  1. Magnetic susceptibility of Inconel alloys 718, 625, and 600 at cryogenic temperatures

    Science.gov (United States)

    Goldberg, Ira B.; Mitchell, Michael R.; Murphy, Allan R.; Goldfarb, Ronald B.; Loughran, Robert J.

    1990-01-01

    After a hydrogen fuel bleed valve problem on the Discovery Space Shuttle was traced to the strong magnetization of Inconel 718 in the armature of the linear variable differential transformer near liquid hydrogen temperatures, the ac magnetic susceptibility of three samples of Inconel 718 of slightly different compositions, one sample of Inconel 625, and on sample of Inconel 600 were measured as a function of temperature. Inconel 718 alloys are found to exhibit a spin glass state below 16 K. Inconel 600 exhibits three different magnetic phases, the lowest-temperature state (below 6 K) being somewhat similar to that of Inconel 718. The magnetic states of the Inconel alloys and their magnetic susceptibilities appear to be strongly dependent on the exact composition of the alloy.

  2. Properties and application study of Inconel alloy tube made in China

    International Nuclear Information System (INIS)

    Yang Xiang; Su Xingwan; Wen Yan

    1997-01-01

    The mech-physical properties and the corrosion resistance properties of the SG tube of Inconel alloy made in China under any conditions are briefly presented, and the test and research for bending and expending the tubes have been performed. In the process of corrosion experiments the Inconel alloy tubes were compared with that of the same kind of materials made in foreign countries. The Inconel alloy tubes have better stress corrosion resistance cracking prosperities than Inconel 600 and Incoloy 800 when they were in the solutions which contained high concentrated chlorine ion and alkali at high temperature

  3. Elevated temperature creep behavior of Inconel alloy 625

    International Nuclear Information System (INIS)

    Purohit, A.; Burke, W.F.

    1984-07-01

    Inconel 625 in the solution-annealed condition has been selected as the clad material for the fuel and control rod housing assemblies of the Upgraded Transient Reactor Test Facility (TREAT Upgrade or TU). The clad is expected to be subjected to temperatures up to about 1100 0 C. Creep behavior for the temperature range of 800 0 C to 1100 0 C of Inconel alloy 625, in four distinct heat treated conditions, was experimentally evaluated

  4. High-temperature reverse-bend fatigue strength of Inconel Alloy 625

    International Nuclear Information System (INIS)

    Purohit, A.; Greenfield, I.G.; Park, K.B.

    1983-06-01

    Inconel 625 has been selected as the clad material for Upgraded Transient Reactor Test Facility (TREAT Upgrade or TU) fuel assemblies. The range of temperatures investigated is 900 to 1100 0 C. A reverse-bend fatigue test program was selected as the most-effective method of determining the fatigue characteristics of Inconel alloy 625 sheet metal. The paper describes the reverse bend fatigue experiments, the results obtained, and the analysis of data

  5. Non-isothermal irradiation creep of nickel alloys Inconel 706 and PE-16

    International Nuclear Information System (INIS)

    Gilbert, E.R.; Chin, B.A.

    1984-06-01

    The results of in-reactor step temperature change experiments conducted on two nickel alloys, PE-16 and Inconel 706, were evaluated to determine the creep behavior under nonisothermal conditions. The effect of the temperature changes was found to be significantly different for the two alloys. Following a step temperature change, the creep rate of PE-16 adjusted to the rate found in isothermal tests at the new temperature. In contrast for Inconel 706, a reduction in temperature from 540 to 425 0 C produced a 300% increase in creep above that measured at 540 0 C in isothermal tests. The response of in-reactor creep in Inconel 706 to temperature changes was attributed to the dissolution of the gamma double-prime phase and subsequent loss of precipitation-strengthening at temperatures below 500 C

  6. High Temperature Degradation Behavior and its Mechanical Properties of Inconel 617 alloy for Intermediate Heat Exchanger of VHTR

    International Nuclear Information System (INIS)

    Jo, Tae Sun; Kim, Se Hoon; Kim, Young Do; Park, Ji Yeon

    2008-01-01

    Inconel 617 alloy is a candidate material of intermediate heat exchanger (IHX) and hot gas duct (HGD) for very high temperature reactor (VHTR) because of its excellent strength, creep-rupture strength, stability and oxidation resistance at high temperature. Among the alloying elements in Inconel 617, chromium (Cr) and aluminum (Al) can form dense oxide that act as a protective surface layer against degradation. This alloy supports severe operating conditions of pressure over 8 MPa and 950 .deg. C in He gas with some impurities. Thus, high temperature stability of Inconel 617 is very important. In this work, the oxidation behavior of Inconel 617 alloy was studied by exposure at high temperature and was discussed the high temperature degradation behavior with microstructural changes during the surface oxidation

  7. Requirements of Inconel 718 alloy for aeronautical applications

    Science.gov (United States)

    Ghiban, Brandusa; Elefterie, Cornelia Florina; Guragata, Constantin; Bran, Dragos

    2018-02-01

    The main requirements imposed by aviation components made from super alloys based on Nickel are presented in present paper. A significant portion of fasteners, locking lugs, blade retainers and inserts are manufactured from Inconel 718 alloy. The thesis describes environmental factors (corrosion), conditions of external aggression (salt air, intense heat, heavy industrial pollution, high condensation, high pressure), mechanical characteristics (tensile strength, creep, density, yield strength, fracture toughness, fatigue resistance) and loadings (tensions, compression loads) that must be satisfied simultaneously by Ni-based super alloy, compared to other classes of aviation alloys (as egg. Titanium alloys, Aluminum alloys). For this alloy the requirements are strength, durability, damage tolerance, fail safety and so on. The corrosion can be an issue, but the fatigue under high-magnitude cyclic tensile loading it what limits the lifetime of the airframe. The excellent malleability and weldability characteristics of the 718 system make the material physical properties tolerant of manufacturing processes. These characteristics additionally continue to provide new opportunities for advanced manufacturing methods.

  8. Corrosion studies and recommendation of alloys for an incinerator of glove-boxes wastes

    International Nuclear Information System (INIS)

    Devisme, F.; Garnier, M.H.

    1992-01-01

    In the framework of the development of an incineration process for high chlorinated wastes, commercial alloys have been investigated by means of parametric laboratory tests in HCl containing gas mixtures and also in field tests. Recommendations may be formulated for the three main components i.e. pyrolyser, calciner and cooler. In very low oxygen-potential atmospheres, the alloys Hastelloy C276 and Inconel 625 present the best behaviours. For the calciner, alloy Inconel 601 is more satisfactory than AISI 310 steel. As for the cooler, only the alloy Haynes 214 appears acceptable at 1100 deg C. Because of the very low stress level affecting the components, thermomechanical properties do not modify these recommendations based on corrosion behaviour

  9. Corrosion of inconel in high-temperature borosilicate glass melts containing simulant nuclear waste

    Science.gov (United States)

    Mao, Xianhe; Yuan, Xiaoning; Brigden, Clive T.; Tao, Jun; Hyatt, Neil C.; Miekina, Michal

    2017-10-01

    The corrosion behaviors of Inconel 601 in the borosilicate glass (MW glass) containing 25 wt.% of simulant Magnox waste, and in ZnO, Mn2O3 and Fe2O3 modified Mg/Ca borosilicate glasses (MZMF and CZMF glasses) containing 15 wt.% of simulant POCO waste, were evaluated by dimensional changes, the formation of internal defects and changes in alloy composition near corrosion surfaces. In all three kinds of glass melts, Cr at the inconel surface forms a protective Cr2O3 scale between the metal surface and the glass, and alumina precipitates penetrate from the metal surface or formed in-situ. The corrosion depths of inconel 601 in MW waste glass melt are greater than those in the other two glass melts. In MW glass, the Cr2O3 layer between inconel and glass is fragmented because of the reaction between MgO and Cr2O3, which forms the crystal phase MgCr2O4. In MZMF and CZMF waste glasses the layers are continuous and a thin (Zn, Fe, Ni, B)-containing layer forms on the surface of the chromium oxide layer and prevents Cr2O3 from reacting with MgO or other constituents. MgCr2O4 was observed in the XRD analysis of the bulk MW waste glass after the corrosion test, and ZrSiO4 in the MZMF waste glass, and ZrSiO4 and CaMoO4 in the CZMF waste glass.

  10. Evaluation of the IGSCC(Intergranular Stress Corrosion Cracking) resistance of inconel alloys by static potential method in high temperature and high pressure environment

    International Nuclear Information System (INIS)

    Maeng, Wan Young; Nam, Tae Woon

    1997-01-01

    Inconel alloys which have good high temperature mechanical properties and corrosion resistance have been used extensively as steam generator tube of nuclear power plants. There have been some reports on the intergranular stress corrosion cracking (IGSCC) failure problems in steam generator tubes of nuclear reactors. In order to evaluate the effects of heat treatment and composition on the IGSCC behavior of inconel alloys in simulated nuclear reactor environment, four different specimens (inconel 600 MA, 600 TT, 690 MA and 690 TT) were prepared and tested by eletrochemical method. Static potential tests for stressed C-ring type inconel specimens were carried out in 10% NaOH solution at 300 deg C (75 atm). It was found that IGSCC was initiated in inconel 600 MA specimen, but the other three specimens were not cracked. Based on the gradients of corrosion current density of the four specimens as a function of test time, thermally treated alloys show better IGSCC resistance than mull-annealed alloys, and inconel 690 TT has better passivation characteristic than inconel 600 MA. Inconel 690 TT shows clear periodic passivation that indicates good SCC resistance. The good IGSCC resistance of inconel 690 TT is due to periodic passivation characteristics of surface layer. (author)

  11. Inconel type resistive alloys based on ultrahigh purity nickel

    International Nuclear Information System (INIS)

    Matsarin, K.A.; Matsarin, S.K.

    2000-01-01

    The new nickel high-ohm alloys (ρ = 1.2-1.4 μOhm · m), containing the W, Al, Mo alloying elements in the quantity, not exceeding their solubility in a solid solution, are developed on the basis of the Inconel-type standard alloy. The optical composition of the alloy was determined by the results of the alloy was determined by the results of the electric resistance measurement and technological effectiveness indices (relative to the pressure and workable metal yield). The following optimal component concentrations were established: 14-17 %Cr; 10-12 %Fe; 0.5-1.0 %Cu; 1.0-1.5 %Mn; 0.1-0.2 %C; 0.4-0.6 %Si; 0.5-3.0 %W; 5-16 %Mo; 0.5-2.0 %Al; the remainder - Ni. The new alloys are recommended as materials for resistive elements of direct-glow cathode nodes of low capacity electron tubes [ru

  12. Selective laser melting of Inconel super alloy-a review

    Science.gov (United States)

    Karia, M. C.; Popat, M. A.; Sangani, K. B.

    2017-07-01

    Additive manufacturing is a relatively young technology that uses the principle of layer by layer addition of material in solid, liquid or powder form to develop a component or product. The quality of additive manufactured part is one of the challenges to be addressed. Researchers are continuously working at various levels of additive manufacturing technologies. One of the significant powder bed processes for met als is Selective Laser Melting (SLM). Laser based processes are finding more attention of researchers and industrial world. The potential of this technique is yet to be fully explored. Due to very high strength and creep resistance Inconel is extensively used nickel based super alloy for manufacturing components for aerospace, automobile and nuclear industries. Due to law content of Aluminum and Titanium, it exhibits good fabricability too. Therefore the alloy is ideally suitable for selective laser melting to manufacture intricate components with high strength requirements. The selection of suitable process for manufacturing for a specific component depends on geometrical complexity, production quantity, and cost and required strength. There are numerous researchers working on various aspects like metallurgical and micro structural investigations and mechanical properties, geometrical accuracy, effects of process parameters and its optimization and mathematical modeling etc. The present paper represents a comprehensive overview of selective laser melting process for Inconel group of alloys.

  13. Effects of Flux Precoating and Process Parameter on Welding Performance of Inconel 718 Alloy TIG Welds

    Science.gov (United States)

    Lin, Hsuan-Liang; Wu, Tong-Min; Cheng, Ching-Min

    2014-01-01

    The purpose of this study is to investigate the effect of activating flux on the depth-to-width ratio (DWR) and hot cracking susceptibility of Inconel 718 alloy tungsten inert gas (TIG) welds. The Taguchi method is employed to investigate the welding parameters that affect the DWR of weld bead and to achieve optimal conditions in the TIG welds that are coated with activating flux in TIG (A-TIG) process. There are eight single-component fluxes used in the initial experiment to evaluate the penetration capability of A-TIG welds. The experimental results show that the Inconel 718 alloy welds precoated with 50% SiO2 and 50% MoO3 flux were provided with better welding performance such as DWR and hot cracking susceptibility. The experimental procedure of TIG welding process using mixed-component flux and optimal conditions not only produces a significant increase in DWR of weld bead, but also decreases the hot cracking susceptibility of Inconel 718 alloy welds.

  14. A Study on Fretting Behavior in Room Temperature for Inconel Alloy 690

    Science.gov (United States)

    Kwon, Jae Do; Chai, Young Suck; Bae, Yong Tak; Choi, Sung Jong

    The initial crack under fretting condition occurs at lower stress amplitude and lower cycles of cyclic loading than that under plain fatigue condition. The fretting damage, for example, can be observed in fossil and nuclear power plant, aircraft, automobile and petroleum chemical plants etc. INCONEL alloy 690 is a high-chromium nickel alloy having excellent resistance to many corrosive aqueous media and high-temperature atmospheres. This alloy is used extensively in the industries of nuclear power, chemicals, heat-treatment and electronics. In this paper, the effect of fretting damage on fatigue behavior for INCONEL alloy 690 was studied. Also, various kinds of tests on mechanical properties such as hardness, tension and plain fatigue tests are performed. Fretting fatigue tests were carried out with flat-flat contact configuration using a bridge type contact pad and plate type specimen. Through these experiments, it is found that the fretting fatigue strength decreased about 43% compared to the plain fatigue strength. In fretting fatigue, the wear debris is observed on the contact surface, and the oblique micro-cracks are initiated at an earlier stage. These results can be used as the basic data in a structural integrity evaluation of heat and corrosion resistant alloy considering fretting damages.

  15. Microstructures and Mechanical Properties of Inconel 718 Alloy at Ultralow Temperatures

    Science.gov (United States)

    Yao, C. G.; Lv, H. J.; Yi, D. Q.; Meng, S.; Xiao, L. R.; Wang, B.

    2018-05-01

    The microstructures and mechanical properties of powder metallurgy Inconel 718 alloy were investigated in the temperatures range between 25 and - 253 °C. Tensile strength increased with the decrease in temperature, while the ductility first increased and then decreased. There was no significant change in impact toughness. When the temperature was - 253 °C, a zigzag stress-strain curve was observed for the alloy, owing to the interaction of dislocation glide and twinning, which effectively maintained the relatively good ductility.

  16. Manufacture of an Inconel pressure vessel

    International Nuclear Information System (INIS)

    Herz, H.; Iversen, K.; Stiefelhagen, B.

    1978-01-01

    The fabrication of a thermo-shock-loaded pressure vessel of high temperature nickel alloys required the individual licensing of the basic and addition materials according to the AD data sheets Contrary to the experience of Duennbleck processars, it was found that the alloy Inconel 718 in its hardened state could not be allowed due to the formation of the brittle daves phase in the welding deposit. Positive experience was acquired however with the non-hardenable alloy Inconel 625 which could be processed as jacket materials without problem. Rods of Inconel 625 were used as similar additive for WIG welding and the same type electrode 112 for E-welding. The heat resistance required of 320 N/cm 2 at 623 0 K and the lowest notch bar value of 35 J/cm 2 at RT were well surpassed. The mixed compounds of Inconel 625 and 718 were also no problem when welding with the non-hardening additives Inconel 625 and 112 and eliminating a thermal treatment. (orig.) [de

  17. Microstructure and Mechanical Properties of Inconel 625 Alloy on Low Carbon Steel by Heat Treatment after Overlay Welding

    International Nuclear Information System (INIS)

    Kim, Seungpil; Jang, Jaeho; Kim, Jungsoo; Kim, Byung Jun; Sohn, Keun Yong; Nam, Dae-Geun

    2016-01-01

    Overlay welding technique is one of methods used to improve metal mechanical properties such as strength, toughness and corrosion resistance. Generally, Inconel 625 alloy is used for overlay welding layer on low carbon steels for economic consideration. However, the method produces some problems in the microstructure of the cast structure and some defects, caused by the elevated temperatures of the overlay process. To resolve these problems, heat treatments are required. In this study, Inconel 625 alloy was welded on a low carbon steel by the overlay welding process to investigate the resulting microstructure and mechanical properties. A double heat treatment was performed to improve the mechanical properties of the welding and substrate layers. It was found that Inconel 625 alloy had an austenite microstructure after the first heat treatment, but the low carbon steel had a ferrite-pearlite microstructure after the second heat treatment. After the double heat treatment, the sample showed the optimum hardness because of grain refinement and homogenization of the microstructure.

  18. Microstructure and Mechanical Properties of Inconel 625 Alloy on Low Carbon Steel by Heat Treatment after Overlay Welding

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Seungpil; Jang, Jaeho; Kim, Jungsoo; Kim, Byung Jun; Sohn, Keun Yong; Nam, Dae-Geun [Korea Institute of Industrial Technology, Busan (Korea, Republic of)

    2016-08-15

    Overlay welding technique is one of methods used to improve metal mechanical properties such as strength, toughness and corrosion resistance. Generally, Inconel 625 alloy is used for overlay welding layer on low carbon steels for economic consideration. However, the method produces some problems in the microstructure of the cast structure and some defects, caused by the elevated temperatures of the overlay process. To resolve these problems, heat treatments are required. In this study, Inconel 625 alloy was welded on a low carbon steel by the overlay welding process to investigate the resulting microstructure and mechanical properties. A double heat treatment was performed to improve the mechanical properties of the welding and substrate layers. It was found that Inconel 625 alloy had an austenite microstructure after the first heat treatment, but the low carbon steel had a ferrite-pearlite microstructure after the second heat treatment. After the double heat treatment, the sample showed the optimum hardness because of grain refinement and homogenization of the microstructure.

  19. Comparison of Inconel 625 and Inconel 600 in resistance to cavitation erosion and jet impingement erosion

    International Nuclear Information System (INIS)

    Hu, H.X.; Zheng, Y.G.; Qin, C.P.

    2010-01-01

    Liquid droplet erosion (LDE), which often occurs in bellows made of nickel-based alloys, threatens the security operation of the nuclear power plant. As the candidate materials of the bellows, Inconel 600 and Inconel 625 were both tested for resistance to cavitation erosion (CE) and jet impingement erosion (JIE) through vibratory cavitation equipment and a jet apparatus for erosion-corrosion. Cumulative mass loss vs. exposure time was used to evaluate the erosion rate of the two alloys. The surface and cross-sectional morphologies before and after the erosion tests were observed by scanning electron microscopy (SEM), the inclusions were analyzed by an energy dispersive spectroscopy (EDS), and the surface roughness was also measured by surface roughness tester to illustrate the evolution of erosion process. The results show that the cumulative mass loss of CE of Inconel 625 is about 1/6 that of Inconel 600 and the CE incubation period of the Inconel 625 is 4 times as long as that of the Inconel 600. The micro-morphology evolution of CE process illustrates that the twinning and hardness of the Inconel 625 plays a significant role in CE. In addition, the cumulative mass loss of JIE of Inconel 625 is about 2/3 that of Inconel 600 at impacting angle of 90 o , and almost equal to that of the Inconel 600 at impacting angle of 30 o . Overall, the resistance to CE and JIE of Inconel 625 is much superior to that of Inconel 600.

  20. Comparison of Inconel 625 and Inconel 600 in resistance to cavitation erosion and jet impingement erosion

    Energy Technology Data Exchange (ETDEWEB)

    Hu, H.X. [State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Science, 62 Wencui Road, Shenyang 110016 (China); Zheng, Y.G., E-mail: ygzheng@imr.ac.c [State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Science, 62 Wencui Road, Shenyang 110016 (China); Qin, C.P. [State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Science, 62 Wencui Road, Shenyang 110016 (China)

    2010-10-15

    Liquid droplet erosion (LDE), which often occurs in bellows made of nickel-based alloys, threatens the security operation of the nuclear power plant. As the candidate materials of the bellows, Inconel 600 and Inconel 625 were both tested for resistance to cavitation erosion (CE) and jet impingement erosion (JIE) through vibratory cavitation equipment and a jet apparatus for erosion-corrosion. Cumulative mass loss vs. exposure time was used to evaluate the erosion rate of the two alloys. The surface and cross-sectional morphologies before and after the erosion tests were observed by scanning electron microscopy (SEM), the inclusions were analyzed by an energy dispersive spectroscopy (EDS), and the surface roughness was also measured by surface roughness tester to illustrate the evolution of erosion process. The results show that the cumulative mass loss of CE of Inconel 625 is about 1/6 that of Inconel 600 and the CE incubation period of the Inconel 625 is 4 times as long as that of the Inconel 600. The micro-morphology evolution of CE process illustrates that the twinning and hardness of the Inconel 625 plays a significant role in CE. In addition, the cumulative mass loss of JIE of Inconel 625 is about 2/3 that of Inconel 600 at impacting angle of 90{sup o}, and almost equal to that of the Inconel 600 at impacting angle of 30{sup o}. Overall, the resistance to CE and JIE of Inconel 625 is much superior to that of Inconel 600.

  1. Influence of microstructure in corrosion behavior of an Inconel 600 commercial alloy in 0.1 M sodium thiosulfate solution

    International Nuclear Information System (INIS)

    Granados, J.; Rodriguez, F.J.; Arganis, C.

    1999-01-01

    The Inconel 600 is used in diverse components of BWR and PWR type reactors, where diverse cases of intergranular stress corrosion have been presented. It has been reported susceptibility to the corrosion of this alloy, in presence of thiosulfates, which come from the degradation of the ion exchange resins of water treatments that use the reactors. The objective of this work is to study the influence of metallurgical condition in the corrosion velocity of Inconel 600 commercial alloy, in a 0.1 M thiosulfates solution. (Author)

  2. Development of the advanced nuclear materials -Development of Inconel alloys-

    International Nuclear Information System (INIS)

    Kuk, Il Hyun; Chang, Jin Sung; Lee, Chang Kyu; Park, Soon Dong; Kim, Woo Kon; Jeong, Man Kyo; Woo, Yoon Myung; Han, Chang Hee

    1995-07-01

    The performance and the integrity of the steam generator U-tubes directly affects the efficiency and economics of nuclear power plant because they are closely interrelated with the maintenance and repair. Also the steam generator U-tubes have been one of world-wide hot issues in nuclear power plants for long time because of their continuing corrosion-related degradation. Right after stress corrosion cracking of Alloy 600 tubes are reported at primary side, in which the environment is believed to be tightly controlled all the time, in mid 80's, alloy 690 has started to replace alloy 600. Alloy 690 is basically same with alloy 600 except more Cr content. Firstly minor elements in alloy 690 (C, B, N, Y, Mo) were added or controlled to improve hot workability and corrosion resistance. It would be much more desirable if the mechanism or basic understanding of the degradation phenomena of steam generator U-tubes in operation conditions can be illuminated through the alloy modification research. Alloy 600 tubes which were preproduced in cooperation with Sammi Special Steel were evaluated, being compared with imported one. Also alloy 600 and alloy 690 tubes were produced from Inconel 600 and 690 INCO- forged bar. These will be closely evaluated with purely Korean-made alloy 600 and 690 tubes. 22 tabs., 93 figs., 14 refs. (Author)

  3. The electrochemical polishing behavior of the Inconel 718 alloy in perchloric-acetic mixed acids

    International Nuclear Information System (INIS)

    Huang, C.A.; Chen, Y.C.; Chang, J.H.

    2008-01-01

    The electropolishing behavior of the Inconel 718 alloy was studied by using rotating disc electrode (RDE) in the HClO 4 -CH 3 COOH mixed acids with different HClO 4 -concentrations. After electropolishing, surface morphologies of RDE specimens were examined with surface profiler, atomic force microscope and scanning electron microscope. According to the surface morphologies observed, three types of anodic dissolution behavior can be characterized in relation to the HClO 4 -content in mixed acids; namely, leveling without brightening of the surface in the mixed acids with 10 and 20 vol% HClO 4 , leveling and brightening of the surface in the mixed acids with 30 and 40 vol% HClO 4 , and a matt and gray surface in the mixed acids with 50 vol% or more HClO 4 . Anodic dissolution in the first and second dissolution types follows a mass-transfer controlled mechanism, in which a linear relationship between the reciprocal of limiting-current density and the reciprocal of square root of rotating speed of RDE specimen can be detected. Owing to precipitation of salt film on the polished surface of the Inconel 718 material, saturated dissolved metallic ions could be the chemical species for the mass-controlled mechanism. The salt film, in addition, could enhance the corrosion resistance of the Inconel 718 alloy

  4. Stress-corrosion cracking of Inconel alloy 600 in high-temperature water: an update

    International Nuclear Information System (INIS)

    Bandy, R.; van Rooyen, D.

    1983-01-01

    Inconel 600 has been tested in high-temperature aqueous media (without oxygen) in several tests. Data are presented to relate failure times to periods of crack initiation and propagation. Quantitative relationships have been developed from tests in which variations were made in temperature, applied load, strain rate, water chemistry, and the condition of the test alloy

  5. Microstructure Stability of Inconel 740H Alloy After Long Term Exposure at 750℃

    Directory of Open Access Journals (Sweden)

    DANG Ying-ying

    2016-09-01

    Full Text Available Unstressed exposure tests of Inconel 740H alloy tube were carried out at 750℃ for 500-3000h. The microstructure evolution and microhardness were studied by means of thermodynamic simulation, OM, FEG-SEM and microhardness testing. The results show that the tube is qualified if both chemical composition and tensile properties of the as-received alloy meet the corresponding requirements of ASME. After long term exposure, the main precipitates are γ' and M23C6, and no η and σ phase. With the prolonging of exposure time, the coarsening of γ' becomes faster and the law of relationship between the radius of γ' and time accords with LSW Ostwald ripening law; meanwhile, the change in size of M23C6 is not so obvious. During the whole process, microhardness increases firstly and then decreases, but the fluctuation is slight. The changes of microstructure and hardness indicate that, after long time exposure, the domestic Inconel 740H has good stability and can be used for further carrying out the investigation on the mechanical property of creep-rupture.

  6. Effect of microstructure on properties of friction stir welded Inconel Alloy 600

    International Nuclear Information System (INIS)

    Sato, Y.S.; Arkom, P.; Kokawa, H.; Nelson, T.W.; Steel, R.J.

    2008-01-01

    Friction stir welding (FSW) has been widely used to metals with moderate melting temperatures, primarily Al alloys. Recently, tool materials that withstand high stresses and temperatures necessary for FSW of materials with high melting temperatures have been developed. In the present study, polycrystalline cubic boron nitride (PCBN) tool was used for partially penetrated FSW of Inconel Alloy 600, and a defect-free weld was successfully produced. Microstructural characteristics, mechanical and corrosion properties in the weld were examined. The weld had better mechanical properties than the base material due to formation of fine grain structure in the stir zone, but exhibited slightly the lower corrosion resistance in a part of the stir zone and heat-affected zone (HAZ)

  7. Sliding wear and friction behavior of zirconium alloy with heat-treated Inconel718

    Energy Technology Data Exchange (ETDEWEB)

    Kim, J.H., E-mail: kimjhoon@cnu.ac.kr [Dept. of Mechanical Design Engineering, Chungnam National University, 99 Daehak-ro, Yuseong-gu, Daejeon 305-764 (Korea, Republic of); Park, J.M. [Dept. of Mechanical Design Engineering, Chungnam National University, 99 Daehak-ro, Yuseong-gu, Daejeon 305-764 (Korea, Republic of); Park, J.K.; Jeon, K.L. [Nuclear Fuel Technology Department, Korea Nuclear Fuel, 1047 Daedukdae-ro, Yuseong-gu, Daejeon 305-353 (Korea, Republic of)

    2014-04-01

    In water-cooled nuclear reactors, the sliding of fuel rod can lead to severe wear and it is an important issue to sustain the structural integrity of nuclear reactor. In the present study, sliding wear behavior of zirconium alloy in dry and water environment using Pin-On-Disk sliding wear tester was investigated. Wear resistance of zirconium alloy against heat-treated Inconel718 pin was examined at room temperature. Sliding wear tests were carried out at different sliding distance, axial load and sliding speed based on ASTM (G99-05). The results of these experiments were verified with specific wear rate and coefficient of friction. The micro-mechanisms responsible for wear in zirconium alloy were identified to be microcutting and microcracking in dry environment. Moreover, micropitting and delamination were observed in water environment.

  8. Study of electrochemical corrosion characteristics of Inconel alloys with addition of trace elements

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Sung Goon; Park, In Ho; Lee, Sang Hoon [Hanyang University, Seoul (Korea)

    2002-04-01

    Inconel alloys which have high temperature mechanical properties and corrosion resistance have been used extensively as steam generator tube of nuclear power plants. But, since environments of steam generator are high temperature and pressure, there have been many reports of the damage cases of steam generators which are made with Inconel 600. The failure through corrosion of steam generator's parts made with Inconel alloy became generally known because of IGSCC result from Cr depletion zone. Therefore, the development of materials added element which obstructs formation of Cr depletion zone on grainboundary were imminent, we intended to investigate the effects on known prevention and different prevention mechanism of corrosion according to added amount of Nb known as proper inhibitor against SCC. Specimens used to experiment were divided into heat treatment(SA and SA SEN) and added amount of Nb(0, 2, 4, 6%), when DL-EPR Tests (measurement of degree of sensitization were executed, composition of electrolyte is aqueous solution mixed 0.5M H2SO4 and 5ppm KSCN , electrolytes were aqueous solution mixed 10% NaOH on potentiodynamic and potentiostatic tests at RT and high temperature. As a result of experiment, degree of sensitization of SA heat treated specimens was lower than that of SA SEN heat treated specimens. According to added Nb, degree of sensitization of specimens over 2% Nb were similar. There is no particularly different experimental results through added element, heat treatment on potentiondynamic and potentiostatic experiments at RT and high temperature. Although heat treatment and added amount of Nb affected a little degree of grainboundary sensitization, these experimental factors didn't have effects on forming the passive film. 13 refs., 19 figs. (Author)

  9. Comparison the machinability of Inconel 718, Inconel 625 and Monel 400 in hot turning operation

    Directory of Open Access Journals (Sweden)

    Asit Kumar Parida

    2018-06-01

    Full Text Available In the present paper, three nickel base alloys (Inconel 718, Inconel 625 and Monel-400 have been studied for chip formation in the hot turning process using flame heating. Cutting force, tool life, chip morphology, tool wear, and surface integrity (surface roughness and microhardness beneath the machined surface have been determined in both room and hot temperature conditions (300 °C and 600 °C. Flame heating (Liquefied petroleum gas and oxygen along with turning operation has been utilized for machining of three materials. It was observed that significant reduction of cutting force, tool wear, chatter formation, surface roughness and increase tool life, chip tool contact length, etc., for all three nickel base alloys in hot machining compared to room temperature machining. Keywords: Hot turning, Nickel base alloys, Machinability, Cutting forces, Tool wear

  10. Surface Roughness and Tool Wear on Cryogenic Treated CBN Insert on Titanium and Inconel 718 Alloy Steel

    International Nuclear Information System (INIS)

    Thamizhmanii, S; Mohideen, R; Zaidi, A M A; Hasan, S

    2015-01-01

    Machining of materials by super hard tools like cubic boron nitride (cbn) and poly cubic boron nitride (pcbn) is to reduce tool wear to obtain dimensional accuracy, smooth surface and more number of parts per cutting edge. wear of tools is inevitable due to rubbing action between work material and tool edge. however, the tool wear can be minimized by using super hard tools by enhancing the strength of the cutting inserts. one such process is cryogenic process. this process is used in all materials and cutting inserts which requires wear resistance. the cryogenic process is executed under subzero temperature -186° celsius for longer period of time in a closed chamber which contains liquid nitrogen. in this research, cbn inserts with cryogenically treated was used to turn difficult to cut metals like titanium, inconel 718 etc. the turning parameters used is different cutting speeds, feed rates and depth of cut. in this research, titanium and inconel 718 material were used. the results obtained are surface roughness, flank wear and crater wear. the surface roughness obtained on titanium was lower at high cutting speed compared with inconel 718. the flank wear was low while turning titanium than inconel 718. crater wear is less on inconel 718 than titanium alloy. all the two materials produced saw tooth chips. (paper)

  11. Microstructure and micro-texture evolution during large strain deformation of Inconel alloy IN718

    Energy Technology Data Exchange (ETDEWEB)

    Nayan, Niraj [Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Trivandrum 695 022 (India); Gurao, N.P. [Department of Materials Science and Engineering, Indian Institute of Technology, Kanpur 208 016 (India); Narayana Murty, S.V.S., E-mail: susarla.murty@gmail.com [Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Trivandrum 695 022 (India); Jha, Abhay K.; Pant, Bhanu; George, Koshy M. [Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Trivandrum 695 022 (India)

    2015-12-15

    The hot deformation behaviour of Inconel alloy IN718 was studied in the temperature range of 950–1100 °C and at strain rates of 0.01 and 1 s{sup −1} with a view to understand the microstructural evolution as a function of strain rate and temperature. For this purpose, a single hit, hot isothermal plane strain compression (PSC) technique was used. The flow curves obtained during PSC exhibited weak flow softening at higher temperatures. Electron backscattered diffraction analysis (EBSD) of the PSC tested samples at the location of maximum strain revealed dynamic recrystallisation occurring at higher temperatures. Based on detailed microstructure and microtexture analyses, it was concluded that single step, large strain deformation has a distinct advantage in the thermo-mechanical processing of Inconel alloy IN718. - Highlights: • Plane strain compression (PSC) on IN718 was conducted. • Evolution of microstructure during large strain deformation was studied. • Flow curves exhibited weak softening at higher temperatures and dipping of the flow curve at a strain rate of 1 s{sup −1}. • Optimization of microstructure and process parameter for hot rolling possible by plane strain compression testing • Dynamic recrystallisation occurs in specimens deformed at higher temperatures and lower strain rates.

  12. Weldability of Inconel 718 - a review

    International Nuclear Information System (INIS)

    Muralidharan, B.G.; Shankar, V.; Gill, T.P.S.

    1996-01-01

    The report discusses the main issues related to weldability of Inconel 718. How the problem of strain age cracking during post weld treatment is avoided in this alloy has also been discussed. It also elaborates phases present in the alloys of 718 and its solidification metallurgy

  13. The fatigue and corrosion fatigue behavior of welded Inconel 625 alloy employed in off-shore platforms; Avaliacao do comportamento a fadiga e a corrosao-fadiga de juntas soldadas da liga Inconel 625 testada para uso em plaaformas off-shore

    Energy Technology Data Exchange (ETDEWEB)

    Pfingstag, M.E.; Schroeder, R.M.; Mueller, I.L. [Universidade Federal do Rio Grande do Sul (LAPEC/UFRGS), Porto Alegre, RS (Brazil). Dept. de Metalurgia. Lab. de Pesquisa em Corrosao], e-mail: maiquel10@walla.com

    2006-07-01

    The fatigue and corrosion fatigue behavior of welded Inconel 625 employed live like risers in off-shore platforms was studied. These risers may be employed integrally of this alloy, or combined with API 52 X60 steel in the form of 'Clads'. One of the most susceptible points in .these structures is the circumferential weld that joint the pipes together. In these regions, stresses and defects are generated by the welding process, and these material remind in contact with aggressive species like, chlorides and Co{sub 2} . Polarization curves, slow strain rate fatigue and corrosion fatigue tests were used to characterize the Inconel alloy behavior. In the welded deposit condition, this alloy shows an excellent resistance corrosion and a good fatigue and corrosion-fatigue behavior.(author)

  14. Investigation on wear resistance and corrosion resistance of electron beam cladding co-alloy coating on Inconel617

    Science.gov (United States)

    Liu, Hailang; Zhang, Guopei; Huang, Yiping; Qi, Zhengwei; Wang, Bo; Yu, Zhibiao; Wang, Dezhi

    2018-04-01

    To improve surface properties of Inconel 617 alloy (referred to as 617 alloy), co-alloy coating metallurgically bonded to substrate was prepared on the surface of 617 alloy by electron beam cladding. The microstructure, phase composition, microhardness, tribological properties and corrosion resistance of the coatings were investigated. The XRD results of the coatings reinforced by co-alloy (Co800) revealed the presence of γ-Co, CoCx and Cr23C6 phase as matrix and new metastable phases of Cr2Ni3 and Co3Mo2Si. These hypoeutectic structures contain primary dendrites and interdendritic eutectics. The metallurgical bonding forms well between the cladding layer and the matrix of 617 alloy. In most studied conditions, the co-alloy coating displays a better hardness, tribological performance, i.e., lower coefficient of frictions and wear rates, corrosion resistance in 1 mol L‑1 HCl solution, than the 617 alloy.

  15. ANALYSIS OF PITTING CORROSION ON AN INCONEL 718 ALLOY SUBMITTED TO AGING HEAT TREATMENT

    Directory of Open Access Journals (Sweden)

    Felipe Rocha Caliari

    2014-10-01

    Full Text Available Inconel 718 is one of the most important superalloys, and it is mainly used in the aerospace field on account of its high mechanical strength, good resistance to fatigue and creep, good corrosion resistance and ability to operate continuously at elevated temperatures. In this work the resistance to pitting corrosion of a superalloy, Inconel 718, is analyzed before and after double aging heat treatment. The used heat treatment increases the creep resistance of the alloy, which usually is used up to 0.6 Tm. Samples were subjected to pitting corrosion tests in chloride-containing aqueous solution, according to ASTM-F746-04 and the procedure described by Yashiro et al. The results of these trials show that after heat treatment the superalloy presents higher corrosion resistance, i.e., the pitting corrosion currents of the as received surfaces are about 6 (six times bigger (~0.15 mA than those of double aged surfaces (~0.025 mA.

  16. High cycle fatigue properties of inconel 690

    International Nuclear Information System (INIS)

    Lee, Young Ho; Lee, Byong Whi; Kim, In Sup; Park, Chi Yong

    1997-01-01

    Inconel 690 is presently used as sleeve material and a replacement alloy in degraded steam generators, as well as the material for new steam generators. But Inconel 690 has low thermal conductivity which are 3-8% less than that of Inconel 600 at operating temperature. For the same power output, conduction area must be increased. As a result, more fluid induced vibration can cause a fatigue damage of Inconel 690. High cycle fatigue ruptures occurred in the U-bend regions of North Anna Unit 1 and Mihama Unit 2 steam generators. At this study, the effect of temperature on fatigue crack growth rate in Inconel 690 steam generator tube was investigated at various temperature in air environment. With increasing temperature, fatigue crack growth rate increased and grain size effect decreased. Chromium carbides which have large size and semi-continuous distribution in the grain boundaries decreased fatigue crack growth rate

  17. Corrosion Performance of Inconel 625 in High Sulphate Content

    Science.gov (United States)

    Ismail, Azzura

    2016-05-01

    Inconel 625 (UNS N06625) is a type of nickel-chromium-molybdenum alloy with excellent corrosion resistance in a wide range of corrosive media, being especially resistant to pitting and crevice corrosion. However, in aggressive environment, Inconel 625 will suffer corrosion attack like other metals. This research compared the corrosion performance of Inconel 625 when exposed to higher sulphate content compared to real seawater. The results reveal that Inconel 625 is excellent in resist the corrosion attack in seawater. However, at increasing temperature, the corrosion resistance of this metal decrease. The performance is same in seawater with high sulphate content at increasing temperature. It can be concluded that sulphate promote perforation on Inconel 625 and become aggressive agents that accelerate the corrosion attack.

  18. Mechanisms of plastic deformation (cyclic and monotonous) of Inconel X750

    International Nuclear Information System (INIS)

    Randrianarivony, H.

    1992-01-01

    Plastic deformation mechanisms under cyclic or monotonous solicitations, are analysed in function of Inconel X750 initial macrostructure. Two heat treated Inconel (first one is treated at 1366 K one hour, air cooled, aged at 977 K 20 hours, and air cooled, the second alloy is aged at 1158 K 24 hours, air cooled, aged at 977 K 20 hours, and air cooled), are characterized respectively by a fine and uniform precipitation of the γ' phase (approximative formulae: Ni 3 (Al,Ti)), and by a bimodal distribution of γ' precipitates. In both alloys, dislocations pairs (characteristic of a shearing by antiphase wall creation) are observed, and the crossing mechanism of the γ' precipitates by creation of overstructure pile defects is the same. But, glissile loops dislocations are less numerous than dislocations pairs in the first alloy, involving denser bands structure for this alloy (dislocations loops are always observed around γ' precipitates). Some comportment explications of Inconel X750 in PWR medium are given. (A.B.). refs., figs., tabs

  19. The interaction of reaction-bonded silicon carbide and inconel 600 with a nickel-based brazing alloy

    Science.gov (United States)

    McDermid, J. R.; Pugh, M. D.; Drew, R. A. L.

    1989-09-01

    The objective of the present research was to join reaction-bonded silicon carbide (RBSC) to INCONEL 600 (a nickel-based superalloy) for use in advanced heat engine applications using either direct brazing or composite interlayer joining. Direct brazing experiments employed American Welding Society (AWS) BNi-5, a commercial nickel-based brazing alloy, as a filler material; composite interlayers consisted of intimate mixtures of α-SiC and BNi-5 powders. Both methods resulted in the liquid filler metal forming a Ni-Si liquid with the free Si in the RBSC, which, in turn, reacted vigorously with the SiC component of the RBSC to form low melting point constituents in both starting materials and Cr carbides at the metal-ceramic interface. Using solution thermodynamics, it was shown that a Ni-Si liquid of greater than 60 at. pct Ni will decompose a-SiC at the experimental brazing temperature of 1200 ‡C; these calculations are consistent with the experimentally observed composition profiles and reaction morphology within the ceramic. It was concluded that the joining of RBSC to INCONEL 600 using a nickel-based brazing alloy is not feasible due to the inevitability of the filler metal reacting with the ceramic, degrading the high-temperature properties of the base materials.

  20. Dynamic strain ageing in Inconel® Alloy 783 under tension and low cycle fatigue

    International Nuclear Information System (INIS)

    Nagesha, A.; Goyal, Sunil; Nandagopal, M.; Parameswaran, P.; Sandhya, R.; Mathew, M.D.; Mannan, Sarwan K.

    2012-01-01

    Highlights: ► Low cycle fatigue (LCF) and tensile tests were performed on Inconel ® Alloy 783. ► A stable cyclic stress response followed by continuous softening was noted under LCF. ► Material exhibited DSA in the temperature range, 573–723 K. ► Occurrence of DSA reduced the extent of cycling softening in LCF. ► Both interstitial and substitutional atoms were found to be responsible for DSA. - Abstract: Low cycle fatigue (LCF) tests were performed on Inconel ® Alloy 783 at a strain rate of 3 × 10 −3 s −1 and a strain amplitude of ±0.6%, employing various temperatures in the range 300–923 K. A continuous reduction in the LCF life was observed with increase in the test temperature. The material generally showed a stable stress response followed by a region of continuous softening up to failure. However, in the temperature range of 573–723 K, the alloy was seen to exhibit dynamic strain ageing (DSA) which was observed to reduce the extent of cyclic softening. With a view to identifying the operative mechanisms responsible for DSA, tensile tests were conducted at temperatures in the range, 473–798 K with strain rates varying from 3 × 10 −5 s −1 to 3 × 10 −3 s −1 . Interaction of dislocations with interstitial (C) and substitutional (Cr) atoms respectively, in the lower and higher temperature regimes was found to be responsible for DSA. Further, the friction stress, as determined using the stabilised stress–strain hysteresis loops, was seen to show a more prominent peak in the DSA range, compared to the maximum tensile stress.

  1. Corrosion Test Results for Inconel 600 vs Inconel-Stainless UG Bellows

    International Nuclear Information System (INIS)

    Osborne, P.E.

    2002-01-01

    The Conversion Project (CP) of the Molten Salt Reactor Experiment at Oak Ridge National Laboratory (ORNL) involves converting slightly less than 40 kg of 233 U to a stable form for safe storage. The operation is performed within a few vessels interconnected by valves and 1/2-in. metal tubing. During this conversion, a particularly toxic and corrosive by-product is formed, namely aqueous hydrofluoric acid (HF). The production of HF is a result of the hydrolysis of UF 6 and subsequent steam treatments of UO 2 F 2 . For each mole of UF 6 converted, 6 mol of HF are produced. The HF that forms during conversion combines with water to produce approximately 1.5 L of 33 wt % HF. As this mixture is transferred within the process system, the tubing and valves are exposed to high concentrations of HF in liquid and vapor form. Of particular concern in the system are the almost 30 valves that have the potential for exposure to HF. For these valves, a vendor-supplied UG valve was installed. UG valves consist of an Alloy 400 (Monel) body and stem tip and Alloy 600 (Inconel) bellows. These valves have been used under experimental conditions that simulate the CP. It has been established that they have a finite life when exposed to a HF and air environment. Most failures were seen around the flange at the bottom of the bellows, and it was suspected that this flange and the weld material were not Inconel. In December 2001, the vendor confirmed that this flange was not Inconel but instead was stainless steel 316. After discussions between the vendor and ORNL staff involved with the CP effort, it was decided that the entire wetted area of the bellows would be fabricated from Alloy 600. In March 2002, four newly fabricated bellows assemblies were received from the vendor for the purposes of corrosion testing in HF. This report presents results from the corrosion tests conducted to determine if the new design of the bellows would enhance their corrosion resistance

  2. Bending of pipes with inconel cladding; Curvamento de tubos revestidos com inconel

    Energy Technology Data Exchange (ETDEWEB)

    Nachpitz, Leonardo; Menezes, Carlos Eduardo B; Vieira, Carlos R. Tavares [PROTUBO, Macae, RJ (Brazil)

    2008-07-01

    The pipes used in offshore equipment, such as wet Christmas trees, sub sea manifolds and rigid platform risers, as well as some pipes for refineries and ships, must have mechanical resistance to high pressure and also be resistant to corrosion from acids. Some special materials, such as stainless steel, duplex and super duplex steel are used to resolve this problem, but the cost is very high. Besides the problem of cost, these materials have other drawbacks, such as the difficulty of welding them, a technology mastered in few countries. As a better alternative, the use has been increasing of carbon steel and API pipes coated internally with inconel by welding deposition. This groundbreaking technology, of proven efficiency, has a far superior cost-benefit relation. Carbon steel and API pipes, besides having better mechanical resistance to high pressure and corrosion resistance, can be fabricated with technology mastered worldwide. Nickel alloys, such as inconel, are highly resistant to corrosion and temperature, and in these aspects are better than stainless steels. The pipes for transportation equipment and for refining hydrocarbons, as mentioned above, require various turns and special geometries, which generally are solved by the use of bends and spools made by high-frequency induction. This technology, already well established for various carbon and stainless steels, was developed to work with pipes coated internally with inconel (inconel cladding). Therefore, our work describes the process of fabricating bends from API steel pipes with inconel cladding, demonstrating the efficacy of this technology along with its quality gains and cost reduction. (author)

  3. Hot corrosion behavior of Ni based Inconel 617 and Inconel 738 superalloys

    Energy Technology Data Exchange (ETDEWEB)

    El-Awadi, G.A., E-mail: gaberelawdi@yahoo.com [Atomic Energy Authority, NRC, Cyclotron Project, Abo-zabal, 13759 Cairo (Egypt); Abdel-Samad, S., E-mail: salem_abdelsamad@yahoo.com [Atomic Energy Authority, NRC, Cyclotron Project, Abo-zabal, 13759 Cairo (Egypt); Elshazly, Ezzat S. [Atomic Energy Authority, NRC, Metallurgy Dept., Abo-zabal, 13759 Cairo (Egypt)

    2016-08-15

    Highlights: • Supperalloy good resistance to high temperature oxidation. • Ni-base alloy IN738 and Inconel 617 good resistance to hot corrosion. • Corrosion resistance of supperalloys depending on environment of abrasive ions such as (NaCl or NaSO{sub 4}). • Hot corrosion resistance depend on what the oxides phases where formed. - Abstract: Superalloys are extensively used at high temperature applications due to their good oxidation and corrosion resistance properties in addition to their high stability were made at high temperature. Experimental measurements of hot corrosion at high temperature of Inconel 617 and Inconel 738 superalloys. The experiments were carried out at temperatures 700 °C, 800 °C and 900 °C for different exposure times to up to 100 h. The corrosive media was NaCl and Na{sub 2}SO{sub 4} sprayed on the specimens. Seven different specimens were used at each temperature. The corrosion process is endothermic and the spontaneity increased by increasing temperature. The activation energy was found to be Ea = 23.54 and E{sub a} = 25.18 KJ/mol for Inconel 738 and Inconel 617 respectively. X-ray diffraction technique (XRD) was used to analyze the formed scale. The morphology of the specimen and scale were examined by scanning electron microscopy (SEM). The results show that the major corrosion products formed were NiCr{sub 2}O{sub 4}, and Co Cr{sub 2}O{sub 4} spinles, in addition to Cr{sub 2}O{sub 3}.

  4. Thermo-Physical Properties of Selected Inconel

    Directory of Open Access Journals (Sweden)

    Krajewski P.K.

    2014-10-01

    Full Text Available The paper brings results of examinations of main thermo-physical properties of selected Inconel alloys, i.e. their heat diffusivity, thermal conductivity and heat capacity, measured in wide temperature range of 20 – 900 oC. Themathematical relationships of the above properties vs. temperature were obtained for the IN 100 and IN 713C alloys. These data can be used when modelling the IN alloys solidification processes aimed at obtaining required structure and properties as well as when designing optimal work temperature parameters.

  5. Ring ductility of irradiated Inconel 706 and Nimonic PE16

    International Nuclear Information System (INIS)

    Huang, F.H.; Fish, R.L.

    1984-01-01

    The tensile ductility of fast neutron-irradiated, precipitation-hardened alloys Inconel 706 and Nimonic PE16 has been observed to be very low for certain test conditions. Explanations for the low ductility behavior have been sought by examination of broken tensile specimens with microscopy and other similar techniques. A ring compression test provides a method of evaluating the ductility of irradiated cladding specimens. Unlike the conventional uniaxial tensile testing in which the tensile specimen is deformed uniformly, the ring specimen is subjected to localized bending where the crack is initiated. The ductility can be estimated through an analysis of the bending of a ring in terms of strain hardening. Ring sections from irradiated, solution-treated Inconel 706 and Nimonic PE16 were compressed in the diametral direction to provide load-deflection records over a wide range of irradiation and test temperatures. Results showed that ductility in both alloys decreased with increasing test temperatures. The poorest ductility was exhibited at different irradiation temperatures in the two alloys - near 550 0 C for PE16 and 460 to 520 0 C for Inconel 706. The ring ductility data indicate that the grain boundary strength is a major factor in controlling the ductility of the PE16 alloy

  6. ANALYSIS OF THE SURFACE PROFILE AND ITS MATERIAL SHARE DURING THE GRINDING INCONEL 718 ALLOY

    Directory of Open Access Journals (Sweden)

    Martin Novák

    2015-05-01

    Full Text Available Grinding is still an important method for surface finishing. At FPTM JEPU research, which deals with this issue is conducted. Experiments are carried out with grinding various materials under different conditions and then selected components of the surface integrity are evaluated. They include roughness Ra, Rm and Rz, Material ratio curve (Abbott Firestone curve and also the obtained roundness. This article deals with grinding nickel Inconel 718 alloy, when selected cutting grinding conditions were used and subsequently the surface profile and the material ratio curve were measured and evaluated.

  7. Variation of microstructures and mechanical properties of hot heading process of super heat resisting alloy Inconel 718

    International Nuclear Information System (INIS)

    Choi, Hong Seok; Ko, Dae Chul; Kim, Byung Min

    2007-01-01

    Metal forming is the process changing shapes and mechanical properties of the workpiece without initial material reduction through plastic deformation. Above all, because of hot working carried out above recrystallization temperature can be generated large deformation with one blow, it can produce with forging complicated parts or heat resisting super alloy such as Inconel 718 has the worst forgeability. In this paper, we established optimal variation of hot heading process of the Inconel 718 used in heat resisting component and evaluated mechanical properties hot worked product. Die material is SKD61 and initial temperature is 300 .deg. C. Initial billet temperature and punch velocity changed, relatively. Friction coefficient is 0.3 as lubricated condition of hot working. CAE is carried out using DEFORM software before marking the tryout part, and it is manufactured 150 ton screw press with optimal condition. It is know that forming load was decreased according to decreasing punch velocity

  8. Quality-productivity decision making when turning of Inconel 718 aerospace alloy: A response surface methodology approach

    Directory of Open Access Journals (Sweden)

    Hamid Tebassi

    2017-06-01

    Full Text Available Inconel 718 is among difficult to machine materials because of its abrasiveness and high strength even at high temperature. This alloy is mainly used in aircraft and aerospace industries. Therefore, it is very important to reveal and evaluate cutting tools behavior during machining of this kind of alloy. The experimental study presented in this research work has been carried out in order to elucidate surface roughness and productivity mathematical models during turning of Inconel 718 superalloy (35 HRC with SiC Whisker ceramic tool at various cutting parameters (depth of cut, feed rate, cutting speed and radius nose. A small central composite design (SCCD including 16 basics runs replicated three times (48 runs, was adopted and graphically evaluated using Fraction of design space (FDS graph, completed by a statistical analysis of variance (ANOVA. Mathematical models for surface roughness and productivity were developed and normality was improved using the Box-Cox transformation. Results show that surface roughness criterion Ra was mainly influenced by cutting speed, radius nose and feed rate, and that the depth of cut had major effect on productivity. Finally, ranges of optimized cutting conditions were proposed for serial industrial production. Industrial benefit was illustrated in terms of high surface quality accompanied with high productivity. Indeed, results show that the use of optimal cutting condition had an industrial benefit to 46.9 % as an improvement in surface quality Ra and 160.54 % in productivity MRR.

  9. Thermal stability and environmental compatibility of Inconel 617

    International Nuclear Information System (INIS)

    Kimball, O.F.

    1989-01-01

    The thermal stability and environmental compatibility of Inconel 617, a prime nuclear process heat steam reformer candidate alloy, are described in this paper. This commercially available wrought nickel-base alloy has excellent high-temperature strength but is subject to loss of toughness and ductility due to thermal instability. Work done to improve the thermal stability of this alloy is discussed. Room-temperature tensile and toughness data and microstructural information for Inconel 617 specimens exposed at elevated temperatures are presented. Preliminary data indicate that controlling the chemistry of Inconel 617 can provide a substantial improvement in thermal stability. Preliminary work to define the range of high-temperature gas-cooled reactor (HTGR) primary coolant compositions within which minimal deleterious gas/metal reactions occur with Inconel 617 is described. Within this gas chemistry range a stable surface oxide forms and only slight carburization occurs. In other gas chemistry ranges, rapid carburization or decarburization can occur. The gas corrosion experiments discussed are part of a series of relatively short-term exposures to HTGR helium in which the effects of different H 2 O concentrations (0.01 to 1.0 Pa) were determined as a function of the systematic variation of a second constituent (CO and CH 4 for this work) in the test gas. The composition of the basic HTGR helium was 40 Pa H 2 , 4 Pa CO, 0.02 Pa CO 2 , 2 Pa CH 4 in helium at 0.2 MPa. Two other CO levels (1 and 12 Pa) and one additional CH 4 level (0.63 Pa) were used in these experiments. Experimental exposure methods are discussed and the results of gas-metal interaction studies are presented. These results include carbon analyses and optical and scanning electron microscopy to determine the morphology and type of surface and subsurface microstructures. (author). 15 refs, 6 figs, 5 tabs

  10. Corrosion Test Results for Inconel 600 vs Inconel-Stainless UG Bellows

    Energy Technology Data Exchange (ETDEWEB)

    Osborne, P.E.

    2002-09-11

    The Conversion Project (CP) of the Molten Salt Reactor Experiment at Oak Ridge National Laboratory (ORNL) involves converting slightly less than 40 kg of {sup 233}U to a stable form for safe storage. The operation is performed within a few vessels interconnected by valves and 1/2-in. metal tubing. During this conversion, a particularly toxic and corrosive by-product is formed, namely aqueous hydrofluoric acid (HF). The production of HF is a result of the hydrolysis of UF{sub 6} and subsequent steam treatments of UO{sub 2}F{sub 2}. For each mole of UF{sub 6} converted, 6 mol of HF are produced. The HF that forms during conversion combines with water to produce approximately 1.5 L of 33 wt % HF. As this mixture is transferred within the process system, the tubing and valves are exposed to high concentrations of HF in liquid and vapor form. Of particular concern in the system are the almost 30 valves that have the potential for exposure to HF. For these valves, a vendor-supplied UG valve was installed. UG valves consist of an Alloy 400 (Monel) body and stem tip and Alloy 600 (Inconel) bellows. These valves have been used under experimental conditions that simulate the CP. It has been established that they have a finite life when exposed to a HF and air environment. Most failures were seen around the flange at the bottom of the bellows, and it was suspected that this flange and the weld material were not Inconel. In December 2001, the vendor confirmed that this flange was not Inconel but instead was stainless steel 316. After discussions between the vendor and ORNL staff involved with the CP effort, it was decided that the entire wetted area of the bellows would be fabricated from Alloy 600. In March 2002, four newly fabricated bellows assemblies were received from the vendor for the purposes of corrosion testing in HF. This report presents results from the corrosion tests conducted to determine if the new design of the bellows would enhance their corrosion resistance.

  11. Deformation characteristics of {delta} phase in the delta-processed Inconel 718 alloy

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, H.Y., E-mail: haiyanzhang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Zhang, S.H., E-mail: shzhang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Cheng, M. [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Li, Z.X. [Beijing Institute of Aeronautica1 Materials, Beijing 100095 (China)

    2010-01-15

    The hot working characteristics of {delta} phase in the delta-processed Inconel 718 alloy during isothermal compression deformation at temperature of 950 deg. C and strain rate of 0.005 s{sup -1}, were studied by using optical microscope, scanning electron microscope and quantitative X-ray diffraction technique. The results showed that the dissolution of plate-like {delta} phase and the precipitation of spherical {delta} phase particles coexisted during the deformation, and the content of {delta} phase decreased from 7.05 wt.% to 5.14 wt.%. As a result of deformation breakage and dissolution breakage, the plate-like {delta} phase was spheroidized and transferred to spherical {delta} phase particles. In the center with largest strain, the plate-like {delta} phase disappeared and spherical {delta} phase appeared in the interior of grains and grain boundaries.

  12. Mechanical properties of nanostructured nickel based superalloy Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Mukhtarov, Sh; Ermachenko, A, E-mail: shamil@anrb.r [Institute for Metals Superplasticity Problems RAS, 39, Khalturina, Ufa, 450001 (Russian Federation)

    2010-07-01

    This paper will describe the investigations of a nanostructured (NS) state of nickel based INCONEL alloy 718. This structure was generated in bulk semiproducts by severe plastic deformation (SPD) via multiple isothermal forging (MIF) of a coarse-grained alloy. The initial structure consisted of {gamma}-phase grains with disperse precipitations of {gamma}{sup -}phase in the forms of discs, 50-75 nm in diameter and 20 nm in thickness. The MIF generated structures possess a large quantity of non-coherent plates and rounded precipitations of {delta}-phase, primarily along grain boundaries. In the duplex ({gamma}+{delta}) structure the grains have high dislocation density and a large number of nonequilibrium boundaries. Investigations to determine mechanical properties of the alloy in a nanostructured state were carried out. Nanocrystalline Inconel 718 (80 nm) possesses a very high room-temperature strength after SPD. Microcrystalline (MC) and NS states of the alloy were subjected to strengthening thermal treatment, and the obtained results were compared in order to determine their mechanical properties at room and elevated temperatures.

  13. Micro-scale mechanical characterization of Inconel cermet coatings deposited by laser cladding

    OpenAIRE

    Chao Chang; Davide Verdi; Miguel Angel Garrido; Jesus Ruiz-Hervias

    2016-01-01

    In this study, an Inconel 625-Cr3C2 cermet coating was deposited on a steel alloy by laser cladding. The elastic and plastic mechanical properties of the cermet matrix were studied by the depth sensing indentation (DSI) in the micro scale. These results were compared with those obtained from an Inconel 600 bulk specimen. The values of Young's modulus and hardness of cermet matrix were higher than those of an Inconel 600 bulk specimen. Meanwhile, the indentation stress–strain curve of the cerm...

  14. Increasing the Useful Life of Quench Reliefs with Inconel Bellows

    Energy Technology Data Exchange (ETDEWEB)

    Soyars, W. M. [Fermilab

    1999-01-01

    Reliable quench relief valves are an important part of superconducting magnet systems. Fermilab developed bellows-actuated cryogenic quench reliefs which have been in use since the early l 980's. The original design uses a stainless steel bellows. A high frequency, low amplitude vibration during relieving events has resulted in fatigue failures in the original design. To take advantage of the improved resistance to fatigue of Inconel, a nickel-chromium alloy, reliefs using Inconel 625 bellows were made. Design, development, and testing of the new version reliefs will be discussed. Tests show that relief valve lifetimes using Inconel bellows are more than five times greater than when using the original stainless steel bellows. Inconel bellows show great promise in increasing the lifetime of quench relief valves, and thus the reliability of accelerator cryogenic systems.

  15. Creep and low cycles fatigue behaviour of inconel 617 and alloy 800H in the temperature range 1073-1223

    International Nuclear Information System (INIS)

    Yun, H.M.

    1984-01-01

    The creep rupture properties of high temperature alloys are being determined as part of the materials programme for the development of the high temperature, gas-cooled reactor (HTGR) as a source of nuclear process heat, especially for the gasification of lignite and coal. INCOLOY 800H AND INCONEL 617 have been tested in the temperature range from 1073 K to 1223 K in air as well as in helium with HTGR specific impurities. The static and dynamic creep behaviour of INCONEL 617 have been determined in constant load creep tests, relaxation tests and stress reduction tests. The results have been interpreted using the internal stress on the applied stress and test temperature was determined. In a few experiments the influence of cold deformation prior to the creep test on the magnitude of the internal stress was also investigated. (Author)

  16. Inconel 718 and UNSM Treated Alloy Study on the Rotary Bending High Temperature Fatigue Characteristics under a Light Concentrating System

    Energy Technology Data Exchange (ETDEWEB)

    Suh, Chang Min [Kyungpook Nat’l Univ., Daegu (Korea, Republic of); Nahm, Seung Hoon [Korea Research Institute of Standards and Science, Daejeon (Korea, Republic of); Woo, Young Han; Hur, Kwang Ho; Hong, Sang Hwui [Gyeongbuk Hybrid Technology Institute, Daegu (Korea, Republic of); Kim, Jun Hyong; Pyun, Young Sik [Sun Moon Univ., Asan (Korea, Republic of)

    2016-11-15

    This study investigated the influence of high temperature and UNSM on the fatigue behavior of Inconel 718 alloy at RT, 300, 500, and 600℃. Fatigue properties of Inconel 718 were reduced at high temperatures compared to those at room temperature. However, the endurance limit was similar to that of the room temperature sample at the design stress level. High-temperature fatigue characteristics of the UNSM-treated specimen were significantly improved at the design stress level as compared to the untreated specimens. Specifically, the influence of temperature on the S-N curves at the design stress level of the UNSM-treated specimen showed the tendency of longer fatigue lives than those of untreated ones. Researchers can obtain rotary fatigue test results simply by heating specimens with a halogen lamp to precise temperatures during specific operations.

  17. Surface chemistry and corrosion behavior of Inconel 625 and 718 in subcritical, supercritical, and ultrasupercritical water

    Science.gov (United States)

    Rodriguez, David; Merwin, Augustus; Karmiol, Zachary; Chidambaram, Dev

    2017-05-01

    Corrosion behavior of Inconel 625 and 718 in subcritical, supercritical and ultrasupercritical water was studied as a function of temperature and time. The change in the chemistry of the as-received surface film on Inconel 625 and 718 after exposure to subcritical water at 325 °C and supercritical water at 425 °C and 527.5 °C for 2 h was studied. After exposure to 325 °C subcritical water, the CrO42- based film formed; however minor quantities of NiFexCr2-xO4 spinel compounds were observed. The oxide film formed on both alloys when exposed to supercritical water at 425 °C consisted of NiFexCr2-xO4 spinel. The surface films on both alloys were identified as NiFe2O4 when exposed to supercritical water at 527.5 °C. To characterize the fully developed oxide layer, studies were conducted at test solution temperatures of 527.5 and 600 °C. Samples were exposed to these temperatures for 24, 96, and 200 h. Surface chemistry was analyzed using X-ray diffraction, as well as Raman and X-ray photoelectron spectroscopies. Inconel 718 exhibited greater mass gain than Inconel 625 for all temperatures and exposure times. The differences in corrosion behavior of the two alloys are attributed to the lower content of chromium and increased iron content of Inconel 718 as compared to Inconel 625.

  18. Rotary bending fatigue properties of Inconel 718 alloys by ultrasonic nanocrystal surface modification technique

    Directory of Open Access Journals (Sweden)

    Jun-Hyong Kim

    2015-08-01

    Full Text Available This study investigates the influence of ultrasonic nanocrystal surface modification (UNSM technique on fatigue properties of SAE AMS 5662 (solution treatment of Inconel 718 alloys. The fatigue properties of the specimens were investigated using a rotary bending fatigue tester. Results revealed that the UNSM-treated specimens showed longer fatigue life in comparison with those of the untreated specimens. The improvement in fatigue life of the UNSM-treated specimens is attributed mainly to the induced compressive residual stress, increased hardness, reduced roughness and refined grains at the top surface. Fractured surfaces were analysed using a scanning electron microscopy (SEM in order to give insight into the effectiveness of UNSM technique on fracture mechanisms and fatigue life.

  19. Solidification paths in modified Inconel 625 weld overlay material

    DEFF Research Database (Denmark)

    Chandrasekaran, Karthik; Tiedje, Niels Skat; Hald, John

    2009-01-01

    Inconel 625 is commonly used for overlay welding to protect the base metal against high temperature corrosion. The efficiency of corrosion protection depends on effective mixing of the overlay weld with the base metal and the subsequent segregation of alloy elements during solidification....... Metallographic analysis of solidified samples of Inconel 625 with addition of selected elements is compared with thermodynamic modelling of segregation during solidification. The influence of changes in the melt chemistry on the formation of intermetallic phases during solidification is shown. In particular...

  20. Swelling in neutron irradiated nickel-base alloys

    International Nuclear Information System (INIS)

    Brager, H.R.; Bell, W.L.

