International Nuclear Information System (INIS)

A new eddy current array probe has been implemented as a straightforward and promising technique for detection of outer diameter (OD) surface-breaking cracks on the extrados of feeder bends. The design is based on previous work performed at AECL, which had demonstrated that eddy current probes with laterally displaced transmit-receive coils can overcome some of the limitations of inspecting ferritic steel components for surface-breaking cracks. The Feeder Integrity Joint Program-CANDU Owners Group Inc. (FIJP-COG) Non-Destructive Evaluation (NDE) Team members commissioned AECL to work in collaboration with the probe manufacturer ZETEC, to develop a field usable eddy current array probe. The objective was to acquire a technique with the following capabilities: fast scanning non-contact inspection technique for surface breaking discontinuities; full inspection of the bend extrados OD surface in a single scan; ability to ...

Energy Technology Data Exchange (ETDEWEB)

We present the synthesis, magnetic and UV spectrometry of NiZn-ferrite nanofiber. The single phase of spinel ferrite was obtained at 600 {sup o}C. The NiZn-ferrite fibers fabricated by an electrospinning process were formed as a polygonal grain growth with firing temperature in fiber matrix. It appeared that the saturation magnetization (M{sub S}) of NiZn-ferrite nanofiber was dependent on Ni/Zn molar ratio which is similar to that of the inverse spinel ferrites. The NiZn-ferrite fibers showed good DNA adsorption efficiency that can be modified and utilized for DNA separation with magnetic nanofiber as a novel material in clinical applications.

International Nuclear Information System (INIS)

Structure of ferrite in drawn pearlitic steel containing 0.9 mass% C was investigated with X-ray diffraction technique using synchrotron radiation. In the detailed analysis of diffraction peaks of ferrite during the drawing process, it was experimentally revealed that the transformation of ferrite from bcc to bct due to the supersaturation of carbon in ferrite of heavily drawn pearlitic steel.

Science.gov (United States)

... Title : THE INFLUENCE OF GRAIN BOUNDARY CARBIDE DENSITY ON THE BRITTLE FRACTURE OF FERRITE PEARLITE STEELS. ...

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

Nanodimensional powders of cubic copper ferrite are synthesized by two-steps procedure of co-precipitation of copper and iron hydroxide carbonates, followed by mechanochemical treatment. X-ray powder diffraction, Moessbauer spectroscopy and temperature-programmed reduction are used for the characterization of the obtained materials. Their catalytic behavior is tested in methanol decomposition to hydrogen and CO and total oxidation of toluene. Formation of nanosized ferrite material is registered even after one hour of milling time. It is established that the prolonging of treatment procedure decreases the dispersion of the obtained product with the appearance of Fe2O3. It is demonstrated that the catalytic behavior of the samples depends not only on their initial phase composition, but on the concomitant ferrite phase transformations by the influence of the reaction medium. -- Graphical abstract: It is demonstrated that the ...

Science.gov (United States)

An American Society of Mechanical Engineers task group on stainless steel weld materials was organized to determine the need for ferrite measurements of production welds required by the US Nuclear Regulatory Commission Regulatory Guide 1.31 (Rev. 1). The task group studied paired ferrite measurements (i.e., calculated and measured ferrite numbers (FNs) for the material qualifications versus measured ferrite numbers for corresponding production welds (PWs)). Our purpose was to compare delta-ferrite content as measured in the filler metal weld qualification pad with that in the resultant PW. Welds made predominantly by three common processes (submerged arc, shielded metal arc, and gas tungsten arc) were included in the study. Weld metals investigated included types 308, 308L, 316, and 316L stainless steel. An initial evaluation of the paired ferrite measurements ...

Science.gov (United States)

pedel supl3od" surfcoe. U => ut::_oer (torso segment or shoulder. 13oint),. L => lower. (legs]. m-I. => mediolatercl a_is re. Doo_,. s-i => ...

Science.gov (United States)

... Accession Number : ADD323869. Title : EFFECTS OF SHIELDING ON PROPERTIES OF EDDY CURRENT PROBES WITH FERRITE CUP CORES. ...

Energy Technology Data Exchange (ETDEWEB)

Mixed microstructures have been studied in low- carbon microalloyed steels suitable for automotive applications, after continuous cooling from the hot-rolled condition. Microstructural features such as polygonal ferrite, bainitic and acicular ferrite and microphase constituent are identified using transmission electron microscopy. The influence of these mixed structures on the tensile strength, impact toughness and fracture behaviour is examined. It is found that improvements in impact toughness as compared with microalloyed medium- carbon ferrite/pearlite steels can be achieved from these predominantly acicular structures developed by controlling alloy composition and continuous cooling of these lower carbon steels. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Production costs for commercial-sized Populus plantations were developed from a series of research programs sponsored by the US Department of Energy's Short Rotation Woody Crops Program. Populus hybrid planted on good quality agricultural sites at a density of 2100 cuttings ha{sup {minus}1} was projected to yield an average of 16 Mg (OD) ha{sup {minus}1}yr{sup {minus}1}. Discounted cash flow analysis of multiple rotations showed pre-harvest production costs of $17 (US) Mg{sup {minus}1}(OD). 19 refs., 1 fig., 3 tabs.

British Library Electronic Table of Contents (United Kingdom)

This paper presents results from a research case study that examined the distribution of travel time of origin-destination (OD) pairs on a transportation network under incident conditions. Using a transportation simulation dynamic traffic assignment (DTA) model, incident on a transportation network is executed under normal conditions, incident conditions without traveler information availability, and incident conditions assuming that users had perfect knowledge of the incident conditions and could select paths to avoid the incident location. The results suggest that incidents have a different impact on different OD pairs. The results confirm that an effective traveler information system has the potential to ease the impacts of incident conditions network wide. Yet it is also important to n...

Energy Technology Data Exchange (ETDEWEB)

Four low activation alloy classes, two austenitic and two ferritic, have been incorporated into the MOTA-1B experiment in the FFTF reactor to provide an early assessment of the suitability of such alloys for reactor service.

International Nuclear Information System (INIS)

The Environmental Management System (EMS) is an instrument to manage the interaction between the organization and the environment. The scope od EMS is to reduce the environmental impact and to achieve improvements in overall performances. In particular, the focus point of EMS implementation is the method for identifying and assessing significant environmental aspects. This paper presents a review of methods and techniques existing in this area, and the definition of the state of the art. The results of the literature, regulation and case studies reviews have shown that rigorous, repeatable and transparent methodologies do not exist.

Energy Technology Data Exchange (ETDEWEB)

Fractal dimensions of three different samples of lanthanum ferrite were computed using single adsorption method. The fractal Dubinin-Radushkevitch isotherm was used to fit directly the experimental nitrogen adsorption data. Avnir-Jaroniec method for fractal dimension determination was also used. Low and intermediate fractal dimensions were obtained according to BET specific surface areas.

Science.gov (United States)

"Precision manufacture of ceramic parts with CNC machining capability for aerospace, lasers, semiconductors and other industries. Materials include alumina, zirconia, glass, ferrites, silicon carbide, silicon nitride, sapphire, cordierite, mullite and others. A.C.T. has seen the number of applications and demand for high-realiability ceramics (aluminum oxide, zirconia, glass, ferrites, silicon carbide, silicon nitride, sapphire, cordierite, mullite, etc...) increase continually within the aerospace, computer and the industrial markets."

International Nuclear Information System (INIS)

Early failure of an induction-hardening carbon steel pipe, which was used to transport tailing slurry, was caused by pitting corrosion. The microstructure on the internal pipe surface layer was found being a mixture of martensite, pearlite and ferrite. In this work, the pitting corrosion behavior of each constitute in the microstructure of steel is investigated with electrochemical noise analyses; the electronic properties of passive films were studied with Mott-Schottky relationship. It is found that the passive films formed on the materials under investigation are highly disordered n-type semiconductors. The high-to-low pitting susceptibility is ferrite > martensite > pearlite. The pitting resistance is related to the semiconductive nature of the passive film formed on each constitute. The pitting susceptibility increases with the donor concentration in the passive films. (author)

British Library Electronic Table of Contents (United Kingdom)

Fatigue crack growth tests of three ferrite-pearlite steels with different size and spacing of pearlite particles, which were uniformly distributed in the ferrite matrix, were carried out to investigate the effect of microstructure on fatigue crack growth behavior in the Paris regime. The fatigue crack growth rates for the three materials did not coincide with each other, even when the crack growth curves were arranged by the effective stress intensity factor range. From in situ observations, crack tip stress shielding phenomena, such as interlocking and branching, were found on the crack wake, which enhanced fatigue crack growth resistance. A small size and spacing of pearlite particle seemed to induce small but frequent crack deflections, which resulted in crack closure phenomena. On the...

