International Nuclear Information System (INIS)

Irradiation of ferritic steels with neutrons in the temperture range of room temperature to #propor to# 450deg C results in lattice hardening, which causes an increase in strength and a decrease in ductility. Eight reduced-activation Cr-W-V stels with chromium concentration varying from 2.25 to 12% were irradiated at 365deg C to #propor to# 7 dpa in the Fast Flux Test Facility. A steel with 2.25% Cr and the combination of 2% W and 0.25% V hardened less than those containing vanadium or tungsten alone or a steel with 1% W and 0.25% V. The amount of hardening was similar for Cr-W-V steels with constant vanadium and tungsten concentrations and containing 2.,25, 5, and 9% Cr; a steel with 12% Cr hardened considerably more. Specimens of two conventional Cr-Mo steels, 9Cr-1MoVNb and ...

Energy Technology Data Exchange (ETDEWEB)

Higher efficiencies of steam power plants are achieved by raising the operating temperature and pressure. The use of ferritic steels helps to minimize the cost and enhance the flexibility (two-shift operation, frequent starting and stopping). The COST programme had the long-term goal of developing and testing 9- 12 % Cr steels with high fatigue strength and to produce,test and operate critical components for an advanced steam power plant (steam temperature 600 C and supercritical pressure). (orig.)

Energy Technology Data Exchange (ETDEWEB)

Strain controlled fatigue experiments on the modified ferritic-martensitic 12% Cr-steel Manet have been performed during, after and without irradiation. Continuous push-pull cycling of the hollow fatigue specimens with a cycle ratio R=-1, an axial strain rate of 8.10{sup -4} s{sup -1} and total strain ranges {Delta}{epsilon}{sub t} between 0.42% and 1.0% has been applied in vacuum (5.10{sup -3} Pa) at T=250 C. For the irradiation, a 104 MeV {alpha}-particle beam was used. Compared to unirradiated specimens, in-beam specimens undergo irradiation hardening at an advanced fatigue/implantation stage. Post-irradiation specimens show significantly higher total stress amplitudes and reduced fatigue lives. TEM investigations of in-beam and post-irradiation specimens reveal helium bubbles with different diameters on internal surfaces and in the matrix. (orig.).

International Nuclear Information System (INIS)

Structure of ferrite in drawn pearlitic steel containing 0.9 mass% C was investigated with X-ray diffraction technique using synchrotron radiation. In the detailed analysis of diffraction peaks of ferrite during the drawing process, it was experimentally revealed that the transformation of ferrite from bcc to bct due to the supersaturation of carbon in ferrite of heavily drawn pearlitic steel.

Energy Technology Data Exchange (ETDEWEB)

Out of the R and D of mesoscopic metal group composite materials, the paper described the fiscal 1997 results. In the in-situ method as a composite material making method, elucidated to some degree were chemical composition of Fe-C-Cr-V-Nb-Mo-W-Ni base multi-dimensional alloys, and wear resistance and oxidation resistance of MC type carbide dispersion multi-phase texture crystallizing as primary crystal and eutectic. In the composite material making with ceramic fiber and alloy by the pressure infiltration method, the paper clarified the texture formation mechanism in solidification/heat treatment by a combination of Al alloys and alumina long fiber, and the relation between fiber configuration and wear resistance. By MA and MG methods as the powder metallurgy composite material making method, a composed body of {alpha}-stainless steel of Fe-12%Cr composition and M23C6 of 40-90vol% are designed for alloy composition, and ...

International Nuclear Information System (INIS)

The effect of W and V on the high temperature strength properties of 12%Cr-15%Mn austenitic steels was studied from the view point of precipitation hardening and internal stress. The contribution of W addition to the tensile and creep-rupture strength was not so large. By contrast the combined addition of W and V increased the strength considerably. These are resulted from the precipitation of fine vanadium nitride (VN) within grains and the enhancement of M_2_3C_6 type carbide precipitation at grain boundaries. The V added material had large internal stress value which is considered to be due to dislocation movement disturbed by fine vanadium nitrides. (author).

Energy Technology Data Exchange (ETDEWEB)

Experimental discussions were given on effect of V and W addition on the high temperature strength properties of 12% Cr-15% Mn austenite steels. The test samples were added with W at 0% to 3.5% and V at 0% to 0.5% in addition to C and N, and were given aging treatment or solution treatment. This paper describes the following matters on the results of high-temperature strength measurements and structural observation: A remarkable trend was observed that M23 Cb type carbides precipitate in the aging treatment, wherein aging hardening appears prominently which is attributable to ultra-fine deposits of vanadium nitride (VN) in the V-added material; the V addition is very effective in increasing the high-temperature tensile strength and creep fracture strength as compared with single W addition, wherein the said carbides that accelerate the precipitation as a result of the V addition make a large contribution, in addition to ...

International Nuclear Information System (INIS)

Mixed microstructures have been studied in low- carbon microalloyed steels suitable for automotive applications, after continuous cooling from the hot-rolled condition. Microstructural features such as polygonal ferrite, bainitic and acicular ferrite and microphase constituent are identified using transmission electron microscopy. The influence of these mixed structures on the tensile strength, impact toughness and fracture behaviour is examined. It is found that improvements in impact toughness as compared with microalloyed medium- carbon ferrite/pearlite steels can be achieved from these predominantly acicular structures developed by controlling alloy composition and continuous cooling of these lower carbon steels. (orig.).

British Library Electronic Table of Contents (United Kingdom)

An ultrafine-grained ferrite/cementite (UGF/C) steel with a local high density of cementite particles was fabricated through caliber-warm-rolling followed by annealing and resulted in a bimodal-sized microstructure. The characteristic bimodal-sized microstructure was attributed to the original ferrite-pearlite structure and cementite spacing, and reflected the original ferrite-pearlite structure. The smaller-sized clusters corresponded to the former pearlite regions and the larger-sized clusters to the proeutectoid ferrite regions. The cementite particles naturally localized within the former pearlite region. Most of the ferrite coarsening did not occur until the cementite particle spacing reached a critical value. The UGF/C microstructure with a bimodal grain size showed a yield strength ...

British Library Electronic Table of Contents (United Kingdom)

A ferritic steel with finely dispersed precipitates was investigated to reveal the fundamental strengthening mechanisms. The steel has a yield strength of 760MPa, approximately three times higher than that of conventional Ti-bearing high strength hot-rolled sheet steels, and its ultimate tensile strength reaches 850MPa with an elongation-to-failure value of 18%. Using energy dispersive X-ray spectroscopy (EDXS) and transmission electron microscope (TEM), fine carbides TiC with an average diameter of 10nm were observed in the ferrite matrix of the 0.08%Ti steel, and some cubic M23C6 precipitates were also observed at the grain boundaries and the interior of the grains. The finely dispersed TiC precipitates in the matrix provide matrix strengthening. The estimated magnitude of precipitation ...

Energy Technology Data Exchange (ETDEWEB)

The impact properties of high-strength low alloy TRIP steels such as 'TRIP-aided dual-phase steel' and 'TRIP-aided bainitic steel' associated with the transformation-induced plasticity (TRIP) of retained austenite were investigated for some applications to the automotive impact members. The TRIP steels possessed far higher impact absorbed value and lower ductile-brittle transition temperature than the conventional ferrite-martensite and ferrite-pearlite steels. The stress relaxation resulting from the strain-induced transformation of retained austenite islands or films improved the impact properties in terms of suppressing void and/or crack initiation and these propagation. The best impact properties were completed in the steel composing of uniform fine bainitic lath structure and a ...

International Nuclear Information System (INIS)

Argon ions irradiation of 12% Cr steels and Fe/Cr alloys results in the hardening up to 10000 MPa. This value exceeds the hardening level even for martensitic transformation. Along with the increase of microhardness following irradiation the shape of X-ray graph of the affected materials changes considerable. Hardening value and behavior are determined by temperature radiation doze, preliminary ageing, extent of cold strain and alloying. The odserved phenomenon is supposed to be caused by irradiation-induced structural transformations. Reversibility of radiation hardening of the materials in question was observed.

British Library Electronic Table of Contents (United Kingdom)

The effect of elastic and plastic strains on the magnetic properties of ferrite-pearlite steels has been studied. It has been shown that the sensitivity to elastic-tensile and bending strains is four to five times greater for remnant magnetization than for coercive force. In order to determine the degree of cold plastic deformation of high-carbon steels, a two-parametric testing technique based on the use of remnant magnetization and coercive force was suggested. An MMT-2 device was recommended for measurement of the required parameters.

Energy Technology Data Exchange (ETDEWEB)

Stainless steels can be nitrided at temperatures {<=}400 C to increase their hardness and wear resistance without a decreasing of their excellent corrosion resistance. Structure and properties of the surface layers produced by plasma nitriding and plasma immersion ion implantation in this temperature range were tested. There are negligible differences in the structure of the produced surface layers in spite of different interaction principles of the used technologies. However there are clear differences between the case of different steels. The case of ferritic chromium steels mainly consists of {epsilon}-nitride. Whereas the cases of austenitic and ferritic austenitic steels are characterized by expanded austenite. The corrosion resistance of the steels is reduced by nitriding only, if evident CrN-formation occurs. (orig.) 11 refs.

International Nuclear Information System (INIS)

Early failure of an induction-hardening carbon steel pipe, which was used to transport tailing slurry, was caused by pitting corrosion. The microstructure on the internal pipe surface layer was found being a mixture of martensite, pearlite and ferrite. In this work, the pitting corrosion behavior of each constitute in the microstructure of steel is investigated with electrochemical noise analyses; the electronic properties of passive films were studied with Mott-Schottky relationship. It is found that the passive films formed on the materials under investigation are highly disordered n-type semiconductors. The high-to-low pitting susceptibility is ferrite > martensite > pearlite. The pitting resistance is related to the semiconductive nature of the passive film formed on each constitute. The pitting susceptibility increases with the donor concentration in the passive films. (author)

International Nuclear Information System (INIS)

A variety of advanced controlled rolling techniques have been developed to improve toughness, strength and weldability of niobium-steels. To achieve optimum properties, control of prior stage rolling conditions and accelerated cooling are needed. In low carbon steel, the addition of niobium results in a greater increase in tensile strength than that of vanadium without a loss of toughness. At the same strength level, niobium-steel has less susceptibility to weld cracking and good toughness in the HAZ of its weldments than similar vanadium steels. Separation and formability of niobium steels are also discussed.

International Nuclear Information System (INIS)

In the feasibility study on commercialized FBR systems, the application of 12Cr steel, with its physical properties and high-temperature strength properties, as structural material is considered in order to greatly reduce construction costs by compacted instruments and structures. In this report, creep, fatigue and the creep-fatigue properties of Mod.9Cr-1Mo steel forging (thickness 550mm) weld, representing conventional steels, were evaluated in order to obtain the needed basic data for the evaluation of the high-temperature strength of 12Cr steel weld. The results obtained are as follows: (1) Metal suitable for HAZ was made by applying thermal treatment to simulate the thermal hysteresis during welding to clearly define creep and fatigue properties in a HAZ softened zone. (2) Creep strength of the weld metal and the ...

British Library Electronic Table of Contents (United Kingdom)

A fully lamellar ferrite/cementite nanostructure was designed in a low C steel by using a specific thermal treatment. The strengthening of such microstructure has been investigated as a function of prestrain by rolling up to a deformation of 300%. As in usual pearlitic structure, its work-hardening shows no saturation and its elongation to fracture remains rather constant instead of decreasing drastically as conventional steels. The hardening by a similitude effect is thus not the privilege of pearlitic steels. Nevertheless, its lower initial work-hardening rate at low strain compared to an equivalent pearlitic steel and a lower hardening potential at high strain let us suspect major differences in the nature and the behaviour of ferrite channels in relation to the morphogenesis of the mic...

International Nuclear Information System (INIS)

Due to thermal gradients and load changes steam-turbine casings suffer combined creep-fatigue loading. Creep and fatigue portions depend on service conditions. Special interest is focused on the behaviour of creep-fatigue cracks, originated from potential defects due to construction and manufacturing weldments, on residual lifetime assessment. The project deals with the crack-growth behaviour at 530deg C and r.t. of welded and unwelded heat-resistant cast steels: 1% CrMoV-cast (GS-17 CrMoV 5 11, two melts: low and high V-content) and 12% CrMoV-cast (G-X 22 CrMoV 12 1). The crack planes of CT-specimens investigated, taken from manual arc-welded plates, were situated in the heat-affected zone (HAZ). The fatigue, creep and combined creep-fatigue crack-growth behaviour was investigated by means of low-frequency (0.5 and 0.05 Hz) tests, holding-time (20 min) tests and constant load tests up to about 5 000 h. Metallographic ...

Energy Technology Data Exchange (ETDEWEB)

To avoid the drop in corrosion resistance of stainless steels in conventional nitriding (precipitation of CrN), low-temperature techniques like ion implantation, plasma immersion ion implantation (PIII, PI{sup 3}) and low-temperature plasma nitriding were developed. In this investigation, four stainless-steel grades (ferritic: X6Cr17, austenitic-ferritic: X2CrNiMoN22.5.3, austenitic: X8CrNiTi18.10 and X5CrNi18.10) were plasma-nitrided between 250 and 500 C. Nitrogen-enriched layers with a high nitrogen content were produced, leading to a significant increase in surface hardness. X-ray diffraction indicated that CrN did not precipitate if treatment temperatures did not exceed 400 C. 'Expanded austenite' formed in the austenitic and duplex steels and {epsilon}-nitride (Fe{sub 2}N{sub 1-x}) in the ferritic steel. The optically ...