    1972-01-01

    Inconel 625, Incoloy 800 and Hastelloy X were neutron irradiated at 500 to 700 0 C. It was found that of the three alloys investigated, Inconel 625 offers the greatest swelling resistance. The superior swelling resistance of Inconel 625 relative to that of Hastelloy-X is probably related to differences in the concentrations of the minor rather than major alloy constituents, and can involve (a) enhanced recombination of defects in the Inconel 625 and (b) preferential attraction of vacancies to incoherent precipitates. (U.S.)

  1. Erosive Wear of Inconel 625 Alloy Coatings Deposited by CMT Method

    Directory of Open Access Journals (Sweden)

    Solecka M.

    2016-06-01

    Full Text Available The article presents the investigation results concerning the determination of the characteristics of erosive wear caused by the impact of Al2O3 solid particles on the surface of Inconel 625 alloy after plastic working and the same material after weld cladding process using the CMT method. Erosion wear tests were performed at two temperatures: 20°C and 650°C. The erosion tests were conducted using the standard ASTM G76. A jet with a specified abrasive waight was directed to the surface of the tested material at an α impingement angle varied in the range of 30-90° at a velocity imparted to the abrasive by the medium, which was compressed air. The eroded surface was examined using a scanning electron microscope (SEM, while the depths of craters caused by the erosion tests were measured with an optical profilometer. The predominant mechanisms of the formation of mass losses during solid particle erosion were microcutting and microfissuring.

  2. Analysis of the effect on growth kinetics of gamma prima phase in Inconel 713C alloys

    International Nuclear Information System (INIS)

    Thorp, S.I.; Versaci, R.A.; Ges, A.; Palacio, H.A.

    1993-01-01

    This work shows the analysis of the effect on growth kinetics of gamma prima phase in Inconel 713C alloy of two thermic treatments. In this study, SEM are used and the results are analyzed by means of the theory developed by Lifshitz, Slyozov and Wagner (LSW theory). The findings have revealed that with such theory it is not possible to determine if the process of growth is controlled either through diffusion or through diffusion in the interface as to the time employed in the experiment (2600 hours); the time required is approximately 10000 hours. (Author)

  3. Welding processes for Inconel 718- A brief review

    Science.gov (United States)

    Tharappel, Jose Tom; Babu, Jalumedi

    2018-03-01

    Inconel 718 is being extensively used for high-temperature applications, rocket engines, gas turbines, etc. due to its ability to maintain high strength at temperatures range 450-700°C complimented by excellent oxidation and corrosion resistance and its outstanding weldability in either the age hardened or annealed condition. Though alloy 718 is reputed to possess good weldability in the context of their resistance to post weld heat treatment cracking, heat affected zone (HAZ) and weld metal cracking problems persist. This paper presents a brief review on welding processes for Inconel 718 and the weld defects, such as strain cracking during post weld heat treatment, solidification cracking, and liquation cracking. The effect of alloy chemistry, primary and secondary processing on the HAZ cracking susceptibility, influence of post/pre weld heat treatments on precipitation, segregation reactions, and effect of grain size etc. discussed and concluded with future scope for research.

  4. Microstructural evolution of inconel 625 during thermal aging

    Directory of Open Access Journals (Sweden)

    S. Malej

    2017-01-01

    Full Text Available Inconel 625 is due to alloying elements prone to precipitation of different intermetallic phases and secondary carbides during thermal aging. The base of investigation is nickel superalloy Inconel 625 in hot rolled state. Thermal aging was conducted at temperature 650 °C with different duration of treatment for each sample. Microstructural analysis was performed by light microscope and scanning electron microscope. The results of microstructure observation showed the precipitation of intermetallic γ››- Ni3Nb phase in the γ matrix and δ-Ni3Nb phase with M23C6 secondary carbides at the grain boundaries.

  5. A Study on the VHCF Fatigue Behaviors of Hydrogen Attacked Inconel 718 Alloy

    Energy Technology Data Exchange (ETDEWEB)

    Suh, Chang-Min [Kyungpook National Univ., DMI Senior Fellow, Daegu (Korea, Republic of); Nahm, Seung-Hoon [Korea Research Institute of Standards and Science, Daejeon (Korea, Republic of); Kim, Jun-Hyong; Pyun, Young-Sik [Sun Moon Univ., Chunan (Korea, Republic of)

    2016-07-15

    This study is to investigate the influence of hydrogen attack and UNSM on fatigue behaviors of the Inconel 718 alloy. The decrease of the fatigue life between the untreated and the hydrogen attacked material is 10-20%. The fatigue lives of hydrogen attacked specimen decreased without a fatigue limit, similar to those of nonferrous materials. Due to hydrogen embrittlement, about 80% of the surface cracks were smaller than the average grain size of 13 μm. Many small surface cracks caused by the embrittling effect of hydrogen attack were initiated at the grain boundaries and surface scratches. Cracks were irregularly distributed, grew, and then coalesced through tearing, leading to a reduction of fatigue life. Results revealed that the fatigue lives of UNSM-treated specimens were longer than those of the untreated specimens.

  6. Metallurgical and mechanical properties of Inconel 600 and stellite; Estudio del comportamiento mecanico-metalurgico de alceacion inconel 600 y estelita

    Energy Technology Data Exchange (ETDEWEB)

    Cstillo, Martin; Villa, Gabriel; Vite, Manuel [Instituto Politecnico Nacional, Mexico D.F. (Mexico); Palacios, Francisco [Instituto Nacional de Investigacion Nuclear (ININ), Estado de Mexico (Mexico); Hernandez, Luis H; Urriolagoita, Guillermo [Instituto Politecnico Nacional, Mexico D.F. (Mexico)

    2005-01-15

    The present work studies the metallurgical and mechanical properties of two alloys, Inconel 600 and stellite, which are within the group of high hardness alloys or superalloys, which are deposited through the electrical weld process to the metallic arc with coated electrode (SMAW) and thereinafter analyzed through electron microscopy, diffractometry and abrasion, Impact and hardness test. The relationship between the microstructure and the final properties of the coating (hardness and abrasion wear resistance) was observed. [Spanish] Este trabajo presenta el estudio sobre las propiedades metalurgicas y mecanicas de dos aleaciones, inconel 600 y estelita, clasificadas dentro del grupo de aleaciones de alta dureza o superaleaciones; las cuales fueron depositadas mediante el proceso de soldadura electrica al arco metalico con electrodo revestido (SMAW) y fueron analizadas mediante microscopia electronica (SEM), difractometria pruebas de abrasion, impacto y dureza. Se observo la relacion entre la microstructura y las propiedades del recubrimiento, como son: dureza, resistencia a la abrasion, resistencia al impacto, ente otras.

  7. Ductile Fracture Behaviour of Hot Isostatically Pressed Inconel 690 Superalloy

    Science.gov (United States)

    Cooper, A. J.; Brayshaw, W. J.; Sherry, A. H.

    2018-04-01

    Herein we assess the differences in Charpy impact behavior between Hot Isostatically Pressed and forged Inconel 690 alloy over the temperature range of 300 °C to - 196 °C. The impact toughness of forged 690 exhibited a relatively small temperature dependence, with a maximum difference of ca. 40 J measured between 300 °C and - 196 °C, whereas the HIP'd alloy exhibited a difference of approximately double that of the forged alloy over the same temperature range. We have conducted Charpy impact testing, tensile testing, and metallographic analyses on the as-received materials as well as fractography of the failed Charpy specimens in order to understand the mechanisms that cause the observed differences in material fracture properties. The work supports a recent series of studies which assess differences in fundamental fracture behavior between Hot Isostatically Pressed and forged austenitic stainless steel materials of equivalent grades, and the results obtained in this study are compared to those of the previous stainless steel investigations to paint a more general picture of the comparisons between HIP vs forged material fracture behavior. Inconel 690 was selected in this study since previous studies were unable to completely omit the effects of strain-induced martensitic transformation at the tip of the Chary V-notch from the fracture mechanism; Inconel 690 is unable to undergo strain-induced martensitic transformation due to the alloy's high nickel content, thereby providing a sister study with the omission of any martensitic transformation effects on ductile fracture behavior.

  8. Surface chemistry and corrosion behavior of Inconel 625 and 718 in subcritical, supercritical, and ultrasupercritical water

    Energy Technology Data Exchange (ETDEWEB)

    Rodriguez, David; Merwin, Augustus; Karmiol, Zachary; Chidambaram, Dev, E-mail: dcc@unr.edu

    2017-05-15

    Highlights: • Mixtures of oxides containing Ni, Fe, Cr and Nb formed on the surface. • Short term exposure tests observed breakdown of native film. • Formation of a Fe rich oxide layer on Inconel 718 prevents mass loss. - Abstract: Corrosion behavior of Inconel 625 and 718 in subcritical, supercritical and ultrasupercritical water was studied as a function of temperature and time. The change in the chemistry of the as-received surface film on Inconel 625 and 718 after exposure to subcritical water at 325 °C and supercritical water at 425 °C and 527.5 °C for 2 h was studied. After exposure to 325 °C subcritical water, the CrO{sub 4}{sup 2−} based film formed; however minor quantities of NiFe{sub x}Cr{sub 2-x}O{sub 4} spinel compounds were observed. The oxide film formed on both alloys when exposed to supercritical water at 425 °C consisted of NiFe{sub x}Cr{sub 2-x}O{sub 4} spinel. The surface films on both alloys were identified as NiFe{sub 2}O{sub 4} when exposed to supercritical water at 527.5 °C. To characterize the fully developed oxide layer, studies were conducted at test solution temperatures of 527.5 and 600 °C. Samples were exposed to these temperatures for 24, 96, and 200 h. Surface chemistry was analyzed using X-ray diffraction, as well as Raman and X-ray photoelectron spectroscopies. Inconel 718 exhibited greater mass gain than Inconel 625 for all temperatures and exposure times. The differences in corrosion behavior of the two alloys are attributed to the lower content of chromium and increased iron content of Inconel 718 as compared to Inconel 625.

  9. Surface chemistry and corrosion behavior of Inconel 625 and 718 in subcritical, supercritical, and ultrasupercritical water

    International Nuclear Information System (INIS)

    Rodriguez, David; Merwin, Augustus; Karmiol, Zachary; Chidambaram, Dev

    2017-01-01

    Highlights: • Mixtures of oxides containing Ni, Fe, Cr and Nb formed on the surface. • Short term exposure tests observed breakdown of native film. • Formation of a Fe rich oxide layer on Inconel 718 prevents mass loss. - Abstract: Corrosion behavior of Inconel 625 and 718 in subcritical, supercritical and ultrasupercritical water was studied as a function of temperature and time. The change in the chemistry of the as-received surface film on Inconel 625 and 718 after exposure to subcritical water at 325 °C and supercritical water at 425 °C and 527.5 °C for 2 h was studied. After exposure to 325 °C subcritical water, the CrO_4"2"− based film formed; however minor quantities of NiFe_xCr_2_-_xO_4 spinel compounds were observed. The oxide film formed on both alloys when exposed to supercritical water at 425 °C consisted of NiFe_xCr_2_-_xO_4 spinel. The surface films on both alloys were identified as NiFe_2O_4 when exposed to supercritical water at 527.5 °C. To characterize the fully developed oxide layer, studies were conducted at test solution temperatures of 527.5 and 600 °C. Samples were exposed to these temperatures for 24, 96, and 200 h. Surface chemistry was analyzed using X-ray diffraction, as well as Raman and X-ray photoelectron spectroscopies. Inconel 718 exhibited greater mass gain than Inconel 625 for all temperatures and exposure times. The differences in corrosion behavior of the two alloys are attributed to the lower content of chromium and increased iron content of Inconel 718 as compared to Inconel 625.

  10. Application of eddy current inspection to the Inconel weld of BWR internals

    International Nuclear Information System (INIS)

    Machida, Eiji; Yusa, Noritaka

    2004-01-01

    In order to definite the basic specifications of application of ECT (Eddy Current Test) to Inconel weld of BWR internals, the inspection and numerical analysis were carried out. The characteristics of the existing ECT probe were studied by making sample as same as CRD stud tube, measuring the relative permeability and electric conductivity of Inconel and alloy and evaluating ECT probe. On the basis of the results obtained, the basic specifications were determined and a new eddy current probe for inspection was designed and produced. The new ECT probe was able to detect small notch in Inconel weld, to classify the defects by eddy current inspection signal and sizing the length and depth. It is concluded that the new ECT probe is able to apply the Inconel weld of BWR internals. (S.Y.)

  11. Micro-scale mechanical characterization of Inconel cermet coatings deposited by laser cladding

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Ch.; Verdi, D.; Garrido, M.A.; Ruiz-Hervias, J.

    2016-07-01

    In this study, an Inconel 625-Cr3C2 cermet coating was deposited on a steel alloy by laser cladding. The elastic and plastic mechanical properties of the cermet matrix were studied by the depth sensing indentation (DSI) in the micro scale. These results were compared with those obtained from an Inconel 600 bulk specimen. The values of Young's modulus and hardness of cermet matrix were higher than those of an Inconel 600 bulk specimen. Meanwhile, the indentation stress–strain curve of the cermet matrix showed a strain hardening value which was more than twice the one obtained for the Inconel 600 bulk. Additionally, the mechanical properties of unmelted Cr3C2 ceramic particles, embedded in the cermet matrix were also evaluated by DSI using a spherical indenter. (Author)

  12. Micro-scale mechanical characterization of Inconel cermet coatings deposited by laser cladding

    Directory of Open Access Journals (Sweden)

    Chao Chang

    2016-07-01

    Full Text Available In this study, an Inconel 625-Cr3C2 cermet coating was deposited on a steel alloy by laser cladding. The elastic and plastic mechanical properties of the cermet matrix were studied by the depth sensing indentation (DSI in the micro scale. These results were compared with those obtained from an Inconel 600 bulk specimen. The values of Young's modulus and hardness of cermet matrix were higher than those of an Inconel 600 bulk specimen. Meanwhile, the indentation stress–strain curve of the cermet matrix showed a strain hardening value which was more than twice the one obtained for the Inconel 600 bulk. Additionally, the mechanical properties of unmelted Cr3C2 ceramic particles, embedded in the cermet matrix were also evaluated by DSI using a spherical indenter.

  13. A Study on Ultrasonic Elliptical Vibration Cutting of Inconel 718

    Directory of Open Access Journals (Sweden)

    Zhao Haidong

    2016-01-01

    Full Text Available Inconel 718 is a kind of nickel-based alloys that are widely used in the aerospace and nuclear industry owing to their high temperature mechanical properties. Cutting of Inconel 718 in conventional cutting (CC is a big challenge in modern industry. Few researches have been studied on cutting of Inconel 718 using single point diamond tool applying the UEVC method. This paper shows an experimental study on UEVC of Inconel 718 by using polycrystalline diamond (PCD coated tools. Firstly, cutting tests have been carried out to study the effect of machining parameters in the UEVC in terms of surface finish and flank wear during machining of Inconel 718. The tests have clearly shown that the PCD coated tools in cutting of Inconel 718 by the UEVC have better performance at 0.1 mm depth of cut as compared to the lower 0.05 mm depth of cut and the higher 0.12 or 0.15 mm depth of cut. Secondly, like CC method, the cutting performance in UEVC increases with the decrease of the feed rate and cutting speed. The CC tests have also been carried out to compare performance of CC with UEVC method.

  14. Graphite to Inconel brazing using active filler metal

    International Nuclear Information System (INIS)

    King, J.F.; Baity, F.W.; Walls, J.C.; Hoffman, D.J.

    1989-01-01

    Ion cyclotron resonant frequency (ICRF) antennas are designed to supply large amounts of auxiliary heating power to fusion-grade plasmas in the Toroidal Fusion Test Reactor (TFTR) and Tore Supra fusion energy experiments. A single Faraday shield structure protects a pair of resonant double loops which are designed to launch up to 2 MW of power per loop. The shield consists of two tiers of actively cooled Inconel alloy tubes with the front tier being covered with semicircular graphite tiles. Successful operation of the antenna requires the making of high integrity bonds between the Inconel tubes and graphite tiles by brazing. This paper discusses this process

  15. Fatigue-crack propagation behavior of Inconel 718

    International Nuclear Information System (INIS)

    James, L.A.

    1975-09-01

    The techniques of linear-elastic fracture mechanics were used to characterize the effect of several variables (temperature, environment, cyclic frequency, stress ratio, and heat-treatment variations) upon the fatigue-crack growth behavior of Inconel 718 base metal and weldments. Relevant crack growth data on this alloy from other laboratories is also presented. (33 fig, 39 references)

  16. Tensile behavior of Inconel alloy X-750 in air and vacuum at elevated temperatures

    International Nuclear Information System (INIS)

    Taplin, D.M.R.; Mukherjee, A.K.; Pandey, M.C.

    1984-01-01

    The hot tensile properties of Inconel alloy X-750 have been investigated experimentally at 700 C in air and vacuum at strain rates varying from 10 to the -7th to 1.2 x 10 to the -6th per s. The strength and ductile characteristics of the specimens tested in vacuum are found to be better than those tested in air. In air, a ductility minimum is observed at 625 C, whereas in vacuum, significant improvements in creep ductility are observed at 575 and 625 C, with the ductility minimum shifting from 625 to 700 C. It is shown that the creep ductility of the specimens tested in air is largely determined by the following two competing processes: (1) deformation-assisted oxygen diffusion and (2) grain boundary migration. 20 references

  17. Mechanical properties and microstructure evaluation of powder bed fused inconel 625 nickel alloy

    Energy Technology Data Exchange (ETDEWEB)

    Brand, Michael J. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2016-04-19

    The objectives of this report were to optimize and fabricate full density Inconel 625 samples using direct metal laser fusion, an additive manufacturing process; and to compare and evaluate precipitation and solid solution strengthening of Inconel 625 produced by PBF to conventional processed material.

  18. Inconel alloy 625 clad steel for application in wet scrubber systems

    International Nuclear Information System (INIS)

    Morse, S.L.; Shoemaker, L.E.

    1984-01-01

    Test panels from INCONEL 625 clad plate were successfully installed in two wet flue gas scrubber systems. In one system INCONEL 625 clad plate was located in the roof section of the absorber just ahead of the outlet ducting. The test plates, including weld seams, showed no signs to corrosion after six months of exposure. In the other scrubber test plates located in the outlet duct of an I.D. fan house, in the stack lining, and in the absorber quench area were unattacked after nine months

  19. Microstructure and Properties of the Ti6Al4V/Inconel 625 Bimetal Obtained by Explosive Joining

    Science.gov (United States)

    Topolski, Krzysztof; Szulc, Zygmunt; Garbacz, Halina

    2016-08-01

    The study is concerned with the bimetallic plate composed of the Ti6Al4V and Inconel 625 alloys. The alloys were joined together using the explosive method with the aim to produce a bimetallic joint. The structure and the mechanical properties of the as-received raw Ti6Al4V and Inconel 625 alloys, the Ti6Al4V/Inconel 625 joint, and the joint after annealing (600 °C for 1 h) were examined. The samples observations were performed using a light microscope and a scanning electron microscope. The mechanical properties were estimated by microhardness measurements, tensile tests, and three-point bending tests. Moreover, the deformation strengthening of the metals and the strength of the joint were analyzed. The explosive process resulted in a good quality bimetallic joint. Both sheets were deformed plastically and the joint surface between the alloys had a wavy shape. In the area of the joint surface, the hardness was increased. For example, the annealing at 600 °C for 1 h resulted in changes of the microhardness in the entire volume of the samples and in changes of the morphology of the joint surface. In three-point bending tests, the samples were examined in two opposite positions (Ti6Al4V on the top or Inconel 625 on the top). The results indicated to depend on the position in which the sample was tested.

  20. Repair of Precision Castings Made of the Inconel 713C Alloy

    Directory of Open Access Journals (Sweden)

    Łyczkowska K.

    2017-09-01

    Full Text Available Inconel 713C precision castings are used as aircraft engine components exposed to high temperatures and the aggressive exhaust gas environment. Industrial experience has shown that precision-cast components of such complexity contain casting defects like microshrinkage, porosity, and cracks. This necessitates the development of repair technologies for castings of this type. This paper presents the results of metallographic examinations of melted areas and clad welds on the Inconel 713C nickel-based superalloy, made by TIG, plasma arc, and laser. The cladding process was carried out on model test plates in order to determine the technological and material-related problems connected with the weldability of Inconel 713C. The studies included analyses of the macro- and microstructure of the clad welds, the base materials, and the heat-affected zones. The results of the structural analyses of the clad welds indicate that Inconel 713C should be classified as a low-weldability material. In the clad welds made by laser, cracks were identified mainly in the heat-affected zone and at the melted zone interface, crystals were formed on partially-melted grains. Cracks of this type were not identified in the clad welds made using the plasma-arc method. It has been concluded that due to the possibility of manual cladding and the absence of welding imperfections, the technology having the greatest potential for application is plasma-arc cladding.

  1. Length change of the alloys Waspaloy and Inconel 718 after long-term annealing

    International Nuclear Information System (INIS)

    Kinzel, Svenja

    2016-01-01

    Within the scope of this work the contraction behavior of Ni-based superalloy Waspaloy could in detail be referred to a combination of different microstructural changes and the results could partially be transferred to Ni-Fe-based alloy Inconel 718. Isothermal annealing of sample rods at temperatures between 450 C and 750 C induces an average relative length contraction of about -2.10"-"4. It is apparent that contraction is more pronounced for lower temperatures (-3.10"-"4 at 550 C) than for higher ones (-1.10"-"4 at 750 C). Within the first 300 hours of annealing the contraction reaches about 70-75% of the value measured after 10,000 hours. This means the major part of the effect takes place at the beginning of long term annealing but even after 10,000 hours no saturation occurs. On the basis of lattice parameter measurements it could be found that within the first 300 hours a significant lattice parameter decrease of matrix and γ"' phase emerged. Longer annealing time does not cause further lattice contraction. This sample behavior can be explained by temperature dependence of phase fractions and phase compositions. Thermodynamic calculations as well as stereological analysis of micrographs show a decrease of stable γ"'-phase content with increasing temperature. In parallel, TEM-EDS measurements and calculated phase fractions show concentration fluctuations due to the different precipitate fraction, which cause contraction of the lattice parameter. Furthermore, within the first 100 hours at temperatures up to 650 C the formation or Ni-Cr rich domains could be observed. As these domains exhibit a smaller lattice parameter than the matrix they contribute to the more pronounced contraction at lower temperatures. While XRD measurements point to the formation of Ni_3Cr, TEM-EDS measurements reveal a composition of (Ni,Co)_2Cr. Stress relief heat treatment at higher temperatures (815 C) after annealing shows that the effect of contraction is reversible. It causes an

  2. Functionally graded Ti6Al4V and Inconel 625 by Laser Metal Deposition

    Science.gov (United States)

    Pulugurtha, Syamala R.

    The objective of the current work was to fabricate a crack-free functionally graded Ti6Al4V and Inconel 625 thin wall structure by Laser Metal Deposition (LMD). One potential application for the current material system is the ability to fabricate a functionally graded alloy that can be used in a space heat exchanger. The two alloys, Inconel 625 and Ti6Al4V are currently used for aerospace applications. They were chosen as candidates for grading because functionally grading those combines the properties of high strength/weight ratio of Ti6Al4V and high temperature oxidation resistance of Inconel 625 into one multifunctional material for the end application. However, there were challenges associated with the presence of Ni-Ti intermetallic phases (IMPs). The study focused on several critical areas such as (1) understanding microstructural evolution, (2) reducing macroscopic cracking, and (3) reducing mixing between graded layers. Finite element analysis (FEA) was performed to understand the effect of process conditions on multilayer claddings for simplified material systems such as SS316L and Inconel 625 where complex microstructures did not form. The thermo-mechanical models were developed using Abaqus(TM) (and some of them experimentally verified) to predict temperature-gradients; remelt layer depths and residual stresses. Microstructure evolution along the functionally graded Ti6Al4V and Inconel 625 was studied under different processing and grading conditions. Thermodynamic modeling using Factsage (v 6.1) was used to construct phase diagrams and predict the possible equilibrium major/minor phases (verified experimentally by XRD) that may be present along the functionally graded Ti6Al4V and Inconel 625 thin wall structures.

  3. Condition monitoring: a study on ageing in Inconel 718

    International Nuclear Information System (INIS)

    Acharya, Vidhi; Murthy, G.V.S.

    2015-01-01

    The development of contemporary high temperature materials is needed to enable the successful introduction of cleaner and more efficient next generation power plants. Due to inherent limitations in steels, new high temperature materials must be selected for a change in operating parameters. Inconel-718 is currently considered to be one of the leading materials for use in high temperature applications. Due to its excellent high-temperature mechanical properties, Inconel-718 is believed to be a contender for forged components of Advanced Ultra-Supercritical (A-USC) power plants. The A-USC power plant with steam conditions of 700°C/35 MPa, is expected to have greater efficiency. Thus the microstructural stability and its impact on the mechanical properties of this alloy at elevated temperatures will certainly be a crucial factor that influences the reliability of the power plants. Therefore it is of imminent importance to study the microstructural evolution of components made out of Inconel-718 preferably by Non-destructive methods

  4. Characterization of serrated yielding in service exposed Inconel 625 alloy

    International Nuclear Information System (INIS)

    Chatterjee, Arnomitra; Sharma, Garima; Chakravartty, J.K.

    2016-01-01

    The Alloy-625 is an austentic alloy which is being used for a variety of components in the aerospace, marine, chemical and nuclear industries. Tensile tests have been carried out on service exposed Inconel 625 ammonia cracker tube used at heavy water production plant to study the effect of microstructure on the mechanical properties of the material. Owing to temperature gradient during in service condition the microstructure was different in top (T), middle (M) and bottom (B) sections of the tube. The stress-strain curve obtained from conventional tensile test was found to exhibit serrated yielding with in an intermediate temperature regime of 250-600 °C. Both normal and inverse Portevin-Le Chatelier (PLC) effect could be identified at lower and higher temperature regime respectively. The normal behavior was associated with type (A+B) serrations and interstitial atom C was held responsible for the aging of dislocations in this region. On the contrary, the serrations were of type C in nature in inverse PLC regime and were attributed to the locking of dislocations by substitutional Mo atoms. Further analyses of activation energy and transition temperature for normal to inverse PLC dynamics, supported with Transmission Electron Microscopy (TEM) observation revealed that the basic deformation mechanism was different in M and B samples than that in the T samples. While the deformation in T samples were achieved by usual dislocation migration, in M and B samples it was through the propagation of stacking faults in large γ” precipitates. The transition temperature from normal to inverse PLC dynamics also varied appreciably in T samples than that of the M and B ones which could be explained in terms of the delayed depletion of Mo solutes in solution for T samples. (author)

  5. TEM Study of High-Temperature Precipitation of Delta Phase in Inconel 718 Alloy

    Directory of Open Access Journals (Sweden)

    Moukrane Dehmas

    2011-01-01

    Full Text Available Inconel 718 is widely used because of its ability to retain strength at up to 650∘C for long periods of time through coherent metastable  Ni3Nb precipitation associated with a smaller volume fraction of  Ni3Al precipitates. At very long ageing times at service temperature,  decomposes to the stable Ni3Nb phase. This latter phase is also present above the  solvus and is used for grain control during forging of alloy 718. While most works available on precipitation have been performed at temperatures below the  solvus, it appeared of interest to also investigate the case where phase precipitates directly from the fcc matrix free of  precipitates. This was studied by X-ray diffraction and transmission electron microscopy (TEM. TEM observations confirmed the presence of rotation-ordered domains in plates, and some unexpected contrast could be explained by double diffraction due to overlapping phases.

  6. Length change of the alloys Waspaloy and Inconel 718 after long-term annealing; Laengenaenderung der Legierungen Waspaloy und Inconel 718 nach Langzeitauslagerung

    Energy Technology Data Exchange (ETDEWEB)

    Kinzel, Svenja

    2016-07-01

    Within the scope of this work the contraction behavior of Ni-based superalloy Waspaloy could in detail be referred to a combination of different microstructural changes and the results could partially be transferred to Ni-Fe-based alloy Inconel 718. Isothermal annealing of sample rods at temperatures between 450 C and 750 C induces an average relative length contraction of about -2.10{sup -4}. It is apparent that contraction is more pronounced for lower temperatures (-3.10{sup -4} at 550 C) than for higher ones (-1.10{sup -4} at 750 C). Within the first 300 hours of annealing the contraction reaches about 70-75% of the value measured after 10,000 hours. This means the major part of the effect takes place at the beginning of long term annealing but even after 10,000 hours no saturation occurs. On the basis of lattice parameter measurements it could be found that within the first 300 hours a significant lattice parameter decrease of matrix and γ{sup '} phase emerged. Longer annealing time does not cause further lattice contraction. This sample behavior can be explained by temperature dependence of phase fractions and phase compositions. Thermodynamic calculations as well as stereological analysis of micrographs show a decrease of stable γ{sup '}-phase content with increasing temperature. In parallel, TEM-EDS measurements and calculated phase fractions show concentration fluctuations due to the different precipitate fraction, which cause contraction of the lattice parameter. Furthermore, within the first 100 hours at temperatures up to 650 C the formation or Ni-Cr rich domains could be observed. As these domains exhibit a smaller lattice parameter than the matrix they contribute to the more pronounced contraction at lower temperatures. While XRD measurements point to the formation of Ni{sub 3}Cr, TEM-EDS measurements reveal a composition of (Ni,Co){sub 2}Cr. Stress relief heat treatment at higher temperatures (815 C) after annealing shows that the effect

  7. [INVITED] Laser treatment of Inconel 718 alloy and surface characteristics

    Science.gov (United States)

    Yilbas, B. S.; Ali, H.; Al-Aqeeli, N.; Karatas, C.

    2016-04-01

    Laser surface texturing of Inconel 718 alloy is carried out under the high pressure nitrogen assisting gas. The combination of evaporation and melting at the irradiated surface is achieved by controlling the laser scanning speed and the laser output power. Morphological and metallurgical changes in the treated surface are analyzed using the analytical tools including optical, electron scanning, and atomic force microscopes, energy dispersive spectroscopy, and X-ray diffraction. Microhardnes and friction coefficient of the laser treated surface are measured. Residual stress formed in the surface region is determined from the X-ray diffraction data. Surface hydrophobicity of the laser treated layer is assessed incorporating the sessile drop method. It is found that laser treated surface is free from large size asperities including cracks and the voids. Surface microhardness increases significantly after the laser treatment process, which is attributed to the dense layer formation at the surface under the high cooling rates, dissolution of Laves phase in the surface region, and formation of nitride species at the surface. Residual stress formed is compressive in the laser treated surface and friction coefficient reduces at the surface after the laser treatment process. The combination of evaporation and melting at the irradiated surface results in surface texture composes of micro/nano-poles and pillars, which enhance the surface hydrophobicity.

  8. Microstructure and oxidation behaviour of aluminized coating of inconel 625

    International Nuclear Information System (INIS)

    Khalid, F.A.; Hussain, N.; Shahid, K.A.; Rehman, S.; Qureshi, A.H.; Khan, I.H.

    1999-01-01

    Microstructural and oxidation characteristics of aluminized coated Inconel 625 have been examined using scanning electron microscopy (SEM) and fine-probe spot and linescan EDS microanalysis techniques. The formation of slowly growing adherent metallic coatings is essential for protection against the severe environments. Aluminising of the superalloy samples was carried out by pack cementation process at 900 deg. C. in an argon atmosphere. The samples were subsequently oxidized in air at various temperatures to examine performance of the pack aluminized coated alloy. The microstructural changes that occurred in the aluminized layer at various exposure temperature and time were examined to study the oxidation behavior and formation of different phases in the aluminized coating deposited on Inconel 625. (author)

  9. Aeronautical requirements for Inconel 718 alloy

    Science.gov (United States)

    Elefterie, C. F.; Guragata, C.; Bran, D.; Ghiban, B.

    2017-06-01

    The project goal is to present the requirements imposed by aviation components made from super alloys based on Nickel. A significant portion of fasteners, locking lugs, blade retainers and inserts are manufactured from Alloy 718. The thesis describes environmental factors (corrosion), conditions of external aggression (salt air, intense heat, heavy industrial pollution, high condensation, high pressure), mechanical characteristics (tensile strength, yield strength and fatigue resistance) and loadings (tensions, compression loads) that must be satisfied simultaneously by Ni-based super alloy, compared to other classes of aviation alloys (as egg. Titanium alloys, Aluminum alloys). For this alloy the requirements are strength durability, damage tolerance, fail safety and so on. The corrosion can be an issue, but the fatigue under high-magnitude cyclic tensile loading it’s what limits the lifetime of the airframe. Also, the excellent malleability and weldability characteristics of the 718 system make the material physical properties tolerant of manufacturing processes. These characteristics additionally continue to provide new opportunities for advanced manufacturing methods.

  10. Phase transformation and liquid density redistribution during solidification of Ni-based superalloy Inconel 718

    Directory of Open Access Journals (Sweden)

    Wang Ling

    2012-08-01

    Full Text Available The influences of chemical segregation and phase transformation on liquid density variation during solidification of Ni-based supperalloy Inconel 718 were investigated using SEM and EDS. It was found that significant segregation in liquid prompts high Nb phase to precipitate directly from liquid, which results in the redistribution of alloy elements and liquid density in their vicinity. The term “inter-precipitate liquid density” is therefore proposed and this concept should be applied to determine the solidification behavior of superalloy Inconel 718.

  11. Stress corrosion cracking of Inconel in high temperature water; Corrosion fissurante sous contrainte de l'Inconel dans l'eau a haute temperature

    Energy Technology Data Exchange (ETDEWEB)

    Coriou,; Grall,; Gall, Le; Vettier, [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires

    1960-07-01

    Some Inconel samples were subjected to hot water corrosion testing (350 deg. C), under stress slightly above the elastic limit. It has been observed that different types of alloys - with or without titanium - could suffer serious intergranular damage, including a complete rupture, within a three months period. In one case, we observed an unusual intergranular phenomenon which appeared quite different from common intergranular corrosion. (author) [French] Des essais de corrosion d'Inconel sont realises dans l'eau a 350 deg. C, et sous contrainte legerement superieure a la limite elastique. On constate que differentes varietes d'alliage avec ou sans titane donnent lieu a des accidents intergranulaires graves allant jusqu'a rupture complete en 3 mois. Dans un cas, on observe un phenomene intergranulaire particulier tres different de la corrosion intergranulaire classique. (auteur)

  12. Nickel based alloys for molten salt applications in pyrochemical reprocessing applications

    International Nuclear Information System (INIS)

    Ningshen, S.; Ravi Shankar, A.; Rao, Ch. Jagadeeswara; Mallika, C.; Kamachi Mudali, U.

    2016-01-01

    Pyrochemical reprocessing route is one of the best option for reprocessing of spent metallic nuclear fuel from future fast breeder in many countries, especially in the US (Integral fast reactor, IFR), Russia (Research Institute of Atomic Reactors, RIAR), Japan, Korea and India. This technology with intrinsic nuclear proliferation resistance is regarded as one of the most promising nuclear fuel cycle technologies of the next-generation. However, the selection of materials of construction for pyrochemical reprocessing plants is challenging because of the extreme environments, i.e., high radiation, corrosive molten salt (LiCl-KCl, LiCl-KCl-CsCl, KCl-NaCl-MgCl 2 , etc.), reactive molten metals, and high temperature. Efforts have been made to develop compatible materials for various unit operations like salt preparation, electrorefining, cathode processing and alloy casting in pyrochemical reprocessing. Nickel and its alloy are the candidate materials for salt purification exposed to molten LiCl-KCl under Cl 2 bubbling, in air or ultra high purity argon environment. In the present study, the corrosion behavior of candidate materials like Inconel 600, Inconel 625, Inconel 690 exposed to molten LiCl-KCl eutectic salt environment at 500 to 600 °C have been carried out. The surface morphology of the exposed samples and scales were examined by SEM/EDX and XRD. The weight loss results indicated that Inconel 600 and Inconel 690 offer better corrosion resistance compared to Inconel 625 in air and chlorine environment. Higher corrosion of Inconel 625 is attributed to development of Mo rich salt layers. However, Ni base alloys exhibited a decreasing trend of weight loss with increasing time of exposure and weight gain was observed under UHP Ar environment. The mechanism of corrosion of Ni base alloys appeared to be due to formation of Cr rich and Ni rich layers of Cr 2 O 3 , NiO and spinel oxides at the surface and subsequent spallation. Based on the present studies, Inconel 690

  13. Some observations on the physical metallurgy of nickel alloy weld metals

    International Nuclear Information System (INIS)

    Skillern, C.G.; Lingenfelter, A.C.

    1982-01-01

    Numerous nickel alloys play critical roles in various energy-related applications. Successful use of these alloys is almost always dependent on the availability of acceptable welding methods and welding products. An understanding of the physical metallurgy of these alloys and their weld metals and the interaction of weld metal and base metal is essential to take full advantage of the useful properties of the alloys. To illustrate this point, this paper presents data for two materials: INCONEL alloy 718 and INCONEL Welding Electrode 132. 8 figures, 9 tables

  14. The sectional size effect on the deformation behaviour of Inconel 718 at different temperatures

    Directory of Open Access Journals (Sweden)

    Zhao R.

    2015-01-01

    Full Text Available Inconel 718, as a multiphase super-alloy, is widely used in aeronautics and astronautics industries. In this field, a modified Hall-Petch equation was used to describe the grain size effect on the deformation behaviour of Inconel 718 sheet in uniaxial tension test. There is a piecewise linearity in the σ-d−1 curve: With the thickness t is a constant, the slope changes obviously after a critical t/d ratio, which increases with strain. Moreover, the influence on sectional curve caused by temperature is also an interesting issue. To address that, the sectionalized curve was fitted at different strains and temperatures, and the phenomena of grain size effect in piecewise curve at different temperatures were further explained. A surface model of Inconel 718 was proposed to explain the intrinsic mechanism of different slopes. The research provided an in-depth understanding of the size effect on the deformation behaviour of Inconel 718 at different hot working temperatures.

  15. Microstructural evolution of cold-sprayed Inconel 625 superalloy coatings on low alloy steel substrate

    International Nuclear Information System (INIS)

    Chaudhuri, Atanu; Raghupathy, Y.; Srinivasan, Dheepa; Suwas, Satyam; Srivastava, Chandan

    2017-01-01

    This study illustrates microstructural evolution of INCONEL 625 superalloy coatings cold-sprayed on a 4130 chrome alloy steel with medium carbon content. INCONEL 625 powder (5–25 μm) were successfully cold sprayed without any oxidation. The comprehensive microstructure analysis of the as-sprayed coatings and of the substrate-coating interface was carried out using EBSD, TEM, and XRD. The coating microstructure at the substrate-coating interface was markedly different from the microstructure away from the interface. The coating microstructure at steel-coating interface consisted of a fine layer of small grains. The microstructure beyond this fine layer can be divided into splats, inter splat and intra splat boundaries. Both splat and splat boundaries exhibited deformation induced dislocations. Dynamic recovery of dislocations-ridden regions inside the splat was responsible for the development of sub grain structure inside a splat with both low and high angle grain boundaries. Splat-splat (inter splat) boundary consisted of a relatively high density of dislocations and shear bands as a result of adiabatic shear flow localisation. This flow instability is believed to enhance the microstructural integrity by eliminating porosity at splat-splat boundaries. Based on the microstructural analysis using electron microscopy, a plausible mechanism for the development of microstructure has been proposed in this work. Cold spray technique can thus be deployed to develop high quality coatings of commercial importance. - Graphical abstract: Schematics of the evolution of microstructure at the 4130 steel substrate close to interface. i) initial deformation close to interface. ii) Accumulation of dislocation in the substrate. iii) Formation of cell structure due to dislocation tangling and arrangement. iv) Dislocation rearrangement and subgrain formation. v.a) Formation HAGB from dislocation accumulation into LAGB. v.b) HAGB formation through DRX by progressive lattice rotation

  16. Relating microstructures to SCC in Inconel 718

    International Nuclear Information System (INIS)

    Sheth, N.K.; Sanchez, J.M.; Hendrix, B.C.; Ide, H.; Miglin, M.T.

    1993-01-01

    Inconel 718, a nickel-iron-base superalloy, is used for stressed applications in the nuclear and oil industries. A major concern facing the continued and expanding use of Inconel 718 in these applications has been their susceptibility to Inter-Granular Stress Corrosion Cracking (IGSCC). Efforts to reduce stress corrosion cracking (SCC) have been aimed at reducing the susceptibility in this alloy to the formation of the deleterious delta (Ni 3 Nb) phase. Microstructural evaluation of SCC test specimens of different thermo-mechanical histories shows that inhomogeneities of all types, including carbides, nitrides, and different morphologies of δ phase, worsen the SCC resistance of IN718. Here the authors study five samples of IN718 with measured hardness and SCC growth rates. A preliminary ranking of the factors mentioned above on SCC resistance finds that precipitation of a fine δ phase, due to over-aging, has the most profound effect on SCC susceptibility of IN718

  17. Effects of Cations on Corrosion of Inconel 625 in Molten Chloride Salts

    Science.gov (United States)

    Zhu, Ming; Ma, Hongfang; Wang, Mingjing; Wang, Zhihua; Sharif, Adel

    2016-04-01

    Hot corrosion of Inconel 625 in sodium chloride, potassium chloride, magnesium chloride, calcium chloride and their mixtures with different compositions is conducted at 900°C to investigate the effects of cations in chloride salts on corrosion behavior of the alloy. XRD, SEM/EDS were used to analyze the compositions, phases, and morphologies of the corrosion products. The results showed that Inconel 625 suffers more severe corrosion in alkaline earth metal chloride molten salts than alkaline metal chloride molten salts. For corrosion in mixture salts, the corrosion rate increased with increasing alkaline earth metal chloride salt content in the mixture. Cations in the chloride molten salts mainly affect the thermal and chemical properties of the salts such as vapor pressure and hydroscopicities, which can affect the basicity of the molten salt. Corrosion of Inconel 625 in alkaline earth metal chloride salts is accelerated with increasing basicity.

  18. Review of corrosion phenomena on zirconium alloys, niobium, titanium, inconel, stainless steel, and nickel plate under irradiation

    International Nuclear Information System (INIS)

    Johnson, A.B. Jr.

    1975-01-01

    The role of nuclear fluxes in corrosion processes was investigated in ATR, ETR, PRTR, and in Hanford production reactors. Major effort was directed to zirconium alloy corrosion parameter studies. Corrosion and hydriding results are reported as a function of oxygen concentration in the coolant, flux level, alloy composition, surface pretreatment, and metallurgical condition. Localized corrosion and hydriding at sites of bonding to dissimilar metals are described. Corrosion behavior on specimens transferred from oxygenated to low-oxygen coolants in ETR and ATR experiments is compared. Mechanism studies suggest that a depression in the corrosion of the Zr--2.5Nb alloy under irradiation is due to radiation-induced aging. The radiation-induced onset of transition on several alloys is in general a gradual process which nucleates locally, causing areas of oxide prosity which eventually encompass the surface. Examination of Zry-2 process tubes reveals that accelerated corrosion has occurred in low-oxygen coolants. Hydrogen contents are relatively low, but show some localized profiles. Gross hydriding has occurred on process tubes containing aluminum spacers, apparently by a galvanic charging mechanism. Titanium paralleled Zry-2 in corrosion behavior under irradiation. Niobium corrosion was variable, but did not appear to be strongly influenced by radiation. Corrosion rates on Inconel and stainless steel were only slightly higher in-flux than out-of-reactor. Corrosion rates on nickel-plated aluminum appeared to vary substantially with preexposure treatments, but the rates generally were accelerated compared to rates on unirradiated coupons. (59 references, 11 tables, 12 figs.)

  19. Effects on stress rupture life and tensile strength of tin additions to Inconel 718

    Science.gov (United States)

    Dreshfield, R. L.; Johnson, W.

    1982-01-01

    Because Inconel 718 represents a major use of columbium and a large potential source of columbium for aerospace alloys could be that of columbium derived from tin slags, the effects of tin additions to Inconel 718 at levels which might be typical of or exceed those anticipated if tin slag derived columbium were used as a melting stock were investigated. Tin was added to 15 pound Inconel 718 heats at levels varying from none added to approximately 10,000 ppm (1 wt%). Limited 1200 F stress rupture testing was performed at stresses from 68,000 to 115,000 psi and a few tensile tests were performed at room temperature, 800 and 1200 F. Additions of tin in excess of 800 ppm were detrimental to ductility and stress rupture life.

  20. FLiNaK compatibility studies with Inconel 600 and silicon carbide

    Energy Technology Data Exchange (ETDEWEB)

    Yoder, Graydon L., E-mail: yodergljr@ornl.gov [Oak Ridge National Laboratory, Bldg. 5700, MS 6167 Bethel Valley Rd., Oak Ridge, TN 37831 (United States); Heatherly, Dennis; Wilson, Dane [Oak Ridge National Laboratory, Bldg. 5700, MS 6167 Bethel Valley Rd., Oak Ridge, TN 37831 (United States); Caja, Mario [Electrochemical Systems, Inc. (ESI), 9320 Collingwood Rd., Knoxville, TN 37922 (United States)

    2016-10-15

    Highlights: • A versatile experimental design has been developed to examine liquid fluoride salt materials compatibility behavior. • Samples of silicon carbide and a grafoil/nickel spiral wound gasket were exposed to FLiNaK salt at 700 °C for 90 days and showed no degradation. • Alloy 600 showed material effects penetrating up to 300 μm below the salt interface after exposure to the salt for 90 days at 700 °C. • Comparison of the Alloy 600 corrosion results with existing data indicated that results were comparable to the few corrosion results available for Alloy 600. • Sapphire viewing windows incorporated in the experiment showed fogging by condensed salt components at the highest test temperatures. - Abstract: A small liquid fluoride salt test apparatus has been constructed and testing has been conducted to examine the compatibility of silicon carbide (SiC), Inconel 600 and a spiral wound gasket material in FLiNaK, the ternary eutectic alkaline metal fluoride salt mixture. These tests were conducted to evaluate materials and sealing systems that could be used in fluoride salt systems. Three months of testing at 700 °C was conducted to assure that these materials and seals would be acceptable when operating under prototypic operating conditions. The SiC specimens showed little or no change over the test period, while the spiral wound gasket material did not show any degradation except that salt might have been seeping into the outermost spirals of the gasket. The Inconel 600 specimens showed regions of voiding which penetrated the specimen surface to about 250 μm in depth. Analysis indicated that the salt had leached chrome from the Inconel surface, as was expected for this material.

  1. Identification of acoustic emission sources in early stages of fatigue process of Inconel 713LC

    Energy Technology Data Exchange (ETDEWEB)

    Bartkova, Denisa; Vlasic, Frantisek; Mazal, Pavel [Brno Univ. of Technology, Brno (Czech Republic). Faculty of Mechanical Engineering

    2014-11-01

    Inconel 713LC is low carbon variant of Inconel 713 nickel-based cast alloy. The biggest advantage of these alloys is their ability to resist a wide variety of operating conditions (corrosive environment, high temperature, high stresses). Main area of applications is aircraft, energetic, chemical and petrochemical industry etc. In many applications, components undergo cyclic stresses. This study presents results of acoustic emission response of Inconel 713LC during high-cycle fatigue testing. In comparison with low-cycle fatigue, stage of initiation of micro cracks is in high-cycle region much more significant and can take several tens of percent of whole fatigue life. This work is focused on comparison of selected parameters of acoustic emission signal in pre-initiation and initiation stage of fatigue crack creation. Signal data were specified by linear location technique, hence only signal from shallow notch was analysed. Acoustic emission signal was correlated with frequency of load reversals which is a function of specimen's rigidity (modulus). Acoustic emission hits with higher stress were detected in pre-initiation stage whereas initiation stage hits exhibited low stress. Acoustic emission signal measurements are supplemented by fractographic and metallographic analysis.

  2. Effect of grain structure on phase transformation events in Inconel 718

    International Nuclear Information System (INIS)

    Dahotre, N.B.; McCay, M.H.; McCay, T.D.; Hubbard, C.R.; Porter, W.D.; Cavin, O.B.

    1993-01-01

    Nickel base superalloys generally obtain their maximum strength from γ'[Ni 3 (Al,Ti)] and γ double-prime[Ni 3 (Al,Ti,Nb)] age hardening precipitates. During welding the γ' precipitation is very rapid and can lead to strain age cracking, which limits weldability. Thus, the weldable superalloys are limited in their Al and Ti content and hence in their ultimate strength. One method of increasing the ultimate strength of a superalloy, while avoiding strain age cracking, is the addition of Nb. This produces Ni 3 Nb(δ), and when used in conjunction with a limited amount of γ', results in an increase in strength without strain age cracking problems. The γ double-prime does not lead to strain age cracking because its transformation kinetics are too slow for formation during ordinary welding practice. This combination of γ' and γ double-prime strengthening is incorporated into the Inconel 718 alloys. The research reported herein was undertaken to determine the time-temperature response of Inconel 718 in the as-cast, wrought and wrought-grain-grown states, using differential thermal analysis (DTA). It is essential to locate the temperature regime of each phase transformation event and to study the transformation sequence in order to tailor sound laser welding techniques for Inconel 718. In the present research, a DTA technique was employed to study both the phase transformation events and the phase transformation sequence as a function of the pre-existing condition of the alloy

  3. A Comprehensive Pitting Study of High Velocity Oxygen Fuel Inconel 625 Coating by Using Electrochemical Testing Techniques

    Science.gov (United States)

    Niaz, Akbar; Khan, Sajid Ullah

    2016-01-01

    In the present work, Inconel 625 was coated on a mild steel substrate using a high velocity oxygen fuel coating process. The pitting propensity of the coating was tested by using open circuit potential versus time, potentiodynamic polarization, electrochemical potentiokinetic reactivation, and scanning electrochemical microscopy. The pitting propensity of the coating was compared with bulk Inconel 625 alloy. The results confirmed that there were regions of different electrochemical activities on the coating which have caused pitting corrosion.

  4. Properties of super alloys for high temperature gas cooled reactor

    International Nuclear Information System (INIS)

    Izaki, Takashi; Nakai, Yasuo; Shimizu, Shigeki; Murakami, Takashi

    1975-01-01

    The existing data on the properties at high temperature in helium gas of iron base super alloys. Incoloy-800, -802 and -807, nickel base super alloys, Hastelloy-X, Inconel-600, -617 and -625, and a casting alloy HK-40 were collectively evaluated from the viewpoint of the selection of material for HTGRs. These properties include corrosion resistance, strength and toughness, weldability, tube making, formability, radioactivation, etc. Creep strength was specially studied, taking into consideration the data on the creep characteristics in the actual helium gas atmosphere. The necessity of further long run creep data is suggested. Hastelloy-X has completely stable corrosion resistance at high temperature in helium gas. Incoloy 800 and 807 and Inconel 617 are not preferable in view of corrosion resistance. The creep strength of Inconel 617 extraporated to 1,000 deg C for 100,000 hours in air was the greatest rupture strength of 0.6 kg/mm 2 in all above alloys. However, its strength in helium gas began to fall during a relatively short time, so that its creep strength must be re-evaluated in the use for long time. The radioactivation and separation of oxide film in primary construction materials came into question, Inconel 617 and Incoloy 807 showed high induced radioactivity intensity. Generally speaking, in case of nickel base alloys such as Hastelloy-X, oxide film is difficult to break away. (Iwakiri, K.)

  5. Residual stresses analysis in ball end milling of nickel-based superalloy Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Junteng; Zhang, Dinghua; Wu, Baohai; Luo, Ming [Key Laboratory of Contemporary Design and Integrated Manufacturing Technology, Northwestern Polytechnical University (China)

    2017-11-15

    Inconel 718 is widely used in the aviation, space, automotive and biomedical industries because of its outstanding properties. Near-surface residual stresses that are induced by ball end milling in Inconel 718 can be crucial for the performance and service time of the machined parts. In this paper, the influences of cutting conditions, including the use of cutting parameters, cutting fluid and spindle angles, on the residual stresses in the ball end milling process of Inconel 718 alloy were investigated experimentally. X-ray diffraction measurements reveal that residual stress distributions are highly influenced by cutting parameters, especially the depth of cut and cutting speed. The milling operation with cooling induces more compressive stresses trend and the magnitude of the residual stresses increases in the tensile direction with the increase of spindle angles. These cutting induced effects were further discussed with respect to thermal- mechanical coupling theory and some observations made by optical microscopy. From this investigation, it is suggested that the machining process parameters are not the smaller the better for the control of residual stresses in the ball end milling process of Inconel 718. (author)

  6. Electromagnetic modeling of stress corrosion cracks in Inconel welds

    International Nuclear Information System (INIS)

    Huang, Haoyu; Miya, Kenzo; Yusa, Noritaka; Hashizume, Hidetoshi; Sera, Takehiko; Hirano, Shinro

    2011-01-01

    This study evaluates suitable numerical modeling of stress corrosion cracks appearing in Inconel welds from the viewpoint of electromagnetic nondestructive evaluations. The stress corrosion cracks analyzed in this study are five artificial ones introduced into welded flat plate, and three natural ones found in a pressurized nuclear power plant. Numerical simulations model a crack as a planar region having a uniform conductivity inside and a constant width, and evaluate the width and conductivity that reproduce the maximum eddy current signals obtained by experiments. The results obtained validate the existence of the minimum value of the equivalent resistance, which is defined by the width divided by conductivity. In contrast, the values of the width and conductivity themselves vary across a wide range. The results also lead to a discussion about (1) the effect of probe utilized on the numerical model, (2) the difference between artificial and natural stress corrosion cracks, and (3) the difference between stress corrosion cracks in base metals and those in Inconel welds in their models. Electromagnetic characteristics of four different Inconel weld alloys are additionally evaluated using a resistance tester and a vibrating sample magnetometer to support the validity of the numerical modeling and the generality of results obtained. (author)

  7. Intercrystalline and transcrystalline vibration fatigue failure in the inconel 718 nickel-based alloy; Inter- und transkristalliner Schwingbruch in der Nickelbasislegierung Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Wanzek, Horst; Fruhner, Annett [Lufthansa Technik AG, Hamburg (Germany). Metallurgical Lab., HAM WR123

    2011-07-01

    The fracture of the turbine rotor disc resulted in the breakdown of the APU and high expenses. The APU is located below the vertical tailplane, at the tail of every major-sized aircraft. The vane receptacle failed in the mode of a vibration fatigue failure of an intercrystalline and transcrystalline progression. The cause of this damage is attributable to the fatigue of the material. This can result from the long service life (21 131 h) and the fact that 9 more vane receptacles exhibited a comparable damage pattern. In INCONEL 718 alloys, cracks propagate in a transcrystalline way when under an alternate bend stress and at temperatures below abt. 600 C. In contrast, cracks propagate because of grain boundary oxidation above abt. 600 C in an intercrystalline way. The phenomenon that the two crack modi occurred alternately on the same fracture area is explained from the fact that the component part was exposed to different temperatures during operation. While the crack progress was transcrystalline in the ''cooler'' starting and stopping phase crack propagation occurred along the grain boundaries (was intercrystalline) in a normal operation above 600 C. Besides a limitation of the running time in its service life, other measures could not be taken for this component part. (orig.)

  8. Fractography analysis of Inconel 718 fatigued at 700°C

    Directory of Open Access Journals (Sweden)

    Michal Jambor

    2016-12-01

    Full Text Available This work deals with the fractography analysis of nickel-base superalloy Inconel 718 fatigued at 700°C in air atmosphere in the high cycle region. During cyclic loading of this alloy at high temperatures some different mechanisms compared to cyclic loading at ambient temperature take place. Cyclic plastic deformation at high temperatures causes some structural changes, which could have some influence on the fatigue process.

  9. Novel microstructural growth in the surface of Inconel 625 by the addition of SiC under electron beam melting

    Energy Technology Data Exchange (ETDEWEB)

    Ahmad, M., E-mail: maqomer@yahoo.com [Physics Division, Pakistan Institute of Nuclear Science and Technology (PINSTECH), P.O. Nilore, Islamabad (Pakistan); Ali, G.; Ahmed, Ejaz; Haq, M.A.; Akhter, J.I. [Physics Division, Pakistan Institute of Nuclear Science and Technology (PINSTECH), P.O. Nilore, Islamabad (Pakistan)

    2011-06-15

    Electron beam melting is being used to modify the microstructure of the surfaces of materials due to its ability to cause localized melting and supercooling of the melt. This article presents an experimental study on the surface modification of Ni-based superalloy (Inconel 625) reinforced with SiC ceramic particles under electron beam melting. Scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction techniques have been applied to characterize the resulted microstructure. The results revealed growth of novel structures like wire, rod, tubular, pyramid, bamboo and tweezers type morphologies in the modified surface. In addition to that fibrous like structure was also observed. Formation of thin carbon sheet has been found at the regions of decomposed SiC. Electron beam modified surface of Inconel 625 alloy has been hardened twice as compared to the as-received samples. Surface hardening effect may be attributed to both the formation of the novel structures as well as the introduction of Si and C atom in the lattice of Inconel 625 alloy.

  10. Novel microstructural growth in the surface of Inconel 625 by the addition of SiC under electron beam melting

    Science.gov (United States)

    Ahmad, M.; Ali, G.; Ahmed, Ejaz; Haq, M. A.; Akhter, J. I.

    2011-06-01

    Electron beam melting is being used to modify the microstructure of the surfaces of materials due to its ability to cause localized melting and supercooling of the melt. This article presents an experimental study on the surface modification of Ni-based superalloy (Inconel 625) reinforced with SiC ceramic particles under electron beam melting. Scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction techniques have been applied to characterize the resulted microstructure. The results revealed growth of novel structures like wire, rod, tubular, pyramid, bamboo and tweezers type morphologies in the modified surface. In addition to that fibrous like structure was also observed. Formation of thin carbon sheet has been found at the regions of decomposed SiC. Electron beam modified surface of Inconel 625 alloy has been hardened twice as compared to the as-received samples. Surface hardening effect may be attributed to both the formation of the novel structures as well as the introduction of Si and C atom in the lattice of Inconel 625 alloy.

  11. Novel microstructural growth in the surface of Inconel 625 by the addition of SiC under electron beam melting

    International Nuclear Information System (INIS)

    Ahmad, M.; Ali, G.; Ahmed, Ejaz; Haq, M.A.; Akhter, J.I.

    2011-01-01

    Electron beam melting is being used to modify the microstructure of the surfaces of materials due to its ability to cause localized melting and supercooling of the melt. This article presents an experimental study on the surface modification of Ni-based superalloy (Inconel 625) reinforced with SiC ceramic particles under electron beam melting. Scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction techniques have been applied to characterize the resulted microstructure. The results revealed growth of novel structures like wire, rod, tubular, pyramid, bamboo and tweezers type morphologies in the modified surface. In addition to that fibrous like structure was also observed. Formation of thin carbon sheet has been found at the regions of decomposed SiC. Electron beam modified surface of Inconel 625 alloy has been hardened twice as compared to the as-received samples. Surface hardening effect may be attributed to both the formation of the novel structures as well as the introduction of Si and C atom in the lattice of Inconel 625 alloy.

  12. Galvanic corrosion resistance of welded dissimilar nickel-base alloys

    International Nuclear Information System (INIS)

    Corbett, R.A.; Morrison, W.S.; Snyder, R.J.

    1986-01-01

    A program for evaluating the corrosion resistance of various dissimilar welded nickel-base alloy combinations is outlined. Alloy combinations included ALLCORR, Hastelloy C-276, Inconel 72 and Inconel 690. The GTAW welding process involved both high and minimum heat in-put conditions. Samples were evaluated in the as-welded condition, as well as after having been aged at various condtions of time and temperature. These were judged to be most representative of process upset conditions which might be expected. Corrosion testing evaluated resistance to an oxidizing acid and a severe service environment in which the alloy combinations might be used. Mechanical properties are also discussed

  13. Microstructural studies on friction surfaced coatings of Ni-based alloys; Gefuegeuntersuchungen an reibgeschweissten Beschichtungen von Ni-Basislegierungen

    Energy Technology Data Exchange (ETDEWEB)

    Akram, Javed; Puli, Ramesh; Kalvala, Prasad Rao; Misra, Mano [Utah Univ., Salt Lake City, UT (United States). Dept. of Metallurgical Engineering

    2015-07-01

    Inconel 625, Inconel 600, Inconel 800H were friction surfaced on steel and Inconel substrates. The interface between steel and Ni-based alloys showed intermixing of two alloys while the interface between two Ni-based alloys showed no such intermixing. The XRD results confirmed that this intermixed zone consisted of mechanical mix two separate metals and no intermetallics were noticed. Friction surfaced Inconel coatings were metallurgically bonded to steel and Inconel substrates with out any physical defects such as voids or cracks. Friction surfaced coatings showed equiaxed fine grained microstructures (4-18 μm) compared with their consumable rod counterparts (12 - 85 μm). Scanning electron microscope electron backscattered diffraction results showed that the coatings consisted of mainly high angle grain boundaries indicative of dynamic recrystallization mechanism. The temperatures recorded using Infra Red camera showed that the temperature attained at the interface between rod and the substrate is about 1100 C. The grain size of the consumable rod was relatively fine near the coating/substrate interface and relatively coarser away from interface indicating the change in strain and temperature the rod experienced at or away from the interface.

  14. The Study of the Impact of Surface Preparation Methods of Inconel 625 and 718 Nickel-Base Alloys on Wettability by BNi-2 and BNi-3 Brazing Filler Metals

    Directory of Open Access Journals (Sweden)

    Lankiewicz K.

    2015-04-01

    Full Text Available The article discusses the impact of surface preparation method of Inconel 625 and 718 nickel-base alloys in the form of sheets on wettability of the surface. The results of the investigations of surface preparation method (such as nicro-blasting, nickel plating, etching, degreasing, abrasive blasting with grit 120 and 220 and manually grinding with grit 120 and 240 on spreading of BNi-2 and BNi-3 brazing filler metals, widely used in the aerospace industry in high temperature vacuum brazing processes, are presented. Technological parameters of vacuum brazing process are shown. The macro- and microscopic analysis have shown that nicro-blasting does not bring any benefits of wettability of the alloys investigated.

  15. The Study Of The Impact Of Surface Preparation Methods Of Inconel 625 And 718 Nickel-Base Alloys On Wettability By BNi-2 And BNi-3 Brazing Filler Metals

    Directory of Open Access Journals (Sweden)

    Lankiewicz K.

    2015-06-01

    Full Text Available The article discusses the impact of surface preparation method of Inconel 625 and 718 nickel-base alloys in the form of sheets on wettability of the surface. The results of the investigations of surface preparation method (such as nicro-blasting, nickel plating, etching, degreasing, abrasive blasting with grit 120 and 220 and manually grinding with grit 120 and 240 on spreading of BNi-2 and BNi-3 brazing filler metals, widely used in the aerospace industry in high temperature vacuum brazing processes, are presented. Technological parameters of vacuum brazing process are shown. The macro- and microscopic analysis have shown that nicro-blasting does not bring any benefits of wettability of the alloys investigated.

  16. Decarburization behavior and mechanical properties of Inconel 617 during high temperature oxidation in He environment

    International Nuclear Information System (INIS)

    Kim, Young Do; Kim, Dae Gun; Jo, Tae Sun; Kim, Hoon Sup; Lim, Jeong Hun

    2010-04-01

    Among Generation IV reactor concepts, high temperature gas-cooled reactors (HTGRs) are high-efficiency systems designed for the economical production of hydrogen and electricity. Inconel 617 is a solid-solution strengthening Ni-based superalloy that shows excellent strength, creep-rupture strength, and oxidation resistance at high temperatures. Thus, it is a desirable candidate for tube material of IHX and HGD in HTGRs. In spite of these excellent properties, aging degradation by long time exposure at high temperature induced to deterioration of mechanical properties and furthermore alloys' lifetime because of Cr-depleted zone and carbide free zone below external scale. Also, machinability of Inconel 617 is a important property for system design. In this study, oxidation and decarbrization behavior were evaluated at various aging temperature and environment. Also, cold rolling was carried out for the machinability evaluation of Inconel 617 and then microstructure change was evaluated

  17. Tritium Permeability of Incoloy 800H and Inconel 617

    Energy Technology Data Exchange (ETDEWEB)

    Philip Winston; Pattrick Calderoni; Paul Humrickhouse

    2012-07-01

    Design of the Next Generation Nuclear Plant (NGNP) reactor and its high-temperature components requires information regarding the permeation of fission generated tritium and hydrogen product through candidate heat exchanger alloys. Release of fission-generated tritium to the environment and the potential contamination of the helium coolant by permeation of product hydrogen into the coolant system represent safety basis and product contamination issues. Of the three potential candidates for high-temperature components of the NGNP reactor design, only permeability for Incoloy 800H has been well documented. Hydrogen permeability data have been published for Inconel 617, but only in two literature reports and for partial pressures of hydrogen greater than one atmosphere, far higher than anticipated in the NGNP reactor. To support engineering design of the NGNP reactor components, the tritium permeability of Inconel 617 and Incoloy 800H was determined using a measurement system designed and fabricated at Idaho National Laboratory. The tritium permeability of Incoloy 800H and Inconel 617, was measured in the temperature range 650 to 950°C and at primary concentrations of 1.5 to 6 parts per million volume tritium in helium. (partial pressures of 10-6 atm)—three orders of magnitude lower partial pressures than used in the hydrogen permeation testing. The measured tritium permeability of Incoloy 800H and Inconel 617 deviated substantially from the values measured for hydrogen. This may be due to instrument offset, system absorption, presence of competing quantities of hydrogen, surface oxides, or other phenomena. Due to the challenge of determining the chemical composition of a mixture with such a low hydrogen isotope concentration, no categorical explanation of this offset has been developed.

  18. Tritium Permeability of Incoloy 800H and Inconel 617

    Energy Technology Data Exchange (ETDEWEB)

    Philip Winston; Pattrick Calderoni; Paul Humrickhouse

    2011-09-01

    Design of the Next Generation Nuclear Plant (NGNP) reactor and its high-temperature components requires information regarding the permeation of fission generated tritium and hydrogen product through candidate heat exchanger alloys. Release of fission-generated tritium to the environment and the potential contamination of the helium coolant by permeation of product hydrogen into the coolant system represent safety basis and product contamination issues. Of the three potential candidates for high-temperature components of the NGNP reactor design, only permeability for Incoloy 800H has been well documented. Hydrogen permeability data have been published for Inconel 617, but only in two literature reports and for partial pressures of hydrogen greater than one atmosphere, far higher than anticipated in the NGNP reactor. To support engineering design of the NGNP reactor components, the tritium permeability of Inconel 617 and Incoloy 800H was determined using a measurement system designed and fabricated at Idaho National Laboratory. The tritium permeability of Incoloy 800H and Inconel 617, was measured in the temperature range 650 to 950 C and at primary concentrations of 1.5 to 6 parts per million volume tritium in helium. (partial pressures of 10-6 atm) - three orders of magnitude lower partial pressures than used in the hydrogen permeation testing. The measured tritium permeability of Incoloy 800H and Inconel 617 deviated substantially from the values measured for hydrogen. This may be due to instrument offset, system absorption, presence of competing quantities of hydrogen, surface oxides, or other phenomena. Due to the challenge of determining the chemical composition of a mixture with such a low hydrogen isotope concentration, no categorical explanation of this offset has been developed.