Energy Technology Data Exchange (ETDEWEB)

In this paper, we investigated the effect of alcohol solvents (ethanol, n-propanol, and n-butanol) and isomeric alcohol solvents (iso-propanol, iso--butanol, and tert-butanol). In addition, we observed the effect of the mixed alcohol solvents on the particle formation as using a mixture od ethanol and butanol at a ratio od 30/70, 50/50 and 70/30 vol %, respectively. In case of ethanol solvent, particle size of silica showed the smallest and the narrowest size distribution among the various solvent. On the contrary, for the n-butanol solvent, largest broad distribution of particle size was observed. For the synthesis of particles having better spherical morphology and less agglomeration, alcohol solvent having no branches was considered appropriate. When mixed alcohol solvents were used, large silica particles with narrow size distribution were obtained, regardless of the ratio. 8 refs., 5 figs., 1 tab.

International Nuclear Information System (INIS)

PWR steam generators have suffered from a variety of degradation phenomena. This paper identifies the corrosion-related defects and their probable causes and suggests approaches to correct and prevent corrosive activity. In the attempt to solve the degradation problems, research programs have concentrated on modifying materials, stresses, and the chemical environment in both new and operating steam generators. The following corrosion-related defects have been studied: tube wastage, denting, primary side (ID) intergranular stress corrosion cracking (IGSCC), OD-initiated intergranular attack (IGA), pitting, and corrosion fatigue. Plants affected by wastage have greatly reduced their problem by adopting an all volatile treatment (AVT). In the case of denting, a less aggressive chemical environment is recommended. Primary side IGSCC responds to temperature reduction, stress relief, and material improvements, while flushing and boric acid addition minimizes ...

Energy Technology Data Exchange (ETDEWEB)

The ODS superalloys MA 6000 and MA 760 were investigated with regard to their behaviour under non-isothermal fatigue stress. For this purpose, strain-controlled thermomechanical and bithermal experiments with different phase relationships between strain and temperature were carried out on the one hand; on the other hand, the deformation behaviour under thermomechanical stress was modelled on the basis of isothermal cyclic creep data. The fatigue experiments show that a diamond-shaped cycle derived from the stress pattern of a turbine blade is clearly less critical than in-phase and out-of-phase cycles. The life of the diamond-shaped cycle is determined by oxidation-induced crack initiation and propagation and can be predicted easily with a suitable damage model. Important damage parameters required by the model can be obtained by the less complicated bithermal fatigue tests. Modelling of the TMF hystereses suggests that cyclic, non-isothermal deformaltion is ...

Energy Technology Data Exchange (ETDEWEB)

The study examines the isothermal fatigue properties of novel ODS iron-base or nickel-base superalloys at temperatures of 850 C and 1050 C. The materials are different in grain structure and texture, so that particularly the effects of grain structures and textures can be studied. In order to also perform examinations of creep-fatigue interactions, various load cycles are applied. It is shown that the LCF-affected life of the grain structures of both alloy types is determined by the elastic modulus. The cyclic lifetimes determined by the conventional Manson-Coffin method for both alloy types exhibit differences of up to two orders of magnitude. Using the product of the total strain range and the elastic modulus, however, will yield precise life predictions. Under conditions of LCF stress only, the grain structure has no effect on the materials` service life, other than in the case of creep-fatigue, but the grain structure has a decisive influence on the damage ...

Science.gov (United States)

We demonstrated direct assimilation of cellooligosaccharide using Escherichia coli displaying beta-glucosidase (BGL). BGL from Thermobifida fusca YX (Tfu0937) was displayed on the E. coli cell surface using a novel anchor protein named Blc. This strain was grown successfully on 0.2% cellobiose, and the optical density at 600 nm (OD(600)) was 1.05 after 20 h. PMID:21742905

British Library Electronic Table of Contents (United Kingdom)

The effect of elastic and plastic strains on the magnetic properties of ferrite-pearlite steels has been studied. It has been shown that the sensitivity to elastic-tensile and bending strains is four to five times greater for remnant magnetization than for coercive force. In order to determine the degree of cold plastic deformation of high-carbon steels, a two-parametric testing technique based on the use of remnant magnetization and coercive force was suggested. An MMT-2 device was recommended for measurement of the required parameters.

International Nuclear Information System (INIS)

Recent data on resistance of modern corrosion-resistant austenitic-ferritic steels to different types of corrosion are generalized. It is shown that these steels are characterized by high resistance to general corrosion in acid, alkali, chloride and other solutions, are not inclined to intercrystalline, pitting and crevice corrosion and are noted for high resistance to corrosion cracking and corrosion fatigue. All this is combined with technological and economical effectiveness. It is advisible to use these steels instead of highly-alloyed and expensive steels and alloys in chemical, power and other industries. 59 refs.; 2 tabs.

Energy Technology Data Exchange (ETDEWEB)

Surface modification of topography and chemistry in order to achieve a specific water contact angle (CA) has been explored by using a novel combinatorial screening platform. The screening arrays consisted of 507 distinct combinations of micro-topographies and chemical compositions. By performing chemical modifications with 1H, 1H, 2H, 2H perfluoroethyltriethoxy-silane (PFS) and n-octadecyltriethoxysilane (ODS) on standard silicon wafers it was possible to include both superhydrophobic and very hydrophilic pad arrays in the same screening platform. Surfaces modified with PFS were more hydrophobic than surfaces modified with ODS, while the unmodified silicon surfaces were hydrophilic. For the PFS modified surfaces the largest CAs were achieved with a small pillar size of X = 1 {mu}m and an intermediate inter-pillar gap size of Y = 4 {mu}m with superhydrophobic CAs over 170 . Surface analysis with X-ray photoelectron spectroscopy (XPS) revealed ...

Science.gov (United States)

Polycrystalline soft ferrite, Cu1+xSixFe2?2xO4 (x=0.0, 0.05, 0.1, 0.15, 0.2 and 0.3) were prepared by standard ceramic technique. The X-ray analysis confirmed the single phase formation of the samples up to x=0.1 beside a second phase for x?0.15. The lattice parameter was found to decrease with composition(x), which is attributed to ionic size difference of cations involved. The bulk density measurements shows two different behavior for x0.15. The IR spectra of Cu Si ferrite system have been analyzed in the frequency range 200 1200 cm?1. It revealed two prominent bands ?1 and ?2 which are assigned to tetrahedral and octahedral metal complexes, respectively. The position of the highest frequency band is around 575 cm?1 while the lower frequency band is around 400 cm?1.

Energy Technology Data Exchange (ETDEWEB)

To avoid the drop in corrosion resistance of stainless steels in conventional nitriding (precipitation of CrN), low-temperature techniques like ion implantation, plasma immersion ion implantation (PIII, PI{sup 3}) and low-temperature plasma nitriding were developed. In this investigation, four stainless-steel grades (ferritic: X6Cr17, austenitic-ferritic: X2CrNiMoN22.5.3, austenitic: X8CrNiTi18.10 and X5CrNi18.10) were plasma-nitrided between 250 and 500 C. Nitrogen-enriched layers with a high nitrogen content were produced, leading to a significant increase in surface hardness. X-ray diffraction indicated that CrN did not precipitate if treatment temperatures did not exceed 400 C. 'Expanded austenite' formed in the austenitic and duplex steels and {epsilon}-nitride (Fe{sub 2}N{sub 1-x}) in the ferritic steel. The optically visible structure of the nitrided cases is comparable with that of the PIII layers, ...

Energy Technology Data Exchange (ETDEWEB)

In the production of heavy-sectioned ferritic spheroidal graphite iron castings for such parts as spent fuel shipping container (cask), undesirable structures like abnormal graphite lamella, pearlite or so-called chinese script type of inclusions tend to appear, deteriorating the mechanical properties at the central part of the section where molten iron freezes last. 500 mm thick cylindrical vessels with bottom, weighing 18 tons and 33 tons, were poured as trial products of casks. Solidification structure and mechanical properties were examined at many portions of the castings. By controlling chemical composition, solidification time and inoculation process the structure and the mechanical properties in the last portion of the section to solidify were improved. Sufficiently homogeneous heavy-sectioned ferritic spheroidal graphite iron castings were successfully produced in the as-cast state. In addition, quality assurance process by using test ...