International Nuclear Information System (INIS)

Neutron irradiation embrittlement of reactor pressure vessel (RPV) steels is one of the critical issues on aging management for long term operation of nuclear power plants. Mechanistic understanding of embrittlement is a key to accurate prediction of embrittlement, especially after long term operation where the mechanical test data are sparse. Since matrix hardening is the source of the embrittlement, we focus on matrix hardening of A533B bainitic pressure vessel steel. Bainitic matrix is composed of lath structure made by ferrite and carbides, therefore it is important to understand how this structure affects hardening behavior, and to understand irradiation response of each phase. As the typical dimension of lath structure of A533B is about one micron, nanoindentation technique is suitable for the estimation of hardening of each phase. MV ion accelerators were used for controlled irradiation because MeV ion irradiation ...

Energy Technology Data Exchange (ETDEWEB)

Duplex-coating procedures consisting of plasma nitriding and Me-C:H hard coating lead to an improved performance of the devices because the Me-C:H coating is supported by the nitrided phase and, therefore, the `eggshell-effect` is avoided. Furthermore, this support leads to a higher load-bearing capacity of the thin film. Two standard procedures (classical high-pressure plasma nitriding and unbalanced magnetron sputtering of Ti-C:H) were performed subsequently to prepare the duplex coatings on X20Cr13 ferritic stainless steel. The corrosion resistance of the steel could be improved by nitriding at 450 C compared to the untreated ferritic substrate. The roughness is determined by the nitriding step. The weakest point of the coating is the transition zone between the nitrided and the untreated substrate and not the interface between the Ti-C:H coating and the nitrided substrate as shown by the Rockwell ...

International Nuclear Information System (INIS)

The synergistic effects of displacement damage and atomic hydrogen and helium on swelling of the ferritic/martensitic steel, F82H, has been investigated. The irradiation was performed at temperatures between 470 and 600 deg. C to 50 dpa (displacement per atoms) under conditions of simultaneous ion beams consisting of Fe"3"+, He"+ and H"+ ions or Fe"3"+ and He"+ ions. The swelling of F82H steel under triple beams with 18 appm He/dpa and 70 appm H/dpa was larger than that under dual beams with 18 appm He/dpa. The swelling in F82H under triple beams increased with decreasing irradiation temperature from 0.1% to 3.2%, while swelling under dual beams was between 0.04% and 0.08%. On the other hand, in the case of triple beam irradiation with a high ratio of gas/dpa, the swelling tended to increase with irradiation temperature. The swelling in ferritic/martensitic steels is significantly ...

International Nuclear Information System (INIS)

The influence of chemical composition and heat treatment on a low-carbon steel, chromium steel and high speed steel has been examined by polarisation curves and electrochemical parameters deduced from the Tafel plots. The electrochemical corrosion resistance, which is small between the as-received steels become greater after heat treatment, following the order: carbon steel < chromium steel #approx# high speed steel. To explain these differences, the nano- and microstructure of the steels has been characterized by the ex situ techniques of atomic force microscopy and optical microscopy, before and after surface etching with Nital (a solution of 5% HNO_3 in ethanol). This causes preferential attack of the ferrite phases showing the carbide phases more clearly. From these nanostructural studies it ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical dissolution behaviour of armco-iron and of the steels C15, C45, C60 and 100Cr6 in concentrated sodium chloride media has been investigated. Anodic metal dissolution experiments have been carried out using the flow channel cell (parallel plate reactor), the rotating cylinder electrode (RCE) and the capillary cell. The microstructure of the steel has been varied through variation of carbon content and heat treatment (e.g. soft annealed with globular carbides or pearlitic). Current-efficiency values have been obtained by gravimetric measurements in the current-density range from i=5 to 60 A/cm{sup 2}. For the soft annealed steels, the divalent ferrite dissolution in combination with electroless cementite removal dominates. For the pearlitic steels, the occurrence of oxygen evolution electronically conductive metal carbides or trivalent ferrite ...

Energy Technology Data Exchange (ETDEWEB)

Transition joints in power plants between ferritic steels and austenitic stainless steels suffer from a mismatch in coefficients of thermal expansion (CTE) and the migration of carbon during service from the ferritic to the austenitic steel. To overcome these, nickel-based consumables are commonly used. The use of a trimetallic combination with an insert piece of intermediate CTE provides for a more effective lowering of thermal stresses. The current work envisages a trimetallic joint involving modified 9Cr-1Mo steel and 316LN austenitic stainless steel as the base materials and Alloy 800 as the intermediate piece. Of the two joints involved, this paper describes the choice of welding consumables for the joint between Alloy 800 and 316LN. Four consumables were examined: 316, 16-8-2, Inconel 82 and Inconel 182. The comparative evaluation was ...

International Nuclear Information System (INIS)

The critical part of the trimetallic transition joint (type 304 stainless steel/Alloy 800/2.25 Cr-1 Mo steel), the Alloy 800/2.25 Cr-1 Mo steel joint welded with Inconel 182, was subjected to thermal cycling between room temperature and 873 K. The thermal cycling test procedure used produces accelerated failures in transition joints similar to those observed in steam generators of operating power plants. On thermal cycling, precipitation at the weld/ferritic steel interface decreased on post-weld heat treatment. This precipitation increased with increased prior ageing and applied stress. The results of these tests indicated a considerable improvement in performance of the trimetallic transition joint compared to the direct (bimetallic) transition joint. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Described herein are effects of nitrogen dissolved in steel on passivity and pitting corrosion, as one of the major corrosion phenomena observed in stainless steel. Mechanisms involved in controlling pitting corrosion by nitrogen are also discussed. Nitrogen contained in austenic stainless steel is concentrated in the surface area, in particular in the vicinity of the interface between the passive film and metal matrix. Nitrogen tends to decrease critical current density in an acid, when it is added to steel of high critical current density (approximately 1mA/cm{sup 2} or higher). This phenomenon is considered to result from accumulation of nitrogen preferentially in the surface area to prevent dissolution of steel. Nitrogen dissolved in the austenic phase improves resistance of the steel to pitting corrosion. This phenomenon is considered to result from ...

Energy Technology Data Exchange (ETDEWEB)

Dissimilar metal welds between ferritic low-alloy and austenitic stainless steels commonly occur in power plant application. In order to overcome some of the problems encountered here, a trimetallic configuration using an intermediate piece (such as Alloy 800) between the austenitic and ferritic steels has been suggested. This paper describes some features of the joints between modified 9Cr-1Mo steel and Alloy 800, produced with Inconel 82/182 filler material. The joints require heat-treatment after welding and the results have shown that a treatment at 760 C for 2 h would be optimal. Although most tensile failures occurred in the weld metal the welds were found to exhibit strength properties that are at least equal to those of Alloy 800, with a tensile elongation lying between those of the two base materials. Similarly, while the weld metals are slightly less tough than the two ...

Energy Technology Data Exchange (ETDEWEB)

This paper reports that the co-deposition of chromium and silicon into a 2.25Cr-1.0Mo-0.15C steel, alloy 800, and type 304 stainless steel has been achieved using the pack cementation process. The ferritic coating produced on the 2.25 Cr-1.0Mo steel was approximately 225 {mu}m (9 mils) thick, whereas the inward diffusion of chromium and silicon produced a two-phase structure of ferrite and austenite for type 304. Chromium and silicon were incorporated into the austenitic solid solution upon diffusion into alloy 800. All coatings had approximately 25 to 35 wt% Cr and 2 to 3% Si at the surface. Cyclic oxidation testing in air of the coated 2.25Cr-1.0Mo steel (T = 700{degrees} C) and type 304 (T = 1035{degrees} C) showed a dramatic decrease in the oxidation kinetics compared to the original uncoated alloys. The cyclic oxidation of alloy 800 was also improved.

Energy Technology Data Exchange (ETDEWEB)

A procedure and correlations are presented for predicting Charpy-impact energy, tensile flow stress, fracture toughness J-R curve, and J{sub IC} of aged cast stainless steels from known material information. The ``saturation`` impact strength and fracture toughness of a specific cast stainless steel, i.e., the minimum value that would be achieved for the material after long-term service, is estimated from the chemical composition of the steel. Mechanical properties as a function of time and temperature of reactor service are estimated from impact energy and flow stress of the unaged material and the kinetics of embrittlement, which are also determined from chemical composition. The J{sub IC} values are determined from the estimated J-R curve and flow stress. Examples of estimating mechanical properties of cast stainless steel components during reactor service are presented. A common ``lower-bound`` J-R ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical behaviour of passive films formed on one austenitic stainless steel (AISI 304) and one ferritic stainless steel (AISI 446) in solutions with pH between 0.6 and 8.4 was studied by capacitance measurements and photocurrent spectroscopy. Compositional characterization of the passive films was done by X-ray photoelectron spectroscopy. The capacitance increases with decreasing pH. Doping densities evaluated from Mott-Schottky plots are in the range 2-6 x 10{sup 20} cm{sup -3} and increased with the pH in the neutral/alkaline range while in pH 0.6, values above 10{sup 21} cm{sup -3} were found. The bandgap energy indicates two transitions, at 2.5-2.8 and 3.2 eV. The analytical data reveal that, as the pH increased, the films become enriched in Fe(II) and Fe(III), whereas the Cr(III) gradually decreases. The films formed at very low pH had a behaviour that contrasts with that of the films formed in the ...

International Nuclear Information System (INIS)

Because of their austenitic-ferritic microstructures, duplex stainless steels offer a good combination of mechanical and corrosion resistance properties. However, heat treatments can lower the mechanical strength of these stainless steels as well as render them susceptible to intergranular corrosion (IGC) and pitting corrosion. In this study, a low-carbon (0.02%) duplex stainless steel is subjected to various heat treatments at 450 to 950 C for 30 min to 10 h. The heat-treated samples than undergo ASTM IGC and pitting corrosion tests, and the results are correlated with the microstructures obtained after each heat treatment. In the absence of Cr_2_3C_6 precipitation, #sigma#-phase precipitates render this duplex stainless steel susceptible to IGC and pitting corrosion. Even submicroscopic #sigma#-phase precipitates are deleterious for IGC resistance. Longer-duration heat treatments ...

Energy Technology Data Exchange (ETDEWEB)

The effect of molybdenum on the electronic structure of the passive films formed on ferritic (Fe-Cr and Fe-Cr-Mo) stainless steels is examined by capacitance and photoelectrochemical measurements. The capacitance study is supported by a mathematical analysis of the Schottky barrier developed at the semiconductor-electrolyte interface in the case of a semiconductor with multiple bulk electronic states in the bandgap. The numerical simulations, based on the more general Mott-Schottky relation proposed, are in good agreement with the experimental results. It can be concluded that the capacitance behavior of the passive films is related to the contributions of a shallow donor level very close to the conduction band and a deep donor level at about 0.4 eV below the conduction band. The addition of molybdenum decreases the donor density of the deep level. Photoeffects observed for subbandgap photon energies reveal that this deep donor level behaves ...

Energy Technology Data Exchange (ETDEWEB)

Microstructural analyses by advanced metallographic techniques were conducted on mockup welds and a cracked BWR core shroud weld fabricated from Type 304L stainless steel. heat-affected zones of the shroud weld and mockup shielded-metal-arc welds were free of grain-boundary carbide, martensite, delta ferrite, or Cr depletion near grain boundaries. However, as a result of exposure to welding fumes, the heat-affected zones of the welds were significantly contaminated by fluorine and oxygen which migrate to grain boundaries. Significant oxygen contamination promotes fluorine contamination and suppresses classical thermal sensitization, even in Type 304 steels. Results of slow-strain-rate tensile tests indicate that fluorine exacerbates the susceptibility of irradiated steels to intergranular stress corrosion cracking. These observations, combined with previous reports on the strong influence of weld flux, ...

Energy Technology Data Exchange (ETDEWEB)

The microstructure of the layers produced by plasma nitriding austenitic stainless steel at different treatment temperatures (400 and 500 C) were studied by transmission electron microscopy (TEM) together with X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that the microstructures were composed of 'expanded austenite' ({gamma}{sub N}) and {alpha}(ferrite)+CrN following plasma nitriding at lower and higher treatment temperatures, respectively. The former contains stacking faults and deformed twin substructures, while the latter is made up of colonies displaying a lamellar structure. Kurdjumov-Sachs or Nishiyama-Wassermann orientation relationships between the {alpha} and CrN layer were observed. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Abstract not provided

Energy Technology Data Exchange (ETDEWEB)

Surface structure analysis, i.e. metallographic analysis of component surfaces with the aid of replicas, is an established method of component monitoring and the only reliable non-destructive method for detecting and analyzing beginning creep damage in the form of creep pores. Creep pore development provides a basis for component condition analysis. It must be noted, however, that the modern martensitic 9-12 % Cr steels - like the established steels 10CrMo9-10 (P22) und X20CrMoV12-1 - have comparatively high creep fracture deformation rates in fatigue tests. This raises the question if these steels can be judged on the basis of data for established steels. The results so far suggest that even with low pore densities (single pores), a higher degree of damage and a shorter time until failure must be assumed. [German] Eine bewaehrte Methode der Bauteilueberwachung ...