  19. The effect of sheet processing on the microstructure, tensile, and creep behavior of INCONEL alloy 718

    Science.gov (United States)

    Boehlert, C. J.; Dickmann, D. S.; Eisinger, Ny. N. C.

    2006-01-01

    The grain size, grain boundary character distribution (GBCD), creep, and tensile behavior of INCONEL alloy 718 (IN 718) were characterized to identify processing-microstructure-property relationships. The alloy was sequentially cold rolled (CR) to 0, 10, 20, 30, 40, 60, and 80 pct followed by annealing at temperatures between 954 °C and 1050 °C and the traditional aging schedule used for this alloy. In addition, this alloy can be superplastically formed (IN 718SPF) to a significantly finer grain size and the corresponding microstructure and mechanical behavior were evaluated. The creep behavior was evaluated in the applied stress (σ a ) range of 300 to 758 MPa and the temperature range of 638 °C to 670 °C. Constant-load tensile creep experiments were used to measure the values of the steady-state creep rate and the consecutive load reduction method was used to determine the values of backstress (σ0). The values for the effective stress exponent and activation energy suggested that the transition between the rate-controlling creep mechanisms was dependent on effective stresses (σ e =σ a σ0) and the transition occurred at σ e ≅ 135 MPa. The 10 to 40 pct CR samples exhibited the greatest 650 °C strength, while IN 718SPF exhibited the greatest room-temperature (RT) tensile strength (>1550 MPa) and ductility (ɛ f >16 pct). After the 954 °C annealing treatment, the 20 pct CR and 30 pct CR microstructures exhibited the most attractive combination of elevated-temperature tensile and creep strength, while the most severely cold-rolled materials exhibited the poorest elevated-temperature properties. After the 1050 °C annealing treatment, the IN 718SPF material exhibited the greatest backstress and best creep resistance. Electron backscattered diffraction was performed to identify the GBCD as a function of CR and annealing. The data indicated that annealing above 1010 °C increased the grain size and resulted in a greater fraction of twin boundaries, which in

  20. Alloy development for cladding and duct applications

    International Nuclear Information System (INIS)

    Straalsund, J.L.; Johnson, G.D.

    1981-01-01

    Three general classes of materials under development for cladding and ducts are listed. Solid solution strengthened, or austenitic, alloys are Type 316 stainless steel and D9. Precipitation hardened (also austenitic) alloys consist of D21, D66 and D68. These alloys are similar to such commercial alloys as M-813, Inconel 706, Inconel 718 and Nimonic PE-16. The third general class of alloys is composed of ferritic alloys, with current emphasis being placed on HT-9, a tempered martensitic alloy, and D67, a delta-ferritic steel. The program is comprised of three parallel paths. The current reference, or first generation alloy, is 20% cold worked Type 316 stainless steel. Second generation alloys for near-term applications include D9 and HT-9. Third generation materials consist of the precipitation strengthened steels and ferritic alloys, and are being considered for implementation at a later time than the first and second generation alloys. The development of second and third generation materials was initiated in 1974 with the selection of 35 alloys. This program has proceeded to today where there are six advanced alloys being evaluated. These alloys are the developmental alloys D9, D21, D57, D66 and D68, together with the commerical alloy, HT-9. The status of development of these alloys is summarized

  1. Studies on the Corrosion Resistance of Laser-Welded Inconel 600 and Inconel 625 Nickel-Based Superalloys

    Directory of Open Access Journals (Sweden)

    Łyczkowska K.

    2017-06-01

    Full Text Available The paper presents the results of the electrochemical corrosion tests of Inconel 600 and Inconel 625 laser-welded superalloys. The studies were conducted in order to assess the resistance to general and pitting corrosion in 3.5% NaCl solution. It was found that Inconel 600 possesses good corrosion resistance, however Inconel 625 is characterized by a greater resistance to general and also to pitting corrosion of the weld as well as the base metal.

  2. Ductility dip cracking susceptibility of Inconel Filler Metal 52 and Inconel Alloy 690

    International Nuclear Information System (INIS)

    Kikel, J.M.; Parker, D.M.

    1998-01-01

    Alloy 690 and Filler Metal 52 have become the materials of choice for commercial nuclear steam generator applications in recent years. Filler Metal 52 exhibits improved resistance to weld solidification and weld-metal liquation cracking as compared to other nickel-based filler metals. However, recently published work indicates that Filler Metal 52 is susceptible to ductility dip cracking (DDC) in highly restrained applications. Susceptibility to fusion zone DDC was evaluated using the transverse varestraint test method, while heat affected zone (HAZ) DDC susceptibility was evaluated using a newly developed spot-on-spot varestraint test method. Alloy 690 and Filler Metal 52 cracking susceptibility was compared to the DDC susceptibility of Alloy 600, Filler Metal 52, and Filler Metal 625. In addition, the effect of grain size and orientation on cracking susceptibility was also included in this study. Alloy 690, Filler Metal 82, Filler Metal 52, and Filler Metal 625 were found more susceptible to fusion zone DDC than Alloy 600. Filler Metal 52 and Alloy 690 were found more susceptible to HAZ DDC when compared to wrought Alloy 600, Filler Metal 82 and Filler Metal 625. Filler Metal 52 exhibited the greatest susceptibility to HAZ DDC of all the weld metals evaluated. The base materials were found much more resistant to HAZ DDC in the wrought condition than when autogenously welded. A smaller grain size was found to offer greater resistance to DDC. For weld metal where grain size is difficult to control, a change in grain orientation was found to improve resistance to DDC

  3. Effect of the Cutting Tool Geometry on the Tool Wear Resistance When Machining Inconel 625

    Directory of Open Access Journals (Sweden)

    Tomáš Zlámal

    2017-12-01

    Full Text Available The paper deals with the design of a suitable cutting geometry of a tool for the machining of the Inconel 625 nickel alloy. This alloy is among the hard-to-machine refractory alloys that cause very rapid wear on cutting tools. Therefore, SNMG and RCMT indexable cutting insert were used to machine the alloy. The selected insert geometry should prevent notch wear and extend tool life. The alloy was machined under predetermined cutting conditions. The angle of the main edge and thus the size and nature of the wear changed with the depth of the material layer being cut. The criterion for determining a more suitable cutting geometry was the tool’s durability and the roughness of the machined surface.

  4. Effect of the Cutting Tool Geometry on the Tool Wear Resistance when Machining Inconel 625

    Directory of Open Access Journals (Sweden)

    Tomáš Zlámal

    2018-03-01

    Full Text Available The paper deals with the design of a suitable cutting geometry of a tool for the machining of the Inconel 625 nickel alloy. This alloy is among the hard-to-machine refractory alloys that cause very rapid wear on cutting tools. Therefore, SNMG and RCMT indexable cutting insert were used to machine the alloy. The selected insert geometry should prevent notch wear and extend tool life. The alloy was machined under predetermined cutting conditions. The angle of the main edge and thus the size and nature of the wear changed with the depth of the material layer being cut. The criterion for determining a more suitable cutting geometry was the tool’s durability and the roughness of the machined surface.

  5. Effect of refining techniques on stress corrosion cracking behaviour of Inconel X-750

    International Nuclear Information System (INIS)

    Mishra, B.; Moore, J.J.

    1988-01-01

    High-strength age-hardenable nickel-base superalloy Inconel X-750, is susceptible to severe intergranular stress corrosion cracking (IGSCC) when used in the triple heat-treated condition. In this research, the slow strain-rate technique has been employed to evaluate the stress corrosion cracking susceptibility of alloy X-750 under simulated nuclear pressurized water reactor (PWR) conditions, using an automated autoclave system at 8 x 10 6 N m -2 pressure and 289 0 C temperature. The alloys produced via electroslag refining (ESR) or vacuum arc refining (VAR) processing routes containing 0.004% and 0.011% sulphur, respectively, were solution annealed at either 1075 or 1240 0 C for 2 h and water quenched followed by ageing in the 704 to 871 0 C temperature range for up to 200 h, followed by air cooling or furnace cooling. The scanning electron microscopy performed on fractured surfaces revealed that Inconel X-750 processed through the ESR route, solution annealed at 1240 0 C for 2 h and water quenched, aged at 871 0 C for 200 h and furnace cooled provided the best combination of strength, ductility and resistance to SCC. A less sensitized area adjacent to the grain boundary was responsible for the improvement in properties and the alloy X-750 is recommended for PWR applications in the above conditions of processing and heat treatment. (author)

  6. Environmentally assisted cracking of Inconel X750

    International Nuclear Information System (INIS)

    Skeldon, P.; Lowick, J.H.B.; Hurst, P.

    1987-05-01

    The resistance of different heat treatments of Inconel X750 to environmentally assisted cracking in simulated PWR primary water at 340 0 C has been assessed by slow strain rate, U-bend and bent beam tests. At the corrosion potential (ca - 670 mV (Ag/AgCl)), in low oxygen conditions (≤ 2 ppb) a single-stage ageing (704 0 C/20 h) gives much improved resistance compared with two-stage ageing (885 0 C/24 h + 704 0 C/20 h). However, material given the former ageing treatment can be susceptible to cracking at highly anodic potentials (> - 200 mV (Ag/AgCl)) if the alloy is significantly sensitized. (author)

  7. The irradiation induced microstructural development and the role of γ' on void formation in Ni-based alloys

    International Nuclear Information System (INIS)

    Kato, T.; Nakata, K.; Masaoka, I.; Takahashi, H.; Takeyama, T.; Ohnuki, S.; Osanai, H.

    1984-01-01

    The microstructural development for Inconel X-750, Ni-13 at% Al, and Ni-11.5 at% Si alloys during irradiation was investigated. These alloys were previously heat-treated at temperatures of 723-1073 K, and γ' precipitates were produced. Irradiation was performed in a high voltage electron microscope in the temperature range 627-823 K. In the case of solution-treated Inconel, interstitial dislocation loops were formed initially, while voids were nucleated after longer times. When the Inconel specimen containing a high number density of small γ' was irradiated, dislocation loops were formed in both the matrix and precipitate-matrix interface. The loops formed on the interface scarcely grew during irradiation. On the other hand, for the Ni-Al alloy fine γ' nucleated during irradiation, the large γ' precipitated by pre-aging, dissolved. A similar resolution process was also observed in Ni-Si alloy. Furthermore, in the Ni-Si alloy precipitates of γ' formed preferentially at interstitial dislocation loops and both specimen surfaces. (orig.)

  8. Faster methods for estimating arc centre position during VAR and results from Ti-6Al-4V and INCONEL 718 alloys

    Science.gov (United States)

    Nair, B. G.; Winter, N.; Daniel, B.; Ward, R. M.

    2016-07-01

    Direct measurement of the flow of electric current during VAR is extremely difficult due to the aggressive environment as the arc process itself controls the distribution of current. In previous studies the technique of “magnetic source tomography” was presented; this was shown to be effective but it used a computationally intensive iterative method to analyse the distribution of arc centre position. In this paper we present faster computational methods requiring less numerical optimisation to determine the centre position of a single distributed arc both numerically and experimentally. Numerical validation of the algorithms were done on models and experimental validation on measurements based on titanium and nickel alloys (Ti6Al4V and INCONEL 718). The results are used to comment on the effects of process parameters on arc behaviour during VAR.

  9. Optimization of process parameters for WEDM of Inconel 825 using grey relational analysis

    Directory of Open Access Journals (Sweden)

    Pawan Kuma

    2018-09-01

    Full Text Available Inconel 825 is high nickel-chromium-based superalloy which retains its mechanical properties and exhibits good corrosion and oxidation resistance at elevated temperature. Inconel 825 is extensively used for making aircraft engine parts like combustor casing and turbine blades in aero space industry. This research proposed the Response Surface Methodology with GRA to optimize multiple responses during Wire-cut EDM of Inconel 825. At optimum combination of input parameters i.e. A4B1C1D5E4F2, increase in MRR from 36.13 mm2/min to 41.822 mm2/min, decrease in SR from 2.842μm to 2.445μm and decrease in WWR from 0.01832 to 0.01758 was obtained. Experimental results showed that pulse-on time, wire feed, pulse-off time, and peak current significantly affected the MRR, and surface integrity of specimen and electrode with the formation of craters, pockmarks, debris, micro cracks, and recast layer. The optimal parametric combination obtained from the present study will be advantageous for working on high strength; high thermal conductivity and low melting point materials like nickel alloys.

  10. Effect of the As-Forged and Heat-Treated Microstructure on the Room Temperature Anisotropic Ductile Fracture of Inconel 718

    Science.gov (United States)

    Teimouri, Javad; Hosseini, Seyed Rahman; Farmanesh, Khosro

    2018-05-01

    The purpose of the present work was to investigate the effect of primary carbides and the δ-phase on the anisotropic ductile fracture of Inconel 718 in the forging process. Inconel 718 alloys were prepared by VIM + VAR processes with various carbon contents (0.009 and 0.027 wt.%). Then, the alloys were forged and annealed at temperatures of 980 and 1030 °C. The room temperature mechanical anisotropy of the alloys was evaluated at the longitudinal direction (LD) and transverse direction (TD). Tensile and impact tests were used to characterize the mechanical properties of the specimens. The microstructural characterization and the fractography of the alloys were carried out by FE-SEM. The obtained results showed that the fracture strain and the impact energy in the TD were 30-50% lower than the LD. The fracture was accelerated by the δ-phase, leading to the reduction of impact energy in the longitudinal and the lateral directions up to 50%. The low-carbon alloy indicated similar characteristics in both the LD and the TD. Aligned carbides changed the fracture path from a zigzag path in the LD to a fibrous path in the TD, while the δ-phase created a flat fracture path. The shear lip area ratio in the tensile fracture cross section was decreased by reducing ductility.

  11. Response surface modelling of tool electrode wear rate and material removal rate in micro electrical discharge machining of Inconel 718

    DEFF Research Database (Denmark)

    Puthumana, Govindan

    2017-01-01

    Inconel 718 is a corrosion-resistant and high strength nickel-based alloy with wide range of applications includingcomponents for cryogenic tankage, liquid fueled rockets and casings for aircraft engines. The material is characterizedby high hardness, high temperature strength, low thermal...

  12. Creep and relaxation behavior of Inconel-617

    International Nuclear Information System (INIS)

    Osthoff, W.; Ennis, P.J.; Nickel, H.; Schuster, H.

    1984-01-01

    The static and dynamic creep behavior of Inconel alloy 617 has been determined in constant load creep tests, relaxation tests, and stress reduction tests in the temperature range 1023 to 1273 K. The results have been interpreted using the internal stress concept: The dependence of the internal stress on the applied stress and test temperature was determined. In a few experiments, the influence of cold deformation prior to the creep test on the magnitude of the internal stress was also investigated. It was found that the experimentally observed relaxation behavior could be more satisfactorily described using the Norton creep equation modified by incorporation of the internal stress than by the conventional Norton creep equation

  13. Corrosion Compatibility Studies on Inconel-600 in NP Decontamination Solution

    Energy Technology Data Exchange (ETDEWEB)

    Park, Sang Yoon; Jung, Jun Young; Won, Huijun; Choi, Wangkyu; Moon, Jeikwon [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2013-05-15

    It is well known that corrosion and contamination process in the primary cooling circuit of nuclear reactors are essentially interrelated: the contaminant isotopes are mostly corrosion products activated in the reactor core, and the contamination takes place on the out-core of Inconel-600 surface. This radionuclide uptake takes place up to the inner oxide layer and oxide/metal interface. So, it is necessary to remove inner oxide layer as well as outer oxide layer for excellent decontamination effects. The outer oxide layers are composed of Fe{sub 3}O{sub 4} and NiFe{sub 2}O{sub 4}. On the other hand, the inner oxide layers are composed of Cr{sub 2}O{sub 3}, (Ni{sub 1-x}Ni{sub x})(Cr{sub 1-y}Fe{sub y}){sub 2}O{sub 4}, and FeCr{sub 2}O{sub 4}. Because of chromium in the trivalent oxidation state which is difficult to dissolve, the oxide layer has an excellent protectiveness and become hard to be decontaminated. Alkaline permanganate (AP) or nitric permanganate (NP) oxidative phase has been used to dissolve the chromium-rich oxide. A disadvantage of AP process is the generation of a large volume of secondary waste. On the other hand, that of NP process is the high corrosion rate for Ni-base alloys. Therefore, for the safe use of oxidative phase in PWR system decontamination, it is necessary to reformulate the NP chemicals for decrease of corrosion rate. This study describes the corrosion compatibility on Inconel-600 and type 304 stainless steel in NP decontamination solution for PWR applications. To evaluate the general corrosion properties, weight change of NP treated specimens was measured. NP treated specimen surface was observed using optical microscope (OM) and scanning electron microscopy (SEM) for the evaluation of the localized corrosion. The effect of additives on the corrosion of the specimens was also evaluated. This study describes the corrosion compatibility on Inconel-600 and type 304 stainless steel in NP decontamination solution for PWR applications

  14. Corrosion Compatibility Studies on Inconel-600 in NP Decontamination Solution

    International Nuclear Information System (INIS)

    Park, Sang Yoon; Jung, Jun Young; Won, Huijun; Choi, Wangkyu; Moon, Jeikwon

    2013-01-01

    It is well known that corrosion and contamination process in the primary cooling circuit of nuclear reactors are essentially interrelated: the contaminant isotopes are mostly corrosion products activated in the reactor core, and the contamination takes place on the out-core of Inconel-600 surface. This radionuclide uptake takes place up to the inner oxide layer and oxide/metal interface. So, it is necessary to remove inner oxide layer as well as outer oxide layer for excellent decontamination effects. The outer oxide layers are composed of Fe 3 O 4 and NiFe 2 O 4 . On the other hand, the inner oxide layers are composed of Cr 2 O 3 , (Ni 1-x Ni x )(Cr 1-y Fe y ) 2 O 4 , and FeCr 2 O 4 . Because of chromium in the trivalent oxidation state which is difficult to dissolve, the oxide layer has an excellent protectiveness and become hard to be decontaminated. Alkaline permanganate (AP) or nitric permanganate (NP) oxidative phase has been used to dissolve the chromium-rich oxide. A disadvantage of AP process is the generation of a large volume of secondary waste. On the other hand, that of NP process is the high corrosion rate for Ni-base alloys. Therefore, for the safe use of oxidative phase in PWR system decontamination, it is necessary to reformulate the NP chemicals for decrease of corrosion rate. This study describes the corrosion compatibility on Inconel-600 and type 304 stainless steel in NP decontamination solution for PWR applications. To evaluate the general corrosion properties, weight change of NP treated specimens was measured. NP treated specimen surface was observed using optical microscope (OM) and scanning electron microscopy (SEM) for the evaluation of the localized corrosion. The effect of additives on the corrosion of the specimens was also evaluated. This study describes the corrosion compatibility on Inconel-600 and type 304 stainless steel in NP decontamination solution for PWR applications. It is revealed that Inconel-600 specimen is more

  15. The irradiation-induced microstructural development and the role of γ' on void formation in Ni-based alloys

    Science.gov (United States)

    Kato, Takahiko; Nakata, Kiyotomo; Masaoka, Isao; Takahashi, Heishichiro; Takeyama, Taro; Ohnuki, Soumei; Osanai, Hisashi

    1984-05-01

    The microstructural development for Inconel X-750, N1-13 at%A1, and Ni-11.5 at%Si alloys during irradiation was investigated. These alloys were previously heat-treated at temperatures of 723-1073 K, and γ' precipitates were produced. Irradiation was performed in a high voltage electron microscope (1000 kV) in the temperature range 673-823 K. In the case of solution-treated Inconel, interstitial dislocation loops were formed initially, while voids were nucleated after longer times. When the Inconel specimen containing a high number density of small γ' was irradiated, dislocation loops were formed in both the matrix and precipitate-matrix interface. The loops formed on the interface scarcely grew during irradiation. On the other hand, for the Ni-Al alloy fine γ' nucleated during irradiation, the large γ' precipitated by pre-aging, dissolved. A similar resolution process was also observed in Ni-Si alloy. Furthermore, in the Ni-Si alloy precipitates of γ' formed preferentially at interstitial dislocation loops and both specimen surfaces.

  16. The influence of laser alloying on the structure and mechanical properties of AlMg5Si2Mn surface layers

    Science.gov (United States)

    Pakieła, W.; Tański, T.; Brytan, Z.; Labisz, K.

    2016-04-01

    The goal of this paper was focused on investigation of microstructure and properties of surface layer produced during laser surface treatment of aluminium alloy by high-power fibre laser. The performed laser treatment involves remelting and feeding of Inconel 625 powder into the aluminium surface. As a base metal was used aluminium alloy AlMg5Si2Mn. The Inconel powder was injected into the melt pool and delivered by a vacuum feeder at a constant rate of 4.5 g/min. The size of Inconel alloying powder was in the range 60-130 µm. In order to remelt the aluminium alloy surface, the fibre laser of 3 kW laser beam power has been used. The linear laser scan rate of the beam was set 0.5 m/min. Based on performed investigations, it was possible to obtain the layer consisting of heat-affected zone, transition zone and remelted zone, without cracks and defects having much higher hardness value compared to the non-alloyed material.

  17. The surface topography of Inconel, stainless steel and copper after argon ion bombardment

    International Nuclear Information System (INIS)

    Vogelbruch, K.; Vietzke, E.

    1983-01-01

    Energetic particle bombardment of metals is known to change the surface topography. To simulate the behaviour of the first wall of a fusion device under real plasma conditions, we have investigated the surface topography of rotating targets after 30 keV argon ion bombardment at 70deg incident angle by electron scanning micrographs. Under these conditions Inconel 600, 601, 625, stainless steel, and copper showed no cones, pyramids or cliffs, but only etching figures and at higher ion doses relatively flat hills. Thus, it can be concluded, that the influence of energetic particles on the first wall of a fusion reactor is smaller than expected from the results of such sputtering experiments, which have dealt with the formation of surface structures under ion bombardment at constant incident direction. (author)

  18. Reciprocating sliding wear of Inconel 600 tubing in room temperature air

    International Nuclear Information System (INIS)

    Kim, Hun; Choi, Jong Hyun; Kim, Jun Ki; Hong, Hyun Seon; Kim, Seon Jin

    2003-01-01

    The sliding wear behavior of the material of a steam generator in a nuclear power station (Inconel 600) was investigated at room temperature. Effects of the wear parameters such as material combination, sliding distance and contact stress were examined with various mating materials including 304 austenitic stainless steel, Inconel 600 and Al-Cu alloy 2011. In the prediction of the wear volume by Archard's wear equation, the standard error range was calculated to be ±4.04x10 -9 m 3 and the reliability to be 71.9% for the combination of Inconel 600 and 304 stainless steel. The error range was considered to be relatively broad because the wear coefficient in Archard's equation was assumed to be a constant, regardless of the changes in the mechanical properties during the wear. In the present study, the sliding wear behavior turned out to be influenced by the material combination; the wear volume of 304 stainless steel did not linearly increase with the sliding distance, while that of other material combinations exhibited linear increases. Based on the experimental results, the wear coefficient was modified as a function of the sliding distance. The calculation with the modified wear equation showed that the error range narrowed down to ±2.60x10 -9 m 3 and the reliability increased to 75.3%, compared to Archard's original equation

  19. Mechanical Behaviour of Inconel 718 Thin-Walled Laser Welded Components for Aircraft Engines

    Directory of Open Access Journals (Sweden)

    Enrico Lertora

    2014-01-01

    Full Text Available Nickel alloys are very important in many aerospace applications, especially to manufacture gas turbines and aero engine components, where high strength and temperature resistance are necessary. These kinds of alloys have to be welded with high energy density processes, in order to preserve their high mechanical properties. In this work, CO2 laser overlap joints between Inconel 718 sheets of limited thickness in the absence of postweld heat treatment were made. The main application of this kind of joint is the manufacturing of a helicopter engine component. In particular the aim was to obtain a specific cross section geometry, necessary to overcome the mechanical stresses found in these working conditions without failure. Static and dynamic tests were performed to assess the welds and the parent material fatigue life behaviour. Furthermore, the life trend was identified. This research pointed out that a full joint shape control is possible by choosing proper welding parameters and that the laser beam process allows the maintenance of high tensile strength and ductility of Inconel 718 but caused many liquation microcracks in the heat affected zone (HAZ. In spite of these microcracks, the fatigue behaviour of the overlap welds complies with the technical specifications required by the application.

  20. THE EFFECT OF THE CONDITIONS OF SHOT PEENING THE INCONEL 718 NICKEL ALLOY ON THE GEOMETRICAL STRUCTURE OF THE SURFACE

    Directory of Open Access Journals (Sweden)

    Kazimierz Zaleski

    2017-06-01

    Full Text Available The article presents the research results of roughness and topography of the surface of Inconel 718 nickel alloy after shot peening. Evaluation of stereometric properties of the surface layer of the examined material was performed based on the amplitude, height and Abbott-Firestone curve parametres. The shot peening was carried out on the impulse shot peening stand. The impact energy Ej, distance between the traces xs and the ball diameter dk were changed in the range: Ej = 60 ÷ 240 mJ, xs = 0,15 ÷ 0,5 mm, dk = 3,95 ÷ 12,45 mm. The T8000 RC 120-140 device of the Hommel-Etamic company, along with the software, was used for measuring the surface roughness and for determining the material bearing curve. As a result of the machin-ing, the surface roughness was reduced and the selected functional parameters were improved.

  1. Study of welding characteristics of inconel 600 alloy using a continuous wave Nd:YAG laser beam

    International Nuclear Information System (INIS)

    Song, Seong Wook; Yoo, Young Tae; Shin, Ho Jun

    2004-01-01

    Laser beam welding is increasingly being used in welding of structural steels. The laser welding process is one of the most advanced manufacturing technologies owing to its high speed and deep penetration. The thermal cycles associated with laser welding are generally much faster than those involved in conventional arc welding processes, leading to a rather small weld zone. Experiments are performed for Inconel 600 plates changing several process parameter such as laser power, welding speed, shielding gas flow rate, presence of surface pollution, with fixed or variable gap and misalignment between plate and plate, etc. The follow conclusions can be drawn that laser power and welding speed have a pronounced effect on size and shape of the fusion zone. Increase in welding speed resulted in an increase in weld depth/ aspect ratio and hence a decrease in the fusion zone size. The penetration depth increased with the increase in laser power. Welding characteristics of austienite Inconel 600 using a continuous wave Nd:YAG laser are experimentally investigated. This paper describes the weld ability of inconel 600 for machine structural use by Nd:YAG laser

  2. Caustic stress corrosion cracking of Inconel-600, Incoloy-800, and Type 304 stainless steel

    International Nuclear Information System (INIS)

    Theus, G.J.

    1976-01-01

    High-temperature electrochemical tests have resulted in the stress corrosion cracking of Inconel-600 and Incoloy-800 (registered trademarks, International Nickel Company), and Type 304 stainless steel in caustic solutions. Results show that stress corrosion cracking of these alloys can be prevented or accelerated by varying their electrochemical potential. To a certain extent, the same effect can be achieved by altering the gas atmosphere above the test solution from a pure nitrogen cover gas to a mixture of 5 percent H 2 and 95 percent N 2 . The effect of the cover gas can then be negated by adjusting the specimen's electrochemical potential either to cause or to inhibit stress corrosion cracking. Some specifics of the test results reveal that in deoxygenated caustic solutions, Inconel-600 cracks intergranularly at mildly anodic potentials; Incoloy-800 cracks transgranularly at reduced potentials (at or near the open circuit potential) and intergranularly at highly oxidizing potentials; and cracking is mixed (transgranular/intergranular) for Type 304 stainless steel at or near the open circuit potential. The severity of cracking for both Inconel-600 and Incoloy-800 in deoxygenated caustic solutions is reduced by giving the materials a simulated post-weld heat treatment (1150 0 F for 18 h). Test results on Inconel-600 show that high-carbon (0.06 percent) material cracks less severely than low-carbon (0.02 percent) material, in both the simulated post-weld heat-treated condition and the mill-annealed condition

  3. Biaxial thermal creep of Inconel 617 and Haynes 230 at 850 and 950 °C

    International Nuclear Information System (INIS)

    Tung, Hsiao-Ming; Mo, Kun; Stubbins, James F.

    2014-01-01

    The biaxial thermal creep behavior of Inconel 617 and Haynes 230 at 850 and 950 °C was investigated. Biaxial stresses were generated using the pressurized tube technique. The detailed creep deformation and fracture mechanism have been studied. Creep curves for both alloys showed that tertiary creep accounts for a greater portion of the materials’ life, while secondary creep only accounts for a small portion. Fractographic examinations of the two alloys indicated that nucleation, growth, and coalescence of creep voids are the dominant micro-mechanisms for creep fracture. At 850 °C, alloy 230 has better creep resistance than alloy 617. When subjected to the biaxial stress state, the creep rupture life of the two alloys was considerably reduced when compared to the results obtained by uniaxial tensile creep tests. The Monkman–Grant relation proves to be a promising method for estimating the long-term creep life for alloy 617, whereas alloy 230 does not follow the relation. This might be associated with the significant changes in the microstructure of alloy 230 at high temperatures

  4. Microstructural Evolution of Inconel 625 and Inconel 686CPT Weld Metal for Clad Carbon Steel Linepipe Joints: A Comparator Study

    Science.gov (United States)

    Maltin, Charles A.; Galloway, Alexander M.; Mweemba, Martin

    2014-07-01

    Microstructural evolution of Inconel 625 and Inconel 686CPT filler metals, used for the fusion welding of clad carbon steel linepipe, has been investigated and compared. The effects of iron dilution from the linepipe parent material on the elemental segregation potential of the filler metal chemistry have been considered. The results obtained provide significant evidence to support the view that, in Inconel 686CPT weld metal, the segregation of tungsten is a function of the level of iron dilution from the parent material. The data presented indicate that the incoherent phase precipitated in the Inconel 686CPT weld metal has a morphology that is dependent on tungsten enrichment and, therefore, iron dilution. Furthermore, in the same weld metal, a continuous network of finer precipitates was observed. The Charpy impact toughness of each filler metal was evaluated, and the results highlighted the superior impact toughness of the Inconel 625 weld metal over that of Inconel 686CPT.

  5. Microstructure and interfacial behaviour of Alumina/Inconel 600 joints prepared by brazing route

    International Nuclear Information System (INIS)

    Laik, A.; Mishra, P.; Bhanumurthy, K.; Kashyap, B.P.

    2010-01-01

    Joining of metals to ceramics remains a technological challenge due to the wide difference in the physical and mechanical properties of the two classes of materials. Attempt was made to produce leak tight joints between Inconel-600 and alumina using the brazing route with Au-Ni brazing alloy. Alumina tubes were metallised following the Mo-Mn route and then coated with Ni. The metallised alumina tubes were brazed to Inconel-600 ferrules using Au-18%Ni brazing alloy under vacuum, at optimised process parameters. In order to study the effect of prolong annealing on the microstructural stability and the micro-chemistry of the brazing zone, brazed joints were subjected to prolong annealing at 400 deg C and 560 deg C for 8000 hrs each. Detailed analysis of the interfacial structure of the brazing zones was done using an electron probe microanalyser (EPMA). X-ray maps of the elements Fe, Ni, Cr, Al, Au, Mo and Mn along with BSE images of the brazing zone are given. These X-ray maps precisely reveal the micro-chemistry of the brazing zones. The various phases formed were identified. The distribution of the various elements across the interfaces was also obtained, which helps to reveal the chemical behaviour of the individual elements during the process of brazing. Two phases appear very distinctly in the brazement, one is rich in Au and the other is rich in Ni. Depending upon their affinity, rest of the elements shows a partitioning in these two phases. While Fe, Cr and Mo get dissolved in the Ni-rich phase, Mn seems to partition in the Au-rich phase. The microstructure and the X-ray maps of the couple annealed at 400 deg C shows that the spatial variation in the composition throughout the brazing zone gets homogenised due to diffusion at high temperatures. This effect is even more pronounced on annealing at 560 deg C. Moreover, the transport of Cr from the Inconel side to the surface of alumina is very evident. On annealing at 560 deg C, a region rich in Cr, was found to

  6. Total hemispherical emissivity of Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Keller, Benjamin P.; Nelson, Shawn E.; Walton, Kyle L.; Ghosh, Tushar K.; Tompson, Robert V.; Loyalka, Sudarshan K., E-mail: LoyalkaS@missouri.edu

    2015-06-15

    Highlights: • We have measured the total hemispherical emissivity for Inconel 718 from about 600–1250 K. • Oxidation in air at 1073 K resulted in an increase in emissivity. • Sandblasting of Inconel 718 was also observed to increase the emissivity. • Coating of graphite powder onto the ‘as-received’ Inconel 718 showed no increase in the emissivity. • Coating of graphite powder onto the 220 grit sandblasted Inconel 718 did show an increase in emissivity. - Abstract: Total hemispherical emissivity for Inconel 718 was measured in anticipation of its application in Very High Temperature Gas Reactors (VHTRs). A majority of current emissivity data for Inconel 718 is in the form of spectral measurements. The data presented here were obtained with an experimental apparatus based on the standard ASTM C835-06 for total hemispherical emittance. Measurements of Inconel 718 were made for four different surface types including: (i) ‘as-received’ from the manufacturer, (ii) oxidized in air and humidified helium, (iii) sandblasted with aluminum oxide powder, and (iv) with a thin coating of nuclear grade graphite powder (grade NGB-18). The emissivity for the ‘as-received’ sample ranged from 0.21 to 0.28 in the temperature interval from 760 K to 1275 K. Oxidation in air at 1073 K resulted in an increase in emissivity into the range from 0.2 at 650 K to 0.52 at 1200 K. There was no dependence on the oxidation times studied here. Oxidation with humidified helium at 1073 K produced less of an increase in emissivity than the oxidation in air but there was an increase up to the range from 0.2 at 600 K to 0.35 at 1200 K. Sandblasting of Inconel 718 was also observed to increase the emissivity up to the range from 0.43 at 780 K to 0.53 at 1270 K when 60 grit sized powder was used and up to the range from 0.45 at 683 K to 0.57 at 1267 K when 120 and 220 grit sized powders were used. Coating of graphite powder onto the ‘as-received’ Inconel 718 showed no increase

  7. Reduction of a thin chromium oxide film on Inconel surface upon treatment with hydrogen plasma

    Energy Technology Data Exchange (ETDEWEB)

    Vesel, Alenka, E-mail: alenka.vesel@guest.arnes.si [Jozef Stefan Institute, Jamova cesta 39, 1000 Ljubljana (Slovenia); Mozetic, Miran [Jozef Stefan Institute, Jamova cesta 39, 1000 Ljubljana (Slovenia); Balat-Pichelin, Marianne [PROMES-CNRS Laboratory, 7 Rue du four solaire, 66120 Font Romeu Odeillo (France)

    2016-11-30

    Highlights: • Oxidized Inconel alloy was exposed to hydrogen at temperatures up to 1500 K. • Oxide reduction in hydrogen plasma started at approximately 1300 K. • AES depth profiling revealed complete reduction of oxides in plasma. • Oxides were not reduced, if the sample was heated just in hydrogen atmosphere. • Surface of reduced Inconel preserved the same composition as the bulk material. - Abstract: Inconel samples with a surface oxide film composed of solely chromium oxide with a thickness of approximately 700 nm were exposed to low-pressure hydrogen plasma at elevated temperatures to determine the suitable parameters for reduction of the oxide film. The hydrogen pressure during treatment was set to 60 Pa. Plasma was created by a surfaguide microwave discharge in a quartz glass tube to allow for a high dissociation fraction of hydrogen molecules. Auger electron depth profiling (AES) was used to determine the decay of the oxygen in the surface film and X-ray diffraction (XRD) to measure structural modifications. During hydrogen plasma treatment, the oxidized Inconel samples were heated to elevated temperatures. The reduction of the oxide film started at temperatures of approximately 1300 K (considering the emissivity of 0.85) and the oxide was reduced in about 10 s of treatment as revealed by AES. The XRD showed sharper substrate peaks after the reduction. Samples treated in hydrogen atmosphere under the same conditions have not been reduced up to approximately 1500 K indicating usefulness of plasma treatment.

  8. Use of Hot Rolling for Generating Low Deviation Twins and a Disconnected Random Boundary Network in Inconel 600 Alloy

    Science.gov (United States)

    Sahu, Sandeep; Yadav, Prabhat Chand; Shekhar, Shashank

    2018-02-01

    In this investigation, Inconel 600 alloy was thermomechanically processed to different strains via hot rolling followed by a short-time annealing treatment to determine an appropriate thermomechanical process to achieve a high fraction of low-Σ CSL boundaries. Experimental results demonstrate that a certain level of deformation is necessary to obtain effective "grain boundary engineering"; i.e., the deformation must be sufficiently high to provide the required driving force for postdeformation static recrystallization, yet it should be low enough to retain a large fraction of original twin boundaries. Samples processed in such a fashion exhibited 77 pct length fraction of low-Σ CSL boundaries, a dominant fraction of which was from Σ3 ( 64 pct), the latter with very low deviation from its theoretical misorientation. The application of hot rolling also resulted in a very low fraction of Σ1 ( 1 pct) boundaries, as desired. The process also leads to so-called "triple junction engineering" with the generation of special triple junctions, which are very effective in disrupting the connectivity of the random grain boundary network.

  9. Phase Transformations in Nickel base Superalloy Inconel 718 during Cyclic Loading at High Temperature

    Directory of Open Access Journals (Sweden)

    Michal Jambor

    2017-06-01

    Full Text Available Nickel base superalloys are hi-tech materials intended for high temperature applications. This property owns a complex microstructure formed by matrix of Ni and variety of precipitates. The type, form and the amount of these phases significantly affect the resulting properties of these alloys. At sufficiently long exposure to high temperatures, the transformation phase can occur, which can lead to degradation of properties of these alloys. A cyclic plastic deformation can accelerate these changes, and they could occur at significantly lower temperatures or in shorter time of exposure. The aim of this study is to describe phase transformation, which can occur by a cyclic plastic deformation at high temperatures in nickel base superalloy Inconel 718.

  10. Normal spectral emittance of Inconel 718 aeronautical alloy coated with yttria stabilized zirconia films

    Energy Technology Data Exchange (ETDEWEB)

    Gonzalez-Fernandez, L. [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain); Industria de Turbo Propulsores, S.A., Planta de Zamudio, Edificio 300, 48170 Zamudio, Bizkaia (Spain); Campo, L. del [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain); Perez-Saez, R.B., E-mail: raul.perez@ehu.es [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain); Tello, M.J. [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain)

    2012-02-05

    Highlights: Black-Right-Pointing-Pointer Emittance of Inconel 718 coated with plasma sprayed yttria stabilized zirconia. Black-Right-Pointing-Pointer The coating is opaque for {lambda} > 9 {mu}m and semi-transparent for {lambda} < 9 {mu}m. Black-Right-Pointing-Pointer In the semi-transparent region the emittance decreases with coating thickness. Black-Right-Pointing-Pointer 300 {mu}m thick coatings are still semi-transparent. Black-Right-Pointing-Pointer In the opaque region the surface roughness determines the emittance level. - Abstract: Knowledge of the radiative behaviour of the yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) is needed to perform radiative heat transfer calculations in industrial applications. In this paper, normal spectral emittance experimental data of atmospheric plasma sprayed (PS) YSZ films layered on Inconel 718 substrates are shown. The spectral emittance was measured between 2.5 and 22 {mu}m on samples with film thicknesses ranging from 20 to 280 {mu}m. The samples were heated in a controlled environment, and the emittance was measured for several temperatures between 330 and 730 Degree-Sign C. The dependence of the spectral emittance with film thickness, surface roughness and temperature has been studied and compared with the available results for YSZ TBCs obtained by electron-beam physical vapour deposition. The PS-TBC samples show a Christiansen point at {lambda} = 12.8 {mu}m. The films are semi-transparent for {lambda} < 9 {mu}m, and opaque for {lambda} > 9 {mu}m. In the semi-transparent region, the contribution of the radiation emitted by the Inconel 718 substrate to the global emittance of the samples is analysed. In addition, the influence of the roughness in the emittance values in the opaque spectral region is discussed. Finally, the total normal emittance is obtained as a function of the TBC thickness.

  11. Nickel base alloys

    International Nuclear Information System (INIS)

    Gibson, R.C.; Korenko, M.K.

    1980-01-01

    Nickel based alloy, the characteristic of which is that it mainly includes in percentages by weight: 57-63 Ni, 7-18 Cr, 10-20 Fe, 4-6 Mo, 1-2 Nb, 0.2-0.8 Si, 0.01-0.05 Zr, 1.0-2.5 Ti, 1.0-2.5 Al, 0.02-0.06 C and 0.002-0.015 B. The aim is to create new nickel-chromium alloys, hardened in a solid solution and by precipitation, that are stable, exhibit reduced swelling and resistant to plastic deformation inside the reactor. These alloys of the gamma prime type have improved mechanical strengthm swelling resistance, structural stability and welding properties compared with Inconel 625 [fr

  12. The Precipitation Processes and Mechanical Properties of Aged Inconel 718 Alloy After Annealing

    Directory of Open Access Journals (Sweden)

    Maj P.

    2017-09-01

    Full Text Available Inconel 718 is a precipitation hardenable nickel-iron based superalloy. It has exceptionally high strength and ductility compared to other metallic materials. This is due to intense precipitation of the γ’ and γ” strengthening phases in the temperature range 650-850°C. The main purpose of the authors was to analyze the aging process in Inconel 718 obtained in accordance with AMS 5596, and its effect on the mechanical properties. Tensile and hardness tests were used to evaluate the mechanical properties, in the initial aging process and after reheating, as a function of temperature and time respectively in the ranges 650°-900°C and 5-480 min. In addition, to link the mechanical properties with the microstructure transmission microscopy observations were carried out in selected specimens. As a result, factors influencing the microstructure changes at various stages of strengthening were observed. The authors found that the γ’’ phase nucleates mostly homogenously in the temperature range 650-750°C, causing the greatest increase in strength. On the other hand, the γ’ and δ phases are formed heterogeneously at 850°C or after longer annealing in 800°C, which may weaken the material.

  13. The study on force, surface integrity, tool life and chip on laser assisted machining of inconel 718 using Nd:YAG laser source.

    Science.gov (United States)

    Venkatesan, K

    2017-07-01

    Inconel 718, a high-temperature alloy, is a promising material for high-performance aerospace gas turbine engines components. However, the machining of the alloy is difficult owing to immense shear strength, rapid work hardening rate during turning, and less thermal conductivity. Hence, like ceramics and composites, the machining of this alloy is considered as difficult-to-turn materials. Laser assisted turning method has become a promising solution in recent years to lessen cutting stress when materials that are considered difficult-to-turn, such as Inconel 718 is employed. This study investigated the influence of input variables of laser assisted machining on the machinability aspect of the Inconel 718. The comparison of machining characteristics has been carried out to analyze the process benefits with the variation of laser machining variables. The laser assisted machining variables are cutting speeds of 60-150 m/min, feed rates of 0.05-0.125 mm/rev with a laser power between 1200 W and 1300 W. The various output characteristics such as force, roughness, tool life and geometrical characteristic of chip are investigated and compared with conventional machining without application of laser power. From experimental results, at a laser power of 1200 W, laser assisted turning outperforms conventional machining by 2.10 times lessening in cutting force, 46% reduction in surface roughness as well as 66% improvement in tool life when compared that of conventional machining. Compared to conventional machining, with the application of laser, the cutting speed of carbide tool has increased to a cutting condition of 150 m/min, 0.125 mm/rev. Microstructural analysis shows that no damage of the subsurface of the workpiece.

  14. In situ corrosion testing of various nickel alloys at Måbjerg waste incineration plant

    DEFF Research Database (Denmark)

    Montgomery, Melanie; Hansson, A. N.; Jensen, S. A.

    2013-01-01

    overlay material currently being used to give improved corrosion resistance. In order to assess the use of alternative nickel alloys, test panels have been manufactured and inserted into Måbjerg waste incineration plant. Inconel 625 as a 50% weld overlay, two layered weld overlay and as a spiral weld......The majority of waste in Denmark is disposed via waste to energy (WTE) incineration plants which are fabricated from carbon steel. However, due to the increasing corrosiveness of waste over the years, more corrosion resistant alloys are required. In Denmark, Inconel 625 (UNSN06625) is the weld...... overlay was exposed. Other nickel materials exposed were weld overlay Alloy 686, Alloy 50 and Sumitomo Super 625 coextruded tube. Exposure has been undertaken from 2003 to 2009 in the first pass and 2005–2009 in the second pass, and sections have been removed and investigated during this period...

  15. Corrosion of high Ni-Cr alloys and Type 304L stainless steel in HNO3-HF

    International Nuclear Information System (INIS)

    Ondrejcin, R.S.; McLaughlin, B.D.

    1980-04-01

    Nineteen alloys were evaluated as possible materials of construction for steam heating coils, the dissolver vessel, and the off-gas system of proposed facilities to process thorium and uranium fuels. Commercially available alloys were found that are satisfactory for all applications. With thorium fuel, which requires HNO 3 -HF for dissolution, the best alloy for service at 130 0 C when complexing agents for fluoride are used is Inconel 690; with no complexing agents at 130 0 C, Inconel 671 is best. At 95 0 C, six other alloys tested would be adequate: Haynes 25, Ferralium, Inconel 625, Type 304L stainless steel, Incoloy 825, and Haynes 20 (in order of decreasing preference); based on composition, six untested alloys would also be adequate. The ions most effective in reducing fluoride corrosion were the complexing agents Zr 4+ and Th 4+ ; Al 3+ was less effective. With uranium fuel, modestly priced Type 304L stainless steel is adequate. Corrosion will be most severe in HNO 3 -HF used occasionally for flushing and in solutions of HNO 3 and corrosion products (ferric and dichromate ions). HF corrosion can be minimized by complexing the fluoride ion and by passivation of the steel with strong nitric acid. Corrosion caused by corrosion products can be minimized by operating at lower temperatures

  16. Electrochemical Impedance Spectroscopy Of Metal Alloys

    Science.gov (United States)

    Macdowell, L. G.; Calle, L. M.

    1993-01-01

    Report describes use of electrochemical impedance spectroscopy (EIS) to investigate resistances of 19 alloys to corrosion under conditions similar to those of corrosive, chloride-laden seaside environment of Space Transportation System launch site. Alloys investigated: Hastelloy C-4, C-22, C-276, and B-2; Inconel(R) 600, 625, and 825; Inco(R) G-3; Monel 400; Zirconium 702; Stainless Steel 304L, 304LN, 316L, 317L, and 904L; 20Cb-3; 7Mo+N; ES2205; and Ferralium 255. Results suggest electrochemical impedance spectroscopy used to predict corrosion performances of metal alloys.

  17. Effects of heat input on the pitting resistance of Inconel 625 welds by overlay welding

    Science.gov (United States)

    Kim, Jun Seok; Park, Young IL; Lee, Hae Woo

    2015-03-01

    The objective of this study was to establish the relationship between the dilution ratio of the weld zone and pitting resistance depending on the heat input to welding of the Inconel alloy. Each specimen was produced by electroslag welding using Inconel 625 as the filler metal. In the weld zone of each specimen, dendrite grains were observed near the fusion line and equiaxed grains were observed on the surface. It was also observed that a melted zone with a high Fe content was formed around the fusion line, which became wider as the welding heat input increased. In order to evaluate the pitting resistance, potentiodynamic polarization tests and CPT tests were conducted. The results of these tests confirmed that there is no difference between the pitting resistances of each specimen, as the structures of the surfaces were identical despite the effect of the differences in the welding heat input for each specimen and the minor dilution effect on the surface.

  18. The study on force, surface integrity, tool life and chip on laser assisted machining of inconel 718 using Nd:YAG laser source

    Directory of Open Access Journals (Sweden)

    K. Venkatesan

    2017-07-01

    Full Text Available Inconel 718, a high-temperature alloy, is a promising material for high-performance aerospace gas turbine engines components. However, the machining of the alloy is difficult owing to immense shear strength, rapid work hardening rate during turning, and less thermal conductivity. Hence, like ceramics and composites, the machining of this alloy is considered as difficult-to-turn materials. Laser assisted turning method has become a promising solution in recent years to lessen cutting stress when materials that are considered difficult-to-turn, such as Inconel 718 is employed. This study investigated the influence of input variables of laser assisted machining on the machinability aspect of the Inconel 718. The comparison of machining characteristics has been carried out to analyze the process benefits with the variation of laser machining variables. The laser assisted machining variables are cutting speeds of 60–150 m/min, feed rates of 0.05–0.125 mm/rev with a laser power between 1200 W and 1300 W. The various output characteristics such as force, roughness, tool life and geometrical characteristic of chip are investigated and compared with conventional machining without application of laser power. From experimental results, at a laser power of 1200 W, laser assisted turning outperforms conventional machining by 2.10 times lessening in cutting force, 46% reduction in surface roughness as well as 66% improvement in tool life when compared that of conventional machining. Compared to conventional machining, with the application of laser, the cutting speed of carbide tool has increased to a cutting condition of 150 m/min, 0.125 mm/rev. Microstructural analysis shows that no damage of the subsurface of the workpiece.

  19. Fatigue-crack propagation response of two nickel-base alloys in a liquid sodium environment

    International Nuclear Information System (INIS)

    Mills, W.J.; James, L.A.

    1979-01-01

    The elevated temperature fatigue-crack propagation response of Inconel 600 and Inconel 718 was characterized within a linear-elastic fracture mechanics framework in air and low-oxygen liquid sodium environments. The crack growth rates of both nickel-base alloys tested in liquid sodium were found to be considerably lower than those obtained in air. This enhanced fatigue resistance in sodium was attributed to the very low oxygen content in the inert sodium environment. Electron fractographic examination of the Inconel 600 and Inconel 718 fatigue fracture surfaces revealed that operative crack growth mechanisms were dependent on the prevailing stress intensity level. Under low growth rate conditions, Inconel 600 and Inconel 718 fracture surfaces exhibited a faceted, crystallographic morphology in both air and sodium environments. In the higher growth rate regime, fatigue striations were observed; however, striations formed in sodium were rather ill-defined. These indistinct striations were attributed to the absence of oxygen in the liquid sodium environment. Striation spacing measurements were found to be in excellent agreement with macroscopic growth rates in both environments

  20. Selection of a high performance alloy for gas turbine blade using finite element methods

    International Nuclear Information System (INIS)

    Khawaja, H.A.; Khan, A.M.; Ali, S.T.

    2007-01-01

    With the extensive increase in the utilization of energy resources in the modern era, the need of energy extraction from various resources has pronounced in recent years. Thus comprehensive efforts have been made around the globe in the technological development of turbo machines where means of energy extraction is energized fluids. This development led the eviation industry to power boost due to better performing engines. Meanwhile, the structural conformability requirements relative to the functional requirements have also increased with the advent of newer, better performing materials. Thus there is a need to study the material behavior and its usage with the idea of selecting the best possible material for its application. In this work a gas turbine blade of a small turbofan engine, where geometry and aerodynamic data was available, was analyzed for its structural behavior in the proposed mission envelope, where the engine turbine is subjected to high thermal, inertial and aerodynamic loads. FE linear stress analysis was carried out on the turbine blade. The results revealed the upper limit of UTS for the blade. Based on the limiting factor, high performance alloys were selected from the literature. The two most recommended alloy categories for gas turbine blades are NIMONIC and INCONEL from where total of 21 types of INCONEL alloys and 12 of NIMONIC alloys, available on on commercial bases, were analyzed individually to meet the INCONEL alloys for further analysis. On the basis of stress-strain behavior of finalized alloys, the FE restriction of UFOS of 1.33 and yield strength. Final selection is made keeping in view other factors like manufacturability and workability in due consideration. (author)

  1. Control of microstructure and mechanical properties of laser solid formed Inconel 718 superalloy by electromagnetic stirring

    Science.gov (United States)

    Liu, Fencheng; Cheng, Hongmao; Yu, Xiaobin; Yang, Guang; Huang, Chunping; Lin, Xin; Chen, Jing

    2018-02-01

    The coarse columnar grains and special interface in laser solid formed (LSFed) Inconel 718 superalloy workpieces seriously affect their mechanical properties. To improve the microstructure and mechanical properties of LSFed Inconel 718 superalloy, electromagnetic stirring (EMS) was introduced to alter the solidification process of the molten pool during LSF. The results show that EMS could not completely eliminate the epitaxially growing columnar grains, however, the strong convection of liquid metals can effectively influence the solid-liquid interface growing mode. The segregation of alloying elements on the front of solid-liquid interface is inhibited and the degree of constitutional supercooling decreases correspondingly. Comparing the microstructures of samples formed under different process parameters, the size and amount of the γ+Laves eutectic phases formed in interdendritic area decrease along with the increasing magnetic field intensity, resulting in more uniformly distributed alloying elements. The residual stress distribution is proved to be more uniform, which is beneficial to the grain refinement after recrystallilzaiton. Mechanical properties testing results show an improvement of 100 MPa in tensile strength and 22% in elongation was obtained after EMS was used. The high cycle fatigue properties at room temperature was also improved from 4.09 × 104 cycles to 8.21 × 104 cycles for the as-deposited samples, and from 5.45 × 104 cycles to 12.73 × 104 cycles for the heat treated samples respectively.

  2. Dynamic mechanical behaviour and dislocation substructure evolution of Inconel 718 over wide temperature range

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Woei-Shyan, E-mail: wslee@mail.ncku.edu.tw [Department of Mechanical Engineering, National Cheng Kung University, Tainan 701, Taiwan (China); Lin, Chi-Feng [National Center for High-Performance Computing, Hsin-Shi Tainan County 744, Taiwan (China); Chen, Tao-Hsing [Department of Mechanical Engineering, National Kaohsiung University of Applied Sciences, Kaohsiung 807, Taiwan (China); Chen, Hong-Wei [Department of Mechanical Engineering, National Cheng Kung University, Tainan 701, Taiwan (China)

    2011-07-25

    A compressive split-Hopkinson pressure bar and transmission electron microscope (TEM) are used to investigate the mechanical behaviour and microstructural evolution of Inconel 718 at strain rates ranging from 1000 to 5000 s{sup -1} and temperatures between -150 and 550 deg. C. The results show that the flow stress increases with an increasing strain rate or a reducing temperature. The strain rate effect is particularly pronounced at strain rates greater than 3000 s{sup -1} and a deformation temperature of -150 deg. C. A significant thermal softening effect occurs at temperatures between -150 and 25 deg. C. The microstructural observations reveal that the strengthening effect in deformed Inconel 718 alloy is a result primarily of dislocation multiplication. The dislocation density increases with increasing strain rate, but decreases with increasing temperature. By contrast, the dislocation cell size decreases with increasing strain rate, but increases with increasing temperature. It is shown that the correlation between the flow stress, the dislocation density and the dislocation cell size is well described by the Bailey-Hirsch constitutive equations.

  3. Friction Freeform Fabrication of Superalloy Inconel 718: Prospects and Problems

    Science.gov (United States)

    Dilip, J. J. S.; Janaki Ram, G. D.

    2014-01-01

    Friction Freeform Fabrication is a new solid-state additive manufacturing process. The present investigation reports a detailed study on the prospects of this process for additive part fabrication in superalloy Inconel 718. Using a rotary friction welding machine and employing alloy 718 consumable rods in solution treated condition, cylindrical-shaped multi-layer friction deposits (10 mm diameter) were successfully produced. In the as-deposited condition, the deposits showed very fine grain size with no grain boundary δ phase. The deposits responded well to direct aging and showed satisfactory room-temperature tensile properties. However, their stress rupture performance was unsatisfactory because of their layered microstructure with very fine grain size and no grain boundary δ phase. The problem was overcome by heat treating the deposits first at 1353 K (1080 °C) (for increasing the grain size) and then at 1223 K (950 °C) (for precipitating the δ phase). Overall, the current study shows that Friction Freeform Fabrication is a very useful process for additive part fabrication in alloy 718.

  4. Oxidization and stress corrosion cracking initiation of austenitic alloys in supercritical water

    International Nuclear Information System (INIS)

    Behnamian, Y.; Li, M.; Luo, J.L.; Chen, W.X.; Zheng, W.; Guzonas, D.A.

    2012-01-01

    This study determined the stress corrosion cracking behaviour of austenitic alloys in pure supercritical water. Austenitic stainless steels 310S, 316L, and Inconel 625 were tested as static capsule samples at 500 o C for up to 5000 h. After that period, crack initiations were readily observed in all samples, signifying susceptibility to stress corrosion cracking. The microcracks in 316L stainless steel and Inconel 625 were almost intergranular, whereas transgranular microcrack initiation was observed in 310S stainless steel. (author)

  5. Oxidization and stress corrosion cracking initiation of austenitic alloys in supercritical water

    Energy Technology Data Exchange (ETDEWEB)

    Behnamian, Y.; Li, M.; Luo, J.L.; Chen, W.X. [Univ. of Alberta, Dept. of Chemical and Materials Engineering, Edmonton, Alberta (Canada); Zheng, W. [Materials Technology Laboratory, NRCan, Ottawa, Ontario (Canada); Guzonas, D.A. [Atomic Energy of Canada Limited, Chalk River, Ontario (Canada)

    2012-07-01

    This study determined the stress corrosion cracking behaviour of austenitic alloys in pure supercritical water. Austenitic stainless steels 310S, 316L, and Inconel 625 were tested as static capsule samples at 500{sup o}C for up to 5000 h. After that period, crack initiations were readily observed in all samples, signifying susceptibility to stress corrosion cracking. The microcracks in 316L stainless steel and Inconel 625 were almost intergranular, whereas transgranular microcrack initiation was observed in 310S stainless steel. (author)

  6. Aeronautical Industry Requirements for Titanium Alloys

    Science.gov (United States)

    Bran, D. T.; Elefterie, C. F.; Ghiban, B.

    2017-06-01

    The project presents the requirements imposed for aviation components made from Titanium based alloys. A significant portion of the aircraft pylons are manufactured from Titanium alloys. Strength, weight, and reliability are the primary factors to consider in aircraft structures. These factors determine the requirements to be met by any material used to construct or repair the aircraft. Many forces and structural stresses act on an aircraft when it is flying and when it is static and this thesis describes environmental factors, conditions of external aggression, mechanical characteristics and loadings that must be satisfied simultaneously by a Ti-based alloy, compared to other classes of aviation alloys (as egg. Inconel super alloys, Aluminum alloys).For this alloy class, the requirements are regarding strength to weight ratio, reliability, corrosion resistance, thermal expansion and so on. These characteristics additionally continue to provide new opportunities for advanced manufacturing methods.

  7. Influence of damages caused by surface defects upon the oxydation mechanism of inconel 600

    International Nuclear Information System (INIS)

    Rousselet, J.M.; Moulin, G.; Huntz, A.M.

    1985-01-01

    The influence of thermochemical and mechanical treatments on the oxidation mechanism of Ni 76 Cr 16 Fe 8 alloys (Inconel 600) was studied from a kinetic and analytical point of view, in order to clarify the role of defects either due to a prestrain or related to impurities such as S, C. for example to overcome sulfur pollution of steam generator tubes of nuclear power plant. For unstrained alloys, the oxidation process is controlled by the diffusion of alloy elements in the metallic substrate. But, beyond a critical strain value, the diffusion rate in the alloy is sufficiently accelerated by the strain induced defects to involve an oxidation control by the diffusion of base-elements (Cr, Ni, Fe) in the oxide scale. Sulfides present in the alloy (due to a pre-sulphidation treatment) strongly accelerate the oxidation kinetics owing to the fact that a first oxidation step, controlled by a chemical process of sulphide decomposition, takes place simultaneously to an internal oxidation; then, a second step related to sulphur diffusion through the oxide scale appears; sulphur in the oxide scale creates defects which accelerate cationic diffusion in the oxides. The baneful influence of sulphur can be balanced by prestraining the material [fr

  8. Microstructure of irradiated Inconel 706 fuel pin cladding

    International Nuclear Information System (INIS)

    Yang, W.J.S.; Makenas, B.J.

    1983-08-01

    A fuel pin from the HEDL-P-60 experiment with a cladding of solution-annealed Inconel 706 breached in an apparently brittle manner at a position 12.7 cm above the bottom of the fuel column with a crack of 5.72 cm in length after 5.0 atomic percent burnup in EBR-II. Temperatures (time-averaged midwall) and fast fluences for the fractured area range from 447 0 C and 5.5 x 10 22 n/cm 2 to 526 0 C and 6.1 x 10 22 n/cm 2 (E > 0.1 MeV). Specimens of the fractured fuel pin section were successfully prepared and examined in both a scanning electron microscope and a transmission electron microscope. The fracture surfaces of the breached section showed brittle intergranular fracture characteristics for both the axial and circumferential cracks. Formation of γ' in the matrix near the breach confirmed that the irradiation temperature at the breached area was below 500 0 C, in agreement with other estimates of the temperature for the area, 447 to 526 0 C. A hexagonal eta-phase, Ni 3 (Ti,Nb), precipitated at boundaries near the breach. A more extensive eta-phase coating at grain boundaries was found in a section irradiated at 650 0 C. The eta-phase plates at grain boundaries are expected to have a detrimental effect on alloy ductility. A plane of weakness in this region along the (111) slip planes will develop in Inconel 706 because the eta-plates have a (111) habit relationship with the matrix

  9. Microstructure and mechanical behavior of direct metal laser sintered Inconel alloy 718

    Energy Technology Data Exchange (ETDEWEB)

    Smith, Derek H. [Department of Mechanical Engineering, University of New Hampshire, Durham, NH 03824 (United States); Bicknell, Jonathan; Jorgensen, Luke [Turbocam Energy Solutions, Turbocam International, Dover, NH 03820 (United States); Patterson, Brian M.; Cordes, Nikolaus L. [Materials Science Division, Los Alamos National Laboratory, Los Alamos, NM 87545 (United States); Tsukrov, Igor [Department of Mechanical Engineering, University of New Hampshire, Durham, NH 03824 (United States); Knezevic, Marko, E-mail: marko.knezevic@unh.edu [Department of Mechanical Engineering, University of New Hampshire, Durham, NH 03824 (United States)

    2016-03-15

    In this paper, we investigate microstructure and quasi-static mechanical behavior of the direct metal laser sintered Inconel 718 superalloy as a function of build direction (BD). The printed material was further processed by annealing and double-aging, hot isostatic pressing (HIP), and machining. We characterize porosity fraction and distribution using micro X-ray computed tomography (μXCT), grain structure and crystallographic texture using electron backscattered diffraction (EBSD), and mechanical response in quasi-static tension and compression using standard mechanical testing at room temperature. Analysis of the μXCT imaging shows that majority of porosity develops in the outer layer of the printed material. However, porosity inside the material is also present. The EBSD measurements reveal formation of columnar grains, which favor < 001 > fiber texture components along the BD. These measurements also show evidence of coarse-grained microstructure present in the samples treated by HIP. Finally, analysis of grain boundaries reveal that HIP results in a large number of annealing twins compared to that in samples that underwent annealing and double-aging. The yield strength varies with the testing direction by approximately 7%, which is governed by a combination of grain morphology and crystallographic texture. In particular, we determine tension–compression asymmetry in the yield stress as well as anisotropy of the material flow during compression. We find that HIP lowers yield stress but improves ductility relative to the annealed and aged material. These results are discussed and critically compared with the data reported for wrought material in the same condition. - Highlights: • Microstructure and mechanical properties of DMLS Inconel 718 are studied in function of build direction. • Inhomogeneity of microstructure in the material in several conditions is quantified by μXCT and EBSD. • Anisotropy and asymmetry in the mechanical response are

  10. Microstructure and mechanical behavior of direct metal laser sintered Inconel alloy 718

    International Nuclear Information System (INIS)

    Smith, Derek H.; Bicknell, Jonathan; Jorgensen, Luke; Patterson, Brian M.; Cordes, Nikolaus L.; Tsukrov, Igor; Knezevic, Marko

    2016-01-01

    In this paper, we investigate microstructure and quasi-static mechanical behavior of the direct metal laser sintered Inconel 718 superalloy as a function of build direction (BD). The printed material was further processed by annealing and double-aging, hot isostatic pressing (HIP), and machining. We characterize porosity fraction and distribution using micro X-ray computed tomography (μXCT), grain structure and crystallographic texture using electron backscattered diffraction (EBSD), and mechanical response in quasi-static tension and compression using standard mechanical testing at room temperature. Analysis of the μXCT imaging shows that majority of porosity develops in the outer layer of the printed material. However, porosity inside the material is also present. The EBSD measurements reveal formation of columnar grains, which favor fiber texture components along the BD. These measurements also show evidence of coarse-grained microstructure present in the samples treated by HIP. Finally, analysis of grain boundaries reveal that HIP results in a large number of annealing twins compared to that in samples that underwent annealing and double-aging. The yield strength varies with the testing direction by approximately 7%, which is governed by a combination of grain morphology and crystallographic texture. In particular, we determine tension–compression asymmetry in the yield stress as well as anisotropy of the material flow during compression. We find that HIP lowers yield stress but improves ductility relative to the annealed and aged material. These results are discussed and critically compared with the data reported for wrought material in the same condition. - Highlights: • Microstructure and mechanical properties of DMLS Inconel 718 are studied in function of build direction. • Inhomogeneity of microstructure in the material in several conditions is quantified by μXCT and EBSD. • Anisotropy and asymmetry in the mechanical response are determined by

  11. Determination of emissivity coefficient of heat-resistant super alloys and cemented carbide

    Directory of Open Access Journals (Sweden)

    Kieruj Piotr

    2016-12-01

    Full Text Available This paper presents the analysis of emissivity engineering materials according to temperature. Experiment is concerned on difficult to machine materials, which may be turned with laser assisting. Cylindrical samples made of nickel-based alloys Inconel 625, Inconel 718, Waspaloy and tungsten-carbides based on cobalt matrix were analyzed. The samples’ temperature in contact method was compared to the temperature measured by non-contact pyrometers. Based on this relative, the value of the emissivity coefficient was adjusted to the right indication of pyrometers.

  12. Evaluation of High Temperature Corrosion Resistance of Finned Tubes Made of Austenitic Steel And Nickel Alloys

    Directory of Open Access Journals (Sweden)

    Turowska A.

    2016-06-01

    Full Text Available The purpose of the paper was to evaluate the resistance to high temperature corrosion of laser welded joints of finned tubes made of austenitic steel (304,304H and nickel alloys (Inconel 600, Inconel 625. The scope of the paper covered the performance of corrosion resistance tests in the atmosphere of simulated exhaust gases of the following chemical composition: 0.2% HCl, 0.08% SO2, 9.0% O2 and N2 in the temperature of 800°C for 1000 hours. One found out that both tubes made of austenitic steel and those made of nickel alloy displayed good resistance to corrosion and could be applied in the energy industry.

