Energy Technology Data Exchange (ETDEWEB)

The kinetics of passive film formation on iron in borate buffer solution has been studied at different anodic potentials. The process of film growth has been found to occur in four distinct stages. About 80-90% of the total film thickness formed in 1h grows during the initial two stages which last for only 1-3s (depending upon potential). The electric field strength across the film is not constant but decreases with progressing film growth. The thickness of the film determined ellipsometrically is less than that calculated from the electric charge consumed. The process of anodic film formation is accompanied by the dissolution of iron which occurs over the whole range of potentials.

Energy Technology Data Exchange (ETDEWEB)

Passive films were formed on a high purity Fe-23 Cr alloy in acid sulfate solutions in the presence and absence of chloride ion. The resulting film composition was investigated by Auger depth profiling. The passivated samples were exposed to a 1M NaCl solution at a constant potential slightly above the critical pitting potential, and the current-time transient was measured in order to compare the relative stability of the different films. The results obtained suggest that the formation conditions influence the chloride content of the passive film and the breakdown behavior. Passive films formed in the presence of chloride contain and are slightly less stable towards breakdown. No chloride was found in films formed in sulfate and subsequently exposed to chloride well below the pitting potential.

Energy Technology Data Exchange (ETDEWEB)

The evolution of strain in the Pd-Si system during the growth of Pd{sub 2}Si thin films on Si (100) substrate has been followed in situ using a double optical beam technique. As was observed for the Pt-Si system, the reaction to form Pd{sub 2}Si yields a compressive intrinsic surface film stress as well as for the silicon-rich suicides as proposed by Angilello et al. [Thin Film Interfaces and Interactions, edited by J. Baglin and J. Poate (The Electrochemical Society, Pennington, NJ, 1980)]. A transmission electron microscopy analysis has revealed grain growth during the formation of Pd{sub 2}Si which cannot account for the compressive film stresses. The formation of silicide at the interfaces rather than the overall change in volume agrees with the sign of the stresses formed. 29 refs., 4 figs., 3 tabs.

International Nuclear Information System (INIS)

... 5. Formation of the annular two-phase flow regime, with a wavy film on the

Energy Technology Data Exchange (ETDEWEB)

The comprehension of passivity and its protective character against corrosion is closely connected with the electronic properties of passive films. Passive films formed anodically on carbon steel in borate/boric acid solution, pH 9.2, have been characterised by electrochemical impedance spectroscopy (EIS). Mott-Schottky plots and impedance measurements were made on films formed at different potentials and times. The investigation allowed the determination of the semiconductive properties of the films. The results of the capacitance response indicate that the passive films behave like highly doped n-type semiconductors, showing that the passive film properties are dominated by iron. The value of donors density (N {sub D}) for the passive film is of the order of 10{sup 21} cm{sup -3} and decreases with increasing formation ...

Energy Technology Data Exchange (ETDEWEB)

In the region of annular liquid film-mist flow, the behavior of the droplets formed from the liquid film and the rate of formation are the subjects to be clarified in connection with the forecast of dry-out point, which becomes a problem in the region of high dryness such as reactor cooling system and steam generators. Many researches have been performed on such problem in vertical tubes, but the characteristics in horizontal flow have not yet been sufficiently clarified. This series of research is to clarify various characteristics, such as the velocity of vapor phase, the flow rate distribution of droplets, the formation and adhesion of droplets and the structure of liquid film, in the region of liquid film-mist flow, where liquid film exists on the bottom of a horizontal rectangular channel, and vapor flow is accompanied by droplets. In ...

Energy Technology Data Exchange (ETDEWEB)

The state of lithium electrode surface after contact with triethylamine-modified propylene carbonate solutions of lithium perchlorate was studied using the pulse galvanostatic technique as well as methods of SIMS and electron microscopy. It was shown that amine added into the solutions stabilizes the state of lithium and prevents the formation of a secondary porous passive film on the lithium surface. Chemical composition of the primary film remains unchanged. Certain properties of passive films formed in electrolyte solutions studied were evaluated.

International Nuclear Information System (INIS)

It is well known that a protective film is formed on the graphite negative electrode in ethylene carbonate (EC) electrolyte solution. This film is lithium-ion conductive and protects the decomposition of the electrolyte solution. In the present paper, the electrode/electrolyte interfaces in lithium-ion rechargeable batteries were characterized by three-dimensional complex impedance plots, whose axes are real, imaginary parts and time. The film resistance R _s_e_i and charge transfer resistance R _c_t were determined for negative electrodes in EC/ethyl methyl carbonate (EMC) electrolyte solution, and the formation mechanisms of the interfacial film were discussed. Furthermore, the contributions of vinylene carbonate and ethylene sulfite, which are added into the electrolyte solution for the film formation, were investigated.

Energy Technology Data Exchange (ETDEWEB)

Depth resolved positron annihilation studies on Pd/Si thin film system have been carried out to investigate silicide phase formation and vacancy defect production induced by thermal annealing. The evolution of defect sensitive S-parameter clearly indicates the presence of divacancy defects across the interface, due to enhanced Si diffusion beyond 870 K consequent to silicide formation. Corroborative glancing incidence X-ray diffraction (GIXRD), Auger electron spectroscopy (AES) and Rutherford backscattering spectrometry (RBS) have elucidated the aspects related to silicide phase formation and Si surface segregation.

Energy Technology Data Exchange (ETDEWEB)

Carbon films have been made by a variety of techniques, including evaporation, sputtering, and laser or thermal pyrolysis of organic polymers. Polyacrylonitrile (PAN) is often used as a carbon precursor, since low-temperature thermo-oxidative pretreatment produces a material which can be pyrolyzed without loss of shape. This is the basis for the production of carbon fibers with good mechanical properties. We report here the formation of very thin films of carbon (500 to 1500 A) by pyrolysis of spin-cast PAN. Using this technique, large, conductive films can be made which are sufficiently robust to allow intact lift-off and transfer of the films from one substrate to another. Such films are chemically inert, but can be photolithographically patterned and etched with an oxygen plasma.

Energy Technology Data Exchange (ETDEWEB)

The formation and breakdown of the passive films on stainless steels are mainly controlled by ionic and electronic transport processes. Both these processes are in part controlled by the electronic properties of the oxide film. Consequently, it is vital to gain a detailed perception of the electronic properties of the passive films together with structural and compositional information for a comprehensive understanding of mechanisms behind passivity and localised corrosion. As a step towards this goal the passive films formed on two main austenitic stainless steels AISI 316L and AISI 304L in borate solution were characterised by in situ Raman spectroscopy and photocurrent spectroscopy coupled with electrochemical measurements. This revealed the formation of an Fe-Cr spinel as the dominant constituent in the passive films with more Cr ...

Energy Technology Data Exchange (ETDEWEB)

Passive films formed on Alloy UNS N06690 were investigated in simulated crevice chemistries. It was found the role of lead in corrosion processes is strongly dependent on the pH value of the testing solutions. At pH 1.5 the effect of lead is narrowly noticeable; while at pH 12.7, lead has a significant influence on the electrochemical performance of alloy UNS N06690. The lead alters the surface morphologies at both pH and account for higher hydroxide content in the surface film at pH 12.7. The lead incorporation hinders the formation of spinel oxides during the passivation in alkaline solution. Nanoindentation tests indicate a significant lead-induced degradation in the mechanical properties of passive films. The passivation degradation is attributed to detrimental effects of lead via interrupting the dehydration process and hindering the formation of protective layers on the alloy ...

British Library Electronic Table of Contents (United Kingdom)

This communication reports the formation of complex Langmuir monolayer at the air-water interface by charge transfer types of interaction with the water soluble N-cetyl Formula Not Shown -trimethyl ammonium bromide (CTAB) molecules doped with rosebengal (RB), with the stearic acid (SA) molecules of a preformed SA Langmuir monolayer. The reaction kinetics of the formation of RB-CTAB-SA complex monolayer was monitored by observing the increase in surface pressure with time while the barrier was kept fixed. Completion of interaction kinetics was confirmed by FTIR study. This complex Langmuir films at the air-water interface was transferred onto solid substrates at a desired surface pressure to form multilayered Langmuir-Blodgett films. Spectroscopic characterizations reveal some molecular lev...

Energy Technology Data Exchange (ETDEWEB)

Significant ion irradiation during film growth is required for the formation of cubic boron nitride (cBN) films. Meanwhile, a huge level of intrinsic stress possibly induced by the ion bombardment has been frequently reported to result in cracking and/or lack of adhesion of deposited cBN films. The present work has been performed to investigate the interfacial and/or the buffer layer structures with better matching to the cBN film by relaxation of the film stress using ion-beam-assisted deposition (IBAD). Boron nitride films have been synthesized on Si(100) wafer and tungsten carbide (WC) substrates by depositing boron vapor under simultaneous bombardment with nitrogen ions and nitrogen-argon mixture ions in the energy range of 0.5-10 keV. Cubic BN films with enhanced tribological properties have been explored by ...

International Nuclear Information System (INIS)

Moss-Schottky plots and photoelectrochemical measurements were made on films formed at different potentials on AISI 304 stainless steel in a borate/boric acid solution, pH 9.2. The results allowed the determination of the semiconductive properties and band structure of the films, which account for the existence of two kinds of films depending on the formation potential. For potentials below 0 V (SCE), the results point out for a film with an inverse spinel structure constituted by Cr-substituted magnetite with two donor levels. Above 0 V only one donor level is detected, which should be Fe"2 "+ on tetrahedral sites.

British Library Electronic Table of Contents (United Kingdom)

In this work, effects of coolant chemistry, including concentrations of chloride ions and ethylene glycol and addition of various ions, on corrosion of 3003 Al alloy were investigated by electrochemical impedance spectroscopy measurements and scanning electron microscopy characterization. In chloride-free, ethylene glycol-water solution, a layer of Al-alcohol film is proposed to form on the electrode surface. With the increase of ethylene glycol concentration, more Al-alcohol film is formed, resulting in the increase in film resistance and charge-transfer resistance. In the presence of Cl- ions, they would be involved in the film formation, decreasing the stability of the film. In 50% ethylene glycol-water solution, the threshold value of Cl- concentration for pitting initiation is within ...

International Nuclear Information System (INIS)

In this work, amorphous hydrocarbon (a-C:H) film deposition on metallic mirrors was studied during working shots in tokamak T-10 and at exposure in Ar/CHD3/D2 dc magnetron discharge in a special laboratory high vacuum setup. Analysis of film composition (including hydrogen content) was carried out using nuclear physical methods. Thickness and optical parameters (refractive and extinction coefficients) of the films were estimated by ellipsometry. Laboratory films can be characterized as soft a-C:H films in comparison with hard tokamak films (? = 1.2 and 1.8 g/cm3, respectively). For the first one, a linear dependence of deposition rate on mirror temperature was observed in a wide temperature range. The addition of methane into initial Ar/D2 magnetron gas mixture leads to an increase of deposition rate. The data obtained should be taken into account to prevent ...

Science.gov (United States)

This report summarizes the results obtained under a contract from 1974 to 1977, focusing on silicide formation of thin metal films on a Si substrate. The main thrust of the effort was directed at: (1) Development of the data base on thin-film silicide formation, and the investigation of the influence of the Si substrate on the silicide formation. When taken in context with results of other studies, the data obtained exhibit a clear pattern of behavior among the various metal films, but the detailed picture appears to be complex; (2) Development of marker experiments by ion-implanted Ar or Xe markers; (3) Clarification of the role played by oxygen contamination in silicide formation; (4) Stability of silicide layers; (5) Reaction of metal layers with SiO/sub 2/; (6) Electrical characteristics of Pd/sub 2/Si; and (7) A computer program was ...

Energy Technology Data Exchange (ETDEWEB)

The hydrogen evolution reaction (HER) was studied on Ni-P{sub x} electrodes containing 8 to 16 weight percent P prepared by potentiostatic deposition. The amount of P in the alloy varied with deposition potential. The activity of the electrodes was dependent on the P concentration, and the formation of a passive film. Cyclic voltametry was used to study the removal of this film. 3 refs.

International Nuclear Information System (INIS)

This report reviews the published literature on the anaerobic oxidation of iron in aqueous solutions which are of particular relevance to Swedish granitic groundwaters. The thermodynamics of iron corrosion in water are briefly considered. Following this the experimental data found in the literature are presented and discussed. Results were found for corrosion of iron in both pure water and solutions containing mineral salts. The literature work in the nature of the films formed on iron surfaces under anaerobic conditions is reviewed and the possible mechanisms of film formation are discussed. Conclusions are drawn on the factors most likely to influence and control film growth. 32 refs.

Energy Technology Data Exchange (ETDEWEB)

Pulsed laser deposition (PLD) is known for its capacity to reproduce a target composition on a substrate. The authors have used this deposition technique to produce thin films of transition metal chalcogenides. However, the deposits were always deficient in Te relative to the starting material (composed by a refractory metal (niobium) and a chalcogene (tellurium)). Variations of the interreticular distances have been observed with respect to fluence and substrate temperature. The authors show that spatial composition of the films is determined by a degree of crystallinity of deposit and by the reaction of formation of Te{sub 2} molecule within laser induced plume. Two kinds of deposits have been obtained: Nb{sub 5}Te{sub 4}-type thin films which have a one-dimensional structure and NbTe{sub 2}-type thin films which have a two-dimensional structure. While NbTe{sub 2} ...

