiggler is presented. The CHI wiggler consists of a central rod and outer ring of alternating ferrite and dielectric spacers. A periodic wiggler field is produced when the CHI structure is immersed in an axial magnetic field. The design under investigation makes use of 1A, 1MV annular electron beam interacting with the TE{sub 01} coaxial waveguide mode at approximately 1 THz ({lambda} = 300 {mu}m). The nominal wiggler period is 0.5 cm and the inner and outer waveguide radii are 0.4 and 0.8 cm, respectively. An axial guide field of 5-10 kG is used. The device performance is modeled with slow-time-scale nonlinear code. Self fields and axial velocity spread are included in the model. Theoretical results will be presented.

International Nuclear Information System (INIS)

Surface-sensitive UV photoelectron yield spectroscopy was employed to study electron acceptor levels at surfaces of chalcopyrite structure Cu-In-Se thin films. Surface Fermi level pinning was observed for Cu-rich films. Shallow acceptor levels ascribable to defects Cu_I_n and V_C_u were observed for near-stoichiometric and In-rich films respectively. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Crude N,N-dialkylcarbamoylmethylphosphonates and phosphine oxide extractants, and particularly crude dihexyl N,N-diethylcarbamoylmethylphosphonate and octylphenyl N,N-diisobutylcarbamoyl phosphine oxide, are purified by distilling the crude materials in a thin film evaporator. Preferably, the crude materials are reacted with concentrated hydrochloric acid and then with aqueous sodium hydroxide prior to distillation in the thin film evaporator to hydrolyze impurities contained in them. The purified extractants are useful for extracting actinides and lanthanides from liquid waste streams. (author).

International Nuclear Information System (INIS)

The phenomenological description of the giant magnetoresistance effect as well as discussion of the requirements which must be fulfilled in giant magnetoresistance thin film structures are given in the first part of our review. In the second part the magnetization reversal and giant magnetoresistance effect of antiferromagnetically coupled multilayers, spin Valve and pseudo-spin valve thin film structures are explained. For these structures we also discuss the influence of the structure defects such as surface roughness and pinholes on the giant magnetoresistance effect. (author)

Energy Technology Data Exchange (ETDEWEB)

A simple and continuous model for the on-state current of polysilicon thin-film transistors, suitable for implementation in circuit simulators, is presented. The model includes the potential barrier at the grain boundaries, the channel length modulation and the excess current due to impact ionization. Comparison between measured output characteristics and the model shows excellent agreement over wide range of bias voltages and for devices with different gate lengths.

International Nuclear Information System (INIS)

Electrodeposition of semiconducting iron oxide (Fe_2O_3) thin film was carried out from an alkaline sulphate bath. A 0.1 M ferrous sulphate (FeSO_4#centre dot#7H_2O) was complexed with 0.1 M citric acid. By addition of 1 N NaOH, pH of the solution was made alkaline (pH=9) and deposition of iron oxide (Fe_2O_3) thin films was carried out potentiostatically at room temperature (300 K). From cyclic voltametry (CV), electrochemical studies were carried out for deposition of iron oxide thin films. The XRD studies reveal that Fe_2O_3 with epsilon (#epsilon#) phase having monoclinic crystal structure is formed. By observing scanning electron microscope (SEM), it is seen that iron oxide films were homogeneous, uniform and well covered to surface of the substrate. Grain size was found to be in nanometers range from XRD analysis. The optical band gap of Fe_2O_3 thin film was estimated to be 1.90 eV. Electrical ...

International Nuclear Information System (INIS)

The effects of gate and drain bias stresses on thin film transistors fabricated in polysilicon films crystallized using the advanced sequential lateral solidification excimer laser annealing (SLS ELA) process, which yields very elongated polysilicon grains and allows the fabrication of TFTs without grain boundary barriers to current flow, are investigated as a function of the active layer thickness and of the TFT orientation relative to the grains. The application of hot carrier stress, with a condition of V_G_S = V_D_S/2, was determined to induce threshold voltage, subthreshold swing and transconductance degradation for TFTs in thicker polysilicon films and the associated stress-induced increase in the active layer trap density was evaluated. However, this device degradation was drastically reduced for TFTs fabricated in ultra-thin films. Furthermore, the application of the same stress condition to TFTs oriented vertically to the elongated ...

International Nuclear Information System (INIS)

From the results of the In-Service Inspection (ISI) measuring the wall thickness of outlet (hot-leg side) feeder pipes performed at two Canadian nuclear power plants, Point Lepreau and Gentilly-2 in 1995 and 1996, respectively, the wall thinning degradation of feeder pipes at the bend part was found to be much more severe than expected. It has been well known that such wall thinning of feeder pipes is caused by the flow accelerated corrosion (FAC) which is one of the mechanical-chemical degradation mechanisms affecting the integrity of piping systems. For the Wolsung unit 1, the wall thickness measurements have been performed during every overhaul period since 1996. The wall thinning rates at the bends of outlet feeder pipes were assessed to exceed the design value. However, for the Wolsung units 2, 3 and 4, the wall thinning rates of all the outlet feeder pipes were assessed not to exceed it. The ...

International Nuclear Information System (INIS)

We give a theoretical design for a locally resonant two-dimensional cylindrical structure involving a pair of C-shaped voids in an elastic medium which we term as double 'C' resonators (DCRs) and imbedded thin stiff bars, that displays the negative refraction effect in the low frequency regime. DCRs are responsible for a low frequency band gap which hybridizes with a tiny gap associated with the presence of the thin bars. Using an asymptotic analysis, typical working frequencies are given in closed form: DCRs behave as Helmholtz resonators modeled by masses connected to clamped walls by springs on either side, while thin bars behave as a periodic bi-atomic chain of masses connected by springs. The discrete models give an accurate description of the location and width of the stop band in the case of the DCR and the first two dispersion bands for the periodic thin bars. We then combine our asymptotic ...

Energy Technology Data Exchange (ETDEWEB)

The influence of high C martensite on the strength and impact behavior of C-Mn-Nb-Al steels has been determined for two distributions: films surrounding the ferrite grains and distinct colonies. In the former case, the impact behavior markedly deteriorated, this deterioration increasing with martensite level. The changes in impact behavior could be explained by regarding the films of martensite as being similar to the brittle grain boundary carbides that are present in ferrite-pearlite steels. These films readily crack, yet are always thick enough to produce a sufficient wide crack to render crack propagation easy. The critical event in fracture then becomes the ability to propagate the cracks through the grain boundaries. The greater the grain boundary coverage by these films, the easier this becomes and the worse is the impact behavior. When the martensite is present as colonies, again the impact performance is seriously impaired, but to a ...

International Nuclear Information System (INIS)

This paper introduces the JNM Special Issue on the development of a first wall for the reaction chamber in a laser fusion power plant. In this approach to fusion energy a spherical target is injected into a large chamber and heated to fusion burn by an array of lasers. The target emissions are absorbed by the wall and encapsulating blanket, and the resulting heat converted into electricity. The bulk of the energy deposited in the first wall is in the form of X-rays (1.0-100 keV) and ions (0.1-4 MeV). In order to have a practical power plant, the first wall must be resistant to these emissions and suffer virtually no erosion on each shot. A wall candidate based on tungsten armor bonded to a low activation ferritic steel substrate has been chosen as the initial system to be studied. The choice was based on the vast experience with these materials in a nuclear environment and the ability to address most of the key remaining issues with existing facilities. This ...