International Nuclear Information System (INIS)

Neutron irradiation embrittlement of reactor pressure vessel (RPV) steels is one of the critical issues on aging management for long term operation of nuclear power plants. Mechanistic understanding of embrittlement is a key to accurate prediction of embrittlement, especially after long term operation where the mechanical test data are sparse. Since matrix hardening is the source of the embrittlement, we focus on matrix hardening of A533B bainitic pressure vessel steel. Bainitic matrix is composed of lath structure made by ferrite and carbides, therefore it is important to understand how this structure affects hardening behavior, and to understand irradiation response of each phase. As the typical dimension of lath structure of A533B is about one micron, nanoindentation technique is suitable for the estimation of hardening of each phase. MV ion accelerators were used for controlled irradiation because MeV ion irradiation can produce defects to the depth greater ...

International Nuclear Information System (INIS)

The synergistic effects of displacement damage and atomic hydrogen and helium on swelling of the ferritic/martensitic steel, F82H, has been investigated. The irradiation was performed at temperatures between 470 and 600 deg. C to 50 dpa (displacement per atoms) under conditions of simultaneous ion beams consisting of Fe"3"+, He"+ and H"+ ions or Fe"3"+ and He"+ ions. The swelling of F82H steel under triple beams with 18 appm He/dpa and 70 appm H/dpa was larger than that under dual beams with 18 appm He/dpa. The swelling in F82H under triple beams increased with decreasing irradiation temperature from 0.1% to 3.2%, while swelling under dual beams was between 0.04% and 0.08%. On the other hand, in the case of triple beam irradiation with a high ratio of gas/dpa, the swelling tended to increase with irradiation temperature. The swelling in ferritic/martensitic steels is significantly enhanced by the synergistic effect of displacement damage, ...

Energy Technology Data Exchange (ETDEWEB)

The aim of this work was the examination of the coarse grain recrystallisation of the {gamma}-free ODS nickel-based alloy PM 1000 depending on the various parameters due to the processing during heat treatment. After isotropic hot compacting (HIP) of the mechanically alloyed powder, one observes a homogeneous sub-microscopic fine grain structure which can coarsen during high temperature heat treatment, due to sufficiently high driving force from the grain boundary energy via abnormal grain growth to 600 times its size. The setting of the elongated high temperature resistant recrystallisation structure is, however, not connected with this. The dependence of the sucess of re-crystallisation on the re-forming parameters (re-forming temperature and degree of re-forming) was shown by a socalled re-forming card. In order to achieve re-crystallisation to a coarse and aligned grain structure, apart from a certain absolute minimum degree of re-forming, the re-forming must ...

British Library Electronic Table of Contents (United Kingdom)

High purity W and W-0.9La2O3 (wt.%) nanopowders were produced by a wet chemical route. The precursor was prepared by the reaction of ammonium paratungstate (APT) with lanthanum salt in aqueous solutions. High resolution electron microscopy investigations revealed that the tungstate particles were coated with oxide precipitates. The precursor powder was reduced to tungsten metal with dispersed lanthanum oxide. Powders were consolidated by spark plasma sintering (SPS) at 1300 and 1400degreeC to suppress grain growth during sintering. The final grain size relates to the SPS conditions, i.e. temperature and heating rate, regardless of the starting powder particle size. Scanning electron microscopy revealed that oxide phases were mainly accumulated at grain boundaries while the tungsten matrix ...

International Nuclear Information System (INIS)

Test Blanket Modules (TBM) will be tested in ITER to verify the capability of tritium breeding and recovery and the extraction of thermal energy suitable for the production of electricity. A Helium Cooled Solid Breeder (HCSB) TBM has been developed in Korea to accomplish these goals. Reduced Activation Ferritic/Martensitic (RAFM) steel has been chosen as the primary candidate structural material for Korean TBM. Due to the complexity of the First wall (FW) and Side wall (SW), it is necessary to develop various joining technologies, such as Hot Isostatic Pressing (HIP), Electron Beam Welding (EBW) and Tungsten Inert Gas (TIG) welding, for the successful fabrication of TBM. In this study, the mechanical properties of TIG welded RAFM steel were investigated. Various mechanical tests of TIG-welded RAFM steel were performed to obtain the optimized TIG welding process for RAFM steel

Energy Technology Data Exchange (ETDEWEB)

Stainless steels can be nitrided at temperatures {<=}400 C to increase their hardness and wear resistance without a decreasing of their excellent corrosion resistance. Structure and properties of the surface layers produced by plasma nitriding and plasma immersion ion implantation in this temperature range were tested. There are negligible differences in the structure of the produced surface layers in spite of different interaction principles of the used technologies. However there are clear differences between the case of different steels. The case of ferritic chromium steels mainly consists of {epsilon}-nitride. Whereas the cases of austenitic and ferritic austenitic steels are characterized by expanded austenite. The corrosion resistance of the steels is reduced by nitriding only, if evident CrN-formation occurs. (orig.) 11 refs.

British Library Electronic Table of Contents (United Kingdom)

Nanocrystalline MnFe"2O"4 ferrite was prepared by using autocombustion technique (flash). The microstructure and magnetic properties are studied. The results of XRD and TEM clarified that, this ferrite is nanosized with particle size (39 nm). Magnetic measurements showed a ferromagnetic behavior with T"C = 613 K, the saturation magnetization M"s = 13.71 emu/g, remanent magnetization M"r = 0.1694 emu/g and, coercivity H"c = 25.6 Oe. Natural material, egg white used as an aqueous medium to extend prepare nanoparticles better than other chemical interesting materials.

International Nuclear Information System (INIS)

Ferrite of system, namely Ni_1_-_xZn_xFe_2O_4 with x = (0.0, 0.2, 0.4, 0.6, 0.8, 1.0), have been prepared by solid state reaction to investigate the effect of gamma rays irradiations using Co"6"0 source on the cation distribution, structural and magnetic properties. The unirradiated and irradiated samples were then subjected to characterization techniques such as X-ray diffraction, magnetization and AC susceptibility. The results of these characterizations are found to be different for irradiated from that of the pristine sample. The modifications in respect of irradiated samples are explained in terms of the ion-induced disorder. The important result of #gamma#-irradiation on the cation distribution, structural and magnetic properties is the change of ratio Fe"2"+/Fe"3"+. Possible reasons on the results are proposed.

Energy Technology Data Exchange (ETDEWEB)

For the purpose of solving the limitations such as shape and dimension for magnetic compact fabricated by conventional anisotropic forming under magnetic orienting field, the feasibility of a new magnetic forming process was studied. Ferrite powder mixed with UV resin was compacted in the die mold and followed by alignment under the magnetic field. Effects of viscosity of UV resin and forming condition on magnetic characteristics of the compact was investigated. Maximum degree of alignment for the ferrite powder reached to 0.826. It was predicted that the proposed method had make it possible to fabricate a high performance magnet having the anisotropic alignment of the magnetic powder. The UV resin is desirable to have low viscosity, good properties such as formability and configuration stability for the compact and also parting- ability between the metal mold and the compact. (author)

Science.gov (United States)

Spike-timing-dependent plasticity (STDP), a form of Hebbian plasticity, is inherently stabilizing. Whether and how GABAergic inhibition influences STDP is not well understood. Using a model neuron driven by converging inputs modifiable by STDP, we determined that a sufficient level of inhibition was critical to ensure that temporal coherence (correlation among presynaptic spike times) of synaptic inputs, rather than initial strength or number of inputs within a pathway, controlled postsynaptic spike timing. Inhibition exerted this effect by preferentially reducing synaptic efficacy, the ability of inputs to evoke postsynaptic action potentials, of the less coherent inputs. In visual cortical slices, inhibition potently reduced synaptic efficacy at ages during but not before the critical period of ocular dominance (OD) plasticity. Whole-cell recordings revealed that the amplitude of unitary IPSCs from parvalbumin positive (Pv+) interneurons to pyramidal neurons ...

British Library Electronic Table of Contents (United Kingdom)

Ultrafine grained steels with different carbon contents were produced through warm caliber rolling and evaluated for their stress-strain behavior along with the reduction in area. It was found that the reduction in area-tensile strength balance is far better than the conventional ferrite+pearlite steels and even superior to bainitic steels for all materials tested in the present study.