Energy Technology Data Exchange (ETDEWEB)

We present the synthesis, magnetic and UV spectrometry of NiZn-ferrite nanofiber. The single phase of spinel ferrite was obtained at 600 {sup o}C. The NiZn-ferrite fibers fabricated by an electrospinning process were formed as a polygonal grain growth with firing temperature in fiber matrix. It appeared that the saturation magnetization (M{sub S}) of NiZn-ferrite nanofiber was dependent on Ni/Zn molar ratio which is similar to that of the inverse spinel ferrites. The NiZn-ferrite fibers showed good DNA adsorption efficiency that can be modified and utilized for DNA separation with magnetic nanofiber as a novel material in clinical applications.

Science.gov (United States)

In this study, four API X80 pipeline steels were fabricated by varying Mo, Cr, and V additions, and their microstructures and crystallographic orientations were analyzed to investigate the effects of their alloying compositions on tensile properties and Charpy impact properties. Because additions of Mo and V promoted the formation of fine acicular ferrite (AF) and granular bainite (GB) while prohibiting the formation of coarse GB, they increased the strength and upper-shelf energy (USE) and decreased the energy transition temperature (ETT). The addition of Cr promoted the formation of coarse GB and hard secondary phases, thereby leading to an increased effective grain size, ETT, and strength, and a decreased USE. The addition of V resulted in a higher strength, a higher USE, a smaller effective grain size, and a lower ETT, because it promoted the formation of fine and homogeneous of AF and GB. The steel that contains 0.3 wt ...

Energy Technology Data Exchange (ETDEWEB)

The influence of high C martensite on the strength and impact behavior of C-Mn-Nb-Al steels has been determined for two distributions: films surrounding the ferrite grains and distinct colonies. In the former case, the impact behavior markedly deteriorated, this deterioration increasing with martensite level. The changes in impact behavior could be explained by regarding the films of martensite as being similar to the brittle grain boundary carbides that are present in ferrite-pearlite steels. These films readily crack, yet are always thick enough to produce a sufficient wide crack to render crack propagation easy. The critical event in fracture then becomes the ability to propagate the cracks through the grain boundaries. The greater the grain boundary coverage by these films, the easier this becomes and the worse is the impact behavior. When the martensite is present as colonies, again the impact ...

British Library Electronic Table of Contents (United Kingdom)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically conductive and corrosion-resistant CrN or Cr2N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of commercially available, high Cr (30-35wt%) Ni-Cr alloys and a ferritic high Cr (29wt%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effect...

Energy Technology Data Exchange (ETDEWEB)

The development and improvement of materials plays a key role in energy technology, particularly in power plant technology, because materials are crucial to plant performance and power availability. This becomes particularly clear when one considers that modern power plants generate temperatures of up to 600 C and pressures of up to 230 bar in order to increase process efficiency, conserve resources and reduce CO{sub 2} emissions. Modern heat-resistant materials for power plant technology are customised materials which have been developed to meet the specific requirements of special applications. After the requirement profile has been determined the material is developed or optimised on the basis of previous experiences gained with materials in power plant technology. Basic heat-resistant materials are ferritic materials containing 9 to 12% Cr as well as additions of Mo, V, Nb and W, amongst other elements. Together with ...

International Nuclear Information System (INIS)

In this work we report a study of the induced changes in structure and corrosion behavior of martensitic stainless steels nitrided by plasma immersion ion implantation (PI"3) at different previous heat treatments. The samples were characterized by x-ray diffraction and glancing angle x-ray diffraction, scanning electron microscopy, energy dispersive x-ray spectroscopy, and potentiodynamic measurements. Depending on the proportion of retained austenite in the unimplanted material, different phase transformations are obtained at lower and intermediate temperatures of nitrogen implantation. At higher temperatures, the great mobility of the chromium yields CrN segregations like spots in random distribution, and the #alpha#"'-martensite is degraded to#alpha#-Fe (ferrite). The nitrided layer thickness follows a fairly linear relationship with the temperature and a parabolic law with the process time. The corrosion resistance depends strongly on ...

Energy Technology Data Exchange (ETDEWEB)

In the present paper, the chemical composition of passive films formed on both phases of two types of duplex stainless steels (UNS S31803 and UNS S32304) is determined at the micro-scale using Auger electron spectroscopy (AES). Samples were either mechanically polished (down to diamond pastes) or electrochemically etched in acidic solutions. The micro-electrochemical behavior of samples was then determined in sodium chloride media by means of the electrochemical micro-cell technique (capillary diameters of 30 {mu}m). The results obtained were analyzed considering the passive film chemical composition. Quantitative relationships between electrochemical parameters and the distribution of chromium and iron in the oxide layer were found. Due to differences in mechanical properties between ferrite and austenite, a heterogeneous stress distribution is generated in both phases. A method based on thermal-mechanical simulation was used to quantify ...

Energy Technology Data Exchange (ETDEWEB)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically conductive and corrosion-resistant CrN or Cr{sub 2}N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of commercially available, high Cr (30-35 wt%) Ni-Cr alloys and a ferritic high Cr (29 wt%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effects for the Ni-Cr base alloys, but beneficial effects for the stainless steel alloy. Positive results from single-cell fuel cell ...

Energy Technology Data Exchange (ETDEWEB)

Fretting wear test in room temperature water was performed to evaluate the wear coefficient of CANDU (CANadian Deuterium Uranium) steam generator (SG) tube material (Alloy 800) against 410 type martensitic stainless steels. The main focus is to compare the wear behaviors between Alloy 800 and Inconel 690. Test conditions are 10{approx}30N of normal load, 200{approx}450mm of sliding amplitude and 30Hz of frequency. The result indicated that the wear rate of Alloy 800 was higher than those of Inconel 690 at various test condition such as normal loads, sliding amplitudes etc. From the results of SEM observation, there was little evidence of plastic deformation layer that were dominantly formed on the worn surfaces of Inconel 690. Also, wear particles in Alloy 800 were released from contacting asperities deformed by severe plastic flow during fretting wear. Main cause of wear rate between Alloy 800 and Inconel 690 may be due to the difference of hardness between ...

Energy Technology Data Exchange (ETDEWEB)

Corrosion of several materials including pure metals Fe, Ni, Cr and also Fe-Cr, Fe-Ni-Cr alloys, has been studied in anisothermal Pb17Li (Tmax = 500 deg C; {Delta}T = 60 deg C). The corrosion rate of pure nickel is two orders of magnitude higher than the chromium one and about three orders of magnitude higher than the iron one. Fe-Cr alloys (1.4914) suffers a dissolution rate equal to the one of its major constituent, iron. With regard to the three austenitic materials (316L and NS20 steels, alloy 800), they exhibit a porous corrosion layer mainly constituted of ferrite but containing also a small amount of {sigma} phase in the case of the alloys with higher Ni content, NS30 steel and alloy 800. Mechanism of formation of this layer is discussed.

Energy Technology Data Exchange (ETDEWEB)

To simulate radiation damage under a future Spallation Neutron Source (SNS) environment, irradiation experiments were conducted on a candidate 9Cr-2WVTa ferritic/martensitic steel using the Triple Ion Facility (TIF) at ORNL. Irradiation was conducted in single, dual, and triple ion beam modes using 3.5 MeV Fe{sup ++}, 360 keV He{sup +}, and 180 keV H{sup +} at 80, 200, and 350{degrees}C. These irradiations produced various defects comprising black dots, dislocation loops, line dislocations, and gas bubbles, which led to hardening. The largest increase in hardness, over 63 %, was observed after 50 dpa for triple beam irradiation conditions, revealing that both He and H are augmenting the hardening. Hardness increased less than 30 % after 30 dpa at 200{degrees}C by triple beams, compatible with neutron irradiation data from previous work which showed about a 30 % increase in yield strength after 27.2 dpa at 365{degrees}C. However, the very large ...

International Nuclear Information System (INIS)

This paper introduces the JNM Special Issue on the development of a first wall for the reaction chamber in a laser fusion power plant. In this approach to fusion energy a spherical target is injected into a large chamber and heated to fusion burn by an array of lasers. The target emissions are absorbed by the wall and encapsulating blanket, and the resulting heat converted into electricity. The bulk of the energy deposited in the first wall is in the form of X-rays (1.0-100 keV) and ions (0.1-4 MeV). In order to have a practical power plant, the first wall must be resistant to these emissions and suffer virtually no erosion on each shot. A wall candidate based on tungsten armor bonded to a low activation ferritic steel substrate has been chosen as the initial system to be studied. The choice was based on the vast experience with these materials in a nuclear environment and the ability to address most of the key remaining issues with existing ...

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

This book contains 10 lectures with the following subjects: On the effect of thermal pretreatment on the structure and creep behaviour of the alloy 800 H (V. Guttmann, J. Timm); Material properties of heat resistant ferritic and austenitic steels after cold forming (W. Bendick, H. Weber); Investigations for judging the working behaviour of components made of alloy 800 and alloy 617 under creep stress (H.J. Penkalla, F. Schubert); Creep behaviour of gas turbine materials in hot gas (K.H. Kloos et al.); Effect of small cold forming on the creep beahviour of gas turbine blades made of Nimonic 90 (K.H. Keienburg et al.); Investigations on creep fatigue alternating load strength of nickel alloys (G. Raule); Change of structure, creep fatigue behaviour and life of X20 Cr Mo V 12 1 (by G. Eggeler et al.); Investigations on thermal fatigue behaviour (K.H. Mayer et al.); Creep behaviour of similar welds of the steels 13 Cr Mo 4 4, ...

Energy Technology Data Exchange (ETDEWEB)

A number of screening tests were performed to determine ion species that effectively reduce wear rates when implanted in four industrial steels. Ball bearing steel 100Cr6 (AISI 52100) showed a wear rate reduction by a factor of 20 when implanted with carbon dioxide to a dose of 5x10{sup 17} cm{sup -2} with a non-mass-separated ion beam and by a factor of {>=}20 when implanted with 5x10{sup 17} cm{sup -2} oxygen ions. For the ferritic and martensite steels X90CrMoV18 (AISI 440B, unhardened and hardened) also a strong wear reduction after implantation of oxygen ions was found. Co-implantation of aluminum and oxygen also reduces wear rates of X90CrMoV18, of S6-5-2 (AISI M2), and of 100Cr6, respectively. For comparison, thin oxide layers were grown in a low-temperature thermal oxidation process. These experiments also yielded reduced wear rates by a factor of 10. The surfaces were investigated and ...

Energy Technology Data Exchange (ETDEWEB)

One aspect of the research program SFB 570 'Distortion engineering' is the in situ X-Ray diffraction analysis of phases and residual stresses during complete heat treatment cycles. These investigations result in experimental evidence available for the extensive computations. The optimisation of the instrumentation will be reported. A surface decarburisation of samples made from the ball bearing steel 100Cr6 could be avoided for a temperature range from 800 to 900 C and a holding time of one hour by a combination of evacuate the furnace and using a certain nitrogen flow as protective gas. At lower temperatures small amounts of ferrite caused by an increased diffusion rate of carbon lead again to a surface decarburisation up to a depth of 2 {mu}m. It was proved that with an evacuation of the X-Ray beam path at constant power of the X-Ray source the intensity of diffraction lines could be increased by more than a factor of 4. The ...

Energy Technology Data Exchange (ETDEWEB)

The significant technical and industrial aspects which have led to main coolant line (MCL) materials selection are addressed from a long term experience and operational practice point of view. They are based on the Siemens/KWU developed basic material concept for its nuclear power plants. It considers the choice of appropriate materials, the evaluation and qualification of the materials and the materials manufacturer, the use of appropriate semi-finished products, the tailoring of material and semi-finished products to the specific requirements of the various systems, the application of adequate manufacturing processes and the proof of the requirements by specifying proper tests and examinations. The main systems are assigned to safety classes in accordance with their safety relevance. Summarizing the operation time of nuclear power plants with ferritic MCL equipped by Siemens/KWU, more than 200 years of operation experience exist and no upgrading or replacement of ...

Energy Technology Data Exchange (ETDEWEB)

Magnetic field, thickness and magnetic forming effect on general mode and quantitative parameters of the domain structure (DS) of ferrite-garnet (EuEr)/sub 3/(FeGa)/sub 5/O/sub 12/ monocrystalline plates (111) is investigated. Field interval of circle (cone) and ring domain stability is determined. It is shown that DS of ferrite-garnet crystals with uniaxial an6sotropy has some peculiarities, that can be explained by cubic anisotropy effect.

Energy Technology Data Exchange (ETDEWEB)

Four low activation alloy classes, two austenitic and two ferritic, have been incorporated into the MOTA-1B experiment in the FFTF reactor to provide an early assessment of the suitability of such alloys for reactor service.