Energy Technology Data Exchange (ETDEWEB)

Nb{sub 2}O{sub 5} thin films were formed on aluminum foils by a sol-gel process in order to increase the capacitance of the aluminum foils which are used as aluminum electrolytic capacitors. Investigations focussed on the preparation and characterization of the coating solution, the formation of Nb{sub 2}O{sub 5} thin films on aluminum foils, and the heat treatment and anodization of the films. The phase transition and electrical properties, such as capacitance, leakage current, and withstand voltage of the Nb{sub 2}O{sub 5} thin films were also measured. The Nb{sub 2}O{sub 5} thin films annealed at temperatures below 550 degree C were found to be amorphous, but they were crystallized to the orthorhombic phase by annealing at temperatures higher than 580 degree C. The capacitance of the coated samples increased with an increase in the thickness of the formed Nb{sub 2}O{sub 5} thin ...

Science.gov (United States)

Elastically deforming thin glass (thickness = 0.13 to 0.80 mm) provides an alternate method of forming a curved glass reflector which can eliminate some of the disadvantages of thicker glass. A concept is described where silvered thin glass is bonded to a steel backing to form a laminate with a reflectance greater than 93%. Subsequent bending of the flat reflector laminate to a concentrating profile produces compressive stresses throughout the glass if the laminate is properly designed. These compressive stresses enhance fracture resistance and the lamination provides protection for the silver. The design of the laminate is outlined for 0.25 and 0.51 mm thickness glass and fabrication procedures are discussed. Thermal/humidity cycling, hail impact, bond strength measurements and reflectance results are presented which demonstrate the performance capabilities of this reflector laminate concept.

Energy Technology Data Exchange (ETDEWEB)

As thin films become increasingly popular (for solar cells, LEDs, microelectronics, batteries), quantitative morphological information is needed to predict and optimize the film's electronic, optical and mechanical properties. This quantification can be obtained quickly and easily with X-ray diffraction using an area detector and synchrotron radiation in two simple geometries. In this paper, we describe a methodology for constructing complete pole figures for thin films with fiber texture (isotropic in-plane orientation). We demonstrate this technique on semicrystalline polymer films, self-assembled nanoparticle semiconductor films, and randomly-packed metallic nanoparticle films. This method can be immediately implemented to help understand the relationship between film processing and microstructure, enabling the development of better and less expensive electronic and optoelectronic devices.

British Library Electronic Table of Contents (United Kingdom)

Dopant-free Bi2Ti2O7 thin films with pyrochlore structure and La-doped bismuth titanate thin films have been fabricated by means of chemical solution decomposition, and characterized by X-ray diffraction, atomic force microscopy, scanning electron microscopy and UV?Vis spectrophotometry in this study. Their photocatalytic activities have been evaluated by photodegrading methyl orange solution, and the optimum processing parameters for the highest photocatalytic activity have been found. Moreover, the effects of La-doping on the phase transformation and the photocalalytic activity have been studied. It has been deduced from the experiment result that substituted La3+ ions can act as a stabilizer of Aurivillus phase BLT and a grain?growth inhibitor in BLT thin films.

Energy Technology Data Exchange (ETDEWEB)

The measurement of local heat transfer coefficients is necessary to record the basic phenomena of heat transfer in thin-film apparatuses. For this reason the so-called electrochemical analogy method was developed and used for this application. The electrochemical method implies a specifically composed electrolyte which substitutes the fluid to be evaporated in the thin-film apparatus. Using the redox electrolyte (0,025 kmol/m/sup 3/ K/sub 4/Fe(CN)/sub 6/ resp. k/sub 4/Fe(CN)/sub 6/ and 2nNaOH) the viscosity was, for the first time, thickened until 0.4 Pa s by the help of hydroxyethyl-cellulose.

International Nuclear Information System (INIS)

High-resolution electron microscope observations confirm the presence of small crystallites in thin TbFeCo films protected by Si_3N_4 overcoats. Selected area electron diffraction patterns in top-view projection indicate that the crystals have a face-centered-cubic structure. Microscope analysis reveals grain growth following annealing of these protected thin films at 200 degree C in vacuum, and Kerr measurements yield large reductions in coercivity relative to the room-temperature value. The typical grain size visible in top-view observations increases from about 3 nm in the as-deposited samples to about 30 nm after annealing at 200 degree C for 36 h while the static coercivity, H_c, drops by about 40%. The fcc structure of the crystals is retained after annealing.

International Nuclear Information System (INIS)

Chromium nitride thin films were deposited on SA-304 stainless steel substrates by using direct-current reactive magnetron sputtering. The influence of process conditions such as nitrogen content in the fed gas, substrate temperature, and different sputtering gases on microstructural characteristics of the films was investigated. The films showed (200) preferred orientation at low nitrogen content (< 30%) in the fed gas. The formation of Cr_2N and CrN phases was observed when 30% and 40% N_2 were used, with a balance of Ar, respectively. Field emission scanning electron microscopy and atomic force microscopy were used to characterize the morphology and surface topography of the thin films, respectively. Microhardness tests showed a maximum hardness of 16.95 GPa for the 30% nitrogen content.

Energy Technology Data Exchange (ETDEWEB)

Silicon thin film with thickness in range 1000-5300 A deposited on rough Cu foil by a radio frequency magnetron sputtering is used as anode materials for Li-ion rechargeable batteries. The SEM, XRD and TEM analysis reveals that the Si thin film has a floccular nano-sized multi-crystalline structure. Li ions insertion/extraction evaluation is performed mainly with constant current charge/discharge cycling and cyclic voltammetry (CV) at room temperature. The cycleability and reversible discharge capacity are found to depend on the film thickness, and thinner films give larger accommodation capacity. A 3120 A Si film provides a reversible specific capacity over 3500 mA hg{sup -1} with excellent cycleability under 0.5 C charge/discharge rate.

UK PubMed Central (United Kingdom)

Testes of jellyfish Phialidium gregarium were fixed in 2 per cent OsO₄ in Veronal-acetate buffer at pH 7.4. Thin sections showed that in young spermatids the spindle fibers...Full Text Available

International Nuclear Information System (INIS)

Iron oxide thin films have been obtained by spray pyrolysis using 100% methanolic and ethanolic solutions of iron tri-chloride. The films were deposited onto ITO-coated glass substrates. The preparative conditions have been optimized to obtain compact, pin-hole-free and smooth thin films which are adherent to the substrate. The structural, morphological and compositional characterizations have been carried out by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray analysis. The films deposited using ethanolic solution results into pure hematite; #alpha#-Fe_2O_3 thin films, however, films deposited using methanolic solution consists of hematite and maghemite-c phases of iron oxide. The films are nanocrystalline with particle size of 30-40 nm. The optical absorbance of the film was of the order of 10"5 cm"-"1. The optical band gap of films was found to be 2.26 and 2.20 eV for the films deposited using ...

International Nuclear Information System (INIS)

Optical absorptance spectra of A-15 compounds were taken using a calorimetric technique in the range 0.2 eV to 4.0 eV. Thermomodulation spectra were taken on several A-15 sputtered films.

UK PubMed Central (United Kingdom)

Catch is a mechanical state occurring in some invertebrate smooth muscles characterized by high force maintenance and resistance to stretch during extremely slow relaxation. During catch, intracellular...Full Text Available

Science.gov (United States)

This report is a continuation of the former efforts to elucidate the behavior of ferrocement concrete in static and dynamic stress fields. The influence of various reinforcements on pre and post cracking of thin sections forms the main topic of this repor...