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

Acid Rock Drainage (ARD) is the product formed by the atmospheric oxidation of the relatively common pyrite and pyrrhotite. Waste rock dumps and tailings containing sulfide mineral have been reported at toxic materials producing ARD. Mining in sulphide bearing rock is one of activity which may lead to generation and release of ARD. ARD has had some major detrimental affects on mining areas. The purpose of this study was carried out to develop disposal method for preventing contamination of water and soil environment by waste rocks dump and tailings, which could discharge the acid drainage with high level of metals. Scope of this study was as following: environmental impacts by mine wastes, geochemical characteristics such as metal speciation, acid potential and paste pH of mine wastes, interpretation of occurrence of ARD underneath tailings impoundment, analysis of slope stability of tailings dam etc. The following procedures were used as part of ARD evaluation and prediction to ...

Energy Technology Data Exchange (ETDEWEB)

The use of linear accelerators in radiotherapy is of great importance in Medicine, and according to international recommendations the electron beam dosimetry has to be performed using plane-parallel ionization chambers, previously calibrated in standard gamma radiation fields at accredited laboratories. In this work, calibration methods of plane-parallel ionization chambers used in dosimetry procedures of high energy electron beams of clinical accelerators were presented, tested and intercompared. The experiments were carried out using gamma radiation beams of {sup 60} Co at the Calibration Laboratory of Clinical Dosemeters at IPEN and electron beams od 4 to 16 MeV at the Radiotherapy Department of Hospital Israelita Albert Einstein, Sao Paulo. A method was chosen to be established at IPEN. Proposals of the calibration procedure, calibration certificate and data sheets are presented. (author)

Energy Technology Data Exchange (ETDEWEB)

One of the main factors that require special attention in a pipeline construction is the cold bending process, once depending on the region that the line will be installed the number of bends may achieve 75%, as it was observed in some areas during Campinas-Rio pipeline construction. A study was carried out to evaluate the X80 cold bending operational parameters in order to make viable the use of high strength pipes in the construction of onshore pipelines. For this analysis three pipes of 34 inches x 0.750 inches had been cold bended, the operation was carried out using a hydraulic equipment with punches applications along the pipe, recording the correspondent angles related to the elastic and plastic deformations in order to assess the material spring-back. After the bending process, samples of the weld, extrados and intrados were subjected to mechanical and metallographic tests, as well as performed dimensional inspection of the pipes. It was possible to obtain a 19 deg curve and ...

Energy Technology Data Exchange (ETDEWEB)

The effect of accelerated thermal cycling on a joint between modified 9Cr-1Mo steel (Grade 91) and Alloy 800 welded with Inconel 82 and 182 filler material is discussed. This is part of a trimetallic transition joint involving Grade 91-Alloy 800-316LN austenitic stainless steel for steam generator application. It has been shown that, during thermal cycling following the typical post-weld tempering treatment at 760 deg. C for 2 h, no carbon diffusion occurs from the ferritic steel towards the weld metal. There is, in fact, a hardness increase at the ferritic steel/weld metal interface which is probably a result of work hardening. Carbon migration sets in only after unusually long post-weld heat treatments for 20 and 50 h at 760 deg. C followed by thermal cycling. Significantly, even under the most severe thermal cycling test conditions imposed, no cracking or oxide notching could be detected, thus demonstrating the superior performance potential ...

International Nuclear Information System (INIS)

Superparamagnetic MFe23+O4 (M=Mn2+, Fe2+ and Co2+) inverse spinel ferrite (ISF) nanoparticles with narrow size distribution having average diameters of 6-8 nm were synthesized by a diol reduction of organic metals and the surface was modified to be hydrophilic by coating with succimer. Magnetic resonance imaging (MRI) contrast enhancement by dipolar coupling defined interactions between the synthesized ISFs and protons in the bulk water was investigated with initial susceptibility, magnetization and anisotropy of the succimer-coated ISFs. The relaxivity ratios, r2/r1, for MnFe2O4, Fe3O4 and CoFe2O4 were measured to be 12.2, 23.1 and 62.3, respectively, which demonstrate the potential usefulness of these magnetic nanoparticles as T2 contrast agents for MRI.

Energy Technology Data Exchange (ETDEWEB)

The low-cycle fatigue properties of the ferritic-martensitic steels MANET I and II and F82H-mod, have been investigated at a temperature of 200 C. The strain-controlled fatigue has been performed with strain ranges between 0,4% and 1,0% and at a strain rate of 8.10{sup -4} s{sup -1}. The steel F82H-mod, is characterised by a higher plastic strain amplitude compared to MANET I and II. Some of the specimens have beenirradiated with a 104 MeV {alpha}-particle beam. The homogeneous implantation of 400 appm He leads to a hardening of the material. At the beginning of the fatigue tests the stress response of the irradiatedspecimens is higher compared to the unirradiated specimens. In general, thematerial shows softening during fatigue. The softening of irradiated material, which is fatigue tested with a high total strain amplitude, is higher than that of the unirradiated material. The lifetime is reduced. For irradiated specimens fatigued at small total strain amplitudes ...

International Nuclear Information System (INIS)

Irradiation of ferritic steels with neutrons in the temperture range of room temperature to #propor to# 450deg C results in lattice hardening, which causes an increase in strength and a decrease in ductility. Eight reduced-activation Cr-W-V stels with chromium concentration varying from 2.25 to 12% were irradiated at 365deg C to #propor to# 7 dpa in the Fast Flux Test Facility. A steel with 2.25% Cr and the combination of 2% W and 0.25% V hardened less than those containing vanadium or tungsten alone or a steel with 1% W and 0.25% V. The amount of hardening was similar for Cr-W-V steels with constant vanadium and tungsten concentrations and containing 2.,25, 5, and 9% Cr; a steel with 12% Cr hardened considerably more. Specimens of two conventional Cr-Mo steels, 9Cr-1MoVNb and 12Cr-1MoVW, were also irradiated, and the hardening of these steels was similar to analogous reduced-activation steels. (orig.).

International Nuclear Information System (INIS)

Past elastic-plastic fracture studies for leak-before-break (LBB) assessment of low alloy steel pipings have been focused mostly on the behavior of base metals and their weld metals. In contrast, the heat-affected zone (HAZ) of a welded pipe has not been studied in detail primarily because the size of the HAZ is too small to make specimens for mechanical properties measurements. In this study, microstructural analyses, microhardness tests, tensile tests and J-R tests have been conducted as a function of distance from a fusion line and temperature for HAZ materials of SA106Gr.C low alloy piping steels. For the ferrite-pearlite steels such as SA106Gr.C, the HAZ specimens showed a higher yield strength and fracture toughness compared with those of its base metal. These characteristics, despite of grain coarsening, can be explained by cleaner microstructures of HAZ materials with a finer morphology of carbides compared with pearlitic-ferritic base ...

Energy Technology Data Exchange (ETDEWEB)

Austenitic stainless steel castings, such as SCS 13, SCS 14, which consists of {delta}/{gamma} duplex phase, are extensively used as structural material in seawater environments. It is known that SCS 14 involving 2wt% Mo is more resistant to pitting corrosion than SCS 13. In this paper, effects of Mo on the pitting corrosion are discussed in terms of microstructure of the material. The corrosion behavior of the materials with different {delta} ferrite contents and cleanlinesses have been evaluated by seawater exposure testing, electrochemical polarization, and TEM-EDX analysis. The results indicate that pits mainly nucleate at nonmetallic inclusions such as MnS and {delta}/{gamma} boundaries, and materials containing {delta} ferrite above 7vol% have high pitting corrosion resistance. The nucleation at {delta}/{gamma} boundaries is assumed to be due to the segregation of P. It is considered that because of segregation of Mo along {delta}/{gamma} ...

Energy Technology Data Exchange (ETDEWEB)

Fe-Cr-Mn stainless steel is one of the candidate materials for the 1`st wall materials and structural applications of fusion reactor as regards reduced radioactivation properties than Fe-Cr-Ni austenitic stainless steels. This report deals with the effects of annealing and aging heat treatment on the microstructure, mechanical properties and corrosion resistance of Fe-Cr-Mn alloys varying Mn and W contents, which were made using vacuum high frequency induction furnace. Increasing Mn contents, austenite phase was increased, and maximum .epsilon. martensite phase was formed at about 21% Mn. W-addition made small amount of ferrite phase in the matrix, and the ferrite contents were increased with raising annealing temperature. Increased Mn contents reduced tensile stress and yield stress but increased the elongation. W-addition raised the high temperature tensile properties. The variation of Mn contents had no influenced on corrosion resistance. ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical behaviour of passive films formed on one austenitic stainless steel (AISI 304) and one ferritic stainless steel (AISI 446) in solutions with pH between 0.6 and 8.4 was studied by capacitance measurements and photocurrent spectroscopy. Compositional characterization of the passive films was done by X-ray photoelectron spectroscopy. The capacitance increases with decreasing pH. Doping densities evaluated from Mott-Schottky plots are in the range 2-6 x 10{sup 20} cm{sup -3} and increased with the pH in the neutral/alkaline range while in pH 0.6, values above 10{sup 21} cm{sup -3} were found. The bandgap energy indicates two transitions, at 2.5-2.8 and 3.2 eV. The analytical data reveal that, as the pH increased, the films become enriched in Fe(II) and Fe(III), whereas the Cr(III) gradually decreases. The films formed at very low pH had a behaviour that contrasts with that of the films formed in the neutral/alkaline media. The films are described by ...