International Nuclear Information System (INIS)

This paper presents the present status of R and D activities on plasma facing components for fusion reactors, such as International Thermonuclear Experimental Reactor (ITER) and fusion demonstration reactor (DEMO). The plasma facing components (PFCs) as typified by divertor and first wall components are subjected to high heat flux and particle flux from fusion plasma. It is essential for these components to have sufficient heat removal capability and robust structure against those loadings. JAEA has been carried out to develop the ITER-PFCs which consist of copper alloys and armor materials with high thermal conductivity, such as carbon fiber composites, tungsten and beryllium. The demonstration of the thermomechanical performance of the ITER-PFCs by using mock-ups has successfully been made under close mutual cooperation between the participant countries of ITER. Currently, the activity on the development of the ITER-PFCs is in a qualification phase prior to the bulk production for ...

International Nuclear Information System (INIS)

A new eddy current array probe has been implemented as a straightforward and promising technique for detection of outer diameter (OD) surface-breaking cracks on the extrados of feeder bends. The design is based on previous work performed at AECL, which had demonstrated that eddy current probes with laterally displaced transmit-receive coils can overcome some of the limitations of inspecting ferritic steel components for surface-breaking cracks. The Feeder Integrity Joint Program-CANDU Owners Group Inc. (FIJP-COG) Non-Destructive Evaluation (NDE) Team members commissioned AECL to work in collaboration with the probe manufacturer ZETEC, to develop a field usable eddy current array probe. The objective was to acquire a technique with the following capabilities: fast scanning non-contact inspection technique for surface breaking discontinuities; full inspection of the bend extrados OD surface in a single scan; ability to inspect first and second ...

Energy Technology Data Exchange (ETDEWEB)

Effect of ultrasonic-wave irradiation on the Mn-Zn ferrite powder suspension prepared by solid-state reaction and alcoholic dehydration methods was investigated. Size, distribution, and morphology of the powders prepared at different temperatures were examined, as a function of irradiation time. It was observed that the powders were reduced in size by ultrasonic energy through distinct routes. 8 refs., 7 figs., 1 tab.

CERN Document Server

Structural steels with improved atmospheric corrosion resistance

International Science & Technology Center (ISTC)

Investigation of Destruction Mechanisms in Reactor Steels and Alloys under Cycling Deformation

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

The Recycler ring magnet will be made of Strontium ferrite permanent magnets. A strontium ferrite permanent magnet without compensation has a temperature coefficient of -0.2 % in dB/dT. To compensate this effect, we are utilizing 30 % Ni 70 % Fe alloy, a temperature compensation ferromagnetic material with a low Curie point. To search for optimum commercially available material and optimum condition, we made a couple of simple model magnets, and tested with several different compensating material. The test results are reported and its optimal conditions are shown. Several different configurations were tested including a possible 2 kG magnet configuration.

Energy Technology Data Exchange (ETDEWEB)

TRITEX was a pumped loop with Pb-15.8Li, fabricated from steel 1.4922. In contact with the molten eutectic were also molybdenum, vanadium and armco-iron. The loop was originally designed to investigate tritium extraction using solid getter metals. Over the years the goal changed to the study of metals, corrosion products and purification of the eutectic mixture. Therefore many modifications were done. The first part of this report describes TRITEX. All parts were enclosed in thermoboxes for a homogeneous temperature. One test section was in an argon glove box and could be opened during operation. Other special equipment`s were: permeation membranes and liquid-metal-covergas-interfaces to study the transport of H{sub 2}, D{sub 2} and {sup 3}H, different purification devices, a quartz observation window to see the liquid metal surface, 4 different kinds of flow measurements, level indicators, freeze valves. The second part describes loop operation. Between 1989 and ...

International Nuclear Information System (INIS)

Full text: It was recently-established for hexagonal barium ferrite-industrially important magnetically hard material that refinement of the crystallite dimensions into the nanoscale regime, typically #<=# 10 nm, leads after heat treatment at temperatures 800-1000 deg C to significant coercivity increase of up to 6.5 kOe (#approx#3-4 times) with saturation magnetisation values of 50-55 emu/g (#approx#95% of bulk at room temperature). High-energy mechanochemical processing has been applied to prepare nanostructural (nanocrystalline-amorphous) composites. High resolution electron microscopy studies reveal that the enhancement of the final magnetic properties was due to formation of magnetically noninteracting #approx#l,#mu#m Ba-ferrite particles with 5-10 nm amorphous surface layer - depending on annealing parameters. Similar situation was established also for ball milled strontium ferrite (SrFe_1_2O_1_9) powders where ...

Science.gov (United States)

A post-accident-heat-removal structural effects analysis for the steel liner in the FFTF concrete containment structure is presented. (JWR)

Science.gov (United States)

Polycrystalline soft ferrite, Cu1+xSixFe2?2xO4 (x=0.0, 0.05, 0.1, 0.15, 0.2 and 0.3) were prepared by standard ceramic technique. The X-ray analysis confirmed the single phase formation of the samples up to x=0.1 beside a second phase for x?0.15. The lattice parameter was found to decrease with composition(x), which is attributed to ionic size difference of cations involved. The bulk density measurements shows two different behavior for x0.15. The IR spectra of Cu Si ferrite system have been analyzed in the frequency range 200 1200 cm?1. It revealed two prominent bands ?1 and ?2 which are assigned to tetrahedral and octahedral metal complexes, respectively. The position of the highest frequency band is around 575 cm?1 while the lower frequency band is around 400 cm?1.

International Nuclear Information System (INIS)

M-type hexagonal ferrite composition, Ba(1-x)SrxFe12O19 (x=0.0, 0.2, 0.4, 0.6, 0.8 and 1.0), was prepared by a two route ceramic method. Complex permittivity (?'-j?'') and complex permeability (?'-j?'') have been measured using a network analyzer from 8.2 to 12.4 GHz X-ray diffraction confirmed the M-type hexagonal structure and a scanned electron micrograph was used to analyze the grain size distribution of ferrite. Substitution of Sr2+ ions causes an increase in porosity that deteriorates the electromagnetic and microstructural properties in the doped samples. Both dielectric constant and dielectric loss are enhanced in comparison to the permeability and magnetic loss over the entire frequency region. This is due to a resistivity variation and the formation of Fe2+ ions, which increases the hopping mechanism between Fe2+ and Fe3+ ions.

Energy Technology Data Exchange (ETDEWEB)

The purpose of this study is to evaluate the synergistic effect of helium and hydrogen on Fe-Cr ferritic model alloys, to provide basic understanding concerning development of fusion reactor components. Single, dual and triple ion-beams consisting of Fe{sup 3+}, He{sup +} and H{sup +} were used for irradiation, at temperatures 470-600 deg. C and dose to 50 dpa at 1 {mu}m. The dual beam irradiation with He enhanced cavity nucleation extensively to swelling of about 0.4%, whereas the dual beam irradiation with H did not significantly affect the microstructure. In the case of triple ion irradiation, the synergistic effect of He and H was confirmed clearly; relative large void formation and enhanced swelling to almost 5%. The synergistic effect suggests that the role of H is important for void growth and dislocation bias.

International Nuclear Information System (INIS)

Ferrite of system, namely Ni_1_-_xZn_xFe_2O_4 with x = (0.0, 0.2, 0.4, 0.6, 0.8, 1.0), have been prepared by solid state reaction to investigate the effect of gamma rays irradiations using Co"6"0 source on the cation distribution, structural and magnetic properties. The unirradiated and irradiated samples were then subjected to characterization techniques such as X-ray diffraction, magnetization and AC susceptibility. The results of these characterizations are found to be different for irradiated from that of the pristine sample. The modifications in respect of irradiated samples are explained in terms of the ion-induced disorder. The important result of #gamma#-irradiation on the cation distribution, structural and magnetic properties is the change of ratio Fe"2"+/Fe"3"+. Possible reasons on the results are proposed.

Science.gov (United States)

... rate on the tensile properties of SA-106 carbon steel pipe, in support of analysis and experimental modeling of postulated pipe whip in nuclear ...

CERN Document Server

Differences in synchrotron radiation induced gas desorption from stainless steel and aluminium alloy

Energy Technology Data Exchange (ETDEWEB)

There are two types in quench distortion of steel parts: thermal distortion and transformation distortion. Quench distortion is caused mainly by uneven cooling rate of steel parts from Austenitising temperature. The rapid cooled side is lengthened (convex deformation); the slow cooled side is shortened (concave deformation). So, to control the quench distortion, it is necessary to regulate the cooling rate of steel parts during quenching. TWO COMPONENTS produce the quench distortion of steel parts: the thermal stress and transformation stress. Generally, the effect of the thermal stress on the quench distortion is stronger than the transformation stress. The quench distortion is caused by uneven cooling rate of the steel parts, from Austenitising temperature to Ms point and Ms-Mf range. So, to control the quench distortion, it is very important to regulate the cooling rate of the ...

International Nuclear Information System (INIS)

Russian (Jan 1976). USSR Mironov, Yu.M. Makarov, VA Nauchno-

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

International Nuclear Information System (INIS)

Short communication.

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

The corrosion rate of low alloy steel SA-508 and carbon steel A-410b in simulated operation and shutdown conditions of pressurized water reactor has been determined Moreover potentiodynamic polarization curves and galvanic effect through coupling of AISI-304 have been carried out under shutdown simulated condition. (Author) 8 refs.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

In this book over 250 alloys are organized by AISI number into 10 major sections: Irons, Carbon Steels, Alloy Steels, Low Alloy Constructional Steels, Ultra High Strength Steels, Tool Steels, Maraging Steels, Wrought Stainless Steels, Heat Resistnat Casting Alloys, and Iron Based Rought Superalloys. Each alloy record lists the designation, specifications, UNS number, composition, product forms and a comment on the high-temperature properties and applications. Referenced data is then given for physical properties such as density, specific heat, thermal conductivity, thermal expansion, electrical conductivity, Poisson's ratio, moduli of elasticity and rigidity, etc. Mechanical properties follow, and include tensile properties, shearing and bearing properties, impact properties, creep, stress rupture and stress relaxation and fatigue ...

International Nuclear Information System (INIS)

The results have been presented of DC polarization and exposure investigations of alloy steels used as construction materials in flue gas desulphurization installations. on the base of analysis of composition of investigated steels and results of polarization studies, conditions have been discussed in which the pitting resistance equivalent (PRE) should be used. Among tested steels the significantly highest resistance to pitting corrosion is exhibited by 654SMO steel, classified as the super austenitic grade. (author). 14 refs, 3 figs, 2 tabs.

International Nuclear Information System (INIS)

author.The chemical and mechanical properties of S235jr structural low carbon mild steel were tested and reported for specimens collected from the Lebanese steel market. European and American standards were presented as references and compared with the achieved results. Discussion was conducted to show the similarities and differences between S235JR steel samples and standard requirements. Some of the reasons for such differences were discussed. A database was furnished through this work for the public and mainly for the Lebanese Standard Organization LIBNOR to easily adopt and implement a standard that has been tested in Lebanon concerning the hot rolled low carbon structural steels

International Nuclear Information System (INIS)

The long-term survival of serologically incompatible red cell units was measured in five patients with antibodies to high-frequency antigens. Initially, the survival of 1 ml of "5"1Cr-labeled incompatible red cells was measured over 1 hour. After demonstrating that the 1-hour survival times were successful (greater than 70%), each patient then received 5 ml of the same "5"1Cr-labeled red cells followed by the transfusion of the remainder of the red cell unit. The long-term T 1/2Cr survival for each case was patient 1 (anti-McCa), 15 days; patient 2 (anti-JMH), 12 days; patient 3 (anti-Kna), 31 days; patient 4 (anti-McCa), 12 days; and patient 5 (anti-Hya), 14 days. Each antibody tested in an in vitro homologous macrophage assay showed less than 5 percent phagocytosis. Anti-JMH was the only antibody to react with IgG subclass antisera and was determined to be IgG4. The macrophage assay, IgG subclass testing, and short-term (1 hour, 1 ml) "5"1Cr survival studies all indicated that the ...

International Nuclear Information System (INIS)

68 replaced carbon steel piping in secondary system of pressurized water reactor (PWR) has been investigated by visual examination for checking thinning conditions. It is well known that the flow-accelerated corrosion (FAC) was inhibited by traces of Cr in steel. Therefore, the chemical compositions of those steels have been measured. In addition, the micro structure and hardness of those steels have been investigated. And the relationship between those material variables and FAC rate was considered. As the results, (1) The Cr contents in those steels were below 0.1 wt% except one sample. Minute quantities of chromium increase the resistance against FAC. But the water velocity was thought to be the dominant factor rather than chemical composition in steel, at least such as below 0.1%Cr. (2) Hardness of all piping has been satisfied the specifications of each ...

Energy Technology Data Exchange (ETDEWEB)

Four commercial stainless steels (mat. Nos. 1.4539, 1.4586, 1.4571 and 1.4462) were tested in 96% and 90% sulfuric acid of 80/sup 0/C as to their corrosion fatigue strength by subjecting notched round bars to the rotary bending test. At the same time, the efficiency of anodic protection was examined. With all four steels, the alternating bending strength obtained in the air is essentially reduced. The semiaustenitic steel Nr. 1.4462 shows a lower corrosion fatigue strength than the three austenitic steels. Although making the corrosion fatigue strength of steels better calculable, anodic protection proves insufficient to completely prevent notched round bars from corrosion fatigue in concentrated sulfuric acid.