Energy Technology Data Exchange (ETDEWEB)

The formation of ZnTe films was investigated on zinc substrates at 640 K by using the following ion exchange and chemical reaction processes,2Zn{sub (substrate)}+Te{sup 4+}{sub (inmoltensalts)}->2Zn{sup 2+}+Te{sub (onsubstrate)}Zn{sub (substrate)}+Te= {sub (onsubstrate)}-> ZnTe{sub (onsubstrate)}The Te{sup 4+} species was supplied to the substrate via the gas phase, vaporized from the eutectic LiCl-KCl molten salt containing TeCl{sub 4} (0.05-0.9 mol%). The phase of the films obtained depended on the reaction time and the TeCl{sub 4} content in the molten chloride. At low TeCl{sub 4} concentrations, ZnTe alloy was not formed over the entire surface even after 3.6 ks. On the other hand, at high TeCl{sub 4} concentrations, tellurium was detected in addition to the ZnTe compound during the first 0.3 ks of the reaction. By selecting appropriate TeCl{sub 4} concentrations and reaction times, a ZnTe ...

British Library Electronic Table of Contents (United Kingdom)

Purpose - This paper aims to discuss the procedures and methods developed at Washington State University to digitize and make accessible historic moving images. Design/methodology/approach - The paper describes the selection and the use of low-cost technologies to transfer analog film to digital formats. Issues related to the conversion, description, and online hosting of digital films are also addressed. Findings - Though the steps involved in digitizing film are not trivial, the benefits of access both for the public and archives staff outweigh the expense and labor involved. The procedures described in this paper involve low upfront costs and are sustained through cost recovery fees. Research limitations/implications - The focus of this paper is on managing, describing, and providing on...

Energy Technology Data Exchange (ETDEWEB)

The kinetics of the electropolymerization of 3-amino-1,2,4-triazole on a brass substrate in alkaline solution containing methanol was investigated using cyclic polarization, chronoamperometry, electrochemical impedance techniques and scanning electronic microscopy. The polymeric film was prepared by successive cycles of potential of a 60Cu-Zn electrode between 0 and 1.6 V. During the second cycle, the oxidation peak of the monomer disappears indicating the formation of the insulating film. We have also shown that the monomer oxidation reaction is essentially irreversible and controlled by a diffusion process. The protective effect of the film formed on brass has been studied in a 3%NaCl and 3%NaCl + S{sup 2-} solution. The results showed important inhibition efficiency, about 96% for 4 h of testing time.

Energy Technology Data Exchange (ETDEWEB)

Thin passive films formed on highly corrosion-resistant type-312L stainless steel, containing 20 mass% chromium and 6 mass% molybdenum, in 2 mol dm{sup -3} HCl solution at 293 K have been analyzed by glow discharge optical emission spectroscopy (GDOES). The stainless steel does not suffer pitting corrosion even in this aggressive solution, showing a wide passive potential region. The depth profiles obtained clearly show a two-layer structure of the air-formed and passive films: an outer iron-rich layer and an inner layer highly enriched in chromium. Alloy-constituting molybdenum is deficient in the inner layer of the passive films and is enriched in the outer layer, particularly at the active dissolution potential. The molybdenum species in the outer layer may retard the active dissolution of stainless steel, promoting the formation of stable passive films highly enriched in ...

Energy Technology Data Exchange (ETDEWEB)

Cathodic arc deposition is an established and industrially applied technique for the formation of nitrides (e.g. TiN); it can also be used for metal oxide thin film formation. A cathodic arc plasma source with the desired cathode material is operated in an oxygen atmosphere of appropriate pressure, and metal oxides of various stoichiometric composition can be formed on different substrates. We report here on a series of experiments on metal oxide formation by cathodic arc deposition for different applications. Black copper oxide has been deposited on accelerator components to increase the radiative heat transfer between the parts. Various metal oxides such as tungsten oxide, niobium oxide, nickel oxide and vanadium oxide have been deposited on ITO glass to form electrochromic films for window applications. Optical waveguide structures can be formed by refractive index variation ...

Energy Technology Data Exchange (ETDEWEB)

Nb{sub 2}O{sub 5} thin films were formed on aluminum foils by a sol-gel process in order to increase the capacitance of the aluminum foils which are used as aluminum electrolytic capacitors. Investigations focussed on the preparation and characterization of the coating solution, the formation of Nb{sub 2}O{sub 5} thin films on aluminum foils, and the heat treatment and anodization of the films. The phase transition and electrical properties, such as capacitance, leakage current, and withstand voltage of the Nb{sub 2}O{sub 5} thin films were also measured. The Nb{sub 2}O{sub 5} thin films annealed at temperatures below 550 degree C were found to be amorphous, but they were crystallized to the orthorhombic phase by annealing at temperatures higher than 580 degree C. The capacitance of the coated samples increased with an increase in the thickness of the formed ...

Energy Technology Data Exchange (ETDEWEB)

When nanometer scale holes (diameters of 50 to a few hundred nm) are imaged in a scanning electron microscope (SEM) at pressures in the 10{sup -5} to 10{sup -6} torr range, hydrocarbon deposits built up and result in the closing of holes within minutes of imaging. Additionally, electron beam deposition of material from a gas source allows the closing of holes with films of platinum or TEOS oxide. In an instrument equipped both with a focused ion beam (FIB), and an SEM, holes can be formed and then covered with a thin film to form nanopores with controlled openings, ranging down to only a few nanometers.

International Nuclear Information System (INIS)

Radioactive "3"1Si was used as a tracer to study silicon self-diffusion in thin film silicides of cobalt, nickel, palladium and platinum. The specimens were prepared by sequential electron beam evaporation of radioactive "3"1Si and of the metal onto cleaned silicon wafers. By vacuum annealing at the appropriate formation temperature a silicide about 250 nm thick containing a sharp radioactive band about 50 nm thick was generally formed. Subsequent heating above the formation temperature resulted in a spreading of the activity owing to silicon self-diffusion. Activity profiles in the silicides were measured by a combination of ion beam sputtering, radioactivity counting and Rutherford backscattering of charged nuclear particles. (orig.).

International Nuclear Information System (INIS)

The effect of phosphorus on the corrosion resistance of Al-bronzes is studied in detail in this work. A literature review showed that there are a lot of things known about the microstructure and the mechanical properties of Al-bronzes. In spite of their corrosion resistance the corrosion properties and the structure of the protective oxide films of Al-bronzes were seldom a matter of interest. Systematic studies of the influence of different alloying elements on the oxide film and the corrosion properties are rare. Therefore, it is not possible to predict the corrosion resistance of Al-bronzes, made by alloying particular elements. The high corrosion resistance of the new alloy CuAl_2_0P_1 was the reason to investigate the influence of phosphorus on the corrosion properties of Al-bronzes in more detail. A systematic study of the microstructure and the corrosion properties of Cu, CuP_x, CuAl_2_0 and CuAl_2_0P_x offers an insight into the effect ...

International Nuclear Information System (INIS)

Ultrathin solid polymer electrolyte membranes containing sulfonic ester groups were prepared by polymerization of methyl benzenesulfonate and octamethylcyclotetrasiloxane in a glow discharge plasma. The sulfonic ester groups of the plasma polymer were transformed to lithium sulfonate groups by treatment with lithium iodide. Hybridization of this plasma polymer containing the lithium sulfonate groups with poly(ethylene oxide) (average Mw 300) resulted in the formation of a single lithium ion conductive film. The hybrid polymer electrolyte films were about 1 #mu#m thick, pinhole-free, adherent to various substrates, and showed ionic conductivities at 60 degrees C of the order of 10"- "6 S cm"- "1 (10"2 #OMEGA# cm"2 resistance per unit area of as-prepared solid polymer electrolyte). This material shows promise for electrochemical applications such as all solid-state lithium batteries, sensors, and electrochemical display ...

Energy Technology Data Exchange (ETDEWEB)

Nano-wire arrays of Niobium were produced by small angle sputtering on facetted sapphire, using the self shadowing effect of the facets. A wire width of about 80 nm was adjusted, the mean (maximum) wire height was about 20 nm (30 nm), the length can be in the cm range. Meander-film morphologies of 20 nm mean (26 nm maximum) thickness were produced by conventional sputtering onto smooth sapphire substrates at elevated temperatures. The morphology of the wires was investigated with atomic force microscopy (AFM), using contact mode. Meander-films were studied by scanning tunnelling microscopy (STM). Hydrogen loading was performed by instantaneously increasing the hydrogen gas pressure above the solubility limit. Thus, an elongated hydride could be monitored in an about 30 nm thick wire. STM studies on meander-films show the presence of cylindrical hydrides. Local out-of-plane and in-plane expansion can be explained by the ...

International Nuclear Information System (INIS)

The interaction of free electrons in the energy range from 0 to 10 eV with molecules at different stages of aggregation is investigated. The mechanism in the gas phase under single collision conditions is described. Fullerenes C_6_0 and C_7_0 are used as targets. Electron impact on condensed molecules can lead to temporary negative ions. The formation of Cl"- from gas phase CCl_4 and the desorption of Cl"- from 6 monolayer CCl_4 film on an Au substrate is determined experimentally. (Suda).

Energy Technology Data Exchange (ETDEWEB)

Contamination of the lube-oil with hard abrasive particles leads to a three-body abrasive wear mechanism that highly accelerates piston ring/cylinder liner wear in coal-fueled diesel engines. One approach to reducing that wear is to modify the size and orientation of surface asperities on the cylinder to enhance the formation of a hydrodynamic film, and to provide avenues of escape for particles that would otherwise be trapped in the wear zone. Another approach is to introduce additives into the contaminated lube-oil that further enhance hydrodynamic film formation, form chemical films on the wearing surfaces, or form films on the contaminant particles. This work focuses on defining the effects of cylinder liner surface finish, various configurations of slots in the cylinder liner surface, and various additives in the contaminated lube-oil on the wear process. ...

International Nuclear Information System (INIS)

Corrosion resistance of Cu-W system condensates in tap water was studies. It is shown that with an increase in W concentration in the condensates of the Cu-W system their corrosion in tap water enhances. In the material designated for power supply facilities the optimal tungsten content is up to 6%. Owing to formation of oxide film on the surface of the samples corrosion is stabilitized 40 h after the test start.

International Nuclear Information System (INIS)

The changes in microstructure of a specially prepared boron nitride (BN) film as a function of film depth were studied by high resolution transmission electron microscopy (HRTEM) and other materials analysis tools. These changes were then correlated to the changes in processing parameters during film growth. The analyzed film was fabricated by the four-step ion-assisted deposition procedure known to be effective in film-stress engineering for the formation and retention of a thick cubic BN (cBN) layer with a three-step buffer-layer deposition. In this deposition, the energy of the ions assisting cBN formation was increased stepwise from 200 to 280, and then to 360 eV [S.F. Wong, C. W. Ong, G.K.H. Pang, K.Z. Baba-Kishi, W. M. Lau, J. Vac. Sci. Technol. A 22 (2004) 676]. The nominal thickness of the cBN layer was 650 nm and that for each of ...

International Nuclear Information System (INIS)

In situ spectroscopic ellipsometry was employed to investigate the initial regime of rare earth metal (REM) conversion coatings formation on AZ31 magnesium alloy. Three REM salts solutions, 0.05 mol.dm"-"3 Ce(NO_3)_3, La(NO)_3 and Sm(NO)_3 solutions, were used for REM conversion coatings preparation. By deconvoluting the ellipsometric data, the surface of the fresh well-polished AZ31 magnesium alloy was found to be covered with 15.80 nm thick native (hydr)oxide film; the refractive indices and the thickness of Ce, La and Sm conversion coatings were obtained. The formation kinetics of three REM coatings follows different exponential functions and the coatings exhibit different optical properties. La conversion coating has the largest n values and the lowest k values while Sm conversion coating is just opposite. Moreover, the pH variation of the bulk conversion solutions upon the coatings formation was ...

Energy Technology Data Exchange (ETDEWEB)

The tribo characteristics of self-lubricating 40-mm-bore ball bearings with a retainer of glass cloth-polytetrafluoroethylene (PTFE) laminate, which has elliptical pockets with a large pocket clearance, were tested under thrust loads at speeds up to 50,000 rpm, 2 million DN, in liquid hydrogen (LH2) and in liquid nitrogen (LN2). During testing, the bearing torque, outer-race temperature, and electric resistance between the inner and outer races were monitored to verify the formation and rupture of a PTFE transfer film. Testing showed that the bearings having the elliptical retainer pockets were superior to the conventional bearings with circular pockets. It was determined that, at the maximum inner race spinning velocity of about 5 m/s, a PTFE transfer film could sustain the maximum Hertz stress, up to about 2000 N/sq mm, in LH2, without severe film rupture resulting in bearing seizure. In LN2, the ...

Energy Technology Data Exchange (ETDEWEB)

The effect of electron and ion beam irradiation on the Sisub(LVV) Auger spectra of SiO/sub 2/, Si/sub 3/N/sub 4/ and Si-oxynitride films was measured by the relative intensity of the 92 eV signal, characteristic for the formation of 'free' silicon during irradiation. While in Si-oxynitride the beam effects were almost negligible, some damage was found in Si/sub 3/N/sub 4/, but SiO/sub 2/ appeared to be extremely sensitive for electron and ion beam irradiation. By low energy electron loss spectroscopy of ion bombarded SiO/sub 2/ and Si/sub 3/N/sub 4/ films new electron states due to broken Si-O and Si-N bonds could be determined within the band gap of the insulators. The measured energy losses were interpreted by means of electron energy level schemes of the amorphous films.