  13. Production and fabrication of vanadium alloys for the radiative divertor program of DIII-D

    International Nuclear Information System (INIS)

    Johnson, W.R.; Smith, J.P.

    1997-01-01

    V-4Cr-4Ti alloy has been selected for use in the manufacture of a portion of the DIII-D Radiative Divertor upgrade. The production of a 1200-kg ingot of V-4Cr-4Ti alloy, and processing into final sheet and rod product forms suitable for components of the DIII-D Radiative Divertor Program (RDP), has been completed by Wah Chang (formerly Teledyne Wah Chang) of Albany, Oregon (WCA). CVN impact tests on sheet material indicate that the material has properties comparable to other previously-processed V-4Cr-4Ti and V-5Cr-5Ti alloys. Joining of V-4Cr-4Ti alloy has been identified as the most critical fabrication issue for its use in the RDP, and research into several joining methods for fabrication of the RDP components, including resistance seam, friction, and electron beam welding, and explosive bonding is being pursued. Preliminary trials have been successful in the joining of V-alloy to itself by resistance, friction, and electron beam welding processes, and to Inconel 625 by friction welding. In addition, an effort to investigate the explosive bonding of V-4Cr-4Ti alloy to Inconel 625, in both tube-to-bar and sheet-to-sheet configurations, has been initiated, and results have been encouraging

  14. Production and fabrication of vanadium alloys for the radiative divertor program of DIII-D

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, W.R.; Smith, J.P.

    1997-08-01

    V-4Cr-4Ti alloy has been selected for use in the manufacture of a portion of the DIII-D Radiative Divertor upgrade. The production of a 1200-kg ingot of V-4Cr-4Ti alloy, and processing into final sheet and rod product forms suitable for components of the DIII-D Radiative Divertor Program (RDP), has been completed by Wah Chang (formerly Teledyne Wah Chang) of Albany, Oregon (WCA). CVN impact tests on sheet material indicate that the material has properties comparable to other previously-processed V-4Cr-4Ti and V-5Cr-5Ti alloys. Joining of V-4Cr-4Ti alloy has been identified as the most critical fabrication issue for its use in the RDP, and research into several joining methods for fabrication of the RDP components, including resistance seam, friction, and electron beam welding, and explosive bonding is being pursued. Preliminary trials have been successful in the joining of V-alloy to itself by resistance, friction, and electron beam welding processes, and to Inconel 625 by friction welding. In addition, an effort to investigate the explosive bonding of V-4Cr-4Ti alloy to Inconel 625, in both tube-to-bar and sheet-to-sheet configurations, has been initiated, and results have been encouraging.

  15. Effect of Powder-Suspended Dielectric on the EDM Characteristics of Inconel 625

    Science.gov (United States)

    Talla, Gangadharudu; Gangopadhyay, S.; Biswas, C. K.

    2016-02-01

    The current work attempts to establish the criteria for powder material selection by investigating the influence of various powder-suspended dielectrics and machining parameters on various EDM characteristics of Inconel 625 (a nickel-based super alloy) which is nowadays regularly used in aerospace, chemical, and marine industries. The powders include aluminum (Al), graphite, and silicon (Si) that have significant variation in their thermo-physical characteristics. Results showed that powder properties like electrical conductivity, thermal conductivity, density, and hardness play a significant role in changing the machining performance and the quality of the machined surface. Among the three powders, highest material removal rate was observed for graphite powder due to its high electrical and thermal conductivities. Best surface finish and least radial overcut (ROC) were attained using Si powder. Maximum microhardness was found for Si due to its low thermal conductivity and high hardness. It is followed by graphite and aluminum powders. Addition of powder to the dielectric has increased the crater diameter due to expansion of plasma channel. Powder-mixed EDM (PMEDM) was also effective in lowering the density of surface cracks with least number of cracks obtained with graphite powder. X-ray diffraction analysis indicated possible formation of metal carbides along with grain growth phenomenon of Inconel 625 after PMEDM.

  16. Requirements of titanium alloys for aeronautical industry

    Science.gov (United States)

    Ghiban, Brânduşa; Bran, Dragoş-Teodor; Elefterie, Cornelia Florina

    2018-02-01

    The project presents the requirements imposed for aeronatical components made from Titanium based alloys. Asignificant portion of the aircraft pylons are manufactured from Titanium alloys. Strength, weight, and reliability are the primary factors to consider in aircraft structures. These factors determine the requirements to be met by any material used to construct or repair the aircraft. Many forces and structural stresses act on an aircraft when it is flying and when it is static and this thesis describes environmental factors, conditions of external aggression, mechanical characteristics and loadings that must be satisfied simultaneously by a Ti-based alloy, compared to other classes of aviation alloys (as egg. Inconel super alloys, Aluminum alloys). For this alloy class, the requirements are regarding strength to weight ratio, reliability, corrosion resistance, thermal expansion and so on. These characteristics additionally continue to provide new opportunities for advanced manufacturing methods.

  17. Microstructural evolution of hydroformed Inconel 625 bellows

    Energy Technology Data Exchange (ETDEWEB)

    Pavithra, E., E-mail: epavithrasenthil@gmail.com; Senthil Kumar, V.S., E-mail: vsskumar@annauniv.edu

    2016-06-05

    Fatigue cycle tests of Inconel 625 superalloy bellows expansion joints were conducted using a Fatigue testing machine at both room and elevated (650 °C) temperatures. Optical Microscope, Scanning Electron Microscope (SEM) and Energy Dispersive X-ray Spectroscopy (EDS) were employed to investigate the microstructure evolution of grains and its boundaries. The intermetallic phases like γ″ were found and carbide precipitates were observed on the grain boundaries at elevated temperature. The recrystallization of the grains and its growth at the elevated temperature is characterized. - Highlights: • The fatigue test is conducted for Inconel 625 bellows in both room and elevated (650 °C) temperatures. • The investigation on the microstructural study of Fatigue behaviour of Inconel 625 Bellows Expansion joints. • The characterisation studies were done by Optical microscope and SEM/EDAS.

  18. Microstructural evolution of hydroformed Inconel 625 bellows

    International Nuclear Information System (INIS)

    Pavithra, E.; Senthil Kumar, V.S.

    2016-01-01

    Fatigue cycle tests of Inconel 625 superalloy bellows expansion joints were conducted using a Fatigue testing machine at both room and elevated (650 °C) temperatures. Optical Microscope, Scanning Electron Microscope (SEM) and Energy Dispersive X-ray Spectroscopy (EDS) were employed to investigate the microstructure evolution of grains and its boundaries. The intermetallic phases like γ″ were found and carbide precipitates were observed on the grain boundaries at elevated temperature. The recrystallization of the grains and its growth at the elevated temperature is characterized. - Highlights: • The fatigue test is conducted for Inconel 625 bellows in both room and elevated (650 °C) temperatures. • The investigation on the microstructural study of Fatigue behaviour of Inconel 625 Bellows Expansion joints. • The characterisation studies were done by Optical microscope and SEM/EDAS.

  19. Formation of the Ni3Nb δ-Phase in Stress-Relieved Inconel 625 Produced via Laser Powder-Bed Fusion Additive Manufacturing

    Science.gov (United States)

    Lass, Eric A.; Stoudt, Mark R.; Williams, Maureen E.; Katz, Michael B.; Levine, Lyle E.; Phan, Thien Q.; Gnaeupel-Herold, Thomas H.; Ng, Daniel S.

    2017-11-01

    The microstructural evolution of laser powder-bed additively manufactured Inconel 625 during a post-build stress-relief anneal of 1 hour at 1143 K (870 °C) is investigated. It is found that this industry-recommended heat treatment promotes the formation of a significant fraction of the orthorhombic D0a Ni3Nb δ-phase. This phase is known to have a deleterious influence on fracture toughness, ductility, and other mechanical properties in conventional, wrought Inconel 625; and is generally considered detrimental to materials' performance in service. The δ-phase platelets are found to precipitate within the inter-dendritic regions of the as-built solidification microstructure. These regions are enriched in solute elements, particularly Nb and Mo, due to the micro-segregation that occurs during solidification. The precipitation of δ-phase at 1073 K (800 °C) is found to require up to 4 hours. This indicates a potential alternative stress-relief processing window that mitigates δ-phase formation in this alloy. Ultimately, a homogenization heat treatment is recommended for additively manufactured Inconel 625 because the increased susceptibility to δ-phase precipitation increases the possibility for significant degradation of materials' properties in service.

  20. Inconel 939 processed by selective laser melting: Effect of microstructure and temperature on the mechanical properties under static and cyclic loading

    Energy Technology Data Exchange (ETDEWEB)

    Kanagarajah, P., E-mail: p.kanagarajah@uni-paderborn.de [Lehrstuhl für Werkstoffkunde (Materials Science), University of Paderborn, Pohlweg 47-49, 33098 Paderborn (Germany); Brenne, F. [Lehrstuhl für Werkstoffkunde (Materials Science), University of Paderborn, Pohlweg 47-49, 33098 Paderborn (Germany); Direct Manufacturing Research Center (DMRC), Mersinweg 3, 33098 Paderborn (Germany); Niendorf, T. [Lehrstuhl für Werkstoffkunde (Materials Science), University of Paderborn, Pohlweg 47-49, 33098 Paderborn (Germany); Maier, H.J. [Direct Manufacturing Research Center (DMRC), Mersinweg 3, 33098 Paderborn (Germany); Institut für Werkstoffkunde, Leibniz Universität Hannover, An der Universität 2, 30823 Garbsen (Germany)

    2013-12-20

    Nickel-based superalloys, such as Inconel 939, are a long-established construction material for high-temperature applications and profound knowledge of the mechanical properties for this alloy produced by conventional techniques exists. However, many applications demand for highly complex geometries, e.g. in order to optimize the cooling capability of thermally loaded parts. Thus, additive manufacturing (AM) techniques have recently attracted substantial interest as they provide for an increased freedom of design. However, the microstructural features after AM processing are different from those after conventional processing. Thus, further research is vital for understanding the microstructure-processing relationship and its impact on the resulting mechanical properties. The aim of the present study was to investigate Inconel 939 processed by selective laser melting (SLM) and to reveal the differences to the conventional cast alloy. Thorough examinations were conducted using electron backscatter diffraction, transmission electron microscopy, optical microscopy and mechanical testing. It is demonstrated that the microstructure of the SLM-material is highly influenced by the heat flux during layer-wise manufacturing and consequently anisotropic microstructural features prevail. An epitaxial grain growth accounts for strong bonding between the single layers resulting in good mechanical properties already in the as-built condition. A heat treatment following SLM leads to microstructural features different to those obtained after the same heat treatment of the cast alloy. Still, the mechanical performance of the latter is met underlining the potential of this technique for producing complex parts for high temperature applications.

  1. THERMAL FATIGUE OF INCONEL ALLOY DA718

    Science.gov (United States)

    2016-10-27

    this material meets the required improvement and offers a low cost alternative to powder metallurgy Rene’95. However, its thermal fatigue resistance...chromel-alumel thermocouple, spot- welded to the mid-length of the specimen. The thermal strain, induced by the expansion and contraction of the...12 FOR OFFICIAL USE ONLY 13. J. F. Radavich, “The Physical Metallurgy of Cast and Wrought Alloy 718,” in Superalloy 718 – Metallurgy and

  2. Production and fabrication of vanadium alloys for the radiative divertor program of DIII-D

    International Nuclear Information System (INIS)

    Johnson, W.R.; Smith, J.P.; Trester, P.W.

    1997-01-01

    V-4Cr-4Ti alloy has been selected for use in the manufacture of a portion of the DIII-D Radiative Divertor upgrade. The production of a 1200-kg ingot of V-4Cr-4Ti alloy, and processing into final sheet and rod product forms suitable for components of the DIII-D Radiative Divertor structure, has been completed at Wah Chang (formerly Teledyne Wah Chang) of Albany, Oregon (WCA). Joining of V-4Cr-4Ti alloy has been identified as the most critical fabrication issue for its use in the RD Program, and research into several joining methods for fabrication of the RD components, including resistance seam, friction, and electron beam welding, is continuing. Preliminary trials have been successful in the joining of V-alloy to itself by electron beam, resistance, and friction welding processes, and to Inconel 625 by friction welding. An effort to investigate the explosive bonding of V-4Cr-4Ti alloy to Inconel 625 has also been initiated, and results have been encouraging. In addition, preliminary tests have been completed to evaluate the susceptibility of V-4Cr-4Ti alloy to stress corrosion cracking in DIII-D cooling water, and the effects of exposure to DIII-D bakeout conditions on the tensile and fracture behavior of V-4Cr-4Ti alloy

  3. Production and fabrication of vanadium alloys for the radiative divertor program of DIII-D

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, W.R.; Smith, J.P.; Trester, P.W.

    1997-04-01

    V-4Cr-4Ti alloy has been selected for use in the manufacture of a portion of the DIII-D Radiative Divertor upgrade. The production of a 1200-kg ingot of V-4Cr-4Ti alloy, and processing into final sheet and rod product forms suitable for components of the DIII-D Radiative Divertor structure, has been completed at Wah Chang (formerly Teledyne Wah Chang) of Albany, Oregon (WCA). Joining of V-4Cr-4Ti alloy has been identified as the most critical fabrication issue for its use in the RD Program, and research into several joining methods for fabrication of the RD components, including resistance seam, friction, and electron beam welding, is continuing. Preliminary trials have been successful in the joining of V-alloy to itself by electron beam, resistance, and friction welding processes, and to Inconel 625 by friction welding. An effort to investigate the explosive bonding of V-4Cr-4Ti alloy to Inconel 625 has also been initiated, and results have been encouraging. In addition, preliminary tests have been completed to evaluate the susceptibility of V-4Cr-4Ti alloy to stress corrosion cracking in DIII-D cooling water, and the effects of exposure to DIII-D bakeout conditions on the tensile and fracture behavior of V-4Cr-4Ti alloy.

  4. 7 CFR 1430.601 - Administration.

    Science.gov (United States)

    2010-01-01

    ... 7 Agriculture 10 2010-01-01 2010-01-01 false Administration. 1430.601 Section 1430.601 Agriculture Regulations of the Department of Agriculture (Continued) COMMODITY CREDIT CORPORATION, DEPARTMENT OF... Program II (DDAP-II) § 1430.601 Administration. (a) DDAP-II shall be administered under the general...

  5. Microstructural evolutions and mechanical behaviour of the nickel based alloys 617 and 230 at high temperature

    International Nuclear Information System (INIS)

    Chomette, S.

    2009-11-01

    High Temperature Reactors (HTR), is one of the innovative nuclear reactor designed to be inherently safer than previous generation and to produce minimal waste. The most critical metallic component in that type of reactor is the Intermediate Heat exchanger (IHX). The constraints imposed by the conception and the severe operational conditions (high temperature of 850 C to 950 C, lifetime of 20,000 h) have guided the IHX material selection toward two solid solution nickel base alloys, the Inconel 617 and the Haynes 230. Inconel 617 is the primary candidate alloy thanks to its good high temperature mechanical and corrosion properties and the large data base developed in previous programs. However, its high cobalt content has to be considered as an issue (nuclear activation). The more recent alloy Haynes 230, in which most of the cobalt has been replaced by tungsten, present characteristics similar to the 617 alloy. The objective of this thesis is to study the high temperature mechanical behaviour of both alloys in relation with their microstructural evolutions. The as received microstructural observations have revealed primary carbides (M 6 C). Most of this precipitates are evenly distributed in the materials. Few M 23 C 6 secondary carbides are observed in both alloys in the as received state. Thermal ageing treatments at 850 C lead to an important M 23 C 6 precipitation on slip lines and at grain boundaries. The size of this carbides increases and their number decreases with increasing ageing duration. The intragranular precipitation of secondary carbides at 950 C is more limited and the intergranular evolution more important than at 850 C. The microstructural observations and the hardness evolution of both alloys show that the main microstructural evolutions occur before 1,000 h at both studied temperatures. The mechanical properties of the Inconel 617 and the Haynes 230 have been studied using tensile, creep, fatigue and relaxation-fatigue tests. Particularly, the

  6. Inconel alloys development -Development of the advanced nuclear materials-

    International Nuclear Information System (INIS)

    Kuk, Il Hiun; Jang, Jin Sung; Rhee, Chang Kyu; Chung, Man Kyo; Woo, Yun Myeoung; Han, Chang Hee

    1994-07-01

    We surveyed the current status and problems in S/G U-tubes in Korea and worldwide. Also we gathered manufacturing specifications of S/G U-tubes and compared/analyzed the differences in them company by company. We produced alloy 600 tubes (in cooperation with Sammi Special Steels) through V.I.M. (Vacuum Induction Melting; 2 ton capacity), 4 steps of hot press forging, hot extrusion (10:1 of reduction ratio), 3 steps of cold pilgerings and so on. We will continue to characterize the tubes and 2nd time preproduce the tubes using the feed-back data. With regard to alloy 690, which is getting popular for S/G U-tubes worldwide, we cast four 60 Kg ingots and two 6 Kg ingots by V.I.M.. We analyzed the chemical composition, macrostructures, hot workability, and so on ; all ingots were good except on 60 Kg ingot. Finally we produced high quality alloy 690 ingot (about 1 Kg) by E.S.R. (Electroslag Remelting) method (in cooperation with Yeoungnam University). We used CaF/CaO/Al2O3/MgO quartenary slag system. We have made directionally grown good ingots by E.S.R. and especially the hot workability at 1100 deg C - the temperature at which V.I.M. ingots showed very poor hot workability - was very much improved (from 30 to 90 % of reduction of area). We continue to analyze the effects of E.S.R. to the structure and properties of alloy 690 (grain size, morphology, and directionality; any changes of inclusions and so on). (Author)

  7. The effect of environment on the creep crack growth behavior of several structural alloys

    International Nuclear Information System (INIS)

    Sadananda, K.; Shahinian, P.

    1980-01-01

    The creep crack growth behaviors of alloy 718, Inconel X-750, Udimet 700 and cold-worked type 304 and annealed and cold-worked type 316 austenitic stainless steels were determined in vacuum at elevated temperatures and the results were compared with those previously obtained in air. Alloy 718 and Inconel X-750 were found to be significantly sensitive to air with crack growth rates one to two orders of magnitude greater than those in vacuum. Udimet 700 is less sensitive to the environment and it is more sensitive to small changes in microstructure than to the environment per se. The austenitic stainless steels are least sensitive of all. Since the environmental sensitivity varies significantly for different materials, the service environment should be considered in the selection of materials for high temperature components. (Auth.)

  8. 14 CFR 27.601 - Design.

    Science.gov (United States)

    2010-01-01

    ... 14 Aeronautics and Space 1 2010-01-01 2010-01-01 false Design. 27.601 Section 27.601 Aeronautics... STANDARDS: NORMAL CATEGORY ROTORCRAFT Design and Construction General § 27.601 Design. (a) The rotorcraft may have no design features or details that experience has shown to be hazardous or unreliable. (b...

  9. 14 CFR 29.601 - Design.

    Science.gov (United States)

    2010-01-01

    ... 14 Aeronautics and Space 1 2010-01-01 2010-01-01 false Design. 29.601 Section 29.601 Aeronautics... STANDARDS: TRANSPORT CATEGORY ROTORCRAFT Design and Construction General § 29.601 Design. (a) The rotorcraft may have no design features or details that experience has shown to be hazardous or unreliable. (b...

  10. FTIR study of the influence of minor alloying elements on the high temperature oxidation of nickel alloys

    International Nuclear Information System (INIS)

    Lenglet, M.; Delaunay, F.; Lefez, B.

    1997-01-01

    The purpose of this paper is to study the reflectance spectra of the different single oxide layer systems : Cr 2 O 3 /Fe, MnCr 2 O 4 /Fe, TiO 2 /Fe, NiCr 2 O 4 /Fe and NiFe 2 O 4 /Fe and to extend the theoretical calculations to multilayer oxide systems on metallic substrates. The interpretation of the resulting reflectance spectra for these systems is used to explain the initial stages of oxide formation and the influence of minor alloying elements on the high temperature oxidation of three commercial nickel alloys : Incoloy 800, Inconel 600 and X. (orig.)

  11. Radiation damage simulation studies of selected austenitic and ferritic/martensitic alloys for fusion reactor structural applications

    International Nuclear Information System (INIS)

    Mazey, D.J.; Walters, G.P.; Buckley, S.N.; Bullough, R.; Hanks, W.; Bolster, D.E.J.; Sowden, B.C.; Lurcook, D.; Murphy, S.M.

    1985-03-01

    Results are given of an investigation of the radiation damage stability of selected austenitic and ferritic alloys following ion bombardment in the Harwell VEC to simulate fusion-reactor exposures up to 110 dpa at temperatures from 425 deg to 625 deg C. Gas production rates appropriate to CTR conditions were simulated using a mixed beam of (4 MeV He + 2 MeV H 2 ) in the ratio 1:4 He:H. A beam of 46 MeV Ni or 20 MeV Cr ions was used in sequence with the mixed gas beam to provide a gas/damage ratio of 13 appm He/dpa at a damage rate of approx. 1 dpa/hr. The materials were investigated using TEM and comprised three austenitic alloys: European reference 316L, 316-Ti, 316-Nb; four high-nickel alloys: Fe/25 Ni/8Cr, Inconel 625, Inconel 706 and Nimonic PE16, and four ferritic/martensitic alloys: FV 448, FV 607, CRM 12 and FI. Some data were obtained for a non-magnetic structural alloy Nonmagne-30. The swelling behaviour is reported. The overall results of the study indicate that on a comparative basis the ferritic alloys are the most swelling-resistant, whilst the high-nickel alloys have an acceptable low swelling response up to 110 dpa. The 316 alloys tested have shown an unfavourable swelling response. (author)

  12. 7 CFR 1230.601 - Act.

    Science.gov (United States)

    2010-01-01

    ... 7 Agriculture 10 2010-01-01 2010-01-01 false Act. 1230.601 Section 1230.601 Agriculture... CONSUMER INFORMATION Procedures for the Conduct of Referendum Definitions § 1230.601 Act. The term Act means the Pork Promotion, Research, and Consumer Information Act of 1985 (7 U.S.C. 4801-4819) and any...

  13. 21 CFR 601.31 - Definition.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 7 2010-04-01 2010-04-01 false Definition. 601.31 Section 601.31 Food and Drugs... Diagnostic Radiopharmaceuticals § 601.31 Definition. For purposes of this part,diagnostic radiopharmaceutical means: (a) An article that is intended for use in the diagnosis or monitoring of a disease or a...

  14. Hardness and electrochemical behavior of ceramic coatings on Inconel

    Directory of Open Access Journals (Sweden)

    C. SUJAYA

    2012-03-01

    Full Text Available Thin films of ceramic materials like alumina and silicon carbide are deposited on Inconel substrate by pulsed laser deposition technique using Q-switched Nd: YAG laser. Deposited films are characterized using UV-visible spectrophotometry and X-ray diffraction. Composite microhardness of ceramic coated Inconel system is measured using Knoop indenter and its film hardness is separated using a mathematical model based on area-law of mixture. It is then compared with values obtained using nanoindentation method. Film hardness of the ceramic coating is found to be high compared to the substrates. Corrosion behavior of substrates after ceramic coating is studied in 3.5% NaCl solution by potentiodynamic polarization and electrochemical impedance spectroscopy measurements. The Nyquist and the Bode plots obtained from the EIS data are fitted by appropriate equivalent circuits. The pore resistance, the charge transfer resistance, the coating capacitance and the double layer capacitance of the coatings are obtained from the equivalent circuit. Experimental results show an increase in corrosion resistance of Inconel after ceramic coating. Alumina coated Inconel showed higher corrosion resistance than silicon carbide coated Inconel. After the corrosion testing, the surface topography of the uncoated and the coated systems are examined by scanning electron microscopy.

  15. Characterization of plasma coated tungsten heavy alloy

    International Nuclear Information System (INIS)

    Bose, A.; Kapoor, D.; Lankford, J. Jr.; Nicholls, A.E.

    1996-01-01

    The detrimental environmental impact of Depleted Uranium-based penetrators have led to tremendous development efforts in the area of tungsten heavy alloy based penetrators. One line of investigation involves the coating of tungsten heavy alloys with materials that are prone to shear localization. Plasma spraying of Inconel 718 and 4340 steel have been used to deposit dense coatings on tungsten heavy alloy substrates. The aim of the investigation was to characterize the coating primarily in terms of its microstructure and a special push-out test. The paper describes the results of the push-out tests and analyzes some of the possible failure mechanisms by carrying out microstructural characterization of the failed rings obtained from the push out tests

  16. Precipitation and clustering in the early stages of ageing in Inconel 718

    International Nuclear Information System (INIS)

    Alam, Talukder; Chaturvedi, Mahesh; Ringer, Simon P.; Cairney, Julie M.

    2010-01-01

    Research highlights: → IN718 could be age hardened rapidly by secondary phase formation. → Co-located phases were observed in the earliest stage of detection. → Clustering of Ti/Al and Nb atoms was observed prior to precipitation. - Abstract: In this report we investigate the onset and evolution of precipitation in the early stages of ageing in the alloy WE 91, a variant of the Ni-Fe-Cr superalloy Inconel 718 (IN718). Transmission electron microscopy and atom probe tomography were used to study the size and volume fraction of γ' and γ'' precipitates and the extent of pre-precipitate clustering of Al/Ti and Nb. Co-located γ' and γ'' precipitates were observed from the shortest ageing times that precipitates could be visualised using atom probe. At shorter times, prior to the observation of precipitates, clustering of Al/Ti and Nb was shown to occur. The respective volume fraction of the γ' and γ'' precipitates and the clustering of Al/Ti and Nb suggest that γ'' nucleates prior to γ' during ageing at 706 deg. C for this alloy.

  17. Influence of temperature, environment, and thermal aging on the continuous cycle fatigue behavior of Hastelloy X and Inconel 617

    International Nuclear Information System (INIS)

    Strizak, J.P.; Brinkman, C.R.; Booker, M.K.; Rittenhouse, P.L.

    1982-04-01

    Results are presented for strain-controlled fatigue and tensile tests for two nickel-base, solution-hardened reference structural alloys for use in several High-Temperature Gas-Cooled Reactor (HTGR) concepts. These alloys, Hastelloy X and Inconel 617, were tested from room temperature to 871 0 C in air and impure helium. Materials were tested in both the solution-annealed and the preaged conditios, in which aging consisted of isothermal exposure at one of several temperatures for periods of up to 20,000 h. Comparisons are given between the strain-controlled fatigue lives of these and several other commonly used alloys, all tested at 538 0 C. An analysis is also presented of the continuous cycle fatigue data obtained from room temperature to 427 0 C for Hastelloy G, Hastelloy X, Hastelloy C-276, and Hastelloy C-4, an effort undertaken in support of ASME code development

  18. A bidirectional shape memory alloy folding actuator

    International Nuclear Information System (INIS)

    Paik, Jamie K; Wood, Robert J

    2012-01-01

    This paper presents a low-profile bidirectional folding actuator based on annealed shape memory alloy sheets applicable for meso- and microscale systems. Despite the advantages of shape memory alloys—high strain, silent operation, and mechanical simplicity—their application is often limited to unidirectional operation. We present a bidirectional folding actuator that produces two opposing 180° motions. A laser-patterned nickel alloy (Inconel 600) heater localizes actuation to the folding sections. The actuator has a thin ( < 1 mm) profile, making it appropriate for use in robotic origami. Various design parameters and fabrication variants are described and experimentally explored in the actuator prototype. (paper)

  19. Development and use of a predictive model of crack propagation in 304/316L, A533B/A508 and Inconel 600/182 alloys in 2880C water

    International Nuclear Information System (INIS)

    Ford, F.P.; Andresen, P.L.

    1988-01-01

    Environmentally assisted cracking (i.e., stress corrosion cracking and corrosion fatigue) continues to present a potential safety and economic problem to both the nuclear and non-nuclear power generation industries. Efforts to develop adequate mitigation actions have been vigorous in the former industry but, of necessity, these have been based primarily on accelerated tests covering a limited fraction of the wide combination of material, environment and stressing conditions that are pertinent to the operation of light water reactors. Previous articles have stressed the potential value of combining these phenomenologically oriented studies of stress corrosion and corrosion fatigue with a mechanistically based model of environmentally assisted cracking. Quite apart from conferring some scientific assurance of the validity of the empirically derived data vis a vis plant performance, the mechanistic knowledge offers the potential of interpreting the isolated experimental data and forming a methodology for making decisions regarding life prediction and life extension. This article briefly reviews the mechanistic basis for predicting the cracking behavior of 304/316 stainless steel, A508/A533B low alloy steels and Inconel 600/182 nickel-base alloys in high temperature water, and then develops the argument for the practical use of this mechanistic knowledge in conjunction with crack monitoring and environmental sensing capabilities

  20. 48 CFR 601.403 - Individual deviations.

    Science.gov (United States)

    2010-10-01

    ... 48 Federal Acquisition Regulations System 4 2010-10-01 2010-10-01 false Individual deviations. 601.403 Section 601.403 Federal Acquisition Regulations System DEPARTMENT OF STATE GENERAL DEPARTMENT OF STATE ACQUISITION REGULATIONS SYSTEM Deviations from the FAR 601.403 Individual deviations. The...

  1. Compatibility of aluminide-coated Hastelloy x and Inconel 617 in a simulated gas-cooled reactor environment

    International Nuclear Information System (INIS)

    Chin, J.; Johnson, W.R.; Chen, K.

    1982-03-01

    Commercially prepared aluminide coatings on Hastelloy X and Inconel 617 substrates were exposed to controlled-impurity helium at 850 0 and 950 0 C for 3000 h. Optical and scanning electron (SEM) microscopy, electron microprobe profiles, and SEM X-ray mapping were used to evaluate and compare exposed and unexposed control samples. Four coatings were evaluated: aluminide, aluminide with platinum, aluminide with chromium, and aluminide with rhodium. With extended time at elevated temperature, nickel diffused into the aluminide coatings to form epsilon-phase (Ni 3 Al). This diffusion was the primary cause of porosity formation at the aluminide/alloy interface

  2. Laser post-processing of Inconel 625 made by selective laser melting

    Science.gov (United States)

    Witkin, David; Helvajian, Henry; Steffeney, Lee; Hansen, William

    2016-04-01

    The effect of laser remelting of surfaces of as-built Selective Laser Melted (SLM) Inconel 625 was evaluated for its potential to improve the surface roughness of SLM parts. Many alloys made by SLM have properties similar to their wrought counterparts, but surface roughness of SLM-made parts is much higher than found in standard machine shop operations. This has implications for mechanical properties of SLM materials, such as a large debit in fatigue properties, and in applications of SLM, where surface roughness can alter fluid flow characteristics. Because complexity and netshape fabrication are fundamental advantages of Additive Manufacturing (AM), post-processing by mechanical means to reduce surface roughness detracts from the potential utility of AM. Use of a laser to improve surface roughness by targeted remelting or annealing offers the possibility of in-situ surface polishing of AM surfaces- the same laser used to melt the powder could be amplitude modulated to smooth the part during the build. The effects of remelting the surfaces of SLM Inconel 625 were demonstrated using a CW fiber laser (IPG: 1064 nm, 2-50 W) that is amplitude modulated with a pulse profile to induce remelting without spallation or ablation. The process achieved uniform depth of melting and improved surface roughness. The results show that with an appropriate pulse profile that meters the heat-load, surface features such as partially sintered powder particles and surface connected porosity can be mitigated via a secondary remelting/annealing event.

  3. 49 CFR 601.45 - Required information.

    Science.gov (United States)

    2010-10-01

    ... 49 Transportation 7 2010-10-01 2010-10-01 false Required information. 601.45 Section 601.45 Transportation Other Regulations Relating to Transportation (Continued) FEDERAL TRANSIT ADMINISTRATION, DEPARTMENT OF TRANSPORTATION ORGANIZATION, FUNCTIONS, AND PROCEDURES Emergency Procedures for Public Transportation Systems § 601.45 Required...

  4. Ultrasonic Sensor Signals and Optimum Path Forest Classifier for the Microstructural Characterization of Thermally-Aged Inconel 625 Alloy

    Directory of Open Access Journals (Sweden)

    Victor Hugo C. de Albuquerque

    2015-05-01

    Full Text Available Secondary phases, such as laves and carbides, are formed during the final solidification stages of nickel-based superalloy coatings deposited during the gas tungsten arc welding cold wire process. However, when aged at high temperatures, other phases can precipitate in the microstructure, like the γ'' and δ phases. This work presents an evaluation of the powerful optimum path forest (OPF classifier configured with six distance functions to classify background echo and backscattered ultrasonic signals from samples of the inconel 625 superalloy thermally aged at 650 and 950 \\(^\\circ\\C for 10, 100 and 200 h. The background echo and backscattered ultrasonic signals were acquired using transducers with frequencies of 4 and 5 MHz. The potentiality of ultrasonic sensor signals combined with the OPF to characterize the microstructures of an inconel 625 thermally aged and in the as-welded condition were confirmed by the results. The experimental results revealed that the OPF classifier is sufficiently fast (classification total time of 0.316 ms and accurate (accuracy of 88.75% and harmonic mean of 89.52 for the application proposed.

  5. Ultrasonic sensor signals and optimum path forest classifier for the microstructural characterization of thermally-aged inconel 625 alloy.

    Science.gov (United States)

    de Albuquerque, Victor Hugo C; Barbosa, Cleisson V; Silva, Cleiton C; Moura, Elineudo P; Filho, Pedro P Rebouças; Papa, João P; Tavares, João Manuel R S

    2015-05-27

    Secondary phases, such as laves and carbides, are formed during the final solidification stages of nickel-based superalloy coatings deposited during the gas tungsten arc welding cold wire process. However, when aged at high temperatures, other phases can precipitate in the microstructure, like the γ'' and δ phases. This work presents an evaluation of the powerful optimum path forest (OPF) classifier configured with six distance functions to classify background echo and backscattered ultrasonic signals from samples of the inconel 625 superalloy thermally aged at 650 and 950 °C for 10, 100 and 200 h. The background echo and backscattered ultrasonic signals were acquired using transducers with frequencies of 4 and 5 MHz. The potentiality of ultrasonic sensor signals combined with the OPF to characterize the microstructures of an inconel 625 thermally aged and in the as-welded condition were confirmed by the results. The experimental results revealed that the OPF classifier is sufficiently fast (classification total time of 0.316 ms) and accurate (accuracy of 88.75%" and harmonic mean of 89.52) for the application proposed.

  6. The effect of vacuum environment on creep rupture properties of Inconel 617 at 1000 deg C

    International Nuclear Information System (INIS)

    Ohnami, Masateru; Imamura, Riuzo

    1981-01-01

    The creep rupture strength of nickel-base superalloy in weakly acidic gas at high temperature above 1000 deg C lowers remarkably as compared with that in the atmosphere, and this problem is one of the important subjects in connection with the research and development of high temperature heat exchangers for multi-purpose high temperature gas-cooled reactor system being developed in Japan. In the case of Inconel 617, abnormal decarbonization phenomenon occurs in weakly acidic gas, and this is regarded as the cause of lowering the creep strength. In this study, the effects of the decarbonization in weak vacuum at 1000 deg C and the oxidation of Inconel 617 on its crack occurrence and propagation were clarified experimentally with notched plate test pieces. The material used was Inconel 617 nickel-base superalloy made by Huntington Alloys Inc. in the U.S. The creep rupture experiment was carried out with a simple tension creep tester. At the nominal stress of 3.5 kg/mm 2 , the creep rupture time in 0.3 Torr was the shortest when the grain size was 78 μm, and the creep rupture time increased as the grain size became larger. The creep rupture time in 0.3 Torr decreased to a half of that in the atmosphere. In 0.3 Torr, cracks occurred early, and propagated fast as compared with in the atmosphere. This is because the local creep velocity at the bottom of notches and in front of creep cracks is fast owing to the lack of protective oxide film. (Kako, I.)

  7. Oxidation of Inconel 625 superalloy upon treatment with oxygen or hydrogen plasma at high temperature

    Science.gov (United States)

    Vesel, Alenka; Drenik, Aleksander; Elersic, Kristina; Mozetic, Miran; Kovac, Janez; Gyergyek, Tomaz; Stockel, Jan; Varju, Jozef; Panek, Radomir; Balat-Pichelin, Marianne

    2014-06-01

    Initial stages of Inconel 625 superalloy (Ni60Cr30Mo10Ni4Nb1) oxidation upon short treatment with gaseous plasma at different temperatures up to about 1600 K were studied. Samples were treated for different periods up to a minute by oxygen or hydrogen plasma created with a microwave discharge in the standing-wave mode at a pressure of 40 Pa and a power 500 W. Simultaneous heating of the samples was realized by focusing concentrated solar radiation from a 5 kW solar furnace directly onto the samples. The morphological changes upon treatment were monitored using scanning electron microscopy, compositional depth profiling was performed using Auger electron spectroscopy, while structural changes were determined by X-ray diffraction. The treatment in oxygen plasma caused formation of metal oxide clusters of three dimensional crystallites initially rich in nickel oxide with the increasing chromium oxide content as the temperature was increasing. At about 1100 K iron and niobium oxides prevailed on the surface causing a drop of the material emissivity at 5 μm. Simultaneously the NiCr2O4 compound started growing at the interface between the oxide film and bulk alloy and the compound persisted up to temperatures close to the Inconel melting point. Intensive migration of minority alloying elements such as Fe and Ti was observed at 1600 K forming mixed surface oxides of sub-micrometer dimensions. The treatment in hydrogen plasma with small admixture of water vapor did not cause much modification unless the temperature was close to the melting point. At such conditions aluminum segregated on the surface and formed well-defined Al2O3 crystals.

  8. Combination of Ultrasonic Vibration and Cryogenic Cooling for Cutting Performance Improvement of Inconel 718 Turning

    Science.gov (United States)

    Lin, S. Y.; Chung, C. T.; Cheng, Y. Y.

    2011-01-01

    The main objective of this study is to develop a thermo-elastic-plastic coupling model, based on a combination skill of ultrasonically assisted cutting and cryogenic cooling, under large deformation for Inconel 718 alloy machining process. The improvement extent on cutting performance and tool life promotion may be examined from this investigation. The critical value of the strain energy density of the workpiece will be utilized as the chip separation and the discontinuous chip segmentation criteria. The forced convection cooling and a hydrodynamic lubrication model will be considered and formulated in the model. Finite element method will be applied to create a complete numerical solution for this ultrasonic vibration cutting model. During the analysis, the cutting tool is incrementally advanced forward with superimposed ultrasonic vibration in a back and forth step-by-step manner, from an incipient stage of tool-workpiece engagement to a steady state of chip formation, a whole simulation of orthogonal cutting process under plane strain deformation is thus undertaken. High shear strength induces a fluctuation phenomenon of shear angle, high shear strain rate, variation of chip types and chip morphology, tool-chip contact length variation, the temperature distributions within the workpiece, chip and tool, periodic fluctuation in cutting forces can be determined from the developed model. A complete comparison of machining characteristics between some different combinations of ultrasonically assisted cutting and cryogenic cooling with conventional cutting operation can be acquired. Finally, the high-speed turning experiment for Inconel 718 alloy will be taken in the laboratory to validate the accuracy of the model, and the progressive flank wear, crater wear, notching and chipping of the tool edge can also be measured in the experiments.

  9. 45 CFR 601.5 - Derivative classification.

    Science.gov (United States)

    2010-10-01

    ... CLASSIFICATION AND DECLASSIFICATION OF NATIONAL SECURITY INFORMATION § 601.5 Derivative classification. Distinct... 45 Public Welfare 3 2010-10-01 2010-10-01 false Derivative classification. 601.5 Section 601.5... classification guide, need not possess original classification authority. (a) If a person who applies derivative...

  10. 45 CFR 1703.601 - Judicial review.

    Science.gov (United States)

    2010-10-01

    ... 45 Public Welfare 4 2010-10-01 2010-10-01 false Judicial review. 1703.601 Section 1703.601 Public Welfare Regulations Relating to Public Welfare (Continued) NATIONAL COMMISSION ON LIBRARIES AND INFORMATION SCIENCE GOVERNMENT IN THE SUNSHINE ACT Judicial Review § 1703.601 Judicial review. Any person may...

  11. Interfacial microstructure of partial transient liquid phase bonded Si3N4-to-Inconel 718 joints

    International Nuclear Information System (INIS)

    Kim, Jae Joong; Park, Jin-Woo; Eagar, Thomas W.

    2003-01-01

    This work presents transmission electron microscopy (TEM) analysis of the interfacial microstructure in Si 3 N 4 -to-Inconel 718 joints with Ni interlayers produced by partial transient liquid phase bonding (PTLPB). Ti and Cu microfoils have been inserted between Si 3 N 4 and the Ni interlayer and joining has been performed at lower temperatures than previous PTLPBs of Si 3 N 4 with the same insert metals. The TEM work is focused on phase identification of the reaction layers between the Si 3 N 4 and the Ni interlayer. According to the TEM analysis, most of the Cu precipitates without reacting with Ti and Ni. Si diffused in the filler metal and thin reaction layer formed at the interface between Si 3 N 4 and the filler metal producing good bond-formation and hence, high interfacial strength. No interfacial fractures occurred after cooling from the bonding temperature of 900 deg. C, which supports the results observed in the TEM analysis. This work confirms that this joining process can produce a more heat resistant Si 3 N 4 -to-Inconel 718 joint than active brazing using Ag-Cu-Ti alloys

  12. 39 CFR 601.100 - Purchasing policy.

    Science.gov (United States)

    2010-07-01

    ... 39 Postal Service 1 2010-07-01 2010-07-01 false Purchasing policy. 601.100 Section 601.100 Postal Service UNITED STATES POSTAL SERVICE PROCUREMENT SYSTEM FOR THE U.S. POSTAL SERVICE: INTELLECTUAL PROPERTY RIGHTS OTHER THAN PATENTS PURCHASING OF PROPERTY AND SERVICES § 601.100 Purchasing policy. The Postal...

  13. 15 CFR 60.1 - Public information.

    Science.gov (United States)

    2010-01-01

    ... 15 Commerce and Foreign Trade 1 2010-01-01 2010-01-01 false Public information. 60.1 Section 60.1 Commerce and Foreign Trade Regulations Relating to Commerce and Foreign Trade BUREAU OF THE CENSUS, DEPARTMENT OF COMMERCE PUBLIC INFORMATION § 60.1 Public information. The rules and procedures regarding...

  14. Multipass forging of Inconel 718 in the delta-Supersolvus domain: assessing and modeling microstructure evolution

    Directory of Open Access Journals (Sweden)

    Zouari Meriem

    2014-01-01

    Full Text Available This work is focused on the evolution of the microstructure of Inconel 718 during multi-pass forging processes. During the forming process, the material is subjected to several physical phenomena such as work-hardening, recovery, recrystallization and grain growth. In this work, transformation kinetics are modeled in the δ-Supersolvus domain (T>Tsolvus where the alloy is single-phase, all the alloying elements being dissolved into the FCC matrix. Torsion tests were used to simulate the forging process and recrystallization kinetics was modeled using a discontinuous dynamic recrystallization (DDRX two-site mean field model. The microstructure evolution under hot forging conditions is predicted in both dynamic and post-dynamic regimes based on the initial distribution of grain size and the evolution of dislocation density distribution during each step of the process. The model predicts recrystallization kinetics, recrystallized grain size distribution and stress–strain curve for different thermo-mechanical conditions and makes the connection between dynamic and post-dynamic regimes.

  15. Effect of microstructure and environment on the crack growth behaviour on Inconel 718 alloy at 650/sup 0/C under fatigue, creep and combined loading

    Energy Technology Data Exchange (ETDEWEB)

    Pedron, J P; Pineau, A

    1982-11-01

    The crack growth properties of various microstructures developed in one heat of Inconel 718 alloy were investigated at 650/sup 0/C under air and vacuum environments. The microstructures included fine-grained material (ASTM grain sizes 6-8), coarse-grained material (ASTM grain sizes 3-4) and material of a necklace structure (ASTM grain sizes 3-4 and 8-10). The effect of grain boundary ..beta.. (Ni/sub 3/Nb) phase precipitation was also studied. Continuous fatigue, creep and creep-fatigue conditions were examined. For continuous fatigue the influence of frequency was investigated over the range between 5x10/sup -2/ and 20 Hz. For creep-fatigue conditions, hold times of 10 and 300 s were superimposed on a 5x10/sup -2/ Hz triangular wave shape signal. It was shown that the grain boundary microstructure had a very strong effect when the fatigue crack propagation behaviour was essentially time dependent. This effect is associated with the occurrence of brittle intergranular fracture and dramatic increases in crack growth rate. The microstructure had no effect under vacuum testing.

  16. Microstructural features of dissimilar welds between 316LN austenitic stainless steel and alloy 800

    International Nuclear Information System (INIS)

    Sireesha, M.; Sundaresan, S.

    2000-01-01

    For joining type 316LN austenitic stainless steel to modified 9Cr-1Mo steel for power plant application, a trimetallic configuration using an insert piece (such as alloy 800) of intermediate thermal coefficient of expansion (CTE) has been sometimes suggested for bridging the wide gap in CTE between the two steels. Two joints are thus involved and this paper is concerned with the weld between 316LN and alloy 800. These welds were produced using three types of filler materials: austenitic stainless steels corresponding to 316,16Cr-8Ni-2Mo, and the nickel-base Inconel 182 1 . The weld fusion zones and the interfaces with the base materials were characterised in detail using light and transmission electron microscopy. The 316 and Inconel 182 weld metals solidified dendritically, while the 16-8-2(16%Cr-8%Ni-2%Mo) weld metal showed a predominantly cellular substructure. The Inconel weld metal contained a large number of inclusions when deposited from flux-coated electrodes, but was relatively inclusion-free under inert gas-shielded welding. Long-term elevated-temperature aging of the weld metals resulted in embrittling sigma phase precipitation in the austenitic stainless steel weld metals, but the nickel-base welds showed no visible precipitation, demonstrating their superior metallurgical stability for high-temperature service. (orig.)

  17. 46 CFR 108.601 - Crane design.

    Science.gov (United States)

    2010-10-01

    ... 46 Shipping 4 2010-10-01 2010-10-01 false Crane design. 108.601 Section 108.601 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) A-MOBILE OFFSHORE DRILLING UNITS DESIGN AND EQUIPMENT Cranes Cranes § 108.601 Crane design. (a) Each crane and crane foundation on a unit must be designed in...

  18. Alloy SCR-3 resistant to stress corrosion cracking

    International Nuclear Information System (INIS)

    Kowaka, Masamichi; Fujikawa, Hisao; Kobayashi, Taiki

    1977-01-01

    Austenitic stainless steel is used widely because the corrosion resistance, workability and weldability are excellent, but the main fault is the occurrence of stress corrosion cracking in the environment containing chlorides. Inconel 600, most resistant to stress corrosion cracking, is not necessarily safe under some severe condition. In the heat-affected zone of SUS 304 tubes for BWRs, the cases of stress corrosion cracking have occurred. The conventional testing method of stress corrosion cracking using boiling magnesium chloride solution has been problematical because it is widely different from actual environment. The effects of alloying elements on stress corrosion cracking are remarkably different according to the environment. These effects were investigated systematically in high temperature, high pressure water, and as the result, Alloy SCR-3 with excellent stress corrosion cracking resistance was found. The physical constants and the mechanical properties of the SCR-3 are shown. The states of stress corrosion cracking in high temperature, high pressure water containing chlorides and pure water, polythionic acid, sodium phosphate solution and caustic soda of the SCR-3, SUS 304, Inconel 600 and Incoloy 800 are compared and reported. (Kako, I.)

  19. 25 CFR 11.601 - Marriage licenses.

    Science.gov (United States)

    2010-04-01

    ... 25 Indians 1 2010-04-01 2010-04-01 false Marriage licenses. 11.601 Section 11.601 Indians BUREAU... ORDER CODE Domestic Relations § 11.601 Marriage licenses. A marriage license shall be issued by the clerk of the court in the absence of any showing that the proposed marriage would be invalid under any...

  20. Pitting resistance and mechanism of TiN-coated Inconel 600 in 100 C NaCl solution

    International Nuclear Information System (INIS)

    In, C.B.; Kim, J.S.; Chun, S.S.; Lee, W.J.

    1995-01-01

    TiN films were deposited on Inconel 600 by PACVD method using a gaseous mixture of TiCl 4 , N 2 , H 2 and Ar, and their pitting resistance and mechanism in 100 C NaCl solution were investigated. Anodic polarization measurement of TiN-coated Inconel 600 was compared with that of bare Inconel 600. TiN-coated Inconel 600 has a higher E np and a lower pit depth than bare Inconel 600. It also shows a smaller pit aspect ratio due to the concentration of the corrosion in the Inconel 600 contacted with the TiN film. When the Inconel 600 has a rough surface, E np decreases and the pit density increases to a great extent. However, E corr , pit depth and pit aspect ratio are not affected. ((orig.))

  1. Bending of pipes with inconel cladding

    Energy Technology Data Exchange (ETDEWEB)

    Nachpitz, Leonardo; Menezes, Carlos Eduardo B; Vieira, Carlos R. Tavares [Primus Processamento de Tubos S.A. (PROTUBO), Macae, RJ (Brazil)

    2009-07-01

    The high-frequency induction bending process, using API pipes coated with Inconel 625 reconciled to a mechanical transformation for a higher degree of resistance, was developed through a careful specification and control of the manufacturing parameters and inherent heat treatments. The effects of this technology were investigated by a qualification process consisting of a sequence of tests and acceptance criteria typically required by the offshore industry, and through the obtained results was proved the effectiveness of this entire manufacturing process, without causing interference in the properties and the quality of the inconel cladding, adding a gain of resistance to the base material, guaranteed by the requirements of the API 5L Standard. (author)

  2. Thermal cycling influence on microstructural characterization of alloys with high nickel content

    International Nuclear Information System (INIS)

    Abrudeanu, M.; Gradin, O.; Vulpe, S. C.; Ohai, D.

    2013-01-01

    The IV nuclear energy generation systems are aimed at making revolutionary improvements in economics, safety and reliability, and sustainability. To achieve these goals, Generation IV systems will operate at higher temperatures and in higher radiation fields. This paper shows the thermal cycling influences on microstructure and hardness of nickel based alloys: Incoloy 800 HT and Inconel 617. These alloys were meekly at a thermal cycling of 25, 50, 75 and 100 cycles. The temperature range of a cycle was between 400 O C and 700 O C. Nickel base alloys develop their properties by solid solution and/or precipitation strengthening. (authors)

  3. Effect of glass-ceramic-processing cycle on the metallurgical properties of candidate alloys for actuator housings

    Energy Technology Data Exchange (ETDEWEB)

    Weirick, L.J.

    1982-01-01

    This report summarizes the results from an investigation on the effect of a glass ceramic processing cycle on the metallurgical properties of metal candidates for actuator housings. The cycle consists of a 980/sup 0/C sealing step, a 650/sup 0/C crystallization step and a 475/sup 0/C annealing step. These temperatue excursions are within the same temperature regime as annealing and heat treating processes normally employed for metals. Therefore, the effect of the processing cycle on metallurgical properties of microstructure, strength, hardness and ductility were examined. It was found that metal candidates which are single phase or solid solution alloys (such as 21-6-9, Hastelloy C-276 and Inconel 625) were not affected whereas multiphase or precipitation hardened alloys (such as Inconel 718 and Titanium ..beta..-C) were changed by the processing cycle for the glass ceramic.

  4. Microstructural study and wear behavior of ductile iron surface alloyed by Inconel 617

    International Nuclear Information System (INIS)

    Arabi Jeshvaghani, R.; Jaberzadeh, M.; Zohdi, H.; Shamanian, M.

    2014-01-01

    Highlights: • The Ni-base alloy was deposited on the surface of ductile iron by TIG welding process. • Microstructure of alloyed layer consisted of carbides embedded in Ni-rich dendrite. • Hardness and wear resistance of coated sample greatly improved. • The formation of oxide layer and delamination were dominant mechanisms of wear. - Abstract: In this research, microstructure and wear behavior of Ni-based alloy is discussed in detail. Using tungsten inert gas welding process, coating of nearly 1–2 mm thickness was deposited on ductile iron. Optical and scanning electron microscopy, as well as X-ray diffraction analysis and electron probe microanalysis were used to characterize the microstructure of the surface alloyed layer. Micro-hardness and wear resistance of the alloyed layer was also studied. Results showed that the microstructure of the alloyed layer consisted of M 23 C 6 carbides embedded in Ni-rich solid solution dendrites. The partial melted zone (PMZ) had eutectic ledeburit plus martensite microstructure, while the heat affected zone (HAZ) had only a martensite structure. It was also noticed that hardness and wear resistance of the alloyed layer was considerably higher than that of the substrate. Improvement of wear resistance is attributed to the solution strengthening effect of alloying elements and also the presence of hard carbides such as M 23 C 6 . Based on worn surface analysis, the dominant wear mechanisms of alloyed layer were found to be oxidation and delamination

  5. Properties of Inconel 625 mesh structures grown by electron beam additive manufacturing

    Energy Technology Data Exchange (ETDEWEB)

    List, F.A., E-mail: listfaiii@ornl.gov [Oak Ridge National Laboratory, 1 Bethel Valley Rd., Oak Ridge, TN (United States); Dehoff, R.R.; Lowe, L.E. [Oak Ridge National Laboratory, 1 Bethel Valley Rd., Oak Ridge, TN (United States); Sames, W.J. [Texas A and M University, College Station, TX (United States)

    2014-10-06

    Relationships between electron beam parameters (beam current, beam speed, and beam focus) and physical properties (mass, diameter, elastic modulus, and yield strength) have been investigated for Inconel 625 mesh cubes fabricated using an additive manufacturing technology based on electron beam melting. The elastic modulus and yield strength of the mesh cubes have been systematically varied by approximately a factor of ten by changing the electron beam parameters. Simple models have been used to understand these relationships. Structural anisotropies of the mesh associated with the layered build architecture have been observed and may contribute, along with microstructural anisotropies, to the anisotropic mechanical properties of the mesh. Knowledge of this kind is likely applicable to other metal and alloy systems and is essential to rapidly realize the full potential of this burgeoning technology.

  6. Properties of Inconel 625 mesh structures grown by electron beam additive manufacturing

    International Nuclear Information System (INIS)

    List, F.A.; Dehoff, R.R.; Lowe, L.E.; Sames, W.J.

    2014-01-01

    Relationships between electron beam parameters (beam current, beam speed, and beam focus) and physical properties (mass, diameter, elastic modulus, and yield strength) have been investigated for Inconel 625 mesh cubes fabricated using an additive manufacturing technology based on electron beam melting. The elastic modulus and yield strength of the mesh cubes have been systematically varied by approximately a factor of ten by changing the electron beam parameters. Simple models have been used to understand these relationships. Structural anisotropies of the mesh associated with the layered build architecture have been observed and may contribute, along with microstructural anisotropies, to the anisotropic mechanical properties of the mesh. Knowledge of this kind is likely applicable to other metal and alloy systems and is essential to rapidly realize the full potential of this burgeoning technology

  7. 47 CFR 25.601 - Equal employment opportunities.

    Science.gov (United States)

    2010-10-01

    ... 47 Telecommunication 2 2010-10-01 2010-10-01 false Equal employment opportunities. 25.601 Section 25.601 Telecommunication FEDERAL COMMUNICATIONS COMMISSION (CONTINUED) COMMON CARRIER SERVICES SATELLITE COMMUNICATIONS Equal Employment Opportunities § 25.601 Equal employment opportunities...

  8. Precipitation and clustering in the early stages of ageing in Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Alam, Talukder, E-mail: talukder.alam@sydney.edu.au [Australian Centre for Microscopy and Microanalysis, University of Sydney, NSW 2006 (Australia); Chaturvedi, Mahesh [Department of Mechanical and Industrial Engineering, University of Manitoba, Winnipeg, MB R3T 5V6 (Canada); Ringer, Simon P.; Cairney, Julie M. [Australian Centre for Microscopy and Microanalysis, University of Sydney, NSW 2006 (Australia)

    2010-11-15

    Research highlights: {yields} IN718 could be age hardened rapidly by secondary phase formation. {yields} Co-located phases were observed in the earliest stage of detection. {yields} Clustering of Ti/Al and Nb atoms was observed prior to precipitation. - Abstract: In this report we investigate the onset and evolution of precipitation in the early stages of ageing in the alloy WE 91, a variant of the Ni-Fe-Cr superalloy Inconel 718 (IN718). Transmission electron microscopy and atom probe tomography were used to study the size and volume fraction of {gamma}' and {gamma}'' precipitates and the extent of pre-precipitate clustering of Al/Ti and Nb. Co-located {gamma}' and {gamma}'' precipitates were observed from the shortest ageing times that precipitates could be visualised using atom probe. At shorter times, prior to the observation of precipitates, clustering of Al/Ti and Nb was shown to occur. The respective volume fraction of the {gamma}' and {gamma}'' precipitates and the clustering of Al/Ti and Nb suggest that {gamma}'' nucleates prior to {gamma}' during ageing at 706 deg. C for this alloy.

  9. Segregation in welded nickel-base alloys

    International Nuclear Information System (INIS)

    Akhtar, J.I.; Shoaib, K.A.; Ahmad, M.; Shaikh, M.A.

    1990-05-01

    Segregation effects have been investigated in nickel-base alloys monel 400, inconel 625, hastelloy C-276 and incoloy 825, test welded under controlled conditions. Deviations from the normal composition have been observed to varying extents in the welded zone of these alloys. Least effect of this type occurred in Monel 400 where the content of Cu increased in some of the areas. Enhancement of Al and Ti has been found over large areas in the other alloys which has been attributed to the formation of low melting slag. Another common feature is the segregation of Cr, Fe or Ti, most likely in the form of carbides. Enrichment of Al, Ti, Nb, Mb, Mo, etc., to different amounts in some of the areas of these materials is in- terpretted in terms of the formation of gamma prime precipitates or of Laves phases. (author)

  10. Study on surface defects in milling Inconel 718 super alloy

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Liu; Chengzu, Ren; Guofeng, Wang; Yinwei, Yang; Lu, Zhang [Tianjin University, Tianjin (China)

    2015-04-15

    Nickel-based alloys have been extensively used as critical components in aerospace industry, especially in the key section of aero engine. In general, these sections are manufactured by milling process because most of them have complex forms. However, surface defects appear frequently in milling due to periodic impact force, which leads to the deterioration of the fatigue life. We conducted milling experiments under different cutting conditions and found that four kinds of defects, i.e., tear, cavity, build up edge (BUE) and groove, commonly appear on the machined surface. Based on the observed results, the morphology and generation regime of these defects are analyzed and the carbide particle cracking is discussed to explain the appearance of the nickel alloy defects. To study the effect of the cutting parameters on the severity of these surface defects, two qualitative indicators, which are named as average number of the defects per field and average area ratio of the defects per field, are presented and the influence laws are summarized based on the results correspondingly. This study is helpful for understanding the generation mechanism of the surface defects during milling process of nickel based super alloy.

  11. Oxidation of Inconel 625 superalloy upon treatment with oxygen or hydrogen plasma at high temperature

    Energy Technology Data Exchange (ETDEWEB)

    Vesel, Alenka; Drenik, Aleksander; Elersic, Kristina; Mozetic, Miran; Kovac, Janez [Jozef Stefan Institute, Jamova 39, SI-1000 Ljubljana (Slovenia); Gyergyek, Tomaz [University of Ljubljana, Faculty of Electrical Engineering, Trzaska 25, SI-1000 Ljubljana (Slovenia); Stockel, Jan; Varju, Jozef; Panek, Radomir [Institute of Plasma Physics, Academy of Sciences of the Czech Republic, Ze Slovankou 3, Praha 8 (Czech Republic); Balat-Pichelin, Marianne, E-mail: marianne.balat@promes.cnrs.fr [PROMES-CNRS Laboratory, 7 rue du four solaire, 66120 Font Romeu Odeillo (France)

    2014-06-01

    Initial stages of Inconel 625 superalloy (Ni{sub 60}Cr{sub 30}Mo{sub 10}Ni{sub 4}Nb{sub 1}) oxidation upon short treatment with gaseous plasma at different temperatures up to about 1600 K were studied. Samples were treated for different periods up to a minute by oxygen or hydrogen plasma created with a microwave discharge in the standing-wave mode at a pressure of 40 Pa and a power 500 W. Simultaneous heating of the samples was realized by focusing concentrated solar radiation from a 5 kW solar furnace directly onto the samples. The morphological changes upon treatment were monitored using scanning electron microscopy, compositional depth profiling was performed using Auger electron spectroscopy, while structural changes were determined by X-ray diffraction. The treatment in oxygen plasma caused formation of metal oxide clusters of three dimensional crystallites initially rich in nickel oxide with the increasing chromium oxide content as the temperature was increasing. At about 1100 K iron and niobium oxides prevailed on the surface causing a drop of the material emissivity at 5 μm. Simultaneously the NiCr{sub 2}O{sub 4} compound started growing at the interface between the oxide film and bulk alloy and the compound persisted up to temperatures close to the Inconel melting point. Intensive migration of minority alloying elements such as Fe and Ti was observed at 1600 K forming mixed surface oxides of sub-micrometer dimensions. The treatment in hydrogen plasma with small admixture of water vapor did not cause much modification unless the temperature was close to the melting point. At such conditions aluminum segregated on the surface and formed well-defined Al{sub 2}O{sub 3} crystals.

  12. 48 CFR 32.601 - General.

    Science.gov (United States)

    2010-10-01

    ... costs related to defaults in performance. (10) Breach of contract obligations concerning progress....601 Federal Acquisition Regulations System FEDERAL ACQUISITION REGULATION GENERAL CONTRACTING REQUIREMENTS CONTRACT FINANCING Contract Debts 32.601 General. (a) Contract debts are amounts that— (1) Have...

  13. 48 CFR 601.303 - Publication and codification.

    Science.gov (United States)

    2010-10-01

    ... 48 Federal Acquisition Regulations System 4 2010-10-01 2010-10-01 false Publication and codification. 601.303 Section 601.303 Federal Acquisition Regulations System DEPARTMENT OF STATE GENERAL DEPARTMENT OF STATE ACQUISITION REGULATIONS SYSTEM Agency Acquisition Regulations 601.303 Publication and...

  14. 20 CFR 702.601 - Definitions.

    Science.gov (United States)

    2010-04-01

    ... 20 Employees' Benefits 3 2010-04-01 2010-04-01 false Definitions. 702.601 Section 702.601 Employees' Benefits EMPLOYMENT STANDARDS ADMINISTRATION, DEPARTMENT OF LABOR LONGSHOREMEN'S AND HARBOR WORKERS' COMPENSATION ACT AND RELATED STATUTES ADMINISTRATION AND PROCEDURE Occupational Disease Which...

  15. Estudio del comportamiento en caliente del Inconel 718

    OpenAIRE

    Thomas, Amandine

    2005-01-01

    Las aleaciones Inconel son superaleaciones base níquel-cromo, que cubren un amplio espectro de composiciones y de propiedades. Son superaleaciones que tienen buenas propiedades de resistencia mecánica y a la corrosión que se mantienen a temperaturas altas. Las aplicaciones de estas aleaciones son muy amplias: recipientes para tratamiento térmico, turbinas, aviación, plantas nucleares generadoras de energía, etc... El Inconel 718 en particular es una aleación endurecible por precipitación, ...

  16. Cutting Zone Temperature Identification During Machining of Nickel Alloy Inconel 718

    Science.gov (United States)

    Czán, Andrej; Daniš, Igor; Holubják, Jozef; Zaušková, Lucia; Czánová, Tatiana; Mikloš, Matej; Martikáň, Pavol

    2017-12-01

    Quality of machined surface is affected by quality of cutting process. There are many parameters, which influence on the quality of the cutting process. The cutting temperature is one of most important parameters that influence the tool life and the quality of machined surfaces. Its identification and determination is key objective in specialized machining processes such as dry machining of hard-to-machine materials. It is well known that maximum temperature is obtained in the tool rake face at the vicinity of the cutting edge. A moderate level of cutting edge temperature and a low thermal shock reduce the tool wear phenomena, and a low temperature gradient in the machined sublayer reduces the risk of high tensile residual stresses. The thermocouple method was used to measure the temperature directly in the cutting zone. An original thermocouple was specially developed for measuring of temperature in the cutting zone, surface and subsurface layers of machined surface. This paper deals with identification of temperature and temperature gradient during dry peripheral milling of Inconel 718. The measurements were used to identification the temperature gradients and to reconstruct the thermal distribution in cutting zone with various cutting conditions.

  17. Interaction between zircaloy tube and inconel spacer grid at high temperature

    International Nuclear Information System (INIS)

    Nagase, Fumihisa; Otomo, Takashi; Uetsuka, Hiroshi; Furuta, Teruo

    1990-09-01

    In order to investigate the interaction between fuel cladding and spacer grid of the pressurized water reactor during a severe accident, isothermal reaction tests were performed at the temperature range from 1248 to 1673K. A specimen consisted of a short Zircaloy-4 cladding tube and a piece of spacer grid of Inconel-718. In the tests in an argon atmosphere, eutectic reaction between Zircaloy and Inconel was observed at the contact points at 1248K. Rapid reaction was observed at higher test temperatures. For example, in the test at 1373K for 300s, Zircaloy reacted with Inconel over the entire thickness (0.62mm) of the tube in the vicinity of the contact point. In the present tests, Zircaloy which has higher melting point than Inconel was dissolved preferentially due to eutectic formation. In the tests in an oxygen atmosphere, no eutectic reaction was observed at temperatures below 1437K. A trace of interaction was found at the contact point of specimen heated at 1573 and 1623K. However, decrease in Zircaloy thickness was not measured. The possibility of eutectic reaction between Zircaloy cladding and Inconel spacer grid seems to be quite limited when sufficient oxygen is supplied. (author)

  18. Microstructural investigation of grain stability in cryomilled inconel 625

    International Nuclear Information System (INIS)

    Chung, K.H.; Lee, J.; Rodriguez, R.; Lavernia, E.J.; Shin, D.H.

    2002-01-01

    The grain growth behavior of nanocrystalline Inconel 625 powders prepared by cryomilling (mechanical milling under a liquid nitrogen environment) was investigated using X-ray diffraction (XRD) and transmission electron microscopy (TEM). The average grain size of powders after 8 hours cryomilling was 22 nm. Along with this fine structure, ultrafine NiO and Cr 2 O 3 oxide particles were distributed in the cryomilled material with average size of 3 nm. It was found that the grain size remain under 250 nm after 4 hours heat treatment at 800 C, which correspond to T/T m ∝0.65. The cryomilled Inconel 625 showed improved grain stability compared to that of conventional Inconel 625 and cryomilled pure-Ni, due to the particle pinning of grain boundary by the oxide particles in addition to solute drag. (orig.)