Wastenet

...3 MtC, with 78% of these emissions from integrated steel making (26.9 MtC) and the rest (22%)...6 MtC, with 71% of these emissions from integrated steel making (21.9 MtC) and the rest (29%)...1 million ton of carbon (MtC) in 1994 (3.9 MtC from integrated steel making, and 2.2 MtC from secondary ...7 MtC in 2002 (3.7 MtC from integrated steel making, and 2.0 MtC from secondary steel making), corresponding ...

International Nuclear Information System (INIS)

Superparamagnetic MFe23+O4 (M=Mn2+, Fe2+ and Co2+) inverse spinel ferrite (ISF) nanoparticles with narrow size distribution having average diameters of 6-8 nm were synthesized by a diol reduction of organic metals and the surface was modified to be hydrophilic by coating with succimer. Magnetic resonance imaging (MRI) contrast enhancement by dipolar coupling defined interactions between the synthesized ISFs and protons in the bulk water was investigated with initial susceptibility, magnetization and anisotropy of the succimer-coated ISFs. The relaxivity ratios, r2/r1, for MnFe2O4, Fe3O4 and CoFe2O4 were measured to be 12.2, 23.1 and 62.3, respectively, which demonstrate the potential usefulness of these magnetic nanoparticles as T2 contrast agents for MRI.

International Nuclear Information System (INIS)

Holmium doped barium based hexaferrites BaFe_1_2_-_2_xHo_2_xO_1_9 with (x = 0.0-1.0) were synthesized by solid state reaction method. Structural and magnetic characterization of these ferrites provide significant information about their reactive physical properties. X-ray analysis reveals that in all samples M-type structure exist with few secondary phases. Scanning electron microscope revealed the grain size of the specimen. The results show that grain size decreases with the substitution degree of Holmium. Thus rare earth element Holmium Ho"3"+ acts as a grain growth inhibitor. The magnetic hysteresis loops show the variation in the values of magnetic parameters like saturation magnetization (M_s), remanent magnetization (M_r) and coercivity (H_c) were observed by changing Ho"3"+ content in BaFe_1_2_-_2_xHo_2_xO_1_9 ferrites. Coercivity showed a maximum value of 2230 Oe for (x = 0.4) and then decreasing trend were observed in the values of ...

Wastenet

...page 50 results per page [1] 2 3 Products: 27 Page 1 of 3 Name List price Handbook of Structural Steel Connection Design and Details, 2nd Edition AU$186.36 ex-GST Terms ...

International Nuclear Information System (INIS)

May 2010 p. 81-84 Japan Ishizawa, Makoto JFE Steel Corporation, Tokyo

UK PubMed Central (United Kingdom)

Hundreds of thousands of people worldwide live or work in close proximity to steel mills. Integrated steel production generates chemical pollution containing compounds that can induce genetic damage...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

Energy Technology Data Exchange (ETDEWEB)

Steel is one of the most versatile materials known to mankind. It is used in a variety of applications. In many of these applications, it is exposed to the atmosphere, leading to rust formation, which weakens structures made using steel. Hence, protection is important. The popular methods to prevent corrosion are painting, galvanizing, electroplating etc. The widely used Chrome etching process is very effective in corrosion inhibition as well as in hardening the steel. But, Chromium and its compounds are highly placed among the toxic chemicals listed under pollution prevention initiatives of the EPA. Hence, it was decided to find alternatives to this process.

Energy Technology Data Exchange (ETDEWEB)

In recent years, the phase stability of austenitic stainless steels, and its effect on the mechanical properties of stainless steels, have been the subject of much interest. With the availability of new experimental techniques, new theoretical methods, and new computational procedures, significant advances have been made in understanding, and being able to predict, phase stability and mechanical properties of stainless steel welds. This paper reviews some of these developments, with an emphasis on recent work that has been done at Oak Ridge National Laboratory.

International Nuclear Information System (INIS)

A study is made into microhardness and structure of coatings on various system steels (37G2S, 25Kh5M, R6M5), obtained by ion nitriding in a low pressure (10"-"1 Pa) arc discharge plasma. A comparison of properties is accomplished for steels nitrided in an arc gas discharge and in a furnace. It is stated that ion-plasma nitriding in an arc gas plasma generator is an efficient method of alloy steels hardening which allows changing the structure and increasing the hardness of a surface layer up to rather great depth

International Nuclear Information System (INIS)

The influence of microalloying vanadium or titanium on improving the corrosion resistance of mild steel in saturated calcium hydroxide solution was investigated. Potential-time, potentiodynamic polarization, and impedance measurement techniques were employed. The corrosion products have been examined by infrared and X-ray diffraction analysis and by scanning electron microscopy. It has been shown that the grain refining, due to microalloying, plays an important role in enhancing the corrosion resistance of steel. Scales of calcite and iron oxides on top of a protective oxide are formed on the investigated steels.

Energy Technology Data Exchange (ETDEWEB)

This study does not recommend the use of a pressure vessel made of integral stainless steel, due to the failure mechanisms under stress corrosion assisted by chlorides or polythionic acid. Are presented case studies of literature and analysis of reports of proceedings of RLAM reactors, showing that the materials produced by bimetallic clad overlay or are more appropriate, in terms of integrity, for use in equipment that the internal environment requires austenitic stainless steel specification.

International Nuclear Information System (INIS)

Effect of scale on determination of 12Kh18N10T steel tendency to intergranular corrosion (IGC) by rapid electrochemical techniques in solution of 10 % H_2SO_4+0.0025 g/l KCNS was investigated. It is shown that scale presence of steel surface accelerates anode dissolving, activates grain boundaries. All this results to the effect of tendency to IGC in steels, not inclined to it. The scale is not completely removed from the surface, but remains partially along grain boundaries in result of successive pickling of scale and then a surface layer of metal. This also couses the effect of tendency to IGC.

International Nuclear Information System (INIS)

... Yoshiaki Toshiba Corp., Nuclear Power Division, Yokohama, Kanagawa (Japan)

Science.gov (United States)

No abstract available.

Energy Technology Data Exchange (ETDEWEB)

Stress-rupture strength tests were made of metal steam pipe (12Kh1MF steel) in various conditions, the original, after aging under laboratory conditions (580{degrees}C, 10,000 h), and after long service. It was shown that the more the steel is hardened by heat treatment or cold plastic working in the original condition, the less it hardens in creep. It was established that softening in creep of steel with a moderate yield strength is caused primarily by aging and with a high yield strength by pore formation.

Energy Technology Data Exchange (ETDEWEB)

High and ultra-high strength steels for pipelines are produced by properly handling the steel microstructure. The metallurgical principles involved in the microstructure control are presented, with emphasis on TMCP processing, that comprises conventional controlled rolling followed by accelerated cooling. (author)

International Nuclear Information System (INIS)

Azobenzene dyes are effective inhibitors for austenitic 304 L and 316 L stainless steel corrosion in high acidic medium up to 7N. A good efficiency is obtained from weight loss and electrochemical Rsub(p) measurements in hydrochloric acid, while no inhibition is observed in sulfuric solutions. Transformation from the primarily azobenzene to other compounds give rise to enhanced protection of steel samples, and probable structures of the inhibiting species are proposed in view of our results.

International Nuclear Information System (INIS)

The pitting corrosion resistance of three different types of stainless steel implanted with silicon is investigated using the potentiokinetic polarization technique. The specimens are tested in 3% NaCl and 0.1 N HCl solutions. Silicon ion implantation inhibits pitting corrosion of the steels in both aqueous media. The corrosion resistance depends on the silicon dose. Post implantation annealing only slightly alters the localized corrosion. (author).

Energy Technology Data Exchange (ETDEWEB)

The use of nickel alloys in Flue Gas Desulfurization (FGD) applications is described. Recently, nickel alloys 625 and C-276 have been clad to carbon steel plate. Production and properties of the clad plate are reviewed and a brief discussion is presented on production, fabrication and welding. Laboratory and field corrosion tests in SO/sub 2/ scrubber environments suggest that alloy 625 and C-276 clad steel plates are as corrosion resistant as the solid alloy plate.

Energy Technology Data Exchange (ETDEWEB)

A number of properties in steel components are detrimentally influenced when exposed to hydrogen environments. Under these conditions, atomic hydrogen is adsorbed on the steel surface, then absorbed and preferentially transported towards tri-dimensional stressed regions in the crystal lattice and into defects such as interfaces or dislocations. The hydrogen embrittlement susceptibility is strongly influenced by various microstructural parameters including the type of inclusions, steel composition and heat treating conditions. One of the alternatives employed in minimizing hydrogen embrittlement is the use of surface barriers for hydrogen permeation. In particular, the presence of surface nitride layers in steels can be considered as an effective barrier. Nitride steel surface layers can be produced by plasma nitriding with the concomitant benefits of improved surface hardness, as ...

Energy Technology Data Exchange (ETDEWEB)

Discussion is presented of world crude steel production, the Japanese steel industry and its expectations of the Canadian coal industry. It is concluded that the Canadian coal industry should pay attention to the trend in customer's requirements regarding coal quality, maintain price competitiveness in the international market place, and remain flexible with regard to the market trend.

International Nuclear Information System (INIS)

Effect of hydroxide nature, concentration and temperature on corrosion resistance of domestic steels and alloys to hot NaOH, KOH, LiOH solutions is considered. It is ascertained that by corrosion growth in relation to stainless steels and nickel alloys, the hydroxides are placed in the following sequence: LiOHsteel and nickel alloy tendency to cracking is manifested, are determined. 12 refs., 12 figs.

International Nuclear Information System (INIS)

Duplex stainless steels are widely used in severe corrosion environments because of their good corrosion performance. This paper deals with the influence of aging treatments on the intergranular corrosion (IGC) resistance of a commercial duplex stainless steel, SAF 2205. Duplex stainless steel was given aging treatments in the range 773-1173 K for time periods ranging from 6 min to 100 h. Optical microscopy and XRD was carried out on the aged stainless steels for the microstructural study. The aged samples were evaluated for the IGC susceptibility with the ASTM standard practices. Potentiodynamic cyclic polarization studies were also carried out to investigate the influence of aging treatments on the passivity breakdown. The results indicate that the sigma phase gets precipitated and is responsible for grain boundary attack. (author).

Energy Technology Data Exchange (ETDEWEB)

The goal of this project was to increase the high-temperature strength of the H-Series of cast austenitic stainless steels by 50% and the upper use temperature by 86 to 140 degrees fahrenheit (30 to 60 degrees celsius). Meeting this goal is expected to result in energy savings of 35 trillion Btu/year by 2020 and energy cost savings of approximately $230 million/year. The higher-strength H-Series cast stainless steels (HK and HP type) have applications for the production of ethylene in the chemical industry, for radiant burner tubes and transfer rolls for secondary processing of steel in the steel industry, and for many applications in the heat treating industry, including radiant burner tubes. The project was led by Duraloy Technologies, Inc., with research participation by Oak Ridge National Laboratory (ORNL) and industrial participation by a diverse group of companies.

Energy Technology Data Exchange (ETDEWEB)

In an effort to minimize the distortion of bearing steel rings during the production process, 100Cr6 steel billets are spray formed with a unique cooling control system to control the cooling and solidification behavior of the deposits. Effects of heating around the deposits, gas cooling at the substrate bottom and the gas flow over the deposits are investigated both by numerical simulation and experiment. Porosity profiles and microstructures of spray formed bearing steel are examined and evaluated. The investigation results show that the thermal boundary conditions of the deposits play important roles on the cooling and solidification behavior of the deposits, especially at the deposit periphery. Porosity in the 100Cr6 bearing steel deposit can be reduced significantly with the special cooling control system.

International Nuclear Information System (INIS)

Nitrogen has been added to stainless steels to improve mechanical strength and corrosion resistance. High nitrogen steel production is limited by high gas pressure requirements and low nitrogen solubility in the melt. One way to overcome this limitation is the addition of nitrogen in solid state because of its higher solubility in austenite. However, gas and salt bath nitriding have been done at temperatures around 550 C, where nitrogen solubility in the steel is still very low. High temperature nitriding has been, thus proposed to increase nitrogen contents in the steel but the presence of oxide layers on top of the steel is a barrier to nitrogen intake. In this paper a modified plasma nitriding process is proposed. The first step of this process is a hydrogen plasma sputtering for oxide removal, exposing active steel surface improving nitrogen pickup. This is ...

Science.gov (United States)

After each archwire was ligated into a bracket with a 0.010-in stainless steel wire, both stainless steel and beta-titanium archwires (0.017- x 0.025-in) were slid through commercially pure titanium brackets (0.018-in slot size) at 34 degrees C in both the dry and wet conditions. As controls, stainless steel archwire versus stainless steel bracket couples were used with comparable dimensions. The drawing forces were measured at 5 angulations (0 degrees, 3 degrees, 7 degrees, 9 degrees, and 11 degrees ) for 5 normal forces (nominally 0.2, 0.4, 0.6, 0.8, and 1.0 kg). Regression lines were determined for each frictional couple (P <.05). In the passive configuration, the kinetic frictional coefficients of control and test couples in the dry condition were comparable to previously reported values at 0.11 +/- 0.01 for stainless steel versus stainless steel, 0.12 ...