Energy Technology Data Exchange (ETDEWEB)

The passivity and breakdown of passivity of 1018 carbon steel in propylene carbonate (PC) and 1,2-dimethoxyethane (DME) mixtures with 0.5 molar lithium hexafluoroarsenate supporting electrolyte were examined via several electrochemical and surface analytical methods. The PC-DME/0.5 M LiAsF{sub 6} mixtures ranged from 10 to 90 mol % PC. The results from the PC/DME mixtures were compared to passivating mechanisms found in pure PC and DME solutions. In PC-rich mixtures, the breakdown of passivity occurred near the oxidation potentials of either organic solvent. Premature breakdown of the carbon steel in PC-DME mixtures occurred at sulfide inclusions as was observed earlier in PC/0.5 M LiAsF{sub 6} solutions although passive films attempted to form at these inclusion sites in mixtures containing at least 10 mol % DME. As the DME content increased in the PC-DME mixtures, the passive films formed on bare steel surfaces possessed an increasing polymer ...

International Nuclear Information System (INIS)

The potentiodynamic polarization measurement of 254SMO stainless steel (UNS 31254) was conducted in 3.5% NaCl solutions with pH ranging from 0.1 to 5. The results indicated that this stainless steel offered excellent pitting corrosion resistance in corrosive environments. Further, it also exhibited various features on the polarization curves in different pH solutions. The electrochemical constant-potential passivation treatment performed at different pH followed by XPS analysis revealed that the primary constituents of the outermost layer of the passive films formed in the weak (pH 5) and strong (pH 0.8) acid solutions are iron oxides and Cr_2O_3 and Cr(OH)_3, respectively. Molybdenum oxides, primarily in the six-valence state, existed in the outermost layer of the passive film. Only very weak signals corresponding to that of nickel oxides were detected in the film formed in the weak acid (pH 5) solution. The ICP-MS ...

International Nuclear Information System (INIS)

Surface analytical studies of high nitrogen austenitic stainless steels exposed to deaerated 0.1M HCl have revealed that nitrogen alloying additions influence the composition of salt layers and the passive film/alloy interface. In this study the authors employ electrochemical techniques and variable angle X-ray Photoelectron Spectroscopy (XPS) to examine the passive films formed on a series of austenitic stainless steels, Fe18Cr8Ni, Fe18Cr8Ni0.2N, Fe20Cr20Ni, Fe20Cr20Ni6Mo and Fe20Cr20Ni6Mo0.2N, in acidic chloride aqueous solution. In addition, several other model alloys, Fe19Cr, Fe19Cr9Ni, Fe19Cr2.5Mo, and Fe19Cr9Ni2.5Mo, were examined before and after electrochemical surface nitriding, a technique proven to have an effect analogous to N alloying. It was shown that nitrogen, nickel and molybdenum additions independently and in certain combinations stimulate selective dissolution of iron, resulting in a significant enrichment of chromium ...

International Nuclear Information System (INIS)

A wide variety of thin film coatings, deposited by different techniques and with potential applications in various important areas, have been characterised by the Phase Modulated Spectroscopic Ellipsometer, installed recently in the Spectroscopy Division, B.A.R.C. The Phase Modulated technique provides a faster and more accurate data acquisition process than the conventional ellipsometry. The measured Ellipsometry spectra are fitted with theoretical spectra generated assuming an appropriate model regarding the sample. The fittings have been done objectively by minimising the squared difference (#chi#"2) between the measured and calculated values of the ellipsometric parameters and thus accurate information have been derived regarding the thickness and optical constants (viz, the refractive index and extinction coefficient) of the different layers, the surface roughness and the inhomogeneities present in the layers. Measurements have been done on (i) ion-implanted ...

Energy Technology Data Exchange (ETDEWEB)

The properties of AlN make this material very attractive for optical, electronic, and tribological application. Also, if the AlN could be formed on the Al surface to enhance its surface properties, Al could be applied for the lightening of machine parts. However, a dense oxide film exists on the surface of Al, which prevents the formation of the Al nitride even during plasma nitriding and plasma coating process. In this study, plasma nitriding has been tried to form an AlN layer on Al after the surface activation processes. During the plasma nitriding, the density of the nitrogen ions was amplified by means of controlling the power of the Al substrates. The film thickness, microstructural features and the mechanical properties such as hardness and wear properties of the AlN layer were examined as a function of the process parameters of pretreatment and plasma nitriding

British Library Electronic Table of Contents (United Kingdom)

Indium sulfide thin films consisting of porous network of nanoplatelets, have been deposited using chemical bath deposition (CBD) method onto the tin-doped indium oxide (ITO) coated glass substrate. Aqueous solutions of indium sulfate and thioacetamide have been used as indium and sulfur precursors. As a complexing agent, acetic acid was used. The chemically deposited indium sulfide thin films were examined for their structural, surface morphological and optical characterizations. The X-ray diffraction analysis revealed the formation of the cubic b-In2S3 onto the substrate. From scanning electron micrograph, it is observed that the surface of substrate is covered by nanoporous platelets type morphology. The optical studies showed a direct band gap of 2.84eV for indium sulfide platelets. Ph...

International Nuclear Information System (INIS)

Transmission electron microscopy and x-ray diffraction data show that rapid thermal anneals of SrS:Ce thin films enhance grain size and reduce crystalline defects. Electron paramagnetic resonance results suggest that these anneals lead to less variance in the crystal field environments at the nearly cubic Ce"3"+ sites along with the formation of another type of Ce"3"+ site believed to involve a nearby Sr vacancy. We suggest that the association of Ce"3"+ sites with V_S_r shifts the electroluminescence towards larger wavelengths as the symmetry of the activator site is lowered. copyright 1997 American Institute of Physics.

Science.gov (United States)

We adapt the Jain-Taylor (2003) shear-ratio geometric lensing method to measure the dark energy equation of state, w = pv/?v and its time derivative from dark matter haloes in cosmologies with arbitrary spatial curvature. The full shear-ratio covariance matrix is calculated for lensed sources, including the intervening large-scale structure and photometric redshift errors as additional sources of noise, and a maximum likelihood method for applying the test is presented. Decomposing the lensing matter distribution into dark matter haloes we calculate the parameter covariance matrix for an arbitrary experiment. Combining with the expected results from the cosmic microwave background (CMB) we design an optimal survey for probing dark energy. This shows that a targeted survey imaging 60 of the largest clusters in a hemisphere with five-band optical photometric redshifts to a median galaxy depth of zm = 0.9 could measure w0 ? w(z = 0) to a marginal 1? error of ?w0 = 0.5. We marginalize over ...

Energy Technology Data Exchange (ETDEWEB)

The morphological aspects of ternary phase formation during the Pd-GaAs reaction have been studied by application of transmission electron microscopy (TEM) and Rutherford backscattering (RBS) techniques. The TEM images show that the first product phase, ''phase I'', forms during deposition of Pd onto (100) GaAs and exhibits the preferred orientation (0001)/sub I/ approx. // (01 anti 1)/sub GaAs/. In the presence of unreacted Pd, the second phase, ''phase II'', nucleates at large-angle grain boundaries in the phase I film as the annealing temperature increases above approx.250C. Energy dispersive analysis of x-rays and RBS suggest the nominal compositions Pd3GaAs and Pd4GaAs for phases I and II, respectively.

International Nuclear Information System (INIS)

By using megaelectronvolt "4He ion backscattering techniques and transmission electron microscopy, the authors have investigated the interactions of ion beams with thin film structures in a number of silicide-forming systems. The mixed layer was found to be an equilibrium compound for near-noble metals and an amorphous phase for refractory metals. Differences in behavior have also been observed in near-noble metal systems. For palladium, the Pd_2Si phase grew with ion dose and remained crystalline up to high dose. For nickel, the compound Ni_2Si was formed initially and became amorphous on prolonged irradiation. All the results indicate the significance of atomic mobility at target temperatures in determining the phase formation and in explaining the sensitivity of the silicides to ion bombardment. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

Dominating factors in plasma nitriding and plasma condition that makes nitriding possible in plasma nitriding process of metals having hard oxide film were studied. In case of stainless steel, oxide film sputtering was easier comparing to nitriding layer. Three phenomena such as sputtering of oxide layer, formation of nitriding layer and sputtering of nitriding layer occurred simultaneously. Nitriding was achieved when the formation of nitriding layer reached the peak comparing to the removal of nitriding layer after the removal of oxide layer. Situations of metallic surface of stainless steel in surface nitriding were divided into four categories and they were, situation where oxide layer remained as it is, situation where nitriding layer was formed although oxide layer remained in some part, situation where only nitriding layer was formed and situation where sputtering was carried out. It was revealed ...

Energy Technology Data Exchange (ETDEWEB)

In this work we present the electrical characterization of non self-aligned p-channel thin film transistors fabricated by using laser doping technique for source/drain contact formation and gate oxide deposited at room temperature by Electron Cyclotron Resonance Plasma Enhanced Chemical Vapour Deposition. These techniques are suitable for a very low temperature process for TFT fabrication. The output characteristics show a current increase at high drain voltage ('kink' effect) rather moderate, if compared to self aligned polysilicon TFTs, probably due to the gradual doping profile induced by laser doping process. After bias stress at low gate voltage and high drain voltage condition a strong reduction of kink current has been observed in the output characteristics at high drain voltage, whereas minor changes has been observed in the transfer characteristics. This behaviour is similar to what observed in n-channel Gate ...

Energy Technology Data Exchange (ETDEWEB)

The Raywell Process Plants unit, which reclaims a wide range of organic solvents, including chlorinated hydrocarbons, is based on thin film evaporation and distillation rather than steam distillation, thus reducing the risk of contamination by water. Henry Balfour and Co.'s Pfaudler Solvent Recovery System gives 96% or better solvent recovery and produces a near-solid waste suitable for landfill disposal; like the Raywell system, it uses a mechanically wiped thin-film evaporator. Midland Oil Refineries uses sa Raywell thin-film evaporator for recovery of waste lubricating oils rather than the conventional sulfuric acid/clay treatment, thus avoiding formation of sulfuric acid sludge waste. The Henry Balfour Bioenergy anaerobic digestion system gives yields of fuel gas with 65-75% methane as high as 0.8 cu m/kg BOD; it achieves 95-98% BOD removal with no pH control or nutrient addition because it ...

Energy Technology Data Exchange (ETDEWEB)

The open circuit potential (OCP) of stainless steels immersed in natural waters generally increases with time. This phenomenon is strongly linked to the formation of a bio-film on the surface. Several studies have proved that the bio-film modifies the reaction of reduction of dissolved oxygen and that it acts mainly on the cathodic processes. One of the hypotheses explaining the action of the bio-film involves certain bacteria which use dissolved oxygen and extracellular enzymes to produce reactive oxygen species. Among this kind of metabolites is hydrogen peroxide H{sub 2}O{sub 2}. This compound interacts with the passive layer of stainless steels and affects their electrochemical behaviour, even when the chloride concentration is low. The aim of this work is to study the influence of an enzymatic reaction (of the oxidoreductase type) on anodic and cathodic processes on AISI 316L stainless steel. ...

International Nuclear Information System (INIS)

Specimen strips of pure alpha titanium and beta titanium alloy were exposed to a range of up to 46 deuterium plasma discharges in the Princeton Large Torus Tokamak (PLT) under simulated first wall conditions, and the amount of trapped deuterium in these specimens was measured, using carbon as a calibration standard for trapping. The Deuterium Nuclear Microprobe was used to study the total trapped deuterium and the deuterium depth distribution in the exposed materials before and after annealing at 373 and 423"0K. The Scanning Auger Microprobe was used to identify the effects of surface impurities on the deuterium distribution. Results indicate that about 20 to 40% of the incident deuterium was trapped by the surface and about 90% of the trapped deuterium remained in a 20A carbonaceous film deposited during plasma exposure. Annealing resulted in a gradual loss from the film. These results indicate the importance of impurity ...

International Nuclear Information System (INIS)

The application of medium energy ion scattering in combination with channelling and blocking to the study of the initial stages of palladium silicide formation is discussed. After a brief description of the experimental arrangement and method, the effects on the Rutherford backscattering spectra of depositing small quantities of palladium on clean Si(111) are reported. The uniformity and thermal stability of thin palladium silicide films grown at room temperature were measured. Finally, channelling and blocking results were used to carry out a structural analysis of thin epitaxial Pd_2Si layers. (Auth.).

International Nuclear Information System (INIS)

Repassivation resulting from the bared metal surface is a critical process for judging whether or not material suffers from corroding or immunizing. Nickel based alloys with high chromium content were developed to increase the corrosion resistant to sulphur compounds. Active humps resulting from active dissolution of nickel were obtained by creating the bared metal surfaces in thiosulphate solutions. The lower the Cr content the higher is the dissolution rate. The passive films formed on the bared metal surface were examined by ac impedance. Results suggest the formation of multi-layers oxide which were affected by active dissolution reactions during repassivation. (author).

Energy Technology Data Exchange (ETDEWEB)

Surface layers on lithium electrodes formed in several solvents including dimethyl carbonate (DMC), diethyl carbonate (DEC), polyethylene glycol 400 dimethyl ether (PEG400DME), and propylene carbonate (PC) have been studied by Raman spectroscopy. Both DMC and DEC were used singly, and also mixed with either methyl acetate or methyl formate. The Raman spectra showed that passive films formed on the Li surface in different solvents may have different chemical structures, which changed during the charging and discharging processes. A solid film of fullerene C6O, which could be used as a cathode in Li rechargeable batteries, was examined in the PEG400DME solution by both electrochemical and Raman spectroscopy. Cyclic voltammograms (CVs) showed five redox peaks which suggested the formation of C6O(-), C6O(2-), C6O(3-), C6O(4-), and C6O(5-). Raman spectra obtained from thin C6O film ...