British Library Electronic Table of Contents (United Kingdom)

Ferroelectric thin films such as BST, PZT and PLZT are extensively being studied for the fabrication of DRAMS since they have high dielectric constant. The large and reversible remnant polarization of these materials makes it attractive for nonvolatile ferroelectric RAM application. In this paper we report the characterization of Ba0.7Sr0.3TiO3 (BST) thin films grown by pulsed laser ablation on oxide electrodes. The structural and electrical properties of the fabricated devices were studied. Growth of crystalline BST films was observed on La0.5Sr0.5CoO3 (LSCO) thin film electrodes at relatively low substrate temperature compared to BST grown on PtSi substrates. Electrical characterization was carried out by fabricating PtSi/LSCO/BST/LSCO heterostructures. The leakage current of the heteros...

Science.gov (United States)

During Phase II multi-junction solar cell will be grown on the large grain thin film produced during Phase I on flexible/low cost metal foil substrate. ...

UK PubMed Central (United Kingdom)

The curvature elastic modulus (bending stiffness) of stearoyloleoyl phosphatidylcholine (SOPC) bilayer membrane is determined from membrane tether formation experiments. R. E. Waugh and R. M. Hochmuth...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A thin film microoxidation test utilizing the concept of the Lubricant Stability Map has been used to study the effect of temperature on deposit formation by lubricants on upper piston locations of low heat rejection engines. The stability maps were established for two formulated lubricants in this study. These two lubricants were also evaluated in a series of engine tests with various piston temperatures. The deposition phenomena observed in the engine tests have been adequately simulated and described by the stability maps. It is concluded that lubricants at upper piston locations are under a thin film condition similar to that achieved by the thin film microoxidation test. The deposit formation trend is determined by the volatility, thermal stability, and oxidative stability of the base stock. Additives have little effect on deposit formation at very high temperatures. A combined consideration of all competing reaction ...

UK PubMed Central (United Kingdom)

An image slicing spectrometer (ISS) for microscopy applications is presented. Its principle is based on the redirecting of image zones by specially organized thin mirrors within a custom fabricated...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

An attempt is made to augment the heat transfer efficiency by means of inserting an oscillating thin plate into a tube of the shell and tube heat exchanger. However, the heat transfer augmenting mechanism has not been fully explained. To elucidate this heat transfer augmenting mechanism, an investigation was given on the heat transfer characteristics of a tube inlet at its preliminary run area when a double-hinged oscillating thin plate is inserted in the inlet. As a result of the experiment, the heat transfer augmentation in the tube as a result of inserting the double-hinged oscillating thin plate was found effective when the preliminary inlet run area is treated as the object. However, in comparison of the effect with the heat transfer in a fully developed turbulent region, it was {eta}- 1. The result thus obtained explains that no sufficient turbulence can be obtained when the deflection angle of the first oscillating ...

Science.gov (United States)

international vehicles, control centers, and ground support personnel. ... consists of thin membranes made from a polymer-based film and ..... (including airplanes and submarines), environmental monitoring, and control ...... sciences can use it to analyze the birth and death of stars, the formation of solar ...

Energy Technology Data Exchange (ETDEWEB)

The authors present the emitter efficiency results for the thin film 25 percent Ho YAG (Yttrium Aluminum Garnet, Y3Al5O12) selective emitter from 1000 to 1700 K with a platinum substrate. Spectral emittance and emissive power measurements were made (1.2 less than lambda less than 3.2 microns) and used to calculate the radiative efficiency. The radiative efficiency and power density of rare earth doped selective emitters are strongly dependent on temperature and experimental results indicate an optimum temperature (1650 K for Ho YAG) for thermophotovoltaic (TPV) applications.

Energy Technology Data Exchange (ETDEWEB)

This paper presents a prototype of an entirely inorganic lithium ions battery cell. LiCoO{sub 2} thin film cathodes and Li{sub 4/3}Ti{sub 5/3}O{sub 4} thin film anodes have been deposited on Li{sub 3x}La{sub 2/3-x}TiO{sub 3} sintered solid electrolyte pellets and the performances of these battery cells have been tested. (J.S.) 5 refs.

Energy Technology Data Exchange (ETDEWEB)

The symposium, Polycrystalline Thin Films - Structure, Texture, Properties, and Applications III, was held at the 1997 Materials Research Society Spring Meeting on March 31--April 4 in San Francisco, California. The topics and investigations were interdisciplinary in nature, and ranged from fundamental to technological. Specifically, the work presented in this volume includes film growth, texture and structural evolution, phase transformation, characterization of grain boundaries and interfaces, stress analysis, and works on polycrystalline Si and SiGe films and devices. Fifty four papers were processed separately for inclusion on the data base.

British Library Electronic Table of Contents (United Kingdom)

Thermal desorption spectroscopy (TDS) was used to study outgassing from polycrystalline SiGe (poly-SiGe), SiC and SiO"2 films used for poly-SiGe-based MEMS thin film vacuum package technology. Primary desorption products were found to be H"2, H"2O and CO"2. The CO"2 outgassing could be correlated with CF"4 plasma interface cleaning used for thick SiGe PECVD, which can leave carbon at the CF"4-plasma-cleaned interface.

International Nuclear Information System (INIS)

The application of medium energy ion scattering in combination with channelling and blocking to the study of the initial stages of palladium silicide formation is discussed. After a brief description of the experimental arrangement and method, the effects on the Rutherford backscattering spectra of depositing small quantities of palladium on clean Si(111) are reported. The uniformity and thermal stability of thin palladium silicide films grown at room temperature were measured. Finally, channelling and blocking results were used to carry out a structural analysis of thin epitaxial Pd_2Si layers. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

A liquid-fillet is formed in front of a rotor blade in the cylinder of a horizontal agitated thin-film evaporator. Its thickness varies due to the gravity while the blade revolves inside the cylinder. In the critical condition, the amplitude of the oscillation becomes infinite and the phase advances 180 degrees. Prior to the critical condition, the experimental data agrees fairly well with the predictions. Near the critical condition, the amplitutde increases and the phase advances 60 degrees. In other words, the transition to the critical condition occurs continuously. (6 figs, 1 ref)

Energy Technology Data Exchange (ETDEWEB)

The half-metallic Heusler alloy Ni{sub 2}MnIn is of high interest for use in spin electronics since at the Ni{sub 2}MnIn/InAs interface a spin polarization of 100% is predicted. We prepare high-quality thin films of 20-60nm thickness by co-evaporation and DC magnetron sputtering. Point-contact Andreev reflection spectroscopy yields a spin polarization of up to 54%. By spectral generalized magneto-optical ellipsometry, the dielectric and magneto-optical properties are determined and ferromagnetic behavior below the Curie temperature T{sub C}=318K is proved.

Energy Technology Data Exchange (ETDEWEB)

Solid-state acoustic sensors for monitoring conditions at a surface immersed in a liquid and for monitoring concentrations of species in a liquid and for monitoring electrical properties of a liquid are formed by placing interdigital input and output transducers on a piezoelectric substrate and propagating acoustic plate modes therebetween. The deposition or removal of material on or from, respectively, a thin film in contact with the surface, or changes in the mechanical properties of a thin film in contact with the surface, or changes in the electrical characteristics of the solution, create perturbations in the velocity and attenuation of the acoustic plate modes as a function of these properties or changes in them.