Energy Technology Data Exchange (ETDEWEB)

The stress corrosion cracking (SCC) susceptibility of 13% Cr martensitic (UNS S42000) and supermartensitic (UNS S41125) steels in sodium chloride solutions in the presence of thiosulphate was evaluated by slow strain rate tests (SSRT). The tests were performed in 5% sodium chloride solutions buffered at pH 2.7, 3.5, 4.5 and 6.0 in the absence and presence of thiosulphate in a concentration range between 10{sup -6} and 10{sup -3} M, at 25 {+-} 0.1 C. The electrochemical behaviour of the two steels in the different solutions was determined by recording the anodic and cathodic polarisation curves. 13% Cr martensitic steel showed SCC in 5% sodium chloride solutions with pH {<=} 4.5 in the presence of 3 x 10{sup -6} thiosulphate. Decreasing the chloride ion concentration from 50 to 10 g/l, the critical concentration of thiosulphate to provoke SCC susceptibility increased from 3 x 10{sup -6} to 1 x 10{sup -5} M. The ...

British Library Electronic Table of Contents (United Kingdom)

In this work, a new sol-gel auto-combustion method has been performed to synthesize single phase nickel ferrite nanocrystalline powders by using n-cetyltrimethylammonium bromide, as a cationic surfactant. The gels were prepared from ferric and nickel nitrates and citric acid. Ammonia was used as pH adjusting agent as well. The effects of the surfactant on the after combustion calcination process and the reduction of the resulting powder crystallite size which affects the magnetic properties of the material were investigated by XRD and DTA/TGA techniques. The results showed that the ignition of the gels in air have a self-propagating behavior. Addition of surfactant to the starting solution affected the crystallite size of the synthesized powders and their phase constitution. The crystallit...

Energy Technology Data Exchange (ETDEWEB)

There have been many stress measurements on welds by neutron diffraction over the past 20 years but there are still a number of serious experimental issues that are often not addressed. The primary fact is that the microstructure generally changes across the weld and accompanying this may be a change in the concentration of strengthening elements in solution. This will lead to a shift in lattice spacing which may be incorrectly interpreted as a strain. Secondly, a gradient of plastic deformation near the weld may be expected. Since plastic deformation by application of a stress always generates intergranular (type-2) strains this may lead to a range of intergranular effects superposed on the conventional weld-related strains. The effects are illustrated by neutron diffraction studies of Zr-4, ferritic and austenitic welds where chemistry, intergranular effects and crystallographic texture can all play a role.

British Library Electronic Table of Contents (United Kingdom)

A concentric reducer tube, which was a part of the top exit roughing hydraulic descaler in a hot strip mill failed prematurely under working pressure. A detailed metallurgical investigation comprising physical examination, optical microscopy, scanning electron microscopy, and electron probe microanalysis was carried out to find out the genesis of the failure. Physical examination revealed cracks located symmetrically around the circumference of the tube that ran along its full length, up to the weld beads at both ends. Optical microscopy of etched samples revealed a banded ferrite-pearlite structure and the existence of forging folds near the change-in-section(160? fillets). Cracks were found to initiate from these forging folds. No structural abnormalities were found in the weld beads and...

Science.gov (United States)

Sensitive and quick-response nonlinear inductance characteristics are found for high Tc superconducting (YBa/sub 2/Cu/sub 3/O/sub 7-chi/) disk cores at 77K in which soft magnetic BH hysteresis loops are observed. Various quick response magnetic devices such as modulators, amplifiers and sensors are built using these cores. The magnetizing frequency can be set to more than 20 MHz, which is difficult for conventional ferromagnetic bulk materials such as Permalloy amorphous alloys and ferrite. New quick-response fluxgate type magnetic-field sensors are made using ac and dc voltage sources. The former is used for second-harmonic type sensors, while the latter is for voltage-output multivibrator type sensors. Stable and quick-response sensor characteristics were obtained for two-core type multivibrators.

International Nuclear Information System (INIS)

Interest in making complex net-shape ceramic parts with good surface finishing and sharp tolerances without machining is a driving force for studying the injection molding technique. This method consists of softhening the ceramic material by means of adding some plastic and heating in order to inject the mixture under pressure into a relatively cold mold where solidification takes place. Essentially, it is the same process used in thermoplastic industry but, in the present case, the ceramic powder load ranges between 80 to 90 wt.%. This work shows results obtained from the fabrication of pieces of different ceramic materials (alumina, barium titanate ferrites, etc.) in a small scale, using equipments developed and constructed in the laboratory. (Author).

Energy Technology Data Exchange (ETDEWEB)

This paper describes an investigation of electrodeposited Zn-14% Ni and aluminium-based SermeTel 1140/962 coatings as possible replacements for cadmium. Slow strain rate tests were performed to measure the extent of direct hydrogen embrittlement of a high strength steel substrate as a result of the coating process and of hydrogen re-embrittlement caused by coating corrosion. The level of re-embrittlement was shown to depend on both the electrochemical potential of the coating and its barrier properties. Zn-14% Ni coatings caused the most re-embrittlement as they had the most active potential and contained through-thickness defects which left the steel exposed to hydrogen uptake. The microstructure of the high strength steel was also shown to be an important factor affecting the extent of embrittlement. AerMet 100 steel was more resistant than 300M steel and this was attributed to ...

Energy Technology Data Exchange (ETDEWEB)

In this paper, the state-of-the-art ultrasonic and magnetic measuring techniques developed at Kawasaki Steel and used in the production process of steel sheets are described. Representative examples shown here are as follows: (1) Magnetic flux leakage testing system for the detection of nonmetallic inclusions, (2) Nondestructive orientation measurement for secondary re-crystallized grains in grain-oriented electrical steel by ultrasonic interferometry, (3) Immersion testing method for the detection of nonmetallic inclusions, (4) Surface wave probe for the detection of surface flaws in rolls used in rolling mills. Developments of these techniques and their applications to actual steel sheets production processes have contributed to advance in technologies for quality assurance and control. With the help of these techniques, steel sheet products with advanced and uniform properties ...

International Nuclear Information System (INIS)

In the heat-affected zones (HAZ) of low alloy steels used for nuclear pressure vessel, microstructural changes, such as grain coarsening, carbide precipitation, and martensite formation, generally occur and cause a deterioration of toughness and an increase in sensitivity to brittle fracture. Metallographic analyses of low alloy steel welds reveal significantly different regions in HAZ microstructures. In 2-pass welds, there were seven characteristic regions in the HAZ determined by the peak temperature, to which the region was exposed during the weld thermal cycle: a coarse-grained region, a fine-grained region, an intercritical region, and subcritical region. The coarse-grained region can be categorized into four zones according to the reheating temperature as follows : an unaltered coarse-grained zone (UCGHAZ), a supercritically reheated coarse grained zone (SCRCGHAZ), an intercritically reheated coarse-grained zone (ICRCGHAZ), and an ...

International Nuclear Information System (INIS)

Previous corrosion studies identified the materials Hastelloy C4, Ti 99.8-Pd, and carbon steels as promising for the manufacture of long-lived high-level waste containers that could act as an engineered barrier in a rock-salt repository. Here, the efficiency of the corrosion-resistant concept using surface-welded Hastelloy C4 as corrosion protection of carbon steel containers is compared with the corrosion-allowance concept using unalloyed or low-alloyed steels. The materials are examined in three disposal relevant brines (two rich in MgCl_2, one rich in NaCl) at 150 C. The results indicate that welded Hastelloy C4 is highly resistant to corrosion in the NaCl-rich brine. In the presence of sulfides or MgCl_2-rich brines, however, severe pitting corrosion occurs. The three steels investigated are resistant to pitting corrosion in all brines, and their general corrosion rates imply corrosion allowances ...

Energy Technology Data Exchange (ETDEWEB)

Inhibition efficiency of some water-soluble hydrazones for C-steel corrosion in hydrochloric acid has been tested by weight loss, polarisation measurements and open circuit technique. The inhibition effect was attributed to the adsorption of the additives on the C-steel surface as supported by adsorption measurements at Pt electrode using cyclic voltammetry. Electrochemical measurements indicated that all the additives behave as cathodic-type inhibitors. The data obtained fit well to both the Temkin adsorption isotherm and the kinetic-thermodynamic model. The inhibition behaviour and its order were explained with the help of the proposed skeletal representation.

International Nuclear Information System (INIS)

The low alloy steels were nitrided in the plasma atmosphere generated by using hollow cathode discharge. For comparison, specimens of 40 Cr steel were in two different potential states. One kind is isolated from cathode and anode between them the discharge was created. The other kind is placed on the plate which is connected to the cathode. The nitriding was carried out at different temperatures. The surface morphology, phase of compound layers and microhardness profiles were analyzed. The optical microscopy observation and X-ray diffraction showed that the compound layers were formed in all experiments. The results of the nitriding treatment are weakly dependent on the potentials applied on the specimens.

Energy Technology Data Exchange (ETDEWEB)

Once again residual austenite as one component of the microstructure of steels is the basis for discussion among experts. Very often the phenomen of the stabilisation of residual austenite is the focus of interest. In this paper the influence of ageing on residual austenite transformations is discussed, with ageing taking place in a temperature range between ambient and M/sub s/-temperature after quenching from different austenitizing temperatures by means of subzero refrigeration. Results which are typical for 100Cr6 steel are presented and discussed.

International Nuclear Information System (INIS)

This paper deals with the pitting corrosion of evaporators in the liquid - radwaste system of nuclear power stations. Corrosion testrs were conducted by the anodic polalization of specimen in the chloride solution. (1) The initiation of the pitting in SUS 304, SUS 316 stainless steels was inhibited by addition of NaOH and H_3BO_3, however, these addition had no effect on the pitting propagation. (2) Inconel 625 had the resitivity against the pitting initiation superior to that of stainless steels, but this was not necessarily in the case of the pitting propagation. (3) It is noticed for pitting prevention that the environmental and material effect on the pitting initiation differed from that on the pitting propagation. (author).

Energy Technology Data Exchange (ETDEWEB)

The effect of aging on the microstructure and tensile properties of a type 316LN stainless steel/Alloy 800 joint, welded with 16-8-2 stainless steel consumable, has been studied to characterize and evaluate the joint for long-term elevated temperature service. The joint was subjected to accelerated againg heat treatments at 873 K up to 5000 h to simulate long-term service exposures. Analysis of the results from this investigation shows that this joint has adequate stability of microstructure and tensile properties even after prolonged exposure at elevated temperatures. (orig.)

Science.gov (United States)

Three bonding agents were evaluated to determine which were most effective in enhancing the bond of resin composite to stainless steel. A light-activated resin composite was bonded to a total of 60 stainless steel specimens using Panavia, Cover-Up, or Silicoating. Tensile bond strength measurements revealed that all three agents provide a satisfactory means of increasing adherence of the esthetic veneer without decreasing bonding through thermocycling of the specimens. Panavia and Cover-Up were significantly more effective than Silicoating and appear to be easier to use. PMID:8297460

Science.gov (United States)

The Asarco-Mission complex (image left) is an active producer of copper and molybdenum (important in making steel and other metal alloys), ...

International Nuclear Information System (INIS)

1974. 20 p. United States Anon. American Society of Mechanical

Energy Technology Data Exchange (ETDEWEB)

Carbon steel is frequently used to construct concentrated sulphuric acid storage tanks. This paper discussed the corrosion performance of carbon steel tanks and outlined the underlying mechanisms responsible for major corrosion modes. Analyses of hydrogen grooving and dilute acid corrosion failure mechanisms were presented. Recent corrosion-induced leak failures were also discussed. The use of anodic protection and organic coatings as a corrosion control measure was also evaluated. The results of laboratory studies that were conducted to understand corrosion-induced failures showed that carbon steel electrodes exhibited transpassive corrosion at relatively high anodic potentials, while stainless steel electrodes exhibited transpassive corrosion at anodic potentials less than 1 V. It was concluded that corrosion-induced leaks can be prevented by using anodic protection and baked phenolic coating ...

International Nuclear Information System (INIS)

... Fuel Limited, Reprocessing Business Division, Rokkasho, Aomori (Japan)

International Nuclear Information System (INIS)

Methods of automated control of 18-10-type steel inclination to IGC are developed and a corresponding automated testing complex (ATS) is created. 08Kh18N10T steel samples had two variants of thermal treatment: 1) 1200 deg (5 h), 600 deg (50 h); 2) 1200 deg (5 h). Methods of non-destructive automated control of 18-10-type steel inclination to IGC are developed on the basis of potentiodynamic reactivation (PR) principle. Automated testing complex is developed, which has undergone experimental running and demonstrated a high confidence of results, reliability and easy operation.

British Library Electronic Table of Contents (United Kingdom)

A mathematical model for heat transfer during solidification in continuous casting of automobile steel, was established on researching under the influence of the solidifying process of bloom quality of CCM in the EAF steelmaking shop, at Shijiazhuang Iron and Steel Co. Ltd. Several steel grades were chosen to research, such as, 40Cr and 42CrMo. According to the results of the high temperature mechanical property tests of blooms, the respective temperature curves for controlling the solidification of different steels were acquired, and a simulating software was developed. The model was verified using two methods, which were bloom pinshooting and surface strand temperature measuring experiments. The model provided references for research on the solidifying process and optimization of a secon...