International Nuclear Information System (INIS)

A combined application of several microtechniques is presented and discussed with the Ti/TiO_2 and Zr/ZrO_2-systems as an example. All measurements were carried out on single grains of technical materials in order to detect and quantify the effect of substrate microstructure on the properties of anodic passive films formed potentiodynamically in 0.5 M H_2SO_4 (dU/dt = 20 mVs"-"1). Anisotropy-micro-ellipsometry (AME) was employed to determine the crystallographic orientation of the substrate grains along with passive film thickness and crystallinity in dependence on the anodization potential. Both the isotropic (amorphous) TiO_2- and the anisotropic (crystalline) ZrO_2-films exhibit a systematic dependence of film thickness on the grain orientation. Local LASER-scanning photocurrent measurements (#lambda#=257 nm) on the same grains likewise show a heterogeneity of the photoelectrochemical reactivity in ...

Energy Technology Data Exchange (ETDEWEB)

In situ scanning tunneling microscopy has been used to study the nucleation and growth mechanisms and the structure of passive films formed on Cu(111) surfaces in 0.1 M borate buffer solution (pH 9.3). A surface topography characterized by terraces with monoatomic steps is obtained after potentiodynamic reduction down to {minus}1.12 V/standard hydrogen electrode (SHE), of the electropolished surface exposed to air. The formation of a single Cu{sub 2}O passive layer at 0.03 V/SHE proceeds first by a roughening of the steps assigned to a locally blocked step flow process due to a competition between dissolution and preferential nucleation of the oxide at the steps. The observed oxide nuclei are 2--3 nm wide and about one atomic plane high. This process leads to the complete coverage of the terraces by a grain-like structure of the oxide film. The initial terrace topography is completely altered. Thickening of this oxide layer ...

Science.gov (United States)

We have grown crack-free antiferroelectric (AFE) Pb{sub 0.92}La{sub 0.08}Zr{sub 0.95}Ti{sub 0.05}O{sub 3} (PLZT) films on nickel foils by chemical solution deposition. To eliminate the parasitic effect caused by the formation of a low-permittivity interfacial oxide, we applied a conductive buffer layer of lanthanum nickel oxide (LNO) on the nickel foil by chemical solution deposition prior to the PLZT deposition. Use of the LNO buffer allowed high-quality film-on-foil capacitors to be prepared at high temperatures in air. With the AFE PLZT deposited on LNO-buffered Ni foils, we observed field-induced phase transformations of AFE to ferroelectric (FE). The AFE-to-FE phase transition field, E{sub AF} = 260 kV cm{sup -1}, and the reverse phase transition field, E{sub FA} = 220 kV cm{sup -1}, were measured at room temperature on a {approx}1.15 {micro}m thick PLZT film grown on LNO-buffered Ni foils. The ...

Energy Technology Data Exchange (ETDEWEB)

'Improvement in understanding of the deposition of ambient dust particles on ECAM (Environmental Continuous Air Monitor) filters, reduction of the alpha-particle interference of radon progeny and other radioactive aerosols in different particle size ranges on filters, and development of ECAM''s with increased sensitivity under dusty outdoor conditions. As of May 1, 1998 (1/2 year into the project) the research-prototype 30-cm pulsed ionization chamber (PIC) is assembled and operational with an alpha particle energy resolution of better than 45 keV for 5-MeV alpha particles. Measurements of spectral resolution for alpha particles from radon decay products have been made as a function of filter type and dust loading conditions. So far, a study of ten filter types has found that the best combination of resolution and throughput is obtained with 3.0 \\265m Millipore fluoropore and 1.0 \\265m Corning FNMB filters. Experiments with gypsum and Portland cement dust ...

Energy Technology Data Exchange (ETDEWEB)

The aim of this work is the comparative study of the properties of the natural graphite/liquid organic electrolyte interface by impedance spectroscopy with respect to different lithium salts (LiX with X = ClO{sub 4}{sup -}, BF{sub 4}{sup -}, CF{sub 3}SO{sub 3}{sup -}, N(CF{sub 3}SO{sub 2}){sub 2}{sup -}, PF{sub 6}{sup -}). The evolution of the interface properties during the first electrochemical reduction suggests different mechanisms of formation of passivation films. A more stable, thin and homogenous film seems to develop when the LiN(CF{sub 3}SO{sub 2}){sub 2} or LiPF{sub 6} lithium salts are used. The chemical diffusion coefficient of lithium in graphite has been determined by impedance spectroscopy. (J.S.) 16 refs.

Energy Technology Data Exchange (ETDEWEB)

The durability of ball bearings, 32-mm- and 45-mm-bore, with a retainer or glass cloth-polytetrafluoroethylene (PTFE) laminate was tested under a high radial load at a speed of 20,000 rpm in LOX or LN2. The retainers were characterized as good self-lubricators because the abrasive glass-cloth fiber tips exposed on the retainer were chemicaly etched away with hydrofluoric acid (HF). During testing, the bearing-cartridge-acceleration was monitored to detect bearing damage. Testing in LOX for about 2.2 hr showed that excellent lubricating conditions were obtained for all bearings. Testing in LN2 for about 5.1 hr detected that the fatigue life of the bearing was about the same as the calculated B10 fatigue life. The HF chemical treatment resulted in a reacted fluoride-oxide material which remained in the etched part of the glass fiber. Several chemical products, particularly MgO, CaO, and CaCO3, enhanced adhesion of PTFE transfer film to the counterface, resulting in ...

Energy Technology Data Exchange (ETDEWEB)

In the nuclear power stations of GDR the rough radioactive waste includes borat-containing evaporator bottoms and spent ion exchanger resins. For its final disposal in deep geological formations (rock salt mines) this waste has to be solidified. The experience of one year lasting operation of a steam heated thin-film evaporator (heating surface 2 m{sup 3}) for evaporator bottoms to be solidified with a solid content of 200-250 g/l are reported on. In short time such amount of water is abstracted from the rough waste that due to the borate content a hot high-viscous product passes from evaporator to waste drum and there solidifies like glass to monolith. The product quality depends on the adjustment of the flow-equilibrium in the evaporator. Boric acid is used as matrix for the radioactive residues. The residual water content of the solidified waste product was about 15-20%, the volume reduction was V{sub f}=5...6. In order to be sure to get a ...

International Nuclear Information System (INIS)

Focused ion beam (FIB) irradiation of a thin Ni_2Si layer deposited on a Si substrate was carried out and studied using an in-situ transmission electron microscope (in-situ TEM). Square areas on sides of 4 by 4 and 9 by 9 microm were patterned at room temperature with a 25 keV Ga"+-FIB attached to the TEM. The structural changes of the films indicate a uniform milling, sputtering of the Ni_2Si layer and the damage introducing to the Si substrate. Annealing at 673 K results in the change of the Ni_2Si layer into an epitaxial NiSi_2 layer outside the FIB irradiated area, but several precipitates appear around the treated area. Precipitates was analyzed by energy dispersive X-ray spectroscopy (EDS). Larger amount of Ni than the surrounding matrix was found in precipitates. Selected area diffraction (SAD) patterns of the precipitates and the corresponding dark field images imply the formation of a Ni rich silicide. The relation between the FIB tail ...

International Nuclear Information System (INIS)

Polycrystalline silicon films have been grown from Si_2H_6 by low-pressure chemical vapour deposition at 800 K and in situ laser annealing (LA) on amorphous silicon seed layers deposited on a metallic Ti/Pd/Ag multilayer. The crystalline volume fraction in the seed layer was controlled by thermal annealing. According to the metal-induced crystallization effect, the presence of the metal induces a lower-temperature crystallization of silicon in the seed layers. X-ray diffraction and scanning electron microscopy data show that the formation of palladium silicides in the seed layer drives the growth of wire-like columns which are found to change morphology depending on the seed layer microstructure and LA parameters. It is suggested that superficial palladium was found to affect also the growth rate by enhancing the Si_2H_6 dissociation.

International Nuclear Information System (INIS)

In this study, growth measurements of fatigue cracks in air and various simulated media for steam turbines were made by means of rupture-mechanical methods. In this connection, it was detected that even pure water leads to a clear increase in the fatigue crack rates of low-pressure rotor steels. In this connection, it was striking to observe that the crack propagation velocities at 100"0C were higher than at 160"0C. It is probable that the kinetics of the film formation at the crack tip was of importance. The inhibiting effect of the alkaline solutions is explained by the increasing stability of a film of Fe(OH)_2 at an increased pH value. Neither the frequency response nor the fractographic result indicate an influence of the stress crack corrosion. This can be explained by the fact that the incubation period (= the period to initiate an intercrystalline crack caused by stress crack corrosion at a transcrystalline fatigue ...

Energy Technology Data Exchange (ETDEWEB)

To clarify the acidic and alkaline Intergranular Stress Corrosion Cracking (IGSCC) mechanism of thermally treated alloy 690 (alloy 690 TT) and shot peened alloy 800 (alloy 800 SP), C-ring tests were conducted in deaerated HCl solutions and in deaerated NaOH solutions at 350degC, compared with the acidic and the alkaline IGSCC susceptibilities of mill-annealed alloy 600 (alloy 600 MA), full-sensitized one (alloy 600 FS) and thermally treated one (alloy 600 TT). Grain boundary characteristics, such as chromium depleted zone and chromium carbide precipitation, were examined using modified Huey test and Transmission Electron Microscopy. Potential-pH diagram for Ni, Cr, Fe-H{sub 2}O system at 350degC was constructed and the solubilities of NiO, Cr{sub 2}O{sub 3} and Fe{sub 3}O{sub 4} were also calculated to evaluate the stability of oxide films which were formed on the surfaces of alloy 690, 800 and 600. Under the acidic condition, the IGSCC susceptibility of alloy 800 ...

British Library Electronic Table of Contents (United Kingdom)

Abstract Thermomechanical behavior of membranes based on blends of poly(vinyl alcohol) (PVA) with different weight percentage (wt %) of glycerol has been studied. Solid-state PVA/Glycerol polymer membranes were prepared by a solution casting method. The films were studied for thermal characteristics by differential scanning calorimetry (DSC) and thermogravimetric analysis and for the mechanical properties including hardness and modulus by nanoindentation method. The dispersion of glycerol within the polymer matrix was examined using scanning electron microscopy. Fourier transform infrared spectroscopy was used to confirm the formation of hydrogen bonding between the plasticizer and PVA in their blends and also to provide information on compatibility and physical interactions between the gl...

Energy Technology Data Exchange (ETDEWEB)

Thin Pt, Pd, Pt/sub 2/Si, PtSi, Pd/sub 2/Si, Ni, Mo, W, Nb, Ti, V films deposited on Si single crystal were treated by using electron beam pulses of 60 ns duration in the 0.4-4 J/cm/sup 2/ energy density range. Irradiation of these structures produces at the same time many phases. Post-thermal annealing of the reacted layer induces the formation of a stable phase, the same obtained by only thermal treatment in a conventional furnace. A linear relationship between the energy density range and the lowest eutectic temperature of the compounds formed has been found. Further SEM observations seem to identify a liquid layer from which the phases are forming by subsequent fast cooling.

British Library Electronic Table of Contents (United Kingdom)

Flue gas desulfurization systems (FGDs) are operated in severely corrosive environments that cause sulfuric acid dew-point corrosion. The corrosion behavior of low-alloy steels was tested using electrochemical techniques (electrochemical impedance spectroscopy, potentiodynamic tests, potentiostatic tests), and the corrosion products were analyzed by scanning electron microscopy and X-ray photoelectron spectroscopy. The electrochemical results showed that alloying W with small amounts of Sb, Cu, and Co improves the corrosion resistance of steels. The results of surface analyses showed that the surface of the steels alloyed with W consisted of W oxides and higher amounts of Sb and Cu oxides. This suggests that the addition of W promotes the formation of a protective WO3 film, in addition to ...

British Library Electronic Table of Contents (United Kingdom)

Effects of some experimental parameters (supporting electrolyte, initial pH and current density) on the performance of electrocoagulation process using iron electrodes were investigated. Results of experiments showed that dissolution of iron is purely electrochemical and fits well with Faraday's law and leads to Fe^2^+ which are chemically oxidized into Fe^3^+ in aerated conditions. In neutral and alkaline conditions, the reaction between hydroxyl ions generated at the cathode and dissolved iron ions forms insoluble hydroxo-iron species. Potentiodynamic polarization tests showed that the formation of passive film on iron anode limits the continuous electrochemical dissolution of iron. Corrosion and pitting potentials largely depend on the nature of supporting electrolyte. The dissolution o...

Energy Technology Data Exchange (ETDEWEB)

A new technique was proposed in order to improve poor corrosion resistance in magnesium. That is, magnesium hydroxide film was formed on the surface of 3 N-Mg by artificial corrosion in 1% MgCl{sub 2} solution for 3.6 ks, which followed by oxidation at 673 K for 3.6 ks in air. Corrosion resistance was evaluated by salt immersion tests in 1% NaCl solution under in situ laser microscopic observations. Bubble evolution, which occurred immediately at the beginning of the immersion test in the case of non-treated specimen, was suppressed by the process. And also, formation of filiform corrosion was suppressed for about 3.6 ks, which occurred at 180 s in the non-treated specimen. (orig.)