International Nuclear Information System (INIS)

Ferritic/martensitic steel, modified 9Cr-1Mo steels have been used most extensively in the power generation industry throughout the world due to having superior high temperature properties such as high strength, creep resistance, and good microstructure stability. These steels are also the primary candidate for the RPVs(Reactor Pressure Vessels) of High Temperature Gas-Cooled Reactors. Currently, many studies has been conducted in laboratory-scale for mod. 9Cr-1Mo steels. However, there is a lack of the study on forged thick- section for RPVs. The differences in characteristics including the through thickness microstructure and mechanical properties between internal and external locations may occur during cooling after austenitization, because the thickness of RPVs is over about 200mm. Therefore, in order to use ferritic/martensitic steel as RPVs, a detailed assessment of the through thickness properties is needed. The purpose of this study is ...

Energy Technology Data Exchange (ETDEWEB)

A prospective study was performed on 50 patients suffering from osteochondritis dissecans of the knee and ankle to define criteria for stability and fixation of osteochondral lesions. Morphological parameters in MRI (size, fragmentation, cartilage, interface) and conventional radiology (separation, fragmentation) were registered and compared with arthroscopical staging. MRI staging based on different types of interfaces was demonstrated on T{sub 1}- and T{sub 2}-weighted images. MRI could correctly predict a Grade 1 lesion in 50%, a Grade 2 lesion in 90%, a Grade 3 lesion on 0%, and a Grade 4 lesion in 79%. Stable lesions were differentiated from unstable lesions in 90%. Radiographic findings corresponded with arthroscopic staging in only 56% of the cases because fibrotic connection may guarantee stability in case of bony separation. (orig./MG) [Deutsch] In einer prospektiven Studie an 50 Patienten mit einer Osteochondrosis dissecans (OD) des Knie- und ...

Energy Technology Data Exchange (ETDEWEB)

Higher efficiencies of steam power plants are achieved by raising the operating temperature and pressure. The use of ferritic steels helps to minimize the cost and enhance the flexibility (two-shift operation, frequent starting and stopping). The COST programme had the long-term goal of developing and testing 9- 12 % Cr steels with high fatigue strength and to produce,test and operate critical components for an advanced steam power plant (steam temperature 600 C and supercritical pressure). (orig.)

International Nuclear Information System (INIS)

A variety of advanced controlled rolling techniques have been developed to improve toughness, strength and weldability of niobium-steels. To achieve optimum properties, control of prior stage rolling conditions and accelerated cooling are needed. In low carbon steel, the addition of niobium results in a greater increase in tensile strength than that of vanadium without a loss of toughness. At the same strength level, niobium-steel has less susceptibility to weld cracking and good toughness in the HAZ of its weldments than similar vanadium steels. Separation and formability of niobium steels are also discussed.

Science.gov (United States)

Using an expanded nuclear data base, the transmutation of PCA, AMCR33 (a reduced activation austenitic steel), HT-9, Rafer2 (a reduced activation ferritic steel), V-15%Cr-5%Ti alloy, and SiAlON (a ceramic) were calculated for two positions in the Fast Flux Test Facility (FFTF), three positions in the High Flux Isotope Reactor (HFIR), and the first wall position of both the STARFIRE and MARS conceptual fusion reactors. The peripheral test (PTP) position, and to a lesser extent the radial beryllium (RB) position, of HFIR show significant transmutations which are often in the opposite direction to the transmutations in the fusion conceptual designs. The positions in FFTF, as well as the hafnium covered location in the HFIR RB position show relative minor transmutations.

British Library Electronic Table of Contents (United Kingdom)

Irradiation of EP-823 (16Cr12MoWsiVNbB) ferritic-martensitic steel with 7-MeV Ni++ ions and with 30- and 70-keV He+ ions at a temperature of 500?C was followed by an increase in the microhardness, which was due to both radiation point defects and changes in the phase composition and the dislocation structure of the steel. It was found that the dependence of the largest relative increase in the microhardness on the concentration of radiation-induced point defects in the near-surface region of the steel under irradiation with different ions correlated with an analogous dependence of the surface segregation of silicon and chromium.

Energy Technology Data Exchange (ETDEWEB)

There have been many stress measurements on welds by neutron diffraction over the past 20 years but there are still a number of serious experimental issues that are often not addressed. The primary fact is that the microstructure generally changes across the weld and accompanying this may be a change in the concentration of strengthening elements in solution. This will lead to a shift in lattice spacing which may be incorrectly interpreted as a strain. Secondly, a gradient of plastic deformation near the weld may be expected. Since plastic deformation by application of a stress always generates intergranular (type-2) strains this may lead to a range of intergranular effects superposed on the conventional weld-related strains. The effects are illustrated by neutron diffraction studies of Zr-4, ferritic and austenitic welds where chemistry, intergranular effects and crystallographic texture can all play a role.

Energy Technology Data Exchange (ETDEWEB)

The pitting resistance of Fe-Cr and Fe-Cr-Mo alloys has been correlated with characteristics of the passive films analyzed by Auger electron spectroscopy (AES). Increased film protectiveness as a result of increased Cr in the alloy can be directly attributed to Cr enrichment of the film and decreased film thickness. Increased Mo in the alloy or passivation at noble potentials promotes passive film resistance to breakdown, but neither does much to change the macrocharacteristics of the film. Rather, it is suggested that the roles of alloying and/or passivation conditions are related to the susceptibility and distribution of weak points of the film. In solutions in which pitting occurs, chloride is generally not incorporated into the film, suggesting that the role of halides is to interact with weak points of the film at the solution/film interface. At 260/sup 0/C, the films are much thicker and likely to be much more defective in structure than those formed at 80/sup 0/C.

British Library Electronic Table of Contents (United Kingdom)

This paper presents a procedure for transferring the CTOD fracture toughness obtained from laboratory specimens to an equivalent CTOD for structural components, taking constraint loss into account. The Weibull stress criterion is applied to correct the CTOD for constraint loss, which leads to an equivalent CTOD ratio, b, defined as b=d/dWP, where d and dWP are CTODs of the standard fracture toughness specimen and the structural component, respectively, at the same level of the Weibull stress. The CTOD ratio b is intended to apply to the fracture assessment of ferritic steel components to stress levels beyond small-scale yielding. Nomographs are given to determine the b-value as a function of the crack type and size in the component, the yield-to-tensile ratio of the material and the Weibul...

International Nuclear Information System (INIS)

The magnetic and magnetostrictive properties of polycrystalline Co1-xMnxFe2O4 (0 ? x ? 0.4) have been studied. Although the Curie temperature decreases continuously with increasing concentration of Mn, the magnetization remains high up to x = 0.3 and unexpectedly low coercivity is observed for this composition showing an unusual magnetostrictive behaviour. This composition shows a relatively larger magnetostriction at low fields. Moreover, the strain derivative which is the slope of the magnetostriction curve at low magnetic fields is almost doubled and the field at which maximum magnetostriction is observed is reduced to almost half for 30% of Mn substitution. The results show that x ? 0.3 in Co1-xMnxFe2O4 is an optimum composition with superior magnetostrictive properties for many applications.

British Library Electronic Table of Contents (United Kingdom)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically conductive and corrosion-resistant CrN or Cr2N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of commercially available, high Cr (30-35wt%) Ni-Cr alloys and a ferritic high Cr (29wt%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effect...