Energy Technology Data Exchange (ETDEWEB)

Described herein are the results of the FY1994 research program for analysis and evaluation for thin film solar cells. The study on quantitative analysis of hydrogen atoms in a plasma determines quantity of hydrogen atoms in the plasma of monosilane diluted with hydrogen. It is found, contrary to expectation, that quantity of hydrogen atoms in the plasma decreases as it is more diluted with hydrogen. The study on light-induced degradation of the thin chlorine-base amorphous silicon films confirms that the plasma CVD method with 20% of dichlorosilane gas added to monosilane gas produces the thin amorphous silicon film 3 times faster than the conventional method. The thin film has essentially the same defect density as the one prepared by the conventional method, showing good photoelectric characteristics. The thin film of chlorinated amorphous silicon has a 1 digit lower defect ...

International Nuclear Information System (INIS)

Several materials, lenses, dry bearings and cables were exposed to a tritiated moisture environment to study the behavior of tritium contamination on candidate materials for ITER remote handling equipment. To optimize the tritium removal procedure, decontamination experiments using a gas purge with three different moisture concentrations were also performed. The surface tritium concentrations of CeO_2 containing alkaline barium glass (NB), CeO_2 containing lead glass (LX) and synthetic quartz (Quartz) after the exposure experiments were 7.80, 10.94 and 0.67 Bq/cm"2, respectively. It was found that the tritium concentration was influenced by the compositions of the materials. The concentrations of tritium on type 831 (solid lubrication material: graphite) and type 237 (solid lubrication material: tungsten disulfate) dry bearings after the exposure experiments were 89.80 and 31.78 Bq/cm"2, respectively. The tritium concentration in an electric cable tested was 5014 ...

Energy Technology Data Exchange (ETDEWEB)

The usefulness of helical CT early phase images optimized by the SmartPrep method for evaluation of wall invasion by colorectal cancer was investigated. Between August 1997 and September 1998, CT was performed to evaluate the primary tumor and local extension in 10 consecutive patients with colorectal cancer confirmed by barium enema- and/or colonoscopy. Early-phase images were acquired by using SmartPrep application software. This method allows the optimal scan delay time to be obtained by continuous monitoring of increases in CT values after injection of contrast medium. Sections of the surgical specimens, close to the same plane as the CT images, and of the same slice thickness, were analyzed histopathologically. All 10 cancers, regardless of size, showed strong enhancement on the early-phase images (81.4-112 HU, mean: 95.1 HU). The strongly enhanced image areas on CT corresponded to the primary cancer areas on histopathological specimens. A low-density zone was ...

International Nuclear Information System (INIS)

Borosilicate based glass formulations have been found suitable for fixing the HLW (high level radioactive liquid waste) generated after reprocessing of the spent nuclear fuel. As the glass experiences continuous irradiation by #alpha#, #beta#a, and #gamma# radiations from the radioactive components of HLW, alteration in the glass structure may occur. Understanding of these structural evolutions of the nuclear waste glasses under irradiation is crucial to secure long term disposal and predict their behavior. In the present work, alkali based barium borosilicate glasses, having composition similar to that of Trombay Research Reactor waste glass were irradiated with high energy "1"2C beam and the radiation induced changes were monitored by micro Raman experiment. Since a "1"2C atom can be considered as a cluster of alphas, this beam was chosen to yield linear energy losses (LET) comparable to that in case of a particles. The irradiations were carried out at 30 deg N ...

Energy Technology Data Exchange (ETDEWEB)

The puborectalis syndrome is a defecation disorder supported by the nonrelaxation of puborectalis sling with consequent dyschezia. They report on a series of 98 patients submitted to clinical examination, defecography, anorectal manometry, electromyography and intestinal transit time studies. The main symptoms of puborectalis syndrome in their patients were incomplete defecation (89 %) and intermittent evacuation (63 %); 28 % of patients turned to finger defecation. In all patients, defecography showed an abnormal increase in puborectalis impression on the posterior anorectal wall, reduced anorectal angle opening under straining (mean value: 113 deg) and prolonged expulsion time with barium pooling in the ampulla (mean evacuation time: 38 seconds). Such anorectal abnormalities as rectal mucosal prolapse (47 cases) and anterior rectocele (36 cases) were also associated. In 33 of 98 patients (34 % of cases), sling assessment by bidigital palpation at preliminary ...

Energy Technology Data Exchange (ETDEWEB)

A procedure and correlations are presented for predicting Charpy-impact energy, tensile flow stress, fracture toughness J-R curve, and J{sub IC} of aged cast stainless steels from known material information. The ``saturation`` impact strength and fracture toughness of a specific cast stainless steel, i.e., the minimum value that would be achieved for the material after long-term service, is estimated from the chemical composition of the steel. Mechanical properties as a function of time and temperature of reactor service are estimated from impact energy and flow stress of the unaged material and the kinetics of embrittlement, which are also determined from chemical composition. The J{sub IC} values are determined from the estimated J-R curve and flow stress. Examples of estimating mechanical properties of cast stainless steel components during reactor service are presented. A common ``lower-bound`` J-R curve for cast stainless steels of unknown chemical composition is also defined for ...

International Nuclear Information System (INIS)

The influence of chemical composition and heat treatment on a low-carbon steel, chromium steel and high speed steel has been examined by polarisation curves and electrochemical parameters deduced from the Tafel plots. The electrochemical corrosion resistance, which is small between the as-received steels become greater after heat treatment, following the order: carbon steel < chromium steel #approx# high speed steel. To explain these differences, the nano- and microstructure of the steels has been characterized by the ex situ techniques of atomic force microscopy and optical microscopy, before and after surface etching with Nital (a solution of 5% HNO_3 in ethanol). This causes preferential attack of the ferrite phases showing the carbide phases more clearly. From these nanostructural studies it was possible to better understand why the passive films formed on chromium steel and high speed steel have superior protective properties to those formed on carbon ...

International Nuclear Information System (INIS)

The results of a combined investigation of splat-quenched Fe-Csub(x) (x<0.05) alloys by resistivity, X-ray diffraction and Moessbauer spectroscopy are presented. The residual resistivity increases linearly with the carbon content (#DELTA#rho=5#mu##OMEGA#cm/at.%) with a slope identical to that observed in the dilute ferritic phase. X-ray diffraction reveals the presence of a martensite structure in addition to a small fraction of residual austenite; the dependence of the a and c lattice parameters on xsub(c) agrees with earlier measurements. A detailed investigation of the relative reflexion intensities shows that the as-quenched martensites consist of a mixing of massive martensite and tetragonal martensite for low carbon content and of tetragonal martensite only for xsub(c) approximately 0.05. The Moessbauer spectra reveal 3 or 4 magnetically non equivalent iron sites. From a detailed analysis of the intensity dependence of the subspectra on carbon content the ...

Energy Technology Data Exchange (ETDEWEB)

Microstructural analyses by several advanced metallographic techniques were conducted on austenitic stainless steel mockup and core shroud welds that had cracked in boiling water reactors. Contrary to previous beliefs, heat-affected zones of the cracked Type 304L, as well as 304 SS core shroud welds and mockup shielded-metal-arc welds, were free of grain-boundary carbides, which shows that core shroud failure cannot be explained by classical intergranular stress corrosion cracking. Neither martensite nor delta-ferrite films were present on the grain boundaries. However, as a result of exposure to welding fumes, the heat-affected zones of the core shroud welds were significantly contaminated by oxygen and fluorine, which migrate to grain boundaries. Significant oxygen contamination seems to promote fluorine contamination and suppress thermal sensitization. Results of slow-strain-rate tensile tests also indicate that fluorine exacerbates the susceptibility of ...