International Nuclear Information System (INIS)

We have developed a chemical process for incorporating copper into indium gallium selenide layers with the goal of creating a precursor structure for the formation of copper indium gallium diselenide (CIGS) photovoltaic absorbers. Stylus profilometry, EDX, Raman spectroscopy, XRD and SIMS measurements show that when indium gallium selenide layers are immersed in a hot copper chloride solution, copper is incorporated as copper selenide with no increase in the thickness of the layers. Further measurements show that annealing this precursor structure in the presence of selenium results in the formation of CIGS and that the supply of selenium during the annealing process has a strong effect on the morphology and preferred orientation of these layers. When the supply of Se during annealing begins only once the substrate temperature reaches ? 400 deg. C , the resulting CIGS layers are smoother and have more pronounced preferred orientation than when ...

International Nuclear Information System (INIS)

A liquid column was used for the experiments reported in Part 1. However, it only gives the observation of the effect of fast reaction because the liquid flow was controlled to uniform laminar flow and the contact is limited to short time of around 10 ms. In practical absorbing operation, turbulence is involved in liquid flow, and the residence time for contact is long. Hence, the absorption of trace iodine in the purified air has been experimented by using a constant interface area type stirred absorption tank. Prior to the experiment, the characteristics of the absorption tank was investigated by conducting pure carbon dioxide absorption test with purified water. It gave the conclusion that the tank was sufficiently usable for fundamental researches. In short contact time absorption, the iodine dissolved and absorbed in liquid phase is affected by reaction of hypoiodous acid and poly-iodide ion formation due to hydrolysis by basic catalyst, proceeding in the ...

International Nuclear Information System (INIS)

Interest to thin film of metals' silicides first of all is conditioned intrinsic al them unique physical properties. On their basis of it is possible to produce extremely sophisticated devices of solid-state electronics, production which needs the controlled change of physics, chemical and electrical properties with high-level of accuracy. On the present time most are in detail investigated composition, structure and properties of three-dimensional samples of metals' silicides. In the last years the intensive are led to researches in the direction of creation and study of physical-chemical properties thin (500-1000 Angstroms) and ultrafine (100-120 Angstroms) films silicides. It has information about composition, morphology of surface and emission of properties of thin film of silicides of barium, of cobalt and of palladium, was obtained in conditions of ultra-high vacuum. Low energy ion implantation and further annealing ...

Energy Technology Data Exchange (ETDEWEB)

The process operation of the hot wall vapor deposition method, formation of dry organic thin film and the control of molecular arrangement were described. This equipment included a substrate on the upper end of the hot wall tube and the vapor source at the lower end. The remarkable features are the hot wall tube which plays the role to hold vaporizing molecules to the high temperature and to transport molecules, and the flip flop mechanism which gives some idle period for the molecular vaporization by shutter closing. Several experiments were carried out by using stearic acid and by changing the distance S from the upper end of hot wall quartz tube to the substrate, the furnace temperature T{sub f} and the substrate temperature T{sub s}. When T{sub f} is equal to or less than the melting point of stearic acid, molectles are preferentialy made to vertical arrangement. In the case of T{sub f} more than the melting point, the molecular rate of the ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

No abstract prepared.

Science.gov (United States)

... Abstract : MANY THIN FILM ACOUSTO-OPTIC INTERACTION EXPERIMENTS FOR ... CONVERTERS, AND FOR FAST SWITCHES HAVE BEEN ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

The objective of this investigation was to perform a preliminary evaluation of the utility of residual materials prepared from Green River Formation (western) and New Albany Shale (eastern) shale oils as recycling agents for aged asphalt pavement. Four petroleum asphalts were first aged by a thin-film accelerated-aging test, which simulates long service life of asphalt in pavement. The aged asphalts were mixed (recycled) with Green River Formation shale oil distillation residua to restore the original viscosities. Separately, for comparison, a commercial recycling agent was used to recycle the aged asphalts under the same circumstances. The recycled asphalts were reaged and the properties of both binder and asphalt-aggregate mixtures studied. Originally, the same study was intended for an eastern shale residua. However, the eastern shale oil distillation residua with the required flash point specification also had the ...

International Nuclear Information System (INIS)

The formation and properties of Pd_2Si formed by focused ion beam implantation of Pd ions into Si is presented in this thesis. An extensive microstructural study using transmission electron microscopy was undertaken and the as-implanted as well as annealed microstructure is shown. Results of other analysis techniques such as Rutherford back scattering and secondary ion mass spectrometry etc. are also presented. Kinetic information on the growth of Pd_2Si obtained by both microstructural and resistance measurements indicates that the activation energy for growth of the silicide is around 0.36 to 0.39 eV. This can be compared with the normally reported value of 1.5 eV for Pd_2Si formed by annealing thin film Pd on Si. The growth of the silicide was found to follow t"1"/"2 kinetics. Microstructural observation of the as-implanted samples showed extensive in-situ formation of Pd_2Di and also surprisingly few defect structures. ...

Science.gov (United States)

Silicon carbide (SiC) based electronic devices are of great importance for applications under the condition of high temperature, high power and high radiation. Schottky diodes of Palladium/SiC are good candidates for hydrogen and hydrocarbon gas sensors at elevated temperature. The detection sensibility of the diodes has been found heavily temperature dependent. In this work, the electrical and chemical properties of Pd/SiC Schottky contacts were studied by XPS and AES at different annealing temperatures. Schottky diodes were made by depositing ultra-thin palladium films onto a silicon carbide substrate. No significant change in the Schottky barrier height of the Pd/SiC contact was found in the temperature range of 300-673K. Palladium diffusion into SiC and the formation of palladium silicides were observed at room temperature and became significant at 300^oC and higher temperature. The mechanism of diffusion and reaction at the Pd/SiC ...

Energy Technology Data Exchange (ETDEWEB)

Lithium ion batteries use an oxide as a positive electrode and a carbon material as a negative electrode. The performances of carbon electrodes have rapidly evolved during the last years thanks to the substitution of soft carbons of Conoco or MCMB-2510 type by graphites (F-399, MCMB-2528) and then by hard carbons. These high capacity carbons (700 mAh/g) have higher service life and volume capacity than graphites but their irreversible losses are greater (>20%). In this work, materials with similar electrochemical performances are prepared by mechanical crushing. Mechanical crushing allows to obtain a wide range of carbon materials with various morphologies, specific surfaces and levels of disorder. The formation of the passivation film is directly linked with the surface of materials. A reaction scheme of the reversible and irreversible capacities has been defined and has permitted to obtain compounds with reversible capacities of 720 mAh/g ...

Energy Technology Data Exchange (ETDEWEB)

the medium to long freezing range alloys of aluminum such as A356, A357, A206, 319 for example are known to exhibit dispersed porosity, which is recognized as a factor affecting ductility, fracture toughness, and fatigue resistance of light alloy castings. The local thermal environment, for example, temperature gradient and freezing from velocity, affect the mode of solidification which, along with alloy composition, heat treatment, oxide film occlusion, hydrogen content, and the extent to which the alloy contracts on solidification, combine to exert strong effects on the porosity formation in such alloys. In addition to such factors, the availability of liquid metal and its ability to flow through the partially solidified casting, which will be affect by the pressure in the liquid metal, must also be considered. The supply of molten metal will thus be controlled by the volume of the riser available for feeding the particular casting location, ...

Energy Technology Data Exchange (ETDEWEB)

The investigation of interfaces between thin organic films and metal surfaces is a field of highest interest because it represents the basis for future applications of organic electronic devices. In this context, phtalocyanines are of particular interest since repulsive intermolecular interaction was found recently for this group of organic molecules. Tin(II)-phtalocyanine (SnPc) is non-planar and can adsorb in two different geometries: with the Sn atom pointing downwards (Sn down) or upwards (Sn up). In our group different Pc molecules have previously been studied using several experimental techniques like SPA-LEED or XSW. Here we present STM studies of SnPc on Ag(111), taken at different coverages and temperatures, and discuss the results in the context of our previous findings. At low coverages the formation of chains can be observed for Sn down molecules while Sn up molecules tend to stay separated. This originates from a strong interaction ...

Energy Technology Data Exchange (ETDEWEB)

Heusler alloys are considered as interesting ferromagnetic electrode materials for magnetic tunnel junctions, because of their high spin polarization. We, therefore, investigated the micromagnetic properties in a prototypical thin film system comprising two different Heusler phases Co{sub 2}MnSi (CMS) and Co{sub 2}FeSi (CFS) separated by a MgO barrier. The magnetic microstructure was investigated by X-ray photoemission electron microscopy (XPEEM). We find a strong influence of the Heusler phase formation process on the magnetic domain patterns. SiO{sub 2}/V/CMS/MgO/CFS and SiO{sub 2}/V/CFS/MgO/CMS trilayer structures exhibit a strikingly different magnetic behavior, which is due to pinhole coupling through the MgO barrier and a strong thickness dependence of the magnetic ordering in Co{sub 2}MnSi.

International Nuclear Information System (INIS)

A novel Ni and Cu-free Zr-based bulk metallic glass (BMG) system with enhancement of glass-forming ability (GFA) and bio-corrosion resistance was prepared by copper mold casting by the addition of Ag. It was found that the addition of Ag can considerably enhance the glass-forming ability, as indicated by the increase of the critical glass dimension from 3 mm diameter of the ternary system to over 10 mm in the alloy of Zr_5_3Co_1_8_._5Al_2_3_._5Ag_5. The bio-corrosion behaviors of the Zr-based BMGs in phosphate buffered solution (PBS) were investigated by electrochemical polarization at 310 K. It was found that the addition of appropriate amount of Ag can enhance the corrosion resistance of the BMGs. The X-ray photoelectron spectroscopy (XPS) indicated that the formation of an Al_2O_3-enriched passive film is mainly responsible for the high corrosion resistance of Ag-bearing alloy in phosphate buffered solution.

Energy Technology Data Exchange (ETDEWEB)

Tantalum and tantalum-based thin films have gained precedence as the diffusion barrier for copper interconnects used in the latest generation of integrated circuits (ICs). The paper presents insight and observations on the covariance of texture and grain size of wrought tantalum sputtering targets and their influence on sputtering performance. Previous studies involving deposition trials of tantalum targets of varying metallurgical character had demonstrated that both grain size and textural homogeneity is critical for assuring reliable sputtering performance of tantalum. Subsequently, a model had been proposed to prescribe how localized texture bands and orientation clusters in tantalum are effectively resistant to sputter erosion. In this paper, results of atomic force microscopy (AFM) and orientation imaging microscopy (OIM{sup TM}) analyses on the eroded surface of a tantalum sputtering target are presented. Initial findings support the model's ...

Energy Technology Data Exchange (ETDEWEB)

It was to be investigated why inexplicable cracking occurred in plain stainless austenitic steel pipes of heat exchangers in discrete sites of the inner surface exposed to acid even with anodic corrosion protection, and what countermeasures must be taken. The following materials were investigated: X 6 CrNiTi 18 10 and X 6 CrNiMoTi 17 12 2. The influence of mechanical vibrations on passive film formation and destruction was investigated in unconstrained pipes and pipes constrained at one end in conditions of anodic protection at frequencies of 0 to 160 Hz and temperatures of 98 to 130 degrees Centigrade in 98% sulphuric acid. The authors were unable to reconstruct the cracks observed in practical operation in anodically protected heat exchanger pipes of stainless austenitic steel. (orig./MM). 5 refs., 2 tabs., 71 figs.

International Nuclear Information System (INIS)

A low-molybdenum austenitic stainless steel (UNS S30100) has been surface implanted with molybdenum ions, using various doses of 50 keV and 140 keV ions at room temperature. It is found that in aqueous sulphate/chloride solutions similar to the constitution of sea-waters the implantation does not affect the potentiostatically-determined critical pitting potential, but does change the density and morphology of corrosion pits. Pitting initiation after the addition of chloride at a fixed potential indicates little change in the time for measurable current increase, but the rate of increase of the current is much lower for implanted material. Detailed examination using optical microscopy, scanning electron microscopy, transmission electron microscopy and selected area diffraction suggests that the pits produced in implanted material are hemispherical with smooth covers of unattacked alloy. The use of half-implanted samples demonstrates that molybdenum implantation causes the ...

International Nuclear Information System (INIS)

In the present work, a rapid deposition anodic stripping voltammetry (ASV) for determination of uranium is presented. For this purpose, the uranyl hexacyanoferrate (K2UO2[Fe(CN)6]) is deposited electrochemically on a thin palladium-aluminum electrode (Pd-Al) from a UO22+ solution in the presence of K3Fe(CN)6. Then, the well stable (K2UO2[Fe(CN)6]) on the electrode was stripped by anodic differential pulse voltammetry for measuring the UO22+ ion concentration. The effect of operational parameters, including: concentration of K3Fe(CN)6, solution pH, deposition potential, and deposition time were studied. In optimum conditions, the calibration graph was linear in the concentration range 105-7 x 10-4 mol L-1 with a detection limit of 6.2 x 10-6 mol L-1. The influence of some concomitant ions in K2UO2[Fe(CN)6] formation was investigated. The proposed method was used for the rapid determination of uranium in some uranium mineral ores. (orig.)