  19. 40 CFR 60.601 - Definitions.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 6 2010-07-01 2010-07-01 false Definitions. 60.601 Section 60.601 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) STANDARDS OF..., transportation, collection, concentration, and purification of organic solvents. It may include enclosures, hoods...

  20. 13 CFR 120.601 - SBA Secondary Market.

    Science.gov (United States)

    2010-01-01

    ... 13 Business Credit and Assistance 1 2010-01-01 2010-01-01 false SBA Secondary Market. 120.601 Section 120.601 Business Credit and Assistance SMALL BUSINESS ADMINISTRATION BUSINESS LOANS Secondary Market Fiscal and Transfer Agent (fta) § 120.601 SBA Secondary Market. The SBA secondary market...

  1. 21 CFR 601.8 - Publication of revocation.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 7 2010-04-01 2010-04-01 false Publication of revocation. 601.8 Section 601.8 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) BIOLOGICS LICENSING General Provisions § 601.8 Publication of revocation. The Commissioner, following...

  2. Complex, Precision Cast Columbium Alloy Gas Turbine Engine Nozzles Coated to Resist Oxidation.

    Science.gov (United States)

    1980-04-01

    with the silicon powder. 7.3 Place the liner and its lid (covered with titanium sponge in the Inconel retort and seal it by TIG welding . 7.4 Leak check...DEVELOPMENT 19 3.1 Casting Process Development 19 3.1.1 Alloy Selection 19 3.1.2 Foundry Practice 21 3.1.3 Process Development 26 3.1.4 Casting...HYDRIDING TITANIUM AND VANADIUM 115 B SPRAY SLURRY PREPARATION PROCEDURE 117 C TELEDYNE WAH CHANG ALBANY COLUMBIUM AND COLUMBIUM 119 ALLOY PLATES

  3. 10 CFR 60.1 - Purpose and scope.

    Science.gov (United States)

    2010-01-01

    ... 10 Energy 2 2010-01-01 2010-01-01 false Purpose and scope. 60.1 Section 60.1 Energy NUCLEAR REGULATORY COMMISSION (CONTINUED) DISPOSAL OF HIGH-LEVEL RADIOACTIVE WASTES IN GEOLOGIC REPOSITORIES General Provisions § 60.1 Purpose and scope. This part prescribes rules governing the licensing (including issuance...

  4. 5 CFR 2635.601 - Overview.

    Science.gov (United States)

    2010-01-01

    ... 5 Administrative Personnel 3 2010-01-01 2010-01-01 false Overview. 2635.601 Section 2635.601 Administrative Personnel OFFICE OF GOVERNMENT ETHICS GOVERNMENT ETHICS STANDARDS OF ETHICAL CONDUCT FOR EMPLOYEES... from particular matters affecting the financial interests of a prospective employer when an employee's...

  5. Surface alloying of nickel based superalloys by laser

    International Nuclear Information System (INIS)

    Rodriguez, G.P.; Garcia, I.; Damborenea, J.J. de

    1998-01-01

    Ni based superalloys present a high oxidation resistance at high temperature as well as good mechanical properties. But new technology developments force to research in this materials to improve their properties at high temperature. In this work, two Ni based superalloys (Nimonic 80A and Inconel 600) were surface alloyed with aluminium using a high power laser. SEM and EDX were used to study the microstructure of the obtained coatings. Alloyed specimens were tested at 1.273 K between 24 and 250 h. Results showed the generation of a protective and continuous coating of alumina on the laser treated specimens surface that can improve oxidation resistance. (Author) 8 refs

  6. 29 CFR 1614.601 - EEO group statistics.

    Science.gov (United States)

    2010-07-01

    ... 29 Labor 4 2010-07-01 2010-07-01 false EEO group statistics. 1614.601 Section 1614.601 Labor... EMPLOYMENT OPPORTUNITY Matters of General Applicability § 1614.601 EEO group statistics. (a) Each agency... provided by an employee is inaccurate, the agency shall advise the employee about the solely statistical...

  7. 12 CFR 268.601 - EEO group statistics.

    Science.gov (United States)

    2010-01-01

    ... 12 Banks and Banking 3 2010-01-01 2010-01-01 false EEO group statistics. 268.601 Section 268.601... RULES REGARDING EQUAL OPPORTUNITY Matters of General Applicability § 268.601 EEO group statistics. (a... solely statistical purpose for which the data is being collected, the need for accuracy, the Board's...

  8. High Speed Finish Turning of Inconel 718 Using PCBN Tools under Dry Conditions

    Directory of Open Access Journals (Sweden)

    José Luis Cantero

    2018-03-01

    Full Text Available Inconel 718 is a superalloy, considered one of the least machinable materials. Tools must withstand a high level of temperatures and pressures in a very localized area, the abrasiveness of the hard carbides contained in the Inconel 718 microstructure and the adhesion tendency during its machining. Mechanical properties along with the low thermal conductivity become an important issue for the tool wear. The finishing operations for Inconel 718 are usually performed after solution heat treatment and age hardening of the material to give the superalloy a higher level of hardness. Carbide tools, cutting fluid (at normal or high pressures and low cutting speed are the main recommendations for finish turning of Inconel 718. However, dry machining is preferable to the use of cutting fluids, because of its lower environmental impact and cost. Previous research has concluded that the elimination of cutting fluid in these processes is feasible when using hard carbide tools. Recent development of new PCBN (Polycrystalline Cubic Boron Nitride grades for cutting tools with higher tenacity has allowed the application of these tool grades in the finishing operations of Inconel 718. This work studies the performance of commercial PCBN tools from four different tool manufacturers as well as an additional grade with equivalent performance during finish turning of Inconel 718 under dry conditions. Wear tests were carried out with different cutting conditions, determining the evolution of machining forces, surface roughness and tool wear. It is concluded that it is not industrially viable the high-speed finishing of Inconel 718 in a dry environment.

  9. 30 CFR 71.601 - Drinking water; quality.

    Science.gov (United States)

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false Drinking water; quality. 71.601 Section 71.601... Water § 71.601 Drinking water; quality. (a) Potable water provided in accordance with the provisions of § 71.600 shall meet the applicable minimum health requirements for drinking water established by the...

  10. Probabilistic and microstructural aspects of fatigue cracks initiation in Inconel 718

    International Nuclear Information System (INIS)

    Alexandre, F.

    2004-03-01

    Thermomechanical treatments have been recently developed to produce Inconel 718DA (Direct Aged). This alloy optimisation leads to an increase of the fatigue life but also the scatter. The aim of this study is on the one hand the understanding of the fatigue crack initiation mechanisms and on the other hand the modelling of the fatigue life and the scatter. An experimental study showed that the fatigue cracks were initiated from carbide particles in fine grain alloy. Interrupted tensile tests show that the particles cracking occurred at the first quarter of the fatigue cycle. Fatigue behaviour tests were also performed on various grain size 718 alloys. The last experimental part was devoted to measurements of the low cycle fatigue crack growth rates using a high focal distance microscope. For these tests, EDM micro-defects were used for the fatigue crack initiation sites. This method was also used to observe the small fatigue crack coalescence. A fatigue life model is proposed. It is based on the three fatigue crack initiation mechanisms competition: particle crack initiation on the surface, internal particle crack initiation and Stade I crack initiation. The particle fatigue crack initiation is supposed instantaneous at a critical stress level. The Tanaka and Mura model is used for analysing the Stage I crack initiation number of cycles. The fatigue crack growth rate was analysed using the Tomkins model identified on the small fatigue crack growth rate measurements. The proposed fatigue life model decomposed in three levels: a deterministic one and two probabilistic with and without crack coalescence. (author)

  11. Characteristics of Inconel Powders for Powder-Bed Additive Manufacturing

    Directory of Open Access Journals (Sweden)

    Quy Bau Nguyen

    2017-10-01

    Full Text Available In this study, the flow characteristics and behaviors of virgin and recycled Inconel powder for powder-bed additive manufacturing (AM were studied using different powder characterization techniques. The results revealed that the particle size distribution (PSD for the selective laser melting (SLM process is typically in the range from 15 μm to 63 μm. The flow rate of virgin Inconel powder is around 28 s·(50 g−1. In addition, the packing density was found to be 60%. The rheological test results indicate that the virgin powder has reasonably good flowability compared with the recycled powder. The inter-relation between the powder characteristics is discussed herein. A propeller was successfully printed using the powder. The results suggest that Inconel powder is suitable for AM and can be a good reference for researchers who attempt to produce AM powders.

  12. 10 CFR 434.601 - General.

    Science.gov (United States)

    2010-01-01

    ... innovative designs, materials, and equipment such as daylighting, passive solar heating, and heat recovery... 10 Energy 3 2010-01-01 2010-01-01 false General. 434.601 Section 434.601 Energy DEPARTMENT OF ENERGY ENERGY CONSERVATION ENERGY CODE FOR NEW FEDERAL COMMERCIAL AND MULTI-FAMILY HIGH RISE RESIDENTIAL...

  13. Effect of carbide precipitation on the corrosion behavior of Inconel alloy 690

    International Nuclear Information System (INIS)

    Sarver, J.M.; Crum, J.R.; Mankins, W.L.

    1987-01-01

    Intergranular carbide precipitation reactions have been shown to affect the stress corrosion cracking (SCC) resistance of nickel-chromium-iron alloys in environments relative to nuclear steam generators. Carbon solubility curves, time-temperature-sensitization plots and other carbide precipitation data are presented for alloy 690 as an aid in developing heat treatments for improved SCC resistance

  14. Chatter identification in milling of Inconel 625 based on recurrence plot technique and Hilbert vibration decomposition

    Directory of Open Access Journals (Sweden)

    Lajmert Paweł

    2018-01-01

    Full Text Available In the paper a cutting stability in the milling process of nickel based alloy Inconel 625 is analysed. This problem is often considered theoretically, but the theoretical finding do not always agree with experimental results. For this reason, the paper presents different methods for instability identification during real machining process. A stability lobe diagram is created based on data obtained in impact test of an end mill. Next, the cutting tests were conducted in which the axial cutting depth of cut was gradually increased in order to find a stability limit. Finally, based on the cutting force measurements the stability estimation problem is investigated using the recurrence plot technique and Hilbert vibration decomposition method.

  15. Effect of location on microstructure and mechanical properties of additive layer manufactured Inconel 625 using gas tungsten arc welding

    International Nuclear Information System (INIS)

    Wang, J.F.; Sun, Q.J.; Wang, H.; Liu, J.P.; Feng, J.C.

    2016-01-01

    Additive layer manufacturing (ALM), using gas tungsten arc welding (GTAW) as heat source, is a promising technology in producing Inconel 625 components due to significant cost savings, high deposition rate and convenience of processing. With the purpose of revealing how microstructure and mechanical properties are affected by the location within the manufactured wall component, the present study has been carried out. The manufactured Inconel 625 consists of cellular grains without secondary dendrites in the near-substrate region, columnar dendrites structure oriented upwards in the layer bands, followed by the transition from directional dendrites to equiaxed grain in the top region. With the increase in deposited height, segregation behavior of alloying elements Nb and Mo constantly strengthens with maximal evolution in the top region. The primary dendrite arm spacing has a well coherence with the content of Laves phase. The microhardness and tensile strength show obvious variation in different regions. The microhardness and tensile strength of near-substrate region are superior to that of layer bands and top region. The results are further explained in detail through the weld pool behavior and temperature field measurement.

  16. Effect of location on microstructure and mechanical properties of additive layer manufactured Inconel 625 using gas tungsten arc welding

    Energy Technology Data Exchange (ETDEWEB)

    Wang, J.F. [State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001 (China); Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209 (China); Sun, Q.J., E-mail: qjsun@hit.edu.cn [State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001 (China); Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209 (China); Wang, H. [State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001 (China); Liu, J.P. [Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209 (China); China Nuclear Industry 23 Construction Co., Ltd., Beijing 101300 (China); Feng, J.C. [State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001 (China); Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209 (China)

    2016-10-31

    Additive layer manufacturing (ALM), using gas tungsten arc welding (GTAW) as heat source, is a promising technology in producing Inconel 625 components due to significant cost savings, high deposition rate and convenience of processing. With the purpose of revealing how microstructure and mechanical properties are affected by the location within the manufactured wall component, the present study has been carried out. The manufactured Inconel 625 consists of cellular grains without secondary dendrites in the near-substrate region, columnar dendrites structure oriented upwards in the layer bands, followed by the transition from directional dendrites to equiaxed grain in the top region. With the increase in deposited height, segregation behavior of alloying elements Nb and Mo constantly strengthens with maximal evolution in the top region. The primary dendrite arm spacing has a well coherence with the content of Laves phase. The microhardness and tensile strength show obvious variation in different regions. The microhardness and tensile strength of near-substrate region are superior to that of layer bands and top region. The results are further explained in detail through the weld pool behavior and temperature field measurement.

  17. X-ray photoelectron spectroscopy study of the passive films formed on thermally sprayed and wrought Inconel 625

    Energy Technology Data Exchange (ETDEWEB)

    Bakare, M.S. [Materials, Mechanics and Structures Research Division, Faculty of Engineering, University of Nottingham, University Park, Nottingham, NG7 2RD (United Kingdom); Voisey, K.T., E-mail: Katy.voisey@nottingham.ac.uk [Materials, Mechanics and Structures Research Division, Faculty of Engineering, University of Nottingham, University Park, Nottingham, NG7 2RD (United Kingdom); Roe, M.J.; McCartney, D.G. [Materials, Mechanics and Structures Research Division, Faculty of Engineering, University of Nottingham, University Park, Nottingham, NG7 2RD (United Kingdom)

    2010-11-15

    There is a well known performance gap in corrosion resistance between thermally sprayed corrosion resistant coatings and the equivalent bulk materials. Interconnected porosity has an important and well known effect, however there are additional relevant microstructural effects. Previous work has shown that a compositional difference exists between the regions of resolidified and non-melted material that exist in the as-sprayed coatings. The resolidified regions are depleted in oxide forming elements due to formation of oxides during coating deposition. Formation of galvanic cells between these different regions is believed to decrease the corrosion resistance of the coating. In order to increase understanding of the details of this effect, this work uses X-ray photoelectron spectroscopy (XPS) to study the passive films formed on thermally sprayed coatings (HVOF) and bulk Inconel 625, a commercially available corrosion resistant Ni-Cr-Mo-Nb alloy. Passive films produced by potentiodynamic scanning to 400 mV in 0.5 M sulphuric acid were compared with air-formed films. The poorer corrosion performance of the thermally sprayed coatings was attributed to Ni(OH){sub 2}, which forms a loose, non-adherent and therefore non-protective film. The good corrosion resistance of wrought Inconel 625 is due to formation of Cr, Mo and Nb oxides.

  18. Structure-Property Relationships of Solid State Additive Manufactured Aluminum Alloy 2219 and Inconel 625

    Science.gov (United States)

    Rivera Almeyda, Oscar G.

    In this investigation, the processing-structure-property relations are correlated for solid state additively manufactured (SSAM) Inconel 625 (IN 625) and a SSAM aluminum alloy 2219 (AA2219). This is the first research of these materials processed by a new SSAM method called additive friction stir (AFS). The AFS process results in a refined grain structure by extruding solid rod through a rotating tool generating heat and severe plastic deformation. In the case of the AFS IN625, the IN625 alloy is known for exhibiting oxidation resistance and temperature mechanical stability, including strength and ductility. This study is the first to investigate the beneficial grain refinement and densification produced by AFS in IN625 that results in advantageous mechanical properties (YS, UTS, epsilonf) at both quasi-static and high strain rate. Electron Backscatter Diffraction (EBSD) observed dynamic recrystallization and grain refinement during the layer deposition in the AFS specimens, where the results identified fine equiaxed grain structures formed by dynamic recrystallization (DRX) with even finer grain structures forming at the layer interfaces. The EBSD quantified grains as fine as 0.27 microns in these interface regions while the average grain size was approximately 1 micron. Additionally, this is the first study to report on the strain rate dependence of AFS IN625 through quasi-static (QS) (0.001/s) and high strain rate (HR) (1500/s) tensile experiments using a servo hydraulic frame and a direct tension-Kolsky bar, respectively, which captured both yield and ultimate tensile strengths increasing as strain rate increased. Fractography performed on specimens showed a ductile fracture surface on both QS, and HR. Alternatively, the other AFS material system investigated in this study, AA2219, is mostly used for aerospace applications, specifically for rocket fuel tanks. EBSD was performed in the cross-section of the AA2219, also exhibiting DRX with equiaxed microstructure

  19. Creep-Rupture Behavior of Ni-Based Alloy Tube Bends for A-USC Boilers

    Science.gov (United States)

    Shingledecker, John

    Advanced ultrasupercritical (A-USC) boiler designs will require the use of nickel-based alloys for superheaters and reheaters and thus tube bending will be required. The American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code Section II PG-19 limits the amount of cold-strain for boiler tube bends for austenitic materials. In this summary and analysis of research conducted to date, a number of candidate nickel-based A-USC alloys were evaluated. These alloys include alloy 230, alloy 617, and Inconel 740/740H. Uniaxial creep and novel structural tests and corresponding post-test analysis, which included physical measurements, simplified analytical analysis, and detailed microscopy, showed that different damage mechanisms may operate based on test conditions, alloy, and cold-strain levels. Overall, creep strength and ductility were reduced in all the alloys, but the degree of degradation varied substantially. The results support the current cold-strain limits now incorporated in ASME for these alloys for long-term A-USC boiler service.

  20. 26 CFR 601.801 - Purpose and statutory authority.

    Science.gov (United States)

    2010-04-01

    ... 26 Internal Revenue 20 2010-04-01 2010-04-01 false Purpose and statutory authority. 601.801 Section 601.801 Internal Revenue INTERNAL REVENUE SERVICE, DEPARTMENT OF THE TREASURY (CONTINUED) INTERNAL REVENUE PRACTICE STATEMENT OF PROCEDURAL RULES Tax Counseling for the Elderly § 601.801 Purpose and...

  1. Beryllium coating on Inconel tiles

    International Nuclear Information System (INIS)

    Bailescu, V.; Burcea, G.; Lungu, C.P.; Mustata, I.; Lungu, A.M.; Rubel, M.; Coad, J.P.; Matthews, G.; Pedrick, L.; Handley, R.

    2007-01-01

    Full text of publication follows: The Joint European Torus (JET) is a large experimental nuclear fusion device. Its aim is to confine and study the behaviour of plasma in conditions and dimensions approaching those required for a fusion reactor. The plasma is created in the toroidal shaped vacuum vessel of the machine in which it is confined by magnetic fields. In preparation for ITER a new ITER-like Wall (ILW) will be installed on Joint European Torus (JET), a wall not having any carbon facing the plasma [1]. In places Inconel tiles are to be installed, these tiles shall be coated with Beryllium. MEdC represented by the National Institute for Laser, Plasma and Radiation Physics, Magurele, Bucharest and in direct cooperation with Nuclear Fuel Plant Pitesti started to coat Inconel tiles with 8 μm of Beryllium in accordance with the requirements of technical specification and fit for installation in the JET machine. This contribution provides an overview of the principles of manufacturing processes using thermal evaporation method in vacuum and the properties of the prepared coatings. The optimization of the manufacturing process (layer thickness, structure and purity) has been carried out on Inconel substrates (polished and sand blasted) The results of the optimization process and analysis (SEM, TEM, XRD, Auger, RBS, AFM) of the coatings will be presented. Reference [1] Takeshi Hirai, H. Maier, M. Rubel, Ph. Mertens, R. Neu, O. Neubauer, E. Gauthier, J. Likonen, C. Lungu, G. Maddaluno, G. F. Matthews, R. Mitteau, G. Piazza, V. Philipps, B. Riccardi, C. Ruset, I. Uytdenhouwen, R and D on full tungsten divertor and beryllium wall for JET TIER-like Wall Project, 24. Symposium on Fusion Technology - 11-15 September 2006 -Warsaw, Poland. (authors)

  2. Dimensional stability of some Fe-Ni-Cr alloys used in nuclear power generation

    International Nuclear Information System (INIS)

    Marucco, A.; Nath, B.

    1983-01-01

    The dimensional stability of four materials used in the nuclear power industry, viz Nimonic PE16, 20Cr-25Ni steel, Alloy 600 and Inconel 690, have been studied using X-ray diffractometry, electrical resistivity and thin foil microscopic techniques. Appreciable reductions in lattice parameters of these alloys occur on exposure to temperatures of 823 deg K and below. An order-disorder transformation has been found to be responsible for the observed behaviour. The transformation kinetics, associated microstructural changes and the implications for the usage of these materials are discussed. (author)

  3. 10 CFR 601.300 - Professional and technical services.

    Science.gov (United States)

    2010-01-01

    ... and analysis directly applying any professional or technical discipline. For example, drafting or a... 10 Energy 4 2010-01-01 2010-01-01 false Professional and technical services. 601.300 Section 601... Activities by Other Than Own Employees § 601.300 Professional and technical services. (a) The prohibition on...

  4. 20 CFR 601.4 - Certification for tax credit.

    Science.gov (United States)

    2010-04-01

    ... 20 Employees' Benefits 3 2010-04-01 2010-04-01 false Certification for tax credit. 601.4 Section 601.4 Employees' Benefits EMPLOYMENT AND TRAINING ADMINISTRATION, DEPARTMENT OF LABOR ADMINISTRATIVE... and Additional Tax Credit and Grant Purposes § 601.4 Certification for tax credit. (a) Within 30 days...

  5. Effect of filler metals on the mechanical properties of Inconel 625 and AISI 904L dissimilar weldments using gas tungsten arc welding

    Science.gov (United States)

    Senthur Prabu, S.; Devendranath Ramkumar, K.; Arivazhagan, N.

    2017-11-01

    In the present research work, dissimilar welding between Inconel 625 super alloy and AISI 904L super austenitic stainless steel using manual multi-pass continuous current gas tungsten arc (CCGTA) welding process employed with ERNiCrMo-4 and ERNiCrCoMo-1 fillers were performed to determine the mechanical properties and weldability. Tensile test results corroborated that the fracture had occurred at the parent metal of AISI 904L irrespective of filler used for all the trials. The presence of the macro and micro void coalescence in the fibrous matrix characterised for ductile mode of fracture. The hardness values at the weld interface of Inconel 625 side were observed to be higher for ERNiCrMo-4 filler due to the presence of strengthening elements such as W, Mo, Ni and Cr. The impact test accentuated that the weldments using ERNiCrMo-4 filler offered better impact toughness (41J) at room temperature. Bend test results showed that the weldments using these fillers exhibited good ductility without cracks.

  6. Oxide films in laser additive manufactured Inconel 718

    International Nuclear Information System (INIS)

    Zhang, Y.N.; Cao, X.; Wanjara, P.; Medraj, M.

    2013-01-01

    A continuous-wave 5 kW fiber laser welding system was used in conduction mode to deposit Inconel® alloy 718 (IN718) by employing filler wire on as-serviced IN718 parent material (PM) substrates. The direct laser deposited (DLD) coupons and as-serviced IN718 PM were then evaluated through tensile testing. To understand the failure mechanisms, the tensile fracture surfaces of the as-serviced IN718 PM, DLD and DLD-PM samples were analyzed using scanning electron microscopy. The fracture surfaces revealed the presence of both Al 2 O 3 and Cr 2 O 3 films, although the latter was reasoned to be the main oxide in IN718. Both the experimental observations and thermodynamic analysis indicated that oxidation of some alloying elements in IN718 cannot be completely avoided during manufacturing, whether in the liquid state under vacuum (for casting, the electron beam melting, welding and/or deposition) or with inert gas protection (for welding or laser deposition). The exposed surface of the oxide film on the fracture surface has poor wetting with the metal and thus can constitute a lack of bonding or a crack with either the metal and/or another non-wetted side of the oxide film. On the other hand, the wetted face of the oxide film has good atom-to-atom contact with the metal and may nucleate some intermetallic compounds, such as Laves, Ni 3 Nb-δ, Nb-rich MC and γ′ compounds. The potential of their nucleation on Cr 2 O 3 was assessed using planar disregistry. Coherent planes were found between these intermetallics and Cr 2 O 3

  7. 48 CFR 601.602-1 - Authority.

    Science.gov (United States)

    2010-10-01

    ... 48 Federal Acquisition Regulations System 4 2010-10-01 2010-10-01 false Authority. 601.602-1... ACQUISITION REGULATIONS SYSTEM Career Development, Contracting Authority, and Responsibilities 601.602-1 Authority. (a) DOS contracts are awarded pursuant to the foreign affairs management responsibilities...

  8. 10 CFR 601.205 - Professional and technical services.

    Science.gov (United States)

    2010-01-01

    ..., drafting of a legal document accompanying a bid or proposal by a lawyer is allowable. Similarly, technical... 10 Energy 4 2010-01-01 2010-01-01 false Professional and technical services. 601.205 Section 601... Activities by Own Employees § 601.205 Professional and technical services. (a) The prohibition on the use of...

  9. Electrochemical impedance spectrometry using 316L steel, hastelloy, maraging, Inconel 600, Elgiloy, carbon steel, TiN and NiCr. Simulation in tritiated water. 2 volumes; Spectrometrie d`impedance electrochimique sur acier 316L, hastelloy, maraging inconel 600, elgiloy, acier au carbone, TiN, NiCr. Simulations en eau tritiee. 2 volumes

    Energy Technology Data Exchange (ETDEWEB)

    Bellanger, G.

    1994-03-01

    Polarization and electrochemical impedance spectrometry curves are presented and discussed. These curves make it possible to ascertain the corrosion domains and to compare the slow and fast kinetics (voltammetry) of different stainless steel alloys. These corrosion kinetics, the actual or simulated tritiated water redox potentials, and the corrosion potentials provide a classification of the steels studied here: 316L, Hastelloy, Maraging, Inconel 600, Elgiloy, carbon steel and TiN and NiCr deposits. From the results it can be concluded that Hastelloy and Elgiloy have the best corrosion resistance. (author). 49 refs., 695 figs., tabs.

  10. Preparation of Inconel 740 superalloy by electron beam smelting

    Energy Technology Data Exchange (ETDEWEB)

    You, Xiaogang [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116023 (China); Laboratory for New Energy Material Energetic Beam Metallurgical Equipment Engineering of Liaoning Province, Dalian 116024 (China); Tan, Yi, E-mail: tanyi@dlut.edu.cn [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116023 (China); Laboratory for New Energy Material Energetic Beam Metallurgical Equipment Engineering of Liaoning Province, Dalian 116024 (China); You, Qifan; Shi, Shuang; Li, Jiayan [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116023 (China); Laboratory for New Energy Material Energetic Beam Metallurgical Equipment Engineering of Liaoning Province, Dalian 116024 (China); Ye, Fei [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116023 (China); Wei, Xin [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116023 (China); Laboratory for New Energy Material Energetic Beam Metallurgical Equipment Engineering of Liaoning Province, Dalian 116024 (China)

    2016-08-15

    A novel method, namely electron beam smelting (EBS) technology was used to prepare the Inconel 740 superalloy. The microstructures, hardness and oxidation behavior were characterized and compared with the traditionally prepared Inconel 740 superalloy. The results imply that the solution treatment gives rise to the coarsening of γ′ precipitates, with further aging treatment, the γ′ precipitates with size of less than 30 nm are distributed dispersively in the matrix, leading to a decreasing of the lattice parameters and an increasing of the misfit. The γ′ precipitates result in shearing mechanism of weakly pair coupling. The EBS 740 superalloy produces better properties than that prepared in the traditional method in both precipitation strengthening effect and oxidation resistance. - Highlights: • Electron beam smelting, a new method, was used to prepare the Inconel 740 superalloy. • The EBS 740 shows higher strengthening effect than 740 made in traditional method. • The EBS 740 shows better oxidation resistance than traditional 740. • It shows application prospect of EBS technology in preparing Ni-base superalloys.

  11. 41 CFR 101-26.601 - [Reserved

    Science.gov (United States)

    2010-07-01

    ... 41 Public Contracts and Property Management 2 2010-07-01 2010-07-01 true [Reserved] 101-26.601 Section 101-26.601 Public Contracts and Property Management Federal Property Management Regulations System FEDERAL PROPERTY MANAGEMENT REGULATIONS SUPPLY AND PROCUREMENT 26-PROCUREMENT SOURCES AND PROGRAM 26.6...

  12. Residual stresses in Inconel 718 engine disks

    Directory of Open Access Journals (Sweden)

    Dahan Yoann

    2014-01-01

    Full Text Available Aubert&Duval has developed a methodology to establish a residual stress model for Inconel 718 engine discs. To validate the thermal, mechanical and metallurgical parts of the model, trials on lab specimens with specific geometry were carried out. These trials allow a better understanding of the residual stress distribution and evolution during different processes (quenching, ageing, machining. A comparison between experimental and numerical results reveals the residual stresses model accuracy. Aubert&Duval has also developed a mechanical properties prediction model. Coupled with the residual stress prediction model, Aubert&Duval can now propose improvements to the process of manufacturing in Inconel 718 engine disks. This model enables Aubert&Duval customers and subcontractors to anticipate distortions issues during machining. It could also be usedt to optimise the engine disk life.

  13. Re-weldability tests of irradiated Inconel 625 by TIG welding method

    International Nuclear Information System (INIS)

    Tsuchiya, K.; Shimizu, M.; Kawamura, H.; Matsuda, F.; Kalinin, G.

    1998-01-01

    Inconel 625 is one of the possible materials for the vacuum vessel (VV) and for the in-vessel components of fusion reactors where high strength and high electrical resistance are required. In particular, Inconel 625 is used for the VV of JET and for flexible branch pipe lines in the ITER design. One of the most important issues for their applications is its re-weldability between un-irradiated and irradiated materials. This has a large impact on the design of in-vessel components. In this study, re-weldability of un-irradiated and/or irradiated Inconel 625 that has been welded by the tungsten inert gas (TIG) welding process has been examined, and effect of helium generation amount on mechanical properties of the weld joint has been discussed. (authors)

  14. Low cycle fatigue life of two nickel-base casting alloys in a hydrogen environment

    International Nuclear Information System (INIS)

    Cooper, R.A.

    1976-01-01

    Results of low cycle fatigue tests on alloy Mar-M-246 and Inconel 713 are presented. Based on the limited data, it was concluded that the Mar-M-246 material had a cyclic life in hydrogen that averaged three times higher than the alloy 713LC material for similar strain ranges. The hydrogen environment reduced life for both materials. The life reduction was more than an order of magnitude for the 713LC material. Porosity content of the cast specimens was as expected and was an important factor governing low cycle fatigue life

  15. 39 CFR 601.111 - Interest on claim amounts.

    Science.gov (United States)

    2010-07-01

    ... that date is later, until the date of payment. Simple interest will be paid at the rate established by... 39 Postal Service 1 2010-07-01 2010-07-01 false Interest on claim amounts. 601.111 Section 601.111... PROPERTY RIGHTS OTHER THAN PATENTS PURCHASING OF PROPERTY AND SERVICES § 601.111 Interest on claim amounts...

  16. 21 CFR 601.29 - Guidance documents.

    Science.gov (United States)

    2010-04-01

    ... Manufacturers Assistance (HFM-40), Center for Biologics Evaluation and Research, Food and Drug Administration... 21 Food and Drugs 7 2010-04-01 2010-04-01 false Guidance documents. 601.29 Section 601.29 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) BIOLOGICS...

  17. Comparison of corrosion behavior between fusion cladded and explosive cladded Inconel 625/plain carbon steel bimetal plates

    International Nuclear Information System (INIS)

    Zareie Rajani, H.R.; Akbari Mousavi, S.A.A.; Madani Sani, F.

    2013-01-01

    Highlights: ► Both explosive and fusion cladding aggravate the corrosion resistance of Inconel 625. ► Fusion cladding is more detrimental to nonuniform corrosion resistance. ► Single-layered fusion coat does not show any repassivation ability. ► Adding more layers enhance the corrosion resistance of fusion cladding Inconel 625. ► High impact energy spoils the corrosion resistance of explosive cladding Inconel 625. -- Abstract: One of the main concerns in cladding Inconel 625 superalloy on desired substrates is deterioration of corrosion resistance due to cladding process. The present study aims to compare the effect of fusion cladding and explosive cladding procedures on corrosion behavior of Inconel 625 cladding on plain carbon steel as substrate. Also, an attempt has been made to investigate the role of load ratio and numbers of fusion layers in corrosion behavior of explosive and fusion cladding Inconel 625 respectively. In all cases, the cyclic polarization as an electrochemical method has been applied to assess the corrosion behavior. According to the obtained results, both cladding methods aggravate the corrosion resistance of Inconel 625. However, the fusion cladding process is more detrimental to nonuniform corrosion resistance, where the chemical nonuniformity of fusion cladding superalloy issuing from microsegregation, development of secondary phases and contamination of clad through dilution hinders formation of a stable passive layer. Moreover, it is observed that adding more fusion layers can enhance the nonuniform corrosion resistance of fusion cladding Inconel 625, though this resistance still remains weaker than explosive cladding superalloy. Also, the results indicate that raising the impact energy in explosive cladding procedure drops the corrosion resistance of Inconel 625.

  18. Fatigue and fracture toughness characteristics of laser rapid manufactured Inconel 625 structures

    International Nuclear Information System (INIS)

    Ganesh, P.; Kaul, R.; Paul, C.P.; Tiwari, Pragya; Rai, S.K.; Prasad, R.C.; Kukreja, L.M.

    2010-01-01

    Research highlights: → Mechanical test results of Laser rapid manufactured (LRM) Inconel 625 are reported. → 12 and 25 mm thick CT specimens of LRM Inconel 625 showed similar fatigue crack growth. → Stage II crack growth behavior is observed in the investigated ΔK range. → Fracture toughness testing by J-integral method yielded J 1c of about 200-250 kJ/m 2 . - Abstract: Fatigue crack growth and fracture toughness characteristics of laser rapid manufactured (LRMed) Inconel 625 compact tension specimens of thickness 12 and 25 mm were investigated. Fatigue crack propagation in all the specimens investigated in the stress intensity range (ΔK) of 14-38 MPa√m, exhibited stage II crack growth in Paris' regime with nearly same slopes of crack growth per cycle versus ΔK plot. Fatigue crack growth rates in the LRMed specimens of present study were found to be lower than the reported values for wrought Inconel 625 in the ΔK range of 14-24 MPa√m and above this range they tended to coincide. X-ray diffraction patterns of the fractured surfaces revealed that the crack propagated along the growth direction of the specimens which was predominantly along the (1 1 1) plane. The fracture toughness values (J 0.2 ) for LRMed Inconel 625 specimens were found to be in the range of about 200-255 kJ/m 2 . The LRMed specimens exhibited stable crack growth during the J-integral test.

  19. Use of indexed sensitivity factors in the analysis of nickel and iron based alloys: study of the decalibration of sheathed Chromel/Alumel thermocouples

    International Nuclear Information System (INIS)

    Christie, W.H.

    1978-01-01

    Sheathed Chromel versus Alumel thermocouples decalibrate when exposed to temperatures in excess of 1100 0 C. Thermocouples sheathed in Inconel-600 and type 304 stainless steel were studied in this work. Quantified SIMS data showed that the observed decalibrations were due to significant alterations that took place in the Chromel and Alumel thermoelements. The amount of alteration was different for each thermocouple and was influenced by the particular sheath material used in the thermocouple construction. Relative sensitivity factors, indexed by a matrix ion species ratio, were used to quantify SIMS data for three nickel-based alloys, Chromel, Alumel, and Inconel-600, and an iron-based alloy, type 304 stainless steel. Oxygen pressure >2 x 10 -6 torr in the sputtering region gave enhanced sensitivity and superior quantitative results as compared to data obtained at instrumental residual pressure

  20. Effect of electric discharge machining on the fatigue life of Inconel 718

    Science.gov (United States)

    Jeelani, S.; Collins, M. R.

    1988-01-01

    The effect of electric discharge machining on the fatigue life of Inconel 718 alloy at room temperature was investigated. Data were generated in the uniaxial tension fatigue mode at ambient temperature using flat 3.175 mm thick specimens. The specimens were machined on a wire-cut electric discharge machine at cutting speeds ranging from 0.5 to 2 mm per minute. The specimens were fatigued at a selected stress, and the resulting fatigue lives compared with that of the virgin material. The surfaces of the fatigued specimens were examined under optical and scanning electron microscopes, and the roughness of the surfaces was measured using a standard profilometer. From the results of the investigation, it was concluded that the fatigue life of the specimens machined using EDM decreased slightly as compared with that of the virgin material, but remained unchanged as the cutting speed was changed. The results are explained using data produced employing microhardness measurements, profilometry, and optical and scanning microscopy.

  1. Thermal expansion studies on Inconel-600[reg] by high temperature X-ray diffraction

    International Nuclear Information System (INIS)

    Raju, S.; Sivasubramanian, K.; Divakar, R.; Panneerselvam, G.; Banerjee, A.; Mohandas, E.; Antony, M.P.

    2004-01-01

    The lattice thermal expansion characteristics of Inconel-600[reg] have been studied by high temperature X-ray diffraction (HT-XRD) technique in the temperature range 298-1200 K. Altogether four experimental runs were conducted on thin foils of about 75-100 μm thickness. The diffraction profiles have been accurately calibrated to offset the shift in 2θ values introduced by sample buckling at elevated temperatures. The corrected lattice parameter data have been used to estimate the instantaneous and mean linear thermal expansion coefficients as a function of temperature. The thermal expansion values estimated in the present study show a fair degree of agreement with other existing dilatometer based bulk thermal expansion estimates. The lattice parameter for this alloy at 300 K is found to be 0.3549(1) nm. The mean linear thermal expansivity is found to be 11.4 x 10 -6 K -1

  2. An assessment of microstructure, mechanical properties and corrosion resistance of dissimilar welds between Inconel 718 and 310S austenitic stainless steel

    International Nuclear Information System (INIS)

    Mortezaie, A.; Shamanian, M.

    2014-01-01

    In the present study, dissimilar welding between Inconel 718 nickel-base superalloy and 310S austenitic stainless steel using gas tungsten arc welding process was performed to determine the relationship between the microstructure of the welds and the resultant mechanical and corrosion properties. For this purpose, three filler metals including Inconel 625, Inconel 82 and 310 stainless steel were used. Microstructural observations showed that weld microstructures for all filler metals were fully austenitic. In tension tests, welds produced by Inconel 625 and 310 filler metals displayed the highest and the lowest ultimate tensile strength, respectively. The results of Charpy impact tests indicated that the maximum fracture energy was related to Inconel 82 weld metal. According to the potentiodynamic polarization test results, Inconel 82 exhibited the highest corrosion resistance among all tested filler metals. Finally, it was concluded that for the dissimilar welding between Inconel 718 and 310S, Inconel 82 filler metal offers the optimum properties at room temperature. - Highlights: • Three filler metals including Inconel 625, Inconel 82 and 310 SS were used. • A columnar to equiaxed dendritic structure was seen for IN-625 weld metal. • A granular austenitic microstructure obtained for Inconel 82 weld metal. • Microstructure of 310 weld metal includes solidification cracks along SSGB. • IN-82 weld metal showed the highest corrosion potential

  3. 5 CFR 831.601 - Purpose and scope.

    Science.gov (United States)

    2010-01-01

    ... 5 Administrative Personnel 2 2010-01-01 2010-01-01 false Purpose and scope. 831.601 Section 831.601 Administrative Personnel OFFICE OF PERSONNEL MANAGEMENT (CONTINUED) CIVIL SERVICE REGULATIONS (CONTINUED) RETIREMENT Survivor Annuities Organization and Structure of Regulations on Survivor Annuities...

  4. Fatigue and fracture toughness characteristics of laser rapid manufactured Inconel 625 structures

    Energy Technology Data Exchange (ETDEWEB)

    Ganesh, P., E-mail: ganesh@rrcat.gov.in [Laser Materials Processing Division, Raja Ramanna Centre for Advanced Technology, Indore (MP) 452013 (India); Kaul, R.; Paul, C.P. [Laser Materials Processing Division, Raja Ramanna Centre for Advanced Technology, Indore (MP) 452013 (India); Tiwari, Pragya; Rai, S.K. [Indus Synchrotrons Utilization Division, Raja Ramanna Centre for Advanced Technology, Indore (MP) 452013 (India); Prasad, R.C. [Metallurgy and Materials Science Department, IIT Bombay, Mumbai 400 076 (India); Kukreja, L.M. [Laser Materials Processing Division, Raja Ramanna Centre for Advanced Technology, Indore (MP) 452013 (India)

    2010-11-15

    Research highlights: {yields} Mechanical test results of Laser rapid manufactured (LRM) Inconel 625 are reported. {yields} 12 and 25 mm thick CT specimens of LRM Inconel 625 showed similar fatigue crack growth. {yields} Stage II crack growth behavior is observed in the investigated {Delta}K range. {yields} Fracture toughness testing by J-integral method yielded J{sub 1c} of about 200-250 kJ/m{sup 2}. - Abstract: Fatigue crack growth and fracture toughness characteristics of laser rapid manufactured (LRMed) Inconel 625 compact tension specimens of thickness 12 and 25 mm were investigated. Fatigue crack propagation in all the specimens investigated in the stress intensity range ({Delta}K) of 14-38 MPa{radical}m, exhibited stage II crack growth in Paris' regime with nearly same slopes of crack growth per cycle versus {Delta}K plot. Fatigue crack growth rates in the LRMed specimens of present study were found to be lower than the reported values for wrought Inconel 625 in the {Delta}K range of 14-24 MPa{radical}m and above this range they tended to coincide. X-ray diffraction patterns of the fractured surfaces revealed that the crack propagated along the growth direction of the specimens which was predominantly along the (1 1 1) plane. The fracture toughness values (J{sub 0.2}) for LRMed Inconel 625 specimens were found to be in the range of about 200-255 kJ/m{sup 2}. The LRMed specimens exhibited stable crack growth during the J-integral test.

  5. Procedures for the characterization of the detritiation of steel, Inconel and graphite

    International Nuclear Information System (INIS)

    Poletiko, C.; Trabuc, P.; Durand, J.; Tormos, B.; Pignoly, L.

    2006-01-01

    Due to its high diffusivity and different trapping phenomena, tritium is present in materials, such as steel or Inconel that are in use in different parts of a nuclear power reactor, or even in graphite which is present in fusion reactor or in future HTR. From waste management point of view, it is necessary to know as accurately as possible the tritium inventory in such materials before disposal. Moreover the knowledge of tritium species (HTO or HT, etc) is also a significant information in case of detritiation prior to storage, since countries regulation already limit tritium contents and releases. Three different strategies for tritiated waste management are foreseen: the first one is based upon a storage with confined packages, the second one is waiting for radioactive decay while the third one consists in the application of detritiation processes. Studies have been performed to determine different processes that could be used for tritium removal. The aim of this paper was, to study, at laboratory scale, different detritiation procedures which may be used for stainless steel, Inconel and carbon materials. Thermal detritiation kinetics till 1300 K has been studied under various atmospheres; full chemical dissolution of samples has also been performed for steel, Inconel and graphite, this to perfectly know the tritium content in such matrices. A particular attention must be applied to Inconel, the main reason is linked to the presence of titanium which is supposed to be a tritium trap. Finally, a study of tritium content in steel and Inconel layers has also been made, to learn about the tritium behaviour. All results are given, allowing the possibility to take a decision either for detritiation procedure or storage conditions. The main result is that thermal out-gassing for steel and graphite enables higher than 95 % tritium extraction from the bulk at temperature in the range of 600 K, without any material destruction under hi-tech gas (Ar + 5% volume H 2 ), on

  6. 39 CFR 601.104 - Postal purchasing authority.

    Science.gov (United States)

    2010-07-01

    ... in writing local buying authority throughout the Postal Service. ... 39 Postal Service 1 2010-07-01 2010-07-01 false Postal purchasing authority. 601.104 Section 601.104 Postal Service UNITED STATES POSTAL SERVICE PROCUREMENT SYSTEM FOR THE U.S. POSTAL SERVICE...

  7. Intercrystalline Stress Corrosion of Inconel 600 Inspection Tubes in the Aagesta Reactor

    Energy Technology Data Exchange (ETDEWEB)

    Groenwall, B; Ljungberg, L; Huebner, W; Stuart, W

    1966-08-15

    caustic solutions and in plain, pure high-temperature water. At this stage it seems most difficult to establish which of these cases is relevant to the Aagesta failure. This is especially true as both these conditions give the same type of intercrystalline cracks, The possible influence of cold work, i. e. residual stresses, originating from milling, indicate the necessity of more stringent delivery control. Also the probable effect of carbides and other precipitates should be avoided by selecting a low carbon, pure iron-nickel-chromium alloy, preferably vacuum-melted. The failures encountered show that Inconel 600 under certain conditions may be susceptible to inter-crystalline stress corrosion cracking in alkaline high-temperature water. It remains to be shown if a satisfactory performance of Inconel 600 for long operating periods can be obtained under similar conditions in water-cooled reactors by proper manufacturing control and judicious design, omitting high stresses and crevices.

  8. Intercrystalline Stress Corrosion of Inconel 600 Inspection Tubes in the Aagesta Reactor

    International Nuclear Information System (INIS)

    Groenwall, B.; Ljungberg, L.; Huebner, W.; Stuart, W.

    1966-08-01

    solutions and in plain, pure high-temperature water. At this stage it seems most difficult to establish which of these cases is relevant to the Aagesta failure. This is especially true as both these conditions give the same type of intercrystalline cracks, The possible influence of cold work, i. e. residual stresses, originating from milling, indicate the necessity of more stringent delivery control. Also the probable effect of carbides and other precipitates should be avoided by selecting a low carbon, pure iron-nickel-chromium alloy, preferably vacuum-melted. The failures encountered show that Inconel 600 under certain conditions may be susceptible to inter-crystalline stress corrosion cracking in alkaline high-temperature water. It remains to be shown if a satisfactory performance of Inconel 600 for long operating periods can be obtained under similar conditions in water-cooled reactors by proper manufacturing control and judicious design, omitting high stresses and crevices

  9. Thermal stability of the superalloys Inconel 625 and Nimonic 86

    International Nuclear Information System (INIS)

    Kohl, H.K.; Peng, K.

    1981-01-01

    The thermal stability of Inconel 625 and Nimonic 86, as received, cold worked (10, 20, and 40%), and solution treated, was investigated in the temperature range 500-900 0 C. The annealing times varied from 0.3 (0.03) to 100 days. Precipitation hardening and recovery (recrystallisation) takes place in cold worked material, beginning after shorter times in cold worked material than in as received material. The temperature interval for precipitation hardening is extended in Nimonic 86, due to cold working, from about 500-600 0 C to about 450-700 0 C. It is possible to suppress or retard the precipitation hardening in solution treated Inconel 625 and Nimonic 86 by fast cooling after solution annealing. Hardness was measured at room temperature with five different loads, so that the parameters k and n from Meyer's-law, and the Brinell hardness number (for F / D 2 = 30) could be determined. The lattice contraction of Inconel 625 due to ageing was investigated with X-ray measurements. The change of intensities of the diffractometer traces due to recovery was also determined. (orig.)

  10. Electrochemical impedance spectrometry using 316L steel, hastelloy, maraging, Inconel 600, Elgiloy, carbon steel, TiN and NiCr. Simulation in tritiated water. 2 volumes

    International Nuclear Information System (INIS)

    Bellanger, G.

    1994-03-01

    Polarization and electrochemical impedance spectrometry curves are presented and discussed. These curves make it possible to ascertain the corrosion domains and to compare the slow and fast kinetics (voltammetry) of different stainless steel alloys. These corrosion kinetics, the actual or simulated tritiated water redox potentials, and the corrosion potentials provide a classification of the steels studied here: 316L, Hastelloy, Maraging, Inconel 600, Elgiloy, carbon steel and TiN and NiCr deposits. From the results it can be concluded that Hastelloy and Elgiloy have the best corrosion resistance. (author). 49 refs., 695 figs., tabs

  11. Improved nickel plating of Inconel X-750

    Science.gov (United States)

    Farmer, M. E.; Feeney, J. E.; Kuster, C. A.

    1969-01-01

    Electroplating technique with acid pickling provides a method of applying nickel plating on Inconel X-750 tubing to serve as a wetting agent during brazing. Low-stress nickel-plating bath contains no organic wetting agents that cause the nickel to blister at high temperatures.

  12. 48 CFR 49.601-2 - Letter notice.

    Science.gov (United States)

    2010-10-01

    ... 48 Federal Acquisition Regulations System 1 2010-10-01 2010-10-01 false Letter notice. 49.601-2 Section 49.601-2 Federal Acquisition Regulations System FEDERAL ACQUISITION REGULATION CONTRACT MANAGEMENT... immediate complete spoilage of work-in-process having a definite commercial value, or (D) to prevent any...

  13. 26 CFR 601.522 - Power of attorney.

    Science.gov (United States)

    2010-04-01

    ... 26 Internal Revenue 20 2010-04-01 2010-04-01 false Power of attorney. 601.522 Section 601.522 Internal Revenue INTERNAL REVENUE SERVICE, DEPARTMENT OF THE TREASURY (CONTINUED) INTERNAL REVENUE PRACTICE... Spirits, Wines, and Beer), Chapter 52 (Cigars, Cigarettes, and Cigarette Papers and Tubes), and chapter 53...

  14. Fatigue-crack propagation behavior of Inconel 600

    International Nuclear Information System (INIS)

    James, L.A.

    1976-05-01

    The techniques of linear-elastic fracture mechanics were employed to characterize the effects of several parameters upon the fatigue-crack propagation behavior of Inconel 600. The parameters studied included temperature, cyclic frequency, stress ratio, thermal aging, and a limited amount of testing in a liquid sodium environment

  15. Corrosion study in molten fluoride salt

    International Nuclear Information System (INIS)

    Keny, S.J.; Kumbhar, A.G.; Rangarajan, S.; Gupta, V.K.; Maheshwari, N.K.; Vijayan, P.K.

    2013-01-01

    Corrosion behaviors of two alloys viz. Inconel 625 and Inconel 617 were tested in molten fluoride salts of lithium, sodium and potassium (FLiNaK) in the temperature range of 550-750 ℃ in a nickel lined Inconel vessel. Electrochemical polarization (Tafel plot) technique was used for this purpose. For both alloys, the corrosion rate was found to increase sharply beyond 650 ℃ . At 600 ℃ , Inconel 625 showed a decreasing trend in the corrosion rate over a period of 24 hours, probably due to changes in the surface conditions. After fifteen days, re-testing of Inconel 625 in the same melt showed an increase in the corrosion rate. Inconel 625 was found to be more corrosion resistant than Inconel 617. (author)

  16. The Evaluation of Surface Integrity During Machining of Inconel 718 with Various Laser Assistance Strategies

    Directory of Open Access Journals (Sweden)

    Wojciechowski Szymon

    2017-01-01

    Full Text Available The paper is focused on the evaluation of surface integrity formed during turning of Inconel 718 with the application of various laser assistance strategies. The primary objective of the work was to determine the relations between the applied machining strategy and the obtained surface integrity, in order to select the effective cutting conditions allowing the obtainment of high surface quality. The carried out experiment included the machining of Inconel 718 in the conventional turning conditions, as well as during the continuous laser assisted machining and sequential laser assistance. The surface integrity was evaluated by the measurements of machined surface topographies, microstructures and the microhardness. Results revealed that surface integrity of Inconel 718 is strongly affected by the selected machining strategy. The significant improvement of the surface roughness formed during machining of Inconel 718, can be reached by the application of simultaneous laser heating and cutting (LAM.

  17. Parametric study of development of Inconel-steel functionally graded materials by laser direct metal deposition

    International Nuclear Information System (INIS)

    Shah, Kamran; Haq, Izhar ul; Khan, Ashfaq; Shah, Shaukat Ali; Khan, Mushtaq; Pinkerton, Andrew J

    2014-01-01

    Highlights: • Functionally graded steel and nickel super-alloy structures have been developed. • Mechanical properties of FGMs can be controlled by process input parameters. • SDAS is strongly dependent on the laser power and powder mass flow rate. • Carbides provide a mechanism to control the hardness and wear resistance of FGM. • Tensile strength of FGM is dependent on the laser power and powder mass flow rate. - Abstract: Laser direct metal deposition (LDMD) has developed from a prototyping to a single and multiple metals manufacturing technique. It offers an opportunity to produce graded components, with differing elemental composition, phase and microstructure at different locations. In this work, continuously graded Stainless Steel 316L and Inconel 718 thin wall structures made by direct laser metal deposition process have been explored. The paper considers the effects of process parameters including laser power levels and powder mass flow rates of SS316L and Inconel 718 during the deposition of the Steel–Ni graded structures. Microstructure characterisation and phase identification are performed by optical microscopy and X-ray diffraction techniques. Mechanical testing, using methods such as hardness, wear resistance and tensile testing have been carried out on the structures. XRD results show the presence of the NbC and Fe 2 Nb phases formed during the deposition. The effect of experimental parameters on the microstructure and physical properties are determined and discussed. Work shows that mechanical properties can be controlled by input parameters and generation of carbides provides an opportunity to selectively control the hardness and wear resistance of the functionally graded material

  18. Property evaluation of Ni base alloy for superconducting generators and its application to seal welded joints

    International Nuclear Information System (INIS)

    Nobuhisa Suzuki; Toshiaki Murakami; Kenichi Suzuki; Satoru Asai; Minorou Tanaka; Yoshio Kobayashi

    1992-01-01

    Property requirements demanded on structural materials for rotors of superconducting generators are quite strict while there are many themes in the technical development of such materials. Components used in the cryogenic temperature are of course required to be nonmagnetic material. Additional requirements demanded on cryogenic structural materials for high response excitation superconducting generators can be summarized as follows: (1) 0.2% yield strength > 800 MPa (RT) (2) Charpy absorbed energy > 25 J (4K) (3) Electrical resistivity > 90 μΩ·cm (4K). As a candidate material which satisfy the above property requirements, we can cite precipitation-hardened Ni base alloys, for example, Inconel 718. However, production of Inconel718 is limited to about 2 tons due to problems related to segregation etc., and therefore fabrication of large-sized ingots for manufacturing generator components may be difficult. Also, there may be problems regarding weldability, especially from the viewpoint of microcracking in the heat affected zone, among strength-supporting parts or the parts requiring functional capability such as seal welded joints. Under such background circumstances, we conducted studies on chemical composition by considering producibility of large-sized ingots and weldability of the alloy as well as property evaluations of materials incorporating such requirements. Further, included in this paper are the application of the alloy to seal welded joints and its unified fatigue strength evaluation method

  19. Effect of deposition strategy on the microstructure and mechanical properties of Inconel 625 superalloy fabricated by pulsed plasma arc deposition

    International Nuclear Information System (INIS)

    Xu, F.J.; Lv, Y.H.; Xu, B.S.; Liu, Y.X.; Shu, F.Y.; He, P.

    2013-01-01

    Highlights: ► PPAD Inconel 625 sample deposited with ICS strategy exhibits improved surface quality. ► ICS sample exhibits finer microstructure and improved mechanical properties. ► Higher level γ′ and γ″ phases are precipitated in the ICS sample. ► STA heat treatment reduced the concentration of Nb element. ► STA heat treatment improved the mechanical properties of PPAD Inconel 625. -- Abstract: Pulsed plasma arc deposition (PPAD), which combines pulsed plasma cladding with rapid prototyping, is a promising technology for manufacturing near net shape components due to its superiority in cost and convenience of processing. The aim of this study was to investigate the influences of interpass cooling strategy (ICS) and continuous deposition strategy (CDS) on microstructure and mechanical properties of the PPAD Inconel 625 non-ferrous alloy. The as-deposited samples in the two conditions were subjected to the post heat treatment: 980 °C solution treatment + direct aging (STA). The microstructures and mechanical properties of the samples were characterized by means of scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS), transmission electron microscopy (TEM), micro-hardness and tensile testers. It was found that the as-deposited microstructure exhibited homogenous cellular dendrite structure, which grew epitaxially along the deposition direction. The as-deposited microstructure of ICS sample revealed smaller dendritic arm spacing, less niobium segregation and discontinuous finer Laves phase in the interdendritic regions compared to the case of continuous deposition strategy (CDS). The ICS sample exhibited better mechanical properties than CDS sample. After STA heat treatment, a large amount of Laves particles in the interdendritic regions were dissolved, resulting in the reduction of Nb segregation and the precipitation of needle-like δ (Ni 3 Nb). The tensile and yield strength of the as-deposited samples were

  20. 15 CFR 970.601 - Logical mining unit.

    Science.gov (United States)

    2010-01-01

    ... 15 Commerce and Foreign Trade 3 2010-01-01 2010-01-01 false Logical mining unit. 970.601 Section... ENVIRONMENTAL DATA SERVICE DEEP SEABED MINING REGULATIONS FOR EXPLORATION LICENSES Resource Development Concepts § 970.601 Logical mining unit. (a) In the case of an exploration license, a logical mining unit is an...

  1. 31 CFR 601.2 - Description of paper.

    Science.gov (United States)

    2010-07-01

    ... 31 Money and Finance: Treasury 3 2010-07-01 2010-07-01 false Description of paper. 601.2 Section... ENGRAVING AND PRINTING, DEPARTMENT OF THE TREASURY DISTINCTIVE PAPER FOR UNITED STATES CURRENCY AND OTHER SECURITIES § 601.2 Description of paper. The paper utilized in the printing of United States currency and...

  2. Stress corrosion cracking of several high strength ferrous and nickel alloys

    Science.gov (United States)

    Nelson, E. E.

    1971-01-01

    The stress corrosion cracking resistance of several high strength ferrous and nickel base alloys has been determined in a sodium chloride solution. Results indicate that under these test conditions Multiphase MP35N, Unitemp L605, Inconel 718, Carpenter 20Cb and 20Cb-3 are highly resistant to stress corrosion cracking. AISI 410 and 431 stainless steels, 18 Ni maraging steel (250 grade) and AISI 4130 steel are susceptible to stress corrosion cracking under some conditions.

  3. The effect of swelling in Inconel 600 on the performance of FFTF [Fast Flux Test Facility] reflector assemblies

    International Nuclear Information System (INIS)

    Makenas, B.J.; Trenchard, R.G.; Hecht, S.L.; McCarthy, J.M.; Garner, F.A.

    1986-02-01

    The Fast Flux Test Facility (FFTF) is designed with non-fueled outer row assemblies, each of which consists of a stack of Inconel 600 blocks penetrated by 316 stainless steel (SS) coolant tubes. These assemblies act as a radial neutron reflector and as a straight but flexible core boundary. During an FFTF refueling outage it was observed that the degree of difficulty in withdrawing an outer row driver fuel assembly was a function of the peak fast fluence of neighboring reflector assemblies. It was subsequently determined through various postirradiation examinations that the reflector assemblies were both bowed and stiff. Measurements of the individual Inconel 600 blocks indicated that the blocks had distorted into a trapezoidal cross section due to differential swelling of Inconel 600 in a steep radial flux gradient. Immersion density results indicate greater irradiation induced volumetric swelling than any previously reported data or correlation for Inconel 600 at equivalent fast fluence. The Inconel 600 swelled approximately the same amount as the SA 316 SS reflector components. Transmission electron microscopy studies on the Inconel blocks and swelling measurements on related materials have been performed and these data have been related to the performance of the reflector materials

  4. Effects of pre-deformation in topological characterization of inconel 600 submitted to isothermal treatments

    International Nuclear Information System (INIS)

    Mourao, D.R.; Monteiro, E.

    1980-01-01

    INCONEL 600 samples were performed at thermal treatment between 550 0 C and 790 0 C during 3 hours after uniaxial tension testing. At each pair hardening-temperature were determined the microhardness and microstrostructure. With the objetive of to determine the influence of the hardening up to INCONEL's mechanical behavior, were plotted microhardness X temperature. (Author) [pt

  5. Structure and Properties of the Aluminide Coatings on the Inconel 625 Superalloy

    Science.gov (United States)

    Adamiak, Stanisław; Bochnowski, Wojciech; Dziedzic, Andrzej; Filip, Ryszard; Szeregij, Eugeniusz

    2016-01-01

    The research samples used in this study were based on the Inconel 625 alloy; the examined samples were coated with aluminide films deposited in a low-activity chemical vapor deposition (CVD) process. The samples' microstructure was investigated with optical and electron microscopy and energy dispersive X-ray spectroscopy analysis. Hardness measurements were performed using Vickers and Berkovich test methods. The adhesion of the aluminide coating was determined by fractography. It was shown that the fracture mechanism was different for the respective zones of the aluminide coating and the substrate material. The outer zone of the aluminide coating is characterized by an intercrystalline fracture, with a small contribution of transcrystalline fracture within individual grains (large crystallites in the bottom of the zone, composed of smaller crystallites, also show an intercrystalline fracture). The substrate material exhibited a ductile intercrystalline fracture. Based on this investigation, an increase of the microhardness of the material occurring at loads below 0.2 N was observed. When determining microhardness of aluminide coating it is necessary to take into account the optimal choice of the indentation tip.

  6. Effect of cutting fluids and cutting conditions on surface integrity and tool wear in turning of Inconel 713C

    Science.gov (United States)

    Hikiji, R.

    2018-01-01

    The trend toward downsizing of engines helps to increase the number of turbochargers around Europe. As for the turbocharger, the temperature of the exhaust gas is so high that the parts made of nickel base super alloy Inconel 713C are used as high temperature strength metals. External turning of Inconel 713C which is used as the actual automotive parts was carried out. The effect of the cutting fluids and cutting conditions on the surface integrity and tool wear was investigated, considering global environment and cost performance. As a result, in the range of the cutting conditions used this time, when the depth of cut was small, the good surface integrity and tool life were obtained. However, in the case of the large corner radius, it was found that the more the cutting length increased, the more the tool wear increased. When the cutting length is so large, the surface integrity and tool life got worse. As for the cutting fluids, it was found that the synthetic type showed better performance in the surface integrity and tool life than the conventional emulsion. However, it was clear that the large corner radius made the surface roughness and tool life good, but it affected the size error etc. in machining the workpiece held in a cantilever style.

  7. Investigation of corrosion resistance of alloys with high mechanical characteristics in some environments of food industry

    International Nuclear Information System (INIS)

    Tremoureux, Yves

    1978-01-01

    This research thesis aimed at improving knowledge in the field of stress-free corrosion of alloys with high mechanical characteristics in aqueous environments, at highlighting some necessary aspects of their behaviour during cleaning or disinfection, and at selecting alloys which possess a good stress-free corrosion resistance in view of a later investigation of their stress corrosion resistance. After a presentation of the metallurgical characteristics of high mechanical strength alloys and the report of a bibliographical study on corrosion resistance of these alloys, the author presents and discusses the results obtained in the study of a possible migration of metallic ions in a milk product which is submitted to a centrifugation, and of the corrosion resistance of selected alloys with respect to the different media they will be in contact with during ultra-centrifugation. The following alloys have been used in this research: Marval 18, Marphynox, Marval X12, 17-4PH steel, Inconel 718 [fr

  8. Effect of welding speed on microstructural and mechanical properties of friction stir welded Inconel 600

    International Nuclear Information System (INIS)

    Song, K.H.; Fujii, H.; Nakata, K.

    2009-01-01

    In order to evaluate the properties of a friction stir welded Ni base alloy, Inconel 600 (single phase type) was selected. Sound friction stir welds without weld defect were obtained at 150 and 200 mm/min in welding speed, however, a groove like defect occurred at 250 mm/min. The electron back scattered diffraction (EBSD) method was used to analyze the grain boundary character distribution. As a result, dynamic recrystallization was observed at all conditions, and the grain refinement was achieved in the stir zone, and it was gradually accelerated from 19 μm in average grain size of the base material to 3.4 μm in the stir zone with increasing the welding speed. It also has an effect on the mechanical properties so that friction stir welded zone showed 20% higher microhardness and 10% higher tensile strength than those of base material.

  9. A study of the machining characteristics of AISI 1045 steel and Inconel 718 with a cylindrical shape in laser-assisted milling

    International Nuclear Information System (INIS)

    Woo, Wan-Sik; Lee, Choon-Man

    2015-01-01

    Laser-assisted machining (LAM) is an effective and economic technique for enhancing the machinability of materials which are difficult-to-cut, such as nickel alloys, titanium alloys and various ceramics. Recently, many researchers have studied the effectiveness of laser-assisted turning (LAT) by measuring its cutting force, tool wear, specific cutting energy and surface roughness. However, research on laser-assisted milling (LAMill) is still in progress because it is difficult to control the laser heating source and tool path to machine the varying shape of the workpiece using this method. Moreover, there have been no researches of workpieces with three-dimensional shapes. During the LAMill process, the material is softened and the mechanical strength of the material is reduced when a laser is used to irradiate the surface of the workpiece. As a result, the cutting force is reduced and the surface roughness is improved with LAMill. The purpose of this study was to develop three-dimensional LAMill and to verify the effectiveness of this approach by comparing it to the conventional machining (CM) method. A thermal analysis was also conducted in order to determine the effective depth of cut (DOC). Also, the cutting force and surface roughness of AISI 1045 steel and Inconel 718 with cylindrical shapes were measured. Measured results of machining characteristics were also analyzed according to the cutting method, i.e., up cut milling, down cut milling and milling style. - Highlights: • The materials with cylindrical shape is first applied to laser-assisted milling (LAMill). • The method determining the depth of cut through thermal analysis is proposed. • The effectiveness of LAMill is verified by comparing the conventional machining. • Down cut milling is recommended for the case of Inconel 718.

  10. Effect of Sulfur and Chlorine on Fireside Corrosion Behavior of Inconel 740 H Superalloy

    Science.gov (United States)

    Jin-tao, Lu; Yan, Li; Zhen, Yang; Jin-yang, Huang; Ming, Zhu; Gu, Y.

    2018-03-01

    Fireside corrosion behavior of Inconel 740H superalloy was studied at 750 °C in simulated coal ash/flue gas environments by means of XRD, SEM and EDS. The results indicated that the corrosion behavior was strongly related to the SO2 levels and was significantly affected by NaCl additions. In presence of the atmospheres with 0.1 % SO2, the alloy exhibited the highest corrosion resistance due to formation of a stable and dense Cr2O3 film. In presence of the atmosphere with 1.5 % SO2, however, a non-coherent and porous Cr2O3 film was formed. The thickness of film and internal sulfides were substantially increased. The NaCl additions significantly accelerated the corrosion process. A non-protective outer oxide film was formed, composed by multiple layers with serious inner sulfide and spallation. The depths of internal oxidizing and sulfuration zones were significantly increased. The mechanism of ash corrosion formation was also discussed.

  11. 39 CFR 601.108 - SDR Official disagreement resolution.

    Science.gov (United States)

    2010-07-01

    ... purchasing decisions and the administrative records concerning those decisions. All disagreements under § 601... time to lodge a disagreement lapses. (e) Disagreement decision process. The SDR Official will promptly...: INTELLECTUAL PROPERTY RIGHTS OTHER THAN PATENTS PURCHASING OF PROPERTY AND SERVICES § 601.108 SDR Official...