International Nuclear Information System (INIS)

In this work we report a study of the induced changes in structure and corrosion behavior of martensitic stainless steels nitrided by plasma immersion ion implantation (PI"3) at different previous heat treatments. The samples were characterized by x-ray diffraction and glancing angle x-ray diffraction, scanning electron microscopy, energy dispersive x-ray spectroscopy, and potentiodynamic measurements. Depending on the proportion of retained austenite in the unimplanted material, different phase transformations are obtained at lower and intermediate temperatures of nitrogen implantation. At higher temperatures, the great mobility of the chromium yields CrN segregations like spots in random distribution, and the #alpha#"'-martensite is degraded to#alpha#-Fe (ferrite). The nitrided layer thickness follows a fairly linear relationship with the temperature and a parabolic law with the process time. The corrosion resistance depends strongly on chromium segregation from ...

International Nuclear Information System (INIS)

The inspection of PFR evaporator tubing, superheater and reheater tubing, and tube plate examinations, are described. Ferritic steel U tubes in the evaporator have been examined by an eddy current system operating at 400 kHz using flexible rotating probes. Surface defects as shallow as 0.1 mm can be detected and sized in the range 0.1 to 0.5 mm deep. An ultrasonic method is under development for wall thickness. Special test coil probes have been developed for examination of the type 316 stainless steel superheater and reheater tubing. Crack-life defects in the bore are detectable at approximately 10% wall thickness and 20% on the outside diameter. Tube plate examinations from the tube holes, have been conducted using eddy current probes which identify surface breaking cracks in the holes. For detecting curtain cracks between tube plate holes, ultrasonic compression wave probes have been used. (U.K.).

International Nuclear Information System (INIS)

In the present paper, the chemical composition of passive films formed on both phases of two types of duplex stainless steels (UNS S31803 and UNS S32304) is determined at the micro-scale using Auger electron spectroscopy (AES). Samples were either mechanically polished (down to diamond pastes) or electrochemically etched in acidic solutions. The micro-electrochemical behavior of samples was then determined in sodium chloride media by means of the electrochemical micro-cell technique (capillary diameters of 30 ?m). The results obtained were analyzed considering the passive film chemical composition. Quantitative relationships between electrochemical parameters and the distribution of chromium and iron in the oxide layer were found. Due to differences in mechanical properties between ferrite and austenite, a heterogeneous stress distribution is generated in both phases. A method based on thermal-mechanical simulation was used to quantify surface stress gradients and ...

Energy Technology Data Exchange (ETDEWEB)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically conductive and corrosion-resistant CrN or Cr{sub 2}N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of commercially available, high Cr (30-35 wt%) Ni-Cr alloys and a ferritic high Cr (29 wt%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effects for the Ni-Cr base alloys, but beneficial effects for the stainless steel alloy. Positive results from single-cell fuel cell testing are also presented. (author)

Energy Technology Data Exchange (ETDEWEB)

Fretting wear test in room temperature water was performed to evaluate the wear coefficient of CANDU (CANadian Deuterium Uranium) steam generator (SG) tube material (Alloy 800) against 410 type martensitic stainless steels. The main focus is to compare the wear behaviors between Alloy 800 and Inconel 690. Test conditions are 10{approx}30N of normal load, 200{approx}450mm of sliding amplitude and 30Hz of frequency. The result indicated that the wear rate of Alloy 800 was higher than those of Inconel 690 at various test condition such as normal loads, sliding amplitudes etc. From the results of SEM observation, there was little evidence of plastic deformation layer that were dominantly formed on the worn surfaces of Inconel 690. Also, wear particles in Alloy 800 were released from contacting asperities deformed by severe plastic flow during fretting wear. Main cause of wear rate between Alloy 800 and Inconel 690 may be due to the difference of hardness between martensitic and ...

Energy Technology Data Exchange (ETDEWEB)

This report summarizes work performed by Argonne National Laboratory on fatigue and environmentally assisted cracking (EAC) in light water reactors from January 1997 to June 1997. Topics that have been investigated include (a) fatigue of carbon, low-alloy, and austenitic stainless steels (SSs) used in reactor piping and pressure vessels, (b) irradiation-assisted stress corrosion cracking of Types 304 and 304L SS, and (c) EAC of Alloys 600 and 690. Fatigue tests were conducted on ferritic and austenitic SSs in water that contained various concentrations of dissolved oxygen (DO) to determine whether a slow strain rate applied during various portions of a tensile-loading cycle is equally effective in decreasing fatigue life. Slow-strain-rate-tensile tests were conducted in simulated boiling water reactor (BWR) water at 288 C on SS specimens irradiated to a low fluence in the Halden reactor and the results were compared with similar data from a control-blade sheath and ...

Science.gov (United States)

In this study, four API X80 pipeline steels were fabricated by varying Mo, Cr, and V additions, and their microstructures and crystallographic orientations were analyzed to investigate the effects of their alloying compositions on tensile properties and Charpy impact properties. Because additions of Mo and V promoted the formation of fine acicular ferrite (AF) and granular bainite (GB) while prohibiting the formation of coarse GB, they increased the strength and upper-shelf energy (USE) and decreased the energy transition temperature (ETT). The addition of Cr promoted the formation of coarse GB and hard secondary phases, thereby leading to an increased effective grain size, ETT, and strength, and a decreased USE. The addition of V resulted in a higher strength, a higher USE, a smaller effective grain size, and a lower ETT, because it promoted the formation of fine and homogeneous of AF and GB. The steel that contains 0.3 wt pct Mo and 0.06 wt pct V without Cr had ...

International Nuclear Information System (INIS)

The deposit of radioactive corrosion products in the cooling systems of nuclear reactors becomes a serious problem for the personnel of facilities. Crud has an important role in the process of depositing radioactive corrosion products. The main components of crud are hematite, magnetite, nickel ferrite and so on, and the particles of these oxide compounds are distributed in water. Most of the behavior of crud are still not known. As for the mechanism of the production of crud, the Potter-Mann model has been proposed. However, the precipitation process of iron ions in water is unknown. The crud is defined as the particles filtered by 0.45 micrometer millipore filters. However, it is not known whether there are crud particles smaller than this size. The crud particles can be adsorbed on the filters by the surface electrochemical interaction. The adsorption of cations to crud particles was studied. The adhesion of crud particles was investigated through some model ...

Energy Technology Data Exchange (ETDEWEB)

The significant technical and industrial aspects which have led to main coolant line (MCL) materials selection are addressed from a long term experience and operational practice point of view. They are based on the Siemens/KWU developed basic material concept for its nuclear power plants. It considers the choice of appropriate materials, the evaluation and qualification of the materials and the materials manufacturer, the use of appropriate semi-finished products, the tailoring of material and semi-finished products to the specific requirements of the various systems, the application of adequate manufacturing processes and the proof of the requirements by specifying proper tests and examinations. The main systems are assigned to safety classes in accordance with their safety relevance. Summarizing the operation time of nuclear power plants with ferritic MCL equipped by Siemens/KWU, more than 200 years of operation experience exist and no upgrading or replacement of ...

Energy Technology Data Exchange (ETDEWEB)

The precipitation hardened, ferrite-pearlite medium-carbon steels microalloyed with vanadium (AFP steels) have been developed over the last few years as materials allowing processing by controlled, continuous cooling down from forging temperatures, for achieving benefits such as reducing the number of required heat treatment and working processes and saving expensive alloying materials. Due to their cost-saving advantages, the steels rapidly have been accepted as an alternative material to the quenched and tempered steels and re particularly used for fabrication of automobile parts. Their drawbacks however are the lower yield strength, and low ductility and toughness as compared to the heat-treatable steels. The research project therefore was intended to enhance the properties of the microalloyed, medium-carbon steels and widen their applicability by establishing further and improving existing thermomechanical treatment processes that will considerably improve the ...