Energy Technology Data Exchange (ETDEWEB)

The preliminary design of a far-infrared free-electron laser with a Coaxial Hybrid Iron (CHI) wiggler is presented. The CHI wiggler consists of a central rod and outer ring of alternating ferrite and dielectric spacers. A periodic wiggler field is produced when the CHI structure is immersed in an axial magnetic field. The design under investigation makes use of 1A, 1MV annular electron beam interacting with the TE{sub 01} coaxial waveguide mode at approximately 1 THz ({lambda} = 300 {mu}m). The nominal wiggler period is 0.5 cm and the inner and outer waveguide radii are 0.4 and 0.8 cm, respectively. An axial guide field of 5-10 kG is used. The device performance is modeled with slow-time-scale nonlinear code. Self fields and axial velocity spread are included in the model. Theoretical results will be presented.

Energy Technology Data Exchange (ETDEWEB)

Raman scattering was observed from thin film optical waveguides of cellulose acetate exposed to water vapor from 0% to 100% relative humidity (RH), and from dilute solutions of water in methyl acetate. Spectra of cellulose acetate (CA398, 39.8% acetyl) at low RH and cellulose triacetate (CTA) at low and high RH are consistent with the presence of water monomers that are weakly hydrogen bonded to acetyl C=O groups. Differences between the spectra of water in CA398 and CTA at low RH are attributed to sequential hydrogen bonding involving OH groups in CA398. At high RH, CA398 and CTA (to a lesser extent) show bands attributed to water/water interactions that are similar to those found in sequentially hydrogen-bonded hydrates. CA398 films that are annealed at high temperatures exhibit decreased water/water interactions at high RH. Exposure of CA398 films to D/sub 2/O converts > 90% of all polymer OH groups to OD groups. This indicates that water is accessible to ...

International Nuclear Information System (INIS)

This paper describes a reactor design to facilitate a room-temperature nuclear fusion/fission reaction to generate heat without generating unwanted neutrons, gamma rays, tritium, or other radioactive products. The room-temperature fusion/fission reaction involves the sequential triggering of billions of single-molecule, "6LiD 'fusion energy pellets' distributed in lattices of a palladium ion accumulator that also acts as a catalyst to produce the molecules of "6LiD from a solution comprising D_2O, "6LiOD with D_2 gas bubbling through it. The D_2 gas is the source of the negative deuterium ions in the "6LiD molecules. The next step is to trigger a first nuclear fusion/fission reaction of some of the "6LiD molecules, according to the well-known nuclear reaction: "6Li + D #-># 2"4He + 22.4 MeV. The highly energetic alpha particles ("4He nuclei) generated by this nuclear reaction within the palladium will cause shock and vibrations in the palladium lattices, leading ...

International Nuclear Information System (INIS)

A simple and specific method has been developed for the simultaneous determination of the four major Cinchona alkaloids and their dihydroderivatives and pyridoxine hydrochloride (Vitamin B_6) by high-performance liquid chromatography (HPLC) with fluorescence detection (#lambda#_e_m=420 nm with #lambda#_e_x=330 nm). The chromatographic separation was performed on a Phenomenex Prodigy ODS column (5 #mu#m, 250 mmx3.2 mm i.d.), recommended for basic compounds, under isocratic reversed-phase conditions. The method allowed a good peak shape and an effective resolution of the tested compounds. The extraction of alkaloids from the Cinchona succirubra bark was carried out in mild and fast conditions (ambient temperature, 20 min) by ultrasonication. The procedure showed to be advantageous respect to a reference method, which involved Soxhlet extraction. The results were compared statistically by means of the Student's t-test and the variance ratio F-test; no significant ...

International Nuclear Information System (INIS)

Full text: The transmutation of nuclear waste to reduce the burden on a geological repository is a relevant topic within the Program of Nuclear Safety Research of the Research Centre Karlsruhe. Several studies have confirmed that a high efficiency of transmutation of actinides is reached in fast neutron spectrum reactor system. Therefore, an important effort is dedicated to the study of transmutation strategies with different fast reactors and their associated technologies. Moreover, in international contexts as Generation IV International Forum (GIF) and Sustainable Nuclear Energy Technology Platform (SNETP), fast reactors are considered in the frame of sustainable development of nuclear energy and reduction of waste. The systems that are currently under investigation, in the frame of the different fuel cycle scenarios, are liquid metal cooled and gas cooled fast reactors as well as Accelerator Driven Sub-critical Transmutation devices (ADS). These innovative reactor systems, call for ...

Energy Technology Data Exchange (ETDEWEB)

The influence of high C martensite on the strength and impact behavior of C-Mn-Nb-Al steels has been determined for two distributions: films surrounding the ferrite grains and distinct colonies. In the former case, the impact behavior markedly deteriorated, this deterioration increasing with martensite level. The changes in impact behavior could be explained by regarding the films of martensite as being similar to the brittle grain boundary carbides that are present in ferrite-pearlite steels. These films readily crack, yet are always thick enough to produce a sufficient wide crack to render crack propagation easy. The critical event in fracture then becomes the ability to propagate the cracks through the grain boundaries. The greater the grain boundary coverage by these films, the easier this becomes and the worse is the impact behavior. When the martensite is present as colonies, again the impact performance is seriously impaired, but to a ...

Energy Technology Data Exchange (ETDEWEB)

Holmium doped barium based hexaferrites BaFe{sub 12-2x}Ho{sub 2x}O{sub 19} with (x = 0.0-1.0) were synthesized by solid state reaction method. Structural and magnetic characterization of these ferrites provide significant information about their reactive physical properties. X-ray analysis reveals that in all samples M-type structure exist with few secondary phases. Scanning electron microscope revealed the grain size of the specimen. The results show that grain size decreases with the substitution degree of Holmium. Thus rare earth element Holmium Ho{sup 3+} acts as a grain growth inhibitor. The magnetic hysteresis loops show the variation in the values of magnetic parameters like saturation magnetization (M{sub s}), remanent magnetization (M{sub r}) and coercivity (H{sub c}) were observed by changing Ho{sup 3+} content in BaFe{sub 12-2x}Ho{sub 2x}O{sub 19} ferrites. Coercivity showed a maximum value of 2230 Oe for (x = 0.4) and then ...

Energy Technology Data Exchange (ETDEWEB)

In this thesis, increased hemicellulose retention during kraft pulping has been studied. The work has been divided into three parts: i) Development of an accessible and reliable method for determination of carbohydrate composition of kraft pulps ii) Investigation of the composition and molecular mass distributions of the carbohydrates in kraft pulps with increased hemicellulose content iii) Investigation of the effect of increased hemicellulose content on the sheet properties of kraft pulps with increased hemicellulose content. A method for carbohydrate determination was developed. In this method, enzymes are used to hydrolyse the pulp into monosaccharides. A relatively mild acid hydrolysis is performed prior to detection on an HPLC with an RI-detector. The pulp is not derivatized and no pre-treatment (mechanical or chemical) is needed to determine the carbohydrate composition using the method developed here. Peak deconvolution software is used to improve the accuracy. Polysulphide and ...

International Nuclear Information System (INIS)

Generally, neutron, ion and electron Irradiations cause a substantial amount of hardening and significantly alter the deformation behavior of metals and alloys at relatively low irradiation temperatures. A radiation hardening is caused by the formation of microstructural defects such as dislocation loops, voids and precipitates under irradiation. Therefore, it is important to have a better knowledge of the irradiation induced microstructural defects under irradiation condition. As a part of the National mid- and long-term atomic energy R and D program, we are dealing with the radiation hardening behavior in Fe-Cr binary alloy. Fe-Cr binary alloy is a base alloy of Ferritic/Martensitic steel(F/M steel) planning to use for the Gen IV nuclear system. In this work, we investigated the radiation hardening and microstructural defect evolution in ion irradiated Fe-Cr alloys with irradiation temperature using nano-indentation measurement and transmission electron ...

Energy Technology Data Exchange (ETDEWEB)

The CALPHAD (calculations of phase diagrams) method is used to examine the effects of applied magnetic fields on the {alpha}/{gamma} phase boundary in the Fe-Si system in the paramagnetic state. The reported susceptibility data for pure Fe is first re-evaluated. The contributions to the total Gibbs energy of the ferrite ({alpha}) and austenite ({gamma}) from the external fields are calculated based on the Curie-Weiss law and the re-evaluated susceptibility data. The Fe-Si phase diagram on the Fe-rich side as a function of applied field is calculated using the Thermo-Calc(TM) package. With increasing field strength, the {gamma} loop shrinks monotonically; that is, the {alpha}/{gamma}-Fe transition temperature increases while that for {gamma}/{delta}-Fe transition decreases, albeit more slowly. Finally, in conformance with the existing CALPHAD databank, Redlich-Kister polynomials are proposed to account for the compositional and temperature dependence of the ...