  12. 49 CFR 601.2 - Organization of the administration.

    Science.gov (United States)

    2010-10-01

    ... 49 Transportation 7 2010-10-01 2010-10-01 false Organization of the administration. 601.2 Section... ADMINISTRATION, DEPARTMENT OF TRANSPORTATION ORGANIZATION, FUNCTIONS, AND PROCEDURES General Provisions § 601.2 Organization of the administration. (a) The headquarters organization of FTA is comprised of eight principal...

  13. Strain rate and temperature effects on the stress corrosion cracking of Inconel 600 steam generator tubing in the primary water conditions

    International Nuclear Information System (INIS)

    Kim, U.C.; van Rooyen, D.

    1985-01-01

    A single heat of Inconel Alloy 600 was examined in this work, using slow strain rate tests (SSRT) in simulated primary water at temperatures of 325 0 -345 0 -365 0 C. The best measure of stress corrosion cracking (SCC) was percent SCC present on the fracture surface. Strain rate did not seem to affect crack growth rate significantly, but there is some question about the accuracy of calculating these values in the absence of a direct indication of when a crack initiates. Demarcation was determined between domains of temperature/strain rate where SCC either did, or did not, occur. Slower extension rates were needed to produce SCC as the temperature was lowered. 10 figs

  14. Microstructural evolution and precipitation behavior in heat affected zone of Inconel 625 and AISI 904L dissimilar welds

    Science.gov (United States)

    Senthur Prabu, S.; Devendranath Ramkumar, K.; Arivazhagan, N.

    2017-11-01

    In the present investigation an attempt has been made to join the dissimilar combination of Inconel 625 super alloy and super austenitic stainless steel (AISI 904L) using manual multi-pass continuous current gas tungsten arc (CCGTA) welding processes. Two different filler wires such as ERNiCrMo-4 and ERNiCrCoMo-1 have been used to compare the metallurgical properties of these welded joints. Both optical microscopy and scanning electron microscopy techniques were adopted to disseminate the microstructure traits of these weldments. Formation of secondary phases at the HAZ and weld interface of AISI 904L was witnessed while using the ERNiCrCoMo-1 filler, along with Solidification Grain Boundary (SGB) and Migrated Grain Boundary (MGB) were also observed at the weld zone.

  15. Microstructural characterisation of Inconel 718 gas tungsten arc welds

    International Nuclear Information System (INIS)

    Ram, G.D.J.; Reddy, A.V.; Rao, K.P.

    2005-01-01

    The presence of Nb-rich, brittle, intermetallic Laves phase in Inconel 718 weld fusion zones is detrimental to weld mechanical properties. In the current work, autogenous bead-on-plate gas tungsten-arc welds were deposited in 2 mm thick IN 718 sheets. The welds were subjected to the following heat treatments: i) direct aging, ii) solution treatment at 980 C followed by aging, and iii) solution treatment at 1080 C followed by aging. Detailed microstructural characterisation was carried out using optical, scanning electron and transmission electron microscopes and electron probe microanalysis. The microstructural features in as-welded and post-weld heat treated conditions are discussed. The results show that post-weld heat treatments alone cannot provide satisfactory solution to the Laves problem in Inconel 718 gas tungsten-arc welds

  16. Fatigue Behavior of Inconel 718 TIG Welds

    Science.gov (United States)

    Alexopoulos, Nikolaos D.; Argyriou, Nikolaos; Stergiou, Vasillis; Kourkoulis, Stavros K.

    2014-08-01

    Mechanical behavior of reference and TIG-welded Inconel 718 specimens was examined in the present work. Tensile, constant amplitude fatigue, and fracture toughness tests were performed in ambient temperature for both, reference and welded specimens. Microstructure revealed the presence of coarse and fine-grained heat-affected zones. It has been shown that without any post-weld heat treatment, welded specimens maintained their tensile strength properties while their ductility decreased by more than 40%. It was found that the welded specimens had lower fatigue life and this decrease was a function of the applied fatigue maximum stress. A 30% fatigue life decrease was noticed in the high cycle fatigue regime for the welded specimens while this decrease exceeded 50% in the low cycle fatigue regime. Cyclic stress-strain curves showed that Inconel 718 experiences a short period of hardening followed by softening for all fatigue lives. Cyclic fatigue response of welded specimens' exhibited cyclically stable behavior. Finally, a marginal decrease was noticed in the Mode I fracture toughness of the welded specimens.

  17. Laser aided direct metal deposition of Inconel 625 superalloy: Microstructural evolution and thermal stability

    International Nuclear Information System (INIS)

    Dinda, G.P.; Dasgupta, A.K.; Mazumder, J.

    2009-01-01

    Direct metal deposition technology is an emerging laser aided manufacturing technology based on a new additive manufacturing principle, which combines laser cladding with rapid prototyping into a solid freeform fabrication process that can be used to manufacture near net shape components from their CAD files. In the present study, direct metal deposition technology was successfully used to fabricate a series of samples of the Ni-based superalloy Inconel 625. A high power CO 2 laser was used to create a molten pool on the Inconel 625 substrate into which an Inconel 625 powder stream was delivered to create a 3D object. The structure and properties of the deposits were investigated using optical and scanning electron microscopy, X-ray diffraction and microhardness test. The microstructure has been found to be columnar dendritic in nature, which grew epitaxially from the substrate. The thermal stability of the dendritic morphology was investigated in the temperature range 800-1200 deg. C. These studies demonstrate that Inconel 625 is an attractive material for laser deposition as all samples produced in this study are free from relevant defects such as cracks, bonding error and porosity.

  18. Laser aided direct metal deposition of Inconel 625 superalloy: Microstructural evolution and thermal stability

    Energy Technology Data Exchange (ETDEWEB)

    Dinda, G.P., E-mail: dindag@focushope.edu [Center for Advanced Technologies, Focus: HOPE, Detroit, MI 48238 (United States); Center for Laser Aided Intelligent Manufacturing, University of Michigan, Ann Arbor, MI 48109 (United States); Dasgupta, A.K. [Center for Advanced Technologies, Focus: HOPE, Detroit, MI 48238 (United States); Mazumder, J. [Center for Laser Aided Intelligent Manufacturing, University of Michigan, Ann Arbor, MI 48109 (United States)

    2009-05-25

    Direct metal deposition technology is an emerging laser aided manufacturing technology based on a new additive manufacturing principle, which combines laser cladding with rapid prototyping into a solid freeform fabrication process that can be used to manufacture near net shape components from their CAD files. In the present study, direct metal deposition technology was successfully used to fabricate a series of samples of the Ni-based superalloy Inconel 625. A high power CO{sub 2} laser was used to create a molten pool on the Inconel 625 substrate into which an Inconel 625 powder stream was delivered to create a 3D object. The structure and properties of the deposits were investigated using optical and scanning electron microscopy, X-ray diffraction and microhardness test. The microstructure has been found to be columnar dendritic in nature, which grew epitaxially from the substrate. The thermal stability of the dendritic morphology was investigated in the temperature range 800-1200 deg. C. These studies demonstrate that Inconel 625 is an attractive material for laser deposition as all samples produced in this study are free from relevant defects such as cracks, bonding error and porosity.

  19. 7 CFR 601.2 - Functions reserved to the Secretary of Agriculture.

    Science.gov (United States)

    2010-01-01

    ... 7 Agriculture 6 2010-01-01 2010-01-01 false Functions reserved to the Secretary of Agriculture. 601.2 Section 601.2 Agriculture Regulations of the Department of Agriculture (Continued) NATURAL RESOURCES CONSERVATION SERVICE, DEPARTMENT OF AGRICULTURE GENERAL FUNCTIONS § 601.2 Functions reserved to...

  20. Laser beam micro-milling of micro-channels in aerospace alloys

    CERN Document Server

    Ahmed, Naveed; Al-Ahmari, Abdulrahman

    2017-01-01

    This volume is greatly helpful to micro-machining and laser engineers as it offers obliging guidelines about the micro-channel fabrications through Nd:YAG laser beam micro-milling. The book also demonstrates how the laser beam micro-milling behaves when operating under wet conditions (under water), and explores what are the pros and cons of this hybrid technique. From the predictive mathematical models, the readers can easily estimate the resulting micro-channel size against the desired laser parametric combinations. The book considers micro-channels in three highly important research materials commonly used in aerospace industry: titanium alloy Ti-6Al-4V, nickel alloy Inconel 718 and aluminum alloy AA 2024. Therefore, the book is highly practicable in the fields of micro-channel heat exchangers, micro-channel aerospace turbine blades, micro-channel heat pipes, micro-coolers and micro-channel pulsating heat plates. These are frequently used in various industries such as aerospace, automotive, biomedical and m...

  1. Experience with Inconel-625 in cracker service in heavy water plants (Paper No. 5.6)

    International Nuclear Information System (INIS)

    Ramamurthy, C.B.; Paknikar, K.; Bhushan, Sashi

    1992-01-01

    In ammonia based heavy water plants working on monothermal process enriched ammonia is cracked into its individual constituents for further processing. The cracking of ammonia, which is an endothermic process, takes place in cracker tubes filled with a catalyst which are fired inside a furnace. The design pressure of the tube is 160 kg per sq.cm and the design temperature 765degC. Inconel-625 both wrought and cast type meet the requirements in the temperature range of operation of the cracker and therefore Inconel-625 is the best suited material for the cracker design on the basis of stress rupture strength. The experience with Inconel-625 is described. (author). 4 tabs., 1 fig

  2. Chemical interactions between as-received and pre-oxidized Zircaloy-4 and Inconel-718 at high temperatures

    International Nuclear Information System (INIS)

    Hofmann, P.; Markiewicz, M.

    1994-06-01

    Isothermal reaction experiments were performed in the temperature range of 1000 - 1300 C in order to determine the chemical interactions between Zircaloy-4 fuel rod cladding and Inconel-718 spacer grids of Pressurized Water Reactors (PWR) under severe accident conditions. It was not possible to apply even higher temperatures since fast and complete liquefaction of the components occurred as a result of eutectic interactions during heatup. The liquid reaction products formed enhance and accelerate the degradation of the material couples and the fuel elements, respectively. Only small amounts of Inconel are necessary to liquefy large amounts of Zircaloy. Thin oxide layers on the Zircaloy surface delay the beginning of the chemical interactions with Inconel but cannot prevent them. In this work the reaction kinetics have been determined for the system: as-received and pre-oxidized Zircaloy-4/Inconel 718. The interactions can be described by parabolic rate laws; the Arrhenius equations for the various interactions are given. (orig.) [de

  3. Corrosion of nickel-base heat resistant alloys in simulated VHTR coolant helium at very high temperatures

    International Nuclear Information System (INIS)

    Shindo, Masami; Kondo, Tatsuo

    1976-01-01

    A comparative evaluation was made on three commercial nickel-base heat resistant alloys exposed to helium-base atmosphere at 1000 0 C, which contained several impurities in simulating the helium cooled very high temperature nuclear reactor (VHTR) environment. The choice of alloys was made so that the effect of elements commonly found in commercial alloys were typically examined. The corrosion in helium at 1000 0 C was characterized by the sharp selection of thermodynamically unstable elements in the oxidizing process and the resultant intergranular penetration and internal oxidation. Ni-Cr-Mo-W type solution hardened alloy such as Hastelloy-X showed comparatively good resistance. The alloy containing Al and Ti such as Inconel-617 suffered adverse effect in contrast to its good resistance to air oxidation. The alloy nominally composed only of noble elements, Ni, Fe and Mo, such as Hastelloy-B showed least apparent corrosion, while suffered internal oxidation due to small amount of active impurities commonly existing in commercial heats. The results were discussed in terms of selection and improvement of alloys for uses in VHTR and the similar systems. (auth.)

  4. Microstructural evolution during transient liquid phase bonding of Inconel 617 using Ni-Si-B filler metal

    International Nuclear Information System (INIS)

    Jalilian, F.; Jahazi, M.; Drew, R.A.L.

    2006-01-01

    The influence of process parameters on microstructural characteristics of transient liquid phase (TLP) bonded Inconel 617 alloy was investigated. Experiments were carried out at 1065 deg. C using nickel based filler metal (Ni-4.5% Si-3% B) with B as the melting point depressant (MPD) element. Two different thickness of interlayer and various holding times were employed. The influence of these processing parameters on the characteristics of the joint area particularly size, morphology and composition of precipitates was investigated. The presence of MoB, Mo 2 B, M 23 C 6 , TiC, M 23 (B, C) 6 and Ni 3 B precipitates in the diffusion layer and Ni 3 B, Ni 3 Si and Ni 5 Si 2 precipitates in the interlayer at the interface between the base metal and interlayer were demonstrated using electron back scattered diffraction (EBSD), energy dispersive spectrometry (EDS) and TEM

  5. The manufacturing of Stress Corrosion Crack (SCC) on Inconel 600 tube

    International Nuclear Information System (INIS)

    Bae, Seunggi; Bak, Jaewoong; Kim, Seongcheol; Lee, Sangyul; Lee, Boyoung

    2014-01-01

    The Stress Corrosion Crack (SCC), taken a center stage in recently accidents about nuclear power plants, is one of the environmentally induced cracking occurred when a metallic structure under tensile stress is exposed to corrosive environment. In this study, the SCC was manufactured in the simulated corrosive environmental conditions on Inconel 600 tube that widely applied in the nuclear power plants. The tensile stress which is one of the main factors to induce SCC was given by GTAW welding in the inner surface of the specimen. The corrosive environment was simulated by using the sodium hydroxide (NaOH) and sodium sulfide (Na 2 S). In this study, SCC was manufactured in the simulated corrosive environmental conditions with Inconel 600 tube that widely applied in the nuclear power plants. 1) The SCC was manufactured on Inconel 600 tube in simulated operational environments of nuclear power plants. In the experiment, the welding heat input which is enough to induce the cracking generated the SCC near the welding bead. So, in order to prevent the SCC, the residual stress on structure should be relaxed. 2) The branch-type cracking was detected

  6. Design, Development and Testing of Inconel Alloy IN718 Spherical Gas Bottle for Oxygen Storage

    Science.gov (United States)

    Chenna Krishna, S.; Agilan, M.; Sudarshan Rao, G.; Singh, Satish Kumar; Narayana Murty, S. V. S.; Venkata Narayana, Ganji; Beena, A. P.; Rajesh, L.; Jha, Abhay K.; Pant, Bhanu

    2017-11-01

    This paper describes the details of design, manufacture and testing of 200 mm diameter spherical gas bottle of Inconel 718 (IN718) with nominal wall thickness of 2.3 mm. Gas bottle was designed for the specified internal pressure loading with a thickness of 2.9 mm at the circumferential weld which was brought down to 2.3 mm at the membrane locations. Hemispherical forgings produced through closed-die hammer forging were machined and electron beam welded to produce a spherical gas bottle. Duly welded gas bottle was subjected to standard aging treatment to achieve the required tensile strength. Aged gas bottle was inspected for dimensions and other stringent quality requirements using various nondestructive testing techniques. After inspection, gas bottle was subjected to pressure test for maximum expected operating pressure and proof pressure of 25 and 37.5 MPa, respectively. Strain gauges were bonded at different locations on the gas bottle to monitor the strains during the pressure test and correlated with the predicted values. The predicted strain matched well with the experimental strain confirming the design and structural integrity.

  7. Investigation on Surface Roughness of Inconel 718 in Photochemical Machining

    Directory of Open Access Journals (Sweden)

    Nitin D. Misal

    2017-01-01

    Full Text Available The present work is focused on estimating the optimal machining parameters required for photochemical machining (PCM of an Inconel 718 and effects of these parameters on surface topology. An experimental analysis was carried out to identify optimal values of parameters using ferric chloride (FeCl3 as an etchant. The parameters considered in this analysis are concentration of etchant, etching time, and etchant temperature. The experimental analysis shows that etching performance as well as surface topology improved by appropriate selection of etching process parameters. Temperature of the etchant found to be dominant parameter in the PCM of Inconel 718 for surface roughness. At optimal etching conditions, surface roughness was found to be 0.201 μm.

  8. The influence of microstructure and operating temperature on the fatigue endurance of hot forged Inconel{sup ®} 718 components

    Energy Technology Data Exchange (ETDEWEB)

    Maderbacher, H., E-mail: hermann.maderbacher@unileoben.ac.at [Chair of Mechanical Engineering, Montanuniversität Leoben, Franz-Josef-Straße 18, 8700 Leoben (Austria); Oberwinkler, B., E-mail: bernd.oberwinkler@bohler-forging.com [Böhler Schmiedetechnik GmbH and Co KG, Mariazellerstraße 25, 8605 Kapfenberg (Austria); Gänser, H.-P., E-mail: hans-peter.gaenser@mcl.at [Materials Center Leoben Forschung GmbH, Roseggerstraße 12, 8700 Leoben (Austria); Tan, W., E-mail: wen.tan@unileoben.ac.at [Chair of Mechanical Engineering, Montanuniversität Leoben, Franz-Josef-Straße 18, 8700 Leoben (Austria); Rollett, M., E-mail: mathias.rollett@stud.unileoben.ac.at [Chair of Mechanical Engineering, Montanuniversität Leoben, Franz-Josef-Straße 18, 8700 Leoben (Austria); Stoschka, M., E-mail: michael.stoschka@stud.unileoben.ac.at [Chair of Mechanical Engineering, Montanuniversität Leoben, Franz-Josef-Straße 18, 8700 Leoben (Austria)

    2013-11-15

    The dependence of the fatigue behavior of hot-forged Inconel{sup ®} 718 aircraft components on the operating temperature and the material microstructure is investigated. To this purpose, possible correlations between a variety of tested microstructural parameters and the results from low-cycle fatigue (LCF) testing are analyzed using statistical methods. To identify the prevailing damage mechanisms, failure analyses are carried out on specimens tested at different temperatures. Optical and scanning electron microscopy are used for the inspection of surface crack networks and of the final fracture surface. In addition, energy dispersive X-ray (EDX) analyses are performed at the crack initiation sites to track down possible accumulations of alloying elements. The results are critically reviewed and used to propose a temperature and microstructure dependent fatigue model for predicting LCF ε⧸N-curves.

  9. Measurements of emissivities on JT-60 first wall materials (inconel 625, Mo, TiC-coated Mo)

    International Nuclear Information System (INIS)

    Nakamura, Hiroo; Shimizu, Masatsugu; Makino, Toshiro; Kunitomo, Takeshi.

    1985-02-01

    To evaluate heat removal performance of JT-60 first wall, emissivities and reflectivities on Inconel 625, Mo, TiC coated Mo with optically smooth surface and actual surface are measured at temperature from a room temperature to 1300 K. Spectra are measured in the rnage of wave lengthes from 0.34 μm to 20 μm. Actual surfaces are machined/pickled surfaces for Inconel 625, electro-polished surfaces for molybdenum, and as-coated surfaces for TiC-coated molybdenum. Results of Inconel 625 and molybdenum with oplically smooth surfaces are examined by a two-electrons-type dispersion model of optical constants. Electronic constants of the equation are given and formulated in order to correlates the macroscopic properties of the radiative heat transfer. Total emissivities, obtained from the spectral emissivities of optically smooth surface, are 0.13(RT) -- 0.21(1300 K) for Inconel 625, 0.035(RT) -- 0.18(1300 K) for Mo, and 0.053(RT) for TiC-coated Mo. Moreover, total emissivities of the actual surface at a room temperature are 0.35(Inconel 625), 0.124(Mo), and 0.073(TiC-coated Mo). Large dependence of the emissivities on temperature and wave length shows that the model including these dependences is necessary for an accurate evaluation of the radiative heat transfer. (author)

  10. Study on the machinability characteristics of superalloy Inconel 718 during high speed turning

    International Nuclear Information System (INIS)

    Thakur, D.G.; Ramamoorthy, B.; Vijayaraghavan, L.

    2009-01-01

    The present paper is an attempt of an experimental investigation on the machinability of superalloy, Inconel 718 during high speed turning using tungsten carbide insert (K20) tool. The effect of machining parameters on the cutting force, specific cutting pressure, cutting temperature, tool wear and surface finish criteria were investigated during the experimentation. The machining parameters have been optimized by measuring forces. The effect of machining parameters on the tool wear was examined through SEM micrographs. During high speed turning acoustic emission signal were collected and analyzed to understand the effect of cutting parameters during online. The research work findings will also provide useful economic machining solution by utilizing economical tungsten carbide tooling during high speed processing of Inconel 718, which is otherwise usually machined by costly PCD or CBN tools. The present approach and results will be helpful for understanding the machinability of Inconel 718 during high speed turning for the manufacturing engineers

  11. Performance and Thrust-to-Weight Optimization of the Dual-Expander Aerospike Nozzle Upper Stage Rocket Engine

    Science.gov (United States)

    2012-06-01

    for chamber cooling jacket, structural jacket, and O2 plumbing INCONEL ® 625 (Annealed) Aluminum 7075 T6 Not compatible with O2 or H2 / Useable for...Special Metals. INCONEL (R) alloy 625 . Publication Number SMC-063. Special Metals Corporation, 2006. [20] Haynes International. "Heat-Resistant Alloy...Copper (C17000 TH04) Oxygen-Free Copper (C10100 1180 Temper) Cobalt (Forged Electrolytic) INCONEL ® 718 (Annealed & Aged) Compatible with O2 / Useable

  12. Aluminizing of steel 316L and the nickel-base alloy inconel 625 and followed by a high-temperature oxidation process

    International Nuclear Information System (INIS)

    Skokanova, P.; Glasbrenner, H.; Zimmermann, H.

    1995-03-01

    The supercritical water oxidation process of hazardous waste has to be carried out in a reactor which is resistant against corrosion and high pressure and temperature. Pressure tube materials are coated for protection against corrosion. In this work, the reactor materials Inconel 625 and steel 316L have been powder pack aluminized. These coated specimens were subsequently oxidized. Powder mixtures of different composition were tested, time and temperature of the coating and the oxidation processes were varied. Good results were obtained on the steel 316L in respect to thickness of the layer, composition, and adherence on the steel. (orig.)

  13. 48 CFR 15.601 - Definitions.

    Science.gov (United States)

    2010-10-01

    ... AND CONTRACT TYPES CONTRACTING BY NEGOTIATION Unsolicited Proposals 15.601 Definitions. As used in this subpart— Advertising material means material designed to acquaint the Government with a...

  14. Tensile Properties and Microstructure of Inconel 718 Fabricated with Electron Beam Freeform Fabrication (EBF(sup 3))

    Science.gov (United States)

    Bird, R. Keith; Hibberd, Joshua

    2009-01-01

    Electron beam freeform fabrication (EBF3) direct metal deposition processing was used to fabricate two Inconel 718 single-bead-width wall builds and one multiple-bead-width block build. Specimens were machined to evaluate microstructure and room temperature tensile properties. The tensile strength and yield strength of the as-deposited material from the wall and block builds were greater than those for conventional Inconel 718 castings but were less than those for conventional cold-rolled sheet. Ductility levels for the EBF3 material were similar to those for conventionally-processed sheet and castings. An unexpected result was that the modulus of the EBF3-deposited Inconel 718 was significantly lower than that of the conventional material. This low modulus may be associated with a preferred crystallographic orientation resultant from the deposition and rapid solidification process. A heat treatment with a high solution treatment temperature resulted in a recrystallized microstructure and an increased modulus. However, the modulus was not increased to the level that is expected for Inconel 718.

  15. 48 CFR 49.601 - Notice of termination for convenience.

    Science.gov (United States)

    2010-10-01

    ... 48 Federal Acquisition Regulations System 1 2010-10-01 2010-10-01 false Notice of termination for convenience. 49.601 Section 49.601 Federal Acquisition Regulations System FEDERAL ACQUISITION REGULATION... termination for convenience. (See 49.402-3(g) for notice of termination for default.) ...

  16. High-Temperature Tensile Strength of Al10Co25Cr8Fe15Ni36Ti6 Compositionally Complex Alloy (High-Entropy Alloy)

    Science.gov (United States)

    Daoud, H. M.; Manzoni, A. M.; Wanderka, N.; Glatzel, U.

    2015-06-01

    Homogenizing at 1220°C for 20 h and subsequent aging at 900°C for 5 h and 50 h of a novel Al10Co25Cr8Fe15Ni36Ti6 compositionally complex alloy (high-entropy alloy) produces a microstructure consisting of an L12 ordered γ' phase embedded in a face-centered cubic solid-solution γ matrix together with needle-like B2 precipitates (NiAl). The volume fraction of γ' phase is ~46% and of needle-like B2 precipitates database; Thermo-Calc Software, Stockholm, Sweden). The high-temperature tensile tests were carried out at room temperature, 600°C, 700°C, 800°C, and 1000°C. The tensile strength as well as the elongation to failure of both heat-treated specimens is very high at all tested temperatures. The values of tensile strength has been compared with literature data of well-known Alloy 800H and Inconel 617, and is discussed in terms of the observed microstructure.

  17. Fiber laser welding of nickel based superalloy Inconel 625

    Science.gov (United States)

    Janicki, Damian M.

    2013-01-01

    The paper describes the application of single mode high power fiber laser (HPFL) for the welding of nickel based superalloy Inconel 625. Butt joints of Inconel 625 sheets 0,8 mm thick were laser welded without an additional material. The influence of laser welding parameters on weld quality and mechanical properties of test joints was studied. The quality and mechanical properties of the joints were determined by means of tensile and bending tests, and micro hardness tests, and also metallographic examinations. The results showed that a proper selection of laser welding parameters provides non-porous, fully-penetrated welds with the aspect ratio up to 2.0. The minimum heat input required to achieve full penetration butt welded joints with no defect was found to be 6 J/mm. The yield strength and ultimate tensile strength of the joints are essentially equivalent to that for the base material.

  18. Effect of Heat Treatment Parameters on the Microstructure and Properties of Inconel-625 Superalloy

    Science.gov (United States)

    Sukumaran, Arjun; Gupta, R. K.; Anil Kumar, V.

    2017-07-01

    Inconel-625 is a solid solution-strengthened alloy used for long-duration applications at high temperatures and moderate stresses. Different heat treatment cycles (temperatures of 625-1025 °C and time of 2-6 h) have been studied to obtain optimum mechanical properties suitable for a specific application. It has been observed that room temperature strength and, hardness decreased and ductility increased with increase in heat treatment temperature. The rate of change of these properties is found to be moderate for the samples heat-treated up to 850 °C, and thereafter, it increases rapidly. It is attributed to the microstructural changes like dissolution of carbides, recrystallization and grain growth. Microstructures are found to be predominantly single-phase austenitic with the presence of fine alloy carbides. The presence of twins is observed in samples heat-treated at lower temperature, which act as nucleation sites for recrystallization at 775 °C. Beyond 850 °C, the role of carbides present in the matrix is subsided by the coarsening of recrystallized grains and finally at 1025 °C, significant dissolution of carbide results in substantial reduction in strength and increase in ductility. Elongation to an extent of >71% has been obtained in sample heat-treated at 1025 °C indicating excellent tendency for cold workability. Failure of heat-treated specimens is found to be mainly due to carbide particle-matrix decohesion which acts as locations for crack initiation.

  19. 45 CFR 60.1 - The National Practitioner Data Bank.

    Science.gov (United States)

    2010-10-01

    ... 45 Public Welfare 1 2010-10-01 2010-10-01 false The National Practitioner Data Bank. 60.1 Section 60.1 Public Welfare DEPARTMENT OF HEALTH AND HUMAN SERVICES GENERAL ADMINISTRATION NATIONAL PRACTITIONER DATA BANK FOR ADVERSE INFORMATION ON PHYSICIANS AND OTHER HEALTH CARE PRACTITIONERS General...

  20. Structural Performance of Inconel 625 Superalloy Brazed Joints

    Science.gov (United States)

    Chen, Jianqiang; Demers, Vincent; Cadotte, Eve-Line; Turner, Daniel; Bocher, Philippe

    2017-02-01

    The purpose of this work was to investigate tensile and fatigue behaviors of Inconel 625 superalloy brazed joints after transient liquid-phase bonding process. Brazing was performed in a vacuum furnace using a nickel-based filler metal in a form of paste to join wrought Inconel 625 plates. Mechanical tests were carried out on single-lap joints under various lap distance-to-thickness ratios. The fatigue crack initiation and crack growth modes were examined via metallographic analysis, and the effect of local stress on fatigue life was assessed by finite element simulations. The fatigue results show that fatigue strength and endurance limit increase with overlap distance, leading to a relatively large scatter of results. Fatigue cracks nucleated in the high-stressed region of the weld fillets from brittle eutectic phases or from internal brazing cavities. The present work proposes to rationalize the results by using the local stress at the brazing fillet. When using this local stress, all fatigue-obtained results find themselves on a single S- N curve, providing a design curve for any joint configuration in fatigue solicitation.

  1. Microstructural evolution during transient liquid phase bonding of Inconel 617 using Ni-Si-B filler metal

    Energy Technology Data Exchange (ETDEWEB)

    Jalilian, F. [McGill University, Department of Mining, Metals and Materials Engineering, 3610 University St., M.H. Wong Building, Montreal Que., H3A 2B2 (Canada); Jahazi, M. [Aerospace Manufacturing Technology Center, National Research Council of Canada (Canada); Drew, R.A.L. [McGill University, Department of Mining, Metals and Materials Engineering, 3610 University St., M.H. Wong Building, Montreal Que., H3A 2B2 (Canada)]. E-mail: robin.drew@mcgill.ca

    2006-05-15

    The influence of process parameters on microstructural characteristics of transient liquid phase (TLP) bonded Inconel 617 alloy was investigated. Experiments were carried out at 1065 deg. C using nickel based filler metal (Ni-4.5% Si-3% B) with B as the melting point depressant (MPD) element. Two different thickness of interlayer and various holding times were employed. The influence of these processing parameters on the characteristics of the joint area particularly size, morphology and composition of precipitates was investigated. The presence of MoB, Mo{sub 2}B, M{sub 23}C{sub 6}, TiC, M{sub 23}(B, C){sub 6} and Ni{sub 3}B precipitates in the diffusion layer and Ni{sub 3}B, Ni{sub 3}Si and Ni{sub 5}Si{sub 2} precipitates in the interlayer at the interface between the base metal and interlayer were demonstrated using electron back scattered diffraction (EBSD), energy dispersive spectrometry (EDS) and TEM.

  2. Microstructure and hardness studies of Inconel 718 manufactured by selective laser melting before and after solution heat treatment

    International Nuclear Information System (INIS)

    Tucho, Wakshum M.; Cuvillier, Priscille; Sjolyst-Kverneland, Atle; Hansen, Vidar

    2017-01-01

    The microstructure of Additive Manufactured (AM) Inconel 718 in general and Selective Laser Melting (SLM), in particular is different from the material produced by conventional methods due to the rapid solidification process associated with the former. As a result, the widely adapted standard solution heat treatment temperature (<1100 °C) for conventional material is found to be not high enough for materials fabricated with SLM method in order to dissolve Laves and other microsegregated phases for releasing the ageing constituents (Nb, Ti, Al) sufficiently into the alloy matrix. In this study, sample of Inconel 718 fabricated with SLM method were solution heat-treated to 1100 °C or 1250 °C at different hold times to investigate the dissolution of macro- and micro-segregated precipitates. Investigations of microstructure and segregation in as-printed and solution heat-treated states have been studied using Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM) and Optical Microscopy (OM). Measurement of material hardness was performed with Vickers hardness tests. The microstructure of the as-printed parts exhibit non-columnar grains, but contain well-shaped columnar/cellular sub-grains. The intergranular boundaries are decorated with high density of dislocations and segregated particles. Tremendous stress relief and grain coarsening were observed with solution heat treatment. In particular, at 1250 °C annealing, the sub-grains, including precipitates and dislocation networks along the sub-grain boundaries, were entirely dissolved. However, the 1100/1250 °C solution heat treatment scheme could not dissolve microsegregated precipitates and carbides completely. Details of the analysis on microstructure, dissolution of precipitates and hardness are presented.

  3. Microstructure and hardness studies of Inconel 718 manufactured by selective laser melting before and after solution heat treatment

    Energy Technology Data Exchange (ETDEWEB)

    Tucho, Wakshum M., E-mail: wakshum.m.tucho@uis.no [Department of Mechanical and Structural Engineering and Materials Science, University of Stavanger, N-4036 Stavanger (Norway); Cuvillier, Priscille [Department of Mechanical and Structural Engineering and Materials Science, University of Stavanger, N-4036 Stavanger (Norway); Sjolyst-Kverneland, Atle [Roxar/Emerson Process Management, POB 112, 4065 Stavanger (Norway); Hansen, Vidar [Department of Mechanical and Structural Engineering and Materials Science, University of Stavanger, N-4036 Stavanger (Norway)

    2017-03-24

    The microstructure of Additive Manufactured (AM) Inconel 718 in general and Selective Laser Melting (SLM), in particular is different from the material produced by conventional methods due to the rapid solidification process associated with the former. As a result, the widely adapted standard solution heat treatment temperature (<1100 °C) for conventional material is found to be not high enough for materials fabricated with SLM method in order to dissolve Laves and other microsegregated phases for releasing the ageing constituents (Nb, Ti, Al) sufficiently into the alloy matrix. In this study, sample of Inconel 718 fabricated with SLM method were solution heat-treated to 1100 °C or 1250 °C at different hold times to investigate the dissolution of macro- and micro-segregated precipitates. Investigations of microstructure and segregation in as-printed and solution heat-treated states have been studied using Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM) and Optical Microscopy (OM). Measurement of material hardness was performed with Vickers hardness tests. The microstructure of the as-printed parts exhibit non-columnar grains, but contain well-shaped columnar/cellular sub-grains. The intergranular boundaries are decorated with high density of dislocations and segregated particles. Tremendous stress relief and grain coarsening were observed with solution heat treatment. In particular, at 1250 °C annealing, the sub-grains, including precipitates and dislocation networks along the sub-grain boundaries, were entirely dissolved. However, the 1100/1250 °C solution heat treatment scheme could not dissolve microsegregated precipitates and carbides completely. Details of the analysis on microstructure, dissolution of precipitates and hardness are presented.

  4. Micro-structure and Mechanical Properties of Nano-TiC Reinforced Inconel 625 Deposited using LAAM

    Science.gov (United States)

    Bi, G.; Sun, C. N.; Nai, M. L.; Wei, J.

    In this paper, deposition of Ni-base Inconel 625 mixed with nano-TiC powders using laser aided additive manufacturing (LAAM) was studied. Micro-structure and mechanical properties were intensively investigated. The results showed that nano-size TiC distributed uniformly throughout the Ni- matrix. Inconel 625 can be reinforced by the strengthened grain boundaries with nano-size TiC. Improved micro-hardness and tensile properties were observed.

  5. Self-powered neutron flux detector assembly

    International Nuclear Information System (INIS)

    Allan, C.J.; McIntyre, I.L.

    1980-01-01

    A self-powered neutron flux detector has both the central emitter electrode and its surrounding collector electrode made of inconel 600. The lead cables may also be made of inconel. Other nickel alloys, or iron, nickel, titamium, chromium, zirconium or their alloys may also be used for the electrodes

  6. 34 CFR 75.601 - Applicant's assessment of environmental impact.

    Science.gov (United States)

    2010-07-01

    ... 34 Education 1 2010-07-01 2010-07-01 false Applicant's assessment of environmental impact. 75.601... Conditions Must Be Met by a Grantee? Construction § 75.601 Applicant's assessment of environmental impact. An applicant shall include with its application its assessment of the impact of the proposed construction on...

  7. Predictive Analysis for the Thermal Diffusion of the Plasma-Assisted Machining of Superalloy Inconel-718 Based on Exponential Smoothing

    Directory of Open Access Journals (Sweden)

    Chen Shao-Hsien

    2018-01-01

    Full Text Available Nickel base and titanium base materials have been widely applied to engines in aerospace industry, and these engines are essential components of airplanes. The machining characteristics of aerospace materials may cause machining cutters to be worn down in a short time and thus reduce the accuracy of processing. The plasma-assisted machining adopted in the research is a kind of the complex machining method. In the cases of nickel base and titanium base alloys, the method can heat workpieces in an extremely short duration to soften the materials for the ease of cutting so that the cutting force, cutter wear, and machining cost will all be reduced. The research adopted plasma heating to soften parts of the materials and aimed to explore the heating of nickel base alloy. The temperature variation of the materials was investigated and measured by adjusting the current and feed velocity. Moreover, Inconel-718 superalloy was adopted for the comparison with nickel base alloy for the observation of the influence and change brought by heat, and the method of exponential smoothing was adopted to conduct the prediction and analysis of thermal diffusion for understanding the influence and change brought by electric current on nickel base materials. Finally, given the current from 20 A to 80 A and feed velocity from 1,000 mm/min to 3,000 mm/min, the influence of thermal diffusion was investigated and the related model was built.

  8. The Corrosion Behavior of Nickel and Inconel 600 in Sodium Hydroxide and Hydrochloric Acid Solution at 280 .deg. C

    International Nuclear Information System (INIS)

    Lee, Ihh Chong; Suk, Tae Won

    1980-01-01

    The corrosion behavior of nickel and Inconel 600 has been investigated by the weight change measurement method at pH ranges 3∼13 of the solution. The specimens were exposed to aqueous solutions in a static autoclave at 280 .deg. C for 210 hours. The pH of the solutions was adjusted by hydrochloric acid and sodium hydroxide and the dissolved oxygen concentration was fixed as 10 ppb by using pure nitrogen gas. Weight loss of Inconel 600 was much less than that of nickel over the tested pH ranges. At pH 9.5, nickel and Inconel 600 showed the minimum weight loss phenomenon and the values of weight loss were 1.5mg/dm 2 and 0.9mg/dm 2 , respectively. Microscopic examination showed that nickel surface was attacked uniformly, whereas Inconel 600 surface was not greatly

  9. Evaluation of candidate alloys for the construction of metal flex hoses in the STS launch environment

    Science.gov (United States)

    Ontiveros, Cordelia

    1988-01-01

    Various vacuum jacketed cryogenic supply lines at the Shuttle launch site use convoluted flexible expansion joints. The atmosphere at the launch site has a very high salt content, and during a launch, fuel combustion products include hydrochloric acid. This extremely corrosive environment has caused pitting corrosion failure in the flex hoses, which were made of 304L stainless steel. A search was done to find a more corrosion resistant replacement material. This study focused on 19 metal alloys. Tests which were performed include electrochemical corrosion testing, accelerated corrosion testing in a salt fog chamber, long term exposure at the beach corrosion testing site, and pitting corrosion tests in ferric chloride solution. Based on the results of these tests, the most corrosion resistant alloys were found to be (in order) Hastelloy C-22, Inconel 625, Hastelloy C-276, Hastelloy C-4, and Inco Alloy G-3. Of these top five alloys, the Hastelloy C-22 stands out as being the best of those tested for this application.

  10. Microstructural and Mechanical Study of Inconel 625 – Tungsten Carbide Composite Coatings Obtained by Powder Laser Cladding

    Directory of Open Access Journals (Sweden)

    Huebner J.

    2017-06-01

    Full Text Available This study focuses on the investigation of fine (~0.54 μm tungsten carbide particles effect on structural and mechanical properties of laser cladded Inconel 625-WC composite. Three powder mixtures with different Inconel 625 – WC weight ratio (10, 20 and 30 weight % of WC were prepared. Coatings were made using following process parameters: laser beam diameter ø ≈ 500 μm, powder feeder rotation speed – 7 m/min, scanning velocity – 10 m/min, laser power – 220 W changed to 320 W, distance between tracks – 1 mm changed to 0.8 mm. Microstructure and hardness were investigated. Coatings produced by laser cladding were crack and pore free, chemically and structurally homogenous. High cooling rate during cladding process resulted in fine microstructure of material. Hardness improved with addition of WC from 396.3 ±10.5 HV for pure Inconel 625, to 469.9 ±24.9 HV for 30 weight % of WC. Tungsten carbide dissolved in Inconel 625 which allowed formation of intergranular eutectic that contains TCP phases.

  11. The Corrosion Rate Measurement of Inconel 690 on High Temperature andPressure by Using CMS100

    International Nuclear Information System (INIS)

    Sriyono; Febrianto

    2000-01-01

    The corrosion rate measurement of Inconel 690 on high temperature andpressure had been done. By using an Autoclave, pressure and temperature canbe simulated. The environment of this experiment is 0.1 ppm of chloridesolution, which permit to dissolved in secondary cooling of steam generator.The corrosion rate measurement was done on temperature between 150 o C and230 o C with step 10 o C. Pressure experiment is the pressure, which occurredin Autoclave. Corrosion rate is measured by CMS100. From the Tafel analysis,corrosion rate of Inconel 690 linearity increased from 6.548 x 10 -5 mpy to4.331 x 10 -4 mpy. It concludes that Inconel 690 is resist on corrosionenvironment, so it's most using on the fabrication of steam generator tubeson the advanced power plant. (author)

  12. 26 CFR 601.102 - Classification of taxes collected by the Internal Revenue Service.

    Science.gov (United States)

    2010-04-01

    ... Rules § 601.102 Classification of taxes collected by the Internal Revenue Service. (a) Principal... 26 Internal Revenue 20 2010-04-01 2010-04-01 false Classification of taxes collected by the Internal Revenue Service. 601.102 Section 601.102 Internal Revenue INTERNAL REVENUE SERVICE, DEPARTMENT OF...

  13. 5 CFR 2604.601 - Electronic posting and submission of annual OGE FOIA report.

    Science.gov (United States)

    2010-01-01

    ... 5 Administrative Personnel 3 2010-01-01 2010-01-01 false Electronic posting and submission of annual OGE FOIA report. 2604.601 Section 2604.601 Administrative Personnel OFFICE OF GOVERNMENT ETHICS... FINANCIAL DISCLOSURE REPORTS Annual OGE FOIA Report § 2604.601 Electronic posting and submission of annual...

  14. Study of superficial films and of electrochemical behaviour of some nickel base alloys and titanium base alloys in solution representation of granitic, argillaceous and salted ground waters

    International Nuclear Information System (INIS)

    Quang, K.V.; Da Cunha Belo, M.; Benabed, M.S.; Bourelier, F.; Jallerat, N.; Pari, F.L.

    1985-01-01

    The corrosion behaviour of the stainless steels 304, 316 Ti, 25Cr-20Ni-Mo-Ti, nickel base alloys Hastelloy C4, Inconel 625, Incoloy 800, Ti and Ti-0.2% Pd alloy has been studied in the aerated or deaerated solutions at 20 0 C and 90 0 C whose compositions are representative of interstitial ground waters: granitic or clay waters or salt brine. The electrochemical techniques used are voltametry, polarization resistance and complexe impedance measurements. Electrochemical data show the respective influence of the parameters such as temperature, solution composition and dissolved oxygen, addition of soluble species chloride, fluoride, sulfide and carbonates, on which depend the corrosion current density, the passivation and the pitting potential. The inhibition efficiency of carbonate and bicarbonate activities against pitting corrosion is determined. In clay water at 90 0 C, Ti and Ti-Pd show very high passivation aptitude and a broad passive potential range. Alloying Pd increases cathodic overpotential and also transpassive potential. It makes the alloy less sensitive to the temperature effect. Optical Glow Discharge Spectra show three parts in the composition depth profiles of surface films on alloys. XPS and SIMS spectrometry analyses are also carried out. Electron microscopy observation shows that passive films formed on Ti and Ti-Pd alloy have amorphous structure. Analysis of the alloy constituents dissolved in solutions, by radioactivation in neutrons, gives the order of magnitude of the Ni base alloy corrosion rates in various media. It also points out the preferential dissolution of alloying iron and in certain cases of chromium

  15. Effects of post-weld heat treatment on microstructure and mechanical properties of TLP bonded Inconel718 superalloy

    International Nuclear Information System (INIS)

    Cao, J.; Wang, Y.F.; Song, X.G.; Li, C.; Feng, J.C.

    2014-01-01

    Transient liquid phase bonding of Inconel718 superalloy was carried out using a commercial Ni–Cr–Si–B amorphous interlayer. The interfacial microstructure of Inconel718 joints was analyzed by a scanning electron microscope and a transmission electron microscope. In particular, the effects of post-weld heat treatment on the interfacial microstructure and joining properties of Inconel718 joints were investigated in detail. The results showed that the precipitation of second phases in joints induced by post-weld heat treatment were beneficial to the improvement of joint properties. A tensile strength of 1130 MPa with an elongation percentage of 7% was achieved for a sample bonded at 1050 °C/60 min+1180 °C/60 min followed by the post-weld heat treatment

  16. 1 Molar concentration hydrofluoric acid effect at 400 C in the corrosion resistance of alloys containing nickel

    International Nuclear Information System (INIS)

    Contreras P, H.

    1992-01-01

    Corrosion rate for pure nickel, Inconel 600 and Monel alloys in a 1 Molar hydrofluoric acid solution at a 40 0 C temperature were determined. For contrasting purposes both SAE 304 SS and SAE 316 SS were included. As expected these Stainless Steels do not show good corrosion performance in the solution used. Several expressions correlating the weight and thickness loss v/s time were obtained. In the particular case of Monel, up to 2.021 hours, two expressions for the weight loss and three expressions for the thickness loss were obtained with a close to 1,0 correlation coefficient value. The Monel showed the best overall corrosion performance among the tested alloys. (author)

  17. 76 FR 41653 - Airworthiness Directives; Bombardier, Inc. Model CL-600-2A12 (CL-601) and CL-600-2B16 (CL-601-3A...

    Science.gov (United States)

    2011-07-15

    ... p.m., Monday through Friday, except Federal holidays. The AD docket contains the NPRM, the.... Model CL-600-2A12 (CL-601) airplanes, serial numbers 3001 through 3066 inclusive on which Bombardier... Variants) airplanes, serial numbers 5001 through 5194 inclusive on which Bombardier Service Bulletin 601...

  18. 47 CFR 64.601 - Definitions and provisions of general applicability.

    Science.gov (United States)

    2010-10-01

    ...) Text telephone (TTY). A machine that employs graphic communication in the transmission of coded signals... applicability. 64.601 Section 64.601 Telecommunication FEDERAL COMMUNICATIONS COMMISSION (CONTINUED) COMMON... Communication by wire or radio as defined in section 3(h) of the Communications Act of 1934, as amended (the Act...

  19. 34 CFR 601.12 - Use of institution and lender name.

    Science.gov (United States)

    2010-07-01

    ... such institution or organization, in the marketing of private education loans to students attending... 34 Education 3 2010-07-01 2010-07-01 false Use of institution and lender name. 601.12 Section 601.12 Education Regulations of the Offices of the Department of Education (Continued) OFFICE OF...

  20. Lubricating Properties of Ceramic-Bonded Calcium Fluoride Coatings on Nickel-Base Alloys from 75 to 1900 deg F

    Science.gov (United States)

    Sliney, Harold E.

    1962-01-01

    The endurance life and the friction coefficient of ceramic-bonded calcium fluoride (CaF2) coatings on nickel-base alloys were determined at temperatures from 75 F to 1900 F. The specimen configuration consisted of a hemispherical rider (3/16-in. rad.) sliding against the flat surface of a rotating disk. Increasing the ambient temperature (up to 1500 F) or the sliding velocity generally reduced the friction coefficient and improved coating life. Base-metal selection was critical above 1500 F. For instance, cast Inconel sliding against coated Inconel X was lubricated effectively to 1500 F, but at 1600 F severe blistering of the coatings occurred. However, good lubrication and adherence were obtained for Rene 41 sliding against coated Rene 41 at temperatures up to 1900 F; no blisters developed, coating wear life was fairly good, and the rider wear rate was significantly lower than for the unlubricated metals. Friction coefficients were 0.12 at 1500 F, 0.15 at 1700 F, and 0.17 at 1800 F and 1900 F. Because of its ready availability, Inconel X appears to be the preferred substrate alloy for applications in which the temperature does not exceed 1500 F. Rene 41 would have to be used in applications involving higher temperatures. Improved coating life was derived by either preoxidizing the substrate metals prior to the coating application or by applying a very thin (less than 0.0002 in.) burnished and sintered overlay to the surface of the coating. Preoxidation did not affect the friction coefficient. The overlay generally resulted in a higher friction coefficient than that obtained without the overlay. The combination of both modifications resulted in longer coating life and in friction coefficients intermediate between those obtained with either modification alone.

  1. 21 CFR 601.43 - Withdrawal procedures.

    Science.gov (United States)

    2010-04-01

    ... LICENSING Accelerated Approval of Biological Products for Serious or Life-Threatening Illnesses § 601.43... the required postmarketing study with due diligence; (3) Use after marketing demonstrates that...

  2. The machinability of nickel-based alloys in high-pressure jet assisted (HPJA turning

    Directory of Open Access Journals (Sweden)

    D. Kramar

    2013-10-01

    Full Text Available Due to their mechanical, thermal and chemical properties, nickel-based alloys are generally included among materials that are hard to machine. An experimental study has been performed to investigate the capabilities of conventional and high-pressure jet assisted (HPJA turning of hard-to-machine materials, namely Inconel 718. The capabilities of different hard turning procedures are compared by means of chip breakability. The obtained results show that HPJA method offers a significant increase in chip breakability, under the same cutting conditions (cutting speed, feed rate, depth of cut.

  3. 48 CFR 25.601 - Definitions.

    Science.gov (United States)

    2010-10-01

    ... 25.601 Definitions. As used in this subpart— Domestic construction material means the following: (1... construction material other than a domestic construction material. Manufactured construction material means any..., mains, power lines, pumping stations, heavy generators, railways, airports, terminals, docks, piers...

  4. Applicability of eddy current inversion techniques to the sizing of defects in Inconel welds of BWR internals

    International Nuclear Information System (INIS)

    Yusa, Noritaka; Janousek, Ladislav; Rebican, Mihai; Chen, Zhenmao; Miya, Kenzo; Machida, Eiji

    2004-01-01

    This paper evaluates the applicability of eddy current inversion techniques to the sizing of defects in Inconel welds with rough surfaces. For this purpose, a plate Inconel weld specimen, which models the welding of a stub tube in a boiling water nuclear reactor, is fabricated, and artificial notches machined into the specimen. Eddy current inspections using six probes in weld inspection evaluated. It is revealed that if suitable probes are applied, an Inconel weld does not provide large noise signals in eddy current inspections even though the surface of the weld is rough. Finally, reconstruction of the notches are performed using eddy current signals measured with the use of the uniform eddy current probe that showed the best results among the six probes in the inspection. A simplified configuration is proposed in order to consider the complicated configuration of the welded specimen in numerical simulations. While reconstructed profiles of the notches are slightly larger than the true profiles, quite good agreements are obtained in spite of the simple approximation of the configuration, which reveals that eddy current testing would be an efficient non-destructive testing method for the sizing of defects in Inconel welds. (author)

  5. The speed of growth of the gamma phase comes prime in nickel based alloys

    International Nuclear Information System (INIS)

    Peretti, M.M; Ges, A.M; Versaci, R.A

    2004-01-01

    Nickel-based alloys have a high fraction in volume of precipitate phase. This precipitate phase provides the characteristics of high mechanical resistance to high temperatures and, therefore, a study of the growth of this phase can predict the behavior of the components in service. This work studies the speed of growth in the alloy INCONEL 713C at temperatures of 800 o C, 875 o C and 950 o C with different treatment times. The present phase in this alloy is Ni3(AlTi), with a very high fraction in volume. The follow-up on the growth of the phase was carried out using scanning and transmission electron microscopy techniques. The speed of growth presents modifications that increase and decrease as a function of time. These variations in speed are attributed to modifications in the size and morphology of the precipitate particles. The changes in size and morphology directly influence the interfacial energy that produces the change in the speed of growth (CW)

  6. 34 CFR 300.601 - State performance plans and data collection.

    Science.gov (United States)

    2010-07-01

    ... Monitoring, Technical Assistance, and Enforcement § 300.601 State performance plans and data collection. (a... 34 Education 2 2010-07-01 2010-07-01 false State performance plans and data collection. 300.601... described in § 300.600(d). (b) Data collection. (1) Each State must collect valid and reliable information...

  7. Influence of sulfur on the passivity of inconel 600 in aqueous environment at 3000C. Relationship with stress corrosion

    International Nuclear Information System (INIS)

    Vancon, D.

    1989-11-01

    Dissolution kinetics and repassivation of inconel 600 in simulated primary coolant circuits of PWR is studied by fast traction experiment under potentiostatic control. The notion of elementary electrochemical transient is introduced. The model of anodic dissolution - film rupture allows the calculation of crack growth in constant deformation rate tests. When sulfur concentration is smaller than 100 micrograms/g the current is low, above the current is high. Calculation of crack growth from high level current are consistent with experimental data. Influence of pH, temperature, solution composition are determined. A Comparative study with nickel, incoloy 690 and a 19% chromium alloy was carried out to understand fast traction phenomena. Chromium plays an important part without pollution a protecting chromium oxide is formed. In polluted environment sulfur prevent nucleation of this compound and chromium hydroxides are precipitated on the surface. With pure nickel there is no passivity in presence of sulfur [fr

  8. 5 CFR 330.601 - Purpose.

    Science.gov (United States)

    2010-01-01

    ... Administrative Personnel OFFICE OF PERSONNEL MANAGEMENT CIVIL SERVICE REGULATIONS RECRUITMENT, SELECTION, AND... Employees § 330.601 Purpose. (a) This subpart implements the President's memorandum of September 12, 1995, to establish agency Career Transition Assistance Plans for Federal employees during a period of...

  9. Microstructures of friction surfaced coatings. A TEM study; Gefuege durch Reibauftragschweissen aufgetragener Beschichtungen. Eine TEM-Untersuchung

    Energy Technology Data Exchange (ETDEWEB)

    Akram, Javed; Kalvala, Prasad Rao; Misra, Mano [Utah Univ., Salt Lake City, UT (United States). Dept. of Metallurgical Engineering; Dilip, J. John Samuel [Louisville Univ., KY (United States). Dept. of Industrial Engineering; Pal, Deepankar; Stucker, Brent [Louisville Univ., KY (United States). Dept. of Industrial Engineering; 3D Sim, Park City, UT (United States)

    2016-05-15

    The microstructures of dissimilar metal welds between 9Cr-1Mo (Modified) (P91) and austenitic stainless steel (AISI 304) with Ni-based alloy interlayers (Inconel 625, Inconel 600 and Inconel 800H) are reported. These interlayers were deposited by the friction surfacing method one over the other on P91 alloy, which was finally friction welded to AISI 304. In this paper, the results of microstructural evolution in the friction surfaced coated interlayers (Inconel 625, 600, 800H) are reported. For comparative purposes, the microstructures of consumable rods (Inconel 625, 600, 800H) and dissimilar metal base metals (P91 and AISI 304) were also reported. Friction surfaced coatings exhibited dynamic recrystallization. In friction surfaced coatings, the carbide particles were found to be finer and distributed uniformly throughout the matrix, compared to their rod counterparts.

  10. Microstructures of friction surfaced coatings. A TEM study

    International Nuclear Information System (INIS)

    Akram, Javed; Kalvala, Prasad Rao; Misra, Mano

    2016-01-01

    The microstructures of dissimilar metal welds between 9Cr-1Mo (Modified) (P91) and austenitic stainless steel (AISI 304) with Ni-based alloy interlayers (Inconel 625, Inconel 600 and Inconel 800H) are reported. These interlayers were deposited by the friction surfacing method one over the other on P91 alloy, which was finally friction welded to AISI 304. In this paper, the results of microstructural evolution in the friction surfaced coated interlayers (Inconel 625, 600, 800H) are reported. For comparative purposes, the microstructures of consumable rods (Inconel 625, 600, 800H) and dissimilar metal base metals (P91 and AISI 304) were also reported. Friction surfaced coatings exhibited dynamic recrystallization. In friction surfaced coatings, the carbide particles were found to be finer and distributed uniformly throughout the matrix, compared to their rod counterparts.

  11. 26 CFR 601.505 - Revocation, change in representation and substitution or delegation of representative.

    Science.gov (United States)

    2010-04-01

    ... authorizes the substitution or delegation. An employee of a recognized representative may not be substituted... substitution or delegation of representative. 601.505 Section 601.505 Internal Revenue INTERNAL REVENUE SERVICE... Practice Requirements § 601.505 Revocation, change in representation and substitution or delegation of...

  12. Underwater laser cladding and seal welding for INCONEL 52

    International Nuclear Information System (INIS)

    Tamura, Masataka; Kouno, Wataru; Makino, Yoshinobu; Kawano, Shohei; Yoda, Masaki

    2007-01-01

    Recently, stress corrosion cracking (SCC) has been observed at aged components of nuclear power plants under water environment and high exposure of radiation. Toshiba has been developing both an underwater laser welding directly onto surface of the aged components as maintenance and repair techniques. This paper reports underwater laser cladding and seal welding for INCONEL 52. (author)

  13. Effect of Alloy 625 Buffer Layer on Hardfacing of Modified 9Cr-1Mo Steel Using Nickel Base Hardfacing Alloy

    Science.gov (United States)

    Chakraborty, Gopa; Das, C. R.; Albert, S. K.; Bhaduri, A. K.; Murugesan, S.; Dasgupta, Arup

    2016-04-01

    Dashpot piston, made up of modified 9Cr-1Mo steel, is a part of diverse safety rod used for safe shutdown of a nuclear reactor. This component was hardfaced using nickel base AWS ER NiCr-B alloy and extensive cracking was experienced during direct deposition of this alloy on dashpot piston. Cracking reduced considerably and the component was successfully hardfaced by application of Inconel 625 as buffer layer prior to hardface deposition. Hence, a separate study was undertaken to investigate the role of buffer layer in reducing the cracking and on the microstructure of the hardfaced deposit. Results indicate that in the direct deposition of hardfacing alloy on modified 9Cr-1Mo steel, both heat-affected zone (HAZ) formed and the deposit layer are hard making the thickness of the hard layer formed equal to combined thickness of both HAZ and deposit. This hard layer is unable to absorb thermal stresses resulting in the cracking of the deposit. By providing a buffer layer of Alloy 625 followed by a post-weld heat treatment, HAZ formed in the modified 9Cr-1Mo steel is effectively tempered, and HAZ formed during the subsequent deposition of the hardfacing alloy over the Alloy 625 buffer layer is almost completely confined to Alloy 625, which does not harden. This reduces the cracking susceptibility of the deposit. Further, unlike in the case of direct deposition on modified 9Cr-1Mo steel, dilution of the deposit by Ni-base buffer layer does not alter the hardness of the deposit and desired hardness on the deposit surface could be achieved even with lower thickness of the deposit. This gives an option for reducing the recommended thickness of the deposit, which can also reduce the risk of cracking.

  14. THE BEHAVIOR OF SOLUBLE METALS ELUTED FROM Ni/Fe-BASED ALLOY REACTORS AFTER HIGH-TEMPERATURE AND HIGH-PRESSURE WATER PROCESS

    Directory of Open Access Journals (Sweden)

    M. Faisal

    2012-05-01

    Full Text Available The behavior of heavy metals eluted from the wall of Ni/Fe-based alloy reactors after high-temperature and high-pressure water reaction were studied at temperatures ranging from 250 to 400oC. For this purpose, water and cysteic acid were heated in two reactor materials which are SUS 316 and Inconel 625. Under the tested conditions, the erratic behaviors of soluble metals eluted from the wall of Ni/Fe-based alloy in high temperature water were observed. Results showed that metals could be eluted even at a short contact time. The presence of air also promotes elution at sub-critical conditions. At sub-critical conditions, a significant amount of Cr was extracted from SUS 316, while only traces of Ni, Fe, Mo and Mn were eluted. In contrast, Ni was removed in significant amounts compared to Cr when Inconel 625 was tested. It was observed that eluted metals tend to increased under acidic conditions and most of those metals were over the limit of WHO guideline for drinking water. The results are significant both on the viewpoint of environmental regulation on disposal of wastes containing heavy metals, toxicity of resulting product and catalytic effect on a particular reaction.

  15. Comparative Analysis of Properties and Microstructure of the Plastically Deformed Alloy Inconel®718, Manufactured by Plastic Working and Direct Metal Laser Sintering

    Directory of Open Access Journals (Sweden)

    Żaba K.

    2016-03-01

    Full Text Available Nickel superalloys as Inconel® are materials widely used in the aerospace industry among others for diffusers, combustion chamber, shells of gas generators and other. In most cases, manufacturing process of those parts are used metal strips, produced by conventional plastic processing techniques, and thus by hot or cold rolling. An alternative technology allowing for manufacturing components for jet engines is the technique of 3D printing (additive manufacturing, and most of all Direct Metal Laser Sintering, which is one of the latest achievement in field of additive technologies.

  16. 12 CFR 308.601 - Definitions.

    Science.gov (United States)

    2010-01-01

    ... independent public accountant by section 36 of the FDIA and 12 CFR part 363, including attestation services. (c) Independent public accountant (accountant) means any individual who performs or participates in... PROCEDURE Removal, Suspension, and Debarment of Accountants From Performing Audit Services § 308.601...

  17. Microhardness and microstructure evolution of TiB2 reinforced Inconel 625/TiB2 composite produced by selective laser melting

    Science.gov (United States)

    Zhang, Baicheng; Bi, Guijun; Nai, Sharon; Sun, Chen-nan; Wei, Jun

    2016-06-01

    In this study, micron-size TiB2 particles were utilized to reinforce Inconel 625 produced by selective laser melting. Exceptional microhardness 600-700 HV0.3 of the composite was obtained. In further investigation, the microstructure and mechanical properties of Inconel 625/TiB2 composite can be significantly influenced by addition of TiB2 particles during SLM. It was found that the long directional columnar grains observed from SLM-processed Inconel 625 were totally changed to fine dendritic matrix due to the addition of TiB2 particles. Moreover, with laser energy density (LED) of 1200 J/m, a Ti, Mo rich interface around TiB2 particles with fine thickness can be observed by FESEM and EDS. The microstructure evolution can be determined by different laser energy density (LED): under 1200 J/m, γ phase in dendrite grains; under 600 J/m, γ phase in combination of dendritic and acicular grains; under 400 J/m, γ phase acicular grains. Under optimized LED 1200 J/m, the dynamic nanohardness (8.62 GPa) and elastic modulus (167 GPa) of SLM-processed Inconel 625/TiB2 composite are higher compared with those of SLM-processed Inconel 625 (3.97 GPa and 135 GPa, respectively).

  18. Microstructural evolution and mechanical properties of Inconel 718 after thermal exposure

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Z.S., E-mail: yuzaisong@tpri.com.cn [State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, No. 28, Xianning West Road, Xi’an 710049 (China); Xi' an Thermal Power Research Institute Co. Ltd., No. 136, Xingqing Road, Xi’an 710032 (China); Zhang, J.X. [State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, No. 28, Xianning West Road, Xi’an 710049 (China); Yuan, Y.; Zhou, R.C.; Zhang, H.J.; Wang, H.Z. [Xi' an Thermal Power Research Institute Co. Ltd., No. 136, Xingqing Road, Xi’an 710032 (China)

    2015-05-14

    Inconel 718 was subjected to various heat treatments, i.e., solution heat treatment, standard ageing treatment and standard ageing plus 700 °C thermal exposure. The mechanical properties of the alloys were determined using tensile tests and Charpy pendulum impact tests at 650 °C and room temperature, respectively. The highest yield strength of 988 MPa was attained in the standard aged specimen, whereas a maximum impact toughness of 217 J cm{sup −2} was attained in the solution-treated specimen. After thermal exposure, the mechanical properties of the specimens degrade. Both the yield strength and impact toughness decreased monotonically with increasing thermal exposure time. Subjected to a 10000-h long-term thermal exposure, the yield strength dramatically decreased to 475 MPa (almost 50% of the maximum strength), and the impact toughness reduced to only 18 J cm{sup −2}. The microstructures of the specimens were characterized using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Coarsening of γ′ and γ″ and the transformation of γ″ to δ-Ni{sub 3}Nb was observed after thermal exposure. However, a complete transformation from metastable γ″ to δ-Ni{sub 3}Nb was never accomplished, even after the 10000-h long-term thermal exposure. Based on the obtained experimental results, the effects of the microstructural evolution on the mechanical properties are discussed.

  19. Anisotropy effects during dwell-fatigue caused by δ-phase orientation in forged Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Saarimäki, Jonas, E-mail: jonas.saarimaki@liu.se [Division of Engineering Materials, Department of Management and Engineering, Linköping University, SE-58183 Linköping (Sweden); Colliander, Magnus Hörnqvist [Department of Applied Physics, Chalmers University of Technology, SE-41296 Göteborg (Sweden); GKN Aerospace Engine Systems, R& T Centre, SE-46181 Trollhättan (Sweden); Moverare, Johan J. [Division of Engineering Materials, Department of Management and Engineering, Linköping University, SE-58183 Linköping (Sweden)

    2017-04-24

    Inconel 718 is a commonly used superalloy for turbine discs in the gas turbine industry. Turbine discs are often subjected to dwell-fatigue as a result of long constant load cycles. The effect of anisotropy on dwell-fatigue cracking in forged turbine discs have not yet been thoroughly investigated. Crack propagation behaviour was characterised using compact tension (CT) samples cut in different orientations from a real turbine disc forging. Samples were also cut in two different thicknesses in order to investigate the influence of plane strain and plane stress condition on the crack propagation rates. The samples were subjected to dwell-fatigue tests at 550 °C with 90 s or 2160 s dwell-times at maximum load. Microstructure characterisation was done using scanning electron microscopy (SEM) techniques such as electron channelling contrast imaging (ECCI), electron backscatter diffraction (EBSD), and light optical microscopy (LOM). The forged alloy exhibits strong anisotropic behaviour caused by the non-random δ-phase orientation. When δ-phases were oriented perpendicular compared to parallel to the loading direction, the crack growth rates were approximately ten times faster. Crack growth occurred preferably in the interface between the γ-matrix and the δ-phase.

  20. 5 CFR 410.601 - Reporting.

    Science.gov (United States)

    2010-01-01

    ... agency shall report the training data for its employees' training and development at such times and in... Administrative Personnel OFFICE OF PERSONNEL MANAGEMENT CIVIL SERVICE REGULATIONS TRAINING Reporting § 410.601 Reporting. (a) Each agency shall maintain records of training plans, expenditures, and activities in such...