Energy Technology Data Exchange (ETDEWEB)

Three kinds of surface modifications were carried out on LiNi{sub 1/2}Mn{sub 3/2}O{sub 4} thin-films to improve the charge and discharge characteristics of LiNi{sub 1/2}Mn{sub 3/2}O{sub 4} positive electrodes. Among them, Zr(OBu){sub 4}/poly(methyl methacrylate) (PMMA)-treated LiNi{sub 1/2}Mn{sub 3/2}O{sub 4} thin-film electrodes showed charge and discharge efficiency of 80-84% in the first cycle, which was much higher than that for an untreated LiNi{sub 1/2}Mn{sub 3/2}O{sub 4} thin-film electrode (73%). The values of the charge and discharge efficiency were still higher than that for an untreated electrode after the 30th cycle. The charge and discharge curves gave two plateaus at around 4.72 and 4.76 V, which were very similar to those for the untreated electrode. Ac impedance spectroscopy revealed that the surface film resistance should not increase by Zr(OBu){sub 4}/PMMA treatment. XPS measurements suggest that a ...

International Nuclear Information System (INIS)

Thermally stable materials with low dielectric constant (k<3.9) are being hotly pursued. They are essential as interlayer dielectrics/intermetal dielectrics in integrated circuit technology, which reduces parasitic capacitance and decreases the RC time constant. Most of the currently employed materials are based on silicon. Low k films based on organic polymers are supposed to be a viable alternative as they are easily processable and can be synthesized with simpler techniques. It is known that the employment of ac/rf plasma polymerization yields good quality organic thin films, which are homogenous, pinhole free and thermally stable. These polymer thin films are potential candidates for fabricating Schottky devices, storage batteries, LEDs, sensors, super capacitors and for EMI shielding. Recently, great efforts have been made in finding alternative methods to prepare low dielectric constant thin films in place of ...

Energy Technology Data Exchange (ETDEWEB)

Fe{sub x}Zn{sub 1-x} alloys were electrochemically deposited on aluminum substrates from a sulfate bath. The K{beta}/K{alpha} x-ray intensity ratios of Zn and Fe in Fe{sub x}Zn{sub 1-x} thin films have been experimentally studied. The energy dispersive x-ray fluorescence (EDXRF) technique was used to measure K x-ray photons. Samples were excited by using 59.5 keV photons emitted by a 50 mCi {sup 241}Am radioactive source. The emitted K x-rays were detected by an Ultra-LEGe detector having a resolution of 150 eV at 5.9 keV. In addition, the effect of bath composition on the phase structure was investigated by x-ray diffraction (XRD) analysis. The composition of the thin films was analyzed by atomic absorption spectrometry analysis. Iron content was shown to strongly affect the structure of Zn-Fe alloys. It was found that the K-shell x-ray intensity ratio changed in Fe{sub x}Zn{sub 1-x} thin films for different values of x. ...

Energy Technology Data Exchange (ETDEWEB)

The long-term stability of pentacene thin-film transistors (TFTs) encapsulated with a transparent SnO{sub 2} thin-film prepared by ion beam-assisted deposition (IBAD) was investigated. After encapsulation process, our organic thin-film transistors (OTFTs) showed somewhat degraded field-effect mobility of 0.5 cm{sup 2}/(V s) that was initially 0.62 cm{sup 2}/(V s), when a buffer layer of thermally evaporated 100 nm SnO{sub 2} film had been deposited prior to IBAD process. However, the mobility was surprisingly sustained up to 1 month and then gradually degraded down to 0.35 cm{sup 2}/(V s) which was still three times higher than that of the OTFT without any encapsulation layer after 100 days in air ambient. The encapsulated OTFTs also exhibited superior on/off current ratio of over 10{sup 5} to that of the unprotected devices ({approx}10{sup 4}) which was reduced from {approx}10{sup 6} before aging. Therefore, the enhanced ...

Science.gov (United States)

Regional cortical thickness was evaluated using CIVET processing of 3D T1-weighted images (i) to compare the variation in cortical thickness between 33 participants with fetal alcohol spectrum disorders (FASD) aged 6-30 years (mean age 12.3 years) versus 33 age/sex/hand-matched controls, and (ii) to examine developmental changes in cortical thickness with age from children to young adults in both groups. Significant cortical thinning was found in the participants with FASD in large areas of the bilateral middle frontal lobe, pre- and post- central areas, lateral and inferior temporal and occipital lobes compared to controls. No significant cortical thickness increases were observed for the FASD group. Cortical thinning with age in a linear model was observed in both groups, but the locations were different for each group. FASD participants showed thinning with age in the left middle frontal, bilateral precentral, bilateral ...

Energy Technology Data Exchange (ETDEWEB)

Various methods for storing hydrogen have been examined in an effort to find ways to store hydrogen in increasingly smaller volumes with decreasing weight of the whole hydrogen storage system. Metal hydrides, in which hydrogen is chemically bound to a metal atom, are considered to be very promising candidates for hydrogen storage because they have high gravimetric and volumetric storage capacities. This study investigated the effect of different magnesium (Mg) and aluminium (Al) ratios on the absorption and desorption properties of thin films. Neutron reflectometry (NR) was used in this study to better understand the absorption and desorption properties of commercially promising hydrogen storage materials. The large negative scattering length of hydrogen atoms changes the reflectivity curve substantially, so that NR can determine the total amount of stored hydrogen as well as the hydrogen distribution along the film normal, with nanometer resolution. In order to ...

Energy Technology Data Exchange (ETDEWEB)

There is a growing interest in using {sup 242m}Am as a nuclear fuel. The advantages of {sup 242m}Am as a nuclear fuel derive from the fact that {sup 242m}Am has the highest thermal fission cross section. The thermal capture cross section is relatively low and the number of neutrons per thermal fission is high. These nuclear properties make it possible to obtain nuclear criticality with ultra-thin fuel elements. The possibility of having ultra-thin fuel elements enables the use of these fission products directly, without the necessity of converting their energy to heat, as is done in conventional reactors. There are three options of using such highly energetic and highly ionized fission products. - Using the fission products themselves for ionic propulsion. - Using the fission products in an MHD generator, in order to obtain electricity directly. - Using the fission products to heat a gas up to a high temperature for propulsion purposes. In this ...

Energy Technology Data Exchange (ETDEWEB)

In this study, WO{sub 3} thin films were grown on glass substrates using an aqueous solution containing tungstate (NH{sub 4}){sub 2}WO{sub 4} as precursor. The substrate temperature incremented from 250 to 500 deg. C, by steps of 50 deg. C. The structural properties were investigated using XRD, atomic force microscopy and scanning electronic microscopy techniques. Microprobe analyses showed that a balanced stoichiometric composition was obtained for thin films prepared at T{sub s} = 350 and 400 deg. C. The X-ray diffraction analyses showed different structure crystallography in function of the substrate temperature. Moreover, films deposited at 400 deg. C were annealed in air for 2 h at 450 and 500 deg. C, respectively and the structural changes due to heat treatment were studied. Finally, the optical properties of these films were carried out using optical measurements of transmittance T({lambda}) and reflectance R({lambda}) spectra in ...