International Nuclear Information System (INIS)

A tri-functional polyhedral oligomeric silsesquioxane (POSS) based silane precursor R_xR_yR_z(SiO_3_/_2)_n (x + y + z = n = 6, 8, 10, ...) bearing 3-(N-(3-triethoxysilylpropyl)ureido)propyl, isooctyl and perfluoropropyl groups was synthesized and investigated as corrosion protective coating for AA 2024 alloy. Infrared reflection-absorption (IR RA) combined with X-ray photoelectron spectroscopy and atomic force microscopy provided information about partial self-assembling of coatings having a fluorine enriched upper layer with a low surface energy (#gamma#"t"o"t = 12.37 mN/m). The structural changes that accompanied corrosion produced under chronocoulometrical conditions were assessed from ex-situ IR RA spectra. A new band at 1690-1700 cm"-"1 appeared above the corrosion potential, and was assigned to the formation of amidonium ions and consequent relaxation of urea-urea associations.

British Library Electronic Table of Contents (United Kingdom)

The K 2010 exhibition saw the introduction of PolyOne Corps OnCap Antifog Additive for polypropylene (PP) films, the first such additive for PP films that does not require corona treatment. According to the company, this new additive simplifies production of antifog films for the flexible food packaging industry, improving production efficiencies for both cast and blown film producers.

Energy Technology Data Exchange (ETDEWEB)

The corrosion and passivation behaviour of bulk polycrystalline martensite Ni{sub 50}Mn{sub 30}Ga{sub 20} and austenite Ni{sub 48}Mn{sub 30}Ga{sub 22} alloys was compared in electrolytes with different pH values. Linear anodic and cyclic potentiodynamic polarisation methods and anodic current transient measurements have been conducted for the alloys and their constituents to analyze free corrosion, anodic dissolution and passive layer formation processes. Electrochemically treated alloy surfaces were characterized with scanning electron microscopy (SEM) and angle-resolved x-ray photoelectron spectroscopy (XPS). The electrochemical response of both alloys is in principal similar and is dominated by the Ni oxidation. In acidic solutions (pH 0.5 and 5) a slightly higher reactivity is detectable for the martensitic alloy which is mainly attributed to enhanced dissolution processes at the multiple twin boundaries. In weakly acidic to strongly alkaline solutions (pH ...

International Nuclear Information System (INIS)

The development of the microstructure on aging of an (#alpha# + #beta#) type titanium alloy containing 6Al-1.6Zr-3.3Mo-0.3Si (VT9) (in weight percent) has been studied. The #beta#-transus temperature of this alloy is approximately 1243 K. Solution treatment in the #beta#-phase field of the alloy followed by quenching in water at room temperature resulted in the formation of a single-phase martensite structure. The martensitic structure was confirmed to be orthorhombic (#alpha# double-prime) using X-ray diffraction. The water-quenched (WQ) specimens were subjected to aging treatments at temperatures of 823, 873, and 973 K for various lengths of time. Aging at 823 K for times between 24 and 100 hours did not bring about any noticeable change in the microstructure. Aging at 823 K for 200 and 300 hours resulted in the heterogeneous precipitation of s_2 silicide particles and thin films of #beta# sandwiched between the interplatelet boundaries of ...

Energy Technology Data Exchange (ETDEWEB)

The friction and wear properties of glass fiber reinforced composites of nylons (nylon 6, nylon 66 and nylon 46) with different crystallinities due to their molecular structures were investigated by sliding them with alumina ceramics and using a pin-on-disk friction machine. The friction coefficients of the glass fiber reinforced nylons in oil were lower and more stable than those in air from the initial stage of friction. The transfer of nylon matrix to adhere onto the alumina surface in air was so much greater than in oil that the alumina surface could not be recognized. Consequently, a different between the friction and wear properties in air and in oil was resulted. Reinforcement of nylons with glass fiber remarkably improved their friction properties in oil by its lubricating action, while the wears were rather high contrary to what was expected. This tendency was conspicuous for nylon 46 with high crystallinity. Breakage and extracting of glass fibers from nylon composites were ...

International Nuclear Information System (INIS)

(Cu_4_7Zr_1_1Ti_3_4Ni_8)_1_0_0_-_xMo _x bulk metallic glasses (BMGs) with x = 0, 1 and 2 at.% and a bulk metallic glass matrix composite with x = 5 at.% were successfully prepared by water-cooled copper mold casting. The effect of the addition of a small amount of Mo on the glass forming ability (GFA), thermal properties of the base alloy (i.e. x = 0) were investigated by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and differential thermal analyzer (DTA). It is found that the addition of appropriate amount of Mo can enhance the GFA of the Cu-based BMG, as indicated by the increase in the reduced glass transition temperature T _r_g (=T _g/T _l) and the parameter #gamma# (=T _x/(T _g + T _l)) with the increase of Mo. On the other hand, the corrosion resistance of the Cu-based BMGs with different Mo contents was examined by electrochemical polarization and weight loss measurement in 1 mol/L H_2SO_4 and 1 mol/L NaOH solutions, respectively. It is found that the ...

Energy Technology Data Exchange (ETDEWEB)

After pioneering work in the 1980s, plasma-based ion implantation (PBII) and plasma-based ion implantation and deposition (PBIID) can now be considered mature technologies for surface modification and thin film deposition. This review starts by looking at the historical development and recalling the basic ideas of PBII. Advantages and disadvantages are compared to conventional ion beam implantation and physical vapor deposition for PBII and PBIID, respectively, followed by a summary of the physics of sheath dynamics, plasma and pulse specifications, plasma diagnostics, and process modeling. The review moves on to technology considerations for plasma sources and process reactors. PBII surface modification and PBIID coatings are applied in a wide range of situations. They include the by-now traditional tribological applications of reducing wear and corrosion through the formation of hard, tough, smooth, low-friction and chemically inert phases ...

Science.gov (United States)

Aluminum, due to its low density and low cost, is a key material for future lightweight applications. However, like other structural materials, aluminum is subject to various forms of corrosion damage that annually costs the United States approximately 5% of its GNP [1]. The main goal is to investigate the effects of various solution anions on aluminum surfaces, and specifically probe pit initiation and inhibition. Using surface analysis techniques including X-ray photoelectron spectroscopy, Auger electron spectroscopy, and scanning electron microscopy, results have been correlated with those obtained from electrochemical methods and a radiolabeling technique developed in the Wieckowski laboratory. Analysis of data has indicated that important variables include type of anion, solution pH, and applied electrode potential. While aggressive anions such as chloride are usually studied to elucidate corrosion processes to work ultimately toward inhibition, its corrosive properties can be ...

Energy Technology Data Exchange (ETDEWEB)

Predictions of the combination of our recent model for the formation of planetary nebulae (due to a diverging pulsational instability) together with nuclear-burning shell flashing, with regard to formation of multiple shells, are explored and discussed.

CERN Document Server

Thermal and Electromigration-Induced Strains in Polycrystalline Films and Conductor Lines

International Nuclear Information System (INIS)

... obtain the film thickness for a given x-ray intensity ratio. 2.3 ANALYSING FOR

Science.gov (United States)

Metastable yttrium-oxide films are synthesized using reactive sputter deposition. The yttrium concentration of the as-deposited film is found to vary as a function of the sputter deposition rate. In addition to the synthesis of the cubic equilibrium phase...

British Library Electronic Table of Contents (United Kingdom)

To eliminate their classical brittleness and flexibility problems zein films were plasticized by incorporation of different phenolic acids (gallic acid (GA), p-hydroxy benzoic acid (HBA) or ferulic acids (FA)) or flavonoids (catechin (CAT), flavone (FLA) or quercetin (QU)). The use of GA, CAT, FA and HBA at 3 mg/cm2 eliminated the brittleness of films and gave highly flexible films showing elongations between 135% and 189%, while FLA and QU caused no considerable effect on film elongation. The films containing FA and HBA showed extreme swelling and lost their structural integrity when hydrated in distilled water. In contrast, CAT and GA containing films maintained their integrity following hydration. Most of the GA (up to 93%) and a considerable portion of CAT (up to 60%) in the films exis...

International Nuclear Information System (INIS)

The combined process of low temperature plasma nitriding and TiN film deposition was realized on the plasma-assisted vacuum arc plating set. The process of plasma nitriding can be done below 200 degree C. The low temperature plasma nitriding and TiN film deposition was realized on the same device. By the SEM analysis of the plating structure, low hardness grads from the substrate to the film was obtained, and it was found that the mixed nitride plating formed at the interface between the substrate and the film. The quantitative measurement of substrate-film adherence showed that the adherence was improved notably by using the process. The adherence between film and substrate can reach to 59.6 MPa without the bias voltage supplying

Science.gov (United States)

Palladium chloride films have been found to be useful as ... when suitably prepared palladium chlo- ride films are exposed ... Like the palladium chloride ( PdCl2) ...

International Nuclear Information System (INIS)

Iron oxide thin films have been obtained by spray pyrolysis using 100% methanolic and ethanolic solutions of iron tri-chloride. The films were deposited onto ITO-coated glass substrates. The preparative conditions have been optimized to obtain compact, pin-hole-free and smooth thin films which are adherent to the substrate. The structural, morphological and compositional characterizations have been carried out by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray analysis. The films deposited using ethanolic solution results into pure hematite; #alpha#-Fe_2O_3 thin films, however, films deposited using methanolic solution consists of hematite and maghemite-c phases of iron oxide. The films are nanocrystalline with particle size of 30-40 nm. The optical absorbance of the film was of the order of ...

Energy Technology Data Exchange (ETDEWEB)

Short communication

Science.gov (United States)

Methods of acidizing a subterranean well formation, acidizing compositions, and sequestering additives for preventing the precipitation of metal compounds in the formation are described. Use of the methods and chemicals described should lead to improved formation permeability as compared to use of previous methods and chemicals. 12 claims.

International Nuclear Information System (INIS)

Surface-sensitive UV photoelectron yield spectroscopy was employed to study electron acceptor levels at surfaces of chalcopyrite structure Cu-In-Se thin films. Surface Fermi level pinning was observed for Cu-rich films. Shallow acceptor levels ascribable to defects Cu_I_n and V_C_u were observed for near-stoichiometric and In-rich films respectively. (orig.).

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

Only two years ago, plastic film recycling was considered an onerous task. Different resins had to be identified, colors had to be separated, and minute contaminants had to be weeded out almost by hand to produce a quality material. But the tide of plastic film recycling is changing now that new technologies have emerged and more organized collection infrastructure have been developed. Today, plastic film recycling maintains a lucrative market for those with the right combination of equipment and know-how.

Energy Technology Data Exchange (ETDEWEB)

The authors study the nonuniformity of a-Si:H films obtained by the method of vacuum condensation, with the help of x-ray small-angle scattering (SLS) and transmission electron microscopy. Films of hydrogenated amorphous silicon are greatest interest, because the electronic properties of this material can be controlled by doping. As a result of the compensation of the ruptured bonds, and possibly, effects of melting, the properties of such films are analogous to those of singlecrystalline silicon. XLS enables a quantitative determination of the prameters of the regions of low electron density (RLD) in such objects.

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

Short communication.

Energy Technology Data Exchange (ETDEWEB)

Short communication.

Science.gov (United States)

9 9 simulated Purex waste oxides was investigated as a function of Na/sub 2/O, CaO and P/sub 2/O/sub 5/ content. All compositions lost some sulfate at 50 to 100 deg C above the softening point. In generai the volatility decreased with increase of either Na/ sub 2/O or CaO relative to P/sub 2/O/sub 5/, but no simple correlation Was indicated. Softening temperatures were lowered by inc ease in Na/sub 2/O vs CaO. Ceramic solids were obtained but no true glasses. Attempts to produce glasses by addition of varying combinations of Al/sub 2/O/sub 3/, PbO, BaO, and B/sub 2/O/ sub 3/ to simulated Pure x waste plus phosphite were unsuccessful. The use of 0.005 M Na/sub 2/C/O/sub 3/ to precipitate calcium from wastes containing up to 3 ppm of phosphate was demonstrated in four pilot plant runs and produced a decrease in the hardness of the waste leaving the clarifier. An inadvertent Sr/ sup 90/ and Cs/sup 137/ breakthrough occurred during one ...

Energy Technology Data Exchange (ETDEWEB)

Passive films formed on stainless steels in a borate buffer solution (pH 9.2) have been investigated by capacitance measurements and photoelectrochemistry. The study was carried out on films formed on AISI type 304 and 316 stainless steels and high purity alloys with differing chromium, nickel, and molybdenum contents. Complementary research by Auger analysis shows that the passive films are composed essentially of an inner chromium region in contact with the metallic substrate and an outer iron oxide region developed at the film/electrolyte interface. The semiconducting properties of the passive films are determined by those of the constituent chromium and iron oxides which are of p-type and n-type, respectively. Thus the influence of the alloying elements on the semiconducting properties of the passive films is explained by changes in the electronic structure ...

Energy Technology Data Exchange (ETDEWEB)

X-Ray reflectivity has been used to investigate the microstructural changes of solution-cast stearic acid films before and after immersion in CoCl{sub 2} solutions. Before immersion, the films possess a well-defined layered structure with an interlayer spacing of 4.01{+-}0.05 nm. After the films were immersed in the CoCl{sub 2} solutions, a new set of equidistant diffraction peaks emerge, the corresponding interlayer spacing of which is 5.13{+-}0.05 nm. The X-ray photoelectron spectra of the films indicate the existence of cobalt ions inside the films after immersion. It is concluded that the permeation of the cobalt ions into the hydrophilic interlayer causes the stearic acid molecules to reorient perpendicular to the films, resulting in the increase of interlayer spacing and the roughening of the interfaces.