  1. Application of eddy current inversion technique to the sizing of defects in Inconel welds with rough surfaces

    International Nuclear Information System (INIS)

    Yusa, Noritaka; Machida, Eiji; Janousek, Ladislav; Rebican, Mihai; Chen, Zhenmao; Miya, Kenzo

    2005-01-01

    This paper evaluates the applicability of eddy current inversion techniques to the sizing of defects in Inconel welds with rough surfaces. For this purpose, a plate Inconel weld specimen, which models the welding of a stub tube in a boiling water nuclear reactor is fabricated, and artificial notches machined into the specimen. Eddy current inspections using six different eddy current probes are conducted and efficiencies were evaluated for the six probes for weld inspection. It is revealed that if suitable probes are applied, an Inconel weld does not cause large noise levels during eddy current inspections even though the surface of the weld is rough. Finally, reconstruction of the notches is performed using eddy current signals measured using the uniform eddy current probe that showed the best results among the six probes in this study. A simplified configuration is proposed in order to consider the complicated configuration of the welded specimen in numerical simulations. While reconstructed profiles of the notches are slightly larger than the true profiles, quite good agreements are obtained in spite of the simple approximation of the configuration, which reveals that eddy current testing would be an efficient non-destructive testing method for the sizing of defects in Inconel welds

  2. Effect of standard heat treatment on the microstructure and mechanical properties of hot isostatically pressed superalloy inconel 718

    International Nuclear Information System (INIS)

    Rao, G. Appa; Kumar, Mahendra; Srinivas, M.; Sarma, D.S.

    2003-01-01

    Ni-Fe base superalloy, Inconel 718, was processed through powder metallurgy (P/M) hot isostatic pressing (HIP) route. In order to balance the strength and ductility, the HIPed material was given the standard heat treatment, viz. solution treatment at 980 deg. C for 1 h/water quenched (WQ) to room temperature and a two-step ageing treatment consisting of 720 deg. C for 8 h/furnace cooling (FC) at 55 deg. C h -1 to 620 deg. C and holding at 620 deg. C for 8 h before air cooling (AC) to room temperature. Optical microscopy and scanning electron microscopy (SEM) studies on the heat treated alloy have shown a homogeneous microstructure with fine grain size (25 μm) along with the presence of prior particle boundary (PPB) networks. Transmission electron microscopy (TEM) on the heat treated material has revealed the presence of oxides, MC carbides and δ-precipitates at the grain boundaries and a uniform precipitation of fine γ'' and γ' strengthening phases in the matrix. Tensile and stress rupture tests were performed on the heat treated material. While the yield strength (YS) and ultimate tensile strength (UTS) of the HIPed and heat treated alloy at room temperature and 650 deg. C were comparable to those of conventionally processed wrought IN 718, its ductility was lower. The stress rupture life of the HIPed alloy improved marginally due to heat treatment and met the minimum specification requirement of life hours but the rupture ductility was found to be inferior to that of the wrought material. The fractography of the failed samples has revealed the transgranular ductile mode of fracture in the as-solution treated alloy, while intergranular mode of failure with the decohesion of PPBs occurred more predominantly in the aged condition. This change of fracture mode with ageing treatment shows the ductility dependence on the relative strength of the matrix and PPBs. The TEM studies on the deformed alloy have revealed that the brittle oxides and carbides at the prior

  3. Fatigue crack growth behavior of Inconel 718 produced by selective laser melting

    Czech Academy of Sciences Publication Activity Database

    Konečná, R.; Kunz, Ludvík; Nicoletto, G.; Bača, A.

    2016-01-01

    Roč. 35, č. 10 (2016), s. 31-40 ISSN 1971-8993 Institutional support: RVO:68081723 Keywords : Inconel 718 * Selective laser melting * Microstructure * Fatigue crack growth * Fractography Subject RIV: JL - Materials Fatigue, Friction Mechanics

  4. 40 CFR 86.601-84 - Applicability.

    Science.gov (United States)

    2010-07-01

    ... Auditing of New Light-Duty Vehicles, Light-Duty Trucks, and Heavy-Duty Vehicles § 86.601-84 Applicability... of the section number. A section remains in effect for subsequent model years until it is superseded...

  5. Influence of pretreatment on creep-rupture-strength and creep-behaviour of a matrix-hardening Ni-base-alloy

    International Nuclear Information System (INIS)

    Schirra, M.

    1982-01-01

    The creep and time-to-rupture behaviour of the matrix hardening Nickel base alloy Inconel 625 was investigated in the temperature range 650-800 0 C. Three different thermo-mechanical pretreatment were used: I = Hot rolled finish; II = 870 0 C annealed; III = Sol. treatment 1150 0 C 1 h. The temperature range of this study is for samples which have undergone treatment I and II well above the temperatures normally used. The results show an anomalous stress dependence of creep and time-to-rupture at around 750 0 C. The reason is to be found in the very complex precipitation processes occurring while the stress is applied. The results are explained according to findings about precipitation in this type of alloy. (orig.) [de

  6. Effect of thermal stabilization on the low-temperature stress-corrosion cracking of Inconel 600

    International Nuclear Information System (INIS)

    Bandy, R.; van Rooyen, D.

    1983-01-01

    The propensity to low-temperature stress-corrosion cracking (SCC) of thermally stabilized Inconel 600 in sulfur-bearing environments has been investigated using U-bends and slow-strain-rate testing. The results have been compared with those of sensitized Inconel 600. The potential dependence of crack-propagation rate has been established in a single test by using several U-bends held at different potentials, by choosing an appropriate electrical circuitry. The difference in SCC susceptibility of the sensitized and stabilized materials is discussed in terms of the grain-boundary chromium depletion and resulting intergranular attack in boiling ferric sulfate-sulfuric acid tests, and electrochemical potentiokinetic reactivation (EPR) tests. 10 figures

  7. 43 CFR 20.601 - General.

    Science.gov (United States)

    2010-10-01

    ... Disciplinary and Remedial Actions § 20.601 General. This subpart deals with disciplinary actions and remedial... this part or in 5 CFR part 2635 or 5 CFR part 3501. Disciplinary action may include oral or written... provisions. Disciplinary action may be imposed independently from and without prior application of remedial...

  8. Electron emission from Inconel under ion bombardment

    International Nuclear Information System (INIS)

    Alonso, E.V.; Baragiola, R.A.; Ferron, J.; Oliva-Florio, A.

    1979-01-01

    Electron yields from clean and oxidized Inconel 625 surfaces have been measured for H + ,H 2 + ,He + ,O + and Ar + ions at normal incidence in the energy range 1.5 to 40 keV. These measurements have been made under ultrahigh vacuum and the samples were freed of surface contaminants by bombarding with high doses of either 20 keV H 2 + or 30 keV Ar + ions. Differences in yields of oxidized versus clean surfaces are explained in terms of differences in the probability that electrons internally excited escape upon reaching the surface. (author)

  9. Fretting wear of Inconel 625 at high temperature and in high vacuum

    International Nuclear Information System (INIS)

    Iwabuchi, A.

    1985-01-01

    The purpose of this work was to investigate the fretting properties of Inconel 625 at high temperature and in high vacuum. Experiments were carried out under constant conditions with a normal load of 14 N and a peak-to-peak slip amplitude of 110 μm and through 6x10 4 cycles. Several environmental conditions were used. Pressure was varied between 10 -3 and 10 5 Pa at temperatures of 20 and 500 0 C. Temperatures up to 500 0 C were also used at pressures of 10 -3 and 10 5 Pa. At 10 -3 Pa and 500 0 C wear loss was negligible but wear scars showed severe damage consisting of deep cracks and accretion of transferred debris. The coefficient of friction then maintained a high value of 1.7 throughout the fretting test. The critical pressure below which oxidation rate becomes reduced is 10 Pa, a value independent of temperature. At pressures below this critical value the coefficient of friction increases steeply and the fretting mechanism changes from one of oxidative wear to one of adhesive wear. A compacted so-called 'glaze' oxide was formed at temperatures above 300 0 C in air (10 5 Pa) and at pressures above 10 3 Pa at 500 0 C. A comparison of results for Inconel 625 with those for S45C and SUS304 steels and Inconel 600 is given. (orig.)

  10. Electrochemical Study about Microorganisms Induced Corrosion in Inconel

    OpenAIRE

    Domínguez-Sánchez, G.; Tiburcio, C. Gaona; Almeraya-Calderón, F.M.; Martínez-Villafañe, A.

    2005-01-01

    Inconel 600 has been designed to heat resistance. It is used in the chemistry industry, food industry and, of course, in the production of electric energy, among others. The goal of this project was to decrease the costs in the equipments and pipes deterioration by prolonging their lifetime, controlling and preventing their deterioration by means of appropriated and programmed maintenance, but above all knowing the mechanism and kinetic of corrosion that affects them. We used polarization cur...

  11. Effect of service exposure on fatigue crack propagation of Inconel 718 turbine disc material at elevated temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Jeong, Dae-Ho [Department of Materials Science and Engineering, RECAPT, Gyeongsang National University, Chinju (Korea, Republic of); Choi, Myung-Je [Korea Aerospace Industry, Sacheon (Korea, Republic of); Goto, Masahiro [Department of Mechanical Engineering, Oita University, Oita (Japan); Lee, Hong-Chul [Republic of Korea Air Force (Korea, Republic of); Kim, Sangshik, E-mail: sang@gnu.ac.kr [Department of Materials Science and Engineering, RECAPT, Gyeongsang National University, Chinju (Korea, Republic of)

    2014-09-15

    In this study, the fatigue crack propagation behavior of Inconel 718 turbine disc with different service times from 0 to 4229 h was investigated at 738 and 823 K. No notable change in microstructural features, other than the increase in grain size, was observed with increasing service time. With increasing service time from 0 to 4229 h, the fatigue crack propagation rates tended to increase, while the ΔK{sub th} value decreased, in low ΔK regime and lower Paris' regime at both testing temperatures. The fractographic observation using a scanning electron microscope suggested that the elevated temperature fatigue crack propagation mechanism of Inconel 718 changed from crystallographic cleavage mechanism to striation mechanism in the low ΔK regime, depending on the grain size. The fatigue crack propagation mechanism is proposed for the crack propagating through small and large grains in the low ΔK regime, and the fatigue crack propagation behavior of Inconel 718 with different service times at elevated temperatures is discussed. - Highlights: • The specimens were prepared from the Inconel 718 turbine disc used for 0 to 4229 h. • FCP rates were measured at 738 and 823 K. • The ΔK{sub th} values decreased with increasing service time. • The FCP behavior showed a strong correlation with the grain size of used turbine disc.

  12. Quality Requirements Put On The Inconel 625 Austenite Layer Used On The Sheet Pile Walls Of The Boiler’s Evaporator To Utilize Waste Thermally

    Directory of Open Access Journals (Sweden)

    Słania J.

    2015-06-01

    Full Text Available Quality requirements and tests taken on the surfacing layer Inconel 625 are presented in the article. The reasons of using surfacing layer Inconel 625 and technologies of its making with a particular emphasis on the CMT method are described. Quality requirements for the surfacing weld Inconel 625 are provided. Basic requirements included in the Merkblatt 1166, as well as additional requirements, which are reflected in the technical specifications of the boilers’ producers are specified.

  13. Materials for advanced high temperature reactors

    International Nuclear Information System (INIS)

    Graham, L.W.

    1976-01-01

    The results recently obtained from the Dragon program are presented to illustrate materials behavior: (a) effect of temperature on oxidation and carburisation in HTR helium (variation in oxide depth and in C content of AISI 321 after 5000 hours in HTR helium; effect of temperature on surface scale formation in the γ' strengthened alloys Nimonic 80A and 713LC); (b) effect of alloy composition on oxidation and carburisation behavior (influence of Nb and Ti on the corrosion of austenitic steels; influence of Ti and Al in IN-102; weight gain of cast high Ni alloys); (c) effect of environment on creep strength (results of tests for hastelloy X, grade I inconel 625, grade II inconel 625 and inconel 617 in He and air between 750 and 800 0 C)

  14. Microstructural Evolution and Creep-Rupture Behavior of A-USC Alloy Fusion Welds

    Science.gov (United States)

    Bechetti, Daniel H.; DuPont, John N.; Siefert, John A.; Shingledecker, John P.

    2016-09-01

    Characterization of the microstructural evolution of fusion welds in alloys slated for use in advanced ultrasupercritical (A-USC) boilers during creep has been performed. Creep-rupture specimens involving INCONEL® 740, NIMONIC® 263 (INCONEL and NIMONIC are registered trademarks of Special Metals Corporation), and Haynes® 282® (Haynes and 282 are registered trademarks of Haynes International) have been analyzed via light optical microscopy, scanning electron microscopy, X-ray diffraction, and thermodynamic and kinetic modeling. Focus has been given to the microstructures that develop along the grain boundaries in these alloys during creep at temperatures relevant to the A-USC process cycle, and particular attention has been paid to any evidence of the formation of local γ'-denuded or γ'-free zones. This work has been performed in an effort to understand the microstructural changes that lead to a weld strength reduction factor (WSRF) in these alloys as compared to solution annealed and aged alloy 740 base metal. γ' precipitate-free zones have been identified in alloy 740 base metal, solution annealed alloy 740 weld metal, and alloy 263 weld metal after creep. Their development during long-term thermal exposure is correlated with the stabilization of phases that are rich in γ'-forming elements ( e.g., η and G) and is suppressed by precipitation of phases that do not contain the γ' formers ( e.g., M23C6 and μ). The location of failure and creep performance in terms of rupture life and WSRF for each welded joint is presented and discussed.

  15. A life evaluation under creep-fatigue-environment interaction of Ni-base wrought alloys

    International Nuclear Information System (INIS)

    Hattori, Hiroshi; Kitagawa, Masaki; Ohtomo, Akira; Itoh, Mitsuyoshi

    1986-01-01

    In order to determine a failure criteria under cyclic loading and affective environment for HTGR systems, a series of strain controlled low-cycle fatigue tests were carried out at HTGR maximum gas temperatures in air, in vacuum and in HTGR helium environments on two nickel-base wrought alloys, namely Inconel 617 and Hastelloy XR. This paper first describes the creep-fatigue-environment properties of these alloys followed by a proposal of an evaluation method of creep-fatigue-environment interaction based on the experimental data to define the more reasonable design criteria, which is a modification of the linear damage summation rule. Second, the creep-fatigue properties of Hastelloy XR at 900 deg C and the result evaluated by this proposed method are shown. This criterion is successfully applied to the life prediction at 900 deg C. In addition, the creep-fatigue properties of Hastelloy XR-II are discussed. (author)

  16. Impact of shelf life on measured prompt fraction of spare Inconel in-core flux detectors

    Energy Technology Data Exchange (ETDEWEB)

    Mohindra, VK; Sadeghi, S. [Atomic Energy of Canada Limited, Mississauga, Ontario (Canada); Crouse, B. [Darlington Nuclear Generating Station, Bowmanville, Ontario (Canada)

    2008-07-01

    Prompt fraction measurements associated with spare self-powered Inconel In-Core Flux Detectors (ICFDs) carried out a few years after installation on Shut Down System number 1 (SDS1) and Reactor Regulating System (RRS) at Darlington Nuclear Generating Station (DNGS), were found to be lower than those of the original detectors. These detectors, spares and originals, were manufactured in the late 80s, however, the former were kept at manufacturer's warehouse and latter were installed in the reactor core within a few years after manufacturing. Although the prompt fractions of the spare detectors were relatively low, the electronic/electrical behavior of the spare detectors was intact. The first batch of the original detectors performed as per the design requirements. Therefore, it is suspected that during shelf life, spare Inconel in-core flux detectors underwent changes that lowered their measured values of prompt fraction, which were taken within a few years after installation in the reactor. Detailed study of detectors' material composition and impurity concentrations revealed no association with the lower prompt fraction measurements. The evaluation of the limited data of the original and spare Inconel ICFDs installed at Darlington showed: 1. The reduction in prompt fraction was roughly proportional to the shelf life of the detectors; and 2. The rate of reduction in prompt fraction during storage was about double the rate of reduction during operation in the reactor. Above observations were based on the data provided by DNGS for a few detectors. The purpose of this paper is two fold, firstly to present the results of the complete study carried out to investigate the cause of relatively low prompt fractions measured on spare SDS1 and RRS Inconel ICFDs at DNGS, and secondly to generate interest/awareness within other CANDU utilities to add to the database of prompt fractions of spare Inconel ICFDs measured after installation. The data will help to improve

  17. 45 CFR 73.735-601 - Applicability.

    Science.gov (United States)

    2010-10-01

    ... concerning active participation in political management and political campaigns. Also exempt are other... Political Activity § 73.735-601 Applicability. (a) All employees in the Executive Branch of the Federal Government, including non-career employees, are subject to basic political activity restrictions in...

  18. Changes In Mechanical Properties Of Heat Resisting Alloy For A Satellite Propulsion System After A Nitriding Process

    Science.gov (United States)

    Kagawa, Hideshi; Fujii, Go; Kajiwara, Kenichi; Kuroda, Daisuke; Suzuki, Takuya; Yamabe-Mitarai, Yoko; Murakami, Hideyuki; Ono, Yoshinori

    2012-07-01

    Haynes25 (L-605) is a common heat resistant alloy used in mono-propellant structures and screen materials for catalyst beds. The lifetime requirements for thrusters have expanded dramatically after studies conducted in the 1970s on mono-propellant materials used to extend the service life. The material design had long remained unchanged, and the L-605 was still used as thruster material due to its good heritage. However, some important incidents involving degradation were found during the test-unit break-up inspection following the thruster life tests. The Japanese research team focused on the L-605 degradations found on the catalyst bed screen mesh used for mono-propellant thruster and analysed the surface of the wire material and the cross- section of the wire screen mesh used in the life tests. The investigation showed that the degradation was caused by nitriding L-605 component elements. The team suggested that the brittle fracture was attributable to tungsten (W) carbides, which formed primarily in the grain boundaries, and chromium (Cr) nitride, which formed mainly in the parts in contact with the hot firing gas. The team also suggested the installation of a platinum coating on the material surface as a countermeasure L-605 nitric degradation. Inconel 625 is now selected as a mono-propellant structure material due to its marginal raw material characters and cost. The team believes that Inconel 625 does not form W carbides since it contains no tungsten component, but does contain Cr and Fe, which form nitrides easily. Therefore, the team agreed that for the Inconel 625, there was a need to evaluate changes in the microstructure and mechanical properties following exposure to hot nitrogen gases. This paper will describe these changes of Inconel 625.

  19. Stability of machining induced residual stresses in Inconel 718 under quasi-static loading at room temperature

    International Nuclear Information System (INIS)

    Madariaga, A.; Esnaola, J.A.; Arrazola, P.J.; Ruiz-Hervias, J.; Muñoz, P.; Ostolaza, K.

    2015-01-01

    Tensile residual stresses are very often generated on the surface when machining nickel alloys. In order to determine their influence on the final mechanical behaviour of the component residual stress stability should be considered. In the present work the evolution of surface residual stresses induced by machining in Inconel 718 under static loading at room temperature was studied experimentally and numerically. An Inconel 718 disc was face turned employing industrial working conditions and specimens for tensile tests were extracted from the disc. Surface residual stresses were measured by X-ray diffraction for initial state and after applying different loads over the material's yield stress. Then, a finite element model based on the surface–core approach was fitted to experimental results and the study was extended to analyse the influence of load level, degree of work-hardening and initial surface conditions. For the studied case, initial tensile surface residual stress (776 MPa) became even more tensile when applying loads higher than the material yield stress, but a shift was observed at the highest applied load (1350 MPa) and initial residual stress was relaxed about 170 MPa. This particular behaviour is associated to the modified stress–strain properties of the machined affected surface layer which was strongly work-hardened. Moreover, if the work-hardened properties are not considered in the finite element model results differ substantially from experiments. Surface residual stress stability also depends on the initial surface residual stress, but the degree of work-hardening induced by the machining process must be considered as well. If the difference between the yield stress of the surface and the yield stress of the core is lower than the initial surface residual stress, the surface begins yielding first and consequently the surface residual stress is decreased. In contrast, if the difference between the yield stress of the surface and the

  20. Stability of machining induced residual stresses in Inconel 718 under quasi-static loading at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Madariaga, A., E-mail: amadariaga@mondragon.edu [Mechanical and Industrial Production Department, Faculty of Engineering, Mondragon Unibertsitatea, Loramendi 4, Mondragon 20500 Gipuzkoa (Spain); Esnaola, J.A.; Arrazola, P.J. [Mechanical and Industrial Production Department, Faculty of Engineering, Mondragon Unibertsitatea, Loramendi 4, Mondragon 20500 Gipuzkoa (Spain); Ruiz-Hervias, J.; Muñoz, P. [Departamento Ciencia de Materiales, ETSI Caminos, Universidad Politécnica de Madrid, c/Profesor Aranguren s/n, Madrid 28040 (Spain); Ostolaza, K. [Materials and Processes Technology Department, ITP S.A., Parque Tecnológico, Edificio 300, 48170 Zamudio (Spain)

    2015-01-03

    Tensile residual stresses are very often generated on the surface when machining nickel alloys. In order to determine their influence on the final mechanical behaviour of the component residual stress stability should be considered. In the present work the evolution of surface residual stresses induced by machining in Inconel 718 under static loading at room temperature was studied experimentally and numerically. An Inconel 718 disc was face turned employing industrial working conditions and specimens for tensile tests were extracted from the disc. Surface residual stresses were measured by X-ray diffraction for initial state and after applying different loads over the material's yield stress. Then, a finite element model based on the surface–core approach was fitted to experimental results and the study was extended to analyse the influence of load level, degree of work-hardening and initial surface conditions. For the studied case, initial tensile surface residual stress (776 MPa) became even more tensile when applying loads higher than the material yield stress, but a shift was observed at the highest applied load (1350 MPa) and initial residual stress was relaxed about 170 MPa. This particular behaviour is associated to the modified stress–strain properties of the machined affected surface layer which was strongly work-hardened. Moreover, if the work-hardened properties are not considered in the finite element model results differ substantially from experiments. Surface residual stress stability also depends on the initial surface residual stress, but the degree of work-hardening induced by the machining process must be considered as well. If the difference between the yield stress of the surface and the yield stress of the core is lower than the initial surface residual stress, the surface begins yielding first and consequently the surface residual stress is decreased. In contrast, if the difference between the yield stress of the surface and the

  1. Modelling the long-term corrosion behaviour of candidate alloys for Canadian SCWR

    Energy Technology Data Exchange (ETDEWEB)

    Steeves, G.; Cook, W., E-mail: wcook@unb.ca, E-mail: graham.steeves@unb.ca [University of New Brunswick, Department of Chemical Engineering, Fredericton, NB (Canada)

    2015-07-01

    Corrosion behaviour of Inconel 625 and Incoloy 800H, two of the candidate fuel cladding materials for Canadian supercritical water (SCW) reactor designs, were evaluated by exposing the metals to SCW in UNB's SCW flow loop. Individual experiments were conducted over a range of 370{sup o}C and 600{sup o}C. Exposure times were typically intervals of 100, 250, and 500 hours. Experimental data was used to create an empirical kinetic equation for each material. Activation energies for the alloys were determined, and showed a distinct difference between low-temperature electrochemical corrosion mechanism and direct high-temperature chemical oxidation. (author)

  2. Microstructure formation and corrosion behaviour in HVOF-sprayed Inconel 625 coatings

    International Nuclear Information System (INIS)

    Zhang, D.; Harris, S.J.; McCartney, D.G.

    2003-01-01

    The nickel-based alloy Inconel 625 was thermally sprayed by two different variants of the high velocity oxy-fuel process. In this study, coatings deposited by a liquid-fuelled gun were compared with those produced by a gas-fuelled system; in general, the former generates higher particle velocities but lower particle temperatures. Investigations into the microstructural evolution of the coatings, using scanning electron microscopy and X-ray diffraction, are presented along with results on their aqueous corrosion behaviour, obtained from salt spray and potentiodynamic tests. It is inferred from coating microstructures that, during spraying, powder particles generally comprised three separate zones as follows: fully melted regions; partially melted zones; and an unmelted core. However, the relative proportions formed in an individual powder particle depended on its size, trajectory through the gun, the gas dynamics (velocity/temperature) of the thermal spray gun and the type of gun employed. Cr 2 O 3 was the principal oxide phase formed during spraying and the quantity appeared to be directly related to the degree to which particles were melted. The salt spray test provides a sensitive means of determining the presence of interconnected porosity in coatings and those produced with the liquid-fuelled gun exhibited reduced interconnected porosity and increased corrosion resistance compared with deposits obtained from the gas-fuelled system. In addition, potentiodynamic tests revealed that passive current densities are 10-20 times lower in liquid-fuel coatings than in those sprayed with the gas-fuelled gun

  3. Fatigue and creep cracking of nickel alloys for 700 C steam turbines

    International Nuclear Information System (INIS)

    Berger, C.; Granacher, J.; Thoma, A.; Roesler, J.; Del Genovese, D.

    2001-01-01

    Four materials of the types Inconel 706 (two heat treatment states), Inconel 617, and Waspaloy were tested as shaft materials for 700 to 720 C steam turbines. At an extrapolation time ratio of 10, Waspaloy was expected to have the highest creep strength (about 270 MPa at 700 C), with values of about 140 MPa at 700 C for Inconel 617. A preliminary evaluation of the 700 C creep rupture tests showed the highest creep rupture resistance for Inconel 617, followed by Waspaloy and Inconel 706 [de

  4. Submarine Propulsion Shaft Life: Probabilistic Prediction and Extension through Prevention of Water Ingress

    Science.gov (United States)

    2014-06-01

    625 (an Inconel ) sleeve. These sleeves exhibit exceptional corrosion performance, and are used as the wear surfaces in contact with the lubricated...it exits the stern tube bearing. There is an alloy 625 ( Inconel ) sleeve, used as a wear surface for the bearing interaction, as seen in the drawing...Industry Day at MIT, October 13, 2011. Alloy 625 sleeve Mild steel shaft Typical Corrosion Area Epoxy Filler Glass Reinforced Plastic Cover

  5. Characterization of dissimilar welding: carbon steel E309L-E308L-ERNiCr3-ENiCrFe3 alloy 600

    International Nuclear Information System (INIS)

    Mucino G, O.

    2015-01-01

    Most BWR type reactors have internal support components, which need to be attached to the inner surface by welding. Specifically, in these joints two materials interact, such as stainless steel and nickel base alloys. Nickel base alloys such as alloy 82 (ERNiCr3) and alloy 182 (ENiCrFe-3) are used for the joining of both dissimilar materials. For joints made with both nickel base alloys, the alloy 182 is prone to stress corrosion cracking (SCC); so it is essential to carry out studies related to this contribution material. In the nuclear industry any study related to this alloy is of importance because experience is gained in its behavior when is part of a system of an operation reactor. This work presents the characterization of the weld deposit of a stainless steel coating (with electrodes E309L and E308L) on a carbon steel plate type A36 and the joining with an Inconel 600 plate, simulating the joining of the internal coating of vessel and the heel of the support leg of the envelope of a BWR reactor. In this work, the mechanical and micro-structural characterization of the alloy deposit 182 was performed. (Author)

  6. 21 CFR 601.94 - Promotional materials.

    Science.gov (United States)

    2010-04-01

    ... LICENSING Approval of Biological Products When Human Efficacy Studies Are Not Ethical or Feasible § 601.94... advertisements, intended for dissemination or publication within 120 days following marketing approval. After 120 days following marketing approval, unless otherwise informed by the agency, the applicant must submit...

  7. Exfoliation on stainless steel and inconel produced by 0.8-4 MeV helium ion bombardment

    International Nuclear Information System (INIS)

    Paszti, F.; Mezey, G.; Pogany, L.; Fried, M.; Manuaba, A.; Kotai, E.; Lohner, T.; Pocs, L.

    1982-11-01

    Trying to outline the energy dependence of surface deformations such as exfoliation and flaking on candidate CTR first-wall materials, stainless steel and two types of inconels were bombarded by 0.8, 1 and 4 MeV helium ions. All the bombarded spots could be characterized by by large exfoliations covering almost the total implanted area. No spontaneous rupture was observed except on one type of inconel where flaking took place right after reaching the critical dose. After mechanical opening of the formations, similar inner morphology was found as in our previous studies on gold. (author)

  8. Creep properties of heat-resistant superalloys for nuclear plants in helium

    International Nuclear Information System (INIS)

    Shimizu, Shigeki; Satoh, Keisuke; Matsuda, Shozo; Murase, Hirokazu; Fujioka, Junzo.

    1979-01-01

    In order to estimate the creep and rupture strengths of candidate alloys for the intermediate heat exchanger of VHTR, creep and stress rupture tests in impure helium were conducted on Hastelloy X, Inconel 617, Inconel 625, Incoloy 800 and Incoloy 807 at 900 0 C. The results were discussed in comparison with those in air and the alloys were examined from the point of view of the elevated temperature structural design. The main results obtained are summarized as follows: (1) No appreciable decrease in creep and rupture strengths in helium as compared with those in air is observed on Hastelloy X and Inconel 625. On the contrary, the creep and rupture strengths of Inconel 617 in helium decrease slightly as compared with those in air. In the case of Incoloy 807, the creep strength to cause 1 percent total strain and that to initiate secondary creep increase remarkably in helium as compared with those in air. However, the creep strength to cause initiation of tertiary creep and the rupture strength in helium remarkably decrease as compared with those in air. (2) The order of magnitude of the S 0 value for each material in helium is as follows; Hastelloy X > Inconel 617 > Incoloy 807 > Inconel 625 > Incoloy 800 Meanwhile, that of the S sub(t) value in helium is; Inconel 617 > Hastelloy X > Incoloy 807 > Inconel 625 > Incoloy 800. (author)

  9. Production and fabrication of vanadium alloys for the radiative divertor program of DIII-D - Annual report input for 1996

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, W.R.; Smith, J.P.; Stambaugh, R.D.

    1996-10-01

    V-4Cr-4Ti alloy has been selected for use in the manufacture of a portion of the DIII-D Radiative Divertor (RD) upgrade. The production of a 1200-kg ingot of V-4Cr-4Ti alloy has been completed at Teledyne Wah Chang of Albany, Oregon (TWCA) to provide {approximately}800-kg of applicable product forms, and two billets have been extruded from the ingot. Chemical compositions of the ingot and both extruded billets were acceptable. Material from these billets will be converted into product forms suitable for components of the DIII-D Radiative Divertor structure. Joining of V-4Cr-4Ti alloy has been identified as the most critical fabrication issue for its use in the RD Program, and research into several joining methods for fabrication of the RD components, including resistance seam, friction, and electron beam welding, is continuing. Preliminary trials have been successful in the joining of V-alloy to itself by electron beam, resistance, and friction welding processes and to Inconel 625 by friction welding.

  10. Production and fabrication of vanadium alloys for the radiative divertor program of DIII-D - Annual report input for 1996

    International Nuclear Information System (INIS)

    Johnson, W.R.; Smith, J.P.; Stambaugh, R.D.

    1996-01-01

    V-4Cr-4Ti alloy has been selected for use in the manufacture of a portion of the DIII-D Radiative Divertor (RD) upgrade. The production of a 1200-kg ingot of V-4Cr-4Ti alloy has been completed at Teledyne Wah Chang of Albany, Oregon (TWCA) to provide ∼800-kg of applicable product forms, and two billets have been extruded from the ingot. Chemical compositions of the ingot and both extruded billets were acceptable. Material from these billets will be converted into product forms suitable for components of the DIII-D Radiative Divertor structure. Joining of V-4Cr-4Ti alloy has been identified as the most critical fabrication issue for its use in the RD Program, and research into several joining methods for fabrication of the RD components, including resistance seam, friction, and electron beam welding, is continuing. Preliminary trials have been successful in the joining of V-alloy to itself by electron beam, resistance, and friction welding processes and to Inconel 625 by friction welding

  11. Experience at the Los Alamos Meson Physics Facility with the use of alloy Inconel 718 as an enclosure for a beam degrader and as a proton beam entry window

    International Nuclear Information System (INIS)

    Sommer, W.F.; Ferguson, P.D.; Brown, R.D.; Cedillo, C.M.; Zimmerman, E.

    1994-01-01

    Operation of the Los Alamos Meson Physics Facility (LAMPF) began in 1972 and continues at present. An injector delivers protons to a 0.8 kin long linear accelerator which produces a particle energy of 800 MeV; the protons are then transported to a variety of experimental areas. The proton beam is transported in a vacuum tube, controlled and bent by electromagnets. The highest intensity beam, at a maximum level of 1 mA, is delivered to the experimental area designated as Area A. At the end of the experimental area, the beam is transported through an interface between beamline vacuum and one atmosphere air pressure. This interface is made of metal and is generally referred to as a beam entry window. At LAMPF, after the beam has exited the vacuum tube, it becomes incident on a number of experiments or ''targets.'' These include capsules for radiation damage studies, a beam ''degrader'' for the long-term neutrino experiment, and as many nine targets in the Isotope Production (IP) stringer system used to produce medically significant isotopes. Following the IP system is a beam stop used for the purpose its name implies. The beam stop also contains a beam entry window, whose purpose is to separate the 250 psig water cooling environment from I atmosphere of air. The beam entry window, the beam degrader, and the beam stop window are made of alloy Inconel 718, have endured a lengthy irradiation service time at LAMPF, and are the subject of this report

  12. Release of corrosion products from construction materials containing cobalt. Pt.2: Inconel X750

    International Nuclear Information System (INIS)

    Falk, I.

    1978-02-01

    This report describes experimental work aimed at determining the release rate for corrosion products from 18Cr8Ni steel and Inconel X750 in BWR environments. For test purposes these environments were simulated in a high pressure loop, where irradiated samples of the materials were exposed for 720 hours. The amounts of released products were determined using gamma spectrometric analysis. The results show that the release from Inconel X750 is higher than that from 18Cr8Ni steel. The release calculated from Co58 measurements is 7 times higher and from Co60 measurements it is 1.5 times higher. Both the filtered and the deposited fractions of the released corrosion products exhibit the same relative concentrations of Co58 and Co60. (author)

  13. Diffusion of Hydrogen and Helium in Inconel 625

    Science.gov (United States)

    Palosz, W.; Gillies, D.; Lehoczky, S.

    2006-01-01

    Diffusion parameters for hydrogen and helium in Inconel 625 were investigated. The dependence of permeability of hydrogen in the temperature range 310 - 750 C is given. Solubility of hydrogen at 1 atm in the range 640 - 860 C was determined and diffusivity of the gas was calculated. Experiments with diffusion and solubility at 0.09 atm suggest a molecular mechanism of solution of hydrogen in the material. Diffusivity of helium was estimated at less than 10(exp -18) sq cm/s (at 1040 C).

  14. 40 CFR 141.601 - Standard monitoring.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 22 2010-07-01 2010-07-01 false Standard monitoring. 141.601 Section... Standard monitoring. (a) Standard monitoring plan. Your standard monitoring plan must comply with paragraphs (a)(1) through (a)(4) of this section. You must prepare and submit your standard monitoring plan...

  15. Fuel Composition Analysis of Endothermically Heated JP-8 Fuel for Use in a Pulse Detonation Engine

    Science.gov (United States)

    2008-06-01

    FHS consisted of two concentric tube heat exchangers fabricated from inconel , a single seven-micron particulate filter, and instrumentation. In...zeolite structure is made from a silica-alumina, however the catalytic agent is proprietary information (Helfrich, 2007:5). Each inconel heat...exchanger was constructed of an inner 41 2 in. alloy 625 schedule 10 pipe and an outer 2 ½ in. alloy 600 schedule 40 pipe, 0.91 m (36 in.) in length

  16. Service experience and stress corrosion of Inconel 600 bellows expansion joints in turbine steam environments

    International Nuclear Information System (INIS)

    Kramer, L.D.; Michael, S.T.; Pement, F.W.

    The purpose of this paper is to discuss the service history of Inconel 600 expansion bellows, to illustrate a typical case of failure, propose S.C.C. mechanisms, and to rationalize the most probable mechanism. Inconel 600 is fully resistant to high-purity power plant steam (720 deg F maximum) for on-going service lifetimes which greatly exceed the incubation periods which are reported or postulated in the literature for delayed stress corrosion cracking in high-purity water tests (630-660 deg F). The only observed stress corrosion environments which are sufficiently rapidly deleterious to be consistent with failure lifetimes are molten NaOH in superheated steam or a very concentrated aqueous caustic solution containing silica contamination. (author)

  17. Predictive methodology to address PWSCC of Alloy 600 locations in PWRS

    International Nuclear Information System (INIS)

    Rao, G.V.

    1992-01-01

    Contributing factors to primary water stress corrosion cracking (PWSCC) are susceptible microstructure, temperature, and residual and applied stresses. In order to predict PWSCC of Inconel 600 components in PWR type reactors, a number of steps were taken. All Inconel 600 components were located, fabrication history, weld procedures and material properties were identified. Service temperatures and approximate stresses were determined. Precise service stress evaluations of Inconel 600 locations by Finite Element and other analytical evaluations were made. Using data analysis, relative PWSCC susceptibility evaluations of Inconel 600 locations were made on the basis of the Westinghouse RSI model. Finally, a prioritized inspection plan for Inconel 600 locations was developed and recommendations provided. 11 figs., 2 tabs

  18. Laser cladding of Inconel 625-based composite coatings reinforced by porous chromium carbide particles

    Science.gov (United States)

    Janicki, Damian

    2017-09-01

    Inconel 625/Cr3C2 composite coatings were produced via a laser cladding process using Cr3C2 reinforcing particles presenting an open porosity of about 60%. A laser cladding system used consisted of a direct diode laser with a rectangular beam spot and the top-hat beam profile, and an off-axis powder injection nozzle. The microstructural characteristics of the coatings was investigated with the use of scanning electron microscopy and X-ray diffraction. A complete infiltration of the porous structure of Cr3C2 reinforcing particles and low degree of their dissolution have been achieved in a very narrow range of processing parameters. Crack-free composite coatings having a uniform distribution of the Cr3C2 particles and their fraction up to 36 vol% were produced. Comparative erosion tests between the Inconel 625/Cr3C2 composite coatings and the metallic Inconel 625 coatings were performed following the ASTM G 76 standard test method. It was found that the composite coatings have a significantly higher erosion resistance to that of metallic coatings for both 30° and 90° impingement angles. Additionally, the erosion performances of composite coatings were similar for both the normal and oblique impact conditions. The erosive wear behaviour of composite coatings is discussed and related to the unique microstructure of these coatings.

  19. Investigation of corrosion and analysis of passive films concerning some nickel alloys and stainless steels in reconstructed geological environments

    International Nuclear Information System (INIS)

    Jallerat, Nelly

    1984-01-01

    This research thesis addresses the corrosion behaviour of materials which might be used for the fabrication of radioactive waste containers. After a bibliographical study on films formed on Fe-Cr-Ni alloys, this research concentrates on passivation and de-passivation phenomena of three nickel-base alloys among the most resistant to corrosion and which also meet processing and economic criteria: Hastelloy C4, Inconel 625 and ZICNDU 25-20. Titanium and Ti-Pd alloy are also studied. Parameters governing pitting corrosion are notably studied. After a recall of knowledge on passive films formed on Fe-Cr-Ni alloys, and a presentation of experimental and technical conditions, the author reports and discussed the results obtained by electrochemical studies, reports the determination of factors governing alloy passivation in geological waters. The influence of some soluble impurities is notably studied. The author reports the analysis by glow discharge optical emission spectrometry to determine the composition of passive films with respect to geological water nature, the immersion duration and the electrode potential. Additional surface analyses are performed by X-ray photoelectron spectrometry (XPS or ESCA) and secondary ion mass spectrometry (SIMS). Finally, the author uses a dosing method by neutron radio-activation of alloy elements to determine dissolution mechanisms [fr

  20. Experimental and modeling results of creep fatigue life of Inconel 617 and Haynes 230 at 850 C

    International Nuclear Information System (INIS)

    Chen, Xiang; Sokolov, Mikhail A.; Sham, Sam; Erdman, Donald L. III; Busby, Jeremy T.; Mo, Kun; Stubbins, James

    2013-01-01

    Creep fatigue testing of Ni-based superalloy Inconel 617 and Haynes 230 were conducted in the air at 850 C. Tests were performed with fully reversed axial strain control at a total strain range of 0.5%, 1.0% or 1.5% and hold time at maximum tensile strain for 3, 10 or 30 min. In addition, two creep fatigue life prediction methods, i.e. linear damage summation and frequency-modified tensile hysteresis energy modeling, were evaluated and compared with experimental results. Under all creep fatigue tests, Haynes 230 performed better than Inconel 617. Compared to the low cycle fatigue life, the cycles to failure for both materials decreased under creep fatigue test conditions. Longer hold time at maximum tensile strain would cause a further reduction in both material creep fatigue life. The linear damage summation could predict the creep fatigue life of Inconel 617 for limited test conditions, but considerably underestimated the creep fatigue life of Haynes 230. In contrast, frequency-modified tensile hysteresis energy modeling showed promising creep fatigue life prediction results for both materials.

  1. Development of an inconel self powered neutron detector for in-core reactor monitoring

    Science.gov (United States)

    Alex, M.; Ghodgaonkar, M. D.

    2007-04-01

    The paper describes the development and testing of an Inconel600 (2 mm diameter×21 cm long) self-powered neutron detector for in-core neutron monitoring. The detector has 3.5 mm overall diameter and 22 cm length and is integrally coupled to a 12 m long mineral insulated cable. The performance of the detector was compared with cobalt and platinum detectors of similar dimensions. Gamma sensitivity measurements performed at the 60Co irradiation facility in 14 MR/h gamma field showed values of -4.4×10 -18 A/R/h/cm (-9.3×10 -24 A/ γ/cm 2-s/cm), -5.2×10 -18 A/R/h/cm (-1.133×10 -23 A/ γ/cm 2-s/cm) and 34×10 -18 A/R/h/cm (7.14×10 -23 A/ γ/cm 2-s/cm) for the Inconel, Co and Pt detectors, respectively. The detectors together with a miniature gamma ion chamber and fission chamber were tested in the in-core Apsara Swimming Pool type reactor. The ion chambers were used to estimate the neutron and gamma fields. With an effective neutron cross-section of 4b, the Inconel detector has a total sensitivity of 6×10 -23 A/nv/cm while the corresponding sensitivities for the platinum and cobalt detectors were 1.69×10 -22 and 2.64×10 -22 A/nv/cm. The linearity of the detector responses at power levels ranging from 100 to 200 kW was within ±5%. The response of the detectors to reactor scram showed that the prompt response of the Inconel detector was 0.95 while it was 0.7 and 0.95 for the platinum and cobalt self-powered detectors, respectively. The detector was also installed in the horizontal flux unit of 540 MW Pressurised Heavy Water Reactor (PHWR). The neutron flux at the detector location was calculated by Triveni code. The detector response was measured from 0.02% to 0.07% of full power and showed good correlation between power level and detector signals. Long-term tests and the dynamic response of the detector to shut down in PHWR are in progress.

  2. Development of an inconel self powered neutron detector for in-core reactor monitoring

    International Nuclear Information System (INIS)

    Alex, M.; Ghodgaonkar, M.D.

    2007-01-01

    The paper describes the development and testing of an Inconel600 (2 mm diameterx21 cm long) self-powered neutron detector for in-core neutron monitoring. The detector has 3.5 mm overall diameter and 22 cm length and is integrally coupled to a 12 m long mineral insulated cable. The performance of the detector was compared with cobalt and platinum detectors of similar dimensions. Gamma sensitivity measurements performed at the 60 Co irradiation facility in 14 MR/h gamma field showed values of -4.4x10 -18 A/R/h/cm (-9.3x10 -24 A/γ/cm 2 -s/cm), -5.2x10 -18 A/R/h/cm (-1.133x10 -23 A/γ/cm 2 -s/cm) and 34x10 -18 A/R/h/cm (7.14x10 -23 A/γ/cm 2 -s/cm) for the Inconel, Co and Pt detectors, respectively. The detectors together with a miniature gamma ion chamber and fission chamber were tested in the in-core Apsara Swimming Pool type reactor. The ion chambers were used to estimate the neutron and gamma fields. With an effective neutron cross-section of 4b, the Inconel detector has a total sensitivity of 6x10 -23 A/nv/cm while the corresponding sensitivities for the platinum and cobalt detectors were 1.69x10 -22 and 2.64x10 -22 A/nv/cm. The linearity of the detector responses at power levels ranging from 100 to 200 kW was within ±5%. The response of the detectors to reactor scram showed that the prompt response of the Inconel detector was 0.95 while it was 0.7 and 0.95 for the platinum and cobalt self-powered detectors, respectively. The detector was also installed in the horizontal flux unit of 540 MW Pressurised Heavy Water Reactor (PHWR). The neutron flux at the detector location was calculated by Triveni code. The detector response was measured from 0.02% to 0.07% of full power and showed good correlation between power level and detector signals. Long-term tests and the dynamic response of the detector to shut down in PHWR are in progress

  3. Evaluation of the Low Heat Input Process for Weld Repair of Nickel-Base Superalloys

    Science.gov (United States)

    Durocher, J.; Richards, N. L.

    2011-10-01

    The repair of turbine blades and vanes commonly involves gas tungsten arc welding or an equivalent process, but unfortunately these components are often susceptible to heat-affected zone (HAZ) cracking during the weld repair process. This is a major problem especially in cast alloys due to their coarse-grain size and where the (Al + Ti) contents is in excess of 3-4%; vacuum brazing is also used but mainly on low stress non-rotating components such as vanes. Micro-welding has the potential to deposit small amounts of filler at low heat input levels with minimum HAZ and thus is an attractive process for depositing a quality weld. As with conventional fusion processes, the filler alloy is deposited by the generation of a low power arc between a consumable electrode and the substrate. The low heat input of this process offers unique advantages over more common welding processes such as gas tungsten arc, plasma arc, laser, and electron beam welding. In this study, the low heat input characteristic of micro-welding has been used to simulate weld repair using Inconel (IN) (Inconel and IN are trademarks of INCO Alloys International) 625, Rene (Rene is a trademark of General Electric Company) 41, Nimonic (Nimonic is a trademark of INCO Alloys International) 105 and Inconel 738LC filler alloys, to a cast Inconel 738LC substrate. The effect of micro-welding process parameters on the deposition rate, coating quality, and substrate has been investigated.

  4. STUDY OF THE MECHANICAL PROPERTIES OF INCONEL 718 SUPERALLOY AFTER HOT TENSILE TESTS

    Directory of Open Access Journals (Sweden)

    Tarcila Sugahara

    2014-10-01

    Full Text Available This research work investigated some important mechanical properties of Inconel 718 superalloy using hot tensile tests like conventional yield strength to 0.2% strain (σe , ultimate strength (σr , and specific elongation (εu . Samples were strained to failure at temperatures of 600°C, 650°C, 700°C, 750°C, 800°C and 850°C and strain rate of 0.5 mm/min (2 × 10–4 s–1 according to ASTM E-8. The results showed higher values σe of yield strength at 700°C, this anomalous behavior can be attributed to the presence of hardening precipitates as observed in the TTT diagram of superalloy Inconel 718. Examination of the sample’s surfaces tensile fracture showed that with increasing temperature test the actuating mechanism changes from intergranular fracture to coalescence of the microcavities.

  5. Influence of Support Configurations on the Characteristics of Selective Laser-Melted Inconel 718

    Science.gov (United States)

    Nadammal, Naresh; Kromm, Arne; Saliwan-Neumann, Romeo; Farahbod, Lena; Haberland, Christoph; Portella, Pedro Dolabella

    2018-03-01

    Samples fabricated using two different support configurations by following identical scan strategies during selective laser melting of superalloy Inconel 718 were characterized in this study. Characterization methods included optical microscopy, electron back-scattered diffraction and x-ray diffraction residual stress measurement. For the scan strategy considered, microstructure and residual stress development in the samples were influenced by the support structures. However, crystallographic texture intensity and the texture components formed within the core part of the samples were almost independent of the support. The formation of finer grains closer to the support as well as within the columnar grain boundaries resulted in randomization and texture intensity reduction by nearly half for the sample built on a lattice support. Heat transfer rates dictated by the support configurations in addition to the scan strategy influenced the microstructure and residual stress development in selective laser-melted Inconel 718 samples.

  6. Tests with Inconel 600 to obtain quantitative stress-corrosion cracking data for evaluating service performance

    International Nuclear Information System (INIS)

    Bandy, R.; van Rooyen, D.

    1982-09-01

    Inconel 600 tubes in pressurized water reactor (PWR) steam generators form a pressure boundary between radioactive primary water and secondary water which is converted to steam and used for generating electricity. Under operating conditions the performance of alloy 600 has been good, but with some occasional small leaks resulting from stress corrosion cracking (SCC), related to the presence of unusually high residual or operating stresses. The suspected high stresses can result from either the deformation of tubes during manufacture, or distortion during abnormal conditions such as denting. The present experimental program addresses two specific conditions, i.e., (1) where deformation occurs but is no longer active, such as when denting is stopped and (2) where plastic deformation of the metal continues, as would occur during denting. Laboratory media consist of pure water as well as solutions to simulate environments that would apply in service; tubing from actual production is used in carrying out these tests. The environments include both normal and off chemistries for primary and secondary water. The results reported here were obtained in several different tests. The main ones are (1) split tube reverse U-bends, (2) constant extension rate tests (CERT), and (3) constant load. The temperature range covered is 290 to 365 0 C

  7. Progress toward determining the potential of ODS alloys for gas turbine applications

    Science.gov (United States)

    Dreshfield, R. L.; Hoppin, G., III; Sheffler, K.

    1983-01-01

    The Materials for Advanced Turbine Engine (MATE) Program managed by the NASA Lewis Research Center is supporting two projects to evaluate the potential of oxide dispersion strengthened (ODS) alloys for aircraft gas turbine applications. One project involves the evaluation of Incoloy (TM) MA-956 for application as a combustor liner material. An assessment of advanced engine potential will be conducted by means of a test in a P&WA 2037 turbofan engine. The other project involves the evaluation of Inconel (TM) MA 6000 for application as a high pressure turbine blade material and includes a test in a Garrett TFE 731 turbofan engine. Both projects are progressing toward these engine tests in 1984.

  8. The effect of phosphorus on the microstructure and mechanical properties of ATI 718Plus alloy

    International Nuclear Information System (INIS)

    Wang, Minqing; Du, Jinhui; Deng, Qun; Tian, Zhiling; Zhu, Jing

    2015-01-01

    Since the discovery in the 1990s of the abnormal improvement produced by phosphorus in the stress rupture and creep life of Inconel 718 (hereafter referred to as 718), a great deal of additional research followed. However, the mechanism of the action of phosphorous in 718 is still in question. This paper details an experimental study that was intended to determine how phosphorus acts upon the microstructure and mechanical properties of Ni–Fe based alloy 718Plus. The results show that phosphorus has little effect on the strength and ductility of alloy 718Plus, but can significantly improve the stress rupture life. Phase constituents such as the δ and γ′ phases were quantitatively analyzed using electrolytic phase isolation and micro-chemical and XRD analysis as the phosphorous content of the alloy was increased. A full atom mapping of the distribution of phosphorus in the 718Plus alloy was quantitatively determined using APT (Atom Probe Tomography) technique. The results showed that there is no significant segregation of phosphorus at the γ′/γ and γ′/γ′ interface, but it significantly segregates at the grain boundaries and δ/γ interface. It was found that phosphorus is extremely depleted in the δ phase, which is believed to inhibit δ-phase precipitation by preventing δ phase nucleation and growth in the 718Plus alloy. Finally, the influence of phosphorus on the microstructure and mechanical properties of the 718Plus alloy was discussed

  9. The effect of phosphorus on the microstructure and mechanical properties of ATI 718Plus alloy

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Minqing, E-mail: minqingw@yahoo.com [Central Iron and Steel Research Institute, Beijing 100081 (China); School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Beijing Key Laboratory of Advanced High Temperature Materials, Beijing 100081 (China); Du, Jinhui; Deng, Qun [Central Iron and Steel Research Institute, Beijing 100081 (China); Beijing Key Laboratory of Advanced High Temperature Materials, Beijing 100081 (China); Tian, Zhiling [Central Iron and Steel Research Institute, Beijing 100081 (China); Zhu, Jing, E-mail: jzhu@mail.tsinghua.edu.cn [School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China)

    2015-02-25

    Since the discovery in the 1990s of the abnormal improvement produced by phosphorus in the stress rupture and creep life of Inconel 718 (hereafter referred to as 718), a great deal of additional research followed. However, the mechanism of the action of phosphorous in 718 is still in question. This paper details an experimental study that was intended to determine how phosphorus acts upon the microstructure and mechanical properties of Ni–Fe based alloy 718Plus. The results show that phosphorus has little effect on the strength and ductility of alloy 718Plus, but can significantly improve the stress rupture life. Phase constituents such as the δ and γ′ phases were quantitatively analyzed using electrolytic phase isolation and micro-chemical and XRD analysis as the phosphorous content of the alloy was increased. A full atom mapping of the distribution of phosphorus in the 718Plus alloy was quantitatively determined using APT (Atom Probe Tomography) technique. The results showed that there is no significant segregation of phosphorus at the γ′/γ and γ′/γ′ interface, but it significantly segregates at the grain boundaries and δ/γ interface. It was found that phosphorus is extremely depleted in the δ phase, which is believed to inhibit δ-phase precipitation by preventing δ phase nucleation and growth in the 718Plus alloy. Finally, the influence of phosphorus on the microstructure and mechanical properties of the 718Plus alloy was discussed.

  10. The Study on bonding test of Inconel 617 Heat Exchanger by Measuring Properties

    International Nuclear Information System (INIS)

    Cho, Il Hwan; Song, Chan Ho; Yoon, Seok Ho; Park, Sang Jin

    2014-01-01

    Basic materials are not melted and bonded through the diffusion of atoms. It is different from welding in a view point of not melting and additional bonding insertion materials are not used which is different from the method in brazing. This bonding method is favor for ultra high temperature and pressure condition, and the bonding part becomes almost same structure and property with high heat resistance and strength when it is compared with brazing method. But the process time is long and the cost is high. The quantitative analysis in bonding surface has not been suggested yet. In this paper, the bonding performance for diffusion bonded heat exchanger is examined and analyzed where its material is Inconel 617. thermal and mechanical properties such as thermal diffusivity and tensile strength are measured and compared for different bonding conditions. In this study, the bonding performance for heat exchanger using Inconel 617 is analyzed by measuring thermal and mechanical properties such as thermal diffusivity and tensile strength. The following results are obtained. From measuring thermal diffusivity, it is found that the difference between the diffusion bonded plates and bond failed plates is within 3%. The tensile strength in diffusion bonding is about 25% lower than that of original plate at 1150 .deg. C, but it is over 600 MPa. As bonding temperature increases, the size of grain boundary decreases From these results, the possibility for Inconel 617 heat exchanger under the high temperature and pressure through diffusion bonding process could be obtained and it is thought to be applied for many industrial equipment

  11. The Study on bonding test of Inconel 617 Heat Exchanger by Measuring Properties

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Il Hwan; Song, Chan Ho; Yoon, Seok Ho; Park, Sang Jin [Korea Institute of Machinery and Materials, Daejeon (Korea, Republic of)

    2014-05-15

    Basic materials are not melted and bonded through the diffusion of atoms. It is different from welding in a view point of not melting and additional bonding insertion materials are not used which is different from the method in brazing. This bonding method is favor for ultra high temperature and pressure condition, and the bonding part becomes almost same structure and property with high heat resistance and strength when it is compared with brazing method. But the process time is long and the cost is high. The quantitative analysis in bonding surface has not been suggested yet. In this paper, the bonding performance for diffusion bonded heat exchanger is examined and analyzed where its material is Inconel 617. thermal and mechanical properties such as thermal diffusivity and tensile strength are measured and compared for different bonding conditions. In this study, the bonding performance for heat exchanger using Inconel 617 is analyzed by measuring thermal and mechanical properties such as thermal diffusivity and tensile strength. The following results are obtained. From measuring thermal diffusivity, it is found that the difference between the diffusion bonded plates and bond failed plates is within 3%. The tensile strength in diffusion bonding is about 25% lower than that of original plate at 1150 .deg. C, but it is over 600 MPa. As bonding temperature increases, the size of grain boundary decreases From these results, the possibility for Inconel 617 heat exchanger under the high temperature and pressure through diffusion bonding process could be obtained and it is thought to be applied for many industrial equipment.

  12. Corrosion fatigue cracking behavior of Inconel 690 (TT) in secondary water of pressurized water reactors

    International Nuclear Information System (INIS)

    Xiao Jun; Chen Luyao; Qiu Shaoyu; Chen Yong; Lin Zhenxia; Fu Zhenghong

    2015-01-01

    Inconel 690 (TT) is one of the key materials for tubes of steam generators for pressurized water reactors, where it is susceptible to corrosion fatigue cracking. In this paper, the corrosion fatigue cracking behavior of Inconel 690 (TT) was investigated under small scale yielding conditions, in the simulated secondary water of pressurized water reactor. It was observed that the fatigue crack growth rate was accelerated by a maximum factor up to 3 in the simulated secondary water, comparing to that in room temperature air. In addition, it was found that the accelerating effect was influenced by out-of-plane cracking of corrosion fatigue cracks and also correlated with stress intensity factor range, maximum stress intensity factor and stress ratio. (authors)

  13. 26 CFR 601.806 - Solicitation of applications.

    Science.gov (United States)

    2010-04-01

    ... Internal Revenue Service Tax Counseling for the Elderly program should request an application from the: Program Manager, Tax Counseling for the Elderly, Taxpayer Service Division TX:T:I, Internal Revenue... 601.806 Internal Revenue INTERNAL REVENUE SERVICE, DEPARTMENT OF THE TREASURY (CONTINUED) INTERNAL...

  14. Production of UT Reference Blocks Containing Artificially Introduced Defects

    International Nuclear Information System (INIS)

    Kaya, A. A.; Ucuncuoglu, S.; Kurkcu, N.; Kandemir, A.; Arslan, H.

    2007-01-01

    Metallic blocks of Inconel 718 and Ti-6A1-4V alloys that contain artificially introduced defects of known type, size, shape and location were prepared to serve as calibration standards in ultrasonic inspection. The synthetic defects employed to serve as reflectors were all pertinent to the specific alloy systems used, i.e. compositional defects termed as 'dirty white' 'white spot' and 'freckle' for Inconel 718; 'hard-alpha' for titanium alloy. Furthermore, as a defect type common to all three materials, spherical voids of various sizes were also incorporated into these calibration blocks. The aim of this study is to introduce defects of known type and size into metallic blocks made of superalloy Inconel 718 and titanium Ti-6A1-4V alloy. The scope of the study entailed determination of the correct parameters for manufacturing processes involved. Based on the results of the preceding phases of this study, it was decided that the method of Vacuum Hot Pressing (VHP) was to be used in this project to manufacture the metallic block containing artificial defects

  15. Design of a single variable helium effects experiment for irradiation in FFTF [Fast Flux Test Facility] using alloys enriched in nickel 59

    International Nuclear Information System (INIS)

    Simons, R.L.; Brager, H.R.; Matsumoto, W.Y.

    1986-03-01

    Nickel enriched in nickel 59 was extracted from the fragments of a fracture toughness specimen of Inconel 600 irradiated in the Engineering Test Reactor (ETR). The nickel contained 2.0% nickel 59. Three heats of austenitic steel doped with nickel-59 were prepared and inserted in the Materials Open Test Assembly (MOTA) of the Fast Flux Test Facility (FFTF). The experiment was single variable in helium effects because chemically identical alloys without nickel-59 were being irradiated side by side with the doped material. The alloys doped with nickel 59 produced 10 to 100 times more helium than the control alloys. The materials included ternary and quaternary alloys in the form of transmission electron microscope (TEM) discs and miniature tensile specimens. The helium to dpa ratio was in the range 5 to 35 and was nearly constant throughout the irradiation. The exposures ranged from 0.25 to 50 displacements per atom (dpa) over the duration of the experiment. The irradiation temperatures covered the range of 360 to 600 0 C

  16. Face compression yield strength of the copper-Inconel composite specimen

    International Nuclear Information System (INIS)

    Horie, T.

    1987-05-01

    A new equation for the face compression yield strength of copper-Inconel composite material has been derived. Elastic-plastic finite element analyses were also made for composite specimens with various aspect ratios to examine the edge effect of the specimen. According to the results of both the new equation and the analyses, the face compression yield strength of the composite should be decreased by about 25% from the value obtained with Becker's equation

  17. Experimental Investigation of Principal Residual Stress and Fatigue Performance for Turned Nickel-Based Superalloy Inconel 718.

    Science.gov (United States)

    Hua, Yang; Liu, Zhanqiang

    2018-05-24

    Residual stresses of turned Inconel 718 surface along its axial and circumferential directions affect the fatigue performance of machined components. However, it has not been clear that the axial and circumferential directions are the principle residual stress direction. The direction of the maximum principal residual stress is crucial for the machined component service life. The present work aims to focuses on determining the direction and magnitude of principal residual stress and investigating its influence on fatigue performance of turned Inconel 718. The turning experimental results show that the principal residual stress magnitude is much higher than surface residual stress. In addition, both the principal residual stress and surface residual stress increase significantly as the feed rate increases. The fatigue test results show that the direction of the maximum principal residual stress increased by 7.4%, while the fatigue life decreased by 39.4%. The maximum principal residual stress magnitude diminished by 17.9%, whereas the fatigue life increased by 83.6%. The maximum principal residual stress has a preponderant influence on fatigue performance as compared to the surface residual stress. The maximum principal residual stress can be considered as a prime indicator for evaluation of the residual stress influence on fatigue performance of turned Inconel 718.

  18. Experimental Investigation of Principal Residual Stress and Fatigue Performance for Turned Nickel-Based Superalloy Inconel 718

    Directory of Open Access Journals (Sweden)

    Yang Hua

    2018-05-01

    Full Text Available Residual stresses of turned Inconel 718 surface along its axial and circumferential directions affect the fatigue performance of machined components. However, it has not been clear that the axial and circumferential directions are the principle residual stress direction. The direction of the maximum principal residual stress is crucial for the machined component service life. The present work aims to focuses on determining the direction and magnitude of principal residual stress and investigating its influence on fatigue performance of turned Inconel 718. The turning experimental results show that the principal residual stress magnitude is much higher than surface residual stress. In addition, both the principal residual stress and surface residual stress increase significantly as the feed rate increases. The fatigue test results show that the direction of the maximum principal residual stress increased by 7.4%, while the fatigue life decreased by 39.4%. The maximum principal residual stress magnitude diminished by 17.9%, whereas the fatigue life increased by 83.6%. The maximum principal residual stress has a preponderant influence on fatigue performance as compared to the surface residual stress. The maximum principal residual stress can be considered as a prime indicator for evaluation of the residual stress influence on fatigue performance of turned Inconel 718.

  19. 3D printing of high-strength aluminium alloys.

    Science.gov (United States)

    Martin, John H; Yahata, Brennan D; Hundley, Jacob M; Mayer, Justin A; Schaedler, Tobias A; Pollock, Tresa M

    2017-09-20

    Metal-based additive manufacturing, or three-dimensional (3D) printing, is a potentially disruptive technology across multiple industries, including the aerospace, biomedical and automotive industries. Building up metal components layer by layer increases design freedom and manufacturing flexibility, thereby enabling complex geometries, increased product customization and shorter time to market, while eliminating traditional economy-of-scale constraints. However, currently only a few alloys, the most relevant being AlSi10Mg, TiAl6V4, CoCr and Inconel 718, can be reliably printed; the vast majority of the more than 5,500 alloys in use today cannot be additively manufactured because the melting and solidification dynamics during the printing process lead to intolerable microstructures with large columnar grains and periodic cracks. Here we demonstrate that these issues can be resolved by introducing nanoparticles of nucleants that control solidification during additive manufacturing. We selected the nucleants on the basis of crystallographic information and assembled them onto 7075 and 6061 series aluminium alloy powders. After functionalization with the nucleants, we found that these high-strength aluminium alloys, which were previously incompatible with additive manufacturing, could be processed successfully using selective laser melting. Crack-free, equiaxed (that is, with grains roughly equal in length, width and height), fine-grained microstructures were achieved, resulting in material strengths comparable to that of wrought material. Our approach to metal-based additive manufacturing is applicable to a wide range of alloys and can be implemented using a range of additive machines. It thus provides a foundation for broad industrial applicability, including where electron-beam melting or directed-energy-deposition techniques are used instead of selective laser melting, and will enable additive manufacturing of other alloy systems, such as non-weldable nickel

  20. 3D printing of high-strength aluminium alloys

    Science.gov (United States)

    Martin, John H.; Yahata, Brennan D.; Hundley, Jacob M.; Mayer, Justin A.; Schaedler, Tobias A.; Pollock, Tresa M.

    2017-09-01

    Metal-based additive manufacturing, or three-dimensional (3D) printing, is a potentially disruptive technology across multiple industries, including the aerospace, biomedical and automotive industries. Building up metal components layer by layer increases design freedom and manufacturing flexibility, thereby enabling complex geometries, increased product customization and shorter time to market, while eliminating traditional economy-of-scale constraints. However, currently only a few alloys, the most relevant being AlSi10Mg, TiAl6V4, CoCr and Inconel 718, can be reliably printed; the vast majority of the more than 5,500 alloys in use today cannot be additively manufactured because the melting and solidification dynamics during the printing process lead to intolerable microstructures with large columnar grains and periodic cracks. Here we demonstrate that these issues can be resolved by introducing nanoparticles of nucleants that control solidification during additive manufacturing. We selected the nucleants on the basis of crystallographic information and assembled them onto 7075 and 6061 series aluminium alloy powders. After functionalization with the nucleants, we found that these high-strength aluminium alloys, which were previously incompatible with additive manufacturing, could be processed successfully using selective laser melting. Crack-free, equiaxed (that is, with grains roughly equal in length, width and height), fine-grained microstructures were achieved, resulting in material strengths comparable to that of wrought material. Our approach to metal-based additive manufacturing is applicable to a wide range of alloys and can be implemented using a range of additive machines. It thus provides a foundation for broad industrial applicability, including where electron-beam melting or directed-energy-deposition techniques are used instead of selective laser melting, and will enable additive manufacturing of other alloy systems, such as non-weldable nickel

  1. Long fatigue crack growth in Inconel 718 produced by selective laser melting

    Czech Academy of Sciences Publication Activity Database

    Konečná, R.; Kunz, Ludvík; Nicoletto, G.; Bača, A.

    2016-01-01

    Roč. 92, NOV (2016), s. 499-506 ISSN 0142-1123. [CP 2015 - International Conference on Crack Paths /5./. Ferrara, 16.09.2015-18.09.2015] Institutional support: RVO:68081723 Keywords : Inconel 718 * Selective laser melting * Microstructure * Fatigue crack growth * Fractography Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 2.899, year: 2016

  2. Influence Of The Laser Cladding Strategies On The Mechanical Properties Of Inconel 718

    International Nuclear Information System (INIS)

    Lamikiz, A.; Tabernero, I.; Ukar, E.; Lopez de Lacalle, L. N.; Delgado, J.