International Nuclear Information System (INIS)

Russian (Mar 1977). USSR Makarov, VA Zarubin, PI Mironov, Yu.M.

Energy Technology Data Exchange (ETDEWEB)

This paper investigates steels 12Kh18N10T, 10Kh17N13M2T, 08Kh22N6T, and 08Kh21N6M2T. In corrosion of stainless steels in sulfuric acid solutions, dissolved sulfur dioxide acts as a cathodic depolarizer, capable of being reduced to elemental sulfur or forming sulfides with the metal. Depending on the conditions, this is associated with some increase in potential and greater or lesser increase in corrosion or facilitation of passivation of active steel. After passivation the influence of SO/sub 2/ is negligible. The results of this investigation were used as initial data for developing systems of anodic protection for shell-and-tube heat exchangers for sulfuric acid.

International Nuclear Information System (INIS)

... Energy Agency, Quantum Beam Science Directorate, Sayo, Hyogo (Japan)

Energy Technology Data Exchange (ETDEWEB)

First French manufacturer of steel boilers, Geminox proposes the THRi series, composed of condensation gas boilers whose four mural for the propane model. (O.M.)

Energy Technology Data Exchange (ETDEWEB)

This report summarizes some experiences gathered when using the semi-empirical temperature model that forms the heart of the steel casting advisory system `TUNDTEMP` in simulating the casting process. The model estimates the evolution of the liquid steel temperature in a tundish of a continuous casting machine through a temperature prediction at a couple of central time instants during the casting process. The results are compared with corresponding actual observations during the castings - measured steel temperatures and recorded casting difficulties and interruptions. Explanations for the possible discrepancies are suggested. Starting from a heuristically chosen set of model parameter values, some developing steps have been tested to reduce the simulation errors. The study concentrates mainly on temperature predictions for single heat castings. At the end of the report, some simulations of sequence castings are also ...

British Library Electronic Table of Contents (United Kingdom)

Flue gas desulfurization systems (FGDs) are operated in severely corrosive environments that cause sulfuric acid dew-point corrosion. The corrosion behavior of low-alloy steels was tested using electrochemical techniques (electrochemical impedance spectroscopy, potentiodynamic tests, potentiostatic tests), and the corrosion products were analyzed by scanning electron microscopy and X-ray photoelectron spectroscopy. The electrochemical results showed that alloying W with small amounts of Sb, Cu, and Co improves the corrosion resistance of steels. The results of surface analyses showed that the surface of the steels alloyed with W consisted of W oxides and higher amounts of Sb and Cu oxides. This suggests that the addition of W promotes the formation of a protective WO3 film, in addition to ...

International Nuclear Information System (INIS)

The effects of modification with Ti and Nb, heat treatment and solute segregation on void suppression in 316 stainless steel were studied using HVEM in the temperature range of 623-873 K after solution treatment at 1323-1473 K. Post-irradiation compositional analysis was performed by an energy dispersive X-ray analyzer. In Ti-modified stainless steel, void swelling peaks appeared at 723 K and 823 K. On the other hand, when the stainless steels modified by both Ti and Nb were irradiated, the void swelling was effectively suppressed, particularly the growth rate of a void was remarkedly retarded. This void suppression effect was easily recognized with increasing Nb concentration. Compositions such as Mo, Cr, Ti and Ni changed during irradiation and Ni, Si and Ti enriched around voids, whereas Cr and Mo depleted. (orig.).

International Nuclear Information System (INIS)

... Dozaki, Koji Takiguchi, Hideki Japan Atomic Power Company, Tokyo (Japan)

International Nuclear Information System (INIS)

The rate of corrosion of alloyed steels in solutions of orthophosphoric acid at the temperatures from 100 to 200 deg C has been ascertained by gravimetric method. It is shown that the 06Kh23N28MDT steel features the highest corrosion resistance, the second in terms of the characteristic mentioned is 08Kh22N6T, then - 10Kh17N13M2T, 08Kh21N6M2T, 12Kh18N9T. Corrosion rate of the steels studied intensifies at the acid concentrations exceeding 10% and increases essentially with the temperature increase. 6 ref., 2 tabs.

International Nuclear Information System (INIS)

Feb 2006 p. 80-84 Japan Mizuno, R. Matsuda, F. Japan Power Engineering

International Nuclear Information System (INIS)

Russian (Dec 1973). USSR Chmovzh, VE Lipshtejn, RA Zalkind, I.Ya. Dik,

Energy Technology Data Exchange (ETDEWEB)

Holmium doped barium based hexaferrites BaFe{sub 12-2x}Ho{sub 2x}O{sub 19} with (x = 0.0-1.0) were synthesized by solid state reaction method. Structural and magnetic characterization of these ferrites provide significant information about their reactive physical properties. X-ray analysis reveals that in all samples M-type structure exist with few secondary phases. Scanning electron microscope revealed the grain size of the specimen. The results show that grain size decreases with the substitution degree of Holmium. Thus rare earth element Holmium Ho{sup 3+} acts as a grain growth inhibitor. The magnetic hysteresis loops show the variation in the values of magnetic parameters like saturation magnetization (M{sub s}), remanent magnetization (M{sub r}) and coercivity (H{sub c}) were observed by changing Ho{sup 3+} content in BaFe{sub 12-2x}Ho{sub 2x}O{sub 19} ferrites. Coercivity showed a maximum value of 2230 Oe for (x = 0.4) and then ...

Energy Technology Data Exchange (ETDEWEB)

The structure and composition of the passive films formed on 304 stainless steel in deaerated IN H{sub 2}SO{sub 4} were studied by RHEED, XPS and AES. The stability of the passive films as a function of passivation potential and passivation time were investigated. The role of bound water in affecting the stability of the passive films is discussed. 7 refs., 3 figs.

Energy Technology Data Exchange (ETDEWEB)

Supplemental fuels are injected at the tuyere level of blast furnaces to reduce coke consumption and increase productivity. Natural gas use in blast furnace injection has increased substantially in recent years as operators became aware of its operating and economic benefits. One of the major conclusions found in the GRI-sponsored tests at A-K Steel was that the prevailing concept of maintaining a high raceway adiabatic flame temperature (RAFT) for high rates of natural gas injection practice was shown to be in error--during tests, RAFT was lowered by about 700 F with no adverse effect on the blast furnace. Subsequent to the field trials, A-K Steel has reported very high productivity on its No. 3 Middletown furnace by injecting over 180 lb/THM of natural gas and by charging over 250 lb/THM of metallic iron as hot briquetted iron. The objectives of these two series of tests on two commercial blast furnaces were to investigate the increase in ...

Energy Technology Data Exchange (ETDEWEB)

The reconstruction of steel lining of the FFTF reactor building is described. The cold part of the lining has a simple structure and represents a steel sheet of 6.35 mm thickness welded to I-shaped imbedded in concrete, the hot part is meant for resisting the hot sodium contacting with it. The reconstruction has been reduced to the substitution of usual lining, the sheets of which are fixed in such a way that dangerous strains in metal arising at evaporation are excluded by the new structure admitting sheet deformation.

International Nuclear Information System (INIS)

The study by impedance and photoelectrochemical measurements of passive films formed on an AISI 304 type stainless steel shows that important parameters of the electronic structure of these films are modified under #alpha# irradiation, namely: width of the space charge region, donors concentration and diffusion length for minority carriers. The consequences of #alpha# irradiation on localized corrosion processes are discussed.

Energy Technology Data Exchange (ETDEWEB)

A growth model of pitting corrosion of carbon steel in cooling water systems was developed on microscopic observations of pits and electrochemical studies. Results of pitting corrosion measurements in laboratory and field conditions with the model, using a newly developed electrochemical device, are discussed. For an actual heat exchanger up to a year operation, the values of pitting depth estimated were in good agreement with the measured values.

International Nuclear Information System (INIS)

Full text of publication follows: Fission neutron irradiation to steels doped with isotope boron-10 is frequently conducted to study effects of the helium production on mechanical properties. The intrinsic mechanical properties of F82H steels could have been changed due to the boron doping. Recently, we reported that co-doping with boron and nitrogen to F82H (F82H+B+N) improved the mechanical properties of F82H doped only with boron. The mechanical properties of F82H+B+N are successfully comparable with the non-doped F82H before irradiation. In order to evaluate the effects of initial microstructure and helium production on radiation hardening, F82H and F82H+B+N were irradiate d Specimens used in this study were standard F82H martensitic steels, F82H steels doped with 60 mass ppm 10B and 200 ppm N (F82H+10B+N) and F82H steels doped with 60 mass ppm 11B and 200 ppm N (F82H+11B+N). ...

Energy Technology Data Exchange (ETDEWEB)

Past and current development of coal utilization technology in the Japanese steel industry is reviewed and some projects currently under research and development briefly described. These include DIOS, an iron making process which directly utilizes both iron ore and coal without a sintering plant or a coke oven; and the development of a new generation coke oven. 15 figs.

British Library Electronic Table of Contents (United Kingdom)

An eddy current probe of the level of molten metal is considered for a sectional machine of continuous casting of steel. The advantages of electromagnetic probes of the level over radiometric ones lie in their insensitivity to the layer of dross and high speed. The results and directions of further studies are given.

Energy Technology Data Exchange (ETDEWEB)

Two austenitic steels, 316 Stainless Steel and Alloy 800, have been examined under conditions of both isothermal low cycle fatigue (LCF) and thermomechanical fatigue (TMF). The TMF tests were conducted between 649 and 360/sup 0/C with a carefully controlled triangular waveform. The LCF tests were performed at 649/sup 0/C and both kinds of tests were subjected to a strain range of 0.5%. TMF shortened life to 40% for 316 Stainless Steel and to 5% for Alloy 800. The microstructural evolution occurring in both alloys has been examined and we conclude these do not play a role in the life shortening caused by TMF. The TMF does produce asymmetric hysteresis loops with large tensile peak stresses in tests where the maximum temperature corresponded with the peak compressive stress. The influence of TMF on fatigue crack growth rates has been measured and it was found that TMF accelerated crack growth in Alloy 800 and slowed it down ...

International Nuclear Information System (INIS)

By using a plasma nitriding procedure at the PUPR Mirror Cusp Plasma machine, surface hardness is increased in 302/304-type stainless steel samples by exposing them to high-ion-density plasma at high vacuum. This method successfully dopes the surface of the material with strengthening nitrogen ions, without the use of chemical procedures that sacrifice the resistance to corrosion of the given material. A 500 V negative bias is placed on the sample exposed to the nitrogen plasma, where high-energy ions are therefore attracted and immersed into the metallic matrix microns into the surface of the stainless steel. This potential maintains a constant surface temperature at approximately 800 deg. C. The plasma parameters including ion density and plasma temperature were diagnosed using single Langmuir probes. The stainless steel samples were then tested using scanning electron microscopy (SEM), and Vickers micro-hardness testing ...

Energy Technology Data Exchange (ETDEWEB)

The aim of this work is to describe the processes during plasma nitriding of Nb-containing, powder metallurgy prepared (PM) tool steel. PM steel was studied containing 2.5% C, 3.3% Si, 6.2% Cr, 2.2% Mo, 2.6% V, 2.6% Nb and 1.0% W, produced by melt atomization and hot isostatic pressing. The hardened and tempered steel was plasma nitrided at temperatures ranging from 470 to 530 deg. C. The nitriding time was 30-180 min. Optical microscopy, electron microscopy, XRD, EDS, WDS and hardness measurements were used to study the steel's properties, microstructure, phases and chemical composition. The nitriding temperature of 470 deg. C was found to be unsuitable for practical use because the layers prepared at this temperature were non-uniform. The compound layer formed by M{sub 2,3}(C,N) and M{sub 4}N was found after nitriding at temperatures of 500 and 530 deg. C for at least 60 min. The effect of ...

Energy Technology Data Exchange (ETDEWEB)

Sandia National Laboratories is currently involved in the optimization of a Plane Shock Generator Explosive Lens (PSGEL). The PSGEL component consists of a detonator, explosive, brass cone and tamper housing. The purpose of the PSGEL component is to transmit a plane shock wave through the 4340 steel bulkhead (wave separator) which has a ferro-electric (PZT)ceramic disk attached to the opposite surface of the steel bulkhead. The planar shock wave depolarizes the PZT 65/35 ferro-electric ceramic to produce an electrical output. One aspect of the optimization program involves the possible replacement of 4340 steel with PH13-8Mo steel for the bulkhead. These materials, as well as the PZT 65/35 ferro-electric ceramic and the brass for the cone, required the stock characterization with respect to Hugoniot parameters. The work presented here gives the shock Hugoniot values for these four materials and ...

Energy Technology Data Exchange (ETDEWEB)

Fe-Ni-Mn martensitic steels are one of the major groups of ultra-high strength steels that have good mechanical properties and ductility in as annealed condition but they suffer from severe inter-granular embitterment after aging. In this paper, the effect of heavy shaped cold rolling and wire drawing on the mechanical properties of Fe-Ni-Mn steel was investigated. This process could provide a large strain deformation in this alloy. The total strain was {epsilon} {approx}7. Aging behavior and tensile properties of Fe-10Ni-7Mn were studied after aging at 753 K. The results showed that the ultimate tensile strength and ductility after cold rolling, wire drawing and aging increased up to 2540 MPa and 7.1 %, respectively, while the conventional steels show a premature fracture stress of 830 MPa with about zero ductility after aging.