International Nuclear Information System (INIS)

The total hemispherical emittance of an oxide film that formed on 6061-T6 aluminium alloy parts in the Tower Shielding Reactor-II at Oak Ridge National Laboratory was measured from 295 to 773 K using an emissometer and/or a calorimeter. The emittance of this film was critically needed for heat transfer calculations in a simulated loss-of-coolant accident of the reactor. X-ray diffraction analysis identified the film as boehmite (Al_2O_3 x H_2O), which dehydrated to alumina (Al_2O_3) upon heating above 473 K. The measured emittances for the alumina film are in excellent agreement with published values for anodized aluminum films and for bulk alumina. Published values of the emittance of boehmite could not be found for comparison, but evidence is presented that some anodization processes for aluminum yield boehmite and not alumina films.

Science.gov (United States)

Critical power at boiling transition is an important factor in a boiling water reactor (BWR) fuel bundle design. Boiling transition under high quality accounts for dryout as the result of the complete disappearance of film flow on a fuel rod. This liquid film vanishing process can be calculated by the liquid film model, which takes into account the evaporation due to heat from the rod surface, liquid film entrainment by steam flow, and liquid droplet deposition. It is known that spacers affect liquid film entrainment and liquid droplet deposition, so the detailed study of spacer effects on hydrodynamic characteristics is necessary for critical power prediction based on the film flow model. Many studies have been conducted to examine spacer effects on liquid film flow. However, most of them are restricted to simple test sections such as a ...

International Nuclear Information System (INIS)

By the methods of small-angle X-ray scattering and translucent electron microscopy the existence of inhomogeneity of electron density in hydrogenated films of amorphous silicon is confirmed. The decreased density regions are extended and form a branched network of channels oriented mostly by the normal direction to the films surface. The typical size of the decreased density regions network constitutes 10 nm in the 100-800 nm films thickness range. The increase of hydrogen total partial pressure in gas mixture in case of films growth results at first in the decrease of extension of these regions and than to micropores generation in the network nodal points of the decreased electron density regions.

International Nuclear Information System (INIS)

The structural ordering of oxygen deficient and Co-doped YBCO (YBa_2Cu_3_-_yCo_yO_6_+_x) have been studied experimentally, and by computer simulations of the oxygen ordering in the basal plane of the structure. The calculations are based on the two-dimensional ASYNNNI model and its modifications. Good agreement is established between the ASYNNNI calculations and the experimentally observed structural properties of the double cell ortho-II structure and the oxygen disordering process from Co-doping into the basal plane. A model that relates the superconducting transition temperature T_c(x) of undoped YBCO and T_c(y) of Co-doped YBCO to the formation of specific domains of the two orthorhombic ordered oxygen phases, ortho-I and ortho-II, shows a close agreement with experimental T_c(x) and T_c(y) data of samples prepared under equilibrium conditions. The structural changes as a result of metal ion substitutions and oxidation/reduction processes have been studied by ...

Energy Technology Data Exchange (ETDEWEB)

Mott-Schottky (M-S) analysis is an effective approach to investigate the electronic property of passive films of metals, and it is well suitable for the passive film with single space charge capacitance. But there is no proper method to analyze the C{sub sc}{sup -2} vs. V{sub m} plots of passive films with several space charge capacitances in series connection, such as bipolar passive films. In this paper, the relationship between the space charge capacitance of the bipolar passive film and the applied potential was deduced and the features of corresponding plots were given out simultaneously. Accordingly, a non-linear fitting method was presented to analyze the C{sub sc}{sup -2} vs. V{sub m} plots of bipolar passive films. Then the method was used to study the semiconductor characteristics of bipolar passive films formed on the surface of ...

Energy Technology Data Exchange (ETDEWEB)

A theoretical model, which describes subband gap photoexcitation involving localized electronic states, was developed. The escape probability of a charge carrier trapped in a localized state is considered via Poole-Frenkel, direct tunneling, or phonon-assisted tunneling processes, as competing escape mechanisms. Photoelectrochemical experiments were performed on the passive films formed on zirconium and amorphous iron-zirconium alloys and on pure HfO/sub 2/ films and HfO/sub 2/ films implanted with varying concentrations of xenon. These films were found to possess some degree of disorder depending on the substrate, the thickness of the film, and the extent of implantation. The spectral dependence of the photocurrent in all of the films studied is considerably different from what was found for crystalline passive films. The potential ...

Energy Technology Data Exchange (ETDEWEB)

A radio frequency sputtering apparatus with a pair of targets has been developed for depositing a film of uniform thickness onto a complex-geometric specimen such as the retainer of a ball bearing. The deposition characteristics of the apparatus were compared with those of the conventional sputtering apparatus. Lubrication properties of MoS/sub 2/ films made by these devices were also compared under a variety of conditions. Finally, friction and wear of MoS/sub 2/ films applied to angular-contact type ball bearings of 20 mm bore were studied in air, nitrogen and vacuo. The two-target sputtering has an advantage mentioned above. However, the films deposited by the method exhibited a rather short wear life because of the temperature rise of the substrate during ion bombardment and during the sputtering process. This temperature dependence was observed in films on those substrates that ...

Energy Technology Data Exchange (ETDEWEB)

The temperature dependence of the spontaneous magnetization of epitaxial iron films with a thickness ranging from d=20 to 200nm has been measured. The films are grown on GaAs (100) substrates which are covered by a 150nm thick silver (100) buffer layer. For three-dimensional BCC iron it was observed already in 1929 that saturation of the spontaneous magnetization for T->0 is perfectly described by a T{sup 2} power law. On the other hand, for thin two-dimensional (2D) iron films a T{sup 3/2} law has been established in many recent experimental investigations. In our iron films grown on diamagnetic silver, this dimensionality change occurs at a thickness between d=100 and 200nm. Comparison of the here-observed T{sup 3/2} coefficients with those on iron films grown on paramagnetic tungsten (110) shows that the 2D interactions are {approx}20 times larger in the ...

International Nuclear Information System (INIS)

The composition of sputter-deposited HgS films was determined by electron microprobe analysis. From the relative x-ray intensity as a function of film thickness, the depth of the ionizations that produce SK sub(#alpha#) and HgM sub(#alpha#) was found to be approximately 0.65 #mu#m at an accelerating voltage of 15 kV. This value agreed well with a value calculated from Castaings' empirical law after absorption correction. The determination of film composition was limited to sufficiently thicker films than this critical value, usually 1 - 2 #mu#m thick. The relation between the conposition of bulk standard determined by chemical analysis and the x-ray intensity ratio was used for the correction of film composition. The results showed that the crystal structure of HgS films was independent of the composition, i.e., the growth of metastable #betta#-HgS ...

British Library Electronic Table of Contents (United Kingdom)

Nanocrystalline chromium oxynitride films were deposited by reactive RF magnetron sputtering of metallic chromium target in argon and helium atmospheres. The paper deals with consequence of increase in oxygen partial pressure on structural, hydrophobic and optical properties of chromium oxynitride films. The film stoichiometry changes from CrN and Cr2O3 to only Cr2O3 with increase in oxygen partial pressure as evident from X-Ray Diffraction analysis in both cases. The average crystallite size decreases with increase in oxygen partial pressure for both gas atmospheres. The thickness calculated from transmission data and surface profilometer are in good harmony with each other. The deposited films are hydrophobic by nature and the contact angle of the films varies as a function of surface ro...

Energy Technology Data Exchange (ETDEWEB)

In 1977 and 1978, Sandia National Laboratories, located in Albuquerque, New Mexico, and operated for the US Department of Energy (DOE), filmed a series of crash and fire tests performed on three casks designed to transport irradiated nuclear fuel assemblies. While the tests were performed to assess the applicability of scale and computer modeling techniques to actual accidents, films of them were quickly pressed into service by the DOE and nuclear utilities as ``proof`` to the public of the safety of the casks. In the public debate over the safety of irradiated nuclear fuel transportation, the films have served as the mainstay for the nuclear industry. Although the scripts of all the films were reviewed by USDOE officials before production, they contain numerous misleading concepts and images, and omit significant facts. The shorter versions eliminated qualifying statements contained in the longer ...

Energy Technology Data Exchange (ETDEWEB)

Grooving CVD diamond films using a focused ion beam (FIB) to quarry micro parts is described. The substrate-side surface of a polycrystalline diamond film which is prepared by means of microwave plasma CVD, is able to be grooved by a focused Ga ion beam scanned straight repeatedly. The groove has cross section whose shape is like an inverted Gaussian distribution curve. And the surface roughness of the films before grooved influences that of grooves. Under the same irradiation conditions, deeper, narrower, in short, high aspect ratio grooves are obtained on B-doped semiconducting microwave plasma CVD diamond films. Coating electrical conductive material is also effective method to obtain high aspect ratio grooves. It is supposed that these results are due to the degree of electrification on the surface and that FIB irradiation is a suitable method for micromachining semiconducting diamond ...

International Nuclear Information System (INIS)

The surface films formed on type 316LN stainless steels (SS) with different nitrogen contents, during potentiodynamic polarization in acidified 1 M NaCl solution, were characterized by Laser Raman Spectroscopy (LRS). LRS confirmed the presence of oxides and oxychlorides of iron and chromium, hydrated chlorides and nitrates in the film. Raman mapping showed increasing nitrate content in the film with increasing nitrogen content. The film on the uncorroded material showed the presence of chromium and molybdenum oxides. The improvement in pitting corrosion resistance of type 316LN SS with increasing nitrogen content was attributed to increased amount of nitrates in the passive film.

International Nuclear Information System (INIS)

The effect of surface treatment on the characteristics of the passive film on a super duplex stainless steel is addressed. Auger Electron Spectroscopy (AES) has been used to provide in-depth chemical profile analyses of the passivation film. This study showed that the constitution of the film is largely dependent on the electrolytic conditions under which it is produced or to which it is submitted. The passive films formed by polarisation in an alkaline solution (boric-borate solution) consist of two regions, an inner region rich in chromium and an outer region rich in iron, whilst the films produced in acid solution only present the chromium - rich region. The film thickness is also greatly affected by the polarisation conditions. It can vary from ca. 8 monolayers to about 20 monolayers for cathodically and anodically polarised specimens respectively. The ...

International Nuclear Information System (INIS)

The effect of Mo addition as an alloying element to stainless steel alloys is investigated by capacitance (Mott Schottky approach), and photoelectrochemistry measurements. Complementary studies were made using Auger electron spectroscopy and X-ray photoelectron spectroscopy. The Mott-Schottky approach and the photoelectrochemical studies showed that the presence of Mo as an alloying element affects the semiconductive properties of the oxide films. The analytical results have shown that the oxide films formed on stainless steels are composed by an external Fe rich region and an inner Cr rich region. No significant amount of Mo was found in the outer layers of the film. The presence of Mo leads to an increase of the chromium content in the inner layers of the film, although without increasing the film thickness. (orig.)

International Nuclear Information System (INIS)

In this work passive films formed in AISI 304 stainless steel were envisaged as semiconductors and studied by means of photoelectrochemistry and Mott-Schottky plots. The passive films were potentiostatically formed at different potentials (0.2-0.8V) in a basic borate/boric acid solution without and with addition of NaCl (0.5 and 1g/l) and at various temperatures in the range 8-60"oC. The influence of these parameters on the photocurrent, quantum efficiency, bandgap energy and density of charge carriers was determined. The results show that the experimental conditions at which the films are formed influence the semiconductive properties of the film, which seem to be related to the higher or lower stability of the film. An Arrhenius type of relationship was also found between the density of charge carriers and temperature, leading to the determination of an activation energy. (author) ...

International Nuclear Information System (INIS)

The thermal stability of low-friction Me-C/a-C:H coatings is important for their potential applications in the tool and automotive industry. Recently we showed that CrC _x/a-C:H coatings prepared by unbalanced magnetron sputtering of a Cr target in Ar + CH_4 glow discharges exhibit a nanocomposite structure where metastable fcc CrC nanocrystals are encapsulated by an a-C:H phase. Here, we present the structural evolution of these nanocomposite CrC/a-C:H coatings during annealing. High-temperature X-ray diffraction in vacuum and differential scanning calorimetry (DSC) combined with thermo-gravimetric analysis in Ar atmosphere indicate decomposition of the formed metastable fcc CrC phase and subsequent formation of Cr_3C_2 and Cr_7C_3 and structural transformation of the a-C:H matrix phase towards higher sp"2 bonding contents at temperatures above 450 deg. C. Combined DSC and mass spectrometer analysis as well as elemental profiling after annealing in vacuum by ...

Science.gov (United States)

As part of the Wisconsin road weather safety initiative, the objective of this study is to assess the effects of rainfall on the severity of single-vehicle crashes on Wisconsin interstate highways utilizing polychotomous response models. Weather-related factors considered in this study include estimated rainfall intensity for 15 min prior to a crash occurrence, water film depth, temperature, wind speed/direction, stopping sight distance and deficiency of car-following distance at the crash moment. For locations with unknown weather information, data were interpolated using the inverse squared distance method. Non-weather factors such as road geometrics, traffic conditions, collision types, vehicle types, and driver and temporal attributes were also considered. Two types of polychotomous response models were compared: ordinal logistic and sequential logistic regressions. The sequential logistic regression was tested with forward and backward ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical dissolution behaviour of armco-iron and of the steels C15, C45, C60 and 100Cr6 in concentrated sodium chloride media has been investigated. Anodic metal dissolution experiments have been carried out using the flow channel cell (parallel plate reactor), the rotating cylinder electrode (RCE) and the capillary cell. The microstructure of the steel has been varied through variation of carbon content and heat treatment (e.g. soft annealed with globular carbides or pearlitic). Current-efficiency values have been obtained by gravimetric measurements in the current-density range from i=5 to 60 A/cm{sup 2}. For the soft annealed steels, the divalent ferrite dissolution in combination with electroless cementite removal dominates. For the pearlitic steels, the occurrence of oxygen evolution electronically conductive metal carbides or trivalent ferrite dissolution, depending on the current density applied, was detected. Microstructure dependent potentiostatic current transients ...