Energy Technology Data Exchange (ETDEWEB)

Microstructural analyses by advanced metallographic techniques were conducted on mockup welds and a cracked BWR core shroud weld fabricated from Type 304L stainless steel. heat-affected zones of the shroud weld and mockup shielded-metal-arc welds were free of grain-boundary carbide, martensite, delta ferrite, or Cr depletion near grain boundaries. However, as a result of exposure to welding fumes, the heat-affected zones of the welds were significantly contaminated by fluorine and oxygen which migrate to grain boundaries. Significant oxygen contamination promotes fluorine contamination and suppresses classical thermal sensitization, even in Type 304 steels. Results of slow-strain-rate tensile tests indicate that fluorine exacerbates the susceptibility of irradiated steels to intergranular stress corrosion cracking. These observations, combined with previous reports on the strong influence of weld flux, indicate that oxygen and fluorine contamination and ...

Energy Technology Data Exchange (ETDEWEB)

One aspect of the research program SFB 570 'Distortion engineering' is the in situ X-Ray diffraction analysis of phases and residual stresses during complete heat treatment cycles. These investigations result in experimental evidence available for the extensive computations. The optimisation of the instrumentation will be reported. A surface decarburisation of samples made from the ball bearing steel 100Cr6 could be avoided for a temperature range from 800 to 900 C and a holding time of one hour by a combination of evacuate the furnace and using a certain nitrogen flow as protective gas. At lower temperatures small amounts of ferrite caused by an increased diffusion rate of carbon lead again to a surface decarburisation up to a depth of 2 {mu}m. It was proved that with an evacuation of the X-Ray beam path at constant power of the X-Ray source the intensity of diffraction lines could be increased by more than a factor of 4. The use of nitrogen as ...

Energy Technology Data Exchange (ETDEWEB)

A 9Cr-1Mo steel with properties improved over other ferritics in the ranges from 9 to 12% Cr and 1 to 2% Mo and over the widely used 2 1/2 Cr-1Mo steel has recently been developed. The main changes in the modified alloy, compared with the standard alloy, include: addition of niobium and vanadium, to improve the alloy's elevated-temperature strength properties; a specified range for each element; and a specification for nitrogen, which is not listed for the standard 9Cr-1Mo. Microstructural work has indicated that the improved strength of the modified alloy comes from two factors: (1) fine M/sub 23/C/sub 6/ precipitate particles nucleate on Nb/C, N, which comes out first during the heat treatment; and (2) the vanadium enters M/sub 23/C/sub 6/ and retards its growth at the service temperature. Mechanical properties discussed were Charpy-impact, tensile, and creep properties. Other properties included were: thermal expansion coefficient, fatigue tests, steam ...

Energy Technology Data Exchange (ETDEWEB)

In the present paper, the chemical composition of passive films formed on both phases of two types of duplex stainless steels (UNS S31803 and UNS S32304) is determined at the micro-scale using Auger electron spectroscopy (AES). Samples were either mechanically polished (down to diamond pastes) or electrochemically etched in acidic solutions. The micro-electrochemical behavior of samples was then determined in sodium chloride media by means of the electrochemical micro-cell technique (capillary diameters of 30 {mu}m). The results obtained were analyzed considering the passive film chemical composition. Quantitative relationships between electrochemical parameters and the distribution of chromium and iron in the oxide layer were found. Due to differences in mechanical properties between ferrite and austenite, a heterogeneous stress distribution is generated in both phases. A method based on thermal-mechanical simulation was used to quantify surface stress gradients ...

International Nuclear Information System (INIS)

Because of their austenitic-ferritic microstructures, duplex stainless steels offer a good combination of mechanical and corrosion resistance properties. However, heat treatments can lower the mechanical strength of these stainless steels as well as render them susceptible to intergranular corrosion (IGC) and pitting corrosion. In this study, a low-carbon (0.02%) duplex stainless steel is subjected to various heat treatments at 450 to 950 C for 30 min to 10 h. The heat-treated samples than undergo ASTM IGC and pitting corrosion tests, and the results are correlated with the microstructures obtained after each heat treatment. In the absence of Cr_2_3C_6 precipitation, #sigma#-phase precipitates render this duplex stainless steel susceptible to IGC and pitting corrosion. Even submicroscopic #sigma#-phase precipitates are deleterious for IGC resistance. Longer-duration heat treatments (at 750 to 850 C) induce chromium diffusion to replenish the chromium-depleted ...

Energy Technology Data Exchange (ETDEWEB)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically- conductive and corrosion-resistant CrN or Cr2N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of two high Cr (30-35 wt%) commercially available Ni-Cr alloys and a ferritic high Cr (29 wt.%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved via nitridation. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effects for the Ni-Cr base alloys, but beneficial effects for the stainless steel alloy. Results of single-cell fuel cell testing are also presented.

International Nuclear Information System (INIS)

Fretting wear test in room temperature water was performed to evaluate the wear coefficient of CANDU (CANadian Deuterium Uranium) steam generator (SG) tube material (Alloy 800) against 410 type martensitic stainless steels. The main focus is to compare the wear behaviors between Alloy 800 and Inconel 690. Test conditions are 10#approx#30N of normal load, 200#approx#450mm of sliding amplitude and 30Hz of frequency. The result indicated that the wear rate of Alloy 800 was higher than those of Inconel 690 at various test condition such as normal loads, sliding amplitudes etc. From the results of SEM observation, there was little evidence of plastic deformation layer that were dominantly formed on the worn surfaces of Inconel 690. Also, wear particles in Alloy 800 were released from contacting asperities deformed by severe plastic flow during fretting wear. Main cause of wear rate between Alloy 800 and Inconel 690 may be due to the difference of hardness between martensitic and ...

Energy Technology Data Exchange (ETDEWEB)

Described herein are effects of nitrogen dissolved in steel on passivity and pitting corrosion, as one of the major corrosion phenomena observed in stainless steel. Mechanisms involved in controlling pitting corrosion by nitrogen are also discussed. Nitrogen contained in austenic stainless steel is concentrated in the surface area, in particular in the vicinity of the interface between the passive film and metal matrix. Nitrogen tends to decrease critical current density in an acid, when it is added to steel of high critical current density (approximately 1mA/cm{sup 2} or higher). This phenomenon is considered to result from accumulation of nitrogen preferentially in the surface area to prevent dissolution of steel. Nitrogen dissolved in the austenic phase improves resistance of the steel to pitting corrosion. This phenomenon is considered to result from controlled decrease in pH level during the initial stage of pitting corrosion, characterized by evolution of micropits, to help ...

British Library Electronic Table of Contents (United Kingdom)

Holmium doped barium based hexaferrites BaFe12-2xHo2xO19 with (x=0.0-1.0) were synthesized by solid state reaction method. Structural and magnetic characterization of these ferrites provide significant information about their reactive physical properties. X-ray analysis reveals that in all samples M-type structure exist with few secondary phases. Scanning electron microscope revealed the grain size of the specimen. The results show that grain size decreases with the substitution degree of Holmium. Thus rare earth element Holmium Ho^3^+ acts as a grain growth inhibitor. The magnetic hysteresis loops show the variation in the values of magnetic parameters like saturation magnetization (Ms), remanent magnetization (Mr) and coercivity (Hc) were observed by changing Ho^3^+ content in BaFe12-2xH...

International Nuclear Information System (INIS)

The deposit of radioactive corrosion products in the cooling systems of nuclear reactors becomes a serious problem for the personnel of facilities. Crud has an important role in the process of depositing radioactive corrosion products. The main components of crud are hematite, magnetite, nickel ferrite and so on, and the particles of these oxide compounds are distributed in water. Most of the behavior of crud are still not known. As for the mechanism of the production of crud, the Potter-Mann model has been proposed. However, the precipitation process of iron ions in water is unknown. The crud is defined as the particles filtered by 0.45 micrometer millipore filters. However, it is not known whether there are crud particles smaller than this size. The crud particles can be adsorbed on the filters by the surface electrochemical interaction. The adsorption of cations to crud particles was studied. The adhesion of crud particles was investigated through some model ...