Energy Technology Data Exchange (ETDEWEB)

In this work we present the electrical characterization of non self-aligned p-channel thin film transistors fabricated by using laser doping technique for source/drain contact formation and gate oxide deposited at room temperature by Electron Cyclotron Resonance Plasma Enhanced Chemical Vapour Deposition. These techniques are suitable for a very low temperature process for TFT fabrication. The output characteristics show a current increase at high drain voltage ('kink' effect) rather moderate, if compared to self aligned polysilicon TFTs, probably due to the gradual doping profile induced by laser doping process. After bias stress at low gate voltage and high drain voltage condition a strong reduction of kink current has been observed in the output characteristics at high drain voltage, whereas minor changes has been observed in the transfer characteristics. This behaviour is similar to what observed in n-channel Gate Overlapped ...

Energy Technology Data Exchange (ETDEWEB)

A method is described for converting radioactive alkali metal into a low level disposable solid waste material. The radioactive alkali metal is atomized and introduced into an aqueous caustic solution having caustic present in the range of from about 20 wt % to about 70 wt % to convert the radioactive alkali metal to a radioactive alkali metal hydroxide. The aqueous caustic containing radioactive alkali metal hydroxide and CO{sub 2} are introduced into a thin film evaporator with the CO{sub 2} present in an amount greater than required to convert the alkali metal hydroxide to a radioactive alkali metal carbonate, and thereafter the radioactive alkali metal carbonate is separated from the thin film evaporator as a dry powder. Hydroxide solutions containing toxic metal hydroxide including one or more metal ions of Sb, As, Ba, Be, Cd, Cr, Pb, Hg, Ni, Se, Ag and Tl can be converted into a low level non-hazardous waste using the ...

Energy Technology Data Exchange (ETDEWEB)

In this paper the authors present the first emitter efficiency results for the thin film 40 percent Er-1.5 percent Ho YAG (Yttrium Aluminum Garnet, Y3Al5O12) and 25 percent Ho YAG selective emitter at 1500 K with a platinum substrate. Spectral emittance and emissive power measurements were made (1.2 less than lambda less than 3.2 microns). Emitter efficiency and power density are significantly improved with the addition of multiple rare earth dopants. Predicted efficiency results are presented for an optimized (equal power density in the Er, (4)I[sub 15/2]-(4)I[sub 13/2] at 1.5 microns, and Ho, (5)I[sub 7]-(5)I[sub 8] at 2.0 micron emission bands) Er-Ho YAG thin film selective emitter.

Energy Technology Data Exchange (ETDEWEB)

Li{sub 1.3}Al{sub 0.3}Ti{sub 1.7}(PO{sub 4}){sub 3} thin films were successfully prepared by the solution deposition using lithium acetate, aluminum nitrate, ammonium dihydrogen phosphate and titanium butoxide as starting materials. The structure, surface morphology, electrochemical window, and ionic conductivity of the films were studied by X-ray diffraction, scanning electron microscopy, cyclic voltammetry and AC impedance. The results showed that Li{sub 1.3}Al{sub 0.3}Ti{sub 1.7}(PO{sub 4}){sub 3} thin films annealed between 750 deg. C and 900 deg. C prepared by this method were well crystallized, homogenous and crack-free. The electrochemical window was beyond 2.4 V and the ionic conductivity was approximately 1.57x10{sup -5} S/cm at room temperature for the film annealed at 800 deg. C for 30 min.

Energy Technology Data Exchange (ETDEWEB)

Vertical thin film evaporators have been used to concentrate and dry solutions because their rotating swing blades prevent scale from being deposited on the heated surfaces. Powdering capacity of the vertical thin film evaporator was examined experimentally for drying applications of radioactive liquid waste generated from nuclear power plants. As a result, it was found that the powdering capacity increased with the blade rotation, changing significantly in the low ratational region and scarcely in the high rotational region. The powdering capacity in the high rotational region was restricted by the lack of heat flux which was theoretically evaluated for the concentrating process. As the critical factor in the low rotational region was not clear, a visual test apparatus was made to observe flow patterns in the evaporator, and a powdering model was obtained. This model showed that powdering process was obstructed when the liquid film lost its ...

Environmental Research Database

ObjectivesThe overall scientific aim of this project is, through development of an appropriate numerical modelling tool, to identify and investigate the mechanisms that control the current observed rapid thinning and acceleration of Greenland outlet glaciers and to investigate their likely future behaviour in the context of climate warming. This aim is addressed through the four major specific objectives below. These objectives build on each and therefore the order of priority is driven by the order in wh [continued...]DescriptionCurrently, the Greenland ice sheet is undergoing rapid changes in the coastal regions which have been attributed to a general warming trend to the regions climate over the last decade. Several of the narrow and fast flowing outlet glaciers that drain the ice sheet into the sea are observed to have accelerated their flow and thinned. For instance, Jakobshavn Isbrae on the West coast of Greenland has almost doubled its ...

International Nuclear Information System (INIS)

We report a new method of generating nano and micro patterns using focused ion beam (FIB) induced adhesion. The method utilizes selective irradiation of thin metallic films grown on substrates by focused ion beam followed by peel off. After peel off of the irradiated thin film it is observed that the ion beam scanned portions are retained on the substrate, creating nano and micro patterns. The method is suitable for materials of which the adhesion to the substrate can be improved by ion bombardment. The phenomenon has been demonstrated by creating gold nano patterns of different shapes and sizes ranging from 500 nm to 5 #mu#m on SiO_2-Si substrate using 10-30 keV Ga FIB at beam currents up to 10 pA. The mechanism involved in the process has been discussed. The technique could be utilized to prepare micro and nano patterns of thin films deposited on an appropriate substrate for optical, plasmonic and sensor related ...

Energy Technology Data Exchange (ETDEWEB)

As the U.S. Department of Energy's (DOE's) Solar Energy Technologies Program initiates new cost-shared solar energy R&D under the Solar America Initiative (SAI), it is useful to analyze the experience gained from cost-shared R&D projects that have been funded through the program to date. This report summarizes lessons learned from two DOE-sponsored photovoltaic (PV) projects: the Photovoltaic Manufacturing Technology/PV Manufacturing R&D (PVMaT/PVMR&D) project and the Thin-Film PV Partnership project. During the past 10-15 years, these two projects have invested roughly $330 million of government resources in cost-shared R&D and leveraged another $190 million in private-sector PV R&D investments. Following a description of key findings and brief descriptions of the PVMaT/PVMR&D and Thin-Film PV Partnership projects, this report presents lessons learned from the projects.

Science.gov (United States)

The specification describes a semiconductor solar cell and fabrication process therefor wherein a thin N-type gallium arsenide layer is deposited on a larger P-type substrate layer which is selected from the group of III-V ternary compounds consisting of aluminum phosphide antimonide, AlPSb, and aluminum indium phosphide, AlInP. P-type impurities are diffused from the substrate layer into a portion of the thin N-type gallium arsenide layer to form P-type region wherein which defines a PN junction in the thin gallium arsenide layer. Thus, the quantity of gallium arsenide required to provide this PN photovoltaic junction layer in the cell is minimized, and th P-type substrate serves as a high bandgap window layer for the cell. Such high bandgap of this window material is especially well suited for efficiently transmitting the blue spectrum of sunlight to the PN junction, thus enhancing the power conversion efficiency of the ...