International Nuclear Information System (INIS)

In PWR's steam generators, ''denting'' resulted from corrosion of support plate material, carbon steel is an important problem. The role of chlorides in corrosion acceleration of mild steel was studied. Corrosion tests were conducted at temperature from 100"0C to 280"0C in deaerated solutions of NaCl and MgCl_2 which are main content of sea water. 1) Solution of MgCl_2 was more corrosive than that of NaCl. The more increased in concentration of each chloride solution, the more corrosive in MgCl_2 soln. but the less corrosive in NaCl soln. 2) The rate of corrosion in the mixed solution of NaCl and MgCl_2 was governed by the concentration of MgCl_2 soln. The corrosion behaviour in sea water was suggested to be not controlled by NaCl but by MgCl_2. 3) Acidification of MgCl_2 soln. could be evaluated by experiment at 100"0C, the degree of acidification increased with increasing the concentration. However, the value of pH during corrosion was kept constant by the concentration of dissolved ...

International Nuclear Information System (INIS)

The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as ...

British Library Electronic Table of Contents (United Kingdom)

An approach to the calculation of the quantity of heat consumed in the process of coal formation is presented. The variability of this parameter in a coalification series is analyzed using coals from the Kuznetsk and Tunguska Basins as an example.

UK PubMed Central (United Kingdom)

The formation of the nicotinamide adenine dinucleotide phosphate-dependent formate dehydrogenase in Clostridium thermoaceticum is stimulated by the presence of molybdate and selenite...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

This paper addresses one source of degradation in OPV devices: the metal/organic interface. The basic approach was to study the completed device stability vs. the stability of the organic film itself as shown in subsequent devices fabricated from the films.

International Nuclear Information System (INIS)

Semiconductor properties of passive films formed on the Fe-18Cr alloy in a borate buffer solution (pH = 8.4) and 0.1 M H_2SO_4 solution were examined using a photoelectrochemical spectroscopy and an electrochemical impedance spectroscopy. Photo current reveals two photo action spectra that derived from outer hydroxide and inner oxide layers. A typical n-type semiconductor behaviour is observed by both photo current and impedance for the passive films formed in the borate buffer solution. On the other hand, a negative photo current generated, the absolute value of which decreased as applied potential increased in the sulfuric acid solution. This indicates that the passive film behaves as a p-type semiconductor. However, Mott-Schottky plot revealed the typical n-type semiconductor property. It is concluded that the passive film on the Fe-18Cr alloy formed in the borate buffer solution is composed of both ...

British Library Electronic Table of Contents (United Kingdom)

Rheological properties of moderately concentrated solutions of cellulose in methylmorpholine N-oxide-dimethylformamide mixtures containing hydrophilic montmorillonite nanoparticles were studied. Film composite materials were prepared, and their physicomechanical properties and structural organization were studied.

British Library Electronic Table of Contents (United Kingdom)

The nanostructure Ni-doped CdO films have been prepared by sol gel spin coating method. Atomic force microscopy results indicate that the CdO films are formed from the nanoparticles and the grain size is changed with nickel content. X-ray diffraction patterns of the films indicate that the undoped and Ni-doped CdO films have polycrystalline structure with a cubic sodium chloride structure, showing two main characteristic peaks assigned to the (111) and (200) planes. The optical band gap values of undoped and Ni-doped CdO films were determined by optical absorption method. The Eg values of the CdO films were found to be in the range of 2.26?2.60?eV. The Eg values of the CdO films increase with the content of Ni dopant (up to 6% Ni). It is evaluated that the optical band gap and grain size o...

Science.gov (United States)

A thin-film evaporator requires only a short heating time to concentrate a solution since it has a high thermal efficiency and has a small capacity. Thus, the chemical industry often uses this type of evaporator for concentrating materials that are subjec...

International Nuclear Information System (INIS)

Optical absorptance spectra of A-15 compounds were taken using a calorimetric technique in the range 0.2 eV to 4.0 eV. Thermomodulation spectra were taken on several A-15 sputtered films.

UK PubMed Central (United Kingdom)

An examination of the noise of polycrystalline silicon thin film transistors, in the context of flat panel x-ray imager development, is reported. The study was conducted in the spirit of exploring...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The passive films formed on iron metal, alloys or stainless steel are extremely thin oxides or hydroxides and possess the properties of high chemical stability in the environment. These films show characteristics interested both electrical as well as electrochemical point of view due to the thin thickness of the films. Auger Electron Spectroscopy, X-ray Photoelectron spectroscopy and so on which are the conventional electrochemical measurement methods or the surface analysis methods are used for the analysis and evaluation of these films, however, at present, the application of research technique focusing the superconductor characteristics of the films are tried. Although, the potential modulation reflection spectroscopy method has merits like possibility of in-situ measurement, high precision, possibility of stable analysis even for extremely thin film and so ...

Energy Technology Data Exchange (ETDEWEB)

In this work we present an ultra-low temperature method for the oxidation of an amorphous silicon-carbide-nitride (SiCN) material. The SiCN is deposited on silicon substrates by plasma enhanced chemical vapor deposition using CH{sub 4}, SiH{sub 4}, and N{sub 2} chemistry. The physical and chemical properties are characterized for the as-deposited SiCN and post-oxidized films are discussed. The SiCN film is exposed to oxygen plasma, where it undergoes a chemical transformation into a binary SiO{sub 2} material system. A 1.7 nm/min oxidation rate is typical for this process and compares favorably to oxidation methods utilizing much higher temperatures. The substrate temperature remains extremely low throughout the oxidation process, T{sub s} < 200 deg. C. Changes in film stress, optical constants, film thickness, surface roughness, and film density are measured. Chemical ...

Science.gov (United States)

... ordnance requirements. Descriptors : *Combustible cartridge cases, *Patents, Laminates, Felts, Flame inhibitors, Films. Subject ...

International Nuclear Information System (INIS)

... Toshiba Corporation, Isogo Engineering Center, Yokohama, Kanagawa (Japan)

International Nuclear Information System (INIS)

17-4PH stainless steel was modified by direct current (DC) plasma nitriding and titanium nitride film duplex treatment in this study. The microstructure, wear resistance and corrosion resistance were characterized by X-ray diffraction (XRD), pin-on-disk tribological test and polarization experiment. The results revealed that the DC plasma nitriding pretreatment was in favor of improving properties of titanium nitride film. The corrosion resistance and wear resistance of duplex treatment specimen was more superior to that of only coated titanium nitride film.

Science.gov (United States)

PMID:21671451

Energy Technology Data Exchange (ETDEWEB)

The symposium, Polycrystalline Thin Films - Structure, Texture, Properties, and Applications III, was held at the 1997 Materials Research Society Spring Meeting on March 31--April 4 in San Francisco, California. The topics and investigations were interdisciplinary in nature, and ranged from fundamental to technological. Specifically, the work presented in this volume includes film growth, texture and structural evolution, phase transformation, characterization of grain boundaries and interfaces, stress analysis, and works on polycrystalline Si and SiGe films and devices. Fifty four papers were processed separately for inclusion on the data base.

Science.gov (United States)

Demand for compact instrumentation, portable field equipment, and new electromagnetic weapons is

International Nuclear Information System (INIS)

(Jun 1982). United States Edelman, Z. Chambre, P. Eilas, E. Naot, D. Technion,

Energy Technology Data Exchange (ETDEWEB)

A temperature gradient across a thick ({ge}.1mm) film selective emitter will produce a significant reduction in the spectral emittance from the no temperature gradient case. Thick film selective emitters of rare earth doped host materials such as yttrium-aluminum-garnet (YAG) are examples where temperature gradient effects are important. In this paper a model is developed for the spectral emittance assuming a linear temperature gradient across the film. Results of the model indicate that temperature gradients will result in reductions the order of 20{percent} or more in the spectral emittance. {copyright} {ital 1997 American Institute of Physics.}

International Nuclear Information System (INIS)

(Apr 1974). Japan Murakami, Akira . Saga Univ. (Japan). Dept. of

International Nuclear Information System (INIS)

One of the main problems related to optical thin film materials used in high power laser environments is the catastrophic damage caused to them due to laser irradiation. While the influence of ion bombardment on the optical properties of oxide thin films is now a well understood subject, the morphology and crystalline behaviour of these films under ion incidence is not so well studied. Hence, it is of great importance to investigate the effects of ion bombardment during growth on the microstructure and crystalline behaviour of oxide materials.

Energy Technology Data Exchange (ETDEWEB)

Photocurrent measurements for stainless steel type 304 in the as-received condition after dc and AV (alternating voltage) passivation have confirmed that significant changes of the passive film properties occur due to AV passivation. The photocurrents were the highest for the sample treated by the AV passivation process (AVPP). The bandgap energy increased from about 2.8 to about 3.05 eV for this treatment. Very similar results have been obtained for pure chromium, which suggests that the AVPP produces a thicker passive film with a less defective nature due to a partial dehydration of the chromium oxide phase in the film.

UK PubMed Central (United Kingdom)

Background and PurposeHemodynamic insults at arterial bifurcations are hypothesized to play a key role in intracranial aneurysm formation. This study investigates...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A hydrous oxide film for the application as dielectric film is synthesized by immersion of pure aluminum in hot water. From a Rutherford backscattering analysis, the ratio of aluminum to oxygen atoms was found to be 3:2 in the anodized aluminum oxide film, and 2:1 in the hydrous oxide layer. Anodization of the hydrous oxide layer was more effective for the transition of amorphous anodic oxides to the crystalline aluminum oxides.

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning the properties of tantalum and tantalum compound films formed by sputtering techniques. Topics include processes, and electrical, magnetic, and dielectric properties of the sputtered films. Tantalum compounds studied include nitrates, oxides, and aluminides. The structural properties of sputtered films are also discussed. (Contains a minimum of 105 citations and includes a subject term index and title list.)

CERN Document Server

We study the growth of colonies of the yeast Pichia membranaefaciens on agarose film. The growth conditions are controlled in a setup where nutrients are supplied through an agarose film suspended over a solution of nutrients. As the thickness of the agarose film is varied, the morphology of the front of the colony changes. The growth of the front is modeled by coupling it to a diffusive field of inhibitory metabolites. Qualitative agreement with experiments suggests that such a coupling is responsible for the observed instability of the front.

International Nuclear Information System (INIS)

The study by impedance and photoelectrochemical measurements of passive films formed on an AISI 304 type stainless steel shows that important parameters of the electronic structure of these films are modified under #alpha# irradiation, namely: width of the space charge region, donors concentration and diffusion length for minority carriers. The consequences of #alpha# irradiation on localized corrosion processes are discussed.

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Science.gov (United States)

In the present work, a new kind of myoglobin (Mb)/Au nanoparticles composite film was fabricated on pyrolytic graphite (PG) electrodes. Oppositely charged chitosan (CS) and silica (SiO(2)) nanoparticles were alternately adsorbed on the PG surface by the electrostatic interaction between them, forming {CS/SiO(2)}(5) layer-by-layer films. Mb and HAuCl(4) in solution were then simultaneously loaded into {CS/SiO(2)}(5) films. The loaded Au(III) in the films were electrochemically reduced into Au nanoparticles, forming nanocomposite films, designated as {CS/SiO(2)}(5)-Mb-Au. Various techniques such as cyclic voltammetry (CV), square wave voltammetry (SWV), quartz crystal microbalance (QCM), electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analysis were used to characterize the films. Compared with ...

British Library Electronic Table of Contents (United Kingdom)

Deposition of CN-based films by a novel version of active screen plasma nitriding, aiming at surface modification of polymers, is reported. The approach relies on the use of pure graphite as the grid material, which was found to act both as an active screen and as a dry source of carbon atoms for the synthesis of thin films consisting mainly of a stoichiometric CN layer with columnar-type structure and dome-like nanostructured morphology.

Energy Technology Data Exchange (ETDEWEB)

A study has been made of the passive film remaining over pits on stainless steel using a high resolution transmission electron microscope. Type 305 stainless steel was passivated in a borate buffer solution and pitted in ferric chloride. Passive films formed at 0.2 V relative to a saturated calomel electrode were found to be amorphous. Films formed at higher potentials showed only broad diffraction rings. The passive film was found to cover a remnant lacy structure formed over pits passivated at 0.8 V. The metallic strands of the lace were roughly hemitubular in shape with the curved surface facing the center of the pit.

Energy Technology Data Exchange (ETDEWEB)

The passive films formed on 316L stainless steel in various NaCl solutions have been investigated by capacitance measurements (Mott-Schottky). Pitting parameters have been determined using the galvano-kinetic polarisation method. The obtained results reveal the existence of a shallow and a deep donor level localised in the band gap of the semiconducting oxide film. These energy levels are due to iron ions in the tetrahedral and octahedral positions. It also appears that the participation of the deep donor level effects the electric field. The study developed allows us to compare characteristic parameters of the electronic structure of the passive film to those related to pitting susceptibility. (authors) 25 refs.