Energy Technology Data Exchange (ETDEWEB)

The significant technical and industrial aspects which have led to main coolant line (MCL) materials selection are addressed from a long term experience and operational practice point of view. They are based on the Siemens/KWU developed basic material concept for its nuclear power plants. It considers the choice of appropriate materials, the evaluation and qualification of the materials and the materials manufacturer, the use of appropriate semi-finished products, the tailoring of material and semi-finished products to the specific requirements of the various systems, the application of adequate manufacturing processes and the proof of the requirements by specifying proper tests and examinations. The main systems are assigned to safety classes in accordance with their safety relevance. Summarizing the operation time of nuclear power plants with ferritic MCL equipped by Siemens/KWU, more than 200 years of operation experience exist and no upgrading or replacement of ...

Energy Technology Data Exchange (ETDEWEB)

The precipitation hardened, ferrite-pearlite medium-carbon steels microalloyed with vanadium (AFP steels) have been developed over the last few years as materials allowing processing by controlled, continuous cooling down from forging temperatures, for achieving benefits such as reducing the number of required heat treatment and working processes and saving expensive alloying materials. Due to their cost-saving advantages, the steels rapidly have been accepted as an alternative material to the quenched and tempered steels and re particularly used for fabrication of automobile parts. Their drawbacks however are the lower yield strength, and low ductility and toughness as compared to the heat-treatable steels. The research project therefore was intended to enhance the properties of the microalloyed, medium-carbon steels and widen their applicability by establishing further and improving existing thermomechanical treatment processes that will considerably improve the ...

Energy Technology Data Exchange (ETDEWEB)

The quantitative measurement of carbon concentration-distance curves serves as fundamental prerequisite for the evaluation of rim zone properties connected with decarburisation processes in material science. This was shown in part 1 of the present work with two samples from through-hardenable rolling bearing steel 100Cr6 (SAE 52100) austenitised in different oxidising atmospheres by position dependent determination of hardness, residual stresses, and X-ray line broadening ({l_brace}211{r_brace} {alpha}'-Fe diffraction line). In practice, it is important to predict carbon concentration-distance curves under prevailing heat treatment conditions or to conclude conversely from profile measurements. Based on a refined kinetics model of a diffusion-controlled process, part 2 therefore presents a simulation tool developed by means of the finite element method (FEM). Apart from the concentration dependence of the diffusion coefficient, it also considers the decarburisation induced ...

Energy Technology Data Exchange (ETDEWEB)

By magnetron sputtering model steel films with specific properties can be prepared for purposive surveys. By changing the deposition parameters certain properties of these films can be influenced. For this thesis steel films with 18% Cr and 8% Ni have been prepared in order to study specific parameters on the corrosion resistance of bulk stainless steel. Chemical composition, microstructure, and surface morphology of these films have been characterized. In comparison to bulk steel sheets with the same chemical composition they have a smaller grain size and a ferritic structure. In contrast to bulk steel sheets they don`t contain any nonmetallic inclusions like Mn-sulfides. The influence of these structural differences on the corrosion resistance has been studied. For this purpose the electrochemical properties of the sputter-deposited steels have been compared with the properties of steel sheets with a similar chemical composition (DIN 1.4301, AISI 304) in neutral ...

International Nuclear Information System (INIS)

This paper presents the present status of R and D activities on plasma facing components for fusion reactors, such as International Thermonuclear Experimental Reactor (ITER) and fusion demonstration reactor (DEMO). The plasma facing components (PFCs) as typified by divertor and first wall components are subjected to high heat flux and particle flux from fusion plasma. It is essential for these components to have sufficient heat removal capability and robust structure against those loadings. JAEA has been carried out to develop the ITER-PFCs which consist of copper alloys and armor materials with high thermal conductivity, such as carbon fiber composites, tungsten and beryllium. The demonstration of the thermomechanical performance of the ITER-PFCs by using mock-ups has successfully been made under close mutual cooperation between the participant countries of ITER. Currently, the activity on the development of the ITER-PFCs is in a qualification phase prior to the bulk production for ...

Energy Technology Data Exchange (ETDEWEB)

This book contains 10 lectures with the following subjects: On the effect of thermal pretreatment on the structure and creep behaviour of the alloy 800 H (V. Guttmann, J. Timm); Material properties of heat resistant ferritic and austenitic steels after cold forming (W. Bendick, H. Weber); Investigations for judging the working behaviour of components made of alloy 800 and alloy 617 under creep stress (H.J. Penkalla, F. Schubert); Creep behaviour of gas turbine materials in hot gas (K.H. Kloos et al.); Effect of small cold forming on the creep beahviour of gas turbine blades made of Nimonic 90 (K.H. Keienburg et al.); Investigations on creep fatigue alternating load strength of nickel alloys (G. Raule); Change of structure, creep fatigue behaviour and life of X20 Cr Mo V 12 1 (by G. Eggeler et al.); Investigations on thermal fatigue behaviour (K.H. Mayer et al.); Creep behaviour of similar welds of the steels 13 Cr Mo 4 4, 14 MoV 6 3, 10 Cr Mo 910 and GS-17 Cr Mo V ...

International Nuclear Information System (INIS)

Effect of helium and hydrogen production on radiation-hardening of F82H irradiated by dual or triple beam condition were investigated. The specimens used were four types of ferritic martensitic steels of F82H-std (Fe-8Cr-2W-0.2V-0.04Ta-0.1C) steels tempered at 750degC for 60 minutes, 20% cold worked F82H steel, F82H tempered for 10 minutes and non-tempered F82H steels. The irradiation was performed at 450degC to 50 dpa under simultaneous dual beams of 10.5 MeV Fe"3"+ and 1.05 MeV He"+ or triple beams of those and 380 keV H"+ ions. The ratios of He (appm)/dpa and H(appm)/dpa were 15 nad 15 (or 150) for dual and triple ion beams. The hardness of the irradiated specimens measured at room temperature using a micro indentation after the irradiations. The hardness in these F82H steels irradiated at 450degC to 18 dpa under triple beam irradiation was harder than that under dual beam irradiation. Irradiation softening and hardening under dual beams was observed in F82H ...

Energy Technology Data Exchange (ETDEWEB)

A number of screening tests were performed to determine ion species that effectively reduce wear rates when implanted in four industrial steels. Ball bearing steel 100Cr6 (AISI 52100) showed a wear rate reduction by a factor of 20 when implanted with carbon dioxide to a dose of 5x10{sup 17} cm{sup -2} with a non-mass-separated ion beam and by a factor of {>=}20 when implanted with 5x10{sup 17} cm{sup -2} oxygen ions. For the ferritic and martensite steels X90CrMoV18 (AISI 440B, unhardened and hardened) also a strong wear reduction after implantation of oxygen ions was found. Co-implantation of aluminum and oxygen also reduces wear rates of X90CrMoV18, of S6-5-2 (AISI M2), and of 100Cr6, respectively. For comparison, thin oxide layers were grown in a low-temperature thermal oxidation process. These experiments also yielded reduced wear rates by a factor of 10. The surfaces were investigated and characterized by XPS, SIMS, TEM, and microhardness measurements to ...

Energy Technology Data Exchange (ETDEWEB)

TRITEX was a pumped loop with Pb-15.8Li, fabricated from steel 1.4922. In contact with the molten eutectic were also molybdenum, vanadium and armco-iron. The loop was originally designed to investigate tritium extraction using solid getter metals. Over the years the goal changed to the study of metals, corrosion products and purification of the eutectic mixture. Therefore many modifications were done. The first part of this report describes TRITEX. All parts were enclosed in thermoboxes for a homogeneous temperature. One test section was in an argon glove box and could be opened during operation. Other special equipment`s were: permeation membranes and liquid-metal-covergas-interfaces to study the transport of H{sub 2}, D{sub 2} and {sup 3}H, different purification devices, a quartz observation window to see the liquid metal surface, 4 different kinds of flow measurements, level indicators, freeze valves. The second part describes loop operation. Between 1989 and 1996, the eutectic ...

International Nuclear Information System (INIS)

Alloy 800 and Alloy 600 are well known for their resistance to corrosion in an aqueous medium at high pressure and temperature, for which they have been widely used for more than 3 decades in different structural components of water refrigerated nuclear reactors, especially as material for the steam generator tubes (SG) in these nuclear plants. The SG tubes in the Atucha I and Embalse Nuclear Plants are made with Alloy 800. The speed of corrosion of these materials in a reactor's refrigerant medium, while very small is perfectly measurable and can be described by parabolic or logarithmic type kinetics. In other words this speed is high in the first states of growth during the formation of a protective oxide film but then drops to almost stationary values. One characteristic of these films is the formation of a double layer (or duplex): i) an internal adhering layer, of approximately constant thickness, formed by small microcrystals (#<=#0.05 mm), ii) a less adhering external one, ...