Energy Technology Data Exchange (ETDEWEB)

The passive films formed on iron metal, alloys or stainless steel are extremely thin oxides or hydroxides and possess the properties of high chemical stability in the environment. These films show characteristics interested both electrical as well as electrochemical point of view due to the thin thickness of the films. Auger Electron Spectroscopy, X-ray Photoelectron spectroscopy and so on which are the conventional electrochemical measurement methods or the surface analysis methods are used for the analysis and evaluation of these films, however, at present, the application of research technique focusing the superconductor characteristics of the films are tried. Although, the potential modulation reflection spectroscopy method has merits like possibility of in-situ measurement, high precision, possibility of stable analysis even for extremely thin film and so forth, it has also demerits like difficulty to response the ...

International Nuclear Information System (INIS)

In this work, the silicon oxynitride layer was studied as a tunneling layer for non-volatile memory application by fabricating low temperature polysilicon thin film transistors on glass. Silicon wafers were oxynitrided by only nitrous oxide plasma under different radio frequency powers and plasma treatment times. Plasma oxynitridation was performed in RF plasma using inductively coupled plasma chemical vapor deposition. The X-ray energy dispersive spectroscopy was employed to analyze the atomic concentration ratio of nitrogen/oxygen in oxynitride layer. The oxynitrided layer formed under radio frequency power of 150 W and substrate temperature of 623 K was found to contain the atomic concentration ratio of nitrogen/oxygen as high as 1.57. The advantage of high nitrogen concentration in silicon oxide layer formed by using nitrous oxide plasma was investigated by capacitance-voltage measurement. The analysis of capacitance-voltage characteristics demonstrated that ...

Energy Technology Data Exchange (ETDEWEB)

Theoretical work supported by this grant has lead to the concept of the specific pinning force Q and the development of new methods to sum elementary interaction forces to find Q. Pinning due to changes in transition temperature or thermodynamic critical field in thin layers (e.g., a grain boundary), is greatly reduced due to the proximity effect and the stress field interaction due to the dislocations in the grain boundary has been shown to be negligible. The crystalline anisotropy (CA) and electron scattering (ES) interactions have been computed for the first time for an arbitrary boundary. Experiments on niobium bicrystals, polycrystalline niobium thin foils doped with oxygen, lead-bismuth alloy thin films and lead-bismuth alloy films in which either lead or thallium has been allowed to diffuse down the grain boundaries and out into the grains provide evidence that confirms the predictions of the theory. These results ...

Science.gov (United States)

This report summarizes the results obtained under a contract from 1974 to 1977, focusing on silicide formation of thin metal films on a Si substrate. The main thrust of the effort was directed at: (1) Development of the data base on thin-film silicide formation, and the investigation of the influence of the Si substrate on the silicide formation. When taken in context with results of other studies, the data obtained exhibit a clear pattern of behavior among the various metal films, but the detailed picture appears to be complex; (2) Development of marker experiments by ion-implanted Ar or Xe markers; (3) Clarification of the role played by oxygen contamination in silicide formation; (4) Stability of silicide layers; (5) Reaction of metal layers with SiO/sub 2/; (6) Electrical characteristics of Pd/sub 2/Si; and (7) A computer program was written to synthesize backscattering spectra for thin-film samples composed of ...

International Nuclear Information System (INIS)

The initial thichnesses of feeder pipes in Wolsung-1 are analyzed to estimate status of feeder thinning. The assumption of the estimation is that feeders of same type are decreased to same thickness by bending and have same thickness after bending. Following three methods are used to estimated thicknesses of the remains besides 52 feeders with initial thickness data in Wolsung-1. First is the estimating initial thickness of same type in Wolsung-1 from initial thickness data of Wolsung-2, -3 and -4. Second is the finding average value of each type from 52 initial thickness data of Wolsung-1. Last is the finding the thickness-after-bending of Wolsung-1 from thickness decrease rate of each type by bending in Wolsung-2, -3 and -4. The first method is eliminated by thickness-before-bending of Wolsung-1 lower than that of Wolsung 2, 3 and 4. The thinning rates of 2nd and 3rd method are compared with the "CANDU Feeder FAC Rate Analysis model' ...

Energy Technology Data Exchange (ETDEWEB)

Thin film ultraviolet detectors based on hydrogenated amorphous silicon alloys are realized with different diode structures (PIN, NIP, PN, and NP). The PIN and NIP detectors exhibit higher sensitivity in the ultraviolet spectrum and a significant lower dark current in comparison to the PN or NP structures. The best detector performance was achieved with a 33 nm thick PIN diode. This detector shows a maximum of quantum efficiency of 36.3% at a wavelength of 310 nm. By varying the thickness of the semi-transparent Ag front contact the selectivity of the detectors with the quantum efficiency peak at 320 nm can be adjusted. Thus, the spectral sensitivity of the detector shifts from a broad UV to a selective UV-B spectrum. (orig.)

International Nuclear Information System (INIS)

This paper is concerned with the fracture analysis of thin cylindrical shells subject to secondary bending stresses with some degree of elastic follow-up. A P.Y.F.M. failure assessment route is utilised for an initial investigation. Results are presented graphically and indicate the differences obtained by considering the stresses as primary or secondary in nature. The Jsup(*) contour integral is computed from the results of a non-linear finite element analysis of a thermally loaded cracked cylinder. Comparison is made between Jsup(*) and the P.Y.F.M. failure criteria demonstrating the degree of conservatism in the latter. It is observed that LEFM may be appropriate for moderate load levels but that the elastic follow-up of the structure causes enhancement of Jsup(*) for higher loads, at which stage LEFM becomes non-conservative. (orig.).

British Library Electronic Table of Contents (United Kingdom)

A novel thin-film composite polyamide nanofiltration membrane was prepared through interfacial polymerization of polymeric polyamine polyvinylamine (PVAm) with isophthaloyl chloride (IPC) on a polysulfone supporting film. The composite membranes were prepared under different conditions and characterized in terms of chemical and morphological structures, surface zeta potential, pure water permeability, and rejection to different solutes including electrolytes and sucrose. The results showed that the membrane performance was significantly affected by the content of amine units of PVAm and the concentrations of PVAm and IPC. The increase of the content of amine units of PVAm and the concentration of IPC resulted in an augment in salt rejection and a decrease in permeability, while the increas...

British Library Electronic Table of Contents (United Kingdom)

Indium sulfide thin films consisting of porous network of nanoplatelets, have been deposited using chemical bath deposition (CBD) method onto the tin-doped indium oxide (ITO) coated glass substrate. Aqueous solutions of indium sulfate and thioacetamide have been used as indium and sulfur precursors. As a complexing agent, acetic acid was used. The chemically deposited indium sulfide thin films were examined for their structural, surface morphological and optical characterizations. The X-ray diffraction analysis revealed the formation of the cubic b-In2S3 onto the substrate. From scanning electron micrograph, it is observed that the surface of substrate is covered by nanoporous platelets type morphology. The optical studies showed a direct band gap of 2.84eV for indium sulfide platelets. Ph...

International Nuclear Information System (INIS)

The influence of hydrogen ion implantation into the channel polysilicon of polysilicon thin film transistors on gate oxide conductivity has been investigated. Data for effective tunnelling barriers at the gate oxide/channel polysilicon interface are presented. A value of 1.2eV for samples with boron doped channel polysilicon is calculated. For hydrogenated boron doped samples tunnelling barriers higher than 2.1 eV are obtained. The tunnelling barriers for phosphorus doped samples are impurity concentration dependent and decrease with increasing phosphorus concentration in the range 3 x 10"1"7 to 3 x 10"1"9 cm"-"3. (Author).