Energy Technology Data Exchange (ETDEWEB)

The volume diffusion of Mo in austenitic CrNiMo(N)-steels was studied using the sandwich method. Accordingly the interdiffusion coefficients of Mo were found to be independent of its concentration for the given steel composition with 12 to 19 wt.% Cr, 12 to 16 wt.% Ni, 0 to 2 wt.% Mo and 0 to 0.27 wt.% N and within the temperature range from 1283 to 1523 K. The diffusivity of Mo is greater than that of Cr, Ni and Fe in such steels. The diffusion parameters of Mo are decreased by alloying addition of nearly 0.25 wt.% N in steel; possibly as a result of lattice expansion or increasing vacancy concentration caused by N. Small variations in Cr and Ni initial contents of examined specimens showed negligible effect on the absolut values of interdiffusion coefficients of Mo. (orig.).

Energy Technology Data Exchange (ETDEWEB)

In this work, a new class of thiadiazole derivatives, namely 3,5-bis(2-thienyl)-1,3,4-thiadiazole (2-TTH) and 3,5-bis(3-thienyl)-1,3,4-thiadiazole (3-TTH), have been studied as possible corrosion inhibitors for mild steel in molar hydrochloric acid (1M HCl). Polarisation curves and AC impedance methods have been used. These studies have shown that the thiadiazole derivatives were very good inhibitors for mild steel in 1M HCl. Comparison of results showed that 3-TTH was the best inhibitor. The potential of zero charge (PZC) of mild steel was studied by ac impedance method, and the mechanism of adsorption has been predicted. X-ray photoelectron spectroscopy surface analysis with thiadiazole derivatives shows that it chemisorbed at the mild steel/HCl interface. The adsorption of these inhibitors followed Langmuir's adsorption isotherm. The electronic properties of 2-TTH and 3-TTH, obtained using ...

International Nuclear Information System (INIS)

An ampoule corrosion tests technique is presented for making a comparative corrosion-proof estimation of austenitic steels and alloys which are candidate materials for the ITER first wall and shield blanket. Influence of Cl"- on the rate and character of corrosion cracking has been determined. The dependence of time before destruction on Cl"- contents was obtained by experiments in twice-distilled water at a Cl"- content value of less than 0.05 mg/l. Kinetics of a corrosion crack growth has been determined by way of acoustic emission and measurement of electrical resistance. It has been revealed, that corrosion cracking of 316L and 316Ti steels in water with 100 mg/l of Cl"- takes place at temperatures over 50 C. For 316L (Russian analogue), 316Ti, 08Cr18Ni10Ti (type 304), 00Cr16Ni15Mo3Nb (type 316) steels and CrNiMo-1 (42-47%Cr, 1%Mo, Ni-base) alloy corrosion long-term strength and crack-resistance characteristics were ...

International Nuclear Information System (INIS)

Plasma nitriding is a powerful technique for modifying the phase-structure of the material surface layers, which affect the mechanical, physical and chemical properties of material. The effect of plasma nitriding on the surface properties of three types of steel (low carbon, AISI-304 and H13 (hardened)) has been investigated. The steel samples were plasma nitrided in vacuum of 10"-"1Pa with gas mixture of (N_2, H_2) at 530 Centigrade degree for a duration of 14 hours. Vickers microhardness measurements and XRD phase analysis of the treated and untreated samples were carried out. The diffraction patterns of treated steels revealed that new phases of #gamma#-Fe_4N, #epsilon#-Fe_3N and (Fe,Cr)_2N were formed. The maximum treated depths were about 5, 6 and 45 #mu#m for low carbon, AISI-304 and H13 (hardened) nitrided steel respectively. The microhardness was increased by about 150%, 200% and 140% for low ...

Energy Technology Data Exchange (ETDEWEB)

The effect of partial and total replacement of tungsten by molybdenum on the mechanical technical properties were investigated with the cold work steel 60 WCrV 7 (DIN 1.2550). While maintaining the total quantity of tungsten atoms and/or molybdenum atoms in the steel, no differences occur in the type of the separated carbides. After annealing in the range of the pearlite stage with annealing times of up to 150 h, the carbide phases M/sub 23/C/sub 6/ and MC are, besides alpha iron, also present. In short-time annealed states also M/sub 6/C carbides occur. These are formed during austeniting and remain in the steel as residual carbides in austeniting treatment carried out under normal conditions. Compared with tungsten alloyed steel, there is an increased formation of M/sub 6/C carbides in molybdenum alloyed steels during austeniting. By a long-time annealing treatment in the range of ...

Energy Technology Data Exchange (ETDEWEB)

Time-temperature-precipitation diagrams have been established for two steels with 6% Mo, 21% Cr, 25% Ni, 0.14 and 0.19% N (Cronifer 1925 h Mo = 1.4529, UNS N 08925) and for one steel with 6% Mo, 20% Cr, 18% Ni and 0.21% N (UNS S 31 254). The corresponding time-temperature-sensitization diagrams (in accordance to SEP 1877/II) and time-temperature-pitting diagrams (testing in 6% FeCl{sub 3} solution) have been evaluated as well. Precipitation of intermetallics occurs rapidly especially in the range between 700 and 1000{sup 0}C. In case of the 18% Ni steel and the 25% Ni/0.14% N steel grain boundaries are covered to a large extent with precipitates after only 15 min at 850 or 950{sup 0}C. In case of the 25% Ni/0.19% N steel precipitation is considerably slower. Therefore, when welding according to established rules and recommendations, no deterioration of the corrosion resistance in ...

Energy Technology Data Exchange (ETDEWEB)

The pitting corrosion properties have been investigated in welded and unwelded condition by polarization tests in sodium chloride solutions. The two steels were TIG welded without adding welding material and as shielding on the bottom side argon gas containing 2, 26 or 99 ppm oxygen was used. In some tests low breakthrough potentials were received, without discovering any pitting corrosion in the specimen surfaces. The unwelded SS 2352 steel had a critical (lowest) pitting temperature (CPT) of 5 degrees C in the more concentrated solution. For the same steel with weld pitting corrosion was obtained at 5 degrees C, which was the lowest temperature for the tests. Thus the CPT value was lower than 5 degrees C, but by looking at the pitting corrosion potentials the following conclusion could be drawn: Welding with higher oxygen content in the shielding gas implied lower pitting corrosion resistance. For the SS 2353 ...

International Nuclear Information System (INIS)

The thermo-chemical treatments of steels with plasma is normally carried out in low-pressure ionized gaseous atmospheres. Among the treatments used most often are: nitruration, carburization and boronized. A plasma can also generate at atmospheric pressure. One way to produce it is with an electrochemical cell that works at a relatively high inter-electrode voltage and under conditions of heavy gas generation. This type of plasma is known as electrolytic plasma. This work studies the feasibility of using electrolytic plasma for the surface processing of steels. Two processes were selected: boronized and nitruration., for the hardening of two types of steel: one with low carbon (1020) and one with low alloy (4140). In the case of the nitruration, the 1020 steel was first aluminized. The electrolytes were aqueous solutions of borax for the boronizing and urea for the nitruration. The electrolytic plasmas ...

Energy Technology Data Exchange (ETDEWEB)

This report summarizes the major features of the advisory tool `TUNDTEMP`, developed to act as a decision support in the continuous steel casting process. `TUNDTEMP` provides a means to predict abnormal phenomena of temperature origin in the casting that may be difficult to foresee in practical situations. The heart of the system is a semi-empirical calculation model that yields an estimate of the evolution of the tundish temperature of the liquid steel on the basis of a few important casting factors. The user interface of the system is to a large extent based on the visual presentation of the simulated results. The system also contains an optional rule based mechanism that provides assistance in the result interpretation and, if wished, linguistically formulates action recommendations. A separate program has been built for the tuning of the calculation model and for maintenance of the system. At the end of the report, the different tuning ...

International Nuclear Information System (INIS)

In this paper, the influence of plasma nitriding at temperature 720 deg. C for 20 h on the surface microstructure and interface microstructure of electroplated chromium coating was investigated. In these conditions, interdiffusion, mixing and reaction phenomena of elements originating from the substrate and coating material are more likely to occur, thus increasing the bonding strength between the coating and carbon steel substrate. The change of the structures from the substrate side to the coating surface, and the effect of the substrate steel on the interface structure were studied by cross-sectional transmission electron microscope observation (XTEM). The nitride layer formed on the surface was analyzed by X-ray diffraction method (XRD). After treatment at above conditions a 6-7 #mu#m thick nitride compound layer was formed in surface region and the same thick carbide compound layer was also formed in the interface region between ...

British Library Electronic Table of Contents (United Kingdom)

Tailor die quenching in the hot stamping of quenchable steel sheets was developed to produce ultra-high strength steel formed parts having strength distribution. Local portions of the heated sheet were quenched by holding grooved tools at the bottom dead centre during the stamping. Non-contact portions were generated in the sheet by grooving the tools, and thus the strength in the contact portions is high owing to the quenching and that in the non-contact portions is low owing to the lack of the quenching. Hat-shaped products having a tensile strength of approximately 1.5GPa only at four corners were formed.

British Library Electronic Table of Contents (United Kingdom)

Plastic injection molds are an important economic sector due to the increasing use of injection molded plastic components. The selection of mold steel material, its processing conditions, and the way it is machined and hardened all have an impact on how it performs during use across its lifecycle for injection molding. For this study, injection molding conditions seen during high volume manufacturing were used to induce wear that would be typical during processing. A 50wt.% glass fiber reinforced Polybutylene Terephthalate (PBT) was used for the research. After 3000 injection operations, surface damage was found only on the steel used for the stationary half of the mold cavity and the corresponding surface of the molded parts. In contrast, the moving half showed no surface damage or increa...

Energy Technology Data Exchange (ETDEWEB)

The effect of sodium gluconate anion (SG) on the corrosion and scale inhibition of ordinary steel in simulated cooling water has been studied using weight loss, polarisation curves, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM) techniques. SG was studied in concentration from 10{sup -4} M to 10{sup -1} M. Results obtained reveal that SG perform excellently as corrosion and scaling inhibitor for ordinary steel in simulated cooling water. An increase of SG concentration leads to the increase of the corrosion potential towards the positive direction. The inhibition efficiency was a low temperature dependence. The inhibitor mechanism was treated as an adsorption process according to Langmuir adsorption isotherm. The SEM/EDAX data show that was a corrosion and scale inhibitor.

British Library Electronic Table of Contents (United Kingdom)

Nowadays, different research teams are engaged on experimental and theoretical studies having as main aim the evaluation of seismic performance of sheathed cold-formed steel frame structures. Although a relatively large number of experimental and theoretical studies are available, the development of useful tools for the seismic design should be improved. As an attempt to overcome this lack, this paper aims to present a structural design procedure that allows, through the definition of three design nomographs, the screw spacing and all the shear walls components to be obtained on the basis of linear dynamic or nonlinear static seismic analysis. In addition, a procedure for the prediction of the whole pushover response curve of sheathed cold-formed steel shear walls, which can be advantageou...

International Nuclear Information System (INIS)

A comprehensive assessment on the eligibility of reduced activation (RA) steels as structural chamber material in Inertial Fusion Energy thick-liquid concepts is performed. As far as alloying elements, it is shown that the activation of tungsten is a question to discuss. Regarding impurity elements, it is analyzed if they could question the possibility of obtaining real RA steels for shallow land burial (SLB). The effect of the thickness of the liquid wall on the SLB response of alloying and impurity elements is computed. It seems that a reasonable liquid thickness of about 80 cm is allowable to obtain SLB acceptability of real RA steels. And above all, we have estimated the impact of cross section uncertainties when addressing the former questions, and we identify those to be improved. The necessary improvement of some tungsten and niobium cross sections is justified. (authors)

British Library Electronic Table of Contents (United Kingdom)

A protective film has been developed on the surface of carbon steel in low chloride aqueous environment using a synergistic mixture of an environmentally friendly phosphonic acid, N,N-bis(phosphonomethyl) glycine (BPMG), and zinc ions. Impedance studies of the metal/solution interface indicated that the surface film is highly protective against the corrosion of carbon steel in the chosen environment. Potentiodynamic polarization studies showed that the inhibitor is a mixed inhibitor. X-ray photoelectron spectroscopic analysis (XPS) of the film showed the presence of the elements iron, phosphorus, nitrogen, oxygen, carbon, and zinc. Deconvolution spectra of these elements in the surface film showed the presence of oxides/hydroxides of iron(III), Zn(OH)2, and [Zn(II)-BPMG] complex. This infe...

International Nuclear Information System (INIS)

P-implantation (10"1"7 ions cm"-"2, 40 KeV) into 304 stainless steel (ss) has been carried out, and an amorphous surface alloy was formed. Polarization studies in deaerated 1N H_2SO_4+ 2% NaCl showed that P-implantation improved both the general and localized corrosion resistance of 304 ss. A comparative study has been carried out between the implanted and unimplanted steel to determine what influence P-implantation has upon the properties of the passive film formed 1N H_2SO_4. The influence of Cl ions on pre-formed passive films was also studied. RHEED, XPS and AES were used to evaluate the nature of the passive films formed in these studies.