    2011-01-01

    This work presents different experimental results of the mechanical properties of Inconel registered 718 test parts built-up by laser cladding. Recently, turbine manufacturers for aeronautical sector have presented high interest on laser cladding processes. This process allows building fully functional structures on superalloys, such as Inconel registered 718, with high flexibility on complex shapes. However, there is limited data on mechanical properties of the laser cladding structures. Moreover, the available data do not include the influence of process parameters and laser cladding strategies. Therefore, a complete study of the influence of the laser cladding parameters and mainly, the variation of the tensile strength with the laser cladding strategy is presented. The results show that there is a high directionality of mechanical properties, depending on the strategies of laser cladding process. In other words, the test parts show a fiber -like structure that should be considered on the laser cladding strategy selection.

  3. Methodology to evaluate the crack growth rate by stress corrosion cracking in dissimilar metals weld in simulated environment of PWR nuclear reactor

    International Nuclear Information System (INIS)

    Paula, Raphael G.; Figueiredo, Celia A.; Rabelo, Emerson G.

    2013-01-01

    Inconel alloys weld metal is widely used to join dissimilar metals in nuclear reactors applications. It was recently observed failures of weld components in plants, which have triggered an international effort to determine reliable data on the stress corrosion cracking behavior of this material in reactor environment. The objective of this work is to develop a methodology to determine the crack growth rate caused by stress corrosion in Inconel alloy 182, using the specimen (Compact Tensile) in simulated PWR environment. (author)

  4. 2 CFR 601.1010 - Suspending Official (Department of Energy supplement to government-wide definition at 2 CFR 180...

    Science.gov (United States)

    2010-01-01

    ... SUSPENSION Definitions § 601.1010 Suspending Official (Department of Energy supplement to government-wide... 2 Grants and Agreements 1 2010-01-01 2010-01-01 false Suspending Official (Department of Energy supplement to government-wide definition at 2 CFR 180.1010). 601.1010 Section 601.1010 Grants and Agreements...

  5. Aspectos metalúrgicos de revestimentos dissimilares com a superliga à base de níquel inconel 625 Metallurgical aspects of dissimilar weld overlays of inconel 625 nickel based superalloys

    Directory of Open Access Journals (Sweden)

    Cleiton Carvalho Silva

    2012-09-01

    Full Text Available Prolongar a vida útil e aumentar a confiabilidade de equipamentos e tubulações de plantas de produção e processamento de petróleo é uma busca constante no setor de petróleo e gás. Tais aspectos dependem essencialmente do uso de ligas resistentes à corrosão. Neste contexto, a soldagem de revestimento com superligas à base de níquel tem sido uma alternativa interessante, pois confere aos equipamentos uma alta resistência à corrosão com um custo inferior, se comparado à fabricação de componentes ou tubulações maciças com superligas. Assim, o objetivo do presente trabalho foi investigar o comportamento metalúrgico de revestimento de superliga à base de níquel do tipo Inconel 625 depositados pelo processo TIG com alimentação de arame frio. As soldagens foram realizadas em uma bancada robotizada, empregando uma fonte eletrônica de soldagem com sistema de aquisição de dados para o monitoramento dos sinais de corrente e tensão. A caracterização microestrutural foi realizada através das técnicas de microscopia eletrônica de varredura (MEV e transmissão (MET, espectroscopia de energia dispersiva de raios-X (EDS. Os resultados mostraram que a microestrutura do metal de solda foi constituída por uma matriz γ com fases secundárias ricas em Nb. Foi encontrada a formação de precipitados complexos de carbonetos/nitretos de Ti e Nb.To extend the life and reliability of pipes and equipment in oil & gas production and processing settings is a continuous demand. These aspects are essentially dependent on corrosion resistant alloys used. In this context, the weld overlay with Ni-based superalloys is a great interesting alternative, since improve the corrosion resistance without increase the cost of manufacture when compared to massive equipment. Thus, the objective of this study was to evaluate the metallurgical aspects of Inconel 625 weld overlays deposited by GTAW cold wire feed process. The welds were performed using a

  6. Evaluating location specific strain rates, temperatures, and accumulated strains in friction welds through microstructure modeling

    Directory of Open Access Journals (Sweden)

    Javed Akram

    2018-04-01

    Full Text Available A microstructural simulation method is adopted to predict the location specific strain rates, temperatures, grain evolution, and accumulated strains in the Inconel 718 friction welds. Cellular automata based 2D microstructure model was developed for Inconel 718 alloy using theoretical aspects of dynamic recrystallization. Flow curves were simulated and compared with experimental results using hot deformation parameter obtained from literature work. Using validated model, simulations were performed for friction welds of Inconel 718 alloy generated at three rotational speed i.e., 1200, 1500, and 1500 RPM. Results showed the increase in strain rates with increasing rotational speed. These simulated strain rates were found to match with the analytical results. Temperature difference of 150 K was noticed from center to edge of the weld. At all the rotational speeds, the temperature was identical implying steady state temperature (0.89Tm attainment. Keywords: Microstructure modeling, Dynamic recrystallization, Friction welding, Inconel 718, EBSD, Hot deformation, Strain map

  7. Chemical decontamination and melt densification

    International Nuclear Information System (INIS)

    Dillon, R.L.; Griggs, B.; Kemper, R.S.; Nelson, R.G.

    1976-01-01

    Preliminary studies on the chemical decontamination and densification of Zircaloy, stainless steel, and Inconel undissolved residues remaining after dissolution of the UO 2 --PuO 2 spent fuel material from sheared fuel bundles are reported. The studies were made on cold or very small samples to demonstrate the feasibility of the processes developed before proceeding to hot cell demonstrations with kg level of the sources. A promising aqueous decontamination method for Zr alloy cladding was developed in which oxidized surfaces are conditioned with HF prior to leaching with ammonium oxalate, ammonium citrate, ammonium fluoride, and hydrogen peroxide. Feasibility of molten salt decontamination of oxidized Zircaloy was demonstrated. A low melting alloy of Zircaloy, stainless steel, and Inconel was obtained in induction heated graphite crucibles. Segregated Zircaloy cladding sections were directly melted by the inductoslag process to yield a metal ingot suitable for storage. Both Zircaloy and Zircaloy--stainless steel--Inconel alloys proved to be highly satisfactory getters and sinks for recovered tritium

  8. Characterization of the dissimilar welding - austenitic stainless steel with filler metal of the nickel alloy

    International Nuclear Information System (INIS)

    Soares, Bruno Amorim; Schvartzman, Monica Maria de Abreu Mendonca; Campos, Wagner Reis da Costa

    2007-01-01

    In elevated temperature environments, austenitic stainless steel and nickel alloy has a superior corrosion resistance due to its high Cr content. Consequently, this alloys is widely used in nuclear reactors components and others plants of energy generation that burn fossil fuel or gas, chemical and petrochemical industries. The object of the present work was to research the welding of AISI 304 austenitic stainless steel using the nickel alloy filler metals, Inconel 625. Gas tungsten arc welding, mechanical and metallographic tests, and compositional analysis of the joint were used. A fundamental investigation was undertaken to characterize fusion boundary microstructure and to better understand the nature and character of boundaries that are associated with cracking in dissimilar welds. The results indicate that the microstructure of the fusion zone has a dendritic structure, inclusions, and precipitated phases containing Ti and Nb are present in the inter-dendritic region. In some parts near to the fusion line it can be seen a band in the weld, probably a eutectic phase with lower melting point than the AISI 304, were the cracking may be beginning by stress corrosion. (author)

  9. Cracking in fusion zone and heat affected zone of electron beam welded Inconel-713LC gas turbine blades

    Energy Technology Data Exchange (ETDEWEB)

    Chamanfar, A., E-mail: achamanfar@gmail.com [Département de Génie Mécanique, École de Technologie Supérieure, 1100 rue Notre-Dame Ouest, Montréal, Québec, Canada H3C 1K3 (Canada); Jahazi, M. [Département de Génie Mécanique, École de Technologie Supérieure, 1100 rue Notre-Dame Ouest, Montréal, Québec, Canada H3C 1K3 (Canada); Bonakdar, A.; Morin, E. [Siemens Canada Limited, 9545 Côte-de-Liesse, Dorval, Québec, Canada H9P 1A5 (Canada); Firoozrai, A. [Département de Génie Mécanique, École de Technologie Supérieure, 1100 rue Notre-Dame Ouest, Montréal, Québec, Canada H3C 1K3 (Canada)

    2015-08-26

    Electron beam welding (EBW) of shrouds in Inconel-713LC low pressure gas turbine blades was associated with cracking in fusion zone (FZ) and heat affected zone (HAZ) leading to a high scrap rate in manufacturing of gas turbine blades. In this study, in order to develop a detailed map of cracks and understand the root cause of cracking, a comprehensive microstructural and numerical analysis was performed. The elemental mapping in scanning electron microscope (SEM)-energy dispersive spectral analysis revealed segregation of alloying elements in the cracked area of FZ and HAZ. In other words, one of the cracking mechanisms in FZ and HAZ was found to be segregation induced liquation and subsequent cracking due to thermal and mechanical tensile stresses generated during EBW. Cracking in FZ also occurred because of low strength of the solidifying weld metal as well as solidification contraction. As well, γ′ dissolution and reprecipitation in HAZ leading to decreased ductility and generation of contraction stresses was another mechanism for cracking in HAZ. The numerical model was capable to predict the cracking location as well as cracking orientation with respect to the weld line.

  10. 31 CFR 601.3 - Use of paper.

    Science.gov (United States)

    2010-07-01

    ... AND PRINTING, DEPARTMENT OF THE TREASURY DISTINCTIVE PAPER FOR UNITED STATES CURRENCY AND OTHER SECURITIES § 601.3 Use of paper. The new distinctive paper shall be used for printing Federal Reserve Notes... of the currency, will be continued for printing of any currency denomination prescribed by the...

  11. Diffusion of Cr, Fe, and Ti ions from Ni-base alloy Inconel-718 into a transition alumina coating

    Energy Technology Data Exchange (ETDEWEB)

    Dressler, M., E-mail: martin.dressler@bam.de; Nofz, M.; Doerfel, I.; Saliwan-Neumann, R.

    2012-04-30

    Heat treating metals at high temperatures trigger diffusion processes which may lead to the formation of oxide layers. In this work the diffusion of Cr, Fe and Ti into an alumina coating applied to Inconel-718 is being investigated. Mass gain measurements, UV-vis spectroscopy and transmission electron microscopy were applied in order to study the evolution of the diffusion process. It was found that mainly Cr as well as minor amounts of Fe and Ti are being incorporated into the alumina coating upon prolonged heat treatment at 700 Degree-Sign C. It could be shown that alumina coatings being void of Cr have the same oxidation related mass gain as uncoated samples. However, incorporation of Cr into the alumina coating decreased their mass gain below that of uncoated substrates forming a Cr oxide scale only. - Highlights: Black-Right-Pointing-Pointer We investigated the diffusion of Cr into alumina coatings applied on IN-718. Black-Right-Pointing-Pointer The ingress of Cr led to the formation of mixed alumina/chromium coatings. Black-Right-Pointing-Pointer The mass gain of mixed alumina/chromium coatings was compared to uncoated IN-718. Black-Right-Pointing-Pointer The mixed alumina/chromium coatings improved the oxidation resistance of IN-718.

  12. Development of an inconel self powered neutron detector for in-core reactor monitoring

    Energy Technology Data Exchange (ETDEWEB)

    Alex, M. [Electronics Division, BARC, Mumbai (India)]. E-mail: maryalex@barc.gov.in; Ghodgaonkar, M.D. [Electronics Division, BARC, Mumbai (India)

    2007-04-21

    The paper describes the development and testing of an Inconel600 (2 mm diameterx21 cm long) self-powered neutron detector for in-core neutron monitoring. The detector has 3.5 mm overall diameter and 22 cm length and is integrally coupled to a 12 m long mineral insulated cable. The performance of the detector was compared with cobalt and platinum detectors of similar dimensions. Gamma sensitivity measurements performed at the {sup 60}Co irradiation facility in 14 MR/h gamma field showed values of -4.4x10{sup -18} A/R/h/cm (-9.3x10{sup -24} A/{gamma}/cm{sup 2}-s/cm), -5.2x10{sup -18} A/R/h/cm (-1.133x10{sup -23} A/{gamma}/cm{sup 2}-s/cm) and 34x10{sup -18} A/R/h/cm (7.14x10{sup -23} A/{gamma}/cm{sup 2}-s/cm) for the Inconel, Co and Pt detectors, respectively. The detectors together with a miniature gamma ion chamber and fission chamber were tested in the in-core Apsara Swimming Pool type reactor. The ion chambers were used to estimate the neutron and gamma fields. With an effective neutron cross-section of 4b, the Inconel detector has a total sensitivity of 6x10{sup -23} A/nv/cm while the corresponding sensitivities for the platinum and cobalt detectors were 1.69x10{sup -22} and 2.64x10{sup -22} A/nv/cm. The linearity of the detector responses at power levels ranging from 100 to 200 kW was within {+-}5%. The response of the detectors to reactor scram showed that the prompt response of the Inconel detector was 0.95 while it was 0.7 and 0.95 for the platinum and cobalt self-powered detectors, respectively. The detector was also installed in the horizontal flux unit of 540 MW Pressurised Heavy Water Reactor (PHWR). The neutron flux at the detector location was calculated by Triveni code. The detector response was measured from 0.02% to 0.07% of full power and showed good correlation between power level and detector signals. Long-term tests and the dynamic response of the detector to shut down in PHWR are in progress.

  13. Effect of temperature upon the fatigue-crack propagation behavior of Inconel X-750

    International Nuclear Information System (INIS)

    James, L.A.

    1976-05-01

    The techniques of linear-elastic fracture mechanics were employed to characterize the effect of temperature upon the fatigue-crack propagation behavior of precipitation heat-treated Inconel X-750 in an air environment over the range 75-1200 0 F. In general, fatigue-crack growth rates increased with increasing test temperature

  14. Mathematical modeling and analysis of WEDM machining ...

    Indian Academy of Sciences (India)

    M P GARG

    analysis and optimization of the WEDM process parameters of Inconel 625. The four ... fields such as aerospace, missile, and nuclear industry, very complex and ... piping, the alloy continues to find new application and ... automobile, chemical processing, oil refining, marine, ... Inconel 625 is a material of choice for gas.

  15. 23 CFR 710.601 - Federal land transfer.

    Science.gov (United States)

    2010-04-01

    ... FEDERAL HIGHWAY ADMINISTRATION, DEPARTMENT OF TRANSPORTATION RIGHT-OF-WAY AND ENVIRONMENT RIGHT-OF-WAY AND REAL ESTATE Federal Assistance Programs § 710.601 Federal land transfer. (a) The provisions of this... agency will be notified and a right-of-entry requested. The land-owning agency shall have a period of...

  16. 5 CFR 551.601 - Minimum age standards.

    Science.gov (United States)

    2010-01-01

    ... ADMINISTRATION UNDER THE FAIR LABOR STANDARDS ACT Child Labor § 551.601 Minimum age standards. (a) 16-year... subject to its child labor provisions, with certain exceptions not applicable here. (b) 18-year minimum... occupation found and declared by the Secretary of Labor to be particularly hazardous for the employment of...

  17. Crack growth threshold under hold time conditions in DA Inconel 718 – A transition in the crack growth mechanism

    Directory of Open Access Journals (Sweden)

    E. Fessler

    2016-01-01

    Full Text Available Aeroengine manufacturers have to demonstrate that critical components such as turbine disks, made of DA Inconel 718, meet the certification requirements in term of fatigue crack growth. In order to be more representative of the in service loading conditions, crack growth under hold time conditions is studied. Modelling crack growth under these conditions is challenging due to the combined effect of fatigue, creep and environment. Under these conditions, established models are often conservative but the degree of conservatism can be reduced by introducing the crack growth threshold in models. Here, the emphasis is laid on the characterization of crack growth rates in the low ΔK regime under hold time conditions and in particular, on the involved crack growth mechanism. Crack growth tests were carried out at high temperature (550 °C to 650 °C under hold time conditions (up to 1200 s in the low ΔK regime using a K-decreasing procedure. Scanning electron microscopy was used to identify the fracture mode involved in the low ΔK regime. EBSD analyses and BSE imaging were also carried out along the crack path for a more accurate identification of the fracture mode. A transition from intergranular to transgranular fracture was evidenced in the low ΔK regime and slip bands have also been observed at the tip of an arrested crack at low ΔK. Transgranular fracture and slip bands are usually observed under pure fatigue loading conditions. At low ΔK, hold time cycles are believed to act as equivalent pure fatigue cycles. This change in the crack growth mechanism under hold time conditions at low ΔK is discussed regarding results related to intergranular crack tip oxidation and its effect on the crack growth behaviour of Inconel 718 alloy. A concept based on an “effective oxygen partial pressure” at the crack tip is proposed to explain the transition from transgranular to intergranular fracture in the low ΔK regime.

  18. Creep crack growth investigations for elevated temperature material application

    International Nuclear Information System (INIS)

    Krompholz, K.; Pierick, J.B.; Grosser, E.D.

    1981-01-01

    Creep crack growth data for the cast alloys IN-519 at 1123 K, Manaurite 36 X at 1123 K and 1173 K, and for the wrought alloys Incoloy 800 H and Inconel 617 at 1123 K, 1173 K, 1223 K, and 1273 K are reported. Up to 1273 K the crack lengths were measured by means of the potential drop technique. The data are plotted da/dt vs. net section stress. These results are compared with data on Inconel 617 analyzed according to stress intensity. (orig.)

  19. The fractography analysis of IN718 alloy after three-point flexure fatigue test

    Directory of Open Access Journals (Sweden)

    Belan Juraj

    2018-01-01

    Full Text Available In this study, the high cycle fatigue (HCF properties of IN718 superalloy with given chemical composition were investigated at three-point flexure fatigue test at room temperature. INCONEL alloy 718 is nickel-chromium-iron hardenable alloy and due to its unique combination of mechanical properties (high-strength; corrosion-resistant and so on used for production of heat resistant parts of aero jet engine mostly. Mechanical properties of this alloy are strongly dependent on microstructure and on presence of structural features such are principal strengthening phase gamma double prime, gamma prime and due to its morphology less desired delta phases. The mentioned phases precipitate at various temperature ranges and Nb content as well. The three-point flexure fatigue test was performed on ZWICK/ROELL Amsler 150 HFP 5100 test equipment with approximate loading frequency f=150 Hz. The S – N (Stress – Number of cycles curve was obtained after testing. With the help of scanning electron microscope (SEM, fractography analyses were performed to disclose the fracture features of specimens in different life ranges. The brief comparison of three-point flexure and push-pull fatigue loading modes and its influence on fatigue life is discussed as well.

  20. J-resistance curves for Inconel 690 and Incoloy 800 nuclear steam generators tubes at room temperature and at 300 °C

    Energy Technology Data Exchange (ETDEWEB)

    Bergant, Marcos A., E-mail: marcos.bergant@cab.cnea.gov.ar [Gerencia CAREM, Centro Atómico Bariloche (CNEA), Av. Bustillo 9500, San Carlos de Bariloche 8400 (Argentina); Yawny, Alejandro A., E-mail: yawny@cab.cnea.gov.ar [División Física de Metales, Centro Atómico Bariloche (CNEA) / CONICET, Av. Bustillo 9500, San Carlos de Bariloche 8400 (Argentina); Perez Ipiña, Juan E., E-mail: juan.perezipina@fain.uncoma.edu.ar [Grupo Mecánica de Fractura, Universidad Nacional del Comahue / CONICET, Buenos Aires 1400, Neuquén 8300 (Argentina)

    2017-04-01

    The structural integrity of steam generator tubes is a relevant issue concerning nuclear plant safety. In the present work, J-resistance curves of Inconel 690 and Incoloy 800 nuclear steam generator tubes with circumferential and longitudinal through wall cracks were obtained at room temperature and 300 °C using recently developed non-standard specimens' geometries. It was found that Incoloy 800 tubes exhibited higher J-resistance curves than Inconel 690 for both crack orientations. For both materials, circumferential cracks resulted into higher fracture resistance than longitudinal cracks, indicating a certain degree of texture anisotropy introduced by the tube fabrication process. From a practical point of view, temperature effects have found to be negligible in all cases. The results obtained in the present work provide a general framework for further application to structural integrity assessments of cracked tubes in a variety of nuclear steam generator designs. - Highlights: •Non-standard fracture specimens were obtained from nuclear steam generator tubes. •Specimens with circumferential and longitudinal through-wall cracks were used. •Inconel 690 and Incoloy 800 steam generator tubes were tested at 24 and 300 °C. •Fracture toughness for circumferential cracks was higher than for longitudinal cracks. •Incoloy 800 showed higher fracture toughness than Inconel 690 steam generator tubes.

  1. Grain size refinement of inconel 718 thermomechanical processing

    International Nuclear Information System (INIS)

    Okimoto, P.C.

    1988-01-01

    Inconel 718 is a Ni-Fe precipitation treated superalloy. It presents good thermal fatigue properties when the material has small grain size. The aim of this work is to study the grain size refinement by thermomechanical processing, through observations of the microstructural evolution and the influence of some of the process variables in the final grain size. The results have shown that this refinement occured by static recrystallization. The presence of precipitates have influenced the final grain size if the deformations are below 60%. For greater deformations the grain size is independent of the precipitate distribution in the matrix and tends to a limit size of 5 μm. (author)

  2. Control of the kerf size and microstructure in Inconel 738 superalloy by femtosecond laser beam cutting

    Energy Technology Data Exchange (ETDEWEB)

    Wei, J.; Ye, Y.; Sun, Z. [Department of Mechanical Engineering, Tsinghua University, Beijing (China); Liu, L., E-mail: liulei@tsinghua.edu.cn [The State Key Laboratory of Tribology, Tsinghua University, Beijing (China); Zou, G., E-mail: sunzhg@tsinghua.edu.cn [Department of Mechanical Engineering, Tsinghua University, Beijing (China)

    2016-05-01

    Highlights: • Effects of processing parameters on the kerf size in Inconel 738 are investigated. • Defocus is a key parameter affecting the kerf width due to the intensity clamping. • The internal surface microstructures with different scanning speed are presented. • The material removal mechanism contains normal vaporization and phase explosion. • Oxidation mechanism is attributed to the trapping effect of the dangling bonds. - Abstract: Femtosecond laser beam cutting is becoming widely used to meet demands for increasing accuracy in micro-machining. In this paper, the effects of processing parameters in femtosecond laser beam cutting on the kerf size and microstructure in Inconel 738 have been investigated. The defocus, pulse width and scanning speed were selected to study the controllability of the cutting process. Adjusting and matching the processing parameters was a basic enhancement method to acquire well defined kerf size and the high-quality ablation of microstructures, which has contributed to the intensity clamping effect. The morphology and chemical compositions of these microstructures on the cut surface have been characterized by a scanning electron microscopy equipped with an energy dispersive X-ray spectroscopy, X-ray diffraction and X-ray photoelectron spectroscopy. Additionally, the material removal mechanism and oxidation mechanism on the Inconel 738 cut surface have also been discussed on the basis of the femtosecond laser induced normal vaporization or phase explosion, and trapping effect of the dangling bonds.

  3. Applicability of a 'marker-technique' to support the examination of crack growth behaviour in brittle and ductile Ni-alloys at 500 and 750 C

    International Nuclear Information System (INIS)

    Schwarze, D.; Schubert, F.

    1999-12-01

    The crack growth behaviour of materials for application in turbines at temperatures of 500- 750 C has been investigated. The creep and fatigue service loadings of a real turbine disc were simulated by introducing hold-times. The materials tested were the superalloy PM N18, Inconel 617 and the intermetallic phase β-NiAl of nominally stoichiometric composition. The crack growth tests were conducted in air and in vacuum (10 -5 mbar) to assess the influence of the test atmosphere. One of the main objectives was to develop a marker method and its application, as support for the crack growth tests carried out. The width of the marker required for the marker bands could be chosen through the number of stress cycles or the crack growth increment in the marker-cycle. At 500 C, the crack surfaces of the CT specimens of Inconel 617 and PM N18 exhibited mixed fractures with trans- and intercrystalline regions. The fracture development could be divided into three, classical parts. At his temperature for both alloys the K I concept for the evaluation of the crack growth may be used. The RCT specimens of the intermetallic phase β-NiAl fractured in a completely brittle manner with no measurable time to failure. At 500 C, Inconel 617 and especially PM N18 were well suited to the use of the marker method. Measurements of the distances between the marker bands gave a good estimate of the crack growth rates. At the higher test temperature of 750 C, the crack growth rates and the proportion of intercrystalline fracture increased for Inconel 617 and PM N18. In all three materials, the formation of pores and dimpled fracture was observed, especially at high ΔK I values, and the coarse-grained β-NiAl exhibited higher crack growth rates than the fine-grained material. For this temperature the evaluation of the crack growth experiments should be by the K I concept for PM N18 and for Inconel 617 the C * concept is recommended. At the higher test temperature, the increased plasticity of

  4. Tribological behavior of inconel 718 in sodium cooled reactor environments

    International Nuclear Information System (INIS)

    Wilson, W.L.; Galioto, T.A.; Schrock, S.L.

    1976-01-01

    Results of the present study on the tribological behavior of Inconel 718 in a sodium environment are summarized as follows: (a) Stroke lengths less than or equal to one-half the test pin diameter result in higher friction coefficients. (b) At elevated temperatures, the formation of a lubricative surface film can significantly influence the frictional behavior. (c) Tangential forces present during static dwell periods result in greater bonding tendencies. (d) Increasing contact pressure during static dwell periods results in lower breakaway friction coefficients

  5. Electrochemical impedance spectrometry using Inconel 690, zircaloy 4, 316Ti steel, 17-4-PH, UR52N et URSB8. Simulation in tritiated water. Tome 2

    International Nuclear Information System (INIS)

    Bellanger, G.

    1994-11-01

    The redox potential of 3 H 2 O, as well as the corrosion potentials in this medium are found, abnormally, in the trans-passive region. This is completely different from behavior in the chemical industry or in the water in nuclear powers. With such behavior, there will be breakdowns of the protective oxide layers, and in the presence of chloride there will be immediate pitting. Polarization and electrochemical impedance spectrometry curves are presented and discussed. These curves make it possible to ascertain the corrosion domains and to compare the kinetics of different stainless steel alloys. These corrosion kinetics and the corrosion potentials provide a classification of the steels studied here: Inconel 690, zircaloy 4, 316 Ti steel, 17-4-PH, UR52N et URSB8. From the results it can be concluded that URSB8 has the best corrosion resistance. (author). 13 refs., 522 figs., tabs

  6. Electrochemical impedance spectrometry using Inconel 690, zircaloy 4, 316Ti steel, 17-4-PH, UR52N et URSB8. Simulation in tritiated water. Tome 1

    International Nuclear Information System (INIS)

    Bellanger, G.

    1994-11-01

    The redox potential of 3 H 2 O, as well as the corrosion potentials in this medium are found, abnormally, in the trans-passive region. This is completely different from the behavior in the chemical industry or in the water in nuclear powers. With such behavior, there will be breakdowns of the protective oxide layers, and in the presence of chloride there will be immediate pitting. Polarization and electrochemical impedance spectrometry curves are presented and discussed. These curves make it possible to ascertain the corrosion domains and to compare the kinetics of different stainless alloys. These corrosion kinetics and the corrosion potentials provide a classification of the steels studied here: Inconel 690, zircaloy 4, 316 Ti steel, 17-4-PH, UR52N et URSB8. From the results it can be concluded that URSB8 has the best corrosion resistance. (author). 279 figs., tabs

  7. Sadhana | Indian Academy of Sciences

    Indian Academy of Sciences (India)

    Inconel 625 is one of the most versatile nickel-based super alloy used in the aerospace, automobile, chemical processing, oil refining, marine, waste treatment, pulp and paper, and power industries. Wire electrical discharge machining (WEDM) is the process considered in the present text for machining of Inconel 625 as it ...

  8. Liquid Oxygen Rotating Friction Ignition Testing of Aluminum and Titanium with Monel and Inconel for Rocket Engine Propulsion System Contamination Investigation

    Science.gov (United States)

    Peralta, S.; Rosales, Keisa R.; Stoltzfus, Joel M.

    2009-01-01

    Metallic contaminant was found in the liquid oxygen (LOX) pre-valve screen of the shuttle main engine propulsion system on two orbiter vehicles. To investigate the potential for an ignition, NASA Johnson Space Center White Sands Test Facility performed (modified) rotating friction ignition testing in LOX. This testing simulated a contaminant particle in the low-pressure oxygen turbo pump (LPOTP) and the high-pressure oxygen turbo pump (HPOTP) of the shuttle main propulsion system. Monel(R) K-500 and Inconel(R) 718 samples represented the LPOTP and HPOTP materials. Aluminum foil tape and titanium foil represented the contaminant particles. In both the Monel(R) and Inconel(R) material configurations, the aluminum foil tape samples did not ignite after 30 s of rubbing. In contrast, all of the titanium foil samples ignited regardless of the rubbing duration or material configuration. However, the titanium foil ignitions did not propagate to the Monel and Inconel materials.

  9. Performance of PVD-Coated Carbide Tools When Turning Inconel 718 in Dry Machining

    Directory of Open Access Journals (Sweden)

    Gusri Akhyar Ibrahim

    2011-01-01

    Full Text Available Inconel 718 has found its niche in many industries, owing to its unique properties such as high oxidation resistance and corrosion resistance even at very high temperatures. Coated carbide tool with hard layer of PVD TiAlN is used to turn Inconel 718. Taguchi method with the orthogonal array L9 is applied in this experiment with the parameter cutting speed of 60–80 m/min, feed rate of 0.2–0.3 mm/rev, and depth of cut of 0.3–0.5 mm. The results show that depth of cut is a significant influence to the tool life. Cutting speed of 60 m/min, feed rate of 0.2 mm/rev, and depth of cut of 0.3 mm are the optimum parameters. The flank wear, crater wear, notch wear, and nose wear are the wear mechanisms on the carbide tool. Through the SEM, abrasion, attrition, and adhesion are the wear mechanisms which can be seen on the cutting tool.

  10. Pitting corrosion of Inconel 600 in chloride and sulfate solutions at low temperature

    International Nuclear Information System (INIS)

    Chang Mingyu; Yu Geping

    1993-01-01

    Pitting corrosion of Inconel 600 was examined in chloride and sulfate solutions through usage of potentiodynamic polarization techniques. The effects of chloride and sulfate concentration were investigated in the range of 0.0001 to 0.1 M. Increasing chloride concentrations resulted in active shifts of the pit nucleation potential. Immunity to pitting corrosion was evident at a chloride level below 0.005 M. Increasing sulfate concentrations resulted in improved pitting resistance of Inconel 600 in chloride solutions. Detrimental effects associated with pitting were evident with low-level sulfate being added to dilute chloride media. The density of pits increased with increasing chloride concentrations or temperature between room temperature and 70 C. Systematic trends for the depth of pits were not evident. The observations of pitting corrosion in open immersion were consistent with those in polarization methods. Corrosion products contained in the pits were enriched in nickel, chromium and iron with a small amount of titanium and silicon. The enrichment of chlorine or sulfur was still, however, not found. (orig.)

  11. Evaluation on mechanical and corrosion properties of steam generator tubing materials

    International Nuclear Information System (INIS)

    Kim, In Sup; Lee, Byong Whi; Lee, Sang Kyu; Lee, Young Ho; Kim, Jun Whan; Lee, Ju Seok; Kwon, Hyuk Sang; Kim, Su Jung

    1998-06-01

    Steam generator is one of the major components of nuclear reactor pressure boundary. It's main function os transferring heat which generated in the reactor to turbine generator through steam generator tube. In these days, steam generator tubing materials of operating plant are used Inconel 600 alloys. But according to the operation time, there are many degradation phenomena which included mechanical damage due to flow induced vibration and corrosion damage due to PWSCC, IGA/SCC and pitting etc. Recently Inconel 690 alloys are selected as new and replacement steam generator tubes for domestic nuclear power plant. But there are few study about mechanical and corrosion properties of Inconel 600 and 690. The objectives of this study is to evaluate and compare mechanical and corrosion propertied of steam generator tube materials

  12. Evaluation on mechanical and corrosion properties of steam generator tubing materials

    Energy Technology Data Exchange (ETDEWEB)

    Kim, In Sup; Lee, Byong Whi; Lee, Sang Kyu; Lee, Young Ho; Kim, Jun Whan; Lee, Ju Seok; Kwon, Hyuk Sang; Kim, Su Jung [Korea Advanced Institute of Science and Technology, Taejon (Korea, Republic of)

    1998-06-15

    Steam generator is one of the major components of nuclear reactor pressure boundary. It's main function os transferring heat which generated in the reactor to turbine generator through steam generator tube. In these days, steam generator tubing materials of operating plant are used Inconel 600 alloys. But according to the operation time, there are many degradation phenomena which included mechanical damage due to flow induced vibration and corrosion damage due to PWSCC, IGA/SCC and pitting etc. Recently Inconel 690 alloys are selected as new and replacement steam generator tubes for domestic nuclear power plant. But there are few study about mechanical and corrosion properties of Inconel 600 and 690. The objectives of this study is to evaluate and compare mechanical and corrosion propertied of steam generator tube materials.

  13. Effects of the aging temperature and stress relaxation conditions on γ′ precipitation in Inconel X-750

    Energy Technology Data Exchange (ETDEWEB)

    Ha, Jeong Won [Department of Materials Science and Engineering, Pusan National University, Busan 609-735 (Korea, Republic of); Research and Development Center, KOS Limited, Yangsan 626-230 (Korea, Republic of); Seong, Baek Seok [Neutron Science Division, HANARO Center, Korea Atomic Energy Research Institute, Daejeon 305-353 (Korea, Republic of); Jeong, Hi Won [Advanced Metallic Materials Division, Korea Institute of Materials Science, Changwon 642-831 (Korea, Republic of); Choi, Yoon Suk [Department of Materials Science and Engineering, Pusan National University, Busan 609-735 (Korea, Republic of); Kang, Namhyun, E-mail: nhkang@pusan.ac.kr [Department of Materials Science and Engineering, Pusan National University, Busan 609-735 (Korea, Republic of)

    2015-02-15

    Highlights: • Stress relaxation after aging 620 °C increased carbides and maintained γ′ fraction. • Aging temperature increase to 732 °C raised the γ′ increment after stress relaxation. • Small increase of carbides induced the large increase of γ′ after stress relaxation. • Loading for stress relaxation raised γ′ increment due to dislocation multiplication. - Abstract: Inconel X-750 is a Ni-based precipitation-hardened superalloy typically used in springs designed for high-temperature applications such as the hold-down springs in nuclear power plants. γ′ is a major precipitate in X-750 alloys which affects the strength, creep resistance, and stress relaxation properties of the spring. In this study, a solution-treated X-750 wire coiled into a spring was used that was aged at various temperatures and submitted to stress relaxation tests with and without loading. Small angle neutron scattering was employed to quantify the size and volume fraction of γ′ phase in the springs as a function of the aging temperature and the application of a load during stress relaxation. The volume fraction of γ′ precipitates increased in the specimen aged at 732 °C following stress relaxation at 500 °C for 300 h. However, the mean size of the precipitates in the samples was not affected by stress relaxation. The specimen aged at the lower temperature (620 °C) contained a smaller γ′ volume fraction and gained a smaller fraction of γ′ during stress relaxation compared with the sample aged at the higher temperature (732 °C). The smaller increase in the γ′ volume fraction for the sample aged at 620 °C was associated with a larger increase in the M{sub 23}C{sub 6} secondary carbide content during relaxation. The Cr depletion zone around the secondary carbides raises the solubility of γ′ thereby decreasing the volume fraction of γ′ precipitates in Inconel X-750. In terms of stress relaxation, a larger increase in the γ′ volume fraction was

  14. Corrosion of Inconel-625, Hastelloy-X280 and Incoloy-800 in 550 - 750°C superheated steam. Influence of alloy heat treatment, surface treatment, steam temperature and steam velocity. Part I: Results up to 6000 hours exposure time. RCN Report

    International Nuclear Information System (INIS)

    Tilborg, P.J. van; Linde, A. van der

    1969-10-01

    Sheet samples of Inconel-625, Hastelloy-X280 and Incoloy-800 were tested, in the solution annealed and in the solution annealed + 20% cold worked + 800°C tempered condition, in steam with a velocity of 5 m/sec. at 550, 650 and 750°C and in steam with a volocity of 15 and 85 m/sec. at 550°C. At 550°C and 750°C the samples were tested in the heat treated, annealed or tempered and the heat treated + electropolished condition. At 650°C moreover as heat treated + ground and pickled samples were tested. Post-corrosion sample investigations involved measurement of the adherent oxide thickness, the total amount of corroded metal, the metal loss to system, and the metallographic and microprobe investigation of the adherent oxide film and adjacent diffusion disturbed alloy layer. The results obtained up to 6000 hours exposure time showed that the surface treatment has a decisive influence on the corrosion behaviour of all three alloys tested. The differences in the corrosion data for the two heat treatment conditions are small. The influence of the steam velocity, as tested at 550°C, on the initial corrosion rate was surprisingly high, while the long-term linear corrosion rates are only slightly influenced by the gas velocity. In general the linear corrosion rates were low, 1-5 mg/dm 2 month, and not consistently affected by the test-temperature. The metal loss to system values were 2 <15 mg/dm 2 in the low velocity steam at all three test temperatures and <30 mg/dm 2 in the high velocity steam at 550°C. The metallographic and microprobe examinations revealed no remarkable results, as compared with the results of analogous tests reported in literature. (author)

  15. High frequency fatigue test of IN 718 alloy – microstructure and fractography evaluation

    Directory of Open Access Journals (Sweden)

    J. Belan

    2015-01-01

    Full Text Available INCONEL alloy 718 is a high-strength, corrosion-resistant nickel chromium material used at -253 °C to 705 °C for production of heat resistant parts of aero jet engine mostly. The fatigue test provided on this kind materials were done via low frequency loading up to this time. Nowadays, needs of results at higher volume of loading cycles leads to high frequency loading with aim to shorten testing time. Fatigue test of experimental material was carried out at frequency 20 kHz with stress ration R = - 1 (push – pull at room temperature. It was found that this superalloy can still fracture after exceeding 108 cycles. Besides fatigue test were microstructural characterisation and scanning electron microscopy (SEM fractography evaluation done.

  16. Surface passivity largely governs the bioaccessibility of nickel-based powder particles at human exposure conditions.

    Science.gov (United States)

    Hedberg, Yolanda S; Herting, Gunilla; Latvala, Siiri; Elihn, Karine; Karlsson, Hanna L; Odnevall Wallinder, Inger

    2016-11-01

    The European chemical framework REACH requires that hazards and risks posed by chemicals, including alloys and metals, are identified and proven safe for humans and the environment. Therefore, differences in bioaccessibility in terms of released metals in synthetic biological fluids (different pH (1.5-7.4) and composition) that are relevant for different human exposure routes (inhalation, ingestion, and dermal contact) have been assessed for powder particles of an alloy containing high levels of nickel (Inconel 718, 57 wt% nickel). This powder is compared with the bioaccessibility of two nickel-containing stainless steel powders (AISI 316L, 10-12% nickel) and with powders representing their main pure alloy constituents: two nickel metal powders (100% nickel), two iron metal powders and two chromium metal powders. X-ray photoelectron spectroscopy, microscopy, light scattering, and nitrogen absorption were employed for the particle and surface oxide characterization. Atomic absorption spectroscopy was used to quantify released amounts of metals in solution. Cytotoxicity (Alamar blue assay) and DNA damage (comet assay) of the Inconel powder were assessed following exposure of the human lung cell line A549, as well as its ability to generate reactive oxygen species (DCFH-DA assay). Despite its high nickel content, the Inconel alloy powder did not release any significant amounts of metals and did not induce any toxic response. It is concluded, that this is related to the high surface passivity of the Inconel powder governed by its chromium-rich surface oxide. Read-across from the pure metal constituents is hence not recommended either for this or any other passive alloy. Copyright © 2016 The Author(s). Published by Elsevier Inc. All rights reserved.

  17. Transient liquid phase bonding of titanium-, iron- and nickel-based alloys

    Science.gov (United States)

    Rahman, A. H. M. Esfakur

    appropriate thermodynamic and kinetic database. In the third phase industrially important alloys such as SS 321, Inconel 718 and Ti-6Al-4V were diffusion bonded. Diffusion bonded SS 321 with Au-12Ge interlayer provided the best microstructure when bonded in either vacuum or argon at 1050°C for 20 h and cooled in air. The maximum strength obtained of the joint was 387+/-4 MPa bonded in vacuum at 1050°C for 20 h and cooled in air. The microstructure of joint centerline of diffusion bonded Inconel 718 using Au-12Ge interlayer at 1050°C for 15 h and cooled in air consisted of residual interlayer (1.3-2.5 microm). The residual interlayer was disappeared by increasing the bonding time by 5 h, however, pores appeared in the joint centerline. As a result, the strength obtained for bonded Inconel 718 was much lower than that of the base alloy. The joint centerline microstructure of bonded Ti-6Al-4V using Cu interlayer was free of intermetallics and solid solution of Cu and base alloy. The strength of the joint is yet to be determined.

  18. The Evaluation of Crevice Corrosion of Inconel-600 and 304 Stainless Steel in Reductive Decontamination Solutions

    International Nuclear Information System (INIS)

    Jung, Junyoung; Park, Sangyoon; Won, Huijun; Choi, Wangkyu; Moon, Jeikwon; Park, Sojin

    2014-01-01

    In this sturdy, we investigated the characteristics of corrosion to Inconel-600 and type 304 stainless steel which are mainly used for the steam generator and primary system of PWR reactor respectively. We conducted the corrosion test for the HYBRID (HYdrazine Based metal Ion Reductive decontamination) which was developed in KAERI, Citrox and Oxalic acid solutions used in reductive decontamination of the inner surface of PWR. Since Citrox and oxalic acid solution were well-known conventional decontamination solutions, it is meaningful to compare the corrosion result of HYBRID with those solutions to confirm the corrosion compatibility. In order to obtain visible results in a limited time, we conducted the crevice corrosion tests under harsh condition. According to the results of crevice corrosion tests, we can conclude that metals such as type 304 stainless steel and Inconel-600 in HYBRID are very stable against crevice corrosion. On the other hand, those metals in Citrox and oxalic acid solutions were very susceptible to the crevice corrosion. Especially when using the oxalic acid solution, severe corrosion was observed not only Inconel-600 but also 304 stainless steel. The degree of corrosion can be expressed as; HYBRID << Citrox < OA. Conclusively, our results support that the HYBRID is more stable to the corrosion of structural materials in primary system than other Citrox and oxalic acid solutions. This finding will appoint the HYBRID solution as a candidate to solve the corrosion problem which is often issued by existing chemical decontamination processes

  19. Effect of lead on Inconel 600 and Incoloy 800 oxide layers formed in simulated steam generator secondary environments

    International Nuclear Information System (INIS)

    Garcia-Mazario, M.; Lancha, A.M.; Hernandez, M.; Maffiotte, C.

    1996-01-01

    The existence of lead in steam generators, detected during the analysis of deposits in the damaged areas of tubing, supports the hypothesis that lead may contribute to the cracking problems experienced in steam generator tubes. In addition, the harmful effect of lead on Inconel 600 is known not only through laboratory tests but also as a result of operating experience. Operating experience of Incoloy 800 is, however, much more limited and there are very few laboratory studies in this area. Taking into account that thin films formed on metals reflect the interaction between such metals and the aqueous environment and also that incoloy 800 is considered to be a suitable material for new steam generators as a substitute for Inconel 600, attempts to determine the effect of lead on corrosion films are considered useful with a view to better understanding the stress-corrosion-cracking behaviour of these materials. For these reasons the objective of this paper is to gain some insights into the effect of lead on the oxide layers forming on Inconel 600 and Incoloy 800 tested in the laboratory in various aggressive lead-containing environments. Auger electron spectroscopy (AES) and electron spectroscopy for chemical analysis (ESCA) have been used to study the composition of these oxide layers. (orig.)

  20. Studies on the weldability, microstructure and mechanical properties of activated flux TIG weldments of Inconel 718

    International Nuclear Information System (INIS)

    Ramkumar, K. Devendranath; Kumar, B. Monoj; Krishnan, M. Gokul; Dev, Sidarth; Bhalodi, Aman Jayesh; Arivazhagan, N.; Narayanan, S.

    2015-01-01

    This research article addresses the joining of 5 mm thick plates of Inconel 718 by activated flux tungsten inert gas (A-TIG) welding process using SiO 2 and TiO 2 fluxes. Microstructure studies inferred the presence of Nb rich eutectics and/or laves phase in the fusion zone of the A-TIG weldments. Tensile studies corroborated that the ultimate tensile strength of TiO 2 flux assisted weldments (885 MPa) was better compared to SiO 2 flux assisted weldments (815 MPa) and the failure was observed in the parent metal for both the cases. Impact test results portrayed that both the weldments were inferior in toughness as compared to the parent metal, which was due to the presence of oxide inclusions. Also, the study investigated the structure–property relationships of the A-TIG weldments of Inconel 718

  1. Solute redistribution and Rayleigh number in the mushy zone during directional solidifi cation of Inconel 718

    Directory of Open Access Journals (Sweden)

    Wang Ling

    2009-08-01

    Full Text Available The interdendritic segregation along the mushy zone of directionally solidifi ed superalloy Inconel 718 has been measured by scanning electron microscope (SEM and energy dispersion analysis spectrometry (EDAXtechniques and the corresponding liquid composition profile was presented. The liquid density and Rayleigh number (Ra profi les along the mushy zone were calculated as well. It was found that the liquid density difference increased from top to bottom in the mushy zone and there was no density inversion due to the segregation of Nb and Mo. However carbide formation in the freezing range and the preferred angle of the orientated dendrite array could prompt the fl uid fl ow in the mushy zone although there was no liquid density inversion. The largest relative Rayleigh number appeared at 1,326 篊 for Inconel 718 where the fl uid fl ow most easily occurred.

  2. Ultrasonic measurements for in-service assessment of wrought Inconel 625 cracker tubes of heavy water plants

    International Nuclear Information System (INIS)

    Kumar, Anish; Rajkumar, K.V.; Jayakumar, T.; Raj, Baldev; Mishra, B.

    2006-01-01

    The degradation in mechanical properties of Inconel 625 ammonia cracker tubes occurs during the service for long duration in heavy water plants. The present study brings out the possibility of using Poisson's ratio (derived from measurement of time of flight of ultrasonic waves) in combination with hardness measurements, as an effective non-destructive tool for assessment of in-service degradation of Inconel 625 cracker tubes and qualification of re-solution annealing heat treatment for their rejuvenation. Further, the study also indicates the feasibility of extending the life of some of the tubes beyond the presently followed 120 000 h, before they are taken up for re-solution annealing, without affecting their serviceability. However, further studies are required to identify quantitative criterion for Poisson's ratio and hardness values, for deciding on the basis for removal of the tubes for rejuvenation

  3. Preliminary stress corrosion cracking modeling study of a dissimilar material weld of alloy (INCONEL) 182 with Stainless Steel 316

    Energy Technology Data Exchange (ETDEWEB)

    Aly, Omar F.; Mattar Neto, Miguel, E-mail: ofaly@ipen.br, E-mail: mmattar@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Schvartzman, Monica M.A.M., E-mail: monicas@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2013-07-01

    Dissimilar welds (DW) are normally used in many components junctions in structural project of PWR (Pressurized Water Reactors) in Nuclear Plants. One had been departed of a DW of a nozzle located at a Reactor Pressure Vessel (RPV) of a PWR reactor, that joins the structural vessel material with an A316 stainless steel safe end. This weld is basically done with Alloy 182 with a weld buttering of Alloy 82. It had been prepared some axial cylindrical specimens retired from the Alloy 182/A316 weld end to be tested in the slow strain rate test machine located at CDTN laboratory. Based in these stress corrosion susceptibility results, it was done a preliminary semi-empirical modeling application to study the failure initiation time evolution of these specimens. The used model is composed by a deterministic part, and a probabilistic part according to the Weibull distribution. It had been constructed a specific Microsoft Excel worksheet to do the model application of input data. The obtained results had been discussed according with literature and also the model application limits. (author)

  4. 26 CFR 601.803 - Program operations and requirements.

    Science.gov (United States)

    2010-04-01

    ... REVENUE PRACTICE STATEMENT OF PROCEDURAL RULES Tax Counseling for the Elderly § 601.803 Program operations... understanding of Federal tax subjects on which they will provide tax return assistance. Volunteers who do not... individuals involved in the program, to respect the confidentiality of income and financial information known...

  5. Single-Track Melt-Pool Measurements and Microstructures in Inconel 625

    Science.gov (United States)

    Ghosh, Supriyo; Ma, Li; Levine, Lyle E.; Ricker, Richard E.; Stoudt, Mark R.; Heigel, Jarred C.; Guyer, Jonathan E.

    2018-02-01

    We use single-track laser melting experiments and simulations on Inconel 625 to estimate the dimensions and microstructure of the resulting melt pool. Our work is based on a design-of-experiments approach which uses multiple laser power and scan speed combinations. Single-track experiments generated melt pools of certain dimensions that showed reasonable agreement with our finite-element calculations. Phase-field simulations were used to predict the size and segregation of the cellular microstructure that formed along the melt-pool boundaries for the solidification conditions that changed as a function of melt-pool dimensions.

  6. Single-Track Melt-Pool Measurements and Microstructures in Inconel 625

    Science.gov (United States)

    Ghosh, Supriyo; Ma, Li; Levine, Lyle E.; Ricker, Richard E.; Stoudt, Mark R.; Heigel, Jarred C.; Guyer, Jonathan E.

    2018-06-01

    We use single-track laser melting experiments and simulations on Inconel 625 to estimate the dimensions and microstructure of the resulting melt pool. Our work is based on a design-of-experiments approach which uses multiple laser power and scan speed combinations. Single-track experiments generated melt pools of certain dimensions that showed reasonable agreement with our finite-element calculations. Phase-field simulations were used to predict the size and segregation of the cellular microstructure that formed along the melt-pool boundaries for the solidification conditions that changed as a function of melt-pool dimensions.

  7. Performance testing of Tesla NNG 601 activity meter in nuclear medicine department

    International Nuclear Information System (INIS)

    Husak, V.; Kleinbauer, K.

    1980-01-01

    The results are presented of testing activity meter Tesla NNG 601 the production of which began in Czechoslovakia in 1978. The meter is provided with a shielded well-type ionization chamber, the well 42 mm in diameter and 140 mm deep. The parameters of the instrument linearity, volume dependence, accuracy and stability, correctness of calibration were compared with those of other instruments (Searle Analytic, Picker and Capinted). The volume dependence of the Czechoslovak NNG 601 instrument is higher than that in the other instruments, other parameters are the same of better

  8. Denting of Inconel steam generator tubes in pressurized water reactors. Third informal report

    International Nuclear Information System (INIS)

    van Rooyen, D.; Weeks, J.R.

    1977-08-01

    The recent plant operating experience and laboratory test results on the phenomenon of denting in recirculating PWR steam generators is reviewed. Although denting was first reported only in plants that were converted from phosphate to AVT, it has now also been observed in plants still on phosphate, as well as in some that started on AVT. In some units, slightly abnormal eddy current signals have been observed at the top of the tube sheets. The degree of denting in operating steam generators may be related to the levels and duration of chloride inleakage. Chloride, however, is not the only active ingredient, and does not seem to give denting until local acid conditions arise; consequently, it may be necessary for soluble copper and/or nickel ions to be present to promote the denting reaction. Chloride concentrations in actively corroding crevices can increase by several orders of magnitude over the bulk coolant. It is thus difficult to develop a basis for Cl - specifications for secondary water. Maintaining Cl - low enough to prevent denting may be unmanageable without full flow condensate demineralization in coastal plants with copper alloy condensors and feedwater lines. Cathodic depolarization by oxidizing species are thought to promote the formation of acid chlorides in crevices and trigger the denting reactions; some ions may also catalyze the rapid formation of magnetite. These, and other mechanistic aspects of denting are discussed. The implications of the Inconel 600 tube defects at Ginna in non-dented areas, originating from the primary side, are also discussed

  9. Residual stress determination of direct metal laser sintered (DMLS) inconel specimens and parts

    Energy Technology Data Exchange (ETDEWEB)

    Watkins, Thomas R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Unocic, Kinga A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Maziasz, Philip J. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Bunn, Jeffrey R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Fancher, Christopher M. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Peralta, Alonso [Honeywell Aerospace, Phoenix, AZ (United States); Sundarraj, Suresh [Honeywell Aerospace, Phoenix, AZ (United States); Neumann, James [Honeywell Aerospace, Phoenix, AZ (United States)

    2018-01-01

    Residual stress determinations and microstructural studies were performed on a series of Inconel 718Plus prisms built using Direct Metal Laser Sintering (DMLS) at Honeywell Aerospace (hereafter also referred to as Honeywell). The results are being used to validate and improve existing models at Honeywell, and ultimately will expedite the implementation of DMLS throughout various industrial sectors (automotive, biomedical, etc.).

  10. Microstructure and strain-stress analysis of the dynamic strain aging in inconel 625 at high temperature

    Science.gov (United States)

    Maj, P.; Zdunek, J.; Mizera, J.; Kurzydlowski, K. J.; Sakowicz, B.; Kaminski, M.

    2017-01-01

    Serrated flow is a result of unstable plastic flow, which occurs during tensile and compression tests on some dilute alloys. This phenomenon is referred as the Portevin Le-Chatelier effect (PLC effect). The aim of this research was to investigate and analyze this phenomenon in Inconel 625 solution strengthened superalloy. The tested material was subjected to tensile tests carried out within the temperature range 200-700 °C, with three different strain rates: 0.002 1/s, 0.01/s, and 0.05 1/s and additional compression tests with high deformation speeds of 0.1, 1, and 10 1/s. The tensile strain curves were analyzed in terms of intensity and the observed patterns of serrations Using a modified stress drop method proposed by the authors, the activation energy was calculated with the assumption that the stress drops' distribution is a direct representation of an average solute atom's interaction with dislocations. Subsequently, two models, the standard vacancy diffusion Bilby-Cottrell model and the realistic cross-core diffusion mechanism proposed by Zhang and Curtin, were compared. The results obtained show that the second one agrees with the experimental data. Additional microstructure analysis was performed to identify microstructure elements that may be responsible for the PLC effect. Based on the results, the relationship between the intensity of the phenomenon and the conditions of the tests were determined.

  11. Influence of the Overlapping Factor and Welding Speed on T-Joint Welding of Ti6Al4V and Inconel 600 Using Low-Power Fiber Laser

    Directory of Open Access Journals (Sweden)

    Shamini Janasekaran

    2016-06-01

    Full Text Available Double-sided laser beam welding of skin-stringer joints is an established method for many applications. However, in certain cases with limited accessibility, single-sided laser beam joining is considered. In the present study, single-sided welding of titanium alloy Ti6Al4V and nickel-based alloy Inconel 600 in a T-joint configuration was carried out using continuous-wave (CW, low-power Ytterbium (Yb-fiber laser. The influence of the overlapping factor and welding speed of the laser beam on weld morphology and properties was investigated using scanning electron microscopy (SEM and X-ray diffraction (XRD, respectively. XRD analysis revealed the presence of intermetallic layers containing NiTi and NiTi2 at the skin-stringer joint. The strength of the joints was evaluated using pull testing, while the hardness of the joints was analyzed using Vickers hardness measurement at the base metal (BM, fusion zone (FZ and heat-affected zone (HAZ. The results showed that the highest force needed to break the samples apart was approximately 150 N at a laser welding power of 250 W, welding speed of 40 mm/s and overlapping factor of 50%. During low-power single-sided laser welding, the properties of the T-joints were affected by the overlapping factor and laser welding speed.

  12. Liquid-phase synthesis of vertically aligned carbon nanotubes and related nanomaterials on preheated alloy substrates

    Science.gov (United States)

    Yamagiwa, Kiyofumi

    2018-02-01

    Carbon nanotubes (CNTs) and related nanocarbons were selectively synthesized on commercially available alloy substrates by a simple liquid-phase technique. Fe- and Ni-rich stainless-steel (JIS SUS316L and Inconel®600, respectively) and Ni-Cu alloy (Monel®400) substrates were used for the synthesis, and each substrate was preheated in air to promote the self-formation of catalyst nanolayers on the surface. The substrates were resistance heated in ethanol without any addition of catalysts to grow CNTs. The yield of the CNTs effectively increased when the preheating process was employed. Highly aligned CNT arrays grew on the SUS316L substrate, while non-aligned CNTs and distinctive twisted fibers were observed on the other substrates. An Fe oxide layer was selectively formed on the preheated SUS316L substrate promoting the growth of the CNT arrays. Characterizations including cyclic voltammetry for the arrays revealed that the CNTs possess a comparatively defect-rich surface, which is a desirable characteristic for its application such as electrode materials for capacitors.

  13. Multi-criteria decision making in the selection of machining parameters for Inconel 718

    International Nuclear Information System (INIS)

    Thirumalai, R.; Senthilkumaar, J. S.

    2013-01-01

    Taguchi's methods and design of experiments are invariably used and adopted as quality improvement techniques in several manufacturing industries as tools for offline quality control. These methods optimize single-response processes. However, Taguchi's method is not appropriate for optimizing a multi-response problem. In other situations, multi-responses need to be optimized simultaneously. This paper presents multi-response optimization techniques. A set of non-dominated solutions are obtained using non-sorted genetic algorithm for multi-objective functions. Multi-criteria decision making (MCDM) is proposed in this work for selecting a single solution from nondominated solutions. This paper addresses a new method of MCDM concept based on technique for order preference by similarity to ideal solution (TOPSIS). TOPSIS determines the shortest distance to the positive-ideal solution and the greatest distance from the negative-ideal solution. This work involves the high-speed machining of Inconel 718 using carbide cutting tool with six objective functions that are considered as attributes against the process variables of cutting speed, feed, and depth of cut. The higher-ranked solution is selected as the best solution for the machining of Inconel 718 in its respective environment.

  14. Multi-criteria decision making in the selection of machining parameters for Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Thirumalai, R. [SNS College of Technology, Coimbatore (India); Senthilkumaar, J. S. [Bharathithasan Engineering College, Nattrampalli (India)

    2013-04-15

    Taguchi's methods and design of experiments are invariably used and adopted as quality improvement techniques in several manufacturing industries as tools for offline quality control. These methods optimize single-response processes. However, Taguchi's method is not appropriate for optimizing a multi-response problem. In other situations, multi-responses need to be optimized simultaneously. This paper presents multi-response optimization techniques. A set of non-dominated solutions are obtained using non-sorted genetic algorithm for multi-objective functions. Multi-criteria decision making (MCDM) is proposed in this work for selecting a single solution from nondominated solutions. This paper addresses a new method of MCDM concept based on technique for order preference by similarity to ideal solution (TOPSIS). TOPSIS determines the shortest distance to the positive-ideal solution and the greatest distance from the negative-ideal solution. This work involves the high-speed machining of Inconel 718 using carbide cutting tool with six objective functions that are considered as attributes against the process variables of cutting speed, feed, and depth of cut. The higher-ranked solution is selected as the best solution for the machining of Inconel 718 in its respective environment.

  15. Carburization of austenitic alloys by gaseous impurities in helium

    International Nuclear Information System (INIS)

    Lai, G.Y.; Johnson, W.R.

    1980-03-01

    The carburization behavior of Alloy 800H, Inconel Alloy 617 and Hastelloy Alloy X in helium containing various amounts of H 2 , CO, CH 4 , H 2 O and CO 2 was studied. Corrosion tests were conducted in a temperature range from 649 to 1000 0 C (1200 to 1832 0 F) for exposure time up to 10,000 h. Four different helium environments, identified as A, B, C, and D, were investigated. Concentrations of gaseous impurities were 1500 μatm H 2 , 450 μatm CO, 50 μatm CH 4 and 50 μatm H 2 O for Environment A; 200 μatm H 2 , 100 μatm CO, 20 μatm CH 4 , 50 μatm H 2 O and 5 μatm CO 2 for Environment B; 500 μatm H 2 , 50 μatm CO, 50 μatm CH 4 and 2 O for Environment C; and 500 μatm H 2 , 50 μatm CO, 50 μatm CH 4 and 1.5 μatm H 2 O for Environment D. Environments A and B were characteristic of high-oxygen potential, while C and D were characteristic of low-oxygen potential. The results showed that the carburization kinetics in low-oxygen potential environments (C and D) were significantly higher, approximately an order of magnitude higher at high temperatures, than those in high-oxygen potential environments (A and B) for all three alloys. Thermodynamic analyses indicated no significant differences in the thermodynamic carburization potential between low- and high-oxygen potential environments. It is thus believed that the enhanced carburization kinetics observed in the low-oxygen potential environments were related to kinetic effects. A qualitatively mechanistic model was proposed to explain the enhanced kinetics. The present results further suggest that controlling the oxygen potential of the service environment can be an effective means of reducing carburization of alloys

  16. Effect of temperature upon the fatigue-crack propagation behavior of Inconel 625

    International Nuclear Information System (INIS)

    James, L.A.

    1977-03-01

    The techniques of linear-elastic fracture mechanics were employed to characterize the effect of temperature upon the fatigue-crack propagation behavior of mill-annealed Inconel 625 in an air environment over the range 75 0 - 1200 0 F (24 0 - 649 0 C). In general, fatigue-crack growth rates increased with increasing test temperature. Two different specimen sizes were employed at each test temperature, and no effects of specimen size upon crack growth were noted

  17. Calculation of the driving force for the radiation induced precipitation of Ni3Si in nickel-silicon alloys

    International Nuclear Information System (INIS)

    Miodownik, A.P.; Watkin, J.S.

    1979-01-01

    The appearance of precipitates which have been identified as Ni 3 Si in irradiated stainless steels and nickel rich alloys such as Inconel is of considerable interest in relation to the swelling behaviour of such materials. Work on binary nickel-silicon alloys has shown that Ni 3 Si can be induced to precipitate in alloys whose silicon content is well below the accepted solubility limit, and it has also been shown that such precipitates redissolve when heat-treatment is continued at the same temperature in the absence of irradiation. Such effects imply an irradiation induced shift of chemical potential, and cannot be explained by merely involving accelerated diffusion. This paper represents an attempt to calculate the shift in chemical potential required to precipitate Ni 3 Si in alloys containing 1-10% Si (at%) over a range of temperatures (300-1000K), and then proceeds to relate this calculated chemical potential with available information concerning the dose rates required to induce such precipitates at various temperatures. Presentation of the results is modelled on the well established methods for handling the Time-Temperature-Transformation behaviour of ordinary alloy systems, with dose rate being substituted for the time axis. Analogous calculations are presented for nickel-germanium alloys, in order to check whether the numerical values deduced from the nickel silicon system have more general applicability, and also to see whether there are any significant differences in a system where the size factor of the solute is of the opposite sign. (orig.) [de

  18. Studies on the weldability, microstructure and mechanical properties of activated flux TIG weldments of Inconel 718

    Energy Technology Data Exchange (ETDEWEB)

    Ramkumar, K. Devendranath, E-mail: ramdevendranath@gmail.com; Kumar, B. Monoj; Krishnan, M. Gokul; Dev, Sidarth; Bhalodi, Aman Jayesh; Arivazhagan, N.; Narayanan, S.

    2015-07-15

    This research article addresses the joining of 5 mm thick plates of Inconel 718 by activated flux tungsten inert gas (A-TIG) welding process using SiO{sub 2} and TiO{sub 2} fluxes. Microstructure studies inferred the presence of Nb rich eutectics and/or laves phase in the fusion zone of the A-TIG weldments. Tensile studies corroborated that the ultimate tensile strength of TiO{sub 2} flux assisted weldments (885 MPa) was better compared to SiO{sub 2} flux assisted weldments (815 MPa) and the failure was observed in the parent metal for both the cases. Impact test results portrayed that both the weldments were inferior in toughness as compared to the parent metal, which was due to the presence of oxide inclusions. Also, the study investigated the structure–property relationships of the A-TIG weldments of Inconel 718.

  19. Hydrogen effect on the fatigue behavior of LBM Inconel 718

    Directory of Open Access Journals (Sweden)

    Puydebois Simon

    2018-01-01

    Full Text Available For several years, Inconel 718 made by Laser Beam Melting (LBM has been used for components of the Ariane propulsion systems manufactured by ArianeGroup. In the aerospace field, many components of space engines are used under hydrogen environment. The risk of hydrogen embrittlement (HE can be therefore a first order problem. Consequently, to improve the HE sensitivity of LBM Inconel 718, a systematic approach needs to be developed to characterize the microstructure at different scales and its interaction with hydrogen. This study addresses the impact of gaseous hydrogen on the material mechanical behavior under fatigue loadings. In a first step, the low cycle fatigue behavior under 300 bar of hydrogen gas has been evaluated with specimen loaded at a constant load ratio of R=0.1 and a frequency of 0.5 Hz. A reduction in the cycle number of fracture is shown. This reduction of fatigue life is a consequence of the impact of hydrogen damage processes. The impact of hydrogen is evaluated at the stages of crack initiation, crack propagation. These results are discussed in relation with the hydrogen embrittlement mechanisms and particularly in terms of hydrogen / plasticity interactions. To achieve this, the fracture surface morphology was first examined using scanning electron microscopy and second samples near the fracture surface were extracted using Focused-Ion Beam machining from regions containing striation. The main result observed is a reduction of the size of dislocation organization in relation with a decrease of the striation distance.

  20. Probabilistic and microstructural aspects of fatigue cracks initiation in Inconel 718; Aspects probabilistes et microstructuraux de l'amorcage des fissures de fatigue dans l'alliage INCO 718

    Energy Technology Data Exchange (ETDEWEB)

    Alexandre, F

    2004-03-15

    Thermomechanical treatments have been recently developed to produce Inconel 718DA (Direct Aged). This alloy optimisation leads to an increase of the fatigue life but also the scatter. The aim of this study is on the one hand the understanding of the fatigue crack initiation mechanisms and on the other hand the modelling of the fatigue life and the scatter. An experimental study showed that the fatigue cracks were initiated from carbide particles in fine grain alloy. Interrupted tensile tests show that the particles cracking occurred at the first quarter of the fatigue cycle. Fatigue behaviour tests were also performed on various grain size 718 alloys. The last experimental part was devoted to measurements of the low cycle fatigue crack growth rates using a high focal distance microscope. For these tests, EDM micro-defects were used for the fatigue crack initiation sites. This method was also used to observe the small fatigue crack coalescence. A fatigue life model is proposed. It is based on the three fatigue crack initiation mechanisms competition: particle crack initiation on the surface, internal particle crack initiation and Stade I crack initiation. The particle fatigue crack initiation is supposed instantaneous at a critical stress level. The Tanaka and Mura model is used for analysing the Stage I crack initiation number of cycles. The fatigue crack growth rate was analysed using the Tomkins model identified on the small fatigue crack growth rate measurements. The proposed fatigue life model decomposed in three levels: a deterministic one and two probabilistic with and without crack coalescence. (author)